KR20170136424A - Printing method - Google Patents

Printing method Download PDF

Info

Publication number
KR20170136424A
KR20170136424A KR1020170058469A KR20170058469A KR20170136424A KR 20170136424 A KR20170136424 A KR 20170136424A KR 1020170058469 A KR1020170058469 A KR 1020170058469A KR 20170058469 A KR20170058469 A KR 20170058469A KR 20170136424 A KR20170136424 A KR 20170136424A
Authority
KR
South Korea
Prior art keywords
gold
powder
silver
printing
silver powder
Prior art date
Application number
KR1020170058469A
Other languages
Korean (ko)
Inventor
윤병식
Original Assignee
윤병식
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 윤병식 filed Critical 윤병식
Publication of KR20170136424A publication Critical patent/KR20170136424A/en

Abstract

The present invention relates to a gold powder and silver powder printing method for three-dimensionally printing gold powder and silver powder for crafts and curing the same by ultraviolet (UV) rays, capable of applying a distinctive gloss of a gold color by giving an effect of painting and coating gold powder over the gold color when expressing a specific pattern or letter in gold on a printed matter such as an edge pattern of a certificate of merit, a business card, a wedding invitation, and the like, enabling aesthetic color expression since the amount of light reflection greatly changes in accordance with the angle due to a high refractive index of light, providing a three-dimensional effect as if it were carved by forming an embossed printed layer having strong hiding power, and requiring no separate drying time. The method comprises: (a) a step of manufacturing a gold powder and silver powder mixture by mixing gold powder and silver powder for crafts with an etching matte UV emulsion; (b) a step of mixing a curing agent with the gold powder and silver powder mixture; (c) a step of forming a thick film by applying a sensitizing solution to the surface of a screen; (d) a step of compressing a film on which a pattern is printed on the screen and exposing the same; (e) a step of removing the film and washing the screen; (f) a step of placing the screen on a raw sheet on which gold powder and silver powder are to be printed, and applying the gold powder and silver powder mixture; and (g) a step of curing the gold powder and silver powder mixture by UV rays.

Description

공예용 금분, 은분을 입체돋움으로 인쇄후 UV자외선에 경화시키는 금분, 은분 인쇄방법{PRINTING METHOD}{PRINTING METHOD} A method of printing a gold powder or a silver powder which is cured by ultraviolet rays after printing with gold powder,

본 발명은 공예용 금분, 은분을 입체돋움으로 인쇄후 UV자외선에 경화시키는 금분, 은분 인쇄방법에 관한 것으로, 더욱 상세하게는 금분과 은분을 전체 비율의 10% 정도로 포함시키면서 까다로운 인쇄 여건을 조합이 되는 금 반짝이, 은 반짝이(금박, 은박을 찍은 폴리에스터 재질을 잘게 부순 가루) 네일 아트로 많이 쓰이는 재질을 50% 정도로 포함을 시켜서 어려운 인쇄의 요건을 충족시키면서 또한 금색, 은색이 금박 은박 보다 더 유리조각처럼 빛에 반짝이며 반응하며, 감광액을 두꺼운 후막의 빠른 건조가 가능한 아조픽스(감광 유제) 2200번을 감광액으로 사용하여 별도의 건조시간이 필요가 없는 UV자외선에 경화되도록 하는 공예용 금분, 은분을 입체돋움으로 인쇄후 UV자외선에 경화시키는 금분, 은분 인쇄방법에 관한 것이다.The present invention relates to a method for printing gold powder and silver powder which is cured in UV ultraviolet rays after printing with gold powder and silver powder for artificial crafts. More specifically, the present invention relates to a method for printing gold powder and silver powder, (Gold foil, silver foil, polished polyester powder). It contains more than 50% of nail art materials, which makes it possible to meet the requirements of difficult printing and also more gold and silver than gold foil and silver foil. Azo PIX (sensitized emulsion), which is able to dry quickly with a thick thick film, is used as a sensitizing solution to cure into UV ultraviolet ray which does not require a separate drying time. And a method of printing silver halide, which is cured in UV ultraviolet rays.

금 색채는 최고의 가치관과 아름다움의 대명사로 그 광택은 포장재의 호화스러움을 나타낸다.Gold color is synonymous with the best values and beauty, and the gloss represents the luxuriousness of the packaging material.

그러나 인쇄로서의 금색은 금박에 의해 반짝이는 정도와 옵셀인쇄는 고급스러움을 구사하는 은폐력을 지닌 별색의 한 색상으로 표현되어 왔고, 그 후가공으로는 요철 동판을 이용해 금색 인쇄나 금박을 형압으로 돋게 만들어 입체를 표현하거나 금색 고유의 반짝거림과 빛 굴절을 원할 때 인쇄가 마르기 전에 금가루를 칠하고 남은 금가루 잔여물을 집진기를 통해 제거하는 방법 등이 현재의 금 인쇄 종류이며, 특히 현재에는 디지털 골드 인쇄방법이 개발되었으나 이 또한 초고가의 장비와 비싼 재료비 또한 수입품으로 이루어지고 그 효과도 종전의 금색 인쇄와 크게 다르지않은 문제점이 있었다.However, the gold color for printing has been expressed by the color of spot color with the hysteresis that has the degree of glitter by gold leaf and the hysteresis that the observer print has the luxury, and after that, it uses irregular copper plate to make golden print or gold leaf, Or when the user desires gold's unique shine and refraction of gold, the method is to apply the gold dust before the print is dried and to remove the remaining gold dust through the dust collector. However, there is also a problem that the high-priced equipment and the expensive material cost are also made into imports, and the effect is not so different from the previous gold printing.

본 발명의 배경이 되는 기술로는 특허등록 제0321117호 "금박인쇄물 및 그 제조방법"(특허문헌 1)이 있다. 상기 배경기술에서는 '금박을 바탕으로 한 금박인쇄물에 있어서, 한쪽 면은 인쇄층이 형성된 투명한 베이스필름과; 상기 베이스필름의 인쇄층이 형성된 면의 다른 쪽 면에 접착되는 금박층을 구비하는 것을 특징으로 하는 금박인쇄물'을 제안한다.As a background of the present invention, there is a patent registration No. 0321117 entitled " a gold leaf printed matter and a method for producing the same "(Patent Document 1). In the background art described above, a gold foil-based gold foil print comprising: a transparent base film having a printing layer on one side; And a gold foil layer adhered to the other surface of the surface of the base film on which the print layer is formed.

그러나 상기 배경기술은 제조방법이 복잡하고 건조시간이 오래걸리는 등의 문제점이 있었다.However, the background art has a problem in that the manufacturing method is complicated and the drying time is long.

특허등록 제0321117호 "금박인쇄물 및 그 제조방법"Patent Registration No. 0321117 "Gold-plated printed matter and method for producing the same"

지금까지의 인쇄에서 금색, 은색 인쇄는 기름으로 형성된 금색, 은색 잉크에 안료를 섞어서 색감 농도를 맞추고 4원색에 후가공 별색으로 약간의 은폐력을 지니면서 고급스럽게 두각되는 용도로 제조되나 그 비용은 배가될 뿐만 아니라 효과가 미비하고 박필름을 이용한 금박이나 금분 인쇄 또한 크나큰 경제적 부담과 작업 공정이 느리고 길어서 제작과정이 까다롭고 효과 또한 평면 인쇄이고 색감의 한계가 있으며, 최고의 후가공인 형압은 두드러지게 효과를 주나 경제적인 면뿐만 아니라 작업공정에 큰 부담이 주어졌다. 상기의 금, 은 인쇄의 배경에서는 부담스런 경제력이 따르고 제조방법이 복잡하고 여러 단계를 거쳐야 하는 등의 문제점이 있었다.The gold and silver prints made up to now have been made from gold and silver inks which are made of oil and are mixed with pigments in order to adjust the color density, and are made of four primary colors with a slight hiding power in post-production colors, In addition, it is difficult to produce gold foil or gold foil using foil film. Also, it has a great economic burden, long work process is slow and long time, and it is difficult to produce, and the effect is also flat print and color limitation. The best finishing pressure is remarkably effective Not only economical but also a great burden on the work process. In the background of the above-mentioned gold and silver printing, there is a problem that the economical power is burdensome, the manufacturing method is complicated, and various steps are required.

본 발명은 상기와 같은 문제점을 해결하기 위한 것으로, 금분과 은분을 전체 비율의 10% 정도로 포함시키면서 까다로운 인쇄 여건을 조합이 되는 금 반짝이, 은 반짝이(금박, 은박을 찍은 폴리에스터 재질을 잘게 부순 가루) 네일 아트로 많이 쓰이는 재질을 50% 정도로 포함을 시켜서 어려운 인쇄의 요건을 충족시키면서 또한 금색, 은색이 금박 은박 보다 더 유리조각처럼 빛에 반짝이며 반응하며, 감광액을 두꺼운 후막의 빠른 건조가 가능한 아조픽스(감광 유제) 2200번을 감광액으로 사용하여 별도의 건조시간이 필요가 없는 UV자외선에 경화되도록 하는 공예용 금분, 은분을 입체돋움으로 인쇄후 UV자외선에 경화시키는 공예용 금분, 은분을 입체돋움으로 인쇄후 UV자외선에 경화시키는 금분, 은분 인쇄방법을 제공하는데 그 목적이 있다.Disclosure of the Invention The present invention has been made to solve the above-mentioned problems, and it is an object of the present invention to provide an ink jet printer which comprises gold and silver in a ratio of about 10% ) It contains 50% of materials used in nail art to meet the requirements of difficult printing, while gold and silver react more to the light like glass sculpture than gold leaf and silver, Fixed (emulsion) 2200 is used as a sensitizing solution, so it is not necessary to dry time separately. Crafts gold, which is cured by ultraviolet rays. Crafts gold and silver that are cured by ultraviolet rays after curing by silver printing. And then curing the resultant in UV ultraviolet light.

본 발명은 (a) 공예용 금분과 은분을 에칭 무광 UV 유제를 혼합시켜 금분, 은분 혼합물을 제조하는 단계; (b) 금분, 은분 혼합물에 경화제를 혼합하는 단계; (c) 스크린의 표면에 감광액을 일정 두께로 도포하되, 1차로 스크린판 후막을 3번 도포 스크린판 상막을 3번 도포 후 건조하고, 2차로 스크린판 후막을 3번 도포 스크린판 상막을 2~3번 도포하고 건조시켜 후막을 형성하는 단계; (d) 문양이 인쇄된 필름을 스크린에 압착한 후 노광하는 단계; (e) 필름을 제거하고 스크린을 세척하는 단계; (f) 금분, 은분이 인쇄될 원지에 스크린을 위치시키고, 금분, 은분 혼합물을 도포하는 단계; (g) 금분, 은분 혼합물을 UV 자외선으로 경화하는 단계;를 포함하여 이루어지는 것을 특징으로 하는 공예용 금분, 은분을 입체돋움으로 인쇄후 UV자외선에 경화시키는 금분, 은분 인쇄방법을 제공하고자 한다.The present invention relates to (a) a process for producing a gold and silver mixture by mixing an artificial quartz UV emulsion with gold powder and silver powder; (b) mixing a curing agent in the gold and silver mixture; (c) Applying the sensitizing solution to the surface of the screen to a predetermined thickness, applying three times of the screen plate thick film three times, applying the three times of the screen plate thick film, and then applying the three times of the screen plate thick film, 3 times and drying to form a thick film; (d) squeezing the pattern printed on the screen and exposing it; (e) removing the film and washing the screen; (f) placing the screen on a substrate to be printed with gold, silver, and applying a mixture of gold and silver; and (g) curing the mixture of gold and silver by UV ultraviolet rays. The present invention also provides a method for printing gold or silver, which comprises curing the gold powder and the silver powder by applying ultraviolet rays after UV printing.

또한, 혼합물은 금 반짝이, 은 반짝이(금박, 은박을 찍은 폴리에스터 재질을 잘게 부순 가루인 금 반짝이, 은 반짝이와 천연 광물로 이루어진 무기 안료인 금분, 은분을 혼합하는 것을 특징으로 하는 공예용 금분, 은분을 입체돋움으로 인쇄후 UV자외선에 경화시키는 금분, 은분 인쇄방법을 제공하고자 한다.The mixture is also characterized in that the mixture is a mixture of gold, silver, which is an inorganic pigment consisting of gold glitter, silver glitter (gold foil, gold-glitter which is a finely crushed polyester material with silver foil, silver glitter and natural minerals, The present invention is to provide a method of printing a silver powder or a silver powder which is cured in UV ultraviolet rays after printing with silver powder.

또한, 감광액은 두꺼운 후막의 빠른 건조가 가능한 아조픽스(감광 유제) 2200번을 감광액으로 사용하는 것을 특징으로 하는 UV공예용 금분, 은분을 입체돋움으로 인쇄후 UV자외선에 경화시키는 금분, 은분 인쇄방법을 제공하고자 한다.In addition, the sensitizing solution is a UV curable gold powder which is used as a sensitizing solution by using AzoPix (emulsion sensitizer) 2200 which is capable of rapid drying of a thick thick film, a gold powder which is cured in UV ultraviolet after printing with silver powder, .

또한, 스크린은 #150 목인 것을 특징으로 하는 UV공예용 금분, 은분을 입체돋움으로 인쇄후 UV자외선에 경화시키는 금분, 은분 인쇄방법을 제공하고자 한다.Further, the present invention provides a gold powder for UV craft, which is characterized by a screen of # 150, and a method for printing gold powder or silver powder which is cured by ultraviolet rays after printing with silver powder.

또한, 감광액을 0.2~0.4mm 두께로 도포하는 것을 특징으로 하는 공예용 금분, 은분을 입체돋움으로 인쇄후 UV자외선에 경화시키는 금분, 은분 인쇄방법을 제공하고자 한다.Also, it is intended to provide a gold powder and a silver powder printing method in which a photosensitive liquid is applied in a thickness of 0.2 to 0.4 mm, which is cured in UV ultraviolet rays after printing with silver powder for artificial silver powder.

본 발명의 공예용 금분, 은분을 입체돋움으로 인쇄후 UV자외선에 경화시키는 금분, 은분 인쇄방법은 금분과 은분을 전체 비율의 10% 정도로 포함시키면서 까다로운 인쇄 여건을 조합이 되는 금 반짝이, 은 반짝이(금박, 은박을 찍은 폴리에스터 재질을 잘게 부순 가루) 네일 아트로 많이 쓰이는 재질을 50% 정도로 포함을 시켜서 어려운 인쇄의 요건을 충족시키면서 또한 금색, 은색이 금박 은박 보다 더 유리조각처럼 빛에 반짝이며 반응하며, 감광액을 두꺼운 후막의 빠른 건조가 가능한 아조픽스(감광 유제) 2200번을 감광액으로 사용하여 별도의 건조시간이 필요가 없는 UV자외선에 경화되도록 하는 공예용 금분, 은분을 입체돋움으로 인쇄후 UV자외선에 경화시키는 매우 유용한 효과가 있다.The gold and silver printing methods of the invention for curing the artificial gold or silver powder by curing and then curing the powder by ultraviolet rays include 10% of the whole ratio of gold and silver, and the combination of gold glitter and silver glitter Gold foil, and silver foil) is used as a nail art material, it is possible to meet the requirements of difficult printing. Moreover, the silver and gold are shining more like glass fragments than gold foil And is used as a sensitizing solution by using AzoPix (emulsion sensitized) 2200, which is capable of fast drying of a thick thick film as a sensitizing solution, to be cured in UV ultraviolet ray which does not require a separate drying time, There is a very useful effect of curing in ultraviolet rays.

도 1은 본 발명의 공예용 금분, 은분을 입체돋움으로 인쇄후 UV자외선에 경화시키는 금분, 은분 인쇄방법의 순서도.
도 2는 본 발명의 공예용 금분, 은분을 입체돋움으로 인쇄후 UV자외선에 경화시키는 금분, 은분 인쇄방법을 개략적으로 도시한 측단면도.
도 3은 본 발명의 인쇄방법으로 인쇄한 실물사진.BRIEF DESCRIPTION OF THE DRAWINGS FIG. 1 is a flow chart of a method for printing gold powder and silver powder, which is a method for curing a gold powder and silver powder for artificial craft of the present invention,
Fig. 2 is a side cross-sectional view schematically showing a method of printing a gold powder or a silver powder for printing a silver powder for artificial crafts of the present invention as a solid, followed by curing in UV ultraviolet rays.
Fig. 3 is a photograph of an actual print printed by the printing method of the present invention. Fig.

아래에서 본 발명은 첨부된 도면에 제시된 실시 예를 참조하여 상세하게 설명이 되지만 제시된 실시 예는 본 발명의 명확한 이해를 위한 예시적인 것으로 본 발명은 이에 제한되지 않는다. DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS The present invention will be described in detail below with reference to the embodiments shown in the accompanying drawings, but the present invention is not limited thereto.

이하 바람직한 실시예에 따라 본 발명의 기술적 구성을 상세히 설명하면 다음과 같다.Hereinafter, the technical structure of the present invention will be described in detail with reference to the preferred embodiments.

도 1은 본 발명의 공예용 금분, 은분을 입체돋움으로 인쇄후 UV자외선에 경화시키는 금분, 은분 인쇄방법의 순서도이고, 도 2는 본 발명의 공예용 금분, 은분을 입체돋움으로 인쇄후 UV자외선에 경화시키는 금분, 은분 인쇄방법을 개략적으로 도시한 측단면도이다.FIG. 1 is a flow chart of a method of printing a gold powder or a silver powder for curing the artificial gold powder or silver powder of the present invention with a three-dimensional appearance and then curing the powder into ultraviolet rays. FIG. 2 is a cross- Fig. 2 is a side cross-sectional view schematically showing a method for printing silver powder and silver powder to be cured.

본 발명의 공예용 금분, 은분을 입체돋움으로 인쇄 후 UV자외선에 경화시키는 금분, 은분 인쇄방법은 도 1에서와 같이, (a) 공예용 금분과 은분을 에칭 무광 UV유제를 혼합시켜 금분, 은분 혼합물(20)을 제조하는 단계; (b) 금분, 은분 혼합물에 경화제를 혼합하는 단계; (c) 스크린의 표면에 감광액을 일정 두께로 도포하되, 1차로 스크린판 후막을 3번 도포 스크린판 상막을 3번 도포 후 건조하고, 2차로 스크린판 후막을 3번 도포 스크린판 상막을 2~3번 도포하고 건조시켜 후막을 형성하는 단계; (d) 문양이 인쇄된 필름을 스크린(11)에 압착한 후 노광하는 단계; (e) 필름을 제거하고 스크린(11)을 세척하는 단계; (f) 금분, 은분이 인쇄될 원지(30)에 스크린(11)을 위치시키고, 금분, 은분 혼합물(20)을 도포하는 단계; (g) 금분, 은분 혼합물(20)을 UV 자외선으로 경화하는 단계;를 포함하여 이루어지는 것을 특징으로 한다.As shown in FIG. 1, the method of printing gold or silver in which the silver powder for artificial crafts of the present invention is printed with a three-dimensional appearance and then cured in UV ultraviolet rays, comprises the steps of: (a) Preparing a mixture (20); (b) mixing a curing agent in the gold and silver mixture; (c) Applying the sensitizing solution to the surface of the screen to a predetermined thickness, applying three times of the screen plate thick film three times, applying the three times of the screen plate thick film, and then applying the three times of the screen plate thick film, 3 times and drying to form a thick film; (d) squeezing the pattern printed on the screen (11) and exposing it; (e) removing the film and washing the screen 11; (f) placing the screen (11) on a paper (30) to be printed with gold and silver, and applying a gold / silver mixture (20); (g) curing the gold and silver mixture 20 by UV ultraviolet light.

먼저, 금분, 은분 혼합물(20)을 제조한다(a).First, a gold and silver mixture 20 is prepared (a).

금분, 은분 혼합물(20)은 칠용 금분 및 은분과 에칭 무광 UV 유제를 혼합시켜 제조한다.A mixture of gold and silver (20) is prepared by mixing an electroless UV emulsion with a gold powder and a silver powder.

금분 및 은분과 UV유제는 다양한 비율로 혼합될 수 있으나 3:5의 비율로 혼합하는 것이 바람직하다.The gold and silver and UV emulsions can be mixed in various ratios, but it is preferred to mix them in a ratio of 3: 5.

이후, 금분, 은분 혼합물(20)에 경화제를 혼합한다(b).Thereafter, the curing agent is mixed with the gold and silver mixture 20 (b).

금분, 은분 혼합물(20)은 경화시간의 조절을 위해 다양한 공지의 경화제를 적당량 첨가하도록 할 수 있으며, 경화제 이외에도 기타 첨가제를 추가 혼합할 수도 있다. 예를 들면 경화제를 혼합 기준치의 20% 수준으로 혼합하고 동유 등의 건조를 지연하는 지연제로 점도를 조절할 수 있다.In order to control the curing time, a mixture of various known curing agents may be appropriately added to the mixture of gold, silver and silver, and other additives may be added in addition to the curing agent. For example, the hardener may be mixed at a level of 20% of the mixing standard and the viscosity may be controlled with a delaying agent to delay drying of the oil.

*금분, 은분에는 UV에칭유제를 4:6 비율로 혼합시켜 자외선 경화용 잉크를 만들고 건조성을 위해 경화제를 혼합 기준치의 20% 수준으로 혼합하면 자외선 경화 후에 더욱 견고하게 굳는 UV자외선 경화잉크가 제공될 수 있다.* UV etch emulsion is mixed with gold etchant and silver etchant at 4: 6 ratio to prepare ultraviolet curing ink. When the curing agent is mixed to the level of 20% of the mixing reference value for drying, UV ultraviolet curing ink hardening after ultraviolet curing is provided .

혼합물 중 에칭 유제는 자외선 경화 후 무광으로 부식효과가 나타나므로 금, 은의 고유 색감을 유리하게 표현하는데 적합하며 유제 자체의 점도가 높아 입체 돋움 인쇄가 더욱 또렷이 조각처럼 형성되어 나타나게 된다.Since the etchant in the mixture has a matting effect after being cured by ultraviolet rays, it is suitable for expressing the intrinsic color of gold and silver, and the viscosity of the emulsion itself is high, so that stereoscopic printing is formed more clearly as a piece.

이후, 스크린(11)의 표면에 감광액을 도포한다(c).Thereafter, the photosensitive liquid is applied to the surface of the screen 11 (c).

실크 스크린 인쇄방법은 최초의 기술 발명이 오래전 외국에서 발명되어 온 기술로서 기본적인 기술로 작업을 해도 인쇄면의 요철이 형성된다. 그 이유는 스크린판의 견장된 실크천과 칠해진 감광액의 약간의 높이가 곧 인쇄면의 요철을 형성하게 된다.The silk screen printing method is a technology that has been invented in a foreign country for a long time before the first technical invention. The reason is that a slight height of the strained silk cloth of the screen plate and the painted liquid of the screen plate soon forms the unevenness of the printed surface.

본 특허의 돋움인쇄의 높이를 조절하는 기술적인 요건은 두꺼운 후막(13b)의 빠른 건조가 가능한 아조픽스(감광 유제) 2200번을 감광액으로 사용하여 1차로 스크린판 후막(13b)을 3번 도포 스크린판 상막(13a)을 3번 도포후 건조한 후, 2차로 스크린판 후막(13b)을 3번 도포 스크린판 상막(13a)을 2~3번(감광액의 농도차이에 따라) 도포하고 건조시키면, 후막(13b)이 형성되고 이 후막(13b)은 인쇄할 형상이 새겨진 필림을 현상기로 현상 후 물로 세척하여 건조시키면 인쇄용 후막(13b)이 만들어진다.The technical requirement to control the height of the print of the patent in this patent is that firstly the screen thick film 13b is applied to the application surface 3 by using the azo fix (emulsion) 2200, which is capable of quick drying of the thick thick film 13b, After applying the plate membrane 13a three times and drying it and then applying the second screen plate thick film 13b to the third screen plate film 13a two or three times (depending on the difference in concentration of the photosensitive liquid) and drying the plate membrane 13a, The thick film 13b is formed by printing a film having a shape to be printed on it with a developing device, washing it with water, and drying the film to form a printing thick film 13b.

아조픽스(AZO-FIX) No.2200는 후막용 감광유제로, 판의 제편성이 아주 우수하고 섬세한 판을 만들 때 사용된다.AZO-FIX No.2200 is a photosensitive emulsion for thick film, which is used for making delicate plates with very good knitting.

이 후막(13b)으로 인쇄시 약 0.2~0.4mm정도의 돋움인쇄(요철)가 형성된다.When the thick film 13b is printed, a stripe print (irregularity) of about 0.2 to 0.4 mm is formed.

참고로 표준 점자의 높이가 0.65~07.mm로 비추어 볼때 그 돋움인쇄의 높이가 가늠된다.For reference, the height of the standard braille is 0.65 ~ 07.mm, and the height of the imprint is estimated.

실크 스크린 인쇄는 평면 옵셀 인쇄와 달리 유제ㅡ 용제, 경화제, 희석제 등의 많은 조합되어 있지 않은 재료들로 인쇄 작업의 여건이 갖춰지고 인쇄용지 또한 스크린판 밑에 맞추고 유제 도포를 하여 인쇄가 가능하면 종이, PP지, 플라스틱, 가죽, 주사기, 도전성 인쇄 등의 모든 대상이 인쇄를 할 수 있는 대상으로 포함된다. Silk screen printing, unlike flat-type observer printing, has many printing materials such as solvents, hardeners, diluents, etc., and the printing paper is also placed under the screen plate. When printing is possible by applying emulsion, PP paper, plastics, leather, syringes, conductive printing, etc. are all included in the printable object.

본 특허는 그 중 특정 부분인 금분, 은분에 국한된 인쇄법을 제공한다.This patent provides a printing method limited to gold and silver, which is a specific part of the patent.

지금껏 실크 스크린 인쇄의 금색, 은색 인쇄는 찍은 후 1장씩 자연건조를 진행하였으며, 그 색상 또한 금박이나 은박 같은 반짝임이 없이 옵셀인쇄처럼 비슷한 색상을 띄며 특히 은색은 복권의 스크레치 인쇄용으로 많이 사용되었으나 그 또한 자연건조로 이루어졌다.The silver and silver prints of silk screen printing have been printed one by one and dried naturally one by one. The color of the silk screen printing has been similar to that of observer printing without gilding or gilding, and especially silver has been widely used for scratch printing of lottery tickets. Natural drying.

본 특허의 금분, 은분은 무기 안료에 속하는 천연 광물로 이루어져 있는 안료로써 그 자체 성분의 인쇄시 단점은 3~4개월 경과 후에는 색상이 약간 검은색으로 변하며 인쇄후 자연 건조조차 어려우며, UV자외선 열에 약하여 겉부분이 큰 기포가 생기며 열에 타는 경향이 있고, 경화제, 용제 등을 사용시 색상이 변해 버리는 어려운 인쇄여건이 따른다.The disadvantage of the printing of its own components is that after 3 ~ 4 months, the color becomes slightly black. It is hard to even natural drying after printing, It has a tendency to burn on the surface due to weak bubbles on the outer surface and hard printing conditions in which the color is changed when a hardener or a solvent is used.

스크린(11)은 크기가 크면 금분, 은분 혼합물이 뭉치는 등의 부작용이 나타나며 너무 작으면 금분이 통과하지 못하기 때문에, 금분, 은분 혼합물(20)의 금분이 통과할 수 있도록 #150 목의 스크린(11)을 준비하여, 스크린의 표면에 감광액을 일정 두께로 도포하되, 상막(13a), 후막(13b)의 두께의 비율을 바람직하게는 1:3 정도로 도포하여 후막(13b)을 형성하도록 한다.If the size of the screen 11 is large, side effects such as accumulation of a mixture of gold and silver appear, and if it is too small, the gold can not pass through. Thus, A thick film 13b is formed by applying a photosensitive liquid to a surface of a screen with a predetermined thickness and applying a ratio of the thickness of the upper film 13a and the thick film 13b to a value of preferably about 1: .

이후, 문양이 인쇄된 필름을 스크린(11)에 압착한 후 노광하도록 한다(d).Thereafter, the printed film is pressed on the screen 11 and exposed (d).

감광액이 도포된 스크린(11)은 건조대에서 대략 30분에서 1시간 정도 건조시킨 후 스크린(11)에 필름을 압착하는 것이 바람직하며, 필름을 압착시킨 상태에서 스크린(11)을 노광시킨다.The screen 11 to which the photosensitive liquid is applied is preferably dried on the drying stand for about 30 minutes to 1 hour, and then the film is pressed onto the screen 11, and the screen 11 is exposed in a compressed state.

이와 같이 감광액을 노광시키면, 필름이 압착되지 않은 부분은 태양광에 노출되어 경화되고, 필름이 압착된 부분은 미경화상태로 남게 된다.When the photosensitive liquid is exposed in this manner, the portion to which the film is not pressed is exposed to sunlight to be cured, and the portion to which the film is pressed remains in an uncured state.

이후, 필름을 제거하고 스크린(11)을 세척하도록 한다(e).Thereafter, the film is removed and the screen 11 is washed (e).

필름을 제거하고 스크린(11)을 세척하게 되면 감광액이 경화된 부분은 남아 있게 되고, 미경화된 부분은 씻겨 나가 도 2에서와 같이 된다.When the film is removed and the screen 11 is cleaned, the cured portion of the photosensitive liquid remains, and the uncured portions are washed away as shown in Fig.

스크린(11)의 세척은 일반 용수로 하는 것이 바람직하다.It is preferable that the screen 11 is cleaned by ordinary water.

이후, 금분, 은분이 인쇄될 원지(30)에 스크린(11)을 위치시키고, 금분, 은분 혼합물(20)을 도포하도록 한다(f).Thereafter, the screen 11 is placed on the raw paper 30 on which the gold powder and silver powder are to be printed, and the gold powder and the silver powder mixture 20 are applied (FIG.

금분, 은분 혼합물(20)은 스크린(11)의 경화된 감광액을 통과하지 못하여 감광액이 씻겨나간 부분으로만 통과하여 원지(30)에 인쇄가 되게 된다.The mixture of gold and silver powder 20 does not pass through the cured photosensitive liquid of the screen 11 and passes through only the washed portion of the photosensitive liquid to be printed on the base paper 30.

마지막으로, 금분, 은분 혼합물(20)을 UV자외선으로 경화하도록 한다(g).Finally, the gold and silver mixture 20 is cured by UV ultraviolet light (g).

또한, 고열이 동반되는 UV자외선 경화시에 써멀유리를 활용하거나, 환충장치등을 이용한 환풍효과로 최대한 열 접촉을 막아주어 필름조각으로 형성된 가루들이 타서 금, 은의 고유색상이 변하는 것을 막아줄 수 있다.In addition, when thermal UV is cured with high heat, thermal glass can be used or ventilation effect can be prevented by the effect of ventilation, so that the powder formed by the film pieces can be prevented from changing the inherent color of gold or silver .

상기와 같은 본 발명의 공예용 금분, 은분을 입체돋움으로 인쇄후 UV자외선에 경화시키는 금분, 은분 인쇄방법은 UV자외선에 의하여 경화되도록 하여 별도의 건조시간이 필요 없으면서도 은폐력이 강한 돋움 인쇄층이 형성되도록 하여 조각된 것과 같은 입체감을 주도록 하는 효과가 있으며, 특히 상장 테 문양, 명함, 청첩장 등의 인쇄물에 특정 문양이나 글씨를 금색 표현할 때에 금색을 금가루를 덧칠해 바른 효과를 주어 금색 특유의 광택을 줄 수 있으며, 가루 한알 한알이 거울조각처럼 빛의 굴절율이 높아 각도에 따라 불규칙적으로 반사되는 양이 크게 변하여 미려한 색표현이 가능하여 금색, 은색 특유의 보석류 색상이 전달되고 대량 생산이 가능하여 품질, 단가, 납기를 한 공정으로 충족시킬 수 있어 경제성이 높은 효과가 있고, 인쇄 용지의 구분이 없고 PP지나 라미네이팅, UV코팅 등에도 더욱 강한 금 색상을 표현할 수 있는 매우 유용한 효과가 있다.The method of printing the gold powder or silver powder for curing the artificial gold powder or silver powder of the present invention as a three-dimensional appearance and then curing the powder into ultraviolet rays is cured by UV ultraviolet rays so that there is no need for a separate drying time, In particular, when a specific pattern or letter is expressed in gold on a printed matter such as a plaid pattern, a business card, a wedding invitation card, etc., it is coated with gold powder to give a right effect, It is possible to give a beautiful color expression by changing the irregular reflection amount according to the angle because the refraction rate of light is high like one piece of powder of a grain of powder, and it is possible to mass-produce the color of gold and silver unique, The unit price and the delivery time can be satisfied by one process, and the economical effect is high. This is not a very useful effect that can also express a stronger gold color, etc. PP over laminating, UV coating.

지금까지 본 발명은 제시된 실시 예를 참조하여 상세하게 설명이 되었지만 이 분야에서 통상의 지식을 가진 자는 제시된 실시 예를 참조하여 본 발명의 기술적 사상을 벗어나지 않는 범위에서 다양한 변형 및 수정 발명을 만들 수 있을 것이다. 본 발명은 이와 같은 변형 및 수정 발명에 의하여 제한되지 않으며 다만 아래에 첨부된 청구범위에 의하여 제한된다. While the present invention has been particularly shown and described with reference to exemplary embodiments thereof, it is evident that many alternatives, modifications and variations will be apparent to those skilled in the art in light of the above teachings. will be. The invention is not limited by these variations and modifications, but is limited only by the claims appended hereto.

11 : 스크린
13a : 감광액 상막
13b : 감광액 후막
20 : 금분, 은분 혼합물
30 : 원지11: Screen
13a:
13b:
20: gold, silver mixture
30: Origin

Claims (5)

(a) 공예용 금분과 은분을 에칭 무광 UV 유제를 혼합시켜 금분, 은분 혼합물(20)을 제조하는 단계;
(b) 금분, 은분 혼합물(20)에 경화제를 혼합하는 단계;
(c) 스크린(11)의 표면에 감광액을 일정 두께로 도포하되, 1차로 스크린판 후막(13b)을 3번 도포 스크린판 상막(13a)을 3번 도포 후 건조하고,
2차로 스크린판 후막(13b)을 3번 도포 스크린판 상막(13a)을 2~3번 도포하고 건조시켜 후막(13b)을 형성하는 단계;
(d) 문양이 인쇄된 필름을 스크린(11)에 압착한 후 노광하는 단계;
(e) 필름을 제거하고 스크린(11)을 세척하는 단계;
(f) 금분, 은분이 인쇄될 원지(30)에 스크린(11)을 위치시키고, 금분, 은분 혼합물(20)을 도포하는 단계;
(g) 금분, 은분 혼합물(20)을 UV자외선으로 경화하는 단계;를 포함하여 이루어지는 것을 특징으로 하는 공예용 금분, 은분을 입체돋움으로 인쇄후 UV자외선에 경화시키는 금분, 은분 인쇄방법.(a) preparing a gold and silver mixture (20) by mixing an etch-free UV tanning agent with gold powder and silver powder;
(b) mixing a curing agent with the gold and silver mixture (20);
(c) applying a sensitizing solution to the surface of the screen 11 to a predetermined thickness, applying the third screen plate thick film 13b to the first screen plate 13a three times,
Applying the second screen plate thick film 13b three times, applying the second screen plate film 13a two or three times, and drying to form a thick film 13b;
(d) squeezing the pattern printed on the screen (11) and exposing it;
(e) removing the film and washing the screen 11;
(f) placing the screen (11) on a paper (30) to be printed with gold and silver, and applying a gold / silver mixture (20);
(g) curing the gold and silver mixture 20 with ultraviolet rays; and curing the gold powder and silver powder by applying ultraviolet rays to the silver powder after printing the silver powder. 제 1항에 있어서,
혼합물은 금 반짝이, 은 반짝이(금박, 은박을 찍은 폴리에스터 재질을 잘게 부순 가루인 금 반짝이, 은 반짝이와 천연 광물로 이루어진 무기 안료인 금분, 은분응 혼합하는 것을 특징으로 하는 공예용 금분, 은분을 입체돋움으로 인쇄후 UV자외선에 경화시키는 금분, 은분 인쇄방법. The method according to claim 1,
The mixture consists of gold, silver, and gold, which is an inorganic pigment consisting of gold glitter, silver glitter (gold foil, silver foil, polyester shavings, A method of printing gold powder or silver powder which is cured by ultraviolet rays after printing with stereoscopic effect. 제 1항에 있어서,
감광액은 두꺼운 후막의 빠른 건조가 가능한 아조픽스(감광 유제) 2200번을 감광액으로 사용하는 것을 특징으로 하는 UV공예용 금분, 은분을 입체돋움으로 인쇄후 UV자외선에 경화시키는 금분, 은분 인쇄방법.The method according to claim 1,
The sensitizing solution is characterized by using AzoPix (sensitized emulsion) No. 2200, which is capable of rapid drying of a thick thick film, as a sensitizing solution, and is a method for printing gold powder or silver powder which is cured in UV ultraviolet rays after printing with gold powder and silver powder. 제 1항에 있어서,
스크린(11)은 #150 목인 것을 특징으로 하는 UV공예용 금분, 은분을 입체돋움으로 인쇄후 UV자외선에 경화시키는 금분, 은분 인쇄방법.The method according to claim 1,
And the screen (11) is a # 150 sieve. The method for printing gold powder or silver powder for UV curing in which the silver powder is cured by ultraviolet rays after printing with silver powder. 제 1항에 있어서,
감광액을 0.2~0.4mm 두께로 도포하는 것을 특징으로 하는 공예용 금분, 은분을 입체돋움으로 인쇄후 UV자외선에 경화시키는 금분, 은분 인쇄방법.The method according to claim 1,
Wherein the sensitizing solution is applied in a thickness of 0.2 to 0.4 mm. The method for printing gold powder or silver powder according to any one of claims 1 to 3, wherein the silver powder is cured in ultraviolet light after printing with silver powder.
KR1020170058469A 2016-05-31 2017-05-11 Printing method KR20170136424A (en)