KR200271537Y1 - bead adhering to clothes and the same - Google Patents

Abstract

The present invention relates to a bead for attaching clothes, wherein the bead for attaching clothes is a mold manufacturing step for producing a silicone mold, and a bead that is mixed with 98% by weight of unsaturated polyester resin with 1% by weight of a curing agent and 1% by weight of an accelerator to produce a bead material. A material generating step, a bead material dissolving step of dissolving the bead material at 170 to 230 ° C., a bead molding step of pouring the bead material into a bead forming groove of the silicon mold to mold a predetermined bead, and removing the beads from the silicon mold. Bead-type step, Bead surface finishing step to put the beads into the surface treatment machine to clean and polish the surface; Bead vibration alignment step to align the back side corresponding to the attachment surface by vibrating to the air The adhesive member applying step of applying the hot melt powder, which is the adhesive member of the adhesive member, and the heating member is heated on the top of the bead alignment plate to which the adhesive member is applied to heat the adhesive member welding step and the heating plate to weld the adhesive member to the back of the bead flatly. After inverting, the bead is bonded to the back side is formed in the bead separation step of removing the beads from the heating plate.

Description

Bead adhering to clothes and the same}

The present invention relates to a bead for attaching clothes, and more particularly, an appropriate amount of an adhesive member is welded to the back of the bead, so that there is no fear of damaging or messing up the adhesion part when attaching the apparel, without degrading the product value of the apparel. It relates to a bead for clothing attachment that can be performed more easily.

In general, beads are beads, which refer to beautiful stones or gems that are rounded to be used as ornaments or rubble, which are widely used for personal goods and jewelry. In Esau, pearls, shells, plants, bamboo tubes, and fruits of trees belong to beads.

These beads were often used in witchcraft and religious life, and as trinkets.

Beads used as ornaments were initially made from natural materials, but later made from artificial materials such as gold, silver, and glass, as well as natural materials that are easy to process, such as the fruits, bones, and horns of trees.

Usually, a hole is drilled in the beads to be tied with strings, depending on the shape and location of the hole.

Such beads (beads) are commonly used to attach various types of decorations to fabrics woven from textile materials or to already manufactured clothes.

In order to attach these beads to the clothing by hand, one by one, the beads were applied one by one, and an adhesive member was applied to the back of the beads, and then the adhesive was fixed to the previous part of the clothing.

However, when the adhesive member is applied to the back side of the bead while holding it by hand, the amount of the adhesive member applied to the back side of the bead becomes inconsistent, and the adhesive member is excessively buried between the bead and the garment when the bead is attached to the garment. In this case, there is a problem that the adhesive part is dirty and the quality of the product is degraded.

In addition, there is a problem that the work is cumbersome when the clothing of the bead is attached to the adhesive member in the worker's hand.

The present invention is to solve the problems as described above, the appropriate amount of the adhesive member is welded to the back of the bead there is no fear of damage or messy adhesive portion when attaching the garment work does not reduce the clothing value of the garment attaching clothes An object of the present invention is to provide a bead for clothing attachment that can be more easily performed.

In order to achieve the above object, the bead for apparel attachment of the present invention in providing a bead for apparel attachment;

A mold making step of manufacturing a silicon mold having a plurality of bead forming grooves;

A bead material generation step of generating a bead material by mixing 98% by weight of an unsaturated polyester resin with 1% by weight of a curing agent and 1% by weight of an accelerator;

A bead material dissolving step of dissolving the resulting bead material at 170 to 230 ° C .;

A bead forming step of pouring the dissolved bead material into the bead forming groove of the silicon mold to mold a predetermined bead;

A bead deforming step of demolding the molded beads from the silicon mold;

Inserting the demolded beads into a surface treatment machine to cleanly wash and polish the surface;

A beads drying step of forcibly drying the washed and polished beads;

A bead vibration alignment step of pouring the dried beads into a bead alignment plate of a vibrator having an alignment groove and vibrating the back surface corresponding to the clothing attachment surface toward the air to align the beads;

An adhesive member applying step of applying an appropriate amount of the hot melt powder, which is an adhesive member, to the rear surface of the beads arranged on the bead alignment plate;

An adhesive member welding step of welding the hot melt powder, which is the adhesive member, to the back of the bead by heating the heating plate on the top surface of the bead alignment plate coated with the hot melt powder as the adhesive member;

After cooling and overturning the heating plate, there is a feature comprising a bead separation step of removing the beads from the heating plate with the adhesive member welded on the back.

Clothing attaching beads of the present invention has the same shape as the bead molding groove of the silicone mold and is characterized in that an adhesive member such as hot melt powder is welded on the back side.

1 is a flow chart schematically showing a manufacturing process of the beads according to the present invention,

Figure 2a is a perspective view showing an embodiment of a silicon mold according to the present invention,

2B is a side cross-sectional view magnifying the main portion of FIG. 2A;

Figure 3a is a perspective view showing an embodiment of the bead according to the present invention,

3B is a side cross-sectional view of FIG. 3A,

Figure 4 is a side cross-sectional view showing an embodiment of a vibrator and a heating plate according to the spring design.

* Description of the symbols for the main parts of the drawings *

10: bead 12: adhesive member

20: silicon mold 22: bead forming groove

30: vibrator 32: bead alignment plate

34: alignment groove 40: heating plate

100: mold production step 110: bead material generation step

120: bead material dissolution step 130: bead molding step

140: bead type step 150: bead surface finishing step

160: bead drying step 170: bead vibration alignment step

180: adhesive member coating step 190: adhesive member welding step

200: bead separation step

Hereinafter, the present invention in more detail by the accompanying drawings as follows.

Figure 1 is a flow chart schematically showing a manufacturing process of the beads according to the present invention, Figure 2a is a perspective view showing an embodiment of a silicon mold according to the present invention, Figure 2b is a side cross-sectional view to enlarge the main portion of Figure 2a. Figure 3a is a perspective view showing an embodiment of the bead according to the present invention, Figure 3b is a side cross-sectional view of Figure 3a, Figure 4 is a side cross-sectional view showing an embodiment of a vibrator and a heating plate according to the spring design.

First, 1% by weight of a curing agent and 1% by weight of an accelerator is added to 98% by weight of an unsaturated polyester resin, and the mixed bead material is dissolved at a high temperature of about 180 ° C.

The melted bead material is injected into the bead forming grooves 22 of the silicon mold 20 to form a predetermined bead 10.

At this time, the bead 10 is a front surface and the back of the bead attached to the clothing, that is, the back of the bead 10 is necessarily formed in a flat shape having a smooth or fine uneven groove, the front of the bead 10 exposed to the outside It is molded into a convex shape so that a three-dimensional shape can be provided.

The beads 10 demolded from the bead forming grooves 22 of the silicone mold 20 are washed cleanly and subjected to surface treatment to improve the adhesion between the rust-prevented metal surface and the paint through the surface finishing process. The liquid is subjected to a wash primer.

The bead 10, which has undergone the above process, is aligned in the bead alignment plate 32 of the vibrator 30 of the vibrator 30 so that the flat back surface attached to the garment faces upward, and then the vibrator 30 is operated to operate the bead. Hot melt powder, which is the adhesive member 12, is evenly applied to the rear surface of the bead 10 properly aligned in the alignment groove 34 of the alignment plate 32.

The hot plate 40 is placed on the upper side of the back surface of the bead 10 to which the hot melt powder is applied as the adhesive member 12, and then heated to a high temperature of 200 ° C. (± 30 ° C.) to beads the hot melt powder as the adhesive member 12. (10) Melt on the back side and firmly weld.

The hot melt powder, which is the dissolved adhesive member 12, is deposited on the back surface of the primer-treated bead 10 and also adheres to the surface of the heating plate 40, but at this time, the heating plate 40 is rapidly cooled by air cooling or water cooling means. When the adhesive member 12 is formed integrally on the back side can be obtained.

The beads 10 thus obtained can be decorated by applying heat to the back and attaching the clothing.

When explaining an embodiment of the present invention as follows.

Example

1. Mold manufacturing step 100; A silicon mold 20 (form of beads made of silicon) having a plurality of bead forming grooves 22 is manufactured.

2. Bead material generation step 110; A bead material is produced by blending 98% by weight of the unsaturated polyester resin with 1% by weight of the curing agent and 1% by weight of the accelerator.

3. Bead material dissolution step 120; The resulting bead material is dissolved at 170 to 230 ° C.

4. bead forming step 130; The melted bead material is poured into the bead forming grooves 22 of the silicon mold 20 to form a predetermined bead 10.

5. bead-type step 140; The molded beads 10 are demolded in the bead forming grooves 22 of the silicon mold 20.

6. Bead surface finishing step 150; The demolded beads 10 are put in a surface treatment machine to cleanly wash and polish the surface.

7. bead drying step 160; The washed and polished beads 10 are forcibly dried.

8. Bead vibration alignment step 170; The dried beads 10 are poured into the bead alignment plate 32 of the vibrator 30 having the alignment grooves 34 to vibrate so that the rear surface corresponding to the garment attachment surface faces upward.

9. Adhesive member applying step 180; An appropriate amount of hot melt powder, which is the adhesive member 12, is applied to the rear surface of the beads 10 aligned with the bead alignment plate 32.

10. adhesive member welding step 190; After heating the heating plate 40 on the bead alignment plate 32 coated with the hot melt powder 32 as the adhesive member 12, the hot melt powder as the adhesive member 12 is flatly deposited on the back surface of the bead 10, and then again. Apply heat to reconfirm and correct so that the back of the bead 10 is a flat surface.

11. Bead separation step 200; The heating plate 40 is cooled and flipped over. At this time, the bead 10 to which the hot melt powder, which is the adhesive member 12, is deposited, is completely attached to the surface of the heating plate 40, and the bead 10 is a conventional paint removal knife. When scraped off the surface of the heating plate 40 using the adhesive member 12 is provided on the back to provide a predetermined bead 10.

The present invention has the effect that the adhesive member is welded on the back of the bead so that the adhesive part may not be damaged or dirty when the clothing is attached, so that the clothing attaching operation can be performed more easily without degrading the product value of the clothing. have.

Claims (1)

Beads for clothing attachment, characterized in that one side of the flat hemispherical bead (10) is formed to form a heat-adhesive adhesive member 12 on a flat surface.