KR20130110120A - Light diffusive ink composition and light guide panel unit using the same - Google Patents
Light diffusive ink composition and light guide panel unit using the same Download PDFInfo
- Publication number
- KR20130110120A KR20130110120A KR1020130104865A KR20130104865A KR20130110120A KR 20130110120 A KR20130110120 A KR 20130110120A KR 1020130104865 A KR1020130104865 A KR 1020130104865A KR 20130104865 A KR20130104865 A KR 20130104865A KR 20130110120 A KR20130110120 A KR 20130110120A
- Authority
- KR
- South Korea
- Prior art keywords
- light
- pigment
- ink composition
- weight
- ink
- Prior art date
Abstract
Description
본 발명은 광확산 잉크 조성물에 관한 것으로서, 보다 상세하게는 유리 재질의 도광패널에 적용되어 광원에서 출사되는 빛에 대해 광확산층을 형성하는 잉크 조성물 및 이를 이용하여 구현된 디스플레이 이미지의 표시가 가능한 유리 재질의 도광패널 및 디스플레이 유닛에 관한 것이다. The present invention relates to a light diffusion ink composition, and more particularly, an ink composition applied to a light guide panel made of glass to form a light diffusion layer with respect to light emitted from a light source, and a glass capable of displaying a display image implemented using the same. A light guide panel and a display unit are made of material.
일반적으로 도광패널은 광원의 빛을 받아 균일한 휘도의 면광원 형태로 출사하기 위한 조명부품으로서, 액정표시장치(LCD)의 백라이트유닛(BLU)를 구현하는 부품으로 적용되고 있다.In general, the light guide panel is an illumination component for emitting light in the form of a surface light source having a uniform brightness by receiving light from a light source, and is applied as a component for implementing a backlight unit (BLU) of a liquid crystal display (LCD).
도 1 및 도 2를 참조하면, 상기 도광패널의 제조에 사용되는 도광부재(4), 예를 들면 플라스틱 또는 유리 재질 등의 도광판이나 도광필름의 표면을 레이저 가공기술을 이용하여 깎아서, 상기 도광부재의 표면에 스크래치(Scratch) 또는 도트(Dot)로 구성되는 패턴(8; Pattern)이 형성되면, 상기 패턴(8)이 상기 광원(3)의 빛을 산란/굴절/반사시킴으로써 상기 도광패널이 면광원 형태로 조명광이 출사한다.1 and 2, the surface of the
그러나 상기 레이저 가공기술에 의해 제조되는 상기 도광패널은 상기 광원(3)의 빛을 상기 광원(3)의 빛과 동일한 색깔의 면광원으로 출사할 뿐이어서 심미적인 조명광의 전달이 어렵고 단조로운 면광원 형태의 조명광을 출사하는데 그친다.However, the light guide panel manufactured by the laser processing technology emits light from the
한편, 근래에는 상기 도광부재(4)에 광확산 잉크를 인쇄하여 상기 도광부재(4)의 표면에 상기 패턴(8)을 도트 형태로 형성함으로써 상기 광원(3)에서 출사되는 빛을 산란/반사시키는 구성의 도광패널이 개발되고 있는데, 이러한 광확산 잉크를 이용한 도광패널 역시 상기 광확산 잉크가 인쇄된 부분이 상기 광원의 빛을 산란/반사시켜서 동일한 색깔과 균일한 휘도로 출력할 뿐이며 상기 도광패널 자체만으로 수려한 느낌의 광이나 특정 디자인의 이미지를 출력할 수 없고, 상기 광확산 잉크가 전체적인 휘도를 개선하기는 하나, 상기 도광패널을 상기 백라이트유닛 이외에 다양한 분야에 적용시키는 데 한계가 있다.On the other hand, in recent years, light diffusion ink is printed on the
다시 말해서, 종래의 도광패널, 보다 구체적으로 상기 도광부재(4)는 액정표시장치의 기판을 고르게 조명하거나, 일정 형태의 이미지(2a)가 구현된 이미지 시트(2; Image Sheet) 예를 들면 광고나 장식을 위한 사진 시트나 그림 시트의 후방에 배치되어, 상기 이미지 시트(2)를 후방에서 상기 이미지 시트(2)의 특정 부분을 상기 광원(3)의 빛과 동일한 색으로 비추어서 조명하는 백라이트 유닛으로만 적용되는 실정이다.In other words, the conventional light guide panel, more specifically, the
이에 본 발명자는 상기 광원을 빛을 변환시켜서 심미적이고 감성적인 형태의 빛으로 출사할 수 있는 광확산 잉크 조성물 및 이를 이용한 도광 패널, 더 나아가 도광패널 자체에 광확산 잉크로 이미지가 구현된 광패턴 이미지 출력형 도광패널을 개발하게 되었다.Accordingly, the present inventors convert a light into a light diffusion ink composition capable of emitting light in aesthetic and emotional form, a light guide panel using the same, and a light pattern image in which an image is implemented as a light diffusion ink in the light guide panel itself. Output light guide panel was developed.
본 발명은 상술한 문제점을 해결하기 위해 안출된 것으로서, 본 발명의 목적은 크리스탈 형태의 광패턴을 출력하여 심미적인 느낌을 줄 수 있는 광확산 잉크 조성물 및 이를 이용한 도광패널을 제공하기 위한 것이다.The present invention has been made to solve the above-described problems, an object of the present invention is to provide a light-diffusing ink composition and a light guide panel using the same that can give an aesthetic feeling by outputting a light pattern of the crystal form.
본 발명의 다른 목적은, 소정 디자인에 맞춰서 광확산 잉크 조성물에 의해 인쇄된 디스플레이 이미지를 출력할 수 있는 도광 패널, 즉 이미지 시트를 후방에서 조명하는 타입이 아닌 자체적으로 디스플레이 이미지를 출력할 수 있는 도광 패널을 제공하는 데 있다.Another object of the present invention is a light guide panel capable of outputting a display image printed by a light diffusing ink composition according to a predetermined design, that is, a light guide capable of outputting a display image by itself rather than a type of illuminating an image sheet from behind. To provide a panel.
본 발명의 또 다른 목적은 다양한 색상이나 형상의 디스플레이 이미지를 상기 도광 패널에 구현할 수 있는 광확산 잉크 조성물 및 이에 의해 구현되는 유색(Color)의 이미지를 출력할 수 있는 도광 패널을 제공하는 데 있다.Still another object of the present invention is to provide a light diffusion ink composition capable of realizing a display image of various colors or shapes on the light guide panel, and a light guide panel capable of outputting a color image implemented thereby.
상술한 목적을 달성하기 위하여, 본 발명은: 광원의 빛을 받아 크리스탈 광패턴을 출력하는 광확산 잉크 조성물로서; 에폭시 수지와 폴리아미드 수지 중 어느 하나를 포함하여 다른 하나와의 혼합에 의해 상기 광확산 잉크 조성물의 경화시키는 잉크 바인더; 크리스탈 광패턴의 구현을 위한 PMMA(Polymethylmethacrylte) 입자; 그리고 잉크 용제를 포함하는 광확산 잉크 조성물을 제공한다.In order to achieve the above object, the present invention provides a light diffusion ink composition for receiving a light of a light source and outputting a crystal light pattern; An ink binder for curing the light diffusing ink composition by mixing any one of an epoxy resin and a polyamide resin; PMMA (Polymethylmethacrylte) particles for the realization of the crystal light pattern; And it provides the light-diffusion ink composition containing an ink solvent.
여기서, 상기 PMMA 입자는 평균입도가 10㎛~50㎛인 PMMA 비드(Bead)인 것을 특징으로 한다. 보다 상세하게는, 상기 PMMA 비드는 평균입도가 15㎛~20㎛인 것을 특징으로 한다.Here, the PMMA particles are characterized in that the PMMA beads (Bead) having an average particle size of 10㎛ ~ 50㎛. More specifically, the PMMA beads are characterized in that the average particle size is 15㎛ ~ 20㎛.
상기 에폭시 수지와 폴리아미드 수지의 혼합물을 포함하여 구성되는 상기 잉크 바인더의 굴절율은 1.52이고, 상기 PMMA 입자는 굴절율이 1.49인 것을 특징으로 한다.The refractive index of the ink binder including the mixture of the epoxy resin and the polyamide resin is 1.52, the PMMA particles are characterized in that the refractive index is 1.49.
그리고 상기 잉크 용제는, 케톤류와 에스테르류와 에테르류와 탄화수소계와 글리콜에테르계 유기용제로 이루어진 군에서 1종 이상 선택될 수 있다.The ink solvent may be at least one selected from the group consisting of ketones, esters, ethers, hydrocarbon-based, and glycol ether-based organic solvents.
상기 PMMA 입자 100 중량부에 대하여 상기 잉크 바인더는 110~250 중량부, 상기 잉크 용제는 50~150 중량부가 혼합된다.110 to 250 parts by weight of the ink binder and 50 to 150 parts by weight of the ink solvent are mixed with respect to 100 parts by weight of the PMMA particles.
상기 잉크 바인더는, 당량비로 상기 에폭시 수지와 상기 폴리아미드 수지의 혼합 함량을 정하며, 일 예로 EEW(Epoxide Equivalent Weight)=200(g/eq) 값을 가지는 에폭시 수지 100 중량부에 대하여 AHEW(Amine Hydrogen Equivalent Weight)=24(g/eq) 값을 가지는 폴리아미드 수지 12 중량부가 혼합된다.The ink binder determines a mixed content of the epoxy resin and the polyamide resin in an equivalent ratio, and for example, AHEW (Amine Hydrogen) based on 100 parts by weight of an epoxy resin having an EEW (Epoxide Equivalent Weight) = 200 (g / eq) value. 12 parts by weight of a polyamide resin having an Equivalent Weight) = 24 (g / eq) value is mixed.
본 발명에 따른 광확산 잉크 조성물 색상 구현을 위한 색상안료를 더 포함하여 구성될 수도 있다. 상기 색상안료는, 투명 색상안료인 것을 특징으로 한다.It may be configured to further include a color pigment for implementing the light-diffusing ink composition color according to the present invention. The color pigment is characterized in that the transparent color pigments.
상기 색상 안료는; 아조계 안료, 프탈로시아닌(Phthalocyanine) 안료, 안트라퀴논계(Anthraquinone) 안료, 티오인디고계(Thioindigo) 안료, 페린온계(Perinone) 안료, 페릴렌계(Perylene) 안료, 퀴나크리돈계(Quninacridone) 안료, 그리고 투명성 색상안료로 이루어진 군에서 1종 이상 선택되는 것을 특징으로 한다.The color pigments; Azo pigments, Phthalocyanine pigments, Anthraquinone pigments, Thioindigo pigments, Perinone® pigments, Perylene pigments, Quinacridone pigments, and transparency Characterized in that at least one selected from the group consisting of color pigments.
상기 아조계 안료로는, 시.아이. 피그먼트 레드(C.I. Pigment Red) 3, 5, 48:1, 48:2,48:3, 48:4, 53:1, 53:2, 57:1, 시. 아이. 피그먼트 엘로우 1, 3, 83, 시.아이. 피그먼트 오렌지 16, 13 등이 있고; 상기 프탈로시아닌 안료로는 시.아이. 피그먼트 블루(C.I. Pigment Blue) 15, 15:3, 17과 시.아이. 피그먼트 그린(C.I. Pigment Green) 7 등이 있다.As said azo pigment, it is C.I. Pigment Red 3, 5, 48: 1, 48: 2,48: 3, 48: 4, 53: 1, 53: 2, 57: 1, hour. children. Pigment Yellow 1, 3, 83, C.I. Pigment orange 16, 13, and the like; The phthalocyanine pigment may be ci. Pigment Blue 15, 15: 3, 17 and C.I. Pigment Green 7 and the like.
그리고 상기 안트라퀴논계 안료의 예로는, 축합다환계 유기안료로 인단트렌 블루 시.아이. 피그먼트 블루60(Indanthrene Blue C.I. Pigment Blue 60)이 있고; 상기 티오인디고계 안료로는, 티오인디고 마젠타 시.아이. 피그먼트 바일롯38(Thioindigo Magenta C.I. Pigment Vilot38) 등이 있으며; 상기 페린온계 안료의 예로는, 페린온 오렌지 시.아이. 피그먼트 오렌지43(Perinone Orange C.I. Pigment Orange 43)이 있다. And examples of the anthraquinone pigments are condensed polycyclic organic pigments indanthrene blue C.I. Pigment Blue 60 (Indanthrene Blue C. I. Pigment Blue 60); Examples of the thioindigo pigments include thioindigo magenta C. eye. Pigment bylot 38 (Thioindigo Magenta C.I. Pigment Vilot 38); Examples of the perinone pigments include perinone orange C.I. Pigment Orange 43 (Perinone Orange C. I. Pigment Orange 43).
상기 페릴렌계 안료의 예로는 페릴렌 마룬 시.아이. 피그먼트 레드179(Perylene Maroon C.I. Pigment Red 179)가 있으며; 상기 퀴나크리돈계 안료의 예로는 퀴나크리돈 레드 시.아이. 피그먼트 바이올렛 19(Quninacridone Red C.I. Pigment Violet 19)이 있고; 상기 투명성 색상안료의 예로는, 시.아이. 피그먼트 레드 177(C.I. Pigment R 177(red))과, 시.아이. 피그먼트 그린 36(CI Pigment G36(green))과, 시.아이. 피그먼트 블루 15:6(C.I. pigment B15:6(blue))과, 시.아이. 피그먼트 옐로우 139(C.I. Pigment Y139(yellow))와, 시.아이. 피그먼트 바이올렛 23(CI Pigment V23(violet)) 등이 있다.Examples of the perylene-based pigments are perylene maroon C. eye. Pigment Red 179 (Perylene Maroon C. I. Pigment Red 179); Examples of the quinacridone pigments include quinacridone red C. eye. Pigment violet 19 (Quninacridone Red C.I. Pigment Violet 19); Examples of the transparent color pigments, S.I. Pigment Red 177 (C.I. Pigment R 177 (red)) and C.I. Pigment green 36 (CI Pigment G36 (green)) and C.I. Pigment Blue 15: 6 (C.I. pigment B15: 6 (blue)) and C.I. Pigment Y139 (yellow) and C.I. Pigment violet 23 (CI Pigment V23 (violet)).
여기서, 상기 PMMA 입자 100 중량부에 대하여 상기 색상안료는 5~50 중량부가 혼합된다.Here, the color pigment is 5 to 50 parts by weight based on 100 parts by weight of the PMMA particles.
다른 일 형태로서 본 발명은; 상술한 구성을 갖는 광확산 잉크 조성물에 형성되는 광확산 잉크층; 그리고 상기 광확산 잉크층이 구비되는 유리 재질의 도광부재;를 포함하여 구성되는 디스플레이 도광패널을 제공한다. In another aspect the present invention provides A light diffusion ink layer formed on the light diffusion ink composition having the above-described configuration; And a light guiding member made of glass provided with the light diffusion ink layer.
상기 도광부재는, 상기 광확산 잉크 조성물이 기결정된 디자인에 맞춰 상기 도광 패널의 표면에 인쇄되어 상기 광확산 잉크층이 상기 도광부재의 표면에 형성하는 이미지를 가지며; 상기 도광부재로 광원의 빛이 출사됨에 따라 상기 도광부재의 전방으로 상기 크리스탈 광패턴의 이미지가 출력되는 것을 특징으로 한다.The light guiding member has an image in which the light diffusing ink composition is printed on a surface of the light guide panel according to a predetermined design so that the light diffusing ink layer is formed on the surface of the light guiding member; As the light of the light source is emitted to the light guide member, an image of the crystal light pattern is output to the front of the light guide member.
본 발명에 따른 광확산 잉크 조성물 및 이를 이용한 도광패널 및 디스플레이 유닛에 따르면 다음과 같은 효과가 있다.According to the light diffusing ink composition and the light guide panel and the display unit using the same according to the present invention, the following effects are obtained.
본 발명에 따르면, 광원의 빛이 크리스탈 광패턴으로 변환되어 출력되므로 심미적이고 감성적인 광을 구현할 수 있고, 이를 이용한 도광패널로 수려한 디자인의 조명을 구현할 수 있다.According to the present invention, since the light of the light source is converted into a crystal light pattern and outputted, aesthetic and emotional light can be realized, and the light of the light guide panel using the light can be realized in a beautiful design.
본 발명에 따르면, 유색의 광확산 잉크 조성물로 유색의 크리스탈 패턴을 구현할 수 있고 광원의 색과 함께 혼합색을 구현할 수 있으므로 다양한 색상의 크리스탈 광패턴을 출력할 수 있다.According to the present invention, the colored light diffusing ink composition may implement a colored crystal pattern and a mixed color together with the color of the light source, thereby outputting crystal light patterns of various colors.
본 발명에 따르면, 상기 광확산 잉크 조성물이 도광패널에 광확산층을 형성하는 동시에 유색 및/또는 무색의 광확산 잉크 조성물을 이용하여 원하는 디자인의 디스플레이 이미지를 도광패널 자체에 구현할 수 있고, 이에 따라 도광패널 자체가 직접 심미적이고 수려한 디자인의 디스플레이 이미지를 크리스탈 광패턴으로 출력할 수 있다.According to the present invention, the light diffusion ink composition may form a light diffusion layer on the light guide panel and simultaneously implement a display image having a desired design on the light guide panel itself by using a colored and / or colorless light diffusion ink composition. The panel itself can directly output display images of aesthetic and beautiful designs in crystal light patterns.
본 발명에 따르면, 별도의 이미지 시트를 도광패널의 전방에 적층하지 않고도 소정 디자인의 이미지가 구현된 장식판이나 간판, 광고판 등의 디스플레이 패널을 제조할 수 있으므로 부품수와 두께와 무게가 감소되고, 상기 도광패널에 적용되는 소정 디자인의 장식이미지나 광고 이미지, 예를 들면 그림이나 로고 등과 문자나 기호 등이 광원이 빛을 받아서 유색 및/또는 무색의 디자인으로 심미적으로 출력될 수 있다.According to the present invention, it is possible to manufacture a display panel such as a decorative plate, a signboard, an advertisement board, etc., in which an image of a predetermined design is implemented without stacking a separate image sheet in front of the light guide panel, thereby reducing the number of parts, thickness, and weight. A decorative image or an advertisement image of a predetermined design applied to the light guide panel, for example, a picture or a logo and the like, may be aesthetically output in a colored and / or colorless design by receiving light.
도 1은 종래의 디스플레이 유닛의 일 예를 나타낸 분해 사시도이다.
도 2는 도 1의 디스플레이 유닛에 구비되는 백라이트 유닛을 나타낸 단면도이다.
도 3은 본 발명에 따른 광확산 잉크 조성물에 의해 구현되는 발광 이미지를 갖는 디스플레이 유닛의 일 실시예를 나타낸 분해 사시도이다.
도 4는 도 3의 디스플레이 유닛을 개략적으로 나타낸 단면도이다.1 is an exploded perspective view showing an example of a conventional display unit.
2 is a cross-sectional view illustrating a backlight unit included in the display unit of FIG. 1.
3 is an exploded perspective view showing an embodiment of a display unit having a light emitting image implemented by the light diffusing ink composition according to the present invention.
4 is a schematic cross-sectional view of the display unit of FIG. 3.
이하, 본 발명에 따른 광확산 잉크 조성물의 바람직한 실시예를 보다 구체적으로 설명한다.Hereinafter, a preferred embodiment of the light diffusion ink composition according to the present invention will be described in more detail.
본 발명에 따른 광확산 잉크 조성물의 일 실시예는 잉크 바인더(Ink Binder)와 광확산제와 잉크 용제를 포함하여 구성된다. 여기서 상기 광확산 잉크 조성물은 첨가제를 더 포함하여 구성될 수 있다.One embodiment of the light diffusion ink composition according to the present invention comprises an ink binder (Ink Binder), a light diffusing agent and an ink solvent. Here, the light diffusion ink composition may further include an additive.
상기 잉크 바인더는, 에폭시 수지와 폴리아미드 수지의 혼합에 의해 구현된다. 다시 말해서 상기 잉크 바인더는 에폭시 수지와 폴리아미드 수지 중 어느 하나를 포함하며 다른 하나와의 혼합에 의해 상기 광확산 잉크 조성물을 경화시킨다. The ink binder is implemented by mixing an epoxy resin and a polyamide resin. In other words, the ink binder comprises any one of an epoxy resin and a polyamide resin and cures the light diffusion ink composition by mixing with the other.
따라서 상기 잉크 바인더는 최종적으로 상기 에폭시 수지와 상기 폴리아미드 수지의 혼합물을 포함하여 구성되는데, 상기 폴리아미드 수지는 상기 에폭시 수지와 혼합되어 시간이 경과함에 따라 본 발명에 따른 광확산 잉크 조성물이 자연적으로 경화된다.Thus, the ink binder finally comprises a mixture of the epoxy resin and the polyamide resin, wherein the polyamide resin is mixed with the epoxy resin so that the light diffusion ink composition according to the present invention naturally Cures.
따라서 상기 폴리아미드 수지는 상기 에폭시 수지와 별도로 서로 분리된 상태로 보존되다가 본 발명에 따른 광확산 잉크 조성물의 사용 직전에 혼합되어 상기 잉크 조성물을 구성한다. 즉 본 발명에 따른 광확산 잉크 조성물의 잉크 바인더는 2액형 타입이 된다.Therefore, the polyamide resin is kept separate from each other separately from the epoxy resin and mixed immediately before use of the light diffusing ink composition according to the present invention to constitute the ink composition. That is, the ink binder of the light-diffusion ink composition according to the present invention is a two-component type.
다음으로, 상기 잉크 용제는, 케톤류와 에스테르류와 에테르류와 탄화수소계와 글리콜에테르계 유기용제로 이루어진 군에서 1종 이상 선택될 수 있다. 상기 케톤류 용제의 예로는 이소포론(Isophorone)과 사이클로헥사논(Cyclohexanone) 등이 있으며, 상기 에스테르류 용제의 예로는 부틸케비톨 아세테이트(Buthyl Cabitol Acetate)과 에틸케비톨 아세테이트(Ethyl Cabitol Acetate) 등이 있고, 상기 에테르류 용제의 예로는 부틸 케비톨(Buthyl Cabitol)과 에틸케비톨 등이 있다.Next, the ink solvent may be at least one selected from the group consisting of ketones, esters, ethers, hydrocarbon-based and glycol ether-based organic solvents. Examples of the ketone solvents include isophorone and cyclohexanone, and examples of the ester solvents include butyl kebitol acetate and ethyl ketitol acetate. Examples of the ether solvents include butyl ketitol and ethyl kebitol.
그리고, 상기 탄화수소계 용제로는 아로마틱 150(Aromatic 150)와 아로마틱 200(Aromatic 200) 등이 있으며, 상기 글리콜에테르계 용제로는 부틸 셀루솔브(Butyl Cellusolve)와 에틸 셀루솔브(Ethyl Cellusolve) 등이 있다.The hydrocarbon solvents include aromatic 150 and aromatic 200, and the glycol ether solvents include butyl cellusolve and ethyl cellusolve. .
상술한 케톤류와 에스테르류와 에테르류와 탄화수소계와 글리콜에테르계 유기용제 중의 1종 또는 2종 이상의 용제가 혼합되어 상기 잉크 용제를 구성할 수 있다.One or two or more kinds of the above-mentioned ketones, esters, ethers, hydrocarbon-based, and glycol ether-based organic solvents may be mixed to constitute the ink solvent.
상기 광확산제는 PMMA(폴리메틸메타크릴레이트; Polymethylmethacrylate) 입자, 특히 PMMA 비드(Bead)로 구성될 수 있으며, 상기 잉크 바인더 및 상기 잉크 용제의 혼합물에 적용되어 크리스탈 광패턴, 예를 들면 크리스탈 유리의 느낌과 같은 관능성을 구현한다.The light diffusing agent may be composed of PMMA (Polymethylmethacrylate) particles, in particular PMMA beads, and is applied to a mixture of the ink binder and the ink solvent to form a crystal light pattern, for example, crystal glass. Implement the same sense of sensuality.
보다 상세하게 설명하면, 상기 PMMA 입자는 크리스탈 광패턴의 구현을 위하여 평균 입도(Grain Size)가 10㎛~50㎛인 PMMA 비드(Bead)들로 구성될 수 있으며, 보다 바람직하게는 상기 PMMA 비드는 평균입도가 13㎛~30㎛, 특히 15㎛~20㎛인 것이 크리스탈 광패턴의 출력에 좋다.In more detail, the PMMA particles may be composed of PMMA beads having an average grain size (Grain Size) of 10 ㎛ ~ 50 ㎛ for implementing the crystal light pattern, more preferably the PMMA beads An average particle size of 13 µm to 30 µm, particularly 15 µm to 20 µm, is good for the output of the crystal optical pattern.
잉크를 이용한 광확산을 위해서는 상기 PMMA 비드들의 평균입도가 10㎛ 보다 작은 경우도 가능하나, 이러한 경우 이러한 경우 헤이즈(Haze) 값이 낮아져 광원의 빛을 단조롭게 출사하는 정도이며 크리스탈 광패턴이 구현되기 어렵거나 크리스탈 광패턴의 출력이 미약하다.For the light diffusion using ink, the average particle size of the PMMA beads may be smaller than 10 μm, but in this case, the haze value is lowered to monotonously emit light of the light source, and it is difficult to realize a crystal light pattern. Or the crystal light pattern output is weak.
보다 상세하게 설명하면, 상기 광확산 잉크 조성물이 도광부재(도 3의 번호 111 참조)에 스크린 인쇄되어 건조됨으로써 상기 도광부재에 광확산층이 형성되는데, 상기 PMMA 비드들의 평균입도가 10㎛ 보다 작은 경우에는 상기 PMMA 비드들이 상기 잉크 바인더 내에 함침되면서 광확산효과가 저하된다. 즉 헤이즈(Haze)가 낮게 나타난다. 그러나 상기 PMMA 비드들의 평균입도가 10㎛ 보다 큰 경우에는 상기 광확산층, 즉 인쇄면이 울퉁불퉁하게 표현되어 유리에 요철(엠보싱)이 형성된 것과 같이 되므로 광원의 빛을 굴절시켜서 크리스탈 광패턴이 출력될 수 있다.In more detail, the light diffusion ink composition is screen printed on the light guiding member (see
그리고, 상기 PMMA 비드의 평균입도는 50㎛를 초과할 수도 있으나 이러한 경우 스크린 메쉬 잉크 빠짐성이 저하된다. 바람직하게는 스크린 메쉬 빠짐성과 입자의 중첩에 의한 헤이즈 현상의 측면에서 상기 PMMA 비드는 평균입도가 15㎛~20㎛인 것이 좋다. In addition, the average particle size of the PMMA beads may be greater than 50 μm, in which case screen mesh ink omission is reduced. Preferably, the PMMA beads have an average particle size of 15 μm to 20 μm in terms of screen mesh omission and haze due to particle overlap.
상기 잉크 바인더는 굴절율이 대략 1.52이 되도록 에폭시 수지와 폴리아미드 수지의 혼합물이 적용되며, 상기 잉크 바인더와 상기 PMMA 입자는 굴절율이 동일하거나 유사한 것이 크리스탈 광패턴의 구현에 효과적이다. 본 실시예에서는 상기 PMMA 입자의 굴절율은 1.49이며, 상기 잉크 바인더로는 굴절율이 1.52인 에폭시 수지와 폴리마이드 수지의 혼합물이 예시된다.The ink binder is a mixture of an epoxy resin and a polyamide resin so that the refractive index is approximately 1.52, and the ink binder and the PMMA particles are the same or similar in the refractive index is effective in the implementation of the crystal optical pattern. In the present embodiment, the refractive index of the PMMA particles is 1.49, and the ink binder includes a mixture of an epoxy resin and a polyamide resin having a refractive index of 1.52.
상기 광확산제는 상기 잉크 바인더와 굴절율이 실질적으로 동일한 것이 크리스탈 광패턴의 구현에 효과적이며, 상기 PMMA 비드 대신 PBMA(Polybutylmethacrylate) 비드 등 굴절율이 높은 구형 비드 특히 상기 잉크 바인더와 굴절율이 실질적으로 동일한 광확산제가 사용될 수도 있다.The light diffusing agent is substantially the same refractive index as the ink binder is effective in the implementation of the crystal optical pattern, spherical beads having a high refractive index, such as polybutylmethacrylate (PBMA) beads, in particular instead of the PMMA beads, especially light having the same refractive index as the ink binder Diffusing agents may also be used.
상기 PMMA 입자 100 중량부에 대하여, 상기 잉크 바인더는 100~300 중량부, 특히 110~250 중량부이고, 상기 잉크 용제는 30~200 중량부, 특히 50~150 중량부가 혼합되며, 이러한 범위를 벗어나서 상기 PMMA 입자의 양이 과도하면 상기 PMMA 입자의 중첩에 의해 전체 광투과량이 저하되고, 부족한 경우에도 광확산 효과가 저하된다.With respect to 100 parts by weight of the PMMA particles, the ink binder is 100 to 300 parts by weight, in particular 110 to 250 parts by weight, the ink solvent 30 to 200 parts by weight, in particular 50 to 150 parts by weight is mixed, out of this range If the amount of the PMMA particles is excessive, the total light transmittance decreases due to the superposition of the PMMA particles, and the light diffusing effect is lowered even if the amount is insufficient.
한편, 상기 잉크 용제 100 중량부를 기준으로 할 때 130~250 중량부의 잉크 바인더, 즉 상기 에폭시 수지와 상기 폴리아미드 수지의 혼합물 130~250 중량부가 상기 잉크 용제 100 중량부에 대한 잉크 바인더로서 적용되나 이에 한정되는 것은 아니다.Meanwhile, based on 100 parts by weight of the ink solvent, 130 to 250 parts by weight of an ink binder, that is, 130 to 250 parts by weight of the mixture of the epoxy resin and the polyamide resin, is applied as an ink binder with respect to 100 parts by weight of the ink solvent. It is not limited.
상기 에폭시 수지와 상기 폴리아미드 수지을 혼합하여 그 혼합물을 잉크바인더로 적용한 잉크의 경화는 잉크 기술분야에서 공지된 것이나, 본 발명에서는 보다 구체적으로, 상기 잉크 바인더에서 상기 에폭시 수지와 상기 폴리아미드 수지의 혼합 비율을 결정하는 일 예로, 당량비를 이용한 에폭시 수지와 폴리아미드 수지의 혼합방식을 개시한다.Curing of the ink in which the epoxy resin and the polyamide resin are mixed and the mixture is applied as an ink binder is known in the ink art, but in the present invention, more specifically, the epoxy resin and the polyamide resin are mixed in the ink binder. As an example of determining the ratio, a method of mixing an epoxy resin and a polyamide resin using an equivalent ratio is disclosed.
예를 들면, EEW(Epoxide Equivalent Weight)=200(g/eq) 값을 가지는 에폭시 수지 100 중량부에 대하여 AHEW(Amine Hydrogen Equivalent Weight)=24(g/eq) 값을 가지는 폴리아미드 수지 12 중량부가 혼합될 수 있으나 이에 한정되는 것은 아니고 실험적으로 다양한 범위의 비율로 상호 혼합될 수 있다. For example, 12 parts by weight of polyamide resin having a value of Amine Hydrogen Equivalent Weight (AHEW) = 24 (g / eq) relative to 100 parts by weight of an epoxy resin having an EEW (Epoxide Equivalent Weight) = 200 (g / eq) value It may be mixed, but is not limited thereto, and may be mixed with each other in a range of ratio experimentally.
이때, 상기 에폭시 수지는 전술한 바와 같이 상기 폴리아미드 수지와 혼합되면 일정시간이 경과된 후 자연 경화되기 때문에 광확산 잉크 조성물의 스크린 인쇄 작업시 혼합하여 사용하는 것이 바람직하다. At this time, when the epoxy resin is mixed with the polyamide resin as described above, after a predetermined time has elapsed, it is preferable to mix and use during the screen printing operation of the light diffusion ink composition.
일 예로, 상기 에폭시 수지와 폴리아미드 수지 중 어느 하나가 포함되지 않은 상태의 광확산 잉크 조성물을 제조한 후 상기 광확산 잉크 조성물의 스크린 인쇄 작업 직전에 상기 에폭시 수지와 폴리아미드 수지 중 상기 광확산 잉크 조성물에 포함되지 않은 물질을 최종적으로 혼합하여 본 발명에 따른 광확산 잉크 조성물을 제조하고, 상기 최종 광확산 잉크 조성물을 이용하여 스크린 인쇄 작업을 수행할 수 있다. For example, after the light diffusion ink composition is prepared without any one of the epoxy resin and the polyamide resin, the light diffusion ink of the epoxy resin and the polyamide resin is immediately before the screen printing operation of the light diffusion ink composition. The light diffusion ink composition according to the present invention may be prepared by finally mixing materials not included in the composition, and screen printing may be performed using the final light diffusion ink composition.
본 발명에 따른 광확산 잉크 조성물 색상 구현을 위한 색상안료를 더 포함하여 구성될 수도 있다. 상기 색상안료로는 투명 색상안료가 사용된다.It may be configured to further include a color pigment for implementing the light-diffusing ink composition color according to the present invention. As the color pigment, a transparent color pigment is used.
상기 색상 안료로는; 아조계 안료, 프탈로시아닌(Phthalocyanine) 안료, 안트라퀴논계(Anthraquinone) 안료, 티오인디고계(Thioindigo) 안료, 페린온계(Perinone) 안료, 페릴렌계(Perylene) 안료, 퀴나크리돈계(Quninacridone) 안료, 그리고 투명성 색상안료 등이 있으며, 상기 광확산 잉크 조성물은 이러한 색상안료들 중 어느 1종 이상을 포함할 수 있다.As said color pigment; Azo pigments, Phthalocyanine pigments, Anthraquinone pigments, Thioindigo pigments, Perinone® pigments, Perylene pigments, Quinacridone pigments, and transparency Color pigments, and the like, and the light diffusion ink composition may include any one or more of these color pigments.
상기 아조계 안료로는, 시.아이. 피그먼트 레드(C.I. Pigment Red) 3, 5, 48:1, 48:2,48:3, 48:4, 53:1, 53:2, 57:1, 시. 아이. 피그먼트 엘로우 1, 3, 83, 시.아이. 피그먼트 오렌지 16, 13 등이 있고; 상기 프탈로시아닌 안료로는 시.아이. 피그먼트 블루(C.I. Pigment Blue) 15, 15:3, 17과 시.아이. 피그먼트 그린(C.I. Pigment Green) 7 등이 있다.As said azo pigment, it is C.I.
그리고 상기 안트라퀴논계 안료의 예로는, 축합다환계 유기안료로 인단트렌 블루 시.아이. 피그먼트 블루60(Indanthrene Blue C.I. Pigment Blue 60)이 있고; 상기 티오인디고계 안료로는, 티오인디고 마젠타 시.아이. 피그먼트 바일롯38(Thioindigo Magenta C.I. Pigment Vilot38) 등이 있으며; 상기 페린온계 안료의 예로는, 페린온 오렌지 시.아이. 피그먼트 오렌지43(Perinone Orange C.I. Pigment Orange 43)이 있다. And examples of the anthraquinone pigments are condensed polycyclic organic pigments indanthrene blue C.I. Pigment Blue 60 (Indanthrene Blue C. I. Pigment Blue 60); Examples of the thioindigo pigments include thioindigo magenta C. eye. Pigment bylot 38 (Thioindigo Magenta C.I. Pigment Vilot 38); Examples of the perinone pigments include perinone orange C.I. Pigment Orange 43 (Perinone Orange C. I. Pigment Orange 43).
상기 페릴렌계 안료의 예로는 페릴렌 마룬 시.아이. 피그먼트 레드179(Perylene Maroon C.I. Pigment Red 179)가 있으며; 상기 퀴나크리돈계 안료의 예로는 퀴나크리돈 레드 시.아이. 피그먼트 바이올렛 19(Quninacridone Red C.I. Pigment Violet 19)이 있고; 상기 투명성 색상안료의 예로는, 시.아이. 피그먼트 레드 177(C.I. Pigment R 177(red))과, 시.아이. 피그먼트 그린 36(CI Pigment G36(green))과, 시.아이. 피그먼트 블루 15:6(C.I. pigment B15:6(blue))과, 시.아이. 피그먼트 옐로우 139(C.I. Pigment Y139(yellow))와, 시.아이. 피그먼트 바이올렛 23(CI Pigment V23(violet)) 등이 있다.Examples of the perylene-based pigments are perylene maroon C. eye. Pigment Red 179 (Perylene Maroon C. I. Pigment Red 179); Examples of the quinacridone pigments include quinacridone red C. eye. Pigment violet 19 (Quninacridone Red C.I. Pigment Violet 19); Examples of the transparent color pigments, S.I. Pigment Red 177 (C.I. Pigment R 177 (red)) and C.I. Pigment green 36 (CI Pigment G36 (green)) and C.I. Pigment Blue 15: 6 (C.I. pigment B15: 6 (blue)) and C.I. Pigment Y139 (yellow) and C.I. Pigment violet 23 (CI Pigment V23 (violet)).
상기 색상안료로서 상술한 색상안료들이 1종 이상이 선택될 수 있으며, 상술한 색상안료들 중에 서로 다른 색의 색상 안료가 혼합되는 경우에는 혼합색이 구현될 수 있다.One or more of the above-described color pigments may be selected as the color pigments, and mixed colors may be implemented when color pigments of different colors are mixed among the color pigments described above.
여기서, 상기 색상안료는 상기 PMMA 입자 100 중량부에 대하여 상기 색상안료는 5~50 중량부가 혼합된다. 보다 상세하게는 상기 PMMA 입자 100 중량부에 대하여 상기 색상안료는 15~40 중량부가 혼합된다. 종래에는 도광패널에서 출사되는 빛의 색이 광원의 색에만 의존하였으나, 상기 색상안료가 본 발명에 따른 광확산 잉크 조성물에 포함됨에 따라 다양한 색의 빛을 출사하는 도광패널을 제조할 수 있다.Here, the color pigment is 5 to 50 parts by weight of the color pigment is mixed with respect to 100 parts by weight of the PMMA particles. More specifically, the color pigment is mixed with 15 to 40 parts by weight based on 100 parts by weight of the PMMA particles. Conventionally, although the color of light emitted from the light guide panel depends only on the color of the light source, the color pigment is included in the light diffusion ink composition according to the present invention, so that the light guide panel may emit light of various colors.
그리고 유색 및/또는 무색의 광확산 잉크 조성물을 사용하여 상기 도광패널, 보다 상세하게는 도광부재의 표면에 인물이나 사물 기타 로고 등의 다양한 디스플레이 이미지를 기설정된 디자인에 따라 구현할 수 있고, 상기 도광패널에 광원의 빛이 조명됨에 따라 상기 도광패널이 상기 이미지를 크리스탈 광패턴으로 직접적으로 출력할 수 있게 되어 심미감과 디자인성이 향상되고, 종래의 이미지 시트를 생략할 수 있으므로 부품이 단순화되고 투명한 도광부재로 깨끗하고 맑게 표현된 장치 기타 물건, 예를 들면 광고나 간판 기타 장식 등을 위한 디스플레이 장치의 구현이 가능해진다.In addition, various display images, such as a person, an object, and a logo, may be implemented on the surface of the light guide panel, more specifically, on the surface of the light guide member by using a colored and / or colorless light diffusion ink composition, and the light guide panel may be implemented. As the light of the light source is illuminated on the light guide panel, the light guide panel can directly output the image as a crystal light pattern, thereby improving aesthetics and design, and omitting a conventional image sheet, thereby simplifying components and transparent light guide members. As a result, it is possible to implement display devices for devices and other objects, such as advertisements, signs, and decorations, which are clearly and clearly expressed.
도 3 및 도 4를 참조하면, 상기 디스플레이 유닛은 상기 도광패널(110)과 광원(120)을 포함하여 구성되며, 상기 도광패널(110)은 상기 도광부재(111)와 광확산층(112)을 포함하여 구성된다. 여기서 상기 광확산층(112)은 상기 광원(120)의 빛을 받아서 크리스탈 광패턴의 디스플레이 이미지(112a)를 상기 도광패널(110)의 전방으로 출력한다.3 and 4, the display unit includes the
다시 말해서 상기 도광패널(110)은 상기 광원(120)에 의해 발광되는 상기 소정 디자인의 디스플레이 이미지(112a)를 가지며, 상기 광확산 잉크 조성물이 상기 디스플레이 이미지(112a)의 디자인에 맞춰서 상기 도광부재(111)의 표면, 보다 상세하게는 상기 도광부재의 배면에 인쇄되어 상기 광확산층(112)을 형성함으로써 상기 디스플레이 이미지(112a)가 크리스탈 광패턴, 즉 크리스탈 느낌으로 구현될 수 있다.In other words, the
따라서 상기 광확산층(112)이 상기 디스플레이 이미지의 디자인의 형상 그대로 상기 도광부재(111)의 표면에 일체로 형성될 수 있으며, 이러한 경우 상기 광확산층(112)의 외관과 상기 디스플레이 이미지(112a)의 외관이 동일하게 된다. 더 나아가 상기 디스플레이 이미지(112a)는 컬러 이미지(Color Image)로 구현될 수도 있는데, 상기 디스플레이 이미지(112a) 중 컬러로 구현되는 부분에 인쇄되는 광확산 잉크 조성물은 상기 색상안료를 포함하게 된다. 따라서 본 발명에 따른 도광패널의 광확산층은 단색 또는 다색의 컬러 디스플레이 이미지를 구현할 수도 있다. 물론 상기 디스플레이 이미지의 일부만이 본 발명에 따른 광확산 잉크 조성물에 의해 인쇄되는 광확산층으로 구성될 수도 있다. Therefore, the
상기 디스플레이 이미지(112a)는 로고나 광고물이나 사진이나 문양이나 표식이나 문자나 기호 등을 포함할 수 있으며, 상기 광확산 잉크 조성물은 상기 도광부재(111)의 표면에 기 설정된 디자인대로 인쇄되고, 상기 광확산 잉크 조성물의 인쇄에 의해 상기 도광부재(111)의 표면에 상기 디자인에 따라 형성되는 상기 광확산층(112)은 상기 로고나 광고물이나 사진이나 문양이나 표식이나 문자나 기호 등의 형상을 갖는다. The
보다 상세하게 설명하면, 본 발명에 있어서 상기 디스플레이 이미지(112a)는 광확산 잉크의 재질로서, 상기 광확산 잉크 조성물이 상기 도광부재(111)의 표면에 코팅(예를 들면 실크 스크린 인쇄법에 의한 인쇄)되어 상기 광확산층(112)을 형성하며, 상기 광확산층(112)이 상기 광원(120)의 빛을 산란/반사/굴절시켜서 변환함으로써 상기 도광패널(110)의 전방으로 상기 디스플레이 이미지(112a)를 크리스탈 면광원으로 출사한다.In more detail, in the present invention, the
상기 광원(120)은 전력 소모성을 고려하여 백색 LED 및/또는 유색 LED가 적용될 수 있고, 상기 도광패널(110)의 측면 모서리를 따라 복수개의 발광램프(121), 즉 LED들이 배치되어 상기 조명광을 출사하며, 상기 발광램프(121)들은 동시에, 순차적으로 또는 교대로 발광되도록 구성될 수 있다. 그리고 상기 광원(120)의 빛과 상기 광확산층(112)의 색상이 혼합되어 혼합색이 구현될 수 있다. The
보다 상세하게 설명하면, 상기 광원(120)의 조명광은 상기 도광 패널(110)의 일측 모서리(입사부)를 통해 입사되며, 상기 광원(120)에서 출사되는 상기 조명광은 상기 도광패널(110)을 투과하여 진행하면서 상기 광확산층(112)에 도달하고 상기 광확산층(112)은 상기 광원에서 출사되는 빛의 방향을 변환시켜 상기 디스플레이 이미지(112a)를 상기 도광패널(110)의 전방으로 출사한다.In more detail, the illumination light of the
이때 상기 광확산 잉크 재질의 광확산층(112)은 상기 도광부재(110)를 통해 투과되는 상기 광원의 빛(조명광)을 산란/반사/굴절 등의 과정을 통해 면광원으로 변환시키고, 상기 광확산층(112)은 기설정된 상기 디스플레이 이미지의 디자인에 따라 상기 도광부재(111)에 인쇄되므로, 상기 도광패널(110)의 전방으로 상기 디스플레이 이미지(125)가 크리스탈 광패턴으로 출사된다. In this case, the
결론적으로 본 발명에 따르면 상기 광원(120)에서 출사되는 조명광이 상기 도광패널(110)의 광확산층(112)에 의해 상기 디스플레이 이미지(125)로 변환되어 크리스탈 광 이미지의 형태로 출사된다. In conclusion, according to the present invention, the illumination light emitted from the
본 발명에 따르면, 상기 도광패널(110)에 광원(120)의 빛이 조명됨에 따라 상기 도광패널이 상기 디스플레이 이미지를 크리스탈 광패턴으로 구현할 수 있게 되어 심미감과 디자인성이 향상되고, 종래의 이미지 시트를 생략할 수 있으므로 부품이 단순화되고 투명한 도광부재로 깨끗하고 맑게 표현된 장치 기타 물건, 예를 들면 광고나 간판 기타 장식 등을 위한 디스플레이 장치의 구현이 가능해진다.According to the present invention, as the light of the
예를 들어 상기 도광부재(111)의 표면에 기업의 로고, 광고물이나 인물 기타 사물 등의 이미지가 소정의 디자인에 맞춰서 상기 광확산 잉크 조성물에 의해 인쇄된 경우에, 상기 도광패널(110)은 상기 광원(120)의 빛을 받아 심미감이 뛰어난 디스플레이 이미지의 표현을 구현할 수 있다.For example, when an image of a company logo, an advertisement, a person, or an object is printed on the surface of the
상기 도광부재의 예로는 플라스틱 또는 유리 소재의 플레이트가 있으나, 본 실시에서는 유리 소재의 기판 또는 필름에 본 발명에 따른 광확산 잉크 조성물이 실크 스크린 인쇄(Silk Screen Printing) 기법으로 인쇄되어 상기 광확산층(광확산 잉크층)을 형성하며, 상기 광확산 잉크층이 소정의 디자인, 즉 기설정된 디자인의 이미지에 따라 인쇄되어 광고, 간판, 장식 등의 디스플레이 패널을 구현할 수 있다.Examples of the light guiding member include a plate made of plastic or glass, but in the present embodiment, the light diffusion ink composition according to the present invention is printed on a glass substrate or film by silk screen printing to obtain the light diffusion layer ( Light diffusion ink layer), and the light diffusion ink layer is printed according to an image of a predetermined design, that is, a predetermined design, thereby implementing a display panel such as an advertisement, a signboard, or a decoration.
상기 디스플레이 이미지(112a)를 구현하는 상기 광확산층(112)은 복수 부분으로 구획되어 부분별로 다른 색상으로 구성될 수도 있고 다른 색상의 광원에 의해 조명될 수도 있다. The
한편, 상기 광확산 잉크 조성물은 첨가제, 예를 들면 소포제와 분산제와 레벨링제 등의 첨가제를 1종 이상 포함할 수 있다. 상기 첨가제는 상기 PMMA 비드 100중량부에 대하여 2~20 중량부, 특히 2.5~10 중량부가 포함되나 이에 한정되는 것은 아니다.Meanwhile, the light diffusion ink composition may include one or more additives such as an antifoaming agent, a dispersing agent, and a leveling agent. The additive includes but is not limited to 2 to 20 parts by weight, in particular 2.5 to 10 parts by weight based on 100 parts by weight of the PMMA beads.
본 실시예에서 개시되는 광확산 잉크 조성물의 구체적인 예는, 잉크 바인더로서 에폭시 수지와 폴리아미드 수지의 혼합물 40~50중량%, 평균입도 6㎛~50㎛, 특히 15㎛~20㎛의 PMMA 비드를 갖는 광확산제 20~35중량%, 케톤류와 에스테르류와 에테르류와 탄화수소계류와 글리콜에테르계 용제 중 1종 이상을 포함하는 잉크 용제 20~30중량%, 기타 첨가제 1~2중량%, 색상안료 2~10중량%로 제조될 수 있다.
Specific examples of the light-diffusion ink composition disclosed in this embodiment include PMMA beads having a mixture of epoxy resin and polyamide resin of 40 to 50% by weight, average particle size of 6 µm to 50 µm, particularly 15 µm to 20 µm. 20 to 35% by weight of light diffusing agent, 20 to 30% by weight of ink solvent containing one or more of ketones, esters, ethers, hydrocarbons and glycol ether solvents, 1-2% by weight of other additives, color pigments It may be prepared in 2 to 10% by weight.
이하 본 발명에 따른 광확산 잉크 조성물의 구체적인 실시예를 설명하며, 하기의 실시예는 본 발명을 예시한 것에 불과하며 본 발명에 하기 실시예에 한정되는 것은 아니다.
Hereinafter, specific examples of the light diffusion ink composition according to the present invention will be described, and the following examples are merely illustrative of the present invention and are not limited to the following examples.
[실시예 1 및 실시예 2의 제조]Preparation of Example 1 and Example 2
다음과 같이 [표 1]의 성분과 함량대로 실시예 1과 실시예 2에 따른 광확산 잉크 조성물 및 비교예 1과 비교예 2에 따른 광확산 잉크 조성물을 제조하고, 이러한 광확산 잉크 조성물을 두께 1cm의 유리 재질 도광부재(도광판)에 인쇄하여 도광패널을 제조하였다.The light-diffusion ink composition according to Example 1 and Example 2 and the light-diffusion ink composition according to Comparative Example 1 and Comparative Example 2 were prepared according to the components and contents of [Table 1] as follows. A light guide panel was manufactured by printing on a glass light guide member (light guide plate) of 1 cm.
1Example
One
2Example
2
1Comparative Example
One
2Comparative Example
2
독일 BYK사의 제품Silicone Defoamer
BYK of Germany
Tego 사 제품 Silicone Leveling Agent
Tego Products
독일 BYK 사의 제품 Acrylic Dispersant
BYK's products in Germany
(평균입도 2㎛)Silicon bead
(
전술한 바와 같이, 광확산 잉크 조성물의 잉크 바인더에서 에폭시 수지와 혼합되는 폴리아미드 수지의 혼합 비율은 에폭시 수지와 혼합되어 상기 에폭시 수지를 경화시킬 수 있는 정도이면 자유롭게 결정할 수 있는데, 보다 구체적으로는 당량비를 이용하여 결정할 수 있으며, 예를 들면 EEW(Epoxide Equivalent Weight)=200(g/eq) 값을 가지는 에폭시 수지 100g을 경화시키기 위해 AHEW(Amine Hydrogen Equivalent Weight)=24(g/eq) 값을 가지는 폴리아미드 수지 12g을 혼합하며, 본 실시예에서는 위 [표 1]에서와 같이 EEW(g/eq)=190~220의 에폭시 수지와 AHEW(g/eq)=100~120의 고이미다졸라인(high-imidazoline) 폴리아미드 수지를 혼합하여 잉크 바인더를 구성하는 경우를 개시하며, 이때 당량비를 고려하면 상기 에폭시 수지와 상기 폴리아미드 수지는 상기 광확산 잉크 조성물의 전체 비율 중 각각 30 중량%와 15 중량%의 함량을 갖도록 혼합될 수 있으나 이에 한정되는 것은 아니다.
As described above, the mixing ratio of the polyamide resin mixed with the epoxy resin in the ink binder of the light diffusion ink composition can be freely determined as long as it can be mixed with the epoxy resin to cure the epoxy resin. For example, to cure 100 g of an epoxy resin having an EEW (Epoxide Equivalent Weight) = 200 (g / eq) value, Amine Hydrogen Equivalent Weight (AHEW) = 24 (g / eq) value 12 g of the polyamide resin is mixed, and in this embodiment, the epoxy resin of EEW (g / eq) = 190-220 and the high imidazole line of AHEW (g / eq) = 100-120 as shown in [Table 1]. A case of constituting an ink binder by mixing a high-imidazoline polyamide resin, wherein the epoxy resin and the polyamide resin are each of the total ratio of the light diffusion ink composition in consideration of the equivalent ratio. It may be mixed to have a content of 30% by weight and 15% by weight, but is not limited thereto.
그리고 위 실시예 1~2와 비교예 1~2를 색차계 및 헤이즈 측정기(HAZE METER)를 사용하여 L, a, b값 및 전체 광투과율, 그리고 HAZE 값을 측정하여 아래 [표 2]에 나타내었다. [표 2]의 측정값은 광원이 켜지기 전의 수치이며, 전체광투과율은 40 이상이고 L 값이 50 이하이고 HAZE 값이 60 이상일 때 광원이 켜진후 크리스탈 형상이 발휘되며, 보다 바람직하게는 전체 광투과율은 50 이상이고 L 값이 40 이하이고 HAZE 값이 75이상이 좋다.
And Examples 1 to 2 and Comparative Examples 1 to 2 by using a color difference meter and a haze meter (HAZE METER) to measure the L, a, b value and total light transmittance, and HAZE value are shown in [Table 2] below It was. The measured value of [Table 2] is the value before the light source is turned on, the crystal shape is exhibited after the light source is turned on when the total light transmittance is 40 or more, the L value is 50 or less and the HAZE value is 60 or more, more preferably, the whole The light transmittance is 50 or more, the L value is 40 or less, and the HAZE value is 75 or more.
(Air)air
(Air)
1Example
One
2Example
2
1Comparative Example
One
2 Comparative Example
2
305 Mesh screen 인쇄 건조후 측정
측정장비 CM-2600D (색차계) 미놀타 Glass LGP (1cm thick)
305 Mesh screen Print After drying
Measuring Equipment CM-2600D (Color Meter) Minolta
광투과율) Tt (full
Light transmittance)
305 Mesh screen 인쇄 건조후 측정
측정장비 HAZE Meter (SUGA, Japan) Glass LGP (1cm thick)
305 Mesh screen Print After drying
Measuring Equipment HAZE Meter (SUGA, Japan)
상기와 같이 본 발명에 따른 바람직한 실시예를 살펴보았으며, 앞서 설명된 실시예 이외에도 본 발명이 그 취지나 범주에서 벗어남이 없이 다른 특정 형태로 구체화 될 수 있다는 사실은 해당 기술에 통상의 지식을 가진 이들에게는 자명한 것이다.As described above, according to the present invention, the present invention can be embodied in other specific forms without departing from the spirit and scope of the present invention. It is obvious to them.
그러므로, 상술된 실시예는 제한적인 것이 아니라 예시적인 것으로 여겨져야 하고, 이에 따라 본 발명은 상술한 설명에 한정되지 않고 첨부된 청구항의 범주 및 그 동등 범위 내에서 변경될 수도 있다.Therefore, the above-described embodiments should be regarded as illustrative rather than restrictive, and thus, the present invention is not limited to the above description and may be modified within the scope of the appended claims and their equivalents.
110: 도광패널 111: 도광부재(도광판)
112: 광확산층 112a: 디스플레이 이미지
120: 광원110: light guide panel 111: light guide member (light guide plate)
112:
120: light source
Claims (13)
에폭시 수지와 폴리아미드 수지 중 어느 하나를 포함하여 다른 하나와의 혼합에 의해 상기 광확산 잉크 조성물의 경화시키는 잉크 바인더;
크리스탈 광패턴의 구현을 위한 PMMA(Polymethylmethacrylte) 입자; 그리고
잉크 용제를 포함하는 광확산 잉크 조성물.A light diffusion ink composition which receives light from a light source and outputs a crystal light pattern;
An ink binder for curing the light diffusing ink composition by mixing any one of an epoxy resin and a polyamide resin;
PMMA (Polymethylmethacrylte) particles for the realization of the crystal light pattern; And
A light diffusing ink composition comprising an ink solvent.
상기 PMMA 입자는 평균 입도가 10㎛~50㎛인 PMMA 비드(Bead)인 것을 특징으로 하는 광확산 잉크 조성물.The method of claim 1,
The PMMA particles are light diffusion ink composition, characterized in that the PMMA beads (Bead) having an average particle size of 10㎛ ~ 50㎛.
상기 PMMA 비드는 평균 입도가 15㎛~20㎛인 것을 특징으로 하는 광확산 잉크 조성물.3. The method of claim 2,
The PMMA beads are light diffusion ink composition, characterized in that the average particle size of 15㎛ ~ 20㎛.
상기 잉크 바인더의 굴절율은 1.52이고, 상기 PMMA 입자는 굴절율이 1.49인 것을 특징으로 하는 광확산 잉크 조성물. The method of claim 1,
The refractive index of the ink binder is 1.52, the light diffusion ink composition, characterized in that the PMMA particles have a refractive index of 1.49.
상기 잉크 용제는, 케톤류와 에스테르류와 에테르류와 탄화수소계와 글리콜에테르계 유기용제로 이루어진 군에서 1종이상 선택되는 것을 특징으로 하는 광확산 잉크 조성물.The method of claim 1,
The ink solvent is a light diffusion ink composition, characterized in that at least one selected from the group consisting of ketones, esters, ethers, hydrocarbons and glycol ether organic solvents.
상기 PMMA 입자 100 중량부에 대하여, 상기 잉크 바인더는 110~250 중량부이고, 상기 잉크 용제는 50~150 중량부인 것을 특징으로 하는 광확산 잉크 조성물.The method of claim 1,
The ink binder is 110 to 250 parts by weight, and the ink solvent is 50 to 150 parts by weight based on 100 parts by weight of the PMMA particles.
상기 잉크 바인더는, 당량비로 상기 에폭시 수지와 상기 폴리아미드 수지의 혼합 함량을 결정하되, EEW(Epoxide Equivalent Weight)=200(g/eq) 값을 가지는 에폭시 수지 100 중량부에 대하여 AHEW(Amine Hydrogen Equivalent Weight)=24(g/eq) 값을 가지는 폴리아미드 수지 12 중량부가 혼합되는 것을 특징으로 하는 광확산 잉크 조성물.The method of claim 1,
The ink binder determines the mixed content of the epoxy resin and the polyamide resin in an equivalent ratio, but with respect to 100 parts by weight of epoxy resin having an EEW (Epoxide Equivalent Weight) = 200 (g / eq), Amine Hydrogen Equivalent 12) by weight of a polyamide resin having a Weight) value of 24 (g / eq) is mixed.
색상 구현을 위한 색상안료를 더 포함하는 광확산 잉크 조성물.The method of claim 1,
Light diffusion ink composition further comprising a color pigment for color implementation.
상기 색상안료는, 투명 색상안료인 것을 특징으로 하는 광확산 잉크 조성물.9. The method of claim 8,
The color pigment is a light diffusion ink composition, characterized in that the transparent pigment.
상기 색상안료는; 퀴나크리돈 레드 시.아이. 피그먼트 바이올렛 19(Quninacridone Red C.I. Pigment Violet 19)와, 시.아이. 피그먼트 레드 177(C.I. Pigment R 177(red))과, 시.아이. 피그먼트 그린 36(CI Pigment G36(green))과, 시.아이. 피그먼트 블루 15:6(C.I. pigment B15:6(blue))과, 시.아이. 피그먼트 옐로우 139(C.I. Pigment Y139(yellow))와, 시.아이. 피그먼트 바이올렛 23(CI Pigment V23(violet))으로 이루어진 군에서 1종이상 선택되는 것을 특징으로 하는 광확산 잉크 조성물.10. The method of claim 9,
The color pigments; Quinacridone Red C. I. Pignacridone Red CI Pigment Violet 19 and C.I. Pigment Red 177 (CI Pigment R 177 (red)) and C.I. Pigment green 36 (CI Pigment G36 (green)) and C.I. Pigment Blue 15: 6 (CI pigment B15: 6 (blue)) and C.I. Pigment yellow 139 (CI Pigment Y139 (yellow)) and C.I. Pigment violet 23 (CI Pigment V23 (violet)) Light diffusion ink composition, characterized in that at least one selected from the group consisting of.
상기 PMMA 입자 100 중량부에 대하여 상기 색상안료는 5~50 중량부가 혼합되는 것을 특징으로 하는 광확산 잉크 조성물.11. The method according to any one of claims 8 to 10,
The color pigment with respect to 100 parts by weight of the PMMA particles light diffusion ink composition, characterized in that 5 to 50 parts by weight is mixed.
상기 광확산 잉크층이 구비되는 유리 재질의 도광부재를 포함하여 구성되는 도광 패널.A light diffusion ink layer formed by the light diffusion ink composition according to any one of claims 1 to 10; And
A light guide panel including a light guide member made of glass provided with the light diffusion ink layer.
상기 도광부재는, 상기 광확산 잉크 조성물이 기결정된 디자인에 맞춰 상기 도광부재의 표면에 인쇄되어 상기 광확산 잉크층이 상기 도광부재의 표면에 형성하는 이미지를 가지며; 상기 도광부재로 광원의 빛이 출사됨에 따라 상기 도광부재의 전방으로 상기 크리스탈 광패턴의 이미지가 출력되는 것을 특징으로 하는 도광 패널.The method of claim 12,
The light guiding member has an image in which the light diffusing ink composition is printed on a surface of the light guiding member in accordance with a predetermined design so that the light diffusing ink layer is formed on the surface of the light guiding member; The light guide panel, characterized in that the image of the crystal light pattern is output to the front of the light guide member as the light of the light source is emitted to the light guide member.