KR20050111817A - Apparatus for testing abrasion resistance of sponge weatherstrip for automobile - Google Patents
Apparatus for testing abrasion resistance of sponge weatherstrip for automobile Download PDFInfo
- Publication number
- KR20050111817A KR20050111817A KR1020040036708A KR20040036708A KR20050111817A KR 20050111817 A KR20050111817 A KR 20050111817A KR 1020040036708 A KR1020040036708 A KR 1020040036708A KR 20040036708 A KR20040036708 A KR 20040036708A KR 20050111817 A KR20050111817 A KR 20050111817A
- Authority
- KR
- South Korea
- Prior art keywords
- specimen
- cable
- rod
- low temperature
- rubber
- Prior art date
Abstract
본 발명은 자동차용 연질가류고무의 저온성능 평가장치에 관한 것으로서, 저온 분위기를 조성 및 유지시키기 위한 저온 챔버와, 이 저온 챔버 내에서 고무시편을 고정하기 위한 시편 고정 지그와, 이 시편 고정 지그에 고정된 고무시편을 케이블에 매달린 로드가 자유 낙하하여 타격하는 방식의 타격장치부와, 상기 케이블을 잡아주어 로드 위치를 고정하는 한편 타이머 작동에 의해 설정 시간 후 케이블을 놓아주어 로드의 낙하가 이루어질 수 있게 하는 케이블 고정부를 포함하여 이루어진 자동차용 연질가류고무의 저온성능 평가장치에 관한 것이다. The present invention relates to an apparatus for evaluating low temperature performance of automotive soft vulcanized rubber, comprising a low temperature chamber for creating and maintaining a low temperature atmosphere, a specimen fixing jig for fixing a rubber specimen in the cold chamber, and a specimen fixing jig. The striking device part in which the rod which hangs the fixed rubber specimen to the cable falls freely and hits the rod, while holding the cable to fix the rod position, and releasing the cable after the set time by the timer operation, the rod can be dropped. It relates to a low-temperature performance evaluation device for soft vulcanized rubber for automobiles comprising a cable fixing portion.
이러한 본 발명의 평가장치에 의하면, 종래의 저온취하시험기와 비교하여, 상온이 아닌 저온 분위기 상태에서 평가가 가능하기 때문에 신뢰도 높은 데이터를 얻을 수 있고, 인체에 유해하고 화재 위험성이 있는 메탄올을 사용하지 않아도 되므로 시험시 안전성을 보장할 수 있으며, 드라이아이스를 사용하지 않기 때문에 시험 비용을 줄일 수 있는 장점과 아울러 저온 챔버에 의해 온도 유지가 이루어지므로 시험과정이 보다 간단해지는 장점이 있게 된다.According to the evaluation apparatus of the present invention, since it is possible to evaluate in a low temperature atmosphere state, not at room temperature, compared to a conventional low temperature withdrawal tester, it is possible to obtain reliable data, and do not use methanol, which is harmful to human body and has a fire risk. Since it is not necessary, it is possible to guarantee safety during the test, and because it does not use dry ice, the test cost can be reduced, and the temperature is maintained by the low temperature chamber, thereby simplifying the test process.
Description
본 발명은 자동차용 연질가류고무의 저온성능 평가장치에 관한 것으로서, 저온 분위기를 조성 및 유지시키기 위한 저온 챔버와, 이 저온 챔버 내에서 고무시편을 고정하기 위한 시편 고정 지그와, 이 시편 고정 지그에 고정된 고무시편을 케이블에 매달린 로드가 자유 낙하하여 타격하는 방식의 타격장치부와, 상기 케이블을 잡아주어 로드 위치를 고정하는 한편 타이머 작동에 의해 설정 시간 후 케이블을 놓아주어 로드의 낙하가 이루어질 수 있게 하는 케이블 고정부를 포함하여 이루어진 자동차용 연질가류고무의 저온성능 평가장치에 관한 것이다.The present invention relates to an apparatus for evaluating low temperature performance of automotive soft vulcanized rubber, comprising a low temperature chamber for creating and maintaining a low temperature atmosphere, a specimen fixing jig for fixing a rubber specimen in the cold chamber, and a specimen fixing jig. The striking device part in which the rod which hangs the fixed rubber specimen to the cable falls freely and hits the rod, while holding the cable to fix the rod position, and releasing the cable after the set time by the timer operation, the rod can be dropped. It relates to a low-temperature performance evaluation device for soft vulcanized rubber for automobiles comprising a cable fixing portion.
일반적으로 연질가류고무는 웨더스트립(weatherstrip), 오일씰, 방진 고무 등 자동차용 고무로 많이 사용되며, 모든 환경조건에 적합하도록 배합 설계가 되어 제품의 소재로 사용된다.In general, soft vulcanized rubber is widely used as automotive rubber such as weatherstrip, oil seal, and dustproof rubber, and it is used as a material of a product with a compounding design suitable for all environmental conditions.
한편, 혹한에 오래 방치된 고무제품의 경우 갑작스런 충격을 받으면 깨지거나 크랙(crack)이 발생하여, 제품 성능의 저하를 야기할 수 있다.On the other hand, in the case of a rubber product that has been left for a long time in the cold, a sudden impact is broken or cracks (crack), it may cause a decrease in product performance.
특히, 연질가류고무는 -40℃ 이하의 혹한에서도 성능을 발휘해야 하는 경우도 있기 때문에, 소재 및 제품 개발과정에서 시험실 및 실차에서 미리 저온성능 평가를 실시한다.In particular, soft vulcanized rubber may have to perform at cold temperatures below -40 ° C. Therefore, low-temperature performance should be evaluated in advance in the laboratory and the actual vehicle during the material and product development process.
통상, 연질가류고무의 저온성능 평가는 도 1 및 도 2에 도시한 바와 같은 저온취하시험기를 이용하여 평가한다.Usually, the low temperature performance evaluation of the soft vulcanized rubber is evaluated using a low temperature withdrawal tester as shown in Figs.
이 장치는 저온취성을 평가하는 장치로서, 저온 상태의 시편을 타격하여 부서지는 정도를 평가하는 장치이다.It is a device for evaluating low temperature brittleness, and for evaluating the degree of breakage by hitting a specimen in a low temperature state.
시험방법을 도 1과 도 2를 참조하여 간단히 설명하면, 장치(1)의 항온조(2) 내부에 메탄올을 일정량 넣은 다음, 드라이아이스를 메탄올에 담가 저온을 만들고, 이후 히터(3)로 온도를 조절하여 요구하는 저온을 만든다.1 and 2, the test method is briefly described in which a certain amount of methanol is added to the inside of the thermostat 2 of the apparatus 1, and then the dry ice is immersed in methanol to make a low temperature. Adjust to make the required low temperature.
이와 같이 요구 온도가 세팅된 상태에서 고무시편(4)을 3분간 담가 시편 내부에 한기가 스며들도록 수킹(soaking)한 후, 시편(4)을 다시 꺼내어 시편 고정 지그(5)에 고정한다.After soaking the rubber specimen 4 for 3 minutes in the state where the required temperature is set and soaking the cold inside the specimen, the specimen 4 is taken out again and fixed to the specimen fixing jig 5.
이후, 커버(6)를 닫고 타격기(7)를 구동하여 시편을 타격하게 되며, 이와 같이 타격한 상태에서 시편의 크랙이나 깨짐 유무를 검사하게 된다.Subsequently, the cover 6 is closed and the blower 7 is driven to hit the specimen, and the crack or crack of the specimen is examined in the hit state.
그러나, 위의 시험장비는 연질가류고무의 저온성능을 짧은 시간에 평가할 수 있는 장점은 있지만, 장치를 가동시키기가 번거롭고, 위험물질에 시험자가 노출될 수 있다는 단점이 있다.However, the above test equipment has the advantage of evaluating the low temperature performance of the soft vulcanized rubber in a short time, but it is cumbersome to operate the device, and the tester can be exposed to dangerous substances.
즉, 시험자는 계속해서 항온조(2) 내 온도를 유지시켜야 하므로 드라이아이스를 넣기도 하고 히터(3)를 가동시켜야 하는 번거로움이 있으며, 시험자가 온도계(8)를 보고 직접 온도를 맞추어야 한다.In other words, the tester has to continuously maintain the temperature in the thermostat (2), so there is a hassle of putting dry ice and operating the heater (3), and the tester has to adjust the temperature by looking at the thermometer (8).
또한, 메탄올은 휘발성 액체이므로 화재의 위험성이 있고, 또한 메탄올 증기는 인체에 유해하기 때문에 시험자에게 치명적이다.In addition, since methanol is a volatile liquid, there is a risk of fire, and methanol vapor is fatal to the tester because it is harmful to the human body.
또한, 드라이아이스는 상온에서 기화되기 때문에 여러 번 시험을 하려면 많은 양의 드라이아이스가 필요하여 많은 시험 비용이 소모된다.In addition, since dry ice is vaporized at room temperature, many tests require a large amount of dry ice, which consumes a lot of test cost.
또한, 기존의 저온성능 평가시에는 저온에서 수킹(soaking)된 시편을 꺼내어 시편 고정 지그에 고정한 후 상온에서 평가를 시행하기 때문에 신속하게 실시하지 않으면 평가 결과의 신뢰도가 떨어진다는 단점이 있다. In addition, the conventional low-temperature performance evaluation has a drawback that the reliability of the evaluation results are lowered if not carried out quickly because the evaluation is performed at room temperature after taking out the specimen soaked at a low temperature and fixed to the specimen fixing jig.
따라서, 본 발명은 상기와 같은 문제점을 해결하기 위하여 발명한 것으로서, 저온 분위기를 조성 및 유지시키기 위한 저온 챔버와, 이 저온 챔버 내에서 고무시편을 고정하기 위한 시편 고정 지그와, 이 시편 고정 지그에 고정된 고무시편을 케이블에 매달린 로드가 자유 낙하하여 타격하는 방식의 타격장치부와, 상기 케이블을 잡아주어 로드 위치를 고정하는 한편 타이머 작동에 의해 설정 시간 후 케이블을 놓아주어 로드의 낙하가 이루어질 수 있게 하는 케이블 고정부를 포함하여 이루어진 자동차용 연질가류고무의 저온성능 평가장치를 제공함으로써, 종래의 저온취하시험기와 비교하여, 상온이 아닌 저온 분위기 상태에서 평가가 가능하기 때문에 신뢰도 높은 데이터를 얻을 수 있고, 인체에 유해하고 화재 위험성이 있는 메탄올을 사용하지 않아도 되므로 시험시 안전성을 보장할 수 있으며, 드라이아이스를 사용하지 않기 때문에 시험 비용을 줄일 수 있는 장점과 아울러 저온 챔버(110)에 의해 온도 유지가 이루어지므로 시험과정이 보다 간단해지는 장점을 제공하는데 그 목적이 있다. Therefore, the present invention has been invented to solve the above problems, and includes a low temperature chamber for creating and maintaining a low temperature atmosphere, a specimen fixing jig for fixing a rubber specimen in the low temperature chamber, and a specimen fixing jig. The striking device part in which the rod which hangs the fixed rubber specimen to the cable falls freely and hits the rod, while holding the cable to fix the rod position, and releasing the cable after the set time by the timer operation, the rod can be dropped. By providing a low temperature performance evaluation device for automotive soft vulcanized rubber including a cable fixing part, it is possible to evaluate in a low temperature atmosphere condition, not room temperature compared to the conventional low temperature withdrawal tester, thereby obtaining reliable data. And do not use methanol, which is harmful to humans and poses a fire hazard. Therefore, it is possible to ensure safety during the test, and because it does not use dry ice, the test cost is reduced and the temperature is maintained by the low temperature chamber 110, and thus the test process becomes simpler. There is this.
이하, 첨부한 도면을 참조하여 본 발명을 상세히 설명하면 다음과 같다.Hereinafter, the present invention will be described in detail with reference to the accompanying drawings.
본 발명에 따른 자동차용 연질가류고무의 저온성능 평가장치는, Low temperature performance evaluation apparatus for soft vulcanized rubber for automobiles according to the present invention,
저온 분위기의 조성 및 유지가 가능하도록 된 저온 챔버와;A low temperature chamber capable of forming and maintaining a low temperature atmosphere;
이 저온 챔버 내에 설치되어 받침대 역할을 하는 지지대와;A support installed in the low temperature chamber and serving as a pedestal;
이 지지대 위에서 고무시편을 고정하기 위한 시편 고정 지그와;A specimen fixing jig for fixing the rubber specimen on the support;
이 시편 고정 지그에 고정된 고무시편을 케이블에 매달린 로드가 자유 낙하하여 타격하도록 구성되는 타격장치부와;A striking device unit configured to freely strike a rod suspended from a cable on a rubber specimen fixed to the specimen fixing jig;
상기 지지대 위에서 상기 케이블이 통과하도록 설치되고 통과하는 케이블을 잡아주어 상기 로드 위치를 고정하는 한편 시험시 상기 케이블을 놓아주어 로드의 낙하가 이루어질 수 있게 하는 케이블 고정부;A cable fixing part configured to hold the cable passing through the cable and to fix the rod position on the support while releasing the cable during the test to allow the rod to fall;
를 포함하여 이루어지고, 상기 시편 고정 지그가 고무시편 일부분만을 압착하여 고정하되 고무시편 나머지 부분이 상기 로드의 낙하경로상에 위치되도록 고정하는 것을 특징으로 한다.It comprises a, the specimen fixing jig is fixed by pressing only a portion of the rubber specimen, characterized in that the remaining rubber specimen is fixed to be positioned on the drop path of the rod.
이하, 첨부한 도면을 참조하여 본 발명을 더욱 상세히 설명하면 다음과 같다.Hereinafter, the present invention will be described in more detail with reference to the accompanying drawings.
종래 저온취하시험기 사용시 시험 위험성과 번거로움을 줄이기 위하여, 본 발명에서는 저온 평가시 널리 사용되고 있는 저온 챔버에서 연질가류고무의 저온성능을 평가하는 장치가 개시된다.In order to reduce the test risk and hassle when using the conventional low temperature withdrawal tester, the present invention discloses a device for evaluating the low-temperature performance of the soft vulcanized rubber in a low temperature chamber that is widely used during low temperature evaluation.
종래기술의 설명에서와 같이, 보통 - 40℃에서 연질가류고무의 저온성능을 평가하는데, 기존 장비는 - 40℃의 액상에 시편을 넣어 시편상태를 조성하므로 수킹(soaking)시간이 짧은 이점이 있다. As in the description of the prior art, the low-temperature performance of the soft vulcanized rubber is usually evaluated at -40 ° C. Existing equipment has a short soaking time because the specimen is put in a liquid phase at -40 ° C to form a specimen state. .
본 발명의 장비를 이용하게 되면, - 40℃의 기상 분위기 온도에서 원하는 시편상태를 조성하므로 수킹시간이 기존 장비에 비해 다소 길어질 수는 있으나, 시험시 별다른 위험요소가 없고, 기존의 저온성능 평가시처럼 수킹(soaking)된 시편을 상온으로 꺼내지 않아도 되므로 신뢰도 높은 데이터를 얻을 수 있게 된다.When using the equipment of the present invention, the soaking time can be somewhat longer than the existing equipment because it forms the desired specimen state at a gaseous atmosphere temperature of-40 ℃, there is no risk factor during the test, when the existing low-temperature performance evaluation As it is not necessary to take out the soaked specimen at room temperature, it is possible to obtain reliable data.
이하, 본 발명의 구성을 첨부한 도면을 참조로 하여 상세히 설명하면 다음과 같다.Hereinafter, the configuration of the present invention will be described in detail with reference to the accompanying drawings.
첨부한 도 3은 본 발명에 따른 저온성능 평가장치를 도시한 구성도이다.3 is a block diagram showing a low temperature performance evaluation apparatus according to the present invention.
이에 도시한 바와 같이, 본 발명의 평가장치(100)는 시편상태 조성 및 타격 평가시에 요구되는 저온 분위기를 조성 및 제공, 유지시키기 위한 저온 챔버(110)를 포함하며, 이 저온 챔버(110) 내에 시편 고정 지그(130)를 포함한 각 구성요소가 설치된 구조로 되어 있다.As shown in the drawing, the evaluation apparatus 100 of the present invention includes a low temperature chamber 110 for forming, providing, and maintaining a low temperature atmosphere required for specimen state composition and impact evaluation, and the low temperature chamber 110. Each component including the specimen holding jig 130 is provided in the structure.
이 저온 챔버(110)로는 - 40℃ 이하의 저온 분위기를 조성 및 유지할 수 있는 챔버가 사용된다.As the low temperature chamber 110, a chamber capable of forming and maintaining a low temperature atmosphere of -40 ° C or lower is used.
상기 저온 챔버(110) 내에 구성되는 구성요소로서, 받침대 역할을 하는 지지대(120), 이 지지대(120) 위에 장착되는 시편 고정 지그(130), 케이블(143)에 매달린 로드(142)가 타격하는 방식으로 상기 시편 고정 지그(130)에 고정된 고무시편(101)을 일정 하중으로 타격하는 타격장치부(140), 상기 케이블(143)을 잡아주어 로드(142) 위치를 고정하는 한편 케이블(143)을 놓아주어 로드(142)의 낙하가 이루어질 수 있게 하는 케이블 고정부(150)가 설치된다.As a component configured in the low temperature chamber 110, a support 120 serving as a pedestal, a specimen fixing jig 130 mounted on the support 120, the rod 142 suspended on the cable 143 hits While holding the cable 143 and the striking device unit 140 that strikes the rubber specimen 101 fixed to the specimen fixing jig 130 by a predetermined load in a manner to fix the position of the rod 142 while the cable 143 The cable fixing part 150 is installed to release the rod 142 so that the fall of the rod 142 may be performed.
먼저, 상기 지지대(120) 위에 시편 고정 지그(130)가 설치되는 바, 이 시편 고정 지그(130)는 고무시편(101)을 고정하는 역할을 한다.First, the specimen fixing jig 130 is installed on the support 120, the specimen fixing jig 130 serves to fix the rubber specimen (101).
첨부한 도 4a는 시편 고정 지그의 정면도이고, 도 4b는 시편 고정 지그의 평면도이며, 도 4c는 시편 고정 지그의 측면도로서, 시편 고정 지그(130)는 지지대(120) 일측 끝부분에 고정 설치되며, 지지대(120) 위에 고정 설치되는 시편 받침대(131)와, 이 시편 받침대(131) 상면과의 사이에 넣어진 고무시편(101) 일부분을 상측에서 압착 고정하게 되는 지그 블록(132)과, 이 지그 블록(132)을 고무시편(101)의 압착상태에서 상기 시편 받침대(131) 상면에 고정하기 위한 고정수단을 포함하여 이루어진다.4A is a front view of the specimen fixing jig, FIG. 4B is a plan view of the specimen fixing jig, and FIG. 4C is a side view of the specimen fixing jig, and the specimen fixing jig 130 is fixedly installed at one end of the support 120. , A jig block 132 to squeeze and fix a portion of the rubber specimen 101 sandwiched between the specimen support 131 fixed to the support 120 and the upper surface of the specimen support 131, and It comprises a fixing means for fixing the jig block 132 to the upper surface of the specimen pedestal 131 in the compressed state of the rubber specimen (101).
또한, 상기 지그 블록(132)의 하면에는 고무시편(101) 일부분이 넣어져 압착될 수 있도록 된 다수개의 장착홈(132a)이 배열 형성되어 있으며, 이 지그 블록(132)을 시편 받침대(131) 위에 고정하기 위한 고정수단으로서 지그 블록(132)의 양 단부에는 각각 다수개의 볼트(133)가 지그 블록(132)의 각 체결홀(132b)을 통해 삽입되어 시편 받침대(131) 상면의 해당 체결홀(131a)에 체결되어진다.In addition, a plurality of mounting grooves 132a are formed on the bottom surface of the jig block 132 so that a portion of the rubber specimen 101 may be inserted and compressed, and the jig block 132 may be mounted on the specimen pedestal 131. A plurality of bolts 133 are inserted through the respective fastening holes 132b of the jig block 132, respectively, at both ends of the jig block 132 as fastening means for fixing thereon, and corresponding fastening holes on the upper surface of the specimen pedestal 131. It is fastened to 131a.
결국, 도 4b에서와 같이, 고무시편(101)은 그 일부분이 지그 블록(132)의 장착홈(132a) 내에 넣어진 상태에서 지그 블록(132)이 볼트(133)에 의해 지지대(120)에 체결됨으로써 지그 블록(132)의 압착에 의해 시편 받침대(131) 위에 완전 고정되어진다.As a result, as shown in FIG. 4B, the rubber specimen 101 has a portion of the jig block 132 attached to the support 120 by the bolt 133 in a state where a part thereof is inserted into the mounting groove 132a of the jig block 132. By fastening, the jig block 132 is completely fixed to the specimen support 131 by pressing.
이 상태에서 상기 고무시편(101)의 나머지 부분이 후술하는 로드(142)의 낙하경로상에 위치되도록, 즉 타격장치부(140)의 가이드 레일(141) 안쪽 공간에 돌출 위치되도록 시편 고정 지그(130)의 위치가 설정되어 있다.In this state, the rest of the rubber specimen 101 is positioned on the falling path of the rod 142 which will be described later, that is, the specimen fixing jig (to protrude in the space inside the guide rail 141 of the striking device 140) 130) is set.
한편, 상기 타격장치부(140)는 케이블(143)에 매달린 로드(142)가 가이드 레일(141)을 따라 수직 낙하하여 상기 지그 블록(132)에 고정된 고무시편(101)을 타격하는 구조로 되어 있으며, 상기 가이드 레일(141)의 하단에는 충격흡수용 재질의 스토퍼(145)가 설치된다.On the other hand, the striking unit 140 has a structure in which the rod 142 suspended on the cable 143 vertically falls along the guide rail 141 to strike the rubber specimen 101 fixed to the jig block 132 The stopper 145 of the shock absorbing material is installed at a lower end of the guide rail 141.
좀 더 상세하게는, 지지대(120) 측방으로 로드(142)를 상하 안내하기 위한 가이드 레일(141)이 수직으로 설치되는 바, 이 가이드 레일(141)은 자유 낙하하게 되는 로드(142)를 안내하게 된다.More specifically, the guide rail 141 for vertically guiding the rod 142 to the side of the support 120 is installed vertically, and the guide rail 141 guides the rod 142 to be free-falled. Done.
상기 로드(142)의 상부면으로 케이블(143) 일단을 걸어 고정하도록 되어 있으며, 이 케이블(143)은 각각 가이드 레일(141) 상단과 지지대(120)쪽으로 고정된 두 개의 고정 도르레(144a,144b)에 의해 안내되어 후술하는 케이블 고정부(150)를 지나도록 되어 있는 바, 이 케이블 고정부(150)를 지난 케이블(143)의 반대쪽 타단에는 손잡이(143a)가 설치된다.One end of the cable 143 is fixed to the upper surface of the rod 142 by the two fixing pulleys 144a and 144b fixed to the top of the guide rail 141 and the support 120, respectively. It is guided by a) to pass through the cable fixing part 150 which will be described later, the handle 143a is installed on the other end of the cable 143 past the cable fixing part 150.
상기 손잡이(143a)는 로드(142)를 들어 올릴 때 시험자가 케이블(143)을 안전하게 당길 수 있도록 구비되는 것이며, 상기 케이블(143)은 일단에 연결된 로드(142)를 상하로 움직이게 하는 역할을 한다.The handle 143a is provided to allow the tester to safely pull the cable 143 when lifting the rod 142, and the cable 143 serves to move the rod 142 connected to one end up and down. .
또한, 상기 로드(142)로서, 1kg ~ 10kg까지 다양한 중량의 로드 다수개가 구비되는 바, 요구되는 타격 하중에 맞게 적절한 로드를 선택하여 케이블(143)에 걸어주도록 되어 있다.In addition, as the rod 142, a plurality of rods of various weights up to 1kg ~ 10kg is provided, so as to select the appropriate rod according to the required impact load to hang on the cable 143.
또한, 상기 가이드 레일(141) 하단에는 로드(142)가 최하단까지 낙하시에 충격을 흡수하게 되는 스토퍼(145)가 설치되며, 이는 충격 흡수를 통해 타격장치부(140)를 보호하는 역할을 하게 된다. In addition, a stopper 145 is installed at the lower end of the guide rail 141 to absorb the shock when the rod 142 falls to the bottom end, which serves to protect the striking unit 140 through shock absorption. do.
한편, 상기 타격장치부(140)의 케이블(143)은 로드(142)가 들어 올려진 상태에서 케이블 고정부(150)에 의해 고정되도록 되어 있는 바, 시험자는 로드(142)가 가이드 레일(141) 상단까지 들어 올려지도록 케이블(143)을 당긴 후 이 케이블 고정부(150)를 이용해 고정하도록 되어 있다.On the other hand, the cable 143 of the striking device unit 140 is to be fixed by the cable fixing unit 150 in the state in which the rod 142 is lifted, the tester rod 142 is a guide rail 141 The cable 143 is pulled to be lifted up to the top, and then fixed using the cable fixing part 150.
이하, 첨부한 도면을 참조하여 케이블 고정부에 대해 보다 상세히 설명하면 다음과 같다.Hereinafter, the cable fixing unit will be described in more detail with reference to the accompanying drawings.
첨부한 도 5는 본 발명의 평가장치에서 케이블 고정부를 도시한 정면도이고, 도 6은 도 5의 선 'A-A'를 따라 취한 단면도이다.5 is a front view showing the cable fixing part in the evaluation apparatus of the present invention, Figure 6 is a cross-sectional view taken along the line 'A-A' of FIG.
또한, 도 7은 본 발명의 평가장치에서 록킹레버의 록킹해제작동을 위한 록킹수단 내 구성의 예를 보여주는 도면이고, 도 8은 본 발명의 평가장치에서 케이블 고정부의 작동상태도이다. In addition, Figure 7 is a view showing an example of the configuration within the locking means for the unlocking operation of the locking lever in the evaluation device of the present invention, Figure 8 is an operating state diagram of the cable fixing part in the evaluation device of the present invention.
상기 케이블 고정부(150)는, 지지대(120) 위에 고정 설치되어 상기 케이블(143)이 상면 위로 통과하도록 된 케이블 받침대(151)와, 지지대(120) 위에 고정 설치되는 본체(152)와, 이 본체(152)의 장착홀(152a) 내에서 스프링(154)에 지지된 상태로 승강동작 및 탄성 상방 이동이 가능하면서 상단 누름조작이 가능하도록 설치되고 누름조작된 상태에서 하단 끝부분이 상기 케이블 받침대(151) 위 케이블(143)을 눌러주어 위치 고정시키는 푸싱로드(153)와, 이 푸싱로드(153)를 누름조작된 상태로 고정 또는 해제하기 위한 록킹수단(155)을 포함하여 이루어진다.The cable fixing part 150 is fixed to the support 120, the cable support 151 to allow the cable 143 to pass over the upper surface, and the main body 152 is fixed to the support 120, and The cable support is installed in the mounting hole 152a of the main body 152 so that the lifting operation and the elastic upward movement are possible while the upper pressing operation is performed and the pressing operation is performed. And a pushing rod 153 for pressing the cable 143 to fix the position, and a locking means 155 for fixing or releasing the pushing rod 153 in a pressed operation.
상기 푸싱로드(153)는 본체(152)의 장착홀(152a) 내에서 스프링(154)에 의해 탄성 지지되어 있으며, 일측면으로는 상기 록킹수단(155)에 의해 록킹이 이루어지는 걸림돌기(153a)가 돌출 형성된 구조로 되어 있다.The pushing rod 153 is elastically supported by the spring 154 in the mounting hole 152a of the main body 152, and the locking protrusion 153a locks by the locking means 155 on one side thereof. Has a protruding structure.
상기 스프링(154)은 푸싱로드(153)의 측면에 형성된 돌기(153b)와 본체(152)의 장착홀(152a) 내면상의 돌출턱(152b) 사이에 설치되며, 상기 푸싱로드(153)가 이 스프링(154) 안쪽으로 삽입된 상태에서 탄성 지지되는 구조로 되어 있는 바, 상단이 아래로 눌러짐과 동시에 하방 이동하는 푸싱로드(153)에 의해 상기 스프링(154)이 압축되고, 상기 록킹수단(155)의 록킹이 해제된 상태에서 압축상태인 스프링(154)의 복원력에 의해 푸싱로드(153)가 위로 복원되도록 되어 있다. The spring 154 is installed between the protrusion 153b formed on the side of the pushing rod 153 and the protruding jaw 152b on the inner surface of the mounting hole 152a of the main body 152. The spring 154 has a structure that is elastically supported in the state of being inserted into the spring 154, the spring 154 is compressed by the pushing rod 153 is moved downward while the upper end is pressed down, the locking means ( The pushing rod 153 is restored upward by the restoring force of the spring 154 which is in a compressed state while the locking of the 155 is released.
상기 록킹수단(155)은 본체(152) 일측에 장착되는 것으로, 푸싱로드(153)를 아래로 눌러진 상태에서 록킹하기 위하여 구비되며, 상기 본체(152)의 장착홀(152a) 내로 탄성 돌출 또는 삽입동작이 가능하도록 설치되는 록킹레버(156)를 가진다.The locking means 155 is mounted on one side of the main body 152 and is provided to lock the pushing rod 153 in a down state, and elastically protrudes into the mounting hole 152a of the main body 152. It has a locking lever 156 that is installed to enable the insertion operation.
상기 푸싱로드(153)는 상단의 누름조작에 의해 하방 이동된 후 자동 록킹이 이루어지도록 되어 있는 바, 상기 록킹레버(156)가 튀어나와 푸싱로드(153)의 걸림돌기(153a)에 걸리어 푸싱로드(153)가 록킹되도록 되어 있고, 이 상태에서 푸싱로드(153)의 상방 이동이 구속되도록 되어 있다.The pushing rod 153 is moved downward by the push operation of the upper bar to automatically lock the bar. The locking lever 156 is protruded and caught by the locking protrusion 153a of the pushing rod 153 to push. The rod 153 is locked, and the upward movement of the pushing rod 153 is restrained in this state.
또한, 이와 같이 록킹상태에서 푸싱로드(153)의 하단이 케이블(143)을 강하게 눌러주는 바, 이에 케이블(143)의 이동이 구속되어지며, 이와 같이 케이블(143)의 위치가 고정된 상태에서는 로드(142)의 상하 위치 또한 고정된 상태가 된다.In addition, the lower end of the pushing rod 153 pushes the cable 143 strongly in the locking state as described above, and thus the movement of the cable 143 is constrained, and thus the position of the cable 143 is fixed. The up-down position of the rod 142 is also fixed.
또한, 상기 록킹레버(156)가 삽입동작하게 되면 록킹레버(156)에 의해 걸려 있던 푸싱로드(153)가 스프링(154)의 탄성복원력에 의해 상방 이동하게 되며, 이때 케이블(143)의 구속이 해제되면서 로드(142)가 수직 낙하하게 된다.In addition, when the locking lever 156 is inserted, the pushing rod 153 held by the locking lever 156 is moved upward by the elastic restoring force of the spring 154, and the restraint of the cable 143 is The rod 142 falls vertically while being released.
바람직하게는, 상기 록킹수단(155)은 시간 조절이 가능한 타이머 기능을 내장하여 설정 시간 후 자동으로 케이블 고정을 해제하여 로드(142)에 의한 시편 타격이 이루어지도록, 즉 설정 시간 후 상기 록킹레버(156)가 자동 삽입동작하도록 구성된다.Preferably, the locking means 155 has a built-in timer function that can adjust the time to automatically release the cable fixed after the set time so that the strike of the specimen by the rod 142 is made, that is, the locking lever after the set time ( 156 is configured to perform an automatic insertion operation.
이러한 구성의 예로서, 타이머 조작부(157)를 시험자가 원하는 시간에 맞춰 놓게 되면, 설정 시간 이후에 타이머(158a)가 내장된 컨트롤러(158)가 릴레이(159a)를 온(on) 동작시키고, 이 릴레이(159a)의 온 동작에 의해 코일(159b)이 전원을 인가 받게 되면서 후방 스프링(156a)에 의해 탄성 지지된 록킹레버(156)가 스프링력을 극복하고 안쪽으로 당겨져 순간 자동 삽입동작(푸싱로드의 록킹이 해제됨)하게 되는 구성으로 실시 가능하다.As an example of such a configuration, when the tester puts the timer control unit 157 at a desired time, the controller 158 with the timer 158a built in turns on the relay 159a after the set time. As the coil 159b is powered by the on operation of the relay 159a, the locking lever 156 elastically supported by the rear spring 156a overcomes the spring force and is pulled inward to instantaneous automatic insertion operation (pushing rod). Can be unlocked).
이하, 본 발명의 평가장치를 이용하여 고무시편의 저온성능을 평가하는 과정을 설명하면 다음과 같다.Hereinafter, the process of evaluating the low temperature performance of the rubber specimen using the evaluation apparatus of the present invention will be described.
먼저, 저온 챔버(110) 내 분위기 온도를 - 40℃로 낮춘다.First, the ambient temperature in the low temperature chamber 110 is lowered to -40 ° C.
이후, 시험자가 저온 챔버(110) 내에 들어가 케이블(143)에 2kg의 로드(142)를 걸어 주고, 손잡이(143a)를 통해 케이블(143)을 당겨 로드(142)를 가이드 레일(141) 상단 위치까지 끌어 올린 후 케이블 고정부(150)를 이용하여 케이블(143)을 고정한다.Thereafter, the tester enters the low temperature chamber 110 to hang the 2kg rod 142 on the cable 143 and pull the cable 143 through the handle 143a to move the rod 142 to the upper position of the guide rail 141. After pulling up to fix the cable 143 using the cable fixing part 150.
이때, 케이블 고정부(150)에서는 푸싱로드(153)가 아래로 눌러지면서 스프링(154)을 압축함과 동시에 푸싱로드(153)의 하단이 케이블(143)을 강하게 눌러주게 되고, 이때 록킹레버(156)가 푸싱로드(153)의 걸림돌기(153a)에 걸린 상태로 록킹이 이루어지면서 케이블(143) 위치 및 로드(142) 위치가 모두 고정되어진다.At this time, in the cable fixing part 150 while pressing the pushing rod 153 is pressed down the spring 154 and at the same time the lower end of the pushing rod 153 is pressed strongly on the cable 143, at this time the locking lever ( As the locking is performed in a state where the 156 is locked to the locking protrusion 153a of the pushing rod 153, both the position of the cable 143 and the position of the rod 142 are fixed.
이후, 두께 2mm, 폭 5mm, 길이 50mm의 고무 시편 5개를 시편 고정 지그(130)에 장착한다.Thereafter, five rubber specimens having a thickness of 2 mm, a width of 5 mm, and a length of 50 mm are mounted on the specimen fixing jig 130.
그리고, 고무시편의 공기 중 수킹(soaking) 시간에 맞추어 타이머의 시간 설정을 하고, 저온 챔버(110)에서 나와 문을 닫는다.Then, the timer is set according to the soaking time in the air of the rubber specimen, and the door exits from the low temperature chamber 110.
시간이 경과되면, 케이블 고정부(150)는 자동으로 케이블(143)을 놓게 되며, 동시에 로드(142)가 중력에 의해 수직 낙하하면서 고무시편(101)을 타격하게 된다.As time passes, the cable fixing part 150 automatically releases the cable 143, and at the same time, the rod 142 strikes the rubber specimen 101 while vertically falling down due to gravity.
이때, 케이블 고정부(150)에서는 타이머 작동에 의해 록킹레버(156)가 자동으로 삽입동작하게 되고, 결국 록킹레버(156)에 의한 록킹이 해제되면서 푸싱로드(153)는 스프링(154)의 탄성복원력에 의해 상방 이동하는 바, 케이블(143) 고정이 해제되어진다.At this time, the locking lever 156 is automatically inserted into the cable fixing part 150 by the timer operation. As a result, the locking rod 156 is released and the pushing rod 153 is elastic to the spring 154. When the cable 143 is moved upward by the restoring force, the fixing of the cable 143 is released.
이와 같이 하여, 시험 종료 후 시편을 꺼내서 크랙 및 파단 유무를 확인하게 된다.In this way, after completion of the test, the specimen is taken out to check for cracks and breakage.
첨부한 도 9는 본 발명의 평가장치에 의한 시험 종료 후 시편상태를 보여주는 사진으로서, 크랙 및 파단 발생된 불합격 시편을 정상의 합격 판정된 시편과 함께 보여주고 있다.9 is a photograph showing the state of the specimen after the end of the test by the evaluation apparatus of the present invention, showing the cracks and fractures failing specimens together with the normal pass-tested specimens.
이상에서 설명한 바와 같이, 본 발명에 따른 자동차용 연질가류고무의 저온성능 평가장치에 의하면 다음과 같은 장점이 있다.As described above, according to the low-temperature performance evaluation apparatus for soft vulcanized rubber for automobiles according to the present invention has the following advantages.
1) 상온이 아닌 저온 분위기 상태에서 평가가 가능하기 때문에 신뢰도 높은 데이터를 얻을 수 있다.1) Reliable data can be obtained because it can be evaluated in a low-temperature atmosphere, not at room temperature.
2) 인체에 유해하고 화재 위험성이 있는 메탄올을 사용하지 않아도 되므로 시험시 안전성을 보장할 수 있다.2) The safety of the test can be guaranteed since it is not necessary to use methanol, which is harmful to humans and poses a fire hazard.
3) 드라이아이스를 사용하지 않기 때문에 시험 비용을 줄일 수 있다.3) The test cost can be reduced because dry ice is not used.
4) 시험실에서 연질가류고무의 저온성능을 미리 예측할 수 있기 때문에 실차 시험시의 시간과 비용을 줄일 수 있어 신차 개발 시간을 단축할 수 있고, 신차 개발 확인 평가시 효율적인 시험 관리가 가능하므로 보다 신속하고 안정화된 제품 개발에 효과적이다. 4) Since the low-temperature performance of soft vulcanized rubber can be predicted in advance in the laboratory, the time and cost of actual vehicle testing can be reduced, which can shorten the development time of new cars and enable efficient test management when evaluating new vehicle development. Effective for the development of stabilized products.
5) 저온 챔버에 의해 온도 유지가 이루어지므로 시험과정이 간단해진다.5) The test process is simplified because the temperature is maintained by the low temperature chamber.
도 1은 종래의 저온취하시험기를 도시한 사시도,1 is a perspective view showing a conventional low temperature withdrawal tester,
도 2는 종래의 저온취하시험기에서 항온조 내부를 도시한 단면도,Figure 2 is a cross-sectional view showing the inside of the thermostat in a conventional cold withdrawal tester,
도 3은 본 발명에 따른 저온성능 평가장치의 구성도,3 is a block diagram of a low temperature performance evaluation apparatus according to the present invention,
도 4a와 도 4b, 도 4c는 본 발명의 평가장치에서 각각 시편 고정 지그를 도시한 정면도와 평면도, 측면도,4a, 4b, 4c is a front view, a plan view, a side view showing a specimen fixing jig in the evaluation apparatus of the present invention, respectively;
도 5는 본 발명의 평가장치에서 케이블 고정부를 도시한 정면도,5 is a front view showing the cable fixing part in the evaluation apparatus of the present invention,
도 6은 도 5의 선 'A-A'를 따라 취한 단면도,6 is a cross-sectional view taken along the line 'A-A' of FIG. 5,
도 7은 본 발명의 평가장치에서 록킹레버의 록킹해제작동을 위한 록킹수단 내 구성의 예를 보여주는 도면,7 is a view showing an example of the configuration within the locking means for the unlocking operation of the locking lever in the evaluation apparatus of the present invention,
도 8은 본 발명의 평가장치에서 케이블 고정부의 작동상태도, 8 is an operation state of the cable fixing part in the evaluation apparatus of the present invention,
도 9는 본 발명의 평가장치에 의한 시험 종료 후 시편상태를 보여주는 사진.Figure 9 is a photograph showing the state of the specimen after the end of the test by the evaluation apparatus of the present invention.
<도면의 주요 부분에 대한 부호의 설명><Explanation of symbols for the main parts of the drawings>
100 : 평가장치 101 : 고무시편100: evaluation apparatus 101: rubber specimen
110 : 저온 챔버 120 : 지지대110: low temperature chamber 120: support
130 : 시편 고정 지그 140 : 타격장치부130: specimen fixing jig 140: impact device
150 : 케이블 고정부150: cable fixing part
Claims (8)