KR20120013493A

KR20120013493A - Washing detergent of paper type having blister-like structures

Info

Publication number: KR20120013493A
Application number: KR1020100075479A
Authority: KR
Inventors: 유병언
Original assignee: 유병언
Priority date: 2010-08-05
Filing date: 2010-08-05
Publication date: 2012-02-15

Abstract

PURPOSE: A washing detergent of paper type is provided not to generate crack when bending, to have excellent touch feeling, and to be easily dissolved into water, by forming foams in thin film soap. CONSTITUTION: A manufacturing method of a washing detergent of paper type comprise: a step of preparing slurry mixture by adding fatty acid metal salts into water-soluble fibers or water-soluble synthetic resins; a step of manufacturing initial composition by putting air into the slurry and mixing; a step of forming moldings by injection-molding the initial composition to the thin film; and a step of drying the moldings through hot air, and surface treating the same by cosmetic oil.

Description

Washing detergent of paper type having blister-like structures

본 발명은 기포를 가진 종이타입의 세탁세제 및 그 제조방법에 관한 것으로, 더욱 상세하게는, 사용하기 편리하고 사용시 물에 쉽게 용해되어 기포력이 좋고, 세척력이 우수하며, 환경보호는 물론 경제성도 갖춘 기포를 가진 종이타입의 세탁세제 및 그의 제조방법에 관한 것이다. The present invention relates to a paper-type laundry detergent having a bubble and a method of manufacturing the same, and more particularly, it is convenient to use and easily dissolved in water when used, and has good foaming power, excellent cleaning power, environmental protection as well as economic efficiency. The present invention relates to a paper-type laundry detergent having a bubble, and a manufacturing method thereof.

종이비누 제조방법에 관하여는 여러가지 기술들이 개발되어 왔다. 예를들면 일본 특허공개 소57-29520호 공보에 기재된 바와 같이, 비이온성 셀룰로오스 에테르, 지방족 비누류, 천연 비누류 등의 비누성분으로 이루어지는 시트형상 세정제가 널리 알려져 있다. 또한 미국특허 제2005/0003991호에서는 수용성 고분자에 계면활성제, 가소제를 첨가하여 물에 빠르게 용해되는 필름 타입의 비누 또는 세정제를 발표하였다. Various techniques have been developed regarding the manufacturing method of paper soap. For example, as described in Japanese Patent Laid-Open No. 57-29520, sheet-like cleaners composed of soap components such as nonionic cellulose ethers, aliphatic soaps, and natural soaps are widely known. In addition, U.S. Patent No. 2005/0003991 discloses a film-type soap or detergent which dissolves rapidly in water by adding a surfactant and a plasticizer to a water-soluble polymer.

그러나 이러한 폴리비닐알코올과 같은 수용성 필름의 경우 흡습 성질을 지니고 있어 다습한 조건에서 수분을 흡수하여 필름끼리 서로 달라붙고 또한 연화되어 원래의 필름 모양을 유지하지 못하고 파손되는 문제점이 있다. However, in the case of the water-soluble film such as polyvinyl alcohol has a hygroscopic property, there is a problem in that it absorbs moisture in high humidity conditions and the films stick to each other and soften and fail to maintain the original film shape.

이러한 문제점을 해결하기 위해 세제 파우치 제품의 경우 유럽 특허 제253566A호(Procter & Gamble)에서는 비수용성이나 수분산성인 시트물질(부직포직물)로 된 외층 물질과 수용성 필름(폴리에틸렌옥사이드)으로 된 제품을 발표하였다. 그러나 이 제품의 경우 높은 습도에서는 안정적이지만 사용 후 용해되지 않는 잔존 물질이 있어 번거로운 문제점이 있다. In order to solve this problem, European Patent No. 253566A (Procter & Gamble), for the detergent pouch product, announces the product which is made of non-aqueous or water-dispersible sheet material (nonwoven fabric) and water-soluble film (polyethylene oxide). It was. However, this product is troublesome because there is a residual material that is stable at high humidity but does not dissolve after use.

또한 국내 공개 특허 1996-071336호의 경우 셀룰로스 필름이 부착된 기포를 가진 박막상 비누를 발표하였으나 셀룰로스 필름의 경우 흡습성질이 약해 상대적으로 습도에는 안정하나 용해도가 상대적으로 떨어지는 문제점이 있다.In addition, in the case of Korean Patent Publication No. 1996-071336, a thin film soap having bubbles having a cellulose film attached thereto has been disclosed, but the cellulose film has a weak hygroscopic property, which is relatively stable in humidity, but has a relatively poor solubility.

위에서 살펴본 바와 같이 지금까지의 박막상 비누의 제조 방법은 모두가 얇은 종이 또는 수용성 합성수지에 비누액 또는 특수세제를 흡착 건조시키는 것임을 알 수 있다. 그러므로 종전 방법에 있어서는 중간에 반드시 종이 등의 기재 필름이나 특별히 제조된 박막층을 두고 그의 상하면에 비누액을 도포하거나, 흡수 또는 흡착시킨 종이비누를 얻는 방법이 전부이었다. 이 때문에 우선 비누의 두께가 중간층 기재의 두께로 인하여 박막비누의 두께가 한정되어 극히 얇은 비누를 얻기가 곤란하고, 또 비누의 고화시에 비누와 종이 등의 중간층이 함께 고화되므로 박막비누에 경도가 생기게 되어 휴대시 절곡되면 균열되거나 부스러질 뿐만 아니라 더러는 종이, 수지를 중간층으로 사용하기 때문에 비누 사용시에는 이 종이나 수지가 남게 되어 주의를 기울이지 않으면 주변이 불결해지고, 수도 배수관 등이 막히는 사고를 유발하기 쉽다.As described above, it can be seen that all of the methods for producing thin-film soaps have been made by adsorbing and drying a soap liquid or a special detergent on a thin paper or a water-soluble synthetic resin. Therefore, in the conventional method, the method of obtaining the paper soap which always made the base film, such as paper, or specially manufactured thin film layer in the middle, and apply | coated the soap liquid to the upper and lower surfaces, or absorbed or adsorb | sucked was all. Therefore, first of all, the thickness of the soap is limited due to the thickness of the base material, so that it is difficult to obtain an extremely thin soap. When bending, it is not only cracked or chipped, but also some paper and resin are used as intermediate layers. So, when using soap, this paper or resin will be left. If you do not pay attention, the surroundings will become dirty and water drain pipes may be clogged. easy.

그리고, 또 한가지 종전의 박막비누의 결점은 촉감이 부드럽지 못하다는 점에 있다. 이러한 결점은 역시 중간층이 종이 등으로서 비누와 전혀 다른 이물질이 비누층 사이에 개재되어 있기 때문이다. 그리하여 현재 시판중에 있는 종전의 종이비누들 그 자체만으로도 우리의 일상생활에서 휴대의 편리함, 획기적인 아이디어의 소산이라고 할 수 있겠으나 전술한 바와 같은 결점으로 인하여 별로 애용되지 못하고 있는 실정에 있다.Another drawback of previous thin film soaps is that they are not soft to the touch. This drawback is also because the intermediate layer is paper or the like and foreign matter completely different from the soap is interposed between the soap layers. Thus, the existing paper soaps that are currently on the market alone can be said to be the convenience of portability and breakthrough ideas in our daily lives, but they are not used favorably due to the shortcomings mentioned above.

그러므로 당업계에 있어서는 이러한 종전의 결점이 완전 해소된 박막비누의 제조 방법이 적절히 추구되고 있다. 그러기 위해서는 비누와 완전히 친화성이 있는 수용성 중간층을 개발 사용하든가, 아니면 비누 자체만으로 된 박막비누를 제조하지 않으면 안될 것이다.Therefore, in the art, a method for producing a thin film soap in which such a shortcoming is completely solved is pursued appropriately. To this end, it is necessary to develop and use a water-soluble intermediate layer that is completely compatible with soap, or to prepare a thin film soap using soap alone.

그러나, 본 발명자는 그러한 중간층의 개발보다는 오히려 비누에 직접 기재를 균일하게 혼합하여 박막비누를 제조하는 방법에 대하여 장기간 연구하여 오던 중, 비누액(세정액)을 특수한 공정으로 처리하면 더욱 품질이 우수한 기포를 가진 종이타입의 세탁세제를 제조할 수 있음을 알게 되어 본 발명에 이르게 되었다.However, the present inventors have been studying for a long time how to prepare a thin film soap by uniformly mixing the substrate directly into the soap, rather than the development of such an intermediate layer, the bubble of excellent quality if the soap liquid (cleaning liquid) is treated by a special process It was found that the paper-type laundry detergent having a lead to the present invention.

즉, 본 발명은 전술한 바와 같은 종전의 방법에서 처럼 종이나 수용성 합성수지를 중간 기재층으로 별도 사용하지 않는 비누 단일층만으로 된 박막비누의 제조 방법을 개발하여 찌꺼기와 잔유물이 남지않는 종이타입의 세탁세제를 제공하는 것이 주 목적이다. That is, the present invention has developed a method for producing a thin film soap using only a single layer of soap, which does not separately use paper or a water-soluble synthetic resin as an intermediate substrate layer, as in the conventional method as described above, and does not leave paper residue and residues. The main purpose is to provide a detergent.

또 다른 목적은 박막비누에 발포를 형성시킴으로써 촉감이 우수하고 절곡시 균열이 발생하거나 부러지는 일이 없고, 물에 잘 녹는 기포를 가진 종이타입 세탁세제의 제조방법을 제공하기 위한 것이다.Another object of the present invention is to provide a method of manufacturing a paper-type laundry detergent having excellent touch and no cracking or breaking during bending, and foaming well in water.

이와 같은 본 발명의 목적과 잇점을 달성하기 위한 수단은, 수용성 섬유질류 또는 수용성 합성수지류를 용해시킨 용액에 지방산 금속염류를 첨가하여 슬러리 혼합물을 만드는 단계; 상기 슬러리 혼합물에 공기를 주입하면서 교반하여 초기 조성물(A)를 제조하는 단계; 상기 초기 조성물(A)을 박막상으로 사출시켜 사출 성형물(B)을 형성하는 단계; 상기 사출 성형물(B)을 온풍으로 건조시킨 다음에 미용오일류로 표면처리하는 단계로 이루어진 것을 특징으로 한다.Means for achieving the object and advantages of the present invention comprises the steps of adding a fatty acid metal salt to a solution in which water-soluble fibers or water-soluble synthetic resins are dissolved to form a slurry mixture; Preparing an initial composition (A) by stirring while injecting air into the slurry mixture; Injecting the initial composition (A) into a thin film to form an injection molded product (B); The injection molding (B) is characterized in that it consists of drying the surface with warm air and then surface treatment with cosmetic oils.

또한, 본 발명의 기포를 가진 종이타입의 세탁세제는, 상기 방법으로 제조된 스폰지 형태로서 미세한 기포가 전 표면에 걸쳐 반복적, 연속적으로 형성되어 있는 0.013 ~ 0.045 mm의 두께와 0.075 ~ 0.39 kg/㎟의 인장강도를 가지며, 명함모양 또는 두루마리 모양을 갖는 것을 특징으로 한다.In addition, the paper-type laundry detergent having bubbles of the present invention is a sponge produced by the above method, the thickness of 0.013-0.045 mm and 0.075-0.39 kg / mm2 in which fine bubbles are repeatedly and continuously formed over the whole surface. It has a tensile strength of, characterized in that it has a business card shape or scroll shape.

본 발명은 상기에 언급한 바와 같이 본 발명의 기포를 가진 종이타입의 세탁세제를 개발, 제품화으로써 휴대의 간편성과 가정에서도 과다한 세제 사용을 줄일 수 있어 경제적인 효과뿐만 아니라 환경보호에도 기여를 할 수 있는 효과가 있다The present invention, as mentioned above, by developing and commercializing a paper-type laundry detergent with bubbles of the present invention can reduce the use of excessive detergents in the convenience and portable at home can contribute to economic protection as well as environmental protection. Have an effect

본 발명은 사용하기 편리하고 사용시 물에 쉽게 용해되며, 기포력이 좋고 세척력이 우수하며, 경제성도 갖춘 종이타입의 세탁세제와 그 제조 방법을 제공하기 위한 것이다.The present invention is to provide a paper-type laundry detergent and a method for manufacturing the same, which are easy to use and easily soluble in water when used, have good foaming power, excellent washing power, and economical efficiency.

본 발명의 기포를 가진 종이타입의 세탁세제를 제조하는 방법은, 정제수에 수용성 섬유질류 또는 수용성 합성수지류를 65~75℃에서 균질하게 용해시키고, 이 용액에 지방산 금속염류를 첨가하여 슬러리 혼합물을 만들고, 공기를 주입하면서 약 1,200 ~ 1,800rpm의 교반속도로 1 ~ 2시간 교반시켜 초기 조성물(A)을 얻고, 이 초기 조성물(A)을 표면에 미용오일류가 도포되어 있는 컨베이어상에 박막상으로 사출시킨 사출 성형물(B)을 컨베이어로 이송시 수평방향에 대하여 상방 40 ~ 50도의 풍향각도로 70 ~ 80℃의 온풍을 약 0.5 ~ 1.5m/초의 풍량으로 건조시킨 다음 후처리 과정에서 그 표면을 미용오일류로 표면처리하여서 제조한다. In the method for producing a paper-type laundry detergent having bubbles of the present invention, a water-soluble fiber or a water-soluble synthetic resin is homogeneously dissolved in purified water at 65-75 ° C., and a fatty acid metal salt is added to this solution to form a slurry mixture. While injecting air, the mixture was stirred for 1 to 2 hours at a stirring speed of about 1,200 to 1,800 rpm to obtain an initial composition (A), and the initial composition (A) was injected into a thin film on a conveyor coated with cosmetic oils on the surface. When the injection molded product (B) is transferred to a conveyor, the warm air of 70 to 80 ° C. is dried at a wind volume of about 0.5 to 1.5 m / sec at a wind direction angle of 40 to 50 degrees upward with respect to the horizontal direction, and then the surface is treated during the post-treatment process. It is prepared by surface treatment with oils.

본 발명에서 사용되는 수용성 섬유질류 또는 수용성 합성수지류로는 많이 알려진 재료를 이용할 수 있는데, 구입하기에 편리한 메틸셀룰로오스, CMC(Carboxy methyl cellulose) 및 폴리비닐알코올중에서 적어도 하나를 선택하여 사용하는 것이 바람직하다.As the water-soluble fibers or water-soluble synthetic resins used in the present invention, many well-known materials can be used. It is preferable to use at least one of methyl cellulose, CMC (Carboxy methyl cellulose) and polyvinyl alcohol, which are convenient to purchase. .

지방산 금속염류도 공지된 것들, 예컨대 야자유지방산 금속염 및 우지지방산나트륨염 중에서 적어도 하나를 선택하여 사용하는 것이 좋다. 이러한 지방산 금속염은 비누, 세제의 재료이다.Fatty acid metal salts are also preferably selected from at least one of known ones such as palm oil fatty acid metal salts and sodium tallow fatty acid salts. Such fatty acid metal salts are materials of soaps and detergents.

본 발명에서는 이상의 수용성 섬유질류 또는 수용성 합성수지류와 지방산 금속염류가 주재료 이지만, 그 외에 보습제로서 폴리에틸렌글리콜, 스쿠알란, 또 살균제, 향료, 색소, 기타 필요에 따른 성분을 첨가하여 배합할 수 있다.In the present invention, the above-mentioned water-soluble fibers or water-soluble synthetic resins and fatty acid metal salts are the main materials. In addition, as the moisturizing agent, polyethylene glycol, squalane, a fungicide, a fragrance, a dye, and other components as necessary may be added and blended.

폴리에틸렌글리콜은 보습작용이 우수하므로 본 발명 비누가 경화되는 것을 방지하는 효과가 있다. 또한 폴리에틸렌글리콜이 존재함으로써 초기 조성물(A)의 조성시 유화작용이 있으며, 또한 사용후에 피부가 부드러워지는 효과도 기대할 수 있다.Polyethylene glycol is excellent in moisturizing action has an effect of preventing the soap of the present invention is cured. In addition, the presence of polyethylene glycol has an emulsification effect in the composition of the initial composition (A), and also the effect of softening the skin after use can be expected.

전술한 본 발명의 방법에 의하면, 주재료의 하나인 수용성 섬유질류 또는 수용성 합성수지류의 수용액과 지방산 금속염 또는 기타 보습제를 혼합한 슬러리에 공기를 주입하면서 10분간 교반 후 컨베이어상에 박막형태로 사출, 성형시키면서 온풍을 가하면 수용성 섬유질류 또는 수용성 합성수지류가 지방산 금속염과 완전히 혼합된 상태에서 주입된 공기에 의해 발포된 채 온풍으로 20분간 건조 고화되므로 성형된 비누는 로울러에 권취되는 동안에도 절단되지 않는 박막을 형성하며, 더욱이 그 박막에는 균일한 기포가 무수히 형성되어 마치 스폰지와 같은 조직을 가지게 된다. According to the method of the present invention described above, after stirring for 10 minutes while injecting air into a slurry of a mixture of an aqueous solution of a water-soluble fiber or a water-soluble synthetic resin and fatty acid metal salt or other moisturizing agent which is one of the main materials, injection and molding in a thin film form on a conveyor When the hot air is applied, the water-soluble fiber or the water-soluble synthetic resin is dried and solidified by hot air for 20 minutes while being foamed by the injected air in a state where the water-soluble fiber or water-soluble synthetic resin is completely mixed with the fatty acid metal salt. In addition, numerous thin bubbles are formed on the thin film to have a sponge-like structure.

본 발명의 박막비누는 후처리 과정에서도 미용 오일류로 아주 얇게 표면처리하기 때문에 습기가 있는 환경내에서도 서로 접착되는 폐단이 없고 촉감이 더욱 향상된다.Since the thin film soap of the present invention is very thin surface treatment with cosmetic oils even in the post-treatment process, there is no closed end adhered to each other even in a humid environment and the touch is further improved.

대체로 본 발명의 방법에 의한 기포를 가진 박막상 비누에 있어서는 약 0.013 ~ 0.045mm의 두께로 약 0.075 ~ 0.395kg/㎟의 인장강도를 갖는 것으로 확인되었다.In general, it was confirmed that the thin film soap having bubbles according to the method of the present invention had a tensile strength of about 0.075 to 0.395 kg / mm 2 at a thickness of about 0.013 to 0.045 mm.

본 발명 방법에 의해 제조되는 기포를 가진 박막상 비누는 전술한 바와 같이 스폰지 형태로서 미세한 기포(현미경 관찰에 의하면 고무풍선과 같은 기공이 중첩된 구조이다)가 박막비누 전면에 걸쳐 반복적으로 연속되어 있기 때문에 사용시 물에 잘 녹고, 절첩하더라도 주변 기온의 영향에 관계없이 균열되거나 절단되는 일이 없고, 표면에 미용오일류가 얇게 발라져 있으므로 비누 상호간에는 수분을 가하지 않는 한 절대로 접착되는 일이 없다.As described above, the thin film soap having bubbles prepared by the method of the present invention is a sponge-like fine bubbles (microscopic observation shows that the pores such as rubber balloons are overlapped) and is continuously repeated throughout the thin film soap. Therefore, it melts well in water and does not crack or cut regardless of the influence of ambient temperature even when folded, and the beauty oils are thinly coated on the surface so that they never adhere to each other unless moisture is added to each other.

따라서 명함모양, 두루마리모양 등으로 하여 휴대하거나, 화장실, 욕실 등에서 자유로이 사용할 수 있음은 물론, 종전의 종이 비누에서와 같이 중간층을 사용하지 않았기 때문에 종이에 묻어서 미처 용해되지 않는 한 비누의 손실 등과 같은 일이 없이 일정 칫수의 비누 전량을 완전히 사용할 수 있으므로 물자절약과 환경보호 면에서도 대단히 바람직하다.Therefore, it can be carried in the form of a business card, a roll, or the like, or can be used freely in a bathroom, a bathroom, or the like, or a loss of soap unless it is dissolved in a paper because it does not use an intermediate layer as in a conventional paper soap. It is very desirable in terms of material saving and environmental protection, because the entire amount of soap can be completely used without this.

또한 본 발명의 박막비누 제조시에 적절한 향료를 첨가할 수도 있으므로 그것을 소지하고 있을 때에는 체취를 제거할 수 있어 유익하다.In addition, since an appropriate fragrance may be added during the production of the thin film soap of the present invention, it is advantageous because the body odor can be removed.

그러나 무엇보다도 본 발명의 기포를 가진 종이타입 세탁세제의 잇점은 전술한 바와 같이 중간 기층(심재)을 전혀 사용하지 않고도 인장 강도가 적절히 유지되어 용해가 완전히 되는 종이타입 세탁세제라는 것이다.However, above all, the advantage of the paper-type laundry detergent with bubbles of the present invention is that the paper-type laundry detergent is completely dissolved by maintaining the tensile strength without using the intermediate base (core material) as described above.

이와 같은 본 발명을 실시예에 의거하여 더욱 상세히 설명하면 다음과 같으며, 하기 배합예는 본 발명의 이해를 돕기 위한 것일뿐 본 발명이 하기 배합예에 한정되는 것은 아니다.The present invention will be described in more detail based on the following examples, and the following compounding examples are provided only to aid the understanding of the present invention, and the present invention is not limited to the following compounding examples.

실시예 Example

표 1(배합예)Table 1 (Combination Example)

정제수 50.50중량%50.50 wt% of purified water

폴리비닐알코올 5.50중량%5.50 wt% polyvinyl alcohol

폴리에틸렌글리콜 12.00중량%Polyethylene glycol 12.00 wt%

야자유지방산나트륨염 32.00중량%Palm oil fatty acid sodium salt 32.00 weight%

살균제 소량Small amount of fungicide

향 료 미량A small amount of spices

색 소 적량Color quantity

상기 표 1에 따라 정제수에 폴리비닐알코올을 65 ~ 75℃에서 균질하게 용해시켜 균질용액을 얻고, 이 용액에 폴리에틸렌글리콜, 야자유지방산나트륨염, 살균제, 향료 및 색소를 첨가한 혼합물을 얻은 다음, 이 혼합물을 교반장치의 호퍼를 통해 교반탱크에 투입하고, 이어서 모터를 작동시켜서 상기 교반탱크의 교반기를 약 1,500rpm으로 약 1 ~ 2시간 회전시킨다. 이 회전축의 공기주입날개에 깨끗한 공기를 여과층으로 통하여 교반탱크에 유입시켜 공기와 세제 조성물이 혼합 교반될 때 세제 조성물에 기포를 형성하게 하므로서 기포를 가진 슬러리인 초기 조성물(A)를 형성하게 된다.According to Table 1, polyvinyl alcohol was homogeneously dissolved in purified water at 65 to 75 ° C. to obtain a homogeneous solution, and a polyethylene glycol, palm oil fatty acid sodium salt, fungicide, flavoring agent, and a pigment were added to this solution. The mixture is introduced into the stirring tank through the hopper of the stirring apparatus, and then the motor is operated to rotate the stirrer of the stirring tank at about 1,500 rpm for about 1 to 2 hours. Clean air is introduced into the agitation tank through the air injection wing of the rotating shaft to form bubbles in the detergent composition when the air and the detergent composition are mixed and stirred, thereby forming an initial composition (A) having a slurry with bubbles. .

교반장치의 측면에 설치된 투시창을 통해 상기 초기 조성물(A)의 점도와 기포상태를 검사하고, 교반이 완료되면 밸브를 열어 회전축의 하단부에 부착시킨 배출날개에 의한 배출력으로 상기 초기 조성물(A)를 배출구를 경유하여 저장조에 이송시켜 저장시킨다.Examine the viscosity and bubble state of the initial composition (A) through a viewing window installed on the side of the stirring device, and when the stirring is completed, the initial composition (A) by the discharge force by the discharge wing attached to the lower end of the rotary shaft by opening the valve It is transferred to a storage tank via an outlet and stored.

다음에 상기 저장조의 하방에 설치된 밸브를 열어 상기 초기 조성물(A)를 사출기에 공급한다. 사출기에 공급된 초기 조성물(A)은 스크류의 사출력에 따라 사출기의 일단의 일직선상에 개구시킨 구경이 극히 좁은 사출구를 통해 이 사출구의 하방에 연결된 로울러에 의해 수평방향으로 움직이는 미용오일류가 표면에 묻어 있는 컨베이어 상에 사출 성형물(B)을 사출시킴으로써 초기 조성물(A)은 박막 상태의 기포를 가진 종이타입의 세탁세제를 형성하게 된다. 이 때 컨베이어 상부에 적절한 높이와 위치에 컨베이어의 수평이동 방향에 대하여 상방으로 약 45도 각도의 풍향각을 가지도록 설치한 건조기에 의해 70 ~ 80℃의 온풍을 상기 컨베이어로 이송중인 박막비누 상에 1m/초의 풍량을 가한다.Next, the valve provided below the reservoir is opened to supply the initial composition (A) to the injection machine. The initial composition (A) supplied to the injection machine has cosmetic oils that move horizontally by a roller connected to the lower part of the injection hole through an injection hole having a very narrow aperture opened at one end of the injection machine according to the dead power of the screw. By injecting the injection molding (B) on a conveyor buried on the surface, the initial composition (A) forms a paper-type laundry detergent having bubbles in a thin film state. At this time, the hot air of 70 ~ 80 ℃ on the thin film soap being transferred to the conveyor by a dryer installed at an appropriate height and position to have a wind angle of about 45 degrees upward with respect to the horizontal movement direction of the conveyor. Add 1m / sec air volume.

이에 따라 박막상태의 종이비누는 적절히 건조되면서 기포를 가진 종이타입의 세탁세제를 형성하게 되고, 이어서 컨베이어의 종단부에 이송되어 온 비누 박막(필름)을 분리 로울러에 의해 박막을 컨베이어에서 분리시켜서 표면처리 로울러를 거쳐 최종 권취로울러에 권취시킨다. 상기 로울러를 통과할 때에는 박막표면에 미용오일등을 도포하여 표면처리를 행할 수 있다.As a result, the paper soap in the thin film state is properly dried to form a paper-type laundry detergent with bubbles, and the soap thin film (film) transferred to the end of the conveyor is separated from the conveyor by a separation roller to the surface. It is wound up to the final winding roller via the processing roller. When passing through the roller, surface treatment may be performed by applying cosmetic oil or the like to the thin film surface.

최종 권취된 기포를 가진 종이타입의 세탁세제는 명함형, 두루마리형 등의 소정 칫수로 절단 및 포장하여 제품으로 할 수 있다.Paper-type laundry detergent having a final wound bubble may be cut and packaged into a predetermined dimension such as a business card type or a roll type to produce a product.

Claims

Adding a fatty acid metal salt to a solution in which a water-soluble fiber or a water-soluble synthetic resin is dissolved to form a slurry mixture;
Preparing an initial composition (A) by stirring while injecting air into the slurry mixture;
Injecting the initial composition (A) into a thin film to form an injection molded product (B);
Method for producing a paper-type laundry detergent with bubbles, characterized in that the injection molded product (B) is dried by warm air and then surface treated with cosmetic oils.

The method according to claim 1,
The water-soluble fibers or water-soluble synthetic resins are selected from at least one selected from methyl cellulose, CMC and polyvinyl alcohol, and the fatty acid metal salts are selected from the group consisting of palm oil fatty acid metal salts and sodium tallow fatty acid. Method for producing a laundry detergent of paper type having.

The method according to claim 1,
The other moisturizing agent is polyethylene glycol, squalane, and a disinfectant, fragrance, pigment, characterized in that the manufacturing method of paper-type laundry detergent having a bubble.

The method according to claim 1,
Method of producing a paper-type laundry detergent having bubbles, characterized in that for stirring for 1 to 2 hours at a stirring speed of 1,200 ~ 1,800rpm after injecting air to the slurry mixture.

The method according to claim 1,
The injection molding (B) is a manufacturing method of a paper-type laundry detergent having bubbles, characterized in that the injection on the conveyor is applied cosmetic cosmetics.

The method according to claim 1,
The drying step is a paper with bubbles, characterized in that carried out at a wind speed of 0.5 ~ 1.5m / sec with a warm air of 70 ~ 80 ℃ at a wind direction angle of 40 to 50 degrees upward relative to the horizontal direction during the transport of the injection molding (B) Method of manufacturing a laundry detergent of the type.

Sponge shape prepared by the method according to claim 1 to 5 characterized in that the fine bubbles have a thickness of 0.013 ~ 0.045 mm and a tensile strength of 0.075 ~ 0.39 kg / ㎜ formed repeatedly and continuously over the entire surface Paper-type laundry detergent with bubble to say.

The method of claim 6,
The paper-type laundry detergent is a paper-type laundry detergent having bubbles, characterized in that the card-like or rolled.