KR20050081805A - Incombustibility composition for a fire door/wall, incombustibility fire door/wall using the same and method for preparing fire door/wall - Google Patents

Abstract

The present invention relates to a non-combustible composition for fire doors (walls), fire doors (walls) using the same, and a method for manufacturing the same. More specifically, 1 to 80% by weight of organic or inorganic fibers, 1 to 80% by weight of fly ash or bottom ash Nonflammable composition for fire doors (walls) comprising%, 1 to 80% by weight of flame retardant, 1 to 30% by weight of hardening flame retardant resin, and 1 to 40% by weight of non-combustible hollow filler, and fly ash or bottom ash in the composition, Flame retardant and curing flame retardant resin is mixed, and the organic fiber or inorganic fiber is dispersed / injected into the mixture, pulverized / mixed, and finally the non-combustible hollow body is mixed with a mixer using air, and then the mixture is pressed under high pressure. Compression molding into a plate or a square using to form a frame of the fire door (wall) with the plate and / or the shell, and to embed a non-combustible core material therein of the fire door (wall) It relates to a manufacturing method and a non-combustible fire door (wall) produced by the above method.

According to the present invention, since 1 to 70% by weight of the non-combustible composition for fire doors (walls) can recycle waste materials, the production cost is low, and all the constituent compositions generate flames and toxic gases even when contacted by different flames. It is suitable for use as building finishing and interior materials.

Description

Non-combustible composition for fire door (wall), non-combustible fire door (wall) using the same and manufacturing method thereof {Incombustibility composition for a fire door / wall, incombustibility fire door / wall using the same and method for preparing fire door / wall}

The present invention relates to a non-combustible composition for fire doors (walls), fire doors (walls) using the same, and a method for manufacturing the same. More specifically, it is safe from fire when used as a finishing and interior material of building fire doors (walls), and spreads flames. It relates to a non-combustible composition for a fire door (wall) having a property of preventing and generating no toxic gas, a fire door (wall) using the same, and a method of manufacturing the same.

In the case of fire doors, most of the typical building materials that are widely used as fire doors in Korea are steel plates made of steel plates, but since these products are made of steel plates, they can block flames and toxic gases. However, there is a lack of heat shielding performance, processing is difficult, and various kinds of finishes are not possible, there is a limitation in the form of the appearance.

Accordingly, it is currently used as a material having only fragmentary characteristics such as being limited in its use because it does not meet the necessary and sufficient conditions for various types of building finishing and interior materials through various compositional changes of materials.

In order to make up for this drawback, it is attempting to attach a flame retardant material on the steel door, but this also is not easy to work, while the development of the flame retardant material is mostly flame retardant to MDF plywood without any flame retardant performance. The main form is to secure the flame retardancy by applying or applying a coating or a thin plate, but this is also impossible to have a complete fire protection function.

On the other hand, wooden fire doors using gypsum-based lumber and mineral boards have been used overseas for a long time, but these products are expensive and heavy due to the thick thickness of the product, and the external appearance is also thick and diverse. It has a disadvantage.

In the case of plate, MDF or plywood is a plate manufactured by compressing and molding wood chips using an organic adhesive. Currently, it is widely used as a finishing and interior material for construction, but these materials are easily ignited by a flame. This material is not flame retardant.

In order to improve this, there is a method of using an inorganic adhesive instead of an organic adhesive, but the product manufactured in this way is less productive due to delamination and breakage, and only the adhesive is inorganic, and the main material is composed of combustible wood chips. It was not commercialized due to problems such as incombustibility and flame retardancy).

In addition, in the case of using a flame retardant gypsum board, various techniques such as attaching a flame retardant plywood to a gypsum board and attaching an iron or aluminum plate, which is a non-flammable material, have been tried. The technology that can replace gypsum material itself due to its heavy weight and impossibility of processing for finishing has not been developed in Korea and abroad. As a result, gypsum board is a representative product for building finishing and interior materials with flame retardancy. .

Other materials may be mentioned cement boards, which were developed by adding various materials to the cement. In terms of its characteristics, first of all, lightweight materials such as paper particles, perlite, styrofoam particles, vermiculite, and bottom ash are used. Most of these materials are mixed with two or more materials according to the composition ratio. As a result, the development of a method of adding various additives is dominant.

However, most of them have only a slight difference in the properties of the cement board, and do not give a fundamental change in physical properties, which are partially utilized as exterior or ceiling materials rather than as finishing and interior materials for construction.

Recently, non-combustible finishing and interior materials developed by compressing and molding non-combustible alumina powder (Al ₂ O ₃ ) have been developed and released, but this material is not only difficult to finish but 10 times more expensive than MDF or plywood. It is so high that it is only partially used for special purposes and is rarely used as a building finishing and interior material which should be widely used for fire safety.

The current building and fire laws regulate the use of non-flammable, semi-non-flammable, and flame-retardant materials for the interior and interior materials used in the building.To prevent the spread of fire and to protect the life of the building, it is necessary to make fire prevention compartments. Fire doors require the installation of fire doors and are required by law to use materials that can withstand fire for 30 minutes or 1 hour.

The standards and performance test methods according to these legal regulations are flame retardant class 1 (non-flammable materials) and flame retardant class 2 (semi-non-flammable) according to the performance standards of Korean Industrial Standard KS F2271 (Test of Flame Retardant Performance of Buildings) for finishing and interior materials Materials) and flame retardant grade 3 (flame retardant materials) .In particular, in the case of fire doors, the fire safety test according to Korean Industrial Standard KS F2257 is carried out for 1 hour, and It is classified as (乙) species and can be used only if it meets the above performance standard.

This is a regulation adopted by most countries around the world as well as Korea, but there may be some differences depending on the contents, but the regulations to use the one that meets the performance standards are almost the same. This is to prevent the spread of flames and to protect the safety of life and property from toxic gases generated during combustion in preparation for fire.

However, as mentioned earlier, many of the building finishes and interior materials currently in use are not suitable for their intended use, and they meet some of the performance criteria for non-combustible, semi-combustible, and flame-retardant materials, but can be used as building finishes and interior materials. The condition is not met.

Currently, various finishes and interior materials have been developed in non-flammable, semi-non-flammable, and flame-retardant performances.However, there are few products with excellent performance. Although it is the most widely used building interior product because it has this low-cost property, it is inferior in water resistance, and is not combustible, semi-non-flammable, or flame-retardant, and is easily burned by flames and spreads a fire. Its use is limited.

In addition, gypsum board is manufactured by manufacturing waste chemical gypsum, plaster, etc. from fertilizer factory or power plant, and has excellent processability and workability, low price, and non-flammable, semi-non-flammable, and flame retardant performance. It is a typical building interior and finishing material with performance standards of non-flammable, semi-non-flammable, and flame retardant currently used, but it is very weak against moisture, easy to break due to low strength, and does not generate much dust during processing and recycling of gypsum board. There is a problem of contamination, and there is a problem that paper is stuck on the surface, so it is restricted to use in various forms of design and use.

In addition, the cement board has high strength, excellent performance of non-combustible, semi-non-combustible and flame retardant, and good water resistance, whereas it has problems such as poor workability and workability, heavy weight and breakage. It is mainly used as exterior wall or surface material of building, and it is hardly used as finishing and interior material for building.

The present invention, in order to solve the above problems, to reinforce and improve the physical and chemical shortcomings of the existing materials, such as the lack of heat shielding performance that has been generated in the existing steel / wood fire doors, various finishes are not applicable It became.

Therefore, the object of the present invention is to use a waste material, environmentally friendly, excellent hardness, strength, water resistance, etc., low cost, and most of all can exhibit a variety of finishes (appearance) having a non-combustible performance safe from fire. The present invention provides a non-combustible composition for fire doors (walls).

Another object of the present invention to provide a method for producing a fire door (wall) using a non-combustible composition that can satisfy the requirements and sufficient conditions as a building material, as well as non-combustible using the composition.

Another object of the present invention is manufactured by the above method is safe from fire when used as a fire door (wall), not only has the basic performance and physical properties of heat shielding and fire prevention, such as preventing the spread of flame and no toxic gas generated, It is to provide a non-combustible fire door (wall) that can be finished and economical.

Non-combustible composition for fire door (wall) of the present invention for achieving the above object is 1 to 80% by weight of organic or inorganic fibers, 1 to 80% by weight of fly ash or bottom ash, 1 to 80% by weight of flame retardant, flame retardant for curing 1 to 30% by weight of the resin and 1 to 40% by weight of the nonflammable hollow body filler.

Method of producing a fire door (wall) using the composition for achieving another object of the present invention comprises the steps of providing the non-combustible composition; Mixing the fly ash or bottom ash, a flame retardant, and a flame retardant resin for curing; Dispersing / injecting organic fibers or inorganic fibers in the mixture to pulverize / mix and then finally mix the non-combustible hollow bodies with a mixer using air; Compressing the mixture into a plate or a square using a high pressure heat press; And constructing a skeleton of the fire door (wall) with the plate and / or the lumber and embedding a non-combustible core material therein.

Non-combustible fire door (wall) for achieving another object of the present invention is manufactured by the above production method.

Hereinafter, the present invention will be described in more detail.

As described above, the non-combustible composition for the board and / or the lumber of the fire door (wall) according to the present invention is 1 to 80% by weight of organic fibers or inorganic fibers (a), 1 to 80% by weight of fly ash or bottom ash (b) 1 to 80% by weight of the flame retardant (c), 1 to 30% by weight of the flame retardant resin (d) for curing, and 1 to 40% by weight of the nonflammable hollow filler (e).

In addition, the compositions of the present invention may further comprise incombustible lightweighting agents (f) and / or other additives such as hardening accelerators, surfactants and / or colorants.

According to the present invention, the amount of the organic fiber or the inorganic fiber (a) is preferably 1 to 80% by weight among the components of the non-combustible composition used as the plate or the shell of the fire door (wall). Paper crushed in the state, wood crushed, waste fibers, rice bran, vegetable fibers or mixtures thereof, and the like, rock wool, glass wool, basalt wool, ceramic wool or a mixture thereof may be used. have. The components may use some waste material.

The organic fiber or inorganic fiber (a) is to allow the molded article made of the composition of the present invention to exhibit the wood characteristics of the MDF or plywood, and can be processed with a small knife (cut knife) to produce a variety of sizes depending on the size Not only this is possible, but also the bonding force with the screw and the like during wall attachment construction will be an important role.

If the amount of the organic fiber or inorganic fiber (a) is less than 1% by weight, flame retardant performance may be improved, but there is a problem in that the hardness is high, such as workability or bonding strength with a screw, etc., and the composition ratio exceeds 80% by weight. If the strength is low, it may be difficult to maintain the shape of the flame-retardant molded article.

According to the present invention, the fly ash or the bottom ash (b) was used to maintain the surface strength and smooth surface, it is possible to adjust the density, surface and compressive strength according to the composition ratio. As used herein, the term "fly ash" refers to a generally light weight residue from coal residues remaining from coal used as a heat source in a thermal power plant, and "bottom ash" refers to a fly ash rather than a fly ash. It means heavy residues that sink to the floor.

These fly ash or bottom ash (b) has a lighter specific gravity than cement, but in the composition of the flame-retardant molded article, component (b) corresponds to a composition having a high specific gravity, so if the composition ratio is high, there will be a problem in weight reduction. However, it is possible to relatively increase the strength and obtain a solid flame retardant molded article.

If the composition ratio of the fly ash or the bottom ash (b) is less than 1% by weight, there is a problem that it is difficult to make a suitable hardness, surface effect and a smooth molded article, when the composition ratio exceeds 80% by weight, the specific gravity is high, weak Easily broken even when the impact occurs, there is a problem that is not suitable for use for the purpose of the plate or each material.

In the present invention, since the organic fiber or inorganic fiber (a) may be a flammable material depending on the material, a flame retardant (c) that minimizes combustion and smoke during flame generation to secure non-combustible and semi-combustible performance, for example, carbonic acid. Calcium, sodium hydrogen carbonate, sodium carbonate, other carbonates or mixtures thereof may be used, and when the temperature of the flame exceeds 500 ° C., the component (c) is decomposed and carbon dioxide gas (CO ₂ ) is generated inside the plate to produce a flame. It can be adjusted to be extinguished, and through the component (c) it can be improved to the performance of the semi-unpaid grade to the non-paid grade, the flame retardant grade or higher than the semi-paid grade in the performance criteria alone.

The amount of the flame retardant (c) is preferably 1 to 80% by weight. If it is less than 1% by weight, it is difficult to expect a role as a flame retardant, and when it exceeds 80% by weight, it tends to affect the strength of the composition.

However, although only non-combustibility can be secured to some extent with the above components, fatal shortcomings such as a lack of sufficient compressive / tensile strength as an important building material, non-combustibility, deformation during curing, and impossibility of attaching various finishes are found.

Therefore, in order to solve such a fatal defect as a building material, a hardened flame retardant resin (d), for example, a phenol resin, a flame retardant polyester resin, or a melamine resin is used to form a molded article that satisfies the performance and non-combustibility as a building material at the same time. It can manufacture.

The amount of the curing flame-retardant resin (d) is preferably 1 to 30% by weight, and less than 1% by weight of the composition is impossible to cure, whereas when it exceeds 30% by weight, the role of curing as a flame-retardant resin is no longer improved. The result is a rise in manufacturing costs.

On the other hand, in order to reduce the weight of the non-combustible fire door (wall) and to improve sound absorption performance, in order to improve the heat insulation and fire resistance of the fire door (wall), a non-combustible hollow filler (e) is used, which is required according to the composition ratio. A material capable of satisfying fire resistance can be produced. The non-combustible hollow filler (e) may be, for example, an inorganic hollow body such as a perlite hollow body, a fly ash hollow body, a ceramic hollow body, a Shirasu balloon, a silica balun, a ganban stone balun, a mineral balun, or one of these. The above mixture can be used.

The composition ratio of the non-combustible hollow filler (e) can be produced molded articles having various specific gravity within the range of 1 to 40% by weight, but when the ratio of the composition is less than 1% by weight, specific gravity, sound absorption and heat insulation / fireproof performance Because it hardly affects the original role can not be expected, if the composition ratio exceeds 40% by weight, the surface is rough, there may be a problem that the strength of the composition is lowered.

In addition, the non-combustible lightweight agent (f) may be used to reduce the weight of the non-combustible molded article, and it is possible to manufacture building finishes and interior materials having various specific gravity depending on the composition ratio. The non-combustible lightweighting agent (f) may use, for example, particulate perlite, particulate vermiculite, diatomaceous earth, zeolite or mixtures of one or more thereof. The particulate perlite or particulate vermiculite may use waste materials.

The amount of the non-flammable lightweighting agent (f) may be used to produce molded articles having various specific gravity within the range of 1 to 50% by weight, but when the ratio of the composition is less than 1% by weight, it hardly affects the specific gravity. If it does not act as a lightweighting agent, and if the composition ratio exceeds 50% by weight, the surface may be rough, the strength is lowered, and the composition may be separated raw materials to obtain a mixture of even distribution.

In the present invention, as an additional option, it is possible to fix the composition in a short time with other additives to improve the productivity of the molded article prepared with the composition and to minimize the shrinkage and deformation that may occur during the curing process. 1 to 10% by weight of a curing accelerator fixing agent (g), for example, a mixture of magnesia, gypsum plaster, a mixture of inorganic or organic acids, calcium silicate or a mixture of one or more thereof may be used.

In addition, it is possible to use a surfactant (h), for example, an alkylbenzene sulfonic acid-based surfactant having a high surface tension, to improve heat insulation and weight reduction of the molded article, and to increase water resistance and water repellency. By lowering the owing to the characteristics that can maintain the shape in water, and in particular, a large number of porous air layers in the interior of the non-combustible molded article can improve the insulation and light weight. However, the composition ratio is 0.1 to 0.3% by weight since it may cause a decrease in strength depending on the composition ratio.

Due to the characteristics of the non-combustible molded article prepared with the composition of the above components, the components (a) and (b) may have a black gray color and thus affect the overall color. In order to improve and supplement this problem, the base color is made pale-white by using 1-10% by weight of a white inorganic colorant (i), for example, titanium dioxide (TiO ₂ ), which is resistant to flame and has excellent hiding power. It is possible to improve the surface treatment such as painting and veneer coating without cumbersome.

In particular, the red or yellow inorganic colorant (j) is mixed in an appropriate ratio to express various colors to vary the background color of the flame-retardant molded article so that the original color may be used as it is without a separate surface coloring.

The manufacturing method for manufacturing a non-combustible plate and the square material by applying the compression molding method to the composition of the present invention as described above,

Providing a nonflammable composition;

Mixing the fly ash or bottom ash, a flame retardant, and a flame retardant resin for curing;

Dispersing / injecting organic fibers or inorganic fibers in the mixture to pulverize / mix and then finally mix the non-combustible hollow bodies with a mixer using air;

Compressing the mixture into a plate or a square using a high pressure heat press; And

And forming a frame of the fire door (wall) with the plate and / or the lumber, and embedding a non-combustible core therein.

Hereinafter, the manufacturing method will be described in detail.

According to the manufacturing method for manufacturing the non-combustible plate and the square material of the present invention, the compression and molding method must go through the first mixing process and the second compression process in order, the first mixing process is first fly ash or bottom ash (b ), A flame retardant (c), a flame retardant resin for curing (d), optionally a non-flammable lightweight agent (f), and the like in the form of a powder mixed with a mixer through a metering system, and then organic or inorganic fibers (a) Disperse / inject

For example, after mixing using a mixer of a sharp blade, such as a super (hensel) mixer while rotating at high speed and evenly pulverized / mixed, the non-combustible hollow filler (e) is mixed, but at this time, It is ideal to mix in a short time using air to prevent component (a) from re-agglomeration, which is then stored and stored in a storage tank for secondary compression.

On the other hand, the mixture is completed through the primary mixing process, the specific gravity required according to the use of the final molded product must be different, the appropriate amount of mixing should be made according to the required specific gravity.

For example, when the specific gravity of the required molded article is 1.0 to 1.2 g / cu · cm, such as the wood fire door (wall), the weight ratio of component (b) increases to increase the specific gravity and strength. In the case of building board, the specific gravity is 0.7 ~ 0.9g / cu · cm, so in this case, lower the weight ratio of component (b) so that the required specific gravity can be reached. The height should be adjusted / mixed in this way.

The high pressure heat press (500 to 3,000 tons) is used to mold the mixed composition according to the required specific gravity in a predetermined thickness and size. The temperature is 60 to 200 ° C. and the time is 1 to 60 minutes. Compression / molding in to complete the non-combustible sheet molding.

In this case, the use of a high-pressure heat press with the addition of a high-frequency heating function allows the curing reaction of the component (d) to proceed rapidly, thereby significantly reducing the molding time in the press.

Incidentally, higher compression and tension can be achieved by placing a reinforcing mesh composed of glass fibers on the top / bottom or inside of it while administering the mixed composition in the press to increase the compression and tensile strength of the sheet being formed. Finished plate moldings with strength.

On the other hand, in manufacturing a fireproof door (wall) square material excellent in non-combustibility, it is possible to manufacture a finished non-combustible square molded article by a method similar to the compression and molding method of the sheet for building interior, it can also be manufactured using the sheet for building interior. have.

The molded article of the present invention having excellent non-combustibility has various product characteristics according to the manufacturing method, but first, the molded article by the compression / molding method has an even surface, there is no deformation and shrinkage in the curing process, and excellent strength.

In addition, in the compression molding step, aluminum, steel, acrylic, or wood may be reinforced in the shell to form a shell or plate in order to increase the compression and tensile strength of the shell.

In the present invention, a frame of a fire door (wall) is formed of the non-combustible plate and / or a square material, and then a non-combustible core material is embedded therein to produce a non-combustible fire door (wall).

The core material is lightweight foamed concrete, ALC (Autoclaved Lightweight Concrete), lightweight foamed mineral board, lightweight foamed glass board, bulk (Bulk) or blanket (Blanket) or mat type rock wool, basalt rock wool, glass wool or ceramic wool Can be.

In addition, the core material is 1 to 80% by weight of the organic or inorganic fibers, 1 to 80% by weight of the fly ash or bottom ash, 1 to 80% by weight of the flame retardant and 1 to 60% by weight of the flame retardant curing agent It may be a non-combustible core material prepared by mixing, then molded by a roller press or an autoclave (Autoclave). Such a core material is pending by the applicant.

In addition, the frame that forms part of the fire door is basically made of the non-combustible plate or square material is completed, but by using the existing steel frame or stainless frame instead of its role, there is a problem in performing the basic functions such as fire protection function It is easy to see that there is no.

If necessary, non-combustible iron plate, mineral board, rock board, silica board, gypsum board, magnesium board or alumina board can be further attached to at least one side of the fire door (wall), and at least one side of the fire door (wall). MDF, plywood, natural veneer, interior film, aluminum sheets or plasterboards can be further attached.

The molded article prepared according to the present invention can be advantageously used in various fields as follows because it shows excellent incombustibility or flame retardancy and physical properties.

① wood fire door

Fire doors manufactured using non-combustible lumber and / or plate made in accordance with the present invention have a number of advantages that steel fire doors do not have, such as ease of processing, various finishes, as well as perfect fire and fire protection, in particular apartments, etc. By installing the interior wood door of the multi-family house as the wood fire door, it is possible to provide a new level of living environment because it can protect lives from flame spread and toxic gases even within the households.

② firewall

In the case of a firewall composed of a non-combustible product manufactured according to the present invention, as well as a reduction in manufacturing cost and load, the existing firewall thickness (average of 100 m / m) is also reduced in a substantial part, thereby reducing cost and internal effective use area. It can also contribute a lot.

The present invention will be described in more detail with reference to the following examples and comparative examples, but the scope of the present invention is not limited to the following examples.

Measurement methods of various physical properties measured in the following Examples and Comparative Examples are as follows.

1) Non-combustible, semi-non-combustible, flame-retardant performance characteristics: flame retardant class 1 (non-flammable material), flame retardant class 2 (semi-combustible material), flame retardant class 3 (flame retardant material) according to Korean Industrial Standard KS F2271 Measured by

2) Specific gravity and density: Determination of specific gravity and density by Korean Industrial Standard KS L5316 (Testing method for physical properties of gypsum sheet)

3) Flame resistance: Flame resistance measurement by Korean Industrial Standard KS F3507 (gypsum board product)

4) Immersion stability: Immersion stability measurement by Korean Industrial Standard KS F3507 (gypsum board product)

Measurement of the most important performance criteria to be achieved in the present invention, that is, the performance standards of non-flammable, semi-non-flammable, and flame retardant, which are examples of the molded articles manufactured by the compression molding method and comparative examples of products widely used in the market. According to Korean Industrial Standard KS F2271, flame retardant grade 1, flame retardant grade 2, non-flammable grade 3, flame retardant grade 3 were measured according to the composition ratio of the composition and the type of molded article.

In addition, the weight change per unit area according to the composition ratio of the composition was measured, and the fire safety of the molded article molded by the composition of the present invention was confirmed through flame resistance.

In particular, most building finishes and interior materials require immersion stability, so their performance was also tested.

Example 1-Example 4

First, fly ash or bottom ash (b), flame retardant (c) and curing flame retardant resin (d) are mixed in a mixer through a metering system in the amounts and amounts shown in Table 1, and then organic or inorganic fibers ( a) by dispersing / injecting and mixing the non-flammable hollow filler (e) evenly by using a super (hensel) mixer and mixing, but at this time, in order to prevent the appropriately pulverized component (a) from agglomeration again After mixing for 10 minutes, and then stored in a storage tank for the secondary compression process and waiting.

Thereafter, the composition is compressed / molded to a thickness of 35 m / m and a size of 900 × 2,100 in a high pressure heat press (about 1,000 tons) at a temperature of about 150 ° C. for about 30 minutes to produce a non-combustible sheet molded product, and The physical properties of the molded article were evaluated by the measurement method, and the measurement results are shown in Table 1.

TABLE 1

The plate material manufactured by the compression and molding method as in Example 1 and Example 2 of Table 1, and the respective materials produced by the compression and molding method as in Examples 3 and 4 are blended with the composition by the compression and molding method. As the use ratio (weight ratio) of the rock wool of the ratio was confirmed that the specific gravity is lower, respectively, it was found that there was no change in the flame retardant performance and flame resistance grade in each Example.

Comparative Example 1 to Comparative Example 5

Meanwhile, five kinds of products for building finishing and interior materials, MDF / plywood, general gypsum board, fireproof gypsum board, slate board, and cement board, which are widely used in connection with the present invention, can be purchased from the market. The physical properties were evaluated, and the measurement results are shown in Table 2 below.

TABLE 2

As mentioned above, in Comparative Example 1 (MDF, plywood) of Table 2, no flame retardant performance was found, and Comparative Example 2 (General Gypsum Board) and Comparative Example 3 (Fireproof Gypsum Board) were The flame retardant performance was shown as flame retardant grade 2 and flame retardant grade 1, respectively, and it was confirmed that there was no problem in fire safety, and in case of comparative example 4 (slate plate) and comparative example 5 (cement wood plate), There appeared to be no problem incombustibility.

However, as shown in Table 2, the non-combustibility of Comparative Example 4 and Comparative Example 5 was the most excellent, but the weight per unit area is 1.0 ~ 1.4 is heavy, there was a problem in the light weight, gypsum board for the immersion stability against moisture It was found to be the most problematic.

Therefore, MDF or plywood, widely used as finishing and interior materials for building, is a material that cannot be used in building and fire law due to fundamental fire safety problems. Gypsum board has restrictions on use and location of buildings. In the case of, slate board and cement board, the weight per unit area is much heavier than MDF and gypsum board.

On the other hand, when comparing the measurement results of the embodiments and comparative examples are as follows.

The weight per unit area of the plate produced by the compression and molding method as in Example 1 and Example 2 of Table 1 was in the range of 0.7 to 0.9, it was confirmed that the weight similar to the MDF of Comparative Example 1 of Table 2, flame retardant The performance and flame resistance were similar to those of the fireproof gypsum board of Comparative Example 3, and the immersion stability against moisture was found to be stable to moisture, such as maintaining its shape in water.

In the case of each material manufactured by the compression and molding method as in Example 3 and Example 4 of Table 1, the flame retardant performance of the slate plate corresponding to Comparative Example 4 of Table 2 and the cement wood plate corresponding to Comparative Example 5 The same flame retardant class 1, flame resistance was also shown to be non-flammable, as the weight per unit area of the slate plate of Comparative Example 4 of Table 2 and the cement wood plate of Comparative Example 5 in the range of 1.0 ~ 1.4 In Example 3 and Example 4 of Table 1, the weight per unit area was found to have a range of 1.0 to 1.2.

Test Example 1

Forming the frame and the frame of the fire door using the plate according to Example 1 of Table 1, and the angular material according to Example 3, embedded a ceramic wool as a core material therein and one side is finished with plywood 35m / The fireproof test of the non-combustible fire door made with the thickness of 900m and the size of 900 × 2,100 was conducted by the Korea Institute of Construction Technology, a national testing laboratory, according to the Korean Industrial Standard KS F2257. Test results complying with the following fire prevention regulations were obtained.

TABLE 3

According to the present invention as described above, 1 to 70% by weight of the non-combustible composition provided in the production of non-flammable / semi-non-flammable / flame retardant plate, each material and core material can be recycled waste material, the production cost is low, constituent composition All of them are suitable for use as building finishing and interior materials because there is no fire and no toxic gas is generated upon contact.

In addition, it is easy to process (sawing, screwing, planing, veneer and film paper adhesion, painting, etc.), product strength and water resistance, no deformation, non-flammable, and can be used for wood or board As a result, it can be used as a variety of interior / exterior materials for construction. Accordingly, in the event of a fire, it is effective in providing a safe living space that prevents the spread of fire and protects our valuable lives and property from flames and toxic gases. have.

Claims (17)

1 to 80% by weight of organic or inorganic fibers, 1 to 80% by weight of fly ash or bottom ash, 1 to 80% by weight of flame retardant, 1 to 30% by weight of flame retardant resin for curing, and 1 to 40% by weight of nonflammable hollow filler Non-combustible composition for fire doors (walls) characterized by including. The method according to claim 1, wherein the organic fiber is a fiber crushed paper fiber, wood flour, waste fiber, rice bran, vegetable fiber or a mixture thereof, the inorganic fiber is rock wool, glass wool, basalt rock wool, ceramic wool or Nonflammable composition, characterized in that a mixture thereof. The nonflammable composition according to claim 1, wherein the flame retardant is calcium carbonate, sodium bicarbonate, sodium carbonate, other carbonates or mixtures thereof. The nonflammable composition according to claim 1, wherein the curing flame retardant resin is a phenol resin, a flame retardant polyester resin or a melamine resin. The non-combustible hollow filler (e) of claim 1, wherein the non-combustible hollow filler (e) is a perlite hollow body, a fly ash hollow body, a ceramic hollow body, a siras balun, a silica balun, a ganban stone balun, a mineral balun, or a mixture thereof. . The method of claim 1, wherein the composition further comprises 1 to 50% by weight of non-combustible lightweighting agent, and / or 1 to 10% by weight of other additives selected from the group consisting of a hardening accelerator, a surfactant and an inorganic colorant. Nonflammable composition. 7. The incombustible composition according to claim 6, wherein the incombustible lightening agent is particulate perlite, particulate vermiculite, diatomaceous earth, zeolite or mixtures thereof. The non-combustible composition according to claim 6, wherein the curing accelerator is magnesia, gypsum plaster, a mixture of inorganic or organic acids, calcium silicate or a mixture thereof. Providing a nonflammable composition according to any one of claims 1 to 8; Mixing the fly ash or bottom ash, a flame retardant, and a flame retardant resin for curing; Dispersing / injecting organic fibers or inorganic fibers in the mixture to pulverize / mix and then finally mix the non-combustible hollow bodies with a mixer using air; Compressing the mixture into a plate or a square using a high pressure heat press; And A method of manufacturing a non-combustible fire door (wall), comprising the step of forming a frame of the fire door (wall) with the plate and / or the lumber, and embedding a non-combustible core material therein. 10. The non-combustible fire door according to claim 9, further comprising the step of reinforcing the mesh composed of glass fibers to the inside and / or the outside of the sheet in order to increase the compressive and tensile strength of the sheet in the compression molding step. Wall). The non-combustible fire door according to claim 9, further comprising the step of reinforcing the aluminum, steel, acrylic or wood in the shape of the material or plate in order to increase the compression and tensile strength of the material in the compression molding step. (Wall) manufacturing method. 10. The method of claim 9, wherein the method further comprises the step of mixing a non-flammable lightweighting agent, a curing accelerator, and / or an inorganic colorant upon mixing the fly ash or the bottom ash, the flame retardant, and the curing flame retardant resin. Manufacturing method of fire door (wall). 10. The method of claim 9, wherein the non-combustible core material is lightweight foam concrete, ALC (Autoclaved Lightweight Concrete), lightweight foam mineral board, lightweight foam glass board, bulk (Bulk), blanket (mat) or mat type rock wool, basalt A method of manufacturing a nonflammable fire door (wall), characterized in that it is cotton, glass wool or ceramic wool. 10. The method according to claim 9, wherein the non-combustible core material comprises 1 to 80% by weight of organic or inorganic fibers, 1 to 80% by weight of fly ash or bottom ash, 1 to 80% by weight of flame retardant and 1 to 60% by weight of flame retardant curing agent. A method of producing a non-combustible fire door (wall), characterized in that it is produced by mixing the non-combustible composition, followed by molding by a roller press or an autoclave. Non-combustible fire door (wall), characterized in that produced by the method according to any one of claims 9-14. 16. The non-combustible fire door (wall) according to claim 15, further comprising a non-combustible iron plate, a mineral board, a rock board, a silica board, a gypsum board, a magnesium board, or an alumina board attached to at least one surface of the fire door (wall). 16. The non-combustible fire door (wall) according to claim 15, further comprising MDF, plywood, natural veneer, interior film, aluminum sheet or plastered paper on at least one side of the fire door (wall).