KR200413522Y1 - Flooring sheet wherein waterproof agent is coated on its side - Google Patents

Flooring sheet wherein waterproof agent is coated on its side Download PDF

Info

Publication number
KR200413522Y1
KR200413522Y1 KR2020060001110U KR20060001110U KR200413522Y1 KR 200413522 Y1 KR200413522 Y1 KR 200413522Y1 KR 2020060001110 U KR2020060001110 U KR 2020060001110U KR 20060001110 U KR20060001110 U KR 20060001110U KR 200413522 Y1 KR200413522 Y1 KR 200413522Y1
Authority
KR
South Korea
Prior art keywords
flooring sheet
sheet
veneer
flooring
present
Prior art date
Application number
KR2020060001110U
Other languages
Korean (ko)
Inventor
이종배
Original Assignee
크레신산업 주식회사
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 크레신산업 주식회사 filed Critical 크레신산업 주식회사
Priority to KR2020060001110U priority Critical patent/KR200413522Y1/en
Application granted granted Critical
Publication of KR200413522Y1 publication Critical patent/KR200413522Y1/en

Abstract

본 고안에서는 합성수지층 및 무늬목을 포함하는 바닥재 시트의 통상의 적층 구성을 구비하는 바닥재 시트에 있어서, 상기 바닥재 시트의 측면에 방수제의 도포층이 형성된 것을 특징으로 하는 바닥재 시트를 제공한다. 본 고안에 따르면 무늬목 및 염화비닐수지나 폴리올레핀계 수지 등의 합성수지층을 포함하는 바닥재 시트에 있어서, 방수제 측면부로부터의 수분 침투와 이에 의한 무늬목 도관을 통한 수분 침투 및 상기 수분 침투에 따른 무늬목 변색의 문제점을 방지할 수 있다. 나아가, 본 고안에 따르면 치수 안정성을 달성하고 강도를 높이면서도 수분 침투 공간을 제공하지 않으므로 무늬목 변색을 더욱 효과적으로 방지할 수 있다. 더욱이 본 고안에 따르면 종래와 같이 왁스 등 보호재를 사용하지 않고서도 내마모성을 개선하여 표면 스크래치성을 향상하여 장기간 타일을 깨끗한 상태로 보관할 수 있다. 또한, 본 고안에 따르면 제품 시공시 시공비를 절감할 수 있고 시공 속도가 빠르게 된다. In the present invention, a flooring sheet having a conventional laminated structure of a flooring sheet including a synthetic resin layer and veneer, provides a flooring sheet characterized in that the coating layer of the waterproofing agent is formed on the side of the flooring sheet. According to the present invention, in the flooring sheet including veneer and synthetic resin layer such as polyvinyl chloride resin or polyolefin resin, moisture infiltration from the side surface of the waterproofing agent and water infiltration through the veneer conduit and the problem of discoloration of the veneer due to the moisture infiltration Can be prevented. Furthermore, according to the present invention, it is possible to more effectively prevent veneer discoloration because it does not provide a space for moisture penetration while achieving dimensional stability and increasing strength. Furthermore, according to the present invention, it is possible to keep the tiles in a clean state for a long time by improving the wear resistance by improving the wear resistance without using a protective material such as wax as in the prior art. In addition, according to the present invention can reduce the construction cost when constructing the product and the construction speed is faster.

바닥재시트, 측면, 방수제, 무늬목, 합성수지층, 도관, 충전, 유리섬유매쉬 Flooring sheet, side, waterproofing, veneer, synthetic resin layer, conduit, filling, glass fiber mesh

Description

방수제가 측면 도포된 바닥재 시트{FLOORING SHEET WHEREIN WATERPROOF AGENT IS COATED ON ITS SIDE}Flooring sheet coated with waterproofing agent {FLOORING SHEET WHEREIN WATERPROOF AGENT IS COATED ON ITS SIDE}

도 1은 종래의 무늬목 바닥재 시트의 적층 구성 예와 무늬목 도관을 나타내는 개략도이다.1 is a schematic diagram showing a laminated configuration example of a conventional veneer flooring sheet and a veneer conduit.

도 2는 도 1에 도시된 바와 같은 무늬목의 실제 도관을 보여주는 확대 사진이다.FIG. 2 is an enlarged photograph showing the actual conduit of the veneer as shown in FIG. 1.

도 3은 본 고안의 제1 실시예에 따른 바닥재 시트에 있어서, 방수제의 도포층이 측면 형성된 바닥재 시트를 나타내는 개략도이다.3 is a schematic view showing a flooring sheet having a coating layer of a waterproofing agent in the flooring sheet according to the first embodiment of the present invention.

도 4는 본 고안의 제2 실시예에 따른 바닥재 시트에 있어서, 무늬목 도관을 추가로 방수제로 충전한 바닥재 시트를 나타내는 개략도이다.Figure 4 is a schematic diagram showing the flooring sheet in the flooring sheet according to a second embodiment of the present invention, the veneer conduit additionally filled with a waterproofing agent.

도 5는 본 고안의 제3 실시예에 따른 바닥재 시트에 있어서, 유리섬유매쉬를 구비하는 바닥재 시트를 나타내는 개략도이다.Figure 5 is a schematic diagram showing a flooring sheet having a glass fiber mesh in the flooring sheet according to a third embodiment of the present invention.

도 6은 본 고안의 제4 실시예에 따른 바닥재 시트에 있어서, 유리 섬유 시트를 구비하는 바닥재 시트를 나타내는 개략도이다. 6 is a schematic view showing a floor covering sheet having a glass fiber sheet in the floor covering sheet according to the fourth embodiment of the present invention.

도 7은 본 고안의 제5 실시예에 따른 바닥재 시트에 있어서, 상부 시트 상에 내마모성 코팅층이 형성된 바닥재 시트를 나타내는 개략도이다.7 is a schematic view showing a flooring sheet having a wear-resistant coating layer formed on the top sheet in the flooring sheet according to a fifth embodiment of the present invention.

도 8은 본 고안의 제6 실시예에 따른 바닥재 시트에 있어서, 바닥부에 이형 지가 부착된 것을 나타내는 측면 개략도이다.8 is a side schematic view showing that the release paper is attached to the bottom in the bottom sheet according to the sixth embodiment of the present invention.

도 9는 도 8의 바닥재 시트를 나타내는 개략적인 사시도이다.FIG. 9 is a schematic perspective view illustrating the floor covering sheet of FIG. 8. FIG.

*주요 도면 부호의 간단한 설명** Short description of the major reference marks *

1, 10 : 상부 시트 2, 20 : 합성수지층1, 10: upper sheet 2, 20: synthetic resin layer

3, 30 : 무늬목 40 : 방수제 도포층3, 30: veneer 40: waterproofing coating layer

50 : 유리섬유매쉬 51 : 매쉬50: glass fiber mesh 51: mesh

60 : 유리 섬유 시트 70 : 내마모성 코팅층60: glass fiber sheet 70: wear-resistant coating layer

80 : 점착제 90 : 이형지 80: pressure-sensitive adhesive 90: release paper

V : 도관 V' : 방수제가 충전된 도관 V: conduit V ': conduit filled with waterproofing agent

본 고안은 방수제가 측면 도포된 바닥재 시트에 관한 것이다. The present invention relates to a flooring sheet coated with a waterproofing agent.

무늬목(Veneer) 및 염화비닐수지(PVC)나 폴리올레핀계 수지 등의 합성수지가 복합된 바닥재 시트는 무늬목에 접착 수지를 도포하거나 접착 시트 등을 열 압착하는 것과 같이 접착 부재를 이용하여 무늬목과 염화비닐수지층 등의 합성수지층을 접착시킨 것으로, 일반적인 목재 마루판보다 값이 저렴하면서도 외관은 목재 마루판과 거의 유사하므로 상기 목재 마루판을 대체하여 널리 사용되고 있다. The flooring sheet with veneer and synthetic resin such as vinyl chloride resin (PVC) or polyolefin resin is mixed with veneer and vinyl chloride using an adhesive member such as applying adhesive resin to the veneer or thermocompressing the adhesive sheet. It is bonded to a synthetic resin layer such as a strata, and is cheaper than a general wooden floorboard, and since the appearance is almost similar to the wooden floorboard, it is widely used to replace the wooden floorboard.

그러나, 상기와 같은 무늬목과 합성수지의 복합 바닥재 시트는 사용시 또는 시공시 수분이 침투하는 문제점이 있고, 이에 따라 무늬목이 변색되는 문제점이 심 각하다. However, the composite flooring sheet of the veneer and synthetic resin as described above has a problem that the moisture penetrates during use or construction, thereby causing a serious problem of discoloration of the veneer.

특히, 바닥재 시트의 구성 중 무늬목에는 다수의 도관(Vessel)이 형성되어 있는데, 이와 같은 도관을 통하여 침투된 수분은 무늬목 내의 수분 함량을 높이며 도관으로부터의 배출도 어려워 무늬목을 심각하게 변색시키는 문제점이 있다. In particular, a plurality of conduits are formed in the veneer of the flooring sheet, and the moisture penetrated through the conduit increases the moisture content in the veneer and is difficult to discharge from the conduit, causing serious discoloration of the veneer. .

도 1은 종래의 무늬목 바닥재 시트의 적층 구성 예 및 무늬목 도관을 나타내는 개략도이고, 도 2는 도 1에 도시된 바와 같은 무늬목의 실제 도관을 보여주는 확대 사진이다. 1 is a schematic diagram showing a laminated configuration example of a conventional veneer flooring sheet and a veneer conduit, and FIG. 2 is an enlarged photograph showing an actual conduit of veneer as shown in FIG. 1.

도 1에 도시된 바와 같이, 종래의 바닥재 시트는 예를 들어 무늬목(3)을 중심으로 상부 시트(1)와 하부의 2층으로 적층된 염화비닐수지나 폴리올레핀계 수지의 합성수지층(2)을 구비한다. As shown in FIG. 1, the conventional flooring sheet includes, for example, a synthetic resin layer 2 of a vinyl chloride resin or a polyolefin resin laminated in two layers of an upper sheet 1 and a lower layer around a veneer 3. Equipped.

이때, 상기 무늬목(3)과 상부 시트(1) 및 하부의 합성수지층(2)은 접착 수지나 접착 시트와 같은 접착 부재를 통하여 접착되고, 상기 상부 시트(1)는 일반적으로 투명 시트 또는 표면도장 시트로서 형성된다. 나아가, 상기 합성수지층(2)의 하부에는 밸런스 시트(도시하지 않음)가 구비될 수 있다.At this time, the veneer (3) and the upper sheet (1) and the lower synthetic resin layer (2) is bonded through an adhesive member such as adhesive resin or adhesive sheet, the upper sheet (1) is generally a transparent sheet or surface coating It is formed as a sheet. Furthermore, a balance sheet (not shown) may be provided below the synthetic resin layer 2.

도 1 및 도 2에 도시된 바와 같이, 종래의 합성수지층과 무늬목을 동시에 구비하는 바닥재 시트는 수분의 침투에 따른 수명 단축의 문제점이 있었으며, 특히, 상기 무늬목(3)에 형성된 다수의 도관(V)을 통한 수분 침투성 증대 및 수분 배출성 저하 등의 문제점이 컸다.As shown in Figure 1 and 2, the flooring sheet having a conventional synthetic resin layer and veneer at the same time had a problem of shortening the life due to the penetration of moisture, in particular, a plurality of conduits (V) formed in the veneer (3) Problems such as increased moisture permeability and lowered water discharge through the).

따라서, 본 고안은 상기한 바와 문제점을 해결하기 위한 것으로, 본 고안의 목적은, 무늬목 및 염화비닐수지나 폴리올레핀계 수지 등의 합성수지층을 포함하는 바닥재 시트에 있어서, 수분의 침투 성향이 가장 현저하고 침투에 따른 악영향이 가장 큰 측면부로부터의 수분 침투의 문제점을 해결하고, 나아가, 상기 측면 수분 침투에 기인한 무늬목의 도관을 통한 수분 침투의 문제점을 해결함으로써, 무늬목 변색의 문제점을 효과적으로 방지할 수 있는 바닥재 시트를 제공하는 것이다. Therefore, the present invention is to solve the problems described above, the object of the present invention, in the flooring sheet comprising a veneer and a synthetic resin layer, such as vinyl chloride resin or polyolefin resin, the penetration of moisture is most remarkable By solving the problem of water penetration from the side portion with the greatest adverse effect of the penetration, and furthermore, by solving the problem of water penetration through the conduit of the veneer caused by the side moisture penetration, it is possible to effectively prevent the problem of discoloration of the veneer It is to provide a flooring sheet.

본 고안의 다른 목적은, 치수 안정성을 달성하고 강도를 높이면서도, 수분 침투 공간을 제공하지 않으므로 무늬목 변색을 더욱 효과적으로 방지할 수 있는 바닥재 시트를 제공하는 것이다.Another object of the present invention is to provide a flooring sheet which can more effectively prevent veneer discoloration because it does not provide a moisture penetration space while achieving dimensional stability and increasing strength.

본 고안의 또 다른 목적은, 종래와 같이 왁스 등 보호재를 사용하지 않고서도 내마모성을 개선하여 표면 스크래치성을 향상하여 장기간 타일을 깨끗한 상태로 보관할 수 있는 바닥재 시트를 제공하는 것이다.Still another object of the present invention is to provide a flooring sheet capable of storing a tile in a clean state for a long time by improving wear resistance by improving wear resistance without using a protective material such as wax as in the prior art.

본 고안의 또 다른 목적은, 제품 시공시 시공비를 절감할 수 있고 시공 속도가 빠른 바닥재 시트를 제공하는 것이다.Another object of the present invention is to provide a flooring sheet that can reduce the construction cost during construction of the product and the construction speed is high.

상기한 바와 같은 목적을 달성하기 위하여, 본 고안에서는 합성수지층 및 무늬목을 포함하는 바닥재 시트의 통상의 적층 구성을 구비하는 바닥재 시트에 있어서, 상기 바닥재 시트의 측면 특히 측면 전체에 방수제 도포층을 형성한 것을 특징으로 하는 바닥재 시트를 제공한다.In order to achieve the above object, in the present invention, in the flooring sheet having a conventional laminated structure of the flooring sheet comprising a synthetic resin layer and veneer, forming a waterproofing coating layer on the side, in particular the entire side of the flooring sheet It provides a flooring sheet characterized in that.

그리고 상기 바닥재 시트는 상기 방수제 도포층의 두께가 균일한 것이 바람직하다.In addition, the flooring sheet is preferably a uniform thickness of the waterproofing agent coating layer.

그리고 상기 바닥재 시트는 상기 무늬목의 도관의 일부 또는 전부가 방수제로 충전되는 것이 바람직하다.And the flooring sheet is preferably part or all of the conduit of the veneer is filled with a waterproofing agent.

그리고 상기 바닥재 시트는 상부 시트; 상기 상부 시트 하부의 무늬목; 상기 무늬목 하부의 제1층 및 제2층으로 적층된 합성수지층;을 포함하는 바닥재 시트로서, 상기 무늬목의 도관의 일부 또는 전부가 방수제로 충전되는 것이 바람직하다.And the bottom sheet is a top sheet; Veneer under the upper sheet; As a flooring sheet comprising a, it is preferable that part or all of the conduit of the veneer is filled with a waterproofing agent.

그리고 상기 바닥재 시트는 매쉬 형상의 유리섬유가 상기 제1층 및 제2층의 합성수지층 사이에 융착되는 것이 바람직하다.And it is preferable that the flooring sheet is fused to a glass fiber of the mesh shape between the synthetic resin layer of the first layer and the second layer.

그리고 상기 바닥재 시트는 유리 섬유 시트가 상기 무늬목 및 상기 제1층 합성수지층 사이에 개재되는 것이 바람직하다.And the flooring sheet is preferably a glass fiber sheet is interposed between the veneer and the first layer synthetic resin layer.

그리고 상기 바닥재 시트는 상기 상부 시트 상에 산화알루미늄의 코팅층이 형성되는 것이 바람직하다.And the bottom sheet is preferably a coating layer of aluminum oxide is formed on the top sheet.

그리고 상기 바닥재 시트는 상기 코팅층이 통상의 UV 도료를 더 포함하는 것이 바람직하다.And the flooring sheet is preferably the coating layer further comprises a conventional UV paint.

그리고 상기 바닥재 시트의 바닥부에는 점착제를 이용하여 이형지가 부착된 것이 바람직하다.And it is preferable that the release paper is attached to the bottom of the flooring sheet using an adhesive.

이하, 본 고안에 따른 방수제가 측면 도포된 바닥재 시트에 대하여 상술한다.Hereinafter, the flooring sheet coated with the waterproofing agent according to the present invention will be described in detail.

도 3은 본 고안의 제1 실시예에 따른 바닥재 시트에 있어서, 방수제의 도포층이 측면 형성된 바닥재 시트를 나타내는 측면 개략도이다. 3 is a side schematic view showing a flooring sheet having a coating layer of a waterproofing agent in the flooring sheet according to the first embodiment of the present invention.

도 3에 도시된 바와 같이, 본 고안의 일실시예에 따른 바닥재 시트는, 위로 부터 상부 시트(10), 무늬목(30), 제1층 및 제2층의 합성수지층(20)의 순서로 적층되어 있다. 그리고 상기 바닥재 시트 평면의 폭과 길이는 직사각형 형태로서 일예로 대략 폭 101mm 및 길이 914mm일 수 있고, 또는 정사각형 형태로서 일예로 대략 폭 45mm 및 길이 45mm 일 수 있다. As shown in Figure 3, the flooring sheet according to an embodiment of the present invention, laminated from the top sheet 10, veneer 30, the first and second layers of synthetic resin layer 20 in the order It is. The width and length of the flooring sheet plane may be, for example, a rectangular shape, and may be, for example, approximately 101 mm wide and 914 mm long, or may be, for example, a square shape, approximately 45 mm wide and 45 mm long.

여기서, 상기 합성수지층은 일반적으로 염화비닐수지를 사용하는 것이 보통이지만, 폴리올레핀계 수지나 기타 합성수지를 사용할 수 있다. 또한, 비록 도 3이 상부 시트(10), 무늬목(30), 제1층 및 제2층 합성수지층(20)의 순서로 적층된 바닥재 시트를 보여주지만, 본 고안이 적용되는 바닥재 시트가 반드시 위와 같은 적층 구조에 한정되지 않음은 물론이며, 합성수지층(20) 하부에 밸런스 시트를 더 포함할 수 있는 것과 같이, 본 고안이 적용되는 바닥재 시트에는 합성수지층 및 무늬목을 포함하는 바닥재 시트의 통상의 적층 구성이 모두 포함된다.Here, the synthetic resin layer is generally used vinyl chloride resin, but polyolefin resin or other synthetic resin can be used. In addition, although Figure 3 shows a flooring sheet laminated in the order of the top sheet 10, veneer 30, the first layer and the second layer of synthetic resin layer 20, the flooring sheet to which the present invention is applied is necessarily Of course, it is not limited to the same laminated structure, as can further include a balance sheet under the synthetic resin layer 20, the flooring sheet to which the subject innovation is applied is a conventional lamination of the flooring sheet comprising a synthetic resin layer and veneer All configurations are included.

본 고안에서는 특히 상기 적층 구성을 가지는 바닥재 시트의 측면에서 방수제를 측면에 도포하여 방수제 도포층(40)을 형성하도록 한다. 이와 같은 방수제 도포층(40)을 특히 측면에 형성하는 것은 수분의 침투가 가장 활발한 측면을 수분으로부터 전면적으로 차단하기 위함이다. 나아가, 본 고안에서는 두께가 매우 얇은 무늬목(30) 만에 방수제를 도포하는 경우의 공정상의 곤란성과 오히려 방수제 도포층(40)에 의하여 시트간 접합시 굴곡이 형성되기 쉬운 점을 해결하기 위하여 상기 방수제 도포층(40)을 바닥재 시트의 측면 전체에 형성하도록 한다. 더욱이, 본 고안에서는, 상기 도포층(40)의 두께를 균일하게 하도록 함으로써 굴곡 형성을 최대한 방지하므로 더욱 바람직하다. 한편, 상기 도포층(40)의 균일한 두께는 예를 들 어 5㎛로 하는 것이 바람직하며, 상기 두께를 초과하여 지나치게 두꺼워지는 경우에는 시트와 시트 간 밀착이 제대로 수행되지 않을 우려가 있다. In the present invention, in particular, the waterproofing agent is applied to the side of the flooring sheet having the laminated structure to form the waterproofing agent coating layer 40. Particularly, the waterproofing agent coating layer 40 is formed on the side to completely block the side where the penetration of moisture is most active from the moisture. Furthermore, in the present invention, in order to solve the difficulty of the process in the case of applying the waterproofing agent only to the very thin veneer 30 and the point that the bending is easily formed when bonding between sheets by the waterproofing coating layer 40, the waterproofing agent The coating layer 40 is formed on the entire side surface of the flooring sheet. Furthermore, in the present invention, it is more preferable because the thickness of the coating layer 40 is made uniform so as to prevent bending formation as much as possible. On the other hand, the uniform thickness of the coating layer 40 is preferably, for example, 5㎛, if the thickness is too thick beyond the thickness there is a fear that the adhesion between the sheet and the sheet may not be performed properly.

도 4는 본 고안의 제2 실시예에 따른 바닥재 시트에 있어서, 무늬목 도관의 전부 또는 일부를 추가로 방수제로 충전한 바닥재 시트를 나타내는 개략도이다.Figure 4 is a schematic diagram showing a flooring sheet in the flooring sheet according to a second embodiment of the present invention, the whole or part of the veneer conduit additionally filled with a waterproofing agent.

도 4에 도시된 바와 같이, 본 고안에서는 상기와 같이 측면에 방수제 도포층(40)을 형성한 상태, 즉, 측면으로부터 수분 침투를 효과적으로 차단한 상태에서, 무늬목의 도관(V)의 전부 또는 일부를 방수제로 추가 충전(V')하는 과정을 통하여 무늬목내로의 수분 침투 억제를 보장하도록 한다. 이에 의하여, 침투된 수분이 무늬목내에서 보유되는 상황이나 배출 곤란의 문제점을 원천적으로 차단할 수 있다.As shown in FIG. 4, in the present invention, in the state in which the waterproofing coating layer 40 is formed on the side as described above, that is, in a state in which water penetration is effectively blocked from the side, all or part of the conduit V of the veneer The additional charge (V ') with a waterproofing agent to ensure the inhibition of water penetration into the veneer. As a result, it is possible to fundamentally block the problem of the situation in which the infiltrated moisture is retained in the veneer or the difficulty of discharge.

도 5는 본 고안의 제3 실시예에 따른 바닥재 시트에 있어서, 유리섬유매쉬를 구비하는 바닥재 시트를 나타내는 측면 개략도이다.Figure 5 is a side schematic view showing a flooring sheet having a glass fiber mesh in the flooring sheet according to a third embodiment of the present invention.

도 5에 도시된 바와 같이, 본 고안의 제3 실시예에 따른 바닥재 시트는, 상기 제1 또는 제2 실시예에 따른 바닥재 시트에 있어서, 그 제1층 및 제2층으로 적층된 합성수지층 사이에 매쉬(51) 형태의 유리섬유인 유리섬유매쉬(50)를 개재시킨 후 열압착으로 융착시킨 것이다. 이와 같이 유리섬유매쉬를 합성수지층 사이에 융착시키는 구성에 의하면, 치수 안정성을 달성하고 강도를 높이면서도 수분 침투 공간을 제공하지 않으므로 무늬목 변색을 더욱 효과적으로 방지할 수 있다.As shown in Figure 5, the flooring sheet according to a third embodiment of the present invention, in the flooring sheet according to the first or second embodiment, between the synthetic resin layer laminated in the first layer and the second layer After interposing a glass fiber mesh 50, which is a glass fiber in the form of a mesh 51, is fused by thermocompression bonding. Thus, according to the configuration in which the glass fiber mesh is fused between the synthetic resin layer, it is possible to more effectively prevent the discoloration of the veneer because it does not provide a space for moisture penetration while achieving dimensional stability and increasing the strength.

도 6은 본 고안의 제4 실시예에 따른 바닥재 시트를 나타내는 개략도이다. 6 is a schematic view showing a flooring sheet according to a fourth embodiment of the present invention.

도 6에 도시된 바와 같이, 본 고안의 제4 실시예에 따른 바닥재 시트는 무늬목(30)과 그 하부의 제1층 합성수지층(20) 사이에 유리 섬유 시트(60)가 개재되어 치수 안정성을 달성하고 강도를 높일 수 있다. 한편, 상기 유리 섬유 시트(60)에는 접착제가 함침되어 있다. As shown in FIG. 6, in the flooring sheet according to the fourth embodiment of the present invention, a glass fiber sheet 60 is interposed between the veneer 30 and the first layer synthetic resin layer 20 thereunder, thereby improving dimensional stability. Can achieve and increase the strength. On the other hand, the glass fiber sheet 60 is impregnated with an adhesive.

도 7은 본 고안의 제5 실시예에 따른 바닥재 시트를 나타내는 개략도이다.7 is a schematic view showing a flooring sheet according to a fifth embodiment of the present invention.

도 7에 도시된 바와 같이, 본 고안의 제5 실시예에 따른 바닥재 시트는 예컨대 상기 제4 실시예에 따른 바닥재 시트의 상부 시트(10) 상에 산화알루미늄(Al2O3)의 코팅층(70) 또는 상기 산화알루미늄 및 통상의 UV 도료의 혼합물의 코팅층(70)을 형성함으로써 일반적으로 상부 시트(10)를 보호하기 위하여 사용되는 왁스 등의 보호재 사용이 없이도 월등한 내마모성을 부여하여 표면 스크래치(scratch)성을 보완하여 해당 바닥재 시트를 장기간 깨끗이 사용할 수 있도록 한다. 상기 코팅층(70)의 두께는 대략 10㎛ 정도로 형성한다.As shown in FIG. 7, the flooring sheet according to the fifth embodiment of the present invention is, for example, a coating layer of aluminum oxide (Al 2 O 3 ) 70 on the top sheet 10 of the flooring sheet according to the fourth embodiment. Or by forming a coating layer 70 of a mixture of the aluminum oxide and the conventional UV paint, giving excellent abrasion resistance without the use of a protective material such as wax, which is generally used to protect the top sheet 10. This supplements the flooring sheet so that the flooring sheet can be used cleanly for a long time. The coating layer 70 has a thickness of about 10 μm.

한편, 도 7은 특히 유리 섬유 시트를 구비하는 본 고안의 제4 실시예에 내마모성 코팅층을 형성하는 것을 도시하고 있지만, 내마모성 코티층의 형성이 상기 실시예에 한정되는 것이 아님은 물론이다.On the other hand, Figure 7 shows the formation of a wear-resistant coating layer in the fourth embodiment of the present invention, particularly provided with a glass fiber sheet, of course, the formation of the wear-resistant coating layer is not limited to the above embodiment.

도 8은 본 고안의 제6 실시예에 따른 바닥재 시트에 있어서, 하측 단부에 이형지가 도포된 것을 나타내는 측면 개략도이고, 도 9는 도 8의 바닥재 시트를 나타내는 개략적인 사시도이다.Figure 8 is a side schematic view showing that the release paper is applied to the lower end in the flooring sheet according to a sixth embodiment of the present invention, Figure 9 is a schematic perspective view showing the flooring sheet of FIG.

도 8 및 도 9에 도시된 바와 같이, 본 고안의 제6 실시예에 따른 바닥재 시트에서는 예를 들어 제5 실시예에 따른 바닥재 시트의 최하측의 바닥부, 즉, 제5 실시예의 경우 제2층 합성수지층(20)의 하면에 점착제를 도포하고 약 0.05mm 정도 의 이형지를 부착한다. 상기 이형지는 상기 바닥재 시트보다 네 변에 있어서 각각 약 5mm 정도로 큰 사이즈의 것을 부착하도록 한다. 한편, 상기 점착제로서 특히 아크릴계의 분산형 점착제를 사용하면 친환경성을 높일 수 있다.8 and 9, in the flooring sheet according to the sixth embodiment of the present invention, for example, the bottom of the bottom of the flooring sheet according to the fifth embodiment, that is, the second case in the fifth embodiment A pressure-sensitive adhesive is applied to the lower surface of the layer synthetic resin layer 20 and a release paper having a thickness of about 0.05 mm is attached. The release paper is to be attached to the size of each larger than about 5mm in four sides than the flooring sheet. On the other hand, when using the acrylic pressure-sensitive adhesive in particular as the pressure-sensitive adhesive can improve the environmental friendliness.

이와 같이 본 고안에서는 특히 바닥재 시트의 바닥부에 점착제를 도포하고 이형지를 부착하는 구성에 의하여 제품의 시공시 별도의 접착제를 사용하지 않고서도 상기 이형지를 제거함으로써 바로 마루판이나 PVC 타일 등과 같은 시공 대상 바닥에 접착할 수 있다. 따라서 상기와 같은 본 고안에 의하면 시공비 절감이 가능하고 시공 속도도 빨라지게 된다.As such, in the present invention, by applying a pressure-sensitive adhesive to the bottom of the flooring sheet and attaching the release paper, it is possible to remove the release paper without using a separate adhesive when constructing the product, such as floorboards or PVC tiles. Can be adhered to. Therefore, according to the present invention as described above it is possible to reduce the construction cost and the construction speed is also faster.

본 고안의 제6 실시예에서는 특히 본 고안의 제4 실시예를 기초로 이형지를 부착하는 것을 도시하고 있지만, 이형지 부착이 상기 제4 실시예를 반드시 전제로 하는 것이 아님은 물론이다.Although the sixth embodiment of the present invention particularly shows the attachment of the release paper based on the fourth embodiment of the present invention, it goes without saying that the release paper is not necessarily premised on the fourth embodiment.

이상에서 설명한 바와 같이, 본 고안에 따르면 무늬목 및 염화비닐수지나 폴리올레핀계 수지 등의 합성수지층을 포함하는 바닥재 시트에 있어서, 특히, 수분의 측면 침투를 차단하는 것에 의하여 무늬목의 도관으로의 연결로를 효과적으로 차단하여 수분 침투 문제를 용이하게 해결할 수 있으며, 나아가, 무늬목의 도관을 방수제로 충전시키는 것에 의하여 침투된 수분의 보유성 및 배출 곤란성의 문제를 해결할 수 있다.As described above, according to the present invention, in the flooring sheet including veneer and synthetic resin layer such as vinyl chloride resin or polyolefin resin, in particular, the path of the veneer to the conduit can be effectively prevented by blocking the side penetration of moisture. Blocking can easily solve the problem of water penetration, and furthermore, by filling the conduit of the veneer with a waterproofing agent can solve the problem of retention of water and difficulty in discharging.

나아가, 본 고안에 따르면 치수 안정성을 달성하고 강도를 높이면서도 수분 침투 공간을 제공하지 않으므로 무늬목 변색을 더욱 효과적으로 방지할 수 있다.Furthermore, according to the present invention, it is possible to more effectively prevent veneer discoloration because it does not provide a space for moisture penetration while achieving dimensional stability and increasing strength.

더욱이, 본 고안에 따르면, 종래와 같이 왁스 등 보호재를 사용하지 않고서도 내마모성을 개선하여 표면 스크래치성을 향상하여 장기간 타일을 깨끗한 상태로 보관할 수 있다.Further, according to the present invention, it is possible to keep the tiles in a clean state for a long time by improving the wear resistance by improving the wear resistance without using a protective material such as wax as in the prior art.

또한, 본 고안에 따르면, 제품 시공시 시공비를 절감할 수 있고 시공 속도가 빠르다.In addition, according to the present invention, it is possible to reduce the construction cost during the construction of the product and the construction speed is fast.

비록 본 고안이 상기 언급된 바람직한 실시예와 관련하여 설명되어졌지만, 고안의 요지와 범위로부터 벗어남이 없이 다양한 수정이나 변형을 하는 것이 가능하다. 따라서 첨부된 실용신안등록청구의 범위는 본 고안의 요지에서 속하는 이러한 수정이나 변형을 포함할 것이다. Although the present invention has been described in connection with the above-mentioned preferred embodiments, it is possible to make various modifications or variations without departing from the spirit and scope of the invention. Therefore, the scope of the utility model registration claims attached will include such modifications or variations that fall within the spirit of the present invention.

Claims (10)

합성수지층 및 무늬목을 포함하는 바닥재 시트의 통상의 적층 구성을 구비하는 바닥재 시트에 있어서, 상기 바닥재 시트의 측면에 방수제 도포층이 형성된 것을 특징으로 하는 바닥재 시트.A flooring sheet having a conventional laminated structure of a flooring sheet comprising a synthetic resin layer and veneer, wherein a floor coating sheet is formed on a side surface of the flooring sheet. 제 1 항에 있어서, 상기 바닥재 시트는, The method of claim 1, wherein the flooring sheet, 상기 방수제 도포층의 두께가 균일한 것을 특징으로 하는 바닥재 시트.Flooring sheet, characterized in that the thickness of the waterproofing coating layer is uniform. 제 1 항에 있어서, 상기 바닥재 시트는, The method of claim 1, wherein the flooring sheet, 상기 무늬목의 도관의 일부 또는 전부가 방수제로 충전되는 것을 특징으로 하는 바닥재 시트.Flooring sheet, characterized in that part or all of the conduit of the veneer is filled with a waterproofing agent. 제 1 항에 있어서, 상기 바닥재 시트는, The method of claim 1, wherein the flooring sheet, 상부 시트; 상기 상부 시트 하부의 무늬목; 상기 무늬목 하부의 제1층 및 제2층으로 적층된 합성수지층;을 포함하는 바닥재 시트로서, Top sheet; Veneer under the upper sheet; As a flooring sheet comprising; synthetic resin layer laminated in the first layer and the second layer of the lower part of the veneer, 상기 무늬목의 도관의 일부 또는 전부가 방수제로 충전되는 것을 특징으로 하는 바닥재 시트.Flooring sheet, characterized in that part or all of the conduit of the veneer is filled with a waterproofing agent. 제 4 항에 있어서, The method of claim 4, wherein 상기 바닥재 시트는 매쉬 형상의 유리섬유가 상기 제1층 및 제2층의 합성수지층 사이에 융착되는 것을 특징으로 하는 바닥재 시트.The flooring sheet is a flooring sheet, characterized in that the mesh-shaped glass fibers are fused between the synthetic resin layer of the first layer and the second layer. 제 4 항에 있어서, The method of claim 4, wherein 상기 바닥재 시트는 유리 섬유 시트가 상기 무늬목 및 상기 제1층 합성수지층 사이에 개재되는 것을 특징으로 하는 바닥재 시트.The flooring sheet is a flooring sheet, characterized in that the glass fiber sheet is interposed between the veneer and the first layer synthetic resin layer. 제 1 항 내지 제 6 항 중 어느 한 항에 있어서,The method according to any one of claims 1 to 6, 상기 바닥재 시트는 상기 상부 시트 상에 산화알루미늄의 코팅층이 형성되는 것을 특징으로 하는 바닥재 시트.The flooring sheet is a flooring sheet, characterized in that the coating layer of aluminum oxide is formed on the top sheet. 제 7 항에 있어서, The method of claim 7, wherein 상기 바닥재 시트는 상기 코팅층이 통상의 UV 도료를 더 포함하는 것을 특징으로 하는 바닥재 시트.The flooring sheet is a flooring sheet, characterized in that the coating layer further comprises a conventional UV paint. 제 1 항 내지 제 6 항 중 어느 한 항에 있어서,The method according to any one of claims 1 to 6, 상기 바닥재 시트의 바닥부에는 점착제를 이용하여 이형지가 부착된 것을 특징으로 하는 바닥재 시트.Flooring sheet, characterized in that the release paper is attached to the bottom of the flooring sheet using an adhesive. 제 7 항에 있어서,The method of claim 7, wherein 상기 바닥재 시트의 바닥부에는 점착제를 이용하여 이형지가 부착된 것을 특징으로 하는 바닥재 시트.Flooring sheet, characterized in that the release paper is attached to the bottom of the flooring sheet using an adhesive.
KR2020060001110U 2006-01-13 2006-01-13 Flooring sheet wherein waterproof agent is coated on its side KR200413522Y1 (en)