KR200357506Y1 - Bank crime prevention structure used a bulletproof glass - Google Patents

Bank crime prevention structure used a bulletproof glass Download PDF

Info

Publication number
KR200357506Y1
KR200357506Y1 KR20-2004-0010955U KR20040010955U KR200357506Y1 KR 200357506 Y1 KR200357506 Y1 KR 200357506Y1 KR 20040010955 U KR20040010955 U KR 20040010955U KR 200357506 Y1 KR200357506 Y1 KR 200357506Y1
Authority
KR
South Korea
Prior art keywords
bulletproof glass
glass
bulletproof
basic unit
bank
Prior art date
Application number
KR20-2004-0010955U
Other languages
Korean (ko)
Inventor
정진교
Original Assignee
정진교
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 정진교 filed Critical 정진교
Priority to KR20-2004-0010955U priority Critical patent/KR200357506Y1/en
Application granted granted Critical
Publication of KR200357506Y1 publication Critical patent/KR200357506Y1/en

Abstract

본 고안은 방탄유리를 이용한 은행용 강도침입방지 구조에 관한 것으로, 은행의 직원이 사용하는 책상(120)의 프론트에 수납공간(110)을 갖도록 지지기둥(111)으로 방탄유리(100)를 형성하고, 상기 방탄유리(100)의 상단으로는 천정(130)에 연결되는 천정연결부(112)를 형성한 것을 특징으로 방탄유리를 이용한 은행용 강도침입방지 구조에 관한 것이다.The present invention relates to a structure for preventing the strength of banks using bulletproof glass, forming a bulletproof glass 100 with a support pillar 111 to have a storage space 110 in the front of the desk 120 used by the staff of the bank. In addition, the upper end of the bulletproof glass 100 relates to a structure for preventing strength intrusion for banks using bulletproof glass, characterized in that the ceiling connection portion 112 is formed to be connected to the ceiling 130.

따라서, 강도가 직원을 위협하여 금품 등을 도둑질하는 일이 없도록 사전에 방지할 수 있는 은행 안내대에 방탄구조를 제공하는데 그 목적이 있다.Therefore, the object of the present invention is to provide a bulletproof structure to a bank guide that can prevent the robbers from threatening the employee and steal money or the like in advance.

Description

방탄유리를 이용한 은행용 강도침입방지 구조{Bank crime prevention structure used a bulletproof glass}Bank crime prevention structure used a bulletproof glass}

본 고안은 방탄유리를 이용한 은행용 강도침입방지 구조에 관한 것으로서, 보다 상세하게는 일반유리의 표면에 폴리에스터필름(Polyester Film)을 접착제로 1차 접합하여 기본 단위의 방탄유리를 제작하고, 이 기본단위 방탄유리를 필요한 강도의 방탄이 요구되는 특성에 따라 최소한 두 겹으로 접합 사용할 때, 기본단위 방탄유리의 사방 가장자리 부위에 일정 폭과 높이를 갖는 충격흡수부재를 접착시켜 기본단위 방탄유리 사이사이에 충격흡수층을 갖도록 방탄유리를 제조하여 은행에 설치함으로써, 은행 강도가 침입하더라도 은행직원의 안전을 기할 수 있도록 된 은행 안내대용 방탄 구조에 관한 것이다.The present invention relates to a structure for preventing strength intrusion for banks using bulletproof glass, and more specifically, to fabricate bulletproof glass of a basic unit by first bonding a polyester film to a surface of ordinary glass with an adhesive. When the base unit bulletproof glass is bonded to at least two layers according to the characteristics requiring bulletproof strength required, between the base unit bulletproof glass by adhering a shock absorbing member having a certain width and height to the four corners of the base unit bulletproof glass. The present invention relates to a bulletproof structure for a bank guide, which manufactures bulletproof glass to have a shock absorbing layer in the bank and installs it in a bank, thereby ensuring the safety of bank employees even if a bank robbery invades.

일반적으로 방탄유리(Bulletproof Glass)는 일반유리에 무색 투명한 방탄용 필름(예를 들면, 폴리에스터 필름(Polyester Film))을 여러 겹 마주 붙여서 외부로부터 어떠한 물리적인 충격이 가해지더라도 유리가 파손 관통되는 일이 없어서 주로 인명이나 재산을 안전하게 보호할 수 있도록 각종 시설물 및 차량 등에 다양하게 사용되고 있다.In general, bulletproof glass is formed by attaching a colorless transparent bulletproof film (for example, a polyester film) to ordinary glass so that glass breaks through any physical impact from the outside. It is mainly used in various facilities and vehicles to protect human life or property safely.

이처럼 방탄유리는 그 사용범위가 대부분이 특수한 시설물 및 차량 등에 선택적으로 사용되고 있는 실정이며, 은행 등에서 구조물로 설치하여 강도의 침입을 막는 경우 및 이러한 구조물은 없었다.As described above, bulletproof glass is mostly used selectively in special facilities and vehicles, and is installed in banks, etc. to prevent intrusion of strength and there was no such structure.

이러한 방탄유리는 종래 일반유리와 일반유리 사이에 어느 정도의 방탄 능력이 있는 접합필름을 넣어 일반유리와 일반유리를 한 장으로 접합하여 제조하는 방법과, 일반유리의 한 표면에 폴리에스터필름을 부착하여 제조하는 방법 및 제너럴 일렉트닉스사(GE; General Electric Company)에서 개발한 폴리카보네이트 제품의일종인 렉산 소재를 이용하여 제조하는 방법 등 다양한 방법으로 제조되고 있다.Such a bulletproof glass is a method of manufacturing by bonding a common glass and a common glass in one sheet by putting a laminated film having a certain degree of ballistic resistance between the conventional glass and the normal glass, and attaching a polyester film on one surface of the ordinary glass It is manufactured by a variety of methods, such as a method of manufacturing by using a Lexan material, which is a kind of polycarbonate products developed by General Electric Company (GE).

현재 국내에서는 상기와 같은 방탄능력을 갖는 방탄유리나 방탄 가공 처리된 폴리에스터 필름을 이용한 방탄유리 및 렉산 소재를 이용한 방탄유리를 수입에 의존하고 있는 실정이기 때문에 방탄유리 수입 및 방탄유리 장착에 따른 비용이 외국으로 지출되고 있는 실정이다.Currently in Korea, the cost of importing bulletproof glass and installing bulletproof glass has been dependent on importing bulletproof glass having bulletproof capability as described above or bulletproof glass using bulletproof processed polyester film and lexan material. It is being spent abroad.

한편, 상기와 같은 방탄유리의 하중에 따른 보완책을 강구하기 위한 재 비용이 추가로 들어가게 됨에 따라 고 비용이 초래되어 경쟁력을 가질 수 없는 문제점이 있었다.On the other hand, there is a problem that can not be competitive due to the high cost as the re-entry cost for taking a supplementary measure according to the load of the bulletproof glass as described above is added.

또한, 건물과 같은 특수 시설물에 방탄유리를 장착하는 경우에 있어서도, 방탄유리의 하중 증가는 여러 가지 문제점을 드러낼 수 있다.In addition, even when the bulletproof glass is mounted in a special facility such as a building, an increase in the load of the bulletproof glass may reveal various problems.

즉, 주요 시설물 등에서 방탄유리의 설치가 필요하여 방탄유리를 설치하고자 할 때, 방탄유리의 두께 및 그 하중이 매우 클 경우에는 방탄유리를 지탱해야할 구조물의 강도 및 두께가 훨씬 강화되어야 함은 물론, 창호 역시 방탄유리의 하중을 지탱하면서 원활하게 작동할 수 있는 설계가 필요하기 때문에 그에 따른 부대 비용이 증가하게 됨은 자명하다 할 것이다.That is, when bulletproof glass is required to install bulletproof glass in major facilities, if the thickness of the bulletproof glass and its load is very large, the strength and thickness of the structure to support the bulletproof glass should be much strengthened, of course, It is obvious that windows and doors also need to be designed to work smoothly while supporting the load of the bulletproof glass.

이와 같은 여러 가지 문제점을 고려하여 국내에서도 방탄유리의 제조방법 및 다양한 방탄유리를 제공하고자 연구 개발되고 있는 실정이다.In view of the various problems as described above, the situation is being researched and developed to provide a bulletproof glass manufacturing method and a variety of bulletproof glass in Korea.

그 예로써, 2000년 10월 30일자 국내 특허출원(출원번호 제2000-64023호) 및 실용신안등록출원(출원번호 제2000-30259호)되어 각각 등록(특허등록번호10-372374호, 2003.2.4.등록; 실용신안등록번호20-0218888호, 2001.1.19.등록)된 방탄유리의제조방법 및 방탄유리의 경우, 도 1 내지 도 3에 도시된 바와 같이, 소정크기의 넓이를 가지며 7㎜∼10㎜의 두께를 갖는 유리(101)의 표면 중 적어도 어느 한 면에 도포된 0.012㎜∼0.017㎜의 접착제(102)에 의한 접착층(102a)과, 상기 접착층(102a)에 진공 접합되는 0.1㎜∼0.15㎜의 폴리에스테르 시트(103;polyester sheet)를 하나의 단위부재(104)로서 방탄유리(101)가 완성되는 구조를 갖도록 되어있다.For example, the domestic patent application (Application No. 2000-64023) and Utility Model Registration Application (Application No. 2000-30259) dated October 30, 2000, respectively (Patent Registration No. 10-372374, February 2003). 4. Registration; Utility Model Registration No. 20-0218888, 2001.1.19. Registered) Method of manufacturing bulletproof glass and bulletproof glass, as shown in FIGS. 1 to 3, has a predetermined size and has a width of 7 mm The adhesive layer 102a by the adhesive 102 of 0.012 mm -0.017 mm apply | coated to at least one surface of the glass 101 which has a thickness of -10 mm, and 0.1 mm vacuum-bonded to the said adhesive layer 102a. A sheet of polyester having a thickness of -0.15 mm (103) is used as one unit member 104 to have a structure in which bulletproof glass 101 is completed.

특히, 상기 선 출원된 방탄유리의 경우, 방탄 성능을 높이기 위해 상기 유리(101)표면에 진공 접합된 폴리에스테르 시트(103)의 노출면에 적어도 하나 이상의 폴리에스테르 시트(103)를 더 접합하도록 되어 있다.In particular, in the case of the previously applied bulletproof glass, at least one polyester sheet 103 is further bonded to the exposed surface of the polyester sheet 103 vacuum-bonded to the surface of the glass 101 in order to increase bulletproof performance. have.

또한, 특수한 방탄 성능을 갖는 방탄유리(101)의 경우에는 적어도 3장 이상의 폴리에스테르 시트(103)가 방탄유리(101)에 진공 접합되어 접착층(102a)과 폴리에스테르 시트(103)의 두께가 적어도 0.336㎜ 두께를 이루는 방탄유리(101)의 폴리에스테르 시트(103) 노출면과 또 다른 방탄유리(101)의 폴리에스테르 시트(103) 노출면을 상호 진공 접합하도록 되어 있다.In addition, in the case of the bulletproof glass 101 having a special bulletproof performance, at least three or more polyester sheets 103 are vacuum bonded to the bulletproof glass 101 so that the thickness of the adhesive layer 102a and the polyester sheet 103 is at least. The polyester sheet 103 exposed surface of the bulletproof glass 101 having a thickness of 0.336 mm and the polyester sheet 103 exposed surface of the other bulletproof glass 101 are mutually vacuum bonded.

즉, 상기한 단위부재(104)의 폴리에스테르 시트(103) 노출면에 접착제(102)를 0.012 ㎜∼0.017 ㎜의 두께로 균일하게 도포한 후, 상기 접착층(102a)에 또 다른 단위부재(104)의 폴리에스테르 시트(103) 노출면을 진공 접합한 후, 상기 접합된 폴리에스테르 시트(103)와 폴리에스테르 시트(103)의 테두리에 형성된 소정 크기의 테두리홈(105)에 실리콘(106)과 테라코타(105) 중 어느 하나를 충진시켜 외부의 공기나 폴리에스테르 시트(103)와 접착층(102a)으로 유입되지 않도록 차단하는구조로 제조된 방탄유리가 제시되어 있는 것이다.That is, after uniformly applying the adhesive 102 to the polyester sheet 103 exposed surface of the unit member 104 to a thickness of 0.012 mm to 0.017 mm, another unit member 104 to the adhesive layer 102a After vacuum-bonding the exposed surface of the polyester sheet 103, the silicon 106 and the edge groove 105 of a predetermined size formed on the edge of the bonded polyester sheet 103 and the polyester sheet 103; Filled with any one of the terracotta 105 is a bulletproof glass is made of a structure to block the outside air or polyester sheet 103 and the adhesive layer (102a) is introduced.

그러나, 상기 선 출원된 특허 및 실용신안에 따른 방탄유리의 제조방법 및 그 방법을 이용한 방탄유리의 경우, 강력한 방탄능력을 위해 방탄유리의 두께를 높여야만 하는 경우에 있어서 전술한 방탄유리의 두께 증가에 따른 여러 가지 경제적인 측면 및 하중의 문제점을 원천적으로 해결하기 어렵다는 문제점을 가지고 있었다.However, in the case of manufacturing the bulletproof glass according to the above-patented patent and utility model and the bulletproof glass using the method, the thickness of the above-described bulletproof glass is increased in the case where the thickness of the bulletproof glass must be increased for the strong bulletproof ability. There was a problem that it is difficult to fundamentally solve the problems of various economic aspects and loads.

본 고안은 상기에서 언급한 종래 공지된 방탄유리 및 상기 선 출원되어 등록된 방탄유리의 제조방법 및 그 방탄유리의 강력한 방탄능력을 구비하고, 방탄유리의 하중을 상대적으로 줄일 수 있는 방안의 하나로 안출된 것으로, 본 고안은 기본단위의 방탄유리를 제조하는 방법 및 이를 이용한 은행용 강도침입방지 구조를 개발하여 강도가 직원을 위협하여 금품 등을 도둑질하는 일이 없도록 사전에 방지할 수 있는 은행 안내대용 방탄구조를 제공하는데 그 목적이 있다.The present invention is provided with the above-mentioned conventionally known bulletproof glass and a method of manufacturing the bulletproof glass registered and registered above, and the strong bulletproof ability of the bulletproof glass, and to reduce the load of the bulletproof glass as one of the ways to reduce the load. The present invention is to develop a method of manufacturing bulletproof glass of the basic unit and a bank robbery prevention structure using the same to prevent bank robbers from stealing money or other goods by threatening employees in advance. The purpose is to provide a bulletproof structure.

요즈음 모든 범죄 사건을 보면 날로 흉폭해지고, 지능적이며 경찰과 경비원의 출동 유무와 관계없이 불과 2~3분만에 범죄를 끝내고 도주하는 속전 속결형이다.These days, all crime cases are violent, intelligent, and fast-paced to escape after only two or three minutes, with or without police and security guards.

우리 나라도 총기의 안전지대가 아니며, 밀수입된 총기가 난무한 실정인 것이다.Korea is not a safe zone for firearms, and smuggled firearms are in trouble.

은행 등에 총기를 들이대고 현금을 강탈해 가는 이러한 허술한 경비시스템을 보안하여 침입자체가 불가능한 침입저지 디펜스 죤을 설치해야할 필요성이 많은 것이다.There is a lot of necessity to install an intrusion prevention defense zone that cannot be intruded by securing such a lax security system that robs banks of guns and robs cash.

누구나 마음먹으면 언제든지 침입이 가능하면 아무리 좋은 경비시스템이든 무인경비시스템이든 또한 경비 숫자를 늘인다하더라도 한계가 있으며, 인건비를 문제삼지 않을 수 없는 현실이다.If anyone can invade at any time, no matter how good security system or unmanned security system also increases the number of guards, there is a limit, the labor cost is a reality that must be a problem.

심지어 장난감 총으로 은행직원을 위협하여도 현금을 건네 줄 수밖에 없는 구조적으로 잘못된 설비를 바꾸어야할 필요가 있는 것이다.Even a toy gun threatens bank employees, so they need to change their structurally faulty equipment, which can only be handed out cash.

따라서, 본 고안은 예금과 지급이 이루어지는 창구에 침입자체를 원천적으로 봉쇄하는 방어적인 창구를 설치하여 강도가 총기를 들고 들어오더라도 창구 안으로 침입이 불가능하고, 위협을 받을 일이 없도록 하는데 그 목적이 있다.Therefore, the present invention provides a defensive window for blocking the invasion itself at the window where deposits and payments are made, so that even if a robber comes in with a firearm, it is impossible to break into the window and is not threatened. have.

도 1은 종래 기술에 따른 방탄유리의 제조과정을 보여주는 분해 사시도,1 is an exploded perspective view showing a manufacturing process of a bulletproof glass according to the prior art,

도 2a는 종래 기술에 따른 방탄유리의 구조를 보여주는 단면도,Figure 2a is a cross-sectional view showing the structure of a bulletproof glass according to the prior art,

도 2b는 종래 기술에 따른 방탄유리의 제조과정을 보여주는 사시도,Figure 2b is a perspective view showing the manufacturing process of the bulletproof glass according to the prior art,

도 3은 본 고안에 따른 방탄유리를 이용한 은행용 강도침입방지 구조의 개략도Figure 3 is a schematic diagram of the bank strength intrusion prevention structure using bulletproof glass according to the present invention

도 4는 본 고안에 따른 방탄유리의 제조과정을 보여주는 분해 사시도,Figure 4 is an exploded perspective view showing a manufacturing process of bulletproof glass according to the present invention,

도 5 및 도 6은 본 고안에 따른 방탄유리의 구조를 보여주는 단면도,5 and 6 are cross-sectional view showing the structure of a bulletproof glass according to the present invention,

* 도면의 주요 부분에 대한 부호의 설명 *Explanation of symbols on the main parts of the drawings

10, 11, 12 : 일반유리 20, 21, 22 : 폴리에스터필름10, 11, 12: general glass 20, 21, 22: polyester film

30, 31 : 충격흡수부재 40, 41 : 프레임30, 31: shock absorbing member 40, 41: frame

100, G : 방탄유리 g1, g2 : 기본단위 방탄유리100, G: bulletproof glass g1, g2: basic unit bulletproof glass

S : 충격흡수층 110 : 수납공간S: Shock absorbing layer 110: Storage space

상기와 같은 목적을 달성하기 위한 본 고안은, 은행의 직원이 사용하는 책상의 프론트에 수납공간을 갖도록 지지기둥으로 방탄유리를 형성하고, 상기 방탄유리의 상단으로는 천정에 연결되는 천정연결부를 형성한 것을 특징으로 한다.The present invention for achieving the above object, to form a bulletproof glass with a support pillar to have a storage space in the front of the desk used by the staff of the bank, the top of the bulletproof glass to form a ceiling connection portion connected to the ceiling It is characterized by one.

또한, 이러한 방탄유리의 구조로서, 총기류 및 폭발물과 같은 강력한 화력을 갖는 총기류의 탄두 및 폭발물의 파편에 의해 가해지는 외부 충격으로부터 보호하기 위해 일반유리의 일측면에 폴리에스터 필름을 접착시켜 구성하는 방탄유리에 있어서, 소정크기의 넓이를 가지며 5㎜∼l2㎜의 두께를 갖는 일반유리의 표면 중 적어도 어느 한 면에 8~20mil의 두께를 갖는 폴리에스터 필름을 접착시켜 형성된 기본 단위의 방탄유리와; 외측방향에 대해 일반유리, 폴리에스터 필름의 순서로 배치된 상기 기본단위의 방탄유리가 일정간격을 두고 배치되도록 복수의 기본단위 방탄유리 사이의 사방 가장자리 부위에 부착된 15㎜∼25㎜의 폭과 5㎜∼10㎜의 높이를 갖는 충격흡수부재와; 상기 복수의 기본단위 방탄유리와 충격흡수부재의 외측을 감싸 고정 결합하는 프레임을 포함하는 것을 특징으로 하는 충격흡수층을 갖는 방탄유리를 제공함으로써 달성된다.In addition, as a structure of the bulletproof glass, ballistics formed by adhering a polyester film to one side of the general glass in order to protect it from external impacts caused by fragments of warheads and explosives of firearms having strong thermal power such as firearms and explosives A glass comprising: a bulletproof glass of a basic unit formed by bonding a polyester film having a thickness of 8 to 20 mil to at least one surface of a common glass having a width of a predetermined size and having a thickness of 5 mm to l2 mm; A width of 15 mm to 25 mm attached to the four edges of the plurality of basic unit bulletproof glass so that the bulletproof glass of the basic unit arranged in the order of ordinary glass and polyester film with respect to the outer direction are arranged at a predetermined interval; An impact absorbing member having a height of 5 mm to 10 mm; It is achieved by providing a bulletproof glass having a shock absorbing layer, characterized in that it comprises a frame which is fixed to the outer side of the plurality of basic unit bulletproof glass and the shock absorbing member.

이때, 본 고안은 상기 기본단위 방탄유리가 최소 두 겹으로 배치 결합되어 제작되는 것을 기본으로 하나, 보다 더 강력한 강도의 방탄능력이 요구되는 경우에 상기 기본단위 방탄유리의 폴리에스터필름 노출면에 상기와 동일하게 충격흡수부재를 매개로 하여 상기 기본단위 방탄유리가 추가로 하나 더 부착되는 것이 바람직하다.At this time, the present invention is based on the base unit bulletproof glass is produced by combining at least two layers at least, if the stronger strength of the bulletproof ability is required, the polyester film exposed surface of the base unit bulletproof glass In the same manner as in the medium through the shock absorbing member, the basic unit is preferably one more bulletproof glass is attached.

그리고, 상기 충격흡수부재는 탄성고무, 실리콘, 압축스폰지, 에어백 중 어느 하나인 것이 바람직하다.In addition, the shock absorbing member is preferably any one of elastic rubber, silicone, compressed sponge, and airbag.

이하, 본 고안의 바람직한 실시예에 대해서 첨부도면을 참조하여 상세히 설명하기로 한다.Hereinafter, preferred embodiments of the present invention will be described in detail with reference to the accompanying drawings.

도 3은 본 고안에 따른 방탄유리를 이용한 은행용 강도침입방지 구조의 개략도로서, 본 고안의 목적을 달성하기 위하여, 은행의 직원이 사용하는 책상(120)의 프론트에 수납공간(110)을 갖도록 지지기둥(111)으로 방탄유리(100)를 형성하고, 상기 방탄유리(100)의 상단으로는 천정(130)에 연결되는 천정연결부(112)를 형성한 것을 특징으로 한다.Figure 3 is a schematic view of the bank strength intrusion prevention structure using bulletproof glass according to the present invention, to achieve the object of the present invention, to have a storage space 110 in the front of the desk 120 used by the staff of the bank The bulletproof glass 100 is formed by the support pillar 111, and a ceiling connection part 112 connected to the ceiling 130 is formed at an upper end of the bulletproof glass 100.

따라서, 강도가 침입할 경우에 총으로 은행 창구의 직원을 위협하더라도 수납공간(110)은 약 20센티미터 정도 떨어져 있고, 상부에 방탄유리(100)가 있기 때문에 강도가 자유로이 활동하지 못하도록 함으로서, 은행직원이 위협을 받는 일이 없고, 통상의 강도 행위는 3분 정도에서 모든 것을 종결하려는 조급한 마음에 방탄유리가 설치되어 직원들을 위협하지 못할 설비를 갖추고 있다고 생각될 경우에는 강도가 아예 처음부터 강도 짓을 하려는 마음이 없어 사전에 이를 예방할 수 있는 것이다.Therefore, even if a robbery invades the staff of the bank teller with a gun, the storage space 110 is about 20 centimeters away, and because the bulletproof glass 100 is located at the top, the robbers can not be freely active. If you don't feel this threat, and you think your usual robbery is about 3 minutes to end everything, you can't threaten your employees with bulletproof glass installed in a hurry. If you do not want to be able to prevent this in advance.

다음은 상기 방탄 유리(100)의 바람직한 실시예에 대해서 첨부도면을 참조하여 상세히 설명하기로 한다.Next, a preferred embodiment of the bulletproof glass 100 will be described in detail with reference to the accompanying drawings.

도 4는 본 고안에 따른 방탄유리의 제조과정을 보여주는 분해 사시도 이고, 도 5는 본 고안에 따른 방탄유리의 구조를 보여주는 단면도이다.Figure 4 is an exploded perspective view showing a manufacturing process of bulletproof glass according to the present invention, Figure 5 is a cross-sectional view showing the structure of the bulletproof glass according to the present invention.

도 4 및 도 5에 도시된 바와 같이, 본 고안에 적용되는 방탄유리(G)는 소정크기의 넓이를 가지며 5㎜∼12㎜의 두께를 갖는 일반유리(10)의 표면 중 적어도 어느 한 면에 8~20mil(여기서, mil은 1/1000inch에 해당한다)의 두께를 갖는 폴리에스터필름(20)(polyester film)을 접착시켜 형성된 방탄유리(g1)를 하나의 기본단위로 하는 구조를 가지고 있으며, 상기 기본단위 방탄유리(g1)를 최소 두 겹 이상으로 일정간격을 두고 배치하여 복수의 기본단위 방탄유리(g1,g2)사이에 15㎜∼25㎜의 폭과 5㎜∼10㎜의 높이를 갖는 충격흡수부재(30)를 통한 충격흡수층(S)을 갖도록 제작한 다음, 상기 복수의 기본단위 방탄유리(g1,g2)와 충격흡수부재(30)의 외측을 프레임(40)으로 감아서 고정 결합하는 구조로 되어 있다.As shown in Figure 4 and 5, the bulletproof glass (G) applied to the present invention has a width of a predetermined size and at least on one side of the surface of the general glass 10 having a thickness of 5mm to 12mm It has a structure in which a bulletproof glass (g1) formed by bonding a polyester film 20 having a thickness of 8 to 20 mils (where mil is equivalent to 1/1000 inch) as one basic unit, The base unit bulletproof glass g1 is arranged at least two layers at regular intervals, and has a width of 15 mm to 25 mm and a height of 5 mm to 10 mm between the plurality of basic unit bulletproof glass g1 and g2. After manufacturing to have a shock absorbing layer (S) through the shock absorbing member 30, the plurality of basic unit bulletproof glass (g1, g2) and the outer side of the shock absorbing member 30 wound around the frame 40 fixedly coupled It is made to structure.

이때, 상기 충격흡수부재(30)는 충격을 흡수할 수 있는 소재인 탄성고무, 실리콘, 압축스폰지, 에어백 중 어느 하나인 것이 바람직하다.At this time, the shock absorbing member 30 is preferably any one of elastic rubber, silicone, compressed sponge, airbag that can absorb shock.

그리고, 상기 프레임(40)의 재질은 기본단위 방탄유리(g1,g2)와 충격흡수부재(30)의 외측을 감아서 기본단위 방탄유리(g1,g2)와 충격흡수부재(30)의 밀착력을 높여 견고하게 고정할 수 있는 구조로 설계 가능한 재질이며 어느 것이나 무방하다.In addition, the material of the frame 40 is wound around the outer side of the basic unit bulletproof glass (g1, g2) and the shock absorbing member 30 to improve the adhesion between the basic unit bulletproof glass (g1, g2) and the shock absorbing member 30. It is a material that can be designed in a structure that can be firmly fixed and fixed.

특히, 상기 기본단위 방탄유리(g1,g2)를 제작하는 과정에서 일반유리(10)의 두께 및 폴리에스터필름(20)의 두께는 사용자가 요구하는 방탄능력을 고려함과 동시에 생산비용 측면에서의 경제성 등을 고려하여 상기 수치적으로 주어진 범위 내에서 다양하게 선택 가능하다.In particular, the thickness of the general glass 10 and the thickness of the polyester film 20 in the process of manufacturing the basic unit bulletproof glass (g1, g2) considering the ballistic capacity required by the user and at the same time economical in terms of production cost In consideration of the above, various selections can be made within the numerically given range.

이는 일반유리(10) 및 폴리에스터필름(20)의 두께가 두꺼울수록 방탄능력이 향상됨이 자명하나, 상기 방탄유리(G)를 장착하는 주요구조물의 구조적 특성 및 경제성을 고려할 때, 무한정으로 방탄능력을 향상시킬 수는 없으므로 상기에서 주어진 일반유리(10) 및 폴리에스터필름(20)의 두께 범위 내에서 최적의 설계를 하는 것이 바람직하다 할 것이다.It is obvious that the thicker the thickness of the general glass 10 and the polyester film 20, the better the bulletproof ability, but considering the structural characteristics and economical efficiency of the main structure for mounting the bulletproof glass (G), infinitely bulletproof capacity Since it may not be improved, it would be desirable to have an optimal design within the thickness range of the general glass 10 and the polyester film 20 given above.

물론, 상기와 같은 최적의 설계조건은 다양한 실험을 통한 실험 데이터를 분석함으로써 가능하게 된다.Of course, the optimal design condition as described above is possible by analyzing the experimental data through a variety of experiments.

이하 다양한 실험을 통해 요구되는 방탄능력에 대한 경험적으로 확인된 최적의 설계 조건에 대한 바람직한 실시예를 보여주고 있다.The following shows a preferred embodiment of the empirically confirmed optimal design conditions for the ballistic capacity required through various experiments.

본 고안의 제1실시예에 따른 방탄유리(G)의 구조가 도 5에 도시되어 있다.The structure of the bulletproof glass G according to the first embodiment of the present invention is shown in FIG. 5.

본 고안의 제1실시예는 방탄유리(G) 전체적인 두께가 34㎜이내를 유지한 상태에서 32구경 권총 및 38구경 권총과 같은 총기류와, 총기류 중에서도 다소 강력한 개인화기 등으로부터 인명 및 재산을 보호할 수 있는 방탄능력을 갖는 방탄유리(G)가 제시되어 있다.The first embodiment of the present invention protects life and property from firearms such as 32-caliber pistols and 38-caliber pistols, and rather powerful personalizers among firearms, while maintaining the overall thickness of bulletproof glass (G) within 34 mm. Bulletproof glass (G) having a bulletproof ability that can be presented.

즉, 도 5에 도시된 바와 같이, 본 고안에 따른 방탄유리(G)는 공기 중에 이물질이나 부유물이 없는 깨끗한 환경(예를 들어, 크린룸)에서 약 12㎜두께의 일반유리(10)의 일측 표면에 세척액과 에어를 분사하여 이물질을 완전히 제거한 후 일반유리(10)의 표면에 접착제를 도포한 다음, 여기에 20mil의 두께를 갖는 폴리에스터필름(20)을 접합시켜 하나의 기본단위 방탄유리(g1)를 제작한다.That is, as shown in Figure 5, the bulletproof glass (G) according to the present invention is one surface of the general glass 10 of about 12 mm thickness in a clean environment (for example, a clean room) free of foreign matter or suspended matter in the air After removing the foreign matter completely by spraying the cleaning liquid and air to the surface of the common glass 10, an adhesive is applied, and then bonded to a polyester film 20 having a thickness of 20 mils on one base unit bulletproof glass (g1 ).

이때, 상기 일반유리(10)의 표면에 도포되는 접착제의 접착층은, 선 출원되어 공지된 특허등록번호10-372374호에도 기재된 바와 같이, 0.012 ㎜∼0.017 ㎜로 균일하게 이루어지는 것이 바람직한 것으로 파악되고 있다.At this time, it is understood that the adhesive layer of the adhesive applied to the surface of the common glass 10 is preferably made uniformly from 0.012 mm to 0.017 mm, as described in the previously registered patent application No. 10-372374. .

즉, 상기 접착제의 접착층이 0.012㎜보다 얇을 경우 접착력이 약화되어 접착제가 강력한 접착력을 발휘하지 못하게 되고, 0.017㎜보다 두꺼울 경우에는 접착제에 의해 접합되는 폴리에스터필름(20)과 접착제에 폭발물의 파편이나 총기류의 탄두에 의해 충격이 가해질 경우에 충격분산효과가 저하되기 때문이다.That is, when the adhesive layer of the adhesive is thinner than 0.012 mm, the adhesive strength is weakened, the adhesive does not exhibit a strong adhesive force, and when the adhesive layer is thicker than 0.017 mm, fragments of explosives on the polyester film 20 and the adhesive bonded by the adhesive This is because the impact dispersion effect is reduced when an impact is applied by the warhead of the firearm.

따라서, 상기 일반유리(10)의 표면에 도포되는 접착제는 0.012 ㎜∼0.017 ㎜의 접착층을 형성하는 것이 바람직하다.Therefore, the adhesive applied to the surface of the common glass 10 preferably forms an adhesive layer of 0.012 mm to 0.017 mm.

그리고, 이렇게 제작된 상기 기본단위 방탄유리(g1)를 전면에 1장 세운 다음, 이 기본단위 방탄유리(g1)의 폴리에스터필름(20)이 노출된 뒤쪽 면의 사방가장 자리에 약 20㎜의 넓이(폭)와 10㎜의 높이를 갖는 충격흡수부재(30)를 부착시켜 충격흡수층(S)을 형성하고, 이 충격흡수부재(30)에 밀착되게 약 10㎜ 두께의 일반유리(11)에 20mil 두께의 폴리에스터필름(21)이 부착된 또 다른 기본단위 방탄유리(g2)를 세워서 설치한다.Then, the basic unit bulletproof glass (g1) thus prepared is erected on one front side, and the polyester film 20 of the basic unit bulletproof glass (g1) is about 20 mm on all sides of the rear surface exposed. A shock absorbing member 30 having a width (width) and a height of 10 mm is attached to form a shock absorbing layer (S), and is attached to the general glass 11 having a thickness of about 10 mm to be in close contact with the shock absorbing member 30. Another basic unit bulletproof glass (g2) with a 20 mil thick polyester film (21) attached is installed upright.

그런 다음, 상기 기본단위 방탄유리(g2)와 상기 충격흡수부재(30)의 외측을 프레임(40)으로 감아서 고정 결합하는 구조를 갖는다.Then, it has a structure of winding the outer side of the base unit bulletproof glass (g2) and the shock absorbing member 30 by the frame 40 and fixed.

한편, 상기 제1실시예에서 보여준 방탄유리(G)의 방탄성능 보다 더 우수한 방탄성능을 갖도록 하기 위해 방탄유리(G)의 구조에 동일한 구조를 갖는 기본단위 방탄유리를 하나 더 추가 설치하는 구조로 제조할 수도 있음은 물론이다.On the other hand, in order to have a better ballistic performance than the bulletproof glass (G) shown in the first embodiment to the structure of the bullet-proof glass (G) to add one more basic unit bulletproof glass having the same structure Of course, it can also manufacture.

이상 설명한 바와 같이 본 고안에 따르면, 강도가 침입할 경우에 총으로 은행 창구의 직원을 위협하더라도 수납공간은 약 20센티미터 정도 떨어져 있고, 상부에 방탄유리가 있기 때문에 강도가 자유로이 활동하지 못하도록 함으로서, 은행직원이 위협을 받는 일이 없고, 조급한 마음에 방탄유리가 설치되어 직원들을 위협하지 못할 설비를 갖추고 있다고 생각될 경우에는 강도가 아예 처음부터 강도짓을 하려는 마음이 없어 사전에 이를 예방할 수 있는 효과가 있다.As described above, according to the present invention, even if a robbery invades the staff of the bank teller with a gun, the storage space is about 20 centimeters away, and the bulletproof glass on the top prevents the robbery from acting freely. If employees are not threatened and bulletproof glass is installed in a hurry and they are equipped with equipment that will not threaten the employees, the robbers do not want to rob in the first place, thus preventing the threat in advance. There is.

또한, 방탄유리 제작에 있어서도 일반유리와 폴리에스터필름의 접착으로 구성된 기본단위 방탄유리 사이에 충격흡수부재를 통한 충격흡수층을 갖는 구조의 방탄유리를 제공함으로써, 사용자의 요구사항에 따른 다양한 위력을 지닌 총기류에서 발사된 탄두 및 강력한 화력을 지닌 각종 폭탄의 파편으로부터 인명 및 재산을 보호하기 위한 강력한 방탄능력을 갖는 차별화 된 방탄유리를 제공하고 있다.In addition, in the production of bulletproof glass, by providing a bulletproof glass having a shock absorbing layer through the shock absorbing member between the basic unit bulletproof glass composed of the bonding of ordinary glass and polyester film, it has various powers according to the user's requirements It provides differentiated bulletproof glass with strong anti-ballistic capability to protect lives and property from warheads fired from firearms and fragments of powerful fire bombs.

Claims (3)

은행의 직원이 사용하는 책상(120)의 프론트에 수납공간(110)을 갖도록 지지 기둥(111)으로 방탄유리(100)를 형성하고, 상기 방탄유리(100)의 상단으로는 천정(130)에 연결되는 천정연결부(112)를 형성한 것을 특징으로 방탄유리를 이용한 은행용 강도침입방지 구조.A bulletproof glass 100 is formed as a support pillar 111 to have a storage space 110 at the front of the desk 120 used by the employees of the bank, and the top of the bulletproof glass 100 is mounted on the ceiling 130. Strength intrusion prevention structure for banks using bulletproof glass, characterized in that the ceiling connection portion 112 is formed to be connected. 제1항에 있어서, 상기 방탄유리(100)는 소정크기의 넓이를 가지며 5㎜∼l2㎜의 두께를 갖는 일반유리의 표면 중 적어도 어느 한 면에 8~20mil의 두께를 갖는 폴리에스터필름을 접착시켜 형성된 기본 단위의 방탄유리와; 외측방향에 대해 일반유리, 폴리에스터필름의 순서로 배치된 상기 기본단위의 방탄유리가 일정간격을 두고 배치되도록 복수의 기본단위 방탄유리 사이의 사방 가장자리 부위에 부착된 15㎜~25㎜의 폭과 5㎜∼10㎜의 높이를 갖는 충격흡수부재와; 상기 복수의 기본단위 방탄유리와 충격흡수부재의 외측을 감싸 고정 결합하는 프레임을 포함하는 것을 특징으로 하는 방탄유리를 이용한 은행용 강도침입방지 구조.The method of claim 1, wherein the bulletproof glass 100 has a width of a predetermined size and adheres a polyester film having a thickness of 8 to 20 mil to at least one surface of a general glass having a thickness of 5 mm to l2 mm Bulletproof glass of the basic unit formed by; A width of 15 mm to 25 mm attached to the four edges of the plurality of basic unit bulletproof glass so that the bulletproof glass of the basic unit arranged in the order of the normal glass and the polyester film with respect to the outer direction are arranged at a predetermined interval; An impact absorbing member having a height of 5 mm to 10 mm; Strength-preventing structure for banks using bullet-proof glass, characterized in that it comprises a frame for binding and fixing the outer side of the plurality of basic unit bulletproof glass and the impact absorbing member. 제2항에 있어서, 상기 기본단위 방탄유리의 폴리에스터필름 노출면에 상기와 동일하게 충격흡수부재를 매개로 하여 상기 기본단위 방탄유리가 추가로 하나 더 부착된 것을 특징으로 하는 방탄유리를 이용한 은행용 강도침입방지 구조.The bank using the bulletproof glass according to claim 2, wherein the basic unit bulletproof glass is further attached to the polyester film exposed surface of the basic unit bulletproof glass through the impact absorbing member as in the above. Strength penetration prevention structure.
KR20-2004-0010955U 2004-04-20 2004-04-20 Bank crime prevention structure used a bulletproof glass KR200357506Y1 (en)