KR20170140119A - Sun protection film adjustable VLT and IRR - Google Patents
Sun protection film adjustable VLT and IRR Download PDFInfo
- Publication number
- KR20170140119A KR20170140119A KR1020170094683A KR20170094683A KR20170140119A KR 20170140119 A KR20170140119 A KR 20170140119A KR 1020170094683 A KR1020170094683 A KR 1020170094683A KR 20170094683 A KR20170094683 A KR 20170094683A KR 20170140119 A KR20170140119 A KR 20170140119A
- Authority
- KR
- South Korea
- Prior art keywords
- film
- irr
- functional
- vlt
- base film
- Prior art date
Abstract
Description
본 발명은 VLT와 IRR 조절이 가능한 태양광 차단필름에 관한 것으로, 시트의 표면에 기능성 패턴라인을 소정의 폭으로 형성하여 가시광선투과율(Visible Light Transimittance;VLT)과 적외선차단율(Infrared Rejection:IRR)을 조절할 수 있는 시트에 관한 것이다.The present invention relates to a solar light shielding film capable of adjusting VLT and IRR, and is characterized in that a functional pattern line is formed on a surface of a sheet to have a predetermined width and a visible light transmittance (VLT) and an infrared ray rejection (IRR) And more particularly,
태양 광선은 가시광 성분 뿐만 아니라 적외선과 같이 인체에 유해한 성분 및 적외선과 같이 밀폐된 공간을 승온시키는 열성분을 포함하고 있다. 태양 광선 중 이와 같은 불필요한 성분을 차단할 목적으로 건물의 외벽 유리나 차창 등에 태양광을 차단하는 필름이 사용된다.The sunlight includes not only visible light components, but also components harmful to the human body such as infrared rays and heat components that heat the enclosed space such as infrared rays. In order to block such unnecessary components of the sunlight, a film that blocks the sunlight is used on the outer wall glass of the building or the windshield.
예컨대, 적외선의 특정 영역의 빛을 흡수하는 물질을 사용하여 필름을 제조하고, 이를 유리면에 부착시켜 열에너지를 차단하는 방안이 제시되고 있다. 그러나, 이런 방식의 필름의 경우, 가시광선투과율(VLT) 투과율이 높으면 적외선차단율(IRR)이 낮아지고, 적외선차단율(IRR)이 높으면 가시광선 영역의 빛도 같이 차단되어 시안성의 문제가 발생하고, 대부분의 적외선 영역의 빛이 흡수되기 때문에 필름이나 유리의 온도가 증가하여 열차단 효율이 저하되는 등의 문제점이 있다.For example, a method of manufacturing a film using a material that absorbs light in a specific region of infrared rays and attaching the film to a glass surface to block heat energy has been proposed. However, in the case of such a film, a high visible ray transmittance (VLT) transmittance lowers an infrared ray blocking rate (IRR), and a high infrared ray blocking rate (IRR) There is a problem that the temperature of the film or the glass is increased due to the absorption of light in most of the infrared region and the efficiency of the heat shield is lowered.
이에 따라 태양광 차단필름은 가시광에 대한 투과 특성이 우수하고 적외선에 대한 차단 특성이 우수할 것이 요구된다.Accordingly, it is required that the solar light shielding film has excellent transmission characteristic for visible light and excellent shielding property against infrared rays.
본 발명이 해결하고자 하는 과제는 시트의 표면에 기능성 패턴라인을 소정의 폭으로 형성하여 가시광선투과율(VLT)과 적외선차단율(IRR)을 조절할 수 있는 시트를 제공하는 데 있다.SUMMARY OF THE INVENTION It is an object of the present invention to provide a sheet having a visible pattern transmittance (VLT) and an infrared cut-off rate (IRR) by forming a functional pattern line with a predetermined width on a surface of a sheet.
본 발명의 다른 해결과제는 시트의 표면에 가시광선투과율(VLT)이 조절된 재료와 적외선차단율(IRR)을 조절하는 재료를 이웃하게 형성하여 시트의 표면을 미끈하게 형성할 수 있는 VLT와 IRR 조절이 가능한 태양광 차단필름을 제공하는 데 있다.Another object of the present invention is to provide a sheet material having a visible light transmittance (VLT) controlled material and an IRR (visible light transmittance) controlled material adjacent to each other, so that the surface of the sheet can be smoothly formed, And to provide a solar-light-shielding film which can be used as such.
본 발명의 제1실시예에 따른 VLT와 IRR 조절이 가능한 태양광 차단필름은 합성수지 필름 등의 판형상의 제작된 기저필름(10)과, 기저필름(10)의 일표면에 소정의 폭으로 형성되는 기능성 재료의 기능성 패턴라인(20)으로 이루어진 것을 특징으로 한다.The sunlight blocking film capable of adjusting VLT and IRR according to the first embodiment of the present invention includes a
본 발명의 제2실시예에 따른 VLT와 IRR 조절이 가능한 태양광 차단필름은 합성수지 필름 등의 판형상의 제작된 기저필름(10)과, 기저필름(10)의 일표면에 형성되며 가시광선투과율(VLT)이 조절되는 투과성 재료의 투과성 코팅층(30)과, 투과성 코팅층(30)의 외측표면에 소정의 폭으로 형성되는 기능성 재료의 기능성 패턴라인(20)으로 이루어지는 것을 특징으로 한다.The sunlight blocking film capable of adjusting VLT and IRR according to the second embodiment of the present invention includes a
본 발명의 제3실시예에 따른 VLT와 IRR 조절이 가능한 태양광 차단필름은 판형상의 제작된 기저필름(10)과; 기저필름(10)의 일표면에 형성되며 적외선차단율(IRR)이 조절되는 기능성 재료의 투과성 코팅층(20-1)과; 투과성 코팅층(30)의 외측표면에 소정의 폭으로 형성되는 기능성 재료의 기능성 패턴라인(20)으로 이루어지는 것을 특징으로 한다.A third embodiment of the present invention provides a solar-light-shielding film capable of adjusting VLT and IRR, comprising: a
바람직하게, 기저필름(10)의 타표면에 접착재료의 접착층(40)이 형성되고, 접착층(40)의 외면에는 접착부재의 접착력을 보호하기 위한 보호필름(50)이 위치하는 것을 특징으로 한다.Preferably, an
바람직하게, 기능성 패턴라인(20)의 외면에 접착층(40-1)이 형성되고, 접착층(40-1)의 외면에 접착부재의 접착력을 보호하기 위한 보호필름(50)이 위치하는 것을 특징으로 한다.Preferably, the adhesive layer 40-1 is formed on the outer surface of the
바람직하게, 기능성 패턴라인(20) 부분은 30~50%의 가시광선투과율(VLT)을 갖고, 80% 이상의 적외선차단율(IRR)을 갖도록 형성되는 것을 특징으로 한다.Preferably, the portion of the
바람직하게, 기능성 패턴라인(20)을 형성하는 기능성 재료는 적외선흡수 재료, 도전성 재료, 방열 재료, 절연성 재료, 전자파 흡수재료 또는 이들을 혼합한 것 중의 어느 하나인 것을 특징으로 한다.Preferably, the functional material forming the
본 발명의 VLT와 IRR 조절이 가능한 태양광 차단필름은 기능성 패턴라인(20)의 개수 또는 폭을 조절하면 시트 전체의 적외선차단율을 간단하게 조절할 수 있기 때문에 간단하게 시트의 가시광선투과율도 함께 조절할 수 있는 장점이 있다.Since the infrared ray blocking rate of the entire sheet can be easily controlled by adjusting the number or width of the
또한, 기능성 패턴라인을 줄무늬 모양, 벌집모양, 사각형 모양 등의 다양한 형상 및 색상으로 형성할 수 있기 때문에 사용자가 원하는 미관을 갖도록 제작할 수 있는 장점이 있다.In addition, since the functional pattern line can be formed in various shapes and colors such as a stripe shape, a honeycomb shape, and a rectangular shape, it is possible to manufacture the functional pattern line to have a desired beauty.
또한, 외부에서 충격이 가해지는 경우에 충격이 패턴라인을 따라 이동하면서 흡수 및 분산되기 때문에 안전시트로도 사용할 수 있는 장점이 있다.Further, when the impact is applied from the outside, the impact is absorbed and dispersed while moving along the pattern line, so that it can be used as a safety sheet.
도 1은 본 발명의 제1실시예에 따른 VLT와 IRR 조절이 가능한 태양광 차단필름의 단면도.
도 2a 내지 도 2c는 본 발명에 따른 기능성 패턴라인의 예시도.
도 3은 본 발명의 제2실시예에 따른 VLT와 IRR 조절이 가능한 태양광 차단필름의 단면도.
도 4는 본 발명의 제3실시예에 따른 VLT와 IRR 조절이 가능한 태양광 차단필름의 단면도.
도 5는 본 발명의 제4실시예에 따른 VLT와 IRR 조절이 가능한 태양광 차단필름의 단면도.
도 6a 및 도 6b는 본 발명의 제5실시예에 따른 VLT와 IRR 조절이 가능한 태양광 차단필름의 단면도.
도 7은 도 6의 태양광 차단필름을 제작하기 위한 공정도.BRIEF DESCRIPTION OF THE DRAWINGS FIG. 1 is a sectional view of a sunlight blocking film capable of adjusting VLT and IRR according to a first embodiment of the present invention; FIG.
Figures 2A-2C illustrate examples of functional pattern lines according to the present invention.
3 is a sectional view of a sunlight blocking film capable of adjusting VLT and IRR according to a second embodiment of the present invention.
4 is a cross-sectional view of a sunlight blocking film capable of controlling VLT and IRR according to a third embodiment of the present invention.
5 is a sectional view of a sunlight blocking film capable of adjusting VLT and IRR according to a fourth embodiment of the present invention.
6A and 6B are sectional views of a sunlight blocking film capable of adjusting VLT and IRR according to a fifth embodiment of the present invention.
7 is a process chart for manufacturing the solar cell blocking film of Fig.
이하, 첨부된 도면을 참조하여 본 발명의 실시예에 대하여 자세히 설명한다. 이때, 각각의 실시예에서 동일한 구성은 동일한 도면부호를 부여하기로 한다.Hereinafter, embodiments of the present invention will be described in detail with reference to the accompanying drawings. Here, the same reference numerals are given to the same components in the respective embodiments.
이하, 본 발명에 따른 접착층(40)이 없는 시트의 개별 구성에 대하여 자세히 살펴본다.Hereinafter, the individual constitution of the sheet without the
도 1에 도시된 바와 같이, 본 발명의 제1실시예에 따른 VLT와 IRR 조절이 가능한 태양광 차단필름은 합성수지 필름 등의 판형상의 제작된 기저필름(10)과, 기저필름(10)의 일표면에 소정의 폭으로 형성되는 기능성 재료의 기능성 패턴라인(20), 기저필름(10)의 타표면에 접착재료의 접착층(40)이 형성되고, 접착층(40)의 외면에는 접착부재의 접착력을 보호하기 위한 보호필름(50)이 위치하는 것이 바람직하다. As shown in FIG. 1, the sunlight blocking film capable of adjusting VLT and IRR according to the first embodiment of the present invention includes a
이때, 기저필름(10)은 에스터계 고분자 필름, 스티렌계 고분자 필름, 카보네이트류 고분자 필름, 이미드류 고분자 필름, 설폰계 고분자 필름, 셀루로오스계 고분자 필름 등의 다양한 재료가 사용가능하다. At this time, various materials such as an ester-based polymer film, a styrene-based polymer film, a carbonate-based polymer film, an imide polymer film, a sulfone-based polymer film, and a cellulose-based polymer film can be used as the
그리고, 기능성 패턴라인(20) 부분은 5%~70%의 가시광선투과율(VLT)을 갖고, 30%~95% 이상의 적외선차단율(IRR)을 갖도록 형성되는 것이 바람직하지만, 기능성 패턴라인(20)의 폭은 시트 전체의 가시광선투과율과 적외선차단율에 따라 조절하게 된다. 기능성 패턴라인(20)을 형성하는 기능성 재료는 나노입자를 분산한 잉크로, MgO, TiO2, CeO, 벤조페논계 등의 적외선흡수 재료, 나노크기의 카본, 금속산화물, ATO(Antimony Tin Oxide), ITO(Indium Tin Oxide), Wo3, Ag-소수성 실리카 에어로겔 등의 적외선흡수 재료, 열차단재료, BaO2, PMMA(Poly Methyl Methacrylate), TiO2, ZnO2등의 확산재료, 나노크기의 그래핀, 그라파이트, 철, 카본변성, 알루미늄, 산화마그네슘 등의 도전성 재료, 방열 재료, 절연성 재료, 전자파 흡수재료에서 선택한 하나 이상의 재료인 것이 바람직하다. 특히, 전도성 물질을 사용하면 상변환 필름으로 사용할 수도 있고, 확산재료를 사용하면 영상 필름으로 사용할 수도 있다.The
이러한 제1실시예에 따른 시트는 기저필름(10)의 일표면에 형성되는 기능성 패턴라인(20)의 개수 또는 폭을 조절하면 시트 전체의 적외선차단율을 간단하게 조절할 수 있기 때문에 간단하게 시트의 가시광선투과율도 함께 조절할 수 있게 된다. 또한, 도 2a 내지 도 2c에 도시된 바와 같이, 패턴라인을 줄무늬 모양, 벌집모양, 사각형 모양 등의 다양한 형상 및 색상으로 형성할 수 있기 때문에 사용자가 원하는 미관을 갖도록 제작할 수 있다. 그리고, 외부에서 충격이 가해지는 경우에 충격이 패턴라인을 따라 이동하면서 흡수 및 분산되기 때문에 안전시트를 제작할 수 있게 된다.Since the infrared ray blocking rate of the entire sheet can be easily adjusted by adjusting the number or the width of the
도 3에 도시된 바와 같이, 본 발명의 제2실시예에 따른 VLT와 IRR 조절이 가능한 태양광 차단필름은 합성수지 필름 등의 판형상의 제작된 기저필름(10)과, 기저필름(10)의 일표면에 형성되며 가시광선투과율(VLT)이 조절되는 투과성 재료의 투과성 코팅층(30)과, 투과성 코팅층(30)의 외측표면에 소정의 폭으로 형성되는 기능성 재료의 기능성 패턴라인(20)으로 이루어지며, 기저필름(10)의 타표면에 접착층(40)이 형성되고, 접착층(40)의 외면에는 접착부재의 접착력을 보호하기 위한 보호필름(50)이 위치하는 것이 바람직하다. 이때, 투과성 코팅층(30)은 60~90%의 가시광선투과율을 갖도록 형성되는 것이 바람직하고, 기능성 패턴라인(20)의 30~50%의 가시광선투과율을 갖고, 80% 이상의 적외선차단율(IRR)을 갖도록 형성되는 것이 바람직하다.As shown in FIG. 3, the sunlight blocking film capable of adjusting VLT and IRR according to the second embodiment of the present invention includes a
이러한 제2실시예에 따른 시트는 기능성 패턴라인(20)의 개수 또는 폭을 조절하면 시트 전체의 가시광선 투과율과 적외선 차단율을 간단하게 조절할 수 있기 때문에 시트가 사용되는 장소에 따른 용도에 적합한 시트를 간단하게 제작할 수 있다. 또한, 패턴라인을 줄무늬 모양, 벌집모양, 사각형 모양 등의 다양한 형상으로 형성할 수 있기 때문에 사용자이 원하는 미관도 제작할 수 있다.Since the sheet according to the second embodiment can easily adjust the visible light transmittance and the infrared cut-off rate of the entire sheet by adjusting the number or width of the
도 4에 도시된실시와 같이, 본 발명의 제3실시예에 따른 VLT와 IRR 조절이 가능한 태양광 차단필름은 합성수지 필름 등의 판형상의 제작된 기저필름(10)과, 기저필름(10)의 일표면에 형성되며 적외선차단율(IRR)이 조절되는 기능성 재료의 기능성 코팅층(20-1)과, 기능성 코팅층(30)의 외측표면에 소정의 폭으로 형성되는 기능성 재료의 기능성 패턴라인(20)으로 이루어지며, 기저필름(10)의 타표면에 접착층(40)이 형성되고, 접착층(40)의 외면에는 접착부재의 접착력을 보호하기 위한 보호필름(50)이 위치하는 것이 바람직하다. 이때, 기능성 코팅층(20-1)과, 기능성 패턴라인(20)은 40~50%의 가시광선투과율을 갖고, 80% 이상의 적외선차단율(IRR)을 갖도록 형성되는 것이 바람직하다.4, the VLT and IRR controllable sunlight blocking film according to the third embodiment of the present invention includes a
이러한 제3실시예에 따른 시트는 기본적인 기능성 코팅층으로 1차적으로 필름에 기능성을 부여하고, 추가적으로 기능성 패턴라인을 형성하기 때문에 시트가 사용되는 장소에 따라서 추가적인 기능성을 부여한 시트를 간단하게 제작할 수 있다.The sheet according to the third embodiment can easily produce a sheet imparting additional functionality depending on the place where the sheet is used since the basic functional coating layer primarily imparts functionality to the film and further forms a functional pattern line.
도 5에 도시된 바와 같이, 본 발명의 제4실시예에 따른 VLT와 IRR 조절이 가능한 태양광 차단필름은 합성수지 필름 등의 판형상의 제작된 기저필름(10)과, 기저필름(10)의 일표면에 형성되며 가시광선투과율(VLT)이 조절되는 투과성 재료의 투과성 코팅층(30)과, 투과성 코팅층(30)의 외측표면에 소정의 폭으로 형성되는 기능성 재료의 기능성 패턴라인(20)으로 이루어지며, 기능성 패턴라인(20)의 외면에 접착층(40-1)이 형성되고, 접착층(40-1)의 외면에 접착부재의 접착력을 보호하기 위한 보호필름(50)이 위치하는 것이 바람직하다. As shown in FIG. 5, the solar light blocking film capable of adjusting the VLT and IRR according to the fourth embodiment of the present invention includes a
이러한 제4실시예에 의한 시트는 기능성 패턴라인(20) 사이에 공간이 형성되어 있어 있기 때문에 기능성 패턴라인(20)의 외면에 형성된 접착층(40-1)이 유리 등의 표면에 부착되면 표면과 투과성 코팅층(30) 사이에 진공층이 형성되어 단열효과를 높일 수 있게 된다.Since the sheet according to the fourth embodiment has a space formed between the
또한, 기능성 패턴라인(20)으로 방열물질을 사용하면 필름에서 흡수된 열이 패턴라인을 따라 외측으로 이동시키면서 외부로 배출시킬 수 있기 때문에 시트에서 흡수한 열이 유리 등의 표면을 통해서 실내 등으로 유입되는 것을 차단할 수 있게 된다. If the heat radiation material is used as the
도 6에 도시된 바와 같이, 본 발명의 제5실시예에 따른 VLT와 IRR 조절이 가능한 태양광 차단필름은 합성수지 필름 등의 판형상의 제작된 기저필름(10)과, 기저필름(10)의 일표면에 소정의 폭으로 형성되는 기능성 재료의 기능성 패턴라인(20)과, 기능성 패턴라인(20) 사이의 기저필름(10)의 표면에 기능성 패턴라인(20)과 동일한 높이로 형성되는 가시광선투과율(VLT)이 조절되는 투과성 재료의 투과성 코팅층(30)으로 이루어지며, 기저필름(10)의 내측표면에 접착층(40)이 형성되거나(도 6a 참조), 또는 기능성 패턴라인(20)과 투과성 코팅층(30)의 외면에 접착층(40)이 형성되고(도 6b 참조), 접착층(40)의 외면에 접착부재의 접착력을 보호하기 위한 보호필름(50)이 위치하는 것이 바람직하다. As shown in FIG. 6, the sunlight blocking film capable of adjusting the VLT and the IRR according to the fifth embodiment of the present invention includes a
이러한, 도 7에 도시된 바와 같이, 제5실시예에 따른 시트의 제조방법은 합성수지 필름 등의 판형상의 제작된 기저필름(10)을 준비하는 공정과, 기저필름(10)의 일표면에 소정의 폭으로 기능성 재료를 도포하여 기능성 코팅라인을 형성하는 공정과, 기능성 코팅라인의 상부면에 계면장력이 낮은 접착물질을 도포하여 결로형 박막을 형성하는 공정과, 기능성 패턴라인(20) 사이의 기저필름(10)의 표면에 투과성 재료를 기능성 코팅라인과 동일한 높이로 도포하여 투과성 코팅층(30)을 형성하는 공정으로 이루어진다. 이때, 계면장력이 낮은 접착물질은 실리콘계 또는 불소계의 접착물질인 것이 바람직하다. 7, the method for manufacturing a sheet according to the fifth embodiment includes the steps of preparing a
이와 같이 기능성 코팅라인을 형성한 후에 투과성 코팅층(30)을 도포하면 계면장력에 의하여 계면장력이 높은 투과성 코팅층(30)이 계면장력이 낮은 결로형 박막의 표면에 쌓이지 않으면서 기능성 패턴라인의 사이에만 채워지면서 기능성 코팅라인과 투과성 코팅층(30)이 동일한 높이로 형성할 수 있게 된다. When the
본 발명이 속하는 기술분야의 통상의 지식을 가진 자는 본 발명이 그 기술적 사상이나 필수적인 특징을 변경하지 않고서 다른 구체적인 형태로 실시될 수 있다는 것을 이해할 수 있을 것이다. 그러므로 이상에서 기술한 실시 예들은 모든 면에서 예시적인 것이며 한정적이 아닌 것으로 이해해야만 한다. 본 발명의 범위는 상기 상세한 설명보다는 후술하는 특허청구의 범위에 의하여 나타내어지며, 특허청구의 범위의 의미 및 범위 그리고 그 균등 개념으로부터 도출되는 모든 변경 또는 변형된 형태가 본 발명의 범위에 포함되는 것으로 해석되어야 한다.It will be understood by those skilled in the art that the present invention may be embodied in other specific forms without departing from the spirit or essential characteristics thereof. It is therefore to be understood that the above-described embodiments are illustrative in all aspects and not restrictive. The scope of the present invention is defined by the appended claims rather than the foregoing detailed description, and all changes or modifications derived from the meaning and scope of the claims and the equivalents thereof are included in the scope of the present invention Should be interpreted.
10 : 기저필름
20 : 기능성 패턴라인
20-1 : 기능성 코팅층
30 : 투과성 코팅층
40 : 접착층
50 : 보호필름10: base film
20: Functional pattern line
20-1: Functional Coating Layer
30: permeable coating layer
40: adhesive layer
50: Protective film
Claims (8)
기저필름(10)의 일표면에 소정의 폭으로 형성되는 기능성 재료의 기능성 패턴라인(20)으로 이루어진 것을 특징으로 하는 VLT와 IRR 조절이 가능한 태양광 차단필름.A base film 10 formed in a plate shape;
And a functional pattern line (20) of a functional material formed on a surface of the base film (10) with a predetermined width.
기저필름(10)의 일표면에 형성되며 가시광선투과율(VLT)이 조절되는 투과성 재료의 투과성 코팅층(30)과;
투과성 코팅층(30)의 외측표면에 소정의 폭으로 형성되는 기능성 재료의 기능성 패턴라인(20)으로 이루어지는 것을 특징으로 하는 VLT와 IRR 조절이 가능한 태양광 차단필름.A base film 10 formed in a plate shape;
A transmissive coating layer (30) of a transmissive material formed on a surface of the base film (10) and having a visible light transmittance (VLT) adjusted;
And a functional pattern line (20) of a functional material formed on an outer surface of the transparent coating layer (30) with a predetermined width.
기저필름(10)의 일표면에 형성되며 적외선차단율(IRR)이 조절되는 기능성 재료의 투과성 코팅층(20-1)과;
투과성 코팅층(20-1)의 외측표면에 소정의 폭으로 형성되는 기능성 재료의 기능성 패턴라인(20)으로 이루어지는 것을 특징으로 하는 VLT와 IRR 조절이 가능한 태양광 차단필름.A base film 10 formed in a plate shape;
A permeable coating layer 20-1 of a functional material formed on one surface of the base film 10 and having an infrared ray blocking rate (IRR) controlled;
And a functional pattern line (20) of a functional material formed on the outer surface of the transparent coating layer (20-1) with a predetermined width.