KR20040023456A - Bandage for functional cast - Google Patents
Bandage for functional cast Download PDFInfo
- Publication number
- KR20040023456A KR20040023456A KR1020020055189A KR20020055189A KR20040023456A KR 20040023456 A KR20040023456 A KR 20040023456A KR 1020020055189 A KR1020020055189 A KR 1020020055189A KR 20020055189 A KR20020055189 A KR 20020055189A KR 20040023456 A KR20040023456 A KR 20040023456A
- Authority
- KR
- South Korea
- Prior art keywords
- weight
- parts
- bandage
- ceramic
- bio
- Prior art date
Abstract
Description
본 고안은 기능성 카스트(cast)용 붕대(繃帶)에 관한 것이다. 종래 외과적 골절이나 탈골을 정형(整形), 고정(固定)하기 위하여 사용되는 카스용 붕대는 주로 신축성을 위한 펀직, 또는 통기성을 위한 조밀도로 직조된 붕대지에 프라스터(석고)나 가습경화성 합성수지 등의 경화제(硬化濟)를 도포하여 붕대로 사용할 때 물에 담궈 가수(加水)시킨 다음 외과적 환부에 카스트용 붕대를 감은 후 건조와 함께 경화되어 뼈가 움직이지 않도록 고정하게 되어 있다.The present invention relates to a bandage for a functional cast. Conventional surgical bandages or casing bandages used for shaping or fixing the dislocations are mainly used for elasticity such as puncture for elasticity, or breathable density bandage papers such as plasters or humidified hardenable synthetic resins. When applied with a bandage of hardener (담 化 濟) and soaked in water to add water ((水水)) and then wound the cast bandages on the surgical affected area is cured with drying to fix the bones do not move.
종래의 카스트용 붕대는 주로 경화제에 의한 붕대의 정형경화(整形硬化)에 주안을 두고 구성되어 있으나 환부에 붕대를 감고 경화시키어 장기간 지나게 되면 피부에 붕대의 압박으로 인하여 혈액순환이 장해를 받아, 저리고 가려우며 때로는 땀등의 습기로 인하여 세균감염에 의한 환부에 피부염이 생기는 등의 문제점이 있었다.Conventional caste bandages are mainly composed of orthopedic hardening of bandages by a hardener, but when the bandage is applied to the affected area and cured, the blood circulation is disturbed due to the pressure of the bandage on the skin. Itching and sometimes there was a problem such as dermatitis caused by bacterial infection due to moisture such as sweat.
본 발명의 목적은 정형외과에서 사용되는 카스트용 붕대에 있어서, 붕대의 경화제에 바이오 세라믹을 배합하여 원적외선이 방출되고 음이온이 생성되며 항균작용이 있는 기능성 붕대를 제조하여, 환부에 붕대를 감아 경화제에 의하여 경화하였을 때, 붕대의 경화제에서 방출되는 원적외선에 의하여 환부의 혈액순환을 촉진하여 저리거나 가려움증이 없고 음이온이 생성되어 피부의 건강을 유지하며 항균작용에 의하여 땀등의 습기로 인한 접촉성 피부염의 감염을 방지하는 카스트용 붕대를 제공하려는데 있다.An object of the present invention in the cast bandage used in orthopedic surgery, by combining bio-ceramic to the curing agent of the bandage to produce a functional bandage with far-infrared radiation, anion is generated and antibacterial action, wound the bandage on the affected area to the curing agent When it is cured, it promotes blood circulation of affected area by far infrared rays emitted from the hardening agent of bandage, there is no tingling or itching, anion is generated to maintain skin health, and antibacterial action causes contact dermatitis due to moisture such as sweat It is to provide a caste bandage to prevent.
본 발명은 상기한 목적을 달성하기 위하여 좌우로 신축성이 양호한 편직으로 된 붕대지, 또는 통기성을 위하여 조밀도로 직조된 붕대지에 프라스터, 또는 폴리우레탄수지등의 경화제를 침지시켜서 된 카스트용 붕대에 있어서, 상기 경화제에, 청맥반석, 지르코니아, 알루미나실리케이트, 해록석, 게르마늄함유 황토, 투어마린, 운모등의 광물질의 혼합물로 된 바이오 세라믹 분말(300메시정도)을 3-15증량% 범위로 배합하여 붕대지에 경화제와 함께 도포시키어 기능성 카스용 붕대를 제조하는 것이다.In order to achieve the above object, the present invention relates to a bandage made of good stretchable knit fabric from side to side, or to a caster bandage made by immersing a curing agent such as a praster or a polyurethane resin on a bandage paper woven in a density for breathability. In the hardening agent, bio-ceramic powder (about 300 mesh) of a mixture of minerals such as blue vein, zirconia, alumina silicate, haeolite, germanium-containing loess, tourmarine, mica, etc. is mixed in a range of 3-15% by weight to bandages. It is apply | coated with a hardening | curing agent, and the bandage for functional casing is manufactured.
본 발명의 카스트용 붕대는 골절이나 탈골등 정형외과적 환부에 솜을 먼저 피부에 소정의 두께로 대고 감는다. 감기전에 물에 침지시켜 가수한 다음 건조전에 붕대를 환부에 조심스럽게 감으면 건조와 더불어 경화되어 환부를 고정시킨다.In the cast bandage of the present invention, the cotton is first wound on the skin to orthopedic lesions such as fractures and dislocations to a predetermined thickness. After winding, soak in water before winding, and carefully wrap the bandage on the affected area before drying, and harden with drying to fix the affected area.
본 발명의 기능성 카스트용 붕대의 경화제에는 바이오 세라믹 분말이 배합되어 있기 때문에 광물질의 특성으로 인하여 원적외선과 음이온이 방출된다.Since the bio-ceramic powder is contained in the hardening agent of the functional cast bandage of this invention, a far infrared ray and an anion are emitted by the characteristic of a mineral.
따라서 붕대로 압박되어 있는 부분이 바이오 세라믹에서 방출되는 원적외선에 의한 내부적 발열작용으로 혈액순환이 촉진된다. 또한 바이오 세라믹에서 방출되는 전자의 전리작용으로 공기중의 산소가 분해되어 산소음이온을 생선시키어 피부에 건강을 부여하고 청록석의 항균작용으로 카스트부분의 피부에 땀의 습기로 인한 세균의 감염이 억제되어 피부염을 방지하게 된다.Therefore, the part pressurized by the bandage is promoted blood circulation by the internal exothermic action by the far infrared rays emitted from the bio-ceramic. In addition, oxygen in the air is decomposed by the ionization of electrons emitted from the bio-ceramic to give oxygen anion to give health to the skin, and the antibacterial action of turquoise prevents the infection of bacteria due to the moisture of sweat on the skin of the cast part. It prevents dermatitis.
본 발명에서 사용되는 청맥반석은 맥반석중 청색상이 보다 강한 응회암으로서 장석과 석영이 주 구성광물이고 여기에 녹염석, 녹니석, 불투명광물 점토광물이 함유된 것으로서 맥반석과 조성이 유사한 바이오 세라믹이다.Blue gangue rock used in the present invention is a tuff rock with a stronger blue phase among gangue rocks, feldspar and quartz are the main constituent minerals, and chlorite, chlorite, and opaque mineral clay minerals are included in the bio-ceramic composition.
해록석은 초도 약돌이라고 하며, 특히 대장균 녹농균에 대한 항균작용이 양호한 바이오 세라믹이다.Haeokseok is called the first stone, and is a particularly good bio-ceramic antibacterial activity against E. coli Pseudomonas aeruginosa.
청맥석과 청록석은 적어도 1200℃에서 3시간 정도 소성하여 광물함유 화학수분이 제거된 것을 사용한다. 또한 이들 혼합광물질은 볼밀에 의하여 적어도 300메시 이상의 미세분말로 분쇄하여 90-100℃의 열풍으로 건조시킨 분말을 사용한다. 이들 바이오 세라믹의 원적외선 및 음이온방출에 대한 실험결과는 이미 여러가지 시험데이터에 의하여 공지되어 있다.Blue veins and cyan stones are calcined at least at 1200 ° C for 3 hours to remove mineral-containing chemical moisture. In addition, these mixed minerals are pulverized into a fine powder of at least 300 mesh by a ball mill and used to dry the powder by hot air of 90-100 ℃. Experimental results for the far infrared and anion emission of these bioceramics are already known by various test data.
본 발명에서는 이러한 바이오 세라믹을 이용하여 카스트용 붕대를 기능성 붕대를 제조한 것이다.In the present invention, using the bio-ceramic to prepare a functional bandage bandage for caste.
본 발명의 카스트 붕대는, 화부에 감아 카스팅하였을 때 장시간이 경과하여 도 혈액순환의 촉징으로 저리거나 가려움증이 없고 통증을 완화하기 때문에 참을성이 부족한 어린이나 피부가 유약한 여성환자를 비롯하여 누구에게나 유용하게 사용할 수 있다.The caste bandage of the present invention is useful for anyone who is impatient or a woman with weak skin because it does not soothe or itch and soothe pain due to blood circulation even after prolonged periods when the cast is wound around the fire department. Can be used.
신축성이 양호한 편직이나 통풍을 위하여 조밀도(粗密度)로 직조된 붕대지(繃帶地)에 프라스터, 또는 폴리우레탄 수지 등의 경화제를 침지시켜서 된 카스트용 붕대에 있어서, 경화제 100 중량부에 대하여 원적외선이 방출되고 음이온이 생성되는 바이오 세라믹 분말을 3- 15중량부를 균일하게 배합하여 기능성 카스트용 붕대를 제조한다.A caster bandage in which a curing agent such as a praster or a polyurethane resin is immersed in a bandage paper woven at a density for good knitting or ventilation, with respect to 100 parts by weight of the curing agent. A bandage for a functional cast is prepared by uniformly blending 3-15 parts by weight of a bio-ceramic powder that emits far infrared rays and generates anions.
상기 바이오 세라믹은 다음의 실시예로 조성된 것을 사용한다.The bio-ceramic uses the composition of the following examples.
(1) 제1실시예(1) First embodiment
청맥반석 60중량부,Blue Lean Rock 60 parts by weight,
지르코니아(zirconia) 10중량부,10 parts by weight of zirconia,
알루미노실리게이트 20중량부,20 parts by weight of aluminosilicate,
코디어라이트(cordierte) 10 중량부를10 parts by weight of cordierite
균질로 혼합하여 상기 바이오 세라믹 5 - 10중량부를 상기 경화제 100중량부에 균질로 배합하여 바이오 세라믹이 배합된 경화제를 붕대지에 침지도포하여 본 발명의 기능성 카스트 붕대를 제조한다.By mixing homogeneously, 5-10 parts by weight of the bio-ceramic compound is homogeneously mixed with 100 parts by weight of the curing agent, the curing agent containing the bio-ceramic is immersed in a bandage to prepare a functional cast bandage of the present invention.
(2) 제2실시예(2) Second Embodiment
청맥반석 30중량부Blue Lean Rock 30 parts by weight
해록석(glauconite) 30중량부30 parts by weight of glauconite
게루마늄함유황토 20중량부20 parts by weight of germanium-containing sulfur
투어멀린(taurmalin) 10중량부10 parts by weight of tourmaline
운모 10중량부를10 parts by weight of mica
균질로 혼합하여 상기 바이오 세라믹 2-5중량부를 상기 경화제 100중량부에배합하여 바이오 세라믹이 배합된 경화제를 붕대지에 침지도포하여 본 발명의 기능성 카스트용 붕대를 제조한다.Mixing homogeneously and mixing 2-5 parts by weight of the bio-ceramic to 100 parts by weight of the curing agent, the curing agent containing the bio-ceramic is immersed in a bandage to prepare a bandage for the functional cast of the present invention.
상기 청맥반석은 적어도 1200℃에서 3시간정도 소성하여 광물함유수분을 제거한 것을 사용하며 모든 광물질은 적어도 300메시 이상의 분말로 분쇄한 것을 사용한다.The blue rock is used to remove mineral-containing water by calcining at least 1200 ℃ for 3 hours, and all minerals are ground to powder of at least 300 mesh or more.
제1실시예의 조성물로 제조된 기능성 카스트용 붕대와, 제2실시예의 조성물로 제조된 기능성 카스트용 붕대는 동일한 용도로 사용하며 고온에서 소성된 바이오 세라믹에 의하여 원적외선이 방출되어 붕대를 감은 환부의 깊숙이 원적외선이 침투하여 발열되면서 혈액순환을 촉진하는 역할을 한다.The functional cast bandage made of the composition of the first embodiment and the functional cast bandage made of the composition of the second embodiment are used for the same purpose, and the deep infrared rays are released by the bio- ceramic fired at a high temperature to cover the bandaged area. Far infrared rays penetrate and generate heat, thereby promoting blood circulation.
제2실시예의 조성물에는 해록석과 게르마늄함유 황토와 투어멀린 및 운모가 포함되어 있기 때문에 이들 광물질에서 전자가 전리작용을 할만큼 에너지를 가지고 방출하기 때문에 붕대를 사용하였을때 경화제에 배합된 바이오 세라믹에서 방출되는 전자에 의하여 공기중의 산소분자가 쉽게 음이온화 되어서 붕대를 감은 환부의 피부의 건강을 촉진하며 항균작용을 갖는다.Since the composition of the second embodiment includes rustite, germanium-containing loess, tourmaline, and mica, electrons are emitted from these minerals with energy enough to ionize, which is then released from the bio-ceramic compounded in the curing agent when the bandage is used. Oxygen molecules in the air are easily anionized by electrons to promote the health of the skin that is bandaged and have antibacterial activity.
해록석에 대한 대장균 및 녹농균에 대한 항균시험성적은 다음 표와 같다.The antimicrobial test results for E. coli and Pseudomonas aeruginosa against halite stone are shown in the following table.
[표 1]TABLE 1
표1에서 해록석에 의하여 가장 흔한 대장균은 95%, 녹농균은 94%의 항균작용을 나타내고 있어 본 발명의 기능성 카스트용 붕대의 항균작용이 있음을 알 수 있다. 또한 해록석은 게르마늄이(Ge) 1.19ppm, 세리움(Se) 0.10ppm이 방출된다.In Table 1, the most common Escherichia coli is 95%, and Pseudomonas aeruginosa has an antibacterial effect of 94%, indicating that there is an antimicrobial activity of the functional caste bandage of the present invention. Also, rustite is released of 1.19 ppm of germanium (Ge) and 0.10 ppm of cerium (Se).
이는 붕대를 감은 부위의 피부에 대한 항균작용이 양호함을 알 수 있다. 또한 청맥반석의 원적외선(5-20㎛)의 방사율 0.94 방사에너지 (W/m².㎛,40℃)는 3.79x102이다.It can be seen that the antimicrobial effect on the skin of the bandaged area is good. In addition, the emissivity 0.94 of the far infrared ray (5-20㎛) of blue vein rock is 3.79x10 2 .
이와 같이 본 발명의 카스트용 붕대는 종래의 것과 달리 경화제에 배합된 바이오 세라믹의 기능성에 의하여 혈액순환의 촉진되어 저리거나 가려움증이 없고 항균작용에 의하여 카스팅부위의 피부질환의 감염을 방지하므로 정형외과의 골절, 탈골등의 정형고정의 카스트용 붕대로서 보다 유용하게 사용할 수 있다.As described above, caste bandages of the present invention are orthopedics because they prevent the infection of the skin disease of the cast site by antibacterial action due to the promotion of blood circulation due to the functionality of the bio-ceramic compounded in the curing agent, without tingling or itching. It can be used more effectively as a bandage for caste of orthopedic fixation such as fractures and dislocations.
본 발명에서 사용되는 청맥반석의 조성의 한 예는 다음과 같다.An example of the composition of the blue vein rock used in the present invention is as follows.
SiO267.44% , Al2O316.00, FeO 3.60, CaO 3.62, MgO 1.03, K2O 2.43, Na2O33.99, 기타 1.68 (한국동력자원 연구소 분석)SiO 2 67.44%, Al 2 O 3 16.00, FeO 3.60, CaO 3.62, MgO 1.03, K 2 O 2.43, Na 2 O 3 3.99, etc. 1.68 (Korea Institute of Energy Research)
기타의 조성으로 된 맥반석도 본 발명의 바이오 세라믹으로 사용이 가능하다. 또 본 발명의 특허청구범위 내에서 바이오 세라믹의 조성물의 일부를 가감하거나 배합비를 조정하는 것도 본 발명의 권리범위에 속하는 것임을 부언한다.Elvan stones with other compositions can also be used as the bio-ceramic of the present invention. In addition, it is also within the scope of the present invention to add or subtract a part of the composition of the bio-ceramic or adjust the compounding ratio within the claims of the present invention.
본 발명은 편직, 또는 직조의 붕대지에 프라스터(석고), 또는 가습경화성 수지등의 경화제가 도포된 카스트(Cast)용 붕대에 있어서, 청매반석, 지르코니아, 알루미노실리게이트, 코디어라이트, 게르마늄함유 황토, 투어말린, 운모등의 광물의 혼합물질로 된 원적외선 및 음이온이 방출되는 바이오 세라믹의 분말을 상기 붕대의 경화제에 혼합하여 기능성 카스트용 붕대를 제조하였기 때문에 정형외과적 환부에 카스트 붕대를 감아 경화하였을 때 피부에 대한 원적외선에 의한 혈액순환의 촉진작용으로 저리거나 가려움증이 없고 음이온에 의한 피부의 건강유지와 항균작용으로 피부염을 방지하여 카스트용 붕대의 기능성에 의한 유용성을 보다 높일 수 있는 효과가 있다.The present invention is in a cast bandage coated with a curing agent such as praster (gypsum), or a humidified curable resin on a bandage of knitted or woven fabrics, the blue rock, zirconia, aluminosilicate, cordierite, germanium The bandages for functional casts were wound around the orthopedic affected area by preparing a functional cast bandage by mixing the powder of bio-infrared and anion-releasing bio-ceramic material containing a mixture of minerals such as ocher, tourmaline, and mica with the curing agent of the bandage. When cured, there is no tingling or itching due to the promotion of blood circulation by the far-infrared rays on the skin, and it prevents dermatitis by maintaining the health of the skin by anion and antibacterial effect, thereby improving the usefulness by the function of caste bandage. have.
Claims (3)