KR20030082019A - Electrophotographic photoconductor - Google Patents

Abstract

PURPOSE: A photoreceptor for electrophotography is provided, to improve the electron transfer capability, the compatibility with a binding resin and the optical properties and to suppress the generation of defect of coating. CONSTITUTION: The photoreceptor comprises a hole transfer material, a charge generation material and an electron transfer material on a conductive substrate, wherein the photoreceptor layer comprises the compound represented by the formula 1 or 2. In the formula 1, R1 and R2 which are identical or different each other represent H, a substituted or unsubstituted alkyl group, a substituted or unsubstituted alkoxy group, a substituted or unsubstituted aryl group, a substituted or unsubstituted allyl group, a substituted or unsubstituted aralkyl group, a substituted or unsubstituted amino group, a substituted or unsubstituted phenyl group or a halogen atom; and in the formula 2, R3 and R4 which are identical or different each other represent H, a substituted or unsubstituted alkyl group, a substituted or unsubstituted alkoxy group, a substituted or unsubstituted aryl group, a substituted or unsubstituted allyl group, a substituted or unsubstituted aralkyl group, a substituted or unsubstituted amino group, a substituted or unsubstituted phenyl group or a halogen atom.

Description

Electrophotographic photosensitive member {ELECTROPHOTOGRAPHIC PHOTOCONDUCTOR}

The present invention relates to an electrophotographic photosensitive member using pyran and a compound thereof.

In image forming apparatuses, such as an electrostatic copying machine, a laser printer, and a plain paper facsimile apparatus, a photosensitive material comprising a charge generating agent that generates charges by light irradiation, a charge transporting agent that transports generated charges, and a binder resin in which these materials are dispersed. Electrophotographic photosensitive members called organophotoreceptors having a layer formed on a conductive gas are widely used.

The organophotoreceptor includes a single-layer photosensitive member comprising a charge generating agent and a charge transporting agent in the same layer, a laminated photosensitive member laminated with a charge generating layer containing a charge generating agent and a charge transporting layer containing a charge transporting agent. The double laminated photosensitive member is common.

In general, a laminated photosensitive member generally forms a charge generating layer and a thicker charge transport layer in this order on the surface of the conductive gas from consideration of mechanical strength.

As the charge transporting agent, there are a hole transporting agent and an electron transporting agent, but most of the known charge transporting agents are carrier transporters having high carrier mobility that can impart practical sensitivity to the photosensitive member.

For this reason, the organophotoreceptor currently put into practical use becomes a secondary type in the case of the laminated type in which the charge transport layer is formed on the surface side.

However, the incident photosensitive laminated photosensitive member needs to be charged by negative polar corona discharge with a large amount of ozone generation.

Therefore, the influence on the environment by ozone and deterioration of the photosensitive member itself become a problem.

In addition, most of the organic photoconductors currently commercialized as described above are laminated photoconductors, whereas single-layer photoconductors are simple in structure and easy to manufacture, and can suppress the occurrence of film defects and improve optical characteristics. There are many advantages.

In addition, the single-layer photosensitive member can be used for both positive and negative transfer types by using an electron transporting agent and a hole transporting agent together as a charge transporting agent, and there is a possibility of expanding the application range of the photosensitive member.

However, no substantial single layer photoreceptor having good matching with the charge generating agent and favorable electron injection from the charge generating agent has been proposed.

Due to the above reasons, the single-layer photosensitive member has not been widely used.

SUMMARY OF THE INVENTION The main object of the present invention is to provide a highly sensitive single layer electrophotographic photosensitive member using pyran and its compound which can be suitably used as an electron transporting agent because of its excellent compatibility with electron transporting properties and binding resins.

Another object of the present invention is to provide a high sensitivity single layer type electrophotographic photosensitive member which can be used for both positive and secondary types.

[Measures for solving the problem]

In order to solve the above problems, the electrophotographic photosensitive member of the present invention is an electrophotographic photosensitive member having a single-layer photosensitive layer on a conductive substrate, wherein the electrophotographic photosensitive member has a single layer photosensitive layer composed of a charge transport material, a charge generating material, and an electron transport material. The electron transporting substance corresponds to the following general formula (I),

(Wherein R1 and R2 are the same as or different from each other, a hydrogen atom, an alkyl group, an alkoxy group, an aryl group, an allyl group, an aralkyl group, an amino group, a phenyl group, a halogen atom or an alkyl group which may have a substituent, an alkoxy group, an aryl group) And an allyl group, an aralkyl group, an amino group, or a phenyl group).

Alternatively, the electrophotographic photosensitive member of the present invention is an electrophotographic photosensitive member having a single-layer photosensitive layer on a conductive substrate, wherein the electron transporting material is included in the single-layer photosensitive layer composed of a charge transport material, a charge generating material and an electron transport material. The following general formula (II),

(Wherein R3 and R4 are the same as or different from each other, a hydrogen atom, an alkyl group, an alkoxy group, an aryl group, an allyl group, an aralkyl group, an amino group, a phenyl group, a halogen atom or an alkyl group which may have a substituent, an alkoxy group, an aryl group) And an allyl group, an aralkyl group, an amino group, or a phenyl group).

1 is a schematic cross-sectional view showing an electrophotographic photosensitive member according to an embodiment of the present invention.

The present invention provides a highly sensitive tomographic electrophotographic photosensitive member using pyran and a compound thereof which can be used as an electron transporting agent because of its excellent compatibility with the electron transporting properties and the binder resin, which are the main objects of the present invention. Another object is to provide a highly sensitive single-layer electrophotographic photosensitive member that can be used in both positive and secondary types,

The present invention provides an electrophotographic photosensitive member having a single layer photosensitive layer on a conductive substrate, wherein the electron transport material is formed in the single layer photosensitive layer composed of a charge transport material, a charge generating material and an electron transport material.

The following general formula (I),

(Wherein R1 and R2 are the same as or different from each other, a hydrogen atom, an alkyl group, an alkoxy group, an aryl group, an allyl group, an aralkyl group, an amino group, a phenyl group, a halogen atom or an alkyl group which may have a substituent, an alkoxy group, an aryl group) And an allyl group, an aralkyl group, an amino group, or a phenyl group).

In addition, although the specific example of the pyran compound which can be used for this invention is shown to the following structural formula (I-1) and structural formula (I-2), it is not limited to these in this invention.

Alternatively, in an electrophotographic photosensitive member having a single layer photosensitive layer on a conductive substrate, an electron transporting material is contained in a single layer photosensitive layer composed of a charge transport material, a charge generating material and an electron transport material.

The following general formula (II),

(Wherein R3 and R4 are the same as or different from each other, a hydrogen atom, an alkyl group, an alkoxy group, an aryl group, an allyl group, an aralkyl group, an amino group, a phenyl group, a halogen atom or an alkyl group which may have a substituent, an alkoxy group, an aryl group) And an allyl group, an aralkyl group, an amino group, or a phenyl group).

In addition, specific examples of thiopyran dioxide compounds which can be used in the present invention are shown in the following structural formulas (II-1) to (II-4).

Hereinafter, exemplary embodiments of the present invention will be described in detail with reference to the accompanying drawings.

However, the following examples are only for illustrating the present invention, and the scope of the present invention is not limited to these examples.

1 is a schematic cross-sectional view showing an example of the configuration of the photoconductor of the present invention, and illustrates a single-layer electrophotographic photoconductor having a photosensitive layer S3 provided by sandwiching a lower layer S2 on a conductive base S1. .

The conductive base S1 serves as an electrode of the photoconductor and also serves as a support for each layer constituting the photoconductor. The conductive base S1 may have any shape such as a cylindrical shape, a plate shape, a film shape, and may be made of aluminum, stainless steel, The conductive treatment may be performed on metals such as nickel or surfaces such as glass and resin.

Servant layer (S2) is made of a metal oxide film such as a resin-based layer or an alumite, and controls charge injection from the conductive substrate to the photosensitive layer, coating defects on the surface of the substrate, and improving adhesion between the photosensitive layer and the substrate. It can provide as needed for the purpose. Examples of the resin material used in the lower layer include insulating polymers such as casein, polyvinyl alcohol, polyamide, melamine, cellulose, conductive polymers such as polythiophene, polypyrrole, and polyaniline. These resins can be used alone or in combination as appropriate. It is also possible to contain metal oxides such as titanium dioxide and zinc oxide in these resins.

The photosensitive layer S3 is composed of a charge generating material and a hole transporting material and an electron transporting material which is a feature of the present invention.

Examples of the charge generating substance include phthalocyanine compounds such as X-type metal-free phthalocyanine, ι-type metal-free phthalocyanine, α-type titanyl phthalocyanine, β-type titanyl phthalocyanine, Y-type titanyl phthalocyanine, amorphous titanium-phthalocyanine, and ε-type copper phthalocyanine. Various azo pigments, anthoanthrone pigments, thiapyrylium pigments, perylene pigments, perinone pigments, squarylium pigments, quinacridone pigments, etc. may be used alone or in appropriate combination, or selenium Alternatively, a selenium compound or the like can be used, and an appropriate material can be selected according to the light wavelength region of the exposure light source used for forming the image.

As the hole transporting material, various hydrazone compounds, styryl compounds, diamine compounds, butadiene compounds, indole compounds, etc. may be used alone or in combination as appropriate, and as a resin binder, bisphenol A type, bisphenol Z type, bisphenol A may be used. Polycarbonate resins, such as a type-biphenyl copolymer, polystyrene resin, polyphenylene resin, etc. can be used individually or in combination suitably, respectively.

As an electron transport material, the following general formula (I) which this invention proposes,

(Wherein R1 and R2 are the same as or different from each other, a hydrogen atom, an alkyl group, an alkoxy group, an aryl group, an allyl group, an aralkyl group, an amino group, a phenyl group, a halogen atom or an alkyl group which may have a substituent, an alkoxy group, an aryl group) Pyran represented by an allyl group, an aralkyl group, an amino group, and a phenyl group) and a compound thereof are used.

Or to the corresponding general formula (II)

(Wherein R3 and R4 are the same as or different from each other, a hydrogen atom, an alkyl group, an alkoxy group, an aryl group, an allyl group, an aralkyl group, an amino group, a phenyl group, a halogen atom or an alkyl group which may have a substituent, an alkoxy group, an aryl group) And an allyl group, an aralkyl group, an amino group, or a phenyl group).

{Example 1}

Hereinafter, the present invention will be described in detail based on Examples.

On the outer circumference of an aluminum cylinder having an outer diameter of 30 mm and a length of 254 mm as the conductive base (S1), 5 parts by weight of alcohol-soluble nylon (Aramimin CM8000, manufactured by Toray Industries, Ltd.) was dissolved in 90 parts by weight of methane as a servant layer. Immersion was also carried out and dried at a temperature of 100 ° C. for 30 minutes to form a lower layer S2 having a thickness of about 2 μm.

On this servant layer S2, 1.5 parts by weight of an X-type metal-free phthalocyanine as a charge generating material and 100 parts by weight of a polycarbonate resin (tough ZB-300, manufactured by Idemitsu Chemical Co., Ltd.) as a resin binder are dichloromethane and dichloro. 60 parts by weight of an equivalent mixture with ethane and 100 parts by weight of a compound represented by Structural Formula (I-1) as an electron transporting material (manufactured by Syntec Co., Ltd.) and a hydrazone compound as a hole transporting material (manufactured by Mitsubishi Paper Co., Ltd.) 100 A single-layer photosensitive layer dispersion prepared by dissolving and dispersing the parts by weight using a homogenizer was applied by an immersion coating method and dried at a temperature of 90 ° C. for 60 minutes to form a charge transport layer having a film thickness of about 25 μm, thereby producing an electrophotographic photosensitive member. do.

{Example 2}

Hereinafter, the present invention will be described in detail based on another embodiment.

On the outer circumference of an aluminum cylinder having an outer diameter of 30 mm and a length of 254 mm as the conductive substrate S1, 5 parts by weight of alcohol-soluble nylon (Aramimin CM8000, manufactured by Toray Industries Co., Ltd.) was dissolved in 90 parts by weight of methanol as a servant layer. It coated and dried for 30 minutes at the temperature of 100 degreeC, and formed the lower layer S2 of about 2 micrometers in film thickness.

On this servant layer S2, 1.5 parts by weight of X-type metal-free phthalocyanine as a charge generating material and 100 parts by weight of a polycarbonate resin (tough ZB-300, manufactured by Idemitsu Chemical Co., Ltd.) as a resin binder are dichloromethane and dichloro. 60 parts by weight of an equivalent mixture with ethane, 100 parts by weight of a compound represented by Structural Formula (II-1) as an electron transporting material, and 100 parts by weight of a benzidine compound (manufactured by Qinghua Co., Ltd.) as a hole transporting material A single layer photosensitive layer dispersion obtained by dissolving and dispersing the part using a homogenizer is applied by an immersion coating method, dried at a temperature of 90 ° C. for 60 minutes to form a charge transport layer having a film thickness of about 25 μm, thereby producing an electrophotographic photosensitive member.

Thus, in order to examine the photosensitive characteristics of the electrophotographic photosensitive members obtained in the above-described examples, the electrophotographic photosensitive member was charged positively while being rotated using an electrostatic radiation test apparatus (Gentec Syndia-00 manufactured by Zentec Corporation).

In addition, by measuring the charge potential (V) of each rotating electrophotographic photosensitive member, using a laser diode having a wavelength of 780nm to expose the surface of the electrophotographic photosensitive member and to obtain the time until the surface potential is 1/2 , Half-life exposure amount E1 / 2 (μJ / cm 2) was calculated. Moreover, the surface potential after 0.15 second after exposure was made into residual potential Vr (V).

Table 1 shows the results of charging and photosensitive characteristics of each electrophotographic photosensitive member obtained in the above-described examples.

From Table 1, it can be seen that the single-layer photosensitive member proposed in the present invention can be used for electrostatic electrostatic photography. In addition, the photoconductor has a number of advantages, such as being simple and easy in structure, to suppress the occurrence of film defects and to improve optical characteristics.

In addition, a single-layer photosensitive member can be used as a charge transporting agent together with an electron transporting agent and a hole transporting agent, so that a single photosensitive member can be used for both positive and negative transfer types, and the application range of the photosensitive member can be expanded.

Although the above has been described with reference to a preferred embodiment of the present invention, those skilled in the art will be variously modified and changed within the scope of the invention without departing from the spirit and scope of the invention described in the claims below. I can understand that you can.

Claims (2)

In a single-layer electrophotographic photosensitive member composed of a hole transport material, a charge generating material and an electron transporting material on a conductive substrate, The photosensitive layer is represented by the following general formula (I), (Wherein R1 and R2 are the same as or different from each other, a hydrogen atom, an alkyl group, an alkoxy group, an aryl group, an allyl group, an aralkyl group, an amino group, a phenyl group, a halogen atom or an alkyl group which may have a substituent, an alkoxy group, an aryl group) And an allyl group, an aralkyl group, an amino group, or a phenyl group). In a single-layer electrophotographic photosensitive member composed of a hole transport material, a charge generating material and an electron transporting material on a conductive substrate, The photosensitive layer is represented by the following general formula (II), (Wherein R3 and R4 are the same as or different from each other, a hydrogen atom, an alkyl group, an alkoxy group, an aryl group, an allyl group, an aralkyl group, an amino group, a phenyl group, a halogen atom or an alkyl group which may have a substituent, an alkoxy group, an aryl group) And an allyl group, an aralkyl group, an amino group, or a phenyl group).