KR20150124159A - Wall panel using polyvinylchloride resin - Google Patents

Wall panel using polyvinylchloride resin Download PDF

Info

Publication number
KR20150124159A
KR20150124159A KR1020140050628A KR20140050628A KR20150124159A KR 20150124159 A KR20150124159 A KR 20150124159A KR 1020140050628 A KR1020140050628 A KR 1020140050628A KR 20140050628 A KR20140050628 A KR 20140050628A KR 20150124159 A KR20150124159 A KR 20150124159A
Authority
KR
South Korea
Prior art keywords
layer
weight
parts
pvc
resin
Prior art date
Application number
KR1020140050628A
Other languages
Korean (ko)
Inventor
김지웅
Original Assignee
(주)엘지하우시스
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by (주)엘지하우시스 filed Critical (주)엘지하우시스
Priority to KR1020140050628A priority Critical patent/KR20150124159A/en
Publication of KR20150124159A publication Critical patent/KR20150124159A/en

Abstract

The present invention relates to a wall panel installed in an indoor space of a building structure and, more specifically, to a wall panel using a PVC resin, capable of freely providing a depth embossing effect in harmony with printed patterns of trees, stone, and the like by using a PVC resin. According to the present invention, the wall panel using a PVC resin to be installed on an indoor wall surface includes a base layer and a surface layer composed of a reinforcing layer, a print layer, and a transparent layer and stacked on the top surface of the base layer, wherein the surface layer is made of a PVC resin.

Description

PVC 수지를 이용한 벽장재 {Wall panel using polyvinylchloride resin}Wall panel using polyvinylchloride resin.

본 발명은 건축 구조물의 실내에 설치되는 벽장재에 관한 것으로, 더욱 상세하게는 PVC 수지를 이용하여 나무, 돌 등의 인쇄패턴에 어울리는 수 있는 깊이 엠보 효과를 자유롭게 구현할 수 있는 PVC 수지를 이용한 벽장재에 관한 것이다.The present invention relates to a closet material installed in a building structure. More specifically, the present invention relates to a closet material using a PVC resin which can be embodied with a depth embossing effect suitable for a printed pattern of wood, .

일반적으로 벽장재는 MDF, HDF 혹은 목재의 일면에 대리석, 원목, 벽돌 등의 패턴을 구현하여 조립식으로 건축물의 실내에 시공되는 인테리어 자재이다. In general, the closet material is MDF, HDF, or an interior material that is installed in the interior of the building by assembling patterns of marble, wood, and brick on one side of the wood.

이러한 벽장재는 벽지와는 달리 접착제를 사용하지 않고 시공이 가능하여 작업이 편리하고, 유해 물질의 배출을 억제할 수 있다는 장점이 있으며, 특히 최근에는 새집 증후군 및 아토피 발생을 억제하기 위하여 광촉매와 은나노가 첨가된 제품도 개발되고 있다.These closet materials have advantages that they can be applied without using adhesives, unlike wallpaper, and are easy to work and can suppress the emission of harmful substances. In recent years, in order to suppress sick building syndrome and atopy, photocatalysts and silver nano- Added products are being developed.

도 1은 종래의 일반적인 벽장재를 예시한 단면도이다.FIG. 1 is a cross-sectional view illustrating a conventional conventional closet material.

도 1은 도시된 바와 같이 종래의 일반적인 벽장재는 베이스층(10)으로 고밀도섬유판(HDF) 혹은 중밀도섬유판(MDF)을 이용하고, 그 상면에 멜라민 함침 모양지(20)를 가지며, 이 모양지(20)의 상면에 다시 멜라민 함침 오버레이 시트층(30)이 적층되고, 베이스층(40)의 저면에 밸런스를 위해 멜라민 함침 밸런스층(40)이 구비된다. As shown in FIG. 1, a typical conventional wall-and-ceiling material includes a high-density fiberboard (HDF) or a medium-density fiberboard (MDF) as the base layer 10 and a melamine impregnated paper 20 on the upper surface thereof. A melamine impregnated overlay sheet layer 30 is laminated on the upper surface of the base layer 20 and a melamine impregnated balance layer 40 is provided on the bottom surface of the base layer 40 for balance.

이러한 벽장재는 일반적으로 라미네이션(Laminating)방법으로 합지된다.Such a closet material is generally laminated by a laminating method.

그런데 모양지(20)와 시트층(30)에 함침되는 멜라민 수지는 따뜻한 느낌보다는 차가운 느낌이 강하고, 일정 이상의 하중이나 날카로운 물체 의해 충격이 가해지면 쉽게 깨지거나 찍히는 등의 부분 파손이 발생하는 단점이 있다.However, the melamine resin impregnated in the shape sheet 20 and the sheet layer 30 has a cold feeling rather than a warm feeling, and a disadvantage that when the impact is applied due to a certain load or a sharp object, the melamine resin easily breaks or is caught have.

또한, 인위적인 인쇄형태로 표현되는 표면은 깊은 엠보를 적용하는데 한계가 있어 자연 질감이 많이 떨어지는 문제점이 있었다.
In addition, there is a problem that the surface expressed by an artificial printing form has a limitation in applying a deep embossing, resulting in a decrease in natural texture.

본 발명은 이러한 종래의 문제점을 해결하기 위한 것으로서, HDF, MDF 또는 합판의 베이스층 상면에 접착되는 표면층을 PVC 수지로 구성하여 표면층 생산시 나무, 돌 등의 인쇄 패턴에 어울릴 수 있는 깊은 엠보를 자유롭게 구현하여 자연 질감을 향상시킬 수 있는 PVC 수지를 이용한 벽장재를 제공하는 데 그 목적이 있다. SUMMARY OF THE INVENTION The present invention has been made to solve such conventional problems, and it is an object of the present invention to provide a surface layer adhered to the upper surface of an HDF, MDF or plywood, The present invention is to provide a closet material using PVC resin which can improve natural texture.

또한, 본 발명은 자연스러운 인쇄층을 갖도록 함과 동시에 시공이 편리하고, 제작이 용이한 벽장재를 제공하는 데 그 목적이 있다.
It is another object of the present invention to provide a closet material having a natural printed layer, a convenient construction, and easy fabrication.

상기 목적을 달성하기 위하여 본 발명의 PVC 수지를 이용한 벽장재는, 건축물의 실내 벽면에 시공되는 벽장재에 있어서, 베이스층; 상기 베이스층의 상면에 보강층, 인쇄층, 투명층으로 이루어진 표면층을 적층하여 구성하되, 상기 표면층은 PVC 수지로 구성된 것을 특징으로 한다.In order to achieve the above object, a closet material using PVC resin according to the present invention is a closet material applied to an indoor wall surface of a building, A surface layer comprising a reinforcing layer, a printing layer and a transparent layer is laminated on an upper surface of the base layer, wherein the surface layer is made of a PVC resin.

또한, 상기 베이스층은 MDF, HDF 혹은 합판 중 하나인 것을 특징으로 한다.The base layer may be one of MDF, HDF, or plywood.

또한, 상기 베이스층의 상면에는 접착제를 50-200g/㎡으로 도포하여 상기 보강층을 접착하는 것을 특징으로 한다.The upper surface of the base layer is coated with an adhesive of 50-200 g / m < 2 > to adhere the reinforcing layer.

또한, 상기 보강층, 인쇄층, 투명층은, PVC 수지에 프탈레이트계 가소제, 에폭시화 대두유, 바륨-아연 안정제, 탄산칼슘 중 하나 이상을 선택적으로 포함하는 수지 조성물로 형성된 것을 특징으로 한다.The reinforcing layer, the printing layer, and the transparent layer are formed of a resin composition that selectively contains at least one of a phthalate plasticizer, an epoxidized soybean oil, a barium-zinc stabilizer, and calcium carbonate in a PVC resin.

또한, 상기 보강층은, 중합도가 1000 ~ 1700인 폴리염화비닐(PVC) 100 중량부, 프탈레이트계 가소제 20 ~ 50 중량부, 에폭시화 대두유(E,S,O) 1 ~ 3 중량부, 바륨-아연 안정제 2 ~ 6 중량부, 탄산칼슘 200 ~ 800중량부를 포함하는 수지 조성물로 형성된 것을 특징으로 한다.Also, the reinforcing layer may include 100 parts by weight of polyvinyl chloride (PVC) having a degree of polymerization of 1000 to 1700, 20 to 50 parts by weight of phthalate plasticizer, 1 to 3 parts by weight of epoxidized soybean oil (E, S, O) 2 to 6 parts by weight of a stabilizer, and 200 to 800 parts by weight of calcium carbonate.

또한, 상기 인쇄층은, 중합도가 1000 ~ 1700인 폴리염화비닐(PVC) 100 중량부, 프탈레이트 가소제 20 ~ 50 중량부, 에폭시화 대두유(E,S,O) 1 ~ 3 중량부, 탄산칼슘 1 ~ 80 중량부, 백색안료인 이산화티탄 0.5 ~ 30 중량부, 바륨-아연 안정제 2 ~ 6 중량부 및 안료를 포함하는 수지 조성물로 형성된 것을 특징으로 한다.The printed layer may further contain 100 parts by weight of polyvinyl chloride (PVC) having a degree of polymerization of 1000 to 1700, 20 to 50 parts by weight of a phthalate plasticizer, 1 to 3 parts by weight of epoxidized soybean oil (E, S, O) To 80 parts by weight of a white pigment, 0.5 to 30 parts by weight of titanium dioxide, 2 to 6 parts by weight of a barium-zinc stabilizer, and a pigment.

또한, 상기 인쇄층은, 상기 보강층의 상면에 그라비아(gravure), 스크린 또는 전사 인쇄를 통해 무늬를 부여하는 것을 특징으로 한다.The printing layer is characterized in that the upper surface of the reinforcing layer is provided with a pattern through gravure, screen or transfer printing.

또한, 상기 투명층은, 중합도가 1000 ~ 1700인 폴리염화비닐(PVC) 100 중량부, 프탈레이트계 가소제 20 ~ 50 중량부, 에폭시화 대두유(E,S,O) 1 ~ 3 중량부, 바륨-아연 안정제 2 ~ 6 중량부를 포함하는 수지 조성물로 형성된 것을 특징으로 한다.The transparent layer may contain 100 parts by weight of polyvinyl chloride (PVC) having a degree of polymerization of 1000 to 1700, 20 to 50 parts by weight of a phthalate plasticizer, 1 to 3 parts by weight of epoxidized soybean oil (E, S, O) And 2 to 6 parts by weight of a stabilizer.

또한, 상기 투명층의 상면에 표면처리층; 을 더 포함할 수 있으며, 상기 표면처리층은, 우레탄 아크릴레이트계 UV 경화성 조성물을 도포하여 형성된 것을 특징으로 한다.
A surface treatment layer on the upper surface of the transparent layer; And the surface treatment layer is formed by applying a urethane acrylate-based UV curable composition.

또한, 상기 베이스층 하부에는 밸런스층; 을 더 포함할 수 있으며, 상기 밸런스층은, 크래프트 종이(Kraft paper)에 페놀(Phenol)수지로 함침한 것을 특징으로 한다.
A balance layer is formed under the base layer. And the balance layer is characterized in that the Kraft paper is impregnated with phenol resin.

이상에서 설명한 바와 같은 본 발명의 PVC 수지를 이용한 벽장재에 따르면 다음과 같은 효과가 있다.According to the closet material using the PVC resin of the present invention as described above, the following effects can be obtained.

HDF, MDF 또는 합판의 베이스층 상면에 접착되는 표면층을 PVC 수지로 구성하여 표면층 생산시 나무, 돌 등의 인쇄 패턴에 어울릴 수 있는 깊은 엠보를 자유롭게 구현하여 자연 질감을 향상시킬 수 있는 효과와 동시에 시공이 편리하고, 제작이 용이한 효과가 있다.
HDF, MDF or the surface layer bonded to the upper surface of the base layer of the MDF or plywood is made of PVC resin, and it is possible to improve the natural texture by freely embodying the deep emboss which can be matched with the print pattern of wood and stone in the production of the surface layer, This is convenient and has an easy manufacturing effect.

도 1은 종래의 일반적인 벽장재를 예시한 단면도.
도 2는 본 발명의 일 실시예에 따른 PVC 수지를 이용한 벽장재의 구조를 나타낸 단면도.
도 3은 본 발명의 다른 실시예에 따른 PVC 수지를 이용한 벽장재의 구조를 나타낸 단면도.1 is a cross-sectional view illustrating a conventional general closet material;
2 is a cross-sectional view illustrating the structure of a closet material using a PVC resin according to an embodiment of the present invention.
3 is a sectional view showing the structure of a closet material using a PVC resin according to another embodiment of the present invention.

이하 첨부한 도면을 참조하여 본 발명의 바람직한 실시예에 대한 구성 및 작용을 상세히 설명하면 다음과 같다. 다만 본 발명의 권리범위는 하기 실시예로 제한되는 것은 아닌 것으로 청구범위 기재에 따라 해석되어야 함은 통상의 기술자에게 자명한 사항이다.
DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS Hereinafter, preferred embodiments of the present invention will be described in detail with reference to the accompanying drawings. It is to be understood by those skilled in the art that the scope of the present invention is not limited to the following embodiments, but should be construed in accordance with the description of the claims.

도 2는 본 발명의 일 실시예에 따른 PVC 수지를 이용한 벽장재의 구조를 나타낸 단면도이고, 도 3은 본 발명의 다른 실시예에 따른 PVC 수지를 이용한 벽장재의 구조를 나타낸 단면도이다.
FIG. 2 is a cross-sectional view illustrating a structure of a closet material using a PVC resin according to an embodiment of the present invention, and FIG. 3 is a cross-sectional view illustrating a structure of a closet material using a PVC resin according to another embodiment of the present invention.

도 2에 도시된 바와 같이, 일 실시예에 따른 본 발명의 PVC 수지를 이용한 벽장재는, 고밀도 섬유판(HDF), 중밀도 섬유판(MDF) 또는 합판을 베이스층(100)으로 하고, 상기 베이스층(100)의 상면에 표면층(200)을 적층시켜 구성하되, 상기 표면층(200)은 보강층(210), 인쇄층(220), 투명층(230)을 포함하고 PVC 수지로 구성되며, 상기 투명층(230) 상면에 형성되는 표면처리층(300)을 더 포함하여 표면층(200)에 나무, 돌 등의 인쇄 패턴에 어울릴 수 있는 깊은 엠보를 자유롭게 구현하여 자연 질감을 향상시킬 수 있는 PVC 수지를 이용한 벽장재를 제공하는 것을 기술적 특징으로 한다.
2, the wall material using the PVC resin according to an embodiment of the present invention includes a base layer 100 made of a high density fiberboard (HDF), a medium density fiberboard (MDF), or a plywood, The surface layer 200 includes a reinforcing layer 210, a print layer 220 and a transparent layer 230 and is made of a PVC resin. The transparent layer 230 is formed of a transparent resin, And a surface treatment layer 300 formed on the upper surface of the top layer 200 so that a deep emboss which can be matched with a printed pattern such as wood and stone can be freely implemented on the surface layer 200, As a technical feature.

이러한 본 발명의 구성에 대해 구체적으로 설명하면 다음과 같다.
The configuration of the present invention will be described in detail as follows.

상기 베이스층(100)은 MDF, HDF 혹은 합판 중 하나로 구성되며, 이중 MDF와 HDF는 이들은 이미 알려진 바와 같이, 원목을 해섬하여 섬유상으로 만든 것에 접착제를 섞어 뭉쳐 편평하게 압축시켜 판상형태로 만든 것이다.The base layer 100 is composed of one of MDF, HDF or plywood. As is known, the MDF and the HDF are formed by laminating the wood and fusing the wood with the adhesive to form a flat plate.

MDF는 전 두께에 걸쳐 섬유분배가 균일하고 조직이 치밀하여 복잡한 기계가공작업을 면이나 측면의 파열 없이 수행할 수 있다. 또한, 면이 견고하고 평활하여 장식용 필름이나 베니어 등을 오버레이 하거나, 페인팅하는 데에도 매우 적합하며, 뛰어난 안정성과 기계 가공성, 높은 강도 때문에 서랍 측면이나 캐비넷 레일, 거울틀, 몰딩은 물론 본 발명과 같이 벽장재로 사용될 수 있다.MDF is able to perform complicated machining operations without rupture of side or side, because the fiber distribution is uniform over the entire thickness and the structure is dense. It is also suitable for overlaying or painting decorating film or veneer with a solid and smooth surface, and because of its excellent stability, machinability and high strength, it can be used for drawer sides, cabinet rails, It can be used as a closet material.

HDF는 밀도가 900kg/㎥ 이상의 고밀도 섬유판으로 강도면에서 MDF 보다 월등히 높아 합판 대체재로 널리 사용되고, 가구재 및 바닥재, 벽장재 등에 많이 사용된다.HDF is a high-density fiberboard with a density of 900kg / ㎥ or more, which is much higher than MDF in terms of strength, and is widely used as a substitute for plywood, and is widely used in furniture, flooring and closet materials.

이러한 상기 베이스층(100)의 두께는 3-15mm가 바람직하다.The thickness of the base layer 100 is preferably 3-15 mm.

상기 표면층(200)은 보강층(210), 인쇄층(220), 투명층(230)으로 이루어진다.The surface layer 200 includes a reinforcing layer 210, a printing layer 220, and a transparent layer 230.

상기 표면층(200)의 두께는 1-5mm가 바람직하다.The thickness of the surface layer 200 is preferably 1-5 mm.

이러한 상기 표면층(200)은 상기 베이스층(100)에 접착층(102)에 의해 접합된다.The surface layer 200 is bonded to the base layer 100 by an adhesive layer 102.

그 중, 상기 보강층(210), 인쇄층(220), 투명층(230) 등의 상기 표면층(200)을 구성하는 수지 조성물은 PVC 수지(Poly Vinyl Chloride)에, 프탈레이트계 가소제, 에폭시화 대두유, 바륨-아연 안정제, 탄산칼슘 중 하나 이상을 선택적으로 포함한다. The resin composition constituting the surface layer 200 such as the reinforcing layer 210, the print layer 220 and the transparent layer 230 may be prepared by adding a plasticizer such as phthalate plasticizer, epoxidized soybean oil, barium - Zinc stabilizer, and optionally one or more of calcium carbonate.

더욱 상세하게는, 상기 보강층은, 중합도가 1000 ~ 1700인 폴리염화비닐(PVC) 100 중량부, 프탈레이트계 가소제 20 ~ 50 중량부, 에폭시화 대두유(E,S,O) 1 ~ 3 중량부, 바륨-아연 안정제 2 ~ 6 중량부, 탄산칼슘 200 ~ 800 중량부를 포함하는 수지 조성물로 형성된 것을 특징으로 한다.More specifically, the reinforcing layer comprises 100 parts by weight of polyvinyl chloride (PVC) having a degree of polymerization of 1000 to 1700, 20 to 50 parts by weight of a phthalate plasticizer, 1 to 3 parts by weight of epoxidized soybean oil (E, S, O) 2 to 6 parts by weight of a barium-zinc stabilizer, and 200 to 800 parts by weight of calcium carbonate.

이러한 상기 보강층(210)의 두께는 0.5-3mm가 바람직하다. The thickness of the reinforcing layer 210 is preferably 0.5-3 mm.

상기 인쇄층(220)은, 중합도가 1000 ~ 1700인 폴리염화비닐(PVC) 100 중량부, 프탈레이트 가소제 20 ~ 50 중량부, 에폭시화 대두유(E,S,O) 1 ~ 3 중량부, 탄산칼슘 1 ~ 80 중량부, 백색안료인 이산화티탄 0.5 ~ 30 중량부, 바륨-아연 안정제 2 ~ 6 중량부 및 안료를 포함하는 수지 조성물로 형성되며, 상기 보강층(210)의 상면에 그라비아(gravure), 스크린 또는 전사 인쇄를 통해 무늬를 부여하여 형성된다. The printing layer 220 may include 100 parts by weight of polyvinyl chloride (PVC) having a degree of polymerization of 1000 to 1700, 20 to 50 parts by weight of phthalate plasticizer, 1 to 3 parts by weight of epoxidized soybean oil (E, S, O) 1 to 80 parts by weight of a white pigment, 0.5 to 30 parts by weight of titanium dioxide, 2 to 6 parts by weight of a barium-zinc stabilizer, and a pigment, and gravure, Screen or transfer printing.

이러한 상기 인쇄층(220)의 두께는 0.05-0.2mm가 바람직하다.The thickness of the print layer 220 is preferably 0.05-0.2 mm.

또한, 상기 투명층(230)은, 중합도가 1000 ~ 1700인 폴리염화비닐(PVC) 100 중량부, 프탈레이트계 가소제 20 ~ 50 중량부, 에폭시화 대두유(E,S,O) 1 ~ 3 중량부, 바륨-아연 안정제 2 ~ 6 중량부를 포함하는 수지 조성물로 형성된 것을 특징으로 한다.The transparent layer 230 may include 100 parts by weight of polyvinyl chloride (PVC) having a degree of polymerization of 1000 to 1700, 20 to 50 parts by weight of a phthalate plasticizer, 1 to 3 parts by weight of epoxidized soybean oil (E, S, O) And 2 to 6 parts by weight of a barium-zinc stabilizer.

이러한 상기 투명층(230)의 두께는 0.05-0.5mm가 바람직하다.The thickness of the transparent layer 230 is preferably 0.05-0.5 mm.

이와 같이 상기 표면층(200)이 PVC 수지로 형성됨으로써, 표면층(200)에 나무, 돌 등의 인쇄 패턴에 어울릴 수 있는 깊은 엠보를 자유롭게 구현하여 자연 질감을 향상시킬 수 있다.
Since the surface layer 200 is formed of PVC resin, the surface layer 200 can be embodied with a deep emboss which can be matched with a print pattern of wood, stone, etc., and thus the natural texture can be improved.

종래의 벽장재의 표면층으로 사용된 멜라민 수지를 함침한 시트는 두께가 얇고 경도가 높아 변형이 잘 일어나지 않기 때문에 깊은 엠보를 자유롭게 구현하기 어렵다. 하지만, PVC 수지로 표면층을 형성하게 되면 상대적으로 두께가 두껍고 경도가 낮아 깊은 엠보 형성이 가능해 자유롭게 인쇄 패턴을 형성할 수 있다.
The sheet impregnated with melamine resin used as the surface layer of the conventional closure material is thin and hard to be deformed because of its high hardness, so it is difficult to freely embody a deep emboss. However, when a surface layer is formed with PVC resin, the thickness is relatively thick and the hardness is low, so that deep embossing can be performed, and a print pattern can be freely formed.

상기 베이스층(100)과 표면층(200)을 접합하는 상기 접착층(102)은 PVAc, EVA 등의 수지가 사용될 수 있으며, 도포량은 50-200g/㎡, 바람직하게는 140-160g/㎡, 더욱 바람직하게는 150g/㎡이 바람직하다.
The adhesive layer 102 joining the base layer 100 and the surface layer 200 may be made of a resin such as PVAc or EVA. The coating amount is preferably 50-200 g / m 2, more preferably 140-160 g / 150 g / m < 2 > is preferable.

한편, 본 발명의 PVC 수지를 이용한 벽장재는 투명층(230) 상면에 표면처리층(300)을 더 포함할 수 있다. Meanwhile, the closure material using the PVC resin of the present invention may further include a surface treatment layer 300 on the upper surface of the transparent layer 230.

상기 표면처리층(300)은 스크래치 혹은 표면 오염을 방지하기 위한 것으로, 우레탄아크릴레이트계 UV 경화형 조성물이 사용되며, 여기에 실리카, 점토광물, 세라믹 등이 포함될 수 있다.The surface treatment layer 300 is used to prevent scratches or surface contamination. A urethane acrylate-based UV curable composition is used, and silica, clay minerals, ceramics and the like may be included in the surface treatment layer 300.

상기 표면처리층(300)의 두께는 0.01-0.1 mm가 바람직하다.
The thickness of the surface treatment layer 300 is preferably 0.01-0.1 mm.

또한, 도 3에 도시된 바와 같이 본 발명의 다른 실시예의 PVC 수지를 이용한 벽장재는 상기 베이스층(100) 하부에는 밸런스층(400)을 더 포함하여 형성할 수 있다.In addition, as shown in FIG. 3, the wall material using the PVC resin according to another embodiment of the present invention may further include a balance layer 400 below the base layer 100.

이러한 상기 밸런스층(400)은 크래프트 종이(Kraft paper)에 페놀(Phenol)수지로 함침하여 형성된다.The balance layer 400 is formed by impregnating kraft paper with phenol resin.

상기 밸런스층(400)의 두께는 0.5-5mm로 제작됨이 바람직하다.
The thickness of the balance layer 400 is preferably 0.5-5 mm.

물론, 필요에 따라서 최상부에 적층되는 상기 표면처리층(300)과 최하부에 적층되는 상기 밸런스층(400) 중 어느 하나 이상을 제외할 수 있다. Of course, at least one of the surface treatment layer 300 stacked on the uppermost layer and the balance layer 400 stacked on the lowermost layer may be excluded, if necessary.

하지만, 상기 표면층(200)의 보호를 위해 표면처리층(300)을 형성하고, 밸런스를 위해 상기 밸런스층(400)을 형성하는 것이 바람직하다.
However, in order to protect the surface layer 200, it is preferable to form the surface treatment layer 300 and to form the balance layer 400 for balance.

실시예 1Example 1

두께 8mm의 MDF로 베이스층(100)을 구성하고, 이 베이스층(100)의 상면에 PVAc계 접착제를 150g/㎡ 량으로 도포하여 접착층(102)을 형성한다.A base layer 100 is formed of MDF having a thickness of 8 mm and a PVAc adhesive is applied on the upper surface of the base layer 100 in an amount of 150 g / m 2 to form an adhesive layer 102.

상기 접착층(102)의 상면에 접합되는 보강층(210)은 중합도가 1000 ~ 1700인 폴리염화비닐(PVC) 100 중량부, 프탈레이트계 가소제 20 ~ 50 중량부, 에폭시화 대두유(E,S,O) 1 ~ 3 중량부, 바륨-아연 안정제 2 ~ 6 중량부, 탄산칼슘 200 ~ 800중량부가 혼합된 수지 조성물로, 두께는 1.2mm로 하여 1차, 2차에 걸쳐 배치된 압연 롤러에 공급하여 압착한다.The reinforcing layer 210 bonded to the upper surface of the adhesive layer 102 may include 100 parts by weight of polyvinyl chloride (PVC) having a degree of polymerization of 1000 to 1700, 20 to 50 parts by weight of a phthalate plasticizer, an epoxidized soybean oil (E, S, 2 to 6 parts by weight of a barium-zinc stabilizer, and 200 to 800 parts by weight of calcium carbonate, to a rolling roller having a thickness of 1.2 mm and arranged in a primary and secondary positions, do.

상기 보강층(210)의 상면의 인쇄층(220)은 중합도가 1000 ~ 1700인 폴리염화비닐(PVC) 100 중량부, 프탈레이트 가소제 20 ~ 50 중량부, 에폭시화 대두유(E,S,O) 1 ~ 3 중량부, 탄산칼슘 1 ~ 80 중량부, 백색안료인 이산화티탄 0.5 ~ 30 중량부, 바륨-아연 안정제 2 ~ 6 중량부 및 안료를 혼합한 수지 조성물로, 이 또한 압연롤러에 의해 공급된다.The printing layer 220 on the upper surface of the reinforcing layer 210 may include 100 parts by weight of polyvinyl chloride (PVC) having a polymerization degree of 1000 to 1700, 20 to 50 parts by weight of a phthalate plasticizer, 1 to 20 parts by weight of an epoxidized soybean oil (E, S, , 1 to 80 parts by weight of calcium carbonate, 0.5 to 30 parts by weight of titanium dioxide as a white pigment, 2 to 6 parts by weight of a barium-zinc stabilizer and a pigment, which are also supplied by a rolling roller.

상기 투명층(230)은 0.15mm 두께로 중합도가 1000 ~ 1700인 폴리염화비닐(PVC) 100 중량부, 프탈레이트계 가소제 20 ~ 50 중량부, 에폭시화 대두유(E,S,O) 1 ~ 3 중량부, 바륨-아연 안정제 2 ~ 6 중량부가 혼합된 수지 조성물로, 이 또한 압연롤러에 의해 공급된다.The transparent layer 230 is formed to have a thickness of 0.15 mm and has a polymerization degree of 1000 to 1700, 100 parts by weight of polyvinyl chloride (PVC), 20 to 50 parts by weight of a phthalate plasticizer, 1 to 3 parts by weight of epoxidized soybean oil (E, , And 2 to 6 parts by weight of a barium-zinc stabilizer, which is also supplied by a rolling roller.

상기 투명층(230)의 상면에 표면처리층(300)을 도포하되, 우레탄 아크릴레이즈계 UV 경화형 조성물을 도포한다.
The surface treatment layer 300 is applied to the upper surface of the transparent layer 230, and the urethane acrylate-based UV curable composition is applied.

실시예 2Example 2

실시예 1로 구성된 상기 베이스층(100)의 하부에 PVAc계 접착제를 150g/㎡ 량으로 도포하여 접착층(102)을 형성한다. A PVAc adhesive is applied to the lower part of the base layer 100 of Example 1 in an amount of 150 g / m 2 to form an adhesive layer 102.

상기 접착층(102)의 하면에 밸런스를 위한 밸런스층(400)은 크래프트 종이(Kraft paper)에 페놀(Phenol)수지로 함침하여 구성되며, 두께는 0.5mm로 하여 열압 프레스에 의해 공급하여 압착하여 벽장재를 완성하였다.
The balance layer 400 for balance on the lower surface of the adhesive layer 102 is made of Kraft paper impregnated with phenol resin and has a thickness of 0.5 mm. The balance layer 400 is supplied by a hot press, Finished ashes.

본 발명인 PVC 수지를 이용한 벽장재는 전술한 실시예에 국한하지 않고, 본 발명의 기술 사상이 허용되는 범위 내에서 다양하게 변형하여 실시할 수 있다.
The closure material using the PVC resin of the present invention is not limited to the above-described embodiments, but can be variously modified within the scope of the technical idea of the present invention.

100: 베이스층 102: 접착층 200: 표면층
210: 보강층 220: 인쇄층 230: 투명층
300: 표면처리층 400: 밸런스층100: base layer 102: adhesive layer 200: surface layer
210: reinforcing layer 220: printing layer 230: transparent layer
300: Surface treatment layer 400: Balance layer

Claims (11)

건축물의 실내 벽면에 시공되는 벽장재에 있어서,
베이스층;
상기 베이스층의 상면에 보강층, 인쇄층, 투명층으로 이루어진 표면층을 적층하여 구성하되,
상기 표면층은 PVC 수지로 구성된 것을 특징으로 하는 PVC 수지를 이용한 벽장재.In a closet material applied to an indoor wall surface of a building,
A base layer;
And a surface layer formed of a reinforcing layer, a printing layer, and a transparent layer on the upper surface of the base layer,
Wherein the surface layer is made of a PVC resin. 제 1항에 있어서, 상기 베이스층은 MDF, HDF 혹은 합판 중 하나인 것을 특징으로 하는 PVC 수지를 이용한 벽장재.The closet as claimed in claim 1, wherein the base layer is one of MDF, HDF or plywood. 청구항 1에 있어서,
상기 베이스층의 상면에는 접착제를 50 ~ 200g/㎡으로 도포하여 상기 보강층을 접착하기 위한 접착층이 형성되는 것을 특징으로 하는 PVC 수지를 이용한 벽장재.The method according to claim 1,
Wherein the adhesive layer is applied to the upper surface of the base layer in an amount of 50 to 200 g / m < 2 > to bond the reinforcing layer. 청구항 1에 있어서,
상기 보강층, 인쇄층, 투명층은,
PVC 수지에 프탈레이트계 가소제, 에폭시화 대두유, 바륨-아연 안정제 중 하나 이상을 선택적으로 포함하는 수지 조성물로 형성된 것을 특징으로 하는 PVC 수지를 이용한 벽장재.The method according to claim 1,
The reinforcing layer, the printing layer,
A closet material using a PVC resin, characterized in that the PVC resin is formed of a resin composition comprising at least one of a phthalate plasticizer, an epoxidized soybean oil, and a barium-zinc stabilizer. 청구항 4에 있어서,
상기 보강층은,
중합도가 1000 ~ 1700인 폴리염화비닐(PVC) 100 중량부, 프탈레이트계 가소제 20 ~ 50 중량부, 에폭시화 대두유(E,S,O) 1 ~ 3 중량부, 바륨-아연 안정제 2 ~ 6 중량부, 탄산칼슘 200 ~ 800중량부를 포함하는 수지 조성물로 형성된 것을 특징으로 하는 PVC 수지를 이용한 벽장재.The method of claim 4,
The reinforcing layer
100 parts by weight of a polyvinyl chloride (PVC) having a degree of polymerization of 1000 to 1700, 20 to 50 parts by weight of a phthalate plasticizer, 1 to 3 parts by weight of an epoxidized soybean oil (E, S, O), 2 to 6 parts by weight of a barium- , And calcium carbonate (200 to 800 parts by weight). 청구항 4에 있어서,
상기 인쇄층은,
중합도가 1000 ~ 1700인 폴리염화비닐(PVC) 100 중량부, 프탈레이트 가소제 20 ~ 50 중량부, 에폭시화 대두유(E,S,O) 1 ~ 3 중량부, 탄산칼슘 1 ~ 80 중량부, 백색안료인 이산화티탄 0.5 ~ 30 중량부, 바륨-아연 안정제 2 ~ 6 중량부 및 안료를 포함하는 수지 조성물로 형성된 것을 특징으로 하는 PVC 수지를 이용한 벽장재.The method of claim 4,
Wherein the print layer comprises:
100 parts by weight of a polyvinyl chloride (PVC) having a degree of polymerization of 1000 to 1700, 20 to 50 parts by weight of a phthalate plasticizer, 1 to 3 parts by weight of epoxidized soybean oil (E, S, O), 1 to 80 parts by weight of calcium carbonate, 0.5 to 30 parts by weight of titanium dioxide, 2 to 6 parts by weight of a barium-zinc stabilizer, and a pigment. 청구항 6에 있어서,
상기 인쇄층(600)은,
상기 보강층의 상면에 그라비아(gravure), 스크린 또는 전사 인쇄를 통해 무늬를 부여하는 것을 특징으로 하는 PVC 수지를 이용한 벽장재.The method of claim 6,
The printing layer (600)
Wherein the upper surface of the reinforcing layer is provided with a pattern by gravure, screen, or transfer printing. 청구항 4에 있어서,
상기 투명층은,
중합도가 1000 ~ 1700인 폴리염화비닐(PVC) 100 중량부, 프탈레이트계 가소제 20 ~ 50 중량부, 에폭시화 대두유(E,S,O) 1 ~ 3 중량부, 바륨-아연 안정제 2 ~ 6 중량부를 포함하는 수지 조성물로 형성된 것을 특징으로 하는 PVC 수지를 이용한 벽장재.The method of claim 4,
The transparent layer
20 to 50 parts by weight of a phthalate plasticizer, 1 to 3 parts by weight of an epoxidized soybean oil (E, S, O) and 2 to 6 parts by weight of a barium-zinc stabilizer are added to 100 parts by weight of a polyvinyl chloride Wherein the resin composition comprises a polyvinyl chloride resin. 청구항 8에 있어서,
상기 투명층의 상면에 표면처리층; 을 더 포함하되,
상기 표면처리층은, 우레탄 아크릴레이트계 UV 경화성 조성물이 도포된 것을 특징으로 하는 PVC 수지를 이용한 벽장재.The method of claim 8,
A surface treatment layer on an upper surface of the transparent layer; , ≪ / RTI >
Wherein the surface treatment layer is coated with a urethane acrylate UV curable composition. 청구항 1에 있어서,
상기 베이스층 하부에는 밸런스를 위한 밸런스층; 을 더 포함하되,
상기 밸런스층은,
크래프트 종이(Kraft paper)를 페놀(Phenol)수지로 함침한 것을 특징으로 하는 PVC 수지를 이용한 벽장재.The method according to claim 1,
A balance layer for balancing is formed below the base layer; , ≪ / RTI >
Wherein the balance layer comprises:
Characterized in that the kraft paper is impregnated with phenol resin. 청구항 10에 있어서,
상기 베이스층과 밸런스층 사이에는 접착층이 형성된 것을 특징으로 하는 PVC 수지를 이용한 벽장재.The method of claim 10,
And an adhesive layer is formed between the base layer and the balance layer.
KR1020140050628A 2014-04-28 2014-04-28 Wall panel using polyvinylchloride resin KR20150124159A (en)