KR20160143195A - Non-Flammable composite for foamed polystyrene - Google Patents
Non-Flammable composite for foamed polystyrene Download PDFInfo
- Publication number
- KR20160143195A KR20160143195A KR1020150079460A KR20150079460A KR20160143195A KR 20160143195 A KR20160143195 A KR 20160143195A KR 1020150079460 A KR1020150079460 A KR 1020150079460A KR 20150079460 A KR20150079460 A KR 20150079460A KR 20160143195 A KR20160143195 A KR 20160143195A
- Authority
- KR
- South Korea
- Prior art keywords
- stirred
- stirrer
- suspension
- solution
- chloride
- Prior art date
Abstract
Description
본 발명은 발포 폴리스타이렌 난연성 접착제 조성물에 관한 것이다.The present invention relates to a foam polystyrene flame retardant adhesive composition.
통상, 스티로폼이라 불리고 있는 발포 폴리스타이렌은 폴리스타이렌 수지에 펜테인이나 뷰테인 등 탄화수소가스를 주입시킨 뒤 이를 증기로 부풀린 발포 제품으로, 체적의 98%가 공기이고 나머지 2%가 수지로 되는 소재로서, 이것은 스타이렌에 펜테인뷰테인가스 등의 발포제를 주입하고 물로 중합한 다음 가열하면 폴리스타이렌 비드(bead: 구상입자)를 얻게 되고, 이 폴리스타이렌 비드를 성형기에 투입하고 증기로 가열 냉각하면 발포된 성형체 형태로 얻을 수 있다.In general, foamed polystyrene which is called styrofoam is a foamed product in which a hydrocarbon gas such as pentane or butane is injected into a polystyrene resin, which is vaporized, and 98% of the volume is air and the remaining 2% is a resin. When styrene is injected with a foaming agent such as pentane butane gas, it is polymerized with water and then heated to obtain polystyrene beads (spherical particles). When the polystyrene beads are charged into a molding machine and heated and cooled by steam, Can be obtained.
이렇게 제조되는 발포 폴리스타이렌 제품은 단열성, 방음성, 경량성, 내약품성이 우수하고, 인체에 무해한 것이면서 제조비용도 저렴하여 건물의 단열재, 물품 포장재 등에 적합한 것이지만, 인화성이 높고 연소 시에 발생하는 유독가스량이 상당하다는 단점을 가지고 있다.The foamed polystyrene product thus produced is excellent in heat insulation, soundproofness, light weight, and chemical resistance, and is harmless to the human body and low in manufacturing cost, so that it is suitable for insulation materials and packaging materials for buildings. However, it has high flammability and toxic gas And the like.
한편, 일각에서는 발포 폴리스타이렌에 난연성을 부여하려는 시도가 진행되고 있다. 예를 들면 난연제에 발포 폴리스타이렌을 함침 시키거나 또는 표면에 스프레이 코팅하는 방법이 실시되고 있지만, 이 방법으로는 난연제가 내부까지 침투되지 않아 그 효과는 기대할 수 없는 수준이다.On the other hand, some attempts have been made to impart flame retardancy to expanded polystyrene. For example, a method of impregnating a flame retardant with expanded polystyrene or spray coating the surface of the flame retardant is performed, but the flame retardant is not penetrated into the interior of the flame retardant by this method, and the effect is not expected.
다음 특허문헌 1은 폴리스타이렌의 표면에 난연제를 코팅하는 방법의 예로서, 폴리스타이렌 알갱이의 표면에 난연성 액상 코팅액을 분사 코팅처리하고 건조하는 과정을 반복하여 샌드위치 패널용 단열재로 제조하였을 때에 화재에 견디는 난연성을 지니게 하는 방법을 개시하고 있으나, 발포 폴리스티렌 알갱이의 표면에 무기성 액상 혼합물을 분사 코팅하고 열풍로에서 건조시키는 과정을 2회 반복하고 장시간 숙성시킨 다음에 샌드위치패널로 성형하는 방법이므로 과정이 번거롭고 소요시간이 길어서 대량생산에는 적합하지 않다.The following Patent Document 1 discloses a method of coating a surface of a polystyrene with a flame retardant agent, wherein a flame retardant liquid coating liquid is spray coated on the surface of the polystyrene particles and dried to produce a flame retardant resistant to fire However, since the process of spraying an inorganic liquid mixture on the surface of foamed polystyrene granules and drying in a hot air furnace is repeated twice, aged for a long time, and then molded into a sandwich panel, the process is troublesome and takes a long time It is not suitable for mass production.
다음 특허문헌 2는 폴리스타이렌 알갱이를 접합시키는 접착제로서, 이소시아네이트를 포함하는 용액과, 폴리올을 포함하는 용액을 혼합하여 되는 무기 계열의 난연성 접착제 조성물을 개시하고, 이 접착제 조성물이 화재로 인한 열을 1차적으로 차단하여 줌에 따라 샌드위치 패널이 화재의 저항성을 갖게 하는 것을 개시하고 있다.The following Patent Document 2 discloses an inorganic flame-retardant adhesive composition in which a solution containing isocyanate and a solution containing a polyol are mixed as an adhesive for bonding polystyrene particles, and this adhesive composition is used as a primary To allow the sandwich panel to have fire resistance upon zooming.
또, 다음 특허문헌 3은 우레탄 바니쉬 및 발포 스타이렌 폼을 포함하는 제1 용액, 알칼리 실리케이트 용액, 알긴산 나트륨 및 카제인산 나트륨 중에서 선택한 1종 이상, 알킬 벤젠 설포네이트계 계면활성제 및 아크릴계 비닐바사테이트 유화물을 포함하는 제2 용액, 탄산칼슘 분말, 실리케이트계 미네랄, 점토질 보강재, 및 수산화물로 이루어진 발포 스타이렌 폼용 난연성 코팅 조성물을 개시하고 있다.Further, the following Patent Document 3 discloses a method for producing a polyurethane foam, which comprises using a first solution containing a urethane varnish and a foamed styrene foam, at least one selected from an alkali silicate solution, sodium alginate and sodium caseinate, an alkylbenzene sulfonate surfactant and an acrylic vinyl valerate emulsion , A calcium carbonate powder, a silicate-based mineral, a clay-reinforcing material, and a hydroxide. The flame retardant coating composition of the present invention is a flame retardant coating composition for foamed styrene foam.
다음 특허문헌 4에도 발포 성형되는 폴리스타이렌 알갱이의 표면에 난연성 유무기 복합 액상 코팅액을 분사 코팅처리하고 건조과정을 반복한 후 발포 폴리스티렌 폼 단열재를 압축 성형한 것을 샌드위치 패널로 성형하여, 화재 발생시 샌드위치 패널에 충전된 단열재가 난연성을 갖게 하는 것으로서, 말토오스, 소수성 나노 실리케이트 용액, 알칼리 금속 탄산염 화합물, 스타이렌-부틸렌 고무 유화물, 알킬 벤젠 설포네이트계 계면활성제, 지오폴리머를 주성분으로 하는 발포 폴리스티렌 폼 단열재의 난연성 조성물이 개시되어 있고, 다음 특허문헌 5에는 폴리비닐아세테이트-폴리부틸아크릴레이트 공중합체 에멀젼 및 알칼리 실리케이트 화합물의 복합 용액, 석회석 분말 및 팽창 흑연을 포함하는 발포 폴리스타이렌 폼 난연성 조성물로서, 폴리비닐알코올 수용액에 비닐아세테이트와 부틸아크릴레이트의 혼합단량체 및 개시제를 투입하여 반응시킨 반응물을 상온에서 냉각하여 폴리비닐아세테이트-폴리부틸아크릴레이트 공중합체 에멀젼을 얻고, 여기에 다시 알칼리 실리케이트 화합물 및 개시제를 투입하여 반응시킨 다음, 황산제이철 암모늄 수용액을 첨가하여 반응을 종료시켜 조성물을 얻는 방법을 개시하고 있다.Also in the following Patent Document 4, the polystyrene granules to be foam-molded are spray coated with a flame retardant organic-inorganic hybrid liquid coating liquid and the drying process is repeated, and the foamed polystyrene foam insulation is compression molded to form a sandwich panel. The flame retardancy of the filled polystyrene foam insulation mainly composed of maltose, a hydrophobic nano-silicate solution, an alkali metal carbonate compound, a styrene-butylene rubber emulsion, an alkylbenzene sulfonate surfactant, and a geopolymer, And the following Patent Document 5 discloses a foamed polystyrene foam-flame retardant composition comprising a composite solution of a polyvinyl acetate-polybutyl acrylate copolymer emulsion and an alkali silicate compound, limestone powder and expanded graphite, A reactant obtained by charging a mixed monomer of vinyl acetate and butyl acrylate and an initiator into a water solution of koal and reacting was reacted at room temperature to obtain a polyvinyl acetate-polybutylacrylate copolymer emulsion, and an alkali silicate compound and initiator were added thereto And then adding a solution of ammonium ferric sulfate aqueous solution to terminate the reaction to obtain a composition.
상기와 같이 종래부터 폴리스타이렌에 난연성을 부여하여, 이것이 주재료로 되는 샌드위치 패널의 가연성을 낮춰 보려는 노력이 경주되고 있으나, 제안된 방법은 신규의 발포 폴리스타일렌에는 효과를 볼 수 있지만, 폐 발포 스타일렌은 표면에 이물이 많은 까닭에 적용할 수 없는 단점이 있다.As described above, conventionally, efforts have been made to reduce flammability of a sandwich panel in which flame retardancy is imparted to polystyrene as a main material. However, the proposed method is effective for a new foamed polystyrene. However, There is a drawback that it can not be applied because there are many foreign objects.
본 발명은 발포 폴리스타이렌 알갱이의 표면으로 코팅되어서 내화염성을 지니게 함과 동시에, 연소 시의 유독가스 발생량도 적은 발포 폴리스타이렌 난연성 접착제 조성물로서, 발포 폴리스타이렌 알갱이일지라도 그 표면에 양호하게 코팅 접합될 수 있는 발포 폴리스타이렌 난연성 접착제를 제공함에 있다.The present invention relates to a foamed polystyrene flame retardant adhesive composition which is coated on the surface of foamed polystyrene granules and has a fire resistance and a small amount of toxic gas generated during combustion, and is a foamed polystyrene flame retardant adhesive composition which is a foamed polystyrene granule, And to provide a flame-retardant adhesive.
상기 목적을 달성하는 본 발명의 발포 폴리스타이렌 난연성 접착제 조성물은, 송진용액, 아교, 강 알칼리성분, 염, 중화제, 상용화제를 물에 용해시킨 현탁액 2.2~2.8%, 응고제 42.8~52.2%, 물 45~55%를 혼합 교반하고 염도 21~25‰ 범위로 조절하여 얻는다.The foamed polystyrene flame retardant adhesive composition of the present invention for achieving the above object is a polystyrene flame retardant adhesive composition comprising 2.2 to 2.8% of a suspension in which a rosin solution, a glue, a strong alkaline component, a salt, a neutralizing agent and a compatibilizing agent are dissolved in water, a coagulant of 42.8 to 52.2% 55% by mixing and stirring and adjusting the salinity in the range of 21 ~ 25 ‰.
더 구체적으로 현탁액은, 송진용액 1~3%, 아교 1.2~3.6%, 강 알칼리성분 5~9%, 염 3~5%, 중화제 0.1~0.3%, 상용화제 8~12%, 물 67.1~81.7%를 혼합 교반하여 조성된다.More specifically, the suspension contains 1 to 3% of a pine root, 1.2 to 3.6% of a glue, 5 to 9% of a strong alkaline component, 3 to 5% of a salt, 0.1 to 0.3% of a neutralizing agent, 8 to 12% of a compatibilizer, % By weight.
송진용액은, 99% 이상의 고순도 송진, 계를 안정시키기 위한 수용성 콜로이드안정제, 상기 송진의 접착력을 증진시키기 위한 연화제, 및 이들 물질이 물에 더 잘 용해되도록 하는 친수성 용제를 혼합 교반하여 조성되는 것이며, 더 구체적으로는 99% 이상의 고순도 송진 26.8~32.8%, 식물성 연화제 1.9~2.8%, 친수성 용제 58.7~67.5%, 콜로이드안정제 1.5~2.4%, 광유계 연화제 2.3~3.3%의 비율로 혼합 교반되어 응집력이 강하고 방수성을 지니는 특징을 갖는 것이다.The rosin solution is prepared by mixing and stirring a high-purity rosin of 99% or more, a water-soluble colloidal stabilizer for stabilizing the system, a softening agent for enhancing the adhesive strength of the rosin, and a hydrophilic solvent for dissolving these substances better in water, More specifically, they were mixed and agitated at a ratio of high purity of 99% or more to 26.8 to 32.8%, vegetable softener of 1.9 to 2.8%, hydrophilic solvent of 58.7 to 67.5%, colloidal stabilizer of 1.5 to 2.4% and mineral oil softener of 2.3 to 3.3% It is strong and waterproof.
99% 이상의 고순도 송진은, 통상의 송진을 증류하여 얻어지는 것으로서 증류과정에서 고분자물질만 남기고 저분자물질은 소멸시킨 것이다. 99% 이상의 고순도 송진에 의해 본 발명의 발포 폴리스타이렌 난연성 접착제 조성물은 접착력과 응집력 및 방수성을 갖게 된다.A high purity of 99% or more is obtained by distilling conventional rosin, leaving only the polymeric material in the distillation process and destroying the low molecular weight material. By the high purity of 99% or more, the foamed polystyrene flame retardant adhesive composition of the present invention has an adhesive force, a cohesive force and a waterproof property.
송진용액에서, 콜로이드안정제는 디에칠렌글리콜, 트리에칠렌글리콜, 폴리에칠렌글리콜 100, 200, 300 중에서 선택한 1종, 또는 2종 이상의 혼합물을 사용할 수 있으며, 이것은 송진용액에서 계를 안정화하는 역할을 한다.In the rosin solution, the colloid stabilizer may be one or a mixture of two or more selected from diethylene glycol, triethylene glycol, polyethylene glycol 100, 200, and 300, which serves to stabilize the system in the rosin solution.
연화제는 본 발명의 발포 폴리스타이렌 난연성 접착제 조성물에 부여된 응집력을 증진시켜주며, 이것은 중쇄지방산(middle chain length triglyceride) 등의 식물성 연화제와, 프로세스오일(process oil), 디옥틸테레플레이트(dioctyl terephthalate) 와 같은 광유계 연화제 중에서 선택한 1종, 또는 2종 이상의 혼합물을 사용할 수 있다.The softener enhances the cohesive force imparted to the foamed polystyrene flame retardant adhesive composition of the present invention, which includes vegetable softeners such as middle chain length triglycerides, process oils, dioctyl terephthalates, And one kind or a mixture of two or more kinds selected from the same mineral oil type softening agents can be used.
또, 친수성 용제는, 첨가된 성분이 물에 잘 녹게 하는 작용을 하여 송진의 용해를 돕는 것으로서, 이것은 이소프로필알코올이 가장 효과적이지만 값이 비싸기 때문에 여기에 비교적 저렴한 메탄올을 적당량 혼합한 것을 채용할 수도 있다.A hydrophilic solvent is one that helps dissolve the pine by dissolving the added components in water. This is because isopropyl alcohol is the most effective, but because of its high price, it is possible to adopt a mixture of an appropriate amount of relatively inexpensive methanol have.
현탁액의 아교는 거친 입도의 것도 상관없이 채용할 수 있고, 이것은 발포 폴리스타이렌 난연성 접착제 조성물에 부여되는 불연성 또는 난연성을 향상시켜주는 작용을 한다.The glue of the suspension can be employed regardless of its coarse particle size, and it acts to improve the incombustibility or flame retardancy imparted to the foamed polystyrene flame retardant adhesive composition.
현탁액에 첨가되는 강 알칼리성분으로는 수산화나트륨, 수산화칼륨, 수산화마그네슘 중에서 선택한 1종, 또는 2종 이상을 혼합하여 첨가할 수 있고, 이것은 송진성분과 아교성분을 연화시켜서 물에 잘 녹을 수 있도록 작용한다.The strong alkaline component to be added to the suspension may be a mixture of one or more selected from sodium hydroxide, potassium hydroxide and magnesium hydroxide, which softens the rosin component and the glue component, do.
염은 현탁액의 pH 안정을 도모하기 위하여 첨가되는 것이며, 이것은 염화나트륨, 염화칼륨, 염화칼슘, 염화은, 염화구리, 염화수은, 염화암모늄, 제3 인산소다 중에서 선택한 1종, 또는 2종 이상의 혼합물을 채용할 수 있으며, 이것은 상기 강알카리성분에 송진이 연화될 때 나타나는 접착력의 저감현상을 보강하는 작용도 겸한다.The salt is added in order to maintain the pH stability of the suspension, and it can employ one kind or a mixture of two or more selected from sodium chloride, potassium chloride, calcium chloride, silver chloride, copper chloride, mercury chloride, ammonium chloride and sodium phosphate This also serves to reinforce the phenomenon of reduction of the adhesive force appearing when the resin is softened in the strong alkaline component.
중화제로는, 약알칼리성분이면 어떤 종류라도 채용가능하고 예를 들면 암모니아, 트리에틸아민, 아미노메틸프로판올 중에서 선택한 1종, 또는 2종 이상의 혼합물을 사용할 수 있으며, 이것은 현탁액의 최종 알카리도를 조절하는 역할을 한다. As the neutralizing agent, any kind of weakly alkaline component can be employed. For example, one kind or a mixture of two or more selected from ammonia, triethylamine, and aminomethylpropanol can be used. This serves to control the final alkalinity of the suspension .
또, 상용화제로는 케톤이 적합하다.A ketone is suitable as a compatibilizing agent.
케톤류는 여러 성분의 액체가 다른 액체와 뒤섞일 수 있게 부유하도록 작용하는 것으로, 아세톤, 3-브로모-사이클로헥사논(3-bromo-cyclohexanone), 헥산-3-원(hexan-3-one) 등의 케톤 종류 중에서 선택한 1종을 채용할 수 있다.The ketones act to float so that liquids of various components can intermingle with other liquids, such as acetone, 3-bromo-cyclohexanone, hexan-3-one, And the like can be adopted.
응고제는 염화마그네슘, 황산칼슘, 염화칼슘 중에서 선택한 1종, 또는 2종 이상의 혼합물을 채용할 수 있으며, 이것은 아교를 굳히기 위하여 첨가된다.The coagulant may be one selected from magnesium chloride, calcium sulfate, and calcium chloride, or a mixture of two or more thereof, which is added to solidify the glue.
상술한 바와 같은 본 발명의 발포 폴리스타이렌 난연성 접착제 조성물은, 99% 이상의 고순도 송진에 의한 강한 응집력과 방수성의 작용, 그리고 친수성 용제에 의해 물과 잘 융합됨에 따라, 신규의 발포 폴리스타일렌 입자는 물론, 발포 폴리스타일렌 입자일지라도 그 표면에 간편하게 도포될 수 있고, 또한 보드 형태로 접합되었을 때는 응고제의 작용으로 발포 폴리스타일렌 입자의 표면에 도포된 아교성분이 굳어지면서 보호막을 형성하게 됨에 따라 본 발명의 난연성 조성물이 사용된 발포 폴리스타일렌 보드는 난연 효과를 갖추게 된다.As described above, the foam polystyrene flame retardant adhesive composition of the present invention is excellent in the cohesive strength and waterproof property by 99% or more of high purity rosin and is well fused with water by the hydrophilic solvent, so that the foamed polystyrene flame- The present invention provides a flame retardant composition of the present invention, which can be easily applied to the surface of the foamed polystyrene particles even when the foamed polystyrene particles are bonded in a board form, The foamed polystyrene boards used have a flame retardant effect.
이하 본 발명을 상세히 설명한다.Hereinafter, the present invention will be described in detail.
본 발명은 고순도 송진의 강한 응집력과 방수성, 그리고 아교의 불연성과 난연성을 발포 폴리스타이렌 입자 표면에 부여하기 위하여, 일차로 상기 송진이 아교와 혼합될 수 있도록 연화제, 콜로이드안정제, 친수성용제 등과 혼합한 송진용액을 준비하고, 이 송진용액에 아교, 강알카리성분, 염, 중화제, 상용화제를 물과 함께 첨가하여 현탁액을 얻고, 이 현탁액에 응고제를 물과 함께 첨가하여 얻어지는 발포 폴리스타일렌 난연성 접착제 조성물을 제안한다.In order to impart strong cohesion and waterproofness of high-purity rosin and water-insoluble properties of glue and non-flammability and flame retardancy of the glue to the surfaces of expanded polystyrene particles, a rosin solution mixed with a softening agent, a colloidal stabilizer and a hydrophilic solvent Flame retardant adhesive composition obtained by preparing a rosin, a strong alkaline component, a salt, a neutralizing agent and a compatibilizing agent together with water to obtain a suspension, and adding a coagulant to the suspension together with water .
더 구체적으로, 본 발명의 발포 폴리스타이렌 난연성 접착제 조성물은, 송진용액 1~3%, 아교 1.2~3.6%, 강 알칼리성분 5~9%, 염 3~5%, 중화제 0.1~0.3%, 상용화제 8~12%, 물 67.1~81.7%의 비율로 혼합된 현탁액 2.2~2.8%에, 응고제 42.8~52.2%, 물 45~55%를 혼합 교반하여 염도를 21~25‰ 범위로 조절하는 것으로 완성된다.More specifically, the foamed polystyrene flame retardant adhesive composition of the present invention comprises 1 to 3% of a rosin solution, 1.2 to 3.6% of glue, 5 to 9% of a strong alkaline component, 3 to 5% of a salt, 0.1 to 0.3% of a neutralizing agent, And 42 ~ 52.2% of coagulant and 45 ~ 55% of water are mixed and stirred to adjust the salinity to the range of 21 ~ 25 ‰, to 2.2 ~ 2.8%
염도 조절은 현탁액과 응고제를 물과 함께 교반기에 투입하고 대략 20분 정도 교반하는 것으로 행해지고, 물의 분량을 가감하는 것으로 조절할 수 있다.Salinity control is carried out by adding the suspension and the coagulant to the agitator together with water and stirring for about 20 minutes, and adjusting the amount of water can be controlled.
본 발명에서, 염도는 발포 폴리스타이렌 난연성 접착제 조성물의 불연성에 큰 영향을 주는 것으로, 실험 결과 염도 25‰ 수준에서 최적의 불연 성능을 나타내었고 그 이하의 염도 20‰ 범위에서는 불연 성능이 거의 나타나지 않았고, 또 염도 25‰를 초과하면 접착제 조성물의 안정성이 저하되기 시작하여 염도 29‰ 이상에서는 사용이 곤란할 정도로 하락하였다.In the present invention, the salinity has a great influence on the incombustibility of the foam polystyrene flame-retardant adhesive composition. As a result, the flame retardancy of the polystyrene-based flame retardant adhesive composition showed an optimum flammability performance at a salt level of 25 ‰, When the salt content exceeds 25%, the stability of the adhesive composition begins to deteriorate, and the use of the adhesive composition is lowered at a salt content of more than 29%.
아교는 본 발명에서 거친 입도의 것이라도 관계없이 채용할 수 있고, 이것은 발포 폴리스타이렌 난연성 접착제 조성물에 부여되는 불연성 또는 난연성을 향상시켜주는 작용을 한다.The glue can be employed regardless of the coarse particle size in the present invention, and this function improves the incombustibility or flame retardancy imparted to the foamed polystyrene flame retardant adhesive composition.
강알칼리성분은 송진과 아교를 연화시켜서 이들이 물에 잘 녹을 수 있게 하고, 이 과정에서 나타나는 송진의 접착력 저감현상은 염에 의한 접착력으로 보강된다.The strong alkali component softens the rosin and glue to allow them to dissolve in water, and the reduction in the adhesive strength of the rosin in this process is reinforced by the adhesion of the salt.
다만, 강알칼리성분은 5% 미만에서 혼합물질의 용해가 제대로 되지 않는 것으로 나타났고, 5%에서 9% 까지는 용해가 양호하게 진행되었으나 9%를 초과하면 용해효과가 더 이상 향상되지 않았다.However, the content of the strong alkaline component was less than 5%, and the dissolution of the mixed material was insufficient. From 5% to 9%, the dissolution was satisfactory, but when it exceeded 9%, the dissolution effect was not further improved.
본 발명에 적합한 강알카리성분으로는, 수산화나트륨, 수산화칼륨, 수산화마그네슘 중에서 선택한 1종, 또는 2종 이상을 혼합해서 사용할 수 있다.As the strong alkaline component suitable for the present invention, one selected from sodium hydroxide, potassium hydroxide and magnesium hydroxide or a mixture of two or more thereof can be used.
염은 현탁액의 pH 안정을 도모하기 위하여 첨가되는 것이며, 이것은 염화나트륨, 염화칼륨, 염화칼슘, 염화은, 염화구리, 염화수은, 염화암모늄, 제3 인산소다 중에서 선택한 1종, 또는 2종 이상의 혼합물을 채용할 수 있다.The salt is added in order to maintain the pH stability of the suspension, and it can employ one kind or a mixture of two or more selected from sodium chloride, potassium chloride, calcium chloride, silver chloride, copper chloride, mercury chloride, ammonium chloride and sodium phosphate have.
상기 강알칼리성분과 염의 투입으로 인하여 현탁액은 알카리성 용액으로 되기 때문에 중화제를 투입하여 pH를 8.5~9.5 로 조절하여 계의 전체 안정성을 도모할 필요가 있다.Since the suspension becomes an alkaline solution due to the introduction of the strong alkali component and the salt, it is necessary to adjust the pH to 8.5 to 9.5 by adding a neutralizing agent so as to achieve the total stability of the system.
본 발명에서 중화제로는 암모니아, 트리에틸아민, 아미노메틸프로판올 중에서 선택한 1종, 또는 2종 이상의 혼합물을 채용하였다.In the present invention, as the neutralizing agent, one selected from ammonia, triethylamine, and aminomethylpropanol, or a mixture of two or more thereof, is employed.
그리고, 현탁액의 상용화제로는 케톤류가 적합하다. As the compatibilizer of the suspension, ketones are suitable.
케톤류는 여러 성분의 액체가 다른 액체와 뒤섞일 수 있게 부유하도록 작용하는 것으로, 아세톤, 3-브로모-사이클로헥사논, 헥산-3-원 등의 케톤 종류 중에서 선택한 1종을 채용할 수 있다.The ketone acts to suspend liquids of various components so as to be mixed with other liquids, and one selected from ketone classes such as acetone, 3-bromo-cyclohexanone, and hexane-3-one can be employed.
응고제는 아교를 굳히는 작용을 하는 것으로, 본 발명에서는 염화마그네슘, 황산칼슘, 염화칼슘 중에서 선택한 1종, 또는 2종 이상의 혼합물을 채용한다.The coagulant acts to strengthen the glue. In the present invention, one kind or a mixture of two or more kinds selected from magnesium chloride, calcium sulfate and calcium chloride is employed.
또한, 상기 현탁액과는 별도로 준비해야 하는 송진용액은, 99% 이상의 고순도 송진 26.8~32.8%, 식물성 연화제 1.9~2.8%, 친수성 용제 58.7~67.5%, 콜로이드안정제 1.5~2.4%, 광유계 연화제 2.3~3.3%를 교반기에서 120℃로 60분간 교반 혼합하면 연한 갈색용액으로 얻을 수 있으며, 이것은 응집력이 강하고 방수성을 갖춘 물성이 있다.In addition, the rosin solution to be prepared separately from the above suspension contains 26.8 to 32.8% of high-purity rosin of 99% or more, 1.9 to 2.8% of vegetable softener, 58.7 to 67.5% of hydrophilic solvent, 1.5 to 2.4% of colloidal stabilizer, 3.3% is mixed with stirring in an agitator at 120 ° C for 60 minutes to obtain a pale brown solution, which has strong cohesive strength and waterproof properties.
99% 이상의 고순도 송진은, 통상의 송진을 증류하여 고분자물질만 남기고 저분자물질이 소멸된 상태의 것이다.The high purity of 99% or more of the pine is in a state in which the low molecular weight material is extinct, leaving only the polymer material, by distilling the usual pine resin.
상기 송진용액이 혼합될 때 계의 안정화가 이루어지게 하는 콜로이드 안정제는, 본 발명에서 디에칠렌글리콜, 트리에칠렌글리콜, 폴리에칠렌글리콜 100, 200, 300 중에서 선택한 1종, 또는 2종 이상의 혼합물을 채용할 수 있으며, 이것에 의해 혼합된 액상물질의 안정화가 유지된다.In the present invention, the colloid stabilizer that stabilizes the system when the rosin solution is mixed can be selected from one or more selected from among diethylene glycol, triethylene glycol, polyethylene glycol 100, 200, and 300, or a mixture of two or more thereof Whereby the stabilization of the mixed liquid material is maintained.
연화제는 중쇄지방산 등의 식물성 연화제, 프로세스오일, 디옥틸테레프탈레이트에서 선택한 1종, 또는 2종 이상의 혼합물과 같은 광유계 연화제를 혼용할 수 있고, 이 연화제는 송진의 접착력을 증진시키는 것이므로 궁극적으로 본 발명의 목적물로 되는 발포 폴리스타이렌 난연성 접착제 조성물의 응집력이 증진되도록 한다.The softening agent may be a vegetable softening agent such as a heavy chain fatty acid, a process oil, a mineral oil softening agent such as a mixture of at least one kind selected from dioctyl terephthalate, or a mixture of two or more kinds thereof, and this softening agent enhances the adhesive force of the rosin. The cohesive force of the foamed polystyrene flame retardant adhesive composition as the object of the invention is enhanced.
또, 친수성 용제로서 이소프로필알코올은 99% 이상의 고순도 송진과 연화제를 용해시켜서 상호 혼합되게 하고 혼합된 여러 종류의 성분물질이 물에 더 잘 녹도록 돕는다. In addition, isopropyl alcohol as a hydrophilic solvent dissolves 99% or more of high-purity rosin and softening agent to be mixed with each other, and helps to mix various kinds of ingredient materials to be dissolved in water.
다만, 이소프로필알코올은 효과가 높지만 값이 비싸므로 경제적 측면에서 비교적 저렴한 메탄올을 대략 2~2.5:1의 비율, 혹은 적당한 비율로 혼합하여 사용할 수도 있다.However, isopropyl alcohol is highly effective, but it is expensive. Therefore, relatively inexpensive methanol may be mixed in a ratio of approximately 2 to 2.5: 1 or an appropriate ratio in view of economy.
다음에 본 발명을 실시 예로서 상세히 설명한다.BEST MODE FOR CARRYING OUT THE INVENTION Next, the present invention will be described in detail by way of examples.
실시 예에서, 송진용액은 99% 이상의 고순도 송진과 연화제, 콜로이드 용액의 첨가량은 증가시키는 반면에 친수성 용제의 첨가량은 줄였고, 현탁액은 송진, 아교, 강알칼리성분, 염, 중화제, 상용화제의 첨가량을 증가시키는 반면에 물의 첨가량을 줄였으며, 최종적으로 얻고자 하는 난연성 접착제에서는 현탁액과 응고제의 첨가량을 증가시키고 물의 첨가량은 줄였을 때에 나타나는 물성변화에 주목하였다.In the examples, the amount of the high-purity rosin, the softening agent, and the colloid solution was increased, while the amount of the hydrophilic solvent was decreased, and the suspension was increased in the amount of the rosin, glue, strong alkali component, salt, neutralizing agent and compatibilizing agent In addition, the amount of water added was decreased. In the flame retardant adhesive finally obtained, the addition amount of the suspension and the coagulant was increased, and the change in the physical properties when the amount of water was decreased was noted.
그리고 비교실시예는 본 발명에서 한정하는 최적의 범위를 벗어나는 비율로 혼합하였을 때 나타나는 물성변화에 주목하였다.And the comparative examples noted the change in physical properties when they were mixed at a ratio outside the optimal range defined in the present invention.
송진용액Songjin solution
99% 이상의 고순도 송진 26.8%99% or more high purity 26.8%
중쇄 지방산 1.90%Heavy chain fatty acid 1.90%
디옥틸 테레프탈레이트 2.30%Dioctyl terephthalate 2.30%
디에칠렌 글리콜 1.50%Diethylene glycol 1.50%
이소프로필 알코올 48.3%Isopropyl alcohol 48.3%
메탄올 19.2%Methanol 19.2%
상기 성분물질을 교반기에 넣고 120℃ 분위기에서 1시간 동안 교반하여 연한 갈색의 점성물질로 된 송진용액을 얻었다.The ingredient materials were placed in a stirrer and stirred for 1 hour in an atmosphere of 120 ° C to obtain a pine rosin solution having a pale brown viscous substance.
현탁액Suspension
송진용액 1.00%Songjin solution 1.00%
아교 1.20%glue 1.20%
수산화나트륨 3.00%Sodium hydroxide 3.00%
수산화칼륨 2.00%Potassium hydroxide 2.00%
염화나트륨 1.00%Sodium chloride 1.00%
제3 인산소다 2.00%Sodium tertiary phosphate 2.00%
암모니아 0.10%ammonia 0.10%
아세톤 8.00%Acetone 8.00%
물 잔량water Balance
상기 성분물질을 교반기에 넣고 상온에서 1시간 동안 교반하여 연한 갈색의 현탁액을 얻었으며 pH는 8.5로 측정되었다.The above material was placed in a stirrer and stirred at room temperature for 1 hour to obtain a pale brown suspension and the pH was measured at 8.5.
난연성 접착제Flame retardant adhesive
현탁액 2.20%Suspension 2.20%
염화마그네슘 42.8%Magnesium chloride 42.8%
물 잔량water Balance
상기 성분물질을 교반기에서 20분간 교반하면서 염도 21‰가 되도록 조절하여 소망의 발포 폴리스타이렌 난연성 접착제 조성물을 얻었다.The component material was stirred for 20 minutes in a stirrer and adjusted to a saltiness of 21 ‰ to obtain a desired foam polystyrene flame retardant adhesive composition.
송진용액Songjin solution
99% 이상의 고순도 송진 26.8%99% or more high purity 26.8%
중쇄 지방산 1.90%Heavy chain fatty acid 1.90%
프로세스 오일 2.30%Process oil 2.30%
디에칠렌 글리콜 1.00%Diethylene glycol 1.00%
트리에칠렌 글리콜 0.50%Triethylene glycol 0.50%
이소프로필 알코올 48.5%Isopropyl alcohol 48.5%
메탄올 19.0%Methanol 19.0%
상기 성분물질을 교반기에 넣고 120℃ 분위기에서 1시간 동안 교반하여 연한 갈색의 점성물질로 된 송진용액을 얻었다.The ingredient materials were placed in a stirrer and stirred for 1 hour in an atmosphere of 120 ° C to obtain a pine rosin solution having a pale brown viscous substance.
현탁액Suspension
송진용액 1.50%Songjin solution 1.50%
아교 1.80%glue 1.80%
수산화칼륨 4.00%Potassium hydroxide 4.00%
수산화마그네슘 2.00%Magnesium hydroxide 2.00%
염화나트륨 1.50%Sodium chloride 1.50%
제3 인산소다 2.00%Sodium tertiary phosphate 2.00%
암모니아 0.15%ammonia 0.15%
3-브로모-사이클로헥사논 9.00%3-Bromo-cyclohexanone 9.00%
물 잔량water Balance
상기 성분물질을 교반기에 넣고 상온에서 1시간 동안 교반하여 연한 갈색의 현탁액을 얻었으며 pH는 8.5로 측정되었다.The above material was placed in a stirrer and stirred at room temperature for 1 hour to obtain a pale brown suspension and the pH was measured at 8.5.
난연성 접착제Flame retardant adhesive
현탁액 2.20%Suspension 2.20%
염화마그네슘 42.8%Magnesium chloride 42.8%
물 잔량water Balance
상기 성분물질을 교반기에서 20분간 교반하면서 염도 22‰가 되도록 조절하여 소망의 발포 폴리스타이렌 난연성 접착제 조성물을 얻었다.The component material was stirred for 20 minutes in a stirrer and adjusted to a saltiness of 22 ‰ to obtain a desired foam polystyrene flame retardant adhesive composition.
송진용액Songjin solution
99% 이상의 고순도 송진 26.8%99% or more high purity 26.8%
중쇄 지방산 1.90%Heavy chain fatty acid 1.90%
프로세스 오일 2.30%Process oil 2.30%
디에칠렌 글리콜 1.00%Diethylene glycol 1.00%
트리에칠렌 글리콜 0.50%Triethylene glycol 0.50%
이소프로필 알코올 48.5%Isopropyl alcohol 48.5%
메탄올 19.0%Methanol 19.0%
상기 성분물질을 교반기에 넣고 115℃ 분위기에서 1시간 동안 교반하여 송진용액을 얻었다. 송진용액은 교반을 거듭할수록 연한 갈색의 점성물질로 변하였다.The ingredient material was placed in a stirrer and stirred in an atmosphere at 115 ° C for 1 hour to obtain a rosin solution. The rosin solution turned into a light brown viscous substance with stirring.
현탁액Suspension
송진용액 2.00%Songjin solution 2.00%
아교 2.40%glue 2.40%
수산화칼륨 5.00%Potassium hydroxide 5.00%
수산화마그네슘 2.00%Magnesium hydroxide 2.00%
염화나트륨 2.00%Sodium chloride 2.00%
염화칼슘 2.00%Calcium chloride 2.00%
아미노메틸프로판 올 0.20%Aminomethyl propane All 0.20%
헥산-3-원 10.0%Hexane-3-one 10.0%
물 잔량water Balance
상기 성분물질을 교반기에 넣고 상온에서 1시간 동안 교반하여 연한 갈색의 현탁액을 얻었으며 pH는 8.8로 측정되었다.The ingredients were placed in a stirrer and stirred at room temperature for 1 hour to obtain a pale brown suspension, pH 8.8.
난연성 접착제Flame retardant adhesive
현탁액 2.20%Suspension 2.20%
염화마그네슘 42.8%Magnesium chloride 42.8%
물 잔량water Balance
상기 성분물질을 교반기에서 20분간 교반하면서 염도 23‰가 되도록 조절하여 소망의 발포 폴리스타이렌 난연성 접착제 조성물을 얻었다.The component material was stirred for 20 minutes in a stirrer to adjust the salt content to 23 ‰, thereby obtaining a desired foam polystyrene flame retardant adhesive composition.
송진용액Songjin solution
99% 이상의 고순도 송진 26.8%99% or more high purity 26.8%
중쇄 지방산 1.90%Heavy chain fatty acid 1.90%
디옥틸 테레프탈레이트 2.30%Dioctyl terephthalate 2.30%
디에칠렌 글리콜 1.00%Diethylene glycol 1.00%
폴리에칠렌글리콜 200 0.50%Polyethylene glycol 200 0.50%
이소프로필 알코올 40.0%Isopropyl alcohol 40.0%
메탄올 27.5%Methanol 27.5%
상기 성분물질을 교반기에 넣고 115℃ 분위기에서 1시간 동안 교반하여 송진용액을 얻었다. 송진용액은 교반을 거듭할수록 연한 갈색의 점성물질로 변하였다.The ingredient material was placed in a stirrer and stirred in an atmosphere at 115 ° C for 1 hour to obtain a rosin solution. The rosin solution turned into a light brown viscous substance with stirring.
현탁액Suspension
송진용액 2.50%Songjin solution 2.50%
아교 3.00%glue 3.00%
수산화나트륨 3.00%Sodium hydroxide 3.00%
수산화칼륨 5.00%Potassium hydroxide 5.00%
염화나트륨 1.00%Sodium chloride 1.00%
염화구리 1.50%Copper chloride 1.50%
제3 인산소다 2.00%Sodium tertiary phosphate 2.00%
암모니아 0.10%ammonia 0.10%
트리메틸아민 0.15%Trimethylamine 0.15%
아세톤 8.30%Acetone 8.30%
물 잔량water Balance
상기 성분물질을 교반기에 넣고 상온에서 1시간 동안 교반하여 연한 갈색의 현탁액을 얻었으며 pH는 8.8로 측정되었다.The ingredients were placed in a stirrer and stirred at room temperature for 1 hour to obtain a pale brown suspension, pH 8.8.
난연성 접착제Flame retardant adhesive
현탁액 2.20%Suspension 2.20%
염화마그네슘 42.8%Magnesium chloride 42.8%
물 잔량water Balance
상기 성분물질을 교반기에서 20분간 교반하면서 염도 24‰가 되도록 조절하여 소망의 발포 폴리스타이렌 난연성 접착제 조성물을 얻었다.The above ingredients were stirred for 20 minutes in a stirrer to adjust the salt content to 24 ‰ to obtain a desired polystyrene flame retardant adhesive composition.
송진용액Songjin solution
99% 이상의 고순도 송진 26.8%99% or more high purity 26.8%
중쇄 지방산 1.90%Heavy chain fatty acid 1.90%
프로세스 오일 2.30%Process oil 2.30%
디에칠렌 글리콜 0.50%Diethylene glycol 0.50%
트리에칠렌글리콜 0.50%Triethylene glycol 0.50%
폴리에칠렌글리콜 300 0.50%Polyethylene glycol 300 0.50%
이소프로필 알코올 44.5%Isopropyl alcohol 44.5%
메탄올 23.0%Methanol 23.0%
상기 성분물질을 교반기에 넣고 120℃ 분위기에서 1시간 동안 교반하여 연한 갈색의 점성물질로 된 송진용액을 얻었다.The ingredient materials were placed in a stirrer and stirred for 1 hour in an atmosphere of 120 ° C to obtain a pine rosin solution having a pale brown viscous substance.
현탁액Suspension
송진용액 3.00%Songjin solution 3.00%
아교 3.60%glue 3.60%
수산화나트륨 3.00%Sodium hydroxide 3.00%
수산화칼륨 3.00%Potassium hydroxide 3.00%
수산화마그네슘 3.00%Magnesium hydroxide 3.00%
염화나트륨 1.00%Sodium chloride 1.00%
제3 인산소다 2.00%Sodium tertiary phosphate 2.00%
염화수은 2.00%Mercury chloride 2.00%
암모니아 0.10%ammonia 0.10%
아미노메틸프로판올 0.10%Aminomethyl propanol 0.10%
트리메틸아민 0.10%Trimethylamine 0.10%
3-브로모-사이클로헥사논 12.0%3-Bromo-cyclohexanone 12.0%
물 잔량water Balance
상기 성분물질을 교반기에 넣고 상온에서 1시간 동안 교반하여 연한 갈색의 현탁액을 얻었으며 pH는 8.9로 측정되었다.The above material was placed in a stirrer and stirred at room temperature for 1 hour to obtain a pale brown suspension. The pH was measured to be 8.9.
난연성 접착제Flame retardant adhesive
현탁액 2.20%Suspension 2.20%
염화마그네슘 23.0%Magnesium chloride 23.0%
황산칼슘 10.0%Calcium sulfate 10.0%
염화칼슘 9.80%Calcium chloride 9.80%
물 잔량water Balance
상기 성분물질을 교반기에서 20분간 교반하면서 염도 25‰가 되도록 조절하여 소망의 발포 폴리스타이렌 난연성 접착제 조성물을 얻었다.The component material was stirred for 20 minutes in a stirrer to adjust the salt content to 25 ‰, thereby obtaining a desired foam polystyrene flame retardant adhesive composition.
송진용액Songjin solution
99% 이상의 고순도 송진 28.3%99% or more high purity 28.3%
중쇄 지방산 2.10%Heavy chain fatty acid 2.10%
프로세스 오일 2.60%Process oil 2.60%
디에칠렌 글리콜 1.00%Diethylene glycol 1.00%
폴리에칠렌글리콜 200 0.70%Polyethylene glycol 200 0.70%
이소프로필 알코올 42.3%Isopropyl alcohol 42.3%
메탄올 23.0%Methanol 23.0%
상기 성분물질을 교반기에 넣고 115℃ 분위기에서 1시간 동안 교반하여 연한 갈색의 점성물질로 된 송진용액을 얻었다.The ingredient material was placed in a stirrer and stirred at 115 ° C for 1 hour to obtain a pine rosin solution of a pale brown viscous substance.
현탁액Suspension
송진용액 1.00%Songjin solution 1.00%
아교 1.20%glue 1.20%
수산화나트륨 3.00%Sodium hydroxide 3.00%
수산화칼륨 2.00%Potassium hydroxide 2.00%
염화나트륨 1.00%Sodium chloride 1.00%
제3 인산소다 2.00%Sodium tertiary phosphate 2.00%
암모니아 0.10%ammonia 0.10%
아세톤 8.00%Acetone 8.00%
물 잔량water Balance
상기 성분물질을 교반기에 넣고 상온에서 1시간 동안 교반하여 연한 갈색의 현탁액을 얻었으며 pH는 8.5로 측정되었다.The above material was placed in a stirrer and stirred at room temperature for 1 hour to obtain a pale brown suspension and the pH was measured at 8.5.
난연성 접착제Flame retardant adhesive
현탁액 2.20%Suspension 2.20%
염화마그네슘 42.8%Magnesium chloride 42.8%
물 잔량water Balance
상기 성분물질을 교반기에서 20분간 교반하면서 염도 25‰가 되도록 조절하여 소망의 발포 폴리스타이렌 난연성 접착제 조성물을 얻었다.The component material was stirred for 20 minutes in a stirrer to adjust the salt content to 25 ‰, thereby obtaining a desired foam polystyrene flame retardant adhesive composition.
송진용액Songjin solution
99% 이상의 고순도 송진 28.3%99% or more high purity 28.3%
중쇄 지방산 2.10%Heavy chain fatty acid 2.10%
디옥틸텔레프탈레이트 2.60%Dioctyl terephthalate 2.60%
폴리에칠렌글리콜 100 1.00%Polyethylene glycol 100 1.00%
폴리에칠렌글리콜 300 0.70%Polyethylene glycol 300 0.70%
이소프로필 알코올 42.3%Isopropyl alcohol 42.3%
메탄올 23.0%Methanol 23.0%
상기 성분물질을 교반기에 넣고 130℃ 분위기에서 1시간 30분 동안 교반하여 송진용액을 얻었다. 얻어진 송진용액은 교반을 거듭할수록 연한 갈색의 점성용액으로 변하였다.The ingredient material was placed in a stirrer and stirred at 130 ° C for 1 hour and 30 minutes to obtain a rosin solution. The resulting rosin solution turned into a light brown viscous solution with stirring.
현탁액Suspension
송진용액 1.50%Songjin solution 1.50%
아교 1.80%glue 1.80%
수산화나트륨 4.00%Sodium hydroxide 4.00%
수산화마그네슘 2.00%Magnesium hydroxide 2.00%
염화나트륨 1.50%Sodium chloride 1.50%
염화칼륨 2.00%Potassium chloride 2.00%
암모니아 0.15%ammonia 0.15%
3-브로모-사이클로헥사논 9.00%3-Bromo-cyclohexanone 9.00%
물 잔량water Balance
상기 성분물질을 교반기에 넣고 상온에서 1시간 동안 교반하여 연한 갈색의 현탁액을 얻었으며 pH는 8.6으로 측정되었다.The above material was placed in a stirrer and stirred at room temperature for 1 hour to obtain a pale brown suspension. The pH was measured to be 8.6.
난연성 접착제Flame retardant adhesive
현탁액 2.20%Suspension 2.20%
염화칼슘 42.8%Calcium chloride 42.8%
물 잔량water Balance
상기 성분물질을 교반기에서 20분간 교반하면서 염도 22‰가 되도록 조절하여 소망의 발포 폴리스타이렌 난연성 접착제 조성물을 얻었다.The component material was stirred for 20 minutes in a stirrer and adjusted to a saltiness of 22 ‰ to obtain a desired foam polystyrene flame retardant adhesive composition.
송진용액Songjin solution
99% 이상의 고순도 송진 28.3%99% or more high purity 28.3%
중쇄 지방산 2.10%Heavy chain fatty acid 2.10%
프로세스 오일 1.30%Process oil 1.30%
디옥틸텔레프탈레이트 1.30%Dioctyl terephthalate 1.30%
디에칠렌 글리콜 0.50%Diethylene glycol 0.50%
폴리에칠렌글리콜 200 0.50%Polyethylene glycol 200 0.50%
폴리에칠렌글리콜 300 0.70%Polyethylene glycol 300 0.70%
이소프로필 알코올 42.3%Isopropyl alcohol 42.3%
메탄올 23.0%Methanol 23.0%
상기 성분물질을 교반기에 넣고 115℃ 분위기에서 1시간 동안 교반하여 연한 갈색을 띈 점성물질로 된 송진용액을 얻었다.The ingredient material was placed in a stirrer and stirred at 115 ° C for 1 hour to obtain a pine rosin solution with a pale brownish viscous substance.
현탁액Suspension
송진용액 2.00%Songjin solution 2.00%
아교 2.40%glue 2.40%
수산화나트륨 5.00%Sodium hydroxide 5.00%
수산화마그네슘 2.00%Magnesium hydroxide 2.00%
염화나트륨 2.00%Sodium chloride 2.00%
염화은 1.00%Silver chloride 1.00%
염화암모늄 1.00%Ammonium chloride 1.00%
아미노메틸프로판올 0.20%Aminomethyl propanol 0.20%
헥산-3-원 10.0%Hexane-3-one 10.0%
물 잔량water Balance
상기 성분물질을 교반기에 넣고 상온에서 1시간 동안 교반하여 연한 갈색의 현탁액을 얻었으며 pH는 8.8로 측정되었다.The ingredients were placed in a stirrer and stirred at room temperature for 1 hour to obtain a pale brown suspension, pH 8.8.
난연성 접착제Flame retardant adhesive
현탁액 2.20%Suspension 2.20%
황산칼슘 42.8%Calcium sulfate 42.8%
물 잔량water Balance
상기 성분물질을 교반기에서 20분간 교반하면서 염도 23‰가 되도록 조절하여 소망의 발포 폴리스타이렌 난연성 접착제 조성물을 얻었다.The component material was stirred for 20 minutes in a stirrer to adjust the salt content to 23 ‰, thereby obtaining a desired foam polystyrene flame retardant adhesive composition.
송진용액Songjin solution
99% 이상의 고순도 송진 28.3%99% or more high purity 28.3%
중쇄 지방산 2.10%Heavy chain fatty acid 2.10%
디옥틸텔레프탈레이트 2.60%Dioctyl terephthalate 2.60%
트리에칠렌글리콜 1.00%Triethylene glycol 1.00%
폴리에칠렌글리콜 200 0.70%Polyethylene glycol 200 0.70%
이소프로필 알코올 42.3%Isopropyl alcohol 42.3%
메탄올 23.0%Methanol 23.0%
상기 성분물질을 교반기에 넣고 115℃ 분위기에서 1시간 동안 교반하여 연한 갈색을 띈 점성물질로 된 송진용액을 얻었다.The ingredient material was placed in a stirrer and stirred at 115 ° C for 1 hour to obtain a pine rosin solution with a pale brownish viscous substance.
현탁액Suspension
송진용액 2.50%Songjin solution 2.50%
아교 3.00%glue 3.00%
수산화마그네슘 2.00%Magnesium hydroxide 2.00%
수산화나트륨 6.00%Sodium hydroxide 6.00%
염화칼륨 1.50%Potassium chloride 1.50%
염화은 1.50%Silver chloride 1.50%
제3 인산소다 1.50%Sodium tertiary phosphate 1.50%
암모니아 0.15%ammonia 0.15%
아미노메틸프로판올 0.10%Aminomethyl propanol 0.10%
아세톤 11.0%Acetone 11.0%
물 잔량water Balance
상기 성분물질을 교반기에 넣고 상온에서 1시간 동안 교반하여 연한 갈색의 현탁액을 얻었으며 pH는 8.5로 측정되었다.The above material was placed in a stirrer and stirred at room temperature for 1 hour to obtain a pale brown suspension and the pH was measured at 8.5.
난연성 접착제Flame retardant adhesive
현탁액 2.20% Suspension 2.20%
염화칼슘 42.8% Calcium chloride 42.8%
물 잔량 water Balance
상기 성분물질을 교반기에서 20분간 교반하면서 염도 24‰가 되도록 조절하여 소망의 발포 폴리스타이렌 난연성 접착제 조성물을 얻었다.The above ingredients were stirred for 20 minutes in a stirrer to adjust the salt content to 24 ‰ to obtain a desired polystyrene flame retardant adhesive composition.
송진용액Songjin solution
99% 이상의 고순도 송진 28.3%99% or more high purity 28.3%
중쇄 지방산 2.10%Heavy chain fatty acid 2.10%
프로세스 오일 1.30%Process oil 1.30%
디옥틸텔레프탈레이트 1.30%Dioctyl terephthalate 1.30%
디에칠렌 글리콜 0.50%Diethylene glycol 0.50%
트리에칠렌글리콜 0.50%Triethylene glycol 0.50%
폴리에칠렌글리콜 200 0.70%Polyethylene glycol 200 0.70%
이소프로필 알코올 42.3%Isopropyl alcohol 42.3%
메탄올 23.0%Methanol 23.0%
상기 성분물질을 교반기에 넣고 120℃ 분위기에서 1시간 동안 교반하여 연한 갈색의 점성물질로 된 송진용액을 얻었다.The ingredient materials were placed in a stirrer and stirred for 1 hour in an atmosphere of 120 ° C to obtain a pine rosin solution having a pale brown viscous substance.
현탁액Suspension
송진용액 3.00%Songjin solution 3.00%
아교 3.60%glue 3.60%
수산화나트륨 3.00%Sodium hydroxide 3.00%
수산화칼슘 3.00%Calcium hydroxide 3.00%
수산화마그네슘 3.00%Magnesium hydroxide 3.00%
염화나트륨 1.00%Sodium chloride 1.00%
염화칼슘 1.00%Calcium chloride 1.00%
염화암모늄 1.00%Ammonium chloride 1.00%
염화수은 2.00%Mercury chloride 2.00%
암모니아 0.10%ammonia 0.10%
아미노메틸프로판올 0.20%Aminomethyl propanol 0.20%
3-브로모-사이클로헥사논 12.0%3-Bromo-cyclohexanone 12.0%
물 잔량water Balance
상기 성분물질을 교반기에 넣고 상온에서 1시간 동안 교반하여 연한 갈색의 현탁액을 얻었으며 pH는 8.9로 측정되었다.The above material was placed in a stirrer and stirred at room temperature for 1 hour to obtain a pale brown suspension. The pH was measured to be 8.9.
난연성 접착제Flame retardant adhesive
현탁액 2.20% Suspension 2.20%
염화마그네슘 23.0%Magnesium chloride 23.0%
황산칼슘 10.0%Calcium sulfate 10.0%
염화칼슘 9.80% Calcium chloride 9.80%
물 잔량water Balance
상기 성분물질을 교반기에서 20분간 교반하면서 염도 21‰가 되도록 조절하여 소망의 발포 폴리스타이렌 난연성 접착제 조성물을 얻었다.The component material was stirred for 20 minutes in a stirrer and adjusted to a saltiness of 21 ‰ to obtain a desired foam polystyrene flame retardant adhesive composition.
송진용액Songjin solution
99% 이상의 고순도 송진 29.8%99% or more high purity 29.8%
중쇄 지방산 2.30%Heavy chain fatty acid 2.30%
디옥틸 테레프탈레이트 2.90%Dioctyl terephthalate 2.90%
디에칠렌 글리콜 1.50%Diethylene glycol 1.50%
폴리에칠렌 글리콜 100 0.40%Polyethylene glycol 100 0.40%
이소프로필 알코올 43.0%Isopropyl alcohol 43.0%
메탄올 20.1%Methanol 20.1%
상기 성분물질을 교반기에 넣고 120℃ 분위기에서 1시간 동안 교반하여 연한 갈색의 점성물질로 된 송진용액을 얻었다.The ingredient materials were placed in a stirrer and stirred for 1 hour in an atmosphere of 120 ° C to obtain a pine rosin solution having a pale brown viscous substance.
현탁액Suspension
송진용액 1.00%Songjin solution 1.00%
아교 1.20%glue 1.20%
수산화칼륨 3.00%Potassium hydroxide 3.00%
수산화마그네슘 2.00%Magnesium hydroxide 2.00%
염화나트륨 1.00%Sodium chloride 1.00%
염화수은 2.00%Mercury chloride 2.00%
암모니아 0.10%ammonia 0.10%
아세톤 9.00%Acetone 9.00%
물 잔량water Balance
상기 성분물질을 교반기에 넣고 상온에서 1시간 동안 교반하여 연한 갈색의 현탁액을 얻었으며 pH는 8.7로 측정되었다.The above material was placed in a stirrer and stirred at room temperature for 1 hour to obtain a pale brown suspension. The pH was measured to be 8.7.
난연성 접착제Flame retardant adhesive
현탁액 2.20%Suspension 2.20%
염화칼슘 42.8%Calcium chloride 42.8%
물 잔량water Balance
상기 성분물질을 교반기에서 20분간 교반하면서 염도 23‰가 되도록 조절하여 소망의 발포 폴리스타이렌 난연성 접착제 조성물을 얻었다.The component material was stirred for 20 minutes in a stirrer to adjust the salt content to 23 ‰, thereby obtaining a desired foam polystyrene flame retardant adhesive composition.
송진용액Songjin solution
99% 이상의 고순도 송진 29.8%99% or more high purity 29.8%
중쇄 지방산 2.30%Heavy chain fatty acid 2.30%
프로세스 오일 1.00%Process oil 1.00%
디옥틸 테레프탈레이트 1.90%Dioctyl terephthalate 1.90%
디에칠렌 글리콜 1.50%Diethylene glycol 1.50%
폴리에칠렌 글리콜 200 0.40%Polyethylene glycol 200 0.40%
이소프로필 알코올 43.0%Isopropyl alcohol 43.0%
메탄올 20.1%Methanol 20.1%
상기 성분물질을 교반기에 넣고 120℃ 분위기에서 1시간 동안 교반하여 연한 갈색의 점성물질로 된 송진용액을 얻었다.The ingredient materials were placed in a stirrer and stirred for 1 hour in an atmosphere of 120 ° C to obtain a pine rosin solution having a pale brown viscous substance.
현탁액Suspension
송진용액 1.50%Songjin solution 1.50%
아교 1.80%glue 1.80%
수산화칼륨 2.00%Potassium hydroxide 2.00%
수산화마그네슘 4.00%Magnesium hydroxide 4.00%
염화구리 1.50%Copper chloride 1.50%
염화암모늄 2.00%Ammonium chloride 2.00%
트리메틸아민 0.15%Trimethylamine 0.15%
3-브로모-사이클로헥사논 9.00%3-Bromo-cyclohexanone 9.00%
물 잔량water Balance
상기 성분물질을 교반기에 넣고 상온에서 1시간 동안 교반하여 연한 갈색의 현탁액을 얻었으며 pH는 8.5로 측정되었다.The above material was placed in a stirrer and stirred at room temperature for 1 hour to obtain a pale brown suspension and the pH was measured at 8.5.
난연성 접착제Flame retardant adhesive
현탁액 2.20%Suspension 2.20%
황산칼슘 22.8%Calcium sulfate 22.8%
염화마그네슘 20.0%Magnesium chloride 20.0%
물 잔량water Balance
상기 성분물질을 교반기에서 20분간 교반하면서 염도 22‰가 되도록 조절하여 소망의 발포 폴리스타이렌 난연성 접착제 조성물을 얻었다.The component material was stirred for 20 minutes in a stirrer and adjusted to a saltiness of 22 ‰ to obtain a desired foam polystyrene flame retardant adhesive composition.
송진용액Songjin solution
99% 이상의 고순도 송진 29.8%99% or more high purity 29.8%
중쇄 지방산 2.30%Heavy chain fatty acid 2.30%
프로세스 오일 2.90%Process oil 2.90%
트리에칠렌 글리콜 0.50%Triethylene glycol 0.50%
디에칠렌 글리콜 0.50%Diethylene glycol 0.50%
폴리에칠렌 글리콜 200 0.40%Polyethylene glycol 200 0.40%
이소프로필 알코올 43.0%Isopropyl alcohol 43.0%
메탄올 20.1%Methanol 20.1%
상기 성분물질을 교반기에 넣고 115℃ 분위기에서 1시간 동안 교반하여 연한 갈색의 점성물질로 된 송진용액을 얻었다.The ingredient material was placed in a stirrer and stirred at 115 ° C for 1 hour to obtain a pine rosin solution of a pale brown viscous substance.
현탁액Suspension
송진용액 2.00%Songjin solution 2.00%
아교 2.40%glue 2.40%
수산화나트륨 4.00%Sodium hydroxide 4.00%
수산화마그네슘 3.00%Magnesium hydroxide 3.00%
염화나트륨 1.00%Sodium chloride 1.00%
염화은 0.50%Silver chloride 0.50%
염화암모늄 2.50%Ammonium chloride 2.50%
트리메틸아민 0.20%Trimethylamine 0.20%
헥산-3-원 10.0%Hexane-3-one 10.0%
물 잔량water Balance
상기 성분물질을 교반기에 넣고 상온에서 1시간 동안 교반하여 연한 갈색의 현탁액을 얻었으며 pH는 8.6로 측정되었다.The above ingredients were placed in a stirrer and stirred at room temperature for 1 hour to obtain a pale brown suspension and the pH was measured to be 8.6.
난연성 접착제Flame retardant adhesive
현탁액 2.20%Suspension 2.20%
염화마그네슘 42.8%Magnesium chloride 42.8%
물 잔량water Balance
상기 성분물질을 교반기에서 20분간 교반하면서 염도 23‰가 되도록 조절하여 소망의 발포 폴리스타이렌 난연성 접착제 조성물을 얻었다.The component material was stirred for 20 minutes in a stirrer to adjust the salt content to 23 ‰, thereby obtaining a desired foam polystyrene flame retardant adhesive composition.
송진용액Songjin solution
99% 이상의 고순도 송진 29.8%99% or more high purity 29.8%
중쇄 지방산 2.30%Heavy chain fatty acid 2.30%
디옥틸 테레프탈레이트 2.90%Dioctyl terephthalate 2.90%
디에칠렌 글리콜 1.50%Diethylene glycol 1.50%
폴리에칠렌 글리콜 0.40%Polyethylene glycol 0.40%
이소프로필 알코올 43.0%Isopropyl alcohol 43.0%
메탄올 20.1%Methanol 20.1%
상기 성분물질을 교반기에 넣고 115℃ 분위기에서 1시간 동안 교반하여 연한 갈색의 점성물질로 된 송진용액을 얻었다.The ingredient material was placed in a stirrer and stirred at 115 ° C for 1 hour to obtain a pine rosin solution of a pale brown viscous substance.
현탁액Suspension
송진용액 2.50%Songjin solution 2.50%
아교 3.00%glue 3.00%
수산화마그네슘 5.00%Magnesium hydroxide 5.00%
수산화나트륨 3.00%Sodium hydroxide 3.00%
염화칼슘 2.50%Calcium chloride 2.50%
염화은 0.50%Silver chloride 0.50%
제3 인산소다 1.50%Sodium tertiary phosphate 1.50%
암모니아 0.20%ammonia 0.20%
아미노메틸프로판올 0.05%Aminomethyl propanol 0.05%
아세톤 12.00%Acetone 12.00%
물 잔량water Balance
상기 성분물질을 교반기에 넣고 상온에서 1시간 동안 교반하여 연한 갈색의 현탁액을 얻었으며 pH는 8.8로 측정되었다.The ingredients were placed in a stirrer and stirred at room temperature for 1 hour to obtain a pale brown suspension, pH 8.8.
난연성 접착제Flame retardant adhesive
현탁액 2.20% Suspension 2.20%
염화마그네슘 32.8%Magnesium chloride 32.8%
황산칼슘 10.0% Calcium sulfate 10.0%
물 잔량 water Balance
상기 성분물질을 교반기에서 20분간 교반하면서 염도 24‰가 되도록 조절하여 소망의 발포 폴리스타이렌 난연성 접착제 조성물을 얻었다.The above ingredients were stirred for 20 minutes in a stirrer to adjust the salt content to 24 ‰ to obtain a desired polystyrene flame retardant adhesive composition.
송진용액Songjin solution
99% 이상의 고순도 송진 29.8%99% or more high purity 29.8%
중쇄 지방산 2.30%Heavy chain fatty acid 2.30%
디옥틸 테레프탈레이트 1.90%Dioctyl terephthalate 1.90%
프로세스 오일 1.00%Process oil 1.00%
트리에칠렌 글리콜 1.00%Triethylene glycol 1.00%
폴리에칠렌 글리콜 100 0.50%Polyethylene glycol 100 0.50%
폴리에칠렌 글리콜 200 0.40%Polyethylene glycol 200 0.40%
이소프로필 알코올 43.0%Isopropyl alcohol 43.0%
메탄올 20.1%Methanol 20.1%
상기 성분물질을 교반기에 넣고 120℃ 분위기에서 1시간 동안 교반하여 연한 갈색의 점성물질로 된 송진용액을 얻었다.The ingredient materials were placed in a stirrer and stirred for 1 hour in an atmosphere of 120 ° C to obtain a pine rosin solution having a pale brown viscous substance.
현탁액Suspension
송진용액 3.00%Songjin solution 3.00%
아교 3.60%glue 3.60%
수산화나트륨 3.00%Sodium hydroxide 3.00%
수산화칼륨 3.00%Potassium hydroxide 3.00%
수산화마그네슘 3.00%Magnesium hydroxide 3.00%
염화나트륨 1.00%Sodium chloride 1.00%
제3 인산소다 2.00%Sodium tertiary phosphate 2.00%
염화수은 2.00%Mercury chloride 2.00%
암모니아 0.10%ammonia 0.10%
아미노메틸프로판올 0.10%Aminomethyl propanol 0.10%
트리메틸아민 0.10%Trimethylamine 0.10%
3-브로모-사이클로헥사논 12.0%3-Bromo-cyclohexanone 12.0%
물 잔량water Balance
상기 성분물질을 교반기에 넣고 상온에서 1시간 동안 교반하여 연한 갈색의 현탁액을 얻었으며 pH는 8.9로 측정되었다.The above material was placed in a stirrer and stirred at room temperature for 1 hour to obtain a pale brown suspension. The pH was measured to be 8.9.
난연성 접착제Flame retardant adhesive
현탁액 2.20%Suspension 2.20%
염화마그네슘 13.0%Magnesium chloride 13.0%
황산칼슘 20.0%Calcium sulfate 20.0%
염화칼슘 9.80%Calcium chloride 9.80%
물 잔량water Balance
상기 성분물질을 교반기에서 20분간 교반하면서 염도 25‰가 되도록 조절하여 소망의 발포 폴리스타이렌 난연성 접착제 조성물을 얻었다.The component material was stirred for 20 minutes in a stirrer to adjust the salt content to 25 ‰, thereby obtaining a desired foam polystyrene flame retardant adhesive composition.
송진용액Songjin solution
99% 이상의 고순도 송진 31.3%99% or more high purity 31.3%
중쇄 지방산 2.50%Heavy chain fatty acid 2.50%
디옥틸 테레프탈레이트 3.10%Dioctyl terephthalate 3.10%
디에칠렌 글리콜 1.00%Diethylene glycol 1.00%
폴리에칠렌글리콜 100 1.10%Polyethylene glycol 100 1.10%
이소프로필 알코올 41.0%Isopropyl alcohol 41.0%
메탄올 20.0%Methanol 20.0%
상기 성분물질을 교반기에 넣고 115℃ 분위기에서 1시간 동안 교반하여 송진용액을 얻었다. 송진용액은 교반을 거듭할수록 연한 갈색의 점성물질로 변하였다.The ingredient material was placed in a stirrer and stirred in an atmosphere at 115 ° C for 1 hour to obtain a rosin solution. The rosin solution turned into a light brown viscous substance with stirring.
현탁액Suspension
송진용액 1.00%Songjin solution 1.00%
아교 1.20%glue 1.20%
수산화칼륨 3.00%Potassium hydroxide 3.00%
수산화마그네슘 2.00%Magnesium hydroxide 2.00%
염화나트륨 1.00%Sodium chloride 1.00%
염화수은 2.00%Mercury chloride 2.00%
암모니아 0.10%ammonia 0.10%
아세톤 8.00%Acetone 8.00%
물 잔량water Balance
상기 성분물질을 교반기에 넣고 상온에서 1시간 동안 교반하여 연한 갈색의 현탁액을 얻었으며 pH는 8.7로 측정되었다.The above material was placed in a stirrer and stirred at room temperature for 1 hour to obtain a pale brown suspension. The pH was measured to be 8.7.
난연성 접착제Flame retardant adhesive
현탁액 2.20%Suspension 2.20%
염화칼슘 42.8%Calcium chloride 42.8%
물 잔량water Balance
상기 성분물질을 교반기에서 20분간 교반하면서 염도 23‰가 되도록 조절하여 소망의 발포 폴리스타이렌 난연성 접착제 조성물을 얻었다.The component material was stirred for 20 minutes in a stirrer to adjust the salt content to 23 ‰, thereby obtaining a desired foam polystyrene flame retardant adhesive composition.
송진용액Songjin solution
99% 이상의 고순도 송진 31.3%99% or more high purity 31.3%
중쇄 지방산 2.50%Heavy chain fatty acid 2.50%
디옥틸 테레프탈레이트 3.10%Dioctyl terephthalate 3.10%
디에칠렌 글리콜 1.00%Diethylene glycol 1.00%
폴리에칠렌글리콜 100 1.10%Polyethylene glycol 100 1.10%
이소프로필 알코올 41.0%Isopropyl alcohol 41.0%
메탄올 20.0%Methanol 20.0%
상기 성분물질을 교반기에 넣고 115℃ 분위기에서 1시간 동안 교반하여 송진용액을 얻었다. 송진용액은 교반을 거듭할수록 연한 갈색의 점성물질로 변하였다.The ingredient material was placed in a stirrer and stirred in an atmosphere at 115 ° C for 1 hour to obtain a rosin solution. The rosin solution turned into a light brown viscous substance with stirring.
현탁액Suspension
송진용액 1.50%Songjin solution 1.50%
아교 1.80%glue 1.80%
수산화칼륨 2.00%Potassium hydroxide 2.00%
수산화마그네슘 4.00%Magnesium hydroxide 4.00%
염화구리 1.50%Copper chloride 1.50%
염화암모늄 2.00%Ammonium chloride 2.00%
트리메틸아민 0.15%Trimethylamine 0.15%
3-브로모-사이클로헥사논 9.00%3-Bromo-cyclohexanone 9.00%
물 잔량water Balance
상기 성분물질을 교반기에 넣고 상온에서 1시간 동안 교반하여 연한 갈색의 현탁액을 얻었으며 pH는 8.5로 측정되었다.The above material was placed in a stirrer and stirred at room temperature for 1 hour to obtain a pale brown suspension and the pH was measured at 8.5.
난연성 접착제Flame retardant adhesive
현탁액 2.20%Suspension 2.20%
황산칼슘 22.8%Calcium sulfate 22.8%
염화마그네슘 20.0%Magnesium chloride 20.0%
물 잔량water Balance
상기 성분물질을 교반기에서 20분간 교반하면서 염도 24‰가 되도록 조절하여 소망의 발포 폴리스타이렌 난연성 접착제 조성물을 얻었다.The above ingredients were stirred for 20 minutes in a stirrer to adjust the salt content to 24 ‰ to obtain a desired polystyrene flame retardant adhesive composition.
송진용액Songjin solution
99% 이상의 고순도 송진 31.3%99% or more high purity 31.3%
중쇄 지방산 2.50%Heavy chain fatty acid 2.50%
디옥틸 테레프탈레이트 3.10%Dioctyl terephthalate 3.10%
디에칠렌 글리콜 1.00%Diethylene glycol 1.00%
폴리에칠렌글리콜 100 1.10%Polyethylene glycol 100 1.10%
이소프로필 알코올 41.0%Isopropyl alcohol 41.0%
메탄올 20.0%Methanol 20.0%
상기 성분물질을 교반기에 넣고 120℃ 분위기에서 1시간 동안 교반하여 송진용액을 얻었다. 송진용액은 교반을 거듭할수록 연한 갈색의 점성물질로 변하였다.The ingredient material was placed in a stirrer and stirred for 1 hour in an atmosphere of 120 ° C to obtain a rosin solution. The rosin solution turned into a light brown viscous substance with stirring.
현탁액Suspension
송진용액 2.00%Songjin solution 2.00%
아교 2.40%glue 2.40%
수산화나트륨 4.00%Sodium hydroxide 4.00%
수산화마그네슘 3.00%Magnesium hydroxide 3.00%
염화나트륨 1.00%Sodium chloride 1.00%
염화은 0.50%Silver chloride 0.50%
염화암모늄 2.50%Ammonium chloride 2.50%
트리메틸아민 0.20%Trimethylamine 0.20%
헥산-3-원 10.0%Hexane-3-one 10.0%
3-브로모-사이클로헥사논 5.00%3-Bromo-cyclohexanone 5.00%
물 잔량water Balance
상기 성분물질을 교반기에 넣고 상온에서 1시간 동안 교반하여 연한 갈색의 현탁액을 얻었으며 pH는 8.9로 측정되었다.The above material was placed in a stirrer and stirred at room temperature for 1 hour to obtain a pale brown suspension. The pH was measured to be 8.9.
난연성 접착제Flame retardant adhesive
현탁액 2.20%Suspension 2.20%
염화마그네슘 42.8%Magnesium chloride 42.8%
물 잔량water Balance
상기 성분물질을 교반기에서 20분간 교반하면서 염도 21‰가 되도록 조절하여 소망의 발포 폴리스타이렌 난연성 접착제 조성물을 얻었다.The component material was stirred for 20 minutes in a stirrer and adjusted to a saltiness of 21 ‰ to obtain a desired foam polystyrene flame retardant adhesive composition.
송진용액Songjin solution
99% 이상의 고순도 송진 31.3%99% or more high purity 31.3%
중쇄 지방산 2.50%Heavy chain fatty acid 2.50%
디옥틸 테레프탈레이트 3.10%Dioctyl terephthalate 3.10%
디에칠렌 글리콜 1.00%Diethylene glycol 1.00%
폴리에칠렌글리콜 100 1.10%Polyethylene glycol 100 1.10%
이소프로필 알코올 41.0%Isopropyl alcohol 41.0%
메탄올 20.0%Methanol 20.0%
상기 성분물질을 교반기에 넣고 130℃ 분위기에서 1시간 30분 동안 교반하여 송진용액을 얻었다. 얻어진 송진용액은 교반을 거듭할수록 연한 갈색의 점성용액으로 변하였다.The ingredient material was placed in a stirrer and stirred at 130 ° C for 1 hour and 30 minutes to obtain a rosin solution. The resulting rosin solution turned into a light brown viscous solution with stirring.
현탁액Suspension
송진용액 2.50%Songjin solution 2.50%
아교 3.00%glue 3.00%
수산화마그네슘 5.00%Magnesium hydroxide 5.00%
수산화나트륨 3.00%Sodium hydroxide 3.00%
염화칼슘 2.50%Calcium chloride 2.50%
염화은 0.50%Silver chloride 0.50%
제3 인산소다 1.50%Sodium tertiary phosphate 1.50%
암모니아 0.20%ammonia 0.20%
아미노메틸프로판올 0.05%Aminomethyl propanol 0.05%
아세톤 12.0%Acetone 12.0%
물 잔량water Balance
상기 성분물질을 교반기에 넣고 상온에서 1시간 동안 교반하여 연한 갈색의 현탁액을 얻었으며 pH는 8.6으로 측정되었다.The above material was placed in a stirrer and stirred at room temperature for 1 hour to obtain a pale brown suspension. The pH was measured to be 8.6.
난연성 접착제Flame retardant adhesive
현탁액 2.20%Suspension 2.20%
염화마그네슘 42.8%Magnesium chloride 42.8%
물 잔량water Balance
상기 성분물질을 교반기에서 20분간 교반하면서 염도 22‰가 되도록 조절하여 폴리스타이렌 난연성 접착제 조성물을 얻었다.The component material was stirred for 20 minutes in a stirrer and adjusted to a salt content of 22 ‰ to obtain a polystyrene flame retardant adhesive composition.
송진용액Songjin solution
99% 이상의 고순도 송진 31.3%99% or more high purity 31.3%
중쇄 지방산 2.50%Heavy chain fatty acid 2.50%
디옥틸 테레프탈레이트 3.10%Dioctyl terephthalate 3.10%
디에칠렌 글리콜 1.00%Diethylene glycol 1.00%
폴리에칠렌글리콜 100 1.10%Polyethylene glycol 100 1.10%
이소프로필 알코올 41.0%Isopropyl alcohol 41.0%
메탄올 20.0%Methanol 20.0%
상기 성분물질을 교반기에 넣고 115℃ 분위기에서 1시간 동안 교반하여 송진용액을 얻었다. 송진용액은 교반을 거듭할수록 연한 갈색의 점성물질로 변하였다.The ingredient material was placed in a stirrer and stirred in an atmosphere at 115 ° C for 1 hour to obtain a rosin solution. The rosin solution turned into a light brown viscous substance with stirring.
현탁액Suspension
송진용액 3.00%Songjin solution 3.00%
아교 3.60%glue 3.60%
수산화나트륨 3.00%Sodium hydroxide 3.00%
수산화칼륨 3.00%Potassium hydroxide 3.00%
수산화마그네슘 3.00%Magnesium hydroxide 3.00%
염화나트륨 1.00%Sodium chloride 1.00%
제3 인산소다 2.00%Sodium tertiary phosphate 2.00%
염화수은 2.00%Mercury chloride 2.00%
암모니아 0.10%ammonia 0.10%
아미노메틸프로판올 0.10%Aminomethyl propanol 0.10%
트리메틸아민 0.10%Trimethylamine 0.10%
3-브로모-사이클로헥사논 12.0%3-Bromo-cyclohexanone 12.0%
물 잔량water Balance
상기 성분물질을 교반기에 넣고 상온에서 1시간 동안 교반하여 연한 갈색의 현탁액을 얻었으며 pH는 8.8로 측정되었다.The ingredients were placed in a stirrer and stirred at room temperature for 1 hour to obtain a pale brown suspension, pH 8.8.
난연성 접착제Flame retardant adhesive
현탁액 2.20%Suspension 2.20%
염화칼슘 42.8%Calcium chloride 42.8%
물 잔량water Balance
상기 성분물질을 교반기에서 20분간 교반하면서 염도 23‰가 되도록 조절하여 소망의 발포 폴리스타이렌 난연성 접착제 조성물을 얻었다.The component material was stirred for 20 minutes in a stirrer to adjust the salt content to 23 ‰, thereby obtaining a desired foam polystyrene flame retardant adhesive composition.
송진용액Songjin solution
99% 이상의 고순도 송진 32.8%99% or more high purity 32.8%
중쇄 지방산 2.80%Heavy chain fatty acid 2.80%
디옥틸 테레프탈레이트 2.30%Dioctyl terephthalate 2.30%
프로세스 오일 1.00%Process oil 1.00%
디에칠렌 글리콜 1.00%Diethylene glycol 1.00%
폴리에칠렌글리콜 100 1.40%Polyethylene glycol 100 1.40%
이소프로필 알코올 43.0%Isopropyl alcohol 43.0%
메탄올 15.7%Methanol 15.7%
상기 성분물질을 교반기에 넣고 120℃ 분위기에서 1시간 동안 교반하여 송진용액을 얻었다. 송진용액은 교반을 거듭할수록 연한 갈색의 점성물질로 변하였다.The ingredient material was placed in a stirrer and stirred for 1 hour in an atmosphere of 120 ° C to obtain a rosin solution. The rosin solution turned into a light brown viscous substance with stirring.
현탁액Suspension
송진용액 1.00%Songjin solution 1.00%
아교 1.20%glue 1.20%
수산화칼륨 4.00%Potassium hydroxide 4.00%
수산화마그네슘 1.00%Magnesium hydroxide 1.00%
염화나트륨 1.00%Sodium chloride 1.00%
염화구리 2.00%Copper chloride 2.00%
트리메틸아민 0.10%Trimethylamine 0.10%
아세톤 8.00%Acetone 8.00%
물 잔량water Balance
상기 성분물질을 교반기에 넣고 상온에서 1시간 동안 교반하여 연한 갈색의 현탁액을 얻었으며 pH는 8.7로 측정되었다.The above material was placed in a stirrer and stirred at room temperature for 1 hour to obtain a pale brown suspension. The pH was measured to be 8.7.
난연성 접착제Flame retardant adhesive
현탁액 2.20%Suspension 2.20%
염화칼슘 42.8%Calcium chloride 42.8%
물 잔량water Balance
상기 성분물질을 교반기에서 20분간 교반하면서 염도 23‰가 되도록 조절하여 소망의 발포 폴리스타이렌 난연성 접착제 조성물을 얻었다.The component material was stirred for 20 minutes in a stirrer to adjust the salt content to 23 ‰, thereby obtaining a desired foam polystyrene flame retardant adhesive composition.
송진용액Songjin solution
99% 이상의 고순도 송진 32.8%99% or more high purity 32.8%
중쇄 지방산 2.80%Heavy chain fatty acid 2.80%
디옥틸 테레프탈레이트 2.30%Dioctyl terephthalate 2.30%
프로세스 오일 1.00%Process oil 1.00%
디에칠렌 글리콜 1.00%Diethylene glycol 1.00%
폴리에칠렌글리콜 100 1.40%Polyethylene glycol 100 1.40%
이소프로필 알코올 43.0%Isopropyl alcohol 43.0%
메탄올 15.7%Methanol 15.7%
상기 성분물질을 교반기에 넣고 120℃ 분위기에서 1시간 동안 교반하여 송진용액을 얻었다. 송진용액은 교반을 거듭할수록 연한 갈색의 점성물질로 변하였다.The ingredient material was placed in a stirrer and stirred for 1 hour in an atmosphere of 120 ° C to obtain a rosin solution. The rosin solution turned into a light brown viscous substance with stirring.
현탁액Suspension
송진용액 1.50%Songjin solution 1.50%
아교 1.80%glue 1.80%
수산화나트륨 3.00%Sodium hydroxide 3.00%
수산화마그네슘 3.00%Magnesium hydroxide 3.00%
염화암모늄 1.50%Ammonium chloride 1.50%
제3 인산소다 2.00%Sodium tertiary phosphate 2.00%
트리메틸아민 0.15%Trimethylamine 0.15%
3-브로모-사이클로헥사논 9.00%3-Bromo-cyclohexanone 9.00%
물 잔량water Balance
상기 성분물질을 교반기에 넣고 상온에서 1시간 동안 교반하여 연한 갈색의 현탁액을 얻었으며 pH는 8.5로 측정되었다.The above material was placed in a stirrer and stirred at room temperature for 1 hour to obtain a pale brown suspension and the pH was measured at 8.5.
난연성 접착제Flame retardant adhesive
현탁액 2.20%Suspension 2.20%
염화칼슘 42.8%Calcium chloride 42.8%
물 잔량water Balance
상기 성분물질을 교반기에서 20분간 교반하면서 염도 25‰가 되도록 조절하여 소망의 발포 폴리스타이렌 난연성 접착제 조성물을 얻었다.The component material was stirred for 20 minutes in a stirrer to adjust the salt content to 25 ‰, thereby obtaining a desired foam polystyrene flame retardant adhesive composition.
송진용액Songjin solution
99% 이상의 고순도 송진 32.8%99% or more high purity 32.8%
중쇄 지방산 2.80%Heavy chain fatty acid 2.80%
디옥틸 테레프탈레이트 2.30%Dioctyl terephthalate 2.30%
프로세스 오일 1.00%Process oil 1.00%
디에칠렌 글리콜 1.00%Diethylene glycol 1.00%
폴리에칠렌글리콜 100 1.40%Polyethylene glycol 100 1.40%
이소프로필 알코올 43.0%Isopropyl alcohol 43.0%
메탄올 15.7%Methanol 15.7%
상기 성분물질을 교반기에 넣고 120℃ 분위기에서 1시간 동안 교반하여 송진용액을 얻었다. 송진용액은 교반을 거듭할수록 연한 갈색의 점성물질로 변하였다.The ingredient material was placed in a stirrer and stirred for 1 hour in an atmosphere of 120 ° C to obtain a rosin solution. The rosin solution turned into a light brown viscous substance with stirring.
현탁액Suspension
송진용액 2.00%Songjin solution 2.00%
아교 2.40%glue 2.40%
수산화나트륨 7.00%Sodium hydroxide 7.00%
염화나트륨 4.00%Sodium chloride 4.00%
트리메틸아민 0.20%Trimethylamine 0.20%
헥산-3-원 10.0%Hexane-3-one 10.0%
물 잔량water Balance
상기 성분물질을 교반기에 넣고 상온에서 1시간 동안 교반하여 연한 갈색의 현탁액을 얻었으며 pH는 8.9로 측정되었다.The above material was placed in a stirrer and stirred at room temperature for 1 hour to obtain a pale brown suspension. The pH was measured to be 8.9.
난연성 접착제Flame retardant adhesive
현탁액 2.20%Suspension 2.20%
염화칼슘 42.8%Calcium chloride 42.8%
물 잔량water Balance
상기 성분물질을 교반기에서 20분간 교반하면서 염도 21‰가 되도록 조절하여 소망의 발포 폴리스타이렌 난연성 접착제 조성물을 얻었다.The component material was stirred for 20 minutes in a stirrer and adjusted to a saltiness of 21 ‰ to obtain a desired foam polystyrene flame retardant adhesive composition.
송진용액Songjin solution
99% 이상의 고순도 송진 32.8%99% or more high purity 32.8%
중쇄 지방산 2.80%Heavy chain fatty acid 2.80%
디옥틸 테레프탈레이트 2.30%Dioctyl terephthalate 2.30%
프로세스 오일 1.00%Process oil 1.00%
디에칠렌 글리콜 1.00%Diethylene glycol 1.00%
폴리에칠렌글리콜 100 1.40%Polyethylene glycol 100 1.40%
이소프로필 알코올 43.0%Isopropyl alcohol 43.0%
메탄올 15.7%Methanol 15.7%
상기 성분물질을 교반기에 넣고 120℃ 분위기에서 1시간 동안 교반하여 송진용액을 얻었다. 송진용액은 교반을 거듭할수록 연한 갈색의 점성물질로 변하였다.The ingredient material was placed in a stirrer and stirred for 1 hour in an atmosphere of 120 ° C to obtain a rosin solution. The rosin solution turned into a light brown viscous substance with stirring.
현탁액Suspension
송진용액 2.50%Songjin solution 2.50%
아교 3.00%glue 3.00%
수산화마그네슘 5.00%Magnesium hydroxide 5.00%
수산화나트륨 3.00%Sodium hydroxide 3.00%
염화칼슘 2.50%Calcium chloride 2.50%
염화은 0.50%Silver chloride 0.50%
제3 인산소다 1.50%Sodium tertiary phosphate 1.50%
암모니아 0.20%ammonia 0.20%
아미노메틸프로판올 0.05%Aminomethyl propanol 0.05%
아세톤 12.0%Acetone 12.0%
물 잔량water Balance
상기 성분물질을 교반기에 넣고 상온에서 1시간 동안 교반하여 연한 갈색의 현탁액을 얻었으며 pH는 8.6으로 측정되었다.The above material was placed in a stirrer and stirred at room temperature for 1 hour to obtain a pale brown suspension. The pH was measured to be 8.6.
난연성 접착제Flame retardant adhesive
현탁액 2.20%Suspension 2.20%
염화칼슘 42.8%Calcium chloride 42.8%
물 잔량water Balance
상기 성분물질을 교반기에서 20분간 교반하면서 염도 24‰가 되도록 조절하여 소망의 발포 폴리스타이렌 난연성 접착제 조성물을 얻었다.The above ingredients were stirred for 20 minutes in a stirrer to adjust the salt content to 24 ‰ to obtain a desired polystyrene flame retardant adhesive composition.
송진용액Songjin solution
99% 이상의 고순도 송진 32.8%99% or more high purity 32.8%
중쇄 지방산 2.80%Heavy chain fatty acid 2.80%
디옥틸 테레프탈레이트 2.30%Dioctyl terephthalate 2.30%
프로세스 오일 1.00%Process oil 1.00%
디에칠렌 글리콜 1.00%Diethylene glycol 1.00%
폴리에칠렌글리콜 100 1.40%Polyethylene glycol 100 1.40%
이소프로필 알코올 43.0%Isopropyl alcohol 43.0%
메탄올 15.7%Methanol 15.7%
상기 성분물질을 교반기에 넣고 120℃ 분위기에서 1시간 동안 교반하여 송진용액을 얻었다. 송진용액은 교반을 거듭할수록 연한 갈색의 점성물질로 변하였다.The ingredient material was placed in a stirrer and stirred for 1 hour in an atmosphere of 120 ° C to obtain a rosin solution. The rosin solution turned into a light brown viscous substance with stirring.
현탁액Suspension
송진용액 3.00%Songjin solution 3.00%
아교 3.60%glue 3.60%
수산화나트륨 9.00%Sodium hydroxide 9.00%
염화칼륨 2.50%Potassium chloride 2.50%
제3 인산소다 2.50%Sodium tertiary phosphate 2.50%
암모니아 0.20%ammonia 0.20%
아미노메틸프로판올 0.15%Aminomethyl propanol 0.15%
3-브로모-사이클로헥사논 13.0%3-Bromo-cyclohexanone 13.0%
물 잔량water Balance
상기 성분물질을 교반기에 넣고 상온에서 1시간 동안 교반하여 연한 갈색의 현탁액을 얻었으며 pH는 8.6으로 측정되었다.The above material was placed in a stirrer and stirred at room temperature for 1 hour to obtain a pale brown suspension. The pH was measured to be 8.6.
난연성 접착제Flame retardant adhesive
현탁액 2.20%Suspension 2.20%
황산칼슘 22.8%Calcium sulfate 22.8%
염화마그네슘 20.0%Magnesium chloride 20.0%
물 잔량water Balance
상기 성분물질을 교반기에서 20분간 교반하면서 염도 22‰가 되도록 조절하여 소망의 발포 폴리스타이렌 난연성 접착제 조성물을 얻었다.The component material was stirred for 20 minutes in a stirrer and adjusted to a saltiness of 22 ‰ to obtain a desired foam polystyrene flame retardant adhesive composition.
송진용액Songjin solution
99% 이상의 고순도 송진 26.8%99% or more high purity 26.8%
중쇄 지방산 1.90%Heavy chain fatty acid 1.90%
프로세스 오일 2.30%Process oil 2.30%
디에칠렌 글리콜 1.00%Diethylene glycol 1.00%
트리에칠렌 글리콜 0.50%Triethylene glycol 0.50%
이소프로필 알코올 48.5%Isopropyl alcohol 48.5%
메탄올 19.2%Methanol 19.2%
상기 성분물질을 교반기에 넣고 120℃ 분위기에서 1시간 동안 교반하여 연한 갈색의 점성물질로 된 송진용액을 얻었다.The ingredient materials were placed in a stirrer and stirred for 1 hour in an atmosphere of 120 ° C to obtain a pine rosin solution having a pale brown viscous substance.
현탁액Suspension
송진용액 1.00%Songjin solution 1.00%
아교 1.20%glue 1.20%
수산화나트륨 3.00%Sodium hydroxide 3.00%
수산화칼륨 2.00%Potassium hydroxide 2.00%
염화나트륨 1.00%Sodium chloride 1.00%
제3 인산소다 2.00%Sodium tertiary phosphate 2.00%
암모니아 0.10%ammonia 0.10%
아세톤 8.00%Acetone 8.00%
물 잔량water Balance
상기 성분물질을 교반기에 넣고 상온에서 1시간 동안 교반하여 연한 갈색의 현탁액을 얻었으며 pH는 8.5로 측정되었다.The above material was placed in a stirrer and stirred at room temperature for 1 hour to obtain a pale brown suspension and the pH was measured at 8.5.
난연성 접착제Flame retardant adhesive
현탁액 2.30%Suspension 2.30%
황산칼슘 25.8%Calcium sulfate 25.8%
염화마그네슘 19.4%Magnesium chloride 19.4%
물 잔량water Balance
상기 성분물질을 교반기에서 20분간 교반하면서 염도 24‰가 되도록 조절하여 소망의 발포 폴리스타이렌 난연성 접착제 조성물을 얻었다.The above ingredients were stirred for 20 minutes in a stirrer to adjust the salt content to 24 ‰ to obtain a desired polystyrene flame retardant adhesive composition.
송진용액Songjin solution
99% 이상의 고순도 송진 26.8%99% or more high purity 26.8%
중쇄 지방산 1.90%Heavy chain fatty acid 1.90%
프로세스 오일 2.30%Process oil 2.30%
디에칠렌 글리콜 1.00%Diethylene glycol 1.00%
트리에칠렌 글리콜 0.50%Triethylene glycol 0.50%
이소프로필 알코올 48.5%Isopropyl alcohol 48.5%
메탄올 19.2%Methanol 19.2%
상기 성분물질을 교반기에 넣고 115℃ 분위기에서 1시간 동안 교반하여 송진용액을 얻었다. 송진용액은 교반을 거듭할수록 연한 갈색의 점성물질로 변하였다.The ingredient material was placed in a stirrer and stirred in an atmosphere at 115 ° C for 1 hour to obtain a rosin solution. The rosin solution turned into a light brown viscous substance with stirring.
현탁액Suspension
송진용액 1.00%Songjin solution 1.00%
아교 1.20%glue 1.20%
수산화마그네슘 2.00%Magnesium hydroxide 2.00%
수산화칼륨 3.00%Potassium hydroxide 3.00%
염화나트륨 1.00%Sodium chloride 1.00%
제3 인산소다 2.00%Sodium tertiary phosphate 2.00%
암모니아 0.10%ammonia 0.10%
아세톤 8.00%Acetone 8.00%
물 잔량water Balance
상기 성분물질을 교반기에 넣고 상온에서 1시간 동안 교반하여 연한 갈색의 현탁액을 얻었으며 pH는 8.5로 측정되었다.The above material was placed in a stirrer and stirred at room temperature for 1 hour to obtain a pale brown suspension and the pH was measured at 8.5.
난연성 접착제Flame retardant adhesive
현탁액 2.50%Suspension 2.50%
염화칼슘 22.8%Calcium chloride 22.8%
염화마그네슘 24.3%Magnesium chloride 24.3%
물 잔량water Balance
상기 성분물질을 교반기에서 20분간 교반하면서 염도 23‰가 되도록 조절하여 소망의 발포 폴리스타이렌 난연성 접착제 조성물을 얻었다.The component material was stirred for 20 minutes in a stirrer to adjust the salt content to 23 ‰, thereby obtaining a desired foam polystyrene flame retardant adhesive composition.
송진용액Songjin solution
99% 이상의 고순도 송진 26.8%99% or more high purity 26.8%
중쇄 지방산 1.90%Heavy chain fatty acid 1.90%
디옥틸 테레프탈레이트 2.30%Dioctyl terephthalate 2.30%
디에칠렌 글리콜 1.00%Diethylene glycol 1.00%
폴리에칠렌글리콜 200 0.50%Polyethylene glycol 200 0.50%
이소프로필 알코올 40.0%Isopropyl alcohol 40.0%
메탄올 27.5%Methanol 27.5%
상기 성분물질을 교반기에 넣고 115℃ 분위기에서 1시간 동안 교반하여 송진용액을 얻었다. 송진용액은 교반을 거듭할수록 연한 갈색의 점성물질로 변하였다.The ingredient material was placed in a stirrer and stirred in an atmosphere at 115 ° C for 1 hour to obtain a rosin solution. The rosin solution turned into a light brown viscous substance with stirring.
현탁액Suspension
송진용액 1.00%Songjin solution 1.00%
아교 1.20%glue 1.20%
수산화나트륨 2.30%Sodium hydroxide 2.30%
수산화칼륨 2.70%Potassium hydroxide 2.70%
염화나트륨 1.00%Sodium chloride 1.00%
제3 인산소다 2.00%Sodium tertiary phosphate 2.00%
암모니아 0.10%ammonia 0.10%
아세톤 8.00%Acetone 8.00%
물 잔량water Balance
상기 성분물질을 교반기에 넣고 상온에서 1시간 동안 교반하여 연한 갈색의 현탁액을 얻었으며 pH는 8.5로 측정되었다.The above material was placed in a stirrer and stirred at room temperature for 1 hour to obtain a pale brown suspension and the pH was measured at 8.5.
난연성 접착제Flame retardant adhesive
현탁액 2.60%Suspension 2.60%
황산칼슘 20.0%Calcium sulfate 20.0%
염화마그네슘 29.0%Magnesium chloride 29.0%
물 잔량water Balance
상기 성분물질을 교반기에서 20분간 교반하면서 염도 24‰가 되도록 조절하여 소망의 발포 폴리스타이렌 난연성 접착제 조성물을 얻었다.The above ingredients were stirred for 20 minutes in a stirrer to adjust the salt content to 24 ‰ to obtain a desired polystyrene flame retardant adhesive composition.
송진용액Songjin solution
99% 이상의 고순도 송진 26.8%99% or more high purity 26.8%
중쇄 지방산 1.90%Heavy chain fatty acid 1.90%
프로세스 오일 2.30%Process oil 2.30%
디에칠렌 글리콜 0.50%Diethylene glycol 0.50%
트리에칠렌글리콜 0.50%Triethylene glycol 0.50%
폴리에칠렌글리콜 300 0.50%Polyethylene glycol 300 0.50%
이소프로필 알코올 44.5%Isopropyl alcohol 44.5%
메탄올 23.0%Methanol 23.0%
상기 성분물질을 교반기에 넣고 120℃ 분위기에서 1시간 동안 교반하여 연한 갈색의 점성물질로 된 송진용액을 얻었다.The ingredient materials were placed in a stirrer and stirred for 1 hour in an atmosphere of 120 ° C to obtain a pine rosin solution having a pale brown viscous substance.
현탁액Suspension
송진용액 1.00%Songjin solution 1.00%
아교 1.20%glue 1.20%
수산화나트륨 4.00%Sodium hydroxide 4.00%
수산화칼륨 1.00%Potassium hydroxide 1.00%
염화나트륨 1.00%Sodium chloride 1.00%
제3 인산소다 2.00%Sodium tertiary phosphate 2.00%
암모니아 0.10%ammonia 0.10%
아세톤 8.00%Acetone 8.00%
물 잔량water Balance
상기 성분물질을 교반기에 넣고 상온에서 1시간 동안 교반하여 연한 갈색의 현탁액을 얻었으며 pH는 8.5로 측정되었다.The above material was placed in a stirrer and stirred at room temperature for 1 hour to obtain a pale brown suspension and the pH was measured at 8.5.
난연성 접착제Flame retardant adhesive
현탁액 2.80%Suspension 2.80%
황산칼슘 32.0%Calcium sulfate 32.0%
염화마그네슘 20.2%Magnesium chloride 20.2%
물 잔량water Balance
상기 성분물질을 교반기에서 20분간 교반하면서 염도 25‰가 되도록 조절하여 소망의 발포 폴리스타이렌 난연성 접착제 조성물을 얻었다.The component material was stirred for 20 minutes in a stirrer to adjust the salt content to 25 ‰, thereby obtaining a desired foam polystyrene flame retardant adhesive composition.
송진용액Songjin solution
99% 이상의 고순도 송진 26.8%99% or more high purity 26.8%
중쇄 지방산 1.90%Heavy chain fatty acid 1.90%
프로세스 오일 2.30%Process oil 2.30%
디에칠렌 글리콜 1.00%Diethylene glycol 1.00%
트리에칠렌 글리콜 0.50%Triethylene glycol 0.50%
이소프로필 알코올 48.5%Isopropyl alcohol 48.5%
메탄올 19.2%Methanol 19.2%
상기 성분물질을 교반기에 넣고 120℃ 분위기에서 1시간 동안 교반하여 연한 갈색의 점성물질로 된 송진용액을 얻었다.The ingredient materials were placed in a stirrer and stirred for 1 hour in an atmosphere of 120 ° C to obtain a pine rosin solution having a pale brown viscous substance.
현탁액Suspension
송진용액 1.50%Songjin solution 1.50%
아교 1.80%glue 1.80%
수산화칼륨 4.00%Potassium hydroxide 4.00%
수산화마그네슘 2.00%Magnesium hydroxide 2.00%
염화나트륨 1.50%Sodium chloride 1.50%
제3 인산소다 2.00%Sodium tertiary phosphate 2.00%
암모니아 0.15%ammonia 0.15%
3-브로모-사이클로헥사논 9.00%3-Bromo-cyclohexanone 9.00%
물 잔량water Balance
상기 성분물질을 교반기에 넣고 상온에서 1시간 동안 교반하여 연한 갈색의 현탁액을 얻었으며 pH는 8.5로 측정되었다.The above material was placed in a stirrer and stirred at room temperature for 1 hour to obtain a pale brown suspension and the pH was measured at 8.5.
난연성 접착제Flame retardant adhesive
현탁액 2.30%Suspension 2.30%
황산칼슘 25.8%Calcium sulfate 25.8%
염화마그네슘 19.4%Magnesium chloride 19.4%
물 잔량water Balance
상기 성분물질을 교반기에서 20분간 교반하면서 염도 24‰가 되도록 조절하여 소망의 발포 폴리스타이렌 난연성 접착제 조성물을 얻었다.The above ingredients were stirred for 20 minutes in a stirrer to adjust the salt content to 24 ‰ to obtain a desired polystyrene flame retardant adhesive composition.
송진용액Songjin solution
99% 이상의 고순도 송진 26.8%99% or more high purity 26.8%
중쇄 지방산 1.90%Heavy chain fatty acid 1.90%
프로세스 오일 2.30%Process oil 2.30%
디에칠렌 글리콜 1.00%Diethylene glycol 1.00%
트리에칠렌 글리콜 0.50%Triethylene glycol 0.50%
이소프로필 알코올 48.5%Isopropyl alcohol 48.5%
메탄올 19.2%Methanol 19.2%
상기 성분물질을 교반기에 넣고 115℃ 분위기에서 1시간 동안 교반하여 송진용액을 얻었다. 송진용액은 교반을 거듭할수록 연한 갈색의 점성물질로 변하였다.The ingredient material was placed in a stirrer and stirred in an atmosphere at 115 ° C for 1 hour to obtain a rosin solution. The rosin solution turned into a light brown viscous substance with stirring.
현탁액Suspension
송진용액 1.50%Songjin solution 1.50%
아교 1.80%glue 1.80%
수산화나트륨 4.00%Sodium hydroxide 4.00%
수산화마그네슘 2.00%Magnesium hydroxide 2.00%
염화나트륨 1.50%Sodium chloride 1.50%
염화칼륨 2.00%Potassium chloride 2.00%
암모니아 0.15%ammonia 0.15%
3-브로모-사이클로헥사논 9.00%3-Bromo-cyclohexanone 9.00%
물 잔량water Balance
상기 성분물질을 교반기에 넣고 상온에서 1시간 동안 교반하여 연한 갈색의 현탁액을 얻었으며 pH는 8.6으로 측정되었다.The above material was placed in a stirrer and stirred at room temperature for 1 hour to obtain a pale brown suspension. The pH was measured to be 8.6.
난연성 접착제Flame retardant adhesive
현탁액 2.50%Suspension 2.50%
염화칼슘 22.8%Calcium chloride 22.8%
염화마그네슘 24.3%Magnesium chloride 24.3%
물 잔량water Balance
상기 성분물질을 교반기에서 20분간 교반하면서 염도 23‰가 되도록 조절하여 소망의 발포 폴리스타이렌 난연성 접착제 조성물을 얻었다.The component material was stirred for 20 minutes in a stirrer to adjust the salt content to 23 ‰, thereby obtaining a desired foam polystyrene flame retardant adhesive composition.
송진용액Songjin solution
99% 이상의 고순도 송진 26.8%99% or more high purity 26.8%
중쇄 지방산 1.90%Heavy chain fatty acid 1.90%
디옥틸 테레프탈레이트 2.30%Dioctyl terephthalate 2.30%
디에칠렌 글리콜 1.00%Diethylene glycol 1.00%
폴리에칠렌글리콜 200 0.50%Polyethylene glycol 200 0.50%
이소프로필 알코올 40.0%Isopropyl alcohol 40.0%
메탄올 27.5%Methanol 27.5%
상기 성분물질을 교반기에 넣고 115℃ 분위기에서 1시간 동안 교반하여 송진용액을 얻었다. 송진용액은 교반을 거듭할수록 연한 갈색의 점성물질로 변하였다.The ingredient material was placed in a stirrer and stirred in an atmosphere at 115 ° C for 1 hour to obtain a rosin solution. The rosin solution turned into a light brown viscous substance with stirring.
현탁액Suspension
송진용액 1.50%Songjin solution 1.50%
아교 1.80%glue 1.80%
수산화칼륨 2.00%Potassium hydroxide 2.00%
수산화마그네슘 4.00%Magnesium hydroxide 4.00%
염화구리 1.50%Copper chloride 1.50%
염화암모늄 2.00%Ammonium chloride 2.00%
트리메틸아민 0.15%Trimethylamine 0.15%
3-브로모-사이클로헥사논 9.00%3-Bromo-cyclohexanone 9.00%
물 잔량water Balance
상기 성분물질을 교반기에 넣고 상온에서 1시간 동안 교반하여 연한 갈색의 현탁액을 얻었으며 pH는 8.5로 측정되었다.The above material was placed in a stirrer and stirred at room temperature for 1 hour to obtain a pale brown suspension and the pH was measured at 8.5.
난연성 접착제Flame retardant adhesive
현탁액 2.60%Suspension 2.60%
황산칼슘 20.0%Calcium sulfate 20.0%
염화마그네슘 29.0%Magnesium chloride 29.0%
물 잔량water Balance
상기 성분물질을 교반기에서 20분간 교반하면서 염도 24‰가 되도록 조절하여 소망의 발포 폴리스타이렌 난연성 접착제 조성물을 얻었다.The above ingredients were stirred for 20 minutes in a stirrer to adjust the salt content to 24 ‰ to obtain a desired polystyrene flame retardant adhesive composition.
송진용액Songjin solution
99% 이상의 고순도 송진 26.8%99% or more high purity 26.8%
중쇄 지방산 1.90%Heavy chain fatty acid 1.90%
프로세스 오일 2.30%Process oil 2.30%
디에칠렌 글리콜 0.50%Diethylene glycol 0.50%
트리에칠렌글리콜 0.50%Triethylene glycol 0.50%
폴리에칠렌글리콜 300 0.50%Polyethylene glycol 300 0.50%
이소프로필 알코올 44.5%Isopropyl alcohol 44.5%
메탄올 23.0%Methanol 23.0%
상기 성분물질을 교반기에 넣고 120℃ 분위기에서 1시간 동안 교반하여 연한 갈색의 점성물질로 된 송진용액을 얻었다.The ingredient materials were placed in a stirrer and stirred for 1 hour in an atmosphere of 120 ° C to obtain a pine rosin solution having a pale brown viscous substance.
현탁액Suspension
송진용액 1.50%Songjin solution 1.50%
아교 1.80%glue 1.80%
수산화칼륨 2.00%Potassium hydroxide 2.00%
수산화마그네슘 4.00%Magnesium hydroxide 4.00%
염화구리 1.50%Copper chloride 1.50%
염화암모늄 2.00%Ammonium chloride 2.00%
트리메틸아민 0.15%Trimethylamine 0.15%
3-브로모-사이클로헥사논 9.00%3-Bromo-cyclohexanone 9.00%
물 잔량water Balance
상기 성분물질을 교반기에 넣고 상온에서 1시간 동안 교반하여 연한 갈색의 현탁액을 얻었으며 pH는 8.5로 측정되었다.The above material was placed in a stirrer and stirred at room temperature for 1 hour to obtain a pale brown suspension and the pH was measured at 8.5.
난연성 접착제Flame retardant adhesive
현탁액 2.80%Suspension 2.80%
황산칼슘 32.0%Calcium sulfate 32.0%
염화마그네슘 20.2%Magnesium chloride 20.2%
물 잔량water Balance
상기 성분물질을 교반기에서 20분간 교반하면서 염도 25‰가 되도록 조절하여 소망의 발포 폴리스타이렌 난연성 접착제 조성물을 얻었다.The component material was stirred for 20 minutes in a stirrer to adjust the salt content to 25 ‰, thereby obtaining a desired foam polystyrene flame retardant adhesive composition.
송진용액Songjin solution
99% 이상의 고순도 송진 26.8%99% or more high purity 26.8%
중쇄 지방산 1.90%Heavy chain fatty acid 1.90%
프로세스 오일 2.30%Process oil 2.30%
디에칠렌 글리콜 1.00%Diethylene glycol 1.00%
트리에칠렌 글리콜 0.50%Triethylene glycol 0.50%
이소프로필 알코올 48.5%Isopropyl alcohol 48.5%
메탄올 19.2%Methanol 19.2%
상기 성분물질을 교반기에 넣고 120℃ 분위기에서 1시간 동안 교반하여 연한 갈색의 점성물질로 된 송진용액을 얻었다.The ingredient materials were placed in a stirrer and stirred for 1 hour in an atmosphere of 120 ° C to obtain a pine rosin solution having a pale brown viscous substance.
현탁액Suspension
송진용액 2.00%Songjin solution 2.00%
아교 2.40%glue 2.40%
수산화칼륨 5.00%Potassium hydroxide 5.00%
수산화마그네슘 2.00%Magnesium hydroxide 2.00%
염화나트륨 2.00%Sodium chloride 2.00%
염화칼슘 2.00%Calcium chloride 2.00%
아미노메틸프로판올 0.20%Aminomethyl propanol 0.20%
헥산-3-원 10.0%Hexane-3-one 10.0%
물 잔량water Balance
상기 성분물질을 교반기에 넣고 상온에서 1시간 동안 교반하여 연한 갈색의 현탁액을 얻었으며 pH는 8.8로 측정되었다.The ingredients were placed in a stirrer and stirred at room temperature for 1 hour to obtain a pale brown suspension, pH 8.8.
난연성 접착제Flame retardant adhesive
현탁액 2.30%Suspension 2.30%
황산칼슘 25.8%Calcium sulfate 25.8%
염화마그네슘 19.4%Magnesium chloride 19.4%
물 잔량water Balance
상기 성분물질을 교반기에서 20분간 교반하면서 염도 24‰가 되도록 조절하여 소망의 발포 폴리스타이렌 난연성 접착제 조성물을 얻었다.The above ingredients were stirred for 20 minutes in a stirrer to adjust the salt content to 24 ‰ to obtain a desired polystyrene flame retardant adhesive composition.
송진용액Songjin solution
99% 이상의 고순도 송진 26.8%99% or more high purity 26.8%
중쇄 지방산 1.90%Heavy chain fatty acid 1.90%
프로세스 오일 2.30%Process oil 2.30%
디에칠렌 글리콜 1.00%Diethylene glycol 1.00%
트리에칠렌 글리콜 0.50%Triethylene glycol 0.50%
이소프로필 알코올 48.5%Isopropyl alcohol 48.5%
메탄올 19.0%Methanol 19.0%
상기 성분물질을 교반기에 넣고 115℃ 분위기에서 1시간 동안 교반하여 송진용액을 얻었다. 송진용액은 교반을 거듭할수록 연한 갈색의 점성물질로 변하였다.The ingredient material was placed in a stirrer and stirred in an atmosphere at 115 ° C for 1 hour to obtain a rosin solution. The rosin solution turned into a light brown viscous substance with stirring.
현탁액Suspension
송진용액 2.00%Songjin solution 2.00%
아교 2.40%glue 2.40%
수산화나트륨 5.00%Sodium hydroxide 5.00%
수산화마그네슘 2.00%Magnesium hydroxide 2.00%
염화나트륨 2.00%Sodium chloride 2.00%
염화은 1.00%Silver chloride 1.00%
염화암모늄 1.00%Ammonium chloride 1.00%
아미노메틸프로판올 0.20%Aminomethyl propanol 0.20%
헥산-3-원 10.0%Hexane-3-one 10.0%
물 잔량water Balance
상기 성분물질을 교반기에 넣고 상온에서 1시간 동안 교반하여 연한 갈색의 현탁액을 얻었으며 pH는 8.8로 측정되었다.The ingredients were placed in a stirrer and stirred at room temperature for 1 hour to obtain a pale brown suspension, pH 8.8.
난연성 접착제Flame retardant adhesive
현탁액 2.50%Suspension 2.50%
염화칼슘 22.8%Calcium chloride 22.8%
염화마그네슘 24.3%Magnesium chloride 24.3%
물 잔량water Balance
상기 성분물질을 교반기에서 20분간 교반하면서 염도 23‰가 되도록 조절하여 소망의 발포 폴리스타이렌 난연성 접착제 조성물을 얻었다.The component material was stirred for 20 minutes in a stirrer to adjust the salt content to 23 ‰, thereby obtaining a desired foam polystyrene flame retardant adhesive composition.
송진용액Songjin solution
99% 이상의 고순도 송진 26.8%99% or more high purity 26.8%
중쇄 지방산 1.90%Heavy chain fatty acid 1.90%
디옥틸 테레프탈레이트 2.30%Dioctyl terephthalate 2.30%
디에칠렌 글리콜 1.00%Diethylene glycol 1.00%
폴리에칠렌글리콜 200 0.50%Polyethylene glycol 200 0.50%
이소프로필 알코올 40.0%Isopropyl alcohol 40.0%
메탄올 27.5%Methanol 27.5%
상기 성분물질을 교반기에 넣고 115℃ 분위기에서 1시간 동안 교반하여 송진용액을 얻었다. 송진용액은 교반을 거듭할수록 연한 갈색의 점성물질로 변하였다.The ingredient material was placed in a stirrer and stirred in an atmosphere at 115 ° C for 1 hour to obtain a rosin solution. The rosin solution turned into a light brown viscous substance with stirring.
현탁액Suspension
송진용액 2.00%Songjin solution 2.00%
아교 2.40%glue 2.40%
수산화나트륨 4.00%Sodium hydroxide 4.00%
수산화마그네슘 3.00%Magnesium hydroxide 3.00%
염화나트륨 1.00%Sodium chloride 1.00%
염화은 0.50%Silver chloride 0.50%
염화암모늄 2.50%Ammonium chloride 2.50%
트리메틸아민 0.20%Trimethylamine 0.20%
헥산-3-원 10.0%Hexane-3-one 10.0%
물 잔량water Balance
상기 성분물질을 교반기에 넣고 상온에서 1시간 동안 교반하여 연한 갈색의 현탁액을 얻었으며 pH는 8.6로 측정되었다.The above ingredients were placed in a stirrer and stirred at room temperature for 1 hour to obtain a pale brown suspension and the pH was measured to be 8.6.
난연성 접착제Flame retardant adhesive
현탁액 2.60%Suspension 2.60%
황산칼슘 20.0%Calcium sulfate 20.0%
염화마그네슘 29.0%Magnesium chloride 29.0%
물 잔량water Balance
상기 성분물질을 교반기에서 20분간 교반하면서 염도 24‰가 되도록 조절하여 소망의 발포 폴리스타이렌 난연성 접착제 조성물을 얻었다.The above ingredients were stirred for 20 minutes in a stirrer to adjust the salt content to 24 ‰ to obtain a desired polystyrene flame retardant adhesive composition.
송진용액Songjin solution
99% 이상의 고순도 송진 26.8%99% or more high purity 26.8%
중쇄 지방산 1.90%Heavy chain fatty acid 1.90%
프로세스 오일 2.30%Process oil 2.30%
디에칠렌 글리콜 0.50%Diethylene glycol 0.50%
트리에칠렌글리콜 0.50%Triethylene glycol 0.50%
폴리에칠렌글리콜 300 0.50%Polyethylene glycol 300 0.50%
이소프로필 알코올 44.5%Isopropyl alcohol 44.5%
메탄올 23.0%Methanol 23.0%
상기 성분물질을 교반기에 넣고 120℃ 분위기에서 1시간 동안 교반하여 연한 갈색의 점성물질로 된 송진용액을 얻었다.The ingredient materials were placed in a stirrer and stirred for 1 hour in an atmosphere of 120 ° C to obtain a pine rosin solution having a pale brown viscous substance.
현탁액Suspension
송진용액 2.00%Songjin solution 2.00%
아교 2.40%glue 2.40%
수산화나트륨 4.00%Sodium hydroxide 4.00%
수산화마그네슘 3.00%Magnesium hydroxide 3.00%
염화나트륨 1.00%Sodium chloride 1.00%
염화은 0.50%Silver chloride 0.50%
염화암모늄 2.50%Ammonium chloride 2.50%
트리메틸아민 0.20%Trimethylamine 0.20%
헥산-3-원 10.0%Hexane-3-one 10.0%
물 잔량water Balance
상기 성분물질을 교반기에 넣고 상온에서 1시간 동안 교반하여 연한 갈색의 현탁액을 얻었으며 pH는 8.9로 측정되었다.The above material was placed in a stirrer and stirred at room temperature for 1 hour to obtain a pale brown suspension. The pH was measured to be 8.9.
난연성 접착제Flame retardant adhesive
현탁액 2.60%Suspension 2.60%
황산칼슘 20.0%Calcium sulfate 20.0%
염화마그네슘 29.0%Magnesium chloride 29.0%
물 잔량water Balance
상기 성분물질을 교반기에서 20분간 교반하면서 염도 24‰가 되도록 조절하여 소망의 발포 폴리스타이렌 난연성 접착제 조성물을 얻었다.The above ingredients were stirred for 20 minutes in a stirrer to adjust the salt content to 24 ‰ to obtain a desired polystyrene flame retardant adhesive composition.
송진용액Songjin solution
99% 이상의 고순도 송진 26.8%99% or more high purity 26.8%
중쇄 지방산 1.90%Heavy chain fatty acid 1.90%
프로세스 오일 2.30%Process oil 2.30%
디에칠렌 글리콜 1.00%Diethylene glycol 1.00%
트리에칠렌 글리콜 0.50%Triethylene glycol 0.50%
이소프로필 알코올 48.5%Isopropyl alcohol 48.5%
메탄올 19.0%Methanol 19.0%
상기 성분물질을 교반기에 넣고 120℃ 분위기에서 1시간 동안 교반하여 연한 갈색의 점성물질로 된 송진용액을 얻었다.The ingredient materials were placed in a stirrer and stirred for 1 hour in an atmosphere of 120 ° C to obtain a pine rosin solution having a pale brown viscous substance.
현탁액Suspension
송진용액 2.50%Songjin solution 2.50%
아교 3.00%glue 3.00%
수산화나트륨 3.00%Sodium hydroxide 3.00%
수산화칼륨 5.00%Potassium hydroxide 5.00%
염화나트륨 1.00%Sodium chloride 1.00%
염화구리 1.50%Copper chloride 1.50%
제3 인산소다 2.00%Sodium tertiary phosphate 2.00%
암모니아 0.10%ammonia 0.10%
트리메틸아민 0.15%Trimethylamine 0.15%
아세톤 11.0%Acetone 11.0%
물 잔량water Balance
상기 성분물질을 교반기에 넣고 상온에서 1시간 동안 교반하여 연한 갈색의 현탁액을 얻었으며 pH는 8.8로 측정되었다.The ingredients were placed in a stirrer and stirred at room temperature for 1 hour to obtain a pale brown suspension, pH 8.8.
난연성 접착제Flame retardant adhesive
현탁액 2.30%Suspension 2.30%
황산칼슘 25.8%Calcium sulfate 25.8%
염화마그네슘 19.4%Magnesium chloride 19.4%
물 잔량water Balance
상기 성분물질을 교반기에서 20분간 교반하면서 염도 24‰가 되도록 조절하여 소망의 발포 폴리스타이렌 난연성 접착제 조성물을 얻었다.The above ingredients were stirred for 20 minutes in a stirrer to adjust the salt content to 24 ‰ to obtain a desired polystyrene flame retardant adhesive composition.
송진용액Songjin solution
99% 이상의 고순도 송진 26.8%99% or more high purity 26.8%
중쇄 지방산 1.90%Heavy chain fatty acid 1.90%
프로세스 오일 2.30%Process oil 2.30%
디에칠렌 글리콜 1.00%Diethylene glycol 1.00%
트리에칠렌 글리콜 0.50%Triethylene glycol 0.50%
이소프로필 알코올 48.5%Isopropyl alcohol 48.5%
메탄올 19.0%Methanol 19.0%
상기 성분물질을 교반기에 넣고 115℃ 분위기에서 1시간 동안 교반하여 송진용액을 얻었다. 송진용액은 교반을 거듭할수록 연한 갈색의 점성물질로 변하였다.The ingredient material was placed in a stirrer and stirred in an atmosphere at 115 ° C for 1 hour to obtain a rosin solution. The rosin solution turned into a light brown viscous substance with stirring.
현탁액Suspension
송진용액 2.50%Songjin solution 2.50%
아교 3.00%glue 3.00%
수산화마그네슘 2.00%Magnesium hydroxide 2.00%
수산화나트륨 6.00%Sodium hydroxide 6.00%
염화칼륨 1.50%Potassium chloride 1.50%
염화은 1.50%Silver chloride 1.50%
제3 인산소다 1.50%Sodium tertiary phosphate 1.50%
암모니아 0.15%ammonia 0.15%
아미노메틸프로판올 0.10%Aminomethyl propanol 0.10%
아세톤 11.0%Acetone 11.0%
물 잔량water Balance
상기 성분물질을 교반기에 넣고 상온에서 1시간 동안 교반하여 연한 갈색의 현탁액을 얻었으며 pH는 8.5로 측정되었다.The above material was placed in a stirrer and stirred at room temperature for 1 hour to obtain a pale brown suspension and the pH was measured at 8.5.
난연성 접착제Flame retardant adhesive
현탁액 2.50%Suspension 2.50%
염화칼슘 22.8%Calcium chloride 22.8%
염화마그네슘 24.3%Magnesium chloride 24.3%
물 잔량water Balance
상기 성분물질을 교반기에서 20분간 교반하면서 염도 23‰가 되도록 조절하여 소망의 발포 폴리스타이렌 난연성 접착제 조성물을 얻었다.The component material was stirred for 20 minutes in a stirrer to adjust the salt content to 23 ‰, thereby obtaining a desired foam polystyrene flame retardant adhesive composition.
송진용액Songjin solution
99% 이상의 고순도 송진 26.8%99% or more high purity 26.8%
중쇄 지방산 1.90%Heavy chain fatty acid 1.90%
디옥틸 테레프탈레이트 2.30%Dioctyl terephthalate 2.30%
디에칠렌 글리콜 1.00%Diethylene glycol 1.00%
폴리에칠렌글리콜 200 0.50%Polyethylene glycol 200 0.50%
이소프로필 알코올 40.0%Isopropyl alcohol 40.0%
메탄올 27.5%Methanol 27.5%
상기 성분물질을 교반기에 넣고 115℃ 분위기에서 1시간 동안 교반하여 송진용액을 얻었다. 송진용액은 교반을 거듭할수록 연한 갈색의 점성물질로 변하였다.The ingredient material was placed in a stirrer and stirred in an atmosphere at 115 ° C for 1 hour to obtain a rosin solution. The rosin solution turned into a light brown viscous substance with stirring.
현탁액Suspension
송진용액 2.50%Songjin solution 2.50%
아교 3.00%glue 3.00%
수산화마그네슘 5.00%Magnesium hydroxide 5.00%
수산화나트륨 3.00%Sodium hydroxide 3.00%
염화칼슘 2.50%Calcium chloride 2.50%
염화은 0.50%Silver chloride 0.50%
제3 인산소다 1.50%Sodium tertiary phosphate 1.50%
암모니아 0.20%ammonia 0.20%
아미노메틸프로판올 0.05%Aminomethyl propanol 0.05%
아세톤 12.0%Acetone 12.0%
물 잔량water Balance
상기 성분물질을 교반기에 넣고 상온에서 1시간 동안 교반하여 연한 갈색의 현탁액을 얻었으며 pH는 8.8로 측정되었다.The ingredients were placed in a stirrer and stirred at room temperature for 1 hour to obtain a pale brown suspension, pH 8.8.
난연성 접착제Flame retardant adhesive
현탁액 2.60%Suspension 2.60%
황산칼슘 20.0%Calcium sulfate 20.0%
염화마그네슘 29.0%Magnesium chloride 29.0%
물 잔량water Balance
상기 성분물질을 교반기에서 20분간 교반하면서 염도 24‰가 되도록 조절하여 소망의 발포 폴리스타이렌 난연성 접착제 조성물을 얻었다.The above ingredients were stirred for 20 minutes in a stirrer to adjust the salt content to 24 ‰ to obtain a desired polystyrene flame retardant adhesive composition.
송진용액Songjin solution
99% 이상의 고순도 송진 26.8%99% or more high purity 26.8%
중쇄 지방산 1.90%Heavy chain fatty acid 1.90%
프로세스 오일 2.30%Process oil 2.30%
디에칠렌 글리콜 0.50%Diethylene glycol 0.50%
트리에칠렌글리콜 0.50%Triethylene glycol 0.50%
폴리에칠렌글리콜 300 0.50%Polyethylene glycol 300 0.50%
이소프로필 알코올 44.5%Isopropyl alcohol 44.5%
메탄올 23.0%Methanol 23.0%
상기 성분물질을 교반기에 넣고 120℃ 분위기에서 1시간 동안 교반하여 연한 갈색의 점성물질로 된 송진용액을 얻었다.The ingredient materials were placed in a stirrer and stirred for 1 hour in an atmosphere of 120 ° C to obtain a pine rosin solution having a pale brown viscous substance.
현탁액Suspension
송진용액 2.50%Songjin solution 2.50%
아교 3.00%glue 3.00%
수산화마그네슘 5.00%Magnesium hydroxide 5.00%
수산화나트륨 3.00%Sodium hydroxide 3.00%
염화칼슘 2.50%Calcium chloride 2.50%
염화은 0.50%Silver chloride 0.50%
제3 인산소다 1.50%Sodium tertiary phosphate 1.50%
암모니아 0.20%ammonia 0.20%
아미노메틸프로판올 0.05%Aminomethyl propanol 0.05%
아세톤 12.0%Acetone 12.0%
물 잔량water Balance
상기 성분물질을 교반기에 넣고 상온에서 1시간 동안 교반하여 연한 갈색의 현탁액을 얻었으며 pH는 8.6으로 측정되었다.The above material was placed in a stirrer and stirred at room temperature for 1 hour to obtain a pale brown suspension. The pH was measured to be 8.6.
난연성 접착제Flame retardant adhesive
현탁액 2.60%Suspension 2.60%
황산칼슘 20.0%Calcium sulfate 20.0%
염화마그네슘 29.0%Magnesium chloride 29.0%
물 잔량water Balance
상기 성분물질을 교반기에서 20분간 교반하면서 염도 24‰가 되도록 조절하여 소망의 발포 폴리스타이렌 난연성 접착제 조성물을 얻었다.The above ingredients were stirred for 20 minutes in a stirrer to adjust the salt content to 24 ‰ to obtain a desired polystyrene flame retardant adhesive composition.
송진용액Songjin solution
99% 이상의 고순도 송진 26.8%99% or more high purity 26.8%
중쇄 지방산 1.90%Heavy chain fatty acid 1.90%
프로세스 오일 2.30%Process oil 2.30%
디에칠렌 글리콜 1.00%Diethylene glycol 1.00%
트리에칠렌 글리콜 0.50%Triethylene glycol 0.50%
이소프로필 알코올 48.5%Isopropyl alcohol 48.5%
메탄올 19.2%Methanol 19.2%
상기 성분물질을 교반기에 넣고 120℃ 분위기에서 1시간 동안 교반하여 연한 갈색의 점성물질로 된 송진용액을 얻었다.The ingredient materials were placed in a stirrer and stirred for 1 hour in an atmosphere of 120 ° C to obtain a pine rosin solution having a pale brown viscous substance.
현탁액Suspension
송진용액 2.50%Songjin solution 2.50%
아교 3.00%glue 3.00%
수산화나트륨 3.00%Sodium hydroxide 3.00%
수산화칼륨 5.00%Potassium hydroxide 5.00%
염화나트륨 1.00%Sodium chloride 1.00%
염화구리 1.50%Copper chloride 1.50%
제3 인산소다 2.00%Sodium tertiary phosphate 2.00%
암모니아 0.10%ammonia 0.10%
트리메틸아민 0.15%Trimethylamine 0.15%
3-브로모-사이클로헥사논 11.0%3-Bromo-cyclohexanone 11.0%
물 잔량water Balance
상기 성분물질을 교반기에 넣고 상온에서 1시간 동안 교반하여 연한 갈색의 현탁액을 얻었으며 pH는 8.8로 측정되었다.The ingredients were placed in a stirrer and stirred at room temperature for 1 hour to obtain a pale brown suspension, pH 8.8.
난연성 접착제Flame retardant adhesive
현탁액 2.30%Suspension 2.30%
황산칼슘 25.8%Calcium sulfate 25.8%
염화마그네슘 19.4%Magnesium chloride 19.4%
물 잔량water Balance
상기 성분물질을 교반기에서 20분간 교반하면서 염도 24‰가 되도록 조절하여 소망의 발포 폴리스타이렌 난연성 접착제 조성물을 얻었다.The above ingredients were stirred for 20 minutes in a stirrer to adjust the salt content to 24 ‰ to obtain a desired polystyrene flame retardant adhesive composition.
송진용액Songjin solution
99% 이상의 고순도 송진 26.8%99% or more high purity 26.8%
중쇄 지방산 1.90%Heavy chain fatty acid 1.90%
프로세스 오일 2.30%Process oil 2.30%
디에칠렌 글리콜 1.00%Diethylene glycol 1.00%
트리에칠렌 글리콜 0.50%Triethylene glycol 0.50%
이소프로필 알코올 48.5%Isopropyl alcohol 48.5%
메탄올 19.2%Methanol 19.2%
상기 성분물질을 교반기에 넣고 115℃ 분위기에서 1시간 동안 교반하여 송진용액을 얻었다. 송진용액은 교반을 거듭할수록 연한 갈색의 점성물질로 변하였다.The ingredient material was placed in a stirrer and stirred in an atmosphere at 115 ° C for 1 hour to obtain a rosin solution. The rosin solution turned into a light brown viscous substance with stirring.
현탁액Suspension
송진용액 3.00%Songjin solution 3.00%
아교 3.60%glue 3.60%
수산화나트륨 3.00%Sodium hydroxide 3.00%
수산화칼슘 3.00%Calcium hydroxide 3.00%
수산화마그네슘 3.00%Magnesium hydroxide 3.00%
염화나트륨 1.00%Sodium chloride 1.00%
염화칼슘 1.00%Calcium chloride 1.00%
염화암모늄 1.00%Ammonium chloride 1.00%
염화수은 2.00%Mercury chloride 2.00%
암모니아 0.10%ammonia 0.10%
아미노메틸프로판올 0.20%Aminomethyl propanol 0.20%
3-브로모-사이클로헥사논 12.0%3-Bromo-cyclohexanone 12.0%
물 잔량water Balance
상기 성분물질을 교반기에 넣고 상온에서 1시간 동안 교반하여 연한 갈색의 현탁액을 얻었으며 pH는 8.9로 측정되었다.The above material was placed in a stirrer and stirred at room temperature for 1 hour to obtain a pale brown suspension. The pH was measured to be 8.9.
난연성 접착제Flame retardant adhesive
현탁액 2.50%Suspension 2.50%
염화칼슘 22.8%Calcium chloride 22.8%
염화마그네슘 24.3%Magnesium chloride 24.3%
물 잔량water Balance
상기 성분물질을 교반기에서 20분간 교반하면서 염도 23‰가 되도록 조절하여 소망의 발포 폴리스타이렌 난연성 접착제 조성물을 얻었다.The component material was stirred for 20 minutes in a stirrer to adjust the salt content to 23 ‰, thereby obtaining a desired foam polystyrene flame retardant adhesive composition.
송진용액Songjin solution
99% 이상의 고순도 송진 26.8%99% or more high purity 26.8%
중쇄 지방산 1.90%Heavy chain fatty acid 1.90%
디옥틸 테레프탈레이트 2.30%Dioctyl terephthalate 2.30%
디에칠렌 글리콜 1.00%Diethylene glycol 1.00%
폴리에칠렌글리콜 200 0.50%Polyethylene glycol 200 0.50%
이소프로필 알코올 40.0%Isopropyl alcohol 40.0%
메탄올 27.5%Methanol 27.5%
상기 성분물질을 교반기에 넣고 115℃ 분위기에서 1시간 동안 교반하여 송진용액을 얻었다. 송진용액은 교반을 거듭할수록 연한 갈색의 점성물질로 변하였다.The ingredient material was placed in a stirrer and stirred in an atmosphere at 115 ° C for 1 hour to obtain a rosin solution. The rosin solution turned into a light brown viscous substance with stirring.
현탁액Suspension
송진용액 3.00%Songjin solution 3.00%
아교 3.60%glue 3.60%
수산화나트륨 3.00%Sodium hydroxide 3.00%
수산화칼륨 3.00%Potassium hydroxide 3.00%
수산화마그네슘 3.00%Magnesium hydroxide 3.00%
염화나트륨 1.00%Sodium chloride 1.00%
제3 인산소다 2.00%Sodium tertiary phosphate 2.00%
염화수은 2.00%Mercury chloride 2.00%
암모니아 0.10%ammonia 0.10%
아미노메틸프로판올 0.10%Aminomethyl propanol 0.10%
트리메틸아민 0.10%Trimethylamine 0.10%
3-브로모-사이클로헥사논 13.0%3-Bromo-cyclohexanone 13.0%
물 잔량water Balance
상기 성분물질을 교반기에 넣고 상온에서 1시간 동안 교반하여 연한 갈색의 현탁액을 얻었으며 pH는 8.9로 측정되었다.The above material was placed in a stirrer and stirred at room temperature for 1 hour to obtain a pale brown suspension. The pH was measured to be 8.9.
난연성 접착제Flame retardant adhesive
현탁액 2.60%Suspension 2.60%
황산칼슘 20.0%Calcium sulfate 20.0%
염화마그네슘 29.0%Magnesium chloride 29.0%
물 잔량water Balance
상기 성분물질을 교반기에서 20분간 교반하면서 염도 24‰가 되도록 조절하여 소망의 발포 폴리스타이렌 난연성 접착제 조성물을 얻었다.The above ingredients were stirred for 20 minutes in a stirrer to adjust the salt content to 24 ‰ to obtain a desired polystyrene flame retardant adhesive composition.
송진용액Songjin solution
99% 이상의 고순도 송진 26.8%99% or more high purity 26.8%
중쇄 지방산 1.90%Heavy chain fatty acid 1.90%
프로세스 오일 2.30%Process oil 2.30%
디에칠렌 글리콜 0.50%Diethylene glycol 0.50%
트리에칠렌글리콜 0.50%Triethylene glycol 0.50%
폴리에칠렌글리콜 300 0.50%Polyethylene glycol 300 0.50%
이소프로필 알코올 44.5%Isopropyl alcohol 44.5%
메탄올 23.0%Methanol 23.0%
상기 성분물질을 교반기에 넣고 120℃ 분위기에서 1시간 동안 교반하여 연한 갈색의 점성물질로 된 송진용액을 얻었다.The ingredient materials were placed in a stirrer and stirred for 1 hour in an atmosphere of 120 ° C to obtain a pine rosin solution having a pale brown viscous substance.
현탁액Suspension
송진용액 3.00%Songjin solution 3.00%
아교 3.60%glue 3.60%
수산화나트륨 3.00%Sodium hydroxide 3.00%
수산화칼륨 3.00%Potassium hydroxide 3.00%
수산화마그네슘 3.00%Magnesium hydroxide 3.00%
염화나트륨 1.00%Sodium chloride 1.00%
제3 인산소다 2.00%Sodium tertiary phosphate 2.00%
염화수은 2.00%Mercury chloride 2.00%
암모니아 0.10%ammonia 0.10%
아미노메틸프로판올 0.10%Aminomethyl propanol 0.10%
트리메틸아민 0.10%Trimethylamine 0.10%
3-브로모-사이클로헥사논 12.0%3-Bromo-cyclohexanone 12.0%
물 잔량water Balance
상기 성분물질을 교반기에 넣고 상온에서 1시간 동안 교반하여 연한 갈색의 현탁액을 얻었으며 pH는 8.8로 측정되었다.The ingredients were placed in a stirrer and stirred at room temperature for 1 hour to obtain a pale brown suspension, pH 8.8.
난연성 접착제Flame retardant adhesive
현탁액 2.60%Suspension 2.60%
황산칼슘 20.0%Calcium sulfate 20.0%
염화마그네슘 29.0%Magnesium chloride 29.0%
물 잔량water Balance
상기 성분물질을 교반기에서 20분간 교반하면서 염도 24‰가 되도록 조절하여 소망의 발포 폴리스타이렌 난연성 접착제 조성물을 얻었다.The above ingredients were stirred for 20 minutes in a stirrer to adjust the salt content to 24 ‰ to obtain a desired polystyrene flame retardant adhesive composition.
송진용액Songjin solution
99% 이상의 고순도 송진 28.3%99% or more high purity 28.3%
중쇄 지방산 2.10%Heavy chain fatty acid 2.10%
프로세스 오일 2.60%Process oil 2.60%
디에칠렌 글리콜 1.00%Diethylene glycol 1.00%
폴리에칠렌글리콜 200 0.70%Polyethylene glycol 200 0.70%
이소프로필 알코올 42.3%Isopropyl alcohol 42.3%
메탄올 23.0%Methanol 23.0%
상기 성분물질을 교반기에 넣고 115℃ 분위기에서 1시간 동안 교반하여 연한 갈색의 점성물질로 된 송진용액을 얻었다.The ingredient material was placed in a stirrer and stirred at 115 ° C for 1 hour to obtain a pine rosin solution of a pale brown viscous substance.
현탁액Suspension
송진용액 1.00%Songjin solution 1.00%
아교 1.20%glue 1.20%
수산화나트륨 3.00%Sodium hydroxide 3.00%
수산화칼륨 2.00%Potassium hydroxide 2.00%
염화나트륨 1.00%Sodium chloride 1.00%
제3 인산소다 2.00%Sodium tertiary phosphate 2.00%
암모니아 0.10%ammonia 0.10%
아세톤 8.00%Acetone 8.00%
물 잔량water Balance
상기 성분물질을 교반기에 넣고 상온에서 1시간 동안 교반하여 연한 갈색의 현탁액을 얻었으며 pH는 8.5로 측정되었다.The above material was placed in a stirrer and stirred at room temperature for 1 hour to obtain a pale brown suspension and the pH was measured at 8.5.
난연성 접착제Flame retardant adhesive
현탁액 2.30%Suspension 2.30%
황산칼슘 25.8%Calcium sulfate 25.8%
염화마그네슘 19.4%Magnesium chloride 19.4%
물 잔량water Balance
상기 성분물질을 교반기에서 20분간 교반하면서 염도 24‰가 되도록 조절하여 소망의 발포 폴리스타이렌 난연성 접착제 조성물을 얻었다.The above ingredients were stirred for 20 minutes in a stirrer to adjust the salt content to 24 ‰ to obtain a desired polystyrene flame retardant adhesive composition.
송진용액Songjin solution
99% 이상의 고순도 송진 28.3%99% or more high purity 28.3%
중쇄 지방산 2.10%Heavy chain fatty acid 2.10%
디옥틸텔레프탈레이트 2.60%Dioctyl terephthalate 2.60%
폴리에칠렌글리콜 100 1.00%Polyethylene glycol 100 1.00%
폴리에칠렌글리콜 300 0.70%Polyethylene glycol 300 0.70%
이소프로필 알코올 42.3%Isopropyl alcohol 42.3%
메탄올 23.0%Methanol 23.0%
상기 성분물질을 교반기에 넣고 130℃ 분위기에서 1시간 30분 동안 교반하여 송진용액을 얻었다. 얻어진 송진용액은 교반을 거듭할수록 연한 갈색의 점성용액으로 변하였다.The ingredient material was placed in a stirrer and stirred at 130 ° C for 1 hour and 30 minutes to obtain a rosin solution. The resulting rosin solution turned into a light brown viscous solution with stirring.
현탁액Suspension
송진용액 1.00%Songjin solution 1.00%
아교 1.20%glue 1.20%
수산화마그네슘 2.00%Magnesium hydroxide 2.00%
수산화칼륨 3.00%Potassium hydroxide 3.00%
염화나트륨 1.00%Sodium chloride 1.00%
제3 인산소다 2.00%Sodium tertiary phosphate 2.00%
암모니아 0.10%ammonia 0.10%
아세톤 8.00%Acetone 8.00%
물 잔량water Balance
상기 성분물질을 교반기에 넣고 상온에서 1시간 동안 교반하여 연한 갈색의 현탁액을 얻었으며 pH는 8.5로 측정되었다.The above material was placed in a stirrer and stirred at room temperature for 1 hour to obtain a pale brown suspension and the pH was measured at 8.5.
난연성 접착제Flame retardant adhesive
현탁액 2.50%Suspension 2.50%
염화칼슘 22.8%Calcium chloride 22.8%
염화마그네슘 24.3%Magnesium chloride 24.3%
물 잔량water Balance
상기 성분물질을 교반기에서 20분간 교반하면서 염도 23‰가 되도록 조절하여 소망의 발포 폴리스타이렌 난연성 접착제 조성물을 얻었다.The component material was stirred for 20 minutes in a stirrer to adjust the salt content to 23 ‰, thereby obtaining a desired foam polystyrene flame retardant adhesive composition.
송진용액Songjin solution
99% 이상의 고순도 송진 28.3%99% or more high purity 28.3%
중쇄 지방산 2.10%Heavy chain fatty acid 2.10%
프로세스 오일 1.30%Process oil 1.30%
디옥틸텔레프탈레이트 1.30%Dioctyl terephthalate 1.30%
디에칠렌 글리콜 0.50%Diethylene glycol 0.50%
폴리에칠렌글리콜 200 0.50%Polyethylene glycol 200 0.50%
폴리에칠렌글리콜 300 0.70%Polyethylene glycol 300 0.70%
이소프로필 알코올 42.3%Isopropyl alcohol 42.3%
메탄올 23.0%Methanol 23.0%
상기 성분물질을 교반기에 넣고 115℃ 분위기에서 1시간 동안 교반하여 연한 갈색을 띈 점성물질로 된 송진용액을 얻었다.The ingredient material was placed in a stirrer and stirred at 115 ° C for 1 hour to obtain a pine rosin solution with a pale brownish viscous substance.
현탁액Suspension
송진용액 1.00%Songjin solution 1.00%
아교 1.20%glue 1.20%
수산화나트륨 2.30%Sodium hydroxide 2.30%
수산화칼륨 2.70%Potassium hydroxide 2.70%
염화나트륨 1.00%Sodium chloride 1.00%
제3 인산소다 2.00%Sodium tertiary phosphate 2.00%
암모니아 0.10%ammonia 0.10%
아세톤 8.00%Acetone 8.00%
물 잔량water Balance
상기 성분물질을 교반기에 넣고 상온에서 1시간 동안 교반하여 연한 갈색의 현탁액을 얻었으며 pH는 8.5로 측정되었다.The above material was placed in a stirrer and stirred at room temperature for 1 hour to obtain a pale brown suspension and the pH was measured at 8.5.
난연성 접착제Flame retardant adhesive
현탁액 2.60%Suspension 2.60%
황산칼슘 20.0%Calcium sulfate 20.0%
염화마그네슘 29.0%Magnesium chloride 29.0%
물 잔량water Balance
상기 성분물질을 교반기에서 20분간 교반하면서 염도 24‰가 되도록 조절하여 소망의 발포 폴리스타이렌 난연성 접착제 조성물을 얻었다.The above ingredients were stirred for 20 minutes in a stirrer to adjust the salt content to 24 ‰ to obtain a desired polystyrene flame retardant adhesive composition.
송진용액Songjin solution
99% 이상의 고순도 송진 28.3%99% or more high purity 28.3%
중쇄 지방산 2.10%Heavy chain fatty acid 2.10%
디옥틸텔레프탈레이트 2.60%Dioctyl terephthalate 2.60%
트리에칠렌글리콜 1.00%Triethylene glycol 1.00%
폴리에칠렌글리콜 200 0.70%Polyethylene glycol 200 0.70%
이소프로필 알코올 42.3%Isopropyl alcohol 42.3%
메탄올 23.0%Methanol 23.0%
상기 성분물질을 교반기에 넣고 115℃ 분위기에서 1시간 동안 교반하여 연한 갈색을 띈 점성물질로 된 송진용액을 얻었다.The ingredient material was placed in a stirrer and stirred at 115 ° C for 1 hour to obtain a pine rosin solution with a pale brownish viscous substance.
현탁액Suspension
송진용액 1.00%Songjin solution 1.00%
아교 1.20%glue 1.20%
수산화나트륨 4.00%Sodium hydroxide 4.00%
수산화칼륨 1.00%Potassium hydroxide 1.00%
염화나트륨 1.00%Sodium chloride 1.00%
제3 인산소다 2.00%Sodium tertiary phosphate 2.00%
암모니아 0.10%ammonia 0.10%
아세톤 8.00%Acetone 8.00%
물 잔량water Balance
상기 성분물질을 교반기에 넣고 상온에서 1시간 동안 교반하여 연한 갈색의 현탁액을 얻었으며 pH는 8.5로 측정되었다.The above material was placed in a stirrer and stirred at room temperature for 1 hour to obtain a pale brown suspension and the pH was measured at 8.5.
난연성 접착제Flame retardant adhesive
현탁액 2.60%Suspension 2.60%
황산칼슘 20.0%Calcium sulfate 20.0%
염화마그네슘 29.0%Magnesium chloride 29.0%
물 잔량water Balance
상기 성분물질을 교반기에서 20분간 교반하면서 염도 24‰가 되도록 조절하여 소망의 발포 폴리스타이렌 난연성 접착제 조성물을 얻었다.The above ingredients were stirred for 20 minutes in a stirrer to adjust the salt content to 24 ‰ to obtain a desired polystyrene flame retardant adhesive composition.
송진용액Songjin solution
99% 이상의 고순도 송진 28.3%99% or more high purity 28.3%
중쇄 지방산 2.10%Heavy chain fatty acid 2.10%
프로세스 오일 2.60%Process oil 2.60%
디에칠렌 글리콜 1.00%Diethylene glycol 1.00%
폴리에칠렌글리콜 200 0.70%Polyethylene glycol 200 0.70%
이소프로필 알코올 42.3%Isopropyl alcohol 42.3%
메탄올 23.0%Methanol 23.0%
상기 성분물질을 교반기에 넣고 115℃ 분위기에서 1시간 동안 교반하여 연한 갈색의 점성물질로 된 송진용액을 얻었다.The ingredient material was placed in a stirrer and stirred at 115 ° C for 1 hour to obtain a pine rosin solution of a pale brown viscous substance.
현탁액Suspension
송진용액 1.50%Songjin solution 1.50%
아교 1.80%glue 1.80%
수산화칼륨 4.00%Potassium hydroxide 4.00%
수산화마그네슘 2.00%Magnesium hydroxide 2.00%
염화나트륨 1.50%Sodium chloride 1.50%
제3 인산소다 2.00%Sodium tertiary phosphate 2.00%
암모니아 0.15%ammonia 0.15%
3-브로모-사이클로헥사논 9.00%3-Bromo-cyclohexanone 9.00%
물 잔량water Balance
상기 성분물질을 교반기에 넣고 상온에서 1시간 동안 교반하여 연한 갈색의 현탁액을 얻었으며 pH는 8.5로 측정되었다.The above material was placed in a stirrer and stirred at room temperature for 1 hour to obtain a pale brown suspension and the pH was measured at 8.5.
난연성 접착제Flame retardant adhesive
현탁액 2.30%Suspension 2.30%
황산칼슘 25.8%Calcium sulfate 25.8%
염화마그네슘 19.4%Magnesium chloride 19.4%
물 잔량water Balance
상기 성분물질을 교반기에서 20분간 교반하면서 염도 24‰가 되도록 조절하여 소망의 발포 폴리스타이렌 난연성 접착제 조성물을 얻었다.The above ingredients were stirred for 20 minutes in a stirrer to adjust the salt content to 24 ‰ to obtain a desired polystyrene flame retardant adhesive composition.
송진용액Songjin solution
99% 이상의 고순도 송진 28.3%99% or more high purity 28.3%
중쇄 지방산 2.10%Heavy chain fatty acid 2.10%
디옥틸텔레프탈레이트 2.60%Dioctyl terephthalate 2.60%
폴리에칠렌글리콜 100 1.00%Polyethylene glycol 100 1.00%
폴리에칠렌글리콜 300 0.70%Polyethylene glycol 300 0.70%
이소프로필 알코올 42.3%Isopropyl alcohol 42.3%
메탄올 23.0%Methanol 23.0%
상기 성분물질을 교반기에 넣고 130℃ 분위기에서 1시간 30분 동안 교반하여 송진용액을 얻었다. 얻어진 송진용액은 교반을 거듭할수록 연한 갈색의 점성용액으로 변하였다.The ingredient material was placed in a stirrer and stirred at 130 ° C for 1 hour and 30 minutes to obtain a rosin solution. The resulting rosin solution turned into a light brown viscous solution with stirring.
현탁액Suspension
송진용액 1.50%Songjin solution 1.50%
아교 1.80%glue 1.80%
수산화나트륨 4.00%Sodium hydroxide 4.00%
수산화마그네슘 2.00%Magnesium hydroxide 2.00%
염화나트륨 1.50%Sodium chloride 1.50%
염화칼륨 2.00%Potassium chloride 2.00%
암모니아 0.15%ammonia 0.15%
3-브로모-사이클로헥사논 9.00%3-Bromo-cyclohexanone 9.00%
물 잔량water Balance
상기 성분물질을 교반기에 넣고 상온에서 1시간 동안 교반하여 연한 갈색의 현탁액을 얻었으며 pH는 8.6으로 측정되었다.The above material was placed in a stirrer and stirred at room temperature for 1 hour to obtain a pale brown suspension. The pH was measured to be 8.6.
난연성 접착제Flame retardant adhesive
현탁액 2.50%Suspension 2.50%
염화칼슘 22.8%Calcium chloride 22.8%
염화마그네슘 24.3%Magnesium chloride 24.3%
물 잔량water Balance
상기 성분물질을 교반기에서 20분간 교반하면서 염도 23‰가 되도록 조절하여 소망의 발포 폴리스타이렌 난연성 접착제 조성물을 얻었다.The component material was stirred for 20 minutes in a stirrer to adjust the salt content to 23 ‰, thereby obtaining a desired foam polystyrene flame retardant adhesive composition.
송진용액Songjin solution
99% 이상의 고순도 송진 28.3%99% or more high purity 28.3%
중쇄 지방산 2.10%Heavy chain fatty acid 2.10%
프로세스 오일 1.30%Process oil 1.30%
디옥틸텔레프탈레이트 1.30%Dioctyl terephthalate 1.30%
디에칠렌 글리콜 0.50%Diethylene glycol 0.50%
폴리에칠렌글리콜 200 0.50%Polyethylene glycol 200 0.50%
폴리에칠렌글리콜 300 0.70%Polyethylene glycol 300 0.70%
이소프로필 알코올 42.3%Isopropyl alcohol 42.3%
메탄올 23.0%Methanol 23.0%
상기 성분물질을 교반기에 넣고 115℃ 분위기에서 1시간 동안 교반하여 연한 갈색을 띈 점성물질로 된 송진용액을 얻었다.The ingredient material was placed in a stirrer and stirred at 115 ° C for 1 hour to obtain a pine rosin solution with a pale brownish viscous substance.
현탁액Suspension
송진용액 1.50%Songjin solution 1.50%
아교 1.80%glue 1.80%
수산화칼륨 2.00%Potassium hydroxide 2.00%
수산화마그네슘 4.00%Magnesium hydroxide 4.00%
염화구리 1.50%Copper chloride 1.50%
염화암모늄 2.00%Ammonium chloride 2.00%
트리메틸아민 0.15%Trimethylamine 0.15%
3-브로모-사이클로헥사논 9.00%3-Bromo-cyclohexanone 9.00%
물 잔량water Balance
상기 성분물질을 교반기에 넣고 상온에서 1시간 동안 교반하여 연한 갈색의 현탁액을 얻었으며 pH는 8.5로 측정되었다.The above material was placed in a stirrer and stirred at room temperature for 1 hour to obtain a pale brown suspension and the pH was measured at 8.5.
난연성 접착제Flame retardant adhesive
현탁액 2.60%Suspension 2.60%
황산칼슘 20.0%Calcium sulfate 20.0%
염화마그네슘 29.0%Magnesium chloride 29.0%
물 잔량water Balance
상기 성분물질을 교반기에서 20분간 교반하면서 염도 24‰가 되도록 조절하여 소망의 발포 폴리스타이렌 난연성 접착제 조성물을 얻었다.The above ingredients were stirred for 20 minutes in a stirrer to adjust the salt content to 24 ‰ to obtain a desired polystyrene flame retardant adhesive composition.
송진용액Songjin solution
99% 이상의 고순도 송진 28.3%99% or more high purity 28.3%
중쇄 지방산 2.10%Heavy chain fatty acid 2.10%
디옥틸텔레프탈레이트 2.60%Dioctyl terephthalate 2.60%
트리에칠렌글리콜 1.00%Triethylene glycol 1.00%
폴리에칠렌글리콜 200 0.70%Polyethylene glycol 200 0.70%
이소프로필 알코올 42.3%Isopropyl alcohol 42.3%
메탄올 23.0%Methanol 23.0%
상기 성분물질을 교반기에 넣고 115℃ 분위기에서 1시간 동안 교반하여 연한 갈색을 띈 점성물질로 된 송진용액을 얻었다.The ingredient material was placed in a stirrer and stirred at 115 ° C for 1 hour to obtain a pine rosin solution with a pale brownish viscous substance.
현탁액Suspension
송진용액 1.50%Songjin solution 1.50%
아교 1.80%glue 1.80%
수산화칼륨 2.00%Potassium hydroxide 2.00%
수산화마그네슘 4.00%Magnesium hydroxide 4.00%
염화구리 1.50%Copper chloride 1.50%
염화암모늄 2.00%Ammonium chloride 2.00%
트리메틸아민 0.15%Trimethylamine 0.15%
3-브로모-사이클로헥사논 9.00%3-Bromo-cyclohexanone 9.00%
물 잔량water Balance
상기 성분물질을 교반기에 넣고 상온에서 1시간 동안 교반하여 연한 갈색의 현탁액을 얻었으며 pH는 8.5로 측정되었다.The above material was placed in a stirrer and stirred at room temperature for 1 hour to obtain a pale brown suspension and the pH was measured at 8.5.
난연성 접착제Flame retardant adhesive
현탁액 2.80%Suspension 2.80%
황산칼슘 32.0%Calcium sulfate 32.0%
염화마그네슘 20.2%Magnesium chloride 20.2%
물 잔량water Balance
상기 성분물질을 교반기에서 20분간 교반하면서 염도 25‰가 되도록 조절하여 소망의 발포 폴리스타이렌 난연성 접착제 조성물을 얻었다.The component material was stirred for 20 minutes in a stirrer to adjust the salt content to 25 ‰, thereby obtaining a desired foam polystyrene flame retardant adhesive composition.
송진용액Songjin solution
99% 이상의 고순도 송진 28.3%99% or more high purity 28.3%
중쇄 지방산 2.10%Heavy chain fatty acid 2.10%
프로세스 오일 2.60%Process oil 2.60%
디에칠렌 글리콜 1.00%Diethylene glycol 1.00%
폴리에칠렌글리콜 200 0.70%Polyethylene glycol 200 0.70%
이소프로필 알코올 42.3%Isopropyl alcohol 42.3%
메탄올 23.0%Methanol 23.0%
상기 성분물질을 교반기에 넣고 115℃ 분위기에서 1시간 동안 교반하여 연한 갈색의 점성물질로 된 송진용액을 얻었다.The ingredient material was placed in a stirrer and stirred at 115 ° C for 1 hour to obtain a pine rosin solution of a pale brown viscous substance.
현탁액Suspension
송진용액 2.00%Songjin solution 2.00%
아교 2.40%glue 2.40%
수산화칼륨 5.00%Potassium hydroxide 5.00%
수산화마그네슘 2.00%Magnesium hydroxide 2.00%
염화나트륨 2.00%Sodium chloride 2.00%
염화칼슘 2.00%Calcium chloride 2.00%
아미노메틸프로판올 0.20%Aminomethyl propanol 0.20%
헥산-3-원 10.0%Hexane-3-one 10.0%
물 잔량water Balance
상기 성분물질을 교반기에 넣고 상온에서 1시간 동안 교반하여 연한 갈색의 현탁액을 얻었으며 pH는 8.8로 측정되었다.The ingredients were placed in a stirrer and stirred at room temperature for 1 hour to obtain a pale brown suspension, pH 8.8.
난연성 접착제Flame retardant adhesive
현탁액 2.30%Suspension 2.30%
황산칼슘 25.8%Calcium sulfate 25.8%
염화마그네슘 19.4%Magnesium chloride 19.4%
물 잔량water Balance
상기 성분물질을 교반기에서 20분간 교반하면서 염도 24‰가 되도록 조절하여 소망의 발포 폴리스타이렌 난연성 접착제 조성물을 얻었다.The above ingredients were stirred for 20 minutes in a stirrer to adjust the salt content to 24 ‰ to obtain a desired polystyrene flame retardant adhesive composition.
송진용액Songjin solution
99% 이상의 고순도 송진 28.3%99% or more high purity 28.3%
중쇄 지방산 2.10%Heavy chain fatty acid 2.10%
디옥틸텔레프탈레이트 2.60%Dioctyl terephthalate 2.60%
폴리에칠렌글리콜 100 1.00%Polyethylene glycol 100 1.00%
폴리에칠렌글리콜 300 0.70%Polyethylene glycol 300 0.70%
이소프로필 알코올 42.3%Isopropyl alcohol 42.3%
메탄올 23.0%Methanol 23.0%
상기 성분물질을 교반기에 넣고 130℃ 분위기에서 1시간 30분 동안 교반하여 송진용액을 얻었다. 얻어진 송진용액은 교반을 거듭할수록 연한 갈색의 점성용액으로 변하였다.The ingredient material was placed in a stirrer and stirred at 130 ° C for 1 hour and 30 minutes to obtain a rosin solution. The resulting rosin solution turned into a light brown viscous solution with stirring.
현탁액Suspension
송진용액 2.00%Songjin solution 2.00%
아교 2.40%glue 2.40%
수산화나트륨 5.00%Sodium hydroxide 5.00%
수산화마그네슘 2.00%Magnesium hydroxide 2.00%
염화나트륨 2.00%Sodium chloride 2.00%
염화은 1.00%Silver chloride 1.00%
염화암모늄 1.00%Ammonium chloride 1.00%
아미노메틸프로판올 0.20%Aminomethyl propanol 0.20%
헥산-3-원 10.0%Hexane-3-one 10.0%
물 잔량water Balance
상기 성분물질을 교반기에 넣고 상온에서 1시간 동안 교반하여 연한 갈색의 현탁액을 얻었으며 pH는 8.8로 측정되었다.The ingredients were placed in a stirrer and stirred at room temperature for 1 hour to obtain a pale brown suspension, pH 8.8.
난연성 접착제Flame retardant adhesive
현탁액 2.50%Suspension 2.50%
염화칼슘 22.8%Calcium chloride 22.8%
염화마그네슘 24.3%Magnesium chloride 24.3%
물 잔량water Balance
상기 성분물질을 교반기에서 20분간 교반하면서 염도 23‰가 되도록 조절하여 소망의 발포 폴리스타이렌 난연성 접착제 조성물을 얻었다.The component material was stirred for 20 minutes in a stirrer to adjust the salt content to 23 ‰, thereby obtaining a desired foam polystyrene flame retardant adhesive composition.
송진용액Songjin solution
99% 이상의 고순도 송진 28.3%99% or more high purity 28.3%
중쇄 지방산 2.10%Heavy chain fatty acid 2.10%
프로세스 오일 1.30%Process oil 1.30%
디옥틸텔레프탈레이트 1.30%Dioctyl terephthalate 1.30%
디에칠렌 글리콜 0.50%Diethylene glycol 0.50%
폴리에칠렌글리콜 200 0.50%Polyethylene glycol 200 0.50%
폴리에칠렌글리콜 300 0.70%Polyethylene glycol 300 0.70%
이소프로필 알코올 42.3%Isopropyl alcohol 42.3%
메탄올 23.0%Methanol 23.0%
상기 성분물질을 교반기에 넣고 115℃ 분위기에서 1시간 동안 교반하여 연한 갈색을 띈 점성물질로 된 송진용액을 얻었다.The ingredient material was placed in a stirrer and stirred at 115 ° C for 1 hour to obtain a pine rosin solution with a pale brownish viscous substance.
현탁액Suspension
송진용액 2.00%Songjin solution 2.00%
아교 2.40%glue 2.40%
수산화나트륨 4.00%Sodium hydroxide 4.00%
수산화마그네슘 3.00%Magnesium hydroxide 3.00%
염화나트륨 1.00%Sodium chloride 1.00%
염화은 0.50%Silver chloride 0.50%
염화암모늄 2.50%Ammonium chloride 2.50%
트리메틸아민 0.20%Trimethylamine 0.20%
헥산-3-원 10.0%Hexane-3-one 10.0%
물 잔량water Balance
상기 성분물질을 교반기에 넣고 상온에서 1시간 동안 교반하여 연한 갈색의 현탁액을 얻었으며 pH는 8.6로 측정되었다.The above ingredients were placed in a stirrer and stirred at room temperature for 1 hour to obtain a pale brown suspension and the pH was measured to be 8.6.
난연성 접착제Flame retardant adhesive
현탁액 2.60%Suspension 2.60%
황산칼슘 20.0%Calcium sulfate 20.0%
염화마그네슘 29.0%Magnesium chloride 29.0%
물 잔량water Balance
상기 성분물질을 교반기에서 20분간 교반하면서 염도 24‰가 되도록 조절하여 소망의 발포 폴리스타이렌 난연성 접착제 조성물을 얻었다.The above ingredients were stirred for 20 minutes in a stirrer to adjust the salt content to 24 ‰ to obtain a desired polystyrene flame retardant adhesive composition.
송진용액Songjin solution
99% 이상의 고순도 송진 28.3%99% or more high purity 28.3%
중쇄 지방산 2.10%Heavy chain fatty acid 2.10%
디옥틸텔레프탈레이트 2.60%Dioctyl terephthalate 2.60%
트리에칠렌글리콜 1.00%Triethylene glycol 1.00%
폴리에칠렌글리콜 200 0.70%Polyethylene glycol 200 0.70%
이소프로필 알코올 42.3%Isopropyl alcohol 42.3%
메탄올 23.0%Methanol 23.0%
상기 성분물질을 교반기에 넣고 115℃ 분위기에서 1시간 동안 교반하여 연한 갈색을 띈 점성물질로 된 송진용액을 얻었다.The ingredient material was placed in a stirrer and stirred at 115 ° C for 1 hour to obtain a pine rosin solution with a pale brownish viscous substance.
현탁액Suspension
송진용액 2.00%Songjin solution 2.00%
아교 2.40%glue 2.40%
수산화나트륨 4.00%Sodium hydroxide 4.00%
수산화마그네슘 3.00%Magnesium hydroxide 3.00%
염화나트륨 1.00%Sodium chloride 1.00%
염화은 0.50%Silver chloride 0.50%
염화암모늄 2.50%Ammonium chloride 2.50%
트리메틸아민 0.20%Trimethylamine 0.20%
헥산-3-원 10.0%Hexane-3-one 10.0%
물 잔량water Balance
상기 성분물질을 교반기에 넣고 상온에서 1시간 동안 교반하여 연한 갈색의 현탁액을 얻었으며 pH는 8.9로 측정되었다.The above material was placed in a stirrer and stirred at room temperature for 1 hour to obtain a pale brown suspension. The pH was measured to be 8.9.
난연성 접착제Flame retardant adhesive
현탁액 2.80%Suspension 2.80%
황산칼슘 32.0%Calcium sulfate 32.0%
염화마그네슘 20.2%Magnesium chloride 20.2%
물 잔량water Balance
상기 성분물질을 교반기에서 20분간 교반하면서 염도 25‰가 되도록 조절하여 소망의 발포 폴리스타이렌 난연성 접착제 조성물을 얻었다.The component material was stirred for 20 minutes in a stirrer to adjust the salt content to 25 ‰, thereby obtaining a desired foam polystyrene flame retardant adhesive composition.
송진용액Songjin solution
99% 이상의 고순도 송진 28.3%99% or more high purity 28.3%
중쇄 지방산 2.10%Heavy chain fatty acid 2.10%
프로세스 오일 2.60%Process oil 2.60%
디에칠렌 글리콜 1.00%Diethylene glycol 1.00%
폴리에칠렌글리콜 200 0.70%Polyethylene glycol 200 0.70%
이소프로필 알코올 42.3%Isopropyl alcohol 42.3%
메탄올 23.0%Methanol 23.0%
상기 성분물질을 교반기에 넣고 115℃ 분위기에서 1시간 동안 교반하여 연한 갈색의 점성물질로 된 송진용액을 얻었다.The ingredient material was placed in a stirrer and stirred at 115 ° C for 1 hour to obtain a pine rosin solution of a pale brown viscous substance.
현탁액Suspension
송진용액 2.50%Songjin solution 2.50%
아교 3.00%glue 3.00%
수산화나트륨 3.00%Sodium hydroxide 3.00%
수산화칼륨 5.00%Potassium hydroxide 5.00%
염화나트륨 1.00%Sodium chloride 1.00%
염화구리 1.50%Copper chloride 1.50%
제3 인산소다 2.00%Sodium tertiary phosphate 2.00%
암모니아 0.10%ammonia 0.10%
트리메틸아민 0.15%Trimethylamine 0.15%
아세톤 11.0%Acetone 11.0%
물 잔량water Balance
상기 성분물질을 교반기에 넣고 상온에서 1시간 동안 교반하여 연한 갈색의 현탁액을 얻었으며 pH는 8.8로 측정되었다.The ingredients were placed in a stirrer and stirred at room temperature for 1 hour to obtain a pale brown suspension, pH 8.8.
난연성 접착제Flame retardant adhesive
현탁액 2.30%Suspension 2.30%
황산칼슘 25.8%Calcium sulfate 25.8%
염화마그네슘 19.4%Magnesium chloride 19.4%
물 잔량water Balance
상기 성분물질을 교반기에서 20분간 교반하면서 염도 24‰가 되도록 조절하여 소망의 발포 폴리스타이렌 난연성 접착제 조성물을 얻었다.The above ingredients were stirred for 20 minutes in a stirrer to adjust the salt content to 24 ‰ to obtain a desired polystyrene flame retardant adhesive composition.
송진용액Songjin solution
99% 이상의 고순도 송진 28.3%99% or more high purity 28.3%
중쇄 지방산 2.10%Heavy chain fatty acid 2.10%
디옥틸텔레프탈레이트 2.60%Dioctyl terephthalate 2.60%
폴리에칠렌글리콜 100 1.00%Polyethylene glycol 100 1.00%
폴리에칠렌글리콜 300 0.70%Polyethylene glycol 300 0.70%
이소프로필 알코올 42.3%Isopropyl alcohol 42.3%
메탄올 23.0%Methanol 23.0%
상기 성분물질을 교반기에 넣고 130℃ 분위기에서 1시간 30분 동안 교반하여 송진용액을 얻었다. 얻어진 송진용액은 교반을 거듭할수록 연한 갈색의 점성용액으로 변하였다.The ingredient material was placed in a stirrer and stirred at 130 ° C for 1 hour and 30 minutes to obtain a rosin solution. The resulting rosin solution turned into a light brown viscous solution with stirring.
현탁액Suspension
송진용액 2.50%Songjin solution 2.50%
아교 3.00%glue 3.00%
수산화마그네슘 2.00%Magnesium hydroxide 2.00%
수산화나트륨 6.00%Sodium hydroxide 6.00%
염화칼륨 1.50%Potassium chloride 1.50%
염화은 1.50%Silver chloride 1.50%
제3 인산소다 1.50%Sodium tertiary phosphate 1.50%
암모니아 0.15%ammonia 0.15%
아미노메틸프로판올 0.10%Aminomethyl propanol 0.10%
아세톤 11.0%Acetone 11.0%
물 잔량water Balance
상기 성분물질을 교반기에 넣고 상온에서 1시간 동안 교반하여 연한 갈색의 현탁액을 얻었으며 pH는 8.5로 측정되었다.The above material was placed in a stirrer and stirred at room temperature for 1 hour to obtain a pale brown suspension and the pH was measured at 8.5.
난연성 접착제Flame retardant adhesive
현탁액 2.50%Suspension 2.50%
염화칼슘 22.8%Calcium chloride 22.8%
염화마그네슘 24.3%Magnesium chloride 24.3%
물 잔량water Balance
상기 성분물질을 교반기에서 20분간 교반하면서 염도 23‰가 되도록 조절하여 소망의 발포 폴리스타이렌 난연성 접착제 조성물을 얻었다.The component material was stirred for 20 minutes in a stirrer to adjust the salt content to 23 ‰, thereby obtaining a desired foam polystyrene flame retardant adhesive composition.
송진용액Songjin solution
99% 이상의 고순도 송진 28.3%99% or more high purity 28.3%
중쇄 지방산 2.10%Heavy chain fatty acid 2.10%
프로세스 오일 1.30%Process oil 1.30%
디옥틸텔레프탈레이트 1.30%Dioctyl terephthalate 1.30%
디에칠렌 글리콜 0.50%Diethylene glycol 0.50%
폴리에칠렌글리콜 200 0.50%Polyethylene glycol 200 0.50%
폴리에칠렌글리콜 300 0.70%Polyethylene glycol 300 0.70%
이소프로필 알코올 42.3%Isopropyl alcohol 42.3%
메탄올 23.0%Methanol 23.0%
상기 성분물질을 교반기에 넣고 115℃ 분위기에서 1시간 동안 교반하여 연한 갈색을 띈 점성물질로 된 송진용액을 얻었다.The ingredient material was placed in a stirrer and stirred at 115 ° C for 1 hour to obtain a pine rosin solution with a pale brownish viscous substance.
현탁액Suspension
송진용액 2.50%Songjin solution 2.50%
아교 3.00%glue 3.00%
수산화마그네슘 5.00%Magnesium hydroxide 5.00%
수산화나트륨 3.00%Sodium hydroxide 3.00%
염화칼슘 2.50%Calcium chloride 2.50%
염화은 0.50%Silver chloride 0.50%
제3 인산소다 1.50%Sodium tertiary phosphate 1.50%
암모니아 0.20%ammonia 0.20%
아미노메틸프로판올 0.05%Aminomethyl propanol 0.05%
아세톤 13.0%Acetone 13.0%
물 잔량water Balance
상기 성분물질을 교반기에 넣고 상온에서 1시간 동안 교반하여 연한 갈색의 현탁액을 얻었으며 pH는 8.8로 측정되었다.The ingredients were placed in a stirrer and stirred at room temperature for 1 hour to obtain a pale brown suspension, pH 8.8.
난연성 접착제Flame retardant adhesive
현탁액 2.60%Suspension 2.60%
황산칼슘 20.0%Calcium sulfate 20.0%
염화마그네슘 29.0%Magnesium chloride 29.0%
물 잔량water Balance
상기 성분물질을 교반기에서 20분간 교반하면서 염도 24‰가 되도록 조절하여 소망의 발포 폴리스타이렌 난연성 접착제 조성물을 얻었다.The above ingredients were stirred for 20 minutes in a stirrer to adjust the salt content to 24 ‰ to obtain a desired polystyrene flame retardant adhesive composition.
송진용액Songjin solution
99% 이상의 고순도 송진 28.3%99% or more high purity 28.3%
중쇄 지방산 2.10%Heavy chain fatty acid 2.10%
디옥틸텔레프탈레이트 2.60%Dioctyl terephthalate 2.60%
트리에칠렌글리콜 1.00%Triethylene glycol 1.00%
폴리에칠렌글리콜 200 0.70%Polyethylene glycol 200 0.70%
이소프로필 알코올 42.3%Isopropyl alcohol 42.3%
메탄올 23.0%Methanol 23.0%
상기 성분물질을 교반기에 넣고 115℃ 분위기에서 1시간 동안 교반하여 연한 갈색을 띈 점성물질로 된 송진용액을 얻었다.The ingredient material was placed in a stirrer and stirred at 115 ° C for 1 hour to obtain a pine rosin solution with a pale brownish viscous substance.
현탁액Suspension
송진용액 2.50%Songjin solution 2.50%
아교 3.00%glue 3.00%
수산화마그네슘 5.00%Magnesium hydroxide 5.00%
수산화나트륨 3.00%Sodium hydroxide 3.00%
염화칼슘 2.50%Calcium chloride 2.50%
염화은 0.50%Silver chloride 0.50%
제3 인산소다 1.50%Sodium tertiary phosphate 1.50%
암모니아 0.20%ammonia 0.20%
아미노메틸프로판올 0.05%Aminomethyl propanol 0.05%
아세톤 12.0%Acetone 12.0%
물 잔량water Balance
상기 성분물질을 교반기에 넣고 상온에서 1시간 동안 교반하여 연한 갈색의 현탁액을 얻었으며 pH는 8.6으로 측정되었다.The above material was placed in a stirrer and stirred at room temperature for 1 hour to obtain a pale brown suspension. The pH was measured to be 8.6.
난연성 접착제Flame retardant adhesive
현탁액 2.80%Suspension 2.80%
황산칼슘 32.0%Calcium sulfate 32.0%
염화마그네슘 20.2%Magnesium chloride 20.2%
물 잔량water Balance
상기 성분물질을 교반기에서 20분간 교반하면서 염도 25‰가 되도록 조절하여 소망의 발포 폴리스타이렌 난연성 접착제 조성물을 얻었다.The component material was stirred for 20 minutes in a stirrer to adjust the salt content to 25 ‰, thereby obtaining a desired foam polystyrene flame retardant adhesive composition.
송진용액Songjin solution
99% 이상의 고순도 송진 29.8%99% or more high purity 29.8%
중쇄 지방산 2.30%Heavy chain fatty acid 2.30%
디옥틸 테레프탈레이트 2.90%Dioctyl terephthalate 2.90%
디에칠렌 글리콜 1.50%Diethylene glycol 1.50%
폴리에칠렌 글리콜 100 0.40%Polyethylene glycol 100 0.40%
이소프로필 알코올 43.0%Isopropyl alcohol 43.0%
메탄올 20.1%Methanol 20.1%
상기 성분물질을 교반기에 넣고 120℃ 분위기에서 1시간 동안 교반하여 연한 갈색의 점성물질로 된 송진용액을 얻었다.The ingredient materials were placed in a stirrer and stirred for 1 hour in an atmosphere of 120 ° C to obtain a pine rosin solution having a pale brown viscous substance.
현탁액Suspension
송진용액 2.50%Songjin solution 2.50%
아교 3.00%glue 3.00%
수산화나트륨 3.00%Sodium hydroxide 3.00%
수산화칼륨 5.00%Potassium hydroxide 5.00%
염화나트륨 1.00%Sodium chloride 1.00%
염화구리 1.50%Copper chloride 1.50%
제3 인산소다 2.00%Sodium tertiary phosphate 2.00%
암모니아 0.10%ammonia 0.10%
트리메틸아민 0.15%Trimethylamine 0.15%
3-브로모-사이클로헥사논 11.0%3-Bromo-cyclohexanone 11.0%
물 잔량water Balance
상기 성분물질을 교반기에 넣고 상온에서 1시간 동안 교반하여 연한 갈색의 현탁액을 얻었으며 pH는 8.8로 측정되었다.The ingredients were placed in a stirrer and stirred at room temperature for 1 hour to obtain a pale brown suspension, pH 8.8.
난연성 접착제Flame retardant adhesive
현탁액 2.30%Suspension 2.30%
황산칼슘 25.8%Calcium sulfate 25.8%
염화마그네슘 19.4%Magnesium chloride 19.4%
물 잔량water Balance
상기 성분물질을 교반기에서 20분간 교반하면서 염도 24‰가 되도록 조절하여 소망의 발포 폴리스타이렌 난연성 접착제 조성물을 얻었다.The above ingredients were stirred for 20 minutes in a stirrer to adjust the salt content to 24 ‰ to obtain a desired polystyrene flame retardant adhesive composition.
송진용액Songjin solution
99% 이상의 고순도 송진 29.8%99% or more high purity 29.8%
중쇄 지방산 2.30%Heavy chain fatty acid 2.30%
프로세스 오일 2.90%Process oil 2.90%
트리에칠렌 글리콜 0.50%Triethylene glycol 0.50%
디에칠렌 글리콜 0.50%Diethylene glycol 0.50%
폴리에칠렌 글리콜 200 0.40%Polyethylene glycol 200 0.40%
이소프로필 알코올 43.0%Isopropyl alcohol 43.0%
메탄올 20.1%Methanol 20.1%
상기 성분물질을 교반기에 넣고 115℃ 분위기에서 1시간 동안 교반하여 연한 갈색의 점성물질로 된 송진용액을 얻었다.The ingredient material was placed in a stirrer and stirred at 115 ° C for 1 hour to obtain a pine rosin solution of a pale brown viscous substance.
현탁액Suspension
송진용액 3.00%Songjin solution 3.00%
아교 3.60%glue 3.60%
수산화나트륨 3.00%Sodium hydroxide 3.00%
수산화칼슘 3.00%Calcium hydroxide 3.00%
수산화마그네슘 3.00%Magnesium hydroxide 3.00%
염화나트륨 1.00%Sodium chloride 1.00%
염화칼슘 1.00%Calcium chloride 1.00%
염화암모늄 1.00%Ammonium chloride 1.00%
염화수은 2.00%Mercury chloride 2.00%
암모니아 0.10%ammonia 0.10%
아미노메틸프로판올 0.20%Aminomethyl propanol 0.20%
3-브로모-사이클로헥사논 12.0%3-Bromo-cyclohexanone 12.0%
물 잔량water Balance
상기 성분물질을 교반기에 넣고 상온에서 1시간 동안 교반하여 연한 갈색의 현탁액을 얻었으며 pH는 8.9로 측정되었다.The above material was placed in a stirrer and stirred at room temperature for 1 hour to obtain a pale brown suspension. The pH was measured to be 8.9.
난연성 접착제Flame retardant adhesive
현탁액 2.50%Suspension 2.50%
염화칼슘 22.8%Calcium chloride 22.8%
염화마그네슘 24.3%Magnesium chloride 24.3%
물 잔량water Balance
상기 성분물질을 교반기에서 20분간 교반하면서 염도 23‰가 되도록 조절하여 소망의 발포 폴리스타이렌 난연성 접착제 조성물을 얻었다.The component material was stirred for 20 minutes in a stirrer to adjust the salt content to 23 ‰, thereby obtaining a desired foam polystyrene flame retardant adhesive composition.
송진용액Songjin solution
99% 이상의 고순도 송진 29.8%99% or more high purity 29.8%
중쇄 지방산 2.30%Heavy chain fatty acid 2.30%
디옥틸 테레프탈레이트 2.90%Dioctyl terephthalate 2.90%
디에칠렌 글리콜 1.50%Diethylene glycol 1.50%
폴리에칠렌 글리콜 0.40%Polyethylene glycol 0.40%
이소프로필 알코올 43.0%Isopropyl alcohol 43.0%
메탄올 20.1%Methanol 20.1%
상기 성분물질을 교반기에 넣고 115℃ 분위기에서 1시간 동안 교반하여 연한 갈색의 점성물질로 된 송진용액을 얻었다.The ingredient material was placed in a stirrer and stirred at 115 ° C for 1 hour to obtain a pine rosin solution of a pale brown viscous substance.
현탁액Suspension
송진용액 3.00%Songjin solution 3.00%
아교 3.60%glue 3.60%
수산화나트륨 3.00%Sodium hydroxide 3.00%
수산화칼륨 3.00%Potassium hydroxide 3.00%
수산화마그네슘 3.00%Magnesium hydroxide 3.00%
염화나트륨 1.00%Sodium chloride 1.00%
제3 인산소다 2.00%Sodium tertiary phosphate 2.00%
염화수은 2.00%Mercury chloride 2.00%
암모니아 0.10%ammonia 0.10%
아미노메틸프로판올 0.10%Aminomethyl propanol 0.10%
트리메틸아민 0.10%Trimethylamine 0.10%
3-브로모-사이클로헥사논 12.0%3-Bromo-cyclohexanone 12.0%
물 잔량water Balance
상기 성분물질을 교반기에 넣고 상온에서 1시간 동안 교반하여 연한 갈색의 현탁액을 얻었으며 pH는 8.9로 측정되었다.The above material was placed in a stirrer and stirred at room temperature for 1 hour to obtain a pale brown suspension. The pH was measured to be 8.9.
난연성 접착제Flame retardant adhesive
현탁액 2.60%Suspension 2.60%
황산칼슘 20.0%Calcium sulfate 20.0%
염화마그네슘 29.0%Magnesium chloride 29.0%
물 잔량water Balance
상기 성분물질을 교반기에서 20분간 교반하면서 염도 24‰가 되도록 조절하여 소망의 발포 폴리스타이렌 난연성 접착제 조성물을 얻었다.The above ingredients were stirred for 20 minutes in a stirrer to adjust the salt content to 24 ‰ to obtain a desired polystyrene flame retardant adhesive composition.
송진용액Songjin solution
99% 이상의 고순도 송진 29.8%99% or more high purity 29.8%
중쇄 지방산 2.30%Heavy chain fatty acid 2.30%
디옥틸 테레프탈레이트 1.90%Dioctyl terephthalate 1.90%
프로세스 오일 1.00%Process oil 1.00%
트리에칠렌 글리콜 1.00%Triethylene glycol 1.00%
폴리에칠렌 글리콜 100 0.50%Polyethylene glycol 100 0.50%
폴리에칠렌 글리콜 200 0.40%Polyethylene glycol 200 0.40%
이소프로필 알코올 43.0%Isopropyl alcohol 43.0%
메탄올 20.1%Methanol 20.1%
상기 성분물질을 교반기에 넣고 120℃ 분위기에서 1시간 동안 교반하여 연한 갈색의 점성물질로 된 송진용액을 얻었다.The ingredient materials were placed in a stirrer and stirred for 1 hour in an atmosphere of 120 ° C to obtain a pine rosin solution having a pale brown viscous substance.
현탁액Suspension
송진용액 3.00%Songjin solution 3.00%
아교 3.60%glue 3.60%
수산화나트륨 3.00%Sodium hydroxide 3.00%
수산화칼륨 3.00%Potassium hydroxide 3.00%
수산화마그네슘 3.00%Magnesium hydroxide 3.00%
염화나트륨 1.00%Sodium chloride 1.00%
제3 인산소다 2.00%Sodium tertiary phosphate 2.00%
염화수은 2.00%Mercury chloride 2.00%
암모니아 0.10%ammonia 0.10%
아미노메틸프로판올 0.10%Aminomethyl propanol 0.10%
트리메틸아민 0.10%Trimethylamine 0.10%
3-브로모-사이클로헥사논 12.0%3-Bromo-cyclohexanone 12.0%
물 잔량water Balance
상기 성분물질을 교반기에 넣고 상온에서 1시간 동안 교반하여 연한 갈색의 현탁액을 얻었으며 pH는 8.8로 측정되었다.The ingredients were placed in a stirrer and stirred at room temperature for 1 hour to obtain a pale brown suspension, pH 8.8.
난연성 접착제Flame retardant adhesive
현탁액 2.80%Suspension 2.80%
황산칼슘 32.0%Calcium sulfate 32.0%
염화마그네슘 20.2%Magnesium chloride 20.2%
물 잔량water Balance
상기 성분물질을 교반기에서 20분간 교반하면서 염도 25‰가 되도록 조절하여 소망의 발포 폴리스타이렌 난연성 접착제 조성물을 얻었다.The component material was stirred for 20 minutes in a stirrer to adjust the salt content to 25 ‰, thereby obtaining a desired foam polystyrene flame retardant adhesive composition.
송진용액Songjin solution
99% 이상의 고순도 송진 29.8%99% or more high purity 29.8%
중쇄 지방산 2.30%Heavy chain fatty acid 2.30%
디옥틸 테레프탈레이트 2.90%Dioctyl terephthalate 2.90%
디에칠렌 글리콜 1.50%Diethylene glycol 1.50%
폴리에칠렌 글리콜 100 0.40%Polyethylene glycol 100 0.40%
이소프로필 알코올 43.0%Isopropyl alcohol 43.0%
메탄올 20.1%Methanol 20.1%
상기 성분물질을 교반기에 넣고 120℃ 분위기에서 1시간 동안 교반하여 연한 갈색의 점성물질로 된 송진용액을 얻었다.The ingredient materials were placed in a stirrer and stirred for 1 hour in an atmosphere of 120 ° C to obtain a pine rosin solution having a pale brown viscous substance.
현탁액Suspension
송진용액 1.00%Songjin solution 1.00%
아교 1.20%glue 1.20%
수산화나트륨 3.00%Sodium hydroxide 3.00%
수산화칼륨 2.00%Potassium hydroxide 2.00%
염화나트륨 1.00%Sodium chloride 1.00%
제3 인산소다 2.00%Sodium tertiary phosphate 2.00%
암모니아 0.10%ammonia 0.10%
아세톤 8.00%Acetone 8.00%
물 잔량water Balance
상기 성분물질을 교반기에 넣고 상온에서 1시간 동안 교반하여 연한 갈색의 현탁액을 얻었으며 pH는 8.5로 측정되었다.The above material was placed in a stirrer and stirred at room temperature for 1 hour to obtain a pale brown suspension and the pH was measured at 8.5.
난연성 접착제Flame retardant adhesive
현탁액 2.30%Suspension 2.30%
황산칼슘 25.8%Calcium sulfate 25.8%
염화마그네슘 19.4%Magnesium chloride 19.4%
물 잔량water Balance
상기 성분물질을 교반기에서 20분간 교반하면서 염도 24‰가 되도록 조절하여 소망의 발포 폴리스타이렌 난연성 접착제 조성물을 얻었다.The above ingredients were stirred for 20 minutes in a stirrer to adjust the salt content to 24 ‰ to obtain a desired polystyrene flame retardant adhesive composition.
송진용액Songjin solution
99% 이상의 고순도 송진 29.8%99% or more high purity 29.8%
중쇄 지방산 2.30%Heavy chain fatty acid 2.30%
프로세스 오일 2.90%Process oil 2.90%
트리에칠렌 글리콜 0.50%Triethylene glycol 0.50%
디에칠렌 글리콜 0.50%Diethylene glycol 0.50%
폴리에칠렌 글리콜 200 0.40%Polyethylene glycol 200 0.40%
이소프로필 알코올 43.0%Isopropyl alcohol 43.0%
메탄올 20.1%Methanol 20.1%
상기 성분물질을 교반기에 넣고 115℃ 분위기에서 1시간 동안 교반하여 연한 갈색의 점성물질로 된 송진용액을 얻었다.The ingredient material was placed in a stirrer and stirred at 115 ° C for 1 hour to obtain a pine rosin solution of a pale brown viscous substance.
현탁액Suspension
송진용액 1.00%Songjin solution 1.00%
아교 1.20%glue 1.20%
수산화마그네슘 2.00%Magnesium hydroxide 2.00%
수산화칼륨 3.00%Potassium hydroxide 3.00%
염화나트륨 1.00%Sodium chloride 1.00%
제3 인산소다 2.00%Sodium tertiary phosphate 2.00%
암모니아 0.10%ammonia 0.10%
아세톤 8.00%Acetone 8.00%
물 잔량water Balance
상기 성분물질을 교반기에 넣고 상온에서 1시간 동안 교반하여 연한 갈색의 현탁액을 얻었으며 pH는 8.5로 측정되었다.The above material was placed in a stirrer and stirred at room temperature for 1 hour to obtain a pale brown suspension and the pH was measured at 8.5.
난연성 접착제Flame retardant adhesive
현탁액 2.50%Suspension 2.50%
염화칼슘 22.8%Calcium chloride 22.8%
염화마그네슘 24.3%Magnesium chloride 24.3%
물 잔량water Balance
상기 성분물질을 교반기에서 20분간 교반하면서 염도 23‰가 되도록 조절하여 소망의 발포 폴리스타이렌 난연성 접착제 조성물을 얻었다.The component material was stirred for 20 minutes in a stirrer to adjust the salt content to 23 ‰, thereby obtaining a desired foam polystyrene flame retardant adhesive composition.
송진용액Songjin solution
99% 이상의 고순도 송진 29.8%99% or more high purity 29.8%
중쇄 지방산 2.30%Heavy chain fatty acid 2.30%
디옥틸 테레프탈레이트 2.90%Dioctyl terephthalate 2.90%
디에칠렌 글리콜 1.50%Diethylene glycol 1.50%
폴리에칠렌 글리콜 0.40%Polyethylene glycol 0.40%
이소프로필 알코올 43.0%Isopropyl alcohol 43.0%
메탄올 20.1%Methanol 20.1%
상기 성분물질을 교반기에 넣고 115℃ 분위기에서 1시간 동안 교반하여 연한 갈색의 점성물질로 된 송진용액을 얻었다.The ingredient material was placed in a stirrer and stirred at 115 ° C for 1 hour to obtain a pine rosin solution of a pale brown viscous substance.
현탁액Suspension
송진용액 1.00%Songjin solution 1.00%
아교 1.20%glue 1.20%
수산화나트륨 2.30%Sodium hydroxide 2.30%
수산화칼륨 2.70%Potassium hydroxide 2.70%
염화나트륨 1.00%Sodium chloride 1.00%
제3 인산소다 2.00%Sodium tertiary phosphate 2.00%
암모니아 0.10%ammonia 0.10%
아세톤 8.00%Acetone 8.00%
물 잔량water Balance
상기 성분물질을 교반기에 넣고 상온에서 1시간 동안 교반하여 연한 갈색의 현탁액을 얻었으며 pH는 8.5로 측정되었다.The above material was placed in a stirrer and stirred at room temperature for 1 hour to obtain a pale brown suspension and the pH was measured at 8.5.
난연성 접착제Flame retardant adhesive
현탁액 2.60%Suspension 2.60%
황산칼슘 20.0%Calcium sulfate 20.0%
염화마그네슘 29.0%Magnesium chloride 29.0%
물 잔량water Balance
상기 성분물질을 교반기에서 20분간 교반하면서 염도 24‰가 되도록 조절하여 소망의 발포 폴리스타이렌 난연성 접착제 조성물을 얻었다.The above ingredients were stirred for 20 minutes in a stirrer to adjust the salt content to 24 ‰ to obtain a desired polystyrene flame retardant adhesive composition.
송진용액Songjin solution
99% 이상의 고순도 송진 29.8%99% or more high purity 29.8%
중쇄 지방산 2.30%Heavy chain fatty acid 2.30%
디옥틸 테레프탈레이트 1.90%Dioctyl terephthalate 1.90%
프로세스 오일 1.00%Process oil 1.00%
트리에칠렌 글리콜 1.00%Triethylene glycol 1.00%
폴리에칠렌 글리콜 100 0.50%Polyethylene glycol 100 0.50%
폴리에칠렌 글리콜 200 0.40%Polyethylene glycol 200 0.40%
이소프로필 알코올 43.0%Isopropyl alcohol 43.0%
메탄올 20.1%Methanol 20.1%
상기 성분물질을 교반기에 넣고 120℃ 분위기에서 1시간 동안 교반하여 연한 갈색의 점성물질로 된 송진용액을 얻었다.The ingredient materials were placed in a stirrer and stirred for 1 hour in an atmosphere of 120 ° C to obtain a pine rosin solution having a pale brown viscous substance.
현탁액Suspension
송진용액 1.00%Songjin solution 1.00%
아교 1.20%glue 1.20%
수산화나트륨 4.00%Sodium hydroxide 4.00%
수산화칼륨 1.00%Potassium hydroxide 1.00%
염화나트륨 1.00%Sodium chloride 1.00%
제3 인산소다 2.00%Sodium tertiary phosphate 2.00%
암모니아 0.10%ammonia 0.10%
아세톤 8.00%Acetone 8.00%
물 잔량water Balance
상기 성분물질을 교반기에 넣고 상온에서 1시간 동안 교반하여 연한 갈색의 현탁액을 얻었으며 pH는 8.5로 측정되었다.The above material was placed in a stirrer and stirred at room temperature for 1 hour to obtain a pale brown suspension and the pH was measured at 8.5.
난연성 접착제Flame retardant adhesive
현탁액 2.80%Suspension 2.80%
황산칼슘 32.0%Calcium sulfate 32.0%
염화마그네슘 20.2%Magnesium chloride 20.2%
물 잔량water Balance
상기 성분물질을 교반기에서 20분간 교반하면서 염도 25‰가 되도록 조절하여 소망의 발포 폴리스타이렌 난연성 접착제 조성물을 얻었다.The component material was stirred for 20 minutes in a stirrer to adjust the salt content to 25 ‰, thereby obtaining a desired foam polystyrene flame retardant adhesive composition.
송진용액Songjin solution
99% 이상의 고순도 송진 29.8%99% or more high purity 29.8%
중쇄 지방산 2.30%Heavy chain fatty acid 2.30%
디옥틸 테레프탈레이트 2.90%Dioctyl terephthalate 2.90%
디에칠렌 글리콜 1.50%Diethylene glycol 1.50%
폴리에칠렌 글리콜 100 0.40%Polyethylene glycol 100 0.40%
이소프로필 알코올 43.0%Isopropyl alcohol 43.0%
메탄올 20.1%Methanol 20.1%
상기 성분물질을 교반기에 넣고 120℃ 분위기에서 1시간 동안 교반하여 연한 갈색의 점성물질로 된 송진용액을 얻었다.The ingredient materials were placed in a stirrer and stirred for 1 hour in an atmosphere of 120 ° C to obtain a pine rosin solution having a pale brown viscous substance.
현탁액Suspension
송진용액 1.50%Songjin solution 1.50%
아교 1.80%glue 1.80%
수산화칼륨 4.00%Potassium hydroxide 4.00%
수산화마그네슘 2.00%Magnesium hydroxide 2.00%
염화나트륨 1.50%Sodium chloride 1.50%
제3 인산소다 2.00%Sodium tertiary phosphate 2.00%
암모니아 0.15%ammonia 0.15%
3-브로모-사이클로헥사논 9.00%3-Bromo-cyclohexanone 9.00%
물 잔량water Balance
상기 성분물질을 교반기에 넣고 상온에서 1시간 동안 교반하여 연한 갈색의 현탁액을 얻었으며 pH는 8.5로 측정되었다.The above material was placed in a stirrer and stirred at room temperature for 1 hour to obtain a pale brown suspension and the pH was measured at 8.5.
난연성 접착제Flame retardant adhesive
현탁액 2.30%Suspension 2.30%
황산칼슘 25.8%Calcium sulfate 25.8%
염화마그네슘 19.4%Magnesium chloride 19.4%
물 잔량water Balance
상기 성분물질을 교반기에서 20분간 교반하면서 염도 24‰가 되도록 조절하여 소망의 발포 폴리스타이렌 난연성 접착제 조성물을 얻었다.The above ingredients were stirred for 20 minutes in a stirrer to adjust the salt content to 24 ‰ to obtain a desired polystyrene flame retardant adhesive composition.
송진용액Songjin solution
99% 이상의 고순도 송진 29.8%99% or more high purity 29.8%
중쇄 지방산 2.30%Heavy chain fatty acid 2.30%
프로세스 오일 2.90%Process oil 2.90%
트리에칠렌 글리콜 0.50%Triethylene glycol 0.50%
디에칠렌 글리콜 0.50%Diethylene glycol 0.50%
폴리에칠렌 글리콜 200 0.40%Polyethylene glycol 200 0.40%
이소프로필 알코올 43.0%Isopropyl alcohol 43.0%
메탄올 20.1%Methanol 20.1%
상기 성분물질을 교반기에 넣고 115℃ 분위기에서 1시간 동안 교반하여 연한 갈색의 점성물질로 된 송진용액을 얻었다.The ingredient material was placed in a stirrer and stirred at 115 ° C for 1 hour to obtain a pine rosin solution of a pale brown viscous substance.
현탁액Suspension
송진용액 1.50%Songjin solution 1.50%
아교 1.80%glue 1.80%
수산화나트륨 4.00%Sodium hydroxide 4.00%
수산화마그네슘 2.00%Magnesium hydroxide 2.00%
염화나트륨 1.50%Sodium chloride 1.50%
염화칼륨 2.00%Potassium chloride 2.00%
암모니아 0.15%ammonia 0.15%
3-브로모-사이클로헥사논 9.00%3-Bromo-cyclohexanone 9.00%
물 잔량water Balance
상기 성분물질을 교반기에 넣고 상온에서 1시간 동안 교반하여 연한 갈색의 현탁액을 얻었으며 pH는 8.6으로 측정되었다.The above material was placed in a stirrer and stirred at room temperature for 1 hour to obtain a pale brown suspension. The pH was measured to be 8.6.
난연성 접착제Flame retardant adhesive
현탁액 2.50%Suspension 2.50%
염화칼슘 22.8%Calcium chloride 22.8%
염화마그네슘 24.3%Magnesium chloride 24.3%
물 잔량water Balance
상기 성분물질을 교반기에서 20분간 교반하면서 염도 23‰가 되도록 조절하여 소망의 발포 폴리스타이렌 난연성 접착제 조성물을 얻었다.The component material was stirred for 20 minutes in a stirrer to adjust the salt content to 23 ‰, thereby obtaining a desired foam polystyrene flame retardant adhesive composition.
송진용액Songjin solution
99% 이상의 고순도 송진 29.8%99% or more high purity 29.8%
중쇄 지방산 2.30%Heavy chain fatty acid 2.30%
디옥틸 테레프탈레이트 2.90%Dioctyl terephthalate 2.90%
디에칠렌 글리콜 1.50%Diethylene glycol 1.50%
폴리에칠렌 글리콜 0.40%Polyethylene glycol 0.40%
이소프로필 알코올 43.0%Isopropyl alcohol 43.0%
메탄올 20.1%Methanol 20.1%
상기 성분물질을 교반기에 넣고 115℃ 분위기에서 1시간 동안 교반하여 연한 갈색의 점성물질로 된 송진용액을 얻었다.The ingredient material was placed in a stirrer and stirred at 115 ° C for 1 hour to obtain a pine rosin solution of a pale brown viscous substance.
현탁액Suspension
송진용액 1.50%Songjin solution 1.50%
아교 1.80%glue 1.80%
수산화칼륨 2.00%Potassium hydroxide 2.00%
수산화마그네슘 4.00%Magnesium hydroxide 4.00%
염화구리 1.50%Copper chloride 1.50%
염화암모늄 2.00%Ammonium chloride 2.00%
트리메틸아민 0.15%Trimethylamine 0.15%
3-브로모-사이클로헥사논 9.00%3-Bromo-cyclohexanone 9.00%
물 잔량water Balance
상기 성분물질을 교반기에 넣고 상온에서 1시간 동안 교반하여 연한 갈색의 현탁액을 얻었으며 pH는 8.5로 측정되었다.The above material was placed in a stirrer and stirred at room temperature for 1 hour to obtain a pale brown suspension and the pH was measured at 8.5.
난연성 접착제Flame retardant adhesive
현탁액 2.60%Suspension 2.60%
황산칼슘 20.0%Calcium sulfate 20.0%
염화마그네슘 29.0%Magnesium chloride 29.0%
물 잔량water Balance
상기 성분물질을 교반기에서 20분간 교반하면서 염도 24‰가 되도록 조절하여 소망의 발포 폴리스타이렌 난연성 접착제 조성물을 얻었다.The above ingredients were stirred for 20 minutes in a stirrer to adjust the salt content to 24 ‰ to obtain a desired polystyrene flame retardant adhesive composition.
송진용액Songjin solution
99% 이상의 고순도 송진 28.3%99% or more high purity 28.3%
중쇄 지방산 2.10%Heavy chain fatty acid 2.10%
프로세스 오일 1.30%Process oil 1.30%
디옥틸텔레프탈레이트 1.30%Dioctyl terephthalate 1.30%
디에칠렌 글리콜 0.50%Diethylene glycol 0.50%
트리에칠렌글리콜 0.50%Triethylene glycol 0.50%
폴리에칠렌글리콜 200 0.70%Polyethylene glycol 200 0.70%
이소프로필 알코올 42.3%Isopropyl alcohol 42.3%
메탄올 23.0%Methanol 23.0%
상기 성분물질을 교반기에 넣고 120℃ 분위기에서 1시간 동안 교반하여 연한 갈색의 점성물질로 된 송진용액을 얻었다.The ingredient materials were placed in a stirrer and stirred for 1 hour in an atmosphere of 120 ° C to obtain a pine rosin solution having a pale brown viscous substance.
현탁액Suspension
송진용액 1.50%Songjin solution 1.50%
아교 1.80%glue 1.80%
수산화칼륨 2.00%Potassium hydroxide 2.00%
수산화마그네슘 4.00%Magnesium hydroxide 4.00%
염화구리 1.50%Copper chloride 1.50%
염화암모늄 2.00%Ammonium chloride 2.00%
트리메틸아민 0.15%Trimethylamine 0.15%
3-브로모-사이클로헥사논 9.00%3-Bromo-cyclohexanone 9.00%
물 잔량water Balance
상기 성분물질을 교반기에 넣고 상온에서 1시간 동안 교반하여 연한 갈색의 현탁액을 얻었으며 pH는 8.5로 측정되었다.The above material was placed in a stirrer and stirred at room temperature for 1 hour to obtain a pale brown suspension and the pH was measured at 8.5.
난연성 접착제Flame retardant adhesive
현탁액 2.80%Suspension 2.80%
황산칼슘 32.0%Calcium sulfate 32.0%
염화마그네슘 20.2%Magnesium chloride 20.2%
물 잔량water Balance
상기 성분물질을 교반기에서 20분간 교반하면서 염도 25‰가 되도록 조절하여 소망의 발포 폴리스타이렌 난연성 접착제 조성물을 얻었다.The component material was stirred for 20 minutes in a stirrer to adjust the salt content to 25 ‰, thereby obtaining a desired foam polystyrene flame retardant adhesive composition.
송진용액Songjin solution
99% 이상의 고순도 송진 29.8%99% or more high purity 29.8%
중쇄 지방산 2.30%Heavy chain fatty acid 2.30%
디옥틸 테레프탈레이트 2.90%Dioctyl terephthalate 2.90%
디에칠렌 글리콜 1.50%Diethylene glycol 1.50%
폴리에칠렌 글리콜 100 0.40%Polyethylene glycol 100 0.40%
이소프로필 알코올 43.0%Isopropyl alcohol 43.0%
메탄올 20.1%Methanol 20.1%
상기 성분물질을 교반기에 넣고 120℃ 분위기에서 1시간 동안 교반하여 연한 갈색의 점성물질로 된 송진용액을 얻었다.The ingredient materials were placed in a stirrer and stirred for 1 hour in an atmosphere of 120 ° C to obtain a pine rosin solution having a pale brown viscous substance.
현탁액Suspension
송진용액 2.00%Songjin solution 2.00%
아교 2.40%glue 2.40%
수산화칼륨 5.00%Potassium hydroxide 5.00%
수산화마그네슘 2.00%Magnesium hydroxide 2.00%
염화나트륨 2.00%Sodium chloride 2.00%
염화칼슘 2.00%Calcium chloride 2.00%
아미노메틸프로판올 0.20%Aminomethyl propanol 0.20%
헥산-3-원 10.0%Hexane-3-one 10.0%
물 잔량water Balance
상기 성분물질을 교반기에 넣고 상온에서 1시간 동안 교반하여 연한 갈색의 현탁액을 얻었으며 pH는 8.8로 측정되었다.The ingredients were placed in a stirrer and stirred at room temperature for 1 hour to obtain a pale brown suspension, pH 8.8.
난연성 접착제Flame retardant adhesive
현탁액 2.30%Suspension 2.30%
황산칼슘 25.8%Calcium sulfate 25.8%
염화마그네슘 19.4%Magnesium chloride 19.4%
물 잔량water Balance
상기 성분물질을 교반기에서 20분간 교반하면서 염도 24‰가 되도록 조절하여 소망의 발포 폴리스타이렌 난연성 접착제 조성물을 얻었다.The above ingredients were stirred for 20 minutes in a stirrer to adjust the salt content to 24 ‰ to obtain a desired polystyrene flame retardant adhesive composition.
송진용액Songjin solution
99% 이상의 고순도 송진 29.8%99% or more high purity 29.8%
중쇄 지방산 2.30%Heavy chain fatty acid 2.30%
프로세스 오일 2.90%Process oil 2.90%
트리에칠렌 글리콜 0.50%Triethylene glycol 0.50%
디에칠렌 글리콜 0.50%Diethylene glycol 0.50%
폴리에칠렌 글리콜 200 0.90%Polyethylene glycol 200 0.90%
이소프로필 알코올 43.0%Isopropyl alcohol 43.0%
메탄올 20.1%Methanol 20.1%
상기 성분물질을 교반기에 넣고 115℃ 분위기에서 1시간 동안 교반하여 연한 갈색의 점성물질로 된 송진용액을 얻었다.The ingredient material was placed in a stirrer and stirred at 115 ° C for 1 hour to obtain a pine rosin solution of a pale brown viscous substance.
현탁액Suspension
송진용액 2.00%Songjin solution 2.00%
아교 2.40%glue 2.40%
수산화나트륨 5.00%Sodium hydroxide 5.00%
수산화마그네슘 2.00%Magnesium hydroxide 2.00%
염화나트륨 2.00%Sodium chloride 2.00%
염화은 1.00%Silver chloride 1.00%
염화암모늄 1.00%Ammonium chloride 1.00%
아미노메틸프로판올 0.20%Aminomethyl propanol 0.20%
헥산-3-원 10.0%Hexane-3-one 10.0%
물 잔량water Balance
상기 성분물질을 교반기에 넣고 상온에서 1시간 동안 교반하여 연한 갈색의 현탁액을 얻었으며 pH는 8.8로 측정되었다.The ingredients were placed in a stirrer and stirred at room temperature for 1 hour to obtain a pale brown suspension, pH 8.8.
난연성 접착제Flame retardant adhesive
현탁액 2.50%Suspension 2.50%
염화칼슘 22.8%Calcium chloride 22.8%
염화마그네슘 24.3%Magnesium chloride 24.3%
물 잔량water Balance
상기 성분물질을 교반기에서 20분간 교반하면서 염도 23‰가 되도록 조절하여 소망의 발포 폴리스타이렌 난연성 접착제 조성물을 얻었다.The component material was stirred for 20 minutes in a stirrer to adjust the salt content to 23 ‰, thereby obtaining a desired foam polystyrene flame retardant adhesive composition.
송진용액Songjin solution
99% 이상의 고순도 송진 29.8%99% or more high purity 29.8%
중쇄 지방산 2.30%Heavy chain fatty acid 2.30%
디옥틸 테레프탈레이트 2.90%Dioctyl terephthalate 2.90%
디에칠렌 글리콜 1.50%Diethylene glycol 1.50%
폴리에칠렌 글리콜 0.40%Polyethylene glycol 0.40%
이소프로필 알코올 43.0%Isopropyl alcohol 43.0%
메탄올 20.1%Methanol 20.1%
상기 성분물질을 교반기에 넣고 115℃ 분위기에서 1시간 동안 교반하여 연한 갈색의 점성물질로 된 송진용액을 얻었다.The ingredient material was placed in a stirrer and stirred at 115 ° C for 1 hour to obtain a pine rosin solution of a pale brown viscous substance.
현탁액Suspension
송진용액 2.00%Songjin solution 2.00%
아교 2.40%glue 2.40%
수산화나트륨 4.00%Sodium hydroxide 4.00%
수산화마그네슘 3.00%Magnesium hydroxide 3.00%
염화나트륨 1.00%Sodium chloride 1.00%
염화은 0.50%Silver chloride 0.50%
염화암모늄 2.50%Ammonium chloride 2.50%
트리메틸아민 0.20%Trimethylamine 0.20%
헥산-3-원 10.0%Hexane-3-one 10.0%
물 잔량water Balance
상기 성분물질을 교반기에 넣고 상온에서 1시간 동안 교반하여 연한 갈색의 현탁액을 얻었으며 pH는 8.6로 측정되었다.The above ingredients were placed in a stirrer and stirred at room temperature for 1 hour to obtain a pale brown suspension and the pH was measured to be 8.6.
난연성 접착제Flame retardant adhesive
현탁액 2.60%Suspension 2.60%
황산칼슘 20.0%Calcium sulfate 20.0%
염화마그네슘 29.0%Magnesium chloride 29.0%
물 잔량water Balance
상기 성분물질을 교반기에서 20분간 교반하면서 염도 24‰가 되도록 조절하여 소망의 발포 폴리스타이렌 난연성 접착제 조성물을 얻었다.The above ingredients were stirred for 20 minutes in a stirrer to adjust the salt content to 24 ‰ to obtain a desired polystyrene flame retardant adhesive composition.
송진용액Songjin solution
99% 이상의 고순도 송진 29.8%99% or more high purity 29.8%
중쇄 지방산 2.30%Heavy chain fatty acid 2.30%
디옥틸 테레프탈레이트 1.90%Dioctyl terephthalate 1.90%
프로세스 오일 1.00%Process oil 1.00%
트리에칠렌 글리콜 1.00%Triethylene glycol 1.00%
폴리에칠렌 글리콜 100 0.50%Polyethylene glycol 100 0.50%
폴리에칠렌 글리콜 200 0.40%Polyethylene glycol 200 0.40%
이소프로필 알코올 43.0%Isopropyl alcohol 43.0%
메탄올 20.1%Methanol 20.1%
상기 성분물질을 교반기에 넣고 120℃ 분위기에서 1시간 동안 교반하여 연한 갈색의 점성물질로 된 송진용액을 얻었다.The ingredient materials were placed in a stirrer and stirred for 1 hour in an atmosphere of 120 ° C to obtain a pine rosin solution having a pale brown viscous substance.
현탁액Suspension
송진용액 2.00%Songjin solution 2.00%
아교 2.40%glue 2.40%
수산화나트륨 4.00%Sodium hydroxide 4.00%
수산화마그네슘 3.00%Magnesium hydroxide 3.00%
염화나트륨 1.00%Sodium chloride 1.00%
염화은 0.50%Silver chloride 0.50%
염화암모늄 2.50%Ammonium chloride 2.50%
트리메틸아민 0.20%Trimethylamine 0.20%
헥산-3-원 10.0%Hexane-3-one 10.0%
물 잔량water Balance
상기 성분물질을 교반기에 넣고 상온에서 1시간 동안 교반하여 연한 갈색의 현탁액을 얻었으며 pH는 8.9로 측정되었다.The above material was placed in a stirrer and stirred at room temperature for 1 hour to obtain a pale brown suspension. The pH was measured to be 8.9.
난연성 접착제Flame retardant adhesive
현탁액 2.80%Suspension 2.80%
황산칼슘 32.0%Calcium sulfate 32.0%
염화마그네슘 20.2%Magnesium chloride 20.2%
물 잔량water Balance
상기 성분물질을 교반기에서 20분간 교반하면서 염도 25‰가 되도록 조절하여 소망의 발포 폴리스타이렌 난연성 접착제 조성물을 얻었다.The component material was stirred for 20 minutes in a stirrer to adjust the salt content to 25 ‰, thereby obtaining a desired foam polystyrene flame retardant adhesive composition.
송진용액Songjin solution
99% 이상의 고순도 송진 31.3%99% or more high purity 31.3%
중쇄 지방산 2.50%Heavy chain fatty acid 2.50%
디옥틸 테레프탈레이트 3.10%Dioctyl terephthalate 3.10%
디에칠렌 글리콜 1.00%Diethylene glycol 1.00%
폴리에칠렌글리콜 100 1.10%Polyethylene glycol 100 1.10%
이소프로필 알코올 41.0%Isopropyl alcohol 41.0%
메탄올 20.0%Methanol 20.0%
상기 성분물질을 교반기에 넣고 115℃ 분위기에서 1시간 동안 교반하여 송진용액을 얻었다. 송진용액은 교반을 거듭할수록 연한 갈색의 점성물질로 변하였다.The ingredient material was placed in a stirrer and stirred in an atmosphere at 115 ° C for 1 hour to obtain a rosin solution. The rosin solution turned into a light brown viscous substance with stirring.
현탁액Suspension
송진용액 2.50%Songjin solution 2.50%
아교 3.00%glue 3.00%
수산화나트륨 3.00%Sodium hydroxide 3.00%
수산화칼륨 5.00%Potassium hydroxide 5.00%
염화나트륨 1.00%Sodium chloride 1.00%
염화구리 1.50%Copper chloride 1.50%
제3 인산소다 2.00%Sodium tertiary phosphate 2.00%
암모니아 0.10%ammonia 0.10%
트리메틸아민 0.15%Trimethylamine 0.15%
아세톤 12.0%Acetone 12.0%
물 잔량water Balance
상기 성분물질을 교반기에 넣고 상온에서 1시간 동안 교반하여 연한 갈색의 현탁액을 얻었으며 pH는 8.8로 측정되었다.The ingredients were placed in a stirrer and stirred at room temperature for 1 hour to obtain a pale brown suspension, pH 8.8.
난연성 접착제Flame retardant adhesive
현탁액 2.30%Suspension 2.30%
황산칼슘 25.8%Calcium sulfate 25.8%
염화마그네슘 19.4%Magnesium chloride 19.4%
물 잔량water Balance
상기 성분물질을 교반기에서 20분간 교반하면서 염도 24‰가 되도록 조절하여 소망의 발포 폴리스타이렌 난연성 접착제 조성물을 얻었다.The above ingredients were stirred for 20 minutes in a stirrer to adjust the salt content to 24 ‰ to obtain a desired polystyrene flame retardant adhesive composition.
송진용액Songjin solution
99% 이상의 고순도 송진 31.3%99% or more high purity 31.3%
중쇄 지방산 2.50%Heavy chain fatty acid 2.50%
디옥틸 테레프탈레이트 3.10%Dioctyl terephthalate 3.10%
디에칠렌 글리콜 1.00%Diethylene glycol 1.00%
폴리에칠렌글리콜 100 1.10%Polyethylene glycol 100 1.10%
이소프로필 알코올 41.0%Isopropyl alcohol 41.0%
메탄올 20.0%Methanol 20.0%
상기 성분물질을 교반기에 넣고 120℃ 분위기에서 1시간 동안 교반하여 송진용액을 얻었다.The ingredient material was placed in a stirrer and stirred for 1 hour in an atmosphere of 120 ° C to obtain a rosin solution.
현탁액Suspension
송진용액 2.50%Songjin solution 2.50%
아교 3.00%glue 3.00%
수산화마그네슘 2.00%Magnesium hydroxide 2.00%
수산화나트륨 6.00%Sodium hydroxide 6.00%
염화칼륨 1.50%Potassium chloride 1.50%
염화은 1.50%Silver chloride 1.50%
제3 인산소다 1.50%Sodium tertiary phosphate 1.50%
암모니아 0.15%ammonia 0.15%
아미노메틸프로판올 0.10%Aminomethyl propanol 0.10%
아세톤 12.0%Acetone 12.0%
물 잔량water Balance
상기 성분물질을 교반기에 넣고 상온에서 1시간 동안 교반하여 연한 갈색의 현탁액을 얻었으며 pH는 8.5로 측정되었다.The above material was placed in a stirrer and stirred at room temperature for 1 hour to obtain a pale brown suspension and the pH was measured at 8.5.
난연성 접착제Flame retardant adhesive
현탁액 2.50%Suspension 2.50%
염화칼슘 22.8%Calcium chloride 22.8%
염화마그네슘 24.3%Magnesium chloride 24.3%
물 잔량water Balance
상기 성분물질을 교반기에서 20분간 교반하면서 염도 23‰가 되도록 조절하여 소망의 발포 폴리스타이렌 난연성 접착제 조성물을 얻었다.The component material was stirred for 20 minutes in a stirrer to adjust the salt content to 23 ‰, thereby obtaining a desired foam polystyrene flame retardant adhesive composition.
송진용액Songjin solution
99% 이상의 고순도 송진 31.3%99% or more high purity 31.3%
중쇄 지방산 2.50%Heavy chain fatty acid 2.50%
디옥틸 테레프탈레이트 3.10%Dioctyl terephthalate 3.10%
디에칠렌 글리콜 1.00%Diethylene glycol 1.00%
폴리에칠렌글리콜 100 1.10%Polyethylene glycol 100 1.10%
이소프로필 알코올 41.0%Isopropyl alcohol 41.0%
메탄올 20.0%Methanol 20.0%
상기 성분물질을 교반기에 넣고 130℃ 분위기에서 1시간 30분 동안 교반하여 송진용액을 얻었다. 얻어진 송진용액은 교반을 거듭할수록 연한 갈색의 점성용액으로 변하였다.The ingredient material was placed in a stirrer and stirred at 130 ° C for 1 hour and 30 minutes to obtain a rosin solution. The resulting rosin solution turned into a light brown viscous solution with stirring.
현탁액Suspension
송진용액 2.50%Songjin solution 2.50%
아교 3.00%glue 3.00%
수산화마그네슘 5.00%Magnesium hydroxide 5.00%
수산화나트륨 3.00%Sodium hydroxide 3.00%
염화칼슘 2.50%Calcium chloride 2.50%
염화은 0.50%Silver chloride 0.50%
제3 인산소다 1.50%Sodium tertiary phosphate 1.50%
암모니아 0.20%ammonia 0.20%
아미노메틸프로판올 0.05%Aminomethyl propanol 0.05%
아세톤 12.0%Acetone 12.0%
물 잔량water Balance
상기 성분물질을 교반기에 넣고 상온에서 1시간 동안 교반하여 연한 갈색의 현탁액을 얻었으며 pH는 8.8로 측정되었다.The ingredients were placed in a stirrer and stirred at room temperature for 1 hour to obtain a pale brown suspension, pH 8.8.
난연성 접착제Flame retardant adhesive
현탁액 2.60%Suspension 2.60%
황산칼슘 20.0%Calcium sulfate 20.0%
염화마그네슘 29.0%Magnesium chloride 29.0%
물 잔량water Balance
상기 성분물질을 교반기에서 20분간 교반하면서 염도 24‰가 되도록 조절하여 소망의 발포 폴리스타이렌 난연성 접착제 조성물을 얻었다.The above ingredients were stirred for 20 minutes in a stirrer to adjust the salt content to 24 ‰ to obtain a desired polystyrene flame retardant adhesive composition.
송진용액Songjin solution
99% 이상의 고순도 송진 31.3%99% or more high purity 31.3%
중쇄 지방산 2.50%Heavy chain fatty acid 2.50%
디옥틸 테레프탈레이트 3.10%Dioctyl terephthalate 3.10%
디에칠렌 글리콜 1.00%Diethylene glycol 1.00%
폴리에칠렌글리콜 100 1.10%Polyethylene glycol 100 1.10%
이소프로필 알코올 41.0%Isopropyl alcohol 41.0%
메탄올 20.0%Methanol 20.0%
상기 성분물질을 교반기에 넣고 115℃ 분위기에서 1시간 동안 교반하여 송진용액을 얻었다. 송진용액은 교반을 거듭할수록 연한 갈색의 점성물질로 변하였다.The ingredient material was placed in a stirrer and stirred in an atmosphere at 115 ° C for 1 hour to obtain a rosin solution. The rosin solution turned into a light brown viscous substance with stirring.
현탁액Suspension
송진용액 2.50%Songjin solution 2.50%
아교 3.00%glue 3.00%
수산화마그네슘 5.00%Magnesium hydroxide 5.00%
수산화나트륨 3.00%Sodium hydroxide 3.00%
염화칼슘 2.50%Calcium chloride 2.50%
염화은 0.50%Silver chloride 0.50%
제3 인산소다 1.50%Sodium tertiary phosphate 1.50%
암모니아 0.20%ammonia 0.20%
아미노메틸프로판올 0.05%Aminomethyl propanol 0.05%
아세톤 12.0%Acetone 12.0%
물 잔량water Balance
상기 성분물질을 교반기에 넣고 상온에서 1시간 동안 교반하여 연한 갈색의 현탁액을 얻었으며 pH는 8.6으로 측정되었다.The above material was placed in a stirrer and stirred at room temperature for 1 hour to obtain a pale brown suspension. The pH was measured to be 8.6.
난연성 접착제Flame retardant adhesive
현탁액 2.80%Suspension 2.80%
황산칼슘 32.0%Calcium sulfate 32.0%
염화마그네슘 20.2%Magnesium chloride 20.2%
물 잔량water Balance
상기 성분물질을 교반기에서 20분간 교반하면서 염도 25‰가 되도록 조절하여 소망의 발포 폴리스타이렌 난연성 접착제 조성물을 얻었다.The component material was stirred for 20 minutes in a stirrer to adjust the salt content to 25 ‰, thereby obtaining a desired foam polystyrene flame retardant adhesive composition.
송진용액Songjin solution
99% 이상의 고순도 송진 31.3%99% or more high purity 31.3%
중쇄 지방산 2.50%Heavy chain fatty acid 2.50%
디옥틸 테레프탈레이트 3.10%Dioctyl terephthalate 3.10%
디에칠렌 글리콜 1.00%Diethylene glycol 1.00%
폴리에칠렌글리콜 100 1.10%Polyethylene glycol 100 1.10%
이소프로필 알코올 41.0%Isopropyl alcohol 41.0%
메탄올 20.0%Methanol 20.0%
상기 성분물질을 교반기에 넣고 115℃ 분위기에서 1시간 동안 교반하여 송진용액을 얻었다. 송진용액은 교반을 거듭할수록 연한 갈색의 점성물질로 변하였다.The ingredient material was placed in a stirrer and stirred in an atmosphere at 115 ° C for 1 hour to obtain a rosin solution. The rosin solution turned into a light brown viscous substance with stirring.
현탁액Suspension
송진용액 2.50%Songjin solution 2.50%
아교 3.00%glue 3.00%
수산화나트륨 3.00%Sodium hydroxide 3.00%
수산화칼륨 5.00%Potassium hydroxide 5.00%
염화나트륨 1.00%Sodium chloride 1.00%
염화구리 1.50%Copper chloride 1.50%
제3 인산소다 2.00%Sodium tertiary phosphate 2.00%
암모니아 0.10%ammonia 0.10%
트리메틸아민 0.15%Trimethylamine 0.15%
3-브로모-사이클로헥사논 11.0%3-Bromo-cyclohexanone 11.0%
물 잔량water Balance
상기 성분물질을 교반기에 넣고 상온에서 1시간 동안 교반하여 연한 갈색의 현탁액을 얻었으며 pH는 8.8로 측정되었다.The ingredients were placed in a stirrer and stirred at room temperature for 1 hour to obtain a pale brown suspension, pH 8.8.
난연성 접착제Flame retardant adhesive
현탁액 2.30%Suspension 2.30%
황산칼슘 25.8%Calcium sulfate 25.8%
염화마그네슘 19.4%Magnesium chloride 19.4%
물 잔량water Balance
상기 성분물질을 교반기에서 20분간 교반하면서 염도 24‰가 되도록 조절하여 소망의 발포 폴리스타이렌 난연성 접착제 조성물을 얻었다.The above ingredients were stirred for 20 minutes in a stirrer to adjust the salt content to 24 ‰ to obtain a desired polystyrene flame retardant adhesive composition.
송진용액Songjin solution
99% 이상의 고순도 송진 31.3%99% or more high purity 31.3%
중쇄 지방산 2.50%Heavy chain fatty acid 2.50%
디옥틸 테레프탈레이트 3.10%Dioctyl terephthalate 3.10%
디에칠렌 글리콜 1.00%Diethylene glycol 1.00%
폴리에칠렌글리콜 100 1.10%Polyethylene glycol 100 1.10%
이소프로필 알코올 41.0%Isopropyl alcohol 41.0%
메탄올 20.0%Methanol 20.0%
상기 성분물질을 교반기에 넣고 120℃ 분위기에서 1시간 동안 교반하여 송진용액을 얻었다.The ingredient material was placed in a stirrer and stirred for 1 hour in an atmosphere of 120 ° C to obtain a rosin solution.
현탁액Suspension
송진용액 3.00%Songjin solution 3.00%
아교 3.60%glue 3.60%
수산화나트륨 3.00%Sodium hydroxide 3.00%
수산화칼슘 3.00%Calcium hydroxide 3.00%
수산화마그네슘 3.00%Magnesium hydroxide 3.00%
염화나트륨 1.00%Sodium chloride 1.00%
염화칼슘 1.00%Calcium chloride 1.00%
염화암모늄 1.00%Ammonium chloride 1.00%
염화수은 2.00%Mercury chloride 2.00%
암모니아 0.10%ammonia 0.10%
아미노메틸프로판올 0.20%Aminomethyl propanol 0.20%
3-브로모-사이클로헥사논 12.0%3-Bromo-cyclohexanone 12.0%
물 잔량water Balance
상기 성분물질을 교반기에 넣고 상온에서 1시간 동안 교반하여 연한 갈색의 현탁액을 얻었으며 pH는 8.9로 측정되었다.The above material was placed in a stirrer and stirred at room temperature for 1 hour to obtain a pale brown suspension. The pH was measured to be 8.9.
난연성 접착제Flame retardant adhesive
현탁액 2.50%Suspension 2.50%
염화칼슘 22.8%Calcium chloride 22.8%
염화마그네슘 24.3%Magnesium chloride 24.3%
물 잔량water Balance
상기 성분물질을 교반기에서 20분간 교반하면서 염도 23‰가 되도록 조절하여 소망의 발포 폴리스타이렌 난연성 접착제 조성물을 얻었다.The component material was stirred for 20 minutes in a stirrer to adjust the salt content to 23 ‰, thereby obtaining a desired foam polystyrene flame retardant adhesive composition.
송진용액Songjin solution
99% 이상의 고순도 송진 31.3%99% or more high purity 31.3%
중쇄 지방산 2.50%Heavy chain fatty acid 2.50%
디옥틸 테레프탈레이트 3.10%Dioctyl terephthalate 3.10%
디에칠렌 글리콜 1.00%Diethylene glycol 1.00%
폴리에칠렌글리콜 100 1.10%Polyethylene glycol 100 1.10%
이소프로필 알코올 41.0%Isopropyl alcohol 41.0%
메탄올 20.0%Methanol 20.0%
상기 성분물질을 교반기에 넣고 130℃ 분위기에서 1시간 30분 동안 교반하여 송진용액을 얻었다. 얻어진 송진용액은 교반을 거듭할수록 연한 갈색의 점성용액으로 변하였다.The ingredient material was placed in a stirrer and stirred at 130 ° C for 1 hour and 30 minutes to obtain a rosin solution. The resulting rosin solution turned into a light brown viscous solution with stirring.
현탁액Suspension
송진용액 3.00%Songjin solution 3.00%
아교 3.60%glue 3.60%
수산화나트륨 3.00%Sodium hydroxide 3.00%
수산화칼륨 3.00%Potassium hydroxide 3.00%
수산화마그네슘 3.00%Magnesium hydroxide 3.00%
염화나트륨 1.00%Sodium chloride 1.00%
제3 인산소다 2.00%Sodium tertiary phosphate 2.00%
염화수은 2.00%Mercury chloride 2.00%
암모니아 0.10%ammonia 0.10%
아미노메틸프로판올 0.10%Aminomethyl propanol 0.10%
트리메틸아민 0.10%Trimethylamine 0.10%
3-브로모-사이클로헥사논 12.0%3-Bromo-cyclohexanone 12.0%
물 잔량water Balance
상기 성분물질을 교반기에 넣고 상온에서 1시간 동안 교반하여 연한 갈색의 현탁액을 얻었으며 pH는 8.9로 측정되었다.The above material was placed in a stirrer and stirred at room temperature for 1 hour to obtain a pale brown suspension. The pH was measured to be 8.9.
난연성 접착제Flame retardant adhesive
현탁액 2.60%Suspension 2.60%
황산칼슘 20.0%Calcium sulfate 20.0%
염화마그네슘 29.0%Magnesium chloride 29.0%
물 잔량water Balance
상기 성분물질을 교반기에서 20분간 교반하면서 염도 24‰가 되도록 조절하여 소망의 발포 폴리스타이렌 난연성 접착제 조성물을 얻었다.The above ingredients were stirred for 20 minutes in a stirrer to adjust the salt content to 24 ‰ to obtain a desired polystyrene flame retardant adhesive composition.
송진용액Songjin solution
99% 이상의 고순도 송진 31.3%99% or more high purity 31.3%
중쇄 지방산 2.50%Heavy chain fatty acid 2.50%
디옥틸 테레프탈레이트 3.10%Dioctyl terephthalate 3.10%
디에칠렌 글리콜 1.00%Diethylene glycol 1.00%
폴리에칠렌글리콜 100 1.10%Polyethylene glycol 100 1.10%
이소프로필 알코올 41.0%Isopropyl alcohol 41.0%
메탄올 20.0%Methanol 20.0%
상기 성분물질을 교반기에 넣고 115℃ 분위기에서 1시간 동안 교반하여 송진용액을 얻었다. 송진용액은 교반을 거듭할수록 연한 갈색의 점성물질로 변하였다.The ingredient material was placed in a stirrer and stirred in an atmosphere at 115 ° C for 1 hour to obtain a rosin solution. The rosin solution turned into a light brown viscous substance with stirring.
현탁액Suspension
송진용액 3.00%Songjin solution 3.00%
아교 3.60%glue 3.60%
수산화나트륨 3.00%Sodium hydroxide 3.00%
수산화칼륨 3.00%Potassium hydroxide 3.00%
수산화마그네슘 3.00%Magnesium hydroxide 3.00%
염화나트륨 1.00%Sodium chloride 1.00%
제3 인산소다 2.00%Sodium tertiary phosphate 2.00%
염화수은 2.00%Mercury chloride 2.00%
암모니아 0.10%ammonia 0.10%
아미노메틸프로판올 0.10%Aminomethyl propanol 0.10%
트리메틸아민 0.10%Trimethylamine 0.10%
3-브로모-사이클로헥사논 12.0%3-Bromo-cyclohexanone 12.0%
물 잔량water Balance
상기 성분물질을 교반기에 넣고 상온에서 1시간 동안 교반하여 연한 갈색의 현탁액을 얻었으며 pH는 8.8로 측정되었다.The ingredients were placed in a stirrer and stirred at room temperature for 1 hour to obtain a pale brown suspension, pH 8.8.
난연성 접착제Flame retardant adhesive
현탁액 2.80%Suspension 2.80%
황산칼슘 32.0%Calcium sulfate 32.0%
염화마그네슘 20.2%Magnesium chloride 20.2%
물 잔량water Balance
상기 성분물질을 교반기에서 20분간 교반하면서 염도 25‰가 되도록 조절하여 소망의 발포 폴리스타이렌 난연성 접착제 조성물을 얻었다.The component material was stirred for 20 minutes in a stirrer to adjust the salt content to 25 ‰, thereby obtaining a desired foam polystyrene flame retardant adhesive composition.
송진용액Songjin solution
99% 이상의 고순도 송진 31.3%99% or more high purity 31.3%
중쇄 지방산 2.50%Heavy chain fatty acid 2.50%
디옥틸 테레프탈레이트 3.10%Dioctyl terephthalate 3.10%
디에칠렌 글리콜 1.00%Diethylene glycol 1.00%
폴리에칠렌글리콜 100 1.10%Polyethylene glycol 100 1.10%
이소프로필 알코올 41.0%Isopropyl alcohol 41.0%
메탄올 20.0%Methanol 20.0%
상기 성분물질을 교반기에 넣고 115℃ 분위기에서 1시간 동안 교반하여 송진용액을 얻었다. 송진용액은 교반을 거듭할수록 연한 갈색의 점성물질로 변하였다.The ingredient material was placed in a stirrer and stirred in an atmosphere at 115 ° C for 1 hour to obtain a rosin solution. The rosin solution turned into a light brown viscous substance with stirring.
현탁액Suspension
송진용액 1.00%Songjin solution 1.00%
아교 1.20%glue 1.20%
수산화나트륨 3.00%Sodium hydroxide 3.00%
수산화칼륨 2.00%Potassium hydroxide 2.00%
염화나트륨 1.00%Sodium chloride 1.00%
제3 인산소다 2.00%Sodium tertiary phosphate 2.00%
암모니아 0.10%ammonia 0.10%
아세톤 8.00%Acetone 8.00%
물 잔량water Balance
상기 성분물질을 교반기에 넣고 상온에서 1시간 동안 교반하여 연한 갈색의 현탁액을 얻었으며 pH는 8.5로 측정되었다.The above material was placed in a stirrer and stirred at room temperature for 1 hour to obtain a pale brown suspension and the pH was measured at 8.5.
난연성 접착제Flame retardant adhesive
현탁액 2.30%Suspension 2.30%
황산칼슘 25.8%Calcium sulfate 25.8%
염화마그네슘 19.4%Magnesium chloride 19.4%
물 잔량water Balance
상기 성분물질을 교반기에서 20분간 교반하면서 염도 24‰가 되도록 조절하여 소망의 발포 폴리스타이렌 난연성 접착제 조성물을 얻었다.The above ingredients were stirred for 20 minutes in a stirrer to adjust the salt content to 24 ‰ to obtain a desired polystyrene flame retardant adhesive composition.
송진용액Songjin solution
99% 이상의 고순도 송진 31.3%99% or more high purity 31.3%
중쇄 지방산 2.50%Heavy chain fatty acid 2.50%
디옥틸 테레프탈레이트 3.10%Dioctyl terephthalate 3.10%
디에칠렌 글리콜 1.00%Diethylene glycol 1.00%
폴리에칠렌글리콜 100 1.10%Polyethylene glycol 100 1.10%
이소프로필 알코올 41.0%Isopropyl alcohol 41.0%
메탄올 20.0%Methanol 20.0%
상기 성분물질을 교반기에 넣고 120℃ 분위기에서 1시간 동안 교반하여 송진용액을 얻었다.The ingredient material was placed in a stirrer and stirred for 1 hour in an atmosphere of 120 ° C to obtain a rosin solution.
현탁액Suspension
송진용액 1.00%Songjin solution 1.00%
아교 1.20%glue 1.20%
수산화나트륨 3.00%Sodium hydroxide 3.00%
수산화칼륨 2.00%Potassium hydroxide 2.00%
염화나트륨 1.00%Sodium chloride 1.00%
제3 인산소다 2.00%Sodium tertiary phosphate 2.00%
암모니아 0.10%ammonia 0.10%
아세톤 8.00%Acetone 8.00%
물 잔량water Balance
상기 성분물질을 교반기에 넣고 상온에서 1시간 동안 교반하여 연한 갈색의 현탁액을 얻었으며 pH는 8.5로 측정되었다.The above material was placed in a stirrer and stirred at room temperature for 1 hour to obtain a pale brown suspension and the pH was measured at 8.5.
난연성 접착제Flame retardant adhesive
현탁액 2.50%Suspension 2.50%
염화칼슘 22.8%Calcium chloride 22.8%
염화마그네슘 24.3%Magnesium chloride 24.3%
물 잔량water Balance
상기 성분물질을 교반기에서 20분간 교반하면서 염도 23‰가 되도록 조절하여 소망의 발포 폴리스타이렌 난연성 접착제 조성물을 얻었다.The component material was stirred for 20 minutes in a stirrer to adjust the salt content to 23 ‰, thereby obtaining a desired foam polystyrene flame retardant adhesive composition.
송진용액Songjin solution
99% 이상의 고순도 송진 31.3%99% or more high purity 31.3%
중쇄 지방산 2.50%Heavy chain fatty acid 2.50%
디옥틸 테레프탈레이트 3.10%Dioctyl terephthalate 3.10%
디에칠렌 글리콜 1.00%Diethylene glycol 1.00%
폴리에칠렌글리콜 100 1.10%Polyethylene glycol 100 1.10%
이소프로필 알코올 41.0%Isopropyl alcohol 41.0%
메탄올 20.0%Methanol 20.0%
상기 성분물질을 교반기에 넣고 130℃ 분위기에서 1시간 30분 동안 교반하여 송진용액을 얻었다. 얻어진 송진용액은 교반을 거듭할수록 연한 갈색의 점성용액으로 변하였다.The ingredient material was placed in a stirrer and stirred at 130 ° C for 1 hour and 30 minutes to obtain a rosin solution. The resulting rosin solution turned into a light brown viscous solution with stirring.
현탁액Suspension
송진용액 1.00%Songjin solution 1.00%
아교 1.20%glue 1.20%
수산화나트륨 2.30%Sodium hydroxide 2.30%
수산화칼륨 2.70%Potassium hydroxide 2.70%
염화나트륨 1.00%Sodium chloride 1.00%
제3 인산소다 2.00%Sodium tertiary phosphate 2.00%
암모니아 0.10%ammonia 0.10%
아세톤 8.00%Acetone 8.00%
물 잔량water Balance
상기 성분물질을 교반기에 넣고 상온에서 1시간 동안 교반하여 연한 갈색의 현탁액을 얻었으며 pH는 8.5로 측정되었다.The above material was placed in a stirrer and stirred at room temperature for 1 hour to obtain a pale brown suspension and the pH was measured at 8.5.
난연성 접착제Flame retardant adhesive
현탁액 2.60%Suspension 2.60%
황산칼슘 20.0%Calcium sulfate 20.0%
염화마그네슘 29.0%Magnesium chloride 29.0%
물 잔량water Balance
상기 성분물질을 교반기에서 20분간 교반하면서 염도 24‰가 되도록 조절하여 소망의 발포 폴리스타이렌 난연성 접착제 조성물을 얻었다.The above ingredients were stirred for 20 minutes in a stirrer to adjust the salt content to 24 ‰ to obtain a desired polystyrene flame retardant adhesive composition.
송진용액Songjin solution
99% 이상의 고순도 송진 31.3%99% or more high purity 31.3%
중쇄 지방산 2.50%Heavy chain fatty acid 2.50%
디옥틸 테레프탈레이트 3.10%Dioctyl terephthalate 3.10%
디에칠렌 글리콜 1.00%Diethylene glycol 1.00%
폴리에칠렌글리콜 100 1.10%Polyethylene glycol 100 1.10%
이소프로필 알코올 41.0%Isopropyl alcohol 41.0%
메탄올 20.0%Methanol 20.0%
상기 성분물질을 교반기에 넣고 115℃ 분위기에서 1시간 동안 교반하여 송진용액을 얻었다. 송진용액은 교반을 거듭할수록 연한 갈색의 점성물질로 변하였다.The ingredient material was placed in a stirrer and stirred in an atmosphere at 115 ° C for 1 hour to obtain a rosin solution. The rosin solution turned into a light brown viscous substance with stirring.
현탁액Suspension
송진용액 1.00%Songjin solution 1.00%
아교 1.20%glue 1.20%
수산화나트륨 4.00%Sodium hydroxide 4.00%
수산화칼륨 1.00%Potassium hydroxide 1.00%
염화나트륨 1.00%Sodium chloride 1.00%
제3 인산소다 2.00%Sodium tertiary phosphate 2.00%
암모니아 0.10%ammonia 0.10%
아세톤 8.00%Acetone 8.00%
물 잔량water Balance
상기 성분물질을 교반기에 넣고 상온에서 1시간 동안 교반하여 연한 갈색의 현탁액을 얻었으며 pH는 8.5로 측정되었다.The above material was placed in a stirrer and stirred at room temperature for 1 hour to obtain a pale brown suspension and the pH was measured at 8.5.
난연성 접착제Flame retardant adhesive
현탁액 2.80%Suspension 2.80%
황산칼슘 32.0%Calcium sulfate 32.0%
염화마그네슘 20.2%Magnesium chloride 20.2%
물 잔량water Balance
상기 성분물질을 교반기에서 20분간 교반하면서 염도 25‰가 되도록 조절하여 소망의 발포 폴리스타이렌 난연성 접착제 조성물을 얻었다.The component material was stirred for 20 minutes in a stirrer to adjust the salt content to 25 ‰, thereby obtaining a desired foam polystyrene flame retardant adhesive composition.
송진용액Songjin solution
99% 이상의 고순도 송진 31.3%99% or more high purity 31.3%
중쇄 지방산 2.50%Heavy chain fatty acid 2.50%
디옥틸 테레프탈레이트 3.10%Dioctyl terephthalate 3.10%
디에칠렌 글리콜 1.00%Diethylene glycol 1.00%
폴리에칠렌글리콜 100 1.10%Polyethylene glycol 100 1.10%
이소프로필 알코올 41.0%Isopropyl alcohol 41.0%
메탄올 20.0%Methanol 20.0%
상기 성분물질을 교반기에 넣고 120℃ 분위기에서 1시간 동안 교반하여 송진용액을 얻었다.The ingredient material was placed in a stirrer and stirred for 1 hour in an atmosphere of 120 ° C to obtain a rosin solution.
현탁액Suspension
송진용액 1.50%Songjin solution 1.50%
아교 1.80%glue 1.80%
수산화칼륨 4.00%Potassium hydroxide 4.00%
수산화마그네슘 2.00%Magnesium hydroxide 2.00%
염화나트륨 1.50%Sodium chloride 1.50%
제3 인산소다 2.00%Sodium tertiary phosphate 2.00%
암모니아 0.15%ammonia 0.15%
3-브로모-사이클로헥사논 9.00%3-Bromo-cyclohexanone 9.00%
물 잔량water Balance
상기 성분물질을 교반기에 넣고 상온에서 1시간 동안 교반하여 연한 갈색의 현탁액을 얻었으며 pH는 8.5로 측정되었다.The above material was placed in a stirrer and stirred at room temperature for 1 hour to obtain a pale brown suspension and the pH was measured at 8.5.
난연성 접착제Flame retardant adhesive
현탁액 2.30%Suspension 2.30%
황산칼슘 25.8%Calcium sulfate 25.8%
염화마그네슘 19.4%Magnesium chloride 19.4%
물 잔량water Balance
상기 성분물질을 교반기에서 20분간 교반하면서 염도 24‰가 되도록 조절하여 소망의 발포 폴리스타이렌 난연성 접착제 조성물을 얻었다.The above ingredients were stirred for 20 minutes in a stirrer to adjust the salt content to 24 ‰ to obtain a desired polystyrene flame retardant adhesive composition.
송진용액Songjin solution
99% 이상의 고순도 송진 31.3%99% or more high purity 31.3%
중쇄 지방산 2.50%Heavy chain fatty acid 2.50%
디옥틸 테레프탈레이트 3.10%Dioctyl terephthalate 3.10%
디에칠렌 글리콜 1.00%Diethylene glycol 1.00%
폴리에칠렌글리콜 100 1.10%Polyethylene glycol 100 1.10%
이소프로필 알코올 41.0%Isopropyl alcohol 41.0%
메탄올 20.0%Methanol 20.0%
상기 성분물질을 교반기에 넣고 130℃ 분위기에서 1시간 30분 동안 교반하여 송진용액을 얻었다. 얻어진 송진용액은 교반을 거듭할수록 연한 갈색의 점성용액으로 변하였다.The ingredient material was placed in a stirrer and stirred at 130 ° C for 1 hour and 30 minutes to obtain a rosin solution. The resulting rosin solution turned into a light brown viscous solution with stirring.
현탁액Suspension
송진용액 1.50%Songjin solution 1.50%
아교 1.80%glue 1.80%
수산화나트륨 4.00%Sodium hydroxide 4.00%
수산화마그네슘 2.00%Magnesium hydroxide 2.00%
염화나트륨 1.50%Sodium chloride 1.50%
염화칼륨 2.00%Potassium chloride 2.00%
암모니아 0.15%ammonia 0.15%
3-브로모-사이클로헥사논 9.00%3-Bromo-cyclohexanone 9.00%
물 잔량water Balance
상기 성분물질을 교반기에 넣고 상온에서 1시간 동안 교반하여 연한 갈색의 현탁액을 얻었으며 pH는 8.6으로 측정되었다.The above material was placed in a stirrer and stirred at room temperature for 1 hour to obtain a pale brown suspension. The pH was measured to be 8.6.
난연성 접착제Flame retardant adhesive
현탁액 2.50%Suspension 2.50%
염화칼슘 22.8%Calcium chloride 22.8%
염화마그네슘 24.3%Magnesium chloride 24.3%
물 잔량water Balance
상기 성분물질을 교반기에서 20분간 교반하면서 염도 23‰가 되도록 조절하여 소망의 발포 폴리스타이렌 난연성 접착제 조성물을 얻었다.The component material was stirred for 20 minutes in a stirrer to adjust the salt content to 23 ‰, thereby obtaining a desired foam polystyrene flame retardant adhesive composition.
송진용액Songjin solution
99% 이상의 고순도 송진 31.3%99% or more high purity 31.3%
중쇄 지방산 2.50%Heavy chain fatty acid 2.50%
디옥틸 테레프탈레이트 3.10%Dioctyl terephthalate 3.10%
디에칠렌 글리콜 1.00%Diethylene glycol 1.00%
폴리에칠렌글리콜 100 1.10%Polyethylene glycol 100 1.10%
이소프로필 알코올 41.0%Isopropyl alcohol 41.0%
메탄올 20.0%Methanol 20.0%
상기 성분물질을 교반기에 넣고 115℃ 분위기에서 1시간 동안 교반하여 송진용액을 얻었다. 송진용액은 교반을 거듭할수록 연한 갈색의 점성물질로 변하였다.The ingredient material was placed in a stirrer and stirred in an atmosphere at 115 ° C for 1 hour to obtain a rosin solution. The rosin solution turned into a light brown viscous substance with stirring.
현탁액Suspension
송진용액 1.50%Songjin solution 1.50%
아교 1.80%glue 1.80%
수산화칼륨 2.00%Potassium hydroxide 2.00%
수산화마그네슘 4.00%Magnesium hydroxide 4.00%
염화구리 1.50%Copper chloride 1.50%
염화암모늄 2.00%Ammonium chloride 2.00%
트리메틸아민 0.15%Trimethylamine 0.15%
3-브로모-사이클로헥사논 9.00%3-Bromo-cyclohexanone 9.00%
물 잔량water Balance
상기 성분물질을 교반기에 넣고 상온에서 1시간 동안 교반하여 연한 갈색의 현탁액을 얻었으며 pH는 8.5로 측정되었다.The above material was placed in a stirrer and stirred at room temperature for 1 hour to obtain a pale brown suspension and the pH was measured at 8.5.
난연성 접착제Flame retardant adhesive
현탁액 2.60%Suspension 2.60%
황산칼슘 20.0%Calcium sulfate 20.0%
염화마그네슘 29.0%Magnesium chloride 29.0%
물 잔량water Balance
상기 성분물질을 교반기에서 20분간 교반하면서 염도 24‰가 되도록 조절하여 소망의 발포 폴리스타이렌 난연성 접착제 조성물을 얻었다.The above ingredients were stirred for 20 minutes in a stirrer to adjust the salt content to 24 ‰ to obtain a desired polystyrene flame retardant adhesive composition.
송진용액Songjin solution
99% 이상의 고순도 송진 32.8%99% or more high purity 32.8%
중쇄 지방산 2.80%Heavy chain fatty acid 2.80%
디옥틸 테레프탈레이트 2.30%Dioctyl terephthalate 2.30%
프로세스 오일 1.00%Process oil 1.00%
디에칠렌 글리콜 1.00%Diethylene glycol 1.00%
폴리에칠렌글리콜 100 1.40%Polyethylene glycol 100 1.40%
이소프로필 알코올 43.0%Isopropyl alcohol 43.0%
메탄올 15.7%Methanol 15.7%
상기 성분물질을 교반기에 넣고 120℃ 분위기에서 1시간 동안 교반하여 송진용액을 얻었다. 송진용액은 교반을 거듭할수록 연한 갈색의 점성물질로 변하였다.The ingredient material was placed in a stirrer and stirred for 1 hour in an atmosphere of 120 ° C to obtain a rosin solution. The rosin solution turned into a light brown viscous substance with stirring.
현탁액Suspension
송진용액 1.50%Songjin solution 1.50%
아교 1.80%glue 1.80%
수산화칼륨 2.00%Potassium hydroxide 2.00%
수산화마그네슘 4.00%Magnesium hydroxide 4.00%
염화구리 1.50%Copper chloride 1.50%
염화암모늄 2.00%Ammonium chloride 2.00%
트리메틸아민 0.15%Trimethylamine 0.15%
3-브로모-사이클로헥사논 9.00%3-Bromo-cyclohexanone 9.00%
물 잔량water Balance
상기 성분물질을 교반기에 넣고 상온에서 1시간 동안 교반하여 연한 갈색의 현탁액을 얻었으며 pH는 8.5로 측정되었다.The above material was placed in a stirrer and stirred at room temperature for 1 hour to obtain a pale brown suspension and the pH was measured at 8.5.
난연성 접착제Flame retardant adhesive
현탁액 2.80%Suspension 2.80%
황산칼슘 32.0%Calcium sulfate 32.0%
염화마그네슘 20.2%Magnesium chloride 20.2%
물 잔량water Balance
상기 성분물질을 교반기에서 20분간 교반하면서 염도 25‰가 되도록 조절하여 소망의 발포 폴리스타이렌 난연성 접착제 조성물을 얻었다.The component material was stirred for 20 minutes in a stirrer to adjust the salt content to 25 ‰, thereby obtaining a desired foam polystyrene flame retardant adhesive composition.
송진용액Songjin solution
99% 이상의 고순도 송진 32.8%99% or more high purity 32.8%
중쇄 지방산 2.80%Heavy chain fatty acid 2.80%
디옥틸 테레프탈레이트 2.30%Dioctyl terephthalate 2.30%
프로세스 오일 1.00%Process oil 1.00%
디에칠렌 글리콜 1.00%Diethylene glycol 1.00%
폴리에칠렌글리콜 100 1.40%Polyethylene glycol 100 1.40%
이소프로필 알코올 43.0%Isopropyl alcohol 43.0%
메탄올 15.7%Methanol 15.7%
상기 성분물질을 교반기에 넣고 120℃ 분위기에서 1시간 동안 교반하여 송진용액을 얻었다. 송진용액은 교반을 거듭할수록 연한 갈색의 점성물질로 변하였다.The ingredient material was placed in a stirrer and stirred for 1 hour in an atmosphere of 120 ° C to obtain a rosin solution. The rosin solution turned into a light brown viscous substance with stirring.
현탁액Suspension
송진용액 2.00%Songjin solution 2.00%
아교 2.40%glue 2.40%
수산화칼륨 5.00%Potassium hydroxide 5.00%
수산화마그네슘 2.00%Magnesium hydroxide 2.00%
염화나트륨 2.00%Sodium chloride 2.00%
염화칼슘 2.00%Calcium chloride 2.00%
아미노메틸프로판올 0.20%Aminomethyl propanol 0.20%
헥산-3-원 10.0%Hexane-3-one 10.0%
물 잔량water Balance
상기 성분물질을 교반기에 넣고 상온에서 1시간 동안 교반하여 연한 갈색의 현탁액을 얻었으며 pH는 8.8로 측정되었다.The ingredients were placed in a stirrer and stirred at room temperature for 1 hour to obtain a pale brown suspension, pH 8.8.
난연성 접착제Flame retardant adhesive
현탁액 2.30%Suspension 2.30%
황산칼슘 25.8%Calcium sulfate 25.8%
염화마그네슘 19.4%Magnesium chloride 19.4%
물 잔량water Balance
상기 성분물질을 교반기에서 20분간 교반하면서 염도 24‰가 되도록 조절하여 소망의 발포 폴리스타이렌 난연성 접착제 조성물을 얻었다.The above ingredients were stirred for 20 minutes in a stirrer to adjust the salt content to 24 ‰ to obtain a desired polystyrene flame retardant adhesive composition.
송진용액Songjin solution
99% 이상의 고순도 송진 32.8%99% or more high purity 32.8%
중쇄 지방산 2.80%Heavy chain fatty acid 2.80%
디옥틸 테레프탈레이트 2.30%Dioctyl terephthalate 2.30%
프로세스 오일 1.00%Process oil 1.00%
디에칠렌 글리콜 1.00%Diethylene glycol 1.00%
폴리에칠렌글리콜 100 1.40%Polyethylene glycol 100 1.40%
이소프로필 알코올 43.0%Isopropyl alcohol 43.0%
메탄올 15.7%Methanol 15.7%
상기 성분물질을 교반기에 넣고 120℃ 분위기에서 1시간 동안 교반하여 송진용액을 얻었다. 송진용액은 교반을 거듭할수록 연한 갈색의 점성물질로 변하였다.The ingredient material was placed in a stirrer and stirred for 1 hour in an atmosphere of 120 ° C to obtain a rosin solution. The rosin solution turned into a light brown viscous substance with stirring.
현탁액Suspension
송진용액 2.00%Songjin solution 2.00%
아교 2.40%glue 2.40%
수산화나트륨 5.00%Sodium hydroxide 5.00%
수산화마그네슘 2.00%Magnesium hydroxide 2.00%
염화나트륨 2.00%Sodium chloride 2.00%
염화은 1.00%Silver chloride 1.00%
염화암모늄 1.00%Ammonium chloride 1.00%
아미노메틸프로판올 0.20%Aminomethyl propanol 0.20%
헥산-3-원 10.0%Hexane-3-one 10.0%
물 잔량water Balance
상기 성분물질을 교반기에 넣고 상온에서 1시간 동안 교반하여 연한 갈색의 현탁액을 얻었으며 pH는 8.8로 측정되었다.The ingredients were placed in a stirrer and stirred at room temperature for 1 hour to obtain a pale brown suspension, pH 8.8.
난연성 접착제Flame retardant adhesive
현탁액 2.50%Suspension 2.50%
염화칼슘 22.8%Calcium chloride 22.8%
염화마그네슘 24.3%Magnesium chloride 24.3%
물 잔량water Balance
상기 성분물질을 교반기에서 20분간 교반하면서 염도 23‰가 되도록 조절하여 소망의 발포 폴리스타이렌 난연성 접착제 조성물을 얻었다.The component material was stirred for 20 minutes in a stirrer to adjust the salt content to 23 ‰, thereby obtaining a desired foam polystyrene flame retardant adhesive composition.
송진용액Songjin solution
99% 이상의 고순도 송진 32.8%99% or more high purity 32.8%
중쇄 지방산 2.80%Heavy chain fatty acid 2.80%
디옥틸 테레프탈레이트 2.30%Dioctyl terephthalate 2.30%
프로세스 오일 1.00%Process oil 1.00%
디에칠렌 글리콜 1.00%Diethylene glycol 1.00%
폴리에칠렌글리콜 100 1.40%Polyethylene glycol 100 1.40%
이소프로필 알코올 43.0%Isopropyl alcohol 43.0%
메탄올 15.7%Methanol 15.7%
상기 성분물질을 교반기에 넣고 120℃ 분위기에서 1시간 동안 교반하여 송진용액을 얻었다. 송진용액은 교반을 거듭할수록 연한 갈색의 점성물질로 변하였다.The ingredient material was placed in a stirrer and stirred for 1 hour in an atmosphere of 120 ° C to obtain a rosin solution. The rosin solution turned into a light brown viscous substance with stirring.
현탁액Suspension
송진용액 2.00%Songjin solution 2.00%
아교 2.40%glue 2.40%
수산화나트륨 4.00%Sodium hydroxide 4.00%
수산화마그네슘 3.00%Magnesium hydroxide 3.00%
염화나트륨 1.00%Sodium chloride 1.00%
염화은 0.50%Silver chloride 0.50%
염화암모늄 2.50%Ammonium chloride 2.50%
트리메틸아민 0.20%Trimethylamine 0.20%
헥산-3-원 10.0%Hexane-3-one 10.0%
물 잔량water Balance
상기 성분물질을 교반기에 넣고 상온에서 1시간 동안 교반하여 연한 갈색의 현탁액을 얻었으며 pH는 8.6로 측정되었다.The above ingredients were placed in a stirrer and stirred at room temperature for 1 hour to obtain a pale brown suspension and the pH was measured to be 8.6.
난연성 접착제Flame retardant adhesive
현탁액 2.60%Suspension 2.60%
황산칼슘 20.0%Calcium sulfate 20.0%
염화마그네슘 29.0%Magnesium chloride 29.0%
물 잔량water Balance
상기 성분물질을 교반기에서 20분간 교반하면서 염도 24‰가 되도록 조절하여 소망의 발포 폴리스타이렌 난연성 접착제 조성물을 얻었다.The above ingredients were stirred for 20 minutes in a stirrer to adjust the salt content to 24 ‰ to obtain a desired polystyrene flame retardant adhesive composition.
송진용액Songjin solution
99% 이상의 고순도 송진 32.8%99% or more high purity 32.8%
중쇄 지방산 2.80%Heavy chain fatty acid 2.80%
디옥틸 테레프탈레이트 2.30%Dioctyl terephthalate 2.30%
프로세스 오일 1.00%Process oil 1.00%
디에칠렌 글리콜 1.00%Diethylene glycol 1.00%
폴리에칠렌글리콜 100 1.40%Polyethylene glycol 100 1.40%
이소프로필 알코올 43.0%Isopropyl alcohol 43.0%
메탄올 15.7%Methanol 15.7%
상기 성분물질을 교반기에 넣고 120℃ 분위기에서 1시간 동안 교반하여 송진용액을 얻었다. 송진용액은 교반을 거듭할수록 연한 갈색의 점성물질로 변하였다.The ingredient material was placed in a stirrer and stirred for 1 hour in an atmosphere of 120 ° C to obtain a rosin solution. The rosin solution turned into a light brown viscous substance with stirring.
현탁액Suspension
송진용액 2.00%Songjin solution 2.00%
아교 2.40%glue 2.40%
수산화나트륨 4.00%Sodium hydroxide 4.00%
수산화마그네슘 3.00%Magnesium hydroxide 3.00%
염화나트륨 1.00%Sodium chloride 1.00%
염화은 0.50%Silver chloride 0.50%
염화암모늄 2.50%Ammonium chloride 2.50%
트리메틸아민 0.20%Trimethylamine 0.20%
헥산-3-원 10.0%Hexane-3-one 10.0%
물 잔량water Balance
상기 성분물질을 교반기에 넣고 상온에서 1시간 동안 교반하여 연한 갈색의 현탁액을 얻었으며 pH는 8.9로 측정되었다.The above material was placed in a stirrer and stirred at room temperature for 1 hour to obtain a pale brown suspension. The pH was measured to be 8.9.
난연성 접착제Flame retardant adhesive
현탁액 2.80%Suspension 2.80%
황산칼슘 32.0%Calcium sulfate 32.0%
염화마그네슘 20.2%Magnesium chloride 20.2%
물 잔량water Balance
상기 성분물질을 교반기에서 20분간 교반하면서 염도 25‰가 되도록 조절하여 소망의 발포 폴리스타이렌 난연성 접착제 조성물을 얻었다.The component material was stirred for 20 minutes in a stirrer to adjust the salt content to 25 ‰, thereby obtaining a desired foam polystyrene flame retardant adhesive composition.
송진용액Songjin solution
99% 이상의 고순도 송진 32.8%99% or more high purity 32.8%
중쇄 지방산 2.80%Heavy chain fatty acid 2.80%
디옥틸 테레프탈레이트 2.30%Dioctyl terephthalate 2.30%
프로세스 오일 1.00%Process oil 1.00%
디에칠렌 글리콜 1.00%Diethylene glycol 1.00%
폴리에칠렌글리콜 100 1.40%Polyethylene glycol 100 1.40%
이소프로필 알코올 43.0%Isopropyl alcohol 43.0%
메탄올 15.7%Methanol 15.7%
상기 성분물질을 교반기에 넣고 120℃ 분위기에서 1시간 동안 교반하여 송진용액을 얻었다. 송진용액은 교반을 거듭할수록 연한 갈색의 점성물질로 변하였다.The ingredient material was placed in a stirrer and stirred for 1 hour in an atmosphere of 120 ° C to obtain a rosin solution. The rosin solution turned into a light brown viscous substance with stirring.
현탁액Suspension
송진용액 2.50%Songjin solution 2.50%
아교 3.00%glue 3.00%
수산화나트륨 3.00%Sodium hydroxide 3.00%
수산화칼륨 5.00%Potassium hydroxide 5.00%
염화나트륨 1.00%Sodium chloride 1.00%
염화구리 1.50%Copper chloride 1.50%
제3 인산소다 2.00%Sodium tertiary phosphate 2.00%
암모니아 0.10%ammonia 0.10%
트리메틸아민 0.15%Trimethylamine 0.15%
아세톤 11.0%Acetone 11.0%
물 잔량water Balance
상기 성분물질을 교반기에 넣고 상온에서 1시간 동안 교반하여 연한 갈색의 현탁액을 얻었으며 pH는 8.8로 측정되었다.The ingredients were placed in a stirrer and stirred at room temperature for 1 hour to obtain a pale brown suspension, pH 8.8.
난연성 접착제Flame retardant adhesive
현탁액 2.30%Suspension 2.30%
황산칼슘 25.8%Calcium sulfate 25.8%
염화마그네슘 19.4%Magnesium chloride 19.4%
물 잔량water Balance
상기 성분물질을 교반기에서 20분간 교반하면서 염도 24‰가 되도록 조절하여 소망의 발포 폴리스타이렌 난연성 접착제 조성물을 얻었다.The above ingredients were stirred for 20 minutes in a stirrer to adjust the salt content to 24 ‰ to obtain a desired polystyrene flame retardant adhesive composition.
송진용액Songjin solution
99% 이상의 고순도 송진 31.3%99% or more high purity 31.3%
중쇄 지방산 2.50%Heavy chain fatty acid 2.50%
디옥틸 테레프탈레이트 3.10%Dioctyl terephthalate 3.10%
디에칠렌 글리콜 1.00%Diethylene glycol 1.00%
폴리에칠렌글리콜 100 1.10%Polyethylene glycol 100 1.10%
이소프로필 알코올 41.0%Isopropyl alcohol 41.0%
메탄올 20.0%Methanol 20.0%
상기 성분물질을 교반기에 넣고 115℃ 분위기에서 1시간 동안 교반하여 송진용액을 얻었다. 송진용액은 교반을 거듭할수록 연한 갈색의 점성물질로 변하였다.The ingredient material was placed in a stirrer and stirred in an atmosphere at 115 ° C for 1 hour to obtain a rosin solution. The rosin solution turned into a light brown viscous substance with stirring.
현탁액Suspension
송진용액 2.50%Songjin solution 2.50%
아교 3.00%glue 3.00%
수산화마그네슘 2.00%Magnesium hydroxide 2.00%
수산화나트륨 6.00%Sodium hydroxide 6.00%
염화칼륨 1.50%Potassium chloride 1.50%
염화은 1.50%Silver chloride 1.50%
제3 인산소다 1.50%Sodium tertiary phosphate 1.50%
암모니아 0.15%ammonia 0.15%
아미노메틸프로판올 0.10%Aminomethyl propanol 0.10%
아세톤 11.0%Acetone 11.0%
물 잔량water Balance
상기 성분물질을 교반기에 넣고 상온에서 1시간 동안 교반하여 연한 갈색의 현탁액을 얻었으며 pH는 8.5로 측정되었다.The above material was placed in a stirrer and stirred at room temperature for 1 hour to obtain a pale brown suspension and the pH was measured at 8.5.
난연성 접착제Flame retardant adhesive
현탁액 2.50%Suspension 2.50%
염화칼슘 22.8%Calcium chloride 22.8%
염화마그네슘 24.3%Magnesium chloride 24.3%
물 잔량water Balance
상기 성분물질을 교반기에서 20분간 교반하면서 염도 23‰가 되도록 조절하여 소망의 발포 폴리스타이렌 난연성 접착제 조성물을 얻었다.The component material was stirred for 20 minutes in a stirrer to adjust the salt content to 23 ‰, thereby obtaining a desired foam polystyrene flame retardant adhesive composition.
송진용액Songjin solution
99% 이상의 고순도 송진 32.8%99% or more high purity 32.8%
중쇄 지방산 2.80%Heavy chain fatty acid 2.80%
디옥틸 테레프탈레이트 2.30%Dioctyl terephthalate 2.30%
프로세스 오일 1.00%Process oil 1.00%
디에칠렌 글리콜 1.00%Diethylene glycol 1.00%
폴리에칠렌글리콜 100 1.40%Polyethylene glycol 100 1.40%
이소프로필 알코올 43.0%Isopropyl alcohol 43.0%
메탄올 15.7%Methanol 15.7%
상기 성분물질을 교반기에 넣고 120℃ 분위기에서 1시간 동안 교반하여 송진용액을 얻었다. 송진용액은 교반을 거듭할수록 연한 갈색의 점성물질로 변하였다.The ingredient material was placed in a stirrer and stirred for 1 hour in an atmosphere of 120 ° C to obtain a rosin solution. The rosin solution turned into a light brown viscous substance with stirring.
현탁액Suspension
송진용액 2.50%Songjin solution 2.50%
아교 3.00%glue 3.00%
수산화마그네슘 5.00%Magnesium hydroxide 5.00%
수산화나트륨 3.00%Sodium hydroxide 3.00%
염화칼슘 2.50%Calcium chloride 2.50%
염화은 0.50%Silver chloride 0.50%
제3 인산소다 1.50%Sodium tertiary phosphate 1.50%
암모니아 0.20%ammonia 0.20%
아미노메틸프로판올 0.05%Aminomethyl propanol 0.05%
아세톤 12.0%Acetone 12.0%
물 잔량water Balance
상기 성분물질을 교반기에 넣고 상온에서 1시간 동안 교반하여 연한 갈색의 현탁액을 얻었으며 pH는 8.8로 측정되었다.The ingredients were placed in a stirrer and stirred at room temperature for 1 hour to obtain a pale brown suspension, pH 8.8.
난연성 접착제Flame retardant adhesive
현탁액 2.60%Suspension 2.60%
황산칼슘 20.0%Calcium sulfate 20.0%
염화마그네슘 29.0%Magnesium chloride 29.0%
물 잔량water Balance
상기 성분물질을 교반기에서 20분간 교반하면서 염도 24‰가 되도록 조절하여 소망의 발포 폴리스타이렌 난연성 접착제 조성물을 얻었다.The above ingredients were stirred for 20 minutes in a stirrer to adjust the salt content to 24 ‰ to obtain a desired polystyrene flame retardant adhesive composition.
송진용액Songjin solution
99% 이상의 고순도 송진 32.8%99% or more high purity 32.8%
중쇄 지방산 2.80%Heavy chain fatty acid 2.80%
디옥틸 테레프탈레이트 2.30%Dioctyl terephthalate 2.30%
프로세스 오일 1.00%Process oil 1.00%
디에칠렌 글리콜 1.00%Diethylene glycol 1.00%
폴리에칠렌글리콜 100 1.40%Polyethylene glycol 100 1.40%
이소프로필 알코올 43.0%Isopropyl alcohol 43.0%
메탄올 15.7%Methanol 15.7%
상기 성분물질을 교반기에 넣고 120℃ 분위기에서 1시간 동안 교반하여 송진용액을 얻었다. 송진용액은 교반을 거듭할수록 연한 갈색의 점성물질로 변하였다.The ingredient material was placed in a stirrer and stirred for 1 hour in an atmosphere of 120 ° C to obtain a rosin solution. The rosin solution turned into a light brown viscous substance with stirring.
현탁액Suspension
송진용액 2.50%Songjin solution 2.50%
아교 3.00%glue 3.00%
수산화마그네슘 5.00%Magnesium hydroxide 5.00%
수산화나트륨 3.00%Sodium hydroxide 3.00%
염화칼슘 2.50%Calcium chloride 2.50%
염화은 0.50%Silver chloride 0.50%
제3 인산소다 1.50%Sodium tertiary phosphate 1.50%
암모니아 0.20%ammonia 0.20%
아미노메틸프로판올 0.05%Aminomethyl propanol 0.05%
아세톤 12.0%Acetone 12.0%
물 잔량water Balance
상기 성분물질을 교반기에 넣고 상온에서 1시간 동안 교반하여 연한 갈색의 현탁액을 얻었으며 pH는 8.6으로 측정되었다.The above material was placed in a stirrer and stirred at room temperature for 1 hour to obtain a pale brown suspension. The pH was measured to be 8.6.
난연성 접착제Flame retardant adhesive
현탁액 2.80%Suspension 2.80%
황산칼슘 32.0%Calcium sulfate 32.0%
염화마그네슘 20.2%Magnesium chloride 20.2%
물 잔량water Balance
상기 성분물질을 교반기에서 20분간 교반하면서 염도 25‰가 되도록 조절하여 소망의 발포 폴리스타이렌 난연성 접착제 조성물을 얻었다.The component material was stirred for 20 minutes in a stirrer to adjust the salt content to 25 ‰, thereby obtaining a desired foam polystyrene flame retardant adhesive composition.
송진용액Songjin solution
99% 이상의 고순도 송진 32.8%99% or more high purity 32.8%
중쇄 지방산 2.80%Heavy chain fatty acid 2.80%
디옥틸 테레프탈레이트 2.30%Dioctyl terephthalate 2.30%
프로세스 오일 1.00%Process oil 1.00%
디에칠렌 글리콜 1.00%Diethylene glycol 1.00%
폴리에칠렌글리콜 100 1.40%Polyethylene glycol 100 1.40%
이소프로필 알코올 43.0%Isopropyl alcohol 43.0%
메탄올 15.7%Methanol 15.7%
상기 성분물질을 교반기에 넣고 120℃ 분위기에서 1시간 동안 교반하여 송진용액을 얻었다. 송진용액은 교반을 거듭할수록 연한 갈색의 점성물질로 변하였다.The ingredient material was placed in a stirrer and stirred for 1 hour in an atmosphere of 120 ° C to obtain a rosin solution. The rosin solution turned into a light brown viscous substance with stirring.
현탁액Suspension
송진용액 2.50%Songjin solution 2.50%
아교 3.00%glue 3.00%
수산화나트륨 3.00%Sodium hydroxide 3.00%
수산화칼륨 5.00%Potassium hydroxide 5.00%
염화나트륨 1.00%Sodium chloride 1.00%
염화구리 1.50%Copper chloride 1.50%
제3 인산소다 2.00%Sodium tertiary phosphate 2.00%
암모니아 0.10%ammonia 0.10%
트리메틸아민 0.15%Trimethylamine 0.15%
3-브로모-사이클로헥사논 11.0%3-Bromo-cyclohexanone 11.0%
물 잔량water Balance
상기 성분물질을 교반기에 넣고 상온에서 1시간 동안 교반하여 연한 갈색의 현탁액을 얻었으며 pH는 8.8로 측정되었다.The ingredients were placed in a stirrer and stirred at room temperature for 1 hour to obtain a pale brown suspension, pH 8.8.
난연성 접착제Flame retardant adhesive
현탁액 2.30%Suspension 2.30%
황산칼슘 25.8%Calcium sulfate 25.8%
염화마그네슘 19.4%Magnesium chloride 19.4%
물 잔량water Balance
상기 성분물질을 교반기에서 20분간 교반하면서 염도 24‰가 되도록 조절하여 소망의 발포 폴리스타이렌 난연성 접착제 조성물을 얻었다.The above ingredients were stirred for 20 minutes in a stirrer to adjust the salt content to 24 ‰ to obtain a desired polystyrene flame retardant adhesive composition.
송진용액Songjin solution
99% 이상의 고순도 송진 32.8%99% or more high purity 32.8%
중쇄 지방산 2.80%Heavy chain fatty acid 2.80%
디옥틸 테레프탈레이트 2.30%Dioctyl terephthalate 2.30%
프로세스 오일 1.00%Process oil 1.00%
디에칠렌 글리콜 1.00%Diethylene glycol 1.00%
폴리에칠렌글리콜 100 1.40%Polyethylene glycol 100 1.40%
이소프로필 알코올 43.0%Isopropyl alcohol 43.0%
메탄올 15.7%Methanol 15.7%
상기 성분물질을 교반기에 넣고 120℃ 분위기에서 1시간 동안 교반하여 송진용액을 얻었다. 송진용액은 교반을 거듭할수록 연한 갈색의 점성물질로 변하였다.The ingredient material was placed in a stirrer and stirred for 1 hour in an atmosphere of 120 ° C to obtain a rosin solution. The rosin solution turned into a light brown viscous substance with stirring.
현탁액Suspension
송진용액 3.00%Songjin solution 3.00%
아교 3.60%glue 3.60%
수산화나트륨 3.00%Sodium hydroxide 3.00%
수산화칼슘 3.00%Calcium hydroxide 3.00%
수산화마그네슘 3.00%Magnesium hydroxide 3.00%
염화나트륨 1.00%Sodium chloride 1.00%
염화칼슘 1.00%Calcium chloride 1.00%
염화암모늄 1.00%Ammonium chloride 1.00%
염화수은 2.00%Mercury chloride 2.00%
암모니아 0.10%ammonia 0.10%
아미노메틸프로판올 0.20%Aminomethyl propanol 0.20%
3-브로모-사이클로헥사논 12.0%3-Bromo-cyclohexanone 12.0%
물 잔량water Balance
상기 성분물질을 교반기에 넣고 상온에서 1시간 동안 교반하여 연한 갈색의 현탁액을 얻었으며 pH는 8.9로 측정되었다.The above material was placed in a stirrer and stirred at room temperature for 1 hour to obtain a pale brown suspension. The pH was measured to be 8.9.
난연성 접착제Flame retardant adhesive
현탁액 2.50%Suspension 2.50%
염화칼슘 22.8%Calcium chloride 22.8%
염화마그네슘 24.3%Magnesium chloride 24.3%
물 잔량water Balance
상기 성분물질을 교반기에서 20분간 교반하면서 염도 23‰가 되도록 조절하여 소망의 발포 폴리스타이렌 난연성 접착제 조성물을 얻었다.The component material was stirred for 20 minutes in a stirrer to adjust the salt content to 23 ‰, thereby obtaining a desired foam polystyrene flame retardant adhesive composition.
송진용액Songjin solution
99% 이상의 고순도 송진 32.8%99% or more high purity 32.8%
중쇄 지방산 2.80%Heavy chain fatty acid 2.80%
디옥틸 테레프탈레이트 2.30%Dioctyl terephthalate 2.30%
프로세스 오일 1.00%Process oil 1.00%
디에칠렌 글리콜 1.00%Diethylene glycol 1.00%
폴리에칠렌글리콜 100 1.40%Polyethylene glycol 100 1.40%
이소프로필 알코올 43.0%Isopropyl alcohol 43.0%
메탄올 15.7%Methanol 15.7%
상기 성분물질을 교반기에 넣고 120℃ 분위기에서 1시간 동안 교반하여 송진용액을 얻었다. 송진용액은 교반을 거듭할수록 연한 갈색의 점성물질로 변하였다.The ingredient material was placed in a stirrer and stirred for 1 hour in an atmosphere of 120 ° C to obtain a rosin solution. The rosin solution turned into a light brown viscous substance with stirring.
현탁액Suspension
송진용액 3.00%Songjin solution 3.00%
아교 3.60%glue 3.60%
수산화나트륨 3.00%Sodium hydroxide 3.00%
수산화칼륨 3.00%Potassium hydroxide 3.00%
수산화마그네슘 3.00%Magnesium hydroxide 3.00%
염화나트륨 1.00%Sodium chloride 1.00%
제3 인산소다 2.00%Sodium tertiary phosphate 2.00%
염화수은 2.00%Mercury chloride 2.00%
암모니아 0.10%ammonia 0.10%
아미노메틸프로판올 0.10%Aminomethyl propanol 0.10%
트리메틸아민 0.10%Trimethylamine 0.10%
3-브로모-사이클로헥사논 12.0%3-Bromo-cyclohexanone 12.0%
물 잔량water Balance
상기 성분물질을 교반기에 넣고 상온에서 1시간 동안 교반하여 연한 갈색의 현탁액을 얻었으며 pH는 8.9로 측정되었다.The above material was placed in a stirrer and stirred at room temperature for 1 hour to obtain a pale brown suspension. The pH was measured to be 8.9.
난연성 접착제Flame retardant adhesive
현탁액 2.60%Suspension 2.60%
황산칼슘 20.0%Calcium sulfate 20.0%
염화마그네슘 29.0%Magnesium chloride 29.0%
물 잔량water Balance
상기 성분물질을 교반기에서 20분간 교반하면서 염도 24‰가 되도록 조절하여 소망의 발포 폴리스타이렌 난연성 접착제 조성물을 얻었다.The above ingredients were stirred for 20 minutes in a stirrer to adjust the salt content to 24 ‰ to obtain a desired polystyrene flame retardant adhesive composition.
송진용액Songjin solution
99% 이상의 고순도 송진 32.8%99% or more high purity 32.8%
중쇄 지방산 2.80%Heavy chain fatty acid 2.80%
디옥틸 테레프탈레이트 2.30%Dioctyl terephthalate 2.30%
프로세스 오일 1.00%Process oil 1.00%
디에칠렌 글리콜 1.00%Diethylene glycol 1.00%
폴리에칠렌글리콜 100 1.40%Polyethylene glycol 100 1.40%
이소프로필 알코올 43.0%Isopropyl alcohol 43.0%
메탄올 15.7%Methanol 15.7%
상기 성분물질을 교반기에 넣고 120℃ 분위기에서 1시간 동안 교반하여 송진용액을 얻었다. 송진용액은 교반을 거듭할수록 연한 갈색의 점성물질로 변하였다.The ingredient material was placed in a stirrer and stirred for 1 hour in an atmosphere of 120 ° C to obtain a rosin solution. The rosin solution turned into a light brown viscous substance with stirring.
현탁액Suspension
송진용액 3.00%Songjin solution 3.00%
아교 3.60%glue 3.60%
수산화나트륨 3.00%Sodium hydroxide 3.00%
수산화칼륨 3.00%Potassium hydroxide 3.00%
수산화마그네슘 3.00%Magnesium hydroxide 3.00%
염화나트륨 1.00%Sodium chloride 1.00%
제3 인산소다 2.00%Sodium tertiary phosphate 2.00%
염화수은 2.00%Mercury chloride 2.00%
암모니아 0.10%ammonia 0.10%
아미노메틸프로판올 0.10%Aminomethyl propanol 0.10%
트리메틸아민 0.10%Trimethylamine 0.10%
3-브로모-사이클로헥사논 12.0%3-Bromo-cyclohexanone 12.0%
물 잔량water Balance
상기 성분물질을 교반기에 넣고 상온에서 1시간 동안 교반하여 연한 갈색의 현탁액을 얻었으며 pH는 8.8로 측정되었다.The ingredients were placed in a stirrer and stirred at room temperature for 1 hour to obtain a pale brown suspension, pH 8.8.
난연성 접착제Flame retardant adhesive
현탁액 2.80%Suspension 2.80%
황산칼슘 32.0%Calcium sulfate 32.0%
염화마그네슘 20.2%Magnesium chloride 20.2%
물 잔량water Balance
상기 성분물질을 교반기에서 20분간 교반하면서 염도 25‰가 되도록 조절하여 소망의 발포 폴리스타이렌 난연성 접착제 조성물을 얻었다.The component material was stirred for 20 minutes in a stirrer to adjust the salt content to 25 ‰, thereby obtaining a desired foam polystyrene flame retardant adhesive composition.
송진용액Songjin solution
99% 이상의 고순도 송진 32.8%99% or more high purity 32.8%
중쇄 지방산 2.80%Heavy chain fatty acid 2.80%
디옥틸 테레프탈레이트 2.30%Dioctyl terephthalate 2.30%
프로세스 오일 1.00%Process oil 1.00%
디에칠렌 글리콜 1.00%Diethylene glycol 1.00%
폴리에칠렌글리콜 100 1.40%Polyethylene glycol 100 1.40%
이소프로필 알코올 43.0%Isopropyl alcohol 43.0%
메탄올 15.7%Methanol 15.7%
상기 성분물질을 교반기에 넣고 120℃ 분위기에서 1시간 동안 교반하여 송진용액을 얻었다. 송진용액은 교반을 거듭할수록 연한 갈색의 점성물질로 변하였다.The ingredient material was placed in a stirrer and stirred for 1 hour in an atmosphere of 120 ° C to obtain a rosin solution. The rosin solution turned into a light brown viscous substance with stirring.
현탁액Suspension
송진용액 1.00%Songjin solution 1.00%
아교 1.20%glue 1.20%
수산화나트륨 3.00%Sodium hydroxide 3.00%
수산화칼륨 2.00%Potassium hydroxide 2.00%
염화나트륨 1.00%Sodium chloride 1.00%
제3 인산소다 2.00%Sodium tertiary phosphate 2.00%
암모니아 0.10%ammonia 0.10%
아세톤 8.00%Acetone 8.00%
물 잔량water Balance
상기 성분물질을 교반기에 넣고 상온에서 1시간 동안 교반하여 연한 갈색의 현탁액을 얻었으며 pH는 8.5로 측정되었다.The above material was placed in a stirrer and stirred at room temperature for 1 hour to obtain a pale brown suspension and the pH was measured at 8.5.
난연성 접착제Flame retardant adhesive
현탁액 2.30%Suspension 2.30%
황산칼슘 25.8%Calcium sulfate 25.8%
염화마그네슘 19.4%Magnesium chloride 19.4%
물 잔량water Balance
상기 성분물질을 교반기에서 20분간 교반하면서 염도 24‰가 되도록 조절하여 소망의 발포 폴리스타이렌 난연성 접착제 조성물을 얻었다.The above ingredients were stirred for 20 minutes in a stirrer to adjust the salt content to 24 ‰ to obtain a desired polystyrene flame retardant adhesive composition.
송진용액Songjin solution
99% 이상의 고순도 송진 32.8%99% or more high purity 32.8%
중쇄 지방산 2.80%Heavy chain fatty acid 2.80%
디옥틸 테레프탈레이트 2.30%Dioctyl terephthalate 2.30%
프로세스 오일 1.00%Process oil 1.00%
디에칠렌 글리콜 1.00%Diethylene glycol 1.00%
폴리에칠렌글리콜 100 1.40%Polyethylene glycol 100 1.40%
이소프로필 알코올 43.0%Isopropyl alcohol 43.0%
메탄올 15.7%Methanol 15.7%
상기 성분물질을 교반기에 넣고 120℃ 분위기에서 1시간 동안 교반하여 송진용액을 얻었다. 송진용액은 교반을 거듭할수록 연한 갈색의 점성물질로 변하였다.The ingredient material was placed in a stirrer and stirred for 1 hour in an atmosphere of 120 ° C to obtain a rosin solution. The rosin solution turned into a light brown viscous substance with stirring.
현탁액Suspension
송진용액 1.00%Songjin solution 1.00%
아교 1.20%glue 1.20%
수산화나트륨 3.00%Sodium hydroxide 3.00%
수산화칼륨 2.00%Potassium hydroxide 2.00%
염화나트륨 1.00%Sodium chloride 1.00%
제3 인산소다 2.00%Sodium tertiary phosphate 2.00%
암모니아 0.10%ammonia 0.10%
아세톤 8.00%Acetone 8.00%
물 잔량water Balance
상기 성분물질을 교반기에 넣고 상온에서 1시간 동안 교반하여 연한 갈색의 현탁액을 얻었으며 pH는 8.5로 측정되었다.The above material was placed in a stirrer and stirred at room temperature for 1 hour to obtain a pale brown suspension and the pH was measured at 8.5.
난연성 접착제Flame retardant adhesive
현탁액 2.50%Suspension 2.50%
염화칼슘 22.8%Calcium chloride 22.8%
염화마그네슘 24.3%Magnesium chloride 24.3%
물 잔량water Balance
상기 성분물질을 교반기에서 20분간 교반하면서 염도 23‰가 되도록 조절하여 소망의 발포 폴리스타이렌 난연성 접착제 조성물을 얻었다.The component material was stirred for 20 minutes in a stirrer to adjust the salt content to 23 ‰, thereby obtaining a desired foam polystyrene flame retardant adhesive composition.
송진용액Songjin solution
99% 이상의 고순도 송진 32.8%99% or more high purity 32.8%
중쇄 지방산 2.80%Heavy chain fatty acid 2.80%
디옥틸 테레프탈레이트 2.30%Dioctyl terephthalate 2.30%
프로세스 오일 1.00%Process oil 1.00%
디에칠렌 글리콜 1.00%Diethylene glycol 1.00%
폴리에칠렌글리콜 100 1.40%Polyethylene glycol 100 1.40%
이소프로필 알코올 43.0%Isopropyl alcohol 43.0%
메탄올 15.7%Methanol 15.7%
상기 성분물질을 교반기에 넣고 120℃ 분위기에서 1시간 동안 교반하여 송진용액을 얻었다. 송진용액은 교반을 거듭할수록 연한 갈색의 점성물질로 변하였다.The ingredient material was placed in a stirrer and stirred for 1 hour in an atmosphere of 120 ° C to obtain a rosin solution. The rosin solution turned into a light brown viscous substance with stirring.
현탁액Suspension
송진용액 1.00%Songjin solution 1.00%
아교 1.20%glue 1.20%
수산화나트륨 2.30%Sodium hydroxide 2.30%
수산화칼륨 2.70%Potassium hydroxide 2.70%
염화나트륨 1.00%Sodium chloride 1.00%
제3 인산소다 2.00%Sodium tertiary phosphate 2.00%
암모니아 0.10%ammonia 0.10%
아세톤 8.00%Acetone 8.00%
물 잔량water Balance
상기 성분물질을 교반기에 넣고 상온에서 1시간 동안 교반하여 연한 갈색의 현탁액을 얻었으며 pH는 8.5로 측정되었다.The above material was placed in a stirrer and stirred at room temperature for 1 hour to obtain a pale brown suspension and the pH was measured at 8.5.
난연성 접착제Flame retardant adhesive
현탁액 2.60%Suspension 2.60%
황산칼슘 20.0%Calcium sulfate 20.0%
염화마그네슘 29.0%Magnesium chloride 29.0%
물 잔량water Balance
상기 성분물질을 교반기에서 20분간 교반하면서 염도 24‰가 되도록 조절하여 소망의 발포 폴리스타이렌 난연성 접착제 조성물을 얻었다.The above ingredients were stirred for 20 minutes in a stirrer to adjust the salt content to 24 ‰ to obtain a desired polystyrene flame retardant adhesive composition.
송진용액Songjin solution
99% 이상의 고순도 송진 32.8%99% or more high purity 32.8%
중쇄 지방산 2.80%Heavy chain fatty acid 2.80%
디옥틸 테레프탈레이트 2.30%Dioctyl terephthalate 2.30%
프로세스 오일 1.00%Process oil 1.00%
디에칠렌 글리콜 1.00%Diethylene glycol 1.00%
폴리에칠렌글리콜 100 1.40%Polyethylene glycol 100 1.40%
이소프로필 알코올 43.0%Isopropyl alcohol 43.0%
메탄올 15.7%Methanol 15.7%
상기 성분물질을 교반기에 넣고 120℃ 분위기에서 1시간 동안 교반하여 송진용액을 얻었다. 송진용액은 교반을 거듭할수록 연한 갈색의 점성물질로 변하였다.The ingredient material was placed in a stirrer and stirred for 1 hour in an atmosphere of 120 ° C to obtain a rosin solution. The rosin solution turned into a light brown viscous substance with stirring.
현탁액Suspension
송진용액 1.00%Songjin solution 1.00%
아교 1.20%glue 1.20%
수산화나트륨 4.00%Sodium hydroxide 4.00%
수산화칼륨 1.00%Potassium hydroxide 1.00%
염화나트륨 1.00%Sodium chloride 1.00%
제3 인산소다 2.00%Sodium tertiary phosphate 2.00%
암모니아 0.10%ammonia 0.10%
아세톤 8.00%Acetone 8.00%
물 잔량water Balance
상기 성분물질을 교반기에 넣고 상온에서 1시간 동안 교반하여 연한 갈색의 현탁액을 얻었으며 pH는 8.5로 측정되었다.The above material was placed in a stirrer and stirred at room temperature for 1 hour to obtain a pale brown suspension and the pH was measured at 8.5.
난연성 접착제Flame retardant adhesive
현탁액 2.80%Suspension 2.80%
황산칼슘 32.0%Calcium sulfate 32.0%
염화마그네슘 20.2%Magnesium chloride 20.2%
물 잔량water Balance
상기 성분물질을 교반기에서 20분간 교반하면서 염도 25‰가 되도록 조절하여 소망의 발포 폴리스타이렌 난연성 접착제 조성물을 얻었다.The component material was stirred for 20 minutes in a stirrer to adjust the salt content to 25 ‰, thereby obtaining a desired foam polystyrene flame retardant adhesive composition.
송진용액Songjin solution
99% 이상의 고순도 송진 32.8%99% or more high purity 32.8%
중쇄 지방산 2.80%Heavy chain fatty acid 2.80%
디옥틸 테레프탈레이트 2.30%Dioctyl terephthalate 2.30%
프로세스 오일 1.00%Process oil 1.00%
디에칠렌 글리콜 1.00%Diethylene glycol 1.00%
폴리에칠렌글리콜 100 1.40%Polyethylene glycol 100 1.40%
이소프로필 알코올 43.0%Isopropyl alcohol 43.0%
메탄올 15.7%Methanol 15.7%
상기 성분물질을 교반기에 넣고 120℃ 분위기에서 1시간 동안 교반하여 송진용액을 얻었다. 송진용액은 교반을 거듭할수록 연한 갈색의 점성물질로 변하였다.The ingredient material was placed in a stirrer and stirred for 1 hour in an atmosphere of 120 ° C to obtain a rosin solution. The rosin solution turned into a light brown viscous substance with stirring.
현탁액Suspension
송진용액 1.50%Songjin solution 1.50%
아교 1.80%glue 1.80%
수산화칼륨 4.00%Potassium hydroxide 4.00%
수산화마그네슘 2.00%Magnesium hydroxide 2.00%
염화나트륨 1.50%Sodium chloride 1.50%
제3 인산소다 2.00%Sodium tertiary phosphate 2.00%
암모니아 0.15%ammonia 0.15%
3-브로모-사이클로헥사논 9.00%3-Bromo-cyclohexanone 9.00%
물 잔량water Balance
상기 성분물질을 교반기에 넣고 상온에서 1시간 동안 교반하여 연한 갈색의 현탁액을 얻었으며 pH는 8.5로 측정되었다.The above material was placed in a stirrer and stirred at room temperature for 1 hour to obtain a pale brown suspension and the pH was measured at 8.5.
난연성 접착제Flame retardant adhesive
현탁액 2.30%Suspension 2.30%
황산칼슘 25.8%Calcium sulfate 25.8%
염화마그네슘 19.4%Magnesium chloride 19.4%
물 잔량water Balance
상기 성분물질을 교반기에서 20분간 교반하면서 염도 24‰가 되도록 조절하여 소망의 발포 폴리스타이렌 난연성 접착제 조성물을 얻었다.The above ingredients were stirred for 20 minutes in a stirrer to adjust the salt content to 24 ‰ to obtain a desired polystyrene flame retardant adhesive composition.
송진용액Songjin solution
99% 이상의 고순도 송진 32.8%99% or more high purity 32.8%
중쇄 지방산 2.80%Heavy chain fatty acid 2.80%
디옥틸 테레프탈레이트 2.30%Dioctyl terephthalate 2.30%
프로세스 오일 1.00%Process oil 1.00%
디에칠렌 글리콜 1.00%Diethylene glycol 1.00%
폴리에칠렌글리콜 100 1.40%Polyethylene glycol 100 1.40%
이소프로필 알코올 43.0%Isopropyl alcohol 43.0%
메탄올 15.7%Methanol 15.7%
상기 성분물질을 교반기에 넣고 120℃ 분위기에서 1시간 동안 교반하여 송진용액을 얻었다. 송진용액은 교반을 거듭할수록 연한 갈색의 점성물질로 변하였다.The ingredient material was placed in a stirrer and stirred for 1 hour in an atmosphere of 120 ° C to obtain a rosin solution. The rosin solution turned into a light brown viscous substance with stirring.
현탁액Suspension
송진용액 1.50%Songjin solution 1.50%
아교 1.80%glue 1.80%
수산화나트륨 4.00%Sodium hydroxide 4.00%
수산화마그네슘 2.00%Magnesium hydroxide 2.00%
염화나트륨 1.50%Sodium chloride 1.50%
염화칼륨 2.00%Potassium chloride 2.00%
암모니아 0.15%ammonia 0.15%
3-브로모-사이클로헥사논 9.00%3-Bromo-cyclohexanone 9.00%
물 잔량water Balance
상기 성분물질을 교반기에 넣고 상온에서 1시간 동안 교반하여 연한 갈색의 현탁액을 얻었으며 pH는 8.6으로 측정되었다.The above material was placed in a stirrer and stirred at room temperature for 1 hour to obtain a pale brown suspension. The pH was measured to be 8.6.
난연성 접착제Flame retardant adhesive
현탁액 2.50%Suspension 2.50%
염화칼슘 22.8%Calcium chloride 22.8%
염화마그네슘 24.3%Magnesium chloride 24.3%
물 잔량water Balance
상기 성분물질을 교반기에서 20분간 교반하면서 염도 23‰가 되도록 조절하여 소망의 발포 폴리스타이렌 난연성 접착제 조성물을 얻었다.The component material was stirred for 20 minutes in a stirrer to adjust the salt content to 23 ‰, thereby obtaining a desired foam polystyrene flame retardant adhesive composition.
송진용액Songjin solution
99% 이상의 고순도 송진 32.8%99% or more high purity 32.8%
중쇄 지방산 2.80%Heavy chain fatty acid 2.80%
디옥틸 테레프탈레이트 2.30%Dioctyl terephthalate 2.30%
프로세스 오일 1.00%Process oil 1.00%
디에칠렌 글리콜 1.00%Diethylene glycol 1.00%
폴리에칠렌글리콜 100 1.40%Polyethylene glycol 100 1.40%
이소프로필 알코올 43.0%Isopropyl alcohol 43.0%
메탄올 15.7%Methanol 15.7%
상기 성분물질을 교반기에 넣고 120℃ 분위기에서 1시간 동안 교반하여 송진용액을 얻었다. 송진용액은 교반을 거듭할수록 연한 갈색의 점성물질로 변하였다.The ingredient material was placed in a stirrer and stirred for 1 hour in an atmosphere of 120 ° C to obtain a rosin solution. The rosin solution turned into a light brown viscous substance with stirring.
현탁액Suspension
송진용액 1.50%Songjin solution 1.50%
아교 1.80%glue 1.80%
수산화칼륨 2.00%Potassium hydroxide 2.00%
수산화마그네슘 4.00%Magnesium hydroxide 4.00%
염화구리 1.50%Copper chloride 1.50%
염화암모늄 2.00%Ammonium chloride 2.00%
트리메틸아민 0.15%Trimethylamine 0.15%
3-브로모-사이클로헥사논 9.00%3-Bromo-cyclohexanone 9.00%
물 잔량water Balance
상기 성분물질을 교반기에 넣고 상온에서 1시간 동안 교반하여 연한 갈색의 현탁액을 얻었으며 pH는 8.5로 측정되었다.The above material was placed in a stirrer and stirred at room temperature for 1 hour to obtain a pale brown suspension and the pH was measured at 8.5.
난연성 접착제Flame retardant adhesive
현탁액 2.60%Suspension 2.60%
황산칼슘 20.0%Calcium sulfate 20.0%
염화마그네슘 29.0%Magnesium chloride 29.0%
물 잔량water Balance
상기 성분물질을 교반기에서 20분간 교반하면서 염도 24‰가 되도록 조절하여 소망의 발포 폴리스타이렌 난연성 접착제 조성물을 얻었다.The above ingredients were stirred for 20 minutes in a stirrer to adjust the salt content to 24 ‰ to obtain a desired polystyrene flame retardant adhesive composition.
송진용액Songjin solution
99% 이상의 고순도 송진 32.8%99% or more high purity 32.8%
중쇄 지방산 2.80%Heavy chain fatty acid 2.80%
디옥틸 테레프탈레이트 2.30%Dioctyl terephthalate 2.30%
프로세스 오일 1.00%Process oil 1.00%
디에칠렌 글리콜 1.00%Diethylene glycol 1.00%
폴리에칠렌글리콜 100 1.40%Polyethylene glycol 100 1.40%
이소프로필 알코올 43.0%Isopropyl alcohol 43.0%
메탄올 15.7%Methanol 15.7%
상기 성분물질을 교반기에 넣고 120℃ 분위기에서 1시간 동안 교반하여 송진용액을 얻었다. 송진용액은 교반을 거듭할수록 연한 갈색의 점성물질로 변하였다.The ingredient material was placed in a stirrer and stirred for 1 hour in an atmosphere of 120 ° C to obtain a rosin solution. The rosin solution turned into a light brown viscous substance with stirring.
현탁액Suspension
송진용액 1.50%Songjin solution 1.50%
아교 1.80%glue 1.80%
수산화칼륨 2.00%Potassium hydroxide 2.00%
수산화마그네슘 4.00%Magnesium hydroxide 4.00%
염화구리 1.50%Copper chloride 1.50%
염화암모늄 2.00%Ammonium chloride 2.00%
트리메틸아민 0.15%Trimethylamine 0.15%
3-브로모-사이클로헥사논 9.00%3-Bromo-cyclohexanone 9.00%
물 잔량water Balance
상기 성분물질을 교반기에 넣고 상온에서 1시간 동안 교반하여 연한 갈색의 현탁액을 얻었으며 pH는 8.5로 측정되었다.The above material was placed in a stirrer and stirred at room temperature for 1 hour to obtain a pale brown suspension and the pH was measured at 8.5.
난연성 접착제Flame retardant adhesive
현탁액 2.80%Suspension 2.80%
황산칼슘 32.0%Calcium sulfate 32.0%
염화마그네슘 20.2%Magnesium chloride 20.2%
물 잔량water Balance
상기 성분물질을 교반기에서 20분간 교반하면서 염도 25‰가 되도록 조절하여 소망의 발포 폴리스타이렌 난연성 접착제 조성물을 얻었다.The component material was stirred for 20 minutes in a stirrer to adjust the salt content to 25 ‰, thereby obtaining a desired foam polystyrene flame retardant adhesive composition.
송진용액Songjin solution
99% 이상의 고순도 송진 32.8%99% or more high purity 32.8%
중쇄 지방산 2.80%Heavy chain fatty acid 2.80%
디옥틸 테레프탈레이트 2.30%Dioctyl terephthalate 2.30%
프로세스 오일 1.00%Process oil 1.00%
디에칠렌 글리콜 1.00%Diethylene glycol 1.00%
폴리에칠렌글리콜 100 1.40%Polyethylene glycol 100 1.40%
이소프로필 알코올 43.0%Isopropyl alcohol 43.0%
메탄올 15.7%Methanol 15.7%
상기 성분물질을 교반기에 넣고 120℃ 분위기에서 1시간 동안 교반하여 송진용액을 얻었다. 송진용액은 교반을 거듭할수록 연한 갈색의 점성물질로 변하였다.The ingredient material was placed in a stirrer and stirred for 1 hour in an atmosphere of 120 ° C to obtain a rosin solution. The rosin solution turned into a light brown viscous substance with stirring.
현탁액Suspension
송진용액 2.00%Songjin solution 2.00%
아교 2.40%glue 2.40%
수산화칼륨 5.00%Potassium hydroxide 5.00%
수산화마그네슘 2.00%Magnesium hydroxide 2.00%
염화나트륨 2.00%Sodium chloride 2.00%
염화칼슘 2.00%Calcium chloride 2.00%
아미노메틸프로판올 0.20%Aminomethyl propanol 0.20%
헥산-3-원 10.0%Hexane-3-one 10.0%
물 잔량water Balance
상기 성분물질을 교반기에 넣고 상온에서 1시간 동안 교반하여 연한 갈색의 현탁액을 얻었으며 pH는 8.8로 측정되었다.The ingredients were placed in a stirrer and stirred at room temperature for 1 hour to obtain a pale brown suspension, pH 8.8.
난연성 접착제Flame retardant adhesive
현탁액 2.30%Suspension 2.30%
황산칼슘 25.8%Calcium sulfate 25.8%
염화마그네슘 19.4%Magnesium chloride 19.4%
물 잔량water Balance
상기 성분물질을 교반기에서 20분간 교반하면서 염도 24‰가 되도록 조절하여 소망의 발포 폴리스타이렌 난연성 접착제 조성물을 얻었다.The above ingredients were stirred for 20 minutes in a stirrer to adjust the salt content to 24 ‰ to obtain a desired polystyrene flame retardant adhesive composition.
송진용액Songjin solution
99% 이상의 고순도 송진 32.8%99% or more high purity 32.8%
중쇄 지방산 2.80%Heavy chain fatty acid 2.80%
디옥틸 테레프탈레이트 2.30%Dioctyl terephthalate 2.30%
프로세스 오일 1.00%Process oil 1.00%
디에칠렌 글리콜 1.00%Diethylene glycol 1.00%
폴리에칠렌글리콜 100 1.40%Polyethylene glycol 100 1.40%
이소프로필 알코올 43.0%Isopropyl alcohol 43.0%
메탄올 15.7%Methanol 15.7%
상기 성분물질을 교반기에 넣고 120℃ 분위기에서 1시간 동안 교반하여 송진용액을 얻었다. 송진용액은 교반을 거듭할수록 연한 갈색의 점성물질로 변하였다.The ingredient material was placed in a stirrer and stirred for 1 hour in an atmosphere of 120 ° C to obtain a rosin solution. The rosin solution turned into a light brown viscous substance with stirring.
현탁액Suspension
송진용액 2.00%Songjin solution 2.00%
아교 2.40%glue 2.40%
수산화나트륨 5.00%Sodium hydroxide 5.00%
수산화마그네슘 2.00%Magnesium hydroxide 2.00%
염화나트륨 2.00%Sodium chloride 2.00%
염화은 1.00%Silver chloride 1.00%
염화암모늄 1.00%Ammonium chloride 1.00%
아미노메틸프로판올 0.20%Aminomethyl propanol 0.20%
헥산-3-원 10.0%Hexane-3-one 10.0%
물 잔량water Balance
상기 성분물질을 교반기에 넣고 상온에서 1시간 동안 교반하여 연한 갈색의 현탁액을 얻었으며 pH는 8.8로 측정되었다.The ingredients were placed in a stirrer and stirred at room temperature for 1 hour to obtain a pale brown suspension, pH 8.8.
난연성 접착제Flame retardant adhesive
현탁액 2.50%Suspension 2.50%
염화칼슘 22.8%Calcium chloride 22.8%
염화마그네슘 24.3%Magnesium chloride 24.3%
물 잔량water Balance
상기 성분물질을 교반기에서 20분간 교반하면서 염도 23‰가 되도록 조절하여 소망의 발포 폴리스타이렌 난연성 접착제 조성물을 얻었다.The component material was stirred for 20 minutes in a stirrer to adjust the salt content to 23 ‰, thereby obtaining a desired foam polystyrene flame retardant adhesive composition.
송진용액Songjin solution
99% 이상의 고순도 송진 32.8%99% or more high purity 32.8%
중쇄 지방산 2.80%Heavy chain fatty acid 2.80%
디옥틸 테레프탈레이트 2.30%Dioctyl terephthalate 2.30%
프로세스 오일 1.00%Process oil 1.00%
디에칠렌 글리콜 1.00%Diethylene glycol 1.00%
폴리에칠렌글리콜 100 1.40%Polyethylene glycol 100 1.40%
이소프로필 알코올 43.0%Isopropyl alcohol 43.0%
메탄올 15.7%Methanol 15.7%
상기 성분물질을 교반기에 넣고 120℃ 분위기에서 1시간 동안 교반하여 송진용액을 얻었다. 송진용액은 교반을 거듭할수록 연한 갈색의 점성물질로 변하였다.The ingredient material was placed in a stirrer and stirred for 1 hour in an atmosphere of 120 ° C to obtain a rosin solution. The rosin solution turned into a light brown viscous substance with stirring.
현탁액Suspension
송진용액 2.00%Songjin solution 2.00%
아교 2.40%glue 2.40%
수산화나트륨 4.00%Sodium hydroxide 4.00%
수산화마그네슘 3.00%Magnesium hydroxide 3.00%
염화나트륨 1.00%Sodium chloride 1.00%
염화은 0.50%Silver chloride 0.50%
염화암모늄 2.50%Ammonium chloride 2.50%
트리메틸아민 0.20%Trimethylamine 0.20%
헥산-3-원 10.0%Hexane-3-one 10.0%
물 잔량water Balance
상기 성분물질을 교반기에 넣고 상온에서 1시간 동안 교반하여 연한 갈색의 현탁액을 얻었으며 pH는 8.6로 측정되었다.The above ingredients were placed in a stirrer and stirred at room temperature for 1 hour to obtain a pale brown suspension and the pH was measured to be 8.6.
난연성 접착제Flame retardant adhesive
현탁액 2.60%Suspension 2.60%
황산칼슘 20.0%Calcium sulfate 20.0%
염화마그네슘 29.0%Magnesium chloride 29.0%
물 잔량water Balance
상기 성분물질을 교반기에서 20분간 교반하면서 염도 24‰가 되도록 조절하여 소망의 발포 폴리스타이렌 난연성 접착제 조성물을 얻었다.The above ingredients were stirred for 20 minutes in a stirrer to adjust the salt content to 24 ‰ to obtain a desired polystyrene flame retardant adhesive composition.
송진용액Songjin solution
99% 이상의 고순도 송진 32.8%99% or more high purity 32.8%
중쇄 지방산 2.80%Heavy chain fatty acid 2.80%
디옥틸 테레프탈레이트 2.30%Dioctyl terephthalate 2.30%
프로세스 오일 1.00%Process oil 1.00%
디에칠렌 글리콜 1.00%Diethylene glycol 1.00%
폴리에칠렌글리콜 100 1.40%Polyethylene glycol 100 1.40%
이소프로필 알코올 43.0%Isopropyl alcohol 43.0%
메탄올 15.7%Methanol 15.7%
상기 성분물질을 교반기에 넣고 120℃ 분위기에서 1시간 동안 교반하여 송진용액을 얻었다. 송진용액은 교반을 거듭할수록 연한 갈색의 점성물질로 변하였다.The ingredient material was placed in a stirrer and stirred for 1 hour in an atmosphere of 120 ° C to obtain a rosin solution. The rosin solution turned into a light brown viscous substance with stirring.
현탁액Suspension
송진용액 2.00%Songjin solution 2.00%
아교 2.40%glue 2.40%
수산화나트륨 4.00%Sodium hydroxide 4.00%
수산화마그네슘 3.00%Magnesium hydroxide 3.00%
염화나트륨 1.00%Sodium chloride 1.00%
염화은 0.50%Silver chloride 0.50%
염화암모늄 2.50%Ammonium chloride 2.50%
트리메틸아민 0.20%Trimethylamine 0.20%
헥산-3-원 10.0%Hexane-3-one 10.0%
물 잔량water Balance
상기 성분물질을 교반기에 넣고 상온에서 1시간 동안 교반하여 연한 갈색의 현탁액을 얻었으며 pH는 8.9로 측정되었다.The above material was placed in a stirrer and stirred at room temperature for 1 hour to obtain a pale brown suspension. The pH was measured to be 8.9.
난연성 접착제Flame retardant adhesive
현탁액 2.80%Suspension 2.80%
황산칼슘 32.0%Calcium sulfate 32.0%
염화마그네슘 20.2%Magnesium chloride 20.2%
물 잔량water Balance
상기 성분물질을 교반기에서 20분간 교반하면서 염도 25‰가 되도록 조절하여 소망의 발포 폴리스타이렌 난연성 접착제 조성물을 얻었다.The component material was stirred for 20 minutes in a stirrer to adjust the salt content to 25 ‰, thereby obtaining a desired foam polystyrene flame retardant adhesive composition.
송진용액Songjin solution
99% 이상의 고순도 송진 32.8%99% or more high purity 32.8%
중쇄 지방산 2.80%Heavy chain fatty acid 2.80%
디옥틸 테레프탈레이트 2.30%Dioctyl terephthalate 2.30%
프로세스 오일 1.00%Process oil 1.00%
디에칠렌 글리콜 1.00%Diethylene glycol 1.00%
폴리에칠렌글리콜 100 1.40%Polyethylene glycol 100 1.40%
이소프로필 알코올 43.0%Isopropyl alcohol 43.0%
메탄올 15.7%Methanol 15.7%
상기 성분물질을 교반기에 넣고 120℃ 분위기에서 1시간 동안 교반하여 송진용액을 얻었다. 송진용액은 교반을 거듭할수록 연한 갈색의 점성물질로 변하였다.The ingredient material was placed in a stirrer and stirred for 1 hour in an atmosphere of 120 ° C to obtain a rosin solution. The rosin solution turned into a light brown viscous substance with stirring.
현탁액Suspension
송진용액 2.50%Songjin solution 2.50%
아교 3.00%glue 3.00%
수산화나트륨 3.00%Sodium hydroxide 3.00%
수산화칼륨 5.00%Potassium hydroxide 5.00%
염화나트륨 1.00%Sodium chloride 1.00%
염화구리 1.50%Copper chloride 1.50%
제3 인산소다 2.00%Sodium tertiary phosphate 2.00%
암모니아 0.10%ammonia 0.10%
트리메틸아민 0.15%Trimethylamine 0.15%
아세톤 11.0%Acetone 11.0%
물 잔량water Balance
상기 성분물질을 교반기에 넣고 상온에서 1시간 동안 교반하여 연한 갈색의 현탁액을 얻었으며 pH는 8.8로 측정되었다.The ingredients were placed in a stirrer and stirred at room temperature for 1 hour to obtain a pale brown suspension, pH 8.8.
난연성 접착제Flame retardant adhesive
현탁액 2.30%Suspension 2.30%
황산칼슘 25.8%Calcium sulfate 25.8%
염화마그네슘 19.4%Magnesium chloride 19.4%
물 잔량water Balance
상기 성분물질을 교반기에서 20분간 교반하면서 염도 24‰가 되도록 조절하여 소망의 발포 폴리스타이렌 난연성 접착제 조성물을 얻었다.The above ingredients were stirred for 20 minutes in a stirrer to adjust the salt content to 24 ‰ to obtain a desired polystyrene flame retardant adhesive composition.
송진용액Songjin solution
99% 이상의 고순도 송진 32.8%99% or more high purity 32.8%
중쇄 지방산 2.80%Heavy chain fatty acid 2.80%
디옥틸 테레프탈레이트 2.30%Dioctyl terephthalate 2.30%
프로세스 오일 1.00%Process oil 1.00%
디에칠렌 글리콜 1.00%Diethylene glycol 1.00%
폴리에칠렌글리콜 100 1.40%Polyethylene glycol 100 1.40%
이소프로필 알코올 43.0%Isopropyl alcohol 43.0%
메탄올 15.7%Methanol 15.7%
상기 성분물질을 교반기에 넣고 120℃ 분위기에서 1시간 동안 교반하여 송진용액을 얻었다. 송진용액은 교반을 거듭할수록 연한 갈색의 점성물질로 변하였다.The ingredient material was placed in a stirrer and stirred for 1 hour in an atmosphere of 120 ° C to obtain a rosin solution. The rosin solution turned into a light brown viscous substance with stirring.
현탁액Suspension
송진용액 2.50%Songjin solution 2.50%
아교 3.00%glue 3.00%
수산화마그네슘 2.00%Magnesium hydroxide 2.00%
수산화나트륨 6.00%Sodium hydroxide 6.00%
염화칼륨 1.50%Potassium chloride 1.50%
염화은 1.50%Silver chloride 1.50%
제3 인산소다 1.50%Sodium tertiary phosphate 1.50%
암모니아 0.15%ammonia 0.15%
아미노메틸프로판올 0.10%Aminomethyl propanol 0.10%
아세톤 11.0%Acetone 11.0%
물 잔량water Balance
상기 성분물질을 교반기에 넣고 상온에서 1시간 동안 교반하여 연한 갈색의 현탁액을 얻었으며 pH는 8.5로 측정되었다.The above material was placed in a stirrer and stirred at room temperature for 1 hour to obtain a pale brown suspension and the pH was measured at 8.5.
난연성 접착제Flame retardant adhesive
현탁액 2.50%Suspension 2.50%
염화칼슘 22.8%Calcium chloride 22.8%
염화마그네슘 24.3%Magnesium chloride 24.3%
물 잔량water Balance
상기 성분물질을 교반기에서 20분간 교반하면서 염도 23‰가 되도록 조절하여 소망의 발포 폴리스타이렌 난연성 접착제 조성물을 얻었다.The component material was stirred for 20 minutes in a stirrer to adjust the salt content to 23 ‰, thereby obtaining a desired foam polystyrene flame retardant adhesive composition.
송진용액Songjin solution
99% 이상의 고순도 송진 32.8%99% or more high purity 32.8%
중쇄 지방산 2.80%Heavy chain fatty acid 2.80%
디옥틸 테레프탈레이트 2.30%Dioctyl terephthalate 2.30%
프로세스 오일 1.00%Process oil 1.00%
디에칠렌 글리콜 1.00%Diethylene glycol 1.00%
폴리에칠렌글리콜 100 1.40%Polyethylene glycol 100 1.40%
이소프로필 알코올 43.0%Isopropyl alcohol 43.0%
메탄올 15.7%Methanol 15.7%
상기 성분물질을 교반기에 넣고 120℃ 분위기에서 1시간 동안 교반하여 송진용액을 얻었다. 송진용액은 교반을 거듭할수록 연한 갈색의 점성물질로 변하였다.The ingredient material was placed in a stirrer and stirred for 1 hour in an atmosphere of 120 ° C to obtain a rosin solution. The rosin solution turned into a light brown viscous substance with stirring.
현탁액Suspension
송진용액 2.50%Songjin solution 2.50%
아교 3.00%glue 3.00%
수산화마그네슘 5.00%Magnesium hydroxide 5.00%
수산화나트륨 3.00%Sodium hydroxide 3.00%
염화칼슘 2.50%Calcium chloride 2.50%
염화은 0.50%Silver chloride 0.50%
제3 인산소다 1.50%Sodium tertiary phosphate 1.50%
암모니아 0.20%ammonia 0.20%
아미노메틸프로판올 0.05%Aminomethyl propanol 0.05%
아세톤 12.0%Acetone 12.0%
물 잔량water Balance
상기 성분물질을 교반기에 넣고 상온에서 1시간 동안 교반하여 연한 갈색의 현탁액을 얻었으며 pH는 8.8로 측정되었다.The ingredients were placed in a stirrer and stirred at room temperature for 1 hour to obtain a pale brown suspension, pH 8.8.
난연성 접착제Flame retardant adhesive
현탁액 2.60%Suspension 2.60%
황산칼슘 20.0%Calcium sulfate 20.0%
염화마그네슘 29.0%Magnesium chloride 29.0%
물 잔량water Balance
상기 성분물질을 교반기에서 20분간 교반하면서 염도 24‰가 되도록 조절하여 소망의 발포 폴리스타이렌 난연성 접착제 조성물을 얻었다.The above ingredients were stirred for 20 minutes in a stirrer to adjust the salt content to 24 ‰ to obtain a desired polystyrene flame retardant adhesive composition.
송진용액Songjin solution
99% 이상의 고순도 송진 32.8%99% or more high purity 32.8%
중쇄 지방산 2.80%Heavy chain fatty acid 2.80%
디옥틸 테레프탈레이트 2.30%Dioctyl terephthalate 2.30%
프로세스 오일 1.00%Process oil 1.00%
디에칠렌 글리콜 1.00%Diethylene glycol 1.00%
폴리에칠렌글리콜 100 1.40%Polyethylene glycol 100 1.40%
이소프로필 알코올 43.0%Isopropyl alcohol 43.0%
메탄올 15.7%Methanol 15.7%
상기 성분물질을 교반기에 넣고 120℃ 분위기에서 1시간 동안 교반하여 송진용액을 얻었다. 송진용액은 교반을 거듭할수록 연한 갈색의 점성물질로 변하였다.The ingredient material was placed in a stirrer and stirred for 1 hour in an atmosphere of 120 ° C to obtain a rosin solution. The rosin solution turned into a light brown viscous substance with stirring.
현탁액Suspension
송진용액 2.50%Songjin solution 2.50%
아교 3.00%glue 3.00%
수산화마그네슘 5.00%Magnesium hydroxide 5.00%
수산화나트륨 3.00%Sodium hydroxide 3.00%
염화칼슘 2.50%Calcium chloride 2.50%
염화은 0.50%Silver chloride 0.50%
제3 인산소다 1.50%Sodium tertiary phosphate 1.50%
암모니아 0.20%ammonia 0.20%
아미노메틸프로판올 0.05%Aminomethyl propanol 0.05%
아세톤 12.0%Acetone 12.0%
물 잔량water Balance
상기 성분물질을 교반기에 넣고 상온에서 1시간 동안 교반하여 연한 갈색의 현탁액을 얻었으며 pH는 8.6으로 측정되었다.The above material was placed in a stirrer and stirred at room temperature for 1 hour to obtain a pale brown suspension. The pH was measured to be 8.6.
난연성 접착제Flame retardant adhesive
현탁액 2.80%Suspension 2.80%
황산칼슘 32.0%Calcium sulfate 32.0%
염화마그네슘 20.2%Magnesium chloride 20.2%
물 잔량water Balance
상기 성분물질을 교반기에서 20분간 교반하면서 염도 25‰가 되도록 조절하여 소망의 발포 폴리스타이렌 난연성 접착제 조성물을 얻었다.The component material was stirred for 20 minutes in a stirrer to adjust the salt content to 25 ‰, thereby obtaining a desired foam polystyrene flame retardant adhesive composition.
송진용액Songjin solution
99% 이상의 고순도 송진 32.8%99% or more high purity 32.8%
중쇄 지방산 2.80%Heavy chain fatty acid 2.80%
디옥틸 테레프탈레이트 2.30%Dioctyl terephthalate 2.30%
프로세스 오일 1.00%Process oil 1.00%
디에칠렌 글리콜 1.00%Diethylene glycol 1.00%
폴리에칠렌글리콜 100 1.40%Polyethylene glycol 100 1.40%
이소프로필 알코올 43.0%Isopropyl alcohol 43.0%
메탄올 15.7%Methanol 15.7%
상기 성분물질을 교반기에 넣고 120℃ 분위기에서 1시간 동안 교반하여 송진용액을 얻었다. 송진용액은 교반을 거듭할수록 연한 갈색의 점성물질로 변하였다.The ingredient material was placed in a stirrer and stirred for 1 hour in an atmosphere of 120 ° C to obtain a rosin solution. The rosin solution turned into a light brown viscous substance with stirring.
현탁액Suspension
송진용액 2.50%Songjin solution 2.50%
아교 3.00%glue 3.00%
수산화나트륨 3.00%Sodium hydroxide 3.00%
수산화칼륨 5.00%Potassium hydroxide 5.00%
염화나트륨 1.00%Sodium chloride 1.00%
염화구리 1.50%Copper chloride 1.50%
제3 인산소다 2.00%Sodium tertiary phosphate 2.00%
암모니아 0.10%ammonia 0.10%
트리메틸아민 0.15%Trimethylamine 0.15%
3-브로모-사이클로헥사논 11.0%3-Bromo-cyclohexanone 11.0%
물 잔량water Balance
상기 성분물질을 교반기에 넣고 상온에서 1시간 동안 교반하여 연한 갈색의 현탁액을 얻었으며 pH는 8.8로 측정되었다.The ingredients were placed in a stirrer and stirred at room temperature for 1 hour to obtain a pale brown suspension, pH 8.8.
난연성 접착제Flame retardant adhesive
현탁액 2.30%Suspension 2.30%
황산칼슘 25.8%Calcium sulfate 25.8%
염화마그네슘 19.4%Magnesium chloride 19.4%
물 잔량water Balance
상기 성분물질을 교반기에서 20분간 교반하면서 염도 24‰가 되도록 조절하여 소망의 발포 폴리스타이렌 난연성 접착제 조성물을 얻었다.The above ingredients were stirred for 20 minutes in a stirrer to adjust the salt content to 24 ‰ to obtain a desired polystyrene flame retardant adhesive composition.
송진용액Songjin solution
99% 이상의 고순도 송진 32.8%99% or more high purity 32.8%
중쇄 지방산 2.80%Heavy chain fatty acid 2.80%
디옥틸 테레프탈레이트 2.30%Dioctyl terephthalate 2.30%
프로세스 오일 1.00%Process oil 1.00%
디에칠렌 글리콜 1.00%Diethylene glycol 1.00%
폴리에칠렌글리콜 100 1.40%Polyethylene glycol 100 1.40%
이소프로필 알코올 43.0%Isopropyl alcohol 43.0%
메탄올 15.7%Methanol 15.7%
상기 성분물질을 교반기에 넣고 120℃ 분위기에서 1시간 동안 교반하여 송진용액을 얻었다. 송진용액은 교반을 거듭할수록 연한 갈색의 점성물질로 변하였다.The ingredient material was placed in a stirrer and stirred for 1 hour in an atmosphere of 120 ° C to obtain a rosin solution. The rosin solution turned into a light brown viscous substance with stirring.
현탁액Suspension
송진용액 3.00%Songjin solution 3.00%
아교 3.60%glue 3.60%
수산화나트륨 3.00%Sodium hydroxide 3.00%
수산화칼슘 3.00%Calcium hydroxide 3.00%
수산화마그네슘 3.00%Magnesium hydroxide 3.00%
염화나트륨 1.00%Sodium chloride 1.00%
염화칼슘 1.00%Calcium chloride 1.00%
염화암모늄 1.00%Ammonium chloride 1.00%
염화수은 2.00%Mercury chloride 2.00%
암모니아 0.10%ammonia 0.10%
아미노메틸프로판올 0.20%Aminomethyl propanol 0.20%
3-브로모-사이클로헥사논 12.0%3-Bromo-cyclohexanone 12.0%
물 잔량water Balance
상기 성분물질을 교반기에 넣고 상온에서 1시간 동안 교반하여 연한 갈색의 현탁액을 얻었으며 pH는 8.9로 측정되었다.The above material was placed in a stirrer and stirred at room temperature for 1 hour to obtain a pale brown suspension. The pH was measured to be 8.9.
난연성 접착제Flame retardant adhesive
현탁액 2.50%Suspension 2.50%
염화칼슘 22.8%Calcium chloride 22.8%
염화마그네슘 24.3%Magnesium chloride 24.3%
물 잔량water Balance
상기 성분물질을 교반기에서 20분간 교반하면서 염도 23‰가 되도록 조절하여 소망의 발포 폴리스타이렌 난연성 접착제 조성물을 얻었다.The component material was stirred for 20 minutes in a stirrer to adjust the salt content to 23 ‰, thereby obtaining a desired foam polystyrene flame retardant adhesive composition.
송진용액Songjin solution
99% 이상의 고순도 송진 32.8%99% or more high purity 32.8%
중쇄 지방산 2.80%Heavy chain fatty acid 2.80%
디옥틸 테레프탈레이트 2.30%Dioctyl terephthalate 2.30%
프로세스 오일 1.00%Process oil 1.00%
디에칠렌 글리콜 1.00%Diethylene glycol 1.00%
폴리에칠렌글리콜 100 1.40%Polyethylene glycol 100 1.40%
이소프로필 알코올 43.0%Isopropyl alcohol 43.0%
메탄올 15.7%Methanol 15.7%
상기 성분물질을 교반기에 넣고 120℃ 분위기에서 1시간 동안 교반하여 송진용액을 얻었다. 송진용액은 교반을 거듭할수록 연한 갈색의 점성물질로 변하였다.The ingredient material was placed in a stirrer and stirred for 1 hour in an atmosphere of 120 ° C to obtain a rosin solution. The rosin solution turned into a light brown viscous substance with stirring.
현탁액Suspension
송진용액 3.00%Songjin solution 3.00%
아교 3.60%glue 3.60%
수산화나트륨 3.00%Sodium hydroxide 3.00%
수산화칼륨 3.00%Potassium hydroxide 3.00%
수산화마그네슘 3.00%Magnesium hydroxide 3.00%
염화나트륨 1.00%Sodium chloride 1.00%
제3 인산소다 2.00%Sodium tertiary phosphate 2.00%
염화수은 2.00%Mercury chloride 2.00%
암모니아 0.10%ammonia 0.10%
아미노메틸프로판올 0.10%Aminomethyl propanol 0.10%
트리메틸아민 0.10%Trimethylamine 0.10%
3-브로모-사이클로헥사논 12.0%3-Bromo-cyclohexanone 12.0%
물 잔량water Balance
상기 성분물질을 교반기에 넣고 상온에서 1시간 동안 교반하여 연한 갈색의 현탁액을 얻었으며 pH는 8.9로 측정되었다.The above material was placed in a stirrer and stirred at room temperature for 1 hour to obtain a pale brown suspension. The pH was measured to be 8.9.
난연성 접착제Flame retardant adhesive
현탁액 2.60%Suspension 2.60%
황산칼슘 20.0%Calcium sulfate 20.0%
염화마그네슘 29.0%Magnesium chloride 29.0%
물 잔량water Balance
상기 성분물질을 교반기에서 20분간 교반하면서 염도 24‰가 되도록 조절하여 소망의 발포 폴리스타이렌 난연성 접착제 조성물을 얻었다.The above ingredients were stirred for 20 minutes in a stirrer to adjust the salt content to 24 ‰ to obtain a desired polystyrene flame retardant adhesive composition.
송진용액Songjin solution
99% 이상의 고순도 송진 32.8%99% or more high purity 32.8%
중쇄 지방산 2.80%Heavy chain fatty acid 2.80%
디옥틸 테레프탈레이트 2.30%Dioctyl terephthalate 2.30%
프로세스 오일 1.00%Process oil 1.00%
디에칠렌 글리콜 1.00%Diethylene glycol 1.00%
폴리에칠렌글리콜 100 1.40%Polyethylene glycol 100 1.40%
이소프로필 알코올 43.0%Isopropyl alcohol 43.0%
메탄올 15.7%Methanol 15.7%
상기 성분물질을 교반기에 넣고 120℃ 분위기에서 1시간 동안 교반하여 송진용액을 얻었다. 송진용액은 교반을 거듭할수록 연한 갈색의 점성물질로 변하였다.The ingredient material was placed in a stirrer and stirred for 1 hour in an atmosphere of 120 ° C to obtain a rosin solution. The rosin solution turned into a light brown viscous substance with stirring.
현탁액Suspension
송진용액 3.00%Songjin solution 3.00%
아교 3.60%glue 3.60%
수산화나트륨 3.00%Sodium hydroxide 3.00%
수산화칼륨 3.00%Potassium hydroxide 3.00%
수산화마그네슘 3.00%Magnesium hydroxide 3.00%
염화나트륨 1.00%Sodium chloride 1.00%
제3 인산소다 2.00%Sodium tertiary phosphate 2.00%
염화수은 2.00%Mercury chloride 2.00%
암모니아 0.10%ammonia 0.10%
아미노메틸프로판올 0.10%Aminomethyl propanol 0.10%
트리메틸아민 0.10%Trimethylamine 0.10%
3-브로모-사이클로헥사논 12.0%3-Bromo-cyclohexanone 12.0%
물 잔량water Balance
상기 성분물질을 교반기에 넣고 상온에서 1시간 동안 교반하여 연한 갈색의 현탁액을 얻었으며 pH는 8.8로 측정되었다.The ingredients were placed in a stirrer and stirred at room temperature for 1 hour to obtain a pale brown suspension, pH 8.8.
난연성 접착제Flame retardant adhesive
현탁액 2.80%Suspension 2.80%
황산칼슘 32.0%Calcium sulfate 32.0%
염화마그네슘 20.2%Magnesium chloride 20.2%
물 잔량water Balance
상기 성분물질을 교반기에서 20분간 교반하면서 염도 25‰가 되도록 조절하여 소망의 발포 폴리스타이렌 난연성 접착제 조성물을 얻었다.The component material was stirred for 20 minutes in a stirrer to adjust the salt content to 25 ‰, thereby obtaining a desired foam polystyrene flame retardant adhesive composition.
[비교 실시예1] [ Comparative Example 1 ]
송진용액Songjin solution
99% 이상의 고순도 송진 26.0%99% or more high purity 26.0%
중쇄 지방산 1.80% Heavy chain fatty acid 1.80%
디옥틸 테레프탈레이트 2.20%Dioctyl terephthalate 2.20%
디에칠렌 글리콜 1.40% Diethylene glycol 1.40%
이소프로필 알코올 46.6% Isopropyl alcohol 46.6%
메탄올 22.0% Methanol 22.0%
상기 성분물질을 교반기에 넣고 120℃ 분위기에서 1시간 동안 교반하여 송진용액을 얻었다. 송진용액은 교반을 거듭할수록 연한 갈색의 점성의 송진용액으로 변화하였다.The ingredient material was placed in a stirrer and stirred for 1 hour in an atmosphere of 120 ° C to obtain a rosin solution. The rosin solution was changed into a light brown viscous rosin solution with stirring.
현탁액Suspension
송진용액 0.50% Songjin solution 0.50%
아 교 1.00% A school 1.00%
수산화나트륨 4.00% Sodium hydroxide 4.00%
제3 인산소다 2.50% Sodium tertiary phosphate 2.50%
암모니아 0.05%ammonia 0.05%
아세톤 7.00% Acetone 7.00%
물 잔량 water Balance
상기 성분물질을 교반기에 넣고 상온에서 1시간 동안 교반하여 연한 갈색의 현탁액을 얻었다.The above material was placed in a stirrer and stirred at room temperature for 1 hour to obtain a pale brown suspension.
현탁액의 산도는 pH 8.9로 측정되었다.The acidity of the suspension was measured at pH 8.9.
난연성 접착제Flame retardant adhesive
현탁액 2.10% Suspension 2.10%
염화마그네슘 42.0% Magnesium chloride 42.0%
물 잔량 water Balance
상기 성분물질을 교반기에서 20분간 교반하면서 염도 20‰가 되도록 조절하여 발포 폴리스타이렌 난연성 접착제 조성물을 얻었다.The above ingredients were stirred in a stirrer for 20 minutes to adjust the salinity to 20 ‰, thereby obtaining a polystyrene flame retardant adhesive composition.
[비교 실시예2] [ Comparative Example 2 ]
송진용액Songjin solution
99% 이상의 고순도 송진 33.2% 99% or more high purity 33.2%
중쇄 지방산 2.90% Heavy chain fatty acid 2.90%
디옥틸 테레프탈레이트 3.40%Dioctyl terephthalate 3.40%
디에칠렌 글리콜 2.50% Diethylene glycol 2.50%
이소프로필 알코올 38.0% Isopropyl alcohol 38.0%
메탄올 20.0% Methanol 20.0%
상기 성분물질을 교반기에 넣고 120℃ 분위기에서 1시간 동안 교반하여 송진용액을 얻었다.The ingredient material was placed in a stirrer and stirred for 1 hour in an atmosphere of 120 ° C to obtain a rosin solution.
현탁액Suspension
송진 용액 3.50%Songjin solution 3.50%
아 교 4.00%A school 4.00%
수산화마그네슘 10.0%Magnesium hydroxide 10.0%
염화나트륨 5.50%Sodium chloride 5.50%
트리메틸아민 0.35%Trimethylamine 0.35%
3-브로모-사이클로헥사논 13.0%3-Bromo-cyclohexanone 13.0%
물 잔량water Balance
상기 성분물질을 교반기에 넣고 상온에서 1시간 동안 교반하여 연한 갈색의 현탁액을 얻었으며 pH 9.0으로 측정되었다.The above ingredients were placed in a stirrer and stirred at room temperature for 1 hour to obtain a pale brown suspension, which was measured at pH 9.0.
난연성 접착제Flame retardant adhesive
현탁액 3.00%Suspension 3.00%
염화마그네슘 54.0%Magnesium chloride 54.0%
물 잔량water Balance
상기 성분물질을 교반기에서 20분간 교반하면서 염도 29‰가 되도록 조절하여 발포 폴리스타이렌 난연성 접착제 조성물을 얻었다.The ingredients were stirred for 20 minutes in a stirrer to adjust the salt content to 29 ‰ to obtain a foam polystyrene flame retardant adhesive composition.
상술한 실시예 1, 25, 50, 75, 100, 125 및 비교실시예 1, 2에서 얻어진 난연성 접착제에 무기 바인더를 섞은 혼합물 25 질량비에, 폐 발포 폴리스타이렌 분말과 입경 1 ~ 2mm의 발포 폴리스타이렌 비드 혼합물 50 부피%, 입도 200 ~ 300 메시의 황토분 5 부피%, 입경 1 ~ 2mm의 건축용 펄라이트 13 부피%, 산화마그네슘 10 부피%를 각각 투입하고 5분 정도 교반하여 잘 섞어 얻어지는 폐 발포 폴리스타이렌 혼합물을, 60 ~ 70℃로 유지되는 성형틀에 주입하고 3분간 체류시켜 발포 성형시키고, 다시 건조실에서 35℃로 2시간 건조 시켜서 제조되는 폐 발포 폴리스타이렌 보드를 육안으로 검사하여 외관의 균열이나 공극, 그리고 손으로 눌러 파쇄되는 부위가 존재하는지를 체크하고 그 결과를 다음 표 1로 나타냈다.To 25 parts by mass of the mixture obtained by mixing the flame-retardant adhesive obtained in Examples 1, 25, 50, 75, 100, 125 and Comparative Examples 1 and 2 with an inorganic binder, a mixture of waste expanded polystyrene powder and a foamed polystyrene bead mixture 5 volume% of loess of 200 to 300 mesh size, 13 volume% of architectural pearlite of 1 to 2 mm particle size, and 10 volume% of magnesium oxide were mixed and stirred for about 5 minutes, respectively, to obtain a mixture of expanded polystyrene, Molded into a mold maintained at 60 to 70 ° C., held for 3 minutes, foamed, and dried in a drying chamber at 35 ° C. for 2 hours. The foamed polystyrene board was visually inspected for cracks, pores, and hands The results are shown in the following Table 1. < tb > < TABLE >
비교실시예 1의 보드는 표면에 1mm 이상의 균열과 공극이 존재하였고, 비교실시예 2는 보드 표면을 부분적으로 눌렀을 때 접착제 도포가 불균일하게 된 부분에서 쉽게 파쇄되는 현상이 나타나 불량으로 판정하였다.The board of Comparative Example 1 had cracks and voids of 1 mm or more on the surface thereof, and Comparative Example 2 was judged to be defective when a part of the board surface was partially pressed and the adhesive application was easily broken at the uneven portion.
다음에, 상기 실시예 50의 폐 발포 폴리스타일렌 보드와, 시판되고 있는 비난연 발포 폴리스타일렌 보드, 역시 시판되고 있고 난연 3급으로 인가된 발포 스타일렌 보드를 각각 지름 45mm, 높이 50mm로 절단하여 준비하고, 각 시료를 국토해양부고시 제2011-39호의 규정에 따라 800℃ 이상의 불꽃을 가하여 연소되는 시간과 연소된 상태를 사진으로 나타냈다.Next, the foamed foamed polystyrene board of Example 50 and a non-defatted foamed polystyrene board, which is also commercially available, and the foamed styrene board applied as flame retardancy Grade 3 were cut into 45 mm in diameter and 50 mm in height, respectively, , And each sample was burned at a temperature of 800 ° C or higher in accordance with the notification of the Ministry of Land, Transport and Maritime Affairs Notice No. 2011-39, and the burned state and the burned state were shown in the photographs.
본 발명시료 비난연시료 난연3급시료 The sample of the present invention Uncleaned sample Flame retardant grade 3 sample
본 발명시료 비난연시료 난연3급시료 The sample of the present invention Uncleaned sample Flame retardant grade 3 sample
(800℃ 5분경과) (800℃ 5초경과) (800℃ 30초경과)(At about 800 DEG C for about 5 minutes) (At 800 ° C for 5 seconds) (At about 800 ° C for about 30 seconds)
상기의 사진으로 본 발명에 관련된 발포 폴리스타일렌 난연성 접착제 조성물로 만들어진 폐 발포 폴리스타일렌 보드의 난연효과가 현저하게 우수한 것임을 입증할 수 있었다.From the above photographs, it was proved that the fire-retarding effect of the closed foamed polystyrene board made of the foamed polystyrene flame retardant adhesive composition according to the present invention is remarkably excellent.
또한, 상기 실시예 50의 폐 발포 스타일렌 보드로 샌드위치 패널을 제조하고 시판중인 비난연 샌드위치패널과 대비하여 각각 토오치 불꽃에 10분 접촉시킨 결과를 사진으로 나타내었다.In addition, the sandwich panel was manufactured using the closed foamed styrene board of Example 50, and the results were shown in comparison with the commercially available unbaked sandwich panel, for 10 minutes, respectively, against the soil flame.
본 발명이 적용된 패널 시판의 비난연 패널The panel to which the present invention is applied Commercially available panel
토오치 불꽃시험의 결과, 본 발명이 적용된 샌드위치 패널은 연기 발생이 극히 적고 불꽃과 접촉된 부분 외에는 연소가 퍼지지 않아 우수한 난연성능을 갖춘 것임을 확인할 수 있었다.As a result of the Touchi flame test, it was confirmed that the sandwich panel to which the present invention is applied has extremely low smoke generation and excellent flame retardancy performance because the combustion does not spread except the portion contacting the flame.
그러나 시판중인 비난연 샌드위치 패널은 불꽃과 접촉되고 얼마 지나지 않아 유독성 연기가 피어 오르고, 게다가 불꽃과 접촉된 부분의 주변으로 연소가 진행되어 화재에 취약성을 노출하였다.However, a commercially available unbaked sandwich panel came into contact with the flame, and toxic smoke soon rose, and the burning progressed to the periphery of the part in contact with the flame to expose the fire to the vulnerability.
Claims (12)
상기 현탁액은, 송진용액 1~3%, 아교 1.2~3.6%, 강 알칼리성분 5~9%, 염 3~5%, 중화제 0.1~0.3%, 상용화제 8~12%, 물 67.1~81.7%의 비율로 혼합 교반하여 얻어짐을 특징으로 하는 발포 폴리스타이렌 난연성 접착제 조성물.The method according to claim 1,
The suspension was prepared by dissolving 1 to 3% of rosin, 1.2 to 3.6% of glue, 5 to 9% of strong alkaline components, 3 to 5% of salt, 0.1 to 0.3% of neutralizing agent, 8 to 12% of compatibilizer and 67.1 to 81.7% By weight based on the total weight of the composition.
상기 응고제는, 염화마그네슘, 황산칼슘, 염화칼슘 중에서 선택한 1종, 또는 2종 이상의 혼합물인 것을 특징으로 하는 발포 폴리스타이렌 난연성 접착제 조성물.The method according to claim 1,
Wherein the coagulant is one or a mixture of two or more selected from magnesium chloride, calcium sulfate and calcium chloride.
상기 강 알칼리성분은, 수산화나트륨, 수산화칼륨, 수산화마그네슘 중에서 선택한 1종, 또는 2종 이상의 혼합물인 것을 특징으로 하는 발포 폴리스타이렌 난연성 접착제 조성물.3. The method of claim 2,
Wherein the strongly alkaline component is one or a mixture of two or more selected from sodium hydroxide, potassium hydroxide and magnesium hydroxide.
상기 염은, 염화나트륨, 염화칼륨, 염화칼슘, 염화은, 염화구리, 염화수은, 염화암모늄, 제3 인산소다 중에서 선택한 1종, 또는 2종 이상의 혼합물인 것을 특징으로 하는 발포 폴리스타이렌 난연성 접착제 조성물.3. The method of claim 2,
Wherein the salt is at least one selected from the group consisting of sodium chloride, potassium chloride, calcium chloride, silver chloride, copper chloride, mercury chloride, ammonium chloride, and sodium tertiary phosphate or a mixture of two or more thereof.
상기 중화제는, 암모니아, 트리에틸아민, 아미노메틸프로판올 중에서 선택한 1종, 또는 2종 이상의 혼합물인 것을 특징으로 하는 발포 폴리스타이렌 난연성 접착제 조성물.3. The method of claim 2,
Wherein the neutralizing agent is one or a mixture of two or more selected from ammonia, triethylamine, and aminomethylpropanol.
상기 상용화제는, 아세톤, 3-브로모-사이클로헥사논, 헥산-3-원 중에서 선택한 1종인 것을 특징으로 하는 발포 폴리스타이렌 난연성 접착제 조성물.3. The method of claim 2,
Wherein the compatibilizer is one selected from the group consisting of acetone, 3-bromo-cyclohexanone, and hexane-3-one.
상기 송진용액은, 99% 이상의 고순도 송진 26.8~32.8%, 식물성 연화제 1.9~2.8%, 친수성 용제 58.7~67.5%, 콜로이드안정제 1.5~2.4%, 광유계 연화제 2.3~3.3%의 비율로 혼합 교반하여 얻어짐을 특징으로 하는 발포 폴리스타이렌 난연성 접착제 조성물.The method according to claim 1,
The rosin solution was mixed and stirred at a ratio of high purity 99% or higher purity 26.8 to 32.8%, vegetable softening agent 1.9 to 2.8%, hydrophilic solvent 58.7 to 67.5%, colloidal stabilizer 1.5 to 2.4% and mineral oil softening agent 2.3 to 3.3% Wherein the foamed polystyrene-based flame-retardant adhesive composition is a flame-retardant adhesive composition.
상기 콜로이드안정제는, 디에칠렌글리콜, 트리에칠렌글리콜, 폴리에칠렌글리콜 100, 200, 300 중에서 선택한 1종, 또는 2종 이상의 혼합물인 것을 특징으로 하는 발포 폴리스타이렌 난연성 접착제 조성물.9. The method of claim 8,
Wherein the colloidal stabilizer is at least one selected from the group consisting of diethylene glycol, triethylene glycol, polyethylene glycol 100, 200, and 300, or a mixture of two or more thereof.
상기 식물성 연화제는, 중쇄지방산인 것을 특징으로 하는 발포 폴리스타이렌 난연성 접착제 조성물.9. The method of claim 8,
Wherein the vegetable softening agent is a heavy chain fatty acid.
상기 광유계 연화제는, 프로세스오일, 디옥틸테레플레이트 중에서 선택한 1종, 또는 2종의 혼합물인 것을 인 것을 특징으로 하는 발포 폴리스타이렌 난연성 접착제 조성물.9. The method of claim 8,
Wherein the mineral oil softening agent is one or a mixture of two selected from the group consisting of process oil and dioctyl terephthalate.
상기 친수성 용제는, 이소프로필알코올, 또는 이소프로필알코올과 메탄올의 혼합물인 것을 특징으로 하는 발포 폴리스타이렌 난연성 접착제 조성물.9. The method of claim 8,
Wherein the hydrophilic solvent is isopropyl alcohol or a mixture of isopropyl alcohol and methanol.