KR20100046978A - Method for manufacturing ceramic formed material - Google Patents

Method for manufacturing ceramic formed material Download PDF

Info

Publication number
KR20100046978A
KR20100046978A KR1020080106045A KR20080106045A KR20100046978A KR 20100046978 A KR20100046978 A KR 20100046978A KR 1020080106045 A KR1020080106045 A KR 1020080106045A KR 20080106045 A KR20080106045 A KR 20080106045A KR 20100046978 A KR20100046978 A KR 20100046978A
Authority
KR
South Korea
Prior art keywords
particles
pearlite
molded body
ceramic molded
binder
Prior art date
Application number
KR1020080106045A
Other languages
Korean (ko)
Other versions
KR100985136B1 (en
Inventor
강대중
Original Assignee
강대중
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 강대중 filed Critical 강대중
Priority to KR1020080106045A priority Critical patent/KR100985136B1/en
Publication of KR20100046978A publication Critical patent/KR20100046978A/en
Application granted granted Critical
Publication of KR100985136B1 publication Critical patent/KR100985136B1/en

Abstract

PURPOSE: A ceramic molding body for construction is provided to reinforce strength, to prevent dust generated from the pearlite particle and to improve water balancing action of the pearlite particle. CONSTITUTION: A ceramic green body for construction is molded by mixing binder for particle combination and mixture in which the pearlite particle is included. The pearlite particle is manufactured by coating with coating solution in which yellow soil is dispersed in the water on the surface of the pearlite particle and drying. The pearlite particle is manufactured by dipping the pearlite particle in a perfume solution or coating the coating solution on the surface of the pearlite particle and drying after spraying the perfume solution on the pearlite particle. The binder for the particle combination is molasse or the starch solution.

Description

건축용 세라믹 성형체{METHOD FOR MANUFACTURING CERAMIC FORMED MATERIAL}Ceramic molded body for construction {METHOD FOR MANUFACTURING CERAMIC FORMED MATERIAL}

본 발명은 건축용 자재로 사용되며 불연성, 단열성, 경량성, 흡음성, 항균성 등의 기능을 갖는 건축용 세라믹 성형체에 관한 것으로, 보다 상세하게는 펄라이트 입자에 황토를 코팅시키고 그 황토가 코팅된 펄라이트 입자가 포함된 배합물을 바인더로 결합시켜 세라믹 성형체를 제조함으로써 강도를 보강할 수 있고, 펄라이트 입자로부터 발생되는 분진을 방지할 수 있으며, 펄라이트 입자의 수분 조절 작용을 향상시키고, 펄라이트 입자에 침투시킨 향의 지속시간을 증가시킬 수 있는 건축용 세라믹 성형체에 관한 것이다.The present invention relates to a building ceramic molded body which is used as a building material and has a function such as non-combustibility, heat insulation, light weight, sound absorption, antibacterial properties, and more particularly, includes perlite particles coated with ocher and coated with loess. The combined formulation with a binder to produce a ceramic molded body, which can reinforce the strength, prevent dust generated from the pearlite particles, improve the moisture control action of the pearlite particles, and the duration of the fragrance penetrated into the pearlite particles The present invention relates to a ceramic molded body that can increase the.

건축에는 다양한 블록, 판넬 등과 같은 다양한 자재가 사용된다. 최근 들어 생활의 수준이 향상되면서 단열, 흡음 등의 기능이 향상되고 인체에 유해하지 않은 친환경 자재의 이용이 증가하고 있으며, 화재 등과 같은 재해 발생시 재해의 확대를 방지할 수 있는 난연, 불연성 등의 기능을 갖도록 펄라이트나 질석 등을 이용한 건축용 자재에 대한 개발이 많이 이루어지고 있다.In construction, various materials such as various blocks, panels, etc. are used. In recent years, as the standard of living has improved, functions such as insulation and sound absorption have been improved, and the use of eco-friendly materials that are not harmful to the human body has been increasing. Development of building materials using pearlite or vermiculite has been made to have a lot.

상기와 같은 건축용 자재에 이용되는 질석은 흑운모의 변질작용에 의해 생성되는 소재로 진주광택이 나며 산(酸)에 쉽게 분해되고 양이온 교환능력이 크며, 가 열 팽창된 질석은 다공질(多孔質)로 흡수능력이 좋아서 내열재료 및 방음재(防音材)로서 널리 이용되고 있으며, 펄라이트는 진주암, 흑요석, 송지석 등을 고온에서 열처리하여 팽창시킨 불연성 무기질재질로 화재시 유독가스의 발생위험이 전혀 없고 무수한 공극이 형성되어 있어 가볍고 흡음성 및 단열성이 우수한 특성을 지니고 있어 건축용 자재로 많이 이용되고 있다.Vermiculite used in the building materials as described above is a material produced by the alteration of biotite, has a pearl luster, is easily decomposed to acid, has a high cation exchange capacity, and the expanded and expanded vermiculite is porous. Due to its excellent absorption ability, it is widely used as heat-resistant material and soundproofing material.Pearlite is a non-combustible inorganic material that is expanded by heat-treating pearlite, obsidian, and pine stone at high temperature, and there is no risk of toxic gas in case of fire. Since it is formed, it is light, has sound absorption and heat insulating properties, and is widely used as a building material.

예를 들면, 대한민국 등록특허 제10-0541414호에는 팽창된 질석 입자와 펄라이트 입자를 가압성형시켜 샌드위치 판넬에 관한 기술이 개시되어 있고, 대한민국 등록특허 제10-0530015호에는 바인더에 펄라이트 입자 등이 포함된 무기물 미립자를 혼합하고 가압,가열 성형시킨 건축용 판넬이 개시되어 있다.For example, Korean Patent No. 10-0541414 discloses a technology related to a sandwich panel by press molding expanded expanded vermiculite particles and pearlite particles, and Korean Patent No. 10-0530015 includes pearlite particles in a binder. Disclosed is a building panel in which mixed inorganic fine particles are mixed, pressurized, and thermoformed.

일반적으로 펄라이트나 질석을 이용한 건축용 세라믹 성형체는 펄라이트나 질석을 미세한 입자로 분쇄하여 가열 팽창시킨 입자를 규산나트륨과 같은 무기질 바인더에 혼합하여 가압성형시켜 제조된다.In general, a ceramic ceramic molded body made of pearlite or vermiculite is prepared by mixing the expanded and expanded particles by grinding the pearlite or vermiculite into fine particles and mixing them with an inorganic binder such as sodium silicate.

그런데, 상기와 같이 제조된 세라믹 성형체는 규산나트륨이 물에 용해되는 성질이 있어 물이나 습기에 의해 세라믹 성형체의 강도가 저하되고 성형체의 표면에 백화현상이 발생될 뿐만 아니라 열을 받으면 가스가 발생하는 문제점을 갖는다.However, the ceramic molded body manufactured as described above has a property of dissolving sodium silicate in water, so that the strength of the ceramic molded body decreases due to water or moisture and whitening phenomenon occurs on the surface of the molded body. I have a problem.

또한, 상기와 같이 제조된 세라믹 성형체는 펄라이트 입자가 발포된 구조이기 때문에 강도가 약할 뿐만 아니라 성형 과정에서 깨진 펄라이트 입자로부터 분진이 발생되는 단점을 갖는다.In addition, the ceramic molded body manufactured as described above has a disadvantage that the strength is not only weak because of the structure in which the pearlite particles are foamed, and dust is generated from the broken pearlite particles during the molding process.

본 발명은 상기와 같은 단점을 해결하기 위하여 안출된 것으로, 본 발명의 목적은 펄라이트 입자에 황토를 코팅시키고 그 황토가 코팅된 펄라이트 입자가 포함된 배합물을 바인더로 결합시켜 세라믹 성형체를 제조함으로써 강도를 보강할 수 있고, 펄라이트 입자로부터 발생되는 분진을 방지할 수 있으며, 펄라이트 입자의 수분 조절 작용을 향상시키고, 펄라이트 입자에 침투시킨 향의 지속시간을 증가시킬 수 있으며, 불연성, 단열성, 경량성, 흡음성, 항균성 등의 기능을 갖는 건축용 세라믹 성형체를 제공하기 위한 것이다.The present invention has been made in order to solve the above disadvantages, an object of the present invention is to coat the clay containing the pearlite particles and the mixture containing the ocher coated pearlite particles with a binder to prepare a ceramic molded body strength It can reinforce, prevent dust generated from pearlite particles, improve the moisture control action of pearlite particles, increase the duration of fragrance penetrated into pearlite particles, non-flammable, heat insulation, light weight, sound absorption And to provide a ceramic ceramic molded body having a function such as antibacterial properties.

본 발명에 따른 건축용 세라믹 성형체는, 펄라이트 입자가 포함된 배합물에 입자 결합용 바인더를 혼합하여 성형시킨 건축용 세라믹 성형체에 있어서, 상기 펄라이트 입자는 표면에 황토가 물에 분산된 코팅용액이 코팅되어 건조된 것을 특징으로 한다.The building ceramic molded body according to the present invention is a building ceramic molded body formed by mixing a binder for mixing particles in a blend containing pearlite particles, wherein the pearlite particles are coated with a coating solution in which ocher is dispersed in water and dried. It is characterized by.

상기와 같이 펄라이트 입자에 황토를 코팅함으로써 펄라이트 입자의 경도가 증가되고, 수분 흡수성질이 매우 큰 펄라이트 입자에 황토가 코팅되어 펄라이트 입자의 수분 흡수 및 배출이 조절되며, 펄라이트 입자가 황토로 코팅되어 펄라이트 입자로부터 분진의 발생을 방지할 수 있게 된다.As described above, by coating ocher on the pearlite particles, the hardness of the pearlite particles is increased, and the ocher is coated on the pearlite particles having a very high water absorbing property to control moisture absorption and discharge of the pearlite particles, and the pearlite particles are coated with ocher pearlite. It is possible to prevent the generation of dust from the particles.

또한, 본 발명에 따른 건축용 세라믹 성형체는, 펄라이트 입자가 포함된 배합물에 입자 결합용 바인더를 혼합하여 성형시킨 건축용 세라믹 성형체에 있어서, 상기 펄라이트 입자는 향료용액에 침지되거나 향료용액이 분사된 다음 표면에 황토가 물에 분산된 코팅용액이 코팅되어 건조된 것을 특징으로 한다.In addition, the building ceramic molded body according to the present invention, in the building ceramic molded body formed by mixing a binder for mixing particles in the blend containing the pearlite particles, the pearlite particles are immersed in the perfume solution or sprayed with the perfume solution to the surface after spraying the perfume solution It is characterized in that the coating solution in which ocher is dispersed in water is coated and dried.

상기와 같이 피톤치드와 같은 향료 용액에 펄라이트 입자를 침지시키거나 향료 용액을 펄라이트 입자에 분사하는 경우 향료 용액이 펄라이트 입자에 흡착되어 그 펄라이트 입자로 제조된 건축용 세라믹 성형체는 향을 발산하게 된다. 특히, 향이 흡착된 펄라이트 입자에 황토가 코팅됨으로써 펄라이트 입자로부터 발산되는 향의 양이 조절되어 향의 지속시간이 향상된다.As described above, when the pearlite particles are immersed in a perfume solution such as phytoncide, or when the perfume solution is sprayed on the pearlite particles, the perfume solution is adsorbed on the pearlite particles, and the building ceramic molded article made of the pearlite particles emits incense. In particular, ocher is coated on the perlite adsorbed pearlite particles to control the amount of incense emitted from the perlite particles, thereby improving the duration of the incense.

또한, 본 발명에 따른 건축용 세라믹 성형체는, 상기 물에는 코팅용 바인더로서 당밀 또는 전분 용액이 혼합된 것을 특징으로 한다.In addition, the building ceramic molded body according to the present invention is characterized in that molasses or starch solution is mixed in the water as a binder for coating.

상기와 같이 코팅용액에 전분이 첨가됨으로써 황토 코팅이 원활하게 이루어지고 펄라이트 입자에 코팅된 황토의 흡착력이 증가된다.As described above, starch is added to the coating solution so that the ocher coating is smoothly performed and the adsorption power of the ocher coated on the pearlite particles is increased.

또한, 본 발명에 따른 건축용 세라믹 성형체는, 상기 배합물에는 질석 입자가 더 포함된 것을 특징으로 한다.In addition, the ceramic ceramic molded article according to the present invention is characterized in that the blend further contains vermiculite particles.

상기와 같이 질석 입자가 첨가됨으로써 성형체의 방음 등의 기능이 향상된 다.By adding vermiculite particles as described above, functions such as sound insulation of the molded body are improved.

또한, 본 발명에 따른 건축용 세라믹 성형체는, 상기 입자 결합용 바인더는 당밀 또는 전분 용액인 것을 특징으로 한다.In addition, the building ceramic molded body according to the present invention is characterized in that the binder for particle bonding is molasses or starch solution.

상기와 같이 입자 결합용 바인더로서 식물성 천연물이 전분을 이용함으로써 친환경적인 건축용 세라믹 성형체를 제조할 수 있게 된다.As described above, plant-based natural products can be manufactured as environmentally friendly building ceramic molded bodies by using starch as a binder for particle bonding.

상기와 같은 구성에 의하여 본 발명에 따른 건축용 세라믹 성형체는, 건축자재로 사용되며 불연성, 단열성, 경량성, 흡음성, 항균성 등의 기능을 갖는 건축용 세라믹 성형체를 제조함에 있어서 펄라이트 입자에 황토를 코팅시키고 그 황토가 코팅된 펄라이트 입자가 포함된 배합물을 바인더로 결합시켜 세라믹 성형체를 제조함으로써 강도를 보강할 수 있고, 펄라이트 입자로부터 발생되는 분진을 방지할 수 있으며, 펄라이트 입자의 수분 조절 작용을 향상시키고, 펄라이트 입자에 침투시킨 향의 지속시간을 증가시킬 수 있는 장점을 갖는다.Building ceramic molded body according to the present invention by the configuration as described above, is used as a building material in the manufacture of a ceramic ceramic molded body having the functions of non-flammability, heat insulation, light weight, sound absorption, antibacterial and the like coated with ocher on the pearlite particles It is possible to reinforce the strength by combining the mixture containing the ocher-coated pearlite particles with a binder to prepare a ceramic molded body, to prevent dust generated from the pearlite particles, to improve the moisture control action of the pearlite particles, It has the advantage of increasing the duration of the fragrance penetrated into the particles.

이하에서는 도면 및 실시예를 참조하여 본 발명에 따른 건축용 세라믹 성형체를 보다 상세하게 설명하기로 한다.Hereinafter, with reference to the drawings and the embodiment will be described in more detail the building ceramic molded body according to the present invention.

도 1은 본 발명의 일실시예에 따른 건축용 세라믹 성형체의 제조 과정을 도시한 흐름도이다.1 is a flowchart illustrating a manufacturing process of a ceramic ceramic molded body according to an embodiment of the present invention.

본 발명의 일실시예에 따른 건축용 세라믹 성형체는 황토가 코팅된 펄라이트 입자 및 질석 입자를 입자 결합용 바인더와 혼합하여 성형시킨 것을 특징으로 한 다.Building ceramic molded body according to an embodiment of the present invention is characterized in that the molded clay is mixed with a pearlite-coated pearlite particles and vermiculite particles combined with a binder for particle bonding.

황토가 코팅된 펄라이트 입자는 펄라이트 입자는 표면에 황토가 물에 분산된 코팅용액을 코팅, 건조시켜 형성된다. 본 발명에서 '펄라이트 입자'란 발포된 상태의 펄라이트 입자를 의미한다. 코팅용액은 황토분말 20~40중량%, 물 50~70중량%, 코팅용 바인더 5~10중량%(바람직하게는 황토분말 25중량%, 물 70중량%, 코팅용 바인더 5중량%)를 혼합하여 제조된다. 상기 코팅용 바인더(점결제)는 황토 분말 입자가 펄라이트 입자의 표면에 잘 부착되도록 하기 위한 것으로, 당밀이나 전분과 같은 천연물질이 사용되는 것이 바람직하다. 황토의 코팅은 펄라이트 입자를 코팅용액에 담가 이루어질 수 있으나, 바람직하게는 펄라이트 입자 알갱이를 굴리면서 그 위로 코팅용액을 분사시켜 이루어지는 황토 코팅막을 균일하게 형성할 수 있다.The ocher coated pearlite particles are formed by coating and drying the coating solution in which ocher is dispersed in water. In the present invention, the term "perlite particles" refers to perlite particles in a foamed state. The coating solution is mixed 20 to 40% by weight of ocher powder, 50 to 70% by weight of water, 5 to 10% by weight of coating binder (preferably 25% by weight of ocher powder, 70% by weight of water, 5% by weight of coating binder). It is manufactured by. The coating binder (binder) is to make the ocher powder particles adhere well to the surface of the pearlite particles, and natural materials such as molasses or starch are preferably used. The coating of ocher may be made by immersing the pearlite particles in the coating solution, but preferably, the ocher coating film formed by rolling the pearlite particles and spraying the coating solution thereon may be uniformly formed.

상기와 같이 황토 코팅용액이 펄라이트 입자에 코팅된 후 건조된다. 건조는 실온에서 음건시키거나 건조시간의 단축을 위해서 40~50℃의 온풍으로 건조시킬 수 있다. As described above, the ocher coating solution is coated on the pearlite particles and then dried. Drying can be dried at room temperature or by a warm air of 40-50 ° C. to shorten the drying time.

한편, 성형체로부터 향기가 발산되도록 펄라이트 입자에 피톤치드와 같은 향료를 흡착시킬 수 있는데, 향료의 흡착은 황토를 펄라이트 입자에 코팅하기 전에 이루어진다. 즉, 상기 펄라이트 입자를 향료용액에 침지시키거나 향료용액을 펄라이트 입자에 분사시킨 다음 그 펄라이트 입자 표면에 황토를 코팅, 건조시킨다. 상기와 같이 향료가 흡착된 펄라이트 입자로부터는 향기가 발산되는데, 그 펄라이트 입자의 표면에 황토가 코팅되어 향기의 발산 속도가 늦어져 향기의 발산기간이 길어지게 된다.On the other hand, the fragrance such as phytoncide can be adsorbed to the pearlite particles so that the fragrance is emitted from the molded body, the adsorption of the fragrance is carried out before coating the loess to the pearlite particles. That is, the pearlite particles are immersed in the perfume solution or the perfume solution is sprayed on the pearlite particles, and then the ocher is coated on the surface of the pearlite particles and dried. As described above, the fragrance is adsorbed from the pearlite particles adsorbed, the ocher is coated on the surface of the pearlite particles, so that the fragrance of the fragrance is slowed down, so that the fragrance of the fragrance is extended.

상기와 같이 황토가 코팅된 펄라이트 입자와 질석 입자가 혼합된 배합물에 입자 결합용 바인더와 혼합되어 판넬이나 블록과 같은 형태의 성형체로 성형된다. 즉, 황토가 코팅된 펄라이트 입자 60~85중량%, 질석 입자 5~20중량%, 입자 결합용 바인더 5~25중량%(바람직하게는 황토가 코팅된 펄라이트 입자 70중량%, 질석 입자 7중량%, 입자 결합용 바인더 23중량%)를 혼합하여 건축용 판넬과 같은 건축용 자재로 성형된다. 본 발명에서 '질석 입자'란 발포된 상태의 질석 입자를 의미한다. 상기 입자 결합용 바인더(점결제)로는 당밀 또는 전분 용액과 같은 천연 재료가 사용되는 것이 바람직하다.The clay-coated pearlite particles and vermiculite particles are mixed with the binder for particle binding to form a molded article such as a panel or a block. That is, 60 to 85% by weight ocher coated pearlite particles, 5 to 20% by weight vermiculite particles, 5 to 25% by weight binder binding particles (preferably 70% by weight ocher coated pearlite particles, 7% by weight vermiculite particles) 23% by weight of a binder for particle bonding) is mixed into a building material such as a building panel. In the present invention, the vermiculite particles mean vermiculite particles in a foamed state. It is preferable that a natural material such as molasses or starch solution is used as the binder for binder binding.

앞에서 설명되고 도면에 도시된 건축용 세라믹 성형체는 본 발명을 실시하기 위한 하나의 실시예에 불과하며, 본 발명의 기술적 사상을 한정하는 것으로 해석되어서는 안된다. 본 발명의 보호범위는 이하의 특허청구범위에 기재된 사항에 의해서만 정하여지며, 본 발명의 요지를 벗어남이 없이 개량 및 변경된 실시예는 본 발명이 속하는 기술분야에서 통상의 지식을 가진 자에게 자명한 것인 한 본 발명의 보호범위에 속한다고 할 것이다.The building ceramic molded body described above and shown in the drawings is only one embodiment for carrying out the present invention, and should not be construed as limiting the technical idea of the present invention. The scope of protection of the present invention is defined only by the matters set forth in the claims below, and the embodiments which have been improved and changed without departing from the gist of the present invention will be apparent to those skilled in the art. It will be said to belong to the protection scope of the present invention.

도 1은 본 발명의 일실시예에 따른 건축용 세라믹 성형체의 제조 과정을 도시한 흐름도1 is a flowchart illustrating a manufacturing process of a ceramic ceramic molded body according to an embodiment of the present invention.

Claims (7)

펄라이트 입자가 포함된 배합물에 입자 결합용 바인더를 혼합하여 성형시킨 건축용 세라믹 성형체에 있어서,In the building ceramic molded body formed by mixing and molding a binder for particle binding in a compound containing pearlite particles, 상기 펄라이트 입자는 표면에 황토가 물에 분산된 코팅용액이 코팅되어 건조된 것을 특징으로 하는 건축용 세라믹 성형체.The pearlite particles are a building ceramic molded body, characterized in that the surface is coated with a coating solution in which ocher is dispersed in water. 펄라이트 입자가 포함된 배합물에 입자 결합용 바인더를 혼합하여 성형시킨 건축용 세라믹 성형체에 있어서,In the building ceramic molded body formed by mixing and molding a binder for particle binding in a compound containing pearlite particles, 상기 펄라이트 입자는 향료용액에 침지되거나 향료용액이 분사된 다음 표면에 황토가 물에 분산된 코팅용액이 코팅되어 건조된 것을 특징으로 하는 건축용 세라믹 성형체.The perlite particles are immersed in the fragrance solution or sprayed with the fragrance solution and then coated with a coating solution in which ocher is dispersed in water on the surface of the building ceramic molded body, characterized in that the dried. 제1항 또는 제2항에 있어서,The method according to claim 1 or 2, 상기 물에는 코팅용 바인더로서 당밀 또는 전분 용액이 혼합된 것을 특징으로 하는 건축용 세라믹 성형체.The ceramic molded body for building, characterized in that the molasses or starch solution is mixed as a coating binder in the water. 제3항에 있어서,The method of claim 3, 상기 배합물에는 질석 입자가 더 포함된 것을 특징으로 하는 건축용 세라믹 성형체.The blend is a building ceramic molded body characterized in that it further comprises vermiculite particles. 제4항에 있어서,The method of claim 4, wherein 상기 입자 결합용 바인더는 당밀 또는 전분 용액인 것을 특징으로 하는 건축용 세라믹 성형체.The binder for particle bonding is a building ceramic molded body, characterized in that molasses or starch solution. 제1항 또는 제2항에 있어서,The method according to claim 1 or 2, 상기 배합물에는 질석 입자가 더 포함된 것을 특징으로 하는 건축용 세라믹 성형체.The blend is a building ceramic molded body characterized in that it further comprises vermiculite particles. 제1항 또는 제2항에 있어서,The method according to claim 1 or 2, 상기 입자 결합용 바인더는 당밀 또는 전분 용액인 것을 특징으로 하는 건축용 세라믹 성형체.The binder for particle bonding is a building ceramic molded body, characterized in that molasses or starch solution.
KR1020080106045A 2008-10-28 2008-10-28 Method for manufacturing ceramic formed material KR100985136B1 (en)