KR20090112416A - Hybrid sheet and protecting products comprising the same - Google Patents
Hybrid sheet and protecting products comprising the same Download PDFInfo
- Publication number
- KR20090112416A KR20090112416A KR1020080038301A KR20080038301A KR20090112416A KR 20090112416 A KR20090112416 A KR 20090112416A KR 1020080038301 A KR1020080038301 A KR 1020080038301A KR 20080038301 A KR20080038301 A KR 20080038301A KR 20090112416 A KR20090112416 A KR 20090112416A
- Authority
- KR
- South Korea
- Prior art keywords
- strength
- hybrid sheet
- fibers
- hybrid
- sheet according
- Prior art date
Abstract
Description
본 발명은 하이브리드 시이트 및 이를 포함하는 보호구에 관한 것으로서, 보다 구체적으로는 전단농화유체(Shear Thickness Fluid ; 이하 "STF" 라고한다)가 함침된 고강력 섬유체 상에 열가소성 수지층이 접착되어 상기 전단농화유체가 사용 중 고화되는 것을 방지하고, 가벼운 중량으로도 방탄성, 방검성 및 충격흡수성이 우수한 하이브리드 시이트 및 이를 포함하는 보호구에 관한 것이다.The present invention relates to a hybrid sheet and a protective device including the same, and more specifically, a thermoplastic resin layer is adhered onto a high-strength fiber impregnated with a shear thickening fluid (hereinafter referred to as "STF"). The present invention relates to a hybrid sheet which prevents the thickening fluid from solidifying during use and is excellent in ballistic resistance, gum resistance and shock absorption even at a light weight, and a protective device including the same.
이하, 본원발명에서는 보호구라는 용어는 방탄복, 방탄판, 방검복, 스키복 등과 같은 충격흡수복을 모두 포함하는 의미로 사용한다.Hereinafter, in the present invention, the term protective equipment is used in the sense including both shock-absorbing suits such as body armor, bulletproof board, sword suit, ski suit, and the like.
종래의 보호구의 일종인 방탄판으로는 고강도 폴리에틸렌 시이트가 널리 사용되어 왔으나, 제조원가가 비싸고 제조가 어려운 문제가 있었다.High-strength polyethylene sheet has been widely used as a bulletproof plate, which is a kind of conventional protective equipment, but there is a problem in that manufacturing cost is high and manufacturing is difficult.
또 다른 종래의 방탄판으로는 세라믹 판과 아라미드 직물을 여러매 적층시킨 아라미드 직물 적층체를 서로 적층시킨 구조의 방탄판이 널리 사용되어 왔다.As another conventional bulletproof plate, a bulletproof plate having a structure in which an aramid fabric laminate obtained by laminating a plurality of ceramic plates and aramid fabrics is laminated on each other has been widely used.
한편, 종래의 방탄복으로는 아라미드 직물을 여러매 적층시킨 아라미드 직물 적층체가 널리 사용되어 왔다.On the other hand, as a conventional body armor, aramid fabric laminate obtained by laminating a plurality of aramid fabrics has been widely used.
본 발명에 있어서, 아라미드 직물이란 경사 및 위사로 전방향족 폴리아미드(일명"아라미드"라고 함) 멀티필라멘트를 사용하여 제직된 직물을 의미한다.In the present invention, an aramid fabric means a fabric woven using warp and weft yarns using wholly aromatic polyamide (aka "aramid") multifilament.
그러나, 종래의 방탄판 또는 방탄복을 구성하는 아라미드 직물은 경사 및 위사 모두가 꼬임이 가해진, 다시말해 연사(撚絲)된 전방향족 폴리아미드 멀티필라멘트들로 이루어져 있기 때문에 상기 직물에 총알로 인한 충격이 가해지면 경사 및 위사의 꼬임부분이 약점(Weak point)로 작용하여 방탄성능이 크게 저하되는 문제가 있었고, 방탄성이 부족하여 원하는 방탄효과를 얻기 위해서는 여러매의 아라미드 직물을 적층해야 하므로 무게가 무거워 지는 문제가 있었다.However, since the aramid fabric constituting the conventional bulletproof plate or body armor consists of twisted and weft yarns, ie, twisted wholly aromatic polyamide multifilaments, the impact of bullets on the fabric There was a problem that the anti-ballistic performance was greatly deteriorated because the twisted part of the ground slope and the weft acted as a weak point, and due to the lack of anti-ballistic properties, several aramid fabrics had to be laminated so that the weight became heavy. There was a problem.
또 다른 방탄재료로는 전단농화유체가 함침된 아라미드 직물이 여러매 겹쳐있는 아라미드 직물 적층체가 일부 사용되고 있으나, 사용 중 아라미드 직물에 함침된 전단농화유체의 용매가 증발하여 상기 전단농화유체가 고화되는 현상으로 사용수명이 단축되는 문제가 있었다.As another ballistic material, some aramid fabric laminates in which several aramid fabrics are impregnated with shear thickening fluid are used. However, the solvent of the thickening fluid impregnated in the aramid fabric is evaporated and the shear thickening fluid is solidified. As a result, the service life was shortened.
본 발명은 가벼운 중량으로도 우수한 방탄성, 방검성, 충격흡수성을 발현하면서도, 고강력 섬유체에 함침된 전단농화유체가 사용 중 고화되지 않아 오랫동안 상기 성능들을 발현하는 하이브리드 시이트 및 이를 포함하는 보호복을 제공하고자 한다.The present invention provides a hybrid sheet and a protective suit comprising the same for a long time because the shear thickening fluid impregnated in the high-strength fiber does not solidify in use while expressing excellent anti-ballistic, anti-glare and shock absorbing properties even at a light weight. To provide.
상기 과제를 달성하기 위한 본 발명의 하이브리드 시이트는 (ⅰ) 고강력 원사로 이루어진 고강력 섬유체; (ⅱ) 상기 고강력 섬유체에 함침된 전단농화유체(Shear Thickness Fluid); 및 (ⅲ) 상기 고강력 섬유체에 접착된 열가소성 수지층으로 구성되는 것을 특징으로 한다.Hybrid sheet of the present invention for achieving the above object is (i) a high-strength fibrous body consisting of a high-tensile yarn; (Ii) a shear thickening fluid impregnated in the high strength fiber; And (iii) a thermoplastic resin layer adhered to the high strength fiber body.
또한, 본 발명의 보호복은 상기 하이브리드 시이트를 포함하는 것을 특징으로 한다.Moreover, the protective suit of this invention is characterized by including the said hybrid sheet.
이하, 본 발명을 보다 구체적인 살펴본다.Hereinafter, the present invention will be described in more detail.
본 발명에 따른 하이브리드 시이트 일례로는 도 1에 도시된 바와 같이 고강력 원사로 이루어진 고강력 섬유체(1)에 전단농화유체(2)가 함침되어 있으며, 상기 고강력 섬유체(1)의 표면과 이면 각각에 열가소성 수지층(3)들이 접착된 구조를 갖는다.As an example of the hybrid sheet according to the present invention, a
도 1은 본 발명에 따른 하이브리드 시이트의 단면 모식도이다.1 is a schematic cross-sectional view of a hybrid sheet according to the present invention.
본 발명에 따른 하이브리드 시이트의 또 다른 일례로는 고강력 원사로 이루어진 고강력 섬유체(1)에 전단농화유체(2)가 함침되어 있으며, 상기 고강력 섬유체(1)의 표면, 이면, 좌측면 및 우측면 각각에 접착된 구조를 갖는다.As another example of the hybrid sheet according to the present invention, a
상기 고강력 섬유체는 직물형태, 부직포형태 또는 종이형태 등이다.The high strength fiber body is in the form of a woven fabric, a nonwoven fabric or a paper.
상기 열가소성 수지층은 폴리프로필렌 수지, 폴리에스테르 수지 또는 폴리아미드 수지 등으로 구성되며, 필름형태 또는 수지코팅층형태 등이다.The thermoplastic resin layer is composed of polypropylene resin, polyester resin or polyamide resin, and the like, and is in the form of a film or a resin coating layer.
본 발명에 따른 하이브리드 시이트는 전단농화유체가 함침된 고강력 섬유체에 열가소성 수지층이 접착되어, 사용 중 상기 전단농화유체내 용매가 증발하여 고화되는 것을 효과적으로 방지하여 오랫동안 방탄성능, 방검성능 또는 충격흡수성능을 유리하도록 한다.In the hybrid sheet according to the present invention, a thermoplastic resin layer is attached to a high-strength fiber impregnated with a shear thickening fluid, and effectively prevents the solvent in the shear thickening fluid from solidifying by evaporation during use. The absorption performance is favored.
상기 고강력 섬유체는 아라미드 섬유체, 폴리이미드 섬유체, 폴리벤즈옥사졸 섬유체, 전방향족 폴리에스테르 섬유체, 고강력 폴리에틸렌 섬유체, 고강력 폴리아미드 섬유체 또는 고강력 폴리에스테르 섬유체 등으로 구성된다.The high strength fibers may be aramid fibers, polyimide fibers, polybenzoxazole fibers, wholly aromatic polyester fibers, high strength polyethylene fibers, high strength polyamide fibers or high strength polyester fibers. It is composed.
상기 전단농화유체(STF)는 10~1,000㎚의 무기입자가 비휘발성이고 무독성인 용매 및 분산제에 50중량% 이상의 농도로 충진되어 있는 유체이다.The shear thickening fluid (STF) is a fluid in which 10 to 1,000 nm of inorganic particles are filled in a nonvolatile and nontoxic solvent and dispersant at a concentration of 50% by weight or more.
상기 무기입자의 일례는 실리카 입자, 이산화티탄 입자 또는 나노카본튜브 등이고, 용매의 일례는 폴리에틸렌글리콜 또는 에틸렌 글리콜 등이고, 분산제의 일례로는 에탄올 또는 메탄올 등이다.Examples of the inorganic particles are silica particles, titanium dioxide particles, nanocarbon tubes, and the like. One example of the solvent is polyethylene glycol or ethylene glycol, and one example of the dispersant is ethanol or methanol.
상기 전단농화유체(STF)는 고강력 섬유체의 전체중량대비 30중량~80중량% 함침될 수 있다.The shear thickening fluid (STF) may be impregnated with 30 to 80% by weight relative to the total weight of the high-strength fiber.
전단농화유체(STF)가 함침된 고강력 섬유체는 총알 등으로 외부에서 급격한 충격이 가해질 경우 액상에서 고체상으로 상변화가 일어나 딱딱해지면서 외부 충격이 내부로 침투하는 것을 방지하는 역할을 수행한다.High-strength fiber impregnated with shear thickening fluid (STF) plays a role of preventing the external impact from penetrating into the interior as the phase change occurs from the liquid phase to the solid phase when a sudden impact is applied from the outside with a bullet.
상기 고강력 섬유체가 직물인 경우, 직물을 구성하는 경사 및 위사가 꼬임을 갖는 경우 총알로 인한 충격이 고강력 섬유체에 가해지면 상기 꼬임 부분은 가해진 충격을 상기 섬유체의 전체 면적으로 효과적으로 분산시키는 것을 방해하는 약 점(Weak point)로 작용하게 되고, 그로인해 방탄성능 등이 크게 저하될 수 있다.When the high-strength fiber body is a fabric, when the warp and weft yarn constituting the fabric has a twist, when the impact due to the bullet is applied to the high-strength fiber body, the twisted portion effectively distributes the applied impact to the entire area of the fiber body It acts as a weak point (Hak point) that interferes with this, and thus bulletproof performance can be greatly reduced.
본 발명에서는 상기와 같은 현상을 방지하여 방탄성능등을 획기적으로 개선하기 위해서, 고강력 직물을 구성하는 경사 및 위사를 무연(無撚)인 고강력 원사로 구성하는 것이 더욱 바람직하다.In the present invention, in order to prevent the above phenomenon and to significantly improve the bulletproof performance, it is more preferable to configure the warp and weft yarn constituting the high-strength fabric with a high-strength yarn having no lead.
상기 고강력 원사는 단사섬도가 0.7~1.6 데니어인 모노필라멘트 400~1,000개로 구성되는 것이 바람직하다.The high strength yarn is preferably composed of 400 ~ 1,000 monofilament having a single yarn fineness of 0.7 ~ 1.6 denier.
또한, 고강력 원사의 인장강도는 22g/d 이상인 것이 바람직하다.In addition, the tensile strength of the high strength yarn is preferably 22g / d or more.
그러나, 본 발명에서는 고강력 원사의 단사섬도 및 개수와 인장강도를 특별히 한정하는 것은 아니다.However, in the present invention, the single yarn fineness and the number and tensile strength of the high strength yarn are not particularly limited.
한편, 상기 고강력 섬유체가 직물인 경우는 인장강도가 7,000~20,000N/5㎝ 이고, 직물조직이 평직 또는 바스켓직인 것이 바람직하고, 경사밀도 및 위사밀도는 각각 5~15본/㎝ 수준인 것이 바람직하다.On the other hand, when the high-strength fiber is a fabric, the tensile strength is 7,000 ~ 20,000N / 5㎝, it is preferable that the fabric structure is a plain weave or basket weave, the inclination density and weft density is that the level of 5 ~ 15 bone / cm each desirable.
그러나, 본 발명에서는 고강력 직물의 인장강도, 조직, 경사밀도 및 위사밀도를 특별하게 한정하는 것은 아니다.However, the present invention does not specifically limit the tensile strength, structure, warp density and weft density of the high strength fabric.
상기의 고강력 섬유체는 앞에서 설명한 무연(無撚)의 고강력 원사를 경사 및 위사로 사용하여 평직 또는 바스켓직 등의 조직으로 5~15본/㎝ 수준의 경사 및 위사밀도로 제직하여 제조할 수 있다.The high-strength fibrous body can be manufactured by weaving the warp and weft density of 5 to 15 bones / cm with a tissue such as plain weave or basket weave using the unleaded high strength yarn described above as warp and weft. Can be.
한편, 본 발명에 따른 보호구는 앞에서 설명한 하이브리드 시이트를 포함하는 것을 특징으로 한다.On the other hand, the protective equipment according to the invention is characterized in that it comprises the hybrid sheet described above.
본 발명에 따른 보호구는 도 2에 도시된 바와 같이 상기 하이브리드 시이트 들이 겹쳐진 적층체(B)가 고강력 섬유체들이 겹쳐져 있는 적층체(A)의 일면에 적층된 구조일 수도 있고, 도 3에 도시된 바와 같이 상기 하이브리드 시이트들이 겹쳐진 적층체(B)가 고강력 섬유체들이 겹쳐져 있는 적층체(A)의 일면에 적층되고 상기 적층체(A)의 나머지 일면에는 세라믹 판(C)이 적층된 구조일 수도 있고, 도 4에 도시된 바와 같이 상기 하이브리드 시이트들이 겹쳐진 적층체(B)가 고강력 섬유체들이 겹쳐져 있는 적층체(A)의 양면에 적층된 구조일 수도 있다.As shown in FIG. 2, the protective device according to the present invention may have a structure in which the laminate B in which the hybrid sheets are overlapped is laminated on one surface of the laminate A in which high-strength fibers are overlapped. As described above, the laminate B in which the hybrid sheets are overlapped is laminated on one surface of the laminate A in which high-strength fibers are overlapped, and the ceramic plate C is laminated on the other surface of the laminate A. As shown in FIG. 4, the laminate B in which the hybrid sheets are stacked may be stacked on both sides of the laminate A in which high-strength fibers are overlapped.
도 2~도 4는 본 발명에 따른 보호구의 단면개략도 이다.2 to 4 are schematic cross-sectional views of the protective equipment according to the present invention.
상기 세라믹 판(C)은 알루미나 판 등이고 두께는 2~12㎜인 것이 바람직하다.It is preferable that the said ceramic plate (C) is an alumina plate etc., and thickness is 2-12 mm.
세라믹 판(C)의 두께가 상기 범위를 벗어나면 방탄성능 등이 저하되거나 중량이 너무 무거워져 바람직하지 못하다.If the thickness of the ceramic plate (C) is out of the above range, the ballistic resistance or the like is lowered or the weight is too heavy, which is not preferable.
한편, 본 발명에 따른 보호구는 방탄성능이 NATO 7.62 × 51mm FMJ(9.6g) 기준으로 845.0 m/초 이상이다.On the other hand, the protective equipment according to the present invention has a bulletproof performance of 845.0 m / sec or more based on NATO 7.62 × 51mm FMJ (9.6g).
방탄성능은 제조된 보호구를 1개월간 실온에서 방치한 후 NATO 7.62 × 51mm(9.6g)를 사용하여 NIJ-STD-0101.04 방법으로 측정한다.Bulletproof performance is measured by NIJ-STD-0101.04 method using NATO 7.62 × 51 mm (9.6 g) after leaving the prepared protective equipment at room temperature for 1 month.
본 발명에 따른 하이브리드 시이트는 단위면적당 중량이 가벼워 착용감이 우수하면서도 방탄효과, 방검효과, 충격흡수효과 등이 우수하여 방탄복, 방검복, 방탄헬멧, 방탄판, 오토바이 탑승자 안전복, 스키복, 경정복 등의 소재로 유용하다.The hybrid sheet according to the present invention has a light weight per unit area and is excellent in wearing comfort, but also has excellent anti-ballistic effect, anti-glare effect, shock absorbing effect, and so on, bulletproof suit, anti-knit suit, bulletproof helmet, bulletproof plate, motorcycle rider safety suit, ski suit, light suit, etc. It is useful as material.
또한, 본 발명에 따른 하이브리드 시이트는 사용 중 고강력 섬유체 내에 함 침된 전단농화유체가 고화되는 것을 효과적으로 방지하여 오랫동안 사용하여도 우수한 방탄효과 등을 나타낸다.In addition, the hybrid sheet according to the present invention effectively prevents the shear thickening fluid impregnated in the high-strength fibers during use, thereby exhibiting excellent antiballistic effect even after long use.
한편, 본 발명에 따른 보호복은 상기 하이브리드 시이트를 포함하여 낮은 단위면적당 중량으로도 원하는 방탄효과, 방검효과, 충격흡수효과 등를 발현할 수 있어서 착용감이 양호하다.On the other hand, the protective clothing according to the present invention can express the desired anti-ballistic effect, the anti-glare effect, shock absorbing effect and the like even with a low weight per unit area including the hybrid sheet is good wear.
이하, 본 발명을 실시예 및 비교실시예를 통하여 보다 구체적으로 살펴본다.Hereinafter, the present invention will be described in more detail through Examples and Comparative Examples.
그러나, 본 발명은 하기 실시예에 의해서 그 권리범위가 한정되는 것은 아니다.However, the present invention is not limited by the following examples.
실시예Example 1 One
단사섬도가 1.5인 전방향족 폴리아미드 모노필라멘트 1,000개로 이루어져 인장강도가 23g/d이고, 꼬임이 부여되지 않아 꼬임수가 0인 전방향족 멀티필라멘트를 경사 및 위사로 사용하여 10본/㎝의 경사밀도와 10본/㎝의 위사밀도로 평직으로 제직하여 평직의 아라미드 직물을 제조하였다.It consists of 1,000 mono-aromatic polyamide monofilaments with a single yarn fineness of 1.5 and has a tensile strength of 23g / d and no twisting, so that an all-aromatic multifilament with zero twist is used as the warp and weft yarns. Weaving of plain weave with a weft density of 10 bones / cm yielded aramid fabric of plain weave.
다음으로, 상기와 같이 제조된 아라미드 직물 20매를 적층하여 아라미드 직물 적층체(A)를 제조하였다.Next, 20 aramid fabrics prepared as described above were laminated to prepare an aramid fabric laminate (A).
한편, 단사섬도가 1.5인 전방향족 폴리아미드 모노필라멘트 1,000개로 이루어져 인장강도가 23g/d이고, 꼬임수가 1m당 0개인인 전방향족 멀티필라멘트를 경사 및 위사로 사용하여 10본/㎝의 경사밀도와 10본/㎝의 위사밀도로 평직으로 제직하여 평직의 아라미드 직물을 제조하고, 이를 폴리에틸렌글리콜내에 입자직경이 100㎚인 실리카 입자가 65중량%로 충진되어 있는 전단농화유체(STF)에 침지하여 상기 전단농화유체(STF)가 40중량% 함침된 아라미드 직물을 제조한 후 그의 표면과 이면에 각각 폴리프로필렌 필름을 접착하여 하이브리드 시이트를 제조하였다. 계속해서 이를 20매 적층하여 하이브리드 시이트 적층체(B)를 제조하였다.On the other hand, it consists of 1,000 mono-aromatic polyamide monofilaments with a single yarn fineness of 1.5, and uses a wholly aromatic multifilament having a tensile strength of 23 g / d and a twist number of 0 per m as a warp and weft yarn, Weaving of plain weave with a weft density of 10 bones / cm produces aramid fabric of plain weave, which is immersed in a shear thickening fluid (STF) filled with 65% by weight of silica particles having a particle diameter of 100 nm in polyethylene glycol. Aramid fabric impregnated with 40% by weight of shear thickening fluid (STF) was prepared, and then a polypropylene film was attached to the front and back surfaces thereof to prepare a hybrid sheet. Subsequently, 20 sheets were laminated | stacked and the hybrid sheet laminated body (B) was manufactured.
다음으로, 상기와 같이 제조된 아라미드 직물 적층체(A) 일면에 도 1과 같이 하이브리드 시이트 적층체(B)를 적층하여 보호구를 제조하였다.Next, the protective sheet was prepared by laminating the hybrid sheet laminate (B) as shown in FIG. 1 on one surface of the aramid fabric laminate (A) prepared as described above.
제조된 보호구의 중량, 방탄성능 및 방검성능 및 방검성능을 평가한 결과는 표 1과 같다.Table 1 shows the results of evaluating the weight, ballistic performance, and the performance of the prepared protective equipment and the sword performance.
실시예Example 2 2
하이브리드 시이트 적층체(B) 제조시 전단농화유체(STF)가 40중량% 함침된 아라미드 직물의 적층매수를 10매로 변경한 것을 제외하고는 실시예 1과 동일하게 하이브리드 시이트 적층체(B)를 제조한 것과, 실시예 1에서 제조한 아라미드 직물 적층체(A) 표면과 이면 각각에 도 3과 같이 상기와 같이 제조된 하이브리드 시이트 적층체(B)를 각각 적층한 것을 제외하고는 실시예 1과 같이 보호구를 제조하였다.A hybrid sheet laminate (B) was manufactured in the same manner as in Example 1, except that the number of sheets of the aramid fabric impregnated with 40% by weight of the shear thickening fluid (STF) was changed to 10 sheets during the manufacture of the hybrid sheet laminate (B). As described in Example 1, except that the hybrid sheet laminate (B) prepared as described above was laminated on each of the front and back surfaces of the aramid fabric laminate (A) prepared in Example 1, respectively. Protective equipment was prepared.
제조된 보호구의 중량, 방탄성능 및 방검성능을 평가한 결과는 표 1과 같다.Table 1 shows the results of evaluating the weight, ballistic resistance, and sword performance of the prepared protective equipment.
실시예Example 3 3
하이브리드 시이트 적층체(B) 제조시 전단농화유체(STF)가 40중량% 함침된 아라미드 직물의 적층매수를 10매로 변경한 것을 제외하고는 실시예 1과 동일하게 하이브리드 시이트 적층체(B)를 제조한 것과, 도 2와 같이 실시예 1에서 제조한 아라미드 직물 적층체(A)의 표면에는 상기와 같이 제조된 하이브리드 시이트 적층체(B)를 적층하고, 이면에는 두께가 2mm인 알루미나 판(C)을 적층한 것을 제외하고는 실시예 1과 같이 보호구를 제조하였다.A hybrid sheet laminate (B) was manufactured in the same manner as in Example 1, except that the number of sheets of the aramid fabric impregnated with 40% by weight of the shear thickening fluid (STF) was changed to 10 sheets during the manufacture of the hybrid sheet laminate (B). As described above, the hybrid sheet laminate (B) prepared as described above is laminated on the surface of the aramid fabric laminate (A) prepared in Example 1, and the alumina plate (C) having a thickness of 2 mm is provided on the back surface. A protective equipment was prepared in the same manner as in Example 1 except for stacking.
제조된 보호구의 중량, 방탄성능 및 방검성능을 평가한 결과는 표 1과 같다.Table 1 shows the results of evaluating the weight, ballistic resistance, and sword performance of the prepared protective equipment.
비교실시예Comparative Example 1 One
단사섬도가 1.5인 전방향족 폴리아미드 모노필라멘트 1,000개로 이루어져 인장강도가 23g/d이고, 꼬임이 부여되지 않아 꼬임수가 0인 전방향족 멀티필라멘트를 경사 및 위사로 사용하여 10본/㎝의 경사밀도와 10본/㎝의 위사밀도로 평직으로 제직하여 평직의 아라미드 직물을 제조하였다.It consists of 1,000 mono-aromatic polyamide monofilaments with a single yarn fineness of 1.5 and has a tensile strength of 23g / d and no twisting, so that an all-aromatic multifilament with zero twist is used as the warp and weft yarns. Weaving of plain weave with a weft density of 10 bones / cm yielded aramid fabric of plain weave.
다음으로, 상기와 같이 제조된 아라미드 직물 20매를 적층하여 아라미드 직물 적층체(A)를 제조하였다.Next, 20 aramid fabrics prepared as described above were laminated to prepare an aramid fabric laminate (A).
한편, 단사섬도가 1.5인 전방향족 폴리아미드 모노필라멘트 1,000개로 이루어져 인장강도가 23g/d이고, 꼬임수가 1m당 0개인인 전방향족 멀티필라멘트를 경사 및 위사로 사용하여 10본/㎝의 경사밀도와 10본/㎝의 위사밀도로 평직으로 제직하여 평직의 아라미드 직물을 제조하고, 이를 폴리에틸렌글리콜내에 입자직경이 100 ㎚인 실리카 입자가 65중량%로 충진되어 있는 전단농화유체(STF)에 침지하여 상기 전단농화유체(STF)가 40중량% 함침된 아라미드 직물(열가소성 수지층이 접착되지 않은 직물임)을 제조하고 계속해서 이를 20매 적층하여 STF 함침 아라미드 직물 적층체를 제조하였다.On the other hand, it consists of 1,000 mono-aromatic polyamide monofilaments with a single yarn fineness of 1.5, and uses a wholly aromatic multifilament having a tensile strength of 23 g / d and a twist number of 0 per m as a warp and weft yarn, Weaving of plain weave with a weft density of 10 bone / cm produces aramid fabric of plain weave, which is immersed in a shear thickening fluid (STF) filled with 65% by weight of silica particles having a particle diameter of 100 nm in polyethylene glycol. An aramid fabric impregnated with 40% by weight of shear thickening fluid (STF) (which is a fabric to which the thermoplastic resin layer is not bonded) was prepared, and then 20 sheets were laminated to prepare an STF-impregnated aramid fabric laminate.
다음으로, 상기와 같이 제조된 아라미드 직물 적층체(A) 일면에 상기 STF 함침 아라미드 직물 적층체를 적층하여 보호구를 제조하였다.Next, a protective equipment was prepared by laminating the STF-impregnated aramid fabric laminate on one surface of the aramid fabric laminate (A) prepared as described above.
제조된 보호구의 중량, 방탄성능 및 방검성능 및 방검성능을 평가한 결과는 표 1과 같다.Table 1 shows the results of evaluating the weight, ballistic performance, and the performance of the prepared protective equipment and the sword performance.
비교실시예Comparative Example 2 2
실시예 1에서 제조한 아라미드 직물 적층체(A) 표면과 이면 각각에 비교실시예 1에서 제조한 STF 함침 아라미드 직물 적층체 각각 적층하여 보호구를 제조하였다.A protective fabric was prepared by laminating each of the STF-impregnated aramid fabric laminates prepared in Comparative Example 1 on each of the aramid fabric laminates (A) prepared in Example 1, and the back surface thereof.
제조된 보호구의 중량, 방탄성능 및 방검성능을 평가한 결과는 표 1과 같다.Table 1 shows the results of evaluating the weight, ballistic resistance, and sword performance of the prepared protective equipment.
비교실시예Comparative Example 3 3
실시예 1에서 제조한 아라미드 직물 적층체(A)의 표면에는 비교실시예 1에서 제조한 STF 함침 아라미드 직물 적층체를 적층하고 이면에는 두께가 2mm인 알루미나 판(C)을 적층하여 보호구를 제조하였다.A protective fabric was prepared by laminating the STF-impregnated aramid fabric laminate prepared in Comparative Example 1 on the surface of the aramid fabric laminate (A) prepared in Example 1 and laminating the alumina plate (C) having a thickness of 2 mm on the back surface. .
제조된 보호구의 중량, 방탄성능 및 방검성능을 평가한 결과는 표 1과 같다.Table 1 shows the results of evaluating the weight, ballistic resistance, and sword performance of the prepared protective equipment.
상기 표의 물성 중 방검성능(침투거리)은 뾰족한 블레이드가 달린 2.6kg의 양날 단도를 1.35m의 낙하높이에서 제조 후 1개월 동안 실온에 방치한 시료(보호구)에 자유 낙하시킬때 상기 양날단도가 시료에 침투하는 거리를 10회 측정한 후 이들의 평균값으로 나타낸 것이다.In the properties of the table, the sword performance (penetration distance) of the double edged edge with a sharp blade of 2.6kg at the drop height of 1.35m is produced when the sample is left at room temperature for 1 month after free-falling. After measuring the distance to penetrate 10 times is shown as their average value.
또한, 방탄성능은 제조 후 1개월 동안 실온에 방치된 시료(보호구)를 사용하여 NZJ-STD-0101.04 방법으로 10회 측정한 후 이들의 평균값으로 나타낸 것이다.In addition, the ballistic resistance is measured by the NZJ-STD-0101.04 method 10 times using a sample (protective device) left at room temperature for one month after the production is shown as their average value.
도 1 은 본 발명에 따른 하이브리드 시이트의 단면 모식도.1 is a schematic cross-sectional view of a hybrid sheet according to the present invention.
도 2 내지 도 4는 본 발명에 따른 보호구의 단면 개략도.2 to 4 are schematic cross-sectional views of the protective device according to the present invention.
*도면 중 주요부분에 대한 부호설명* Code description of main parts of drawing
1 : 고강력 섬유체 1a : 고강력 섬유체의 위사DESCRIPTION OF SYMBOLS 1: High
1b : 고강력 섬유체의 경사 2 : 전단농화유체1b: slope of high strength fiber body 2: shear thickening fluid
3 : 열가소성 수지층 4 : 전단농화유체가 함침된 고강력 섬유체3: thermoplastic resin layer 4: high strength fiber impregnated with shear thickening fluid
A : 고강력 원사들로 이루어진 고강력 섬유체들이 겹쳐져 있는 적층체.A: A laminate in which high-strength fibers made of high-strength yarns are stacked.
B : 하이드리드 시이트들이 겹쳐져 있는 적층체.B: The laminate in which the hydride sheets are stacked.
C : 세라믹 판C: ceramic plate
Claims (20)