Abstract

The present invention relates to a Hanji (traditional Korean paper) gypsum air freshener, and to a manufacturing method thereof. The Hanji gypsum air freshener is made from a Hanji paste prepared by mixing 3-35 wt% of Hanji and a certain amount of gypsum in water in a mulberry porridge form. Because of Hanjis particularly long fibers, Hanji has a tough texture, and can be stored for a long period of time. Thus, the Hanji plaster air freshener is lighter than a conventional plaster air freshener by combining Hanji with high strength gypsum, and has reduced amount of flying powder while having enhanced durability. Also, the Hanji gypsum air freshener has deodorant properties, quick drying properties, and antibacterial properties by mixing mulberry fibers of Hanji having effects of dehumidification, deodorization, and antibacterial activity.

Description

TECHNICAL FIELD [0001] The present invention relates to an aromatic gypsum fragrance,

본 발명은 방향제 및 그의 제조 방법에 관한 것으로, 보다 상세하게는 한지 석고 방향제는 특유의 장섬유로 인하여 종이가 질기고 오래 보존이 가능한 한지를 고강도 석고와 결합시켜 기존 석고방향제 보다 가벼우며, 가루날림은 줄이고 내구성이 향상되며 발향 지속 시간이 증가된 한지 석고 방향제 및 그의 제조 방법에 관한 것이다.
The present invention relates to a fragrance agent and a method for producing the same. More particularly, a Korean paper gypsum fragrance is a lighter than a conventional gypsum fragrance by combining paper with a high strength gypsum, And an improvement in durability and an increase in duration of smell diffusion, and a method for producing the same.

일반적으로 방향제란 좋은 향을 가지고 있는 약제를 통틀어 이르는 것으로, 이러한 방향제를 사용하는 방향용구는 그 사용 형태에 따라 분무형, 휘발형, 그리고 승화형 등으로 분류된다. Generally, fragrances are a mixture of medicines having a good fragrance, and the fragrance articles using such fragrance are classified into spraying, volatile, and sublimation depending on their use forms.

우선 분무형 방향용구는 방향제 용액을 펌핑하여 미세한 입자로 직접 공기 중에 분무하거나 혹은 가스 등에 섞어 분무하는 형태이다. 그리고 휘발형 방향용구는 액체 방향제를 직접적으로 또는 별도의 매체, 예를 들어 다공체로 이루어진 발향스틱 등을 통해 빨아들여 간접적으로 기화시키는 형태인 것이다. 마지막으로 승화형 방향용구는 고체 방향제를 직접 기체로 승화시키는 형태이다. First of all, the sprayer is sprayed with the fragrant solution and sprayed directly into the air or mixed with gas or the like. The volatile-type directional device is a type in which the liquid aromatic agent is directly or indirectly vaporized by sucking it through a separate medium, for example, an eroding stick made of a porous body or the like. Finally, the sublimation type device is a type in which the solid aromatic agent is sublimated directly into gas.

특히, 승화형 방향용구는 분무형 및 휘발형보다 그 지속성이 오래가는 장점 때문에 최근에 유행하고 있는 방향용구이다. Especially, the sublimation type direction tool is a tool which is popular in recent years because of its advantage over the spray type and the volatile type.

일 예로, 석고방향제는 생활 속 냄새를 제거하고, 석고방향제에 다양한 방향 오일을 뿌리거나 같이 제작하여 실내 공기를 향기롭게 할 수 있어서 최근에 많이 사용되고 있다.For example, the gypsum fragrance has recently been widely used since it removes the odor in daily life, and can spray the various directional oils to the gypsum fragrance or fragrance the room air.

그러나 석고방향제는 그 재료인 석고의 특성 상 가루가 날려서 오히려 실내 공기가 탁하게 되는 문제점, 상대적으로 무게가 많이 나가는 문제점, 적절한 배합 비율로 제조되지 않으면 석고가 부서지는 문제점이 발생한다.
However, the gypsum aroma is a problem of gypsum being broken due to the characteristics of the gypsum that is the material thereof, rather, the indoor air becomes cloudy due to the powder, the problem of relatively heavy weight,

한국등록특허 제10-1443127호(허브향을 지속적으로 발산하는 항균 기능성 한지 벽지)Korean Patent No. 10-1443127 (Antibacterial Functional Hanji Wall Paper Continuously Spreading Herb Fragrance) 한국등록특허 제10-1208525호(황토 숯 방향 탈취제 및 이의 제조방법)Korean Patent No. 10-1208525 (deodorant in the direction of loess charcoal and production method thereof)

본 발명은 이와 같은 문제점을 감안한 것으로서, 본 발명은 한지를 고강도 석고와 결합시켜 기존 석고방향제 보다 가벼우며, 가루날림은 줄이고 내구성이 향상된 한지 석고 방향제를 을 제공하는 것이다.SUMMARY OF THE INVENTION The present invention has been made in view of the above problems, and it is an object of the present invention to provide a Korean gypsum aroma agent which combines Korean paper with high strength gypsum, which is lighter than conventional gypsum fragrance and has reduced dusting and improved durability.

본 발명은 상기 한지 석고 방향제를 제조하기 위한 한지 석고 방향제의 제조방법을 제공하는 것이다. The present invention provides a method for producing a Korean gypsum aroma agent for producing the Korean gypsum aromatic agent.

본 발명은 상기 한지 석고 방향제를 포함하는 한지 석고 방향장치를 제공하는 것이다.
The present invention provides a Korean paper gypsum direction apparatus including the above-mentioned Korean gypsum fragrance.

본 발명의 실시예들에 따른 한지 석고 방향제의 제조방법은 물에 천연광 물질을 녹이는 단계; 상기 천연광 물질이 녹은 물에 석고를 배합하고 반죽하는 단계; 상기 배합된 물과 석고의 혼합물에 닥죽 상태의 한지를 찢어 넣어가면서 반죽하는 단계; 상기 반죽된 물, 석고와 한지의 혼합물을 틀에 넣고 건조하는 단계; 상기 건조된 물, 석고와 한지의 혼합물을 틀에서 탈거하여 추가적으로 건조하는 단계; 및 상기 추가적으로 건조된 물, 석고와 한지의 혼합물에 방향 오일을 넣는 단계를 포함한다. According to embodiments of the present invention, a method of preparing a Korean gypsum aroma agent comprises: dissolving a natural light material in water; Blending and kneading gypsum with water in which the natural light material is melted; Kneading the mixture of water and gypsum while tearing the Korean paper in a frozen state; Casting a mixture of the kneaded water, gypsum and Korean paper into a mold and drying; Removing the mixture of the dried water, gypsum and paper, and further drying the same; And adding the directional oil to the mixture of the further dried water, gypsum and paper.

본 발명의 다른 실시예들에 따른 한지 석고 방향제의 제조방법은 물에 석고를 배합하고 반죽하는 단계; 상기 반죽된 물과 석고의 혼합물에 닥죽 상태의 한지를 찢어서 배합하는 단계; 상기 배합된 물, 석고와 한지의 혼합물을 반죽하는 단계; 상기 반죽된 물, 석고와 한지의 혼합물에 천연광 물질을 넣고 추가적으로 반죽하는 단계; 상기 추가적으로 반죽된 물, 석고와 한지의 혼합물을 틀에 넣고 건조하는 단계; 상기 건조된 물, 석고와 한지의 혼합물을 틀에서 탈거하여 추가적으로 건조하는 단계; 및 상기 추가적으로 건조된 물, 석고와 한지의 혼합물에 방향 오일을 넣는 단계를 포함한다. According to another embodiment of the present invention, there is provided a method of producing a Korean gypsum aroma agent, comprising: mixing and kneading gypsum in water; Tearing a mixture of the kneaded water and the gypsum and kneading the kneaded Korean paper; Kneading the blended water, a mixture of gypsum and paper, Adding a natural light material to the mixture of the kneaded water, gypsum and Korean paper, and further kneading; Drying the mixture of the additional kneaded water, gypsum and paper, into a mold and drying; Removing the mixture of the dried water, gypsum and paper, and further drying the same; And adding the directional oil to the mixture of the further dried water, gypsum and paper.

본 발명의 실시예들에 있어서, 상기 물에 석고를 배합하는 단계에서 상기 석고는 물 중량 대비 80% 내지 85%를 배합한다. In the embodiments of the present invention, in the step of mixing gypsum with water, the gypsum is blended with 80% to 85% by weight of water.

본 발명의 실시예들에 있어서, 상기 닥죽 상태의 한지를 배합하는 단계에서 상기 닥죽 상태의 한지는 전체 중량 대비 3% 내지 35%를 배합한다. In the embodiments of the present invention, in the step of blending the Korean paper of the frozen state, 3% to 35% of the frozen ground is added to the total weight of the paper.

본 발명의 실시예들에 있어서, 상기 혼합물을 틀에 넣고 건조하는 단계는 20시간 이상 실행하고, 상기 틀에서 탈거하여 추가적으로 건조하는 단계는 10일 이상 실행한다. In embodiments of the present invention, the step of casting and drying the mixture is performed for at least 20 hours, and the step of removing from the mold and further drying is performed for at least 10 days.

본 발명의 실시예들에 따른 한지 석고 방향제는 닥죽 상태로 배합되어 건조된 한지와 석고로 이루어진다. According to the embodiments of the present invention, the Korean gypsum aroma agent is composed of Korean paper and gypsum blended in a dry state and dried.

본 발명의 실시예들에 있어서, 상기 닥죽 상태의 한지는 전체 중량 대비 3% 내지 35% 정도 배합된다. In the embodiments of the present invention, the frozen ground beans are blended in an amount of about 3% to 35% based on the total weight.

본 발명의 실시예들에 따른 한지 석고 방향장치는 지지부; 및 상기 지지부의 상부에서 상기 지지부와 결합되며, 닥죽 상태로 배합되어 건조된 한지와 석고로 이루어진 한지 석고 방향제를 포함한다. According to embodiments of the present invention, And a Korean gypsum fragrance which is composed of Korean paper and gypsum, which is combined with the support part at the upper part of the support part and dried and blended in a dry state.

본 발명의 실시예들에 있어서, 상기 닥죽 상태의 한지는 상기 한지 석고 방향제의 전체 중량 대비 3% 내지 35%를 배합된다. In the embodiments of the present invention, the hardness of the ground state is 3 to 35% based on the total weight of the hardy gypsum fragrance.

본 발명의 실시예들에 있어서, 상기 지지부는 상부면에 수용 공간을 갖는 홈이 형성되고, 하부면이 적어도 일 방향으로 기울어지도록 라운드(round)되어 형성된 홀더; 및 상기 홀더의 홈에 삽입되며 상기 지지부의 무게 중심을 유지할 수 있도록 상기 홀더보다 무거운 재질로 이루어진 무게추를 포함한다. In the embodiments of the present invention, the support portion may include a holder formed with a groove having a receiving space on an upper surface thereof and formed to be rounded so that a lower surface thereof is inclined at least in one direction; And a weight attached to the groove of the holder and made of a material heavier than the holder so as to maintain the center of gravity of the support.

본 발명의 실시예들에 있어서, 상기 지지부는 상부면에 수용 공간을 갖는 홈이 형성되고, 하부면이 적어도 일 방향으로 기울어지도록 라운드(round)되어 형성된 홀더; 및 금속재질로 이루어지고 상기 홀더의 홈의 내부면에 형성된 링 형태의 결합부를 포함한다.
In the embodiments of the present invention, the support portion may include a holder formed with a groove having a receiving space on an upper surface thereof and formed to be rounded so that a lower surface thereof is inclined at least in one direction; And a ring-shaped coupling portion formed of a metal material and formed on an inner surface of the groove of the holder.

이상에서 설명한 바와 같은 한지 석고 방향제 및 그의 제조 방법에 따르면 다음과 같은 효과가 있다.According to the above-described Korean gypsum fragrance and the method for producing the same, the following effects can be obtained.

첫째, 색을 입히기 위한 천연광 물질을 물에 충분히 녹인 다음에 석고와 닥죽 상태의 한지를 배합 및 반죽함으로써, 천연광 물질의 색이 석고와 한지에 균일하게 입혀진 방향제를 제조할 수 있다. First, it is possible to prepare a fragrance in which the color of natural light material is uniformly coated on the gypsum and the paper by thoroughly dissolving the natural light material for coloring in water, and then mixing and kneading the gypsum and frozen ground paper.

둘째, 물과 석고와 닥죽 상태의 한지를 찢어서 배합 및 반죽한 이후에 색을 입히기 위한 천연광 물질을 배합 및 반죽함으로써, 천연광 물질의 색이 석고와 한지에 연하게 입혀지고 한지의 느낌을 그대로 살릴 수 있다. Second, by tearing the water, gypsum and frosted Korean paper and blending and kneading, natural light material for coloring is kneaded and kneaded, and the color of natural light material is coated on plaster and paper, Can save.

셋째, 물과 석고, 한지의 배합 반죽 과정과 색을 입히기 위한 천연광 물질의 투입 순서 및 반죽순서에 따라 한지의 장섬유를 이용하여 대리석과 같은 마블링 효과를 살릴 수 있다.Third, the marbling effect of marble can be utilized by using the long fiber of Korean paper according to the mixing process of water, gypsum, and Korean paper, the order of putting the natural light material for coloring, and the order of kneading.

넷째, 특유의 장섬유로 인하여 종이가 질기고 오래 보존이 가능한 한지를 고강도 석고와 결합시켜 기존 석고방향제보다 내구성을 향상시킬 수 있으며, 발향 지속기간을 늘릴 수 있다.Fourth, it is possible to improve the durability of existing gypsum fragrance and to increase duration of fragrance by combining Korean paper with high strength gypsum which can be preserved because of its unique long fiber.

다섯째, 한지와 석고를 적절한 배율로 배합함으로써, 석고의 응집력을 낮추지 않아 석고의 날림 현상을 방지할 수 있다. Fifth, by blending Korean paper and gypsum at an appropriate magnification, the cohesion of the gypsum is not lowered, thereby preventing the plaster from being scattered.

여섯째, 기존의 석고방향제에 상대적으로 가벼운 한지를 배합 및 반죽함으로써, 동일한 부피의 석고방향제 보다 훨씬 가벼운 장점이 있다. Sixth, by mixing and kneading relatively light Korean paper with the existing gypsum fragrance, it is much lighter than the same volume of gypsum fragrance.

일곱째, 한지와 석고가 배합된 방향제에 사용자가 원하는 방향 오일을 넣음으로써, 실내 방향의 효과를 높일 수 있다.
Seventh, you can increase the effect of the direction of the room by putting the direction oil you want in the fragrance with the mixture of Korean paper and gypsum.

도 1은 본 발명의 일 실시예에 따른 한지 석고 방향제의 제조방법을 설명하기 위한 순서도이다.
도 2는 본 발명의 다른 실시예에 따른 한지 석고 방향제의 제조방법을 설명하기 위한 순서도이다.
도 3은 본 발명의 일 실시예에 따른 한지 석고 방향장치를 설명하기 위한 사시도이다.
도 4는 본 발명의 일 실시예에 따른 한지 석고 방향장치를 설명하기 위한 분해 단면도이다.
도 5는 본 발명의 다른 실시예에 따른 한지 석고 방향장치를 설명하기 위한 분해 사시도이다.1 is a flow chart for explaining a method of producing a Korean gypsum aroma agent according to an embodiment of the present invention.
2 is a flow chart for explaining a method of producing a Korean gypsum aroma agent according to another embodiment of the present invention.
3 is a perspective view for explaining a traditional Chinese gypsum board directional device according to an embodiment of the present invention.
4 is an exploded cross-sectional view for explaining a traditional Chinese gypsum board directional device according to an embodiment of the present invention.
5 is an exploded perspective view for explaining a traditional Korean gypsum board directional apparatus according to another embodiment of the present invention.

첨부한 도면을 참조하여 본 발명의 실시예들에 따른 한지 석고 방향제 및 그의 제조 방법에 대하여 상세히 설명한다. 본 발명은 다양한 변경을 가할 수 있고 여러 가지 형태를 가질 수 있는바, 특정 실시예들을 도면에 예시하고 본문에 상세하게 설명하고자 한다. 그러나 이는 본 발명을 특정한 개시 형태에 대해 한정하려는 것이 아니며, 본 발명의 사상 및 기술 범위에 포함되는 모든 변경, 균등물 내지 대체물을 포함하는 것으로 이해되어야 한다. 각 도면을 설명하면서 유사한 참조부호를 유사한 구성요소에 대해 사용하였다. 첨부된 도면에 있어서, 구조물들의 치수는 본 발명의 명확성을 기하기 위하여 실제보다 확대하거나, 개략적인 구성을 이해하기 위하여 실제보다 축소하여 도시한 것이다.DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS The present invention will now be described more fully with reference to the accompanying drawings, in which exemplary embodiments of the invention are shown. The present invention is capable of various modifications and various forms, and specific embodiments are illustrated in the drawings and described in detail in the text. It is to be understood, however, that the invention is not intended to be limited to the particular forms disclosed, but on the contrary, is intended to cover all modifications, equivalents, and alternatives falling within the spirit and scope of the invention. Like reference numerals are used for like elements in describing each drawing. In the accompanying drawings, the dimensions of the structures are enlarged to illustrate the present invention, and are actually shown in a smaller scale than the actual dimensions in order to understand the schematic structure.

또한, 제1 및 제2 등의 용어는 다양한 구성요소들을 설명하는데 사용될 수 있지만, 상기 구성요소들은 상기 용어들에 의해 한정되어서는 안 된다. 상기 용어들은 하나의 구성요소를 다른 구성요소로부터 구별하는 목적으로만 사용된다. 예를 들어, 본 발명의 권리 범위를 벗어나지 않으면서 제1 구성요소는 제2 구성요소로 명명될 수 있고, 유사하게 제2 구성요소도 제1 구성요소로 명명될 수 있다. 한편, 다르게 정의되지 않는 한, 기술적이거나 과학적인 용어를 포함해서 여기서 사용되는 모든 용어들은 본 발명이 속하는 기술 분야에서 통상의 지식을 가진 자에 의해 일반적으로 이해되는 것과 동일한 의미를 가지고 있다. 일반적으로 사용되는 사전에 정의되어 있는 것과 같은 용어들은 관련 기술의 문맥 상 가지는 의미와 일치하는 의미를 가지는 것으로 해석되어야 하며, 본 출원에서 명백하게 정의하지 않는 한, 이상적이거나 과도하게 형식적인 의미로 해석되지 않는다.
Also, the terms first and second, etc. may be used to describe various components, but the components should not be limited by the terms. The terms are used only for the purpose of distinguishing one component from another. For example, without departing from the scope of the present invention, the first component may be referred to as a second component, and similarly, the second component may also be referred to as a first component. On the other hand, unless otherwise defined, all terms used herein, including technical or scientific terms, have the same meaning as commonly understood by one of ordinary skill in the art to which this invention belongs. Terms such as those defined in commonly used dictionaries are to be interpreted as having a meaning consistent with the contextual meaning of the related art and are to be interpreted as either ideal or overly formal in the sense of the present application Do not.

도 1은 본 발명의 일 실시예에 따른 한지 석고 방향제의 제조방법을 설명하기 위한 순서도이다. 1 is a flow chart for explaining a method of producing a Korean gypsum aroma agent according to an embodiment of the present invention.

도 1을 참조하면, 본 발명의 일 실시예에 따른 한지 석고 방향제의 제조방법은 물에 천연광 물질을 녹이는 단계; 상기 천연광 물질이 녹은 물에 석고를 배합하고 반죽하는 단계; 상기 배합된 물과 석고의 혼합물에 닥죽 상태의 한지를 찢어 넣어가면서 반죽하는 단계; 상기 반죽된 물, 석고와 한지의 혼합물을 틀에 넣고 건조하는 단계; 상기 건조된 물, 석고와 한지의 혼합물을 틀에서 탈거하여 추가적으로 건조하는 단계; 및 상기 추가적으로 건조된 물, 석고와 한지의 혼합물에 방향 오일을 넣는 단계를 포함한다. Referring to FIG. 1, a method for producing a Korean gypsum aroma agent according to an exemplary embodiment of the present invention includes: dissolving a natural light material in water; Blending and kneading gypsum with water in which the natural light material is melted; Kneading the mixture of water and gypsum while tearing the Korean paper in a frozen state; Casting a mixture of the kneaded water, gypsum and Korean paper into a mold and drying; Removing the mixture of the dried water, gypsum and paper, and further drying the same; And adding the directional oil to the mixture of the further dried water, gypsum and paper.

한지 석고 방향제를 제조하기 위하여, 먼저 물에 천연광 물질을 넣고 녹여준다. 예를 들어, 전체 200g을 기준으로 60㎖에 천연광 물질을 5 내지 10% 정도를 넣고 충분히 녹을 때까지 교반한다. 이 때, 천연광 물질을 방향제의 색을 표현하기 위한 것으로, 사용자가 원하는 색의 방향제를 제조하기 위한 것이다(S100).To prepare a Korean gypsum fragrance, first add natural light material to water and dissolve it. For example, about 60 g of the total 200 g of natural light material is put into about 5 to 10%, and the mixture is stirred until it is sufficiently melted. In this case, the natural light material is used to express the color of the fragrance, and it is intended to produce the fragrance of the color desired by the user (S100).

천연광 물질을 물에 충분히 녹인 다음, 천연광 물질이 녹은 물에 석고를 배합하고 반죽한다. 이 때, 석고는 방향제의 내구성을 높이고 가루 날림 현상을 최소화하기 위하여 고강도 석고를 사용하는 것이 바람직하다. 그리고, 석고는 물 중량 대비 80 내지 85% 정도의 분량을 배합한다(S110).After dissolving the natural light material in water, mix the gypsum in the water with natural light material and knead it. At this time, it is preferable to use high-strength gypsum in order to increase the durability of the fragrance and minimize the dusting phenomenon. The gypsum is blended in an amount of about 80 to 85% of the water weight (S110).

이어서, 물에 석고를 배합하고 충분히 반죽한 다음, 한지를 넣어서 반죽한다. 이 때, 한지는 닥죽 상태로 물과 석고의 혼합물에 배합하고, 닥죽 상태의 한지를 찢어 넣는 것이 바람직하다. 닥죽 상태의 한지를 넣는 것은 배합 시 적당한 양의 수분이 필요하기 때문이다. Then, gypsum is added to water, kneaded sufficiently, and then kneaded with Korean paper. At this time, it is preferable to blend a mixture of water and gypsum in a state of frosting and tear the frozen ground paper. It is because the proper amount of water is needed for mixing when putting the Korean paper in the frozen state.

본 발명의 실시예들에 있어서, 닥죽 상태의 한지는 전체 중량 대비 3% 내지 35%를 배합한다. 예를 들어, 전체 200g 기준으로 A4 사이즈 한지의 3장 내지 9장 정도의 분량이 배합되는 것이다(S120). In the embodiments of the present invention, the frozen ground bean is mixed with 3% to 35% of the total weight. For example, three to nine sheets of A4 sized paper are mixed on a total basis of 200 g (S120).

이 때, 닥죽 상태의 한지를 3% 이하로 배합하는 경우, 방향제를 틀 내외부에서 건조하는데 시간을 줄일 수 있으나 한지 닥섬유의 텍스쳐가 방향제 표면에 표현되지 않고, 실제 방향제에서 한지의 효과가 극히 미비한 문제점이 발생한다. 또한, 닥둑 상태의 한지를 35% 이상으로 배합하는 경우, 석고 함량의 감소로 응집력이 약해져 제품의 먼지가 발생할 수 있으며,건조기간이 길어지는 문제점이 발생한다.In this case, when the paper is mixed with not more than 3% of the ground paper, it is possible to reduce the drying time of the fragrance inside and outside the frame. However, the texture of the paper fiber is not expressed on the surface of the fragrance, Lt; / RTI > In addition, when the ground paper of the skirting state is blended at a ratio of 35% or more, the cohesive force is weakened due to the decrease of the gypsum content, dust of the product may occur, and the drying period becomes longer.

이어서, 반죽된 물, 석고와 한지의 혼합물을 틀에 넣고 건조한다. 만일 20시간 이하로 건조를 하게 되면, 틀의 형상을 갖추지 못하게 되는 문제점이 발생하므로, 건조는 적어도 20시간 이상 실행한다(S130).Then, the mixture of the kneaded water, gypsum and paper is put into a mold and dried. If the drying is performed for 20 hours or less, the shape of the frame may not be formed, so that the drying is performed for at least 20 hours (S130).

그리고, 1차 건조된 물, 석고와 한지의 혼합물을 틀에서 탈거하여 추가적으로 건조한다. 이 때, 건조는 10일 이상 실행한다. 이 때의 건조는 틀에서 형상을 갖춘 방향제를 추가적으로 굳게 만들어서, 추후 방향제로 사용할 때 으스러지거나 부서지는 현상을 방지하기 위한 것이다(S140).Then, the mixture of primary dried water, gypsum and Korean paper is removed from the mold and further dried. At this time, drying is carried out for 10 days or more. In this case, the drying is performed to further strengthen the frame-shaped fragrance to prevent the fragrance or breakage of the fragrance when the fragrance is used as a fragrance (S140).

이어서, 최종적으로 건조된 혼합물에 방향 오일을 넣는다. 이 때, 사용자가 원하는 방향 오일을 건조된 혼합물에 넣을 수 있다(S150). The directional oil is then added to the finally dried mixture. At this time, the directional oil desired by the user may be put into the dried mixture (S150).

이와 같이, 물에 천연광 물질을 충분히 녹인 다음에, 석고와 한지를 배합하여 반죽함으로써, 천연광 물질의 색이 석고와 한지로 이루어진 방향제에 전체적으로 균일하게 입혀진다. 또한 석고에 장섬유로 이루어진 한지를 찢어서 배합 반죽함으로써, 방향제의 내구성을 높이고 발향 지속시간을 증가시킬 수 있을 뿐만 아니라 가루날림 현상을 방지할 수 있다. 나아가 닥섬유와 고강도 석고의 결합으로 한지의 기다랗고 부드러운 텍스쳐가 표면에 그대로 살아나 기존 석고방향제에서 느낄 수 없었던 새로운 재질 표현이 가능하다.
In this way, the natural light material is sufficiently melted in water, and then the gypsum and the paper are blended and kneaded, whereby the color of the natural light material is uniformly applied uniformly to the aromatic agent composed of gypsum and paper. In addition, by tearing and kneading the Korean paper made of long fibers into the gypsum, it is possible to increase the durability of the fragrance and increase the duration of smell diffusion, as well as to prevent dusting phenomenon. Furthermore, the combination of dodecahedra and high-strength gypsum allows a long, soft texture of Korean paper to survive on the surface, allowing a new material expression that was not felt in conventional gypsum fragrances.

도 2는 본 발명의 다른 실시예에 따른 한지 석고 방향제의 제조방법을 설명하기 위한 순서도이다. 2 is a flow chart for explaining a method of producing a Korean gypsum aroma agent according to another embodiment of the present invention.

도 2를 참조하면, 본 발명의 다른 실시예들에 따른 한지 석고 방향제의 제조방법은 물에 석고를 배합하고 반죽하는 단계(S200); 상기 반죽된 물과 석고의 혼합물에 닥죽 상태의 한지를 찢어서 배합하는 단계 및 상기 배합된 물, 석고와 한지의 혼합물을 반죽하는 단계(S210); 상기 반죽된 물, 석고와 한지의 혼합물에 천연광 물질을 넣고 추가적으로 반죽하는 단계(S220); 상기 추가적으로 반죽된 물, 석고와 한지의 혼합물을 틀에 넣고 건조하는 단계(S230); 상기 건조된 물, 석고와 한지의 혼합물을 틀에서 탈거하여 추가적으로 건조하는 단계(S240); 및 상기 추가적으로 건조된 물, 석고와 한지의 혼합물에 방향 오일을 넣는 단계(S250)를 포함한다.Referring to FIG. 2, a method of manufacturing a Korean gypsum aroma agent according to another embodiment of the present invention includes mixing and kneading gypsum with water (S200); Tearing the mixture of the kneaded water and the gypsum with tearing and kneading the kneaded Korean paper, and kneading the blended mixture of the water, the gypsum and the Korean paper (S210); Adding a natural optical material to the mixture of the kneaded water, gypsum and Korean paper, and further kneading (S220); (S230) a mold and a mixture of the above-mentioned additional kneaded water, gypsum and paper, and drying the mixture; Removing the mixture of the dried water, gypsum and Korean paper from the mold and further drying (S240); And adding the directional oil to the mixture of the further dried water, gypsum and paper (S250).

본 발명의 다른 실시예에 따른 한지 석고 방향제의 제조방법은 도 1을 참조하여 설명한 일 실시예에 따른 한지 석고 방향제의 제조방법과 비교할 때, 방향제에 색을 입히기 위한 천연광 물질을 투입하는 시기가 큰 차이점이므로, 이를 중심으로 설명하고 나머지 설명은 생략하기로 한다. The method of manufacturing a Korean gypsum aroma agent according to another embodiment of the present invention is similar to the method of producing a Korean gypsum aromatic agent according to the embodiment described with reference to Figure 1, And therefore, the description thereof will be omitted.

물에 석고를 배합하고 반죽한 다음에, 닥죽 상태의 한지를 찢어 넣어가면서 배합하고 반죽한다. Mix gypsum in water and knead, then knead the kneaded Korean paper while tearing it.

이어서, 물, 석고와 한지가 배합 반죽된 혼합물에 천연광 물질을 넣고 가볍게 반죽한다. 이 때, 천연광 물질을 석고와 한지가 배합 반죽된 다음에 배합하여 반죽함으로써 천연광 물질의 색이 전체적으로 균일하게 입혀지는 것이 아니라, 일부분에만 색이 입혀지거나, 찢어서 배합 반죽된 한지의 느낌이 최대한 유지된 상태에서 색이 입혀지는 효과가 있다. Next, add natural light material to the mixture of water, gypsum and Korean paper and knead lightly. In this case, the natural light material is mixed with the gypsum and the Korean paper followed by kneading, so that the color of the natural light material is not uniformly applied as a whole, but only a part of the color is clogged or torn, There is an effect that the color is coated in the maintained state.

이어서, 천연광 물질까지 배합 반죽된 혼합물을 틀 내에서 20시간 이상, 틀에서 빼낸 다음 10일 이상 건조하고, 원하는 방향 오일을 넣어서 방향제를 완성한다. Subsequently, the blended mixture is extracted from the mold for 20 hours or more, then dried for 10 days or more, and the desired aromatic oil is added to complete the aromatic agent.

이와 같이, 석고와 한지를 배합하여 반죽한 다음에 천연광 물질을 넣어서 반줌함으로써, 천연광 물질의 색이 방향제의 일 부분에만 입혀지고 한지의 느낌을 최대한 살릴 수 있다. 또한 석고에 장섬유로 이루어진 한지를 찢어서 배합 반죽함으로써, 방향제의 내구성을 높이고 발향 지속시간을 증가시킬 수 있을 뿐만 아니라 가루날림 현상을 방지할 수 있다.
In this way, by blending gypsum and Korean paper, kneading and then adding natural light material, the color of natural light material is coated on only one part of the fragrance, and the feeling of Korean paper can be maximized. In addition, by tearing and kneading the Korean paper made of long fibers into the gypsum, it is possible to increase the durability of the fragrance and increase the duration of smell diffusion, as well as to prevent dusting phenomenon.

도 3은 본 발명의 일 실시예에 따른 한지 석고 방향장치를 설명하기 위한 사시도이다.3 is a perspective view for explaining a traditional Chinese gypsum board directional device according to an embodiment of the present invention.

도 3을 참조하면, 본 발명의 일 실시예에 따른 한지 석고 방향장치는 지지부(100)와 한지 석고 방향제(200)를 포함한다. Referring to FIG. 3, the Korean gypsum gauze apparatus according to an embodiment of the present invention includes a support 100 and a Korean gypsum aroma agent 200.

본 발명의 실시예들에 있어서, 지지부(100)가 하측에 위치하고, 한지 석고 방향제(200)가 지지부(100)의 상부에서 결합된다. In the embodiments of the present invention, the support portion 100 is located on the lower side, and the Korean gypsum aroma agent 200 is coupled to the upper portion of the support portion 100.

한편 지지부(100)는 한지 석고 방향제(200)를 하부에서 지지하는 역할을 한다. 하부면이 적어도 일 방향으로 기울어지도록 라운드(round)되어 형성된다. 일 예로, 지지부(100)는 반구 형상으로 이루어질 수 있다. 이와 달이, 지지부(100)는 안정감을 유지하기 위하여 바닥면이 평평한 형상을 가질 수도 있다. On the other hand, the supporting part 100 serves to support the Korean gypsum aroma agent 200 from below. So that the lower surface is inclined at least in one direction. For example, the support 100 may be hemispherical. In order to maintain a sense of stability, the supporting portion 100 may have a flat bottom surface.

한지 석고 방향제(200)는 닥죽 상태로 배합되어 건조된 한지와 석고로 이루어진다. 이 때, 닥죽 상태의 한지는 전체 중량 대비 3% 내지 35% 정도 배합될 수 있다. The Korean gypsum aroma agent (200) is composed of Korean paper and gypsum which are blended and dried. At this time, the frozen ground water can be blended in an amount of about 3% to 35% based on the total weight.

따라서 한지 석고 방향제(200)가 지지부의 상부에 구비되어 방향을 함으로써, 안정감 있게 설치될 수 있다.
Therefore, the Korean gypsum aroma agent 200 is provided on the upper part of the support part and can be installed in a stable manner.

도 4는 본 발명의 일 실시예에 따른 한지 석고 방향장치를 설명하기 위한 분해 단면도이다.4 is an exploded cross-sectional view for explaining a traditional Chinese gypsum board directional device according to an embodiment of the present invention.

도 4를 참조하면, 본 발명의 일 실시예에 따른 한지 석고 방향장치(10)는 지지부(100)와 지지부(100)의 상부에서 결합된 한지 석고 방향제(200)를 포함한다. Referring to FIG. 4, a Korean lime gypsum direction apparatus 10 according to an embodiment of the present invention includes a support 100 and a Korean gypsum fragrance 200 combined at the upper part of the support 100.

지지부(100)는 하부면이 적어도 일 방향으로 기울어지도록 라운드(round)되어 형성된 홀더(110)를 포함한다. 이 때, 홀더(110)의 상부면에 수용 공간을 갖는 홈(120)이 형성된다. 특히, 홈(120)은 홀더(110)의 상부면 중앙에 형성된다. The support portion 100 includes a holder 110 formed to be rounded such that the lower surface thereof is inclined at least in one direction. At this time, a groove 120 having a receiving space is formed on the upper surface of the holder 110. In particular, the groove 120 is formed at the center of the upper surface of the holder 110.

그리고 홀더(110)의 홈(120)에는 지지부(100)의 무게 중심을 유지할 수 있도록 홀더(110)보다 무거운 재질로 이루어진 무게추(130)가 삽입된다. 예를 들어, 홀더(110)는 나무 재질로 이루어지고, 무게추(130)는 금속 재질로 이루어지거나, 홀더(110)보다 무거운 나무 재질로 이루어진다. A weight 130 made of a material heavier than the holder 110 is inserted into the groove 120 of the holder 110 to maintain the center of gravity of the support 100. For example, the holder 110 is made of a wood material, and the weight 130 is made of a metal material or a wood material heavier than the holder 110.

따라서 홀더(110)의 하부면 형상에 의하여 한쪽 방향으로 기울어질 수 있는 현상이 홈(120)에 삽입된 무게추(130)에 의하여 억제될 수 있다. 즉, 지지부(100)는 한지 석고 방향제(200)를 상부에 안착한 상태에서 오뚜기와 같이 일정 각도로 기울어질 수 있도록 형성되어, 한지 석고 방향제(200)의 방향 효과를 더 높일 수 있다.
Therefore, a phenomenon that the holder 110 can be tilted in one direction due to the bottom surface shape can be suppressed by the weight 130 inserted into the groove 120. In other words, the supporting part 100 can be inclined at a predetermined angle like a crosshair when the Korean gypsum aroma agent 200 is seated on the upper part, so that the orienting effect of the Korean gypsum aroma agent 200 can be further enhanced.

도 5는 본 발명의 다른 실시예에 따른 한지 석고 방향장치를 설명하기 위한 분해 사시도이다.5 is an exploded perspective view for explaining a traditional Korean gypsum board directional apparatus according to another embodiment of the present invention.

도 5를 참조하면, 본 발명의 다른 실시예에 따른 한지 석고 방향장치(20)는 지지부(300)와 지지부(300)의 상부에서 결합된 한지 석고 방향제(400)를 포함한다.Referring to FIG. 5, a Korean lime gypsum apparatus 20 according to another embodiment of the present invention includes a support 300 and a Korean gypsum aroma agent 400 coupled to the upper part of the support 300.

지지부(300)는 하부면이 적어도 일 방향으로 기울어지도록 라운드(round)되어 형성된 홀더(310)를 포함한다. 이 때, 홀더(310)의 상부면에 수용 공간을 갖는 홈(320)이 형성된다. 특히, 홈(320)은 홀더(310)의 상부면 중앙에 형성된다. The support portion 300 includes a holder 310 formed to be rounded such that the lower surface thereof is inclined at least in one direction. At this time, a groove 320 having a receiving space is formed on the upper surface of the holder 310. In particular, the groove 320 is formed at the center of the upper surface of the holder 310.

그리고 홀더(310)의 홈(320)에는 링 형태의 결합부(330)가 삽입된다. 이에 링 형태의 결합부(330)가 홈(320)의 내부면에 접하면서 홈(320)에 끼워진다. 그리고 한지 석고 방향제(400)의 하단이 결합부(330)의 링에 대응되도록 형성되고, 한지 석고 방향제(400)의 하단이 결합부(330)에 끼워지게 된다. 따라서 지지부(300)와 한지 석고 방향제(400)가 끼움 결합됨으로써, 한지 석고 방향제(400)가 지지부(300)의 상단에 안정적으로 위치할 수 있다. A ring-shaped coupling part 330 is inserted into the groove 320 of the holder 310. And a ring-shaped coupling portion 330 is fitted in the groove 320 while contacting the inner surface of the groove 320. The lower end of the gypsum gypsum aroma agent 400 is formed to correspond to the ring of the coupling part 330 and the lower end of the gypsum gypsum aroma agent 400 is inserted into the coupling part 330. Therefore, the supporting part 300 and the Korean gypsum fragrance 400 can be stably positioned at the upper end of the supporting part 300 by fitting the Korean gypsum fragrance 400 into the supporting part 300.

또한, 결합부(330)는 금속재질로 이루어진다. 한편 홀더(310)는 나무 재질로 이루어지고, 결합부(330)는 금속 재질 이외에 홀더(310)보다 무거운 나무 재질로 이루어질 수 있다. 따라서 결합부(330)의 무거운 재질 특성에 의하여 지지부(100)의 무게 중심이 유지될 수 있다. 즉, 지지부(300)는 한지 석고 방향제(400)를 결합한 상태에서 오뚜기와 같이 일정 각도 만큼 기울어질 수 있도록 형성되어, 한지 석고 방향제(400)의 방향 효과를 더 높일 수 있다.
The coupling portion 330 is made of a metal material. Meanwhile, the holder 310 is made of a wood material, and the coupling part 330 may be made of a wood material that is heavier than the holder 310 in addition to the metal material. Therefore, the center of gravity of the supporting portion 100 can be maintained by the heavy material characteristic of the coupling portion 330. That is, the supporting part 300 can be inclined by a certain angle like a crosshair when the Korean gypsum aroma agent 400 is combined, so that the orienting effect of the Korean gypsum aroma agent 400 can be further enhanced.

이와 같이, 본 발명에 따른 한지 석고 방향제가 석고 반죽물에 닥죽 형태의 한지를 배합하여 형성됨으로써, 기존 석고방향제 보다 가벼우며, 가루날림은 줄이고 내구성이 향상될 뿐만 아니라 발향 지속 시간을 증가시킬 수 있다. 또한, 본 발명에 따른 한지 석고 방향제는 고강도 석고와 더불어 제습, 탈취, 항균의 효과를 가지는 한지의 닥섬유를 배합하여 소취성, 속건성, 항균성 등의 효과를 높였다. 또한, 닥섬유와 고강도 석고의 결합으로 한지의 기다랗고 부드러운 텍스쳐가 표면에 그대로 살아나 기존 석고방향제에서 느낄 수 없었던 새로운 재질 표현이 가능하게 되었다.
As described above, since the Korean gypsum aroma agent according to the present invention is formed by mixing the Korean rice gypsum-shaped Korean paper with the gypsum kneaded product, it is lighter than the conventional gypsum aroma agent, and the flour is reduced and the durability is improved, . In addition, the Korean gypsum aroma agent according to the present invention improves the effect of deodorizing, quick-drying, and antibacterial effects by blending high-strength gypsum with Korean paper fiber having dehumidification, deodorization and antibacterial effect. In addition, due to the combination of duck fiber and high strength gypsum, a long and smooth texture of Korean paper is alive on the surface, and new material expression that was not felt in conventional gypsum fragrance became possible.

앞서 설명한 본 발명의 상세한 설명에서는 본 발명의 바람직한 실시예들을 참조하여 설명하였지만, 해당 기술 분야의 숙련된 당업자 또는 해당 기술 분야에 통상의 지식을 갖는 자라면 후술될 특허청구범위에 기재된 본 발명의 사상 및 기술 영역으로부터 벗어나지 않는 범위 내에서 본 발명을 다양하게 수정 및 변경시킬 수 있음을 이해할 수 있을 것이다.
While the present invention has been described in connection with what is presently considered to be practical and exemplary embodiments, it is to be understood that the invention is not limited to the disclosed embodiments, but, on the contrary, It will be understood by those skilled in the art that various changes in form and details may be made therein without departing from the spirit and scope of the invention as defined by the appended claims.

10 : 한지 석고 방향장치 100, 300 : 지지부
110, 310 : 홀더 120, 320 : 홈
130 : 무게추 330 : 결합부
200, 400 : 한지 석고 방향제10: Korean gypsum board 100, 300: Support
110, 310: holder 120, 320: groove
130 weight weight 330 coupling unit
200, 400: Korean plaster aromatic

Claims

A method for producing a Korean gypsum fragrance mixed with Korean paper and gypsum,
Dissolving the natural light material in water;
Blending and kneading gypsum with water in which the natural light material is melted;
Kneading the mixture of water and gypsum while tearing the Korean paper in a frozen state;
Casting a mixture of the kneaded water, gypsum and Korean paper into a mold and drying;
Removing the mixture of the dried water, gypsum and paper, and further drying the same; And
And adding the directional oil to the mixture of the further dried water, gypsum and Korean paper.

A method for producing a fragrance mixed with Korean paper and gypsum,
Mixing and kneading gypsum in water;
Tearing a mixture of the kneaded water and the gypsum and kneading the kneaded Korean paper;
Kneading the blended water, a mixture of gypsum and paper,
Adding a natural light material to the mixture of the kneaded water, gypsum and Korean paper, and further kneading;
Drying the mixture of the additional kneaded water, gypsum and paper, into a mold and drying;
Removing the mixture of the dried water, gypsum and paper, and further drying the same; And
And adding the directional oil to the mixture of the further dried water, gypsum and Korean paper.

3. The method according to claim 1 or 2,
In the step of mixing gypsum in the water
Wherein the gypsum is blended with 80% to 85% by weight of water.

3. The method according to claim 1 or 2,
In the step of blending the frozen ground paper,
Wherein the frozen ground water is mixed with 3% to 35% of the total weight of the water.

3. The method according to claim 1 or 2,
The step of casting and drying the mixture is carried out for at least 20 hours,
Wherein the step of removing from the mold and further performing drying is performed for 10 days or more.

A Korean paper gypsum fragrance produced by the method of any one of claims 1 and 2.

In the perfume,
A Korean paper gypsum fragrance consisting of Korean paper and gypsum blended in dry state.

8. The method of claim 7,
Characterized in that the frozen ground water is mixed in an amount of about 3% to 35% based on the total weight of the ground water.

In a Korean paper gypsum direction device,
A support;
And a gypsum gypsum fragrance which is combined with the supporting part at the upper part of the support part and composed of dried gypsum and dried gypsum blended in a dry state.

10. The method of claim 9,
Characterized in that the hyssop powder is mixed with 3% to 35% of the total weight of the Korean gypsum fragrance.

10. The apparatus according to claim 9,
A holder formed on the upper surface with a groove having a receiving space and rounded so that the lower surface is inclined at least in one direction; And
And a weight attached to the groove of the holder and made of a material heavier than the holder so as to maintain the center of gravity of the support.

10. The apparatus according to claim 9,
A holder formed on the upper surface with a groove having a receiving space and rounded so that the lower surface is inclined at least in one direction; And
And a ring-shaped coupling part made of a metal material and formed on an inner surface of the groove of the holder.