KR20130055211A - Loess brick and loess mortar containing cone - Google Patents

Loess brick and loess mortar containing cone Download PDF

Info

Publication number
KR20130055211A
KR20130055211A KR1020110120845A KR20110120845A KR20130055211A KR 20130055211 A KR20130055211 A KR 20130055211A KR 1020110120845 A KR1020110120845 A KR 1020110120845A KR 20110120845 A KR20110120845 A KR 20110120845A KR 20130055211 A KR20130055211 A KR 20130055211A
Authority
KR
South Korea
Prior art keywords
weight
parts
ocher
pine cone
pine
Prior art date
Application number
KR1020110120845A
Other languages
Korean (ko)
Inventor
김용근
Original Assignee
김용근
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 김용근 filed Critical 김용근
Priority to KR1020110120845A priority Critical patent/KR20130055211A/en
Publication of KR20130055211A publication Critical patent/KR20130055211A/en

Abstract

PURPOSE: A red clay brick and red clay mortar containing a pine cone are provided to ensure mechanical strength by containing mica, a firming agent, a decomposition of granite, and quicklime. CONSTITUTION: A red clay brick is made of a mixture of 100 parts by weight of red clay, 10-20 parts by weight of a powdered pine cone, and 10-20 parts by weight of a powdered pine nut. The red clay brick also contains mica, a firming agent, a decomposition of granite, quicklime, a powdered pine tree, and a powdered nut pine. Red clay mortar contains 100 parts by weight of red clay, 10-20 parts by weight of a powered pine cone, 10-20 parts by weight of a powdered pine nut, and 20 parts by weight of purified water. The red clay mortar is added by mica, a firming agent, decomposition of granite, illite, sepiolite, a powdered pine tree, and a powdered nut pine.

Description

솔방울 성분이 함유된 황토벽돌 및 황토몰탈 {LOESS BRICK AND LOESS MORTAR CONTAINING CONE}Loess brick and ocher mortar containing pine cones {LOESS BRICK AND LOESS MORTAR CONTAINING CONE}

본 발명은 솔방울 성분이 함유된 황토벽돌 및 황토몰탈에 관한 것으로, 더욱 상세하게는 항균 및 항염 효과가 우수한 솔방울 및 잣솔방울 성분이 함유된 황토벽돌 및 황토몰탈에 관한 것이다.The present invention relates to ocher bricks and ocher mortar containing pine cone components, and more particularly, to ocher bricks and ocher mortar containing pine cone and pine cone components having excellent antibacterial and anti-inflammatory effects.

본 발명은 솔방울 성분이 함유된 황토벽돌 및 황토몰탈에 관한 것으로, 더욱 상세하게는 항균 및 항염 효과가 우수한 솔방울 및 잣솔방울 성분이 함유된 황토벽돌 및 황토몰탈에 관한 것이다.The present invention relates to ocher bricks and ocher mortar containing pine cone components, and more particularly, to ocher bricks and ocher mortar containing pine cone and pine cone components having excellent antibacterial and anti-inflammatory effects.

대부분의 현대인들은 사회활동으로 인한 스트레스로 숙면을 취하지 못하고 불면과, 불편, 긴장의 연속인 상태로 생활하여 건강을 서서히 해치고 있다. 따라서 지금까지 사용해오던 생활방식에서 탈피하고자 시멘트바닥의 단점과 불편을 제거하고 전통 한국식 온돌의 효과를 갖도록 많은 연구가 있어 왔다.Most of the modern people do not get a good night's sleep due to the stress of social activities, and they are gradually harming their health by living in a state of insomnia, discomfort, and tension. Therefore, there have been many studies to remove the shortcomings and inconveniences of cement floors and to have the effect of traditional Korean ondol in order to escape from the lifestyle used so far.

예로부터 황토는 황토에서 원적외선이 방출되어 건강에 유익하다고 알려져 황토를 이용한 건축물 또는 황토온돌방이 보급이 늘어나면서 많은 관심을 끌어 왔다.Since ancient times, ocher is known to be beneficial for health by the emission of far-infrared radiation from ocher.

그러나 종래에 황토성분으로 이루어진 황토벽돌 및 몰탈은 현대에 들어서 건물이, 고층화 및 대형화됨으로 인해 그 적용분야가 한정되는 문제점이 있었다.However, in the past, ocher bricks and mortar made of ocher components have a problem in that their applications are limited due to the high and large building size.

이러한 문제점으로 인해 건축재료로 황토보다는 콘크리트가 사용되고 있는 실정인데, 이것은 황토는 그 강도에 있어서 고층, 대형 건물을 지지할 수 있을 정도의 강도를 보이지 못하기 때문이었다. 한편, 콘크리트 건물이나 주택은 통기성이 나쁘고, 곰팡이나 해충이 서식하기 좋을 뿐 아니라 콘크리트에서 방출되는 나노 가스가 환경에 축적되어 인체에 나쁜 영향을 미치고 있고, 이를 해결하기 위한 방안이 다각적으로 검토되고 있는데, 그 중 하나가 황토를 건축자재로 이용하려는 시도이다. 그러나, 위에서 언급한 바와 같이, 황토를 건축자재로 이용하기 위해서는 황토로 만든 벽돌이 일정 이상의 강도 및 내구성을 지녀야 하는데, 아직까지 산업현장에서 요구되는 강도를 만족하는 황토벽돌에 대해서는 알려진 바 없다.Due to this problem, concrete is used rather than loess as a building material, because the loess does not show strength enough to support high-rise and large buildings. On the other hand, concrete buildings and houses are badly breathable, not only mold or pests are inhabited, but also nano gases emitted from concrete are accumulating in the environment, which adversely affects the human body. One of them is the attempt to use loess as a building material. However, as mentioned above, in order to use ocher as a building material, bricks made of ocher must have a certain strength and durability, and there are no known ocher bricks that satisfy the strength required in industrial sites.

또한, 종래에 황토벽돌 및 몰탈은 곰팡이 등과 같은 세균의 서식을 방지할 수 없는 문제점이 있었다.In addition, the conventional ocher brick and mortar had a problem that can not prevent the habitat of bacteria such as mold.

본 발명의 목적은 솔방울 성분이 함유되어 우수한 항균 및 항염 효과를 나타내는 솔방울 성분이 함유된 황토벽돌 및 황토몰탈을 제공하는 것이다.It is an object of the present invention to provide an ocher brick and ocher mortar containing a pine cone component which contains a pine cone component and exhibits excellent antibacterial and anti-inflammatory effects.

본 발명의 다른 목적은 운모, 고화제 및 마사 등과 같은 성분이 함유되어 기계적 강도가 향상된 솔방울 성분이 함유된 황토벽돌 및 황토몰탈을 제공하는 것이다.Another object of the present invention is to provide a loess brick and ocher mortar containing a pine cone component containing components such as mica, hardening agent and martha improved mechanical strength.

본 발명의 목적은 황토, 솔방울 분말 및 잣솔방울 분말로 이루어지는 것을 특징으로 하는 솔방울 성분이 함유된 황토벽돌을 제공함에 의해 달성된다.An object of the present invention is achieved by providing an ocher brick containing pine cone components, characterized in that consisting of loess, pine cone powder and pine cone powder.

본 발명의 바람직한 특징에 따르면, 상기 솔방울 성분이 함유된 황토벽돌은 황토 100 중량부에 솔방울 분말 10 내지 20 중량부 및 잣솔방울 분말 10 내지 20 중량부를 혼합하여 이루어지는 것으로 한다.According to a preferred feature of the present invention, the ocher brick containing the pine cone component is to be made by mixing 10 to 20 parts by weight of pine cone powder and 10 to 20 parts by weight of pine cone powder to 100 parts by weight of ocher.

본 발명의 더 바람직한 특징에 따르면, 상기 솔방울 성분이 함유된 황토벽돌에는 운모 5 내지 10 중량부, 고화제 10 내지 20 중량부, 마사 5 내지 20 중량부 및 생석회 5 내지 10 중량부가 더 함유되는 것으로 한다.According to a more preferable feature of the present invention, the ocher brick containing the pine cone component is 5 to 10 parts by weight of mica, 10 to 20 parts by weight of hardener, 5 to 20 parts by weight of martha and 5 to 10 parts by weight of quicklime do.

본 발명의 더욱 바람직한 특징에 따르면, 상기 고화제는 시멘트, 고로슬래그 및 자연석고로 이루어진 그룹으로부터 선택된 하나 이상으로 이루어지는 것으로 한다.According to a more preferred feature of the invention, the hardening agent is to be made of one or more selected from the group consisting of cement, blast furnace slag and natural gypsum.

본 발명의 더욱 더 바람직한 특징에 따르면, 상기 솔방울 성분이 함유된 황토벽돌에는 소나무 분말 2 내지 5 중량부 및 잣나무 분말 2 내지 5 중량부가 더 함유되는 것으로 한다.
According to a further preferred feature of the present invention, the ocher brick containing the pine cone component is to contain 2 to 5 parts by weight of pine powder and 2 to 5 parts by weight of pine wood powder.

또한, 본 발명의 목적은 황토, 솔방울 분말, 잣솔방울 분말 및 정제수로 이루어지는 것을 특징으로 하는 솔방울 성분이 함유된 황토몰탈을 제공함에 의해서도 달성될 수 있다.In addition, the object of the present invention can also be achieved by providing a loess mortar containing pine cone components, characterized in that consisting of loess, pine cone powder, pine cone powder and purified water.

본 발명의 바람직한 특징에 따르면, 상기 솔방울 성분이 함유된 황토몰탈은 황토 100 중량부에 솔방울 분말 10 내지 20 중량부, 잣솔방울 분말 10 내지 20 중량부 및 정제수 20 중량부로 이루어지는 것으로 한다.According to a preferred feature of the present invention, the ocher mortar containing the pine cone component is composed of 10 to 20 parts by weight of pine cone powder, 10 to 20 parts by weight of pine cone powder and 20 parts by weight of purified water.

본 발명의 더 바람직한 특징에 따르면, 상기 솔방울 성분이 함유된 황토몰탈은 운모 5 내지 10 중량부, 고화제 10 내지 20 중량부, 마사 5 내지 20 중량부, 일라이트 1 내지 5 중량부, 세피오라이트 1 내지 5 중량부 및 토르말린 1 내지 5 중량부가 더 첨가되는 것으로 한다.According to a more preferable feature of the present invention, the ocher mortar containing the pine cone component is 5 to 10 parts by weight of mica, 10 to 20 parts by weight of hardener, 5 to 20 parts by weight of martha, 1 to 5 parts by weight of illite, sepiolite 1 It is assumed that 5 parts by weight and 1 to 5 parts by weight of tourmaline are added.

본 발명의 더욱 바람직한 특징에 따르면, 상기 고화제는 시멘트, 고로슬래그 및 자연석고로 이루어진 그룹으로부터 선택된 하나 이상으로 이루어지는 것으로 한다.According to a more preferred feature of the invention, the hardening agent is to be made of one or more selected from the group consisting of cement, blast furnace slag and natural gypsum.

본 발명의 더욱 더 바람직한 특징에 따르면, 상기 솔방울 성분이 함유된 황토몰탈은 소나무 분말 2 내지 5 중량부 및 잣나무 분말 2 내지 5 중량부가 더 함유되는 것으로 한다.According to an even more preferable feature of the present invention, the ocher mortar containing the pine cone component is to be contained 2 to 5 parts by weight of pine powder and 2 to 5 parts by weight of pine wood powder.

본 발명에 따른 솔방울 성분이 함유된 황토벽돌 및 황토몰탈은 솔방울 성분이 함유되어 탁월한 항균 및 항염 효과를 나타낸다.The ocher brick and the ocher mortar containing the pine cone component according to the present invention contains the pine cone component and shows excellent antibacterial and anti-inflammatory effects.

또한, 운모, 고화제, 마사 및 생석회 등과 같은 성분이 함유되어 우수한 기계적 강도를 나타낸다.In addition, components such as mica, hardener, martha and quicklime are included to show excellent mechanical strength.

이하에는, 본 발명의 바람직한 실시예와 각 성분의 물성을 상세하게 설명하되, 이는 본 발명이 속하는 기술분야에서 통상의 지식을 가진 자가 발명을 용이하게 실시할 수 있을 정도로 상세하게 설명하기 위한 것이지, 이로 인해 본 발명의 기술적인 사상 및 범주가 한정되는 것을 의미하지는 않는다.
Hereinafter, preferred embodiments of the present invention and physical properties of the respective components will be described in detail with reference to the accompanying drawings. However, the present invention is not limited thereto, And this does not mean that the technical idea and scope of the present invention are limited.

본 발명에 따른 황토벽돌은 황토, 솔방울 분말 및 잣솔방울 분말로 이루어지는데, 황토 100 중량부에 솔방울 분말 10 내지 20 중량부 및 잣솔방울 분말 10 내지 20 중량부를 혼합하여 이루어지는 것이 더욱 바람직하다.
The ocher brick according to the present invention is composed of ocher, pine cone powder and pine cone powder, more preferably made by mixing 10 to 20 parts by weight of pine cone powder and 10 to 20 parts by weight of pine cone powder to 100 parts by weight of ocher.

상기 황토는 100 중량부가 첨가되며, 황토벽돌을 이루는 주재의 역할을 하는데, 황토는 주로 가는 모래로 되어 있으며 다량의 탄산칼슘을 가지고 있다. 이 탄산칼슘에 의해 쉽게 부서지지 않은 점력을 지니고 물을 가하면 찰흙으로 변하는 성질이 있다. 또한, 황토는 석영, 장석, 운모, 방해석등이 들어 있어서 이들 물질이 철분과 함께 산화작용을 받아 황색, 자색, 적색, 회색, 미녹색등의 색깔을 나타낸다. 예부터 황토는 그 자체로 건축자재로서 이용되어 오고 있으며, 특히 황토에서 내뿜는 원적외선에 의해 인체의 생리작용을 활성화시켜 건강증진에 도움을 줌과 아울러, 황토가 본질적으로 지니고 있는, 습도조절, 항균 및 방충, 공기정화, 탈취, 보온효과로 인해서 황토는 최고의 건축자재로 된다.The ocher is added to 100 parts by weight, and serves as a main material forming the ocher brick, the ocher is mainly made of fine sand and has a large amount of calcium carbonate. This calcium carbonate has a viscosity that is not easily broken, and when water is added, it turns into clay. In addition, ocher contains quartz, feldspar, mica, calcite, and the like, and these materials are oxidized with iron to show colors of yellow, purple, red, gray, and pale green. Since ancient times, ocher has been used as a building material in itself, and in particular, it promotes health by activating the physiology of the human body by far-infrared rays emitted from ocher, and in addition to the humidity control, antibacterial and Insect repellent, air purifying, deodorizing, and warming effect make ocher the best building material.

본 발명에 사용되는 황토는, 입자가 미세하고 깨끗하며 지표로부터 80 내지100cm 아래에 위치한 것으로서, 이를 채취하여 건조하고, 이를 분쇄하여 사용한다.The ocher used in the present invention is fine and clean, and is located below 80 to 100 cm from the surface of the earth, which is collected by drying it, and then used by pulverizing it.

이때, 황토는 주로 실트 크기의 지름 0.002 내지 0.005mm인 입자로 이루어진 퇴적물이며 주로 세입모래와 점토가 섞여 있으며, 공극률이 매우 크므로 습기 또는 동해(冬害)에 매우 약하며, 딱딱하게 고화시키는 기술이 매우 어렵다. 그러나, 본 발명에 의해 제공되는 황토벽돌은, 황토의 수분을 제거하고 공극률을 작게 함으로서 동해에도 견딜 수 있는 견운모 및 고화제를 혼합할 경우, 견운모, 황토의 장점을 유지하면서 단단하게 고화시킬 수 있다.
At this time, loess is a sediment mainly composed of particles of 0.002 to 0.005mm diameter of silt size, mainly mixed with sand and clay, and very high porosity, so it is very weak against moisture or East Sea, and the technology of solidifying hardly Very difficult. However, the ocher brick provided by the present invention can be solidified while maintaining the advantages of the mica and loess when mixing the mica and the hardening agent which can withstand the East Sea by removing the moisture of the loess and reducing the porosity. .

상기 솔방울 분말은 10 내지 20 중량부가 첨가되며, 본 발명에 따른 황토벽돌에 항균성 및 항염효과를 부여하는 역할을 할 뿐만 아니라, 본 발명에 의해 제조된 황토벽돌은 솔방울 분말에서 방출되는 특유의 향기로 인해 머리를 맑게 해주는 효과도 나타낸다.The pine cone powder is added in an amount of 10 to 20 parts by weight, and not only serves to impart antimicrobial and anti-inflammatory effects to the ocher brick according to the present invention, the ocher brick prepared by the present invention has a unique fragrance emitted from the pine cone powder. It also clears your hair.

솔방울 분말의 함량이 10 중량부 미만이면, 솔방울이 갖는 특유의 기능을 발휘하지 못하며, 솔발울 분말의 함량이 20 중량부를 초과하게 되면, 황토벽돌의 기계적 강도가 저하될 수 있다.If the content of the pine cone powder is less than 10 parts by weight, it does not exhibit the unique function of the pine cone, if the content of the pine cone powder exceeds 20 parts by weight, the mechanical strength of the ocher brick may be lowered.

이때, 솔방울 분말은 상기 황토와 고르게 혼합되기 위해 지름이 0.05 내지 0.1밀리미터로 미분쇄되는 것이 바람직하다.
At this time, the pine cone powder is preferably pulverized to 0.05 to 0.1 millimeters in diameter in order to be evenly mixed with the loess.

상기 잣솔방울 분말은 10 내지 20 중량부가 첨가되며, 본 발명에 따른 황토벽돌에 항균성 및 항염효과를 부여하는 역할을 할 뿐만 아니라, 잣솔방울 분말에서 방출되는 특유의 향기로 인해 머리를 맑게 해주는 효과를 나타낸다.10 to 20 parts by weight of the pine cone powder is added, not only serves to impart antimicrobial and anti-inflammatory effect to the ocher bricks according to the present invention, the effect of clearing the hair due to the peculiar aroma emitted from the pine cone powder Indicates.

또한, 잣솔방울 분말은 특유의 향과 독성으로 인해 파리 모기는 물론, 황토 건축물 등에서 해충의 발생을 억제하는 효과도 나타내는데, 잣솔방울의 함량이 10 중량부 미만이면, 해충발생 억제효과가 미미하며, 20 중량부를 초과하게 되면 황토벽돌의 기계적 강도를 저하시킨다.In addition, pine cone powder has the effect of suppressing the occurrence of pests in mosquitoes, as well as ocher building due to the peculiar aroma and toxicity, if the content of pine cone droplets less than 10 parts by weight, the pest suppression effect is insignificant, When it exceeds 20 parts by weight, the mechanical strength of the ocher brick is lowered.

이때, 잣솔방울 분말은 상기 황토와 고르게 혼합되기 위해 지름이 0.05 내지 0.1밀리미터로 미분쇄되는 것이 바람직하다.
At this time, the pine cone powder is preferably pulverized to 0.05 to 0.1 millimeters in diameter in order to be evenly mixed with the loess.

또한, 상기 솔방울 성분이 함유된 황토벽돌에는 황토벽돌의 기계적 강도를 향상시키기 위해, 운모 5 내지 10 중량부, 고화제 10 내지 20 중량부, 마사 5 내지 20 중량부 및 생석회 5 내지 10 중량부가 더 함유될 수도 있다.In addition, in order to improve the mechanical strength of the ocher brick, the ocher brick containing the pine cone component further includes 5 to 10 parts by weight of mica, 10 to 20 parts by weight of hardener, 5 to 20 parts by weight of martha and 5 to 10 parts by weight of quicklime. It may be contained.

상기와 같은 운모, 고화제, 마사 및 생석회가 함유된 황토벽돌은 다층구조의 건축물이나, 대형 건축물에 적합한 기계적 물성을 갖게된다.The loess bricks containing mica, hardener, martha and quicklime as described above have mechanical properties suitable for multi-layered buildings or large buildings.

이때, 상기 고화제는 시멘트, 고로슬래그 및 자연석고로 이루어진 그룹으로부터 선택된 하나 이상으로 이루어지는 것이 바람직하며, 상기 생석회는 예로부터 시멘트 대용으로 사용되어 강도를 증진시키는 역할을 하던 성분으로, 석축, 성벽 및 무덤 입관시에 흙과 함께 다지면 그 효과가 탁월하였고, 본 발명에 따른 황토벽돌의 기계적 강도록 더욱 향상시키는 역할을 한다.
At this time, the solidifying agent is preferably made of one or more selected from the group consisting of cement, blast furnace slag and natural gypsum, the quicklime is used as a substitute for cement used to enhance the strength from the old, such as masonry, wall and When it is crushed together with the soil at the entrance of the grave, the effect was excellent, and serves to further improve the mechanical strength of the ocher brick according to the present invention.

또한, 상기 솔방울 성분이 함유된 황토벽돌에는 소나무 분말 2 내지 5 중량부 및 잣나무 분말 2 내지 5 중량부가 더 함유될 수도 있는데, 소나무 분말 및 잣나무 분말이 더 함유된 황토벽돌은 항균 및 함염 효과가 더욱 증대된다.In addition, the ocher brick containing the pine cone component may further contain 2 to 5 parts by weight of pine powder and 2 to 5 parts by weight of pine tree powder, and the ocher brick further containing pine powder and pine tree powder further has an antibacterial and salting effect. Is increased.

이때, 소나무 분말 및 잣나무 분말도 상기 황토와 고르게 혼합될 수 있도록 지름이 0.05 내지 0.1 밀리미터로 미분쇄되는 것이 바람직하다.
At this time, the pine powder and pine tree powder is preferably finely pulverized to 0.05 to 0.1 millimeters in diameter so as to be evenly mixed with the loess.

또한, 본 발명에 따른 황토몰탈은 황토, 솔방울 분말, 잣솔방울 분말 및 정제수로 이루어지는데, 황토 100 중량부에 솔방울 분말 10 내지 20 중량부, 잣솔방울 분말 10 내지 20 중량부 및 정제수 20 중량부로 이루어지는 것이 더욱 바람직하다.
In addition, ocher mortar according to the present invention is composed of loess, pine cone powder, pine cone powder and purified water, 10 to 20 parts by weight of pine cone powder, pine cone powder 10 to 20 parts by weight and purified water 20 parts by weight of ocher More preferred.

상기 황토성분, 솔방울 분말 및 잣솔방울 분말은 상기 황토벽돌에 사용된 것과 성분 및 역할이 동일함으로 그에 대한 설명은 생략하기로 한다.The ocher component, pine cone powder and pine cone powder are the same components and roles as those used in the ocher brick, so the description thereof will be omitted.

상기 정제수는 20 중량부가 첨가되며, 상기 황토몰탈에 유동성을 부여하여 상기 황토벽돌로 이루어진 건축물을 제조할 때, 몰탈로 사용될 수 있도록 하는 역할을 한다.
20 parts by weight of the purified water is added, and gives fluidity to the ocher mortar serves to be used as a mortar when manufacturing the building made of the ocher brick.

또한, 상기 황토몰탈에는 운모 5 내지 10 중량부, 고화제 10 내지 20 중량부, 마사 5 내지 20 중량부, 일라이트 1 내지 5 중량부, 세피오라이트 1 내지 5 중량부 및 토르말린 1 내지 5 중량부가 더 첨가될 수도 있는데, 상기 운모, 고화제 및 마사는 상기 황토벽돌에 기재된 것과 성분 및 역할이 동일함으로 이에 대한 설명은 생략하기로 한다.In addition, the ocher mortar is 5 to 10 parts by weight of mica, 10 to 20 parts by weight of hardener, 5 to 20 parts by weight of martha, 1 to 5 parts by weight of illite, 1 to 5 parts by weight of sepiolite and 1 to 5 parts by weight of tourmaline. The mica, hardener, and martha may be added, and thus the description thereof will be omitted because the components and roles thereof are the same as those described in the ocher brick.

상기 일라이트, 세피오라이트 및 토르말린은 원적외선과 음이온을 방출하여, 상기의 성분의 적용된 황토몰탈이 사용된 건축물의 내부에서는 인체에 유익한 원적외선과 음이온이 다량 방출된다.The illite, sepiolite and tourmaline emit far infrared rays and anions, and a large amount of far infrared rays and anions that are beneficial to the human body are emitted in the interior of the building using the applied loess mortar of the above components.

또한, 상기 황토몰탈에는 소나무 분말 2 내지 5 중량부 및 잣나무 분말 2 내지 5 중량부가 더 함유되는데, 상기 소나무 분말 및 잣나무 분말은 상기 황토벽돌에 사용된 것과 성분 및 역할이 동일함으로 이에 대한 설명은 생략하기로 한다.In addition, the ocher mortar further contains 2 to 5 parts by weight of pine powder and 2 to 5 parts by weight of pine tree powder, and the pine powder and pine tree powder have the same components and roles as those used for the ocher brick, and thus description thereof is omitted. Let's do it.

전술한 바와 같이, 본 발명에 따른 솔방울 성분이 함유된 황토벽돌 및 황토몰탈은 솔방울 성분이 함유되어 탁월한 항균 및 항염 효과를 나타내며, 또한, 운모, 고화제 및 마사 등과 같은 성분이 함유되어 우수한 기계적 강도를 나타낸다.As described above, the ocher brick and ocher mortar containing the pine cone component according to the present invention exhibits excellent antimicrobial and anti-inflammatory effects due to the pine cone component, and also contains components such as mica, hardening agent, and martha, and has excellent mechanical strength. Indicates.

뿐만 아니라, 상기 황토몰탈에는 일라이트, 세피오라이트 및 토르말린과 같이 원적외선 및 음이온을 다량 방출하는 성분이 함유되어 있어 인체에 유익한 효과를 나타내며, 본 발명에 따른 황토벽돌과 황토몰탈은 함께 사용되어 건축물에 적용되었을 때, 그 효과가 더욱 향상된다.In addition, the ocher mortar contains a component that emits a large amount of far infrared rays and anions such as illite, sepiolite and tourmaline shows a beneficial effect on the human body, the ocher brick and the ocher mortar according to the present invention is used together to apply to buildings When it is done, the effect is further improved.

Claims (10)

황토, 솔방울 분말 및 잣솔방울 분말로 이루어지는 것을 특징으로 하는 솔방울 성분이 함유된 황토벽돌.Ocher brick containing pine cone components, characterized in that consisting of loess, pine cone powder and pine cone powder. 청구항 1에 있어서,
상기 솔방울 성분이 함유된 황토벽돌은 황토 100 중량부에 솔방울 분말 10 내지 20 중량부 및 잣솔방울 분말 10 내지 20 중량부를 혼합하여 이루어지는 것을 특징으로 하는 솔방울 성분이 함유된 황토벽돌.The method according to claim 1,
The ocher brick containing the pine cone component is ocher brick containing pine cone component, characterized in that by mixing 10 to 20 parts by weight of pine cone powder and 10 to 20 parts by weight of pine cone powder to 100 parts by weight of ocher. 청구항 1에 있어서,
상기 솔방울 성분이 함유된 황토벽돌에는 운모 5 내지 10 중량부, 고화제 10 내지 20 중량부, 마사 5 내지 20 중량부 및 생석회 5 내지 10 중량부가 더 함유되는 것을 특징으로 하는 솔방울 성분이 함유된 황토벽돌.The method according to claim 1,
The ocher brick containing the pine cone component contains 5 to 10 parts by weight of mica, 10 to 20 parts by weight of hardener, 5 to 20 parts by weight of martha and 5 to 10 parts by weight of quicklime. brick. 청구항 3에 있어서,
상기 고화제는 시멘트, 고로슬래그 및 자연석고로 이루어진 그룹으로부터 선택된 하나 이상으로 이루어지는 것을 특징으로 하는 솔방울 성분이 함유된 황토벽돌.The method according to claim 3,
The solidifying agent is an ocher brick containing pine cone component, characterized in that consisting of at least one selected from the group consisting of cement, blast furnace slag and natural gypsum. 청구항 1에 있어서,
상기 솔방울 성분이 함유된 황토벽돌에는 소나무 분말 2 내지 5 중량부 및 잣나무 분말 2 내지 5 중량부가 더 함유되는 것을 특징으로 하는 솔방울 성분이 함유된 황토벽돌.The method according to claim 1,
The ocher brick containing pine cone component ocher brick containing pine cone component, characterized in that it contains 2 to 5 parts by weight of pine powder and 2 to 5 parts by weight of pine wood powder. 황토, 솔방울 분말, 잣솔방울 분말 및 정제수로 이루어지는 것을 특징으로 하는 솔방울 성분이 함유된 황토몰탈.Ocher mortar containing pine cone components, characterized in that consisting of loess, pine cone powder, pine cone powder and purified water. 청구항 6에 있어서,
상기 솔방울 성분이 함유된 황토몰탈은 황토 100 중량부에 솔방울 분말 10 내지 20 중량부, 잣솔방울 분말 10 내지 20 중량부 및 정제수 20 중량부로 이루어지는 것을 특징으로 하는 솔방울 성분이 함유된 황토몰탈.The method of claim 6,
The ocher mortar containing the pine cone component is ocher mortar mortar containing a pine cone component, characterized in that consisting of 10 to 20 parts by weight of pine cone powder, 10 to 20 parts by weight of pine cone powder and 20 parts by weight of purified water. 청구항 6에 있어서,
상기 솔방울 성분이 함유된 황토몰탈은 운모 5 내지 10 중량부, 고화제 10 내지 20 중량부, 마사 5 내지 20 중량부, 일라이트 1 내지 5 중량부, 세피오라이트 1 내지 5 중량부 및 토르말린 1 내지 5 중량부가 더 첨가되는 것을 특징으로 하는 솔방울 성분이 함유된 황토몰탈.The method of claim 6,
The ocher mortar containing the pine cone component is 5 to 10 parts by weight of mica, 10 to 20 parts by weight of hardener, 5 to 20 parts by weight of martha, 1 to 5 parts by weight of illite, 1 to 5 parts by weight of sepiolite and 1 to 5 of tourmaline. Ocher mortar containing a pine cone component, characterized in that the weight part is further added. 청구항 6에 있어서,
상기 고화제는 시멘트, 고로슬래그 및 자연석고로 이루어진 그룹으로부터 선택된 하나 이상으로 이루어지는 것을 특징으로 하는 솔방울 성분이 함유된 황토몰탈.The method of claim 6,
The solidifying agent is ocher mortar containing pine cone component, characterized in that consisting of at least one selected from the group consisting of cement, blast furnace slag and natural gypsum. 청구항 6에 있어서,
상기 솔방울 성분이 함유된 황토몰탈은 소나무 분말 2 내지 5 중량부 및 잣나무 분말 2 내지 5 중량부가 더 함유되는 것을 특징으로 하는 솔방울 성분이 함유된 황토몰탈.The method of claim 6,
The ocher mortar containing the pine cone component is ocher mortar mortar containing pine cone powder, characterized in that it contains 2 to 5 parts by weight of pine powder and 2 to 5 parts by weight of pine tree powder.
KR1020110120845A 2011-11-18 2011-11-18 Loess brick and loess mortar containing cone KR20130055211A (en)