KR20070079387A - Method for manufacturing a block made by yellow earth and a block thereby - Google Patents

Method for manufacturing a block made by yellow earth and a block thereby Download PDF

Info

Publication number
KR20070079387A
KR20070079387A KR1020060010004A KR20060010004A KR20070079387A KR 20070079387 A KR20070079387 A KR 20070079387A KR 1020060010004 A KR1020060010004 A KR 1020060010004A KR 20060010004 A KR20060010004 A KR 20060010004A KR 20070079387 A KR20070079387 A KR 20070079387A
Authority
KR
South Korea
Prior art keywords
ocher
block
weight
parts
manufacturing
Prior art date
Application number
KR1020060010004A
Other languages
Korean (ko)
Inventor
김영남
Original Assignee
김영남
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 김영남 filed Critical 김영남
Priority to KR1020060010004A priority Critical patent/KR20070079387A/en
Publication of KR20070079387A publication Critical patent/KR20070079387A/en

Abstract

A method for manufacturing yellow earth block comprising yellow earth, elvan and unslaked lime is provided to prevent generation of toxic substances such as toxic gases emitted from cement floor material, thereby providing sound housing environment. A method including the steps of: kneading yellow earth (S1); molding the kneaded yellow earth in a rectangular shape(S2); drying the mold at 20 to 25 deg.C for 3 to 5 hours (S3); and baking the dried mold at 700 to 1100 deg.C for 6 to 12 hours. The method further comprises adding at least one selected from charcoal, jade, elvan and unslaked lime. Based on 100 weight parts of yellow earth, the charcoal is 15 to 25 weight parts, jade is 5 to 10 weight parts, elvan is 10 to 15 weight parts and unslaked lime is 15 to 20 weight parts.

Description

황토 블록의 제조방법 및 그에 의해 제조된 황토 블록{Method for manufacturing a block made by yellow earth and a block thereby}Method for manufacturing a block made by yellow earth and a block thereby

도 1은 본 발명에 의한 황토 블록을 제조하는 과정을 도시한 순서도,1 is a flow chart illustrating a process of manufacturing an ocher block according to the present invention,

도 2a는 본 발명의 실시예에 의해 제조된 황토 블록을 도시한 도면, 및2a shows an ocher block made by an embodiment of the invention, and

도 2b는 본 발명의 또 다른 실시예에 의해 제조된 황토 블록을 도시한 도면.Figure 2b is a view showing an ocher block produced by another embodiment of the present invention.

본 발명은 황토 블록의 제조방법 및 그에 의해 제조된 황토 블록에 관한 것으로서, 보다 상세하게는 황토를 주성분으로 하고 숯, 옥, 맥반석 또는 생석회를 더 첨가하여 황토 구들장 및 황토 보도블록으로 사용되어 인체에 유익한 주거환경을 설계할 수 있는 황토 블록의 제조방법 및 그에 의해 제조된 황토 블록에 관한 것이다.The present invention relates to a method for producing ocher blocks and to ocher blocks produced by the same, and more particularly, to ocher, which is used as an ocher gouldjang and ocher sidewalk block by adding ocher as a main component and further adding charcoal, jade, gangue stone or quicklime. The present invention relates to a method for manufacturing ocher blocks capable of designing an advantageous residential environment and to ocher blocks produced thereby.

일반적으로 황토는 다량의 탄산칼슘(CaCO3) 외에 실리카(SiO2), 알루미나(Al2O3), 철분, 마그네슘(Mg), 나트륨(Na), 칼리 등을 함유하고 있으며, 이중 다량의 탄산칼슘으로 인해, 황토는 쉽게 부서지지 않는 점력을 가지고 있으며, 물을 첨 가하면 찰흙으로 변하는 성질을 가지고 있다.In general, ocher contains silica (SiO 2 ), alumina (Al 2 O 3 ), iron, magnesium (Mg), sodium (Na), and kali, in addition to a large amount of calcium carbonate (CaCO 3 ). Due to calcium, ocher has a viscous force that does not break easily, and when water is added, it turns into clay.

또한, 황토는 습한 환경에서는 수분을 흡수하고, 건조한 환경에서는 수분을 방출하는 습도조절기능이 매우 우수할 뿐만 아니라, 그 표면이 넓은 벌집구조로, 수많은 공간이 복층을 이루고 있으며, 이러한 구멍안에는 원적외선이 다량 흡수 및 저장되어 있어, 열을 받으면 원적외선을 발산하여 다른 물체의 분자활동을 자극하게 된다.In addition, the yellow soil absorbs moisture in a humid environment and emits moisture in a dry environment, and has a very good honeycomb structure, and has a large honeycomb structure, and a large number of spaces form a double layer. It is absorbed and stored in large quantities, and when heated, it emits far infrared rays, stimulating the molecular activity of other objects.

황토의 가장 근본적인 효능은 황토에서 파장되는 이와 같은 원적외선인데, 원적외선은 세포의 생리작용을 활발하게 해주고, 열에너지를 발생시켜 유해 물질을 방출하며, 인체의 독을 제거해주는 제독제, 해독제로도 사용된다. 황토에서 원적외선이 복사되어 인체에 흡수되면, 신진대사가 원활히 이루어져 노화방지, 신진대사 촉진, 만성피로 방지, 각종 성인병 예방 및 적조 현상을 막는 효과도 있다. The most basic effect of ocher is far infrared rays, which are wavelengthd from ocher. Far infrared rays are used as detoxifying agents and detoxifiers to activate the physiology of cells, generate heat energy, release harmful substances, and remove human poison. . Far-infrared radiation from the loess is absorbed by the human body, the metabolism is smoothly prevented aging, promoting metabolism, preventing chronic fatigue, preventing various adult diseases and red tide.

한편, 종래의 시멘트 등으로 제조되는 보도블록은 여름에 비가 많이 오거나, 겨울에 눈이 오게 되면, 물을 흡수할 수 없어, 길이 질퍽거리거나, 기온이 많이 떨어질 때는 눈이나 비가 얼어 미끄럽게 되는 문제가 있었다.On the other hand, the sidewalk block made of conventional cement or the like is a lot of rain in the summer, or snow in winter, can not absorb the water, when the road flutters, or the temperature drops a lot of snow or rain freezing problem There was.

또한, 종래의 암석을 쪼개어 만든 구들장은 높이 및 크기가 일정치 않아, 시공 및 유지보수에 많은 문제점이 있었는바, 이를 개선하기 위해 주거건물의 바닥재 및 구들장으로 시멘트를 주성분으로 하여 제조되는 경우가 많았으나, 시멘트에서는 인체에 유해한 여러가지 화학물질이 배출되며, 특히, 시멘트 양생과정에서는 각종 유해가스가 발생하여 주거자의 건강에 해를 끼치는 문제가 있었다.In addition, since the height and size of the conventional gouldjang made by splitting the rock was not consistent, there were many problems in construction and maintenance, in order to improve this, the flooring and the gouldard of the residential building were often manufactured with cement as a main component. However, in the cement, various chemicals harmful to the human body are discharged, and in particular, in the cement curing process, various harmful gases are generated, which has a problem of damaging the health of the residents.

본 발명의 목적은 상기와 같은 문제점을 해결하기 위한 것으로서, 원적외선을 방출하는 황토를 주성분으로 하고, 숯, 옥, 맥반석, 생석회를 선택적으로 더 첨가하여 황토 블록을 제조함으로써, 구들장이나 보도블록으로 사용되어, 편평하고 장방형의 규격화된 황토 블록을 제공하면서도 기존의 시멘트 바닥재에서 방출되는 유해가스 등의 인체에 유해한 성분의 발생을 방지하여 보다 쾌적한 주거환경을 만들기 위한 황토 블록의 제조방법 및 그에 의해 제조된 황토 블록을 제공하는 것이다.An object of the present invention is to solve the above problems, the main component of the loess emitting far infrared rays, and by further adding charcoal, jade, elvan, quicklime to manufacture the ocher block, used as a saddle field or sidewalk block To provide a flat and rectangular standardized ocher block while preventing the generation of harmful components such as harmful gas emitted from the existing cement flooring material, and the manufacturing method of the ocher block for making a more comfortable living environment To provide ocher blocks.

상기 목적을 달성하기 위한 본 발명의 황토 블록의 제조방법은 황토를 준비하여 반죽하는 단계(S1); 상기 반죽된 황토를 직육면체 형태로 성형하여 성형체를 제조하는 단계(S2); 상기 성형체를 20~25℃에서 3~5시간 동안 건조하는 단계(S3); 상기 건조된 성형체를 700~1100℃에서 6~12시간 동안 소성하는 단계(S4)를 포함하는 것을 특징으로 한다.Ocher block manufacturing method of the present invention for achieving the above object comprises the steps of preparing and kneading ocher (S1); Forming a dough by molding the kneaded ocher into a rectangular parallelepiped form (S2); Drying the molded body at 20 to 25 ° C. for 3 to 5 hours (S3); It characterized in that it comprises the step (S4) for firing the dried molded body for 6 to 12 hours at 700 ~ 1100 ℃.

여기에서, 상기 황토를 준비하여 반죽하는 단계(S1)에 후속하여, 상기 황토에 숯, 옥, 맥반석 및 생석회를 포함하는 그룹에서 선택된 하나 이상의 물질을 첨가하여 혼합하는 단계를 더 포함할 수 있는바, 이때, 황토 100 중량부를 기준으로 상기 숯은 15~20 중량부, 옥은 5~10 중량부, 맥반석은 10~15 중량부, 생석회는 15~20 중량부인 것이 바람직하다.Here, after the step of preparing and kneading the ocher (S1), may further comprise the step of mixing by adding one or more substances selected from the group containing charcoal, jade, elvan and quicklime to the ocher In this case, the char is 15 to 20 parts by weight, jade is 5 to 10 parts by weight, ganban stone is 10 to 15 parts by weight, quicklime is preferably 15 to 20 parts by weight based on 100 parts by weight of ocher.

또한, 본 발명은 주성분으로 황토를 포함하는 것을 특징으로 하는 황토 블록을 제공하며, 상기 황토 블록은 황토 100 중량부를 기준으로 숯 15~20 중량부, 옥 5~10 중량부, 맥반석 10~15 중량부 및 생석회 15~20중량부를 포함하는 그룹에서 선택된 하나 이상의 성분을 더 포함하는 것을 특징으로 한다.In addition, the present invention provides an ocher block characterized in that it comprises ocher as a main component, the ocher block is based on 100 parts by weight of ocher 15 to 20 parts by weight of charcoal, 5 to 10 parts by weight of jade, 10 to 15 parts by weight of elvan And at least one component selected from the group comprising 15-20 parts by weight of quicklime.

이하, 첨부된 도면을 참조하여 본 발명의 황토 블록의 제조방법 및 그에 의해 제조된 황토 블록에 대하여 보다 상세히 설명하면 다음과 같다.Hereinafter, with reference to the accompanying drawings will be described in more detail with respect to the manufacturing method of the ocher block of the present invention and the ocher block produced by it.

도 1은 본 발명에 의한 황토 블록을 제조하는 과정을 단계적으로 도시한 순서도이다.Figure 1 is a flow chart illustrating a step-by-step process for producing an ocher block according to the present invention.

도 1에 나타난 바와 같이, 먼저, 반죽단계(S1)에서는, 본 발명에 의한 황토 블록의 주성분인 황토를 준비하여 반죽한다.As shown in Figure 1, first, in the kneading step (S1), to prepare the kneading ocher which is the main component of the ocher block according to the present invention.

이때, 상기 황토만으로도 블록의 제조가 가능하지만, 경우에 따라서는 황토 반죽에 숯, 옥, 맥반석 또는 생석회를 한가지 이상 더 첨가하는 것이 가능하다. 첨가되는 각각의 양은 황토 100 중량부를 기준으로 숯 10~15 중량부, 옥 5~10 중량부, 맥반석 10~15 중량부, 생석회 15~20 중량부인 것이 바람직하다. At this time, it is possible to manufacture the block only by the loess, but in some cases it is possible to add more than one charcoal, jade, ganban stone or quicklime to the loess dough. Each amount added is 10 to 15 parts by weight of charcoal, 5 to 10 parts by weight of jade, 10 to 15 parts by weight of ganbanite, and 15 to 20 parts by weight of quicklime based on 100 parts by weight of ocher.

아래 표 1에는 각각의 실시예에 따른 황토 블록 제조에 첨가되는 황토, 숯, 옥, 맥반석 및 생석회의 양이 나타나있다.Table 1 below shows the amount of ocher, charcoal, jade, elvan and quicklime added to the ocher block preparation according to each example.

구분division 황토(중량부)Yellow soil (parts by weight) 숯(중량부)Charcoal (part by weight) 옥(중량부)Jade (part by weight) 맥반석(중량부)Elvan Stone (parts by weight) 생석회(중량부)Quicklime (parts by weight) 실시예 1Example 1 100100 -- -- -- 실시예 2Example 2 100100 10~1510-15 -- -- 실시예 3Example 3 100100 -- 5~105-10 -- 실시예 4Example 4 100100 -- -- 10~1510-15 실시예 5Example 5 100100 15~2015-20 실시예 6Example 6 100100 10~1510-15 5~105-10 -- 실시예 7Example 7 100100 10~1510-15 10~1510-15 실시예 8Example 8 100100 10~1510-15 -- 15~2015-20 실시예 9Example 9 100100 -- 5~105-10 10~1510-15 실시예 10Example 10 100100 5~105-10 15~2015-20 실시예 11Example 11 100100 10~1510-15 15~2015-20 실시예 12Example 12 100100 10~1510-15 5~105-10 10~1510-15 실시예 13Example 13 100100 10~1510-15 5~105-10 15~2015-20 실시예 14Example 14 100100 10~1510-15 10~1510-15 15~2015-20 실시예 15Example 15 100100 5~105-10 10~1510-15 15~2015-20 실시예 16Example 16 100100 10~1510-15 5~105-10 10~1510-15 15~2015-20

이때, 첨가되는 숯, 옥 및 맥반석의 특징을 자세히 살펴보면 다음과 같다.At this time, look at the characteristics of the added charcoal, jade and ganban stone in detail as follows.

숯은 직경이 0.1~0.7cm 크기인 것이 바람직하며, 숯의 탄소성분으로 인하여 음이온 및 원적외선을 방출하며, 전자파 차단 및 공기를 정화하는 기능이 있다. 또한, 탈취, 항균 및 해독 작용이 원활하여, 주거환경 개선에 큰 효과가 있다.Charcoal preferably has a diameter of 0.1 ~ 0.7cm size, emits anion and far infrared rays due to the carbon component of the charcoal, has the function of blocking the electromagnetic waves and purifying the air. In addition, deodorization, antibacterial and detoxification effect is smooth, there is a great effect in improving the living environment.

옥은 인체에 필요한 광물질, 칼슘 및 마그네슘을 함유하고 있으며, 이중 마그네슘은 인체 세포를 구성하고 있는 마그네슘과 같아, 옥에서 나오는 기파동과 인체 세포의 기파동이 같은 파동이므로, 옥에서 발산하는 원적외선과 파동이 인체 세포에 골고루 침투하여 공명공진 작용을 함으로써, 세포조직의 부활, 혈액순환, 혈액의 약 알칼리화, 체내 유해 노폐물의 배설 등의 효과가 있다.Jade contains minerals, calcium, and magnesium needed for the human body, and magnesium is the same as magnesium that constitutes human cells. The waves evenly penetrate the human cells and resonate resonantly, resulting in the resurgence of cellular tissues, blood circulation, weak alkalinization of blood, and the excretion of harmful wastes in the body.

맥반석에서는 인체에 활력을 주는 40여종 이상의 미네랄이 용출되어 신진대사와 피부건강관리에 효과가 있으며, 맥반석의 넓은 표면적으로 인해 오염물질, 중금속 등을 흡착, 분해할 뿐만 아니라, 시멘트에서 나오는 독성을 중화하고, 항균, 방충의 효과가 있다.Elvan rocks have more than 40 kinds of minerals that elevate the human body and are effective for metabolism and skin health management.The large surface area of elvan rocks not only adsorbs and decomposes pollutants and heavy metals, but also neutralizes toxic from cement. It has the effect of antibacterial and insect repellent.

또한, 생석회는 산화칼슘(CaO)으로 단기간에 굳는 성질로 인하여, 토목건축 재료로 많이 이용되며, 항균 작용의 효과가 있다. 이러한 생석회를 본 발명의 황토 블록에 첨가하게 되면, 황토 블록이 보다 단단해지며 빨리 굳는 효과를 얻을 수 있다.In addition, quicklime is a calcium oxide (CaO) due to its hardening property in a short time, it is widely used as a civil engineering building material, there is an antibacterial effect. When the quicklime is added to the ocher block of the present invention, the ocher block becomes harder and a fastening effect can be obtained.

다음, 성형단계(S2)에서는 상기 단계(S1)에서 준비된 반죽을 직사각형 형태로 프레스 가공하여 도 2a 및 도 2b에 도시된 형태와 같이 성형한다.Next, in the forming step (S2), the dough prepared in the step (S1) is press-molded into a rectangular shape and molded as shown in Figures 2a and 2b.

건조단계(S3)에서는 상기 성형단계(S2)에서 성형된 직사각형 형태의 성형체를 20~25℃의 온도에서 3~5시간 동안 건조하여, 황토 블록을 완성한다.In the drying step (S3) to dry the molded body of the rectangular shape formed in the molding step (S2) for 3 to 5 hours at a temperature of 20 ~ 25 ℃, to complete the ocher block.

소성단계(S4)에서는 상기 황토 블록을 건조된 로(爐)에서 700~1100℃의 온도에서 6~12시간 동안 가열한다. 이때, 로의 온도가 700℃보다 낮거나, 가열시간이 6시간보다 짧으면, 완성된 블록의 강도가 낮아 깨지기 쉬우며, 로의 온도가 1100℃보다 높거나, 가열시간이 12시간보다 길게 되면, 블록의 열전도 능력 및 온도 지속효과가 떨어지는 문제점이 있다.In the firing step (S4) the ocher block is heated for 6-12 hours at a temperature of 700 ~ 1100 ℃ in a dried furnace (爐). At this time, if the furnace temperature is lower than 700 ℃, or the heating time is less than 6 hours, the strength of the finished block is low and fragile, and if the furnace temperature is higher than 1100 ℃, or the heating time is longer than 12 hours, There is a problem that the heat conduction ability and the temperature lasting effect is inferior.

상기의 방법으로 제조된 본 발명의 황토 블록은 주거용 건물의 구들장 또는 인도의 보도블록으로 사용하는 것이 가능하다.The ocher block of the present invention produced by the above method can be used as a saddleyard or sidewalk block of a residential building.

먼저, 황토 구들장으로 사용할 경우, 도 2a 및 도 2b에 도시된 바와 같이, 사용되는 용도에 따라 크기를 변형하여 성형하여 사용하는 것이 가능하며, 도 2a에 도시된 황토 블록은 재래식 시공방법으로 구들장을 설치하는데 적합한 형태로서, 직육면체 형상이며, a는 40~45cm, b는 35~40cm, c는 4~6cm인 것이 바람직하며, 특히, a는 43cm, b는 38cm, c는 5cm인 것이 가장 바람직하다. First, in the case of using the ocher saddle field, as shown in Figures 2a and 2b, it is possible to use the molded by changing the size according to the intended use, the ocher block shown in Figure 2a is a conventional construction method As a form suitable for installation, it is a rectangular parallelepiped shape, a is preferably 40 to 45 cm, b is 35 to 40 cm, c is 4 to 6 cm, and particularly, a is 43 cm, b is 38 cm, and c is 5 cm. .

또한, 도 2b에 도시된 황토 블록은 도 2a에 도시된 황토 블록에 비하여 두께가 얇은 직육면체 형태로서, 현재 시공된 아파트 바닥의 시멘트 및 보일러 위에 본 발명에 의한 황토 블록을 올려서 완성하기에 적합한 형태이다. 도 2b에서 d는 20~45cm, e는 20~40cm, f는 1~2cm인 것이 바람직하며, 특히, d는 43cm, e는 38cm, f는 1.6cm인 것이 가장 바람직하다.In addition, the ocher block shown in Figure 2b is a thin rectangular parallelepiped shape than the ocher block shown in Figure 2a, is suitable for completing the loess block according to the present invention on the cement and boiler of the currently constructed apartment floor . In Figure 2b, d is 20 ~ 45cm, e is 20 ~ 40cm, f is preferably 1 ~ 2cm, in particular, d is 43cm, e is 38cm, f is most preferably 1.6cm.

이와 같이 황토 블록을 구들장으로 사용하게 되면, 아파트의 시멘트 및 보일러 위에 시공하여 사용이 가능함으로써, 시멘트에서 나오는 유해가스 등을 흡수하여 보다 개선된 주거환경을 제공할 수 있다.When the ocher block is used as a saddle field, it is possible to construct and use it on the cement and the boiler of the apartment, thereby providing a more improved living environment by absorbing harmful gases from the cement.

또한, 본 발명에 의한 황토 블록을 인도용 보도블록으로 사용할 경우, 황토의 특성으로 인하여 겨울에 눈이 와도 바닥이 잘 얼지 않아 미끄럽지 않으며, 여름에 비가 많이 와도 황토가 물을 흡수하여 길이 질퍽거리지 않는 효과가 있다.In addition, when the ocher block according to the present invention is used as a sidewalk block for sidewalk, due to the characteristics of the ocher, even if it snows in winter, the bottom does not freeze well because it does not slip, and even when it rains a lot in summer, the ocher absorbs water so that the road does not flutter. It works.

또한, 황토 블록의 주성분인 황토, 숯, 옥, 맥반석 등에서 방출되는 원적외선 및 항균 작용 등으로 인하여, 황토 보도블록을 설치한 주변의 환경이 정화되어, 주거환경이 개선되는 효과가 있다.In addition, due to the far-infrared rays and antimicrobial activity emitted from loess, charcoal, jade, elvan, etc., the main component of the ocher block, the environment around the ocher sidewalk block is purified, thereby improving the residential environment.

본 발명에 의한 황토 블록은 물질을 활성화시키는데 가장 효력이 있는 원적외선과 열에너지를 발생하는 황토를 주성분으로 제조되었으므로, 이러한 황토 블록을 사용함으로써, 인체 내의 유해물질을 방출하며, 사계절 쾌적한 온도를 유지하고, 여름철의 습기를 흡수했다가 건조한 계절에 뿜어주고, 흙 미립자 틈 속으로 바 람이 통해서 환풍기 구실도 한다는 장점이 있다.The ocher block according to the present invention has been manufactured with the main component of the far-infrared rays and thermal energy generating the most energy to activate the material, by using such ocher blocks, to release the harmful substances in the human body, to maintain a comfortable temperature four seasons, It has the advantage of absorbing moisture in summer and blowing it out in the dry season, and also acting as a fan through the wind into the soil particles.

Claims (6)

황토를 준비하여 반죽하는 단계(S1);Preparing ocher to knead (S1); 상기 반죽된 황토를 직육면체 형태로 성형하여 성형체를 제조하는 단계(S2);Forming a dough by molding the kneaded ocher into a rectangular parallelepiped form (S2); 상기 성형체를 20~25℃에서 3~5시간 동안 건조하는 단계(S3);Drying the molded body at 20 to 25 ° C. for 3 to 5 hours (S3); 상기 건조된 성형체를 700~1100℃에서 6~12시간 동안 소성하는 단계(S4)를 포함하는 것을 특징으로 하는 황토 블록의 제조방법.The dried molded body manufacturing method of the ocher block comprising the step (S4) of firing for 6 to 12 hours at 700 ~ 1100 ℃. 제 1항에 있어서,The method of claim 1, 상기 황토를 준비하여 반죽하는 단계(S1)에 후속하여, 상기 황토에 숯, 옥, 맥반석 및 생석회를 포함하는 그룹에서 선택된 하나 이상의 물질을 첨가하여 혼합하는 단계를 더 포함하는 것을 특징으로 하는 황토 블록의 제조방법.After the step of preparing and kneading the ocher (S1), the ocher block further comprises the step of adding and mixing at least one substance selected from the group containing charcoal, jade, elvan and quicklime to the ocher Manufacturing method. 제 2항에 있어서,The method of claim 2, 상기 황토 100 중량부를 기준으로 상기 숯은 15~20 중량부, 옥은 5~10 중량부, 맥반석은 10~15 중량부, 생석회는 15~20 중량부인 것을 특징으로 하는 황토 블록의 제조방법.Based on 100 parts by weight of the ocher, the charcoal is 15 to 20 parts by weight, jade is 5 to 10 parts by weight, elvan is 10 to 15 parts by weight, quicklime is a manufacturing method of the ocher block, characterized in that 15 to 20 parts by weight. 제 2항에 있어서,The method of claim 2, 상기 황토 100 중량부를 기준으로 상기 숯은 15~20 중량부, 생석회는 15~20 중량부인 것을 특징으로 하는 황토 블록의 제조방법.The charcoal is based on 100 parts by weight of the loess 15 to 20 parts by weight, quicklime is a manufacturing method of the ocher block, characterized in that 15 to 20 parts by weight. 제 1항 내지 제 4항 중 어느 한 항에 있어서, The method according to any one of claims 1 to 4, 상기 황토 블록은 황토 구들장 또는 황토 보도블록인 것을 특징으로 하는 황토 블록의 제조방법.The ocher block is a manufacturing method of the ocher block, characterized in that the ocher saddle or ocher sidewalk block. 제 1항 내지 제 5항 중 어느 한 항의 제조방법에 의해 제조되는 것을 특징으로 하는 황토 블록.Claims 1 to 5 characterized in that the ocher block is produced by the manufacturing method of any one of claims.
KR1020060010004A 2006-02-02 2006-02-02 Method for manufacturing a block made by yellow earth and a block thereby KR20070079387A (en)