KR20180088773A - Mixture of early strength for cement concrete including calcium compound and manufacturing method of the same - Google Patents

Mixture of early strength for cement concrete including calcium compound and manufacturing method of the same Download PDF

Info

Publication number
KR20180088773A
KR20180088773A KR1020180087888A KR20180087888A KR20180088773A KR 20180088773 A KR20180088773 A KR 20180088773A KR 1020180087888 A KR1020180087888 A KR 1020180087888A KR 20180087888 A KR20180087888 A KR 20180087888A KR 20180088773 A KR20180088773 A KR 20180088773A
Authority
KR
South Korea
Prior art keywords
weight
parts
calcium
mixture
cement concrete
Prior art date
Application number
KR1020180087888A
Other languages
Korean (ko)
Inventor
이용진
이종훈
Original Assignee
이지스 주식회사
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 이지스 주식회사 filed Critical 이지스 주식회사
Priority to KR1020180087888A priority Critical patent/KR20180088773A/en
Publication of KR20180088773A publication Critical patent/KR20180088773A/en

Abstract

The present invention relates to a crude steel mixture for cement concrete containing a calcium compound and to a manufacturing method thereof, wherein the crude steel mixture contains calcium compounds, metal oxides, hydroxides such as alkali metals, dispersants and water. In addition, the crude steel mixture for the cement concrete according to the present invention contains calcium compounds and the like to be useful for recycling of industrial by-products, to reduce the content of cement, to be economical, to save energy and to be eco-friendly as environmental pollution can be reduced by reducing the generation of carbon dioxide. The addition of the crude steel mixture to the cement concrete mixture has an effect of increasing the early strength of the cement concrete.

Description

칼슘 화합물을 포함하는 시멘트 콘크리트용 조강혼합물 및 이의 제조방법 {MIXTURE OF EARLY STRENGTH FOR CEMENT CONCRETE INCLUDING CALCIUM COMPOUND AND MANUFACTURING METHOD OF THE SAME}TECHNICAL FIELD The present invention relates to a crude steel mixture for cement concrete containing calcium compounds and a method for producing the same, and a method for producing the same. BACKGROUND ART < RTI ID = 0.0 > [0002]

본 발명은 시멘트 콘크리트용 조강혼합물에 관한 것으로서, 보다 상세하게는 시멘트 콘크리트 혼합물에 칼슘 화합물을 포함하는 조강혼합물을 첨가하여 시멘트를 기존보다 적게 사용하면서도 높은 조기강도를 낼 수 있는 시멘트 콘크리트용 조강혼합물에 관한 것이다.The present invention relates to a crude steel mixture for cement concrete, and more particularly, to a method for preparing a crude steel mixture for cement concrete, which comprises adding a crude steel mixture containing a calcium compound to a cement concrete mixture, .

최근 시멘트의 생산량이 감소함에 따라 시멘트의 가격이 상승하는 한편, 플라이애쉬, 고로슬래그 등의 산업부산물은 연간 2,000 만 톤 이상 발생되고 있다. 따라서 콘크리트를 제조할 시에 중요한 재료가 되는 시멘트의 비율을 줄이고 시멘트의 대체제로 가능한 값싼 산업부산물의 사용이 요구되고 있다. 이러한 산업부산물의 발생량은 해마다 증가하는 추세에 있어 시멘트의 대체제로 더욱 바람직하다. 그러나 산업부산물을 적용할 경우에 콘크리트의 조기강도가 감소한다는 문제점이 발생된다. 따라서 이를 해결한 조강첨가제의 필요성이 점차 대두되고 있다.Recently, cement prices have risen as cement production decreases, while industrial by-products such as fly ash and blast furnace slag have been generated more than 20 million tons a year. Therefore, it is required to reduce the proportion of cement, which is an important material in the production of concrete, and to use cheap industrial byproducts as a substitute for cement. The amount of such industrial byproducts is increasing year by year, and is more preferable as a substitute for cement. However, when industrial byproducts are applied, the early strength of concrete decreases. Therefore, the necessity of the crude steel additive to solve this problem is increasing.

종래 시멘트 콘크리트의 강도를 조기에 발현할 수 있는 몇 가지 방법들이 제시되고 있으며, 각각의 장단점에 따라 선택적으로 활용하여 사용되고 있다.Several methods have been proposed to express the strength of cement concrete in the early stage, and they have been selectively used according to their advantages and disadvantages.

국내특허 제 10-120942호는 부배합 콘크리트로 제조하여 강도를 상향 조정하는 방법을 개시하고 있다. 그러나, 이는 시멘트량의 증가에 따른 재료비 상승 및 부가적인 골재 등의 사용량 증가에 따라 공사비가 큰 폭으로 증가하는 문제점이 있다.Korean Patent No. 10-120942 discloses a method of adjusting the strength by making the concrete with the unsupported concrete. However, there is a problem that the cost of construction increases greatly due to an increase in the material cost due to an increase in the amount of cement and an increase in the amount of additional aggregate and the like.

국내특허 제 10-615826호는 응결촉진형 혼화제 조성물 및 이를 함유하는 조기강도발현형 콘크리트 조성물을 개시하고 있다. 이러한 콘크리트 조성물은 단가 상승요인이 비교적 낮고, 적용성도 편할 수 있으나, 혼화제의 조성물이 많기 때문에 물성변화가 생길 우려가 많으며, 성능의 저하가 발생할 수 있고, 콘크리트 물성변화(공기량, 슬럼프) 및 납품처 간의 품질 변동이 있어 현장에서 품질관리가 용이하지 않다는 단점이 있다.Korean Patent No. 10-615826 discloses a condensation-promoting admixture composition and an early strength-expressing concrete composition containing the same. Such a concrete composition has a relatively low factor of increase in unit cost and can be applied easily. However, since there are many compositions of an admixture, there is a possibility that a change in physical properties is likely to occur and a performance deterioration may occur, and a concrete property change (air quantity, slump) There is a disadvantage that quality control is not easy in the field due to quality fluctuation.

한국등록특허 제 10-120942호Korean Patent No. 10-120942 한국등록특허 제 10-615826호Korean Patent No. 10-615826

본 발명은 상기와 같은 문제점들을 개선하기 위하여 안출된 것으로서, 산화칼슘, 수산화칼슘, 탄산칼슘 등을 포함하여 시멘트의 함량을 낮춤에도 콘크리트의 조기강도를 높게 유지할 수 있는 시멘트 콘크리트용 조강혼합물을 제공하는 것을 목적으로 한다.SUMMARY OF THE INVENTION The present invention has been made in order to solve the above problems and provides a crude steel mixture for cement concrete which can contain calcium oxide, The purpose.

또한, 본 발명은 상기 시멘트 콘크리트용 조강 혼합물의 제조방법을 제공하는 것을 또 다른 목적으로 한다.It is another object of the present invention to provide a method for producing a crude steel mixture for cement concrete.

본 발명의 시멘트 콘크리트용 조강혼합물은 상술한 바와 같은 목적을 달성하기 위하여, In order to achieve the above object, the present invention provides a crude steel mixture for cement concrete,

산화칼슘, 수산화칼슘, 탄산칼슘 및 그 혼합물로 이루어진 군에서 선택된 칼슘 화합물 100 중량부, 100 parts by weight of a calcium compound selected from the group consisting of calcium oxide, calcium hydroxide, calcium carbonate,

규소, 알루미늄, 철, 마그네슘, 그 산화물 및 혼합물로 구성된 군에서 선택된 화합물 0.1 내지 200 중량부, 바람직하게는 0.1 내지 100 중량부, 보다 바람직하게는 0.1 내지 50 중량부, 보다 더 바람직하게는 0.1 내지 30 중량부,0.1 to 200 parts by weight, preferably 0.1 to 100 parts by weight, more preferably 0.1 to 50 parts by weight, still more preferably 0.1 to 50 parts by weight of a compound selected from the group consisting of silicon, aluminum, iron, magnesium, 30 parts by weight,

알칼리금속 또는 알칼리토금속의 수산화물, 트리에탄올아민 또는 그 혼합물, 바람직하게는 수산화나트륨 0.5 내지 30 중량부, 바람직하게는 2 내지 20 중량부, A hydroxide of an alkali metal or an alkaline earth metal, triethanolamine or a mixture thereof, preferably 0.5 to 30 parts by weight, preferably 2 to 20 parts by weight,

분산제 1 내지 50 중량부, 바람직하게는 5 내지 30 중량부, 및 1 to 50 parts by weight, preferably 5 to 30 parts by weight, of a dispersant, and

물 50 내지 600 중량부, 바람직하게는 150 내지 450 중량부를 포함하고, 50 to 600 parts by weight, preferably 150 to 450 parts by weight of water,

시멘트 콘크리트의 시멘트 100 중량부 당 0.1 내지 10 중량부, 바람직하게는 0.5 내지 10 중량부, 보다 바람직하게는 1 내지 10 중량부, 더욱 바람직하게는 3 내지 8 중량부를 혼합하여 상기 시멘트 콘크리트에 조강성을 부여하는 것을 특징으로 한다.Preferably 0.1 to 10 parts by weight, more preferably 1 to 10 parts by weight, and even more preferably 3 to 8 parts by weight per 100 parts by weight of the cement of the cement concrete, Is given.

또한, 본 발명의 시멘트 콘크리트용 조강혼합물은 상기 칼슘 화합물 100 중량부 당, Further, the crude steel mixture for cement concrete of the present invention contains, per 100 parts by weight of the calcium compound,

알칼리금속 또는 알칼리토금속의 초산염, 포름산염, 질산염, 아질산염, 황산염, 티오황산염, 탄산염, 염화물, 할로겐화물, 알칸올아민, 염화철, 칼슘알루미네이트실리케이트, 및 그 혼합물로 이루어진 군에서 선택된 수화반응 촉진제, 바람직하게는 알칼리금속 또는 알칼리토금속의 질산염, 보다 바람직하게는 질산칼슘 1 내지 50 중량부, 바람직하게는 5 내지 30 중량부를 추가로 포함할 수 있다.A hydration reaction promoter selected from the group consisting of an alkali metal or alkaline earth metal acetate, a formate, a nitrate, a nitrite, a sulfate, a thiosulfate, a carbonate, a chloride, a halide, an alkanolamine, a chloride, a calcium aluminate silicate, Preferably an alkali metal or an alkaline earth metal nitrate, more preferably 1 to 50 parts by weight, and preferably 5 to 30 parts by weight, of calcium nitrate.

또한, 본 발명의 시멘트 콘크리트용 조강혼합물은 상기 칼슘 화합물 100 중량부 당, Further, the crude steel mixture for cement concrete of the present invention contains, per 100 parts by weight of the calcium compound,

시멘트 0.01 내지 5 중량부를 추가로 포함할 수 있다.0.01 to 5 parts by weight of cement may be further included.

또한, 본 발명의 시멘트 콘크리트용 조강혼합물은 상기 칼슘 화합물 100 중량부 당, Further, the crude steel mixture for cement concrete of the present invention contains, per 100 parts by weight of the calcium compound,

플라이애쉬, 바텀애쉬, 실리카퓸, 실리카, 규산염, 물유리, 슬래그 및 그 혼합물로 이루어진 군에서 선택된 실리카 화합물 10 내지 100 중량부, 바람직하게는 20 내지 70 중량부를 추가로 포함할 수 있다.10 to 100 parts by weight, preferably 20 to 70 parts by weight, of a silica compound selected from the group consisting of fly ash, bottom ash, silica fume, silica, silicate, water glass, slag and mixtures thereof.

또한, 본 발명의 시멘트 콘크리트용 조강혼합물은 상기 칼슘 화합물 100 중량부 당, Further, the crude steel mixture for cement concrete of the present invention contains, per 100 parts by weight of the calcium compound,

칼슘실리케이트하이드레이트 0.1 내지 20 중량부를 추가로 포함할 수 있다.And 0.1 to 20 parts by weight of calcium silicate hydrate.

또한, 상기 칼슘 화합물의 평균입경은 0.01 내지 100 ㎛, 바람직하게는 0.01 내지 50 ㎛, 보다 바람직하게는 0.01 내지 30 ㎛일 수 있다.The average particle diameter of the calcium compound may be 0.01 to 100 占 퐉, preferably 0.01 to 50 占 퐉, more preferably 0.01 to 30 占 퐉.

또한, 상기 시멘트의 평균입경은 0.01 내지 100 ㎛, 바람직하게는 0.01 내지 50 ㎛, 보다 바람직하게는 0.01 내지 30 ㎛일 수 있다.The average particle diameter of the cement may be 0.01 to 100 占 퐉, preferably 0.01 to 50 占 퐉, more preferably 0.01 to 30 占 퐉.

또한, 상기 실리카 화합물의 평균입경은 0.01 내지 100 ㎛, 바람직하게는 0.01 내지 50 ㎛, 보다 바람직하게는 0.01 내지 30 ㎛일 수 있다.The average particle diameter of the silica compound may be 0.01 to 100 占 퐉, preferably 0.01 to 50 占 퐉, more preferably 0.01 to 30 占 퐉.

또한, 상기 시멘트 콘크리트용 조강혼합물의 고형분 함량은 10 내지 80 무게%, 바람직하게는 20 내지 70 무게%, 보다 바람직하게는 30 내지 60 무게%, 더욱 바람직하게는 40 내지 55 무게%, 더욱 더 바람직하게는 45 내지 55 무게%일 수 있다.The solid content of the crude steel mixture for cement concrete is 10 to 80% by weight, preferably 20 to 70% by weight, more preferably 30 to 60% by weight, further preferably 40 to 55% by weight, By weight and 45 to 55% by weight.

또한, 상기 시멘트 콘크리트용 조강혼합물은 상기 칼슘 화합물 100 중량부 당, Further, the crude steel mixture for cement concrete contains, per 100 parts by weight of the calcium compound,

습윤제 0.001 내지 5 중량부, 바람직하게는 0.01 내지 1 중량부를 추가로 포함할 수 있다.0.001 to 5 parts by weight, preferably 0.01 to 1 part by weight, of the wetting agent.

또한, 상기 시멘트 콘크리트용 조강혼합물은 상기 칼슘 화합물 100 중량부 당, Further, the crude steel mixture for cement concrete contains, per 100 parts by weight of the calcium compound,

증점제 0.001 내지 5 중량부, 바람직하게는 0.01 내지 1 중량부를 추가로 포함할 수 있다.0.001 to 5 parts by weight, preferably 0.01 to 1 part by weight, of a thickening agent.

또한, 본 발명의 시멘트 콘크리트용 조강혼합물은 상기 칼슘 화합물 100 중량부 당, Further, the crude steel mixture for cement concrete of the present invention contains, per 100 parts by weight of the calcium compound,

소포제 0.001 내지 5 중량부, 바람직하게는 0.1 내지 5 중량부를 추가로 포함할 수 있다.0.001 to 5 parts by weight, preferably 0.1 to 5 parts by weight, of the antifoaming agent.

또한, 상기 시멘트 콘크리트용 조강혼합물의 점도는 100 내지 3000 cPs일 수 있다.In addition, the viscosity of the crude steel mixture for cement concrete may be 100 to 3000 cPs.

또한, 상기 시멘트 콘크리트용 조강혼합물의 연간 점도 변화량은 0 내지 1000 cPs일 수 있다.Also, the annual viscosity change of the crude steel mixture for cement concrete may be 0 to 1000 cPs.

또한, 상기 시멘트 콘크리트용 조강혼합물의 pH는 10 내지 14일 수 있다.Also, the pH of the crude steel mixture for cement concrete may be 10 to 14.

한편, 본 발명의 시멘트 콘크리트용 조강혼합물의 제조방법은 Meanwhile, the method for producing a crude steel mixture for cement concrete according to the present invention comprises

(A) 산화칼슘, 수산화칼슘, 탄산칼슘 및 그 혼합물로 이루어진 군에서 선택된 칼슘 화합물 100 중량부, (A) 100 parts by weight of a calcium compound selected from the group consisting of calcium oxide, calcium hydroxide, calcium carbonate,

규소, 알루미늄, 철, 마그네슘, 그 산화물 및 혼합물로 구성된 군에서 선택된 화합물 0.1 내지 200 중량부, 바람직하게는 0.1 내지 100 중량부, 보다 바람직하게는 0.1 내지 50 중량부, 보다 더 바람직하게는 0.1 내지 30 중량부, 0.1 to 200 parts by weight, preferably 0.1 to 100 parts by weight, more preferably 0.1 to 50 parts by weight, still more preferably 0.1 to 50 parts by weight of a compound selected from the group consisting of silicon, aluminum, iron, magnesium, 30 parts by weight,

분산제 1 내지 50 중량부, 바람직하게는 5 내지 30 중량부, 및 1 to 50 parts by weight, preferably 5 to 30 parts by weight, of a dispersant, and

물 50 내지 600 중량부, 바람직하게는 150 내지 450 중량부를 혼합하여 주제를 제조하는 단계; Mixing 50 to 600 parts by weight, preferably 150 to 450 parts by weight of water to prepare a subject;

(B) 상기 칼슘 화합물 100 중량부 당, (B) Per 100 parts by weight of the calcium compound,

알칼리금속 또는 알칼리토금속의 수산화물, 트리에탄올아민 또는 그 혼합물, 바람직하게는 수산화나트륨 0.5 내지 30 중량부, 바람직하게는 2 내지 20 중량부, A hydroxide of an alkali metal or an alkaline earth metal, triethanolamine or a mixture thereof, preferably 0.5 to 30 parts by weight, preferably 2 to 20 parts by weight,

물 1 내지 50 중량부, 바람직하게는 10 내지 50 중량부를 혼합하여 보조제를 제조하는 단계; 및 Mixing 1 to 50 parts by weight, preferably 10 to 50 parts by weight of water to prepare an adjuvant; And

(C) 상기 주제와 보조제를 혼합하는 단계를 포함하는 것을 특징으로 한다.(C) And mixing the subject matter with an auxiliary agent.

또한, 본 발명의 시멘트 콘크리트용 조강혼합물의 제조방법은 Further, the method for producing a crude steel mixture for cement concrete of the present invention

단계 (A) 중, In step (A)

상기 규소, 알루미늄, 철, 마그네슘, 그 산화물 및 혼합물로 구성된 군에서 선택된 화합물, 칼슘 화합물, 분산제 및 물을 혼합한 후 상기 규소, 알루미늄, 철, 마그네슘, 그 산화물 및 혼합물로 구성된 군에서 선택된 화합물 및 칼슘 화합물을 평균입경 0.01 내지 100 ㎛가 되도록 분쇄하는 단계를 추가로 포함할 수 있다.A compound selected from the group consisting of silicon, aluminum, iron, magnesium, an oxide thereof, and a mixture thereof after mixing a compound selected from the group consisting of silicon, aluminum, iron, magnesium, And pulverizing the calcium compound to have an average particle diameter of 0.01 to 100 mu m.

또한, 본 발명의 시멘트 콘크리트용 조강혼합물의 제조방법은 Further, the method for producing a crude steel mixture for cement concrete of the present invention

단계 (C) 이후에, After step (C)

상기 주제와 보조제의 혼합물을 5 내지 100 ℃, 바람직하게는 60 내지 80 ℃에서 0.5 내지 24 시간, 바람직하게는 0.5 내지 12 시간 동안 유지하는 단계를 추가로 포함할 수 있다.The method may further comprise maintaining the mixture of the subject and the adjuvant at 5 to 100 캜, preferably 60 to 80 캜, for 0.5 to 24 hours, preferably 0.5 to 12 hours.

또한, 상기 단계 (C)의 혼합은 주제를 보조제로 적가하거나, 보조제를 주제로 적가하는 것일 수 있다.In addition, the mixing of step (C) may be to add the subject as an adjuvant, or to add the adjuvant as a subject.

또한, 본 발명의 시멘트 콘크리트용 조강혼합물의 제조방법은 상기 주제에 상기 칼슘 화합물 100 중량부 당, The present invention also provides a process for preparing a crude steel mixture for cement concrete,

알칼리금속 또는 알칼리토금속의 초산염, 포름산염, 질산염, 아질산염, 황산염, 티오황산염, 탄산염, 염화물, 할로겐화물, 알칸올아민, 염화철, 칼슘알루미네이트실리케이트, 및 그 혼합물로 이루어진 군에서 선택된 수화반응 촉진제, 바람직하게는 알칼리금속 또는 알칼리토금속의 질산염, 보다 바람직하게는 질산칼슘 1 내지 50 중량부, 바람직하게는 5 내지 30 중량부를 추가로 포함할 수 있다.A hydration reaction promoter selected from the group consisting of an alkali metal or alkaline earth metal acetate, a formate, a nitrate, a nitrite, a sulfate, a thiosulfate, a carbonate, a chloride, a halide, an alkanolamine, a chloride, a calcium aluminate silicate, Preferably an alkali metal or an alkaline earth metal nitrate, more preferably 1 to 50 parts by weight, and preferably 5 to 30 parts by weight, of calcium nitrate.

또한, 본 발명의 시멘트 콘크리트용 조강혼합물의 제조방법은 상기 주제에 상기 칼슘 화합물 100 중량부 당, The present invention also provides a process for preparing a crude steel mixture for cement concrete,

시멘트 0.01 내지 5 중량부를 추가로 포함할 수 있다.0.01 to 5 parts by weight of cement may be further included.

또한, 본 발명의 시멘트 콘크리트용 조강혼합물의 제조방법은 상기 주제에 상기 칼슘 화합물 100 중량부 당, The present invention also provides a process for preparing a crude steel mixture for cement concrete,

플라이애쉬, 바텀애쉬, 실리카퓸, 실리카, 규산염, 물유리, 슬래그 및 그 혼합물로 이루어진 군에서 선택된 실리카 화합물 10 내지 100 중량부, 바람직하게는 20 내지 70 중량부를 추가로 포함할 수 있다.10 to 100 parts by weight, preferably 20 to 70 parts by weight, of a silica compound selected from the group consisting of fly ash, bottom ash, silica fume, silica, silicate, water glass, slag and mixtures thereof.

또한, 본 발명의 시멘트 콘크리트용 조강혼합물의 제조방법은 상기 주제에 상기 칼슘 화합물 100 중량부 당, The present invention also provides a process for preparing a crude steel mixture for cement concrete,

칼슘실리케이트하이드레이트 0.1 내지 20 중량부를 추가로 포함할 수 있다.And 0.1 to 20 parts by weight of calcium silicate hydrate.

또한, 본 발명의 시멘트 콘크리트용 조강혼합물의 제조방법은 단계 (A) 도중에, 상기 칼슘 화합물을 분쇄할 때 상기 시멘트 역시 함께 분쇄할 수 있고, 상기 분쇄 후의 상기 시멘트의 평균입경은 0.01 내지 100 ㎛, 바람직하게는 0.01 내지 50 ㎛, 보다 바람직하게는 0.01 내지 30 ㎛일 수 있다.In the method for producing a crude steel mixture for cement concrete according to the present invention, when the calcium compound is crushed during the step (A), the cement may be crushed together with the crushed cement having an average particle diameter of 0.01 to 100 μm, Preferably 0.01 to 50 mu m, more preferably 0.01 to 30 mu m.

또한, 본 발명의 시멘트 콘크리트용 조강혼합물의 제조방법은 단계 (A) 도중에, 상기 칼슘 화합물을 분쇄할 때 상기 실리카 화합물 역시 함께 분쇄할 수 있고, 상기 분쇄 후의 상기 실리카 화합물의 평균입경은 0.01 내지 100 ㎛, 바람직하게는 0.01 내지 50 ㎛, 보다 바람직하게는 0.01 내지 30 ㎛일 수 있다.In the method for producing a crude steel mixture for cement concrete according to the present invention, the silica compound may be pulverized together with the silica compound when the calcium compound is pulverized during step (A), and the average particle diameter of the silica compound after pulverization is from 0.01 to 100 Mu] m, preferably 0.01 to 50 [mu] m, and more preferably 0.01 to 30 [mu] m.

또한, 상기 시멘트 콘크리트용 조강혼합물의 고형분 함량은 10 내지 80 무게%, 바람직하게는 20 내지 70 무게%, 보다 바람직하게는 30 내지 60 무게%, 더욱 바람직하게는 40 내지 55 무게%, 더욱 더 바람직하게는 45 내지 55 무게%일 수 있다.The solid content of the crude steel mixture for cement concrete is 10 to 80% by weight, preferably 20 to 70% by weight, more preferably 30 to 60% by weight, further preferably 40 to 55% by weight, By weight and 45 to 55% by weight.

또한, 본 발명의 시멘트 콘크리트용 조강혼합물의 제조방법은 상기 주제에 상기 칼슘 화합물 100 중량부 당, The present invention also provides a process for preparing a crude steel mixture for cement concrete,

습윤제 0.001 내지 5 중량부, 바람직하게는 0.01 내지 1 중량부를 추가로 포함할 수 있다.0.001 to 5 parts by weight, preferably 0.01 to 1 part by weight, of the wetting agent.

또한, 본 발명의 시멘트 콘크리트용 조강혼합물의 제조방법은 상기 주제에 상기 칼슘 화합물 100 중량부 당, The present invention also provides a process for preparing a crude steel mixture for cement concrete,

증점제 0.001 내지 5 중량부, 바람직하게는 0.01 내지 1 중량부를 추가로 포함할 수 있다.0.001 to 5 parts by weight, preferably 0.01 to 1 part by weight, of a thickening agent.

또한, 본 발명의 시멘트 콘크리트용 조강혼합물의 제조방법은 상기 주제에 상기 칼슘 화합물 100 중량부 당, The present invention also provides a process for preparing a crude steel mixture for cement concrete,

소포제 0.001 내지 5 중량부, 바람직하게는 0.1 내지 5 중량부를 추가로 포함할 수 있다.0.001 to 5 parts by weight, preferably 0.1 to 5 parts by weight, of the antifoaming agent.

또한, 본 발명의 시멘트 콘크리트용 조강혼합물은 상기 방법에 의해 제조된 것을 특징으로 한다.Further, the crude steel mixture for cement concrete of the present invention is characterized by being produced by the above-mentioned method.

본 발명은 산화칼슘, 수산화칼슘, 탄산칼슘 등을 사용하여 산업부산물의 재활용에 해당하며, 시멘트의 함량을 낮출 수 있어 비용절감 및 에너지 절약의 효과가 있고, 이산화탄소의 발생을 저감시켜 환경 오염을 감소시키는데에 도움이 된다. 또한 본 발명은 조강혼합물의 사용으로 낮은 시멘트의 함량에도 콘크리트의 조기강도가 높게 발현될 수 있고, 공사기간 단축 등의 작업효율성을 향상을 기대할 수 있으며, 산업부산물과 같은 재생골재의 사용으로 발생되는 콘크리트 품질저하 문제를 해결할 수 있다.The present invention relates to the recycling of industrial byproducts by using calcium oxide, calcium hydroxide, calcium carbonate, etc., and it is possible to lower the content of cement, thereby reducing costs and saving energy and reducing environmental pollution by reducing the generation of carbon dioxide . Also, the present invention can improve the work efficiency such as shortening the construction period because the early strength of the concrete can be expressed at a low cement content by using the crude steel mixture, and it can be expected that the use of recycled aggregate such as industrial by- It is possible to solve the problem of deterioration of concrete quality.

이하, 본 발명의 바람직한 실시예에 대해서 상세히 설명하기로 한다.Hereinafter, preferred embodiments of the present invention will be described in detail.

이에 앞서, 본 명세서 및 청구범위에 사용된 용어나 단어는 통상적이거나 사전적인 의미로 한정해서 해석되어서는 안 되며, 본 명세서에 기재된 내용들이 본 발명의 기술적 사상을 모두 대변하는 것은 아니므로 본 출원시점에 있어서 이들은 대체할 수 있는 다양한 변형예들이 있을 수 있음을 이해하여야 한다. 또한, 본 발명을 설명함에 있어서, 관련된 공지 기능 혹은 구성에 대한 구체적인 설명이 본 발명의 요지를 불필요하게 흐릴 수 있다고 판단되는 경우 그 상세한 설명을 생략한다.Prior to this description, terms and words used in the present specification and claims should not be construed as limited to ordinary or dictionary meanings, and the contents described in this specification do not necessarily represent the technical ideas of the present invention, It should be understood that there may be many variations that can be substituted for these. In the following description of the present invention, detailed description of known functions and configurations incorporated herein will be omitted when it may make the subject matter of the present invention rather unclear.

본 발명의 바람직한 실시예에 따른 시멘트 콘크리트용 조강혼합물은 산화칼슘, 수산화칼슘, 탄산칼슘 및 그 혼합물로 이루어진 군에서 선택된 칼슘 화합물, 규소, 알루미늄, 철, 마그네슘, 그 산화물 및 혼합물로 구성된 군에서 선택된 화합물, 알칼리금속 또는 알칼리토금속의 수산화물, 트리에탄올아민 또는 그 혼합물, 분산제, 및 물을 포함한다.The crude steel mixture for cement concrete according to a preferred embodiment of the present invention may be a compound selected from the group consisting of calcium compounds selected from the group consisting of calcium oxide, calcium hydroxide, calcium carbonate and mixtures thereof, silicon, aluminum, iron, magnesium, , Hydroxides of alkali metals or alkaline earth metals, triethanolamine or mixtures thereof, dispersants, and water.

상기 시멘트 콘크리트용 조강혼합물은 상기 산화칼슘, 수산화칼슘, 탄산칼슘 및 그 혼합물로 이루어진 군에서 선택된 칼슘 화합물을 100 중량부 함유하며, 상기 규소, 알루미늄, 철, 마그네슘, 그 산화물 및 혼합물로 구성된 군에서 선택된 화합물 0.1 내지 200 중량부, 바람직하게는 0.1 내지 100 중량부, 보다 바람직하게는 0.1 내지 50 중량부, 보다 더 바람직하게는 0.1 내지 30 중량부를 함유하고, 상기 알칼리금속 또는 알칼리토금속의 수산화물, 트리에탄올아민 또는 그 혼합물, 바람직하게는 수산화나트륨 0.5 내지 30 중량부, 바람직하게는 2 내지 20 중량부를 함유한다. 그리고 상기 분산제 1 내지 50 중량부, 바람직하게는 5 내지 30 중량부를 함유하며, 상기 물은 50 내지 600 중량부, 바람직하게는 150 내지 450 중량부를 함유한다. 그리고 본 발명의 시멘트 콘크리트용 조강 혼합물은 시멘트 콘크리트의 시멘트 100 중량부 당 0.1 내지 10 중량부, 바람직하게는 0.5 내지 10 중량부, 보다 바람직하게는 1 내지 10 중량부, 더욱 바람직하게는 3 내지 8 중량부를 혼합하여 상기 시멘트 콘크리트에 조강성을 부여한다.Wherein the crude steel mixture for cement concrete contains 100 parts by weight of a calcium compound selected from the group consisting of calcium oxide, calcium hydroxide, calcium carbonate and a mixture thereof and is selected from the group consisting of silicon, aluminum, iron, magnesium, , 0.1 to 200 parts by weight, preferably 0.1 to 100 parts by weight, more preferably 0.1 to 50 parts by weight, and even more preferably 0.1 to 30 parts by weight of the compound, the hydroxide of the above alkali metal or alkaline earth metal, triethanolamine Or a mixture thereof, preferably 0.5 to 30 parts by weight, preferably 2 to 20 parts by weight, of sodium hydroxide. And 1 to 50 parts by weight, preferably 5 to 30 parts by weight, of the dispersant, and the water contains 50 to 600 parts by weight, preferably 150 to 450 parts by weight. The crude steel mixture for cement concrete according to the present invention is used in an amount of 0.1 to 10 parts by weight, preferably 0.5 to 10 parts by weight, more preferably 1 to 10 parts by weight, more preferably 3 to 8 parts by weight, By weight, to give the cement concrete a toughness.

상기 산화칼슘, 수산화칼슘, 탄산칼슘 및 그 혼합물로 이루어진 군은 시멘트의 응결 및 경화 과정에서 염기를 활성화시켜 칼슘실리케이트하이드레이트의 형성을 촉진한다. 상기 군에서 산화칼슘은 수분과 이산화탄소를 흡수하여 수산화칼슘과 탄산칼슘으로 분해된다.The group consisting of calcium oxide, calcium hydroxide, calcium carbonate and mixtures thereof promotes the formation of calcium silicate hydrate by activating the base during the curing and curing of the cement. In the above group, calcium oxide absorbs water and carbon dioxide and is decomposed into calcium hydroxide and calcium carbonate.

본 발명의 가장 주요한 특징은 저가의 원료를 이용하여 조강혼합물을 제공하는 것이다. 이 때문에 상기 칼슘 화합물은 순도가 낮아 필연적으로 규소, 알루미늄, 철, 마그네슘 등과 같은 금속의 산화물을 포함하고 있고, 이들 산화물의 함유량은 상기 칼슘 화합물 100 중량부 당 0.1 내지 200 중량부, 바람직하게는 0.1 내지 100 중량부, 보다 바람직하게는 0.1 내지 50 중량부, 보다 더 바람직하게는 0.1 내지 30 중량부일 수 있다. 상기 산화물의 함유량이 0.1 중량부 미만이면 상기에서 언급한 저가 원료가 아닌 높은 순도의 고가 원료이므로 본 발명에서 의도하는 원료가 아니고, 반대로 200 중량부를 초과하면 조강혼합물이 제조되지 않으며 제조된다고 하더라도 성능 발현이 제대로 이루어지지 않는다.The most important feature of the present invention is to provide a crude steel mixture using low-cost raw materials. Therefore, the calcium compound has a low purity and necessarily contains an oxide of a metal such as silicon, aluminum, iron, magnesium, etc. The content of these oxides is 0.1 to 200 parts by weight, preferably 0.1 to 200 parts by weight, To 100 parts by weight, more preferably 0.1 to 50 parts by weight, still more preferably 0.1 to 30 parts by weight. If the content of the oxide is less than 0.1 part by weight, it is not a raw material intended for the present invention because it is a high-priced raw material having a high purity and is not a low cost raw material mentioned above. On the other hand, if the content exceeds 200 parts by weight, This is not done properly.

본 발명의 조강혼합물을 구성하는 주요성분 중 하나인 상기 알칼리금속 또는 알칼리토금속의 수산화물, 트리에탄올아민 또는 그 혼합물은 시멘트의 응결 및 경화에 필요한 염기성 환경을 제공한다. 이들 염기성 물질의 함유량은 상기 칼슘 화합물 100 중량부 당 0.5 내지 30 중량부, 바람직하게는 2 내지 20 중량부일 수 있다. 상기 염기성 물질의 함유량이 0.5 중량부 미만이면 본 발명 조강혼합물의 생성속도가 지나치게 낮아 제조에 너무 긴 시간이 소요되고, 반대로 30 중량부를 초과하면 조기 강도의 발현에는 유리할 수 있으나, 콘크리트의 알칼리 골재 반응에 영향을 줄 수 있으며, 지나치게 빠르게 굳어 현장 타설과 같은 작업성은 떨어지게 된다.The alkali metal or alkaline earth metal hydroxides, triethanolamine, or mixtures thereof, which is one of the major constituents of the instant steel mixture of the present invention, provide a basic environment for cementing and curing the cement. The content of the basic substance may be 0.5 to 30 parts by weight, preferably 2 to 20 parts by weight per 100 parts by weight of the calcium compound. If the content of the basic substance is less than 0.5 parts by weight, the production rate of the present invention crude starch mixture is too low to take too long to produce. On the other hand, if the content of the basic substance exceeds 30 parts by weight, And the workability such as putting on the scene is lowered.

상기 분산제는 본 발명의 조강혼합물을 구성하는 칼슘 화합물, 금속 산화물, 염기성 물질 등의 입자간 응집을 저해하고, 정전기적 또는 물리적 반발력을 이용하여 상기 입자들이 서로 이격되도록 한다. 이를 통해 시멘트 콘크리트의 전체 영역에서 고른 강도가 발현되고, 배합되는 물의 양을 적게 하면서도 충분한 작업성을 확보할 수 있게 된다. 이러한 분산제의 함유량은 상기 칼슘 화합물 100 중량부 당 1 내지 50 중량부, 바람직하게는 5 내지 30 중량부일 수 있다. 상기 분산제의 함유량이 1 중량부 미만이면 조강혼합물의 점도가 지나치게 높아져 제조도 사용도 어렵게 되고, 반대로 50 중량부를 초과하면 경제성이 떨어질 뿐만 아니라 조강혼합물의 구성성분끼리 상분리가 발생할 수 있다. 또한 기포발생으로 인한 강도 저하가 발생되어 이를 해결하기 위해 불필요한 소포제를 사용하는 경우가 발생되고, 이밖에 다량의 분산제로 인하여 콘크리트의 조기강도 저하 요인이 발생될 수 있다.The dispersant inhibits intergranular aggregation of calcium compounds, metal oxides, basic substances and the like constituting the crude steel mixture of the present invention and allows the particles to be separated from each other by electrostatic or physical repulsive force. Through this, uniform strength is exhibited in the entire area of cement concrete, and sufficient workability can be ensured while reducing the amount of water to be blended. The content of such a dispersant may be 1 to 50 parts by weight, preferably 5 to 30 parts by weight, per 100 parts by weight of the calcium compound. If the content of the dispersing agent is less than 1 part by weight, the viscosity of the crude steel mixture becomes excessively high, making it difficult to use and manufacture. Conversely, if the content exceeds 50 parts by weight, not only the economical efficiency is deteriorated but also the constituents of the crude steel mixture are phase- In addition, in order to solve this problem, the defoaming agent may be used in an undesirable manner. In addition, a large amount of the dispersing agent may cause deterioration of the early strength of the concrete.

그리고, 상기 물의 함유량은 상기 칼슘 화합물 100 중량부 당 50 내지 600 중량부, 바람직하게는 150 내지 450 중량부일 수 있다. 상기 물의 함유량이 50 중량부 미만이면 조강혼합물의 점도가 지나치게 높아져 제조도 사용도 어렵게 되고, 반대로 600 중량부를 초과하면 물류비용의 증가를 초래할 뿐만 아니라 조강혼합물의 구성성분끼리 상분리가 발생할 수 있다.The content of the water may be 50 to 600 parts by weight, preferably 150 to 450 parts by weight, per 100 parts by weight of the calcium compound. If the content of water is less than 50 parts by weight, the viscosity of the crude steel mixture becomes excessively high, which makes it difficult to use and manufacture. On the other hand, if the water content exceeds 600 parts by weight, the cost of logistics is increased and phase separation among the components of the crude steel mixture may occur.

또한, 본 발명의 시멘트 콘크리트용 조강혼합물은 상기 칼슘 화합물 100 중량부 당, 알칼리금속 또는 알칼리토금속의 초산염, 포름산염, 질산염, 아질산염, 황산염, 티오황산염, 탄산염, 염화물, 할로겐화물, 알칸올아민, 염화철, 칼슘알루미네이트실리케이트, 및 그 혼합물로 이루어진 군에서 선택된 수화반응 촉진제, 바람직하게는 알칼리금속 또는 알칼리토금속의 질산염, 보다 바람직하게는 질산칼슘 1 내지 50 중량부, 바람직하게는 5 내지 30 중량부를 추가로 포함할 수 있다. 상기 수화반응 촉진제의 함유량이 상기 범위 이내일 때 적절한 수화반응 속도를 확보할 수 있어 원하는 조기강도를 얻는 것이 가능하다. Further, the crude steel mixture for cement concrete according to the present invention may contain, per 100 parts by weight of the calcium compound, at least one selected from the group consisting of nitrates, formates, nitrates, nitrates, sulfates, thiosulfates, carbonates, chlorides, halides, alkanolamines, Preferably from 1 to 50 parts by weight, preferably from 5 to 30 parts by weight, of a hydration reaction promoter selected from the group consisting of iron chloride, calcium aluminate silicate, and mixtures thereof, preferably an alkali metal or alkaline earth metal nitrate, more preferably calcium nitrate May be further included. When the content of the hydration reaction promoter is within the above range, a proper hydration reaction rate can be ensured and desired early strength can be obtained.

상기 수화반응 촉진제는 칼슘실리케이트하이드레이트 주변의 피막을 약화시켜 그 결정 성장을 촉진하고 그 결과 시멘트의 응결 및 경화가 용이하게 진행되도록 한다. 이들 화합물은 전술한 칼슘 화합물에 의해 활성화되어 반응에 참여하게 된다. 이러한 수화반응 촉진제로는 유기성분으로 초산나트륨, 초산칼슘, 초산칼륨, 초산염, 알칼올아민, 포름산, 포름산칼슘, 포름산염 등이 있으며, 무기성분으로는 질산칼슘, 아질산칼슘, 염화칼슘, 브롬화칼슘, 요오드화칼슘, 가용성칼슘염, 염화철, 염화마그네슘, 염화나트륨, 황산염, 수산화칼륨, 탄산염, 티오황산염, 칼슘알루미네이트실리케이트 등이 있다. The hydration reaction promoter weakens the coating around the calcium silicate hydrate and accelerates its crystal growth so that condensation and curing of the cement can proceed easily. These compounds are activated by the above-mentioned calcium compounds to participate in the reaction. Examples of such hydration reaction accelerators include sodium acetate, calcium acetate, potassium acetate, acetic acid salt, alkanolamine, formic acid, calcium formate and formate salts as organic components. Examples of inorganic components include calcium nitrate, calcium nitrite, calcium chloride, Calcium iodide, soluble calcium salt, iron chloride, magnesium chloride, sodium chloride, sulfate, potassium hydroxide, carbonate, thiosulfate, calcium aluminate silicate and the like.

또한, 본 발명의 시멘트 콘크리트용 조강혼합물은 보다 신속하게 조강성능이 발현될 수 있도록 상기 칼슘 화합물 100 중량부 당, 시멘트 0.01 내지 5 중량부를 추가로 포함할 수 있다. 상기 시멘트의 함유량이 상기 범위 이내일 때 전술한 바와 같이 보다 신속하게 조강성능을 발현시키는 것이 가능해진다.Further, the crude steel mixture for cement concrete of the present invention may further include 0.01 to 5 parts by weight of cement per 100 parts by weight of the calcium compound so that the quick-setting steel performance can be exhibited. When the content of the cement is within the above range, it is possible to express the steel-making performance more quickly as described above.

또한, 본 발명의 시멘트 콘크리트용 조강혼합물은 시멘트의 응결 및 경화 과정에서 염기를 활성화시켜 칼슘실리케이트하이드레이트의 형성을 촉진하기 위하여 상기 칼슘 화합물 100 중량부 당, 플라이애쉬, 바텀애쉬, 실리카퓸, 실리카, 규산염, 물유리, 슬래그 및 그 혼합물로 이루어진 군에서 선택된 실리카 화합물 10 내지 100 중량부, 바람직하게는 20 내지 70 중량부를 추가로 포함할 수 있다. 또한, 시멘트의 응결 및 경화 과정에서 응결핵으로서의 작용을 위해 칼슘 화합물 100 중량부 당, 칼슘실리케이트하이드레이트 0.1 내지 20 중량부를 추가로 포함할 수 있다. 상기 실리카 화합물 및 칼슘실리케이트하이드레이트의 함유량이 상기 범위 이내일 때 콘크리트의 반응속도를 적절하게 유지할 수 있어 원하는 조기강도를 얻는 것이 가능하다. In order to accelerate the formation of calcium silicate hydrate by activating the base during the curing and curing process of the cement concrete, the crude steel mixture for cement concrete according to the present invention may contain at least one component selected from the group consisting of fly ash, bottom ash, silica fume, silica, 10 to 100 parts by weight, preferably 20 to 70 parts by weight, of a silica compound selected from silicates, water glasses, slag, and mixtures thereof. In addition, 0.1 to 20 parts by weight of calcium silicate hydrate may be further added per 100 parts by weight of the calcium compound for acting as a condensation nucleus in the condensation and curing process of the cement. When the content of the silica compound and the calcium silicate hydrate is within the above range, the reaction rate of concrete can be appropriately maintained, and it is possible to obtain a desired early strength.

또한, 상기 칼슘 화합물, 시멘트 및 실리카 화합물의 평균입경은 서로 독립적으로 0.01 내지 100 ㎛, 바람직하게는 0.01 내지 50 ㎛, 보다 바람직하게는 0.01 내지 30 ㎛일 수 있다. 이들 입자들이 전술한 바와 같은 미세 크기를 가짐으로써 충진율이 증가하고, 그 결과 조기강도가 발현될 뿐만 아니라 최종 콘트리트 구조물(몰드)의 압축강도가 증가하게 된다. 상기 평균입경이 상기 범위 이내일 때 높은 충진율 효과로 인한 높은 강도발현이 가능하고, 정전기로 인한 뭉침현상 및 상분리를 방지할 수 있어 제품의 안정성을 확보할 수 있다. The average particle diameter of the calcium compound, the cement and the silica compound may be 0.01 to 100 탆, preferably 0.01 to 50 탆, more preferably 0.01 to 30 탆, independently of each other. These particles have a fine size as described above, thereby increasing the filling rate. As a result, not only the early strength is manifested but also the compressive strength of the final concrete structure (mold) is increased. When the average particle diameter is within the above range, high strength can be exhibited due to a high filling rate effect, and aggregation and phase separation due to static electricity can be prevented, thereby ensuring stability of the product.

또한 상기 시멘트 콘크리트용 조강혼합물의 고형분 함량은 10 내지 80 무게%, 바람직하게는 20 내지 70 무게%, 보다 바람직하게는 30 내지 60 무게%, 더욱 바람직하게는 40 내지 55 무게%, 더욱 더 바람직하게는 45 내지 55 무게%일 수 있다. 상기 고형분 함량이 상기 범위 이내인 것이 원하는 조강성능을 발현하면서도 물류비용을 낮출 수 있어 바람직하다.The solid content of the crude steel mixture for cement concrete is 10 to 80% by weight, preferably 20 to 70% by weight, more preferably 30 to 60% by weight, further preferably 40 to 55% by weight, May be from 45 to 55% by weight. When the solid content is within the above range, it is possible to lower the cost of logistics while exhibiting desired performance of the steel making.

또한, 상기 시멘트 콘크리트용 조강혼합물은 상기 칼슘 화합물 100 중량부당, 습윤제 0.001 내지 5 중량부, 바람직하게는 0.01 내지 1 중량부를 추가로 포함할 수 있다. 상기 습윤제는 입자의 표면장력을 감소시켜 물이 표면에 퍼지게 하는 것으로 그 함유량이 상기 범위 이내일 때 경제성까지 고려한 적절한 범위의 조강성능을 확보할 수 있다. The crude steel mixture for cement concrete may further contain 0.001 to 5 parts by weight, preferably 0.01 to 1 part by weight, of the wetting agent per 100 parts by weight of the calcium compound. The wetting agent reduces the surface tension of the particles and spreads the water on the surface. When the content of the wetting agent is within the above range, the wetting agent can secure an adequate range of steel-making performance in consideration of economical efficiency.

또한, 상기 시멘트 콘크리트용 조강혼합물은 상기 칼슘 화합물 100 중량부 당, 증점제 0.001 내지 5 중량부, 바람직하게는 0.01 내지 1 중량부를 추가로 포함할 수 있다. 상기 증점제의 함유량이 상기 범위 이내일 때 구성성분의 상분리를 억제하면서도 원활한 작업을 가능케 하는 적절한 점도를 확보할 수 있다. The crude steel mixture for cement concrete may further contain 0.001 to 5 parts by weight, preferably 0.01 to 1 part by weight, of a thickener per 100 parts by weight of the calcium compound. When the content of the thickener is within the above range, it is possible to ensure a suitable viscosity which allows smooth work while suppressing the phase separation of the constituent components.

또한, 본 발명의 시멘트 콘크리트용 조강혼합물은 상기 칼슘 화합물 100 중량부 당, 소포제 0.001 내지 5 중량부, 바람직하게는 0.1 내지 5 중량부를 추가로 포함할 수 있다. 상기 소포제의 함유량이 상기 범위 이내일 때 경제성까지 고려하면서 시멘트 콘크리트 내의 기포로 인한 강도 저하를 억제할 수 있다. Further, the crude steel mixture for cement concrete of the present invention may further contain 0.001 to 5 parts by weight, preferably 0.1 to 5 parts by weight, of a defoaming agent per 100 parts by weight of the calcium compound. When the content of the antifoaming agent is within the above range, it is possible to suppress the strength reduction due to the bubbles in the cement concrete while considering the economical efficiency.

상기 소포제는 본 발명의 시멘트 콘크리트용 조강혼합물을 구성하는 성분들을를 혼합하였을 때 발생하는 기포를 제거하기 위해 사용한다. 상기 시멘트 콘크리트용 조강혼합물에 기포가 발생할 경우, 콘크리트의 강도가 감소되는 문제가 생길 수 있다. The antifoaming agent is used to remove air bubbles generated when components constituting the crude steel mixture for cement concrete of the present invention are mixed. When bubbles are generated in the crude steel mixture for cement concrete, the strength of the concrete may be reduced.

또한, 상기 시멘트 콘크리트용 조강혼합물의 점도는 100 내지 3000 cPs일 수 있다. 상기 점도가 상기 범위 이내일 때 구성성분의 상분리를 억제하면서도 원활한 작업이 가능해져 적절한 수준의 작업성을 확보할 수 있다. In addition, the viscosity of the crude steel mixture for cement concrete may be 100 to 3000 cPs. When the viscosity is within the above range, it is possible to smoothly perform work while suppressing the phase separation of the constituent components, thereby ensuring an appropriate level of workability.

또한, 상기 시멘트 콘크리트용 조강혼합물의 연간 점도 변화량은 0 내지 1000 cPs일 수 있다. 상기 연간 점도 변화량이 1000 cPs 이하일 때 적절한 범위의 상품성을 확보할 수 있다.Also, the annual viscosity change of the crude steel mixture for cement concrete may be 0 to 1000 cPs. When the annual viscosity change amount is 1000 cPs or less, an appropriate range of merchantability can be secured.

또한, 상기 시멘트 콘크리트용 조강혼합물의 pH는 10 내지 14 일 수 있다. 상기 pH가 상기 범위 이내일 때 빠른 속도의 수화반응을 발현시킬 수 있어 바람직하다. Also, the pH of the crude steel mixture for cement concrete may be 10 to 14. When the pH is within the above range, a hydration reaction at a high rate can be expressed, which is preferable.

본 발명의 조강혼합물은 시멘트 콘크리트의 시멘트 100 중량부 당 0.1 내지 10 중량부, 바람직하게는 0.5 내지 10 중량부, 보다 바람직하게는 1 내지 10 중량부, 더욱 바람직하게는 3 내지 8 중량부를 혼합하는 것을 특징으로 한다. 시멘트 콘크리트에 배합되는 양이 시멘트 100 중량부 당 0.1 중량부 미만이면 콘크리트의 강도 발현이 미미하며, 반대로 10 중량부를 초과하면 콘크리트의 발열로 인해 균열, 블리딩 등의 문제가 발생할 수 있다. The crude steel mixture of the present invention is mixed with 0.1 to 10 parts by weight, preferably 0.5 to 10 parts by weight, more preferably 1 to 10 parts by weight, and still more preferably 3 to 8 parts by weight per 100 parts by weight of cement of cement concrete . If the amount added to cement concrete is less than 0.1 parts by weight per 100 parts by weight of cement, the strength of the concrete is not sufficiently exhibited. Conversely, if it exceeds 10 parts by weight, problems such as cracking and bleeding may occur due to heat generation of concrete.

한편, 본 발명의 바람직한 실시예에 따른 시멘트 콘크리트용 조강혼합물의 제조방법은 Meanwhile, a method of manufacturing a crude steel mixture for cement concrete according to a preferred embodiment of the present invention includes:

(A) 산화칼슘, 수산화칼슘, 탄산칼슘 및 그 혼합물로 이루어진 군에서 선택된 칼슘 화합물 100 중량부; 규소, 알루미늄, 철, 마그네슘, 그 산화물 및 혼합물로 구성된 군에서 선택된 화합물 0.1 내지 200 중량부, 바람직하게는 0.1 내지 100 중량부, 보다 바람직하게는 0.1 내지 50 중량부, 보다 더 바람직하게는 0.1 내지 30 중량부; 분산제 1 내지 50 중량부, 바람직하게는 5 내지 30 중량부; 및 물 50 내지 600 중량부, 바람직하게는 150 내지 450 중량부를 혼합하여 주제를 제조하는 단계;(A) 100 parts by weight of a calcium compound selected from the group consisting of calcium oxide, calcium hydroxide, calcium carbonate and mixtures thereof; 0.1 to 200 parts by weight, preferably 0.1 to 100 parts by weight, more preferably 0.1 to 50 parts by weight, still more preferably 0.1 to 50 parts by weight of a compound selected from the group consisting of silicon, aluminum, iron, magnesium, 30 parts by weight; 1 to 50 parts by weight, preferably 5 to 30 parts by weight, of a dispersant; And 50 to 600 parts by weight, preferably 150 to 450 parts by weight of water to prepare a subject;

(B) 상기 칼슘 화합물 100 중량부 당, 알칼리금속 또는 알칼리토금속의 수산화물, 트리에탄올아민 또는 그 혼합물, 바람직하게는 수산화나트륨 0.5 내지 30 중량부, 바람직하게는 2 내지 20 중량부; 물 1 내지 50 중량부, 바람직하게는 10 내지 50 중량부를 혼합하여 보조제를 제조하는 단계; 및(B) 0.5 to 30 parts by weight, preferably 2 to 20 parts by weight, of a hydroxide of an alkali metal or an alkaline earth metal, triethanolamine or a mixture thereof, preferably sodium hydroxide, per 100 parts by weight of the calcium compound; Mixing 1 to 50 parts by weight, preferably 10 to 50 parts by weight of water to prepare an adjuvant; And

(C) 상기 주제와 보조제를 혼합하는 단계를 포함한다.(C) And mixing the subject matter with an adjuvant.

본 발명에 따른 시멘트 콘크리트용 조강혼합물의 제조방법은 먼저 산화칼슘, 수산화칼슘, 탄산칼슘 및 그 혼합물로 이루어진 군에서 선택된 칼슘 화합물 100 중량부에 규소, 알루미늄, 철, 마그네슘, 그 산화물 및 혼합물로 이루어진 군에서 선택된 칼슘 화합물 100 중량부, 그리고 규소, 알루미늄, 철, 마그네슘, 그 산화물 및 혼합물로 구성된 군에서 선택된 화합물 0.1 내지 200 중량부, 바람직하게는 0.1 내지 100 중량부, 보다 바람직하게는 0.1 내지 50 중량부, 보다 더 바람직하게는 0.1 내지 30 중량부를 혼합한다. 상기 혼합물에 분산제 1 내지 50 중량부, 바람직하게는 5 내지 30 중량부, 및 물 50 내지 600 중량부, 바람직하게는 150 내지 450 중량부를 혼합하여 주제를 제조하는 단계로부터 시작된다.The method for preparing a crude steel mixture for cement concrete according to the present invention comprises the steps of mixing 100 parts by weight of a calcium compound selected from the group consisting of calcium oxide, calcium hydroxide, calcium carbonate and a mixture thereof, And 0.1 to 200 parts by weight, preferably 0.1 to 100 parts by weight, more preferably 0.1 to 50 parts by weight of a compound selected from the group consisting of silicon, aluminum, iron, magnesium, More preferably from 0.1 to 30 parts by weight, per 100 parts by weight of the composition. Mixing the mixture with 1 to 50 parts by weight, preferably 5 to 30 parts by weight of a dispersing agent, and 50 to 600 parts by weight, preferably 150 to 450 parts by weight, of a dispersing agent.

상기 주제를 제조하는 단계 도중에, 상기 칼슘 화합물을 평균입경 0.01 내지 100 ㎛, 바람직하게는 0.01 내지 50 ㎛, 보다 바람직하게는 0.01 내지 30 ㎛가 되도록 분쇄하는 단계를 추가로 포함할 수 있다.The calcium compound may be further pulverized so as to have an average particle diameter of 0.01 to 100 탆, preferably 0.01 to 50 탆, more preferably 0.01 to 30 탆, during the step of manufacturing the subject matter.

상기 주제의 제조와 별도로 상기 칼슘 화합물 100 중량부 당, 알칼리금속 또는 알칼리토금속의 수산화물, 트리에탄올아민 또는 그 혼합물, 바람직하게는 수산화나트륨 0.5 내지 30 중량부, 바람직하게는 2 내지 20 중량부, 물 1 내지 50 중량부, 바람직하게는 10 내지 50 중량부를 혼합하여 보조제를 제조한다. Separately from the preparation of the subject matter, per 100 parts by weight of the calcium compound, a hydroxide of an alkali metal or alkaline earth metal, triethanolamine or a mixture thereof, preferably 0.5 to 30 parts by weight, preferably 2 to 20 parts by weight, To 50 parts by weight, and preferably from 10 to 50 parts by weight, of the composition is mixed to prepare an auxiliary agent.

상기 주제와 보조제가 제조되면 이들을 혼합한다. 상기 혼합은 주제를 보조제로 적가하거나, 보조제를 주제로 적가하는 것일 수 있다.When the subject and adjuvant are manufactured, they are mixed. The mixing may be to add the subject as an adjuvant, or to drop the adjuvant on a subject.

상기 주제와 보조제를 혼합하는 단계 이후에, 상기 주제와 보조제의 혼합물을 5 내지 100 ℃, 바람직하게는 60 내지 80 ℃에서 0.5 내지 24 시간, 바람직하게는 0.5 내지 12 시간 동안 유지하는 단계를 추가로 포함할 수 있다. 상기 유지온도 및 유지시간이 상기 범위 이내일 때 물의 기화를 방지하고 경제성을 유지하면서도 반응을 충분히 진행시킬 수 있어 본 발명 조강혼합물의 성능 및 안정성을 확보할 수 있다. The step of maintaining the mixture of the subject and the adjuvant at 5 to 100 DEG C, preferably at 60 to 80 DEG C for 0.5 to 24 hours, preferably 0.5 to 12 hours, . When the holding temperature and the holding time are within the above range, vaporization of water can be prevented and the reaction can be sufficiently advanced while maintaining economical efficiency, thereby ensuring the performance and stability of the instant invention crude steel mixture.

또한, 본 발명의 시멘트 콘크리트용 조강혼합물의 제조방법은 상기 주제에 상기 칼슘 화합물 100 중량부 당, 알칼리금속 또는 알칼리토금속의 초산염, 포름산염, 질산염, 아질산염, 황산염, 티오황산염, 탄산염, 염화물, 할로겐화물, 알칸올아민, 염화철, 칼슘알루미네이트실리케이트, 및 그 혼합물로 이루어진 군에서 선택된 수화반응 촉진제, 바람직하게는 알칼리금속 또는 알칼리토금속의 질산염, 보다 바람직하게는 질산칼슘 1 내지 50 중량부, 바람직하게는 5 내지 30 중량부를 추가로 포함할 수 있다.The method for producing a crude steel mixture for cement concrete according to the present invention is characterized in that the above-mentioned subject matter contains, per 100 parts by weight of the calcium compound, an alkali metal or alkaline earth metal nitrate, formate, nitrate, nitrite, sulfate, thiosulfate, carbonate, Preferably from 1 to 50 parts by weight of a hydration reaction promoter selected from the group consisting of hydrocarbons, cargoes, alkanolamines, iron chloride, calcium aluminate silicates, and mixtures thereof, preferably an alkali metal or alkaline earth metal, more preferably calcium nitrate May further comprise 5 to 30 parts by weight.

또한, 본 발명의 시멘트 콘크리트용 조강혼합물의 제조방법은 상기 주제에 상기 칼슘 화합물 100 중량부 당, 시멘트 0.01 내지 5 중량부를 추가로 포함할 수 있다. The method for preparing a crude steel mixture for cement concrete according to the present invention may further include 0.01 to 5 parts by weight of cement per 100 parts by weight of the calcium compound.

또한, 본발명의 시멘트 콘크리트용 조강혼합물의 제조방법은 상기 주제에 상기 칼슘 화합물 100 중량부 당, 플라이애쉬, 바텀애쉬, 실리카퓸, 실리카, 규산염, 물유리, 슬래그 및 그 혼합물로 이루어진 군에서 선택된 실리카 화합물 10 내지 100 중량부, 바람직하게는 20 내지 70 중량부를 추가로 포함할 수 있다.The method for producing a crude steel mixture for cement concrete according to the present invention is characterized in that the above-mentioned subject matter contains, per 100 parts by weight of the calcium compound, silica selected from the group consisting of fly ash, bottom ash, silica fume, silica, silicate, water glass, 10 to 100 parts by weight, preferably 20 to 70 parts by weight, of the compound.

또한, 본발명의 시멘트 콘크리트용 조강혼합물의 제조방법은 상기 주제에 상기 칼슘 화합물 100 중량부 당, 칼슘실리케이트하이드레이트 0.1 내지 20 중량부를 추가로 포함할 수 있다.The method for preparing a crude steel mixture for cement concrete according to the present invention may further comprise 0.1 to 20 parts by weight of calcium silicate hydrate per 100 parts by weight of the calcium compound.

또한, 본 발명의 시멘트 콘크리트용 조강혼합물의 제조방법은 주제의 제조단계 도중에, 상기 칼슘 화합물을 분쇄할 때 상기 시멘트 역시 함께 분쇄할 수 있고, 상기 분쇄 후의 상기 시멘트의 평균입경은 0.01 내지 100 ㎛, 바람직하게는 0.01 내지 50 ㎛, 보다 바람직하게는 0.01 내지 30 ㎛일 수 있다.Further, in the method for producing a crude steel mixture for cement concrete according to the present invention, the cement may be crushed together with the calcium compound during crushing the calcium compound during the production of the subject matter. The crushed cement has an average particle diameter of 0.01 to 100 탆, Preferably 0.01 to 50 mu m, more preferably 0.01 to 30 mu m.

또한, 본 발명의 시멘트 콘크리트용 조강혼합물의 제조방법은 상기 주제의 제조단계 도중에, 상기 칼슘 화합물을 분쇄할 때 상기 실리카 화합물 역시 함께 분쇄할 수 있고, 상기 분쇄 후의 상기 실리카 화합물의 평균입경은 0.01 내지 100 ㎛, 바람직하게는 0.01 내지 50 ㎛, 보다 바람직하게는 0.01 내지 30 ㎛일 수 있다.In the method for producing a crude steel mixture for cement concrete according to the present invention, when the calcium compound is pulverized during the production of the subject matter, the silica compound may also be pulverized together, and the average particle diameter of the silica compound after pulverization is 0.01 - 100 mu m, preferably 0.01 to 50 mu m, and more preferably 0.01 to 30 mu m.

또한, 본 발명의 시멘트 콘크리트용 조강혼합물의 제조방법은 상기 주제에 상기 칼슘 화합물 100 중량부 당, 습윤제 0.001 내지 5 중량부, 바람직하게는 0.01 내지 1 중량부를 추가로 포함할 수 있다. The method for preparing a crude steel mixture for cement concrete according to the present invention may further include 0.001 to 5 parts by weight, preferably 0.01 to 1 part by weight, of a wetting agent per 100 parts by weight of the calcium compound.

또한, 본 발명의 시멘트 콘크리트용 조강혼합물의 제조방법은 상기 주제에 상기 칼슘 화합물 100 중량부 당, 증점제 0.001 내지 5 중량부, 바람직하게는 0.01 내지 1 중량부를 추가로 포함할 수 있다.The method for producing a crude steel mixture for cement concrete according to the present invention may further include 0.001 to 5 parts by weight, preferably 0.01 to 1 part by weight, of a thickener per 100 parts by weight of the calcium compound.

또한, 본 발명의 시멘트 콘크리트용 조강혼합물의 제조방법은 상기 주제에 상기 칼슘 화합물 100 중량부 당, 소포제 0.001 내지 5 중량부, 바람직하게는 0.1 내지 5 중량부를 추가로 포함할 수 있다.The method for preparing a crude steel mixture for cement concrete according to the present invention may further include 0.001 to 5 parts by weight, preferably 0.1 to 5 parts by weight, of a defoaming agent per 100 parts by weight of the calcium compound.

또한, 본 발명의 시멘트 콘크리트용 조강혼합물은 상기 방법에 의해 제조된 것을 특징으로 한다.Further, the crude steel mixture for cement concrete of the present invention is characterized by being produced by the above-mentioned method.

이하 본 발명을 실시예를 들어 상세히 설명하고자 하나, 하기 실시예는 본 발명을 예시하기 위한 것일 뿐 이로 인해 본 발명의 범위가 제한되는 것은 아니다.EXAMPLES Hereinafter, the present invention will be described in detail with reference to Examples. However, the following Examples are intended to illustrate the present invention and are not to be construed as limiting the scope of the present invention.

실시예Example

실시예 1 : 조강혼합물의 제조 (1)Example 1: Preparation of crude steel mixture (1)

물 200 g에 소석회 150 g, 질산칼슘 20 g, 및 분산제 (이지스, 한국) 7 g을 첨가하고, 평균입경 5 ㎛로 분쇄하여 주제를 제조하였다. 상기 주제와 별도로 물 15 g에 수산화나트륨 15 g을 첨가하여 보조제를 제조하였다. 상기 주제를 플라스크에 넣고 상기 보조제를 적가한 후 70 ℃에서 교반하며 8 시간 동안 유지시켜 본 발명의 시멘트 콘크리트용 조강혼합물을 제조하였다.150 g of calcium hydroxide, 20 g of calcium nitrate, and 7 g of a dispersant (Aegis, Korea) were added to 200 g of water and ground to an average particle size of 5 탆 to prepare a subject. Adjuvants were prepared by adding 15 g of sodium hydroxide to 15 g of water separately from the subject. The above-mentioned subject matter was placed in a flask, the auxiliary agent was added dropwise, and the mixture was stirred at 70 DEG C for 8 hours to prepare a crude steel mixture for cement concrete according to the present invention.

실시예 2 : 조강혼합물의 제조 (2)Example 2: Preparation of crude steel mixture (2)

실시예 1과 동일한 과정을 거치되, 상기 주제 제조시 상기 분산제는 적가하여 본 발명의 시멘트 콘크리트용 조강혼합물을 제조하였다.The same procedure as in Example 1 was carried out, and the dispersant was added dropwise at the time of preparing the subject to prepare a crude steel mixture for cement concrete of the present invention.

실시예 3 : 조강혼합물의 제조 (3)Example 3: Preparation of crude steel mixture (3)

물 200 g에 소석회 150 g 및 분산제 (이지스, 한국) 7 g을 첨가하고, 평균입경 5 ㎛로 분쇄하여 주제를 제조하였다. 상기 주제와 별도로 물 50 g에 수산화나트륨 15 g을 첨가하여 보조제를 제조하였다. 그리고, 물 30 g에 질산칼슘 20 g을 첨가하고, 평균입경 5 ㎛로 분쇄하여 질산칼슘 수용액을 제조하였다. 상기 주제를 플라스크에 넣고 상기 보조제 및 질산칼슘 수용액을 적가한 후 70 ℃에서 교반하며 8 시간 동안 유지시켜 본 발명의 시멘트 콘크리트용 조강혼합물을 제조하였다.150 g of slaked lime and 7 g of a dispersant (Aegis, Korea) were added to 200 g of water and ground to an average particle diameter of 5 탆 to prepare a subject. Adjuvants were prepared by adding 15 g of sodium hydroxide to 50 g of water separately from the subject. Then, 20 g of calcium nitrate was added to 30 g of water and ground to an average particle diameter of 5 탆 to prepare an aqueous calcium nitrate solution. The above-mentioned subject matter was placed in a flask, the auxiliary agent and an aqueous solution of calcium nitrate were added dropwise, and the mixture was stirred at 70 캜 for 8 hours to prepare a crude steel mixture for cement concrete of the present invention.

제조예 1 내지 7 : 시멘트 모르타르의 제조Production Examples 1 to 7: Preparation of Cement Mortar

하기 표 1의 혼합비율로 시멘트 모르타르를 제조하였다. (감수제: 이지스, 한국)Cement mortar was prepared in the mixing ratio shown in Table 1 below. (Water reducing agent: Aegis, Korea)

Figure pat00001
Figure pat00001

시험예 1 : 조성 변화에 따른 시멘트 모르타르의 압축강도 변화Test Example 1: Compressive Strength Change of Cement Mortar According to Composition Variation

상기 제조예 1 내지 6에서 제조한 시멘트 모르타르에 대해 조강혼합물의 첨가에 따른 압축강도를 측정하였다. 측정은 온도 15 ℃, 상대습도 60 %에서 24 시간 동안 양생한 후에 이루어졌으며, 그 결과를 표 2에 나타내었다.The compressive strength of the cement mortar prepared in Preparation Examples 1 to 6 was measured according to the addition of the crude steel mixture. The measurement was carried out after curing for 24 hours at a temperature of 15 ° C and a relative humidity of 60%, and the results are shown in Table 2.

Figure pat00002
Figure pat00002

시험예 2 : 온도 변화에 따른 시멘트 모르타르의 압축강도 변화Test Example 2: Compressive Strength Change of Cement Mortar with Temperature

상기 제조예 1 내지 6에서 제조한 시멘트 모르타르에 대해 조강혼합물의 양생온도에 따른 압축강도를 측정하였다. 측정은 상대습도 60 %에서 24 시간 동안 양생한 후에 이루어졌으며, 그 결과를 표 3에 나타내었다.The cement mortar prepared in Preparation Examples 1 to 6 was measured for compressive strength according to the curing temperature of the crude steel mixture. The measurement was carried out after curing for 24 hours at a relative humidity of 60%, and the results are shown in Table 3.

Figure pat00003
Figure pat00003

상기 시험예 1 및 2의 결과를 보면 시멘트의 양이 동일할 때 본 발명의 조강혼합물을 첨가함으로써 보다 큰 조기 압축강도값을 얻음을 알 수 있었다.The results of Test Examples 1 and 2 show that when the amount of cement is the same, a premature compression strength value is obtained by adding the crude steel mixture of the present invention.

제조예 8 내지 13 : 시멘트 콘크리트의 제조Production Examples 8 to 13: Preparation of cement concrete

하기 표 4의 혼합비율로 시멘트 콘크리트를 제조하였다. (감수제: 이지스, 한국)Cement concrete was prepared by mixing ratios shown in Table 4 below. (Water reducing agent: Aegis, Korea)

Figure pat00004
Figure pat00004

시험예 3 : 조성 변화에 따른 시멘트 콘크리트의 압축강도 변화Test Example 3: Compressive Strength Change of Cement Concrete According to Composition Variation

상기 제조예 8 내지 13에서 제조한 시멘트 콘크리트에 대해 조강혼합물의 첨가에 따른 압축강도를 측정하였다. 측정은 온도 15 ℃, 상대습도 60 %에서 24 시간 동안 양생한 후에 이루어졌으며, 그 결과를 표 5에 나타내었다.The compressive strength of the cement concrete prepared in Preparation Examples 8 to 13 was measured according to the addition of the crude steel mixture. The measurement was carried out after curing for 24 hours at a temperature of 15 ° C and a relative humidity of 60%, and the results are shown in Table 5.

Figure pat00005
Figure pat00005

상기 시험예 3의 결과를 보면 시멘트의 양이 동일할 때 본 발명의 조강혼합물을 첨가함으로써 보다 큰 조기 압축강도값을 얻음을 알 수 있었다.The results of Test Example 3 show that when the amount of cement is the same, a higher early compression strength value is obtained by adding the crude steel mixture of the present invention.

이상에서 본 발명의 바람직한 실시예에 대해서 설명하였으나, 본 발명은 상술한 특정의 실시예에 한정되지 아니하며, 당해 기술분야에서 통상의 지식을 가진 자라면 본원 발명의 요지를 벗어남이 없이 다양한 변형 실시가 가능함은 물론이다. 따라서, 본 발명의 범위는 위의 실시예에 국한해서 해석되어서는 안되며, 후술하는 특허청구범위 뿐만 아니라 이 특허청구범위와 균등한 것들에 의해 정해져야 할 것이다.While the present invention has been described in connection with what is presently considered to be practical exemplary embodiments, it is to be understood that the invention is not limited to the disclosed embodiments, but, on the contrary, Of course it is possible. Accordingly, the scope of the present invention should not be construed as being limited to the above-described embodiments, but should be determined by equivalents to the appended claims, as well as the following claims.

Claims (1)

(A) 산화칼슘, 수산화칼슘, 탄산칼슘 및 그 혼합물로 이루어진 군에서 선택된 칼슘 화합물 100 중량부,
규소, 알루미늄, 철, 그 산화물 및 혼합물로 구성된 군에서 선택된 화합물 0.1 내지 200 중량부,
분산제 1 내지 50 중량부,
물 50 내지 600 중량부를 혼합하여 주제를 제조하는 단계;
(B) 상기 칼슘 화합물 100 중량부 당,
알칼리금속 또는 알칼리토금속의 수산화물, 또는 그 혼합물 0.5 내지 30 중량부,
물 1 내지 50 중량부를 혼합하여 보조제를 제조하는 단계; 및
(C) 상기 주제와 보조제를 혼합하는 단계를 포함하고,
연간 점도 변화량은 0 내지 1000 cPs이고,
상기 규소, 알루미늄, 철, 그 산화물 및 혼합물로 구성된 군에서 선택된 화합물은 상기 칼슘 화합물 원료에 포함되어, 상기 칼슘 화합물 원료의 순도를 저하시키고,
상기 칼슘 화합물 원료 중 칼슘 화합물과 상기 규소, 알루미늄, 철, 그 산화물 및 혼합물로 구성된 군에서 선택된 화합물의 함량은 상기 칼슘 화합물 100 중량부 당 상기 규소, 알루미늄, 철, 그 산화물 및 혼합물로 구성된 군에서 선택된 화합물이 0.1 내지 200 중량부인,
시멘트 콘크리트용 조강혼합물의 제조방법.(A) 100 parts by weight of a calcium compound selected from the group consisting of calcium oxide, calcium hydroxide, calcium carbonate and mixtures thereof,
0.1 to 200 parts by weight of a compound selected from the group consisting of silicon, aluminum, iron,
1 to 50 parts by weight of a dispersant,
Mixing 50 to 600 parts by weight of water to prepare a subject;
(B) per 100 parts by weight of the calcium compound,
0.5 to 30 parts by weight of a hydroxide of an alkali metal or an alkaline earth metal, or a mixture thereof,
Mixing 1 to 50 parts by weight of water to prepare an adjuvant; And
(C) mixing the subject matter with an adjuvant,
The annual viscosity variation is between 0 and 1000 cPs,
A compound selected from the group consisting of silicon, aluminum, iron, an oxide thereof, and a mixture is included in the calcium compound raw material to lower the purity of the calcium compound raw material,
The content of the calcium compound and the compound selected from the group consisting of silicon, aluminum, iron, an oxide thereof, and a mixture thereof in the calcium compound raw material is preferably in the range of 1 to 100 parts by weight per 100 parts by weight of the silicon, aluminum, iron, Wherein the selected compound is 0.1 to 200 parts by weight,
Process for preparing crude steel mixture for cement concrete.
KR1020180087888A 2018-07-27 2018-07-27 Mixture of early strength for cement concrete including calcium compound and manufacturing method of the same KR20180088773A (en)