KR20140008777A - Chaff and clay containing charcoal and its manufacturing method - Google Patents

Chaff and clay containing charcoal and its manufacturing method Download PDF

Info

Publication number
KR20140008777A
KR20140008777A KR20120075846A KR20120075846A KR20140008777A KR 20140008777 A KR20140008777 A KR 20140008777A KR 20120075846 A KR20120075846 A KR 20120075846A KR 20120075846 A KR20120075846 A KR 20120075846A KR 20140008777 A KR20140008777 A KR 20140008777A
Authority
KR
South Korea
Prior art keywords
chaff
charcoal
mixing
mixture
ocher
Prior art date
Application number
KR20120075846A
Other languages
Korean (ko)
Inventor
윤석남
Original Assignee
윤석남
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 윤석남 filed Critical 윤석남
Priority to KR20120075846A priority Critical patent/KR20140008777A/en
Publication of KR20140008777A publication Critical patent/KR20140008777A/en

Abstract

Disclosed is a manufacturing method of a chaff and red clay containing charcoal which comprises: a step of grinding a pure charcoal and red clay (S1); a step of mixing and stirring a ground pure charcoal with chaff (S2); a step of firstly mixing the mixed and stirred mixture of pure charcoal and chaff with corn powder paste (S3); a step of maturing in order to infiltrate the corn powder paste in the mixture of pure charcoal and chaff (S4); a step of secondly mixing the mixture of pure charcoal, chaff and corn powder paste with the ground red clay (S5); a step of kneading the mixture of pure charcoal, chaff, corn powder paste and red clay with water (S6); a step of performing a compression molding with the kneaded mixture in the mold (S7); a step of firstly drying the compression molded product in the shade (S8); a step of secondly drying the product in the shade (S9). [Reference numerals] (S1) Step of grinding; (S2) Step of mixing and stirring; (S3) Step of firstly mixing; (S4) Step of maturing; (S5) Step of secondly mixing; (S6) Step of kneading; (S7) Step of performing a compression molding; (S8) First drying process; (S9) Second coating process

Description

왕겨와 황토를 함유한 숯 및 그 제조방법{CHAFF AND CLAY CONTAINING CHARCOAL AND ITS MANUFACTURING METHOD}Charcoal containing chaff and ocher and its manufacturing method {CHAFF AND CLAY CONTAINING CHARCOAL AND ITS MANUFACTURING METHOD}

본 발명은 로스터에 적용되는 왕겨와 황토를 함유한 숯에 관한 것으로, 왕겨, 참숯가루, 황토가루, 옥수수 가루 풀을 일정한 배합 비율로 혼합한 후 압착 성형한 왕겨와 황토를 함유한 숯 및 그 제조 방법에 관한 것이다.The present invention relates to a charcoal containing the chaff and ocher applied to the roaster, and after the chaff, charcoal flour, ocher powder, corn flour paste mixed in a constant mixing ratio, the charcoal containing the chaff and ocher char and press It is about a method.

예로부터 농업을 중요시하는 우리나라는 쌀을 주식으로 생활하여 왔으며, 벼의 도정시 발생 되는 부산물인 왕겨는 농촌에서 연료 및 농업용 퇴비로 사용되어 왔으나, 최근에는 연료 문화 및 화학 비료의 발달로 이의 사용이 매우 미미한 실정이다. 또한 왕겨는 연료 및 농업용 퇴비로의 사용 외에 축사의 방습제, 용광로 응고방지제, 연료용 왕겨탄 등 특수한 목적에 사용되고 있으나 그 사용량이 매우 적어 년간 110 만톤 씩 발생 되는 왕겨의 대부분은 그대로 버려지거나 방치되어 있었다.Since ancient times, agriculture has focused on rice as a staple food, and chaff, a by-product of rice planting, has been used as fuel and agricultural compost in rural areas. It is very slight. In addition to the use of fuel and agricultural compost furnaces, chaff is used for special purposes such as barn desiccant, blast furnace anticoagulant, and fuel chaff, but most of the chaff, which is generated at 1.1 million tons per year, has been discarded or left unattended. .

이러한 왕겨를 이용한 왕겨숯은 탄화하는 과정에서 수많은 미세한 구멍을 만드는데 그 표면적은 왕겨숯 1g 당 600m 이상의 면적이 되고, 왕겨 자체의 형태로 탄화되기 그 어떤 종류의 숯보다 통기성 및 보습성이 뛰어나다.Chaff charcoal using such chaff makes a number of fine holes during carbonization, its surface area is over 600m per 1g of chaff charcoal, and it is more breathable and moisturizing than any kind of charcoal to be carbonized in the form of chaff itself.

본 발명은 이러한 왕겨의 특징을 이용하여 제1차 연소 후 제2차 연소시에 그 통기성 및 보습성을 이용하여 발열량도 함께 증대시키기 위한 것이다.The present invention is to increase the amount of heat generated by using the breathability and moisture retention at the time of the second combustion after the first combustion by using the characteristics of the chaff.

또한, 왕겨숯은 원적외선과 음이온을 발산하며, 유해성분이 전혀 없는 230 여종의 각종 미네랄과 산소가 다량함유되어 있는바, 탄화 과정에서 강한 흡착력을 발휘하는데 이는 해로운 바이러스나 독소 등을 선택적으로 흡수하는 기능을 한다.In addition, chaff charcoal emits far-infrared rays and anions, and contains 230 kinds of various minerals and oxygen which have no harmful components, and shows strong adsorptive power during carbonization, which selectively absorbs harmful viruses and toxins. Do it.

황토 역시 동식물의 성장에 꼭 필요한 원적외선을 다량 방사 하며, 일명 황토를 살아있는 생명체라 부른다. Ocher also emits a large amount of far-infrared rays necessary for the growth of animals and plants. So-called ocher is called living organisms.

황토는 표면이 넓은 벌집 구조로 수많은 공간이 복층 구조를 이루고 있으며, 이 스펀지 같은 구멍 안에는 원적외선이 다량흡수, 저장되어 있어 열을 받으면 발산하여 다른 물체의 분자활동을 자극한다. 즉 황토는 유수한 세월동안 태양에너지를 흡수하고, 규소성 광물로서 쉽게 말해 태양에너지 저장고라고 할 수 있다.Ocher is a honeycomb structure with a large surface, and a large number of spaces have a multi-layered structure. In this sponge-like hole, far-infrared rays are absorbed and stored in a large amount, and radiate when heated to stimulate molecular activity of other objects. In other words, loess absorbs solar energy for many years, and can be called a solar energy reservoir as a silicon mineral.

황토의 가장 근본적인 효능은 황토에서 파장되는 원적외선이다. 원적외선은 세포의 생리작용을 활발히 하고, 열 에너지를 발생시켜 유해 물질을 방출하는 광전효과가 있으며, 유기체의 심층조직 속 4~5cm 까지 침투하며, 유기체에 흡수될 때 일반 열보다 80배나 깊숙이 피하 심층으로 스며든다. 그리고 유기체 내 세포를 구성하는 수분과 단백질 분자에 방사되어 세포를 1분에 2000번씩 미세하게 흔들어 주는 진동을 통해 세포 조직을 활성화시켜 생명 활동을 보다 왕성하게 해 준다.The most fundamental effect of ocher is the far-infrared wavelengths of the ocher. Far-infrared rays have a photoelectric effect that activates the physiology of cells, generates heat energy, and releases harmful substances, penetrates 4 ~ 5cm into the deep tissue of the organism, and is 80 times deeper than normal heat when absorbed by the organism. Soak into And it radiates to the water and protein molecules that make up the cells in the organism, and vibrates the cells finely 2000 times a minute, activating the cell tissues, thereby making life more active.

이로 인해 조리를 할 경우 방사열에 의해 내부의 육즙을 그대로 간직하면서 익혀주므로 그 맛이 각별하고, 고유의 맛을 유지할 수가 있다.Because of this, when cooking, the heat is retained by the radiant heat while being cooked as it is, so the taste is exceptional and the original taste can be maintained.

그러나, 이러한 황토의 경우 압착, 소성 등을 통해 연료로 이용하려는 노력이 있었으나, 그 제조 단가가 높고, 소성을 할 경우 황토 내부의 일정량의 원적외선을 방사 함으로써 근본적인 원적외선 효능을 감소시키는 문제가 있었다.However, in the case of such ocher, there have been efforts to use it as fuel through compression, sintering, etc., but the manufacturing cost is high, and when firing, there is a problem of reducing the fundamental far-infrared efficacy by emitting a certain amount of far-infrared rays inside the loess.

또한, 종래에는 이러한 다양한 효과를 가지는 왕겨와 황토가루 및 참숯가루를 어느 정도의 비율로 혼합해야 황토가 왕겨 및 참숯가루에 고루 배합되는지 알 수 없었으며, 위와 같은 재료로 혼합된 로스터용 숯도 전무 한 상태였다.In addition, in the past, it was not possible to know how much the ocher is evenly blended with the chaff and the charcoal powder in the ratio of chaff and ocher powder and true charcoal powder having various effects, the roasting charcoal mixed with the above materials It was a condition.

본 발명은 상기와 같은 왕겨와 황토를 참숯가루와 옥수수 가루 풀을 이용하여 적절한 배합비로 혼합하여 친환경적이고 고기의 잡내음을 없앨 수 있는 왕겨와 황토를 함유한 숯 및 그의 제조방법에 관한 것이다.The present invention relates to chaff and ocher-containing charcoal and its manufacturing method that can be mixed with the chaff and ocher in the appropriate mixing ratio by using a charcoal powder and corn flour grass to eliminate the noise of meat.

특히, 본 발명의 배합비율로 왕겨와 참숯가루를 혼합한 후 황토가루를 함께 배합 교반 하는 경우 황토가 왕겨 및 참숯가루에 고루 배합되는 효과를 가진다.In particular, when the mixture ratio of chaff and sesame charcoal mixture of the present invention and then mixing and stirring ocher powder together, the ocher has the effect of being evenly mixed with chaff and charcoal powder.

또한, 기존의 황토로 이루어진 숯의 경우 1차적으로 손님에게 제공하여 발열시킨 후 다시 2차적으로 사용하는 경우 그 발열량이 충분치 않는 문제점이 있었으며, 또한 기존에는 황토와 물을 혼합하여 성형하였으나, 이러한 경우 황토숯의 발열량이 감소 되며, 황토 자체가 잘 뭉치지 않는 문제점이 있었다.In addition, in the case of the charcoal made of the conventional loess, the first generation provided to the customer to generate heat and then use the secondary again, the amount of heat generated was not enough, and in the past, the mixture was formed by mixing the loess and water, The calorific value of the ocher charcoal is reduced, there was a problem that the loess itself is not agglomerated well.

(선행기술 1) 한국등록특허공보 제10-0842353호(2008.06.24)(Prior art 1) Korean Patent Publication No. 10-0842353 (2008.06.24) (선행기술 2) 한국등록특허공보 제10-0996853호(2010.11.22)(Prior art 2) Korean Patent Publication No. 10-0996853 (2010.11.22)

이에 본 발명은 상기한 바와 같은 종래의 제반 문제점을 해소하기 위해 창안된 것으로, 그 목적은 왕겨, 참숯가루, 황토가루, 옥수수 가루 풀의 비율이 어느 정도 되어야 황토가 골고루 분배되고, 다 타버린 후에도 재의 날림이나 떨어짐이 없이 처음 성형한 그대로의 형태를 유지하며, 사용시간이 길고 간편한 로스터용 왕겨와 황토를 함유한 숯 및 그 제조방법을 제공함에 있다.Therefore, the present invention was devised to solve the conventional problems as described above, and its purpose is that the ratio of chaff, charcoal powder, ocher powder, and corn flour grass should be somewhat to some extent, even after the ocher is evenly distributed and burned out. It maintains the shape as it was first formed without blowing or falling ash, and provides a charcoal containing a long time and simple roaster chaff and ocher and its manufacturing method.

상기와 같은 목적을 달성하기 위한 본 발명의 로스터용 왕겨와 황토를 함유한 숯의 제조방법은, 참숯 및 황토를 분쇄하는 단계; 분쇄된 참숯을 왕겨와 배합 교반 하는 단계; 상기 배합 교반된 왕겨와 참숯 혼합물에 옥수수 가루 풀을 1차적으로 혼합하는 단계; 상기 옥수수 가루 풀이 왕겨와 참숯 혼합물에 스며들기 위해 숙성하는 단계; 상기 옥수수 가루 풀에 의해 혼합된 왕겨와 참숯 혼합물에 분쇄된 황토를 2차적으로 혼합하는 단계; 상기 혼합된 왕겨, 참숯, 황토, 옥수수 가루 풀을 물과 반죽하는 단계; 상기 반죽 된 혼합물을 성형 틀에서 압축 성형하는 단계; 상기 압축 성형 된 제품을 그늘에서 1차적으로 건조하는 단계; 상기 제품을 그늘에서 2차로 건조하는 단계; 를 포함하는 것을 특징으로 한다.Roasted rice husk and loess of the charcoal of the present invention for achieving the above object is a step of grinding the charcoal and loess; Stirring the ground charcoal with chaff; Primarily mixing corn flour paste with the blended stirred chaff and charcoal mixture; Aging the corn flour paste to soak into the chaff and charcoal mixture; Secondarily mixing the chaff mixed with the corn flour paste and the ground ocher ground to a charcoal mixture; Kneading the mixed chaff, charcoal, ocher, and corn flour paste with water; Compression molding the kneaded mixture in a mold; Primarily drying the compression molded product in the shade; Second drying the product in the shade; And a control unit.

상기 분쇄된 참숯을 왕겨와 배합 교반 하는 단계에 있어서, 상기 왕겨도 분쇄한 후 상기 참숯과 배합 교반 하는 것을 특징으로 하며, 상기 압축 성형 된 제품을 그늘에서 1차적으로 건조하는 단계를 거친 후 상기 황토에 포함된 이물질을 제거하기 위해 상기 제품을 3분 정도 가열하는 단계를 포함하는 것을 특징으로 한다.In the step of mixing and stirring the crushed sesame charcoal, chaff is also characterized in that the mixture and stirring with the charcoal after grinding the chaff, and after the step of drying the compression-molded product in the shade first the ocher It characterized in that it comprises the step of heating the product for about 3 minutes to remove the foreign matter contained in.

상기와 같은 제조방법에 의해 생산되는 왕겨와 황토를 함유한 숯은,Charcoal containing chaff and ocher produced by the manufacturing method as described above,

참숯 및 황토를 분쇄하는 단계; 분쇄된 참숯을 왕겨와 배합 교반 하는 단계; 상기 배합 교반된 왕겨와 참숯 혼합물에 옥수수 가루 풀을 1차적으로 혼합하는 단계; 상기 옥수수 가루 풀이 왕겨와 참숯 혼합물에 스며들기 위해 숙성하는 단계; 상기 옥수수 가루 풀에 의해 혼합된 왕겨와 참숯 혼합물에 분쇄된 황토를 2차적으로 혼합하는 단계; 상기 혼합된 왕겨, 참숯, 황토, 옥수수 가루 풀을 물과 반죽하는 단계; 상기 반죽 된 혼합물을 성형 틀에서 압축 성형하는 단계; 상기 압축 성형 된 제품을 그늘에서 1차적으로 건조하는 단계;상기 제품을 그늘에서 2차로 건조하는 단계; 를 거친 숯 본체의 직경이 25 ~ 35 mm 인 구 형상인 것을 특징으로 한다.Grinding the charcoal and loess; Stirring the ground charcoal with chaff; Primarily mixing corn flour paste with the blended stirred chaff and charcoal mixture; Aging the corn flour paste to soak into the chaff and charcoal mixture; Secondarily mixing the chaff mixed with the corn flour paste and the ground ocher ground to a charcoal mixture; Kneading the mixed chaff, charcoal, ocher, and corn flour paste with water; Compression molding the kneaded mixture in a mold; First drying the compression molded product in the shade; second drying the product in the shade; The charcoal body is characterized in that the sphere shape of 25 ~ 35 mm in diameter.

상기 분쇄된 참숯을 왕겨와 배합 교반하는 단계에 있어서, 상기 왕겨도 분쇄한 후 상기 참숯과 배합 교반 하는 과정을 포함하되, 상기 숯의 형상이 두께가 10 mm 이고, 직경은 50~60 mm 로 성형 되며 다수개의 구명이 상하로 관통된 납작한 판상으로 구성된 것을 특징으로 한다.In the step of mixing and stirring the crushed sesame charcoal, chaff also comprises a step of grinding and mixing with the charcoal after the chaff, the shape of the char is 10 mm thick, 50 ~ 60 mm in diameter And it is characterized by consisting of a flat plate through which a plurality of lifesaving penetrated up and down.

본 발명의 왕겨와 황토를 함유한 숯의 제조방법에 있어서, 옥수수전분이 더 혼합되어 숯이 제조되며, 이를 위해 참숯 및 황토를 분쇄하는 단계; 분쇄된 참숯을 분쇄된 왕겨와 배합 교반 하는 단계; 상기 배합 교반된 왕겨와 참숯 혼합물에 옥수수 전분을 1차적으로 혼합하는 단계; 상기 옥수수 전분이 혼합된 왕겨와 참숯 혼합물에 분쇄된 황토를 2차적으로 혼합하는 단계; 상기 2차적으로 혼합하는 단계를 거친 혼합물을 압출기에 넣어 인출하는 단계; 를 포함하는 것을 특징으로 한다.In the method of producing charcoal containing chaff and ocher of the present invention, the corn starch is further mixed to produce a charcoal, pulverizing the charcoal and loess for this; Mixing the ground charcoal with the ground chaff and stirring; Primarily mixing corn starch in the blended stirred chaff and charcoal mixture; Secondarily mixing the ground chaff mixed with the corn starch and ground ocher in a charcoal mixture; Putting the mixture passed through the secondary mixing into an extruder and withdrawing; And a control unit.

또한 상기의 방법으로 생산된 숯은 참숯 및 황토를 분쇄하는 단계; 분쇄된 참숯을 분쇄된 왕겨와 배합 교반 하는 단계; 상기 배합 교반된 왕겨와 참숯 혼합물에 옥수수 전분을 1차적으로 혼합하는 단계; 상기 옥수수 전분이 혼합된 왕겨와 참숯 혼합물에 분쇄된 황토를 2차적으로 혼합하는 단계; 상기 2차적으로 혼합하는 단계를 거친 혼합물을 압출기에 넣어 인출하는 단계; 를 거친 숯 본체가 스크류 형상인 것을 특징으로 한다.In addition, the char produced by the above method is a step of grinding the charcoal and loess; Mixing the ground charcoal with the ground chaff and stirring; Primarily mixing corn starch in the blended stirred chaff and charcoal mixture; Secondarily mixing the ground chaff mixed with the corn starch and ground ocher in a charcoal mixture; Putting the mixture passed through the secondary mixing into an extruder and withdrawing; The charcoal body is characterized in that the screw shape.

본 발명인 로스터용 왕겨와 황토를 함유한 숯 및 그 제조방법을 이용하면 아래와 같은 다양한 이점이 있다.Using the present invention roaster chaff and loess char and its manufacturing method has the following various advantages.

첫째, 로스터에서 왕겨와 황토를 함유한 숯을 넣어 과열하는 경우 왕겨와 숯가루가 타면서 왕겨향이 고기의 잡내음을 없애며, 보습효과의 이점이 있다.First, when the charcoal containing the chaff and ocher in the roaster is overheated, the chaff flavor eliminates the noise of the meat as the chaff and charcoal burns, and there is a moisturizing effect.

둘째, 황토가루가 혼합된바 황토가루가 열을 받아 다량의 원적외선을 방출하면서 왕겨 및 숯가루 재의 분진을 잡아주는 이점이 있다.Second, the ocher powder is mixed with the ocher powder is heated to release a large amount of far infrared rays has the advantage of catching the dust of chaff and charcoal ash.

셋째, 타고난 재는 형태가 부서지지 않으며, 본 발명의 왕겨와 황토를 함유한 숯은 친환경적인 부수적인 이점도 있다.Third, the natural ash is not broken in shape, charcoal containing the chaff and ocher of the present invention is also an environmentally friendly side benefit.

넷째, 발열량이 우수하고 또한 제품이 경량이므로 운반 등이 용이하고, 연소후에 발생 되는 재는 퇴비로 사용할 수 있는 이점이 있다.Fourth, since the calorific value is excellent and the product is light, it is easy to transport and the like, the ash generated after combustion has the advantage that can be used as compost.

다섯째, 왕겨가 함유된바 제1차적으로 본 발명의 숯을 사용한 뒤 다시 2차적으로 사용하는 경우 왕겨가 타고난 자리에 공극이 형성되어 이 공극에 의해 산소 공급이 원활하게 유지되어 발열량이 기존보다 높은 이점이 있다.Fifth, when the chaff is contained, the first use of the charcoal of the present invention after the second use again, the pores are formed in the place where the chaff is born, the oxygen supply is smoothly maintained by the pores, so that the calorific value is higher than before. There is an advantage.

여섯째, 혼합된 왕겨, 참숯, 황토에 옥수수가루풀을 혼합하여 물과 반죽하는 단계를 통해 혼합물이 잘 뭉치는 효과 외에 이 숯을 이용하여 사용하는 경우 짧은 시간에 발열 되고, 그 발열량도 높다는 이점이 있다.Sixth, in addition to the effect of agglomeration of the mixture by mixing the chaff, sesame charcoal, and corn flour with water and kneading the mixture, the charcoal is heated in a short time and the calorific value is high. have.

도 1 및 도 2는 본 발명의 왕겨와 황토를 함유한 숯의 제조 방법에 대한 단계별 흐름도.
도 3a, 도 3b 및 도 4는 본 발명의 제조 방법에 의해 생산되는 왕겨와 황토를 함유한 숯의 외형 및 그 단면을 나타내는 도면.
도 5는 본 발명의 옥수수 전분이 혼합된 숯의 제조 방법에 대한 단계별 흐름도.
도 6a 및 도 6b는 본 발명의 옥수수 전분이 혼합된 숯의 외형을 나타내는 도면.1 and 2 are a step-by-step flowchart of the method for producing charcoal containing chaff and ocher of the present invention.
Figures 3a, 3b and 4 is a view showing the appearance and cross-section of the charcoal containing chaff and ocher produced by the production method of the present invention.
5 is a step-by-step flowchart of the method for producing charcoal mixed with corn starch of the present invention.
6a and 6b is a view showing the appearance of the char mixed with the corn starch of the present invention.

이하에서는 첨부된 도면을 참조하여 본 발명의 바람직한 실시 예에 따른 왕겨와 황토를 함유한 숯 및 그 제조방법에 대하여 설명한다.Hereinafter, with reference to the accompanying drawings will be described with respect to charcoal containing chaff and ocher according to a preferred embodiment of the present invention and a method of manufacturing the same.

다만, 왕겨와 황토를 함유한 숯은 이하 '황겨탄' 이라 명칭하여 설명한다.However, the charcoal containing chaff and loess will be described as 'hwang charcoal'.

도 1은, 본 발명의 황겨탄의 제조 방법에 대한 단계별 흐름도로,1 is a step-by-step flow chart for the production method of the sulfur bran coal of the present invention,

본 발명인 황겨탄의 제조 방법은, 참숯 및 황토를 분쇄하는 단계(S1); 분쇄된 참숯을 왕겨와 배합 교반 하는 단계(S2); 상기 배합 교반된 왕겨와 참숯 혼합물에 옥수수 가루 풀을 1차적으로 혼합하는 단계(S3); 상기 옥수수 가루 풀이 왕겨와 참숯 혼합물에 스며들기 위해 숙성하는 단계(S4); 상기 옥수수 가루 풀에 의해 혼합된 왕겨와 참숯 혼합물에 분쇄된 황토를 2차적으로 혼합하는 단계(S5); 상기 혼합된 왕겨, 참숯, 황토, 옥수수 가루 풀을 물과 반죽하는 단계(S6); 상기 반죽 된 혼합물을 성형 틀에서 압축 성형하는 단계(S7); 상기 압축 성형 된 제품을 그늘에서 1차적으로 건조하는 단계(S8); 상기 제품을 그늘에서 2차로 건조하는 단계(S9); 를 포함하는 것을 특징으로 한다.The method of producing a yellow bran charcoal of the present invention, the step of grinding the charcoal and loess (S1); Mixing and stirring the ground charcoal with chaff (S2); First mixing the corn flour paste in the blended stirred chaff and charcoal mixture (S3); The corn flour paste is aged to soak into the chaff and charcoal mixture (S4); Secondly mixing the chaff and chaff mixed with the charcoal mixture by the corn flour paste and crushed ocher; Kneading the mixed chaff, sesame charcoal, ocher, and corn flour paste with water (S6); Compression molding the kneaded mixture in a mold (S7); First drying the compression-molded product in a shade (S8); Drying the product secondaryly in the shade (S9); And a control unit.

본 발명에 사용되는 왕겨는 이하 설명하는 것처럼 분쇄하여 사용하기도 하지만, 왕겨 자체를 상기 분쇄된 참숯에 배합 교반 하는 것을 특징으로 한다.The chaff used in the present invention may be ground and used as described below, but the chaff itself is characterized by mixing and stirring the ground charcoal.

왕겨 자체가 참숯 및 황토와 교반, 혼합하여 숯이 되는 경우, 이 숯을 이용하여 음식점에서 고기를 굽는 경우 왕겨 자체의 특유한 향이 고기에 흡수되어 손님들이 고기를 씹는 경우 그 미감이 향상되며, 왕겨의 효능으로 고기의 잡내음도 잡을 수 있는 장점이 있다.When the chaff itself is stirred and mixed with charcoal and ocher to be charcoal, when the meat is grilled in a restaurant using the charcoal, the unique aroma of the chaff itself is absorbed by the meat and the taste is improved when customers chew the meat. Efficacy has the advantage of catching the catch of meat.

더군나나, 왕겨가 포함된 본 발명은 그 탄화하는 과정에서 왕겨 자체의 부피로 인해 수많은 미세한 구멍이 형성되며, 그 결과 구명에 의해 숯의 표면적이 증가하여 발열량도 역시 함께 증대되며, 왕겨 자체의 형태로 탄화되므로 그 어떤 종류의 숯보다 통기성 및 보습력이 우수한 효과가 있다.Furthermore, in the present invention, which includes chaff, in the carbonization process, numerous fine pores are formed due to the volume of the chaff itself, and as a result, the surface area of char is increased by lifesaving, so that the calorific value is also increased, and the shape of the chaff itself. As it is carbonized, it has better breathability and moisturizing power than any kind of charcoal.

도 3a는 이러한 왕겨가 포함된 본 발명의 외형을 나타내며, 도 3b는 본 발명의 황겨탄을 1차적으로 연소시킨 후 그 내부를 절단한 단면이다.Figure 3a shows the appearance of the present invention that includes such chaff, Figure 3b is a cross-sectional view of the interior after cutting the yellow charcoal of the present invention primarily.

도 3b에 도시된 바와 같이 왕겨 자체의 부피로 인해 본 발명의 '황겨탄'은 그 내부에 수많은 공극이 생기며, 이로 인해 2차 연소시 기존의 숯보다 공극의 표면적과 공간이 형성되어 발열량이 우수해지며, 그 통기성도 우수해지는 효과가 있다.As shown in FIG. 3b, due to the volume of the chaff itself, the 'hwangchatan charcoal' of the present invention has a large number of pores therein, so that the surface area and space of the pores are formed than the existing charcoal at the time of secondary combustion, thereby generating excellent heat generation. It becomes effective, and its breathability is also excellent.

본 발명에 사용되는 왕겨는 분쇄기로 분쇄하여 미세입자의 왕겨분말을 얻어 '황겨탄' 생산이 가능하다.The chaff used in the present invention is pulverized with a grinder to obtain a fine grain chaff powder can be produced 'sulfur charcoal'.

상기의 왕겨는 농촌의 정미소에서 벼를 정미하는 과정에서 대량으로 발생 되는 왕겨를 이용하는 것으로서, 이를 그대로 사용하는 경우에는 부피가 많으며, 입자간의 접착력이 떨어져서 고체상태로 접착할 수 없고, 또한 완전 연소를 도모할 수 없기 때문에 이를 미세한 입자로 가공할 필요성이 있는 것으로, 상기 왕겨를 미세입자로 분쇄하기 위해서는 공지의 분쇄기를 사용하여 이를 0.4 ~ 0.7 mm 의 망으로 배출시켜 미세분말로 만들게 된다.The chaff is a chaff that is generated in a large amount in the process of refining rice in a rural rice mill, and when it is used as it is, it is bulky, and the adhesion between particles is poor, so that it cannot be adhered to a solid state, and also complete combustion is performed. Since it is impossible to plan it, there is a need to process it into fine particles. In order to grind the chaff into fine particles, it is made into fine powder by discharging it into a mesh of 0.4 to 0.7 mm using a known grinder.

물론, 본원발명은 이러한 접착상태의 문제점을 해결하기 위해 물과 함께 옥수수풀을 그 접착제로 이용하고 있다.Of course, the present invention uses corn grass as an adhesive with water to solve this problem of adhesion.

상기의 왕겨를 미세한 입자로 분쇄하는 이유는 부피를 현저히 줄여 밀도를 높이고, 입자 간의 접착력을 증대시켜 고체화할 수 있으며, 최적의 연소 조건으로 완전연소를 도모하여 최대의 열량을 얻기 위함이다. The reason for crushing the rice husk into fine particles is to significantly reduce the volume, increase the density, increase the adhesion between the particles to solidify, and to obtain the maximum amount of heat by achieving complete combustion under optimum combustion conditions.

또한 황토분말은 자연환경에서 채취한 양질의 황토를 물이 충만 된 탱크에 투입하여 물에 섞어 풀면 석분은 아래로 가라 않고 물에 풀어진 황토분말이 높이 1.5 m 의 침전지로 보내어 72시간 정도 침전시켜 석분을 제거한 황토분말을 얻는다.In addition, ocher powder is put in a tank filled with water, and the ocher powder is collected from the natural environment, and mixed with water. The stone powder does not go down. The ocher powder released in water is sent to a 1.5 m high sedimentation basin and settled for 72 hours. To remove the ocher powder.

황토는 일정한 접착력을 가지고 있으므로, 왕겨 입자 간의 접착이 가능하여 연료를 고체화하기 위하여 필수 불가결한 요소이며, 연소시 서서히 연소 되므로 화력조절이 용이하고, 왕겨와 접착되어 성형 되므로 풍량에 의한 재의 비산을 방지할 수 있으며, 연소된 재를 퇴비로 활용하기 위하여는 가장 이상적인 재료이다.Ocher has a certain adhesive force, so it is indispensable to solidify the fuel due to the adhesion between the chaff particles, it is easy to control the fire power because it is gradually burned during combustion, and prevents the scattering of ash due to the air volume because it is molded with the chaff. This is the ideal material for composting combusted ash.

참숯 역시 분쇄기에서 0.1 ~ 1 mm 크기로 미분쇄하여 황토 및 왕겨와 함께 혼합되기 위해 준비된다.Charcoal is also ground in a mill to a size of 0.1 to 1 mm and prepared for mixing with ocher and chaff.

도 2에 도시된 바와 같이, 본 발명의 첫 번째 단계로, 위와 같이 준비된 왕겨와 참 숯가루를 배합 교반 하는 단계로 시작하며, 이때, 왕겨와 참숯은 바람직하게는 최종적으로 생산되는 황겨탄의 질량이 400g 기준인 경우 왕겨는 50g, 참 숯가루는 80g 으로 혼합한다.As shown in Figure 2, the first step of the present invention, starting with the step of mixing and stirring the chaff and sesame charcoal powder prepared as above, the chaff and the charcoal is preferably the mass of the sulfur bran is finally produced In the case of 400g, 50g of chaff and 80g of charcoal flour are mixed.

즉, 분쇄된 왕겨 12.5 중량% 와 참숯 20 중량% 를 배합 교반 하는 단계를 거치게 되는 경우, 추후 황토가루가 혼합되는 경우 황토가루가 왕겨와 참숯가루에 고루 배합되는 효과가 있으며, 그 접착력도 우수하여 발열량도 우수해 지는 효과가 있다.In other words, when the mixture is agitated by mixing 12.5% by weight of chaff and 20% by weight of charcoal, when the ocher powder is mixed in the future, the ocher powder is mixed evenly with the chaff and charcoal powder, and the adhesion is excellent. There is also an effect that the calorific value is excellent.

상기 배합 교반 된 왕겨 및 참숯에 옥수수 가루 풀을 함께 혼합하는 단계를 거친다.The blended stirred chaff and charcoal are mixed with corn flour paste.

이때, 접착제로서 액상 또는 분말 규산나트륨으로 접착시킨 후 압착 및 성형도 가능 하지만, 본 발명의 경우 수많은 실험을 통해 상기 왕겨와 참숯가루의 혼합비율에 옥수수 가루 풀을 혼합하는 경우 황토 및 왕겨가 충분히 그 기능이 발휘되는 것을 확인하였으며,At this time, it is possible to squeeze and mold after adhering with liquid or powdered sodium silicate as an adhesive, but in the case of the present invention, when the corn flour paste is mixed in the mixing ratio of the chaff and the charcoal powder through numerous experiments, the ocher and chaff are sufficiently We confirmed that the function is performed,

바람직하게는, 최종 생산되는 황겨탄의 질량이 400g 기준인 경우 옥수수 가루 풀은 200g으로 혼합된다. 즉, 옥수수 가루 풀의 경우 50 중량% 로 상기 배합 교반 된 왕겨 및 참숯에 혼합되는 것이다.Preferably, the corn flour paste is mixed at 200 g when the mass of the final produced yellow bran is 400 g. That is, in the case of corn flour paste 50% by weight is mixed in the blended stirred chaff and charcoal.

옥수수 가루 풀이 왕겨 및 참숯에 스며들기 위해서는 1시간 정도 숙성하는 단계가 필요하며, 다만 왕겨와 참숯의 품질에 따라 위 숙성하는 시간은 변동이 가능함은 당연하다.In order for the cornmeal grass to soak into rice hulls and charcoal, it is necessary to ripen it for about 1 hour.

상기와 같이 왕겨, 참숯가루 및 옥수수 가루 풀을 혼합한 후에 분쇄된 황토가루를 2차적으로 혼합하는 단계가 이루어진다.After mixing the chaff, charcoal powder and corn flour paste as described above, the second step of mixing the ground ocher powder is made.

황토가루는, 열을 받을 경우 다량의 원적외선을 방출한다는 점에서 인체에 유익하며, 동시에 연소시 왕겨 및 참숯가루의 재의 분진을 잡아주는 효과가 있다.Ocher powder is beneficial to the human body in that when it receives heat, it emits a large amount of far infrared rays, and at the same time has the effect of catching ash dust of chaff and charcoal powder during combustion.

이때, 바람직하게는 최종적으로 생산되는 황겨탄의 질량이 400 g 기준인 경우, 황토가루는 70 g 으로 혼합되면, 즉 황토 17.5 중량% 로 2차적으로 혼합된다.At this time, preferably when the mass of the final produced yellow bran charcoal is based on 400 g, when the ocher powder is mixed in 70 g, that is, 17.5% by weight of the ocher mixed second.

상기와 같이 왕겨 12.5 중량%, 참숯 20 중량%, 옥수수 가루 풀 50 중량%, 황토 17. 5 중량% 로 혼합한 경우 황토가 왕겨 및 참숯가루에 고루 배합되며, 이러한 배합 비율로 구성된 황겨탄을 이용하는 경우 고기의 맛이 더욱 풍미해 지고, 고기 특유의 잡내음도 확실히 없어지는 효과가 발생한다.When mixed with 12.5% by weight chaff, 20% by weight of charcoal, 50% by weight of corn flour, 17.5% by weight ocher, ocher is evenly blended with rice hull and charcoal flour, using the yellow rice charcoal composed of such a mixing ratio. In this case, the taste of the meat becomes more flavorful, and the distinctive effect of meat is definitely lost.

상기와 같은 배합비율은 왕겨를 분쇄하지 않고 혼합하는 황겨탄의 제조방법에도 이용된다.The blending ratio as described above is also used in the method for producing sulfur bran which is mixed without crushing rice hulls.

상기 혼합된 왕겨, 참숯, 황토, 옥수수 가루 풀을 원재료 대비 5% 정도의 물과 희석하여 반죽하는 과정이 필요하며, 상기와 같이 반죽 과정을 거친 제품을 프레스를 이용한 성형틀에서 압축 성형 과정을 거친 후, 통풍이 잘 되는 그늘에서 1차적으로 12시간 정도 건조하는 과정을 거친다.The mixed chaff, sesame charcoal, ocher, corn flour paste is required to knead by diluting with about 5% water compared to the raw material, and the product undergoes the kneading process as described above is subjected to a compression molding process in a molding mold using a press After that, the process is first dried for about 12 hours in a well-ventilated shade.

건조가 된 황겨탄을 3분 정도 가열하여 황토 속에 들어 있는 불필요한 이물질을 연소시키게 된다.The dried yellow charcoal is heated for about 3 minutes to burn out unnecessary foreign matter in the loess.

이러한 경우 황토 속에 포함된 왕겨가 연소될 수 있는바 왕겨가 연소 되지 않을 정도로 미열의 열을 이용하여 연소함이 바람직하다.In this case, the chaff contained in the loess may be burned, so it is preferable to burn using heat of low heat so that the chaff is not burned.

상기 제품을 마지막으로 통풍이 잘 되는 그늘에서 2차적으로 8시간 정도 건조하는 단계를 거치면 최종적으로 제품이 완성된다.Finally, the product is finally dried in a well-ventilated shade for about 8 hours to complete the product.

본 발명인 로스터용 황겨탄의 제조방법에 의해 생산되는 황겨탄에 대해 설명한다.The yellow bran charcoal produced by the manufacturing method of the yellow bran charcoal for roaster which is this invention is demonstrated.

다시 도 3a를 참조하면, 본 발명의 황겨탄은 구 형상, 즉 돌덩이 형상으로 사용되는 것이 바람직하다. 도시된 바와 같이 황겨탄의 내부에는 왕겨가 포함되어 있으며, 도 3b는 이러한 황겨탄을 1차 연소한 후에 그 내부의 단면을 나타내고 있으며, 왕겨가 탄화되면서 그 자리에 공극이 형성된 것을 확인할 수 있을 것이다.Referring again to FIG. 3A, the sulfur bran charcoal of the present invention is preferably used in a spherical shape, that is, a lump shape. As shown, the inside of the yellow bran is included chaff, Figure 3b shows the internal cross-section after the first combustion of the yellow bran, and will be confirmed that the pores formed in place as the chaff is carbonized. .

다만, 본 발명의 숯은 구 형상이나 이 구 형상에 구애받지 않고 다양하게 성형될 수 있음은 자명하며, 특히 사용되는 로스터의 구조에 따라 숯의 다양한 변형이 가능함은 본 발명이 속해 있는 기술분야에서 당연하다.However, it is apparent that the charcoal of the present invention may be variously formed regardless of the spherical shape or the spherical shape, and in particular, it is possible to variously change the charcoal according to the structure of the roaster used. Of course.

도 4는 왕겨 자체를 사용하지 않고, 왕겨를 분쇄한 후 황겨탄을 생산하되 그 형상이 납작한 판상으로 이루어진 것을 나타내는 도면이다.4 is a view showing that the chaff is crushed without using chaff itself to produce yellow rice bran, but the shape is made of a flat plate shape.

참숯 및 황토를 분쇄하는 단계(S1); 분쇄된 참숯을 왕겨와 배합 교반 하는 단계(S2); 상기 배합 교반된 왕겨와 참숯 혼합물에 옥수수 가루 풀을 1차적으로 혼합하는 단계(S3); 상기 옥수수 가루 풀이 왕겨와 참숯 혼합물에 스며들기 위해 숙성하는 단계(S4); 상기 옥수수 가루 풀에 의해 혼합된 왕겨와 참숯 혼합물에 분쇄된 황토를 2차적으로 혼합하는 단계(S5); 상기 혼합된 왕겨, 참숯, 황토, 옥수수 가루 풀을 물과 반죽하는 단계(S6); 상기 반죽 된 혼합물을 성형 틀에서 압축 성형하는 단계(S7); 상기 압축 성형 된 제품을 그늘에서 1차적으로 건조하는 단계(S8);상기 제품을 그늘에서 2차로 건조하는 단계(S9); 를 거치나, 상기 분쇄된 참숯을 왕겨와 배합 교반하는 단계(S2)에 있어서, 상기 왕겨도 분쇄한 후 상기 참숯과 배합 교반 하는 과정을 포함하는 것을 특징으로 한다. Grinding the charcoal and loess (S1); Mixing and stirring the ground charcoal with chaff (S2); First mixing the corn flour paste in the blended stirred chaff and charcoal mixture (S3); The corn flour paste is aged to soak into the chaff and charcoal mixture (S4); Secondly mixing the chaff and chaff mixed with the charcoal mixture by the corn flour paste and crushed ocher; Kneading the mixed chaff, sesame charcoal, ocher, and corn flour paste with water (S6); Compression molding the kneaded mixture in a mold (S7); Drying the compression molded product first in a shade (S8); drying the product secondly in a shade (S9); In the step (S2) of mixing and stirring the crushed sesame charcoal with chaff, characterized in that it comprises a step of crushing the chaff and then mixing with the charcoal.

황겨탄은 프레스로 성형할 때 10mm 의 두께(T)를 갖게 하여 보온을 오랫동안 유지할 수 있게 하고, 직경(L)은 50 ~ 60 mm 의 크기로 하여 로스터에 다수개를 올려놓아 사용이 가능하게 구성된다.The yellow charcoal has a thickness (T) of 10mm when it is molded in a press to keep warm for a long time, and the diameter (L) has a size of 50 to 60 mm so that a large number can be placed on the roaster. do.

구멍(20)의 갯수는 황겨탄(10)의 형상에 비례하여 선택적으로 작업이 가능하다.The number of holes 20 can be selectively operated in proportion to the shape of the yellow bran coal (10).

황겨탄의 외형은 도면에 도시된 바와 같이 육각형으로 구성될 수도 있으며. 로스터의 구성에 따라 원반형, 팔각형도 가능할 수 있음은 당연하다.The appearance of the yellow charcoal may be composed of a hexagon as shown in the figure. Obviously, the shape of the roaster may be disk or octagonal.

본 발명의 또 다른 특징은 분쇄된 참숯을 왕겨와 배합 교반하는 단계에서 옥수수전분을 더 포함하여 참숯과 왕겨 및 옥수수전분을 배합 교반하는 것을 특징으로 한다.Another feature of the present invention is characterized by further comprising a mixture of corn starch in the step of mixing and stirring the crushed sesame charcoal chaff and chaff and chaff and corn starch.

옥수수전분은 옥수수녹말로 콘스타치라고도 하며, 단맛을 주고 제품의 크기를 부풀게 하는 성질이 있다.Corn starch, also known as cornstarch, has the property of giving sweetness and inflating the size of the product.

본 출원인은 이에 옥수수전분을 참숯 및 왕겨와 배합 교반하는 경우 숯의 발열량이 높아지고, 그 특유의 고소한 냄새로 고기의 잡내음이 더욱 사라지는 것을 확인하게 되었다. 또한 옥수수전분이 포함되는 경우 본 발명의 숯의 성형도 용이하다는 이점이 있다.Applicant has confirmed that when the corn starch is mixed and mixed with the charcoal and chaff, the calorific value of the charcoal is increased, and the sniffing of the meat disappears further due to its peculiar smell. In addition, when the corn starch is included there is an advantage that the shaping of the charcoal of the present invention is easy.

이를 위해, 우선 참숯 및 황토를 분쇄하는 단계(11)를 거친 후, 분쇄된 참숯을 분쇄된 왕겨와 배합 교반 하는 단계(12)와 상기 배합 교반된 왕겨와 참숯 혼합물에 옥수수 전분을 1차적으로 혼합하는 단계(13) 및 상기 옥수수 전분이 혼합된 왕겨와 참숯 혼합물에 분쇄된 황토를 2차적으로 혼합하는 단계(14), 상기 2차적으로 혼합하는 단계(14)를 거친 혼합물을 압출기(30)에 넣어 인출하는 단계(15) 를 포함하는 것을 특징으로 한다.To this end, first, after the step (11) of crushing the charcoal and loess, the step of mixing and mixing the crushed charcoal with the crushed chaff (12) and the corn starch mixed primarily in the blended stirred chaff and the charcoal mixture To the extruder (30) and the second mixture of the chaff mixed with the corn starch and crushed ocher charcoal mixture (14), the second mixing step (14) It characterized in that it comprises a step (15) to put out.

상기 옥수수 전분이 혼합되는 1차 혼합단계에서 옥수수 전분은 그 자체가 식물성 기름인 바 고기의 맛도 담백해지며, 더군다나 옥수수전분 자체에 수분이 함유되어 있어 별도의 물과 혼합할 필요가 없다는 장점이 있으며, 옥수수전분 자체의 특성으로 끓음도 없고, 왕겨와 참숯 혼합물에 옥수수 전분을 혼합시켜 그 후 황토를 혼합하는 경우 빠른 시간내에 균일하게 혼합되는 특징이 있다.In the first mixing step in which the corn starch is mixed, the corn starch itself is vegetable oil, and the taste of the meat becomes light, and furthermore, the corn starch itself does not need to be mixed with water because it contains moisture. In addition, there is no boiling as a characteristic of the corn starch itself, and when the corn starch is mixed with chaff and charcoal mixture and then the ocher is mixed, there is a characteristic that it is uniformly mixed within a short time.

또한, 이러한 옥수수 전분이 포함되는 경우 옥수수 전분과 함께 혼합되는 왕겨와 숯, 황토가 서로 섞이는 동안 재료 분리가 일어나지 않는 장점이 있으며, 이에 본 출원인은 옥수수 전분 50 ~ 60 중량%, 분쇄된 왕겨 15 중량%, 황토 10 중량%, 참숯가루 15 중량% 를 혼합한 경우 숯의 발열량도 높아지며, 고기의 잡내음도 충분히 잡을 수 있는 이상적인 비율임을 확인하였다.In addition, when the corn starch is included, there is an advantage that material separation does not occur while the chaff and charcoal and ocher mixed with the corn starch are mixed with each other, and thus the applicant has 50 to 60% by weight of corn starch and 15% of the crushed chaff. When mixing%, ocher 10% by weight, 15% by weight of charcoal powder, the calorific value of the charcoal is also increased, it was confirmed that the catch of the meat is also an ideal ratio to catch enough.

도 5는 이러한 숯의 제조방법의 단계를 나타내는 것이며, 별도로 물을 혼합하지 않는 특징이 있다. Figure 5 shows the steps of the production method of such charcoal, there is a feature that does not mix water separately.

이러한 숯은 압출기를 이용하여 생산되며, 압출기의 입구는 150℃ 이며, 스크류를 통해 참숯, 황토, 왕겨 및 옥수수전분이 혼합된 혼합물이 압력과 고온에 의한 열을 받아 인출된다.The charcoal is produced using an extruder, the inlet of the extruder is 150 ℃, through the screw is a mixture of charcoal, loess, rice husk and corn starch is drawn out under pressure and heat.

상기와 같은 단계를 거친 왕겨와 황토를 함유한 숯은, 참숯 및 황토를 분쇄하는 단계(11), 분쇄된 참숯을 분쇄된 왕겨와 배합 교반 하는 단계(12), 상기 배합 교반된 왕겨와 참숯 혼합물에 옥수수 전분을 1차적으로 혼합하는 단계(13), 상기 옥수수 전분이 혼합된 왕겨와 참숯 혼합물에 분쇄된 황토를 2차적으로 혼합하는 단계(14), 상기 2차적으로 혼합하는 단계(14)를 거친 혼합물을 압출기(30)에 넣어 인출하는 단계(15), 를 거친 숯 본체가 스크류 형상인 것을 특징으로 한다.Charcoal containing the chaff and ocher after the above step, the step of crushing the charcoal and ocher (11), the step of mixing and stirring the crushed charcoal with the crushed chaff (12), the blended stirred chaff and the charcoal mixture First mixing the corn starch (13), the second step of mixing the chaff mixed with the corn starch and crushed ocher in the charcoal mixture (14), the second mixing step (14) Step 15 of taking out the coarse mixture into the extruder 30, characterized in that the coarse char body is screw-shaped.

상기의 압출기에 의해 인출된 숯은 도 6a 에 도시된 바와 같이 스크류 형상이며, 다만 숯 제조환경에 따라 도 6b 에 도시된 '콘칩' 형상의 숯도 가능하다.The char taken out by the extruder is a screw shape as shown in Figure 6a, it is also possible to 'char chips' char shown in Figure 6b depending on the charcoal manufacturing environment.

본 발명은 특정한 실시 예에 관련하여 도시하고 설명하였지만, 이하의 특허청구범위에 의해 제공되는 본 발명의 기술적 사상을 벗어나지 않는 한도 내에서, 본 발명이 다양하게 개량 및 변화될 수 있다는 것은 당 업계에서 통상의 지식을 가진자에게 있어서 자명할 것이다.
While the present invention has been particularly shown and described with reference to specific embodiments thereof, it will be understood by those skilled in the art that various changes in form and details may be made therein without departing from the spirit and scope of the invention as defined by the following claims It will be apparent to those of ordinary skill in the art.

S1 : 분쇄하는 단계 S2 : 배합 교반하는 단계
S3 : 1차 혼합하는 단계 S4 : 숙성하는 단계
S5 : 2차 혼합하는 단계 S6 : 반죽하는 단계
S7 : 압축 성형하는 단계 S8 : 1차 건조하는 단계
S9 : 2차 건조하는 단계 10 : 황겨탄
20 : 구멍 30 : 압출기S1: grinding step S2: mixing step
S3: first mixing step S4: ripening step
S5: second mixing step S6: kneading step
S7: step of compression molding S8: step of primary drying
S9: secondary drying step 10: yellow bran coal
20: hole 30: extruder

Claims (7)

참숯 및 황토를 분쇄하는 단계(S1);
분쇄된 참숯을 왕겨와 배합 교반 하는 단계(S2);
상기 배합 교반된 왕겨와 참숯 혼합물에 옥수수 가루 풀을 1차적으로 혼합하는 단계(S3);
상기 옥수수 가루 풀이 왕겨와 참숯 혼합물에 스며들기 위해 숙성하는 단계(S4);
상기 옥수수 가루 풀에 의해 혼합된 왕겨와 참숯 혼합물에 분쇄된 황토를 2차적으로 혼합하는 단계(S5);
상기 혼합된 왕겨, 참숯, 황토, 옥수수 가루 풀을 물과 반죽하는 단계(S6);
상기 반죽 된 혼합물을 성형 틀에서 압축 성형하는 단계(S7);
상기 압축 성형 된 제품을 그늘에서 1차적으로 건조하는 단계(S8);
상기 제품을 그늘에서 2차로 건조하는 단계(S9); 를 포함하는 것을 특징으로 하는 왕겨와 황토를 함유한 숯의 제조방법.Grinding the charcoal and loess (S1);
Mixing and stirring the ground charcoal with chaff (S2);
First mixing the corn flour paste in the blended stirred chaff and charcoal mixture (S3);
The corn flour paste is aged to soak into the chaff and charcoal mixture (S4);
Secondly mixing the chaff and chaff mixed with the charcoal mixture by the corn flour paste and crushed ocher;
Kneading the mixed chaff, sesame charcoal, ocher, and corn flour paste with water (S6);
Compression molding the kneaded mixture in a mold (S7);
First drying the compression-molded product in a shade (S8);
Drying the product secondaryly in the shade (S9); Method of producing charcoal containing chaff and ocher characterized in that it comprises a. 청구항 1에 있어서,
상기 분쇄된 참숯을 왕겨와 배합 교반 하는 단계(S2)에서 상기 왕겨도 분쇄한 후 상기 참숯과 배합 교반 하는 것을 특징으로 하는 왕겨와 황토를 함유한 숯의 제조방법.The method according to claim 1,
The method of producing charcoal containing chaff and ocher, characterized in that the chaff and the mixture of the chaff and the oak after crushing the chaff in the step of mixing and stirring the chaff and chaff. 청구항 1에 있어서,
상기 압축 성형 된 제품을 그늘에서 1차적으로 건조하는 단계(S8)를 거친 후 상기 황토에 포함된 이물질을 제거하기 위해 상기 제품을 3분 정도 가열하는 단계를 포함하는 것을 특징으로 하는 왕겨와 황토를 함유한 숯의 제조방법.The method according to claim 1,
After the step of drying the compression-molded product in the shade (S8) to the first step to remove the foreign matter contained in the ocher chaff and ocher characterized in that it comprises the step of heating the product for about 3 minutes Method of producing charcoal containing. 참숯 및 황토를 분쇄하는 단계(S1); 분쇄된 참숯을 왕겨와 배합 교반 하는 단계(S2); 상기 배합 교반된 왕겨와 참숯 혼합물에 옥수수 가루 풀을 1차적으로 혼합하는 단계(S3); 상기 옥수수 가루 풀이 왕겨와 참숯 혼합물에 스며들기 위해 숙성하는 단계(S4); 상기 옥수수 가루 풀에 의해 혼합된 왕겨와 참숯 혼합물에 분쇄된 황토를 2차적으로 혼합하는 단계(S5); 상기 혼합된 왕겨, 참숯, 황토, 옥수수 가루 풀을 물과 반죽하는 단계(S6); 상기 반죽 된 혼합물을 성형 틀에서 압축 성형하는 단계(S7); 상기 압축 성형 된 제품을 그늘에서 1차적으로 건조하는 단계(S8);상기 제품을 그늘에서 2차로 건조하는 단계(S9); 를 거친 숯 본체의 직경이 25 ~ 35 mm 인 구 형상인 것을 특징으로 하는 왕겨와 황토를 함유한 숯. Grinding the charcoal and loess (S1); Mixing and stirring the ground charcoal with chaff (S2); First mixing the corn flour paste in the blended stirred chaff and charcoal mixture (S3); The corn flour paste is aged to soak into the chaff and charcoal mixture (S4); Secondly mixing the chaff and chaff mixed with the charcoal mixture by the corn flour paste and crushed ocher; Kneading the mixed chaff, sesame charcoal, ocher, and corn flour paste with water (S6); Compression molding the kneaded mixture in a mold (S7); Drying the compression molded product first in a shade (S8); drying the product secondly in a shade (S9); Charcoal containing chaff and ocher characterized in that the shape of the body of the coarse charcoal having a diameter of 25 ~ 35 mm. 청구항 4에 있어서,
상기 분쇄된 참숯을 왕겨와 배합 교반하는 단계(S2)에서 상기 왕겨도 분쇄한 후 상기 참숯과 배합 교반 하는 과정을 포함하되, 상기 숯의 형상이 두께가 10 mm 이고, 직경은 50~60 mm 로 성형 되며 다수개의 구명이 상하로 관통된 납작한 판상으로 구성된 것을 특징으로 하는 왕겨와 황토를 함유한 숯.The method of claim 4,
In the step of mixing and stirring the crushed sesame charcoal chaff (S2), including the step of pulverizing the chaff after mixing with the charcoal, the shape of the char is 10 mm thick, 50 ~ 60 mm in diameter Charcoal containing chaff and ocher, characterized in that it consists of a flat plate with a plurality of life spans penetrated up and down. 참숯 및 황토를 분쇄하는 단계(11);
분쇄된 참숯을 분쇄된 왕겨와 배합 교반 하는 단계(12);
상기 배합 교반된 왕겨와 참숯 혼합물에 옥수수 전분을 1차적으로 혼합하는 단계(13);
상기 옥수수 전분이 혼합된 왕겨와 참숯 혼합물에 분쇄된 황토를 2차적으로 혼합하는 단계(14);
상기 2차적으로 혼합하는 단계(14)를 거친 혼합물을 압출기(30)에 넣어 인출하는 단계(15); 를 포함하는 것을 특징으로 하는 왕겨와 황토를 함유한 숯의 제조방법.Grinding 11 of charcoal and loess;
Blending and stirring the ground charcoal with the ground chaff (12);
Primary mixing (13) the corn starch in the blended stirred chaff and charcoal mixture;
Secondly mixing the chaff mixed with the corn starch and ground charcoal in a charcoal mixture (14);
Putting the mixture passed through the second mixing step (14) into an extruder (30) and withdrawing (15); Method of producing charcoal containing chaff and ocher characterized in that it comprises a. 참숯 및 황토를 분쇄하는 단계(11); 분쇄된 참숯을 분쇄된 왕겨와 배합 교반 하는 단계(12); 상기 배합 교반된 왕겨와 참숯 혼합물에 옥수수 전분을 1차적으로 혼합하는 단계(13); 상기 옥수수 전분이 혼합된 왕겨와 참숯 혼합물에 분쇄된 황토를 2차적으로 혼합하는 단계(14); 상기 2차적으로 혼합하는 단계(14)를 거친 혼합물을 압출기(30)에 넣어 인출하는 단계(15); 를 거친 숯 본체가 스크류 형상인 것을 특징으로 하는 왕겨와 황토를 함유한 숯Grinding 11 of charcoal and loess; Blending and stirring the ground charcoal with the ground chaff (12); Primary mixing (13) the corn starch in the blended stirred chaff and charcoal mixture; Secondly mixing the chaff mixed with the corn starch and ground charcoal in a charcoal mixture (14); Putting the mixture passed through the second mixing step (14) into an extruder (30) and withdrawing (15); Charcoal containing chaff and ocher characterized in that the charcoal body is screw-shaped
KR20120075846A 2012-07-12 2012-07-12 Chaff and clay containing charcoal and its manufacturing method KR20140008777A (en)