KR20040003737A - Surface treatment method for the rim of a pair of spectacles - Google Patents

Abstract

PURPOSE: A method for processing a surface of a glass frame is provided to reduce the allergy due to nickel plating by processing the surface of the glass frame with a material are good to a human body. CONSTITUTION: A surface of a glass frame is plated with a nickel. An ocherous coating layer(3) is formed on the nickel coating layer(2) by spraying a mixture of a fine loess powder and a distilled water or performing an electrodeposition coating. The ocherous coating layer(3) emits infrared rays to a skin to increase the effect of infrared rays. An elvan coating layer(4) is formed on the ocherous coating layer(3) by mixing an elvan powder with a coating paint and spraying the mixture. The elvan coating layer(4) eliminates a contaminant, an organic matter, and various germs. Thereafter, the glass frame is dried.

Description

Surface treatment method for the rim of a pair of spectacles}

The present invention relates to a method for treating the surface of the spectacle frame, and in particular, in the process of surface treatment on the surface of the spectacle frame, various effects such as far infrared rays such as far-infrared rays obtained from the above components are included in the human body. It is intended to work directly.

As is well known, the surface of metal glasses is usually plated with nickel. Nickel has a problem in that a significant proportion of wearers cause allergic reactions, and thus the nickel plated layer is coated with a transparent or colored coating.

However, these coatings alone are not a sufficient countermeasure against allergens caused by nickel, since the coatings are often peeled off and the frames are inevitably pressed against the skin, which makes these wears unhealthy for the human body. It is natural that it will not affect.

In view of the above problems, the present invention devised to help the problem caused by the basic skin pressure in wearing glasses is to improve the strength of the coating by adding an ingredient beneficial to the human body in applying the surface treatment of the eyeglass frame nickel plating The goal is to completely solve the problem and to avoid other problems in the pressured areas.

1 is an enlarged cross-sectional view showing an embodiment of the surface structure configuration of the spectacle frame by the method of the present invention

Figure 2 is an enlarged cross-sectional view showing another embodiment of the surface structure configuration of the spectacle frame by the method of the present invention

3 is a graph showing the spectral emissivity according to the first embodiment of the present invention

4 is a graph showing the amount of spectral radiant energy according to the first embodiment of the present invention.

5 is a graph showing spectral emissivity according to a second embodiment of the present invention;

6 is a graph showing the amount of spectral radiant energy according to the second embodiment of the present invention.

7 is a graph showing the spectral emissivity by the conventional general coating

8 is a graph showing the amount of spectral radiant energy by the conventional general coating

*** Description of the symbols for the main parts of the drawings ***

1: glasses frame

2: nickel plated layer

3: ocher coating layer

4: Elvan coating layer

5: sericite coating layer

The components of the present invention contemplated for achieving the above object are ocher, elvan, and sericite.

In terms of such components, the ocher contains about 20,000 kinds of microorganisms that our bodies need, and the active activity of mysterious elements germanium and selenium receives external heat to store energy and circulate energy. It emits more than 700 times of far-infrared rays than normal clay, so it increases body temperature and releases heavy metals, wastes and toxins in the body through sweat.

Therefore, the far-infrared ray emitted from the yellow soil adds vitality to the mind and body through the promotion of blood and metabolism, and excellent antibacterial and healing effect of various diseases such as headache, low back pain, cold cold, neuralgia, arthritis, high blood pressure, liver disease, It also helps skin care and obesity.

In particular, germanium is a mysterious substance that supplies oxygen to the body smoothly, and it is known to clear blood and release heavy metals in the body.It is also effective in preventing various diseases and preventing diseases, and it is effective in recovering from fatigue and preventing aging. It is spotlighted as a mysterious element with excellent effects.

More specifically, germanium has excellent antiperspirant effect, so it is easy to alkalinize the acid constitution by helping the discharge of the old waste water and shows excellent effect on chronic fatigue and arthritis. In addition, it is effective for strengthening kidney function, preventing aging, and restoring fatigue, which is particularly useful for women's skin beauty.

Elvan has a strong adsorption effect, which causes capillary phenomena as porous rocks, which adsorbs and removes water vapor, pollutants, organics, and various bacteria, and elutes the major components such as magnesium, calcium, and germanium, which are required for human body and plants. Kills bacteria and increases oxygen supply

In addition, strong acidic or strong alkaline water is immersed in ganbanite and is measured to pH 7.4% in neutral, and bangan powder or granules are also neutral in soil. Dipping elvan reduces the COD (chemical oxygen demand) or BOD (biological oxygen demand), which prevents the decay of water and revitalizes the organism.

In addition, there are ions and medicinal effects. Because they are composed of multi-elements and porous materials, they do not remove impurities and smell in water by performing ions and radiative effects, and water does not decay and turns into weak water. It is known that there is a lot of effects such as to promote the activation of cells by the corresponding action of nucleic acids and amino acids, which are the basis of human cells, related to the production and activity of hormones called insulin.

Sericite, also known as chorus, is a generic term for dense or fine scaly mica.

It is produced as a secondary alteration such as feldspar, cordierite, and hongseokseok, and is the most common constituent mineral of feldspar slate or stony rock subjected to light power metamorphism. The pottery stone is caused by the deterioration of volcanic rock, which is composed of quartz (70%) and biotite (30%). Cicada is used as a mixing material for ceramics and firebrick, and has various uses such as paints, electrical insulators, slide materials, and cosmetics.

This material can expect strong antibacterial effect and odor prevention function such as decomposing nitrogen oxide and sulfur oxide to purify the air and completely prevent mold.

The present invention is an invention characterized by including the surface of the spectacle frame, ocher, elvan, and sericite, which have been described above. Hereinafter, a preferred embodiment for implementing the present invention will be described in detail.

Example 1

1st process

Nickel plating is performed on the surface of the manufactured spectacle frame by a known method.

2nd process

In coating a known protective layer on the outer surface of the nickel plated layer, it contains an ocher component, and after preparing a fine ocher powder from which impurities are removed, distilled water is mixed and mixed with a conventional coating paint to spray or electrodeposition coating. An ocher coating layer is formed on the outer surface of the nickel plating layer.

Mixing distilled water allows the ocher to mix well with the coating.

3rd process

After mixing fine elvan rock powder with a coating paint on the outer surface of the ocher coating layer and spraying again, the elvan coating layer is constituted.

4th process

Dry to complete surface treatment.

Example 2

1st process

Nickel plating is performed on the surface of the manufactured spectacle frame by a known method.

2nd process

In the coating of a known protective layer on the outer surface of the nickel plating layer, it contains a sericite component, and after preparing a fine sericite powder, distilled water is mixed, mixed with a conventional coating paint, and sprayed or electrodeposited coating. A sericite coating layer is formed on the outer surface of the plating layer.

3rd process

Dry to complete surface treatment.

In the first and second embodiments described above, it is appropriate to mix ocher, elvan, and sericite, which are mixed with the coating material, in the same volume ratio as the coating material.

This mixing ratio does not limit the rights in the present invention, and does not obtain an effect at a ratio of more or less, but far-infrared is less than 0.6 if the ocher, elvan, and sericite mixed when the volume of the coating material is 1 or less. It is difficult to obtain the desired effect because the emissivity is very small, it was found that more than 1.5 is not suitable for coating by spraying or electrodeposition.

Look at the surface treatment structure of the finished frame in this way.

The surface treatment structure of the spectacle frame according to Example 1 is a nickel plated layer (2) known on the outer surface of the spectacle frame (1) as shown in Fig. 1 and coated on the outer surface by mixing the ocher powder with a general coating material The ocher coating layer 3 is constituted, and on the outer surface thereof, the coating of the elvan coating layer 4 is formed by mixing the elvan powder with a general coating material.

The surface treatment structure of the spectacle frame according to Example 2 is a nickel plated layer (2) known on the outer surface of the spectacle frame (1) as shown in Fig. 2 and coated with a sericite powder mixed with a general coating material on the outer surface The sericite coating layer 5 is constituted.

The spectacle frame 1 manufactured in this manner can more clearly prevent the nickel component harmful to the human body from directly contacting the skin when worn.

In other words, since the ocher coating layer 3 is formed on the outer surface of the nickel plated layer 2 and the elvan coating layer 4 is formed on the outer surface of the nickel plated layer 2, it is a natural result that the risk of peeling is considerably reduced since the coating layers 3 and 4 are solid double layers. will be. In addition, the containing of the ocher component and the elvan component in the known coating layer will lead to the improvement of the strength of the coating layer.

And the ocher component contained in the ocher coating layer (3) of the present invention has a lot of effects according to the large amount of far-infrared rays as described above, so that the far-infrared effect can be obtained not only on the skin area where the spectacle frame (1) contacts but also on the entire face. It is.

In addition, by the strong adsorption action that is the effect of elvan, it is possible to obtain a lot of effects on the skin such as adsorption decomposition removal of water vapor film, contaminants, organic matter, and various bacteria.

In addition, the sericite coating layer 5 according to the second embodiment can also obtain a far-infrared divergence effect with the strengthening of the coating layer.

More specifically, in comparison with the case of the conventional general coating based on the test report attached to the results of the test of the degree of radiation of the far infrared according to the embodiment of the present invention as follows.

The experimental condition is the temperature is 40 ℃ and measured by the black body (black body) using the FT-IR Spectrometer.

Figure 7 shows the far-infrared emissivity by conventional coating, the emissivity is 0.846, which is 84.6%.

In addition, Figure 8 shows the amount of radiation energy, it can be seen that 3.41 × 10 ² (W / ㎡).

3 and 4, which are experimental results according to the first embodiment of the present invention, show that the emissivity is 0.917 and the radiation energy is 3.70 × 10 ² (W / m 2). Can be.

5 and 6, which are the experimental results according to the second embodiment of the present invention, the emissivity is 0.916 and the emission energy is 3.70 × 10 ² (W / m 2). Can be.

According to the present invention as described above to provide a surface treatment method and a spectacle frame according to the spectacle frame to enjoy the effect of far-infrared rays in a simple way, and easily solve the side effects such as allergy due to conventional nickel plating, and also due to the far infrared It can be said that it is a useful invention that can further develop the spectacle frame to the next level, such as the effect and the effect by elvan can be obtained sufficiently and effectively.

Claims (2)

Performing nickel plating on a surface of the manufactured spectacle frame by a known method; In applying a well-known protective layer coating on the outer surface of the nickel plated layer, fine ocher powder and impurities having been removed therefrom and distilled water are mixed with a conventional coating paint or sprayed or electrodeposited to form an ocher coating layer on the outer surface of the nickel plated layer. Process; Mixing the fine elvan rock powder with a coating paint on the outer surface of the ocher coating layer and then spraying again to form the elvan rock coating layer; The surface treatment method of the spectacle frame, characterized in that consisting of a step of drying to complete the surface treatment. Performing nickel plating on a surface of the manufactured spectacle frame by a known method; Process of forming a sericite coating layer on the outer surface of the nickel plated layer by applying a known protective layer coating on the outer surface of the nickel plated layer, by spraying a fine sericite powder and distilled water to a conventional coating paint or by electrodeposition coating. and; The surface treatment method of the spectacle frame, characterized in that consisting of a step of drying to complete the surface treatment.