Abstract

PURPOSE: A moxa cautery is provided to have improved ignitionability and combustibility. CONSTITUTION: A moxa cautery(10) for one-time-use moxa apparatus(100) comprises 1-5 parts by weight of expanded microspheres, on the basis of 100 parts by weight of the moxa carbide. The moxa cautery additionally comprises 3-10 parts by weight of moxa fiber, 5-20 parts by weight of alpha starch, 5-20 parts by weight of sodium alginate.

Description

Moxa Cautery, Moxa Cautery Apparatus and a Manufacturing Method for Moxa cautery}

The present invention relates to a mugwort moxibustion rod and a mugwort moxibustion device for moxibustion on a certain part of the human body.

Moxa moxibustion is a traditional treatment that uses heat and smoke generated when burning wormwood to give heat stimulation and fumigation to acupuncture points or sore spots of the human body, thereby allowing the qi to warm up and warm the blood. This moxibustion has been transmitted as one of the important treatments in oriental medicine along with the treatment of decoction and acupuncture.

The principle of moxa moxibustion is that hot heat and medicinal ingredients of mugwort are absorbed into the body through the menstrual blood of the skin, and cold and moist energy is accumulated to communicate with the parts of the blood by removing the causes of various diseases and treating them.

These moxibustion can be divided roughly into direct and indirect moxibustion.

Direct moxibustion is a method of burning mugwort directly on the skin of the human body, which is called a soybean herb, and is mainly used in the treatment of acupuncture points.

Although direct moxibustion is highly effective by strong thermal stimulation, there is a disadvantage in that a lot of pain is followed during treatment and scars remain on the skin after treatment. Therefore, recently, indirect moxibustion of burning mugwort has been preferred to prevent the mugwort from reaching the human body rather than direct moxibustion.

During the indirect moxibustion, so-called hot air (溫灸) is used to warm certain parts of the human body to circulate the blood and blood well to smooth the metabolism of the human body and to relieve pain. In the above-mentioned warm mouth, the wormwood is usually placed on the moxa plate through which the central hole penetrates and ignites the moxibustion.

The ignition rod, which is ignited from the top, burns from top to bottom and from the outer surface to the inside, and as the combustion progresses, the skin gradually feels the heat. The temperature at the time of firing of the mugwort rod is less than 150 degrees Celsius, but as combustion progresses, the temperature inside the mugwort rod rises to about 350 ° C. The wormwood liquid generated by burning wormwood at a high temperature falls along the hole formed in the center of the mugwort rod and penetrates the human skin to promote blood circulation. These moxa moxibustion varies depending on individual differences, but only 40 to 50 minutes of moxa moxibustion moxa moxibustion is known to show its efficacy in the place.

However, if you want to moxibustion as above, it was difficult for a general user to perform a long time while maintaining a constant temperature of moxa. Accordingly, in recent years, a variety of moxa moxibustion has been provided to facilitate moxa moxibustion, but this moxa moxa is usually in the shape of a jar, and after the moxa is put into the inside of the moth, the moxa moxa is to be moxa moxibustion. When the skin area is flat, smooth moxibustion was possible, but when the skin area was bent or inclined, there was a problem that it was difficult to achieve smooth moxibustion, and there was a problem that the user did not move the body at all during moxa moxibustion. In addition, the smoke generated by ignition of moxa moxibustion during the moxibustion causes the user to feel unpleasant because the smell of moxa is intact. There are problems such as polluting moxibustion moxibustion is good for the body, but there is a phenomenon to avoid. In addition, during the moxibustion, the heat generated by the wormwood is difficult to maintain the integrity of the moxibustion efficiency of the moxibustion or the moxibustion of the moxa moxibustion caused excessive damage to the user's skin had a problem .

Therefore, in order to solve the problems of the conventional moxa moxibustion method, the present invention aims to provide a moxa moxa rod with improved ignition and combustibility.

In addition, the present invention, including the mugwort rod to improve the ignition and combustibility, and easy to place the mugwort device on the desired site, easy to move and not fall well to the user's movement, and at the same time, by including a holder using tourmaline or germanium It is an object of the present invention to provide a disposable moxa moxibustion device to preserve and promote the efficacy of moxa moxibustion.

In addition, an object of the present invention is to provide a method for producing the mugwort moxa bar.

Therefore, the present invention for achieving the above object relates to a mugwort moxibustion rod for disposable mugwort device comprising 1-5 parts by weight of mugwort carbide and 100 parts by weight of the mugwort carbide. Preferably the mugwort moxa bar further comprises 3 to 10 parts by weight of mugwort fibers, 5 to 20 parts by weight of alpha starch, 5 to 20 parts by weight of sodium alginate.

In addition, the present invention is the main moxibustion rod 10, the central holder 20 formed in a cylindrical shape at the lower end of the moxa moxibustion rod so that the lower portion of the moxa moxibustion rod is inserted into a cylindrical shape at the bottom of the holder to be attached to support the holder The present invention relates to a disposable moxa moxibustion device comprising a lower portion of the lower branch pipe 30 serving as a handle and an adhesive portion 40 formed on the lower end of the lower branch pipe so that the lower branch pipe adheres to a predetermined part of the human body for moxibustion. Preferably the holder 20 comprises tourmaline or germanium.

In another aspect, the present invention is the first step of producing a mugwort carbide by heating at a temperature of 450 ~ 500 ℃ 25 ~ 35 minutes using a carbonizing device; 1 to 5 parts by weight of expanded microspheres, 3 to 10 parts by weight of mugwort fiber, 5 to 20 parts by weight of alpha starch, 5 to 20 parts by weight of sodium alginate and 20 to 50 parts by weight of water A second step of preparing a mixture for granulation, followed by granulation; And after molding the granulated moxa moxibustion mixture in a predetermined form, the present invention relates to a method for producing a disposable moxa moxibustion rod for a moxa moxibustion device comprising a third step of coating and drying.

As described above, the mugwort moth bar of the present invention is prepared by preparing, mixing, granulating, forming, coating, and drying the mugwort carbide by low temperature carbonization, so that it is easy to ignite and has no smoke, and there is no effect of odor due to the removal of tartar tar. have. In addition, by coating with natural pozzolanic containing a germanium component to produce the mugwort moth has an effect that can double the efficacy of moxa moxibustion by the release of anion and far infrared rays.

In addition, the moxa moxibustion device according to the present invention can be moxa moxibustion without a separate moxibustion, and to further enhance the efficacy of moxibustion by including a tourmaline or germanium to the central holder holder is inserted into the lower part of the moxa moxibustion, There is an effect to keep the heat retention of the mugwort bar, and on the other hand, because the material of the holder is an inorganic material, there is no fear that the holder during deignition and combustion.

In addition, the moxa moxibustion device according to the present invention to facilitate the movement of the moxa moxibustion device by the lower branch pipe, while the handle of the branch pipe is not hot, there is no fear of burns, in addition to the warming action of the holder in addition to the heat retention action in the branch pipe It is to be able to maintain the long-term heat caused by the combustion of moxa moxa rods can significantly increase moxa moxibustion effect.

In addition, the bottom portion of the moxa moxibustion device is provided with an easy to put or move on the user's body and do not fall well to the user's movement has an effect of remarkably improved the ease of use.

Figure 1 shows a perspective view of the disposable moxa moxibustion apparatus of the present invention.
Figure 2 shows a cross-sectional view of the disposable moxa moxibustion apparatus of the present invention.
Figure 3 shows an example of the use of the disposable moxa moxibustion apparatus of the present invention.

Hereinafter, exemplary embodiments of the present invention will be described in detail with reference to the accompanying drawings.

1 and 2, the moxa moxibustion apparatus 100 of the present invention is a moxa moxibustion rod 10, the central holder 20 formed in a cylindrical shape at the bottom of the moxa moxa rod so that the lower part of the moxa moxa rod is inserted into the holder; The lower branch pipe 30, which is formed in a cylindrical shape at the bottom of the holder to be attached to support the handle, and the adhesive portion 40 formed at the lower end of the lower branch pipe so that the lower branch pipe is adhered to a predetermined portion of the human body for moxibustion. It is configured to include).

The moxa moxibustion rod 10 located at the upper reaches the human body part where the moxa moxibustion device is placed through the central holder 20 formed at the bottom of the moxa moxibustion rod and the lower branch pipe 30 at the bottom of the holder as the moxa moxa rod 10 is ignited and burned. It will be able to provide a thermal effect by moxa moxibustion.

In addition, the central holder 20 is formed in a hollow cylindrical shape at the bottom of the moxa moxibustion rod so that the lower portion of the moxa moxibustion rod 10 is inserted, so that the heat by the combustion of the moxa moxa rod 10 can be kept constant. In addition, the central holder 20 includes a tourmaline or germanium to provide far-infrared rays and anion radiation by tourmaline or germanium during combustion of the mugwort rod 10, thereby improving the efficacy of the mugwort combustion of the mugwort rod 10. By the heat can be kept more constant. In the following preparation example, a center holder was manufactured using tourmaline.

In addition, the lower branch pipe 30 is formed in a cylindrical shape at the bottom of the center holder to be attached to support the center holder 20 to serve as a handle, the moxa moxibustion device 100 of the present invention is moved to the desired human body part. When or after removing the moxa moxibustion device 100 after the end of the moxa treatment is to make it easier to use to hold the lower branch pipe (30).

In addition, since the lower branch pipe (30) is able to further preserve the heat by the combustion of the moxa moxibustion rod 10, in addition to the thermal action by the above-mentioned center holder, the thermal action by the lower branch pipe is added to the same size Compared with the mugwort moxibustion of the heat is kept constant for a long time to see a better moxa moxibustion effect.

In addition, the adhesive part 40 is formed to be attached to the lower end of the lower branch pipe 30 so that the lower branch pipe 30 is adhered to a predetermined body part of the user for moxibustion, so as not to fall off the user's movement well. It is possible to reduce the risk caused by falling down of the moxa moxibustion device 100 according to the user's movement, and the body part can be attached to the bent and inclined parts so that the moxa moxa can be raised without restriction of the human part.

Referring to Figure 3, moxa moxibustion is made in a number of parts of the human body at the same time it is common that a plurality of moxa moxibustion device in one bundle, the moxa moxibustion device 100 of the present invention is attached to a plurality of peeling paper, moxa moxibustion device ( 100) peeled one by one from the release paper and stick directly to the desired human body part and burned the moxa moxibustion, so that the moxibustion can be floated, and there is no hassle to separate the peeling base from each moxa moxibustion device. It can be remarkably improved.

<Production example>

1. Manufacturing of mugwort mop

The preparation of mugwort moxa rods was prepared by first preparing mugwort carbide, then blending and granulating it, followed by molding, coating and drying.

(1) Preparation of mugwort carbide: Low-temperature activated carbide obtained by heating only pure wormwood at a temperature of 450-500 ° C. for 30 minutes without any other additives in a lead-free carbonization apparatus was used as mugwort moxa.

The general carbonization temperature is 500-800 ° C, but in the present invention, a low-temperature carbonization method of 500 ° C or less maintains the temperature at the time when smoke is generated when burning the mugwort, thereby suppressing unnecessary heating to retain the beneficial ingredients contained in the mugwort as much as possible. At the same time, it improves the combustibility of mugwort moxibustion so that there is little smoke.

(2) Blending and granulation: 1 to 5 parts by weight of expanded microspheres, 3 to 10 parts by weight of wormwood fiber, 5 to 20 parts by weight of alpha starch, 5 to 20 parts by weight of sodium alginate, based on 100 parts by weight of wormwood carbide. Part, 20 to 50 parts by weight of water was well blended to prepare the mugwort bar mixture, and granulated using a granulator.

Due to the characteristics of the carbide, the ignition or combustibility is not good, so the wormwood can not be used as the main material of moxibustion, in the manufacture of worm moxibustion rod of the present invention by introducing expanded microspheres as described above to improve the combustibility of wormwood ignition and combustibility Improved. That is, by incorporating the expanded microspheres into the moxa moxibustion rods to make the gap between the moxa moxa rod particles into a more irregular network structure to promote the combustion by increasing the oxygen content in the moxa moxa structure. At this time, it is preferable that the spacing between the moxa moxibustion particles is not easily broken, or the moxa moxibustion is not easily broken, or the moxa moxibustion is maintained at a predetermined time to include 1 to 5 parts by weight in order to obtain the efficacy of moxa moxa.

In addition, the alpha (α) starch can be dried while maintaining a high gelatinization state as a starch in a heat-enhanced state, thereby improving the ignition and combustibility of the mugwort sticks by increasing the drying efficiency in manufacturing the mugwort stick mixture.

In addition, the sodium alginate (Sodium Alginate) as a stabilizer and thickener to increase the viscosity in the production of the mugwort moxa bar mixture to maintain the shape of the mugwort moth bar if it is contained less than 5 parts by weight, the shape of the moxa moth bar is easily broken It may be, when included in excess of 20 parts by weight may inhibit the combustibility of the moxa moxa rod is preferably 5 to 20 parts by weight.

(3) Molding: The compounded granules prepared above were filled into a mold and compression-molded with a low pressure compression press within 0.1 ton to form a mugwort mould.

(4) Coating: First, a coating solution was prepared by mixing 3-15 parts of gelite powder, 100 parts by weight of alcohol, and 1-3 parts by weight of sodium alginate based on 100 parts by weight of water. The gellite powder is a natural pozzolanic powder containing more than 180 times the germanium of ocher, which can be included in the coating liquid to obtain the effect of releasing far infrared rays and anions.

Next, the molded mugwort moxa rod was dried at 85 ° C. for 2 hours in a dryer, and then the surface of the mugwort moxa rod was coated with the moxa moxa bar coating solution.

(5) Drying: The coated mugwort moth was dried at 85 ° C. for at least 3 hours in a drier.

After drying the molded moxa moxa rods as described above, the shape of the moxa moxa rod can be maintained intact by coating and drying again using the prepared coating solution. Particularly, the tourmaline or germanium component is coated on the surface by the moxa moxa. When the rod is burned, far infrared rays and negative ions are released to further increase the effect of moxibustion. In addition, the pores on the surface of the mugwort rod are filled by the pozzolanic reaction of the gelite among the components of the coating solution, so that the capillary pores are reduced and the tissue on the mugwort rod is tightly closed, thereby contributing to the prevention of resorption after drying.

2. Manufacture of center holder

With respect to 100 parts by weight of natural mineral powder such as tourmaline or germanium powder, 7-15 parts by weight binder, 7-15 parts by mold release agent, 3-10 parts by weight colorant, and 13-20 parts by weight as an additive are mixed and mixed in granule form. After making, it is filled into a mold and compression-molded by a compression press of 10 tons or less to form a central holder body of a certain shape. In this production example, 10 parts by weight of dextrin as a binder, 10 parts by weight of Jiyurac ^TM as a release agent, 5 parts by weight of titanium dioxide as a colorant, and 16.7 parts by weight of DET as an additive were mixed and blended to form a central holder body.

By producing a central holder to include a tourmaline or germanium as described above it is possible to give a synergistic effect when the moxibustion by the release of negative ions and far infrared rays.

3. Manufacturing of lower branch pipe

a tube of φ 23.5 (3.5T) x 15mm was prepared.

4. Adhesion Part Manufacturing

The double-sided sticker which worked by Thomson of phi 24 x phi 16.0 was produced.

Moxa moxa rod according to the present invention by increasing the oxygen content in the moxa moxa rod structure tissue by including expanded microspheres to improve the ignition and combustibility, and also by the gelite (natural pozzolanic) coated moxa moxa rods to prevent re-absorption, including Disposable moxa moxibustion device of the present invention can be attached to the desired human body immediately without a separate moxibustion and ignited moxa moxibustion to float the moxibustion, light activity is possible even during moxibustion remarkably improve the convenience of use, holder and It is expected that the industrial applicability will be very high because the heat retention effect of the branch pipe is increased to double the efficacy of moxa.

100: disposable moxa moxibustion device
10: mugwort
20: center holder
30: lower branch pipe
40: adhesion part

Claims

Mugwort carbide and the mugwort moxibustion rod for disposable mugwort device containing 1 to 5 parts by weight of expanded microspheres (Expanded Microspheres) based on 100 parts by weight of mugwort carbide.

The method of claim 1,
The mugwort moxa moxibustion bar for the mugwort moxibustion device further comprising 3 to 10 parts by weight of wormwood fibers, 5 to 20 parts by weight of alpha starch, 5 to 20 parts by weight of sodium alginate.

The mugwort moxa bar 10 according to claim 1,
A central holder 20 formed in a cylindrical shape at the bottom of the mugwort rod so that the bottom of the mugwort rod is inserted, and a lower branch pipe 30 formed in a cylindrical shape at the bottom of the holder to support the holder;
Disposable moxa moxibustion device comprising a pressure-sensitive adhesive portion 40 formed on the lower end of the lower branch pipe so that the lower branch pipe is attached to a predetermined portion of the human body for moxibustion.

The method of claim 3, wherein
The holder 20 is a disposable moxa device containing a tourmaline or germanium.

A first step of producing mugwort carbide by heating at a temperature of 450 to 500 ° C. for 25 to 35 minutes using a carbonization apparatus;
1 to 5 parts by weight of expanded microspheres, 3 to 10 parts by weight of mugwort fiber, 5 to 20 parts by weight of alpha starch, 5 to 20 parts by weight of sodium alginate and 20 to 50 parts by weight of 100 parts by weight of mugwort carbide A second step of preparing a mixture for moxa moxibustion by combining the granules and then granulating it; And
Method for producing a disposable mugwort moxibustion rod for a mugwort moxibustion device comprising the third step of compressing and molding the granulated mixture for moxa moxibustion in a predetermined form.