KR20100093679A - Multipotent adsorbent using sludge in water supplies or ashes - Google Patents

Abstract

PURPOSE: Since having the far better specific surface area, all kinds of the harmful materials and dirt kind can be adsorbed. Particularly, 10kg is sprinkled based on the piggery 330m. CONSTITUTION: A multi-functional adsorbent With you who is dried with cold wind and is crushed. Because of the constant error, the phosphoric acid supply source of 5~15 parts by weight is mixed about 100 parts by weight and it stirs and ages 10~30 for hour. With the powder phosphoric acid material heating in 100°C~300°C 5~15 for hour and is matured. With the crushed you dried with cold wind is smashed. Because of the constant error, the sulfuric acid supply source of 5~15 parts by weight is mixed about 100 parts by weight and it stirs and ages 10~30 for hour.

Description

Multipotent Adsorbent Using Sludge in Water Supplies or Ashes

The present invention relates to an adsorbent for adsorbing odor-causing substances and fine dust and the like, and pig mortar reducing agent, manure fertilizer additive, activated carbon substitute, and industrial deodorant including the adsorbent. Specifically, the present invention relates to a multifunctional adsorbent that can be applied to various sites manufactured by mixing purified sludge or ash with waste sulfuric acid and waste phosphoric acid. More specifically, the adsorbent according to the present invention reduces pig mortality and improves the growth environment, pig mortar reducing agent, manure additive additive to control the smell of peculiar odor, activated carbon substitute used for filter in dust collection equipment, various odor induction It can be applied to industrial deodorant which controls odor by applying to facility.

Sewage sludge has been recycled to pollen materials, land improvers, landfill materials, bricks, etc., but it is known that wastewater is difficult to sell or commercialize due to the low treatment cost. However, Sow sludge is composed of allium-based components, silicon, and organic materials, so that various types of applications are possible, and it is a waste with high need for recycling.

While the demand for recycling of purified water sludge is increasing, the purified water sludge has the same properties as cakes, so there is a limit in reducing the moisture content, which causes problems in commercialization. The inventors of the present invention repeated the experiment and analysis of the above problems, and developed a method of dramatically reducing the water content using phosphoric acid or sulfuric acid to complete the purified sludge as an adsorbent, and similar methods were applied to ashes to adsorbents. It was completed as.

On the other hand, the present invention by applying the adsorbent in a variety of fields, firstly, by controlling the ammonia generated in pigs and collecting fine dust to reduce the pig mortality at the same time, and secondly, as a good raw material of fertilizer To solve the problem that the range of application is limited due to the bad smell of poultry, it provides additives necessary to produce manure fertilizer with excellent efficacy. Third, it is difficult to secure raw materials and provides substitute of activated carbon which is continuously increasing in price. By saving foreign currency and providing cheaper products to consumers, Fourth, industrial deodorants that control various types of odors generated from environmental foundations, food processing plants and other odor-producing facilities, and control odors generated from refrigerators and vehicles. It is to provide.

Since the sludge having undergone physical dehydration has a cake state, it is difficult to expect a decrease in moisture content anymore. However, according to the present invention, by mixing an appropriate amount of phosphoric acid or sulfuric acid and stirring for a predetermined time, after the aging process, the pore water, chemical bonding water, surface water, etc. distributed in the constant sludge is dissociated to bring additional water content reduction, The mixture of purified water sludge and phosphoric acid has a structure of Poriferous Multiple Cylinder (PMC), and afterwards, it is possible to provide a multifunctional adsorbent by maximizing the specific surface area through a drying process.

The adsorbent according to the present invention can adsorb various harmful substances and dusts, which is understood to be due to the superior specific surface area by the PMC structure. In particular, when spraying 10kg of the adsorbent according to the present invention on the basis of pigs 330m ² , to control the odor generated in pigs from the next day to reduce the mortality rate of pigs and improve the growth environment, and consequently easy livestock wastewater treatment It will increase the income of livestock farmers and improve the work of pig workers.

In addition, since the flour is continuously produced a large amount of odor, even though it is composed of an excellent component as a fertilizer, it is difficult to control the odor is difficult to resource the compost. However, when using the manure fertilizer additive containing the adsorbent according to the present application can effectively control the malodor can be actively utilized manure fertilizer. When stirring by adding a 10% weight ratio of quicklime to the system, the moisture in the system decreases due to the hydration reaction of the quicklime, and the pH changes to alkali as the temperature rises to about 40. After 1 hour, the adsorbent according to the present is added and stirred. When the odor is controlled after about 3 hours, 98% of the odor generated after 24 hours is controlled, and at the same time, the manure fertilizer having an excellent fertilizer component can be produced. These manure fertilizers are less odor than the fermentation compost and excellent fertilizer components can contribute to the generation of a side income of farmers operating the poultry farm, and also helps to operate the sewage treatment facilities.

It is observed that the adsorbent according to the present invention has a specific surface area of 2 to 4 times larger than that of activated carbon, which shows that the physical adsorption capacity is excellent. In general, activated carbon is not known to adsorb various odorous substances, but the adsorbent according to the present invention can control not only the field of application of activated carbon, but also the odorous substances that activated carbon does not control, and can sufficiently replace the existing activated carbon.

In addition, food waste and slaughter residues are generally known as representative aversive odor-causing substances that cause thousands of odors including polymer-based odors such as aldehydes, sulfides, and amines. When the mixture of the adsorbent according to the present invention is mixed with 10-30% by weight, the odor is controlled from 1 hour, and after 24 hours, more than 98% of the odor is generated to improve working conditions. Inducement blocking, various recycling measures can be established.

Observing the adsorbent according to the present invention by SEM (electron microscope), it can be seen that the structure contains a large amount of Poriferous Multiple Cylinder (PMC), the adsorbent according to the present invention is a multi-functional Can have 1 shows an image of the adsorbent according to the present invention at SEM of 9000 magnification. As can be seen in Figure 1, the adsorbent according to the present invention has a multilayer porous cylindrical structure, the shape is powder or pellets, the hardness is characterized in that 92% or more.

In one aspect of the present invention, the adsorbent containing the purified sludge is described in detail. Sludge sludge used as the main raw material of the present invention is a final product generated in the course of water treatment, and refers to a microbial mass separated by physicochemically floating or sedimenting after being propagated by ingesting nutrients dissolved in the constant water. By the way, such water purification sludge has hardly been recycled, and is mainly dumped at sea and buried, and thus the problem of environmental pollution has emerged.

As a result of various experiments, it can be recycled to have useful characteristics for the environmental industry without causing environmental problems, and it is expected that its utility value will continue to increase in the future, but its utilization is very small at present. According to the present invention, by utilizing such a constant water sludge, it is possible to provide an adsorbent which not only contributes to pollution prevention but also has excellent adsorption capacity.

The adsorbent according to the present application uses cold sludge dried with stirring. Preferably, the adsorbent is crushed dried sludge as described above, mixed and stirred 5-15 parts by weight of phosphoric acid source with respect to the crushed purified sludge and 100 parts by weight of the purified sludge, stirred and aged for 10 to 30 hours, and 100 to 300 100 to 200 mesh powdered phosphoric acid material aged by heating at 5 ° C. for 5 to 15 hours, further comprising mixing 5-15 parts by weight of sulfuric acid source with respect to 100 parts by weight of the crushed sludge Aged aging for 30 hours, and 100-200 mesh powdered sulfuric acid material aged by heating at 100-300 ° C. for 5-15 hours.

At this time, the phosphoric acid source or sulfuric acid source is preferably phosphoric acid or sulfuric acid. However, it is not necessary to use expensive phosphoric acid or sulfuric acid, and inexpensive recycled phosphoric acid or sulfuric acid can be used. Specifically, as long as the phosphoric acid concentration is 60% to 90%, waste phosphoric acid and regenerated phosphoric acid may also be used, and waste phosphoric acid that is used after use as an etching solution in a semiconductor manufacturing process may be used. On the other hand, sulfuric acid source can be used sulfuric acid, regeneration sulfuric acid if the sulfuric acid concentration is 30 ~ 70%.

In another embodiment of the present invention, the adsorbent may use ash, which is a byproduct of thermal power generation, instead of the above-mentioned sludge. Ash is an essential by-product of thermal power plants, and one thermal power plant generates a large amount of about 80,000 to 100,000 tons per year, but more than 90% of landfills are buried because there is no proper recycling plan.

However, ash can be recycled to have useful characteristics for the environmental industry without causing environmental problems as a result of various experiments, and it is expected that its utilization value will increase in the future, but its utilization is very small at present. According to the present invention, by utilizing such an ash, it is possible to provide an adsorbent excellent in adsorption capacity as well as contributing to pollution prevention.

Another aspect of the present invention relates to an adsorbent prepared by using water sludge or ash as a main raw material, and the adsorbent is characterized in that it is versatile, which is applicable to various fields such as pig sand, manure fertilizer, odor inducing facilities, and dust collecting facilities.

The adsorbent according to the present invention is a highly functional recycled product made using only by-products, and although the manufacturing cost is very low, the adsorption effect is much better than that of the conventional adsorbent. The adsorbent of the present invention can be applied as a pig mortality reducing agent, manure fertilizer additive, activated carbon substitute, industrial deodorant, and the like.

First, the application example of the pig lung mortality reducing agent containing the adsorbent according to the present invention will be described. Pigs, regardless of location or season, have intense breathing gas on their eyes and nose, making it difficult for the average person to breathe and keep their eyes open. Pigs are always congested in their eyes, and their eyes are pinched, and they lie down almost except when they eat. This phenomenon is addicted to a large amount of ammonia gas generated in the manure. Ammonia is inhaled through the respiratory organs of pigs along with the dust in the air, which acts as a major cause of pig mortality, but can still efficiently control ammonia gas. There is no commercial product in the market, so it is burning the farmers.

After spraying the pig mortality reducing agent comprising the adsorbent according to the present invention to the bottom of 1 kg per pig area 33 m ² , ammonia concentration begins to decrease after about 3 hours and ammonia is effectively reduced after 24 hours. The day after the spray, you can feel the disappearance of the gas that stabs the eyes and nose of the person, and you can see the redness of the pig's eyeballs begin to relieve, You will see that.

As a result, it is believed that it contributes to raising the income of livestock farmers by reducing the mortality rate of pigs and improving the growth environment, and contributing to enhancing the competitiveness of workers and improving the quality of life of livestock farmers by improving the working environment of workers.

Next, in the case of chicken flour, it contains nitrogen, phosphorus, organic matter, etc., but it is recognized as an excellent raw material of fertilizer. However, a large amount of odor by uric acid and other causative substances is caused by deterioration of fertilizer working efficiency and secondary gas generation. Due to various problems such as dead-ends, the reality is that they are avoiding use in fertilizer factories and farms. On the other hand, composts made from dairy or pig meals are becoming less profitable due to the continuous rise in sawdust prices and supply shortages.

When the manure is produced as a fertilizer using the manure fertilizer additive containing the adsorbent according to the present invention, it was confirmed through field tests that a good fertilizer can be made without using sawdust. When concrete case is indicated, when stirring and mixing 10 parts by weight of quicklime with 100 parts by weight of quicklime, the quicklime absorbs the water in the powder and causes a hydration reaction to generate heat above 25 to 40 degrees. Is changed. If the type of odor generated in this process is changed and reacted for about 1 hour, and then the manure additive is added and stirred, 95% of the odor generated after 24 hours starts to control the odor. The control is reduced. You can also see white mold on the surface, which means that the ripening process takes place.

The manure fertilizer produced in this way was tested to meet the legal conditions as a compost through the fertilizer process standard test, and lettuce cultivation experiments showed that the lettuce yield between the manure spreading and non-spreading was about 30%. Furthermore, these manure fertilizers are added with quicklime to improve the soil, and the inherent fertilizer effect and calcium, the main ingredient of lime, enhance the crop's texture and nutrient absorption in the land, resulting in higher crop quality and yield. do.

Next, the adsorbent according to the present invention can also be utilized as an alternative to activated carbon. Activated carbon is mainly palm-based activated carbon and coal-based activated carbon, which is dependent on imports. The main source of import of coal-based activated carbon is China. In 2006, the arrival of Incheon Port was 700,000 won per ton, and currently imports at 1.5 million won per ton. The price has soared more than twice, increasing the burden on the company. In addition, the development of alternative materials is urgent given that the Chinese government is gradually reducing the export of natural resources. In addition, most plant facilities operating in Korea require dust collection facilities and odor prevention facilities in accordance with the related laws. Most of them use activated carbon as adsorbent and the market size is estimated to be about 1 trillion won per year.

It is observed that the adsorbent according to the present invention has a specific surface area of about 2 to 4 times larger than that of coal-based activated carbon, which is due to the above-described PMC structure. Can be replaced sufficiently. In general, activated carbon is known to be effective for adsorption of a specific malodorous substance, and the adsorbent according to the present invention can absorb and control a malodorous substance that activated carbon cannot control in addition to the specific malodorous substance. In addition, the iodine adsorption test results were measured at more than 1,050g / g, the hardness was measured at more than 92% was confirmed to meet the specifications of the existing activated carbon.

The adsorbent according to the present invention is evaluated to have the same or superior adsorption capacity with activated carbon by the PMC. Thus, the present inventors prepare the adsorbent according to the present invention in powder form and pellets, and process the leather processing plant and food waste. The application of on-site applications in facilities, composting plants, slaughterhouses, etc. confirmed the potential as an activated carbon substitute. A granular adsorbent prepared according to the invention is shown in FIG. 2.

As a specific application, a large amount of odor was generated in a leather factory in Busan, which caused civil complaints and had a great negative effect on worker's work efficiency. Occurrence of odor began to elapse after 48 hours, and it was confirmed that the odor was controlled so that detection by sensory method was difficult.

Finally, the adsorbent according to the present application can be applied as an industrial deodorant and the inventors have confirmed this through several routes. Representative examples include food waste and slaughter residues. They contain aldehydes, amines, sulfides and many other odorous substances, and there is no deodorant that can effectively control such odorous substances. It is also causing another problem such as deterioration.

However, by mixing 10-30 parts by weight of the adsorbent (industrial deodorant) according to the present invention to 100 parts by weight of copper material and aging at room temperature, the odor generated after 24 hours is reduced by more than 98% to improve the working environment of workers, It will be useful as an industrial deodorant by bringing various effects such as securing a recycling point and solving odor complaints.

Preferred methods of preparing the adsorbent according to the invention are detailed.

Preferably, the adsorbent according to the present invention comprises: a first step of air drying with stirring the purified sludge; A second step of crushing the cold-dried purified sludge; A third step of mixing and stirring the phosphate material selected from the group consisting of waste phosphoric acid, regenerated phosphoric acid and phosphoric acid and stirring the crushed purified sludge for 10 to 30 hours; A fourth step of mixing and stirring a sulfuric acid material selected from the group consisting of waste sulfuric acid, regenerated sulfuric acid and sulfuric acid and the crushed purified sludge for 10 to 30 hours; A fifth step of powdering the resultant of the third and fourth steps by heating at 100 to 300 ° C. for 5 to 15 hours; A sixth step of grinding the resultant product of the fifth step into 100 to 150 meshes; The result of the third step and the fourth step through the sixth step may be prepared by a method consisting of the seventh step of mixing the mixing ratio (A) to 55%: 45% <A <100: 0%.

Optionally, in the above method, the purified sludge and the phosphate material and the sulfuric acid may be mixed at the same time. In this case, the third and fourth steps may be performed by mixing the crushed purified sludge and the phosphate and the sulfuric acid together. Is possible.

In addition, the deodorant of the present invention is preferably a phosphate material selected from the group consisting of waste phosphoric acid, regenerated phosphoric acid, phosphoric acid and a sulfuric acid material selected from the group consisting of a first deodorant, waste sulfuric acid, regenerative sulfuric acid, sulfuric acid It can be prepared by a method of preparing a second deodorant mixed with the water sludge, and a third deodorant mixed with the first deodorant and the second deodorant, the first deodorant and the second deodorant forming the third deodorant in the present invention The content ratio (A) of preferably satisfies the range of 55:45 <A <100: 0.

Hereinafter, the method of preparing the adsorbent according to the present invention will be described in more detail step by step.

In the present invention, the first step of preparing the adsorbent is to perform cold air drying while stirring the purified sludge. While stirring may be used a general stirrer used in the art, it is preferred to use a rotary stirrer. In addition, it is preferable to carry out cold air drying or room temperature drying at the time of drying, and it is preferable to carry out drying for about 1 day-2 days or more preferably the period beyond.

After drying the purified sludge, it is crushed using a crusher, and then mixed with a mixture of waste phosphoric acid or regenerated phosphoric acid or phosphoric acid, and aged for 10 to 30 hours. At this time, it is also possible to use an ash instead of optionally dried purified sludge.

The amount of waste phosphoric acid or regenerative phosphoric acid or phosphoric acid is preferably added in an amount of 5 parts by weight to 15 parts by weight based on the total mass of the purified sludge or ash. Similarly, in the case of adding spent sulfuric acid, regenerated sulfuric acid or sulfuric acid after drying the sludge, the amount thereof is preferably about 5 parts by weight to 15 parts by weight based on the total amount of the purified sludge or ash.

Then, these are reacted at 100 to 300 for 5 to 15 hours to react the mixtures. At this time, the mixture of purified sludge and / or ash and waste phosphoric acid (or recycled phosphoric acid or phosphoric acid) and the mixture of purified sludge and / or ash and waste sulfuric acid (or recycled sulfuric acid or sulfuric acid) are separately heated. It is also possible to use the results separately or to combine them properly.

They are then crushed into 100-200 mesh using a Tyler Standard Sieve, followed by a mixture (first deodorant) such as purified sludge and / or ash and waste phosphate, and purified sludge and / or ash. The mixture with the spent sulfuric acid (second deodorant) is mixed with each other to produce a final deodorant (third deodorant), the mixing ratio (A) of which is preferably 50:50 <A <100: 10 by mass.

In a preferred embodiment, a total of four kinds of adsorbents can be produced as described above, and each of these adsorbents can be specialized for each application.

Hereinafter, specific embodiment of this invention is described. However, the following embodiment only introduces the preferable aspect of this invention, and this invention is not limited to the aspect shown in these Examples.

Example  1 to Example  6

The sludge and / or ash was cold-dried for 1 day and then crushed using a crusher. The sludge and / or ash was then mixed with waste phosphoric acid at a concentration of 63% or spent sulfuric acid at a concentration of 50% and heated at 200 for 10 hours, which was then ground to 200 mesh. The amount of purified sludge, ash, waste phosphoric acid and waste sulfuric acid, and a detailed manufacturing method are shown in Table 1 below.

Water purifier
ash
Waste Phosphoric Acid
Spent sulfuric acid
quite
Example 1

125 g
12 g
Prepared by mixing 125g of purified water with 12g of waste phosphoric acid and heating it at 200 for 10 hours.

Example 2

125 g
12 g
Prepared by mixing 125g of purified water with 12g of waste sulfuric acid and heating it at 200 for 10 hours.

Example 3
125 g
6.25 g
6.25 g
Prepared by mixing 62.5g of purified water sludge with 6.25g of waste phosphoric acid and heating it at 200 hours for 10 hours.

Example 4
62.5 g
62.5 g
12.5 g
62.5 g of purified water sludge and 62.5 g of ash are mixed first, and then mixed with 12.5 g of waste phosphoric acid and heated at 200 for 10 hours.

Example 5
62.5 g
2.5g One
2.5g
62.5 g of purified water sludge and 62.5 g of ash are mixed first, and then mixed with 12.5 g of waste sulfuric acid and heated at 200 for 10 hours.

Example 6
2.5g
2.5g
62.5 g
62.5 g
Prepared by mixing 62.5g of purified water sludge with 6.25g of waste phosphoric acid and heating it at 200 hours for 10 hours.

The following is an example of the actual test. Test Example 1 is applied to pig mortality reducing agent, Test Example 2 is applied to fertilizer additives, and Test Example 3 is applied to activated carbon substitutes. Example 4 shows an application example for the industrial deodorant, the adsorbent according to the present invention has a versatility that can be applied to various fields in addition to.

Test Example  One

The deodorization experiment was performed using the pig mortality reducing agent prepared in Examples 1-6. 10 kg of pig powder was mixed in a mixed digestion reactor, mixed for 5 minutes, and evenly mixed. After 2 minutes of 2 kg of pig lung reducing agent was stirred, the ammonia concentration was first measured by a detection tube. Are recorded and presented in Table 2.

Pig mortality reducing agent
Elapsed time
(minute)
Money
(ppm)
Money Bundle + Pig Lung Reduction Agent
(ppm)
Ammonia Control Rate (%)
Example 1


5
150
-
-
25
149
70
53.02
185
150
15
90.00
365
147
7
95.24
725
145
5
96.55
1445
140
2
98.57

Test Example  2

Deodorization experiments were carried out using the fertilizer additives prepared in Examples 1-6. Put 10 kg of poultry in the mixed digestion reactor, mix it by stirring for 5 minutes, mix 1 kg of quicklime and stir the reaction time so that the hydration reaction takes place for 1 hour, and then add 2 kg of fertilizer additives and stir for about 30 minutes. Since the first measurement of the ammonia concentration with a detection tube from the beginning and then measured a total of five times to record the results are shown in Table 3.

Fertilizer Additives
Elapsed time
(minute)
Step by step + quicklime
(ppm)
Poultry + quicklime + fertilizer additives (ppm)
Ammonia Control Rate (%)


Example 2


5
340
-
-
65
450
420
06.67
95
430
370
13.95
185
425
174
59.60
725
410
57
86.10
1445
370
8
97.84

Test Example  3

Experiments were carried out using the adsorbents prepared in Examples 1-6 for applicability as activated carbon substitutes. The activated carbon substitute (adsorbent) was molded into pellets having a diameter of 5 mm, and then the adsorption amount and the hardness of iodine were confirmed.

Item
1st grade
2nd class
Level 3
Activated Carbon Alternatives
Loss on Drying (%)
5 or less
5 or less
5 or less
5
Hardness(%)
over 90
over 90
over 90
92
Filling density (g / ml)
0.48 or less
0.52 or less
0.56 or less
0.53
Iodine Adsorption (mg / g)
1,100 or more
1,000 or more
More than 900
1,050
Benzene equilibrium adsorption performance (%)
35 or more
33 or more
30 or more
33
Particle size (%)
95 or more
over 90
over 90
93

Test Example  4

Adsorption experiments were performed using the industrial deodorant prepared in Examples 1-6. The industrial deodorant (adsorbent) is molded into pellets with a diameter of 5mm, and then put into a bag filter and installed in an odor prevention facility with a capacity of 20 cc / cm ² / sec installed in the slaughterhouse. Presented in 5.

unit: %
Industrial deodorants
Bag Filter (PE)
Bag Filter (Industrial Deodorant)
Example 3
95
94

As can be seen from the results summarized in the above table, the adsorbent according to the present invention has excellent adsorptive power, and shows extremely excellent application as a pig waste reducing agent, manure fertilizer additive, activated carbon substitute, and industrial deodorant. It can be seen that the product has high economical efficiency.

When using the adsorbent of the present invention industrially, the government budget of about 20 billion won for the treatment of landfill sludge (landfill, incineration, etc.), the pig waste reduction market estimated to be 90 billion won per year, the amount of 47 billion won Considering the fertilizer additive market, the market of activated carbon nearing KRW 1 trillion annually, and the deodorant market reaching KRW 300 billion annually, the market share is estimated to be 150 billion assuming a 10% market share.

In particular, in the case of activated carbon, it is expected to bring various economic, industrial and environmental positive effects such as blocking foreign currency outflow, securing stable resources, and import substitution effect.

1 is a SEM photograph of an adsorbent according to the present invention at 9000 magnification.

2 is a pellet adsorbent prepared according to the present invention.

Claims (10)

Crush the cold-dried purified sludge, and mix and stir 5-15 parts by weight of phosphoric acid source with respect to the crushed purified sludge and 100 parts by weight of the purified sludge for 10 to 30 hours, and aged at 100 ℃ to 300 ℃ Powdered phosphoric acid material aged by heating for 15 hours; And Crush the cold-dried purified sludge, mix and stir 5-15 parts by weight of a sulfuric acid source with respect to the crushed purified sludge and 100 parts by weight of the purified sludge for 10 to 30 hours, and aged at 100 ° C to 300 ° C. In the adsorbent comprising a powdered sulfuric material aged by heating for 15 hours, The phosphoric acid source is a phosphoric acid concentration of 60 to 90%, at least one selected from the group consisting of waste phosphoric acid, regenerated phosphoric acid and phosphoric acid, The sulfuric acid source is sulfuric acid concentration of 30 to 70%, at least one selected from the group consisting of spent sulfuric acid, regenerated sulfuric acid and sulfuric acid, The powdered phosphate material and the powdered sulfuric acid material is a powder of 100 ~ 200 mesh, The adsorbent has a powder or pellet shape, the hardness is 92% or more, wherein the powder and pellet shape is a multi-layer porous cylindrical structure, characterized in that the multifunctional adsorbent. The adsorbent of claim 1, wherein the adsorbent comprises the powdered phosphate material and the powdered sulfuric acid material such that a mixing ratio (A) is 55%: 45% <A <100%: 0%. Ash and by-product of thermal power generation and mixed with 5 to 15 parts by weight of phosphoric acid source with respect to 100 parts by weight of the ash, stirred and aged for 10 to 30 hours, the powdered phosphoric acid material aged by heating for 5 to 15 hours at 100 ℃ ~ 300 ℃ ; And Ash, a byproduct of thermal power generation, and 5-15 parts by weight of sulfuric acid source were mixed and stirred with respect to 100 parts by weight of the ash, stirred and aged for 10 to 30 hours, and the powdered sulfuric acid material aged by heating for 5 to 15 hours at 100 ° C to 300 ° C. In the adsorbent comprising: The phosphoric acid source is a phosphoric acid concentration of 60 to 90%, at least one selected from the group consisting of waste phosphoric acid, regenerated phosphoric acid and phosphoric acid, The sulfuric acid source is sulfuric acid concentration of 30 to 70%, at least one selected from the group consisting of spent sulfuric acid, regenerated sulfuric acid and sulfuric acid, The powdered phosphate material and the powdered sulfuric acid material is a powder of 100 ~ 200 mesh, The adsorbent has a powder or pellet shape, the hardness is 92% or more, wherein the powder and pellet shape is a multi-layer porous cylindrical structure, characterized in that the multifunctional adsorbent. The adsorbent of claim 3, wherein the powdered phosphate material and the powdered sulfuric acid material are included such that a mixing ratio (A) satisfies 55%: 45% <A <100%: 0%. The adsorbent according to any one of claims 1 to 4, wherein the adsorbent adsorbs at least one selected from the group consisting of ammonia gas, hydrogen sulfide, amines, sulfides, and aldehydes. The adsorbent according to any one of claims 1 to 4, wherein the adsorbent adsorbs dust. A pig mortality reducing agent comprising the adsorbent according to any one of claims 1 to 4 and which can reduce pig mortality. A manure fertilizer additive comprising the adsorbent according to any one of claims 1 to 4, wherein the manure can be recycled as a fertilizer. An activated carbon substitute comprising the adsorbent according to any one of claims 1 to 4 and having a specific surface area capable of replacing activated carbon. An industrial deodorant comprising the adsorbent according to any one of claims 1 to 4.