KR20040022495A

KR20040022495A - Net's frame and the manufacture method for fishhook

Info

Publication number: KR20040022495A
Application number: KR1020020054083A
Authority: KR
Inventors: 정광재
Original assignee: 임봉규
Priority date: 2002-09-09
Filing date: 2002-09-09
Publication date: 2004-03-16

Abstract

PURPOSE: Provided are net's frame for fishhook and manufacturing method thereof, to reduce weight and to improve strength and corrosion resistance. CONSTITUTION: The net frame for fishhook is manufactured by cutting an aluminum tube(1) in 0.3mm thickness and 7mm diameter; winding a carbon tape(2) around the aluminum tube; bending the aluminum tube(1) to make a frame(3); placing the frame(3) in a furnace and heating at 140 deg.C for 30-50 minutes to make sure that the carbon tape(2) is sufficiently adhered to the aluminum tube(1); and connecting other parts of the net to both ends of the frame(3). For convenience of night fishing, noctilucent material is formed on the carbon tape(2).

Description

Frame for fishing nets and manufacturing method thereof {Net's frame and the manufacture method for fishhook}

본 발명은 낚시용 뜰채의 프레임 및 그 제조방법에 관한 것으로 뜰채를 구성하는 프레임을 좀 더 가볍고 강도와 내부식성이 우수하게 하며, 야간낚시할 때 편리하도록 한 것이다.The present invention relates to a frame for fishing nets and a method for manufacturing the same, and makes the frame constituting the nets lighter, better strength and corrosion resistance, and convenient when fishing at night.

주지하는 바와 같이 낚시용 뜰채는 낚시로 잡은 고기를 떠올릴 때 사용하는것으로서 한 손에는 낚시대를 잡고 있어야 하기 때문에 뜰채는 주로 한 손으로 사용한다.As it is known, fishing nets are used to think of the fish caught by fishing, and they are usually used by one hand because fishing rods must be held in one hand.

그렇기 때문에 좋은 뜰채의 조건은 가볍고 또, 큰 고기를 떠올려도 프레임의 형상이 변하지 않는 강도를 가지고 있어야 하며 또한, 민물이나 바닷물에서 사용하기 때문에 내부식성이 우수해야 한다.Therefore, the conditions of good gardening should be light and have the strength that the shape of the frame does not change even when thinking of big meat. Also, it should be excellent in corrosion resistance because it is used in fresh or salt water.

종래 상기와 같은 용도의 낚시용 뜰채는 고기를 담을 수 있는 망체와 망체가 결합된 프레임이 있고, 프레임에는 직경이 다른 다단의 관체를 연결하여 원거리에 있는 고기를 망체로 떠올릴 수 있도록 구성되어 있다.Conventional fishing nets for use as described above has a frame that combines the mesh and the mesh can hold the meat, the frame is configured to connect the multi-stage pipe of different diameters to remind the meat in the distance to the mesh. .

그리고, 망체가 결합되는 프레임은 대부분 알루미늄 관체로 구성되는데 상기와 같은 알루미늄 관체는 경금속으로서 스테인레스 관체에 비하여 가볍고 냉간 소성가공이 용이한 장점이 있으나 부식이 잘 되기 때문에 부식을 방지하기 위하여 프레임에 코팅을 하고 또, 사용할 때 프레임으로서 요구되는 강도를 얻기 위하여 관체의 두께가 최소한 3㎜정도는 되어야 한다.In addition, the frame to which the mesh is bonded is composed mostly of aluminum tubing, such aluminum tubing is a light metal as compared to the stainless steel tubing, the advantages of light and cold plastic processing is easy, but because the corrosion is well coated on the frame to prevent corrosion In order to achieve the required strength as a frame when used, the thickness of the tube should be at least 3 mm.

그러나 상기와 같이 약 3㎜정도의 두께를 갖는 알루미늄 관체로 프레임을 형성하더라도 뜰채가 큰 것은 한 손으로 사용하기에 무겁기 때문에 사용할 때 불편하였다.However, even when the frame is formed of an aluminum tube having a thickness of about 3 mm as described above, the large cheonchae was inconvenient when used because it is heavy to use with one hand.

또, 뜰체를 사용하는 중에 뜰채를 구성하는 프레임이 갯바위에 자주 부딪치고 또, 물속에 잠기는 것이 반복되는 원인으로 인하여 프레임의 코팅층이 벗겨지므로 부식이 매우 빠르게 진행되며, 야간낚시를 위한 야광점이 떨어지는 등의 문제점이 있었다.In addition, during the use of gardening, the frame constituting the gardening is frequently hit by the rock, and the coating layer of the frame is peeled off due to repeated submersion in the water. There was a problem.

본 발명은 상기한 문제점을 해결하기 위하여 스테인레스 또는 알루미늄 관체의 두께를 종래 것에 비하여 얇은 것을 선택하고 소정의 길이로 절단한 후에 카본 테이프 또는 무늬나 문자가 인쇄된 카본 테이프, 야광물질이 형성된 카본 테이프를 알루미늄 관체에 나선형으로 감은 후에 소정의 프레임 모양으로 밴딩하고 노(爐)에 넣어서 약 140도 정도의 온도로 약 30-50분간 가열하여 카본 테이프를 알루미늄 관체와 일체로 접착 및 경화시킴으로써, 가볍고 또, 고강도 및 내부식성이 우수하고 야간낚시할 때 편리한 낚시용 뜰채를 제공하는데 소기의 목적하는 바가 있다.The present invention is to solve the above problems, the thickness of the stainless steel or aluminum tube is thinner than the conventional one is selected and cut to a predetermined length after the carbon tape or carbon tape printed with patterns or letters, carbon tape formed luminous material After winding spirally on the aluminum tube, it is bent into a predetermined frame shape, put into a furnace, heated for about 30-50 minutes at a temperature of about 140 degrees, and the carbon tape is bonded and cured integrally with the aluminum tube. Its purpose is to provide high strength and corrosion resistance, and a convenient fishing net for night fishing.

도 1은 본 발명에 따른 제조공정도1 is a manufacturing process diagram according to the present invention

도 2는 본 발명에 따른 프레임의 단면도2 is a cross-sectional view of the frame according to the present invention.

도 3은 본 발명에 따른 뜰채의 예시도Figure 3 is an illustration of the garden vegetables according to the present invention

***도면중 주요 부분에 대한 부호의 설명****** Description of the symbols for the main parts of the drawings ***

1: 알루미늄 관체1: aluminum tube

2: 카본 테이프2: carbon tape

3: 프레임3: frame

4: 연결구4: connector

본 발명에 따른 낚시용 뜰채의 프레임 및 그 제조방법에 관한 구성을 이하 첨부되는 도면과 관련하여 상세하게 설명하면 다음과 같다.Hereinafter, a detailed description will be given of a structure of a fishing net according to the present invention and a method for manufacturing the same in detail with reference to the accompanying drawings.

도 1은 본 발명의 제조공정도이고, 도 2는 본 발명에 의해 제조된 프레임의 단면도이다.1 is a manufacturing process diagram of the present invention, Figure 2 is a cross-sectional view of the frame produced by the present invention.

먼저 본 발명에 따른 공정도를 살펴본다First, look at the process chart according to the present invention

제 1공정(소재준비 및 절단공정)1st process (material preparation and cutting process)

약 0.3㎜ 정도의 두께와 약 7㎜ 정도의 지름을 갖는 알루미늄 관체(1)를 계산된 길이로 절단한다.An aluminum tube 1 having a thickness of about 0.3 mm and a diameter of about 7 mm is cut to the calculated length.

제 2공정(카본 테이프 권취공정)2nd process (carbon tape winding process)

제 1공정으로 준비된 알루미늄 관체(1)에 카본 테이프(2)를 일정한 간격이 되도록 나선형으로 감는데 카본 테이프(2) 또는 무늬나 문자를 인쇄한 카본테이프(2) 또는 야광물질이 형성된 카본 테이프(2)를 사용할 수 있다.The carbon tape 2 is spirally wound on the aluminum tube 1 prepared in the first step so as to have a predetermined interval, and the carbon tape 2 or the carbon tape 2 printed with patterns or letters or the carbon tape having luminous material ( 2) can be used.

제 3공정(밴딩공정)3rd process (banding process)

제 2공정을 통하여 알루미늄 관체(1)에 카본 테이프(2)를 나선형으로 권취한 상태에서 소정의 모양으로 밴딩한다.The carbon tape 2 is wound in a predetermined shape in a spiral wound state on the aluminum tube 1 through the second step.

제 4공정(경화공정)4th process (hardening process)

제 2공정과 제 3공정을 통하여 알루미늄 관체(1)에 카본 테이프(2)를 권취하고 소정의 모양으로 밴딩된 프레임(3)을 노(爐)에 넣고 약 140도 정도의 온도로 약 30-50분 가열하여 알루미늄 관체(1)에 카본 테이프(2)를 접착/경화시킨다.The carbon tape 2 is wound around the aluminum tube 1 through the second and third steps, and the frame 3, which is bent in a predetermined shape, is placed in a furnace at a temperature of about 140 degrees. It heats for 50 minutes, and the carbon tape 2 is adhere | attached / hardened on the aluminum tube 1.

그러면 도 2에서 도시한 것과 같이 알루미늄 관체(1)에 카본 테이프(2)가 일체로 경화된 단면을 갖는다.Then, as shown in FIG. 2, the carbon tape 2 is integrally cured on the aluminum tube 1.

제 5공정(조립공정)5th process (assembly process)

상기의 공정들을 통하여 제조된 프레임(3)의 양단에 공지의 연결구(4)를 조립하여 낚시용 뜰채의 프레임의 조립을 완성시킨다.By assembling a known connector 4 on both ends of the frame (3) manufactured through the above process to complete the assembly of the frame of the fishing net.

이러한 공정들을 통하여 낚시용 뜰채를 구성하는 프레임(3)은 알루미늄 관체(1)의 두께가 약 0.3 ㎜이기 때문에 매우 가볍고 또, 카본 테이프(2)가 상기 알루미늄 관체(1)에 일체로 경화되어 있기 때문에 카본이 가지고 있는 고강도의 성질이 알루미늄에 접목되어 결과적으로 프레임의 강도를 높이게 되므로 큰 고기를 떠올리더라도 프레임의 형상이 유지될 수 있는 것이다.The frame 3 constituting the fishing net through these processes is very light because the thickness of the aluminum tube 1 is about 0.3 mm, and the carbon tape 2 is hardened integrally with the aluminum tube 1. Therefore, the high strength properties of carbon are combined with aluminum, and as a result, the strength of the frame is increased, so that the shape of the frame can be maintained even when recalling large meat.

또한, 카본 테이프(2)가 알루미늄 관체(1)를 감싸면서 일체로 경화되어 있기 때문에 프레임은 카본 테이프(2)에 의해서 프레임(3)의 표면 경도가 매우 높게 형성된다.In addition, since the carbon tape 2 is integrally cured while covering the aluminum tube 1, the frame is formed with a very high surface hardness of the frame 3 by the carbon tape 2.

따라서 고기를 떠올리는 과정에서 뜰채를 구성하는 프레임이 갯바위에 부딪치더라도 표면의 손상을 줄일 수 있으며, 심한 충격으로 표면이 손상되더라도 카본 은 부식되지 않고 무늬나 문자를 인쇄한 카본 테이프(2)를 사용하였을 때 광고효과도 얻을 수 있으며, 또한 야광물질이 형성된 카본 테이프(2)를 프레임에 사용하였을 경우에는 야간낚시할 때 프레임의 위치를 정확하게 알 수 있으므로 고기를 망체에 담아서 떠올릴 때 용이하다.Therefore, even if the frame constituting the gardener hits the sea rock in the process of thinking of the meat, the surface damage can be reduced, and even if the surface is damaged by severe impact, the carbon tape does not corrode and the printed carbon tape (2) is printed. When used, it is also possible to obtain an advertising effect, and when using the carbon tape (2) formed with a luminous material in the frame when the night fishing can know exactly the position of the frame is easy to put the meat in the net.

상기의 공정에서 알루미늄 관체 대용으로 스테인레스 관체를 사용하여도 제조 및 작용에 있어서 동일하다.The use of a stainless tube instead of an aluminum tube in the above process is the same in production and operation.

이상과 같은 본 발명은 알루미늄 관체의 두께가 종래 것에 비하여 매우 얇기 때문에 가벼운 뜰채를 제공할 수 있는 효과가 있고, 카본이 가지고 있는 고강도의 성질을 알루미늄 관체 또는 에 접목함으로써 고강도와 내부식성을 향상된 뜰채를 제공할 수 있으며, 카본 테이프에 야광물질이 도포되어 있기 때문에 사용할 때 편리함과 뜰채의 사용기간을 장구하게 할 수 있는 효과가 있다.The present invention as described above has the effect of providing a light garden because the thickness of the aluminum tube is very thin compared to the conventional one, and by combining the high-strength property of carbon with an aluminum tube or the It can provide, and because the luminous material is coated on the carbon tape has the effect of convenience and long life of the garden can be used when using.

Claims

Spirally winding the carbon tape 2 to the prepared aluminum tube 1 at regular intervals; Bending in the shape of a predetermined frame (3);

The method of manufacturing a fishing net frame comprising the steps of hardening integrally with the carbon tape (2) in the aluminum tube (1) by heating in a furnace at a temperature of about 140 degrees for about 30-50 minutes. .

A fishing net frame made by the method of claim 1, wherein a pattern and a letter are printed on the carbon tape (2).

Frame of fishing nets manufactured by the method of claim 1, characterized in that the luminous material is formed on the carbon tape (2).