KR20090019044A - Pile fabric using microfiber - Google Patents

Abstract

A pile fabric made of micro-fiber for a tower is provided to prevent resilience degrading at a wetting state with use of folding fabric and to increase water absorption and ability of wiping. A pile fabric made of micro-fiber(21) comprises a loop(20) including the micro-fiber in a ground fabric(10) to be protruded. Knitting form is better for the ground fabric than woven fabric to manufacture the fabric. The ground fabric made of polyester and nylon like synthetic fiber. The micro-fiber can use polyester nylon partitioned type micro-fiber. The thick filament(22) is made of the mother yarn which is thicker than 20D(denier) or film yarn of 0.5~1mm width.

Description

Pile fabric using microfiber}

The present invention relates to pile paper using microfiber, and more particularly to pile paper using microfiber, to improve resilience, in particular, resilience and durability when wet and the ability to remove solid contaminants.

Microfiber has been widely used for mop, cloth, towel paper, etc. because of the formation of fine space on the surface, wide surface area, and excellent water absorption ability. However, since the fineness is very high, it is soft, flexible, and has a good decontamination ability. When the moisture repulsive elasticity is weak and absorbs moisture, it is in close contact with the floor and does not push well.

In order to solve this problem, as shown in Korean Utility Model Publication No. 20-0148937, an attempt has been made to satisfy the cleanliness and work convenience at the same time by weaving regular fiber threads and microfibers repeatedly in a file shape at a predetermined width. .

However, the forge woven in the form of alternately arranging general fiber and microfiber yarns at a predetermined width interval in this form achieves the purpose by reducing the area occupied by the microfiber yarn in the drawing, resulting in close contact with the floor. As the phenomenon is improved, the wiping property itself is inferior, which is undesirable.

The present invention has been made to solve the above problems, while minimizing deterioration of the wiping property, but excellent in resilience, the sliding property due to the adhesion to the bottom surface in the wet state, which is a problem of the conventional mop pile paper made of microfiber An object of the present invention is to provide a pile paper using microfiber with a minimum of bad problems.

Pile paper using a microfiber according to the present invention for achieving the above object,

It is a pile paper in which a twisted yarn of microfibers and a spun yarn or film yarn type of yarn is formed in a loop and protrudes on the surface of the ground forge. The fall of the resilience elasticity is prevented.

When using the pile paper using the microfiber according to the present invention as a cloth cloth, while the absorbency and decontamination ability is exhibited by the microfiber, the loop is not adhered to the bottom even when wet because of the excellent resilience elasticity of the Taesomsa. There is an advantage that does not require excessive force during cleaning.

In addition, when the pile using the microfiber according to the present invention is used to produce a bath mat, etc., while exhibiting excellent absorbency by the microfiber, the resilience of the loop pile is excellent due to the resilience by the Taisum yarn form deformation is good This has the advantage of being small and excellent in touch.

Hereinafter, a filing paper using a microfiber according to the present invention will be described in more detail with reference to the accompanying drawings.

1 is a schematic diagram showing a cross-sectional structure of a pile paper using a microfiber according to the present invention.

Referring to FIG. 1, the pile paper 1 using the microfiber according to the present invention has a form in which the loop 20 pile including the microfiber is protruded from the ground forge 10.

Here, the ground forge 10 may be in the form of a knitted fabric or a woven fabric, but a knitted fabric is advantageous in that it is easy to manufacture. Although the kind of fiber used for knitting the said ground forge is not specifically limited, Synthetic fiber yarns, such as polyester and nylon, can be used.

In this example, a ground forge knitted using 150 denier / 48 filament polyester yarn was used.

On the other hand, the loop 20 pile is formed by enclosing the twisted yarn of the form in which the microfiber yarn 21 and the Taesom yarn 22 are projected to the upper portion of the ground forge 10.

Here, the microfiber yarn 21 may use a commercially available polyester nylon split microfiber yarn (NP yarn), and as the taem yarn 22, a single yarn fineness of 20 or more denier split yarns or a width of 0.5 to 1 mm Film yarn can be used.

The constitution of the twisted yarn of these microfiber yarns 21 and the Taesom yarns 22 is, for example, two yarns in which NP 150 denier 6 strands and polyester splitting yarn 300 denier / 10 filament 1 strand are joined with Z 200 strands. It can be done by coalescing together.

In addition, the twisted yarn may be made by combining the NP 150 denier 6 strands and 38 ㎛ thick, PET film yarns of 0.75mm width Zyyeon, and then joining these two strands of yarn again S200.

In addition, the twisted yarn, the NP 150 denier four strands and a polyester fiber split yarn 200 denier / 10 filament strands of the two strands of the yarn combined in the S500 strands again Z500, or NP 150 denier four strands and 38 ㎛ thickness, 0.75 width Combine two strands of yarn with a 300mm PET film yarn to S300, or two yarns with four NP 150 denier and 38mm thick and 0.75mm wide PET film. It can also be obtained by coalescing with Z500 stations.

When the microfiber according to the present invention is manufactured by using a combination of the microfiber yarn and the Taesom yarn of the above configuration, it is made of a pile fabric of a known type in the form of a knitted paper such as terry cloth fabric, warp knitted terry, circular knitted terry or Russell paper. The used pile paper 1 can be obtained.

On the other hand, in the construction of such a pile, it may be configured by using the combined yarn of the microfiber yarn and the Taesom yarn, or a stripe structure in which the portion composed of only the microfiber yarn and the twisted yarn of the Microfiber yarn and the Taesom yarn are alternately arranged. It can also be configured as.

In the pile paper 1 using the microfiber according to the present invention, since the microfiber yarn 21 and the taem yarn 22 are joined together and wound around the protruding loop 20, the tassel yarn 22 is used. As the microfiber yarn 21 is supported in a twisted shape, the shape of the loop is maintained as it is even when wet, and even when the coarse pollutant is removed by using the microfiber, the microfiber does not break up, thereby improving durability and solid contaminants. Wipeability is improved, and the adhesion to the floor is prevented, so that the cleaning can be performed without great effort.

1 is a schematic diagram showing a cross-sectional structure of a pile paper using a microfiber according to the present invention.

*** Explanation of symbols for main parts of drawing ***

1: file

10: Ground Forge

20: loop

21: microfiber yarn

22: Taesomsa Temple

Claims (1)

A pile of microfibers and twisted yarns in the form of loop yarns or film yarns, which form a loop and protrude on the surface of the ground forge, showing excellent wiping property by the microfibers, and at the same time being wetted by the yarns. Pile paper using a microfiber, characterized in that the fall of the resilience of the repellent is prevented.