KR20050004318A - Glass decoration film and preparing method thereof - Google Patents

Glass decoration film and preparing method thereof Download PDF

Info

Publication number
KR20050004318A
KR20050004318A KR1020030044454A KR20030044454A KR20050004318A KR 20050004318 A KR20050004318 A KR 20050004318A KR 1020030044454 A KR1020030044454 A KR 1020030044454A KR 20030044454 A KR20030044454 A KR 20030044454A KR 20050004318 A KR20050004318 A KR 20050004318A
Authority
KR
South Korea
Prior art keywords
film
polyester film
glass
glass decorative
mold
Prior art date
Application number
KR1020030044454A
Other languages
Korean (ko)
Other versions
KR100620610B1 (en
Inventor
정경원
Original Assignee
정경원
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 정경원 filed Critical 정경원
Priority to KR1020030044454A priority Critical patent/KR100620610B1/en
Publication of KR20050004318A publication Critical patent/KR20050004318A/en
Application granted granted Critical
Publication of KR100620610B1 publication Critical patent/KR100620610B1/en

Abstract

PURPOSE: Provided is glass decorating film capable of being adhered on face of the glass without additional adhesive by transfer of enamel face of polyester film to side opposite to pattern formed by compression of the polyester film and formed in varied shapes by simply changing molds thereto. CONSTITUTION: The glass decorating film comprises polyvinyl chloride or polyolefine based resin layer having pattern, transparent polyester film thermally pressed or heat-transfer polyester film having enamel layer, and protective releasing film attached to surface of the enamel layer and comprising polyester film. Such decorating film is formed by introducing polyvinyl chloride raw material then forming patterns in desirable mold at 50 to 110 deg.C; compressing transparent polyester film and/or heat-transfer polyester film using press-roll in the mold.

Description

유리장식용 필름 및 그 제조방법{Glass decoration film and preparing method thereof}Glass decoration film and preparing method

본 발명은 유리장식용 필름 및 그 제조방법에 관한 것으로, 더욱 상세하게는 원료로 폴리비닐클로라이드 또는 폴리올레핀계 수지를 투입 후 일정 온도로 유지되는 금형에서 무늬를 형성시킨 후 바로 금형에서 투명 폴리에스테르 필름 또는 전사용 폴리에스테르 필름을 프레스 롤로 압착시켜 유리장식용 필름을 제조함으로써, 폴리에스테르 필름의 압착에 의해 성형된 무늬 반대면에 폴리에스테르 필름의 에나멜(enamel) 면이 전이되어 접착제 없이도 유리 위에 부착이 가능한 유리장식용 필름 및 그 제조방법에 관한 것이다.The present invention relates to a glass decorative film and a method for manufacturing the same, and more particularly, after forming a pattern in a mold maintained at a constant temperature after the addition of polyvinyl chloride or polyolefin resin as a raw material, a transparent polyester film or By pressing the transfer polyester film with a press roll to produce a glass decorative film, the enamel side of the polyester film is transferred to the opposite side of the pattern formed by the pressing of the polyester film so that the glass can be attached onto the glass without an adhesive. A decorative film and its manufacturing method.

사생활 보호 및 차광의 목적으로, 투명한 창 유리에 특정 필름으로 코팅하여, 실내 또는 차량 내부를 쉽게 볼 수 없도록 하는 것이 널리 시행된다.For the purpose of privacy and shading, it is widely practiced to coat the transparent window glass with a certain film so that the interior or the inside of the vehicle cannot be easily seen.

시중에 상기와 같은 목적을 위해 유리용 장식필름(Decoration Film) 또는 윈도우 레이스(Window Lace)라는 이름의 상품들이 유통되고 있다. 이들은 필름 또는 레이스를 유리 면에 붙여 내부가 잘 보이지 않게 하는 커텐(Curtain) 대용으로 쓰이기도 하고, 유리의 장식용으로 사용하기도 하며, 경우에 따라서는 유리가 깨어질 때 파편이 튀지 않도록 안전을 고려해서 사용하기도 한다.For this purpose, commercially available products named Decoration Film or Window Lace for glass are being distributed. They are used as a curtain instead of a film or lace on the glass surface, making it difficult to see inside, and sometimes used as a decoration for glass.In some cases, safety is taken to prevent fragments from splashing when the glass is broken. Also used.

시중에 가장 많이 유통되는 유리용 장식필름은 폴리에스테르 필름(이하 'PET Film'라 한다) 위에 유리의 뒷면이 보이지 않을 정도의 불투명 상태의 여러 무늬를 인쇄하거나 또는 경질 PVC 필름 표면을 엠보싱(Embossing) 처리하고, PET 필름 또는 경질 PVC 필름이 유리에 잘 붙을 수 있도록 접착제 코팅공정을 거친 후 다시 접착제 코팅 면을 보호하기 위하여 또 다른 PET 필름을 붙여만든 상품으로 유통되고 있다. 이런 제품을 소비자가 사용 시에는 접착제면 위에 붙어있는 PET 필름을 분리해 떼어낸 후 접착제 면을 유리 면에 붙여 위에서 설명한 바와 같은 장식용 필름으로서의 목적을 달성한다.The most widely used glass decorative film on the market is to print various opaque patterns on the polyester film (hereinafter referred to as 'PET Film') or to emboss the surface of the rigid PVC film. After the treatment, the PET film or the hard PVC film is adhered to the glass, the adhesive coating process, and then again to protect the adhesive coating side is distributed as a product made with another PET film. When using such a product, the PET film attached to the adhesive side is separated and peeled off, and then the adhesive side is attached to the glass side to achieve the purpose as a decorative film as described above.

그러나, 이러한 제품의 결점은 접착제를 사용해서 유리 면에 붙이기 때문에 장기간 사용하면 접착제가 화학변화(가수분해 등)를 일으켜 장식필름에 주름이 잡히기도 하고 장식필름을 떼어낸 후 다시 다른 상품을 붙일 때 유리 면에 남아있는 분해 된 접착제의 제거가 큰 문제점으로 부각되고 있다. 또한 인쇄한 PET 필름이나 투명 PET 필름 또는 경질 PVC 필름 표면을 엠보싱 한 필름을 유리에 붙이는정도이기 때문에 제품의 입체감이 전혀 없으며, 넓은 면적을 붙일 때는 공기 주머니가 남아 있어 깨끗하게 처리하는 것이 매우 어렵기도 하다.However, the drawback of these products is that they adhere to the glass surface using adhesives, so when used for a long time, the adhesive may cause chemical changes (hydrolysis, etc.), causing wrinkles in the decorative film, or when removing the decorative film and then attaching another product. The removal of the disintegrated adhesive remaining on the glass surface is a major problem. In addition, since the printed PET film, transparent PET film, or embossed film on the surface of the hard PVC film is attached to the glass, there is no three-dimensional effect of the product, and when attaching a large area, air bags remain, which makes it very difficult to clean it. .

현재 외국에서는 이러한 유리용 PET 필름의 결점을 보완한 제품으로 PVC 필름을 여러 단계의 과정을 거쳐 접착제를 사용하지 않고 유리에 붙일 수 있는 유리용 연질 PVC 장식필름이 개발되어 있다. 즉, 연질 PVC 필름을 가공한 이 유리용 장식필름은 유리 면에 붙이는 PVC 필름면이 유리알 같이 고광택이 나는 에나멜면을 형성하면 유리와 밀착성이 좋아져 접착제 없이도 붙일 수 있다는 원리를 이용하고 있다.Currently, foreign countries have developed a flexible PVC decorative film for glass that can be applied to glass without using an adhesive through a multi-step process to compensate for the drawbacks of such glass PET film. In other words, this decorative film for glass processed soft PVC film uses the principle that if the PVC film surface attached to the glass surface forms an enameled surface with high gloss like glass grains, the adhesion with the glass is good and can be attached without adhesive.

이러한 제품은 인쇄된 PVC 필름을 150 ∼ 200 ℃ 정도의 고온으로 필름을 열처리하면서 그 필름 위에 프레스 롤(Press Roll)로 PET 필름을 압착시켜 제품을 만드는데 PET 필름 표면의 거울 면이 PVC 필름에 전이되는 원리이다. 이러한 공정을 거친 PVC 필름은 아직은 투명하기 때문에 유리가리개로서의 소기의 목적을 달성하기 위해서 다시 150 ∼ 200 ℃의 고열 하에서 이번에는 엠보싱 롤(Embossing Roll)로 고압 하에서 필름 표면에 요철을 주어 빛 굴절의 산란현상 때문에 유리의 뒷면이 보이지 않게 되기도 하고 아예 불투명 무광 엠보싱 처리를 하기도 하여 제품이 완성된다.These products heat the printed PVC film to a high temperature of 150 ~ 200 ℃ and press the PET film with a press roll on the film to make a product.The mirror surface of the PET film surface is transferred to the PVC film. It is a principle. Since the PVC film which has undergone such a process is still transparent, in order to achieve the desired purpose as a glass shader, this time under the high temperature of 150 to 200 ° C, this time, the embossing roll is used to give unevenness to the surface of the film under high pressure to scatter light refraction. Due to the phenomenon, the back side of the glass may be invisible or the opaque matte embossing may be completed.

이와 같이 PVC 필름을 이용한 유리용 장식필름은 필름의 인쇄 →인쇄면 보호를 위한 다른 PVC 필름의 적층(Lamination) →고온 하에서 PET 필름의 접합 →고온 하에서 전체 엠보싱 처리 등 여러 공정을 거쳐야 하기 때문에 공정과 설비가 복잡하고 따라서 생산성에 문제가 제기되며, 제품으로서의 풍부한 입체감이 없는 것이또한 결점이다.As such, the decorative film for glass using a PVC film has to go through several processes such as printing the film → lamination of other PVC films for protecting the printed surface → bonding the PET film under high temperature → whole embossing treatment under high temperature. It is also a drawback that the plant is complex and therefore raises productivity problems, and lack of a rich three-dimensional feel as a product.

위에서 언급한 것과 같이 접착제를 사용한 유리용 인쇄 장식필름이나 접착제를 사용하지 않지만 제조공정이 복잡한 유리용 PVC 장식필름은 모두가 그 나름대로 장점이 있으나 또한 단점도 많이 가지고 있다.As mentioned above, glass PVC decorative films using adhesives or glass PVC decorative films which do not use adhesives are complicated, but all have advantages in their own way, but also have many disadvantages.

상기의 제품 중 단점을 보완하면서 유리 면에 접착제 없이 부착 시 입체감이 풍부한 새로운 개념의 유리용 레이스(이하 '윈도우 레이스'라 한다) 제품이 외국에서 소개되고 있는데 이는 페이스트(Paste) PVC를 이용한 캐스팅(Casting) 제품으로 이것은 일종의 PVC벽지 생산과 같은 개념의 공정을 거쳐 제품을 만든다. 즉, 이동되는 벨트 콘베이어(Belt Conveyer)를 따라서 PET 필름 또는 이형지(Release Paper)를 이동시키면서 졸(Sol) 상태(페이스트 PVC+디옥틸프탈레이트+첨가제)의 PVC를 벽지 생산방식과 같은 인쇄방식으로 레이스를 성형시킨 후 200 ℃ 전후의 열처리에 의해서 겔(Gel)화시키는 캐스팅 제품으로 이후에는 필요에 따라 인쇄공정을 다시 거치게 된다.Complementing the shortcomings of the above products, a new concept of glass lace (hereinafter referred to as 'window lace'), which is rich in three-dimensional effect when attached to the glass surface without adhesive, is introduced from abroad, which is cast using paste PVC ( Casting) It is a product made through the same concept process as the production of PVC wallpaper. In other words, while moving the PET film or release paper along the belt conveyor, the PVC in sol (paste PVC + dioctylphthalate + additive) is laced in the same way as the wallpaper production method. After molding, the casting product is gelized by heat treatment at about 200 ° C. Afterwards, the printing process is performed again as necessary.

이 제품은 레이스를 접착제 없이 유리 면에 붙이는 윈도우 레이스라는 새로운 개념을 도입하여 풍부한 입체감을 가지는 등 장점은 있으나 결점으로는 유리용 PET 장식필름이나 PVC 장식필름처럼 투명한 제품을 만들 수 없고 단지 불투명에 의한 은폐력으로 유리 면을 가릴 수 있어 투명용도에 따른 미적 감각은 부여할 수 없고, 또 레이스의 개념을 이용한 간단한 제품을 만드는데 많은 시설(예를 들면 벨트 콘베이어 시설을 이용한 PET 필름 위에 인쇄방식의 부분 코팅 설비, 200 ℃ 이상 유지되는 고온의 챔버 등)을 필요로 하게 된다.This product has the advantage of introducing a new concept of window lace that glues the lace to the glass surface without adhesive, but it has the advantages of rich three-dimensional effect, but the disadvantage is that it cannot make transparent products like PET decorative film or PVC decorative film for glass. Covering the glass surface with concealment force, it cannot give aesthetic sense according to the transparent use, and many facilities to make simple products using the concept of lace (for example, partial coating equipment of printing method on PET film using belt conveyor facility) , A high temperature chamber maintained at 200 ° C. or higher).

이에, 본 발명자는 상기와 같은 문제점을 해결하기 위해 원료로 폴리비닐클로라이드 또는 폴리올레핀계 수지를 투입 후 일정 온도로 유지되는 금형에서 무늬를 형성시킨 후 바로 금형에서 투명 폴리에스테르 필름 또는 전사용 폴리에스테르 필름을 프레스 롤로 압착시켜 유리장식용 필름을 제조하면 폴리에스테르 필름의 압착에 의해 성형된 무늬 반대면(유리부착면)에 폴리에스테르 필름의 에나넬(enamel) 면이 전이되어 접착제 없이도 유리 위에 부착이 가능함을 알게 되어 본 발명을 완성하였다.Thus, the present inventors form a pattern in a mold maintained at a constant temperature after the addition of polyvinyl chloride or polyolefin resin as a raw material in order to solve the above problems, a transparent polyester film or a transfer polyester film in the mold immediately after After pressing the film with a press roll to produce a glass decorative film, the enamel side of the polyester film is transferred to the opposite surface (glass adhesion side) formed by pressing the polyester film, so that it can be attached onto the glass without adhesive. The present invention has been completed.

따라서, 본 발명은 접착제를 사용하지 않으면서 유리에 부착이 가능하며 간단한 공정으로 필름을 제조할 수 있는 유리장식용 필름 및 그 제조방법을 제공하는데 그 목적이 있다.Accordingly, an object of the present invention is to provide a glass decorative film and a method of manufacturing the same, which can be attached to glass without using an adhesive and can produce a film in a simple process.

도 1은 본 발명에 따른 유리장식용 필름을 제조하기 위한 생산라인의 일례를 나타낸 것이다.1 shows an example of a production line for producing a glass decorative film according to the present invention.

도 2는 본 발명에 따른 유리장식용 필름의 단면도를 나타낸 것이다.Figure 2 shows a cross-sectional view of the glass decorative film according to the present invention.

본 발명은 무늬가 형성된 폴리비닐클로라이드 또는 폴리올레핀계 수지층과, 그 수지층 표면에 열압착된 투명 폴리에스테르 필름 또는 전사용 폴리에스테르 필름의 에나멜층, 그리고 그 폴리에스테르 필름으로 이루어진 에나멜층 표면에 부착된 이형용 보호필름층으로 구성된 유리장식용 필름을 그 특징으로 한다.The present invention adheres to a patterned polyvinyl chloride or polyolefin resin layer, an enamel layer of a transparent polyester film or a transfer polyester film thermocompression-bonded to the resin layer surface, and an enamel layer surface comprising the polyester film. It is characterized by a glass decorative film composed of a release protective film layer.

이와같은 본 발명을 더욱 상세히 설명하면 다음과 같다.Referring to the present invention in more detail as follows.

본 발명은 접착제를 사용하지 않으면서 유리에 부착이 가능하며 간단한 공정으로 필름을 제조할 수 있는 유리장식용 필름 및 그 제조방법에 관한 것으로, 유리장식용 필름은 도 2에 나타난 바와 같이 무늬가 형성된 폴리비닐클로라이드 또는 폴리올레핀계 수지층과, 그 수지층 표면에 열압착된 투명 폴리에스테르 필름 또는 전사용 폴리에스테르 필름의 에나멜층, 그리고 그 폴리에스테르 필름으로 이루어진 에나멜층 표면에 부착된 이형용 보호필름층으로 구성되어 있다.The present invention relates to a glass decorative film that can be attached to glass without using an adhesive and to produce a film in a simple process, and a method for manufacturing the glass decorative film, as shown in Figure 2 polyvinyl formed with a pattern It consists of a chloride or polyolefin resin layer, an enamel layer of a transparent polyester film or a transfer polyester film thermocompression-bonded to the resin layer surface, and a protective film layer for release release adhered to the enamel layer surface which consists of this polyester film. have.

그리고, 상기 유리장식용 필름은 윈도우 레이스(Window Lace) 또는 장식 필름(Decoration Film)을 포함한다.In addition, the glass decorative film includes a window lace or a decoration film.

상기와 같은 유리장식용 필름을 제조하기 위한 방법을 상세히 설명하면 다음과 같다.Referring to the method for producing a glass decorative film as described above in detail.

먼저, 원료로 폴리비닐클로라이드(PVC) 컴파운드(compound)를 압출기에 넣고, 일반 PVC 레이스 생산시의 공정조건처럼 140 ∼ 170 ℃까지로 예열 과정(압출기 Screw 공정)과 180 ∼ 200 ℃로 유지되는 T-다이 공정을 거치면서 컴파운드가 흐를 수 있을 정도까지 점도가 떨어진 PVC 원료를 회전되고 있는 연속공정의 금형 위로 압출시키면서 닥터 나이프(Doctor Knife)로 금형의 무늬대로 PVC를 성형시켜 수지층을 형성시킨다. 이때, 회전되는 금형의 온도를 50 ∼ 110 ℃로 유지시키면 금형 무늬 위에 성형된 PVC의 온도가 80 ∼ 90 ℃ 정도 유지되기 때문에 이때 PET 필름을 금형에 붙이면서 프레스 롤로 압착하면 PET 필름과 온도가 높은 PVC 성형품이 접착되면서 계속 PET 필름의 장력(Tension)에 의해서 PVC 성형품이 금형으로부터 PET 필름 위에 늘어남이 없이 안정된 금형의 치수를 유지하면서 박리된다. 상기 PET 필름은 투명 PET 필름 또는 다양한 문양으로 인쇄한 전사용 PET 필름을사용할 수 있다. 이때, 전사용 PET 필름을 사용하면 복잡한 인쇄처리공정을 거치지 않아도 간단히 미려한 인쇄효과를 낼 수 있다.First, polyvinyl chloride (PVC) compound is put into the extruder as a raw material, and preheating process (extruder screw process) up to 140 ~ 170 ℃ and T-maintained at 180 ~ 200 ℃ as the process conditions in general PVC lace production -The resin material is formed by molding PVC according to the pattern of the mold with Doctor Knife while extruding the PVC raw material whose viscosity is low enough to allow the compound to flow through the die process. At this time, if the temperature of the rotating mold is maintained at 50 ~ 110 ℃ temperature of the PVC formed on the mold pattern is maintained at 80 ~ 90 ℃ about this time, if the PET film is pressed to the mold with a press roll while pressing the PET film and high temperature PVC As the molded article is adhered, the PVC molded article is peeled off while maintaining a stable mold dimension without stretching the PET molded article from the mold onto the PET film. The PET film may be a transparent PET film or a transfer PET film printed in various patterns. At this time, using the transfer PET film can produce a beautiful printing effect simply without going through a complicated print processing process.

이후 자연대기 냉각 과정을 거치면 제품이 완성된다. 이때 필요에 따라 부분인쇄 또는 금박지, 은박지 등 전사지를 이용한 인쇄공정을 거쳐 미적 감각이 부여된 부가가치가 높은 유리용 장식필름을 제조할 수도 있다(도 1 참조).After the natural air cooling process, the product is completed. In this case, a high value-added glass decorative film given aesthetics may be manufactured through a printing process using partial printing or transfer paper such as gold foil or silver foil as needed (see FIG. 1).

즉, 본 발명은 압출방식에 의해 유리장식용 필름을 제조하는 데 있어서, 원료로 폴리비닐클로라이드 투입 후 50 ∼ 110 ℃ 온도로 유지되는 금형에서 무늬를 형성시킨 후 바로 금형에서 투명 폴리에스테르 필름 또는 전사용 폴리에스테르 필름을 프레스 롤로 압착 접합시켜 에나멜층을 형성시킴으로써, PET 필름의 압착에 의해서 성형된 무늬의 반대면에 PET 필름의 에나멜 면이 전이되고 따라서 접착제 없이 유리 위에 부착이 가능하다. 이때, 온도 범위가 50 ℃ 미만이면 PET 필름과의 접착이 어려우며, 110 ℃를 초과하면 성형된 원료와 금형과의 접착력이 강해서 금형에서 성형품의 박리가 어려운 문제가 있다.That is, the present invention in the manufacture of a glass decorative film by the extrusion method, after forming a pattern in a mold maintained at a temperature of 50 ~ 110 ℃ after polyvinyl chloride as a raw material for forming a transparent polyester film or transfer in the mold By press bonding the polyester film with a press roll to form an enamel layer, the enamel side of the PET film is transferred to the opposite side of the pattern formed by the crimping of the PET film, and thus it is possible to adhere onto the glass without adhesive. At this time, when the temperature range is less than 50 ℃ it is difficult to bond with the PET film, if it exceeds 110 ℃ there is a problem that the peeling of the molded product in the mold is difficult because the adhesive strength between the molded raw material and the mold is strong.

본 발명의 유리장식용 필름을 제조하기 위한 또 다른 방법은 다음과 같다.Another method for producing a glass decorative film of the present invention is as follows.

압출방식에 의해 유리장식용 필름을 제조하는 데 있어서, 압출방식 생산공정에 의한 완성된 폴리비닐클로라이드 레이스를 150 ∼ 200 ℃로 가열한 후 투명 폴리에스테르 필름 또는 전사용 폴리에스테르 필름을 프레스 롤로 압착 접합시켜 유리장식용 필름을 제조한다.In manufacturing the glass decorative film by the extrusion method, the finished polyvinyl chloride lace by the extrusion method production process is heated to 150 ~ 200 ℃ and then the transparent polyester film or the transfer polyester film by compression bonding with a press roll A glass decorative film is prepared.

압출방식 생산공정에 의한 폴리비닐클로라이드 레이스의 통상적 제조방법을간단히 설명하면 다음과 같다. 즉 선택된 금형을 Set-up한 후 원료인 PVC 컴파운드를 140 ∼ 170 ℃ 정도로 유지되는 압출기 스크류 공정 →약 200 ℃로 유지되는 T-다이 공정 →40 ∼ 70 ℃로 유지되는 금형 위에 압출 →닥터 나이프에 의한 금형 문양대로 PVC의 성형 →성형품의 금형으로부터 분리 →냉각공정을 거쳐 PVC 레이스를 얻는다.Brief description of the conventional production method of polyvinyl chloride lace by the extrusion production process is as follows. In other words, after setting up the selected mold, the extruder screw process to keep the PVC compound as 140 ~ 170 ℃ → T-die process maintained at about 200 ℃ → Extrusion on the mold maintained at 40 ~ 70 ℃ PVC lace is obtained by molding → separating from molded product mold → cooling process according to mold pattern.

본 발명은 이러한 레이스 제조공정을 거친 PVC 레이스를 레이스 표면이 열에 의해 녹을 수 있도록 150 ∼ 200 ℃로 가열한 후 투명 폴리에스테르 필름 또는 전사용 폴리에스테르 필름을 프레스 롤로 압착시켜 접합시켜 유리장식용 필름, 즉 윈도우 레이스 또는 장식 필름을 제조한다. 이때, 온도 범위가 150 ℃ 미만이면 PET 필름과의 접착이 어려우며, 200 ℃를 초과하면 성형된 원료와 PET 필름과의 접착력이 강해서 PET 필름과 성형품의 박리가 어려운 문제가 있다.The present invention is heated to 150 to 200 ℃ so that the lace surface is melted by heat after the lace manufacturing process, the transparent polyester film or the transfer polyester film is pressed with a press roll to bond the glass decorative film, that is, Manufacture window lace or decorative film. At this time, when the temperature range is less than 150 ℃ it is difficult to bond with the PET film, if it exceeds 200 ℃ there is a problem that the peeling of the PET film and the molded article is difficult because the adhesive strength between the molded raw material and the PET film is strong.

상기와 같이, 본 발명은 평상시 압출방식에 의한 PVC 레이스를 생산하다가 필요시 간단한 PET 필름 압착공정을 거치면 윈도우 레이스를 생산할 수 있다.As described above, the present invention can produce a window lace through a simple PET film compression process when necessary to produce a PVC lace by the usual extrusion method.

본 발명의 유리장식용 필름을 제조하기 위한 또 다른 방법은 다음과 같다.Another method for producing a glass decorative film of the present invention is as follows.

원료로 폴리올레핀계 수지를 압출기에 투입 →140 ∼ 160 ℃로 유지되는 스크류 예열 공정 →170 ∼ 180 ℃로 유지되는 티-다이 공정 →50 ∼ 80 ℃로 유지되는 금형 위에 원료수지의 압출 →닥터 나이프에 의한 금형 무늬 성형 →금형에서 PET 필름의 압착 →자연냉각 공정을 거쳐 유리장식용 필름을 제조한다.As a raw material, polyolefin resin is introduced into the extruder → Screw preheating process maintained at 140 to 160 ° C. T-die process maintained at 170 to 180 ° C. Extrusion of raw material resin onto mold maintained at 50 to 80 ° C. to doctor knife Molded pattern by molding → compression of PET film in the mold → natural cooling process to produce a glass decorative film.

즉, 본 발명은 압출방식에 의해 유리장식용 필름을 제조하는 데 있어서, 원료로 폴리올레핀계 수지를 투입 후 50 ∼ 80 ℃ 온도로 유지되는 금형에서 무늬를 형성시킨 후 바로 금형에서 투명 폴리에스테르 필름 또는 전사용 폴리에스테르 필름을 프레스 롤로 압착시켜 접합시킴으로써, PET 필름의 압착에 의해서 성형된 무늬의 반대면에 PET 필름의 에나멜 면이 전이되고 따라서 접착제 없이 유리 위에 부착이 가능하다.That is, the present invention in the manufacture of a glass decorative film by the extrusion method, after forming a pattern in a mold maintained at a temperature of 50 to 80 ℃ after adding the polyolefin-based resin as a raw material, a transparent polyester film or a front in the mold By bonding the used polyester film with a press roll and bonding, the enamel side of the PET film is transferred to the opposite side of the pattern formed by the pressing of the PET film, and thus it is possible to adhere onto the glass without adhesive.

유리장식용 필름의 원료로 PVC가 사용되고 있으나, 이러한 PVC는 세계적으로 공해문제를 일으키는 원료로 그 사용에 규제가 가해지므로 본 발명은 상기 PVC를 대체할 수 있는 원료로 폴리올레핀계 수지를 사용하여 유리장식용 필름을 제조하였다. 상기 폴리올레핀계 수지는 에틸렌 비닐 아세테이트(EVA), 스티렌 부타디엔 스티렌(SBS) 및 에틸렌 프로필렌 고무(EPR) 이루어진 그룹에서 선택 사용할 수 있으며, 바람직하게는 에틸렌 비닐 아세테이트, 스티렌 부타디엔 스티렌 및 에틸렌 프로필렌 고무가 6:2:2의 혼합비로 혼합된 것을 사용하는 것이 좋다.PVC is used as a raw material of the glass decorative film, but the PVC is a raw material causing pollution problems in the world, and thus the present invention regulates the use of the glass decorative film using polyolefin resin as a raw material to replace the PVC. Was prepared. The polyolefin resin may be selected from the group consisting of ethylene vinyl acetate (EVA), styrene butadiene styrene (SBS) and ethylene propylene rubber (EPR), preferably ethylene vinyl acetate, styrene butadiene styrene and ethylene propylene rubber 6: It is better to use a mixture in a 2: 2 mixing ratio.

이와같이 폴리올레핀계 수지를 사용하여 유리장식용 필름을 제조하는 방법은 상기 PVC를 사용하여 제조하는 방법과 유사하나 회전되는 금형의 온도를 50 ∼ 80 ℃로 유지시키고 여기에 투명 폴리에스테르 필름 또는 전사용 폴리에스테르 필름을 프레스 롤로 압착 접합시켜 유리장식용 필름을 제조하는데 그 특징이 있다. 이때, 온도 범위가 50 ℃ 미만이면 PET 필름과의 접착이 어려우며, 80 ℃를 초과하면 성형된 원료와 금형과의 접착력이 강해서 금형에서 성형품의 박리가 어려운 문제가 있다.As described above, a method of manufacturing a glass decorative film using polyolefin resin is similar to the method of manufacturing using PVC, but the temperature of the rotating mold is maintained at 50 to 80 ° C., and the transparent polyester film or the transfer polyester is added thereto. The film is press-bonded with a press roll to produce a glass decorative film. At this time, when the temperature range is less than 50 ℃ it is difficult to bond with the PET film, if it exceeds 80 ℃ there is a problem that the peeling of the molded product in the mold is difficult because the adhesion between the molded raw material and the mold is strong.

본 발명의 유리장식용 필름을 제조하기 위한 또 다른 방법은 다음과 같다.Another method for producing a glass decorative film of the present invention is as follows.

압출방식에 의해 유리장식용 필름을 제조하는 데 있어서, 압출방식 생산공정에 의한 완성된 폴리올레핀계 수지 레이스를 레이스 표면이 녹을 수 있도록 150 ∼ 200 ℃로 가열한 후 투명 폴리에스테르 필름 또는 전사용 폴리에스테르 필름을 프레스 롤로 압착 접합시켜 유리장식용 필름을 제조한다.In manufacturing the glass decorative film by the extrusion method, the finished polyolefin resin lace by the extrusion method production process is heated to 150 ~ 200 ℃ so that the race surface melts, then a transparent polyester film or a transfer polyester film Was press-bonded with a press roll to prepare a glass decorative film.

압출방식 생산공정에 의한 폴리올레핀계 레이스는 통상적으로 사용하는 방법에 따라 제조된 완성품을 사용한 것으로, 그 제조방법을 간단히 설명하면 다음과 같다. 폴리올레핀계 수지를 압출기에 공급한 후 140 ∼ 160 ℃ 예열공정 →170 ∼ 180 ℃ 의 T-다이 공정 →40 ∼ 60 ℃로 유지되는 금형 위로 압출 →닥터 나이프에 의한 성형 →성형품의 유지되는 금형으로부터 분리 →냉각공정을 거쳐 폴리올레핀계 수지 레이스를 얻는다.The polyolefin-based lace by the extrusion method production process is to use the finished product prepared according to the conventional method, the production method briefly described as follows. After supplying polyolefin resin to the extruder, extrude 140 ~ 160 ° C → T-die process of 170 ~ 180 ° C → Extrude to mold maintained at 40 ~ 60 ° C → Molding by doctor knife → Separation from retained mold of molded product → a polyolefin resin lace is obtained through a cooling process.

본 발명은 이러한 폴리올레핀계 수지 레이스를 150 ∼ 200 ℃로 가열한 후 투명 폴리에스테르 필름 또는 전사용 폴리에스테르 필름을 프레스 롤로 압착시켜 접합시켜 유리장식용 필름, 즉 윈도우 레이스 또는 장식 필름을 제조한다. 이때, 온도 범위가 150 ℃ 미만이면 PET 필름과의 접착이 어려우며, 200 ℃를 초과하면 성형된 원료와 PET 필름과의 접착력이 강해서 PET 필름과 성형품의 박리가 어려운 문제가 있다.The present invention is to heat the polyolefin resin lace to 150 ~ 200 ℃ and then bonded by bonding a transparent polyester film or a polyester film for transfer using a press roll to produce a glass decorative film, that is, a window lace or decorative film. At this time, when the temperature range is less than 150 ℃ it is difficult to bond with the PET film, if it exceeds 200 ℃ there is a problem that the peeling of the PET film and the molded article is difficult because the adhesive strength between the molded raw material and the PET film is strong.

상기와 같이, 본 발명은 평상시 압출방식에 의한 폴리올레핀계 수지 레이스를 생산하다가 필요시 간단한 PET 필름 압착공정을 거치면 윈도우 레이스를 생산할 수 있다.As described above, the present invention can produce a window lace through a simple PET film pressing process when the polyolefin-based resin lace is produced by the usual extrusion method.

또한, 필요에 따라서는 접합공정 후에 레이스 표면을 부분인쇄 하거나 PET전사 필름으로 전사시켜 인쇄효과를 얻을 수 있다.In addition, if necessary, after printing, the lace surface may be partially printed or transferred to a PET transfer film to obtain a printing effect.

본 발명은 상기와 같은 방법으로 제조한 폴리비닐클로라이드 또는 폴리올레핀계 수지에 무늬를 형성시키고 그 반대표면에 투명 폴리에스테르 필름 또는 전사용 폴리에스테르 필름을 프레스 롤로 압착시켜 접합시킨 유리장식용 필름을 포함한다. 상기 유리장식용 필름은 윈도우 레이스(Window Lace) 또는 장식 필름(Decoration Film)을 포함한다.The present invention includes a glass decorative film formed by forming a pattern on the polyvinyl chloride or polyolefin-based resin prepared in the above manner and bonding the transparent polyester film or the transfer polyester film to the opposite surface by pressing with a press roll. The glass decorative film includes a window lace or a decoration film.

상술한 바와 같이, 본 발명에 따른 유리장식용 필름은 접착제를 사용하지 않으면서 유리용 장식필름으로부터 캐스팅 방식에 의한 윈도우 레이스까지의 여러 종류의 제품을 간단히 금형만 바꾸어 가면서 같은 기계로 간단히 만들 수 있는 장점을 가지고 있다.As described above, the glass decorative film according to the present invention has the advantage that can easily be made with the same machine by simply changing the mold of various kinds of products from the decorative film for glass to the window lace by the casting method without using an adhesive Have

또 PVC 수지나 EVA를 중심으로 한 폴리올레핀계 수지 등 여러 가지 원료를 필요에 따라 바꾸어 가면서 같은 기계로 제조할 수 있는 장점도 있다.In addition, there is an advantage that can be produced by the same machine while changing a variety of raw materials, such as polyolefin resins, mainly PVC resin and EVA.

Claims (8)

무늬가 형성된 폴리비닐클로라이드 또는 폴리올레핀계 수지층과, 그 수지층 표면에 열압착된 투명 폴리에스테르 필름 또는 전사용 폴리에스테르 필름의 에나멜층, 그리고 그 폴리에스테르 필름으로 이루어진 에나멜층 표면에 부착된 이형용 보호필름층으로 구성된 것을 특징으로 하는 유리장식용 필름.Release protection adhering to the enamel layer surface which consists of a polyvinyl chloride or polyolefin resin layer in which the pattern was formed, the transparent polyester film or the transfer polyester film thermocompression-bonded to the resin layer surface, and the polyester film Glass decorative film comprising a film layer. 제 1 항에 있어서, 상기 유리장식용 필름은 윈도우 레이스(Window Lace) 또는 장식 필름(Decoration Film)인 것을 특징으로 하는 유리장식용 필름.The glass decorative film of claim 1, wherein the glass decorative film is a window lace or a decoration film. 압출방식에 의해 유리장식용 필름을 제조하는 데 있어서, 원료로 폴리비닐클로라이드 투입 후 50 ∼ 110 ℃ 온도로 유지되는 금형에서 무늬를 형성시킨 후 바로 금형에서 투명 폴리에스테르 필름 또는 전사용 폴리에스테르 필름을 프레스 롤로 압착시켜 접합시킨 것을 특징으로 하는 유리장식용 필름의 제조방법.In manufacturing a glass decorative film by extrusion method, after forming polyvinyl chloride as a raw material, a pattern is formed in a mold maintained at a temperature of 50 to 110 ° C., and then a transparent polyester film or a transfer polyester film is pressed from the mold. The manufacturing method of the glass decoration film characterized by crimping and bonding with a roll. 압출방식에 의해 유리장식용 필름을 제조하는 데 있어서, 압출방식 생산공정에 의한 완성된 폴리비닐클로라이드 레이스를 150 ∼ 200 ℃로 가열한 후 투명 폴리에스테르 필름 또는 전사용 폴리에스테르 필름을 프레스 롤로 압착시켜 접합시킨 것을 특징으로 하는 유리장식용 필름의 제조방법.In manufacturing the glass decorative film by the extrusion method, the completed polyvinyl chloride lace by the extrusion method production process is heated to 150 ~ 200 ℃ and then bonded by pressing a transparent polyester film or a transfer polyester film with a press roll Method for producing a glass decorative film characterized in that. 압출방식에 의해 유리장식용 필름을 제조하는 데 있어서, 원료로 폴리올레핀계 수지를 투입 후 50 ∼ 80 ℃ 온도로 유지되는 금형에서 무늬를 형성시킨 후 바로 금형에서 투명 폴리에스테르 필름 또는 전사용 폴리에스테르 필름을 프레스 롤로 압착시켜 접합시킨 것을 특징으로 하는 유리장식용 필름의 제조방법.In manufacturing a glass decorative film by extrusion method, after the polyolefin-based resin is added as a raw material, a pattern is formed in a mold maintained at a temperature of 50 to 80 ° C., and then a transparent polyester film or a transfer polyester film is immediately removed from the mold. The manufacturing method of the glass decoration film characterized by crimping | bonding by pressing roll. 제 5 항에 있어서, 상기 폴리올레핀계 수지는 에틸렌 비닐 아세테이트, 스티렌 부타디엔 스티렌 및 에틸렌 프로필렌 고무로 이루어진 그룹에서 선택되는 것을 특징으로 하는 유리장식용 필름의 제조방법.The method of claim 5, wherein the polyolefin resin is selected from the group consisting of ethylene vinyl acetate, styrene butadiene styrene, and ethylene propylene rubber. 제 5 항 또는 제 6 항에 있어서, 상기 폴리올레핀계 수지는 에틸렌 비닐 아세테이트, 스티렌 부타디엔 스티렌 및 에틸렌 프로필렌 고무가 6:2:2의 혼합비로 혼합된 것을 특징으로 하는 유리장식용 필름의 제조방법.7. The method of claim 5 or 6, wherein the polyolefin resin is ethylene vinyl acetate, styrene butadiene styrene, and ethylene propylene rubber mixed at a mixing ratio of 6: 2: 2. 압출방식에 의해 유리장식용 필름을 제조하는 데 있어서, 압출방식 생산공정에 의한 완성된 폴리올레핀계 수지 레이스를 150 ∼ 200 ℃로 가열한 후 투명 폴리에스테르 필름 또는 전사용 폴리에스테르 필름을 프레스 롤로 압착시켜 접합시킨 것을 특징으로 하는 유리장식용 필름의 제조방법.In manufacturing the glass decorative film by the extrusion method, the completed polyolefin resin lace by the extrusion method production process is heated to 150 ~ 200 ℃ and then bonded by pressing a transparent polyester film or a transfer polyester film with a press roll Method for producing a glass decorative film characterized in that.
KR1020030044454A 2003-07-02 2003-07-02 Glass decoration film and preparing method thereof KR100620610B1 (en)