KR20120100371A - Method for manufacturing glass window and glass window manufactured by the same method - Google Patents

Method for manufacturing glass window and glass window manufactured by the same method Download PDF

Info

Publication number
KR20120100371A
KR20120100371A KR1020110019222A KR20110019222A KR20120100371A KR 20120100371 A KR20120100371 A KR 20120100371A KR 1020110019222 A KR1020110019222 A KR 1020110019222A KR 20110019222 A KR20110019222 A KR 20110019222A KR 20120100371 A KR20120100371 A KR 20120100371A
Authority
KR
South Korea
Prior art keywords
glass
film
pattern
pattern layer
manufacturing
Prior art date
Application number
KR1020110019222A
Other languages
Korean (ko)
Inventor
이연우
Original Assignee
주식회사 프로코텍
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 주식회사 프로코텍 filed Critical 주식회사 프로코텍
Priority to KR1020110019222A priority Critical patent/KR20120100371A/en
Publication of KR20120100371A publication Critical patent/KR20120100371A/en

Abstract

PURPOSE: A manufacturing method of glass windows and a glass window manufactured by the same are provided to form a plurality of pattern layers on one disk glass at once. CONSTITUTION: A manufacturing method of glass windows comprises the following steps: forming photoresist pattern layers(21) on a disk glass(10); manufacturing a plurality divided glasses(11) by removing a pattern layer not formed part from the disk glass; and removing the pattern layer from the divided glass. The pattern layer formation step comprises the following steps: (S11) respectively attaching photosensitive films(20) on both sides of the disk glass; (S12) respectively attaching printed firms(30) in which a pattern is formed on the surface of photosensitive film; (S13) curing the photosensitive film along the pattern of the printed film by irradiating the disk glass with UV; (S14) removing the printed film from the exposed disk glass; and (S15) removing the non-cured part of the photosensitive film by using a developer. [Reference numerals] (AA) Non-cured part; (BB) Cured part

Description

글라스윈도우 제조방법 및 이에 의해 제조된 글라스윈도우{METHOD FOR MANUFACTURING GLASS WINDOW AND GLASS WINDOW MANUFACTURED BY THE SAME METHOD}METHOD FOR MANUFACTURING GLASS WINDOW AND GLASS WINDOW MANUFACTURED BY THE SAME METHOD}

본 발명은 터치스크린 및 휴대단말기에 사용되는 글라스윈도우의 제조방법에 관한 것으로서, 더욱 상세하게는 포토레지스트를 이용한 식각(etching) 기술을 적용함으로써 생산성이 향상될 수 있도록 한 글라스윈도우 제조방법 및 이에 의해 제조된 글라스윈도우에 관한 것이다.
The present invention relates to a method for manufacturing a glass window used in a touch screen and a portable terminal, and more particularly, to a glass window manufacturing method for improving productivity by applying an etching technique using a photoresist and thereby It relates to a manufactured glass window.

일반적으로 핸드폰 등의 터치스크린 및 휴대단말기 등에 적용되는 글라스윈도우(glass window)는 액정표시부분의 외층에 해당되는 것으로서, LCD 등의 액정표시부에 스크래치가 생성되는 것을 방지하거나 외부 충격으로부터 보호하는 기능을 담당하도록 장착된다.
Generally, a glass window applied to a touch screen and a mobile terminal such as a mobile phone corresponds to an outer layer of the liquid crystal display, and prevents scratches from being generated on the liquid crystal display such as an LCD or protects it from external impact. It is equipped to take charge.

한편, 이러한 글라스윈도우 제조방법에 관한 기술로는,On the other hand, as a technology relating to such a glass window manufacturing method,

본 출원인에 의해 출원된 대한민국공개특허 제10-2011-0005346호(2011년 1월 18일 공개, 이하 '선행기술'이라고 함) 『터치스크린 및 휴대단말기용 강화 글라스윈도우 가공방법』이 제시되어 있는바,Korean Patent Application Publication No. 10-2011-0005346 filed by the present applicant (published on January 18, 2011, hereinafter referred to as 'advanced technology') `` reinforced glass window processing method for touch screens and mobile terminals '' is proposed bar,

상기 선행기술은,The prior art,

"원판 글라스의 양면에 필름을 각각 부착하는 제1단계와;"A first step of attaching films to both sides of the original glass;

상기 P.V.C 계열의 필름이 부착된 원판 글라스에 평판 커팅 및 레이저 커팅기 가공을 통해 필름 부분을 절단하여 이미지를 마킹 처리하는 제2단계와;A second step of marking an image by cutting a portion of the film through a plate cutting and a laser cutting machine on the P.V.C-based film-attached glass;

상기 원판 글라스를 샌딩 에칭하여 마킹된 이미지를 따라 물리적 절단하여 원판 글라스로부터 글라스윈도우를 절취 및 분할해내는 제3단계와;A third step of cutting and dividing the glass window from the original glass by sand-etching the original glass and physically cutting along the marked image;

상기 샌딩 에칭을 통해 분할해낸 글라스윈도우의 외형측면을 면취 가공하는 제4단계와;A fourth step of chamfering the outer surface of the glass window divided by the sanding etching;

상기 이미지의 마킹 처리에 사용된 필름을 글라스윈도우로부터 분리해내는 제5단계"A fifth step of separating the film used for marking the image from the glass window "

를 포함하여 이루어진 것으로서,And,

작업시간 절감 및 불량률 감소와 더불어 생산성을 향상시킬 수 있도록 한 기술이다.
It is a technology that can improve productivity while reducing working time and reducing defective rate.

상기 선행기술은 평판 커팅 및 레이저 커팅을 이용한 이미지 마킹 및 건식 에칭의 공정을 수행함과 아울러 자동화공정으로 처리할 수 있어 기존에 비해 제조공정 및 작업시간을 크게 줄일 수 있고 재료적 누수를 없앨 수 있으며 제조되는 글라스윈도우의 불량률을 감소시킬 수 있음은 물론 인건비 절감과 함께 생산성을 향상시킬 수 있도록 하고는 있으나,The prior art can perform the process of image marking and dry etching using plate cutting and laser cutting, and also can be processed by an automated process, which can greatly reduce the manufacturing process and working time and eliminate material leakage and manufacture Although it is possible to reduce the defective rate of glass windows, it is possible to improve productivity while reducing labor costs.

하나의 원판글라스로 다수의 글라스윈도우를 제작하고자 할 경우, 상기 이미지 마킹 단계에서 많은 시간이 소요되는 문제가 있다.In the case of manufacturing a plurality of glass windows with one disc glass, there is a problem that takes a lot of time in the image marking step.

즉, 상기 평판 커팅 및 레이저 커팅 가공 시 다수의 이미지를 각각 마킹처리해야함으로써 생산성이 저하되는 것이다.
That is, productivity is reduced by marking a plurality of images respectively during the flat plate cutting and the laser cutting process.

상기와 같은 과제를 해결하기 위하여 본 발명에 따른 글라스윈도우 제조방법은,In order to solve the above problems, the glass window manufacturing method according to the present invention,

원판글라스에 포토레지스트 패턴층을 형성하는 패턴층형성단계;A pattern layer forming step of forming a photoresist pattern layer on the original glass;

상기 원판글라스에서 상기 패턴층 비(非)형성부를 제거하여 다수의 분할글라스를 제작하는 에칭단계; 및An etching step of manufacturing a plurality of divided glasses by removing the pattern layer non-formed portion from the original glass; And

상기 분할글라스에서 상기 패턴층을 제거하는 박리단계;A peeling step of removing the pattern layer from the split glass;

를 포함하여 이루어진 것을 특징으로 한다.
And a control unit.

여기서 상기 패턴층형성단계는Wherein the pattern layer forming step

상기 원판글라스의 양면에 감광성필름을 각각 부착하는 감광성필름부착단계,A photosensitive film attaching step of attaching the photosensitive film to both sides of the original glass,

상기 감광성필름 표면에 패턴이 형성된 인쇄필름을 각각 부착하는 인쇄필름부착단계,A printing film attaching step of attaching a printing film having a pattern formed on the surface of the photosensitive film, respectively;

상기 인쇄필름부착단계를 거친 원판글라스에 UV(Ultraviolet)를 조사하여 상기 인쇄필름의 패턴을 따라 상기 감광성필름을 경화시키는 노광단계,An exposure step of curing the photosensitive film along the pattern of the printing film by irradiating UV (Ultraviolet) on the original glass that has undergone the printing film attaching step,

상기 노광단계를 거친 원판글라스에서 상기 인쇄필름을 제거하는 인쇄필름제거단계, 그리고A print film removing step of removing the print film from the original glass that has undergone the exposure step; and

현상액을 이용하여 상기 감광성필름의 비(非)경화부를 제거하는 현상단계A developing step of removing the non-hardened portion of the photosensitive film using a developing solution.

를 포함하여 이루어진 것을 특징으로 한다.
And a control unit.

그리고 상기 에칭단계 또는 상기 박리단계를 거친 상기 분할글라스의 테두리를 다듬는 면취단계를 더 포함하여 이루어진 것을 특징으로 하는 글라스윈도우 제조방법.
And a chamfering step of trimming the edge of the divided glass that has undergone the etching step or the peeling step.

본 발명에 따른 글라스윈도우 제조방법은,Glass window manufacturing method according to the invention,

포토레지스트에 의한 식각 기술을 이용함으로써, 하나의 원판글라스에 다수의 패턴층을 동시에 형성할 수 있어 생산성이 크게 향상되는 효과가 있다.
By using an etching technique using a photoresist, a plurality of pattern layers can be simultaneously formed on one disc glass, and thus the productivity is greatly improved.

도 1은 본 발명에 따른 글라스윈도우 제조방법을 나타낸 흐름도.
도 2는 본 발명에 따른 글라스윈도우 제조방법을 나타낸 공정 순서도.1 is a flow chart showing a glass window manufacturing method according to the present invention.
Figure 2 is a process flow chart showing a glass window manufacturing method according to the present invention.

이하 본 발명의 실시예를 첨부된 도면을 참조하여 상세하게 설명한다.Hereinafter, embodiments of the present invention will be described in detail with reference to the accompanying drawings.

도 1 및 도 2에서와 같이, 본 발명에 따른 글라스윈도우 제조방법(이하 '제조방법'이라고 함)은 크게 패턴층형성단계(S10), 에칭단계(S20) 및 박리단계(S30)로 이루어진다.1 and 2, the glass window manufacturing method according to the present invention (hereinafter referred to as 'manufacturing method') is largely composed of a pattern layer forming step (S10), etching step (S20) and peeling step (S30).

이하 각 단계에 대해 살펴보면,
For each step below,

상기 패턴층형성단계(S10)는The pattern layer forming step (S10)

원판글라스(10)에 포토레지스트 패턴층(21)을 형성하는 단계로서,As the step of forming the photoresist pattern layer 21 on the disc glass 10,

상기 원판글라스(10)의 양면에 감광성필름(Dry Film Photoresist, 20)을 각각 부착하는 감광성필름부착단계(S11),A photosensitive film attaching step (S11) for attaching a photosensitive film (Dry Film Photoresist, 20) on each side of the original glass 10,

상기 감광성필름(20) 표면에 패턴(31)이 형성된 인쇄필름(30)을 각각 부착하는 인쇄필름부착단계(S12),Print film attaching step (S12) for attaching each of the print film 30, the pattern 31 is formed on the surface of the photosensitive film 20,

상기 인쇄필름부착단계(S12)를 거친 원판글라스(10)에 UV(Ultraviolet)를 조사하여 상기 인쇄필름(30)의 패턴(31)을 따라 상기 감광성필름(20)을 경화시키는 노광단계(S13),Exposure step (S13) of curing the photosensitive film 20 along the pattern 31 of the printing film 30 by irradiating UV (Ultraviolet) to the original glass 10 passed through the printing film attaching step (S12). ,

상기 노광단계(S13)를 거친 원판글라스(10)에서 상기 인쇄필름(30)을 제거하는 인쇄필름제거단계(S14), 그리고Print film removal step (S14) for removing the print film 30 in the original glass 10 subjected to the exposure step (S13), and

현상액을 이용하여 상기 감광성필름(20)의 비(非)경화부를 제거하는 현상단계(S15)Developing step (S15) of removing the non-hardened portion of the photosensitive film 20 by using a developer

를 포함하여 이루어진다.
.

여기서 상기 감광성필름부착단계(S11)는 상기 감광성필름(20)을 가열된 롤러를 이용하여 상기 원판글라스(10)에 압착시키는 공정으로 이루어진다.
Here, the photosensitive film attaching step (S11) is performed by pressing the photosensitive film 20 on the disc glass 10 using a heated roller.

상기 인쇄필름(30)은 상기 감광성필름(20) 표면에 각각 적층되며, 이에 형성된 패턴(31)은 UV가 잘 투과될 수 있도록 하되, 상기 패턴(31)이 비(非)형성된 부분은 UV가 차단될 수 있도록 하는 것이 바람직하다.The print film 30 is laminated on the surface of the photosensitive film 20, respectively, the pattern 31 is formed so that the UV can be transmitted well, the portion where the pattern 31 is not formed (UV) is It is desirable to be able to shut off.

상기 패턴(31)은 제작될 글라스윈도우의 형상이 다수 배열되어 이루어지며, 필요에 따라 키 버튼이나 카메라렌즈 등의 장착에 사용되는 장착홀(11a)의 형상을 포함하여 이루어질 수 있다.
The pattern 31 may be formed by arranging a plurality of shapes of the glass window to be manufactured, and may include a shape of a mounting hole 11a used for mounting a key button or a camera lens, if necessary.

결국, 상기 노광단계(S13)를 거친 후 상기 감광성필름(20)은 상기 인쇄필름(30)의 패턴(31)에 위치하게 되는 부분이 UV에 의해 경화되고, 이후 현상액에 의해 상기 감광성필름(20)에서 비(非)경화부가 제거되면 상기 패턴(31)의 형상에 상응하는 형상으로 다수의 패턴층(21)이 형성되는 것이다.
As a result, after the exposure step (S13), the portion of the photosensitive film 20 to be positioned in the pattern 31 of the printing film 30 is cured by UV, and then the photosensitive film 20 by a developer. When the non-cured portion is removed, the plurality of pattern layers 21 are formed in a shape corresponding to the shape of the pattern 31.

상기 에칭단계(S20)는The etching step (S20)

상기 패턴층형성단계(S10)를 거친 원판글라스(10)에서 상기 패턴층(21) 비(非)형성부를 제거하여 다수의 분할글라스(11)를 제작하는 단계이다.
The pattern glass forming step S10 removes the non-formed portion of the pattern layer 21 from the original glass 10 to produce a plurality of split glasses 11.

상기 에칭단계(S20)에서는 금강사 및 산화알루미늄분말을 이용한 샌드에칭 공정을 실시함으로써 상기 원판글라스(10)에서 상기 패턴층(21)이 형성된 부분만을 적출해내게 되고, 따라서 상기 패턴층(21)이 형성된 개수만큼의 분할글라스(11)가 제작된다.In the etching step (S20), by performing a sand etching process using gold steel and aluminum oxide powder, only the portion where the pattern layer 21 is formed in the original glass 10 is extracted, and thus the pattern layer 21 is removed. The divided glass 11 is produced as many as the formed number.

그리고 이때 상기 분할글라스(11)에는 상기 패턴(31) 및 상기 패턴층(21)의 형상에 따라 상기 장착홀(11a)이 함께 형성될 수 있다.
In this case, the mounting glass 11a may be formed together in the split glass 11 according to the shape of the pattern 31 and the pattern layer 21.

상기 박리단계(S30)는The peeling step (S30) is

상기 분할글라스(11)에서 상기 패턴층(21)을 제거하는 단계이다.Removing the pattern layer 21 from the split glass 11 is performed.

상기 박리단계(S30)에서는 박리액을 이용하여 상기 각 분할글라스(11)에 형성된 상기 패턴층(21)을 제거하게 된다.
In the peeling step (S30), the pattern layer 21 formed on each of the split glasses 11 is removed using a peeling solution.

한편, 상기 에칭단계(S20) 또는 상기 박리단계(S30) 이후에는 면취단계(S40)가 더 포함될 수 있다.On the other hand, after the etching step (S20) or the peeling step (S30) may be further included a chamfering step (S40).

상기 면취단계(S40)는 상기 에칭단계(S20) 또는 상기 박리단계(S30)를 거친 상기 분할글라스(11)를 다듬는 단계로서, NC(Numerial Control)가공장치를 이용하여 상기 분할글라스(11)의 테두리를 연마 처리하는 단계이다.The chamfering step (S40) is a step of trimming the split glass 11 through the etching step (S20) or the peeling step (S30). The edge is polished.

이때 상기 분할글라스(11)에 장착홀(11a)이 형성된 경우, 이를 함께 연마 처리하는 것이 바람직하다.
At this time, when the mounting hole (11a) is formed in the split glass 11, it is preferable to polish it together.

또한, 상기 면취단계(S40) 또는 상기 박리단계(S30) 이후에는 필요에 따라 상기 분할글라스(11)를 열처리하는 강화단계(S50)가 더 진행될 수 있으며, 이후 수세단계(S60) 및 건조단계(S70)를 거치면 글라스윈도우의 제조가 완료된다.
In addition, after the chamfering step (S40) or the peeling step (S30), a strengthening step (S50) of heat-treating the split glass 11 as needed may be further progressed, and then washed with water (S60) and drying step ( After passing through S70, the manufacture of the glass window is completed.

10 ; 원판글라스 11 ; 분할글라스
20 ; 감광성필름 21 ; 패턴층
30 ; 인쇄필름 31 ; 패턴10; Original glass 11; Split glass
20; Photosensitive film 21; Pattern layer
30; Printing film 31; pattern

Claims (4)

원판글라스(10)에 포토레지스트 패턴층(21)을 형성하는 패턴층형성단계(S10);
상기 원판글라스(10)에서 상기 패턴층(21) 비(非)형성부를 제거하여 다수의 분할글라스(11)를 제작하는 에칭단계(S20); 및
상기 분할글라스(11)에서 상기 패턴층(21)을 제거하는 박리단계(S30);
를 포함하여 이루어진 글라스윈도우 제조방법.
A pattern layer forming step (S10) of forming a photoresist pattern layer 21 on the disc glass 10;
An etching step (S20) of manufacturing the plurality of divided glasses 11 by removing the non-formed portion of the pattern layer 21 from the disc glass 10; And
A peeling step (S30) of removing the pattern layer 21 from the split glass 11;
Glass window manufacturing method comprising a.
제1항에 있어서,
상기 패턴층형성단계(S10)는
상기 원판글라스(10)의 양면에 감광성필름(20)을 각각 부착하는 감광성필름부착단계(S11),
상기 감광성필름(20) 표면에 패턴(31)이 형성된 인쇄필름(30)을 각각 부착하는 인쇄필름부착단계(S12),
상기 인쇄필름부착단계(S12)를 거친 원판글라스(10)에 UV(Ultraviolet)를 조사하여 상기 인쇄필름(30)의 패턴(31)을 따라 상기 감광성필름(20)을 경화시키는 노광단계(S13),
상기 노광단계(S13)를 거친 원판글라스(10)에서 상기 인쇄필름(30)을 제거하는 인쇄필름제거단계(S14), 그리고
현상액을 이용하여 상기 감광성필름(20)의 비(非)경화부를 제거하는 현상단계(S15)
를 포함하여 이루어진 것을 특징으로 하는 글라스윈도우 제조방법.
The method of claim 1,
The pattern layer forming step (S10)
A photosensitive film attaching step (S11) for attaching the photosensitive film 20 to both surfaces of the disc glass 10, respectively;
Print film attaching step (S12) for attaching each of the print film 30, the pattern 31 is formed on the surface of the photosensitive film 20,
Exposure step (S13) of curing the photosensitive film 20 along the pattern 31 of the printing film 30 by irradiating UV (Ultraviolet) to the original glass 10 passed through the printing film attaching step (S12). ,
Print film removal step (S14) for removing the print film 30 in the original glass 10 subjected to the exposure step (S13), and
Developing step (S15) of removing the non-hardened portion of the photosensitive film 20 by using a developer
Glass window manufacturing method comprising a.
제1항 또는 제2항에 있어서,
상기 에칭단계(S20) 또는 상기 박리단계(S30)를 거친 상기 분할글라스(11)의 테두리를 다듬는 면취단계(S40)를 더 포함하여 이루어진 것을 특징으로 하는 글라스윈도우 제조방법.
The method according to claim 1 or 2,
Glass etching method comprising the step of chamfering (S40) for trimming the edge of the split glass (11) after the etching step (S20) or the peeling step (S30).
제1항 또는 제2항의 방법에 의해 제조된 글라스윈도우.
A glass window manufactured by the method of claim 1.
KR1020110019222A 2011-03-04 2011-03-04 Method for manufacturing glass window and glass window manufactured by the same method KR20120100371A (en)