KR20100025926A - Dash board for automobile and the manufacturing method - Google Patents

Dash board for automobile and the manufacturing method Download PDF

Info

Publication number
KR20100025926A
KR20100025926A KR1020080084682A KR20080084682A KR20100025926A KR 20100025926 A KR20100025926 A KR 20100025926A KR 1020080084682 A KR1020080084682 A KR 1020080084682A KR 20080084682 A KR20080084682 A KR 20080084682A KR 20100025926 A KR20100025926 A KR 20100025926A
Authority
KR
South Korea
Prior art keywords
photocatalyst
photocatalyst particles
board body
dash board
car
Prior art date
Application number
KR1020080084682A
Other languages
Korean (ko)
Inventor
이중헌
박규협
Original Assignee
현대제철 주식회사
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 현대제철 주식회사 filed Critical 현대제철 주식회사
Priority to KR1020080084682A priority Critical patent/KR20100025926A/en
Publication of KR20100025926A publication Critical patent/KR20100025926A/en

Abstract

PURPOSE: A vehicle dashboard and a method of manufacture thereof are provided, which can keep vehicle indoor environment agreeable using oxidation and reduction of the optical catalyst. CONSTITUTION: A vehicle dashboard is constituted as follows. A board body part(2) made of the plastic material is installed in the front side of the passenger seat and driver's seat and compartmentalizes the engine room and the indoor place. A plurality of photocatalyst particles(1a) are exposed to the surface of the board body part. The photocatalyst particle is titanium dioxide.

Description

자동차용 대쉬 보드와 그의 제조 방법{Dash Board for Automobile And The Manufacturing Method}Dash Board for Automobile and the Manufacturing Method

본 발명은 자동차용 대쉬 보드와 제조 방법에 대한 것으로 더 상세하게는 자동차 실내의 환경을 더욱 쾌적하게 유지할 수 있도록 발명된 것이다.The present invention relates to a dash board for automobiles and a manufacturing method, and more particularly, to invent a more comfortable environment of an automobile interior.

일반적으로 자동차의 실내에서 운전석 및 조수석의 전면에는 자동차의 엔진 룸과 자동차의 실내를 구분하는 대쉬 보드가 장착되며, 대쉬 보드는 계기판 및 오디오 장치, 공기 조화 장치의 디프로스트 그릴, 글로브 박스 등이 장착되는 인스트루 먼트 패널을 포함하여 구성되는 것이다.In general, in the interior of the car, the front of the driver's seat and passenger seat is equipped with a dashboard that distinguishes the engine room of the car from the interior of the car, and the dashboard is equipped with instrument panel and audio device, defrost grill of air conditioner, glove box, etc. It is configured to include an instrument panel.

한편, 자동차에는 탑승객의 호흡이나 외부 대기 상태, 외부의 온도변화 등에 의하여 오염된 실내를 신선한 상태로 유지하거나 실내 온도를 냉, 난방하여 탑승자의 신체에 적합한 온도로 유지시켜 쾌적한 실내 환경을 형성할 수 있도록 함은 물론 유리창의 흐림과 서리 등을 제거하여 운전자의 시계를 확보하고 안전한 운전을 할 수 있도록 하는 공조장치가 설치된다.On the other hand, in the car, the indoors contaminated by the passenger's breathing, external air condition, or external temperature change can be kept fresh or the indoor temperature can be cooled and heated to maintain a comfortable temperature for the passenger's body. In addition, air-conditioning devices are installed to secure the driver's watch and to drive safely by removing cloudy and frost on the windows.

차실내의 냉, 난방과 환기를 목적으로 자동차에 설치되는 공조장치(HVAC : Heating, Ventilating & Air Conditioning System)는, 자동차의 프론트로부터 차실 내 외부로 연통되는 덕트를 통하여 차실내에 대한 냉 온풍 공급 또는 환기 기능을 수행하는 것으로, 대부분 주행 중 자동차의 실내 환경은 상기 공조 장치의 작동으로 유지되는 것이다.The HVAC (Heating, Ventilating & Air Conditioning System) installed in the car for the purpose of cooling, heating and ventilation in the car is supplied with cold and hot air to the inside of the car through a duct communicating from the front of the car to the outside of the car Alternatively, by performing a ventilation function, most of the indoor environment of the vehicle while driving is maintained by the operation of the air conditioning apparatus.

그러나 자동차의 실내는 상기한 바와 같이 밀폐된 상태로 공기 조화 장치에 의해 환기되는데, 이때 공기 조화 장치의 필터를 주기적으로 교체하지 않을 경우 자동차의 실내로 공급되는 공기중에는 미세한 먼지 및 세균, 바이러스 곰팡이 등의 유해 물질이 많이 포함되어 자동차의 실내 환경이 나빠지는 문제점이 있었던 것이다.However, the interior of the vehicle is ventilated by the air conditioner in a sealed state as described above, in which case the air supplied to the interior of the vehicle is fine dust, bacteria, virus mold, etc., unless the air conditioner filter is periodically replaced. There is a problem that the interior environment of the car worsens because of a lot of harmful substances.

또, 장기간 사용 시 자동차의 실내에는 구석진 부분에서 곰팡이 및 세균이 발생하고, 이로 인한 악취가 발생하는 문제점이 있었던 것이다.In addition, there is a problem that mold and bacteria are generated in the corners of the car during long-term use, resulting in bad smell.

또한 실외 공기 역시 도시 내의 자동차의 증가로 인해 질소 산화물 및 황화물로 인한 오염이 날로 심해지고 있고, 이렇게 오염된 공기가 자동차의 실내로 유입됨으로써 자동차의 실내 환경이 나쁜 문제점이 있었던 것이다.In addition, the outdoor air is also increasingly polluted by nitrogen oxides and sulfides due to the increase of automobiles in the city, and the polluted air flows into the interior of the vehicle, thereby causing a bad indoor environment of the vehicle.

특히, 새 차의 경우에는 실내에서 독성 화학물질이 기준치 이상으로 배출되어 운전자 및 탑승자의 건강을 해치는 문제점이 있었던 것이다.In particular, in the case of a new car, there was a problem in that toxic chemicals are discharged above a reference value in a room, which damages the health of drivers and passengers.

본 발명의 목적은 광촉매의 산화, 환원 작용을 이용하여 운전자 및 탑승자에게 해로운 물질을 제거함으로써 자동차의 실내 환경을 쾌적하게 유지할 수 있게 하는 자동차용 대쉬 보드와 그의 제조 방법을 제공하는 데 있다.An object of the present invention is to provide a dash board for automobiles and a method of manufacturing the same, which are capable of keeping the interior environment of a vehicle comfortable by removing substances harmful to the driver and occupant by using the oxidation and reduction effects of the photocatalyst.

이러한 본 발명의 과제는 자동차의 실내에서 운전석 및 조수석의 전면에 설치되어 자동차의 엔진 룸과 자동차의 실내를 구분하는 합성수지재의 보드 몸체부를 가지며, 보드 몸체부의 표면에 복수의 광촉매 입자가 노출되게 구비된 자동차용 대쉬 보드를 제공함으로써 해결되는 것이다.The object of the present invention is installed on the front of the driver's seat and the passenger seat in the interior of the vehicle has a board body portion of the synthetic resin material that separates the engine room of the vehicle and the interior of the vehicle, and a plurality of photocatalyst particles are exposed on the surface of the board body portion This is solved by providing an automobile dash board.

또한 합성 수지 재질로 형성된 패널 재료의 표면에 광촉매 입자를 뿌려 도포하는 광촉매 도포 공정과;A photocatalyst coating step of spraying and applying photocatalyst particles onto a surface of the panel material formed of a synthetic resin material;

광촉매가 도포된 패널 재료를 가열하는 패널 가열 공정과;A panel heating step of heating the panel material coated with the photocatalyst;

상기 표면 가열을 거친 패널 재료의 표면을 가압하여 표면에 도포된 광촉매 입자를 표면에 압착시키는 압착 공정과;Pressing the surface of the panel material subjected to the surface heating to pressurize the photocatalyst particles applied to the surface to the surface;

상기 압착 공정을 거친 패널 재료를 대쉬 보드의 형상을 가지는 보드 몸체부로 성형하여 제조하는 대쉬 보드 성형 공정을 포함한 자동차용 대쉬보드 제조 방법을 제공함으로써 해결되는 것이다.It is solved by providing an automobile dashboard manufacturing method including a dash board forming process for forming the panel material subjected to the pressing process into a board body having a shape of a dash board.

본 발명은 표면에 압입된 광촉매 입자의 산화, 환원 작용으로 자동차의 실내 의 유해 물질 제거 및 공기 정화의 효과를 얻어 자동차의 실내 환경을 개선할 수 있는 것이다.The present invention can improve the indoor environment of the vehicle by obtaining the effect of removing the harmful substances in the interior of the vehicle and purifying the air by the oxidation and reduction of the photocatalyst particles pressed into the surface.

또한 본 발명은 자동차의 실내 환경을 개선하여 운전자 및 탑승자의 건강을 보호하고, 자동차의 상품성을 증대시키는 효과가 있는 것이다.In addition, the present invention is to improve the indoor environment of the car to protect the health of drivers and passengers, and to increase the merchandise of the car.

본 발명의 바람직한 실시 예를 첨부된 도면에 의해 상세히 설명하면 다음과 같다.Preferred embodiments of the present invention will be described in detail with reference to the accompanying drawings.

도 1은 본 발명의 일 실시 예를 도시한 요부확대 단면도로서, 대쉬 보드의 보드 몸체부 표면에 광촉매 입자가 외부로 노출되게 압착되어 구비된 예를 확대하여 나타내고 있다.FIG. 1 is an enlarged cross-sectional view illustrating main parts of an embodiment of the present invention, in which the photocatalyst particles are compressed and exposed to the outside of the board body of the dash board.

도 2는 본 발명의 다른 실시 예를 도시한 요부확대 단면도로서, 대쉬 보드의 보드 몸체부 표면에 광촉매 입자로 형성된 광촉매 코팅층이 형성된 예를 확대하여 나타내고 있다.Figure 2 is an enlarged cross-sectional view showing the main portion of another embodiment of the present invention, an enlarged example of the photocatalyst coating layer formed of photocatalyst particles formed on the surface of the board body of the dash board.

도 3은 본 발명인 대쉬 보드 제조 방법에 대한 블록도로서, 본 발명인 대쉬 보드을 제조하는 방법을 순차적으로 나타낸 것이다.3 is a block diagram of a method of manufacturing a dash board of the present invention, showing a method of manufacturing the dash board of the present invention sequentially.

도 4는 본 발명의 사용 상태도로서, 본 발명인 대쉬 보드가 자동차의 실내에 장착되어 사용되어 지는 예를 나타내고 있다.4 is a diagram showing the use state of the present invention, showing an example in which the dash board of the present invention is mounted and used in a vehicle interior.

이하, 본 발명인 대쉬 보드(1)의 보드 몸체부(2)는 통상 합성 수지재로 자동차에 따라 각기 다른 형상으로 제조되어 자동차의 실내에서 운전석 및 조수석의 전면에 설치됨으로써 엔진 룸과 자동차의 실내를 구분하여 엔진 룸을 차단하는 것을 이는 종래의 공지된 것으로 상세한 설명은 생략함을 밝혀둔다.Hereinafter, the board body portion 2 of the dash board (1) of the present invention is usually made of a synthetic resin material in different shapes according to the vehicle, and installed in the front of the driver's seat and the passenger seat in the interior of the vehicle, thereby maintaining the engine room and the interior of the vehicle. It is to be noted that blocking the engine room separately is well known in the art and detailed description thereof is omitted.

상기 대쉬 보드(1)의 보드 몸체부(2)는 도 1 내지 도 2에서 도시한 바와 같이 표면에 복수의 광촉매 입자(1a)가 노출되게 구비되는 것이다.The board body 2 of the dash board 1 is provided to expose a plurality of photocatalyst particles 1a on the surface as shown in FIGS.

상기 광촉매 입자(1a)는 도 1에서 도시한 바와 같이 보드 몸체부(2)의 표면에 일부가 노출되게 압입될 수도 있으며, 도 2에서 도시한 바와 같이 보드 몸체부(2)의 표면에 일정한 두께로 도포된 상태로 압착되어 광촉매 코팅층(1b)을 형성할 수도 있는 것이다.As shown in FIG. 1, the photocatalyst particles 1a may be press-fitted to expose a part of the surface of the board body 2, and as shown in FIG. 2, the photocatalyst particle 1a may have a predetermined thickness on the surface of the board body 2. It may be pressed in a coated state to form a photocatalyst coating layer 1b.

상기 광촉매는 광과 촉매의 합성어로서 빛을 받아 화학 반응을 촉진시키는 물질로 반도체의 일종이며, 빛 에너지를 받아 활성 상태가 되어 강력한 산화, 환원 작용을 발생시키고, 이러한 산화, 환원에 의해 공기 중의 휘발성 유기 화합물(VOC;Volatile Organic Compounds), 악취, 각종 세균, 바이러스, 곰팡이 등의 유해물질을 분해하게 되는 것이다.The photocatalyst is a compound word of light and catalyst, which is a substance that receives a light and promotes a chemical reaction, is a kind of semiconductor, and receives light energy to become an active state, thereby generating a strong oxidation and reduction effect. VOCs (Volatile Organic Compounds), odors, various bacteria, viruses, fungi and other harmful substances will be broken down.

상기 광촉매 입자(1a)로는 이산화티탄(TiO2)을 사용하는 것을 기본으로 한다.Titanium dioxide (TiO 2 ) is used as the photocatalyst particles 1a.

상기 이산화티탄은 자원적으로 풍부한 티탄을 사용하여 제조되는 것으로 제조방법이 단순하고, 원재료인 티탄의 값이 저렴함은 물론 산, 알칼리와 생물학적으로 안정하여 인체에 무해한 장점이 있는 것이다.The titanium dioxide is manufactured using resource-rich titanium, and the manufacturing method is simple, and the raw material of titanium is inexpensive, as well as acid, alkali and biologically stable, which is harmless to the human body.

또한 상기 이산화티탄은 자외선에 의해 활성되고, 광부식이 없어 햇빛을 이용한 산화, 환원 작용이 원활히 이루어질 수 있는 것이다.In addition, the titanium dioxide is activated by ultraviolet rays, and there is no photocorrosion so that oxidation and reduction using sunlight can be performed smoothly.

한편, 상기한 대쉬 보드(1)를 제조하는 방법은 하기와 같다.On the other hand, the method of manufacturing the above-mentioned dash board 1 is as follows.

일단 대쉬 보드 제조용으로 합성 수지 재질로 형성된 패널 재료의 표면에 광촉매 입자(1a)를 뿌려 도포하는 광촉매 도포 공정(10)을 행한다.The photocatalyst application | coating process 10 which sprays and apply | coats the photocatalyst particle 1a to the surface of the panel material formed from the synthetic resin material for the manufacture of a dash board is performed once.

상기 광촉매 도포 공정(10)에서 사용되는 광촉매 입자(1a)는 30 ∼100㎛의 크기를 가지는 이산화 티탄 분말을 사용하는 것을 기본으로 하며, 이외에도 빛 에너지를 받아 활성화되어 산화, 환원 작용을 하는 어떠한 것도 사용이 가능함을 밝혀둔다.Photocatalyst particles (1a) used in the photocatalyst application step 10 is based on the use of titanium dioxide powder having a size of 30 ~ 100㎛, in addition to anything that is activated by receiving light energy to oxidize, reduce Note that it can be used.

상기 이산화티탄은 자원적으로 풍부한 티탄을 사용하여 제조되는 것으로 제조방법이 단순하고, 원재료인 티탄의 값이 저렴함은 물론 산, 알칼리와 생물학적으로 안정하여 인체에 무해한 장점이 있는 것이다.The titanium dioxide is manufactured using resource-rich titanium, and the manufacturing method is simple, and the raw material of titanium is inexpensive, as well as acid, alkali and biologically stable, which is harmless to the human body.

또한 상기 이산화티탄은 자외선에 의해 활성되고, 광부식이 없어 햇빛을 이용한 산화, 환원 작용이 원활히 이루어질 수 있는 것이다.In addition, the titanium dioxide is activated by ultraviolet rays, and there is no photocorrosion so that oxidation and reduction using sunlight can be performed smoothly.

상기 광촉매 도포 공정(10)은 광촉매 입자(1a)를 패널 재료의 표면에 고르게 도포하여 각 광촉매 입자(1a)가 후술될 압착 공정(30)을 통해 패널 재료의 표면에 압입되도록 할 수도 있으며, 임의의 두께를 가지도록 광촉매 입자(1a)를 도포하여 후술될 압착 공정(30)을 통해 패널 재료의 표면에 광촉매 코팅층(1b)을 형성할 수도 있는 것이다.The photocatalyst application step 10 may apply the photocatalyst particles 1a evenly to the surface of the panel material so that each photocatalyst particle 1a is pressed onto the surface of the panel material through a compression process 30 which will be described later. The photocatalyst particles 1a may be applied to form the photocatalyst coating layer 1b on the surface of the panel material through the pressing process 30 to be described later.

상기 광촉매 도포 공정(10)을 거친 패널 재료는 패널 가열 공정(20)에서 히터 장치로 가열된다.The panel material which has undergone the photocatalytic application step 10 is heated by the heater device in the panel heating step 20.

상기 패널 가열 공정(20)은 패널 재료를 패널 재료의 재질에 대한 용융점 정 도로 가열하는 것으로, 이 가열 온도는 대쉬 패널의 제조 시 패널 재료의 재질, 즉, 합성 수지재의 용융점에 따라 달라지므로, 대쉬 패널의 재질에 따라 다양하게 실시될 수 있음을 밝혀둔다.The panel heating process 20 is to heat the panel material to the melting point of the material of the panel material, the heating temperature depends on the material of the panel material, that is, the melting point of the synthetic resin material in the manufacture of the dash panel, Note that it can be carried out in various ways depending on the material of the panel.

상기 패널 가열 공정(20)을 거친 패널 재료는 이격된 상, 하 가압 롤 사이로 통과되어 광촉매 입자(1a)를 패널 재료의 표면에 압착하여 열 융착시키는 압착 공정(30)을 행하게 되는 것이다.The panel material which passed through the said panel heating process 20 passes between spaced up and down press rolls, and performs the crimping process 30 which crimps | bonds the photocatalyst particle 1a to the surface of panel material, and thermally fuses it.

상기 압착 공정(30)을 통해 광촉매 입자(1a)는 가열된 패널 재료의 표면으로 압입되어 패널 재료의 표면으로 일부 노출되는 것이다.Through the pressing process 30, the photocatalyst particles 1a are pressed into the surface of the heated panel material and partially exposed to the surface of the panel material.

그리고 상기한 압착 공정(30)을 거친 패널 재료는 설계된 대쉬 보드(1)의 형상으로 성형하여 보드 몸체부(2)를 제조하는 대쉬 보드 성형 공정(40)을 행하게 되는 것이다.Then, the panel material that has undergone the pressing process 30 is formed into a shape of the designed dash board 1 to perform the dash board forming process 40 for manufacturing the board body 2.

상기 대쉬 보드 성형 공정(40)은 프레스, 블랭킹, 펀칭 등의 가공을 통해 패널 재료를 대쉬 보드(1)의 형상 즉, 설계된 보드 몸체부(2)로 성형하는 것으로 이러한 성형 공정은 공지된 대쉬 패널 제조 공정과 동일하므로 상세한 설명은 생략함을 밝혀둔다.The dash board forming process 40 forms a panel material into the shape of the dash board 1, that is, the designed board body 2 through a process such as pressing, blanking, punching, and the like. Since the same as the manufacturing process, it will be noted that the detailed description is omitted.

상기한 바와 같이 제조된 대쉬 보드(1)는 도 4에서 도시한 바와 같이 자동차의 실내에서 운전석과 조수석의 정면에 설치되는데, 자동차의 프론트 글라스(3), 또는 양 측 도어의 윈도우 글라스를 통해 자동차 실내로 햇빛이 비춰질 경우 대쉬 보드(1)의 표면에 노출된 광촉매 입자(1)가 햇빛에 포함된 자외선과 반응하여 전자 (e-), 전공(h+) 쌍을 발산하는 것이다.The dash board 1 manufactured as described above is installed at the front of the driver's seat and the passenger seat in the interior of the vehicle as shown in FIG. 4, and the vehicle is provided through the front glass 3 of the vehicle, or the window glass of both side doors. When sunlight is emitted into the room, the photocatalyst particles 1 exposed on the surface of the dashboard 1 react with the ultraviolet rays included in the sunlight to emit electron (e-) and electron (h +) pairs.

그리고 상기 광촉매 입자(1)는 발산된 전자와 전공이 자동차 실내에 포함된 공기 오염 물질, 즉, NOx, SOx, CL2, NH3 등의 분자, 휘발성 유기 화합물(VOC;Volatile Organic Compounds)과 산화, 환원 작용을 하면서, 상기한 공기 오염물질을 제거하는 것이다.In addition, the photocatalyst particles 1 are composed of air pollutants, ie, NOx, SOx, CL2, NH3, and other volatile organic compounds (VOCs) and oxidized, reduced electrons and electrons in a vehicle interior. Functioning to remove the air pollutants.

또한 광촉매 입자(1)는 자동차의 밀폐된 실내 공간에서 발생하는 악취 및 미생물 등을 광산화, 환원 반응을 통해 흡착 분해하여 제거하며, 항균 기능으로 자동차의 실내 공간 내에 세균의 발생을 억제하는 역할을 하는 것이다.In addition, the photocatalyst particles 1 absorb and decompose odors and microorganisms generated in an enclosed interior space of an automobile through photooxidation and reduction reactions, and act as an antibacterial function to suppress the generation of bacteria in the interior space of the vehicle. will be.

따라서 본 발명인 대쉬 보드(1)는 표면에 도포된 광촉매 입자(1)로 자동차의 실내 공간에 존재하는 인체 유해 물질을 제거하고 공기를 정화함으로써, 쾌적한 실내 환경을 유지하도록 하는 것이다.Therefore, the present invention the dash board (1) is to remove the harmful substances present in the interior space of the vehicle with the photocatalyst particles (1) applied to the surface to purify the air, to maintain a comfortable indoor environment.

본 발명은 상기한 실시 예에 한정되는 것이 아니라, 본 발명의 요지에 벗어나지 않는 범위에서 다양하게 변경하여 실시할 수 있으며 이는 본 발명의 구성에 포함됨을 밝혀둔다.The present invention is not limited to the above-described embodiments, and various changes can be made without departing from the gist of the present invention, which is understood to be included in the configuration of the present invention.

도 1은 본 발명의 일 실시 예를 도시한 요부확대 단면도Figure 1 is an enlarged cross-sectional view showing the main portion of an embodiment of the present invention

도 2는 본 발명의 다른 실시 예를 도시한 요부확대 단면도Figure 2 is an enlarged cross-sectional view of the main portion showing another embodiment of the present invention

도 3은 본 발명인 대쉬 보드 제조 방법에 대한 블록도Figure 3 is a block diagram of the present inventor dash board manufacturing method

도 4는 본 발명의 사용 상태도4 is a state diagram used in the present invention

*도면 중 주요 부호에 대한 설명** Description of the major symbols in the drawings *

1 : 대쉬 보드 1a : 광촉매 입자1: dashboard 1a: photocatalyst particles

2 : 보드 몸체부2: board body

Claims (6)

자동차의 실내에서 운전석 및 조수석의 전면에 설치되어 자동차의 엔진 룸과 자동차의 실내를 구분하는 합성수지재의 보드 몸체부를 가지며, 보드 몸체부의 표면에 복수의 광촉매 입자가 노출되게 구비된 것을 특징으로 하는 자동차용 대쉬 보드.It is installed on the front of the driver's seat and the passenger seat in the interior of the car has a board body portion of the synthetic resin material that separates the engine room of the car and the interior of the car, and a plurality of photocatalyst particles are exposed on the surface of the board body portion Dash board. 청구항 1에 있어서,The method according to claim 1, 상기 광촉매 입자는 이산화티탄(TiO2)을 사용하는 것을 특징으로 하는 자동차용 대쉬 보드.The photocatalyst particle is a dashboard for automobiles, characterized in that using titanium dioxide (TiO 2 ). 청구항 1에 있어서,The method according to claim 1, 상기 보드 몸체부의 표면에는 광촉매 입자가 압입되어 구비되는 것을 특징으로 하는 자동차용 대쉬 보드.Automobile dashboard, characterized in that the photocatalyst particles are pressed into the surface of the board body portion. 청구항 1에 있어서,The method according to claim 1, 상기 보드 몸체부의 표면에는 광촉매 입자를 포함한 광촉매 코팅층이 형성되는 것을 특징으로 하는 자동차용 대쉬 보드.Automobile dashboard, characterized in that the photocatalyst coating layer including the photocatalyst particles is formed on the surface of the board body portion. 합성 수지 재질로 형성된 패널 재료의 표면에 광촉매 입자를 뿌려 도포하는 광촉매 도포 공정과;A photocatalyst coating step of spraying and coating photocatalyst particles on a surface of the panel material formed of a synthetic resin material; 광촉매 입자가 도포된 패널 재료를 가열하는 패널 가열 공정과;A panel heating step of heating the panel material coated with the photocatalyst particles; 상기 표면 가열을 거친 패널 재료의 표면을 가압하여 표면에 도포된 광촉매 입자를 표면에 압착시키는 압착 공정과;Pressing the surface of the panel material subjected to the surface heating to pressurize the photocatalyst particles applied to the surface to the surface; 상기 압착 공정을 거친 패널 재료를 대쉬 보드의 형상을 가지는 보드 몸체부로 성형하여 제조하는 대쉬 보드 성형 공정이 순차적으로 행해지는 것을 특징으로 하는 자동차용 대쉬보드 제조 방법.And a dash board forming step of forming the panel material which has undergone the pressing process into a board body having a shape of a dash board. 청구항 5에 있어서,The method according to claim 5, 상기 광촉매 입자는 이산화티탄(TiO2)을 사용하는 것을 특징으로 하는 자동차용 대쉬 보드.The photocatalyst particle is a dashboard for automobiles, characterized in that using titanium dioxide (TiO 2 ).
KR1020080084682A 2008-08-28 2008-08-28 Dash board for automobile and the manufacturing method KR20100025926A (en)