KR20050087949A - Method to improve the quality of water using porous concrete and construction used in the method - Google Patents

Abstract

In the present invention is installed on the embankment, the treated water is introduced, porous concrete, vegetation planting plants in porous concrete or porous concrete or permeable filter made of the porous concrete and the vegetation concrete; And a storage tank installed on one side of the basement region of the river in which the treated water passing through the permeable filter medium installed on the bank surface is stored. And a stream reservoir for flowing out the treated water discharged from the storage tank; and a structure for improving the water quality using porous concrete, and further, the treated water to be treated is installed on the banks of the porous concrete and the porous concrete. Passing the plant through a permeable filter comprising vegetation concrete or the porous concrete and the vegetation concrete planted (S1); Storing the treated water passing through the permeable filter medium in a storage tank installed at an underground side of the blunt region (S2); And discharging the treated water stored in the storage tank to the river reservoir (S3). The method of improving water quality using porous concrete is disclosed. According to the water quality improvement method using the porous concrete of the present invention and its structure, water quality improvement can be efficiently achieved, and furthermore, it is possible to install high-quality flow rate in areas where water flow is difficult to secure especially when water is recycled by reusing and recycling sewage into rivers. Since it can be stably secured, it is possible to solve the problem of lack of flow rate and water pollution caused by drying. In addition, by efficiently using the bank's bank slope, blunt space, and drainage ditches, etc., there is no difficulty in selecting the site for the construction of the structure, and it is suitable in terms of cost. Also suitable for.

Description

Method to improve the quality of water using porous concrete and construction used in the method}

The present invention relates to a method for improving water quality using porous concrete, and a structure thereof. Specifically, a predetermined permeable filter medium is made of porous concrete or vegetation concrete prepared by planting plants therein, and in particular, a bank slope and // Or by installing on the shore of the lake to improve the water quality, and furthermore, by using the storage tank established in the basement of the Dunchi at the same time, it is possible to adequately utilize the rainwater and sewage at the time of galcheon to secure enough river maintenance flow The present invention relates to a method for improving water quality using porous concrete and a structure thereof that can be prevented.

In the present invention, the treated water means the target water to be treated, such as sewage, sewage, wastewater or rainwater.

In the present invention, the stream maintenance flow rate means a flow rate necessary to maintain the normal function and state of the river at a major point in river maintenance.

Recently, environmental pollution caused by industrial development and rapid urbanization has emerged as a social problem. Accordingly, efforts for water quality recovery in public waters are increasing. However, a large amount of sewage, sewage, and wastewater, such as domestic wastewater, factory wastewater, and industrial wastewater, are discharged into public waters, which is a major cause of pollution of rivers and lakes.

Therefore, it is necessary to develop water quality improvement media to efficiently apply water quality to rivers.

On the other hand, industrial development, green land development, asphalting, etc., result in an increase in the impermeable layer area, which causes a decrease in the amount of water supplemented by the existing groundwater in terms of hydrology. Therefore, when a rainfall event occurs, all the flow rates of the streams are discharged within a short period of time, and in a period when there is no rain, the amount of groundwater is insufficient and the river is depleted.

Such a lack of river maintenance flow due to the drying of the small rivers causes a lack of agricultural water and industrial water in various agricultural lands, including rivers, and also increases the water pollution, making it difficult to efficiently use the river water. And the secondary cost increase resulting from this causes a lot of economic losses and negatively affects the hydrophilic function, which is recently gaining attention.

Therefore, it is necessary to improve the quality of the water and prevent the dryness of the stream. Conventionally, in order to prevent the dryness of the stream, discharge through simple transport, discharge through wetlands, discharge through an oxidative storage tank, discharge through infiltration, etc. Was used.

First, the discharge through the simple transfer is easy to maintain because the system is simple by distilling the sewage treatment water from the sewage treatment plant through the pipe to the upstream part and discharged to the stream. Has the disadvantage that water quality is directly affected by treatment efficiency of sewage treatment plant.

Next, the discharge through the wetland is a method of improving the water quality of the sewage treatment water once again through natural or artificial wetland after the sewage treatment water upstream. The water quality improvement effect is estimated to be 1-34% for T-N and 60-75% for T-P. This method is eco-friendly and thus ecosystem recovery is possible. However, large areas are required for the construction of wetlands, and there are problems due to pest habitat such as mosquitoes in summer.

Next, the discharge through the oxidizing storage tank passes the underground storage facility and the oxidation treatment tank in the middle part where the sewage treatment water flows upstream, thereby improving the water quality of the sewage treatment water and discharging it to the stream. The same water quality can be improved. The water quality improvement effect is estimated to be 20% T-N and 24% T-P. However, this method has the disadvantage that it is difficult to control the flow rate when it is discharged to the river as the storage facility and the oxidation treatment tank are constructed in the upstream water, and it is difficult to supply the flow rate when a problem occurs in the system.

Next, the discharge through the infiltration is to discharge the treated water treated and treated at the sewage treatment plant directly into the stream, and to discharge the treated water through the soil to the groundwater or the river. It has the effect of improving. However, there are disadvantages in that soil maintenance is difficult and discharge control is difficult.

Therefore, the present invention has been made to solve the above problems,

An object of the present invention is to increase the efficiency of the water quality improvement by appropriately using the vegetation concrete planted in the porous concrete or porous concrete, and further, to prevent the drying of the stream as the water quality improvement system, The present invention provides a method for improving water quality using porous concrete and its structure, which is easy in supply and control, low site cost, and low installation and maintenance cost, and is economically superior.

An object of the present invention as described above, installed on the banks, the treated water flows in, porous concrete, vegetational concrete planting plants in the porous concrete or permeable media made of the porous concrete and the vegetation concrete; And a storage tank installed on one side of the basement region of the river in which the treated water passing through the permeable filter medium installed on the bank surface is stored. And it is achieved by the structure for improving the water quality using porous concrete, characterized in that it comprises a; and a river reservoir to the treated water discharged from the reservoir.

In addition, the river reservoir, in which the treated water passes, the porous concrete, vegetation concrete planted in the porous concrete, or a permeable filter made of the porous concrete and the vegetation concrete; It is preferable that the structure further comprises a discharge pipe embedded in the basement of the blunt area for discharging the treated water from the storage tank to the river reservoir.

The structure may further include a storage tank for storing the treated water to be treated and discharging the stored treated water to a permeable filter medium installed on the bank surface, wherein the structure includes sewage from the sewage source. It is preferable to further include a; sewage water pipe to be transferred to the reservoir.

It is also an object of the present invention, the step of passing the treated water to be treated in the vegetation concrete planted in the porous concrete, porous concrete, or the permeable filter made of the porous concrete and the vegetation concrete is installed on the bank surface (S1) ); Storing the treated water passing through the permeable filter medium in a storage tank installed at an underground side of the blunt region (S2); And discharging the treated water stored in the storage tank to the river reservoir (S3). It is achieved by the water quality improvement method using porous concrete, characterized in that it comprises a.

And, the step S3, the step of passing the permeable media consisting of the vegetation concrete or the porous concrete and the vegetation concrete planted in the porous concrete, porous concrete, installed in the lake before the treated water is discharged to the river reservoir ( S3-1); It is preferable to further include, and the step S1, it is preferable to provide to the water-permeable medium as the treated water to treat the sewage collected from the sewage source.

Hereinafter, a method for improving water quality using porous concrete and a structure thereof according to the present invention will be described in detail.

The water quality improvement method using the porous concrete and the structure thereof according to the present invention, the permeable media consisting of porous concrete and / or vegetation concrete for the purification of sewage, sewage, wastewater, rainwater, etc. By improving the efficiency of the water quality, and further, through the storage tank installed in the basement area of the river, the sewage and the like is stored and discharged to the reservoir of the stream, at this time, by maintaining the stream by adjusting the discharge amount The flow rate can be easily secured to prevent dryness of the river, and when the sewage light is introduced, the sewage light in the storage tank naturally flows into the permeable media, thereby eliminating a separate complicated facility for tap water. Required to improve water quality and prevent dryness by using bank slopes, blunt underground spaces and / or lakes It is based on the technical idea of minimizing the costs and other maintenance costs required to select and secure the site.

First, the water quality improvement method using the porous concrete and the structure thereof according to the present invention will be described in detail.

1 is a schematic view showing a structure for improving water quality using porous concrete according to an embodiment of the present invention.

As shown in FIG. 1, a structure according to an exemplary embodiment of the present invention is largely in a structure having a riverbank slope area 10, a river blister area 20, and a river reservoir area 30. , Porous concrete, vegetation concrete planted in the porous concrete, porous concrete or the permeable filter (12) made of the porous concrete and the vegetation concrete installed on the bank surface 11, the treatment passed through the permeable filter (12) It includes a storage tank (23) installed in the basement underground space for storing water and the river reservoir (31) through which the treated water discharged from the storage tank (23) flows out, so as to the shore 33 of the river reservoir (31) It may further include a porous concrete, a vegetation concrete planted with a plant in the porous concrete or a permeable filter 32 made of the porous concrete and the vegetation concrete.

The permeable filter media 12 installed on the bank slope forms a primary slope contact tank for purification of sewage.

The porous concrete is concrete made by attaching a paste to coarse aggregate, and satisfies the continuous performance of no-fines concrete characteristics and the general performance and function of concrete, and also provides environmental harmony and comfort. Holds. In addition, porous concrete has excellent permeability and air permeability, and since the continuous void portion is used for the living space of living organisms, it is suitable for reducing environmental load since it can maintain harmony and symbiosis with the ecosystem.

When such porous concrete is applied to water quality improvement, as can be seen in the following examples, appropriate porosity and strength are required.

The vegetation concrete, which is based on the porous concrete, is based on the vegetation function and the basic mechanical properties of the concrete that plants can grow in the concrete.

In the case of vegetation concrete, four conditions such as light for living plants, space for growth, atmosphere, and soil are required. Therefore, in order to grow plants directly on concrete, it is necessary to give concrete the same function as soil. need.

In order to provide enough space for the seed of the plant to germinate or for the plant to take root and grow, there must be many voids in the concrete and continuous voids through which water can pass.

In addition, the soil generally contains moisture of a suitable pH (usually 5 to 8, high 9.5) for the growth of plants, but in the case of concrete exhibits strong alkalinity due to the hydrate produced by hydration of cement, In the production of vegetation concrete, the neutralization of the concrete must be accompanied.

In the present invention, even without neutralization treatment such as a separate acid treatment, as can be seen in the following examples, alkali was easily removed by immersion in flowing water for about 4 hours or more.

The vegetation concrete includes porous soil, for example, surface soils, cultured soils as fillers, aggregates, nonwoven fabrics, soils, and the like, and herbaceous concrete is mainly used for herbaceous plants such as grass, strips, crova, cosmos, and chaehwa.

The storage tank 23 stores the treated water passed through the water-permeable filter media 12 installed on the bank surface, and the water-permeable filter media installed in the reservoir 31 or the revet 33 as described below. It is useful to discharge the treated water stored in 32) by allowing the underground space to be used if it is buried underground on one side of the river basin area.

In the discharge, the discharge pipe 24 is used, and the discharge pipe 24 is also buried underground in the blunt area 20.

Like the permeable media 12 installed on the banks, the permeable media 32 installed on the bank 33, the porous concrete, the vegetation concrete planted in the porous concrete or the porous concrete and the vegetation concrete The secondary slope contact tank is formed in the revet 33.

In addition, in the case of the permeable filter medium used for the embankment 11 or the revetment 12, in particular, in order to normalize the operation of the structure early, the permeable filter medium is first immersed in the river for a predetermined time, and the It can be used after the adhesion film is formed.

In order to ensure the maintenance flow rate, in particular when using the sewage may be further provided with a conduit pipe 46 for watering the sewage from the sewage source 45, as described above, the sewage received by the water pipe 46 is on the bank surface (11) Before being supplied to the primary slope contact tank having the permeable media 12 installed therein, it may be temporarily stored in the reservoir 47 of the treated water.

Next, a water quality improvement method using porous concrete according to the present invention will be described in detail.

In the water quality improvement method using porous concrete according to the present invention, the sewage or the like is temporarily stored in a storage tank as treated water through a tap or direct inflow method, and then the treated water is discharged by a natural dripping method. Installed in the), to pass through the porous concrete, vegetation concrete planted in the porous concrete or the permeable filter media 12 made of the porous concrete and the vegetation concrete (S1),

Such a water permeable filter 12 is used as a filter paper, it is possible to achieve an improvement in water quality, especially when using sewage.

In particular, when the sewage is introduced into the reservoir and stored as treated water, for example, the final discharge water treated in the sewage source 45 such as a sewage treatment plant is used as a water pipe 46 by using a metering pump upstream of the embankment 11. After passing through and temporarily storing it in the sewage storage tank 47, it naturally flows down for a predetermined time and passes through the permeable filter media 12 installed on the embankment 11.

The treated water processed through the first permeable filter 12 is stored in the storage tank 23 embedded in the basement region 20 (S2).

After being stored in the storage tank 23, by controlling the discharge of the stored treated water, it is possible to facilitate the supply and control of the flow rate flowing into the river. In this way, the treated water stored in the storage tank 23 is discharged in a state where the discharge is controlled, if necessary, the discharge is made through the discharge pipe 24 buried in the basement area (S3).

The discharge can be made directly to the reservoir 23 of the stream, particularly in the case of sewage, porous concrete, porous concrete, installed in the lake 33 before the treated water is discharged to the river reservoir 31 to further increase the purification rate. The secondary purification effect is achieved by passing the water-permeable filter material 32 made of vegetation concrete or the porous concrete and the vegetation concrete planted in a secondary manner (S3-1).

Such a method for improving water quality using the porous concrete and the structure according to the present invention can be applied in various sizes and shapes according to the shape of the blunt area of the river, embankment, reservoir, lake.

Hereinafter, the present invention will be described in more detail by explaining preferred embodiments of the present invention. However, the present invention is not limited to the following examples, and various forms of embodiments can be implemented within the scope of the appended claims, and the following examples are only common in the art while making the disclosure of the present invention complete. It is intended to facilitate the implementation of the invention to those with knowledge.

EXAMPLE

In this embodiment, a river has a bank surface area, a blunt area, a reservoir channel area, has permeable media 12 and 32 on the bank surface 11 and the lake 33, respectively, and has a storage tank in the basement of the blunt. The continuous flow reactor was produced.

2 is a photograph showing a continuous flow reactor prepared according to the present embodiment. As shown in FIG. 2, the continuous flow reaction tank in this embodiment corresponds to a lake provided with a first slope contact tank, a storage tank, and a permeable filter, corresponding to a bank of inflow water, an embankment in which a permeable filter is installed. A continuous flow reactor including a second slope contacting tank and a reservoir, having a length of 1 m 30 cm, a width of 50 cm, and a height of 58 cm (total capacity 90 l).

The continuous flow reactor was installed in the sewage treatment plant of Kyung Hee University in the same manner as the actual site conditions, and installed a roof through which sunlight could penetrate and eliminate artificial conditions such as rainfall.

The operation was performed for 10 days each, and the residence time was adjusted to 35 minutes.

The sample of the introduced sewage was introduced using a metering pump from the final sedimentation tank of the sewage treatment plant in Kyung Hee University, and the effluent was collected at a certain time every day from the time when the effluent was stabilized.

As the permeable filter media 12 and 32, porous concrete and vegetation concrete were used, and after immersion in the river for 12 days to normalize the operation of the continuous flow reactor, the adhesive film formed by the algae was used.

Figure 3 shows a porous concrete according to this embodiment, Figures 4a and 4b shows examples of vegetation concrete planted plants according to this embodiment.

The process of manufacturing the porous concrete and vegetation concrete based on the same is as follows.

In the case of porous concrete, the porosity formed by filling cement paste with respect to the total porosity (porosity of aggregate) formed by the aggregate itself was called theoretical porosity (porosity designed in the compound).

For the fabrication of porous concrete, we went through the aggregate measurement process, cement measurement process, compounding process, mold process, filling process, compaction process, and drying process. In other words, after measuring the aggregate and cement, the mixture was mixed with water, filled into a mold (20 × 10 × 5cm), compacted 30 times, and then subjected to standard wet curing until the measurement age (7 days). , As shown in FIG. 3, a porous concrete was prepared.

Table 1 shows the mixing ratio of the porous concrete according to the present embodiment.

Theoretical porosity (%)) W / C P / A W Unit volume (kg / m ³ ) Unit volume (kg / m ³ ) C A C A 30 25 12 32 43 625 135 1,588

W: water, P: paste, C: cement, A: aggregate

Cement was one kind of ordinary portland cement with a specific gravity of 3.15. The crushed stone had a specific gravity of 2.54 and an average size of 9 to 13 mm.

In the case of vegetation concrete, a suitable pH (usually 5-9, 9.5 if high) is needed to grow plants, so the yellow irises are removed after leaving the produced porous concrete in running tap water for 1 week to remove alkalis. A vegetation concrete was produced as shown in FIGS. 4A and 4B by laying porous concrete under a container of constant size and placing yellow irises on it so that the roots penetrated the porous concrete and the plants settled in the concrete.

In this example, the alkali dissolution (pH) characteristics of the compressive strength and the neutralization were measured for the purpose of evaluating the physical and chemical properties of the fabricated porous media and vegetation concrete.

First, the neutralization treatment effect was measured. In this embodiment, in order to determine the pH change according to the presence or absence of neutralization treatment in porous concrete, the neutralization treatment was performed by diluting 1N hydrochloric acid solution in tap water and the neutralization treatment. In the case of not having a total of two conditions, the hydrogen ion concentration (pH) was measured by the method of KS M 0011 over time after immersing porous concrete and flowing tap water.

5 is a graph showing the change in the concentration of hydrogen ions over time.

As shown in FIG. 5, the pH before the neutralization treatment was 12 or more, but after the neutralization treatment, the pH rapidly decreased to 8.25, and increased to around pH 9 with age, and the pH was stabilized to 7.0 after 28 hours. Appeared to be.

When the neutralization treatment was not performed, the pH decrease rate with time was slower than when the neutralization treatment was performed, but after 4 hours, the pH was close to the neutralization treatment, and after 28 hours, the pH was 7.5. appear. Therefore, even without the neutralization treatment it was found that there is no obstacle to the growth of plants and is suitable for actual river applications. On the other hand, when the neutralization treatment, it was found that the initial pH value can be significantly lowered.

Since a suitable pH for growing a plant is usually 5 to 8 or 9.5 when it is high, in this embodiment, irrespective of the neutralization treatment as described above, a certain time (especially 28 hours) in water flowing through the porous concrete If soaked during), the eluted alkali component is washed with water and the pH is lowered.

Then, the compressive strength was measured as follows.

The compressive strength of the prepared specimens was carried out by randomly extracting three pieces after 7 days of age. The 28-day strength was estimated using the age-specific compressive strength estimates specified in the concrete design criteria. Equation 1 below shows an estimate of 28-day compressive strength.

In Equation 1 , f ₂₈ represents the compressive strength of the 28-day design reference, and f _cu (t) represents the compressive strength at the t day.

And, β _cc (t) = exp [ β _SC (1- )], And β _SC represents three kinds of cement in the case of 0.2, one kind and five kinds of cement in the case of 0.25, and two kinds of cement in the case of 0.38.

Table 2 shows the porous concrete compressive strength results measured by the above formula.

Number Theoretical porosity (%) f _cu (7) (kgf / cm ² ) f ₂₈ (t) (kgf / cm ² ) One 30 179 218 2 165 202 3 159 194

As a result of measuring the 28-day compressive strength of the porous concrete, it showed a strength of 194 ~ 218 (average 205) kgf / ㎠. The above results show that it is above 180 kgf / cm 2, which is known as the lowest compressive strength level of structural concrete, and thus can be sufficiently used as a permeable media of the river in this embodiment.

Next, the purification efficiency of the media through the batch test was examined.

In order to investigate the efficiency of organic matter removal by porous concrete and vegetation concrete, two types of media are immersed in the stream, microorganisms are attached to the inside and outside of the concrete, and then transferred to the laboratory, and each of them is placed in a separately prepared batch reaction tank and batch tested. Was performed.

As the batch reaction tank, an acrylic reactor having an effective capacity of 5 L was used, and the initial DOC concentration of the influent was mixed by mixing tap water and Glucose while keeping the temperature and light constant in the culture room conditions (20 ° C, 8,000 to 10,000 Lux). / l and the total flow rate into the reactor was 4 liters.

Samples were collected and filtered at regular intervals, and DOC was measured to investigate the removal efficiency of organic matter according to the amount of microorganisms attached to the two media. In addition, in order to determine the removal efficiency of nitrogen and phosphorus according to the filter medium, the sample collected for a certain time was filtered, and then the measurement results according to the predetermined items and methods were analyzed.

Table 3 shows the analysis items and analysis methods.

Item Analytical Method NH ₄ -N Phenate method NO ₃ -N Ultraviolet Spectrophotometric Screening Method PO ₄ -P Ascorbic Acid Method DOC Total Organic Carbon Analyzer (SHIMADZU: TOC-5000A)

6 is a graph showing a change in concentration of organic matter (DOC) of the porous concrete and vegetation concrete according to the present embodiment, Figure 7 is a graph showing the removal efficiency of organic matter (DOC) of the porous concrete and vegetation concrete according to the present embodiment.

6 and 7, the average organic matter removal efficiency of the vegetation concrete was 75%, the total average organic matter removal efficiency of the porous concrete was 73% did not show a significant difference.

In addition, after 10 hours of vegetation concrete, organic matter concentration of 30 mg / L was 4.2 mg / L, which showed the highest removal efficiency of 86%. In the case of porous concrete, organic matter concentration was 5.6 mg / L after 12 hours, showing 81% removal efficiency, and relatively fast removal rate of vegetation concrete.

The organic removal efficiency measured in this way is an important factor in designing the natural treatment method, that is, it is used as an important factor in determining the residence time of the catalytic oxidation process using porous concrete and vegetation concrete.

8 is a graph showing the NH ₄ -N concentration change by the porous concrete and vegetation concrete according to the present embodiment, Figure 9 is a graph showing the NO ₃ -N concentration change by the porous concrete and vegetation concrete according to this embodiment 10 is a graph showing the PO ₄ -P concentration change by the porous concrete and vegetation concrete according to the present embodiment.

As shown in Figure 8, in the nitrogen and phosphorus removal efficiency, the removal efficiency of porous concrete at the NH ₄ -N concentration is 46% from 10.96 mg / l to 5.88 mg / l, the removal efficiency of vegetation concrete is 10.58 mg The removal efficiency of vegetation concrete was about 22%, which was 68% from 3.39 to 3.39 mg / ℓ.

In addition, the slope of the trend line was larger in vegetation concrete than in porous concrete, indicating that the removal efficiency of ammonia with time was high.

This is because ammonia nitrogen is easily ingested by plants and microorganisms, and microorganisms attached to plant roots decompose organic nitrogen.

As shown in FIG. 9, in the case of NO ₃ -N concentration, the removal efficiency of porous concrete is 97% from 2.65 mg / L to 0.08 mg / L, and the removal efficiency of vegetation concrete is 0.21 mg / L at 2.16 mg / L. In the case of porous concrete, removal efficiency was about 7% higher in the case of porous concrete.

This seems to be due to different absorption preferences of ammonia nitrogen and nitrate nitrogen depending on the plant species. In the case of vegetation concrete, NO ₃ -N concentration was initially decreased rapidly.

As shown in FIG. 10, in the case of PO ₄ -P concentration, the removal efficiency of porous concrete is 38% from 0.33 mg / L to 0.69 mg / L, and the removal efficiency of vegetation concrete is 0.36 mg / L from 0.62 mg / L. The removal efficiency was 42%.

As such, the removal efficiency by vegetation concrete was slightly higher than that of phosphorus, because plants generally absorb nitrogen faster than phosphorus.

Table 4 shows the measurement results after 24 hours. In Table 4 the units are mg / m ³ / day.

       Experiment Item Organic matter removal NH ₄ -N NO ₃ -N PO ₄ -P Porous concrete 3,850 847 428 40 Vegetation concrete 3,733 1,198 325 43

As can be seen from Table 4, the organic matter removal concentration per unit volume was investigated at 3,850 mg / m ³ / day for porous concrete and 3,733 mg / m ³ / day for vegetation concrete.

The removal concentration of NH ₄ -N was 847 mg / m ³ / day for porous concrete and 1,198 mg / m ³ / day for vegetation concrete. The removal concentration of NO ₃ -N was 428 mg / m ³ / day for porous concrete and 325 mg / m ³ / day for vegetation concrete. The removal concentration of PO ₄ -P was 40 mg / m ³ / day for porous concrete and 43 mg / m ³ / day for vegetation concrete.

From these results, it was confirmed that vegetation concrete showed NH ₄ -N removal ability remarkably superior to porous concrete, and similar or slightly lower in removal ability of other items. It was found to be an advantageous contact medium.

On the other hand, in the present embodiment, the water quality analysis when applied to the continuous flow reactor produced as described above was carried out, the water quality analysis was taken from the influent, the first slope contact tank, the second slope contact tank at a predetermined time, the predetermined analysis The experiment was carried out according to the item and the analysis method.

Table 5 shows the water quality analysis items and methods of this example.

Analysis item Analytical Method Temperature pH Meter (WTW 330) pH pH Meter (WTW 330) EC EC Meter (HANNA) DO Azide Modification SS Vacuum Filtration (Glass Fiber Filter, GF / C) BOD Azide Modification COD Closed Reflux, Titrimetric Method (Standard Method) T-N Ultraviolet Spectrophotometric Screening Method NH ₄ -N Phenate method NO ₂ -N Ultraviolet Spectrophotometric Screening Method NO ₃ -N Ultraviolet Spectrophotometric Screening Method T-P Ascorbic Acid Method PO ₄ -P Ascorbic Acid Method

On the other hand, Table 6 shows the properties of the influent irradiated during the operation period when the porous concrete is applied in this embodiment.

Item Inflow concentration range Average Temp (℃) 19.2-22.9 20.9 pH 7.7 to 8.3 7.95 EC (㎲ / cm) 778 to 817 803 DO (mg / L) 7.4 ~ 9.7 8.5 BOD (mg / L) 4.16 to 9.32 6.6 COD (mg / L)  8.8-10.8 9.8 SS (mg / L) 5.7 to 13 9.5 T-N (mg / L)  25.6 to 39 33 T-P (mg / L) 8 to 9 8.5

11 is a graph showing a change in pH during the operation of the reactor using the porous concrete of the present embodiment, Figure 12 is a graph showing a change in DO during the operation of the reactor using the porous concrete of the present embodiment, Figure 13 It is a graph which shows the change of the water temperature during the operation period of the reaction tank using the porous concrete of this Example, and FIG. 14 is the graph which shows the change of EC during the operation period of the reaction tank using the porous concrete of this Example.

As shown in Figure 11 to 14, when the porous concrete is applied, the average pH is influent 7.95 (8.25 ~ 7.73), the primary slope contact tank 8.33 (7.97 ~ 8.62), the secondary slope contact tank 8.55 (8.1 ~ 9.2 In case of DO, inflow average 8.5 (7.4 ~ 9.7) mg / L, primary slope contact tank average 9.1 (8.7 ~ 9.9) mg / L, secondary slope contact tank average 11 (8.9 ~ 15.4) mg / Appeared as L.

In the case of water temperature, the inflow water averaged 20.9 (19.2 ~ 22.9) ℃, the primary slope contact tank average 22.8 (20 ~ 26.9) ℃, the secondary slope contact tank average 22.4 (19.7 ~ 26.8) ℃ The average 803 (778 ~ 817) ㎲ / ㎝, the first slope contact tank average 798 (736 ~ 836) ㎲ / cm, the second slope contact tank average 806 (744 ~ 817) ㎲ / ㎝.

The DO and pH of the secondary slope contact tank were higher than the influent water, but the increase in pH caused the algae attached to the inside and outside of the concrete to perform photosynthetic activity during the experiment and consume CO ₂ in the water. This is because the consumption of algae is larger than the amount of CO ₂ introduced into the reactor.

Water is CO ₂ there is gradually reduced as the photosynthetic activity of the bird maximize, this CO ₂ loss form the alkalinity in the water HCO ₃ ^- in the CO ₃ ^2- and OH ^- and changes in the form and is a factor of raising the pH.

In addition, the cause of DO's synergistic effect is that aeration due to slope contact and photosynthetic activity due to photosynthetic microorganisms and adherent algae may have a significant effect.

Figure 15 is a graph showing the SS concentration change and removal efficiency when the porous concrete of the present embodiment is applied, Figure 16 is a graph showing the BOD concentration change and removal efficiency when the porous concrete of the present embodiment, Figure 17 is a view of this embodiment It is a graph showing the change in COD concentration and removal efficiency when applying the porous concrete, Figure 18 is a graph showing the change in TN concentration and removal efficiency when applying the porous concrete of the present embodiment, Figure 19 is a change in TP concentration and when applying the porous concrete of the present embodiment A graph showing removal efficiency.

As shown in Figure 15, first, in the case of SS concentration change and removal efficiency, influent average 9.5 (5.7 ~ 13) mg / L, primary slope contact tank average 5.6 (4.3 ~ 6.2) mg / L, secondary slope The average contact tank was 4.4 (2 ~ 5) mg / L, the removal rate was 38.6% and the total removal efficiency was 53% in the first slope contact tank. The removal efficiency of SS varies greatly with the influent SS concentration and other flow rates.

The reason why the porous concrete shows high SS treatment efficiency is that the specific surface area is larger than that of other contact media, and it has pores inside so that it can show the efficiency of floating material not only outside but also inside. see.

As shown in Figure 16, in the case of BOD concentration change and removal efficiency, the influent average 6.6 (4.16 ~ 9.32) mg / L, primary slope contact tank average 4.4 (3 ~ 5.9) mg / L, secondary slope contact tank 3.9 (2.8 ~ 4.9) mg / L on average, the removal rate in the first slope contact tank section was 33% on average and the removal rate in the entire section was about 40% on average. Porous concrete was laid to show a noticeable BOD reduction effect.

As shown in FIG. 17, in the case of the COD concentration change and the removal efficiency, the COD concentration was 9.8 (8.8-10.8) mg / L in the inflow average, 8.7 (7.6-10.4) mg / L in the primary slope contact tank, and the secondary The average slope contact tank was 7.8 (6.8 ~ 9.6) mg / L. The removal rate in the first slope contact tank section was about 11% on average and the removal rate in the entire section was about 20% on average.

In the case of porous concrete, it shows higher processing efficiency than other contact media. Because porous concrete has a larger specific surface area than other media and continuous pores are formed inside, various microorganisms live inside and various biomass Because it is formed. In addition, aerobic microorganisms are attached to the surface and anaerobic microorganisms are formed therein, indicating high organic matter (BOD, COD) treatment efficiency.

As shown in FIG. 18, in the case of the change in TN concentration and the removal efficiency, the TN concentration was 33 (25.6 to 39) mg / L of influent, 24.4 (22.2 to 27.2) mg / L of primary slope contact tank, and secondary. The average slope contact tank was 20.7 (17.5 ~ 24.9) mg / L, and the removal rate in the first slope contact tank section was about 24% on average and the removal rate in the entire section was about 37% on average.

In the case of using porous concrete, the biofilm is well formed in the media and the bioconversion rate is high, and the removal of nitrogen by the nitrification microorganism appears to be due to the aerobic microorganisms attached to the media and the anaerobic microorganisms attached to the media.

As shown in Figure 19, in the case of TP concentration change and removal efficiency, the TP concentration is 8.5 (8 ~ 9) mg / L on the influent average, 5.3 (4.1 ~ 6.7) mg / L on the first slope contact tank, secondary The average slope contact tank was 4.9 (3.2 ~ 5.8) mg / L, and the removal rate in the first slope contact tank section was about 38% on average and the removal rate in the entire section was about 42% on average.

Like TN TP there to show a good removal efficiency of 42%, which misaengmulche removal by conversion of an organic substance, which is a glass that is inorganic phosphate PO ₄ ^3- is glass containing Fe, Ca, Mg, etc. and cationic reactions on media It appears to be due to the properties of porous concrete that, at the same time, form a poorly soluble salt and a removal mechanism in which the salt can be adsorbed, absorbed and removed by the microbial membrane or media, can occur simultaneously.

In addition, in the present embodiment, in the case of vegetation concrete, the effect of water quality improvement under the residence time conditions such as porous concrete was examined, and the applicability of the vegetation concrete for water purification was evaluated.

Table 7 shows the influent characteristics when the vegetation concrete is applied in the present embodiment.

Item Inflow concentration range Average Temp (℃) 17.4-19.5 18.4 pH 7.2 to 7.8 7.6 EC (㎲ / cm) 783-817 807 DO (mg / L) 6.7 to 8.6 8 BOD (mg / L) 3.6 to 7.5 5.6 COD (mg / L) 8.8-10.4 9.3 SS (mg / L) 10.8 to 22 15 T-N (mg / L) 24.2 to 36.5 29.8 T-P (mg / L) 5.2 to 6.7 5.9

20 is a graph showing a change in pH during the operation of the reactor using the vegetation concrete of the present embodiment, Figure 21 is a graph showing a change in DO during the operation of the reactor using the vegetation concrete of the present embodiment, Figure 22 Fig. 23 is a graph showing the change in water temperature during the operation of the reactor using the vegetation concrete of this embodiment, Fig. 23 is a graph showing the change of EC during the operation of the reactor using the vegetation concrete of this embodiment.

As shown in Figure 20 to 23, when the vegetation concrete is applied, the pH is influent 7.6 (7.2 ~ 7.8), primary slope contact tank 7.7 (7.2 ~ 7.8), secondary slope contact tank 7.7 (7.4 ~ 8) In the case of DO, inflow average 7.99 (6.7 ~ 8.6) mg / L, primary slope contact tank average 7.79 (6.4 ~ 8.2) mg / L, secondary slope contact tank average 8.16 (7 ~ 8.6) mg / L.

In the case of water temperature, the inflow water average 18.4 (17.4 ~ 19.5) ℃, the first slope contact tank average 18.8 (16.9 ~ 19.5) ℃, the second slope contact tank average 18.4 (17.1 ~ 20.5) ℃ The water temperature was stable with almost no change.In the case of EC, inflow water averaged 807 (783 ~ 817) ㎲ / ㎝, average slope contact tank 804 (796 ~ 810) ㎲ / cm, secondary slope contact tank average 804 (792 to 812) dl / cm.

24 is a graph showing the SS concentration change and removal efficiency when the vegetation concrete of this embodiment is applied, Figure 25 is a graph showing the BOD concentration change and removal efficiency when applying the vegetation concrete of this embodiment, Figure 26 is a view of this embodiment COD concentration change and removal efficiency when applying vegetation concrete, Figure 27 is a graph showing the TN concentration change and removal efficiency when applying vegetation concrete of the present embodiment, Figure 28 is the TP concentration change and when applying vegetation concrete of this embodiment and A graph showing removal efficiency.

As shown in FIG. 24, in the case of SS concentration change and removal efficiency, the inflow average 15 (10.8 to 22) mg / L, the first slope contact tank average 9.5 (6.3 to 14, the secondary slope contact tank average 6.4 (4.3 ~ 9.8) mg / Lmg / L, total removal efficiency was 57.3% on average, and removal efficiency in primary slope contact tank was 36.4% on average.

In the case of applying vegetation concrete, the removal efficiency was increased about 5% than in the case of the application of porous concrete, which is caused by the filtration of solid matter in the root zone of aquatic plants and by the aquatic plants shading the surface As a result, the growth of algae (moss) can be suppressed by preventing light from passing through to some extent, and the concentration of SS seems to be reduced by inhibiting algae growth.

As shown in Figure 25, when vegetation concrete is applied, the influent average BOD concentration is 5.6 (3.6 ~ 7.5) mg / L, primary slope contact tank average 4 (2.6 ~ 5.4) mg / L, secondary slope contact BOD removal rate in the first slope contact tank section was about 28% and total removal rate was about 41%, with the average of 3.3 (1.6 ~ 5.1) mg / L, and when the vegetation concrete was applied, the porous concrete was applied. The removal efficiency increased by about 3%.

This is because bacteria growing on the roots decompose organic matter, and aquatic plants transport oxygen released from photosynthesis to the basement through ventilation tissues. Release seems to decompose the organic matter and reduce BOD.

As shown in Fig. 26, when vegetation concrete is applied, the inflow average COD concentration is 9.3 (8.8 ~ 10.4) mg / L, the primary slope contact tank average 7.6 (6.4 ~ 8.8) mg / L, secondary slope contact The tank average was 6.9 (6 ~ 8.4) mg / L, and the COD removal rate in the first slope contact tank section was about 19%, and the total removal rate was about 26%. The removal efficiency increased by about 6%.

It is believed that aquatic plants breathe and absorb substances by releasing oxygen in a reduced body of water or low soil. Therefore, when aquatic plants release oxygen, organic matters are oxidized and decomposed to increase COD removal efficiency.

As shown in Figure 27, when vegetation concrete is applied, the influent average TN concentration is 29.8 (24.2 ~ 36.5) mg / L, the primary slope contact tank 22 (18.5 ~ 24.6) mg / L, secondary slope contact The tank average 13.4 (7 ~ 17) mg / L, the TN removal rate in the first slope contact tank section is about 26%, and the total removal rate is about 55% .In general, when vegetation concrete is applied, when porous concrete is applied The removal efficiency increased by about 9%.

The microorganisms attached to the roots of the plant decompose organic nitrogen and convert it into NH ₄ ⁺ and NO ₃ ⁻ forms that can be used by the plant.

As shown in Figure 28, when vegetation concrete is applied, the average influent TP concentration is 5.9 (5.2 ~ 6.7) mg / L, primary slope contact tank average 4.6 (4.1 ~ 5) mg / L, secondary slope contact The average 2.8 (2.5 ~ 3.7) mg / L of the tanks indicates that the removal rate of TP in the first slope contact tank section is about 23% and the total removal rate is about 53%. Removal efficiency increased by about 10%.

Unlike nitrogen removal, phosphorus is not transformed into gaseous form and can be removed only by absorption of plants and adherent microorganisms. Phosphorus which plants can absorb is in the form of PO ₄ ^3- , H ₂ PO ₄ , HPO ₄ ^2- and is obtained by filtration and precipitation around the root of particulate phosphorus preferentially like nitrogen. The removal efficiency seems to increase because the dissolved phosphorus is removed by cell synthesis of adherent microorganisms.

Table 8 shows the water purification efficiency according to each medium in the continuous flow reactor of the present embodiment in comparison with the inflow and outflow.

Experiment Item SS (mg / ℓ) BOD (mg / ℓ) COD (mg / l) T-N (mg / l) T-P (mg / ℓ) Porous concrete Influent 9.5 6.6 98 33 8.5 Runoff 4.4 3.9 7.8 20.7 4.9 Removal efficiency 53% 40% 20% 37% 42% Vegetation concrete Influent 15 5.6 9.3 29.8 5.9 Runoff 6.4 3.3 6.9 13.4 2.8 Removal efficiency 57.3% 41% 26% 55% 53%

As can be seen from Table 8, as a result of comparing the continuous flow reactor through the first and second slope contact between the porous concrete and the vegetation concrete used as the media, SS 4.3%, BOD 1%, COD compared to the porous concrete Removal efficiency increased by 6%, TN 18% and TP 11%.

As a result, the vegetation concrete was found to be slightly higher in the water purification efficiency compared to the porous concrete used as the water purification medium, and thus, it was found that the vegetation concrete was highly useful as the water quality improvement medium. In addition, it is expected that the planting of vegetation concrete for water quality improvement will provide the habitat for underwater and waterside organisms, increase self-cleaning ability by water purification, and improve river landscape.

As such, according to the method and structure of the present invention, the high water purification effect of SS 57.3%, BOD 41%, COD 26%, TN 55%, TP 53% in the water purification efficiency of the final effluent can be confirmed, Furthermore, it can be seen that the river maintenance flow rate can be easily managed to prevent dryning.

Table 9 shows the expected water quality evaluation results when the continuous flow reactor of the present example was applied to an actual river (concentration: mg / L, flow rate: m ³ / day).

Sewage Treatment Plant Water Quality Concentration and Discharge Flow Conditions of application of media Estimation of Water Quality Improvement Effect after Application of Media River Water Quality and Flow Rate Minimum required flow rate (considering river landscape and aquatic fish habitat) Osan River (City River) SS: 6.0BOD: 12.7T-N: 11.1T-P: 0.98 Flow rate: 57,000 Porosity 30% Stay time 35 minutes Thickness 10 minutes SS: 2.5BOD: 7.4T-N: 0.4T-P: 0.46 SS: 37BOD: 4T-N: 6.6T-P: 2.27 Flow rate: 72,921 Water surface width: 12 ~ 15m Flow rate: 0.3m / s Depth: 0.3 ~ 0.35m Flow rate: 93,312 ~ 136,080 Gyeongancheon (Rural River) SS: 9.0 BOD: 23T-N: 38T-P: 10 Flow rate: 41,000 Porosity 30% Stay time 35 minutes Thickness 10 minutes SS: 3.8BOD: 13.5T-N: 17.1T-P: 4.7 SS: 9.6BOD: 6.7T-N: 4.1T-P: 0.15 Flow rate: 14,429 Water width: 8 ~ 9m Flow rate: 0.2 ~ 0.25m / s Depth: 0.2 ~ 0.3m Flow rate: 27,648 ~ 58,320

Table 10 shows the expected water quality evaluation results when the continuous flow reactor of the present example was applied to actual rivers (concentration mg / L when the stream maintenance flow rate was minimized). In this case, no separate reservoir is required.

River water quality before filter media River water quality after filter media Water quality improvement efficiency (%) Osan River (city river) SS: 23.4BOD: 7.8T-N: 8.5T-P: 1.70 SS: 21.8BOD: 5.4T-N: 3.8T-P: 1.48 SS: 6.6BOD: 29.7T-N: 54.7T-P: 13.4 Gyeongancheon (Rural River) SS: 9.1BOD: 18.7T-N: 29.1T-P: 7.44 SS: 5.3BOD: 11.7T-N: 13.7T-P: 3.52 SS: 42.0BOD: 37.5T-N: 53.0T-P: 52.7

Table 11 shows the expected water quality evaluation results when the continuous flow reactor of the present example was applied to actual rivers (concentration mg / L, flow rate: m ³ / day when the stream holding flow rate was maximized). In this case, it is expected that the capacity of the storage tank will be smaller than that since the maintenance flow is maximized.

River Water Quality and Required Flow Before Filter Application River water quality after filter media Water Quality Improvement Efficiency (%) Days to go (day) Reservoir size Osan River (city river) SS: 22.6BOD: 8.0T-N: 8.6T-P: 1.67 Flow rate: 6,159 SS: 20.9BOD: 5.5T-N: 3.7T-P: 1.43 SS: 7.2BOD: 30.6T-N: 57.2T-P: 14.4 30 Required Storage Tank Capacity (184,770m ³ ) Gyeongancheon (Rural River) SS: 9.1BOD: 18.9T-N: 29.6T-P: 7.56 Flow rate: 2,891 SS: 5.2BOD: 11.8T-N: 13.8T-P: 3.57 SS: 42.8BOD: 37.7T-N: 53.1T-P: 52.7 30 Required Storage Tank Capacity (86,730m ³ )

When evaluating the results of the method and the structure of the present invention by simply comparing the estimated results of the water quality improvement effect of the existing sewage treatment method, the water quality improvement effect is based on other systems, that is, the discharge through simple transport, the discharge through wetlands, and the oxidation storage tank. It is judged to be higher than the system such as discharge through and discharge through infiltration, and at the same time, it is superior in terms of securing and maintaining stable flow rate.

In addition, the method and the structure of the present invention is an efficient way to use the banks, banks and reservoirs of existing rivers, so that there is no difficulty in selecting a site, does not require a large site, and does not require long-distance sewage from the sewage storage tank. As it adopts the natural flow type, it does not need the power cost or water pipe, which is a significant improvement over the existing method in terms of cost and maintenance.

As a result, it can be seen that the method and the structure of the present invention secure a higher water purification effect and a stable flow rate than the conventional method of using sewage treatment water for preventing dry water.

Furthermore, according to the method and structure of the present invention, since the storage tank is buried underground, a sports facility or other facility may be located in the blunt space, and further, a good permeability contact agent (porous concrete and vegetation concrete) provides a growth space for microorganisms. Therefore, it is excellent in terms of environmental restoration and has various advantages, such as being able to form a natural aesthetic appearance by greening all around the river.

On the other hand, when water quality is improved through contact, sediment may be generated on the bank surface. To prevent this problem, the bank can be cleaned by using different banks and banks with different cycles, or by making contact areas in the form of boxes to be replaced. Can be.

According to the water quality improvement method using the porous concrete of the present invention and its structure, water quality improvement can be efficiently achieved, and furthermore, it is possible to install high-quality flow rate in areas where water flow is difficult to secure especially when water is recycled by reusing and recycling sewage into rivers. Since it can be stably secured, it is possible to solve the problem of lack of flow rate and water pollution caused by dry weathering. In addition, the efficient use of the bank's embankment slope, blunt space, reservoir waterway, etc., it is suitable in terms of cost and maintenance, such as no difficulty in site selection, and does not require a large site.

Although the present invention has been described in connection with the above-mentioned preferred embodiments, it is possible to make various modifications or variations without departing from the spirit and scope of the invention. Accordingly, the appended claims will cover such modifications and variations as fall within the spirit of the invention.

1 is a schematic view showing a structure for improving water quality using porous concrete according to an embodiment of the present invention;

Figure 2 is a photograph showing a continuous flow reactor produced in accordance with an embodiment of the present invention,

3 is a photograph showing a porous concrete according to an embodiment of the present invention,

4 is a photograph showing examples of vegetation concrete planted with plants according to an embodiment of the present invention,

5 is a graph showing a change in the concentration of hydrogen ions over time, to determine the pH change with or without neutralization treatment of porous concrete according to an embodiment of the present invention,

Figure 6 is a graph showing the change in organic matter (DOC) concentration of porous concrete and vegetation concrete according to an embodiment of the present invention,

7 is a graph showing the removal efficiency of organic matter (DOC) of porous concrete and vegetation concrete according to an embodiment of the present invention,

8 is a graph showing the NH ₄ -N concentration change by the porous concrete and vegetation concrete according to an embodiment of the present invention,

9 is a graph showing the NO ₃ -N concentration change by the porous concrete and vegetation concrete according to an embodiment of the present invention,

10 is a graph showing the PO ₄ -P concentration change by the porous concrete and vegetation concrete according to an embodiment of the present invention,

11 is a graph showing a change in pH during the operation of the reactor using a porous concrete according to an embodiment of the present invention,

12 is a graph showing the change of DO during the operation of the reactor using porous concrete according to an embodiment of the present invention,

13 is a graph showing the change in water temperature during the operation of the reactor using porous concrete according to an embodiment of the present invention,

14 is a graph showing the change of EC during the operation period of the reaction vessel using a porous concrete according to an embodiment of the present invention,

15 is a graph showing the SS concentration change and removal efficiency when the porous concrete according to an embodiment of the present invention,

16 is a graph showing a change in BOD concentration and removal efficiency when applying porous concrete according to an embodiment of the present invention;

17 is a graph showing the change in COD concentration and removal efficiency when applying porous concrete according to an embodiment of the present invention;

18 is a graph showing the T-N concentration change and removal efficiency when applying porous concrete according to an embodiment of the present invention,

19 is a graph showing the T-P concentration change and removal efficiency when applying the porous concrete according to an embodiment of the present invention,

20 is a graph showing a change in pH during the operation of the reactor using vegetation concrete according to an embodiment of the present invention,

21 is a graph showing the change of DO during the operation of the reactor using vegetation concrete according to an embodiment of the present invention,

22 is a graph showing the change in water temperature during the operation of the reactor using vegetation concrete according to an embodiment of the present invention,

23 is a graph showing the change of EC during the operation of the reactor using vegetation concrete according to an embodiment of the present invention,

24 is a graph showing the SS concentration change and removal efficiency when applying vegetation concrete according to an embodiment of the present invention,

25 is a graph showing changes in BOD concentration and removal efficiency when applying vegetation concrete according to an embodiment of the present invention;

26 is a graph showing the change in COD concentration and removal efficiency when applying vegetation concrete according to an embodiment of the present invention;

27 is a graph showing the T-N concentration change and removal efficiency when applying vegetation concrete according to an embodiment of the present invention,

28 is a graph showing the T-P concentration change and removal efficiency when applying vegetation concrete according to an embodiment of the present invention.

* Short description of the major reference marks *

10: embankment area 11: embankment

12: Permeable media installed on the bank slope 20: Blunt area

21: Dunchi 23: Reservoir

24: discharge pipe 30: river area

31: Permeable media installed in lakes 32: Lakes

33: Hoan 45: Osuwon

46: water pipe 47: reservoir

Claims (8)

A permeable media 12 formed of the vegetation concrete or the porous concrete and the vegetation concrete planted in the porous concrete, the porous concrete, installed on the bank surface 11, the treated water flows; And A storage tank 23 installed at an underground one side of the blunt region of the river, in which treated water passing through the permeable filter media 12 installed on the bank surface 11 is stored; And Water quality improvement structure using a porous concrete, characterized in that it comprises ;; river reservoir (31) for outflow of the treated water discharged from the reservoir (23). The method of claim 1, wherein the river reservoir 31 In the lake 33, the treated water passes through, porous concrete, vegetation concrete planted in the porous concrete or the water-permeable filter material 32 made of the porous concrete and the vegetation concrete; characterized in that is further installed Structure for water quality improvement using porous concrete. The method of claim 1, wherein the structure, Water discharge structure using a porous concrete, characterized in that it further comprises; a discharge pipe (24) buried in the basement of the blunt area for discharging the treated water from the storage tank (23) to the river reservoir (31). The method of claim 1, wherein the structure, The storage tank for storing the treated water to be treated, and discharged the stored treated water in the permeable filter media installed on the bank surface, the water quality improvement structure using a porous concrete further comprising. The method of claim 4, wherein the structure, Water quality improvement structure using porous concrete, characterized in that it further comprises; a sewage water pipe (46) for watering the sewage from the sewage source (45) to the reservoir (47). Passing the treated water to be treated in the porous concrete, vegetation concrete planted in the porous concrete, porous concrete or the permeable filter (12) consisting of the porous concrete and the vegetation concrete (S1); Storing the treated water that has passed through the permeable filter media 12 in a storage tank 23 installed at an underground side of the blunt region (S2); And Discharging the treated water stored in the storage tank (23) to the river reservoir (31); Water quality improvement method using a porous concrete comprising a. The method of claim 6, wherein the step S3, Before passing the treated water to the river reservoir 31 to pass through the porous concrete, vegetation concrete planted in the porous concrete, porous concrete or the permeable filter 32 made of the porous concrete and the vegetation concrete Step (S3-1); Water quality improvement method using a porous concrete, characterized in that it further comprises. The method of claim 6, wherein the step S1, Method for improving the water quality using porous concrete, characterized in that provided to the permeable filter medium as the treated water to be treated from the sewage source 45.