Abstract

PURPOSE: Provided is an attachable board which shows excellent water impermeability and an increased surface hardness by UV coating and is able to be attached to other places using a removable adhesive. CONSTITUTION: The attachable board is produced by UV coating a reactive material(1) comprising isocyanate-reactive binder with NOC/OH equivalent ratio of 3:1.5 to 1.5:3 onto one surface of a polypropylene resin(2) using a 80 to 180 mesh roll; applying an adhesive material(3) onto the other surface of the resin; forming a print layer(4) on one surface of a polypropylene resin(5); and applying a removable adhesive(6) onto the other surface of the resin, followed by attaching a releasable paper(7). The isocyanate-reactive binder comprises 30 to 80 % by weight of urethane acrylate, 10 to 20 % by weight of 1,6-hexandiol and 5 to 10 % by weight of phenylphosphine oxide.

Description

Adhesive type board {Adhesion type board}

본 발명은 접착형 보드에 관한 것으로, 특히 UV 코팅하여 시트 표면의 경도를 높여주고 리무버블(Removable) 접착제를 사용하여 다른 장소에 쉽게 탈부착하여 사용할 수 있도록 한 비침수성, 비침투성이 우수한 접착형 보드에 관한 것이다.The present invention relates to an adhesive board, in particular to a non-invasive, non-invasive adhesive board that can be used by UV coating to increase the hardness of the sheet surface and to be easily removable to another place using a removable adhesive (Removable) adhesive It is about.

일반적으로 가정을 비롯하여 사무실, 레스토랑 등에서 메모를 하고자할 때에 주로 메모 용지를 사용하여 메모를 하게 되는데, 이때 메모용지를 분실하여 당황하게 되는 현상이 종종 발생 한다.In general, when you want to take notes in homes, offices, restaurants, etc., a memo is mainly used to take notes. At this time, the memo paper is lost and embarrassed.

또한, 근래에는 각종 정보를 인쇄시킨 인쇄용지를 투명한 비닐지로 씌워 책받침 형태로 코팅시켜서된 각종 광고판이 제공되는데, 이와 같이 메모할 수 있도록 하는 메모판으로 제공되는 광고판은 부착시킬 수 없도록 되어 있으므로 쉽게 분실하여 장기간 보관할 수 없었고, 메모를 할때에는 거의 지워지지 않는 사인펜이나 유성펜 등을 사용하기 때문에 사용이 거듭될수록 메모할 수 있는 공간이 점차적으로 줄어들게 될 뿐만 아니라 표면이 지저분해져 버리게 된다.In addition, recently, various advertisement boards provided by printing a variety of information printed on a transparent plastic sheet and coated in the form of a book support are provided. The advertisement board provided as a memo board for memo can be attached so that it is easily lost. It couldn't be stored for a long time, and since it uses a signature pen or oil pen that is hardly erased when taking notes, the space for taking notes is gradually reduced as the use is repeated, and the surface becomes dirty.

또한, 학교나 학원 등에서 강의를 할때에는 주로 칠판에 분필을 이용하여 글씨를 쓰게되므로 강의자의 건강을 해치고 주변을 심하게 오염시키게 되며, 이러한 현상을 해소하기 위하여 근래에는 화이트보드와 수성펜을 사용하기도 하지만 화이트보드를 별도로 구입하여야 하고 화이트보드에 쓰여진 글씨는 시간이 지남에 따라 잘 지워지지 않는 문제점이 있다.In addition, when lectures in schools or academies are mainly written using chalk on the blackboard, so as to harm the lecturer's health and heavily pollute the surroundings. The board has to be purchased separately and the writing on the whiteboard is a problem that does not erase well over time.

본 발명의 목적은 손쉽게 메모내용을 수분으로 소거되도록 한 접착형 보드를 제공하는데 있다.SUMMARY OF THE INVENTION An object of the present invention is to provide an adhesive board for easily erasing memo contents with moisture.

본 발명의 다른 목적은 수분이 침투되지 않는 성질이 있는 투명한 보드의 이면에 각종 문구와 글씨 및 그림 도형을 인쇄하고 그 이면에 점착제를 도포시켜 접합하고 , 상기 또 다른 이면에는 접착제를 도포하여 이형지를 부착시켜서 된 접착형 보드를 제공하는데 있다.Another object of the present invention is to print a variety of phrases, letters and figures on the back of the transparent board having a property that does not penetrate the water and to apply a pressure-sensitive adhesive on the back, the other back surface by applying an adhesive to the release paper It is to provide an adhesive board made by attaching.

본 발명의 또다른 목적은 시트에서 이형지를 분리시킨 후 특정하지 않은 어느곳에도 부착하여 사용이 가능하고, 칠판이나 화이트보드의 대용 및 메모판으로활용할 수 있도록 한 접착형 보드를 제공하는데 있다.Still another object of the present invention is to provide a self-adhesive board that can be used to remove the release paper from the sheet and then attach it to any place not specified, and can be used as a substitute for a blackboard or a white board and a memo board.

도 1 은 본 발명에 따른 접착형 보드의 실시예를 나타낸 단면도.1 is a cross-sectional view showing an embodiment of an adhesive board according to the present invention.

<도면의 주요 부분에 대한 부호의 설명><Explanation of symbols for the main parts of the drawings>

1 : UV 코팅면 2 : PP시트1: UV coated surface 2: PP sheet

3 : 점착제 4 : 인쇄층3: adhesive 4: printed layer

5 : PP시트 6 : 접착제5: PP sheet 6: adhesive

7 : 이형지7: release paper

이하, 첨부도면을 참조하여 본 발명에 따른 바람직한 실시예에 대하여 상세히 설명한다.Hereinafter, exemplary embodiments of the present invention will be described in detail with reference to the accompanying drawings.

도 1 은 본 발명에 따른 접착형 보드의 실시예를 나타낸 단면도이다.1 is a cross-sectional view showing an embodiment of an adhesive board according to the present invention.

본 발명은 출원번호 20-2000-0033602(실용신안)로 선출원한 함수소거 메모펜용 접착형 메모판의 개량 발명으로, 선출원된 내용과 중복되는 부분의 설명은 생략 한다.The present invention is an improved invention of the adhesive memo pad for water-absorbing memo pens, filed in application number 20-2000-0033602 (utility model), and the description of the overlapping portions of the previously filed contents will be omitted.

본 발명의 접착형 보드는 표면의 경도를 높여주기 위하여 UV코팅 하는 것으로, 우레탄 수지를 사용하고 경도를 높이기 위하여 빛 반응제를 사용하여 자외선 건조를 하며, 보드 표면의 무반사(무광)를 향상시키기 위하여 80∼180 메쉬(mesh) 롤(roll)을 사용한다.Adhesive board of the present invention is to UV coating to increase the hardness of the surface, using a urethane resin and UV drying using a light reactant to increase the hardness, in order to improve the antireflection (matte) of the surface of the board 80 to 180 mesh rolls are used.

더욱 구체적으로는 폴리 프로필렌수지(2)에 두께가 다른 인쇄층(4)이 형성된 폴리 프로필렌수지(5)를 점착제(3)를 도포하여 접합시킨 것의 이면에는 접착제를 도포한 다음 이형지를 부착시키고 다른 이면에는 UV반응성 물질로 코팅을 한다. 즉, 폴리프로필렌수지(2)이면에 UV 반응성물질로 UV코팅(1)을 하고 다른 이면에는 점착물질(3)을 코팅하거나 열접착하고, 폴리프로필렌수지(5)의 이면에 인쇄층(4)을 형성하며 다른 이면에는 접착제(6)를 형성하여 이형지(7)를 부착한다.More specifically, the polypropylene resin 5 having the printed layer 4 having a different thickness on the polypropylene resin 2 is coated with an adhesive 3, and then the adhesive is applied to the back side of the polypropylene resin 5, and then the release paper is attached. The back side is coated with UV reactive material. In other words, the polypropylene resin (2) is UV coated (1) with a UV reactive material on the other side, the adhesive material (3) is coated or thermally bonded on the other side, and the printing layer (4) on the back of the polypropylene resin (5) Form the adhesive and on the other side to form an adhesive (6) to attach the release paper (7).

UV 반응성 코팅물질은 UV 반응성물질1-99%과 반응성 희석제를 1-15중량%를 혼합한 것을 사용하고, 점도는 45,000 내지 400,000 센티포이즈가 적당하다.The UV reactive coating material is a mixture of 1-99% by weight of the UV reactive material and 1-15% by weight of the reactive diluent, and a viscosity of 45,000 to 400,000 centipoise is appropriate.

상기 UV 반응성 물질은 아크릴화 에폭시수지,아크릴화 우레탄 수지,수성폴리올 중의 어느 한 종류가 선택 사용되고. 반응성 희석제로는 이소옥틸 아크릴레이트,라우릴 아크릴레이트,라우릴 메타크릴레이트,히드록시프로필 아크릴레이트, 헥실 아크릴레이트, 헥실 메타 아크릴레이트등의 어느 한종류가 선택 사용된다.The UV reactive material may be selected from any one of acrylated epoxy resins, acrylated urethane resins, and aqueous polyols. As the reactive diluent, any one of isooctyl acrylate, lauryl acrylate, lauryl methacrylate, hydroxypropyl acrylate, hexyl acrylate and hexyl methacrylate is optionally used.

또 다른 UV 반응성 코팅물질은 NCO/OH 의 당량비가 3 : 1.5 내지 1.5 : 3인 이소시아네이트-반응성결합제로 코팅한다. .Another UV reactive coating material is coated with an isocyanate-reactive binder having an equivalent ratio of NCO / OH of 3: 1.5 to 1.5: 3. .

상기 이소시아네이트-반응성결합제는 우레탄 아크릴레이트30-80중량%, 1,6-헥산디올 10-20중량% ,페닐포스핀 옥사이드 5-10중량%로 조성된다.The isocyanate-reactive binder is composed of 30-80% by weight of urethane acrylate, 10-20% by weight of 1,6-hexanediol, and 5-10% by weight of phenylphosphine oxide.

또한, 보드 표면의 무반사를 향상시키기 위하여 80∼180 메쉬 롤을 사용하여 코팅를 행한다.Moreover, in order to improve the antireflection of the board surface, coating is performed using 80-180 mesh rolls.

상기 롤의 메쉬가 80메쉬 이하인 경우에는 보드에 문자를 쓸 때 운필성이 없어지고, 180메쉬 이상인 경우에는 운필성은 좋으나 지움성이 떨어지는 문제점이 있다. 바람직하게는 150 메쉬, 175 메쉬 롤이 가장 좋다..When the mesh of the roll is 80 mesh or less, the writing property is lost when writing a character on the board, and when the mesh is more than 180 mesh, the writing property is good but the eraseability is inferior. Preferably, 150 mesh and 175 mesh rolls are best.

UV코팅의 필름은 0.1T∼0.2T 두께의 PP 필름(2)을 사용하는 것으로, 표면의 무반사를 위하여 80∼175 메쉬 롤을 사용하고 필름 사출방법으로 다이스 공법을 이용한다. 상기 0.1T∼0.2T 두께의 PP 필름의 사용으로 표면의 UV 코팅시 흡착이 용이하게 된다.The film of UV coating uses the PP film 2 of 0.1T-0.2T thickness, uses 80-175 mesh rolls for the surface antireflection, and uses the die-casting method as a film injection method. The use of the 0.1T to 0.2T thick PP film facilitates the adsorption upon UV coating of the surface.

인쇄층의 필름은 0.25T∼0.5T 두께의 PP 필름(5)을 사용하는 것으로, 필요에 따라 다양한 색상(안료첨가)을 혼합하여 다양한 색상의 미를 쉬트상에 표현할 수 있으며, 그 위에 인쇄층(4)을 형성하여 학교칠판용 암선, 월중계획표, 띠선, 게시판 등 다양한 용도로 이용할 수 있다. 필름 사출방법으로 카렌더(calander) 공법을 이용하며. 상기 0.25T∼0.5T 두께의 PP 필름(7)의 사용으로 후면의 비쳐나옴등을 방지한다.The film of the printing layer uses a PP film 5 having a thickness of 0.25T to 0.5T, and various colors (pigments) can be mixed as necessary to express the beauty of various colors on a sheet, and the printing layer thereon. (4) can be formed and used for various purposes such as school boards, monthly schedules, bands, bulletin boards, etc. The film injection method uses a calender method. The use of the 0.25T to 0.5T thickness of the PP film 7 prevents the back surface from shining and the like.

점착제(3)는 상지 PP시트필름(2)와 하지시트PP 필름(5)를 상호 점착시킨다. 일반용으로 고강도 점착제를 사용하거나 또는 열접합 방법을 이용한다.The adhesive 3 adhere | attaches the upper PP sheet film 2 and the lower sheet PP film 5 mutually. Use a high-strength adhesive for the general purpose or use a thermal bonding method.

하지시트PP 필름(5)에는 아크릴계 수용성 접착제나 리무버블(removable)접착제를 도포하고 이형지(4)를 붙여 보드 사용시 이형지(4)를 벗겨내고 사용표면에 붙인다. 특히 리무버블 접착제(6)를 사용하면 면의 손상을 방지하고 다른 장소에 쉽게 이동하여 사용할 수 있는 장점이 있으며, 스프레이 타입과 테이프 타입이 있다.The base sheet PP film 5 is coated with an acrylic water-soluble adhesive or a removable adhesive, and a release paper 4 is attached to the base sheet PP film 5 to peel off the release paper 4 and adhere to the surface of use. In particular, the use of the removable adhesive (6) has the advantage of preventing damage to the surface and can be easily moved to other places, there are spray type and tape type.

이와 같이 제조된 보드는 "물로 소거되는 잉크"를 사용한 펜으로 필기가 가능하고, 표면이 무광 상태이므로 기존의 화이트보드의 유광으로 인한 눈의 피로도 및 조명의 반사를 줄일 수 있다.The board manufactured as described above can be written with a pen using “ink erased with water”, and since the surface is matte, eye fatigue and reflection of light due to the gloss of the existing whiteboard can be reduced.

또한, 시트 표면을 UV 코팅(1) 처리하여 기존의 화이트보드보다 경도가 강하여 내구성 및 긁힘이 적어 장시간 사용이 가능하다.In addition, by treating the surface of the sheet with a UV coating (1), the hardness is stronger than the existing whiteboard, and durability and scratches are less likely to be used for a long time.

그리고 기존의 화이트보드는 1회성이나 본 발명의 보드는 표면 손상시 쉽게 신제품으로 교체가 가능하며 학교 칠판, 유아용 보드, 월중 행사표 및 회의용, 유아가 사용할 수 있는 낙서용 벽지, 컴퓨터 마우스 패드 등 다양한 분야에 널리 사용이 가능하다.And the existing whiteboard is a one-time, but the board of the present invention can be easily replaced with a new product when the surface is damaged, various school boards, baby boards, monthly calendars and meetings, graffiti wallpaper for children, computer mouse pads, etc. It can be widely used in the field.

이상에서 설명한 바와 같이 본 발명에 의하면, 메모내용을 물휴지로 소거하는 것이 가능하고, 보드 표면이 무광 상태이므로 눈의 피로도 및 조명의 반사를 줄일 수 있으며, 또한, 보드 표면을 UV 코팅 처리함으로 내구성이 강하고 긁힘이 적어 장시간 사용이 가능하고, 표면 손상시 쉽게 시트의 교체가 가능하며, 리무버블(removable)접착제를 사용하여 접착함으로써 다른 장소에 쉽게 이동하여 사용할 수 있는 장점이 있다.As described above, according to the present invention, it is possible to erase the contents of the memo by water rest, and since the board surface is matte, eye fatigue and light reflection can be reduced, and the board surface is UV-coated for durability. Strong and less scratches can be used for a long time, the sheet can be easily replaced when the surface is damaged, there is an advantage that can be easily moved to another place by using a removable (removable) adhesive.

Claims

The polypropylene resin (2) is a reactive material composed of an isocyanate-reactive binder having an equivalent ratio of NCO / OH of 3: 1.5 to 1.5: 3, and is UV coated (1) using an 80 to 180 mesh roll. Heat-bonding with the material (3), forming a printing layer (4) on the back side of the polypropylene resin (5), and applying the removable adhesive (6) on the other side to attach the release paper (7). Adhesive board.

The adhesive board according to claim 1, wherein the isocyanate-reactive binder is composed of 30-80% by weight of urethane acrylate, 10-20% by weight of 1,6-hexanediol, and 5-10% by weight of phenylphosphine oxide. .