KR20160077273A - Polyamide based polymer compositions having high flowability and mechanical strength and polyamide based composite comprising the same - Google Patents

Polyamide based polymer compositions having high flowability and mechanical strength and polyamide based composite comprising the same Download PDF

Info

Publication number
KR20160077273A
KR20160077273A KR1020140185929A KR20140185929A KR20160077273A KR 20160077273 A KR20160077273 A KR 20160077273A KR 1020140185929 A KR1020140185929 A KR 1020140185929A KR 20140185929 A KR20140185929 A KR 20140185929A KR 20160077273 A KR20160077273 A KR 20160077273A
Authority
KR
South Korea
Prior art keywords
weight
polymer composition
polyamide
flow control
control agent
Prior art date
Application number
KR1020140185929A
Other languages
Korean (ko)
Inventor
유영재
원종찬
김용석
김병각
최환석
하성민
권오환
Original Assignee
한국화학연구원
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 한국화학연구원 filed Critical 한국화학연구원
Priority to KR1020140185929A priority Critical patent/KR20160077273A/en
Publication of KR20160077273A publication Critical patent/KR20160077273A/en

Abstract

The present invention provides a polymer composition comprising: 20-90 wt% of a polyamide-based resin; 10-80 wt% of a glass fiber; and a flow control agent, which is a p-phenylene bis stearamide. According to the present invention, the polymer composition has an effect of significantly reducing torque by effectively dispersing a polyamide-based resin and a glass fiber and reducing friction between a molten resin and a processing device by using a flow control agent, which is p-phenylene bis stearamide. Therefore, according to the present invention, a composite material manufactured from a polymer composition can be usefully used for compounding or extruding and injection molding polyamide-based engineering plastic including a high content of glass fiber.

Description

The present invention relates to a polyamide-based polymer composition having excellent flowability and mechanical strength, and a polyamide-based composite material containing the same.

The present invention relates to a polyamide-based polymer composition having excellent flowability and mechanical strength, and a polyamide-based composite material containing the same.

In recent years, automakers have been making continuous efforts to reduce the weight of automobiles as the automobile fuel efficiency and exhaust emission regulations of governments around the world are strengthened. As a means to reduce vehicle weight, the number of parts is reduced by optimizing design and maximizing parts performance, and the application of lightweight substitute materials such as aluminum, magnesium, engineering plastics, fiber reinforced plastics and fiber reinforced composites. Among these, the application of lightweight substitute materials enables not only the weight reduction of the parts but also the optimum design and integration of parts, thus maximizing the effect of light weight.

Fiber reinforced plastic or fiber reinforced composite material is a general term of composite material reinforced with glass fiber, carbon fiber, aramid fiber and the like using plastic as a matrix. Recently, it is required to have high strength and heat resistance . In recent years, automobile and industrial products have become increasingly high performance and lightweight, and component parts are required to have more precise shapes than before, and performance such as high heat resistance and high rigidity is required.

Polyamide composite materials are excellent materials such as rigidity, toughness and chemical resistance. They are excellent in light weight, impact resistance, thermal expansion coefficient and economical efficiency, so they can be used as alternative materials such as aluminum and steel. %, It is possible to present solutions using the advanced materials to the automobile market which requires the weight reduction of automobile, design flexibility, and easiness of molding when it is applied not only to automobile exterior but also to internal parts including housing.

As an example related to the polyamide-based composite material as described above, Korean Patent Laid-Open No. 10-2009-0063382 discloses a polyamide-reinforced resin composition. Specifically, TGA analysis at 300 占 폚 (after 10 minutes elapsed) showed a weight loss of 5% or less, a fluidity of 20 g / 10 min or more according to ASTM evaluation method D1238, and an irradiation intensity of 65 W / And a flexural strength according to the ASTM evaluation method D790 is in the range of 1,300 to 3,000 kg / m < 2 >.

However, in order to realize the high performance of polyamide-based composite, a compounding technique with various reinforcing materials is essential. When a high amount of glass fiber is added, the flowability is poor. When the physical properties are satisfied, Molding is difficult through process or injection process. Since the processability of the polymer is limited by improvement of the monomer, molecular weight, and molecular structure, it is necessary to use a flow control agent such as a lubricant which influences the viscosity behavior of the melt as well as the selection of processing equipment do.

In particular, studies on high-content glass fiber reinforced composites with a content of 50% or more have limitations on productivity and physical properties due to fracture of glass fiber, and the bending elastic modulus of 15 GPa compared to that of advanced countries is 25 GP %, It is necessary to research and develop to overcome this.

Accordingly, the inventors of the present invention have been studying a polymer composition having excellent flowability and mechanical strength, wherein 20 wt% to 90 wt% of a polyamide resin; A polymer composition comprising 10 wt% to 80 wt% of glass fiber and a flow control agent, which is p-phenylene bis stearamide, was added to the polymer composition. The fluidity and mechanical properties of the polymer composition Strength, and completed the present invention.

An object of the present invention is to provide a polyamide-based polymer composition having excellent flowability and mechanical strength, and a polyamide-based composite material containing the same.

In order to achieve the above object,

20% to 90% by weight of a polyamide-based resin;

10% to 80% by weight of glass fibers; And

and a flow control agent which is p-phenylene bis stearamide.

In addition,

And a flow control agent which is 20 to 90% by weight of a polyamide based resin, 10 to 80% by weight of a glass fiber, and a p-phenylene bis stearamide, A method for preparing a composition is provided.

Further,

20% to 90% by weight of a polyamide-based resin; And 10 to 80% by weight of a glass fiber; and a flow regulator, which is p-phenylene bis stearamide, to the polymer composition to improve the mechanical strength of the polymer composition do.

In addition,

And a polyamide composite material containing the above polymer composition.

Further,

(Step 1) of 20 to 90% by weight of a polyamide based resin, 10 to 80% by weight of a glass fiber, and a flow control agent which is p-phenylene bis stearamide;

Hot extruding the mixture of step 1 (step 2); And

And a step (3) of injection-molding the extrudate of the step (2). The present invention also provides a process for producing a polyamide-based composite material comprising the above polymer composition.

The polymer composition according to the present invention has the effect of reducing the friction between the molten resin and the processing machine and effectively dispersing the polyamide resin and the glass fiber by using the flow control agent which is p-phenylenebisstearamide to significantly reduce the torque . Accordingly, the composite material produced from the polymer composition according to the present invention can be usefully used for compounding, extrusion and injection molding of a polyamide engineering plastic containing a high amount of glass fibers.

The present invention

20% to 90% by weight of a polyamide-based resin;

10% to 80% by weight of glass fibers; And

and a flow control agent which is p-phenylene bis stearamide.

Hereinafter, the polymer composition according to the present invention will be described in detail.

The polymer composition according to the present invention comprises 20 to 90% by weight of a polyamide resin; A polymer composition comprising 10 to 80% by weight of a glass fiber, wherein a flow control agent is added to a polymer composition comprising p-phenylene bis stearamide, wherein the p-phenylene bisstearamide By including the flow control agent, the polymer composition can exhibit excellent flowability and excellent mechanical strength.

When a composite material is produced from a polymer composition exhibiting excellent fluidity and excellent mechanical strength, it can be advantageously applied to compounding, extrusion and injection molding of a polyamide engineering plastic containing a high amount of glass fibers.

Specifically, the polymer composition according to the present invention exhibits an effect of decreasing viscosity toward the high-speed shear region, which improves fluidity under actual extrusion and extrusion conditions, thereby reducing the load on the equipment, thereby increasing the service life of the equipment , Lowering production power and output energy, and lowering the overall production cost. At the same time, since the polymer composition according to the present invention has excellent mechanical strength, it can be applied to various fields.

In the polymer composition according to the present invention, the flow control agent, which is p-phenylene bis stearamide, is a compound represented by the following formula (1).

≪ Formula 1 >

Figure pat00001

The flow control agent, which is p-phenylene bis stearamide used in the present invention, may exhibit a very good flowability as compared with the conventional flow control agent.

In addition, the flow control agent preferably comprises 0.1 to 5.0 parts by weight based on the total polymer composition. When the flow control agent contains less than 0.1 part by weight of the total polymer composition, there is a problem that excellent flowability obtained by adding a flow control agent is not obtained. When the flow control agent is contained in an amount exceeding 5.0 parts by weight, There is a problem that the mechanical strength of the composite material becomes poor.

In the polymer composition according to the present invention, the polymer composition comprises 20 to 90% by weight of a polyamide resin; And 10 to 80% by weight of glass fibers; 20 to 50% by weight of a polyamide-based resin; And 50 to 80% by weight of glass fibers. The polymer composition according to the present invention can be used as a polymer composition for producing a high content of glass fiber reinforced composite material containing 50% by weight or more of glass fiber.

Conventionally, when a high content of glass fibers is contained, the productivity and the property improvement due to the breakage of the glass fiber have been limited. However, the polymer composition according to the present invention is not limited to p-phenylene bis stearamide, can exhibit excellent fluidity as well as excellent mechanical strength.

In addition,

And a flow control agent which is 20 to 90% by weight of a polyamide based resin, 10 to 80% by weight of a glass fiber, and a p-phenylene bis stearamide, A method for preparing a composition is provided.

The method for producing a polymer composition according to the present invention comprises the steps of: preparing a polymer composition comprising 20 to 90% by weight of a polyamide resin, 10 to 80% by weight of a glass fiber, and a flow of p-phenylene bis stearamide A method of melt mixing the modifier is used.

Specifically, the polymer composition comprises 20% by weight to 50% by weight of a polyamide resin; And 50 to 80% by weight of glass fibers. The method for producing a polymer composition according to the present invention is a method for preparing a polymer composition for producing a high content of glass fiber reinforced composite material containing 50% by weight or more of glass fiber, and conventionally, However, the use of a flow control agent, which is p-phenylene bis stearamide, exhibits excellent flowability as well as excellent mechanical strength. .

The flow control agent, which is p-phenylene bis stearamide, is preferably used in an amount of 0.1 to 5.0 parts by weight based on the total polymer composition. If the flow control agent is used in an amount of less than 0.1 part by weight based on the total polymer composition, there is a problem that excellent flowability obtained by adding a flow control agent can not be obtained. When the flow control agent is used in an amount exceeding 5.0 parts by weight, There is a problem that the mechanical strength of the composite material becomes poor.

Further, the melt mixing is not limited as long as the polyamide based resin can be melted, and may be performed at a temperature of 200 ° C to 500 ° C.

In addition,

20% to 90% by weight of a polyamide-based resin; And 10 to 80% by weight of a glass fiber; and a flow regulator, which is p-phenylene bis stearamide, to the polymer composition to improve the mechanical strength of the polymer composition do.

Hereinafter, a method for improving the mechanical strength of the polymer composition according to the present invention will be described in detail.

A method for improving the mechanical strength of the polymer composition according to the present invention comprises: 20 to 90% by weight of a polyamide-based resin; By adding a flow control agent such as p-phenylene bis stearamide to a polymer composition comprising 10 to 80% by weight of glass fiber, a flow control agent such as p-phenylenebisstearamide , The polymer composition can exhibit excellent fluidity and can exhibit excellent mechanical strength including a high content of glass fibers.

When a composite material is produced from a polymer composition exhibiting excellent fluidity and excellent mechanical strength, it can be advantageously applied to compounding, extrusion and injection molding of a polyamide engineering plastic containing a high amount of glass fibers.

Specifically, the polymer composition comprises 20% by weight to 50% by weight of a polyamide resin; And 50 to 80% by weight of glass fibers. In the method of improving the mechanical strength of the polymer composition according to the present invention, when the glass fiber is contained in an amount of 50% by weight or more, the productivity is improved and the physical properties are improved due to the breakage of the glass fiber. However, By using a flow control agent, which is p-phenylene bis stearamide, not only excellent flowability but also excellent mechanical strength can be exhibited even when a high content of glass fiber is included.

The flow control agent, which is p-phenylene bis stearamide, is preferably used in an amount of 0.1 to 5.0 parts by weight based on the total polymer composition. If the flow control agent is used in an amount of less than 0.1 part by weight based on the total polymer composition, there is a problem that excellent flowability obtained by adding a flow control agent can not be obtained. When the flow control agent is used in an amount exceeding 5.0 parts by weight, There is a problem that the mechanical strength of the composite material becomes poor.

Further,

And a polyamide composite material containing the above polymer composition.

Since the polyamide composite material comprising the polymer composition according to the present invention comprises a polymer composition comprising a flow control agent which is p-phenylene bis stearamide, it contains a high content of glass fibers , There is no reduction in physical properties, and thus excellent mechanical strength can be exhibited.

Further,

(Step 1) of 20 to 90% by weight of a polyamide based resin, 10 to 80% by weight of a glass fiber, and a flow control agent which is p-phenylene bis stearamide;

Hot extruding the mixture of step 1 (step 2); And

And a step (3) of injection-molding the extrudate of the step (2). The present invention also provides a process for producing a polyamide-based composite material comprising the above polymer composition.

Hereinafter, the method for producing the polyamide composite material according to the present invention will be described in detail for each step.

First, in the method for producing a polyamide composite material according to the present invention, step 1 is a step of preparing a polyamide-based composite material by mixing 20 wt% to 90 wt% of a polyamide resin, 10 wt% to 80 wt% (p-phenylene bis stearamide).

Specifically, the polyamide-based resin of step 1 is 20 wt% to 50 wt%, and the glass fiber is more preferably mixed 50 wt% to 80 wt%. A high content of glass fiber reinforced composite material containing 50 wt% or more of glass fiber can exhibit excellent mechanical strength. However, when a high content of glass fibers is used as described above, productivity and physical properties due to fracture of glass fiber have been limited. However, in the present invention, p-phenylene bis stearamide Can exhibit not only excellent flowability but also excellent mechanical strength.

The flow regulator used as the p-phenylene bis stearamide in step 1 is preferably used in an amount of 0.1 to 5.0 parts by weight based on the total polymer composition. If the flow control agent of step 1 is used in an amount of less than 0.1 part by weight based on the total polymer composition, there is a problem that excellent fluidity can not be obtained by adding a flow control agent. When the flow control agent is used in an amount exceeding 5.0 parts by weight, There is a problem in that the mechanical strength of the composite material produced from the composition deteriorates.

Further, the melt mixing of step 1 above is not limited as long as it is capable of melting the polyamide-based resin, and may be performed at a temperature of 200 ° C to 500 ° C.

Next, in the method for producing a polyamide composite material according to the present invention, Step 2 is a step of subjecting the mixture of Step 1 to hot extrusion.

Specifically, the hot extrusion of step 2 is preferably performed at a temperature of 200 ° C to 350 ° C. If the hot extrusion of the step 2 is carried out at a temperature lower than 200 ° C, it is difficult to uniformly mix the polyamide-based resin and the glass fiber. If the extrusion is carried out at a temperature higher than 350 ° C, the mechanical properties There is a problem that the cost is reduced due to the process at a high temperature.

Next, in the method for producing a polyamide composite material according to the present invention, Step 3 is injection molding the extrudate of Step 2 above.

As a specific example, the injection molding of step 3 can be performed by a known method using an apparatus such as an injection molding machine.

Hereinafter, the present invention will be described in detail with reference to the following examples and experimental examples.

It should be noted, however, that the following examples and experimental examples are illustrative of the present invention, but the scope of the invention is not limited by the examples and the experimental examples.

≪ Example 1 > Preparation of polymer composition 1

50% by weight of a polyamide-based resin (24AE1K from RHODIA), 50% by weight of glass fiber (Owens Corning, length: 3 mm, diameter: 13 탆, 123D in chopped form), p-phenylenebisstearamide 1 part by weight (based on 100 parts by weight of the total polymer composition) of p-phenylene bis stearamide (PDA) were uniformly mixed.

Then, the mixture was kneaded for 4 minutes at a temperature of 270 DEG C and a screw rotation speed of 80 rpm using a 15 cc microcompounder (DSM Xplore) in the form of a twin screw, to prepare a polymer composition.

≪ Comparative Example 1 &

100 weight% of a polyamide resin (24AE1K manufactured by RHODIA) was kneaded for 4 minutes at a temperature of 270 DEG C and a screw rotation speed of 80 rpm using a 15 cc microcompounder (DSM Xplore) in the form of a twin screw to prepare a polymer composition Respectively.

≪ Comparative Example 2 &

100 parts by weight of a polyamide resin (24AE1K manufactured by RHODIA), 1 phr of p-phenylene bis stearamide (p-PDA) as a flow control agent (parts by weight based on 100 parts by weight of the total polymer composition) And uniformly mixed.

Then, the mixture was kneaded for 4 minutes at a temperature of 270 DEG C and a screw rotation speed of 80 rpm using a 15 cc microcompounder (DSM Xplore) in the form of a twin screw, to prepare a polymer composition.

≪ Comparative Example 3 &

A polymer composition was prepared in the same manner as in Comparative Example 1, except that SUNLUBE EBS (Pioneer Chemical) commercialized as a flow modifier in Comparative Example 1 was used.

≪ Comparative Example 4 &

A polymer composition was prepared in the same manner as in Comparative Example 1, except that TR 063A (STRUKTOL®), which was used as a flow control agent in Comparative Example 1, was used.

≪ Comparative Example 5 &

50 wt% of a polyamide based resin (24AE1K manufactured by RHODIA), and 50 wt% of glass fibers (Owens Corning, length: 3 mm, diameter: 13 탆, chopped type 123D) were uniformly mixed.

Then, the mixture was kneaded for 4 minutes at a temperature of 270 DEG C and a screw rotation speed of 80 rpm using a 15 cc microcompounder (DSM Xplore) in the form of a twin screw, to prepare a polymer composition.

≪ Comparative Example 6 >

A polymer composition was prepared in the same manner as in Example 1 except that SUNLUBE EBS (Pure Chemical), which was commercialized as a flow modifier in Example 1, was used.

≪ Comparative Example 7 &

A polymer composition was prepared in the same manner as in Example 1 except that TR 063A (STRUKTOL (R)), which was used as a flow modifier in Example 1, was used.

≪ Experimental Example 1 >

In order to measure the average torque of the polymer composition according to the present invention, the following experiment was conducted.

The polymer composition prepared in Example 1 and Comparative Examples 1 to 7 was extruded using a 15 cc microcompounder (DSM Xplore) in the form of a biaxial screw at a temperature of 270 DEG C and a screw rotation speed of 80 rpm for 4 minutes The average torque was measured by kneading. The results are shown in Table 1 below.

Polyamide resin
(weight%) glass fiber
(weight%) Flow regulator
Kinds content
(phr) Average torque
(N) Example 1 50 50 p-PDA One 1752 Comparative Example 1 100 0 - 0 1794 Comparative Example 2 100 0 p-PDA One 407 Comparative Example 3 100 0 EBS One 1587 Comparative Example 4 100 0 TR 063A One 1511 Comparative Example 5 50 50 - 0 1945 Comparative Example 6 50 50 EBS One 1891 Comparative Example 7 50 50 TR 063A One 1811

As shown in Table 1, the polymer composition comprising p-phenylenebisstearamide as a flow modifier according to the present invention is excellent in the average torque reduction effect. In particular, when Comparative Example 1 which does not contain glass fibers and Comparative Example 2 are compared with each other, the average torque of the polymer composition containing p-phenylenebisstearamide in Comparative Example 2 is lower than that of the p- Which is about 77% as compared with the average torque of the polymer composition containing no imide.

In addition, it was confirmed that the average torque reduction effect was excellent when the flow control agent comprising p-phenylenebisstearamide according to the present invention was included in comparison with the polymer composition containing the flow control agent conventionally used in the prior art.

EXPERIMENTAL EXAMPLE 2 Viscosity Analysis of Polymer Composition

In order to measure the viscosity of the polymer composition according to the present invention, the following experiment was conducted.

The viscosity of the polymer composition prepared in Example 1 and Comparative Examples 5 to 7 was measured using a capillary viscometer (GOTTFERT, RHEOGRAPH25). The results are shown in Table 2 below.

Flow regulator
Kinds content
(phr) Shear rate
(1 / s) shear
(Pa) Viscosity
(Pa.s) Comparative Example 5 - 0 100.0 59157.5 591.6 1000.0 130323.3 260.6 5000.0 170085.0 170.1 10000.0 388515.0 77.7 Comparative Example 6 EBS One 100.0 56607.8 566.1 1000.0 108376.9 216.7 5000.0 102986.5 103.0 10000.0 273631.1 54.7 Comparative Example 7 TR 063A One 100.0 55472.0 554.7 1000.0 90679.0 181.3 5000.0 81929.9 81.9 10000.0 269746.0 53.9 Example 1 p-PDA One 100.0 53428.3 534.3 1000.0 168820.0 168.8 5000.0 361947.5 72.4 10000.0 504165.0 50.4

As shown in Table 2, it can be confirmed that the polymer composition comprising p-phenylene bisstearamide as the flow modifier according to the present invention exhibits an effect of decreasing the viscosity toward the high shear region.

This improves the fluidity under the actual extrusion and injection conditions, which reduces the load on the equipment, thereby increasing the service life of the equipment, lowering the production power and output energy, and lowering the overall production cost.

<Experimental Example 3> Measurement of physical properties of polymer composition

In order to measure the physical properties of the polymer composition according to the present invention, the following experiment was conducted.

The physical properties of the polymer compositions prepared in Example 1, Comparative Example 1, Comparative Example 2 and Comparative Examples 5 to 7 were measured using an universal testing machine (Instron) and an Izod impact testing machine (Instron) , And the results are shown in Table 3 below.

Polyimide resin
(weight%) glass fiber
(weight%) Flow regulator
Kinds content
(phr) Flexural modulus
(GPa) Impact strength
(kJ / m 2 ) Example 1 50 50 p-PDA One 14.18 14.51 Comparative Example 1 100 0 - 0 2.97 3.67 Comparative Example 2 100 0 p-PDA One 2.94 2.84 Comparative Example 5 50 50 - 0 12.86 13.87 Comparative Example 6 50 50 EBS One 11.48 11.83 Comparative Example 7 50 50 TR0 63A One 11.03 12.29

As shown in Table 3, the polymer composition comprising p-phenylenebisstearamide as a flow modifier according to the present invention is excellent in flowability during molding and has excellent mechanical properties as compared with conventional flow control agents .

As described above, the polymer composition of the present invention reduces the friction between the molten resin and the processing machine and effectively disperses the polyamide-based resin and the glass fiber using the flow control agent, which is p-phenylenebisstearamide, It was confirmed that there is an effect.

Accordingly, the composite material produced from the polymer composition according to the present invention can be usefully used for compounding, extrusion and injection molding of a polyamide engineering plastic containing a high amount of glass fibers.

Claims (10)

20% to 90% by weight of a polyamide-based resin;
10% to 80% by weight of glass fibers; And
and a flow control agent which is p-phenylene bis stearamide.
The method according to claim 1,
Wherein the flow control agent comprises 0.1 to 5 parts by weight based on the total polymer composition.
The method according to claim 1,
20% by weight to 50% by weight of a polyamide-based resin; And
And 50% by weight to 80% by weight of glass fibers.
And a flow control agent which is 20 to 90% by weight of a polyamide based resin, 10 to 80% by weight of a glass fiber, and a p-phenylene bis stearamide, &Lt; / RTI &gt;
5. The method of claim 4,
Wherein the melt mixing is performed at a temperature of 200 ° C to 500 ° C.
20% to 90% by weight of a polyamide-based resin; And 10 to 80% by weight of a glass fiber; and adding a flow regulator, which is p-phenylene bis stearamide, to the polymer composition to improve the mechanical strength of the polymer composition.
The method according to claim 6,
Wherein the flow control agent comprises 0.1 to 5 parts by weight based on the total polymer composition.
The method according to claim 6,
20% by weight to 50% by weight of a polyamide-based resin; And 50 to 80% by weight of glass fibers.
A polyamide-based composite material comprising the polymer composition of claim 1.
(Step 1) of 20 to 90% by weight of a polyamide based resin, 10 to 80% by weight of a glass fiber, and a flow control agent which is p-phenylene bis stearamide;
Hot extruding the mixture of step 1 (step 2); And
And a step (3) of injection molding the extrudate of step (2). The method of producing a polyamide based composite material according to claim 1,
KR1020140185929A 2014-12-22 2014-12-22 Polyamide based polymer compositions having high flowability and mechanical strength and polyamide based composite comprising the same KR20160077273A (en)