KR200307756Y1 - High absorbent towel - Google Patents
High absorbent towel Download PDFInfo
- Publication number
- KR200307756Y1 KR200307756Y1 KR20-2002-0037333U KR20020037333U KR200307756Y1 KR 200307756 Y1 KR200307756 Y1 KR 200307756Y1 KR 20020037333 U KR20020037333 U KR 20020037333U KR 200307756 Y1 KR200307756 Y1 KR 200307756Y1
- Authority
- KR
- South Korea
- Prior art keywords
- yarn
- towel
- cotton
- present
- leaf
- Prior art date
Abstract
본 고안은 고흡수성 수건에 관한 것으로서, 파일사는 면사와 4엽상 PET사와의 합연사로 되어 있고 지조직은 4엽상 PET사로 된 것이다.The present invention relates to a superabsorbent towel, pile yarn is a combination yarn of cotton yarn and 4-leaf PET yarn, the branch tissue is made of 4-leaf PET yarn.
본 고안은 파일사를 구성하고 있는 면사가 4엽상 PET사 보다 길게 돌출되어 있으므로 이 부분으로부터 수분을 신속하게 흡수한 후 4엽상 PET 사의 모세관을 통하여 전이 확산시키므로 수분의 흡수, 확산성이 우수하다.In the present invention, since the cotton yarn constituting the pile yarn protrudes longer than the four-leaf PET yarn, it absorbs moisture from this portion quickly and then spreads and spreads through the capillary tube of the four-leaf PET yarn, so the moisture absorption and diffusion are excellent.
따라서 면수건 보다 축축한 감을 주지 않으며 항상 뽀송뽀송한 쾌적감을 부여한다.Therefore, it does not give moist feeling than cotton towel and always gives a soft feeling of comfort.
본 고안의 고흡수성 수건은 수분확산면적비가 1.3 이상이다.The superabsorbent towel of the present invention has a water diffusion area ratio of 1.3 or more.
Description
본 고안은 흡수성과 수분 확산성이 우수하며 사용시 수분에 의한 축축한 촉감을 감소시켜서 항상 쾌적한 상태를 유지시켜주는 고흡수성 수건에 관한 것이다.The present invention relates to a superabsorbent towel that is excellent in absorbency and moisture diffusion and maintains a comfortable state at all times by reducing the moist touch caused by moisture during use.
종래의 세면용 수건은 거의 대부분 면을 소재로 한 것이었는데 이는 면 소재가 자연스럽고 부드러운 촉감과 흡수성이 양호하기 때문이다.Most conventional towels are made of cotton because the cotton material is natural and has a soft touch and good absorbency.
여기서 세면이라 함은 수영, 목욕, 샤워 등과 같이 신체부위를 물과 접촉시키는 모든 행위를 포함하는 것이고, 수건이라 함은 세면행위를 하기 전 및 후에 신체의 수분을 제거하는데 사용하는 도구를 총칭하는 것으로 그것의 크기나 형태에 무관하다.The term "washing" includes all the activities of contacting body parts with water, such as swimming, bathing and showering, and the "towel" refers to the tools used to remove water from the body before and after washing. Regardless of its size or shape.
이와 같은 용도의 수건들은 촉감이 부드러워 이물감이 없어야하고 무엇보다흡수성이 양호하여 사용후에 수분을 신속히 흡수하여 확산시킬 수 있어야 한다.Towels for this purpose should be soft to the touch, there should be no foreign matter, and above all, the good absorbency should be able to quickly absorb and diffuse moisture after use.
지금까지 면이 수건용으로 가장 보편적으로 사용되어진 이유는, 일반적인 화섬 소재에 비해 월등히 높은 공정 수분율에 기인한다.The reason why cotton is most commonly used for towels so far is due to the significantly higher process moisture content compared to common fiber materials.
그러나 면을 소재로한 수건은 수분을 순간적으로 흡수하는 능력(static water absorptivity)이 낮아 초기 사용시 쾌적하지 못하고 수분 확산성이 낮아 흡수한 수분을 오랫동안 보유함으로써 건조성이 낮으며 또 세탁 횟수가 증가할수록 촉감이 뻣뻣해지는 단점을 가진다.However, cotton-based towels have low static water absorptivity, which makes them uncomfortable at the time of initial use. It has the disadvantage of being stiff.
이러한 단점을 개선하기 위하여 흡습가공과 같은 후가공을 병행하는 경우가 있으나 이와 같은 흡습가공은 소재 고유의 촉감을 저하시키고 세탁에 대한 내구성이 불량하다는 결점이 있다.In order to improve this disadvantage, there is a case in which post-processing such as hygroscopic processing is performed in parallel, but such hygroscopic processing has a drawback that the material's inherent touch is lowered and durability for washing is poor.
따라서, 본 고안의 목적은 상기와 같은 문제점을 해결하기 위해 안출한 것으로, 종래의 면 소재의 수건보다 촉감은 뒤지지 않으며서 수분 확산성이 높아 건조성이 높고, 세탁 횟수를 늘려도 부드러운 촉감을 유지할 수 있는 우수한 세면용 고흡수성 수건을 제공함에 있다.Therefore, the object of the present invention was devised to solve the above problems, it does not lag behind the towel of the conventional cotton material, high moisture diffusion, high dryness, it is possible to maintain a soft touch even by increasing the number of washing To provide an excellent washable superabsorbent towel.
도 1은 본 고안에 사용되는 폴리에틸렌 테레프탈레이트 장섬유사의 확대 횡단면도.1 is an enlarged cross-sectional view of a polyethylene terephthalate long fiber yarn used in the present invention.
도 2는 수건의 파일사로부터 면사가 돌출되어 있는 상태를 표시하고 있는 설명도.2 is an explanatory diagram showing a state in which a cotton yarn protrudes from a pile yarn of a towel;
본 고안을 예시도면에 의하여 상세히 설명한다.The present invention will be described in detail by way of illustration.
본 고안은 지조직(1)과 상기 지조직의 상부에 부출(floating) 되어 있는 파일사(2)로 구성되어 있다.The present invention consists of a paper tissue (1) and pile yarn (2) floating on the upper portion of the paper tissue (floating).
본 고안에서 파일사(2)는 면사(2a)와 횡단면 모양이 4개의 돌출부를 갖는 폴리에틸렌 테레프탈레이트 장섬유사(2b)(이하 4엽상 PET사라고 약칭함)를 합연한 합연사로 되어 있으며, 지조직(1)은 횡단면 모양이 4개의 돌출부를 갖는 폴리에틸렌 테레프탈레이트 장섬유사(2b)로 되어 있다.In the present invention, the pile yarn 2 is a twisted yarn that combines a cotton yarn 2a and a polyethylene terephthalate long fiber yarn 2b (hereinafter, abbreviated as 4-leaf PET yarn) having four protruding cross sections. The tissue 1 is made of polyethylene terephthalate long fiber yarn 2b having four protrusions in cross-sectional shape.
본 고안의 4엽상 PET사(2b)는 돌출부 사이에 모세관(2c)이 길게 형성되어 있다.The 4-leaf PET yarn 2b of the present invention has a long capillary tube 2c formed between the protrusions.
본 고안에 의한 수건의 원단은 직물, 편물 모두 가능하나, 더욱 바람직하게는 경편 조직으로 하는 것이 좋다.The fabric of the towel according to the present invention can be both a woven fabric and a knitted fabric, but more preferably a warp knitted fabric.
경편조직의 수건은 환편 제품보다 우수한 형태안정성을 가지므로 수건의 일부분이 파손된 후에도 실이 풀려 나오는 문제가 없으며 생산성도 높아서 가격도 저렴하다.Towels of warp knitting tissue have better shape stability than circular knitting products, so there is no problem of thread unraveling even after a part of the towel is broken, and the productivity is high and the price is low.
본 고안의 수건은 도 2에 도시한 바와 같이 표면으로 돌출된 파일사(2)는 면사(2a)와 4엽상 PET사(2b)의 합연사로 되어 있지만 원단을 염색, 열 셋팅등의 후가공처리를 하면 4엽상 PET사(2b)는 수축을 일으키므로 자연스럽게 면사(2a)부분이 돌출하여 파일사(2)로부터 면사(2a) 부분이 더 길게 연장되는 형태를 이루게 된다.In the towel of the present invention, as shown in Fig. 2, the pile yarn 2 protruding to the surface is made of a twisted yarn of cotton yarn 2a and 4-leaf PET yarn 2b, but the post-processing treatment such as dyeing and heat setting the fabric When the 4-leaf PET yarn (2b) causes the contraction, the cotton yarn (2a) portion naturally protrudes to form a form in which the cotton yarn (2a) portion is extended longer from the pile yarn (2).
이렇게 되면 수건을 사용할 때 길게 돌출되어 있는 면사(2a)부분이 수분을 먼저 흡수한 다음에 인접한 4엽상 PET사(2b)에 형성되어 있는 모세관(2c)을 통하여 수분이 신속하게 전이 되기 때문에 본 고안의 고흡수성 수건은 수분의 흡수성과 확산성이 매우 우수하므로 축축한 감을 주는 면수건에 비하여 항상 뽀송뽀송한 쾌적감을 줄 수 있다.In this case, the cotton yarn (2a) protruding long when using the towel absorbs the water first, and then the moisture is quickly transferred through the capillary (2c) formed in the adjacent 4-leaf PET yarn (2b) The superabsorbent towels have excellent moisture absorption and diffusivity, so they can always give a soft and comfortable feeling compared to cotton towels that give a damp feeling.
본 고안의 고흡수성 수건은 면수건의 경우 물방울이 떨어진 면과 그 반대면간의 수분확산비를 1.0이라고 할때 상술한 바와 같이 수분의 확산성이 우수하기 때문에 수분확산비가 적어도 1.3 이상이 된다.The superabsorbent towel of the present invention has a water diffusion ratio of at least 1.3 or more because the water diffusion ratio is excellent as described above when the water towel between the surface where the water droplet is dropped and the opposite surface is 1.0.
이하 예시를 통하여 본 고안을 더욱 구체적으로 설명한다.The present invention will be described in more detail with reference to the following examples.
그리고 여러 가지 기능성의 측정 방법은 아래의 방법을 적용하였다.In addition, the following method was used for measuring various functionalities.
[흡수성(Static water absorptivity)의 측정][Measurement of static water absorptivity]
시료를 길이 25㎝, 폭 2.5㎝의 시료를 만든 후 JIS L 1096 B법의 방법으로 단위 시간당 수분의 흡수 높이를 측정하여 5회 평균치로 흡수성을 비교하였다.After making the sample 25 cm in length and 2.5 cm in width, the absorption height of water per unit time was measured by the method of JISL1096B method, and water absorption was compared with the average value of 5 times.
[건조성의 측정][Measurement of Dryness]
가로×세로를 7.5㎝×7.5㎝가 되도록 시료를 만든 후 항온항습실에서 하루 동안 방치 후 무게(Wo)를 측정하고, 27℃±2℃의 증류수 욕조에 침지 시켜 30분간 충분히 침지시킨 후 10초간 탈수하여 무게(Wa)를 측정한다.After making the sample so that the width × length to 7.5 ㎝ × 7.5 ㎝, it is left in a constant temperature and humidity room for one day and then the weight (Wo) is measured, immersed in a distilled water bath of 27 ℃ ± 2 ℃ sufficiently immersed for 30 minutes and dehydrated for 10 seconds Measure the weight Wa.
이 상태의 시료를 상온에서 건조시키면서 10분마다 무게(Wb)를 측정하여 수분이 완전히 건조되어 더 이상 무게의 변화가 없을 때까지 측정하여 수분 건조량을 산출한다.While drying the sample in this state at room temperature, the weight (Wb) is measured every 10 minutes until the moisture is completely dried and no more change in weight to calculate the moisture dry amount.
이것을 5회 반복하면서 아래 수식에 따라 수분 건조량의 평균치를 산출한다.Repeating this five times, the average value of the moisture drying amount is calculated according to the following formula.
초기 잔존 수분량 = Wa-WoInitial amount of remaining water = Wa-Wo
10분 후 잔존 수분량 = Wb-WoWater content remaining after 10 minutes = Wb-Wo
10분 후 건조량(Z10) = (초기 잔존 수분량) - (10분 후 잔존 수분량)Drying amount after 10 minutes (Z10) = (Initial remaining water content)-(Remaining water content after 10 minutes)
20분 후 건조량(Z20) = (10분 후 잔존 수분량) - (20분 후 잔존 수분량)Drying amount after 20 minutes (Z20) = (remaining moisture after 10 minutes)-(remaining moisture after 20 minutes)
※10분 간격으로 건조까지 반복한다.※ Repeat drying every 10 minutes.
[흡수량의 측정][Measurement of Absorption]
가로×세로를 7.5㎝×7.5㎝가 되도록 시료를 만든 후 항온항습실에서 하루 동안 방치 후 무게(Wo)를 측정하고, 27℃±2℃의 증류수 욕조에 침지 시켜 30분간 충분히 침지시킨 후 10초간 탈수하여 무게(Wa)를 측정한 후 아래 식에 의거하여 흡수율을 계산한다.After making the sample so that the width × length to 7.5 ㎝ × 7.5 ㎝, it is left in a constant temperature and humidity room for one day and then the weight (Wo) is measured, immersed in a distilled water bath of 27 ℃ ± 2 ℃ sufficiently immersed for 30 minutes and dehydrated for 10 seconds After measuring the weight (Wa), calculate the absorption based on the following equation.
[확산성의 측정][Measurement of Diffusion]
가로×세로를 7.5㎝×7.5㎝가 되도록 시료를 만든 후 항온항습실에서 하루 동안 방치한 후 0.3cc의 물을 수건 표면 2㎝ 높이에서 낙하시켜 낙하면과 반대면에서 수분이 확산되는 직경을 측정After making the sample so that the width × length is 7.5cm × 7.5cm, it is allowed to stand in the constant temperature and humidity room for one day, and then 0.3cc of water is dropped at the height of 2cm from the towel surface to measure the diameter of water diffusion from the opposite surface.
실시예Example
도 1에 도시한 단면 모양의 150데니어/144필라멘트 폴리에틸렌테레프탈레이트 장섬유 가연가공사와 면 30수를 합연하여 제조한 합연사를 이용하여 4bar 경편 기에서 파일 조직으로 파일편지를 제조하였다.A pile letter was prepared from a 4bar warp knitting machine using a plywood yarn prepared by combining 150 denier / 144 filament polyethylene terephthalate long-fiber combustible with 30 cross-sections shown in FIG.
상기 파일편지를 일반적인 면과 폴리에스테르 복합제품의 염색, 가공 공정으로 가공하여서 본 고안의 고흡수성 수건을 제조하였다.The pile letter was processed by dyeing and processing a general cotton and polyester composite product to prepare a super absorbent towel of the present invention.
이렇게 제조된 수건의 기능성 평가를 위하여 상기의 평가 법에 따라 시중에 판매 중인 면 소재의 수건과 비교 평가를 실시하여 그 결과를 표 1에 나타내었다.In order to evaluate the functionalities of the towels thus manufactured, a comparative evaluation was performed with cotton towels on the market in accordance with the above evaluation method, and the results are shown in Table 1.
< 표 1 ><Table 1>
본 고안은 상기에 기술된 실시예들에 의해 한정되지 않고, 당업자들에 의해 다양한 변형 및 변경을 가져올 수 있으며, 이는 첨부된 청구항에서 정의되는 본 고안의 취지와 범위에 포함된다.The present invention is not limited to the embodiments described above, and various changes and modifications can be made by those skilled in the art, which are included in the spirit and scope of the present invention as defined in the appended claims.
본 고안에 의한 고흡수성 수건은 기존의 면 수건에 비하여 흡수성과 수분확산성이 매우 우수하므로 사용시 축축한 느낌을 주지않으며 항상 쾌적한 상태를 유지한다.The superabsorbent towel according to the present invention has excellent water absorption and moisture diffusion compared to the conventional cotton towel, so it does not give a damp feeling when used and always maintains a comfortable state.
본 고안의 수건은 가정용 세면 수건 뿐 아니라 골프 등 스포츠용으로 적합하며 행주, 목용 용품 등의 가정 용품으로도 적합하다.The towel of the present invention is suitable not only for home toilet towel but also for sports such as golf, and also for household goods such as dishcloth and neck goods.
Claims (3)