KR20040060267A - A Security Seat And Product Method To Be Anti-forgery Effect, A Security paper Prepared Security Thread - Google Patents
A Security Seat And Product Method To Be Anti-forgery Effect, A Security paper Prepared Security Thread Download PDFInfo
- Publication number
- KR20040060267A KR20040060267A KR1020020086816A KR20020086816A KR20040060267A KR 20040060267 A KR20040060267 A KR 20040060267A KR 1020020086816 A KR1020020086816 A KR 1020020086816A KR 20020086816 A KR20020086816 A KR 20020086816A KR 20040060267 A KR20040060267 A KR 20040060267A
- Authority
- KR
- South Korea
- Prior art keywords
- colored
- layer
- silver wire
- transparent film
- ultra
- Prior art date
Abstract
Description
본 발명은 은행권 수표를 비롯하여 유가증권 용지를 제조할 때에 위조방지용 으로 사용되어지는 위조방지용 은선시트 및 그 제조방법과 이를 이용한 보안용지에 관한 것이다.The present invention relates to an anti-counterfeiting hidden wire sheet that is used for anti-counterfeiting when manufacturing securities paper, including banknote checks, and a manufacturing method thereof, and a security paper using the same.
이를 좀더 상세히 설명하면, 투명필름에 글씨나 그림과 같은 문양을 다양하게 인쇄하고, 인쇄된 문양 위에 초박막금속층을 증착시키되 초박막금속증착층은 두께 조절이 용이한 상온 플라스마(Plasma)법에 의한 통상의 이온 스퍼터링(Ion Sputtering)방법에 의해 증착시켜서 된 위조방지용 은선 시트를 제공하고, 상기와 같이 제조된 위조방지용 은선시트를 소정의 크기로 재단하여 환망 초지기에서 통상의 은선 투입방법에 의해 지필 내에 삽입하거나 부분 노출시켜서 된 보안용지를 제공하려는 것이다.To explain this in more detail, various patterns such as letters and pictures are printed on a transparent film, and an ultra-thin metal layer is deposited on the printed pattern, but the ultra-thin metal deposition layer is conventionally prepared by using a room temperature plasma method. Provide a counterfeit-proof silver wire sheet deposited by ion sputtering method, cut the counterfeit-resistant silver wire sheet prepared as described above into a predetermined size, and insert it into paper by a conventional silver wire feeding method in a ring paper machine. It is to provide security paper with partial exposure.
은행권 수표를 비롯하여 증권류 등 각종 유가증권용지로 사용되어지는 종이를 제조할 때에 종이의 내부에는 위조를 방지하기 위하여 은선시트를 소정의 크기로 재단한 은선을 삽입하여 제조하고 있다.When manufacturing paper used for various securities papers such as banknote checks and securities, the inside of the paper is manufactured by inserting a hidden wire cut into a predetermined size to prevent counterfeiting.
일반적으로 종래에는 미국특허 제 4652015호 등에 기술된 바와 같이, 알루미늄 등의 금속소재를 필름에 증착하여 은선시트를 제조하고 상기 은선시트를 소정의 크기로 재단하여서 된 은선을 종이를 제조할 때에 삽입하여 제조하였는데, 이와 같이 종이를 제조할 때에 은선을 삽입시키게 되면 금속층이 투과되는 빛에는 어둡게 보이지만 반사되는 빛에는 잘 나타나지 않게 되는 효과를 얻을 수 있게 된다.Generally, as described in US Pat. No. 465,2015, a metal material such as aluminum is deposited on a film to produce a silver wire sheet, and the silver wire cut by cutting the silver wire sheet to a predetermined size is inserted into the paper. In this case, when the silver wire is inserted in the manufacturing of the paper, it is possible to obtain the effect that the metal layer is dark in the transmitted light but does not appear in the reflected light.
상기와 같은 방법을 보다 개선하여 현재 가장 많이 사용되는 방법으로는 미국특허 제 4652015호와 유럽특허 제 319157호에 의해 도 1에 예시된바와 같은 위조방지용 은선시트(1)가 알려져 있다. 이는 투명필름(2)에 글자 또는 문양이 투명하게 나타나도록 금속피복층(3)을 증착시킨 클리어 텍스트(Clear Text)로 형성하여서 된 것으로써, 이 역시 광학적 효과를 주로 얻도록 된 것이나, 글자 또는 문자를 투명하게 나타내는 금속피복층(3)의 클리어 텍스트(Clear Text)는 제조과정이 너무 보편화되어 상업적으로 많이 활용되고 기술로서 일반인들도 용이하게 제조할 수 있으므로 쉽게 도용되거나 모방되어 위조방지효과를 얻을 수 없는 문제가 있었다.The anti-counterfeiting hidden wire sheet 1 as illustrated in FIG. 1 by US Patent No. 4652015 and European Patent No. 319157 is known as a method of improving the method as described above. This is formed by the clear text in which the metal coating layer 3 is deposited so that letters or patterns appear transparently on the transparent film 2, which is mainly intended to obtain an optical effect, but letters or letters Clear Text (Clear Text) of the metal coating layer (3) that is transparent to show that the manufacturing process is so common that it is widely used commercially and can be easily manufactured by the public as a technology, so it can be easily stolen or imitated to obtain an anti-counterfeiting effect. There was no problem.
이를 보다 기술적으로 개선되어 보다 우수한 효과를 얻도록 하는 방법으로는 국내 특허 등록 제 69251호를 비롯하여 GB-A-1552853호 및 GB-A-1604463호가 알려져 있는데, 이는 은선을 종이 내부에 삽입시키거나 혹은 부분 노출의 형태로 활용하되 주로 부분 노출되도록 활용되며, 위조를 하기 위하여 복사를 실시할 때에 금속의 반사로 인하여 은선이 검은색으로 나타나는 특성을 갖고 있으므로 매우 중요한 보안요소로 활용되고 있다.There are known methods to improve this technically to obtain a better effect, including GB-A-1552853 and GB-A-1604463, including domestic patent registration No. 69251, which inserts a hidden line inside the paper or It is used in the form of partial exposure, but mainly used for partial exposure, and is used as a very important security element because the silver line appears black due to the reflection of metal when copying for forgery.
또 국내 특허 등록 제 146374호에는 일반적으로 금속증착을 시킨 후에 탈 금속화과정을 통하여 문자나 패턴을 형성시킨 클리어 텍스트(Clear Text)형에 이들이 부분적으로 전기적 특성이 떨어지는 문제를 보완하기 위하여 인듐 - 주석 산화물에 의한 스퍼터링방법에 의해 50%의 투광율을 얻으면서 전기적 특성을 보완하도록 하거나 또는 알루미늄을 20㎎/㎡의 양으로 얇게 진공 증착하여 유사한 효과를 얻도록 한 것이 제안되어 있다.In addition, in Korean Patent Registration No. 146374, indium-tin is used to compensate for the problem that they are partially deteriorated in the Clear Text type in which letters or patterns are formed through metallization and then metallization. The sputtering method using oxides has been proposed to achieve electrical properties while obtaining 50% light transmittance, or to obtain similar effects by thin vacuum deposition of aluminum in an amount of 20 mg / m 2.
그러나 국내의 특허 등록 제 69251호 및 특허 등록 제 146374호는 앞서 언급된바와 같이 반투명효과를 얻기 위하여 알루미늄 층의 광학적 밀도를 0.3이하 또는 20㎎/㎡정도의 박막으로 증착할 경우에 부분적으로 가능할 수도 있으나, 실질적인 박막으로 증착시키기 위한 제조공정상의 문제로 인하여 전체 제품에 대해 균일한 품질로 제조하는 데에는 상당히 많은 문제점이 대두되어 용이하게 실용화시킬 수 없는 문제가 있었으며, 이 범위를 벗어나게 되면 반투명 등 광학적 효과가 현저하게 떨어지는 문제가 있었다.However, domestic patent registration No. 69251 and patent registration No. 146374 may be partially possible when the optical density of the aluminum layer is deposited in a thin film of less than 0.3 or 20 mg / m 2 in order to obtain a translucent effect as mentioned above. However, due to problems in the manufacturing process for the deposition of a thin film, there are a lot of problems to produce a uniform quality for the entire product, there was a problem that can not be easily put to practical use, and beyond this range, optical effects such as translucent There was a problem that fell significantly.
특히, 특허 등록 제 69251호에서는 박막을 증착시킬 때에 탈 금속층을 보호하기 위하여 이 층이 아닌 반대면에 증착시키거나 다른 유색필름 등에 증착하여 붙이는 방법 등을 사용하고 있는데, 이는 제조공정이 복잡하고 작업이 어려운 문제가 있으며, 이를 보완하기 위하여 스퍼터링방법을 적용하기도 하지만 이 또한 방법이 다양하여 박막을 균일하게 증착시키려면 작업조건 등을 충분히 검토하여야하는 번거로운 폐단이 있었다.Particularly, in Patent Registration No. 69251, in order to protect the demetallized layer when depositing a thin film, a method of depositing it on the opposite side of the layer or depositing it on another color film or the like is used. There is a difficult problem, and in order to compensate for this, the sputtering method may be applied. However, this method also has a variety of methods.
또한 특허 등록 제 146374호는 투광율을 50%수준으로 유지시시키면서 전기적인 특성을 강화시켜 주기 위하여 인듐 - 주석산화물을 이용하여 일반적인 스퍼터링방법에 의해 직접적으로 부분 탈 금속층을 형성하거나 또는 반대면에 박막의 금속층을 증착시키는 방법을 채택하고 있으나, 투명성이 우수한 인듐 - 주석산화물을 제외한 스퍼터링에서 흔히 사용되는 다른 금속, 알루미늄, 니켈 등은 투광율 50%정도에서는 전기전도성과 부분 탈 금속층의 효과를 다소 얻을 수 있으나 인쇄방법에 의한 문자 판독성이나 형광특성이 현저하게 떨어져 이를 종이의 내부에 삽입시킬 때에 위조방지효과가 떨어지는 등의 문제가 제기 되었다.In addition, Patent Registration No. 146374 uses indium-tin oxide to form a partial demetallization layer directly by a general sputtering method or to maintain a light transmittance at a level of 50%. Although a method of depositing a metal layer is adopted, other metals, aluminum and nickel, which are commonly used in sputtering except indium-tin oxide, which have excellent transparency, may have some effects of electrical conductivity and partial demetallization at a transmittance of about 50%. The problem that the anti-counterfeiting effect is lowered when inserting it into the paper due to the remarkable drop in character readability and fluorescence characteristics by the printing method.
이외에도 미국특허 제 5314739호를 비롯하여 제 4813989호 및 제 5419424호에 의해 도 2에 예시된바와 같은 위조방지용 은선시트(1-1)가 알려져 있는데, 이는 투명필름(2)에 흑색 또는 유색의 문자나 문양으로 된 유색인쇄층(4)을 인쇄하여서 된 것으로, 필요에 따라 유색인쇄층(4)의 상측에 형광처리를 부가적으로 실시하기도하고, 투명 또는 금속필름에 전기전도성, 자성, 홀로그램특성, 색 변환 등 다양한 요소를 적용하여 제조하기도 하게 되는데, 이들 은선은 0.5 - 5 mm 정도의 좁은 폭으로 가늘게 재단하여 종이를 제조할 때에 종이의 내부에 삽입하여 유가증권의 위조방지요소로 활용하고 있으며, 이 또한 보안요소로서 매우 중요한 역할을 하고 있다.In addition, US Pat. No. 5,314,739, 4813989 and 5419424, as shown in Figure 2, for example, the anti-counterfeiting silver wire sheet (1-1), which is known as black or colored letters on the transparent film (2) It is made by printing a colored printed layer 4 in a pattern, and if necessary, fluorescence treatment may be additionally performed on the colored printed layer 4, and electrical conductivity, magnetic properties, hologram characteristics, It is also manufactured by applying various factors such as color conversion, and these hidden lines are cut into narrow widths of about 0.5-5 mm and inserted into the inside of paper when they are manufactured to use them as anti-counterfeiting elements of securities. This also plays a very important role as a security factor.
또한 WO 99451A1에서 언급된 것으로 도 3에 예시된 위조방지용 은선시트(1-2)는 전술한 클리어 텍스트(Clear Text)와 유색문자를 조합하여 여러 가지 특성을 혼합하여 다(여러)기능을 부여하기 위하여, 투명필름(2)에 클리어 텍스트부(5-1:Clear Text)와 유무색의 미세문자 또는 문양을 인쇄시킨 유색문자부(5-2) 및 유색문양부(5-3)를 반복적으로 형성시킨 유색문자문양층(5)을 인쇄하여서 된 것으로써, 클리어 텍스트부(5-1:Clear Text)는 금속층의 내부에 글씨(또는 문양)가 투명하게 형성되어 있으므로 투명한 글자(또는 문양)부분은 투과광으로 볼 때에 투명하게 보여 지고 다른 금속층부분은 광학적 효과에 의해 은선의 기본적인 반사 등 광학적 특성을 충족시켜 주며, 유색문자부(5-2) 및 유색문양부(5-3)는 소정의 문자 또는 문양을 유색 계통의 잉크 등을 사용하여 일반적인 그라비어 등의 인쇄방법에 의해 인쇄(기록)하거나 여기에 형광특성 등을 가미하여 유색 색상이 광학적 특성을 이용하여 위/변조 방지 요소로 활용한 것이나 유색부분이 칼라복사 또는 스캐너 등에 의해 부분적으로 색상이 재현되어 복사를 방지하기 위한 위조를 방지하기 위한 근본적인 원래의 목적에 미흡한 문제점이 있음에도 불구하고 인쇄에 의해 문자의 농도 및 형광 등 기능적인 여러 특성을 복합적으로 양호하게 나타나도록 용이하게 조절할 수 없는 문제가 있었다.In addition, the anti-counterfeiting hidden line sheet 1-2 illustrated in FIG. 3 as referred to in WO 99451A1 is a combination of the above-described clear text and colored letters to mix various characteristics to impart multi-functions. In order to repeatedly print the clear text portion (5-1: Clear Text) and colorless fine characters or patterns on the transparent film 2, the colored character portion 5-2 and the colored pattern portion 5-3 are repeatedly printed. The colored text pattern layer 5 is formed by printing the clear text portion 5-1 (Clear Text) because the letters (or patterns) are formed transparently inside the metal layer. Silver is transparent when seen through transmitted light, and the other metal layer part meets optical characteristics such as basic reflection of the hidden line by the optical effect, and the colored character part 5-2 and the colored pattern part 5-3 are predetermined characters. Or use a pattern of colored ink, etc. It is printed (recorded) by printing methods such as ingravure, or the fluorescent color is added to it, and the colored color is used as an anti-counterfeiting element by using the optical characteristic, or the colored part is partially colored by color copying or scanner, etc. This problem cannot be easily adjusted so that various functional characteristics such as density and fluorescence of characters can be easily mixed by printing even though there is a problem inherent in the original purpose for preventing counterfeiting to prevent copying. There was.
따라서 기본적인 유색문자나 문양을 효과적으로 살리면서도 이 부분이 칼라복사(스캐너)에 의해 재현되어지지 않도록 하기 위해서는 종이 내에 삽입시켰을 때에 일반적인 은선에 의해 절대적으로 필요한 특성인 투과되는 빛에는 보이지만 반사되는 빛에는 잘 나타나지 않도록 하고 부분적으로 노출되는 은선으로 사용될 때에 노출부분이 고유한 금속색상으로부터 광 반사에 의해 색상이 변화도록 하는 광학적 효과를 증대시키면서도 유색문자나 형광특성 등을 유지시켜주어야 할 필요성이 절실히 요구되고 있다.Therefore, in order to make effective use of basic colored letters or patterns, and to prevent this part from being reproduced by color copying (scanner), it is visible to the transmitted light, which is an absolutely necessary characteristic of the general hidden line when inserted into the paper, but is well reflected on the reflected light. When it is used as a partially exposed silver wire, it is urgently needed to maintain colored characters and fluorescent characteristics while increasing the optical effect that the exposed part changes color due to light reflection from an inherent metal color. .
이러한 문제를 해소하기 위하여 본인은 특허 출원번호 제 200? - 84594호에의해 도 4a 및 도 4b에 예시된바와 같은 위조방지용 은선시트(1-3)(1-4)를 제안하였는데, 도 4a에 예시된 위조방지용 은선시트(1-3)는 투명필름(2)의 상면에 문자나 문양을 인쇄시킨 유색문자문양층(5)을 증착하고 유색문자문양층(5)에 접착층(8)을 도포한 후에 금속증착층(6)과 투명필름(7)을 차례로 증착하며 투명필름(2)의 저면에 금속증측층(6)을 증착시켜서 된 것이고, 도 4b에 예시된 위조방지용 은선시트(1-4)는 투명필름(2)의 상면에 문자나 문양을 인쇄시킨 유색문자문양층(5)을 증착시키되 유색문자문양층(5)의 상면과 투명필름(2)의 저면에는 접착층(8)과 금속증착층(6) 및 투명필름(7)을 차례로 도포 증착시켜서 된 것이다.In order to solve this problem, I apply for Patent Application No. 200? 84594 proposed anti-counterfeiting silver wire sheet (1-3) (1-4) as illustrated in Figures 4a and 4b, the anti-counterfeiting silver wire sheet (1-3) illustrated in Figure 4a is a transparent film After depositing a colored character pattern layer (5) printed with letters or patterns on the upper surface of (2) and applying an adhesive layer (8) to the colored character pattern layer (5), the metal deposition layer (6) and the transparent film (7). By depositing the metal thickening layer 6 on the bottom of the transparent film 2 in sequence, and the anti-counterfeiting silver wire sheet 1-4 illustrated in FIG. 4B has a letter or a pattern on the upper surface of the transparent film 2. Deposit a colored letter pattern layer (5) on which the upper surface of the colored letter pattern layer (5) and the bottom surface of the transparent film (2) are attached, followed by an adhesive layer (8), a metal deposition layer (6), and a transparent film (7). It was made by coating deposition.
그러나 이는 인쇄면에 금속증착층(6)을 초박막으로 증착시키기가 기술적으로 어려움이 있었고, 유색문자문양층(5)의 상면과 투명필름(2)의 저면에는 접착층(8)과 금속증착층(6) 및 투명필름(7)을 차례로 도포 증착시키는 경우에는 제조공정이 너무 어렵고 복잡할 뿐만 아니라 두께기 너무 두꺼워져 종이의 내부에 삽입시킬 때에 종이의 불필요한 두께가 필요 이상으로 증가되어 실용성에 문제가 야기되었다.However, it was technically difficult to deposit the metal deposition layer 6 on the printing surface as an ultra-thin film. The upper surface of the colored character pattern layer 5 and the bottom surface of the transparent film 2 had an adhesive layer 8 and a metal deposition layer ( 6) and the transparent film 7 are applied in order to be deposited in order, the manufacturing process is not only difficult and complicated, but also the thickness is so thick that the unnecessary thickness of the paper is increased more than necessary when inserting it into the paper, causing problems in practicality. Caused.
본 발명은 상기와 같은 문제와 폐단을 해소할 수 있도록 더욱 개선된 위조방지용 은선 시트 및 이를 이용한 보안용지를 제공하려는 것이다.The present invention is to provide a further improved anti-counterfeiting silver wire sheet and security paper using the same to solve the above problems and closure.
본 발명은 투명필름에 글씨나 그림과 같은 문양을 다양하게 인쇄하고, 인쇄된 문양 위에 초박막금속층을 증착시키되 초박막금속증착층은 두께 조절이 용이한 상온 플라스마(Plasma)법에 의한 통상의 이온 스퍼터링(Ion Sputtering)방법에 의해 증착시켜서 된 위조방지용 은선 시트를 제공하고, 상기와 같이 제조된 위조방지용 은선시트를 소정의 크기로 재단하여 환망 초지기에서 통상의 은선 투입방법에 의해 지필 내에 삽입하거나 부분 노출시켜서 된 보안용지를 제공하려는데 그 목적이 있다.The present invention prints a variety of patterns such as letters and pictures on the transparent film, and depositing an ultra-thin metal layer on the printed pattern, the ultra-thin metal deposition layer is a conventional ion sputtering by the plasma temperature method (Plasma) method is easy to control the thickness ( Providing the anti-counterfeiting silver wire sheet deposited by the ion sputtering) method, cut the anti-counterfeiting silver wire sheet prepared as described above to a predetermined size and inserted or partially exposed in the paper by a conventional silver wire injection method in a ring paper machine The purpose is to provide secure paper.
본 발명의 다른 목적은 은선의 문자 및 패턴과 형광 등에 의한 기본적인 효과를 얻도록 하고, 금속반사에 따른 광학적 효과를 증대시키기 위해 금속층을 초박막으로 코팅하여 투광율을 향상시키고 반투명효과에 의한 보안요소의 특성을 향상시킬 수 있도록 하며, 종이의 내부에 삽입시켜 주더라도 외부에서 용이하게 식별되지 않도록 하면서도 동시에 금속증착밀도를 높여 전자기적 특성도 충분히 갖도록 하여 기기감응요소로서의 활용이 가능하도록 하여 위조방지효과를 크게 향상시킬 수 있도록 된 위조방지용 은선 시트 및 이를 이용한 보안용지를 제공하려는데 있다.Another object of the present invention is to obtain the basic effect of the letter and pattern and fluorescence of the silver line, and to increase the optical effect according to the metal reflection to improve the light transmittance by coating the metal layer with ultra-thin properties of the security element by the translucent effect It is possible to improve the anti-counterfeiting effect by making it possible to use it as a device-sensing element by increasing the metal deposition density and not only making it easily identified from the outside even when inserted into the paper, but also increasing the metal deposition density. The purpose of the present invention is to provide an anti-counterfeiting hidden wire sheet and a security paper using the same.
본 발명의 또 다른 목적은 인쇄된 문양 위에 초박막금속층을 증착시킬 때에 상온 플라스마(Plasma)법에 의한 통상의 이온 스퍼터링(Ion Sputtering)방법에 의해 증착시키도록 하여 금속증착층의 두께를 용이하게 조절하면서 균일하고 치밀한 초박막으로 직접 증착시킬 수 있도록 하여, 초박막에 의한 투명효과와 치밀한 금속층에 의한 광반사율을 향상시킬 수 있도록 된 위조방지용 은선 시트 및 이를 이용한 보안용지를 제공하는데 있다.Another object of the present invention is to deposit the ultra-thin metal layer on the printed pattern by a conventional ion sputtering method by the plasma method (Plasma method) to easily control the thickness of the metal deposition layer It is possible to directly deposit a uniform and dense ultra-thin film, to provide an anti-counterfeiting silver wire sheet and a security paper using the same to improve the transparency effect of the ultra-thin film and the light reflectance by the dense metal layer.
본 발명의 또 다른 목적은 인쇄층의 상부에 금속증착층을 직접 증착시켜 줌으로서 인쇄층을 다양하게 인쇄시키고 초박막 금속증착을 통하여 클리어 텍스트효과를 얻을 수 있도록 하고, 다른 부가적인 기능도 부여할 수 있도록 된 위조방지용은선 시트 및 이를 이용한 보안용지를 제공하는데 있다.Another object of the present invention is to deposit a metal deposition layer directly on top of the printing layer to print a variety of printing layer and to obtain a clear text effect through ultra-thin metal deposition, and to provide other additional functions. The anti-counterfeiting is to provide a line sheet and a security paper using the same.
본 발명의 상기 및 기타 목적은,The above and other objects of the present invention,
투명필름(11)의 상면에 클리어 텍스트부(12-1) 및 유색문자부(12-2)와 유색문양부(12-3)를 인쇄시켜서 된 것에 있어서,In the case where the clear text portion 12-1, the colored character portion 12-2 and the colored pattern portion 12-3 are printed on the upper surface of the transparent film 11,
투명필름(11)의 상면에 통상의 클리어 텍스트부(12-1) 및 유색문자부(12-2)와 유색문양부(12-3)로 되는 유색문자문양층(12)을 인쇄하고, 유색문자문양층(12)의 상측에 초박막금속증착층(20)을 도포 증착시켜서 된 것을 특징으로 하는 위조방지용 은선시트(10)에 의해 달성된다.On the upper surface of the transparent film 11, the colored text pattern layer 12 which consists of the normal clear text part 12-1 and the colored character part 12-2 and the colored pattern part 12-3 is printed, and it is colored. It is achieved by the anti-counterfeiting silver wire sheet 10, characterized in that the ultra-thin metal deposition layer 20 is applied and deposited on the upper side of the character pattern layer (12).
본 발명의 다른 상기 및 기타 목적은,Other above and other objects of the present invention,
투명필름(11)의 상면에 클리어 텍스트부(12-1) 및 유색문자부(12-2)와 유색문양부(12-3)를 인쇄시키는 것에 있어서,In printing the clear text portion 12-1, the colored character portion 12-2 and the colored pattern portion 12-3 on the upper surface of the transparent film 11,
투명필름(11)의 상면에 통상의 클리어 텍스트부(12-1) 및 유색문자부(12-2)와 유색문양부(12-3)로 되는 유색문자문양층(12)을 인쇄하는 공정과,Printing the colored text pattern layer 12 including the normal clear text portion 12-1, the colored character portion 12-2, and the colored pattern portion 12-3 on the upper surface of the transparent film 11; ,
유색문자문양층(12)의 상측에 초박막금속증착층(20)을 도포 증착시키되, 상기 초박막금속증착층(20)은 상온 플라스마(Plasma)법에 의한 이온 스퍼터링(Ion Sputtering)방법에 의해 증착시켜 주는 공정이 포함되는 것을 특징으로 하는 위조방지용 은선시트의 제조방법에 의해 달성된다.The ultra-thin metal deposition layer 20 is coated and deposited on the colored character pattern layer 12, and the ultra-thin metal deposition layer 20 is deposited by an ion sputtering method by a plasma method. The giving is achieved by a method of manufacturing a forged silver wire sheet for preventing a forgery is included.
본 발명의 다른 상기 및 기타 목적은,Other above and other objects of the present invention,
은선시트를 소정의 크기로 재단하여 은선을 형성하고, 상기 재단된 은선을 종이를 제조할 때에 투입시켜서 된 것에 있어서,In that the hidden wire sheet is cut to a predetermined size to form a hidden wire, and the cut hidden wire is introduced into the paper during manufacture.
투명필름(11)의 상면에 통상의 클리어 텍스트부(12-1) 및 유색문자부(12-2)와 유색문양부(12-3)로 되는 유색문자문양층(12)이 인쇄되고 그 상측에 초박막금속증착층(20)이 상온 플라스마(Plasma)법에 의한 이온 스퍼터링(Ion Sputtering)방법에 의해 증착된 위조방지용 은선시트(10)를 소정의 크기로 재단하고, 소정의 크기로 재단된 위조방지용 은선시트(10)의 은선을 종이를 환망 초지기공정에서 투입하여 제조시켜서 된 것을 특징으로 하는 위조방지용 은선 시트를 이용한 보안용지에 의해 달성된다.On the upper surface of the transparent film 11, a plain text pattern layer 12-1, and a colored text pattern layer 12 consisting of the colored text portion 12-2 and the colored pattern portion 12-3 are printed and the upper side thereof. The forged cut sheet 10 to which the ultra-thin metal deposition layer 20 is deposited by ion sputtering by the plasma method at room temperature to a predetermined size, and cut to a predetermined size. The silver wire of the anti-hidden wire sheet 10 is achieved by the security paper using the anti-counterfeiting silver wire sheet, characterized in that the paper is manufactured by putting the paper in the ring paper machine process.
도 1은 투명필름의 위에 금속피복층을 피복시킨 종래의 위조방지용 은선시 트를 보인 예시도.1 is an exemplary view showing a conventional anti-counterfeiting silver wire sheet coated with a metal coating layer on a transparent film.
도 2는 투명필름의 위에 문자문양을 인쇄시킨 종래의 위조방지용 은선시 트를 보인 예시도.Figure 2 is an illustration showing a conventional anti-counterfeit silver line sheet printed with a character pattern on the transparent film.
도 3은 투명필름의 위에 금속피복층과 문자문양을 반복적으로 피복 및 인 쇄시킨 종래의 위조방지용 은선 시트를 보인 예시도.Figure 3 is an exemplary view showing a conventional anti-counterfeiting silver wire sheet repeatedly coated and printed with a metal coating layer and a letter pattern on the transparent film.
도 4a 및 도 4b는 본 인에 의해 선 출원된 위조방지용 은선 시트를 보인 다 면도.4A and 4B show an anti-counterfeiting hidden wire sheet filed by the present person.
도 5는 본 따른 발명에 위조방지용 은선시트를 보인 예시도.5 is an exemplary view showing the anti-counterfeiting silver wire sheet according to the present invention.
도 6은 본 따른 발명에 위조방지용 은선시트의 다른 실시 예의 예시도.Figure 6 is an illustration of another embodiment of the anti-counterfeiting silver wire sheet according to the present invention.
도 7은 본 따른 발명에 위조방지용 은선시트의 또 다른 실시 예의 예시도.Figure 7 is an illustration of another embodiment of the anti-counterfeiting silver wire sheet according to the present invention.
도 8a 내지 도 8c는 본 따른 발명에 위조방지용 은선시트와 이를 흑백 및 칼라복사한 상태의 예시도.Figures 8a to 8c is an illustration of the anti-counterfeiting silver wire sheet and the state in black and white and color copying in accordance with the present invention.
* 도면의 주요부분에 대한 부호의 설명 *Explanation of symbols on the main parts of the drawings
1.1-1.1-2.1-3.1-4.10.10-1.10-2. 위조방지용 은선시트1.1-1.1-2.1-3.1-4.10.10-1.10-2. Counterfeit Silver Wire Sheet
2.11.15. 투명필름 3. 금속피복층 4. 유색인쇄층2.11.15. Transparent film 3. Metal coating layer 4. Colored printing layer
12. 유색문자문양층 13. 접착층 14. 금속증착층12. Colored character pattern 13. Adhesive layer 14. Metal deposition layer
20. 초박막금속증착층 21. 형광인쇄층20. Ultra thin metal deposition layer 21. Fluorescent printing layer
본 발명의 상기 및 기타 목적과 특징은 첨부도면에 의거한 다음의 상세한 설명에 의해 더욱 명확하게 이해 할 수 있을 것이다.The above and other objects and features of the present invention will be more clearly understood by the following detailed description based on the accompanying drawings.
첨부도면 도 5 내지 도 8c는 본 발명에 따른 위조방지용 은선 시트의 구체적인 실현 예를 보인 예시도로서, 도 5는 본 따른 발명에 위조방지용 은선시트를 보인 일 예시도이고, 도 6 및 도 7은 본 따른 발명의 각기 다른 실시 예의 예시도이며, 도 8a 내지 도 8c는 본 따른 발명에 위조방지용 은선시트와 이를 흑백 및 칼라로 복사한 상태의 예시도이다.Figures 5 to 8c is an exemplary view showing a specific embodiment of the anti-counterfeiting silver wire sheet according to the present invention, Figure 5 is an exemplary view showing the anti-counterfeiting silver wire sheet according to the present invention, Figures 6 and 7 8A to 8C are exemplary views of the anti-counterfeiting hidden wire sheet and the state copied in black and white and the color according to the present invention.
도 5는 본 따른 발명에 위조방지용 은선시트(10)의 기본적인 실시 예를 보인 예시도이다.5 is an exemplary view showing a basic embodiment of the anti-counterfeiting silver wire sheet 10 according to the present invention.
투명필름(11)의 상면에 문자와 문양부분을 제외한 다른 부분에 금속이 피복되어지도록 하는 클리어 텍스트부(12-1)와 문자가 유색으로 인쇄되어지는 유색문자부(12-2) 및 각종문양을 유색으로 인쇄하여 나타내는 유색문양부(12-3)를 반복적으로 인쇄하여 유색문자문양층(12)을 형성하였고, 유색문자문양층(12)의 상측에 초박막금속증착층(20)을 증착시키되 상온 플라스마(Plasma)법에 의한 이온 스퍼터링(Ion Sputtering)방법을 이용하여 증착시켰다.Clear text portion 12-1 to allow metal to be coated on the upper surface of the transparent film 11 except for the character and the pattern portion, colored character portion 12-2 in which the characters are printed in color, and various patterns To print the colored pattern portion (12-3) that is printed by colored to form a colored character pattern layer 12, and to deposit the ultra-thin metal deposition layer 20 on the upper side of the colored character pattern layer (12) It was deposited using an ion sputtering method by the plasma plasma method.
도 6은 본 발명의 다른 실시예인 위조방지용 은선시트(10-1)를 보인 것으로서, 투명필름(11)의 위에 문자와 문양이 클리어 텍스트부(12-1)와 같이 요홈(Negative)형으로 형성되어지는 Nega형 문자문양인쇄층(13)을 인쇄하고, Nega형 문자문양인쇄층(13)의 상측에 초박막금속증착층(20)을 상온 플라스마(Plasma)법에 의한 이온 스퍼터링(Ion Sputtering)방법을 이용하여 증착시켜서 된 것이다.Figure 6 shows another embodiment of the anti-counterfeiting silver wire sheet 10-1 of the present invention, the letters and patterns on the transparent film 11 is formed in the groove (Negative) type, such as clear text portion 12-1 An ion sputtering method of printing a Nega type character pattern printing layer 13 and an ultra-thin metal deposition layer 20 on the upper side of the Nega type character pattern printing layer 13 by a normal temperature plasma method. It was deposited by using.
도 7은 본 발명의 또 다른 실시예인 위조방지용 은선시트(10-2)를 보인 것으로서, 투명필름(11)의 위에 유색문자문양층(12)을 형성하였고, 유색문자문양층(12)의 상측에 형광인쇄층(21)을 피복시켰으며, 형광인쇄층(21)의 상측에 초박막금속증착층(20)을 증착시키되 상온 플라스마(Plasma)법에 의한 이온 스퍼터링(Ion Sputtering)방법을 이용하여 증착시켜서 된 것이다.Figure 7 shows another embodiment of the anti-counterfeiting silver wire sheet 10-2 of the present invention, the colored character pattern layer 12 was formed on the transparent film 11, the upper side of the colored character pattern layer 12 The fluorescent printed layer 21 was coated on the substrate, and the ultra-thin metal deposition layer 20 was deposited on the fluorescent printed layer 21, but deposited using an ion sputtering method using a plasma method. It was made.
상기에서 은선시트(10)의 제조할 때에 기본적으로 사용되어지는 투명필름(11)은 통상적으로 사용되어지는 플라스틱 필름으로서, 그 재질로서는 나일론과 같은 폴리아미드를 비롯하여 폴리에스테르, 폴리아크릴, 폴리비닐아세테이트, 폴리에틸렌 및 폴리비닐 등을 들 수 있다.The transparent film 11 which is basically used in the manufacture of the silver wire sheet 10 is a plastic film which is commonly used, and the material may include polyester, polyacryl, polyvinylacetate, including polyamide such as nylon. , Polyethylene, polyvinyl, and the like.
투명필름(11)의 상면에 금속증착 및 문자나 문양을 인쇄시키는 유색문자문양층(12)의 클리어 텍스트부(12-1) 및 유색문자부(12-2)와 유색문양부(12-3)는 도 1 내지 도 4에 예시된 종래의 위조방지용 은선시트(1 ~ 1-4)에 예시된 유색문자문양층(5)의 클리어 텍스트부(5-1) 및 유색문자부(5-2)와 유색문양부(5-3)와 동일한 방법으로 인쇄하였다.Clear text portion 12-1, colored character portion 12-2 and colored pattern portion 12-3 of the colored character pattern layer 12 for depositing metal and printing characters or patterns on the upper surface of the transparent film 11 ) Is a clear text portion 5-1 and colored character portion 5-2 of the colored character pattern layer 5 illustrated in the conventional anti-counterfeit hidden line sheets 1 to 1-4 illustrated in FIGS. 1 to 4. ) And colored patterns (5-3).
상기 유색문자문양층(12)은 칼라복사를 실시할 때에 어느 정도는 재현될 가능성이 있으므로, 본 발명에서는 유색문자문양층(12)의 상측에 광학적 특성을 부여하기 위하여 금속을 초박막으로 증착하여 초박막금속증착층(20)을 형성하였다Since the colored character glyph layer 12 may be reproduced to some extent when color copying is performed, in the present invention, in order to give optical characteristics to the upper side of the colored character glyph layer 12, the ultra thin layer is deposited by depositing a metal with an ultra-thin film. The metal deposition layer 20 was formed.
통상적으로 금속층을 플라스틱 투명필름에 증착시킬 경우에 금속을 비롯하여 금속화합물 또는 합금을 1300℃정도의 높은 온도와 진공도 10-4torr 정도의 조건에서 가열 증발시켜서 증발금속 또는 증발금속에 의한 화합물을 목적물의 표면에 응축시켜 박막(薄膜)을 형성시키는 방법을 사용하고 있는데, 이러한 방법은 분당 60m 이상의 속도로 증착작업이 용이하지만 피막의 두께가 200 ~ 300 Å 정도로 두꺼워지게 되므로 금속증착부가 색상부분과 겹치거나 중첩될 경우에 유색색상이 보이지 않게 되어 소기의 목적을 달성할 수 없게 되며, 필요한 정도로 얇게 피막을 형성하게 되면 박막의 증착은 용이하게 실시할 수 있으나 균일한 품질을 얻을 수 없게 된다.In general, when the metal layer is deposited on a plastic transparent film, a metal, a metal compound or an alloy and a high temperature of about 1300 ℃ Vacuum degree 10-4It is a method of forming a thin film by condensing the evaporated metal or the compound by the evaporated metal on the surface of the target object by evaporating it under the condition of about torr. Since the thickness of the layer becomes thick about 200 ~ 300 유, when the metal deposition part overlaps or overlaps with the color part, the colored color becomes invisible, and the desired purpose cannot be achieved. Can be easily carried out, but a uniform quality cannot be obtained.
따라서 본 발명에서는 금속증착층의 두께를 용이하게 조절하면서 균일하게 피막시킬 수 있는 이온 스퍼터링(Ion Sputtering)방법을 이용하여 특수 용도로 쓰이는 인듐-주석 산화물이 아닌 일반적으로 많이 이용되는 알루미늄, 니켈 등 저가의 금속과 금, 은 등 고가의 금속을 필요에 따라 얇게 피막시켜 줌으로서 소기의 효과를 얻을 수 있도록 하였다.Therefore, in the present invention, by using the ion sputtering method that can easily coat the thickness of the metal deposition layer easily, indium tin oxide, which is not commonly used for special purposes, is generally used, such as aluminum, nickel, and the like. Expensive metals such as metals, gold, and silver were thinly coated as necessary to obtain desired effects.
도 4a 및 도 4b에 예시된 위조방지용 은선시트(1-3)(1-4)를 제조할 때에 유사한 방법을 사용하기도하지만 이는 기술적인 문제로 인하여 문자문양인쇄층(5)의 바로 위에 금속증착층(6)을 증착시킬 수 없었으므로 두장의 투명필름(7)에 얇은 금속증착층(6)을 각각 증착시킨 후에 두 투명필름(7)을 합쳐 주는 방법을 채택하였으며, 이와 같은 방법에 의해 제조된 은선시트는 두께가 너무 두꺼워 종이를 제조할 때에 은선을 삽입시키게 되면 은선삽입부의 두께가 너무 두꺼워져 종이 두께의 변화가 너무 심하게 발생하였고, 종이를 다량으로 쌓는 경우에는 굴곡이 심하게 일어나는 등의 문제가 발생하였었다.A similar method may be used to manufacture the anti-counterfeit silver wire sheets 1-3 and 1-4 illustrated in Figs. 4A and 4B, but due to technical problems, metal deposition is performed directly on the character pattern printing layer 5. Since the layer 6 could not be deposited, a method of combining the two transparent films 7 after depositing the thin metal deposition layers 6 on the two transparent films 7, respectively, was adopted. When the silver wire sheet is too thick, when the silver wire is inserted when manufacturing the paper, the thickness of the silver wire insertion portion is too thick, and the change of the paper thickness is too severe. When the paper is stacked in a large amount, the bending occurs badly. Had occurred.
본 발명에서는 상기와 같은 문제를 해소할 수 있도록 하기 위하여 상온 플라스마(Plasma)법에 의한 이온 스퍼터링(Ion Sputtering)방법을 이용하여 피막(증착)시켜 주었는데, 진공도 10-4torr에서 조건을 안정화시킨 후에 최종적으로 10-3내지 8 X 10-4torr 조건에서 3m 이하의 저속으로 필름 및 유색문자문양층(12)의 위에 직접 초박막금속증착층(20)을 균일하고 조밀하게 증착시키는 방법을 채택하여 증착공정을 단순화시키고 효율은 크게 증가시킬 수 있도록 하면서 위조방지용 은선시트(10)를 용이하게 제조할 수 있도록 하였다.In the present invention, in order to solve the above problems, the film was deposited (deposited) using an ion sputtering method by a plasma method at room temperature, and after stabilizing conditions at a vacuum degree of 10 -4 torr, Finally, the method is deposited by adopting a method of uniformly and densely depositing the ultra-thin metal deposition layer 20 directly on the film and the colored character pattern layer 12 at a low speed of 3 m or less under the condition of 10 -3 to 8 X 10 -4 torr. While simplifying the process and allowing the efficiency to be greatly increased, it was possible to easily manufacture the anti-counterfeiting silver wire sheet 10.
상기와 같이 이온 스퍼터링(Ion Sputtering)방법을 이용하여 유색문자문양층(12)의 위에 초박막금속증착층(20)을 피막(증착)시킬 때에 광학적 반사 및 반투명효과를 얻을 수 있도록 하기 위하여 초박막금속증착층(20)의 두께를 50 ~ 100 Å정도 이하가 되도록 하였으며, 이를 효율적으로 확인하기 위하여 광학적 밀도(Optical Density: OD)를 측정 비교하였는데, 발명의 목적에 부합되는 여러 가지 특성을 고려하여 다음의 공식1에 의해 산출되는 광학적 밀도(Optical Density: OD)는 0.15 ~ 0.3, 광투과량이 70%에 가깝도록 하였다.As described above, in order to obtain an optical reflection and a translucent effect when the ultra thin metal deposition layer 20 is deposited (deposited) on the colored character glyph layer 12 using the ion sputtering method, ultra thin metal deposition is performed. The thickness of the layer 20 was set to 50 ~ 100 이하 or less, and the optical density (OD) was measured and compared in order to check this efficiently. The optical density (OD) calculated by Equation 1 was 0.15 to 0.3 and the light transmittance was close to 70%.
공식 1: 광학적 밀도(OD) = log10(I0/I) Formula 1 : optical density (OD) = log 10 (I 0 / I)
(I(I 00 : 필름에 유입되는 초기 빛의 세기, I:필름을 투과하여 나오는 빛의 세기): Initial light intensity entering the film, I: Light intensity passing through the film)
본 발명에서 초박막금속증착층(20)을 증착시키는데 사용되는 금속으로는 광학적반사율이 우수한 알루미늄을 비롯하여 니켈, 금, 은, 티탄 등을 들 수 있으며, 상기 금속을 단일물질로 하여 사용하거나, 반사율을 향상시키기 위하여 두 종류 이상의 금속을 복합하여 사용할 수 있으며, 또한 필요에 따라 유색문자문양층(12)의 위에 또는 상기 유색문자문양층(12)의 위와 투명필름(11)의 저면에 증착시킬 수 있으나 어느 일면에만 증착시키더라도 필요한 광학적 성질 및 전자기적 특성을 충족시키는 것으로 확인되었다.Examples of the metal used for depositing the ultra-thin metal deposition layer 20 in the present invention include aluminum, nickel, gold, silver, and titanium, which are excellent in optical reflectivity. In order to improve, two or more kinds of metals may be used in combination, and may be deposited on the colored character pattern layer 12 or on the colored character pattern layer 12 and the bottom of the transparent film 11 as necessary. Deposition only on one side was found to meet the required optical and electromagnetic properties.
특히, 광학적 특성을 얻기 위하여 필요에 따라 티탄 등의 금속을 질소산화물로 변환시켜 본 발명에 따른 이온 스퍼터링(Ion Sputtering)방법에 의해 증착시킬 수 있으며, 이와 같이 실시하게 되면 다양한 외관의 색상을 얻을 수 있게 된다.Particularly, in order to obtain optical properties, metals such as titanium may be converted into nitrogen oxides as needed to be deposited by ion sputtering according to the present invention. Will be.
도 6에 예시된 위조방지용 은선시트(10-2)는 투명필름(11)의 위에 통상의 인쇄방법을 이용하여 Nega형 문자문양인쇄층(13)을 인쇄하고, 그 위에 이온 스퍼터링(Ion Sputtering)방법에 의해 초박막금속증착층(20)을 증착시키되 금속층을 100 Å정도 또는 양면에 70 Å정도를 부가하여 줌으로써 부분제거금속방법을 이용하는 클리어 텍스트부(12-1)가 되도록 하였으며, 특히 Nega형 문자문양인쇄층(13)을 인쇄시킬 때에 광학적 또는 전기적 효과를 향상시키기 위하여 일반잉크에 알루미늄 등의 메탈릭잉크를 5 ~ 20% 정도 혼합시켜 사용할 수 있다.The anti-counterfeiting silver wire sheet 10-2 illustrated in FIG. 6 prints the Nega type letter pattern printing layer 13 on the transparent film 11 by using a conventional printing method, and ion sputtering thereon. The ultra-thin metal deposition layer 20 was deposited by the method, but the metal layer was added to about 100 mm or 70 mm on both sides to form a clear text portion 12-1 using the partially removed metal method. In order to improve the optical or electrical effect when printing the pattern printing layer 13, it can be used by mixing a metallic ink such as aluminum to about 5 to 20%.
상기와 같이 제조된 본 발명에 따른 위조방지용 은선시트(10)(10-1)(10-2)는 복사를 실시하더라도 색상이 재현되지 않게 되고 반사에 의한 광학적 효과에 의해 투입여부가 잘 나타나지 않으면서도 전자기적 특성을 갖고 있으므로 기기감응 요소로 활용할 수 있을 뿐만 아니라 위조방지 및 진위감별을 효과적으로 수행할 수 있게 된다.The anti-counterfeiting silver wire sheet 10 (10-1) (10-2) according to the present invention manufactured as described above is not reproduced even if the copy is carried out, if the addition is not well represented by the optical effect due to reflection In addition, because it has electromagnetic characteristics, it can be used not only as a device-sensing factor, but also effectively perform counterfeit prevention and authenticity discrimination.
본 발명에 따른 위조방지용 은선시트(10)(10-1)(10-2)는 최종적으로 1 ~ 5mm의 폭으로 재단하여 보안용지를 제조할 때에 사용(투입)되어지는 은선으로 제조되어지는데, 상기와 같이 제조된 은선은 보안용지를 제조하는 공정 중에서 일반적으로 환망 또는 장망에서 종이 지필이 생성되는 과정 중에 삽입(투입)하여 제조하거나 또는 지필이 생성된 후에 2개의 종이를 합지하는 과정 중에 종이의 사이에 투입하여 제조하게 되며, 상기 은선은 종이의 내부에 완전히 삽입시키거나 또는 부분적으로 노출시키면서 제조할 수 있다.Anti-counterfeiting silver wire sheet 10 (10-1) (10-2) according to the present invention is made of a silver wire that is used (input) when finally cut to a width of 1 ~ 5mm to manufacture a security paper, The silver wire manufactured as described above is manufactured by inserting (inserting) paper in the process of producing security paper in the process of manufacturing security paper, or by laminating two papers after paper is produced. It is prepared by putting in between, and the silver wire may be prepared by fully inserting or partially exposing the inside of the paper.
이하, 본 발명을 실시 예 및 비교 예에 이해 구체적으로 설명한다. 본 발명이 이들 실시 예 및 비교 예에 의해 한정되거나 제한되지 않음을 밝혀둔다.Hereinafter, the present invention will be specifically described in Examples and Comparative Examples. It is to be understood that the invention is not limited or limited by these Examples and Comparative Examples.
은선시트 및 은선의 제조Manufacture of hidden line sheet and hidden line
실시 예 1Example 1
두께가 25미크론인 투명(플라스틱)필름(11)에 문자 문양이 클리어 텍스트부(12-1)와 같은 Negative형으로 형성되어지도록 Nega형 문자문양인쇄층(13)을 그라비어방법으로 인쇄하고, Nega형 문자문양인쇄층(13)의 위에 본 발명에 따른 이온 스퍼터링(Ion Sputtering)방법으로 초박막금속증착층(20)을 70 Å두께로 증착하여 위조방지용 은선시트 A를 제조하였다.The Nega type character pattern printing layer 13 is printed on the transparent (plastic) film 11 having a thickness of 25 microns by the gravure method so that the character pattern is formed in a negative type such as the clear text part 12-1. The anti-counterfeiting silver wire sheet A was prepared by depositing the ultra-thin metal deposition layer 20 at a thickness of 70 mm on the type-pattern-printed layer 13 by the ion sputtering method according to the present invention.
상기와 같이 제조된 위조방지용 은선시트A를 1.2mm의 폭으로 재단하여 은선을 제조하였다.The anti-counterfeiting silver wire sheet A prepared as described above was cut to a width of 1.2 mm to prepare a silver wire.
실시 예 2Example 2
두께가 25미크론인 투명(플라스틱)필름(11)에 문자 문양이 클리어 텍스트부(12-1)와 같은 Negative형으로 형성되어지도록 Nega형 문자문양인쇄층(13)을 그라비어방법으로 인쇄하고, Nega형 문자문양인쇄층(13) 및 뒷면에 본 발명에 따른 이온 스퍼터링(Ion Sputtering)방법으로 60 Å두께의 초박막금속증착층(20)을 양면 증착하여 위조방지용 은선시트(B)를 제조하였다.The Nega type character pattern printing layer 13 is printed on the transparent (plastic) film 11 having a thickness of 25 microns by the gravure method so that the character pattern is formed in a negative type such as the clear text part 12-1. The anti-counterfeiting silver wire sheet (B) was prepared by depositing both surfaces of the ultra-thin metal deposition layer 20 having a thickness of 60 mm on the type-pattern-printed layer 13 and the ion sputtering method according to the present invention.
상기와 같이 제조된 위조방지용 은선시트(B)를 1.5mm의 폭으로 재단하여 은선을 제조하였다.The anti-counterfeiting silver wire sheet (B) prepared as described above was cut to a width of 1.5mm to produce a silver wire.
실시 예 3Example 3
두께가 25미크론인 투명(플라스틱)필름(11)에 문자 문양을 그라비어방법으로 인쇄하여 은선시트(B)를 형성하고, 상기 은선시트(B)에 클리어 텍스트부(12-1)를 형성시키기 위해 수세 가능한 잉크로 소정의 문자를 인쇄한 후에 일반적인 금속증착방법에 의해 금속층을 증착시킨 후에 수세 처리하여 은선시트(C)를 형성하였으며, 이와 같이 형성된 은선시트(C)에 본 발명에 따른 이온 스퍼터링(Ion Sputtering)방법에 의해 60 Å두께의 초박막금속증착층(20)을 증착하여 위조방지용 은선시트(D)를 제조하였다.In order to form a hidden line sheet B by printing a character pattern on a transparent (plastic) film 11 having a thickness of 25 microns by a gravure method, and to form a clear text portion 12-1 on the hidden line sheet B. After printing a predetermined letter with a washable ink, a metal layer was deposited by a general metal deposition method, followed by washing with water to form a hidden wire sheet C. The ion sputtering according to the present invention was performed on the formed silver wire sheet C. The anti-counterfeiting silver wire sheet (D) was prepared by depositing an ultra-thin metal deposition layer 20 having a thickness of 60 mm by ion sputtering).
상기와 같이 제조된 위조방지용 은선시트(D)를 1.5mm의 폭으로 재단하여 은선을 제조하였다.The anti-counterfeiting silver wire sheet (D) prepared as described above was cut to a width of 1.5mm to produce a silver wire.
비교 예 1Comparative Example 1
두께가 25미크론인 투명(플라스틱)필름(11)에 일반적인 방법으로 금속피복층을 증착한 후에 문자 및 문양이 형성되도록 선택적으로 금속을 제거시켜 클리어 텍스트(Clear Text)형으로 되는 도 1에 예시된바와 같은 위조방지용 은선시트를 제조하였고, 상기와 같이 제조된 위조방지용 은선시트를 1.5mm의 폭으로 재단하여 은선을 제조하였다.After depositing a metal coating layer on a transparent (plastic) film 11 having a thickness of 25 microns in a general manner, the metal and the pattern may be selectively removed to form a clear text, as illustrated in FIG. The same anti-counterfeiting silver wire sheet was prepared, and the anti-counterfeiting silver wire sheet prepared as described above was cut to a width of 1.5 mm to prepare a silver wire.
비교 예 2Comparative Example 2
두께가 25미크론인 투명(플라스틱)필름(11)의 일면에 그라비어인쇄방법에 의해 1.0mm의 문자 및 문양을 유색으로 인쇄하고, 클리어 텍스트(Clear Text)부를 성형시키기 위해 수세잉크로 일정한 문자를 재차 인쇄하며, 일반 금속증착방법에 의해 금속층을 증착시킨 후에 수세 처리하여 도 3에 예시된바와 같은 위조방지용 은선시트를 제조하였고, 상기와 같이 제조된 위조방지용 은선시트를 1.5mm의 폭으로 재단하여 은선을 제조하였다.On the one side of the transparent (plastic) film 11 having a thickness of 25 microns, 1.0 mm of letters and patterns are printed in color by a gravure printing method, and certain characters are washed again with a flush ink to form a clear text part. After printing, by depositing a metal layer by a general metal deposition method and washing with water to prepare a forged anti-counterfeit silver wire sheet as shown in Figure 3, the anti-counterfeiting silver wire sheet prepared as described above cut to 1.5mm in width Was prepared.
보안용지의 제조Manufacture of security paper
실시 예 4Example 4
실시 예 1과 실시 예3에 의해 제조된 은선을 보안용지를 제조할 때에 환망 초지기에서 통상의 은선투입방법으로 투입하여 단일지필 내에 직접 삽입하여 은선이 완전 삽입되는 은폐형 보안용지를 제조하였다.When the silver wires prepared by Examples 1 and 3 were prepared for the security paper, a concealed security paper in which the silver wire was completely inserted was prepared by directly inserting the silver wire into a single paper by using a conventional silver wire injection method in a paper machine.
실시 예 5Example 5
실시 예 2에 의해 제조된 은선을 보안용지를 제조할 때에 환망 초지기에서 통상의 부분노출은선제조방법으로 종이에 투입하여 은선이 부분적으로 노출되는 부분노출형 보안용지를 제조하였다.When the silver wire produced in Example 2 was manufactured for the security paper, a partial exposure type security paper in which the silver wire was partially exposed was prepared by inserting the conventional partial exposure to paper by a preliminary manufacturing method in a ring paper machine.
비교 예 3Comparative Example 3
비교 예 1에 의해 제조된 은선을 보안용지를 제조할 때에 환망 초지기에서 통상의 부분노출은선제조방법으로 종이에 투입하여 은선이 부분적으로 노출되는 부분노출형 보안용지를 제조하였다.When producing the security paper of the silver wire produced by Comparative Example 1, a conventional partially exposed silver paper was introduced into a paper by a preliminary manufacturing method to produce a partially exposed security paper in which the silver wire was partially exposed.
비교 예 4Comparative Example 4
비교 예 2에 의해 제조된 은선을 보안용지를 제조할 때에 환망 초지기에서 통상의 은선투입방법으로 투입하여 은선이 완전 삽입되는 은폐형 보안용지를 제조하였다.When the silver wire produced in Comparative Example 2 was prepared for the security paper, a hidden type security paper into which the silver wire was completely inserted was prepared by inserting the silver wire into a conventional silver wire feeding method in a paper machine.
상기 실시 예에 의해 제조된 은선의 보안요소로서의 특성을 확인하기 위하여 본 발명에 따른 은선 자체 및 보안용지와 기존의 방법으로 제조된 은선 및 보안용지의 광학적 특성 및 전자기적 특성을 측정 비교하였다.In order to confirm the characteristics of the hidden line manufactured as a security element according to the above embodiment, the optical and electromagnetic properties of the hidden line itself and the security paper according to the present invention and the hidden line and the security paper manufactured by the conventional method were measured and compared.
광학적 특성은 칼라복사 및 스캐너에 의한 재현성을 검토하였고, 기기 감응요소로 활용하기위한 전자기적 특성은 보안요소가 실제적으로 활용할 때에 종이의 내부에 삽입되어 있는 점을 감안하여 여러 형태의 은선을 종이의 내부에 삽입하고 본 실험에 부합되도록 실험적으로 제조된 장비를 이용하여 각 시료의 정전용량(Capacitance)을 측정하여 비교 검토하였다.The optical characteristics were reviewed by the color copying and the reproducibility by the scanner.The electromagnetic characteristics to be used as the device-sensitizing elements were taken into consideration by the fact that the security elements were inserted inside the paper when they were actually used. The capacitance of each sample was measured and compared with each other by using the equipment that was inserted inside and experimentally manufactured to meet the present experiment.
그 결과를 다음의 측정비교표에 기록하였다.The results are recorded in the following comparison tables.
(측정비교표)(Measurement comparison table)
상기 측정비교표에서 확인되는 바와 같이, 실시 예1 및 실시 예2의 방법에 의해 제조된 은선시트의 은선은 비교 예1의 기존 은선시트의 은선과는 특성 면에서 별다른 차이가 없었을 뿐만 아니라 초박막금속층의 반사에 의해 독특한 금속색상도 나타나 복사방지효과가 매우 뛰어난 것으로 판단되었다.As can be seen from the measurement comparison table, the silver wire of the silver wire sheet manufactured by the method of Example 1 and Example 2 was not significantly different from the silver wire of the conventional silver wire sheet of Comparative Example 1, as well as the ultra thin metal layer. It was also judged that the anti-radiation effect was very excellent due to the unique metal color caused by the reflection.
또한 부분노출형인 실시 예3과 같은 방법으로 제조된 은선시트의 은선을 베교 예2의 방법에 의해 제조된 은선시트의 은선과 비교하여 볼 때에 본 발명에 따른 은선시트의 은선은 칼라복사를 실시하게 되면 유색문자의 색상이 재현되지 않으면서도 육안에 의해서는 인쇄된 유색문자를 확인할 수 없었을 뿐만 아니라 형광효과를 그대로 나타내고 있었으며, 따라서 위조를 방지하는 효과뿐만 아니라 전자기적 특성도 우수하여 전반적으로 위조 및 변조 방지요소로서의 활용성이 매우 양호함을 확인할 수 있었다.In addition, when the silver wire of the silver wire sheet manufactured by the same method as Example 3 of the partially exposed type is compared with the silver wire of the silver wire sheet prepared by the method of Example 2, the hidden wire of the silver wire sheet according to the present invention is subjected to color copying. When the color of the colored letters was not reproduced, the printed colored letters could not be confirmed by the naked eye, and the fluorescence effect was shown as it is. It was confirmed that the utility as a preventive element is very good.
특히 도 8a 예시된바와 같이 본 발명에 따른 위조방지용 은선시트(10)(10-1)(10-2)를 통상의 고성능 복사기를 사용하여 흑백 및 칼라로 복사한 결과 도 8b 및 도 8c에 예시된바와 같이 원본인도 8a 의 위조방지용 은선시트(10)(10-1)(10-2)와는 전혀 다르게 복사되어 위조가 불가능함을 확인할 수 있었다.In particular, as illustrated in FIG. 8A, the anti-counterfeiting silver wire sheet 10, 10-1, 10-2 according to the present invention is copied in black and white and color using a conventional high-performance copier, and is illustrated in FIGS. 8B and 8C. As shown, the original Indian 8a counterfeit anti-counterfeit sheet 10 (10-1) (10-2) was completely different from the copy could be confirmed that the forgery.
이상에서와 같이 본 발명에 따른 위조방지용 은선시트는, 초박막금속층이 반투명효과를 갖고 있어 인쇄에 의한 여러 가지의 효과를 효율적으로 부각시킬 수 있고, 복사를 실시할 때에 전혀 원본과 다르게 재현되어 위조방지기능의 효과가 매우 우수한 특징을 갖게 되며, 금속의 전자기적 특성도 우수하여 현대사회의 기기자동화에 부합되는 기기감응 요소로서의 활용성도 매우 높일 수 있게 된다.As described above, the anti-counterfeiting silver wire sheet according to the present invention, the ultra-thin metal layer has a translucent effect, can effectively highlight various effects by printing, and is reproduced differently from the original when copying, thereby preventing counterfeiting. The effect of the function is very excellent, and the electromagnetic characteristics of the metal are also excellent, so that the utilization as a device-sensing factor that is suitable for the automation of devices in the modern society can be greatly enhanced.
Claims (12)