KR20180044691A - Waterproof sound-transmitting sheet and waterproof sound-transmitting sheet manufacturing method - Google Patents

Waterproof sound-transmitting sheet and waterproof sound-transmitting sheet manufacturing method Download PDF

Info

Publication number
KR20180044691A
KR20180044691A KR1020160138507A KR20160138507A KR20180044691A KR 20180044691 A KR20180044691 A KR 20180044691A KR 1020160138507 A KR1020160138507 A KR 1020160138507A KR 20160138507 A KR20160138507 A KR 20160138507A KR 20180044691 A KR20180044691 A KR 20180044691A
Authority
KR
South Korea
Prior art keywords
waterproof
layer
waterproof layer
spinning solution
solvent
Prior art date
Application number
KR1020160138507A
Other languages
Korean (ko)
Other versions
KR102290013B1 (en
Inventor
서인용
Original Assignee
주식회사 아모그린텍
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 주식회사 아모그린텍 filed Critical 주식회사 아모그린텍
Priority to KR1020160138507A priority Critical patent/KR102290013B1/en
Publication of KR20180044691A publication Critical patent/KR20180044691A/en
Application granted granted Critical
Publication of KR102290013B1 publication Critical patent/KR102290013B1/en

Abstract

Provided are a waterproof and sound-transmitting sheet, and a waterproof and sound-transmitting sheet production method, intended to improve waterproofness while increasing sound transmission efficiency by forming a pore-free layer on the bottom of a waterproof layer formed in a nanoweb-like structure using a solvent contained in a spinning solution for electrospinning. To this end, the provided waterproof and sound-transmitting sheet production method comprises the following steps: electrospinning the spinning solution made of a polymeric material and the solvent to one side of a collection support so as to form the nanoweb-like waterproof layer; and dissolving down the bottom side adjacent to one side of the collection support on the waterproof layer with the solvent contained in the spinning solution, so as to form the pore-free layer.

Description

방수 통음 시트 및 방수 통음 시트 제조 방법{WATERPROOF SOUND-TRANSMITTING SHEET AND WATERPROOF SOUND-TRANSMITTING SHEET MANUFACTURING METHOD}BACKGROUND OF THE INVENTION 1. Field of the Invention [0001] The present invention relates to a waterproofing sheet, a waterproofing sheet, and a waterproofing sheet. BACKGROUND OF THE INVENTION 1. Field of the Invention [0001]

본 발명은 방수 통음 시트 및 방수 통음 시트 제조 방법에 관한 것으로, 더욱 상세하게는 음전달 효율을 높이면서 방수성을 향상시킨 방수 통음 시트 및 방수 통음 시트 제조 방법에 관한 것이다.BACKGROUND OF THE INVENTION 1. Field of the Invention [0002] The present invention relates to a waterproof and soundproof sheet and a method for manufacturing a waterproof and soundproof sheet, and more particularly, to a waterproof soundproof sheet and a waterproof soundproof sheet.

최근 휴대용 단말기, 디지털 카메라, 노트북 등과 같은 모바일 전자기기의 사용이 날로 증가하고 있다. 이러한 모바일 전자기기는 휴대하면서 사용하기 때문에 방수 기능을 갖는 것이 요구되고 있다. 하지만, 스피커나 마이크 등이 설치되는 부분에는 소리를 방출시키는 음향 홀이 형성되고, 이 음향 홀을 통해 물이나 먼지가 전자기기 내부로 침투하게 된다.Recently, the use of mobile electronic devices such as portable terminals, digital cameras, notebooks and the like is increasing. Such mobile electronic devices are required to have a waterproof function because they are used while being portable. However, sound holes for emitting sound are formed in a portion where a speaker or a microphone is installed, and water or dust penetrates into the electronic device through the acoustic holes.

따라서, 음향 홀에는 소리는 통과시키고 물이나 먼지를 차단하는 방수통음시트가 설치된다. 이러한 방수통음시트는 방수성 및 음전달 효율을 모두 고려하여 제조되어야 한다. Therefore, the sound hole is provided with a waterproof sound insulating sheet for passing sound and blocking water or dust. Such a waterproofing soundproof sheet should be manufactured in consideration of both waterproofness and sound transmission efficiency.

방수통음시트 관련하여, 공개특허공보 제10-2010-0041839호(2010년 04월 22일)는 폴리테트라플루오로에틸렌 다공질막으로 형성된 구성을 개시하고 있다. 하지만, 종래의 방수 통음막은 폴리테트라플루오로에틸렌 다공질막으로만 구성되기 때문에 사용기간이 길어짐에 따라 외부에서 가해지는 충격이나 소리의 압력 등으로 인하여 다공질막의 미세 구멍이 점차적으로 커지게 되고, 이에 따라 방수 성능이 저하되는 문제가 있다.With respect to the waterproofing sheet, Patent Document 10-10-2010-0041839 (April 22, 2010) discloses a structure formed of a polytetrafluoroethylene porous film. However, since the conventional watertight sound insulating membrane is composed only of a polytetrafluoroethylene porous film, the micropores of the porous membrane gradually become larger due to external shocks and sound pressure as the use period becomes longer, There is a problem that the waterproof performance is deteriorated.

한국공개특허 제10-2010-0041839호(명칭: 방수 통음막, 방수 통음막의 제조 방법 및 그것을 사용한 전기 제품)Korean Patent Laid-Open No. 10-2010-0041839 (name: a method for manufacturing a waterproofing membrane, a waterproofing membrane, and an electric product using the same)

본 발명은 상기한 종래의 문제점을 해결하기 위해 제안된 것으로, 전기방사용 방사용액에 포함된 솔벤트로 나노 웹 형태로 형성된 방수층의 하면에 무기공층을 형성하여 음전달 효율을 높이면서 방수성을 향상되도록 한 방수 통음 시트 및 방수 통음 시트 제조 방법을 제공하는 것을 목적으로 한다.The present invention has been proposed in order to overcome the above-described problems of the prior art, and it is an object of the present invention to provide an inorganic porous layer on the lower surface of a waterproof layer formed of a nano- And a method for manufacturing a waterproofing and soundproofing sheet.

상기한 목적을 달성하기 위하여 본 발명의 실시예에 따른 방수 방음 시트 제조 방법은 포집 지지체를 준비하는 단계, 고분자 물질 및 솔벤트로 녹여 방사용액을 준비하는 단계, 방사용액을 포집 지지체의 일면에 전기방사하여 나노 웹 형태의 방수층을 형성하는 단계 및 방수층 중 포집 지지체의 일면에 인접한 일부를 솔벤트로 녹여 무기공층을 형성하는 단계를 포함한다.In order to achieve the above object, a method for manufacturing a waterproof and soundproof sheet according to an embodiment of the present invention includes the steps of preparing a collection support, preparing a spinning solution by melting with a polymer material and a solvent, Forming a water-repellent layer in the form of a nano-web; and dissolving a portion of the water-repellent layer adjacent to one side of the collecting support with a solvent to form an inorganic porous layer.

포집 지지체를 준비하는 단계는 필름형의 무기공성 부재로 형성되는 포집 지지체를 준비하는 단계를 포함할 수 있다. 이때, 포집 지지체를 준비하는 단계는 이형지(release paper), 아트지(art papper), 코트지(coated paper), 광택지(glossy paper) 중에 적어도 하나인 포집 지지체를 준비하는 단계를 포함할 수 있다.The step of preparing the collection support may include preparing a collection support formed of a film-like inorganic porous member. At this time, the step of preparing the collecting support may include preparing a collecting support which is at least one of release paper, art papper, coated paper, and glossy paper.

상기한 목적을 달성하기 위하여 본 발명의 실시예에 따른 방수 방음 시트는 방사용액을 전기방사하여 나노웹 형태로 형성된 방수층을 포함하고, 방수층은 하면이 방사용액에 포함된 솔벤트에 의해 녹아 무기공층을 형성한다.To achieve the above object, a waterproof and soundproof sheet according to an embodiment of the present invention includes a waterproof layer formed in the form of a nanoweb by electrospinning a spinning solution, and the waterproof layer is formed by dissolving the inorganic layer by the solvent contained in the spinneret. .

본 발명에 의하면, 방수 방음 시트는 나노 웹 형태의 기공성 방수층이 형성되며, 방수층의 하층에 무기공층이 형성됨에 따라, 전체 부피 대비해서 무기공 필름으로 구성되는 종래의 방수 방음 시트에 비해 무게가 가볍고 신축성이 우수한 효과가 있다.According to the present invention, since the waterproof soundproof sheet has a porous waterproof layer in the form of a nano-web and the inorganic porous layer is formed in the lower layer of the waterproof layer, the weight of the waterproof soundproof sheet is smaller than that of the conventional waterproof soundproof sheet It is light and has excellent stretch effect.

또한, 방수 방음 시트는 나노 웹 형태의 기공성 방수층이 형성되며, 방수층의 하층에 무기공층을 형성하여 무게가 가볍고 신축성이 우수함으로써, 음향특성 면에서 진동을 하기에 좋은 구조로 이루어져 있으며, 완전한 기공 형태보다 일부는 무기공 형태로 필름화 되어 있어 고내수압으로 갈수록 방수 성능에서 장점이 있다.In addition, the waterproof soundproof sheet is formed of a porous waterproof layer in the form of a nano-web, and has an inorganic porous layer formed in the lower layer of the waterproof layer, and is light in weight and excellent in stretchability, Some of them are in the form of inorganic balls rather than the shape, and the water resistance is improved as the water pressure increases.

도 1은 본 발명의 실시예에 따른 방수 방음 시트 제조 방법을 설명하기 위한 도면.
도 2 내지 도 8은 본 발명의 실시예에 따른 방수 방음 시트를 설명하기 위한 도면.
1 is a view for explaining a method of manufacturing a waterproof and soundproof sheet according to an embodiment of the present invention;
2 to 8 are views for explaining a waterproof soundproof sheet according to an embodiment of the present invention.

이하, 본 발명이 속하는 기술분야에서 통상의 지식을 가진 자가 본 발명의 기술적 사상을 용이하게 실시할 수 있을 정도로 상세히 설명하기 위하여, 본 발명의 가장 바람직한 실시예를 첨부 도면을 참조하여 설명하기로 한다. 우선 각 도면의 구성요소들에 참조부호를 부가함에 있어서, 동일한 구성요소들에 대해서는 비록 다른 도면상에 표시되더라도 가능한 한 동일한 부호를 가지도록 하고 있음에 유의해야 한다. 또한, 본 발명을 설명함에 있어, 관련된 공지 구성 또는 기능에 대한 구체적인 설명이 본 발명의 요지를 흐릴 수 있다고 판단되는 경우에는 그 상세한 설명은 생략한다.DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS Hereinafter, preferred embodiments of the present invention will be described in detail with reference to the accompanying drawings in order to facilitate a person skilled in the art to easily carry out the technical idea of the present invention. . In the drawings, the same reference numerals are used to designate the same or similar components throughout the drawings. In the following description of the present invention, a detailed description of known functions and configurations incorporated herein will be omitted when it may make the subject matter of the present invention rather unclear.

도 1을 참조하면, 본 발명의 실시예에 따른 방수 통음 시트 제조 방법은 포집 지지체를 준비하는 단계(S100), 방사용액을 준비하는 단계(S200), 전기방사를 통해 방수층을 형성하는 단계(S300), 방수층에 무기공층을 형성하는 단계(S400)를 포함하여 구성된다.Referring to FIG. 1, a method for manufacturing a waterproofing sheet according to an embodiment of the present invention includes preparing a collection support (S100), preparing a spinning solution (S200), forming a waterproof layer through electrospinning And forming an inorganic porous layer on the waterproof layer (S400).

포집 지지체를 준비하는 단계(S100)는 표면에 방수 통음 시트가 형성될 포집 지지체를 준비한다. 이때, 포집 지지체는 필름형의 무기공성 부재로 형성된다. 일례로, 포집 지지체는 이형지(release paper), 아트지(art papper), 코트지(coated paper), 광택지(glossy paper) 중에 하나일 수 있다.In step S100 of preparing a collection support, a collection support on which a waterproofing sheet is to be formed is prepared. At this time, the collecting support body is formed of a film-like inorganic porous member. For example, the collection support may be one of release paper, art papper, coated paper, and glossy paper.

방사용액을 준비하는 단계(S200)는 고분자 물질 및 솔벤트를 포함하는 방사 용액을 준비한다. In preparing the spinning solution (S200), a spinning solution containing a polymer material and a solvent is prepared.

이때, 고분자 물질은 폴리아마이드, 폴리이미드, 폴리아마이드이미드, 폴리(메타-페닐렌 이소프탈아미이드), 폴리설폰, 폴리에테르케톤, 폴리에테르 이미드, 폴리에틸렌텔레프탈레이트, 폴리트리메틸렌텔레프탈레이트, 폴리에틸렌 나프탈레이트 등과 같은 방향족 폴리에스터, 폴리테트라플루오로에틸렌, 폴리디페녹시포스파젠, 폴리{비스[2-(2-메톡시에톡시)포스파젠]} 같은 폴리포스파젠류, 폴리우레탄 및 폴리에테르우레탄을 포함하는 폴리우레탄공중합체, 셀룰로오스 아세테이트, 셀룰로오스 아세테이트 부틸레이트, 셀룰로오스 아세테이트 프로피오네이트 등을 사용할 수 있다. 또한 폴리비닐리덴플루오라이드(PVDF), 폴리(비닐리덴플루오라이드-코-헥사플루오로프로필렌), 퍼풀루오로폴리머, 폴리비닐클로라이드 또는 폴리비닐리덴 클로라이드 및 이들의 공중합체 및 폴리에틸렌글리콜 디알킬에테르 및 폴리에틸렌글리콜 디알킬에스터를 포함하는 폴리에틸렌글리콜 유도체, 폴리(옥시메틸렌-올리 고-옥시에틸렌), 폴리에틸렌옥사이드 및 폴리프로필렌옥사이드를 포함하는 폴리옥사이드, 폴리비닐아세테이트, 폴리(비닐피롤리돈-비닐아세테이트), 폴리스티렌 및 폴리스티렌 아크릴로니트릴 공중합체, 폴리아크릴로니트릴, 폴리아크릴로니트릴 메틸메타크릴레이트 공중합체를 포함하는 폴리아크릴로니트릴 공중합체, 폴리메틸메타크릴레이트, 폴리메틸메타크릴레이트 공중합체 및 이들의 혼합물로도 형성될 수 있다. The polymeric material may be selected from the group consisting of polyamide, polyimide, polyamideimide, poly (meta-phenylene isophthalamide), polysulfone, polyether ketone, polyether imide, polyethylene terephthalate, polytrimethylene terephthalate, polyethylene Aromatic polyesters such as naphthalate and the like, polyphosphazenes such as polytetrafluoroethylene, polydiphenoxaphospazene and poly {bis [2- (2-methoxyethoxy) phosphazene], polyurethanes and polyethers Urethane-containing polyurethane copolymer, cellulose acetate, cellulose acetate butyrate, cellulose acetate propionate and the like can be used. It is also possible to use polyvinylidene fluoride (PVDF), poly (vinylidene fluoride-co-hexafluoropropylene), perfluoropolymers, polyvinyl chloride or polyvinylidene chloride and copolymers thereof and polyethylene glycol dialkyl ethers and (Polyvinylpyrrolidone-vinyl acetate), polyethylene glycol derivatives including polyethylene glycol dialkyl esters, poly (oxymethylene-oligo-oxyethylene), polyoxides including polyethylene oxide and polypropylene oxide, polyvinyl acetate, , Polystyrene and polystyrene acrylonitrile copolymers, polyacrylonitrile, polyacrylonitrile copolymers including polyacrylonitrile methyl methacrylate copolymers, polymethyl methacrylate, polymethyl methacrylate copolymers and the like May also be formed.

방사용액을 준비하는 단계(S200)는 고분자 물질, 솔벤트 및 비드(bead)를 포함하는 방사 용액을 준비할 수 있다.In preparing the spinning solution (S200), a spinning solution containing a polymer material, a solvent, and a bead may be prepared.

전기방사를 통해 방수층을 형성하는 단계(S300)는 포집 지지체의 적어도 일면에 방사용액을 전기방사하여 나노 웹 형태의 방수층을 형성한다.In the step S300 of forming the waterproof layer through the electrospinning, a spinning solution is electrospun on at least one surface of the collection support to form a waterproof layer in the form of a nano-web.

방수층은 포집 지지체의 전면 및 후면 중 적어도 일면에 필름형으로 형성된다. 그리고, 방수층은 복수개의 미세 섬유 가닥이 교차 적층된 다공성 나노 웹으로 형성된다.The waterproof layer is formed in a film shape on at least one surface of the front surface and the rear surface of the collection support. The waterproof layer is formed of a porous nano-web in which a plurality of fine fiber strands are cross-laminated.

여기서, 나노 웹은 일반적으로 수백 나노의 직경을 갖는 미세 섬유 가닥이 교차하여 적층된 구조를 의미하지만, 본 발명의 실시예에서는 수백 나노에서 수천 나노까지의 직경을 갖는 미세 섬유 가닥이 교차하여 적층된 구조를 포함한다.Here, the nano-web generally refers to a structure in which fine fiber strands having a diameter of several hundred nanometers are stacked alternately, but in the embodiment of the present invention, fine fiber strands having diameters of several hundred nanometers to several thousand nanometers are cross- Structure.

방수층에 무기공층을 형성하는 단계(S400)는 포집 지지체에 방사된 방사용액에 포함된 솔벤트로 방수층의 일부를 녹여 무기공층을 형성한다. 즉, 방수층을 형성하는 단계(S300)에서 전기방사시 고분자 물질과 함께 솔벤트가 포집 지지체의 표면으로 방사된다.The step of forming an inorganic layer in the waterproof layer (S400) comprises dissolving a part of the waterproof layer with the solvent contained in the spinning solution radiated to the collection support to form an inorganic layer. That is, in step S300 of forming the waterproof layer, the solvent is radiated to the surface of the collection support together with the polymer material during electrospinning.

이때, 솔벤트는 일반적으로 솔벤트로 구성되기 때문에 대부분이 공기 중으로 기화되지만, 일부의 솔벤트는 방수층의 하층(즉, 포집 지지체에 인접한 부분)으로 고인다.At this time, most of the solvent is vaporized into the air because the solvent is generally composed of a solvent, but some of the solvent is concentrated in the lower layer of the waterproof layer (that is, the portion adjacent to the collection substrate).

그에 따라, 방수층의 하층 일부(즉, 포집 지지체에 인접한 일부)에 고인 솔벤트에 의해 나노 웹이 녹아 방수층의 하면에 무기공층이 형성한다.Thereby, the nano-web is melted by the solvent which is poured into a part of the lower layer of the waterproof layer (that is, a part adjacent to the collecting support), and an inorganic porous layer is formed on the lower surface of the waterproof layer.

상술한 과정을 통해, 방수 방음 시트는 나노 웹 형태의 기공성 방수층이 형성되며, 방수층의 하층에 무기공층이 형성됨에 따라, 전체 부피 대비해서 무기공 필름으로 구성되는 종래의 방수 방음 시트에 비해 무게가 가볍고 신축성이 우수한 효과가 있다.Through the above-described process, the waterproof soundproof sheet has a porous waterproof layer in the form of a nano-web, and as the inorganic porous layer is formed on the lower layer of the waterproof layer, compared with the conventional waterproof soundproof sheet composed of inorganic porous film Is light in weight and excellent in stretchability.

또한, 방수 방음 시트는 나노 웹 형태의 기공성 방수층이 형성되며, 방수층의 하층에 무기공층을 형성하여 무게가 가볍고 신축성이 우수함으로써, 음향특성 면에서 진동을 하기에 좋은 구조로 이루어져 있으며, 완전한 기공 형태보다 일부는 무기공 형태로 필름화 되어 있어 고내수압으로 갈수록 방수 성능에서 장점이 있다.In addition, the waterproof soundproof sheet is formed of a porous waterproof layer in the form of a nano-web, and has an inorganic porous layer formed in the lower layer of the waterproof layer, and is light in weight and excellent in stretchability, Some of them are in the form of inorganic balls rather than the shape, and the water resistance is improved as the water pressure increases.

도 2를 참조하면, 본 발명의 실시예에 따른 방수 방음 시트(200)는 상층이 나노 웹 형태로 형성되고, 하층이 무기공 형태로 형성된 방수층(220)으로 구성된다.Referring to FIG. 2, the waterproofing and soundproofing sheet 200 according to the embodiment of the present invention is formed of a waterproof layer 220 in which an upper layer is formed as a nano-web and a lower layer is formed as an inorganic ball.

방수층(220)은 포집 지지체(100)의 적어도 일면에 방사용액을 전기방사하여 형성된다. 방수층(220)은 나노 웹 형태로 형성되어, 복수의 기공을 갖도록 형성된다. 이때, 방수층(220)은 포집 지지체(100)의 전면 및 후면 중 적어도 일면에 필름형으로 형성된다. 그리고, 방수층(220)은 복수개의 미세 섬유 가닥이 교차 적층된 다공성 나노 웹으로 형성된다. 여기서, 나노 웹은 일반적으로 수백 나노의 직경을 갖는 미세 섬유 가닥이 교차하여 적층된 구조를 의미하지만, 본 발명의 실시예에서는 수백 나노에서 수천 나노까지의 직경을 갖는 미세 섬유 가닥이 교차하여 적층된 구조를 포함한다.The waterproof layer 220 is formed by electrospinning a spinning solution on at least one surface of the collection support 100. The waterproof layer 220 is formed in the form of a nanoweb, and is formed to have a plurality of pores. At this time, the waterproof layer 220 is formed in a film shape on at least one side of the front surface and the rear surface of the collection support 100. The waterproof layer 220 is formed of a porous nano-web in which a plurality of fine fiber strands are cross-laminated. Here, the nano-web generally refers to a structure in which fine fiber strands having a diameter of several hundred nanometers are stacked alternately, but in the embodiment of the present invention, fine fiber strands having diameters of several hundred nanometers to several thousand nanometers are cross- Structure.

이때, 포집 지지체(100)는 이형지(release paper), 아트지(art papper), 코트지(coated paper), 광택지(glossy paper) 등과 같이 필름형의 무기공성 부재일 수 있다.At this time, the collecting support body 100 may be a film-type inorganic porous member such as release paper, art papper, coated paper, glossy paper and the like.

방사용액은 고분자 물질 및 솔벤트를 포함한다. 이때, 고분자 물질은 폴리아마이드, 폴리이미드, 폴리아마이드이미드, 폴리(메타-페닐렌 이소프탈아미이드), 폴리설폰, 폴리에테르케톤, 폴리에테르 이미드, 폴리에틸렌텔레프탈레이트, 폴리트리메틸렌텔레프탈레이트, 폴리에틸렌 나프탈레이트 등과 같은 방향족 폴리에스터, 폴리테트라플루오로에틸렌, 폴리디페녹시포스파젠, 폴리{비스[2-(2-메톡시에톡시)포스파젠]} 같은 폴리포스파젠류, 폴리우레탄 및 폴리에테르우레탄을 포함하는 폴리우레탄공중합체, 셀룰로오스 아세테이트, 셀룰로오스 아세테이트 부틸레이트, 셀룰로오스 아세테이트 프로피오네이트 등을 사용할 수 있다. 또한 폴리비닐리덴플루오라이드(PVDF), 폴리(비닐리덴플루오라이드-코-헥사플루오로프로필렌), 퍼풀루오로폴리머, 폴리비닐클로라이드 또는 폴리비닐리덴 클로라이드 및 이들의 공중합체 및 폴리에틸렌글리콜 디알킬에테르 및 폴리에틸렌글리콜 디알킬에스터를 포함하는 폴리에틸렌글리콜 유도체, 폴리(옥시메틸렌-올리 고-옥시에틸렌), 폴리에틸렌옥사이드 및 폴리프로필렌옥사이드를 포함하는 폴리옥사이드, 폴리비닐아세테이트, 폴리(비닐피롤리돈-비닐아세테이트), 폴리스티렌 및 폴리스티렌 아크릴로니트릴 공중합체, 폴리아크릴로니트릴, 폴리아크릴로니트릴 메틸메타크릴레이트 공중합체를 포함하는 폴리아크릴로니트릴 공중합체, 폴리메틸메타크릴레이트, 폴리메틸메타크릴레이트 공중합체 및 이들의 혼합물로도 형성될 수 있다. The spinning solution includes a polymer material and a solvent. The polymeric material may be selected from the group consisting of polyamide, polyimide, polyamideimide, poly (meta-phenylene isophthalamide), polysulfone, polyether ketone, polyether imide, polyethylene terephthalate, polytrimethylene terephthalate, polyethylene Aromatic polyesters such as naphthalate and the like, polyphosphazenes such as polytetrafluoroethylene, polydiphenoxaphospazene and poly {bis [2- (2-methoxyethoxy) phosphazene], polyurethanes and polyethers Urethane-containing polyurethane copolymer, cellulose acetate, cellulose acetate butyrate, cellulose acetate propionate and the like can be used. It is also possible to use polyvinylidene fluoride (PVDF), poly (vinylidene fluoride-co-hexafluoropropylene), perfluoropolymers, polyvinyl chloride or polyvinylidene chloride and copolymers thereof and polyethylene glycol dialkyl ethers and (Polyvinylpyrrolidone-vinyl acetate), polyethylene glycol derivatives including polyethylene glycol dialkyl esters, poly (oxymethylene-oligo-oxyethylene), polyoxides including polyethylene oxide and polypropylene oxide, polyvinyl acetate, , Polystyrene and polystyrene acrylonitrile copolymers, polyacrylonitrile, polyacrylonitrile copolymers including polyacrylonitrile methyl methacrylate copolymers, polymethyl methacrylate, polymethyl methacrylate copolymers and the like May also be formed.

방수층(220)의 하층은 포집 지지체(100)에 방사된 방사용액에 포함된 솔벤트에 의해 일부가 녹아 무기공층(240)을 형성한다. 즉, 전기방사시 고분자 물질과 함께 솔벤트가 포집 지지체(100)의 표면으로 방사된다. 이때, 포집 지지체(100)로 방사된 솔벤트는 대부분이 공기 중으로 기화되지만, 일부의 솔벤트는 방수층(220)의 하층(즉, 포집 지지체(100)에 인접한 부분)으로 고이며, 방수층(220)의 하층에 고인 솔벤트(즉, 솔벤트)에 의해 나노 웹이 녹아 기공을 막아 방수층(220)의 하층 일부(즉, 포집 지지체(100)에 인접한 일부)에 무기공층(240)이 형성된다.The lower layer of the waterproof layer 220 is partially melted by the solvent contained in the spinning solution spun into the collection support 100 to form the inorganic hollow layer 240. That is, in the electrospinning, the solvent is radiated to the surface of the collection support 100 together with the polymer material. At this time, most of the solvent radiated to the collection support 100 is vaporized into the air, but some of the solvent is concentrated in the lower layer of the waterproof layer 220 (i.e., the portion adjacent to the collection support 100) The inorganic nanoparticle 240 is formed on a part of the lower layer of the waterproof layer 220 (that is, a part adjacent to the collecting support 100) by blocking the pores by melting the nanobeb by a solvent (i.e., solvent)

그에 따라, 도 3 및 도 4를 참조하면, 방수층(220)의 상층은 나노 웹 형태의 기공성층으로 형성된다.Accordingly, referring to FIGS. 3 and 4, the upper layer of the waterproof layer 220 is formed of a porous layer in the form of a nano-web.

이에 반해, 도 5 및 도 6을 참조하면, 방수층(220)의 하층은 솔벤트에 의해 녹아 기공이 제거된 무기공층(240)으로 형성된다.5 and 6, the lower layer of the waterproof layer 220 is formed of the inorganic porous layer 240, which is dissolved in the solvent to remove the pores.

한편, 도 7 및 도 8을 참조하면, 방사용액에 비드(bead)가 포함된 경우, 방수층(220)의 상층은 비드가 포함된 나노 웹 형태의 기공성층이 형성된다.7 and 8, when a bead is contained in the spinning liquid, a nano-web type porous layer containing beads is formed as an upper layer of the waterproof layer 220.

이상에서 본 발명에 따른 바람직한 실시예에 대해 설명하였으나, 다양한 형태로 변형이 가능하며, 본 기술분야에서 통상의 지식을 가진자라면 본 발명의 특허청구범위를 벗어남이 없이 다양한 변형예 및 수정예를 실시할 수 있을 것으로 이해된다.While the present invention has been described in connection with what is presently considered to be practical exemplary embodiments, it is to be understood that the invention is not limited to the disclosed embodiments, but many variations and modifications may be made without departing from the scope of the present invention. It will be understood that the invention may be practiced.

100: 포집 지지체 200: 방수 방음 시트
220: 방수층 240: 무기공층
100: collection support body 200: waterproof soundproof sheet
220: Waterproof layer 240: Inorganic layer

Claims (4)

포집 지지체를 준비하는 단계;
고분자 물질 및 솔벤트로 녹여 방사용액을 준비하는 단계;
상기 방사용액을 상기 포집 지지체의 일면에 전기방사하여 나노 웹 형태의 방수층을 형성하는 단계; 및
상기 방수층 중 상기 포집 지지체의 일면에 인접한 일부를 상기 솔벤트로 녹여 무기공층을 형성하는 단계를 포함하는 방수 통음 시트 제조 방법.
Preparing a collection support;
Preparing a spinning solution by dissolving the spinning solution with a polymer material and a solvent;
Forming a waterproof layer in the form of a nano-web by electrospinning the spinning solution on one side of the collection support; And
And dissolving a part of the waterproof layer adjacent to one surface of the collecting support body with the solvent to form an inorganic porous layer.
제1항에 있어서,
상기 포집 지지체를 준비하는 단계는,
필름형의 무기공성 부재로 형성되는 포집 지지체를 준비하는 단계를 포함하는 방수 통음 시트 제조 방법.
The method according to claim 1,
Wherein the step of preparing the collection support comprises:
A method for manufacturing a waterproofing soundproof sheet, comprising the steps of: preparing a collecting support body formed of a film-like inorganic porous member.
제1항에 있어서,
상기 포집 지지체를 준비하는 단계는,
이형지(release paper), 아트지(art papper), 코트지(coated paper), 광택지(glossy paper) 중에 적어도 하나인 포집 지지체를 준비하는 단계를 포함하는 방수 통음 시트 제조 방법.
The method according to claim 1,
Wherein the step of preparing the collection support comprises:
Preparing a collecting support which is at least one of release paper, art papper, coated paper, and glossy paper.
방사용액을 전기방사하여 나노웹 형태로 형성된 방수층을 포함하고,
상기 방수층은 하면이 상기 방사용액에 포함된 솔벤트에 의해 녹아 무기공층을 형성한 방수 통음 시트.
And a waterproof layer formed in the form of a nano-web by electrospinning the spinning solution,
Wherein the waterproof layer is formed of an inorganic filler by melting a lower surface of the solvent contained in the spinning solution.
KR1020160138507A 2016-10-24 2016-10-24 Waterproof sound-transmitting sheet and waterproof sound-transmitting sheet manufacturing method KR102290013B1 (en)