KR200401841Y1 - covering yarn using stainless wire - Google Patents

covering yarn using stainless wire Download PDF

Info

Publication number
KR200401841Y1
KR200401841Y1 KR20-2005-0015714U KR20050015714U KR200401841Y1 KR 200401841 Y1 KR200401841 Y1 KR 200401841Y1 KR 20050015714 U KR20050015714 U KR 20050015714U KR 200401841 Y1 KR200401841 Y1 KR 200401841Y1
Authority
KR
South Korea
Prior art keywords
yarn
stainless wire
coated
stainless
polyethylene filament
Prior art date
Application number
KR20-2005-0015714U
Other languages
Korean (ko)
Inventor
이철호
Original Assignee
이철호
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 이철호 filed Critical 이철호
Priority to KR20-2005-0015714U priority Critical patent/KR200401841Y1/en
Application granted granted Critical
Publication of KR200401841Y1 publication Critical patent/KR200401841Y1/en

Abstract

본 고안은 스테인레스 와이어 심사의 둘레에 고강도 폴리에틸렌 필라멘트사를 서로 다른 방향으로 피복하면서 두 겹으로 제조함에 따라 고강도 사(絲)가 되기 때문에 판면이 날카롭거나 운반시 또는 작업시 손바닥 등의 신체 부위에 상처를 줄 위험물 취급에 적합한 장갑을 직조하는데 사용함으로써 찢어짐이나 안전사고를 방지하고 착용감을 향상시킬 수 있는 스테인레스 와이어 피복사에 관한 것이다.The present invention is made of two layers of high-strength polyethylene filament yarn coated around the stainless steel screen in different directions, so that the plate becomes sharp and is applied to body parts such as the palm of the hand or the like during transportation or work. The present invention relates to a stainless wire-coated yarn which can be used to weave gloves suitable for handling dangerous goods that can be damaged to prevent tearing or safety accidents and to improve fit.

Description

스테인레스 와이어 피복사{covering yarn using stainless wire}Covering yarn using stainless wire}

본 고안은 스테인레스 와이어 피복사에 관한 것으로, 보다 상세하게는 스테인레스 와이어 심사에 고강도 폴리에틸렌 필라멘트사를 서로 다른 방향으로 피복하여 두 겹으로 피복함에 따라 고강도 사(絲)를 제조하기 때문에 판면이 날카롭거나 운반시 또는 작업시 손바닥 등의 신체 부위에 상처를 줄 위험물 취급에 적합한 장갑을 직조하는데 사용함으로써 찢어짐이나 안전사고를 방지하고 착용감을 향상시킬 수 있는 스테인레스 와이어 피복사에 관한 것이다.The present invention relates to a stainless steel wire coated yarn, and more particularly, because the high strength polyethylene filament yarn is covered in two different layers by coating the high-strength polyethylene filament yarn in a different direction, so the plate surface is sharp or The present invention relates to a stainless wire sheath that can be used to weave gloves suitable for handling dangerous goods that may damage body parts such as palms during transportation or work, thereby preventing tearing or safety accidents and improving wearing comfort.

일반적인 유형의 피복사는 모노 필라멘트 또는 멀티 필라멘트로서 된 고 탄성사를 심사(core yarn)로서 구비하는데, 그것은 고 탄성 심사를 보호하기 위한 권취사에 의해 감싸진다. A common type of sheath is provided as a core yarn of high elastic yarn, either monofilament or multifilament, which is wrapped by a winding yarn to protect the high elastic yarn.

상기 고 탄성 심사는 피복사의 탄성 및 연신을 일으키는 반면에 권취사는 원하는 직물 외관을 심사에 부여하여 그에 상응하는 특성 및 감촉을 최종 제품에 제공한다. The high elasticity screening gives rise to elasticity and stretching of the coated yarn while the winding yarn gives the desired fabric appearance to the screening to provide the corresponding properties and feel to the final product.

이러한 피복사는 예컨대 여성용 양말, 팬티스타킹, 장갑 등을 제조하는 데 사용된다.Such sheaths are used, for example, to make women's socks, pantyhose, gloves and the like.

그러한 제품에서는 양말을 연신된 상태에서 착용하도록 신체 또는 발에 양호하게 안착되어 접하는 것이 요구된다. Such products require good seating and contact with the body or foot to wear the socks in the stretched state.

이때, 연신은 200 내지 500%에 달할 수 있다. At this time, the stretching may amount to 200 to 500%.

그런데, 격심한 연신으로 인해 심사와 권취사의 층 이동이 이루어져서 촘촘히 감쌌음에도 불구하고 심사가 종종 보호되지 못한 채로 드러나는 문제점이 생기게 된다. However, due to intense stretching, the screening and winding movements are carried out, and even though the packing is closely packed, the screening is often unprotected.

최근에는 완성된 피복사의 연신량이 증대됨에 따라 권취사의 필라멘트가 서로 평행하게 놓여져 펴지는 한편, 고 탄성 심사가 권취사를 매우 가파른 나선으로 휘감도록 할 경우에 놀랍게도 심사의 피복 능력 및 차폐가 우수해진다는 인식에 그 기반을 두고 있다. In recent years, as the amount of stretched finished yarn is increased, the winding filaments are laid out in parallel with each other, while surprisingly excellent coating ability and shielding are provided when the high elasticity yarn causes the winding yarn to be wound in very steep spirals. It is based on the perception of getting lost.

그래서, 연신된 상태에서는 늘어나 있는 권취사가 심사에 의해 다만 가볍게만 휘감기게 된다. Therefore, in the stretched state, the increased winding yarn is only wound lightly by the examination.

늘어난 권취사의 펴져 있는 필라멘트는 그러한 휘감김에 의해 쪼그라들지 않고, 그에 따라 권취사가 연신된 상태에서도 매우 우수한 피복 능력을 낼 수 있게 된다.The stretched filament of the stretched winder does not crumble by such a winding, and thus can give a very good covering ability even in the stretched state.

즉, 도 1에 도시된 바와 같이, 종래의 피복사(12)는 일반 직물 재질인 탄성 심사(2)와, 상기 탄성 심사(2)의 둘레에 코일 형상으로 감고 있으며 다중 필라멘트사인 권취사(1)로 이루어진다.That is, as shown in FIG. 1, the conventional coated yarn 12 is wound in a coil shape around the elastic screening 2, which is a general fabric material, and the elastic screening 2, and the multi-filament yarn winding yarn 1 )

상기 탄성 심사(2)를 감싸는 권취사(1)는 조밀한 권선으로 헐겁게 탄성 심사(2)를 휘감고, 특히 권선의 반대 방향으로 꼬임을 갖는다. The winding yarn 1 surrounding the elastic screen 2 is wrapped around the elastic screen 2 loosely with a dense winding, and in particular has a twist in the opposite direction of the winding.

즉, 상기 권취사(1)는 장력이 걸리지 않은 상태에서는 그러한 역방향 꼬임에 의해 합쳐져서 개별 필라멘트(11)가 다발로 된 것처럼 보이게 된다. That is, the wound yarn 1 is joined by such reverse twisting in a state where tension is not applied, so that the individual filaments 11 appear to be bundled.

반면에, 제품에서 사용될 때에 그러한 바와 같이 피복사(12)가 연신되면, 역방향 꼬임이 해체되어 권취사(1)가 펴지고, 개별 필라멘트(11)가 대략 서로 평행하게 나란히 놓여져서 연신된 피복사(12)의 구조가 된다.On the other hand, when the coated yarn 12 is stretched as such when used in a product, the reverse twist is broken to unwind the winding yarns 1, and the individual filaments 11 are laid in parallel with each other approximately parallel to each other. It becomes the structure of 12).

그러나, 종래의 피복사는 거친 외부 물체와 접하여 마찰되거나 날카로운 곳에 의해 쉽게 해지거나 파단되는 문제점이 있었다.However, conventional coated yarns have a problem in that they are easily broken or broken by friction or sharp contact with rough external objects.

본 고안은 상기와 같은 문제점을 해결하기 위해 안출한 것으로, 판면이 날카롭거나 운반시 또는 작업시 손바닥 등의 신체 부위에 상처를 줄 위험물 취급에 적합한 장갑을 직조하는데 있어 내부에 길이방향으로 스테인레스 와이어 심사를 구비하고, 그 둘레에 서로 다른 방향으로 고강도 폴리에틸렌 필라멘트사를 두 겹으로 피복하여 강도를 높임에 따라 닳거나 찢어짐을 방지하고, 착용감을 증대시킨 스테인레스 와이어 피복사를 제공하는데 그 목적이 있다.The present invention has been made to solve the above problems, the stainless steel wire in the longitudinal direction in the inner side in the weaving gloves suitable for handling dangerous goods that the plate surface is sharp or will hurt the body parts such as palms during transportation or work. It is an object of the present invention to provide a stainless wire-coated yarn having a screening and covering two layers of high-strength polyethylene filament yarns in different directions around it to prevent wear or tear as the strength thereof is increased, and to increase the fit.

상기한 목적을 달성하기 위한 본 고안은 강도를 증가시키기 위해 스테인레스 와이어 재질로서 중심에 길이방향으로 한 가닥 이상 구비한 스테인레스 와이어 심사와, 상기 스테인레스 와이어 심사의 둘레에 두 겹으로 피복하는 폴리에틸렌 재질의 사(絲)로서, 서로 반대 방향으로 피복함으로써 강도를 향상시킴과 아울러 착용감을 증대시키기 위한 고강도 폴리에틸렌 필라멘트사로 이루어진 스테인레스 와이어 피복사를 제공하려는 것이다.The present invention for achieving the above object is a stainless wire screen having at least one strand in the longitudinal direction at the center as a stainless wire material in order to increase the strength, and two layers of polyethylene coated with a circumference of the stainless wire screen (Iii) To provide a stainless wire-covered yarn made of high strength polyethylene filament yarn for improving strength by increasing coating strength by coating in opposite directions.

이하, 본 고안의 일실시예를 첨부한 도면을 참조하여 더욱 상세히 설명한다. Hereinafter, with reference to the accompanying drawings an embodiment of the present invention will be described in more detail.

도 2는 본 고안의 실시예에 따른 스테인레스 와이어 피복사의 제조 상태를 보인 구조도이고, 도 3은 본 고안의 실시예에 따른 스테인레스 와이어 피복사로 직조한 장갑의 사시도이다.Figure 2 is a structural diagram showing a state of manufacturing a stainless wire sheath according to an embodiment of the present invention, Figure 3 is a perspective view of a glove woven with a stainless wire sheath according to an embodiment of the present invention.

도 2에 도시된 바와 같이, 본 고안의 실시예에 따른 피복사(62a,62b)는 소정의 강도를 갖는 목적으로 중심에 길이방향으로 한 가닥 이상의 스테인레스 와이어 심사(stainless wire yarn,52)를 구비하고, 상기 스테인레스 와이어 심사(52)의 둘레에 한 방향으로 고강도 폴리에틸렌 필라멘트사(55a)를 피복하여 전도성을 갖는 스테인레스 와이어 심사(52)의 외부 노출을 방지하는 피복사(62a)와, 상기 스테인레스 와이어 심사(52)의 둘레에 한 방향으로 고강도 폴리에틸렌 필라멘트사(55a)를 피복한 그 위에 다른 방향으로 고강도 폴리에틸렌 필라멘트사(55b)를 피복하여 강도를 향상시키며 착용감을 좋게 한 피복사(62b)로 이루어진다.As shown in Fig. 2, the coated yarns 62a and 62b according to the embodiment of the present invention have at least one strand of stainless wire yarn in the longitudinal direction at the center for the purpose of having a predetermined strength. And a coated yarn 62a for covering the high-strength polyethylene filament yarn 55a in one direction around the stainless wire screen 52 to prevent external exposure of the conductive stainless wire screen 52 and the stainless wire. The high-strength polyethylene filament yarn 55a is coated in one direction around the screen 52, and the high-strength polyethylene filament yarn 55b is coated in the other direction, thereby improving the strength and providing a comfortable fit. .

상기 스테인레스 와이어 심사(52)는 강도가 우수함으로써, 이를 피복사(62a,62b)로 사용하면 판면이 날카롭거나 운반시 또는 작업시 손바닥 등의 신체에 상처를 줄 위험물 취급에 적합하다.The stainless wire screen 52 is excellent in strength, and when used as the coated yarns 62a and 62b, the stainless steel screen 52 is sharp and suitable for handling dangerous goods that may hurt the body such as palms during transportation or work.

또한, 상기 피복사(62a,62b)의 고강도 폴리에틸렌 필라멘트사(55a,55b)는 길이방향으로 길게 설치된 스테인레스 와이어 심사(52)의 둘레에 코일 형상으로 피복되며 겹을 이룬다.The high-strength polyethylene filament yarns 55a and 55b of the coated yarns 62a and 62b are coated in a coil shape around the stainless wire screen 52 that is provided in the longitudinal direction and are stacked.

상기 고강도 폴리에틸렌 필라멘트사(55a)는 스테인레스 와이어 심사(52)와 직접적으로 접촉하며 둘레에 한 방향으로 피복되고, 다른 고강도 폴리에틸렌 필라멘트사(55b)는 스테인레스 와이어 심사(52)와 접한 고강도 폴리에틸렌 필라멘트사(55a)의 둘레에서 이 고강도 폴리에틸렌 필라멘트사(55a)와 반대 방향으로 감긴다.The high strength polyethylene filament yarn 55a is in direct contact with the stainless wire screening 52 and coated in one direction around the other, and the other high strength polyethylene filament yarn 55b is a high strength polyethylene filament yarn in contact with the stainless wire screening 52 ( It winds around the 55a) in the opposite direction to this high strength polyethylene filament yarn 55a.

그래서, 상기 고강도 폴리에틸렌 필라멘트사(55a,55b)는 스테인레스 와이어 심사(52)의 둘레에 서로 다른 방향으로 감기기 때문에 쉽게 풀리지 않게 된다.Thus, the high strength polyethylene filament yarns 55a and 55b are not easily loosened because they are wound around the stainless wire screen 52 in different directions.

이때, 상기 고강도 폴리에틸렌 필라멘트사(55a,55b)에서 폴리에틸렌은 가볍고,유연,전기절연성,내약품성,내수성이 양호한 성질을 갖고, 필라멘트사는 무한히 긴 섬유를 말한다.In this case, the polyethylene in the high strength polyethylene filament yarn (55a, 55b) is a light, flexible, electrical insulation, chemical resistance, water resistance has good properties, filament yarn refers to an infinitely long fiber.

즉, 상기 고강도 폴리에틸렌 필라멘트사(55a,55b)는 비도전성 재질이고, 내충격성이 우수하며, 무한히 긴 섬유를 코일 형상으로 꼬아 제조함으로써 착용감을 증대시키는 성질을 갖는다.That is, the high-strength polyethylene filament yarn (55a, 55b) is a non-conductive material, excellent impact resistance, and has the property of increasing the wearing feeling by twisting infinitely long fibers in a coil shape.

또한, 상기 피복사(62a,62b)는 장갑, 방탄조끼 또는 사냥시 착용하는 안전복 등을 제작하는데 사용된다.In addition, the coated yarns 62a and 62b are used to manufacture gloves, bulletproof vests or safety clothing to be worn when hunting.

그래서, 상기 피복사(62a,62b)의 스테인레스 와이어 심사(52)는 0.05 내지 0.08mm의 굵기 형성된다.Thus, the stainless wire screen 52 of the coated yarns 62a and 62b is formed to have a thickness of 0.05 to 0.08 mm.

상기 스테인레스 와이어 심사(52)가 0.05mm 이하의 굵기로 형성되면 뾰족한 판면 등의 외부 환경에 의해 쉽게 절단될 우려가 있고, 0.08mm 이상일 경우 착용시 너무 무겁게 느껴질 수가 있다.When the stainless wire screen 52 is formed to a thickness of 0.05 mm or less, it may be easily cut by an external environment such as a pointed plate surface, and when it is 0.08 mm or more, it may feel too heavy when worn.

그리고, 상기 스테인레스 와이어 심사(52)는 장갑, 방탄조끼 또는 안전복 등을 제작시 1 내지 3 가닥으로 구성됨이 가장 바람직하다.And, the stainless wire screening 52 is most preferably composed of 1 to 3 strands when manufacturing gloves, bulletproof vests or safety clothing.

이때, 상기 스테인레스 와이어 심사(52)가 3 가닥을 초과할 경우 중압감을 느끼게 된다.At this time, when the stainless wire screening 52 exceeds three strands, a feeling of pressure is felt.

편의상, 도면에서 스테인레스 와이어 심사(52)가 한 가닥 구비된 것으로 도시한다.For convenience, the drawing shows that the stainless wire screen 52 is provided with one strand.

또한, 상기 피복사(62a,62b)에서 스테인레스 와이어 심사(52)의 둘레를 겹으로 감싸고 있는 고강도 폴리에틸렌 필라멘트사(55a,55b)는 400 내지 900 데니어(Denier)의 굵기로 이루어진다.In addition, the high-strength polyethylene filament yarns 55a and 55b enclosing the circumference of the stainless wire screen 52 in the coated yarns 62a and 62b are made of a thickness of 400 to 900 deniers.

이때, 데니어는 항장식 번수(恒長式 番手)의 하나로, 주로 생사, 인견, 합성섬유 등의 실 또는 섬유의 굵기[纖度]를 표시하는 데 사용되는 국제 단위이다.At this time, denier is one of the decorative counts, and is an international unit mainly used to express the thickness of yarn or fibers such as raw silk, honeycomb, and synthetic fibers.

그리고, 상기 고강도 폴리에틸렌 필라멘트사(55a,55b)가 400 데니어 미만의 굵기를 갖으면 강도가 약해 장갑, 방탄조끼 또는 안전복 제작시 쉽게 닳으며 강도를 향상시킬 수 없고, 900 데니어를 초과할 경우 너무 두꺼워 착용감이 반감되게 된다.In addition, when the high strength polyethylene filament yarn (55a, 55b) has a thickness of less than 400 denier, the strength is weak, can be easily worn when making gloves, bulletproof vest or safety suit, can not improve the strength, too much if more than 900 denier It is thick, and the fit is halved.

결과적으로, 상기 스테인레스 와이어 심사(52)의 둘레에는 직접적으로 접하는 고강도 폴리에틸렌 필라멘트사(55a)가 한 방향의 코일 형상으로 피복되어 스테인레스 와이어 심사(52)의 외부 노출을 방지함으로써 도전성을 방지하며 소정의 강도를 유지하고, 상기 고강도 폴리에틸렌 필라멘트사(55a)의 둘레에는 고강도 폴리에틸렌 필라멘트사(55b)가 한번 더 피복되어 강도를 향상시키면서 착용감을 증가시킨다.As a result, the high-strength polyethylene filament yarn 55a directly contacting the circumference of the stainless wire screen 52 is coated in a coil shape in one direction to prevent the external exposure of the stainless wire screen 52 to prevent conductivity and to prevent The strength is maintained, and the high-strength polyethylene filament yarn 55b is coated once more around the high-strength polyethylene filament yarn 55a to increase the wearing comfort while improving the strength.

도 3은 본 고안의 실시예에 따른 스테인레스 와이어 심사(52)의 둘레에 겹의 고강도 폴리에틸렌 필라멘트사(55a,55b)를 상호 반대 방향으로 피복한 피복사(62b)를 이용하여 장갑(50)을 제조한 것이다.FIG. 3 shows a glove 50 using a sheathed yarn 62b coated with plies of high strength polyethylene filament yarns 55a and 55b around each other in a stainless wire screen 52 according to an embodiment of the present invention. It is manufactured.

상기한 바와 같이 본 고안에 따른 스테인레스 와이어 피복사는 스테인레스 와이어 심사를 코어(core)로 사용하고 그 둘레에 겹의 고강도 폴리에틸렌 필라멘트사를 반대 방향으로 피복하여 편물, 직물 및 피복 등을 제조함으로써 날카로운 판면이나 작업시 닳거나 절단을 방지할 수 있어 손 등 신체의 상해를 예방할 수 있음과 아울러 착용감을 증가시킬 수 있는 있다.As described above, the stainless wire sheathing yarn according to the present invention uses a stainless steel wire as a core and coats high-strength polyethylene filament yarn of the circumference in the opposite direction to produce a knitted fabric, a fabric, and a sheath. It can prevent wear or cutting during work, which can prevent injury to the body such as hands and increase the fit.

또한, 상기 한 쌍의 고강도 폴리에틸렌 필라멘트사가 반대방향으로 피복되기 때문에 고강도 폴리에틸렌 필라멘트사의 풀림을 방지하고, 피복사의 도전성 재질인 스테인레스 와이어 심사의 외부 노출을 방지함으로써 비도전성을 유지하는 효과가 있다.In addition, since the pair of high-strength polyethylene filament yarn is coated in the opposite direction, it is effective to prevent loosening of the high-strength polyethylene filament yarn and to prevent external exposure of stainless wire screening, which is a conductive material of the coated yarn, to maintain non-conductivity.

도 1은 종래 피복사의 요부 사시도.1 is a perspective view of main parts of a conventional coating yarn;

도 2는 본 고안의 실시예에 따른 스테인레스 와이어 피복사의 제조 상태를 보인 구조도.Figure 2 is a structural diagram showing a state of manufacture of the stainless steel wire sheath according to an embodiment of the present invention.

도 3은 본 고안의 실시예에 따른 스테인레스 와이어 피복사로 직조한 장갑의 사시도.Figure 3 is a perspective view of a glove woven with a stainless wire sheath according to an embodiment of the present invention.

*도면의 주요부분에 대한 부호의 설명** Description of the symbols for the main parts of the drawings *

50: 장갑 2: 탄성 심사50: gloves 2: elastic screening

12,62a,62b: 피복사 55a,55b: 고강도 폴리에틸렌 필라멘트사12,62a, 62b: coated yarn 55a, 55b: high strength polyethylene filament yarn

Claims (3)

강도를 증가시키기 위해 스테인레스 와이어 재질로서 중심에 길이방향으로 한 가닥 이상 구비한 스테인레스 와이어 심사와;A stainless wire screen having at least one strand in the longitudinal direction at the center as a stainless wire material to increase strength; 상기 스테인레스 와이어 심사의 둘레에 두 겹으로 피복하는 폴리에틸렌 재질의 사(絲)로서, 서로 반대 방향으로 피복함으로써 강도를 향상시킴과 아울러 착용감을 증대시키기 위한 고강도 폴리에틸렌 필라멘트사로 이루어지는 것을 특징으로 하는 스테인레스 와이어 피복사.A stainless steel thread coated with two layers around the stainless steel wire screen, wherein the stainless steel wire is made of a high strength polyethylene filament yarn for improving strength and wearing comfort by coating in opposite directions. copy. 제 1항에 있어서,The method of claim 1, 상기 스테인레스 와이어 심사는 0.05 내지 0.08mm의 굵기로, 1 내지 3 가닥으로 이루어지는 것을 특징으로 하는 스테인레스 와이어 피복사.The stainless wire screening is stainless steel coated yarn, characterized in that consisting of 1 to 3 strands, the thickness of 0.05 to 0.08mm. 제 1항에 있어서,The method of claim 1, 상기 고강도 폴리에틸렌 필라멘트사는 400 내지 900 데니어(Denier)의 굵기로 이루어진 것을 특징으로 하는 스테인레스 와이어 피복사.The high-strength polyethylene filament yarn 400 to 900 denier (denier) stainless steel wire sheath characterized in that made of a thickness.
KR20-2005-0015714U 2005-04-29 2005-06-01 covering yarn using stainless wire KR200401841Y1 (en)