KR20180113228A - Non-woven fabric for Disposable absorbent articles - Google Patents
Non-woven fabric for Disposable absorbent articles Download PDFInfo
- Publication number
- KR20180113228A KR20180113228A KR1020170044148A KR20170044148A KR20180113228A KR 20180113228 A KR20180113228 A KR 20180113228A KR 1020170044148 A KR1020170044148 A KR 1020170044148A KR 20170044148 A KR20170044148 A KR 20170044148A KR 20180113228 A KR20180113228 A KR 20180113228A
- Authority
- KR
- South Korea
- Prior art keywords
- nonwoven fabric
- disposable absorbent
- emulsion
- hydrophilic
- fiber
- Prior art date
Abstract
Description
본 발명은 친수성 유제가 표면에 처리된 섬유와 소수성 유제가 표면에 처리된 섬유를 포함하는, 투과성이 증가되고 역류량이 감소된 일회용 흡수제품용 부직포에 관한 것이다.The present invention relates to a nonwoven fabric for disposable absorbent articles having increased permeability and reduced backflow, wherein the hydrophilic emulsion comprises a surface-treated fiber and the hydrophobic emulsion comprises a surface-treated fiber.
일반적으로 일회용 흡수제품은 사람이 생리적 작용에 의해 배설하는 체액을 흡수하는 제품 즉, 오줌, 대변을 흡수하는 제품으로, 좀더 구체적으로는 유아가 사용하는 기저귀(baby diaper), 요실금자가 사용하는 기저귀(adult diaper), 여성용 생리대(sanitary napkin), 및 팬티라이너(panty liner) 등이 있다.Generally, the disposable absorbent article is a product that absorbs body fluids excreted by a physiological action, that is, a product that absorbs urine and feces. More specifically, the disposable absorbent article includes a baby diaper, a diaper adult diaper, sanitary napkin, and panty liner.
상기 종래 일회용 흡수제품인, 기저귀는 착용시 착용자의 피부와 직접 접촉하는 액체투과성의 상부시트(top sheet)와, 착용시 외부표면을 형성하는 액체불투과성의 배면시트(back sheet)와, 액체투과성의 상부시트와 액체불투과성의 배면시트 사이에 위치하는 고흡수성의 고분자(SAP:Super Absorbent Polymer)를 포함하는 흡수체(Absorbent core)로 이루어져 있다. The disposable absorbent product of the prior art has a liquid permeable top sheet in direct contact with the wearer's skin when worn, a liquid impermeable back sheet forming an outer surface when worn, And an absorber core including a superabsorbent polymer (SAP) positioned between the upper sheet and the liquid-impermeable back sheet.
이들 일회용 기저귀의 구성요소 중 액체투과성의 상부시트로는 체액이 흡수시트로 신속하게 투과할 수 있도록 합성부직포 또는 구멍이 형성된 필름이 사용된다. 합성부직포는 흡수체에 체액이 빨리 전달되도록 하기 위하여 통상 소수성 섬유에 친수성 처리를 하여 사용하고 있다. Among the components of these disposable diapers, a synthetic nonwoven fabric or a hole-formed film is used as the liquid-permeable upper sheet so that the body fluids can be quickly transmitted to the absorbent sheet. The synthetic nonwoven fabric is usually hydrophilic treated with a hydrophobic fiber in order to rapidly transfer the body fluids to the absorber.
액체불투과성의 배면시트는 일회용 기저귀에 의해 흡수되고 투과된 체액이 흡수체 밑으로 샘이 발생하여 착용자의 의복이나 주변 환경이 오염되는 것을 방지하는 역할을 하며, 폴리에틸렌 필름 등의 소수성 소재를 사용하고 있다.The liquid impermeable back sheet is absorbed by the disposable diaper and prevents the permeated body fluids from leaking under the absorbent body to prevent contamination of the clothes or the surrounding environment of the wearer, and a hydrophobic material such as a polyethylene film is used .
상기 흡수체는 통상적으로 솜털펄프(fluff pulp), 고흡수성 수지(super absorbent polymer)와 이를 포장하는 티슈(tissue) 등으로 이루어지며, 액체투과성의 상부시트를 투과한 체액을 빠른 속도로 흡수하고, 일단 흡수된 체액이 다시 피부와 접촉하는 것을 방지하기 위해 체액을 흡수하고 보유하는 역할을 한다.The absorbent body is typically made up of fluff pulp, super absorbent polymer and a tissue packing the same. The absorbent absorbs the body fluid permeated through the liquid-permeable upper sheet at a high speed, It absorbs and retains the body fluids to prevent the absorbed body fluids from coming into contact with the skin again.
종래, 열풍 혹은 가열 롤의 열원을 이용하여 열융착을 통해 부직포를 형성하는 복합섬유는 일회용 흡수제품, 생활용품, 필터와 같은 산업자재로 널리 사용되고 있다. 이중 일회용 흡수제품은 피부에 직접 접촉하여, 촉감이 좋고 오줌, 혈액 등의 액체 투과성(친수성)이 우수하며 체액 등의 잔류량과 역류량이 적어야 한다. 하지만, 기존의 일회용 흡수제품의 경우 액체 투과성이 너무 좋아지면 체액의 잔류량과 역류량이 오히려 증가하게 되는 문제점이 있다. BACKGROUND ART [0002] Conventionally, conjugated fibers that form a nonwoven fabric by heat welding using a heat source of a hot air or a heating roll are widely used as industrial materials such as disposable absorbent articles, household articles, and filters. These disposable absorbent products are in direct contact with the skin and have a good feel and good liquid permeability (hydrophilic property) such as urine and blood, and should have a small residual amount and back flow amount of body fluids. However, in the case of a conventional disposable absorbent product, if the liquid permeability is excessively improved, there is a problem that the residual amount of the body fluid and the backflow amount are rather increased.
또한, 일회용 흡수제품의 상부시트(Topsheet) 부분에 부직포를 적용하고 있는 데, 부직포를 구성하는 섬유의 형태에 따라 단섬유 부직포, 장섬유 부직포로 구분될 수 있으며, 통상적으로 일회용 흡수제품에 적용되는 단섬유 부직포의 경우에는 구성되는 섬유가 폴리프로필렌으로 소수성 특성을 가지므로 일회용 흡수제품의 상부시트용으로 적용하기 위해서는 섬유에 친수가공이 필요하다. 단섬유 부직포의 경우에는 친수성을 부여하는 유제처리를 섬유 방사시 처리하여 친수성을 가지는 부직포를 제조하고 있다. In addition, a nonwoven fabric is applied to the topsheet portion of the disposable absorbent article. Depending on the type of the fibers constituting the nonwoven fabric, the nonwoven fabric may be divided into a short fiber nonwoven fabric and a long fiber nonwoven fabric. In the case of short-fiber non-woven fabrics, since the fibers constituting the fibers have hydrophobic properties due to polypropylene, hydrophilic processing is required to apply the fibers to the upper sheet of the disposable absorbent article. In the case of a short-fiber nonwoven fabric, an emulsion treatment imparting hydrophilicity is treated at the time of fiber spinning to produce a hydrophilic nonwoven fabric.
상기와 같은 일회용 흡수제품의 경우, 상부시트에 의해 투과된 체액이 흡수체에 모두 흡수되어야 하나, 친수성 유제가 표면에 처리된 섬유만으로 제조된 부직포를 이용한 상부시트의 경우, 흡수체에 모두 흡수되지 않고, 다시 역류하여 피부가 짓무르게 되게 특히, 자극에 민감한 신생아 및 유아들의 피부에 발진을 일으키는 등 좋지 않은 영향을 주는 문제점이 있다. 또한, 일회용 흡수제품의 상부시트는 착용시 착용자의 피부와 접촉하는 면을 포함하는데, 일반적으로 상부시트의 경우 배뇨 후 착용자의 피부와 넓은 면이 접촉하여 체액이 기저귀 내에 흡수되는 면적도 지나치게 넓어져 착용감이 좋지 않으며, 착용자의 피부에 좋지 않은 영향을 미치는 단점이 있다. 또한, 체액 등의 투과성이 좋아질수록 체액의 잔류면적과 역류량이 오히려 증가하게 되는 문제점이 있어, 양립하는 성능의 부직포를 얻기 어렵다.In the case of the disposable absorbent article as described above, the body fluid permeated by the upper sheet must be absorbed by the absorber in its entirety, but in the case of the upper sheet using the nonwoven fabric produced only by the fibers treated with the hydrophilic emulsion, There is a problem that adverse effects such as back flushing can cause skin irritation, especially rash on newborn infants and infants who are sensitive to irritation. In addition, the upper sheet of the disposable absorbent article includes a surface that comes into contact with the wearer's skin when worn. Generally, in the case of the upper sheet, the area of the absorbent body fluid absorbed into the diaper is too wide There is a disadvantage that it is not comfortable to wear and adversely affects the wearer's skin. Further, as the permeability of the body fluid or the like becomes better, the residual area of the body fluid and the amount of backflow increase rather than increase, and it is difficult to obtain a nonwoven fabric having compatible performance.
이에, 상기와 같이 부직포로 제조된 상부시트를 적용하여 제조된 일회용 흡수제품에 있어, 상부시트를 투과하여 흡수된 체액이 흡수체에 흡수되어 다시 역류되지 않으면서, 투과성이 우수하면서, 체액 중량 대비 흡수되는 부직포 또는 상부시트의 단위면적이 감소될 수 있는 일회용 흡수제품용 부직포를 제조하고자 하였다. Thus, in the disposable absorbent article manufactured by applying the upper sheet made of the nonwoven fabric as described above, the absorbed body fluids permeated through the upper sheet are absorbed by the absorbent body and are not backflowed again, Woven fabric or a nonwoven fabric for a disposable absorbent article in which the unit area of the topsheet can be reduced.
본 발명의 목적은 친수성 유제가 표면에 처리된 섬유와 소수성 유제가 표면에 처리된 섬유를 포함하는, 투과성이 증가되고 역류량이 감소된 일회용 흡수제품용 부직포를 제공하는 것이다.It is an object of the present invention to provide a nonwoven fabric for a disposable absorbent article having increased permeability and reduced backflow amount, wherein the hydrophilic emulsion comprises a surface treated fiber and a hydrophobic emulsion surface treated fiber.
본 발명의 다른 목적은 상기 일회용 흡수제품용 부직포를 포함하는 일회용 흡수제품용 상부시트를 제공하는 것이다.It is another object of the present invention to provide a topsheet for a disposable absorbent article comprising the nonwoven for the disposable absorbent article.
본 발명의 다른 목적은 상기 일회용 흡수제품용 부직포 또는 상부시트를 포함하는 일회용 흡수제품을 제공하는 것이다.It is another object of the present invention to provide a disposable absorbent product comprising the nonwoven fabric or top sheet for the disposable absorbent article.
본 발명에서는 친수성 유제가 표면에 처리된 섬유와 소수성 유제가 표면에 처리된 섬유를 포함하는, 부직포와 상기 부직포를 포함하는 일회용 흡수제품용 상부시트, 그리고 상기 부직포 또는 상기 상부시트를 포함하는, 일회용 흡수제품의 경우, 친수성 유제가 표면에 처리된 섬유만을 이용하여 제조된 일회용 흡수제품용 상부시트에 비해, 부직포 또는 상부시트를 투과하여 흡수된 체액이 흡수체에 흡수되어 다시 역류되지 않으면서, 투과성이 우수하며, 체액 중량 대비 흡수되는 부직포 또는 상부시트의 단위면적이 감소되어, 착용감이 우수한 것을 확인하고 본 발명을 완성하였다. The present invention relates to a disposable absorbent article comprising a nonwoven fabric and a top sheet for disposable absorbent articles comprising the nonwoven fabric, wherein the hydrophilic emulsion comprises a surface-treated fiber and a hydrophobic emulsion, In the case of the absorbent product, compared to the top sheet for the disposable absorbent article produced by using only the fiber treated on the surface of the hydrophilic emulsion, the absorbed body fluid permeated through the nonwoven fabric or the top sheet is absorbed by the absorber and does not backflow again, And the unit area of the nonwoven fabric or the top sheet absorbed relative to the weight of the body fluid is reduced, and the wearing feeling is excellent. Thus, the present invention has been completed.
상기 목적을 달성하기 위하여, 본 발명은 친수성 유제가 표면에 처리된 섬유와 소수성 유제가 표면에 처리된 섬유를 포함하는, 투과성이 증가되고 역류량이 감소된 일회용 흡수제품용 부직포를 제공한다. In order to achieve the above object, the present invention provides a nonwoven fabric for disposable absorbent articles having increased permeability and reduced backflow amount, wherein the hydrophilic emulsion comprises a surface treated fiber and a hydrophobic emulsion surface treated fiber.
상기 용어 "일회용 흡수제품"은 사람이 생리적 작용에 의해 배설하는 체액을 흡수하는 제품 즉, 오줌, 대변을 흡수하는 제품으로, 좀더 구체적으로는 유아가 사용하는 기저귀(baby diaper), 요실금자가 사용하는 기저귀(adult diaper) 및 여성용 생리대(sanitary napkin), 팬티라이너(panty liner) 등이 있다.The term "disposable absorbent product" refers to a product that absorbs body fluids excreted by a physiological action, that is, a product that absorbs urine and feces, and more specifically, a baby diaper used by infants, Adult diapers, sanitary napkins, panty liners, and the like.
상기 기저귀 등의 일회용 흡수제품은 착용시 착용자의 피부와 직접 접촉하는 액체투과성의 상부시트(top sheet)와, 착용시 외부표면을 형성하는 액체불투과성의 배면시트(back sheet)와, 액체투과성의 상부시트와 액체불투과성의 배면시트 사이에 위치하는 고흡수성의 고분자(SAP:Super Absorbent Polymer)를 포함하는 흡수체(Absorbent core)로 이루어져 있다.The disposable absorbent article such as the diaper has a liquid permeable top sheet that directly contacts the wearer's skin when worn, a liquid impermeable back sheet that forms an outer surface when worn, And an absorber core including a superabsorbent polymer (SAP) positioned between the upper sheet and the liquid-impermeable back sheet.
본 발명에서 상기 용어 "상부시트"는 기저귀 등의 일회용 흡수제품의 착용시 착용자의 피부와 직접 접촉하는 가장 탑 부분의 시트로, 액체투과성 기능을 가진다. In the present invention, the term "top sheet" is the topmost sheet that directly contacts the skin of the wearer when wearing a disposable absorbent article such as a diaper, and has a liquid permeable function.
본 발명의 상기 친수성 유제가 표면에 처리된 섬유와 소수성 유제가 표면에 처리된 섬유를 포함하는 부직포는 일회용 흡수제품용 상부시트에 적용될 수 있으며, 상기 일회용 흡수제품용 부직포 또는 상기 부직포를 포함하는 상부시트는 기저귀 등의 일회용 흡수제품에 적용될 수 있다. The nonwoven fabric of which the hydrophilic emulsion of the present invention has been treated on the surface and the fiber comprising the hydrophobic emulsion treated surface can be applied to an upper sheet for a disposable absorbent article, The sheet can be applied to disposable absorbent articles such as diapers.
본 발명에서 상기 용어 "친수성 유제가 표면에 처리된 섬유"는 친수성 유제 처리에 의해 섬유의 표면이 친수성을 지닌다. In the present invention, the term "fiber treated with a hydrophilic emulsion" means that the surface of the fiber is hydrophilic by the hydrophilic emulsion treatment.
본 발명에서 상기 용어 "소수성 유제가 표면에 처리된 섬유"는 소수성 유제 처리에 의해 섬유의 표면이 소수성을 지닌다.In the present invention, the term "fiber treated with a hydrophobic emulsion" means that the surface of the fiber is hydrophobic by the hydrophobic emulsion treatment.
상기 친수성, 소수성 유제가 처리되는 섬유는 일반적인 단일 성분 섬유 또는 심초형 복합섬유일 수 있다. The fibers treated with the hydrophilic, hydrophobic emulsions may be conventional single component fibers or core-sheath type conjugated fibers.
상기 단일 성분 섬유는 고밀도 폴리에틸렌, 선형저밀도 폴리에틸렌, 및 폴리프로필렌로 이루어진 폴리올레핀계 섬유에서 선택되는 하나이거나, 또는 폴리에틸렌테레프탈레이트, 폴리트리메틸렌테레프탈레이트, 및 폴리부틸렌테레프탈레이트로 이루어진 폴리에스터계 섬유에서 선택되는 하나일 수 있다. Wherein the single-component fiber is one selected from polyolefin-based fibers consisting of high-density polyethylene, linear low-density polyethylene, and polypropylene, or a polyester fiber composed of polyethylene terephthalate, polytrimethylene terephthalate, and polybutylene terephthalate Can be selected.
상기 심초형 복합섬유의 초(Sheath)부는 폴리에틸렌, 폴리프로필렌, 및 저융점 폴리에스터 수지로 이루어진 군에서 선택되는 하나이며, 심부(Core)는 폴리프로필렌, 폴리에틸렌테레프탈레이트, 폴리트리메틸렌테레프탈레이트, 및 폴리부틸렌테레프탈레이트 수지로 이루어진 군에서 선택되는 하나 일 수 있다. 또한 심초 수지간의 융점이 10 이상 차이 나는 것이 바람직하다.Wherein the sheath portion of the core-sheath type conjugate fiber is one selected from the group consisting of polyethylene, polypropylene, and low melting point polyester resin, and the core is selected from the group consisting of polypropylene, polyethylene terephthalate, polytrimethylene terephthalate, Polybutylene terephthalate resin, and polybutylene terephthalate resin. It is also preferable that the melting point of the core-sheath resin is different by 10 or more.
친수성 유제는 일회용 흡수제품의 상부시트용 부직포에 사용되는 단일 성분 섬유 또는 심초형 복합섬유의 표면에 처리되어 액체의 투과성을 증대시키는 역할을 한다. 보다 구체적으로는 착용감 향상을 위해 실리콘계 성분을 5~10% 이내로 포함하는 내구친수성 유제일 수 있다. 한편, 소수성 유제는 일회용 흡수제품의 배면시트 혹은 사이드게더용 부직포에 사용되는 단섬유의 표면에 처리되어 액의 누출을 방지하는 역할을 하는 데, 본 발명에서는 친수성 유제가 처리된 섬유와 소수성 유제가 처리된 섬유를 함께 사용하여 상부시트용 부직포를 제조하였다. 상기 소수성 유제는 착용감 및 소수성 향상을 위해 실리콘계 성분을 5~40% 이내로 포함하고, 소수성 발현을 위해 폴리알킬렌 옥사이드 성분을 10~40% 이내로 포함하며, 폴리알킬렌옥사이드의 탄소수는 16개 이상인 소수성 유제일 수 있다. The hydrophilic emulsion is applied to the surface of single-component fibers or core-sheath type conjugate fibers used in the nonwoven fabric for the top sheet of the disposable absorbent product to increase the permeability of the liquid. More specifically, it may be a durable hydrophilic emulsion containing a silicone component in an amount of 5 to 10% for improving the feeling of wearing. On the other hand, the hydrophobic emulsion is treated on the surface of the short fibers used for the back sheet of the disposable absorbent article or the side getter nonwoven fabric to prevent the leakage of the liquid. In the present invention, the hydrophilic emulsion- The treated fibers were used together to produce a nonwoven for the topsheet. The hydrophobic emulsion preferably contains a silicone component in an amount of 5 to 40% for enhancing comfortability and hydrophobicity, a polyalkylene oxide component within 10 to 40% for hydrophobic development, and a polyalkylene oxide having 16 or more hydrophobic May be emulsion.
본 발명에서, 상기 일회용 흡수제품용 부직포를 제조하기 위하여, 부직포를 구성하는 단일 성분 섬유 또는 심초형 복합섬유를 먼저 제조할 수 있으며, 단섬유의 제조방법은 다음과 같다. In the present invention, in order to produce the nonwoven fabric for disposable absorbent article, the single component fiber or the core-sheath type conjugate fiber constituting the nonwoven fabric may be produced first, and the method for producing the monofilament is as follows.
본 발명의 단일 성분 섬유 또는 심초형 복합섬유를 제조하는 방법은 통상적으로 알려진 열가소성 섬유의 제조방법과 동일하며, 이는 방사, 연신, 권축 및 절단의 공정으로 나뉘어져 있으며, 필요에 따라 원-스텝(One-Step) 혹은 투-스텝(Two-Step) 섬유제조공정을 선택함으로써 제조가 가능하다. The method for producing the single-component fiber or the core-sheath type conjugate fiber of the present invention is the same as the conventional method for producing the thermoplastic fiber, and is divided into spinning, drawing, crimping and cutting processes. -Step) or a two-step fiber manufacturing process.
상기의 방사공정 중 친수성, 소수성 유제를 부착하는 방법에는 다양한 방법이 있으며 방사, 연신공정에서 접촉식 롤러를 이용하여 유제를 1차적으로 부착하고 분무식 혹은 침지방법으로 최종적으로 유제를 부착시킴으로써 친수성과 소수성을 각각 단일 성분 섬유 또는 심초형 복합섬유에 부여할 수 있다.There are various methods of attaching the hydrophilic and hydrophobic emulsions in the above spinning process. In the spinning and stretching processes, the emulsions are primarily attached using contact rollers, and the emulsions are finally attached by spraying or immersion, Hydrophobicity can be imparted to the single component fiber or the core-sheath type conjugated fiber, respectively.
일회용 흡수제품에 있어, 부직포의 적용은 부직포의 제조 공법에 따라 사용되는 부분이 구분되어 있다. 본 발명에서는 부직포를 구성하는 섬유로 단일 성분 섬유 또는 심초형 복합성유를 사용할 수 있다. 또한, 상기 부직포는 친수성 유제가 표면에 처리된 섬유와 소수성 유제가 표면에 처리된 섬유를 포함하며, 상기 친수성 유제가 표면에 처리된 섬유와 소수성 유제가 표면에 처리된 섬유의 혼합 비율은 20:80 내지 30:70의 비율이며, 보다 구체적으로 40:60 내지 60:40의 비율로 혼합될 수 있다.In the disposable absorbent product, the application of the nonwoven fabric is divided into the parts used in accordance with the manufacturing method of the nonwoven fabric. In the present invention, single component fibers or core-sheath complex oil may be used as the fibers constituting the nonwoven fabric. The non-woven fabric includes fibers having a surface-treated hydrophilic emulsion and fibers having a surface treated with a hydrophobic emulsion. The blend ratio of the fiber on which the hydrophilic emulsion is surface-treated and the fiber on which the hydrophobic emulsion is surface-treated is 20: 80 to 30:70, and more specifically in a ratio of 40:60 to 60:40.
상기 친수성 유제가 표면에 처리된 섬유와 소수성 유제가 표면에 처리된 섬유를 상기의 비율로 블렌딩한 후, 카딩(Carding) 하여 카딩 웹을 형성하고, 열풍을 이용한 에어스루본드 혹은 써멀본드(포인트본드) 방법으로 부직포를 얻을 수 있다. 또한, 상기 제조된 일회용 흡수제품용 부직포를 일회용 흡수제품용 상부시트에 이용이 가능하다. 상기 에어스루본드 방법을 이용해 제조한 부직포 시트는 18g/m2 내지 60g/m2의 범위, 써멀본드(포인트본드) 방법을 이용해 제조한 부직포 시트는 18g/m2내지 25g/m2의 범위에서 선택될 수 있다. The fibers treated with the hydrophilic emulsions on the surface and the fibers treated with the hydrophobic emulsions are blended at the above ratios, carding is performed to form a carded web, and air through or heat bonds using hot air ) Method to obtain a nonwoven fabric. In addition, the nonwoven fabric for the disposable absorbent article can be used for the top sheet for disposable absorbent products. Non-woven fabric sheet manufactured by using the air-through bonding method is 18g / m 2 to the range of 60g / m 2, a thermal-bonding a nonwoven fabric sheet made (point-bonding), using the method is in the range of 18g / m 2 to 25g / m 2 Can be selected.
본 발명의 친수성 유제가 표면에 처리된 섬유와 소수성 유제가 표면에 처리된 섬유를 포함하는 부직포는 체액의 투과성이 증가되고 역류량이 감소되며, 체액이 흡수되는 단위면적이 감소되는 특징이 있다. The nonwoven fabric of which the hydrophilic emulsions of the present invention have been treated on the surface and the fibers containing the hydrophobic emulsions have been treated on the surface thereof is characterized in that the permeability of the body fluid is increased, the amount of backwash is reduced, and the unit area in which body fluids are absorbed is reduced.
다른 하나의 양태로, 본 발명은 상기 일회용 흡수제품용 부직포를 포함하는 일회용 흡수제품용 상부시트를 제공한다. In another aspect, the present invention provides an upper sheet for a disposable absorbent article comprising the nonwoven for the disposable absorbent article.
본 발명에서 용어 "일회용 흡수제품", "부직포"에 대한 설명은 전술한 바와 같다. The terms "disposable absorbent article "," nonwoven fabric "and " nonwoven fabric "
본 발명에서 용어 "상부시트"는 일회용 흡수제품 착용시 착용자의 피부와 직접 접촉하는 액체투과성의 시트로, 체액을 1차적으로 흡수하는 역할을 한다. 다음으로, 흡수체는 상부시트를 투과한 체액을 빠른 속도로 흡수하여, 일단 흡수된 체액이 다시 피부와 접촉하는 것을 방지하기 위해 체액을 흡수하고 보유하는 역할을 한다. The term "top sheet " in the present invention is a liquid-permeable sheet that directly contacts the wearer's skin when the disposable absorbent article is worn, and serves to primarily absorb body fluids. Next, the absorber absorbs and retains body fluids to absorb body fluids that have permeated the upper sheet at a high rate and prevent once the absorbed body fluids come into contact with the skin again.
다른 하나의 양태로, 본 발명은 상기 일회용 흡수제품용 부직포 또는 일회용 흡수제품용 상부시트를 포함하는 일회용 흡수제품을 제공한다. In another aspect, the present invention provides a disposable absorbent article comprising the nonwoven for the disposable absorbent article or the top sheet for the disposable absorbent article.
본 발명에서, 용어 "일회용 흡수제품" "부직포", "상부시트"에 대한 설명은 전술한 바와 같으므로, 생략한다. In the present invention, the terms "disposable absorbent article "," nonwoven fabric ", and "top sheet"
본 발명의 친수성 유제가 표면에 처리된 섬유와 소수성 유제가 표면에 처리된 섬유를 포함하는, 일회용 흡수제품용 부직포 또는 상기 부직포를 포함하는 일회용 흡수제품용 상부시트, 상기 부직포 또는 상부시트를 포함하는 일회용 흡수제품은 상기 부직포를 투과하여 흡수된 체액이 흡수체에 흡수되어 다시 역류되지 않으면서, 체액 중량 대비 흡수되는 부직포 또는 상부시트의 단위면적이 감소되어, 착용감이 우수하다. A topsheet for a disposable absorbent article comprising a nonwoven fabric for disposable absorbent articles or a topsheet for a disposable absorbent article comprising the nonwoven fabric or topsheet, wherein the hydrophilic emulsion of the present invention comprises a surface treated fiber and a hydrophobic emulsion, The disposable absorbent article is excellent in wearing feeling because the absorbent body fluid absorbed by the nonwoven fabric is absorbed by the absorbent body and is not backflowed again, and the unit area of the nonwoven fabric or the top sheet absorbed relative to the body fluid weight is reduced.
이하, 본 발명을 실시예에 의해 보다 상세히 설명한다. 단, 하기 실시예는 본 발명을 예시하는 것일 뿐, 본 발명의 내용이 하기의 실시예에 한정되는 것은 아니다.Hereinafter, the present invention will be described in more detail by way of examples. However, the following examples are illustrative of the present invention, and the contents of the present invention are not limited to the following examples.
1. 친수성 유제가 표면에 처리된 섬유 제조1. Fabrication of surface-treated fibers by hydrophilic emulsions
실시예 1.Example 1.
방사공정에서 접촉식 롤러를 이용하여 유제를 1차적으로 부착하고 분무식 혹은 침지방법으로 최종적으로 유제를 부착시킴으로써 친수성 유제가 표면에 처리된 단일 성분의 폴리프로필렌 섬유를 제조하였다. In the spinning process, a single component polypropylene fiber with hydrophilic emulsions was prepared by first attaching the emulsion using contact rollers and finally attaching the emulsion by spraying or dipping method.
실시예 2.Example 2.
방사공정에서 접촉식 롤러를 이용하여 유제를 1차적으로 부착하고 분무식 혹은 침지방법으로 최종적으로 유제를 부착시킴으로써 친수성 유제가 표면에 처리된 초부(Sheath)성분은 고밀도 폴리에틸렌, 심부(Core)성분은 폴리프로필렌인 섬유를 제조하였다. In the spinning process, the sheath component treated with a hydrophilic emulsion on the surface by attaching the emulsion to the primary by using a contact type roller and finally attaching the emulsion by a spraying or immersion method has a high density polyethylene and a core component Polypropylene fibers were prepared.
2. 소수성 유제가 표면에 처리된 섬유 제조2. Manufacture of surface-treated fibers by hydrophobic emulsions
실시예 3.Example 3.
방사공정에서 접촉식 롤러를 이용하여 유제를 1차적으로 부착하고 분무식 혹은 침지방법으로 최종적으로 유제를 부착시킴으로써 소수성 유제가 표면에 처리된 단일 성분의 폴리프로필렌 섬유를 제조하였다.In the spinning process, a single-component polypropylene fiber with a hydrophobic emulsion treated on its surface was prepared by first attaching the emulsion using contact rollers and finally attaching the emulsion by spraying or immersion.
실시예 4.Example 4.
방사공정에서 접촉식 롤러를 이용하여 유제를 1차적으로 부착하고 분무식 혹은 침지방법으로 최종적으로 유제를 부착시킴으로써 소수성 유제가 표면에 처리된 초부(Sheath)성분은 고밀도 폴리에틸렌, 심부(Core)성분은 폴리프로필렌인 섬유를 제조하였다. In the spinning process, the primary component of the emulsion is adhered to the surface of the hydrophilic emulsion by attaching the emulsion to the primary emulsion using a contact type roller, and finally the emulsion is adhered by a spraying or immersion method. The sheath component is a high density polyethylene, Polypropylene fibers were prepared.
3. 일회용 흡수제품용 부직포 제조3. Manufacture of non-woven fabric for disposable absorbent products
실시예 5.Example 5.
실시예 1에서 제조된 친수성 유제가 표면에 처리된 섬유와 실시예 3의 소수성 유제가 표면에 처리된 섬유 또는 실시예 2에서 제조된 친수성 유제가 표면에 처리된 섬유와 실시예 4의 소수성 유제가 표면에 처리된 섬유를 20:80 내지 30:70의 비율로 블렌딩 한 후, 카딩(Carding)하여 카딩 웹을 제조하였으며, 열풍을 이용한 에어스루본드 혹은 써멀본드(포인트본드) 방법으로 부직포를 제조하였다. The fiber prepared by treating the surface of the hydrophilic emulsion prepared in Example 1, the fiber treated with the hydrophobic emulsion of Example 3 or the hydrophilic emulsion prepared in Example 2 and the hydrophobic emulsion of Example 4 The treated fibers on the surface were blended at a ratio of 20:80 to 30:70, carded to produce a carded web, and a nonwoven fabric was produced by an air through bond or a thermal bond (point bond) method using hot air .
실시예 6.Example 6.
상기 친수성 유제가 표면에 처리된 섬유와 소수성 유제가 표면에 처리된 섬유의 혼합 비율만을 달리한 것을 제외하고, 실시예 5와 동일한 방법으로, 부직포를 제조하였다. A nonwoven fabric was produced in the same manner as in Example 5, except that the hydrophilic emulsion had a surface-treated fiber and the hydrophobic emulsion had a surface-treated fiber having a different mixing ratio.
실시예 7.Example 7.
상기 친수성 유제가 표면에 처리된 섬유와 소수성 유제가 표면에 처리된 섬유의 혼합 비율만을 달리한 것을 제외하고, 실시예 5와 동일한 방법으로, 부직포를 제조하였다. A nonwoven fabric was produced in the same manner as in Example 5, except that the hydrophilic emulsion had a surface-treated fiber and the hydrophobic emulsion had a surface-treated fiber having a different mixing ratio.
비교예 1.Comparative Example 1
실시예 1에서 제조된 친수성 유제가 표면에 처리된 섬유만을 이용하여 부직포를 제조한 것을 제외하고는 실시예 5와 동일한 방법으로 부직포를 제조하였다. A nonwoven fabric was prepared in the same manner as in Example 5, except that the nonwoven fabric was prepared using only the fibers having been treated on the surface of the hydrophilic emulsion prepared in Example 1.
4. 일회용 흡수제품용 상부시트 제조4. Manufacture of top sheet for disposable absorbent products
실시예 8.Example 8.
상기 실시예 5에서 제조된 상부시트용 부직포를 이용하여 적층 등의 방법으로 일회용 흡수제품용 상부시트를 제조하였다. An upper sheet for a disposable absorbent article was prepared by lamination or the like using the nonwoven fabric for an upper sheet prepared in Example 5 above.
실시예 9.Example 9.
상기 실시예 6에서 제조된 상부시트용 부직포를 이용한 것을 제외하고, 실시예 8과 동일한 방법으로 일회용 흡수제품용 상부시트를 제조하였다. An upper sheet for a disposable absorbent article was prepared in the same manner as in Example 8 except that the nonwoven fabric for an upper sheet prepared in Example 6 was used.
실시예 10.Example 10.
상기 실시예 7에서 제조된 상부시트용 부직포를 이용한 것을 제외하고, 실시예 8과 동일한 방법으로 일회용 흡수제품용 상부시트를 제조하였다. An upper sheet for a disposable absorbent article was prepared in the same manner as in Example 8 except that the nonwoven fabric for an upper sheet prepared in Example 7 was used.
비교예 2.Comparative Example 2
상기 비교에 1에서 제조된 상부시트용 부직포를 이용한 것을 제외하고, 실시예 8과 동일한 방법으로 상부시트를 제조하였다.An upper sheet was prepared in the same manner as in Example 8, except that the nonwoven fabric for the upper sheet produced in Example 1 was used.
5. 기저귀 제조5. Diaper manufacturing
실시예 11.Example 11.
상기 실시예 8에서 제조된 상부시트를 이용하여, 상부시트, 흡수체, 배면시트로 이루어진 간단한 구조의 기저귀를 제조하였다. Using the upper sheet manufactured in Example 8, a simple diaper comprising an upper sheet, an absorbent body and a back sheet was produced.
실시예 12.Example 12.
상기 실시예 9에서 제조된 상부시트를 이용하여, 기저귀를 제조한 것을 제외하고는 실시예 11과 동일한 방법으로 기저귀를 제조하였다. A diaper was prepared in the same manner as in Example 11, except that the diaper was produced using the upper sheet produced in Example 9 above.
실시예 13.Example 13.
상기 실시예 10에서 제조된 상부시트를 이용하여, 기저귀를 제조한 것을 제외하고는 실시예 11과 동일한 방법으로 기저귀를 제조하였다. A diaper was prepared in the same manner as in Example 11, except that the diaper was produced using the top sheet produced in Example 10 above.
비교예 3.Comparative Example 3
상기 비교예 2에서 제조된 상부시트를 이용하여, 기저귀를 제조한 것을 제외하고는 실시예 11과 동일한 방법으로 기저귀를 제조하였다. A diaper was prepared in the same manner as in Example 11, except that the diaper was prepared using the top sheet produced in Comparative Example 2. [
실험예Experimental Example 1: 부직포, 상부시트 또는 기저귀의 투과성 비교 1: Comparison of permeability of nonwoven fabric, top sheet or diaper
상기 실시예들과 비교예들에서 제조된 부직포, 상부시트 또는 기저귀를 이용하여 투과성을 측정하였다. 그 결과, 실시예들을 이용한 부직포, 상부시트, 또는 기저귀의 투과성이 비교예들을 이용한 부직포, 상부시트, 또는 기저귀에 비해 우수하였다. The permeability was measured using the nonwoven fabric, the top sheet or the diaper prepared in the above Examples and Comparative Examples. As a result, the permeability of the nonwoven fabric, the top sheet, or the diaper using the embodiments was superior to that of the nonwoven fabric, the top sheet, or the diaper using the comparative examples.
실험예Experimental Example 2: 부직포, 상부시트 또는 기저귀의 역류성 비교 2: Comparison of reflux of nonwoven fabric, top sheet or diaper
상기 실시예들과 비교예들에서 제조된 부직포, 상부시트 또는 기저귀를 이용하여 역류성을 측정하였다. 그 결과, 실시예들을 이용한 부직포, 상부시트, 또는 기저귀의 역류성이 비교예들을 이용한 부직포, 상부시트, 또는 기저귀에 비해 우수하였다. The counterflow properties were measured using the nonwoven fabric, the top sheet or the diaper prepared in the above Examples and Comparative Examples. As a result, the nonwoven fabric, the top sheet, or the diaper was superior to the nonwoven fabric, the top sheet, or the diaper using the examples in terms of the reflux of the diaper.
실험예Experimental Example 3: 부직포, 상부시트 또는 3: nonwoven fabric, top sheet or 기저귀의 기저귀의Diaper 체액이 흡수되는 단위면적 비교 Comparison of unit area where body fluids are absorbed
상기 실시예들과 비교예들에서 제조된 부직포, 상부시트 또는 기저귀를 이용하여 기저귀의 체액이 흡수되는 단위면적을 측정하였다. 그 결과, 실시예들을 이용한 부직포, 상부시트, 또는 기저귀의 체액이 흡수되는 단위면적이 비교예들을 이용한 부직포, 상부시트, 또는 기저귀에 비해 감소하였다.The unit area in which the body fluid of the diaper was absorbed was measured using the nonwoven fabric, the top sheet or the diaper prepared in the above-described Examples and Comparative Examples. As a result, the unit area in which the body fluid of the nonwoven fabric, the top sheet, or the diaper was absorbed was reduced as compared with the nonwoven fabric, the top sheet, or the diaper using the comparative examples.
이상의 설명으로부터, 본 발명이 속하는 기술분야의 당업자는 본 발명이 그 기술적 사상이나 필수적 특징을 변경하지 않고서 다른 구체적인 형태로 실시될 수 있다는 것을 이해할 수 있을 것이다. 이와 관련하여, 이상에서 기술한 실시 예들은 모든 면에서 예시적인 것이며 한정적인 것이 아닌 것으로서 이해해야만 한다. 본 발명의 범위는 상기 상세한 설명보다는 후술하는 특허 청구범위의 의미 및 범위 그리고 그 등가 개념으로부터 도출되는 모든 변경 또는 변형된 형태가 본 발명의 범위에 포함되는 것으로 해석되어야 한다.From the above description, it will be understood by those skilled in the art that the present invention may be embodied in other specific forms without departing from the spirit or essential characteristics thereof. In this regard, it should be understood that the above-described embodiments are to be considered in all respects as illustrative and not restrictive. The scope of the present invention should be construed as being included in the scope of the present invention without departing from the scope of the present invention as defined by the appended claims.
Claims (10)