KR20140008765A - Method for painting parts of vehicle - Google Patents

Abstract

The present invention relates to a method for painting parts of a vehicle. More specifically a method for painting parts of a vehicle comprises the following steps: coating a colored paint composition on a polyolefin based substrate layer for parts of a vehicle; coating transparent paint on the substrate layer coated with the colored paint composition; and baking the substrate layer. The colored paint composition contains non-halogen based polyolefin with a polar group, a (meth)acrylate based copolymer resin, a colored pigment, and a solvent.

Description

METHOD FOR PAINTING PARTS OF VEHICLE [0001]

The present invention relates to a vehicle component painting method. More particularly, the present invention relates to a method of coating a vehicle part, which can maintain the physical properties of a coating film equal to or more than necessary without a primer pretreatment step, and which has a shortened process time and cost reduction owing to the absence of a primer pretreatment step .

The vehicle bumper is molded and manufactured from a polyolefin material including polypropylene and the like. The surface of the vehicle bumper is coated with paint such as paint to improve appearance and physical properties.

Generally, a polypropylene-based resin is known as a material having poor adhesion as a non-polar material. In order to improve the adhesion, the surface of the polypropylene substrate is subjected to various surface treatments or a primer composed of chlorinated polypropylene, chlorinated polyethylene or cyclic rubber is applied. The primer improves the adhesion between the substrate layer made of polypropylene and the coating layer. Further, in order to enhance primer coating efficiency and adhesion before primer application, the substrate layer made of polypropylene may be subjected to plasma treatment.

However, it is difficult to obtain the desired coating film properties only by the primer coating process. Therefore, the primer is painted using the coating material after the intermediate or top coat is painted. Consequently, several painting processes are required to paint the substrate layer made of polypropylene , The whole process is complicated and the production cost is increased.

Further, in case of coating with only one primer application, the coating composition should contain an additional adhesive component. However, such a viscous component may deteriorate appearance after coating, and physical properties such as weather resistance may deteriorate due to a large amount of tacky components used for securing adhesion.

The background art of the present invention is disclosed in Korean Patent No. 10-0250826 filed on Jan. 11, 2000, entitled " Coating composition used for painting a polypropylene resin molded article ".

An object of the present invention is to provide a vehicle component coating method capable of coating a substrate layer for vehicle parts without a primer pretreatment process.

Another object of the present invention is to provide a vehicle component coating method capable of maintaining the same physical properties as in the case of primer pretreatment without primer pretreatment.

In order to solve the above problems, the vehicle parts coating method of the present invention is coated with a colored paint composition on the polyolefin-based base material layer for vehicle parts, a transparent paint is applied to the base material layer coated with the colored paint composition, and baking ), Wherein the colored coating composition may include a non-halogen-based polyolefin, (meth) acrylic copolymer resin, colored pigment, and solvent having a polar group introduced therein.

The step of applying the colored coating composition to the substrate layer may not include the step of applying the primer to the substrate layer.

The colored coating composition may contain 30 to 50% by weight of the non-halogenated polyolefin to which the polar group is introduced, 10 to 20% by weight of the (meth) acrylic copolymer resin, 5 to 20% by weight of the colored pigment, and a residual solvent.

The non-halogenated polyolefin to which the polar group is introduced may be polypropylene grafted with maleic anhydride.

The method may further comprise plasma treating the substrate layer prior to applying the colored coating composition to the substrate layer.

According to the present invention, a substrate layer of a vehicle component can be coated without a primer pretreatment process, and the same physical properties can be maintained in such a coating method, and as a result, the process can be shortened and the cost can be reduced.

1 is a cross-sectional view of a painted bumper in accordance with one embodiment of the present invention.
100: painted bumper, 10: bumper base layer, 20: colored paint layer, 30: transparent paint layer

The method for painting a vehicle component according to an embodiment of the present invention includes a step of applying a colored coating composition containing a halogen-free polyolefin, a (meth) acrylic copolymer resin, and a colored pigment into which a polar group is introduced, can do.

Vehicle parts coating method according to an embodiment of the present invention is to apply a colored paint composition to a polyolefin-based base material layer for vehicle parts, to apply a transparent paint to the base layer to which the colored paint composition is applied, and baking It may include a step.

The process of pretreating a base material layer for a vehicle component with a primer in coating a conventional vehicle part has been an indispensable step. This is because the polyolefin-based substrate layer is low in paint adhesion so as to enhance the adhesion of the paint to the substrate layer.

The coating composition of the present invention can simultaneously provide the effect of improving the adhesion by the conventional primer as well as the effect of providing and maintaining the color by the colored pigment. As a result, the coating method of the present invention can simultaneously achieve the adhesion of the substrate layer to the coating material and the color effect by applying the coating composition to the substrate layer without primer treatment, even if it does not include the primer pretreatment step.

The colored coating composition may include a non-halogenated polyolefin, a (meth) acrylic copolymer resin, a colored pigment and a solvent into which a polar group is introduced.

The non-halogenated polyolefin to which the polar group is introduced has no phenomenon of discoloration or corrosion of the colored pigment due to the conventional halogenated polyolefin and has good compatibility with the conventional color providing resin so that there is no color change during storage, It is possible to maintain the physical properties of the coating film after coating.

The non-halogenated polyolefin to which the polar group is introduced is a polyolefin denatured with maleic anhydride and free from halogen. Modification by maleic anhydride includes a form in which maleic anhydride is grafted to polyolefin by heat treatment or chemical treatment. The polyolefin may include, but is not limited to, high density polyethylene, low density polyethylene, polypropylene and the like.

In a non-halogenated polyolefin having a polar group introduced therein, the graft ratio is not limited but may be 1-90%.

The (meth) acrylic copolymer resin may include a (meth) acrylic monomer alone or a copolymer resin of a (meth) acrylic monomer and another monomer capable of polymerization with the (meth) acrylic monomer. The (meth) acrylic copolymer resin can be used without limitation as long as it is a (meth) acrylic copolymer resin commonly used in coating for vehicle parts.

The colored pigments are intended to provide color to vehicle parts, and any organic or inorganic pigment conventionally used may be used without limitation.

The solvent can be used without limitation as long as it is a solvent for dissolving a non-halogenated polyolefin, a (meth) acrylic copolymer resin or a colored pigment into which a polar group is introduced. For example, the solvent may be an aqueous solvent, an organic solvent, or a mixture thereof.

The aqueous solvent may be water containing deionized water or the like, and examples of the organic solvent include alcohol-based solvents such as hydrocarbon solvents and ethanol, and ketone solvents such as methyl ethyl ketone.

The colored coating composition may contain 30 to 50 wt% of a non-halogenated polyolefin having a polar group introduced therein, 10 to 20 wt% of a (meth) acrylic copolymer resin, 5 to 20 wt% of a colored pigment, and a residual solvent. Within the above range, adhesion to the substrate layer that has not been pretreated with the primer may be good, and the color may be satisfactory and there may be no problem of defective appearance. Preferably, the coating composition may contain 35 to 45% by weight of a non-halogenated polyolefin having a polar group introduced therein, 10 to 20% by weight of a (meth) acrylic copolymer resin, 5 to 15% by weight of a colored pigment and a residual solvent.

The colored coating composition may further comprise a polyurethane other than the above-mentioned components. Preferably, when an aqueous solvent is used as the solvent, it further includes a polyurethane for improving the adhesion and improving the appearance. The polyurethane is included in the form of a dispersion, and may be included in the composition in an amount of 10 to 20% by weight. Within the above range, the effect of improving adhesion and appearance can be further enhanced.

The colored coating composition may further comprise 10 to 20% by weight of the polyester in addition to the above-mentioned components. Within the above range, the effect of improving adhesion and appearance can be further enhanced.

The colored coating composition may further contain usual additives in addition to the above-mentioned components. Additives include, but are not limited to, leveling agents, UV stabilizers, antiwear agents, dispersants, UV absorbers, and the like.

The application of the colored coating composition can be carried out in a conventional manner. For example, it is possible to supply the colored paint composition to the painting gun of the painting robot and to paint each time the vehicle parts pass.

The colored coating composition may be coated to a thickness of 10 탆 to 30 탆. Within the above range, adhesion to the substrate layer that has not been pretreated with the primer may be good, and the color may be satisfactory and there may be no problem of defective appearance.

A clear coating is applied to the substrate layer applied with the colored coating composition.

The clear paint serves as a coating film for the coating composition applied to the substrate layer.

As the transparent paint, a urethane paint prepared by urethane bonding acryl and isocyanate can be used. In addition, the curing agent may further include a curing agent, for example, a polyisocyanate type curing agent for curing.

The clear paint may be applied in a thickness of 25 占 퐉 to 40 占 퐉. Within the above range, weatherability, water resistance, chemical resistance and environmental resistance may be good.

The vehicle parts are baked after the clear paint is applied. In the baking step, the coating composition and the transparent coating composition applied to the substrate layer are heat cured.

Baking can be performed at 70-90 ° C. for 5-60 minutes. Within this range, the color may be good and there may be no problem of appearance defects. Particularly, when an organic solvent is used as the solvent, it can be performed at 70-90 ° C for 30-60 minutes, and when an aqueous solvent is used, it can be performed at 70-90 ° C for 5-20 minutes.

In the case where an aqueous solvent is used as the solvent, an effect such as adhesiveness can be enhanced by performing a baking process after applying the colored paint composition and before applying the transparent paint.

The substrate layer for vehicle parts may be subjected to a step of cleaning the base layer before application of the coating composition for improving the adhesion of the colored coating composition and improving the appearance after painting. The cleaning can be carried out in a conventional manner, for example, by a whipping method using isopropyl alcohol (IPA) or the like.

The substrate layer for vehicle parts may be subjected to plasma treatment of the base layer before application of the colored coating composition for improving the adhesion of the colored coating composition and for improving appearance after coating. The plasma treatment includes a method of spraying a plasma generated by a plasma burner onto a substrate layer for a vehicle component.

The vehicle component may include body color paint parts including bumper, side sill molding, side garnish, side protector, and other polypropylene-based materials. However, it is not limited thereto.

1 is a cross-sectional view of a painted bumper 100 made in accordance with one embodiment of the present invention. As shown in Fig. 1, a colored paint layer 20 and a transparent paint layer 30 are sequentially laminated on the bumper base layer 10.

Hereinafter, the structure and operation of the present invention will be described in more detail with reference to preferred embodiments of the present invention. It is to be understood, however, that the same is by way of illustration and example only and is not to be construed in a limiting sense.

The contents not described here are sufficiently technically inferior to those skilled in the art, and a description thereof will be omitted.

Example  One

A vehicle bumper of HR580 or HR570, a thermo plastic olefin (TPO) material, was rinsed with isopropyl alcohol. A coating composition comprising 40% by weight of a non-halogenated polyolefin to which a polar group is introduced, 15% by weight of an acrylic copolymer resin, 10% by weight of a black pigment and a residual solvent (organic solvent which is a mixture of hydrocarbon series, alcohol series and ketone series) Were prepared. A transparent urethane paint was dissolved in a solvent having the same composition as the above-mentioned solvent to prepare a clear paint, and a curing agent for a clear paint was separately prepared. The paint composition was applied to the vehicle bumper, the transparent paint was applied after 5 to 10 minutes, and after 5 to 10 minutes, it was heat treated at 80 DEG C for 30 minutes.

Example  2

In Example 1, TPO materials HR580, HR580E, using a polar group introduced non-halogen-based polyolefin 40% by weight, acrylic copolymer resin 15% by weight, black pigment 10% by weight, polyurethane dispersion 20% by weight and the remaining amount The same method was carried out except that the coating composition was mixed with an aqueous solvent (deionized water) and baking was performed at 80 ° C. for 10 minutes. At this time, baking may be further performed after the application of the colored paint composition and before the application of the transparent paint.

Comparative Example  One

A vehicle bumper of HR580 or HR570, a thermo plastic olefin (TPO) material, was rinsed with isopropyl alcohol. The vehicle bumper was primed with chlorinated polypropylene. A coating composition containing 15% by weight of an acrylic copolymer resin, 10% by weight of a black pigment and a residual amount of a solvent (mixed solvent of a hydrocarbon series, an alcohol series and a ketone series) was prepared. A transparent urethane paint was dissolved in a solvent having the same composition as the above-mentioned solvent to prepare a clear paint, and a curing agent for a clear paint was separately prepared. The paint composition was applied to the vehicle bumper, the transparent paint was applied after 5 to 10 minutes, and after 5 to 10 minutes, it was heat treated at 80 DEG C for 30 minutes.

The adhesion, appearance, water resistance, weather resistance, and chemical resistance of the painted vehicle bumper painted in the above Examples and Comparative Examples were evaluated.

Attachment is made by grasping eleven lines at intervals of 2mm each on the car bumper which has been completed. It is judged whether or not the coating film of the vehicle bumper is peeled off when the acrylic tape is attached and then detached. Measure more than 3 times. The number of peelings is evaluated as 0-10 points. The higher the score, the better the adhesion.

The appearance of the bumper of the final manufactured vehicle was evaluated as 0-10 points based on the occurrence of stains and color uniformity. The higher the score, the better the appearance.

The water resistance was evaluated in the same manner as the above-described adhesion evaluation after 10 days from the application of the coating film to water at 40 캜. 0-10 points, and the higher the score, the better the water resistance.

Weatherability is evaluated by measuring the degree of chromaticity change and adhesion after applying a coating to a weathering resistance tester and irradiating light. 0-10 points, and the higher the score, the better the weatherability.

The chemical resistance was evaluated by treating the coating film with grease, gasoline, and enamel oil, and changing the state of the coating film after 2 hours in an oven at 80 ° C. 0-10 points, and the higher the score, the better the chemical resistance.

Adhesion Exterior Water resistance Weatherability Chemical resistance Example 1 10 10 10 10 10 Example 2 10 10 10 10 10 Comparative Example 1 10 8 10 10 10

As shown in Table 1, the coating method according to the present invention showed better physical properties such as paint adhesion, appearance, water resistance, and the like without the primer pretreatment process as compared with the conventional coating method including the primer treatment of Comparative Example 1. [ As a result, the process can be shortened and the cost reduction effect can be realized.

Simple modifications or changes of the present invention can be easily carried out by those skilled in the art, and all such modifications or changes can be seen to be included in the scope of the present invention.

Claims (8)

A colored coating composition is applied to a polyolefin based substrate layer for vehicle parts,
Applying a clear paint to the substrate layer to which the colored coating composition is applied, and
Baking,
The colored coating composition is a vehicle component coating method comprising a non-halogen-based polyolefin, (meth) acrylic copolymer resin, colored pigments and solvents introduced with a polar group. The method of claim 1, wherein the step of applying the colored coating composition to the substrate layer does not include primer pretreatment of the substrate layer. The colored coating composition according to claim 1, wherein the colored coating composition comprises 30 to 50% by weight of the non-halogenated polyolefin into which the polar group is introduced, 10 to 20% by weight of the (meth) acrylic copolymer resin, 5 to 20% Of the vehicle. The method of claim 1, wherein the solvent is an organic solvent, an aqueous solvent, or a mixture thereof. The method of claim 1, wherein the non-halogenated polyolefin to which the polar group is introduced is polypropylene grafted with maleic anhydride. The method of claim 1, further comprising plasma treating the substrate layer prior to applying the colored coating composition to the substrate layer. The method of claim 1, wherein the colored paint composition further comprises 10-20% by weight of at least one of polyurethane and polyester in the composition. The method of claim 1, wherein the baking is performed at 70-90 ° C. for 5 minutes-60 minutes.

Images