KR20130063228A - Natural based adhesive composition containing poly latic acid emulsion - Google Patents
Natural based adhesive composition containing poly latic acid emulsion Download PDFInfo
- Publication number
- KR20130063228A KR20130063228A KR1020110129643A KR20110129643A KR20130063228A KR 20130063228 A KR20130063228 A KR 20130063228A KR 1020110129643 A KR1020110129643 A KR 1020110129643A KR 20110129643 A KR20110129643 A KR 20110129643A KR 20130063228 A KR20130063228 A KR 20130063228A
- Authority
- KR
- South Korea
- Prior art keywords
- emulsion
- polylactic acid
- parts
- weight
- adhesive composition
- Prior art date
Abstract
Description
본 발명은 천연소재 접착제 조성물에 관한 것으로, 더욱 상세하게는 천연소재로 폴리유산수지 에멀전을 함유하는 천연소재 접착제 조성물에 관한 것이다.The present invention relates to a natural adhesive composition, and more particularly to a natural adhesive composition containing a polylactic acid resin emulsion as a natural material.
인류는 삶의 질 향상을 위해 노력한 결과 많은 성과를 거두고 있으나, 그 결과에서 발생하는 환경오염으로 인해 삶의 질이 오히려 심각하게 위협을 받고 있는 실정이다. 환경 오염을 유발하는 물질 중 하나로 휘발성 유기화합물(volatile organic compounds, VOC's)과 유해대기오염물질(hazardous air pollutants, HAPs)이 있는데, 정책적으로 이들의 사용을 규제하고, 감축하는 것이 대두되고 있다.Mankind has achieved many results as a result of efforts to improve the quality of life, but the quality of life is rather seriously threatened by the environmental pollution resulting from it. Among the pollutants that cause environmental pollution are volatile organic compounds (VOC's) and hazardous air pollutants (HAPs), which are being regulated and reduced in policy.
또한, 석유화학계 원료의 지속적인 사용으로 말미암아 발생하는 이산화탄소도 환경 오염을 유발하는 대표적 물질인데, 이로 인해 지구 온난화 및 기상이변 등의 문제들이 발생하고 있다. In addition, carbon dioxide generated by the continuous use of petrochemical raw materials is also a representative material causing environmental pollution, which causes problems such as global warming and extreme weather.
이러한 문제들을 해결하기 위해 천연소재를 대체소재로 활용하여 제품에 응용하는 예가 미국, 유럽 등에서 활발히 전개되고 있고, 접착제 역시 천연소재의 대체가 절실히 필요한 품목 중 하나이다. In order to solve these problems, the application of natural materials as a substitute material to the product is actively developed in the United States, Europe, etc., and adhesive is also one of the items urgently needed to replace natural materials.
접착제 중 건축물이나 산업용품 등의 건축재료로 사용되는 합판, MDF, HDF 등의 섬유판에 PVC, PET, PP 필름을 접착할 때 사용하는 수성접착제도 천연소재로의 대체가 절실히 필요한 상황인데, 현재 국내에서는 석유화학계 제품이 거의 100% 사용되고 있다. Among the adhesives, water-based adhesives, which are used to bond PVC, PET, and PP films to plywood, MDF, and HDF, which are used as building materials for buildings and industrial products, are urgently needed to be replaced with natural materials. Almost 100% of petrochemical products are used.
한편, 종래 사용되는 접착제는 수성접착제라도 톨루엔(toluene), 자일렌(xylene) 등의 유기용제를 일정량 이상 포함하고 있어 장시간 작업시 유기용제에 의한 두통, 현기증, 구토 등의 유해성, 화재 위험성, 환경오염 등의 문제를 유발한다. On the other hand, conventionally used adhesives contain more than a certain amount of organic solvents such as toluene and xylene, even in an aqueous adhesive, and therefore, harmful effects such as headache, dizziness, vomiting, fire hazard, and environment caused by organic solvents during long working hours. It causes problems such as contamination.
또한, 오버레이 작업을 완료한 후에도 유기용제의 증발 현상이 지속하여, 2차 작업 공정 시에도 상기의 문제들의 여전히 발생하므로, 해결 대책이 더욱 절실히 요구되고 있는 실정이다.In addition, since the evaporation phenomenon of the organic solvent continues even after the completion of the overlay operation, the above problems still occur during the secondary work process, the situation is that the solution is more urgently required.
따라서, 휘발성 용제의 방출을 감소시켜 환경친화적이며, 천연소재를 포함함으로써 이산화탄소 발생문제를 개선하고, 생분해성을 부여하는 동시에 종래 접착제와 대등한 정도의 물성과 접착력을 가지는 접착제의 개발이 필요한 실정이다.Therefore, it is necessary to develop an adhesive that is environmentally friendly by reducing the release of volatile solvents, and includes natural materials to improve the carbon dioxide generation problem, impart biodegradability, and have adhesive properties similar to those of conventional adhesives. .
이에 본 발명이 목적은 유기용제 대신 천연소재를 포함하면서도 흐름성 및 접착성이 우수한 천연소재 함유 접착제 조성물을 개발하여 제공하는데 있다. Accordingly, an object of the present invention is to develop and provide a natural material-containing adhesive composition, including natural materials instead of organic solvents and excellent flowability and adhesion.
또한, 본 발명의 다른 목적은 종래 유기용제 및 석유화학계 원료 사용 시 야기되던 이산화탄소 방출, 오존 고갈, 가연성 등의 문제를 해결하여 환경친화적이고, 인체친화적이며, 시공 시 또는 시공 후 심한 약품냄새의 발생을 억제하여 별도의 환기가 요구되지 않아 작업 능률을 향상시킬 수 있는 천연소재 함유 접착제 조성물을 개발하여 제공하는 것이다.In addition, another object of the present invention is to solve the problems such as carbon dioxide emission, ozone depletion, flammability, etc. caused by the use of organic solvents and petrochemical raw materials in the prior art, environmentally friendly, human-friendly, severe chemical smell during construction or after construction By suppressing the additional ventilation is not required to develop and provide a natural material-containing adhesive composition that can improve the work efficiency.
상기 목적을 달성하기 위하여 본 발명은 폴리유산수지 에멀젼; 초산비닐에틸렌 에멀젼; 폴리우레탄수지 에멀젼 또는 아크릴수지 에멀젼; 및 필름 조막제; 를 포함하되, 폴리유산수지 에멀젼 및 초산비닐에틸렌 에멀젼의 혼합액 100 중량부에 대하여, 폴리우레탄수지 에멀젼 또는 아크릴수지 에멀젼 1 내지 30 중량부, 필름 조막제 1 내지 20 중량부의 비율로 포함하는 것을 특징으로 하는 폴리유산수지 에멀젼 함유 접착제 조성물을 제공한다. In order to achieve the above object, the present invention is a polylactic acid resin emulsion; Vinyl ethylene acetate emulsion; Polyurethane resin emulsions or acrylic resin emulsions; And film film forming agents; To include, but 100 parts by weight of the mixture of the polylactic acid resin emulsion and vinyl ethylene acetate emulsion, 1 to 30 parts by weight of polyurethane resin emulsion or acrylic resin emulsion, characterized in that it comprises a ratio of 1 to 20 parts by weight of film film forming agent It provides a polylactic acid emulsion-containing adhesive composition.
본 발명에 사용되는 폴리유산수지 에멀젼(poly lactic acid emulsion, PLA 에멀젼)은 본 발명 접착제 조성물에 주성분으로 사용된다. 폴리유산수지 에멀젼은 환경 친화적인 생분해성 수지인 폴리유산계 수지를 물에 분산한 제품이다. 상기 폴리유산수지 에멀젼은 식물로부터 유래한 수지를 원료로 하고 있으므로, 지구 온난화 방지에 기여할 수 있는데, 폴리유산수지를 고형분 함량으로 30~60%(w/v) 함유하는 것이 바람직하며, 최저 조막 온도가 0~200℃ 사이인 제품을 사용하는 것이 좋다.Polylactic acid emulsion (PLA emulsion) used in the present invention is used as a main component in the adhesive composition of the present invention. Polylactic acid emulsion is a product in which polylactic acid resin, an environmentally friendly biodegradable resin, is dispersed in water. Since the polylactic acid resin emulsion is made of a resin derived from a plant, it may contribute to preventing global warming, but it is preferable to contain 30 to 60% (w / v) of polylactic acid as a solid content, and the minimum film forming temperature. It is recommended to use a product that is between 0 ~ 200 ℃.
한편, 본 발명에 사용되는 상기 초산비닐에틸렌 에멀젼(ethylene vinyl acetate emulsion, EVA 에멀젼)은 본 발명 접착제 조성물에 주성분으로 사용된다. 초산비닐에틸렌 에멀젼은 에틸렌 모노머와 초산비닐 모노머를 공중합시켜 제조한다. 에틸렌 모노머와 초산비닐 모노머는 당업계에서 사용되는 통상의 모노머를 사용할 수 있음은 물론이며, 특히 에틸렌 모노머 10~20 중량% 및 초산비닐 모노머 80~90 중량%의 함량으로 공중합시키는 것이 좋다. 초산비닐에틸렌 에멀젼은 초산비닐에틸렌이 고형분 함량으로 40~60%(w/v) 함유되는 것이 바람직한데, 고형분 함량이 상기 범위 내일 경우, 용매를 사용하지 않고서도 우수한 흐름성과 작업성을 나타낼 수 있기 때문이다. On the other hand, the ethylene vinyl acetate emulsion (EVA emulsion) used in the present invention is used as a main component in the adhesive composition of the present invention. Vinyl acetate ethylene emulsion is prepared by copolymerizing ethylene monomer and vinyl acetate monomer. Of course, the ethylene monomer and the vinyl acetate monomer can be used in the conventional monomers used in the art, in particular, the copolymerization in the content of 10 to 20% by weight of ethylene monomer and 80 to 90% by weight of vinyl acetate monomer. The vinyl ethylene acetate emulsion preferably contains 40 to 60% (w / v) of vinyl ethylene acetate as a solid content. If the solid content is within the above range, it can exhibit excellent flowability and workability without using a solvent. Because.
본 발명에서 상기 초산비닐에틸렌은 상기 폴리유산수지 에멀젼 100 중량부에 대하여 10~300 중량부의 비율로 포함되는 것이 좋다. In the present invention, the vinyl ethylene acetate is preferably included in a ratio of 10 to 300 parts by weight based on 100 parts by weight of the polylactic acid emulsion.
한편, 본 발명에 사용되는 폴리우레탄수지 에멀젼은 PVC 필름 등에 접착력을 향상시키며, 내수성 및 내열성을 향상시키는 작용을 한다. 폴리우레탄수지 에멀젼은 폴리올과 이소시아네이트의 반응에 의해 제조된 수지로서, 알리파틱계와 아로마틱계 등을 사용할 수 있다. 폴리우레탄수지 에멀젼는 상기 폴리유산수지 에멀젼과 초산비닐에틸렌 에멀젼을 혼합한 혼합액 100 중량부에 대하여 1 내지 30 중량부의 비율로 첨가될 수 있다. 이때, 바람직하게는 5 내지 20 중량부의 비율로 첨가되는 것이 좋은데, 함량이 상기 범위일 경우, 접착제의 접착력을 현저히 증가시킬 수 있으며, 접착제의 내수, 내열성 및 내구성을 현저히 향상시키기 때문이다. On the other hand, the polyurethane resin emulsion used in the present invention improves the adhesive force, such as PVC film, and serves to improve the water resistance and heat resistance. The polyurethane resin emulsion is a resin produced by the reaction of a polyol and an isocyanate, and an aliphatic, aromatic, or the like can be used. The polyurethane resin emulsion may be added in a ratio of 1 to 30 parts by weight based on 100 parts by weight of the mixed solution of the polylactic acid emulsion and the vinyl ethylene acetate emulsion. At this time, preferably added in a ratio of 5 to 20 parts by weight, if the content is in the above range, it is possible to significantly increase the adhesive strength of the adhesive, because it significantly improves the water resistance, heat resistance and durability of the adhesive.
한편, 본 발명에서는 폴리우레탄수지 에멀젼 대신 아크릴수지 에멀젼을 사용할 수도 있다. 아크릴 에멀젼은 아크릴 모노머를 기재로 하고, 기능성 모노머를 혼합한 에멀젼으로, 중합 가능한 모노머는 아크릴산 에스테르(ester acrylate), 아크릴산(acrylic acid, CH2=CHCOOH), 에틸렌, 스틸렌, 아크릴레이트 또는 메타크릴레이트 등이 있는데, 특히 아크릴산 에스테르 또는 아크릴산을 사용하는 것이 가장 바람직하다. 구체적으로, 상기 아크릴산 에스테르로는 부틸 아크릴레이트 모노머(butyl acrylate monomer), 에틸 아크릴레이트 모노머(ethyl acrylate monomer), 에틸헥실 아크릴레이트 모노머(ethylhexyl acrylate monomer), 메틸 아크릴레이트 모노머(methyl acrylate monomer), 아크릴 아마이드, 엔 메티롤 아크릴 아마이드 등을 사용할 수 있다. Meanwhile, in the present invention, an acrylic resin emulsion may be used instead of the polyurethane resin emulsion. Acrylic emulsions are based on acrylic monomers, and functional monomers are mixtures. Polymerizable monomers are ester acrylates, acrylic acids (CH 2 = CHCOOH), ethylene, styrene, acrylates, or methacrylates. Etc., with acrylic acid esters or acrylic acid being most preferred. Specifically, the acrylate ester, butyl acrylate monomer (butyl acrylate monomer), ethyl acrylate monomer (ethyl acrylate monomer), ethylhexyl acrylate monomer (ethylhexyl acrylate monomer), methyl acrylate monomer (methyl acrylate monomer), acrylic Amide, enmethyrol acrylamide, etc. can be used.
아크릴수지 에멀젼은 상기의 초산비닐에틸렌 에멀젼과 함께 사용되어 접착제 조성물에 점착력을 부여하는 작용을 한다. 폴리우레탄수지 에멀젼 또는 아크릴수지 에멀젼은 상기 폴리유산수지에멀젼과 초산비닐에틸렌 에멀젼을 혼합한 혼합액 100 중량부에 대하여 1 내지 30 중량부의 비율로 혼합된다. The acrylic resin emulsion is used together with the vinyl acetate ethylene emulsion to act to impart adhesion to the adhesive composition. The polyurethane resin emulsion or the acrylic resin emulsion is mixed at a ratio of 1 to 30 parts by weight based on 100 parts by weight of the mixed solution of the polylactic acid emulsion and the vinyl ethylene acetate emulsion.
한편, 본 발명에 사용되는 필름 조막제(film forming agent)는 접착제의 접착력을 향상시키는 작용을 한다. 필름 조막제는 디에틸렌 글리콜 모노부틸 에테르 아세테이트(diethylene glycol monobutyl ether acetate), 에틸렌 글리콜 모노부틸 에테르 아세테이트(ethylene glycol monobutyl ether acetate), 에틸렌 글리콜 모노에틸 에테르 아세테이트(ethylene glycol monoethyl ether acetate), 에틸렌 글리콜 디아세테이트(ethylene glycol diacetate), n-헥실 카비톨(n-hexyl carbitol), 푸르푸릴 알콜(furfuryl alcohol) 또는 텍사놀(texanol)을 사용할 수 있다. On the other hand, the film forming agent (film forming agent) used in the present invention serves to improve the adhesive force of the adhesive. The film forming agent is diethylene glycol monobutyl ether acetate, ethylene glycol monobutyl ether acetate, ethylene glycol monoethyl ether acetate, ethylene glycol di Acetate (ethylene glycol diacetate), n-hexyl carbitol, furfuryl alcohol or texanol may be used.
한편, 본 발명에서는 필름 조막제로 비프탈레이트계 가소제를 사용할 수도 있다. 비프탈레이트계 가소제는 종래 환경 호르몬 방출의 문제점을 가지는 프탈레이트계 가소제를 사용하지 않음으로써 환경친화적이고, 인체친화적이며, 상기 초산비닐에틸렌 에멀젼과 함께 사용되어 큰 흐름성을 요구하는 작업 시에 접착제 조성물에 흐름성 및 점성을 부여하는 작용을 한다. 비프탈레이트계 가소제로는 디프로필렌 글리콜 디벤조에이트(dipropylen glycol dibenzoate, DP), 디에틸렌 글리콜 디벤조에이트(diethylene glycol dibenzoate, DE) 또는 이 성분들을 일정비율로 혼합한 혼합물(benzoplex) 등을 사용할 수 있다.In addition, in this invention, a nonphthalate plasticizer can also be used as a film film forming agent. Non-phthalate plasticizers are environmentally friendly, human-friendly, and are used together with the vinyl ethylene acetate emulsions in applications that require greater flowability by not using phthalate-based plasticizers that have conventional problems of environmental hormone release. It acts to impart flow and viscosity. As the non-phthalate plasticizer, dipropylene glycol dibenzoate (DP), diethylene glycol dibenzoate (DE), or a mixture of these components in a proportion (benzoplex) can be used. have.
상기 필름 조막제는 상기 폴리유산수지 에멀젼 및 초산비닐에틸렌 에멀젼의 혼합액 100 중량부에 대하여 1 내지 20 중량부의 비율로 첨가된다. 이때, 바람직하게는 초산비닐에틸렌 에멀젼 100 중량부 기준으로 0.1 내지 10 중량부 첨가되는 것이 좋은데, 함량이 상기 범위 내일 경우 접착제 조성물의 접착력을 향상시킬 수 있기 때문이다.The film forming agent is added at a ratio of 1 to 20 parts by weight based on 100 parts by weight of the mixed solution of the polylactic acid emulsion and the vinyl ethylene acetate emulsion. At this time, preferably 0.1 to 10 parts by weight is added based on 100 parts by weight of vinyl ethylene acetate emulsion, since the adhesive strength of the adhesive composition can be improved when the content is in the above range.
한편, 본 발명의 접착제 조성물은 필요에 따라 이소시아네이트 화합물을 추가로 포함할 수 있다. 이소시아네이트 화합물은 상기 접착제 조성물의 초기 접착강도를 향상시키고, 접착제 조성물이 적당한 점도와 경도를 유지함으로써 경화시간을 단축할 수 있으며, 가사시간(pot life)을 단축시켜 작업성을 현저히 향상시키는 작용을 한다. 이소시아네이트 화합물은 NCO기를 25~35% 함유한 것이 바람직하다. 이소시아네이트 화합물은 한 분자 중에 2개 이상의 이소시아네이트기를 함유하는 화합물인 것이 좋으며, 특히 무용제형 폴리머릭-디페닐메탄-4,4-디이소시아네이트 (polymeric-dipehenyl methane-4,4-diisocyanate, P-MDI) 화합물, 톨루엔-디이소시아테이트(toleuen-diisocyanate, TDI), 수소화TDI, 트리메틸 프로판-TDI(trimethyl propane-TDI), 트리페닐메탄-트리이소시아네이트(triphenylmethane- triisocyanate, TTI), 디페닐메탄-4,4-디이소시아네이트(diphenyl methane-4,4-diisocianate, MDI), 수소화MDI 또는 헥산메틸렌-디이소시아네이트(hexamethylene-diisocyanate, HDI) 등을 사용하는 것이 바람직하며, 더욱 바람직하게는 무용제형 폴리머릭-디페닐메탄-4,4-디이소시아네이트 (Polymeric-dipehenyl methane-4,4-diisocianate, MDI) 화합물을 사용하는 것이 좋다. Meanwhile, the adhesive composition of the present invention may further include an isocyanate compound as necessary. Isocyanate compound improves the initial adhesive strength of the adhesive composition, the adhesive composition can shorten the curing time by maintaining the appropriate viscosity and hardness, and serves to significantly improve the workability by reducing the pot life (pot life) . It is preferable that an isocyanate compound contains 25 to 35% of NCO groups. The isocyanate compound is preferably a compound containing two or more isocyanate groups in one molecule, and in particular, solvent-free polymeric-dipehenyl methane-4,4-diisocyanate (P-MDI). Compound, toluen-diisocyanate (TDI), hydrogenated TDI, trimethyl propane-TDI, triphenylmethane- triisocyanate (TTI), diphenylmethane-4,4 Diisocyanate (diphenyl methane-4,4-diisocianate (MDI), hydrogenated MDI or hexanemethylene-diisocyanate (HDI) and the like are preferably used, more preferably solvent-free polymeric-diphenyl Preference is given to using poly-dipehenyl methane-4,4-diisocianate (MDI) compounds.
이소시아네이트 화합물은 본 발명의 상기 초산비닐에틸렌 에멀젼 100 중량부에 대하여 1 내지 20 중량부로 포함되는 것이 바람직한데, 함량이 상기 범위 내인 경우, 접착제 조성물의 초기 접착강도를 현저히 향상시킬 수 있기 때문이다.The isocyanate compound is preferably included in an amount of 1 to 20 parts by weight based on 100 parts by weight of the vinyl ethylene acetate emulsion of the present invention, since the initial adhesive strength of the adhesive composition can be significantly improved when the content is within the above range.
상기와 같은 성분으로 이루어지는 본 발명의 접착제 조성물은 통상의 접착제 조성물에 사용되는 기능성 충진제, 분산제, 소포제, 안정제, 레벨링제, 점착부여제, 항균제, 증점제 또는 촉매 등의 첨가제를 추가로 포함할 수 있다.The adhesive composition of the present invention comprising the above components may further include additives such as functional fillers, dispersants, antifoaming agents, stabilizers, leveling agents, tackifiers, antibacterial agents, thickeners or catalysts used in conventional adhesive compositions. .
본 발명의 접착제는 PVC, PET, 또는 PP 필름과 PB(particle board), MDF(medium density fiber board), HDF(high density fiber board) 또는 합판의 접착시, 엣지(edge) 작업시 PVC 밴드와 목재의 접착시, 각종 모양지와 합판, MDF, 또는 HDF를 접착시 등 모두 적용할 수 있다.The adhesive of the present invention is a PVC band and wood when the PVC, PET, or PP film and PB (particle board), MDF (medium density fiber board), HDF (high density fiber board) or plywood, the edge (edge) At the time of gluing, various shapes such as plywood, MDF, or HDF may be applied.
본 발명의 접착제는 피착면에 30~100 g/㎡ 정도로 도포하는 것이 바람직하며, 접착제 도포후 필름을 접착하여 20~30분 이상 1~5 ㎏f/㎠(적재) 이상의 압력으로 압착한 후 양생하여 제작할 수 있다.It is preferable to apply the adhesive of the present invention to the surface to be adhered about 30 ~ 100 g / ㎡, and after curing the adhesive, the film is bonded and cured after pressing at a pressure of 1 ~ 5 ㎏f / ㎠ (loading) 20 to 30 minutes or more Can be produced.
본 발명에 따른 천연소재 함유 접착제 조성물은 용제를 사용하지 않고서도 흐름성 및 저온접착성이 우수할 뿐만 아니라, 종래 유기용제 및 석유화학계 원료 사용 시 야기되던 독성 방출, 오존 고갈, 가연성 등의 문제를 해결하여 환경친화적이고 인체 친화적이며, 이산화탄소 발생 문제를 해결하고, 생분해성을 부여한다. The natural material-containing adhesive composition according to the present invention not only has excellent flowability and low temperature adhesiveness without using a solvent, but also solves problems such as toxic emission, ozone depletion, and flammability caused by using conventional organic solvents and petrochemical raw materials. It is environmentally friendly and human-friendly, solves the carbon dioxide generation problem and gives biodegradability.
또한, 본 발명에 따른 천연소재함유 접착제 조성물은 접착강도, 내수 접착강도 및 저온접착력이 우수하고, 시공 시 또는 시공 후 심한 약품냄새의 발생을 억제하여 별도의 환기를 시키지 않고서도 작업자가 용이하게 작업할 수 있는 등 작업성이 우수한 효과가 있다.In addition, the natural material-containing adhesive composition according to the present invention is excellent in adhesive strength, water-resistant adhesive strength and low temperature adhesive strength, and easy for the worker to work without additional ventilation by suppressing the occurrence of severe chemical smell during or after construction There is an excellent workability such as can be.
이하, 본 발명의 내용을 하기 실시예 및 실험예를 통하여 더욱 상세히 설명하고자 한다. 다만, 본 발명의 권리범위가 하기 실시예에만 한정되는 것은 아니고, 그와 등가의 기술적 사상의 변형까지를 포함한다.
Hereinafter, the content of the present invention will be described in more detail through the following examples and experimental examples. However, the scope of the present invention is not limited to the following embodiments, and includes modifications of equivalent technical ideas.
[실시예 1]Example 1
고형분 함량이 50%(w/v)인 폴리유산수지 에멀젼 30 중량부에 대하여, 고형분 함량이 55%(w/v)인 초산비닐에틸렌 에멀젼(DA-613, Dairen사) 70 중량부, 폴리우레탄수지 에멀젼 2 중량부 및 필름 조막제(texanol, EASTMAN사) 0.1 중량부를 혼합하여 최종 고형분 함량이 50~60%(w/v)인 무용제형 접착제 조성물 1kg을 제조하였다.
70 parts by weight of vinyl acetate emulsion (DA-613, Dairen) having a solid content of 55% (w / v) to 30 parts by weight of a polylactic acid emulsion having a solid content of 50% (w / v), polyurethane 2 parts by weight of the resin emulsion and 0.1 parts by weight of a film forming agent (texanol, EASTMAN Co., Ltd.) were mixed to prepare 1 kg of a solvent-free adhesive composition having a final solid content of 50 to 60% (w / v).
[실시예 2][Example 2]
비프탈레이트계 필름 조막제로 텍사놀(texanol) 대신 벤조플렉스(Benzopflex 2088, VELSICOL사)를 사용한 것을 제외하고는 상기 실시예 1과 동일한 조성 및 방법으로 무용제형 접착제 조성물을 1kg을 제조하였다.
Except for using benzoflex (Benzopflex 2088, VELSICOL) instead of texanol as a non-phthalate-based film film forming agent 1kg of a solvent-free adhesive composition was prepared in the same composition and method as in Example 1.
[실시예 3][Example 3]
실시예 1의 조성에 NCO기를 30~33% 함유한 이소시아네이트 화합물 0.1 중량부를 추가로 첨가한 것을 제외하고는 상기 실시예 1과 동일한 조성 및 방법으로 무용제형 접착제 조성물 1kg을 제조하였다.
A solvent-free adhesive composition 1kg was prepared in the same composition and method as Example 1, except that 0.1 part by weight of an isocyanate compound containing 30 to 33% of NCO groups was further added to the composition of Example 1.
[비교예 1 내지 2][Comparative Examples 1 and 2]
비교예 1 내지 2로서 시중에 판매되는 PVC/목재 EVA 수성 접착제 2종{각 (주)오공의 용제포함 석유화학계 원료 전량 사용 PVC/목재 접착제 195P와 (주)오공의 용제 포함 석유화학계 원료 전량 사용 PVC/목재 접착제 195W}을 각각 사용하였다.
Two commercially available PVC / wood EVA water-based adhesives as Comparative Examples 1 and 2 {Use of total amount of petrochemical raw materials including solvents of Okubo Co., Ltd. PVC / wood adhesive 195 W} was used respectively.
[실험예 1][Experimental Example 1]
상기 실시예 1 내지 3 및 비교예 1 내지 2의 접착제를 사용하여 하기의 방법으로 냄새 및 작업성, 초기 접착성, 저온 필름조막성, 내열성, 내수성을 측정하고, 그 결과를 하기 표 1에 나타내었다. Using the adhesive of Examples 1 to 3 and Comparative Examples 1 and 2, the smell and workability, initial adhesiveness, low temperature film forming property, heat resistance, and water resistance were measured by the following methods, and the results are shown in Table 1 below. It was.
ㄱ) 냄새 및 작업성 - 실시예 1 내지 3 및 비교예 1 내지 2의 접착제에 대해 냄새가 전혀 없는 것을 5점, 약간 나는 것을 3점, 심하게 나는 것을 1점으로 하여 10 회 반복하여 평균치를 기재하였다. 또한, 작업성은 우수한 것을 5점, 보통인 것을 3점, 나쁜 것을 1점으로 하여 10 회 반복하여 평균치를 기재하였다.A) Odor and workability-For the adhesives of Examples 1 to 3 and Comparative Examples 1 and 2, the average value is repeated 10 times with 5 points of no odor, 3 points of slightly odor and 1 point of severe odor. It was. In addition, the workability was repeated 10 times with 5 points of excellent, 3 points of normal, and 1 point of bad, and described the average value.
ㄴ) 초기 접착성 - 상기 실시예 1 내지 3 및 비교예 1 내지 2의 접착제를 HDF와 PVC 필름의 부착 시 80 g/㎡의 두께로 도포하고, 30 초간 압착한 후, 24 시간 동안 양생시키고 180도 Peel strength를 측정하였다.B) Initial adhesiveness-the adhesive of Examples 1 to 3 and Comparative Examples 1 and 2 to a thickness of 80 g / ㎡ at the time of the adhesion of the HDF and PVC film After applying, pressing for 30 seconds, curing for 24 hours and measuring the Peel strength 180 degrees.
ㄷ) 저온 필름조막성 - 상기 실시예 1 내지 3 및 비교예 1 내지 2의 접착제를 깨끗한 슬라이드 유리 위의 한쪽 면에 넓게 도포하고, 4℃ 항온항습기에 넣어 4℃, 55~65%의 상대습도를 유지하면서 건조시켜 두께 0.1~0.3 ㎜의 균일한 피막을 형성하였다. 그 다음 상기 건조물이 균일한 연속 피막인지의 여부와 피막이 백탁되어 있는지의 여부를 육안으로 관찰하여 측정하였다.C) Low temperature film forming property-The adhesives of Examples 1 to 3 and Comparative Examples 1 and 2 are widely applied on one surface on a clean slide glass, and placed in a 4 ° C constant temperature and humidity chamber at 4 ° C and 55-65% relative humidity. Drying was carried out to form a uniform coating having a thickness of 0.1 to 0.3 mm. Then, it was measured by visually observing whether the dried product was a uniform continuous coating and whether the coating was cloudy.
ㄹ) 저온 접착성 - 상기 실시예 1 내지 3 및 비교예 1 내지 2의 접착제를 무연마형 HDF와 PVC 필름의 부착 시 80 g/㎡의 두께로 도포하고 30초간 압착한 후, 4℃ 항온항습기에 넣어 4℃, 55~65%의 상대습도를 유지하면서 건조하였다. 그 다음 상기 건조물이 균일한 연속 피막인지의 여부와 피막이 백탁되어 있는지 여부를 육안으로 관찰하여 측정하였다.D) low temperature adhesiveness-the adhesive of Examples 1 to 3 and Comparative Examples 1 and 2 to a thickness of 80 g / ㎡ in the adhesion of the abrasive-free HDF and PVC film After coating and pressing for 30 seconds, the resultant was placed in a 4 ° C. constant temperature and humidity cabinet and dried while maintaining a relative humidity of 4 ° C. and 55% to 65%. Then, it was measured by visually observing whether the dried product was a uniform continuous coating and whether the coating was cloudy.
ㅁ) 내수성 - 상기 실시예 1 내지 3 및 비교예 1 내지 2의 접착제를 25℃, 55~65%의 조건에서 7일 동안 양생시킨 후, 30℃의 물에 4시간 동안 침지시킨 후, 180도 Peel strength를 측정하였다.
ㅁ) Water resistance-After curing the adhesive of Examples 1 to 3 and Comparative Examples 1 to 2 for 7 days at 25 ℃, 55 ~ 65% conditions, after immersed in water of 30 ℃ for 4 hours, 180 degrees Peel strength was measured.
(시편 파괴율)Low temperature adhesive
Specimen Destruction Rate
본 발명에 따른 실시예 1 내지 3의 접착제는 비교예 1 내지 2와 같이 유기용제를 함유하는 석유화학계 접착제와 비교하여 독한 약품 냄새를 현저히 감소시킬 수 있을 뿐만 아니라, 초기 접착력, 저온 필름조막성, 저온 접착력, 내수성이 우수함을 확인할 수 있었다. The adhesives of Examples 1 to 3 according to the present invention can not only significantly reduce the odor of chemicals compared to petrochemical adhesives containing organic solvents as in Comparative Examples 1 to 2, but also have an initial adhesive strength, low temperature film forming properties, It was confirmed that the low temperature adhesive strength and water resistance is excellent.
또한, 본 발명에 따른 실시예 1 내지 3의 접착제는 비교예 1 내지 2의 접착제와 비교하여 점도 변형과 흐름성을 조절하여 작업성 또한 우수함을 알 수 있었다.In addition, it can be seen that the adhesives of Examples 1 to 3 according to the present invention are also excellent in workability by adjusting the viscosity deformation and flowability as compared with the adhesives of Comparative Examples 1 to 2.
Claims (7)
폴리유산수지 에멀젼 및 초산비닐에틸렌 에멀젼의 혼합액 100 중량부에 대하여, 폴리우레탄수지 에멀젼 또는 아크릴수지 에멀젼 1 내지 30 중량부, 필름 조막제 1 내지 20 중량부의 비율로 포함하는 것을 특징으로 하는 폴리유산수지 에멀젼 함유 접착제 조성물.Polylactic acid emulsions; Vinyl ethylene acetate emulsion; Polyurethane resin emulsions or acrylic resin emulsions; And film film forming agents; Including but not limited to:
A polylactic acid resin comprising 1 to 30 parts by weight of a polyurethane resin emulsion or an acrylic resin emulsion and 1 to 20 parts by weight of a film film forming agent, based on 100 parts by weight of a mixed solution of a polylactic acid resin emulsion and a vinyl ethylene acetate emulsion. Emulsion-containing adhesive composition.
상기 초산비닐에틸렌은,
상기 폴리유산수지 에멀젼 100 중량부에 대하여 10~300 중량부의 비율로 포함되는 것을 특징으로 하는 폴리유산수지 에멀젼 함유 접착제 조성물.The method of claim 1,
The vinyl ethylene acetate,
The polylactic acid resin emulsion-containing adhesive composition, characterized in that contained in a ratio of 10 to 300 parts by weight based on 100 parts by weight of the polylactic acid resin emulsion.
상기 폴리유산수지 에멀젼은,
폴리유산수지가 고형분 함량으로 30~60%(w/v) 함유되어 있는 것을 특징으로 하는 풀리유산수지 에멀젼 함유 접착제 조성물.The method according to claim 1 or 2,
The polylactic acid emulsion,
A polylactic acid resin-containing emulsion composition, characterized in that the polylactic acid resin is contained in a solid content of 30 to 60% (w / v).
상기 초산비닐에틸렌 에멀젼은,
초산비닐에틸렌이 고형분 함량으로 40~60%(w/v) 함유되어 있는 것을 특징으로 하는 폴리유산수지 에멀젼 함유 접착제 조성물.The method according to claim 1 or 2,
The vinyl ethylene acetate emulsion,
A polylactic acid resin emulsion-containing adhesive composition, wherein vinyl ethylene acetate is contained in a solid content of 40 to 60% (w / v).
상기 폴리우레탄수지 에멀젼은,
폴리우레탄수지가 고형분 함량으로 40~60%(w/v) 함유되어 있는 것을 특징으로 하는 폴리유산수지 에멀젼 함유 접착제 조성물.The method of claim 1,
The polyurethane resin emulsion,
Polyurethane resin emulsion-containing adhesive composition, characterized in that the polyurethane resin contains 40 to 60% (w / v) in the solid content.
상기 필름 조막제(film forming agent)는,
디에틸렌 글리콜 모노부틸 에테르 아세테이트(diethylene glycol monobutyl ether acetate), 에틸렌 글리콜 모노부틸 에테르 아세테이트(ethylene glycol monobutyl ether acetate), 에틸렌 글리콜 모노에틸 에테르 아세테이트(ethylene glycol monoethyl ether acetate), 에틸렌 글리콜 디아세테이트(ethylene glycol diacetate), n-헥실 카비톨(n-hexyl carbitol), 푸르푸릴 알콜(furfuryl alcohol), 및 텍사놀(texanol)로 이루어지는 군으로부터 선택되는 어느 1종 이상의 가소제이거나,
비프탈레이트계 가소제로서, 디프로필렌 글리콜 디벤조에이트(dipropylen glycol dibenzoate, DP), 디에틸렌 글리콜 디벤조에이트(diethylene glycol dibenzoate, DE) 및 이들의 혼합물(benzoplex)로 이루어지는 군으로부터 선택되는 어느 1종 이상의 가소제인 것을 특징으로 하는 폴리유산수지 에멀젼 함유 접착제 조성물.The method of claim 1,
The film forming agent,
Diethylene glycol monobutyl ether acetate, ethylene glycol monobutyl ether acetate, ethylene glycol monoethyl ether acetate, ethylene glycol diacetate diacetate, n-hexyl carbitol, furfuryl alcohol, and one or more plasticizers selected from the group consisting of texanol, or
At least one selected from the group consisting of dipropylen glycol dibenzoate (DP), diethylene glycol dibenzoate (DE), and a mixture thereof (benzoplex) as a nonphthalate plasticizer. A polylactic acid resin emulsion-containing adhesive composition, which is a plasticizer.
상기 접착제 조성물은,
NCO기를 25~35% 함유하는 이소시아네이트 화합물을 초산비닐에틸렌 에멀젼 100 중량부에 대하여 1 내지 20 중량부의 비율로 추가로 포함하는 것을 특징으로 하는 폴리유산수지 에멀젼 함유 접착제 조성물.The method of claim 1,
The above-
A polylactic acid resin emulsion-containing adhesive composition, further comprising an isocyanate compound containing 25 to 35% NCO group in a ratio of 1 to 20 parts by weight based on 100 parts by weight of vinyl ethylene acetate emulsion.