KR20020080632A

KR20020080632A - Antibacterial Coloring Method of Sand & Gravel

Info

Publication number: KR20020080632A
Application number: KR1020010020312A
Authority: KR
Inventors: 황정호
Original assignee: 황정호
Priority date: 2001-04-16
Filing date: 2001-04-16
Publication date: 2002-10-26

Abstract

PURPOSE: Provided is a process for coloring sand and gravel with an antimicrobial paint having strong antimicrobial function, deodorizing function, antistatic function, and far infrared ray emitting function. CONSTITUTION: The process is performed by preparing the antimicrobial epoxy paint and coating the sand and gravel with the antimicrobial epoxy paint, wherein the antimicrobial epoxy paint is produced by mixing a conventional epoxy paint with 1-5% of silica, alumina, zeolite powder, or a mixture thereof having an average particle diameter of less then 3micron and containing 0.1-5% of Ag ion, Cu ion, Zn ion, Ti ion, or a mixture thereof.

Description

Antibacterial Coloring Method of Sand ＆ Gravel}

종래에 수족관, 어항, 관상용 화분에 사용하는 모래나 조약돌에 미려한 외관의 구성ㆍ유지를 위하여 에폭시 페인트 등 합성수지 도료 착색제를 도포하여 사용하였으나 통상의 에폭시 페인트 등 합성수지 도료 착색제는 착색제 차체로서는 형성된 도막(塗膜)의 내수성, 내약품성, 내마모성, 색상 등이 우수하다는 장점을 갖고 있으나 물 속이나 온ㆍ습도 변화가 많은 기후조건에서 외기에 노출되었을 때에는 에폭시 등 합성수지 도막의 내ㆍ외부에 박테리아 및 곰팡이 등이 부착ㆍ번식함으로 인하여, 단 기간 내에 수조 또는 어항의 물이 부패하거나 흐려지고, 관상용 화분의 경우 물 때 및 이끼가 끼어서 악취가 발생하고 외관 상태도 불량하게 되어 관상용으로서의 가치를 상실하는 문제점을 갖고 있다.In the past, synthetic resin paints such as epoxy paints were used by applying sand or pebbles to the sand, pebbles used in aquariums, fish tanks, ornamental pots, and synthetic resin paints such as epoxy paints. Iii) It has the advantages of excellent water resistance, chemical resistance, abrasion resistance, color, etc., but when exposed to outdoor air under water or climatic conditions with a lot of temperature and humidity changes, bacteria and mold inside and outside of synthetic resin coating film such as epoxy Due to attachment and propagation, water in the tank or fish tank becomes decayed or blurred within a short period of time, and in the case of ornamental flower pots, water and moss get caught, odors occur and appearance is poor, resulting in the loss of ornamental value. .

본 발명은 위에서 설명한 문제점을 해결하기 위하여, 원적외선방사 목적으로 실리카, 대전방지 목적으로 알루미나, 항균ㆍ가스분해목적으로 은이온, 동이온, 아연이온, 티탄이온 등 금속이온, 가스흡착ㆍ제습목적으로 제오라이트 등 각소재로 이루어 지며, 강력한 항균기능과 탈취기능,ㆍ정전기제거기능, 원적외선 방출기능을동시에 그리고 반영구적으로 발휘하는 미크론단위의 분말상태의 무기(無機)항균제를 종래의 에폭시 페인트 등 합성수지 도료에 첨가하여 항균성 합성수지 도료 착색제를 제조하고 이를 모래 및 조약돌에 도포하여 사용함으로서 미려한 외관의 구성ㆍ유지라는 사용목적에 최적인 상태를 통상의 에폭시 페인트 등 합성수지 도료를 도포한 모래 및 조약돌을 사용한 경우에 비해 월등하게 장기간 유지시켜주는 방법을 제공한다.The present invention is to solve the problems described above, silica for far-infrared radiation, alumina for antistatic purposes, silver ions, copper ions, zinc ions, titanium ions, such as titanium ions for antibacterial and gas decomposition purposes, gas adsorption and dehumidification purposes It is composed of various materials such as zeolite, and it is a micron powder inorganic antimicrobial agent that exhibits strong antibacterial function, deodorization function, electrostatic removal function, and far infrared emission function simultaneously and semi-permanently. By adding an antimicrobial synthetic resin paint colorant and applying it to sand and pebble, it is optimal to be used for the purpose of construction and maintenance of beautiful appearance compared to the case of using sand and pebble coated with synthetic resin paint such as epoxy paint. It provides a way to maintain superior long-term maintenance.

지금까지 수조, 어항 및 관상용 화분에 사용하는 모래 및 조약돌에 미려한 외관을 구성ㆍ유지하기 위하여 모래 및 조약돌 위에 통상의 에폭시 페인트 등 합성수지 도료 착색제를 도포하여 사용하여왔다. 그러나 통상의 에폭시 페인트 등 합성수지 도료 착색제를 도포한 모래 및 조약돌이 물 속이나 온ㆍ습도 변화가 많은 기후조건에서 외기에 노출되었을 때에는 에폭시 등 도막의 내ㆍ외부에 박테리아 및 곰팡이 등이 부착ㆍ번식함으로 인하여, 단 기간 내에 수조 또는 어항의 물이 부패하거나 흐려지고, 관상용 화분의 경우 물 때 및 이끼가 끼어서 악취가 발생하고 외관 상태도 불량하게 되어 관상용으로서의 가치를 상실하는 문제점을 갖고 있다. 이를 개선하기 위한 방법으로 형성된 에폭시 등 합성수지 도막 내외부에 박테리아나 곰팡이가 부착ㆍ번식하는 것을 방지하기 위하여, 모래 및 조약돌 위에 통상의 에폭시 페인트 등 합성수지 도료 착색제를 도포하고나서 건조후 형성된 에폭시 등 합성수지 도막위에 세균억제 또는 멸균의 목적으로 유기소독제제를 추가로 분무하여 도포하거나, 통상의 에폭시 페인트 등 합성수지 도료 착색제에 신너와 함께 유기 소독제를 첨가하여 도포하는 등의 방법을 사용하였으나, 유기 소독제 자체의 불쾌한냄새와 강한 독성 때문에 사용상 제약이 많았고 사용자체를 기피하는 경향이 많았다. 또한 종래의 유기 소독제는 화학물질 자체의 화학반응을 이용한 것으로서, 일반적으로 유기 화학물질은 수일 또는 수주 내에 자외선 및 산소 등의 산화작용에 의해 분해되어 버리고 마는 특성이 있기 때문에, 효과가 짧은 시간 밖에 지속되지 못하므로 도막의 내외부에 세균이나 곰팡이가 번식하는 것을 방지할 수 없었고 결과적으로 수조, 어항 및 관상용 화분의 미려한 외관의 구성ㆍ유지하기 위해 사용한 착색된 모래 및 조약돌의 사용목적을 달성할 수 없었다.Until now, in order to construct and maintain a beautiful appearance in sand and pebbles used in tanks, fish tanks and ornamental pots, synthetic resin paint colorants such as ordinary epoxy paints have been applied to sand and pebbles. However, when sand and pebble coated with a synthetic resin paint colorant such as ordinary epoxy paint are exposed to the air in water or in climatic conditions with a great change in temperature and humidity, bacteria and molds adhere to and grow inside and outside the epoxy film. Due to this, the water in the tank or fish tank is decayed or blurred within a short period of time, and in the case of the ornamental potted plants, there is a problem in that the smell and moss caused by the bite and moss are caught and the appearance is also poor, thereby losing the value for ornamental use. In order to prevent bacteria and mold from adhering and propagating on the inside and outside of the synthetic resin coating film formed by the method for improving this, a synthetic resin paint colorant such as ordinary epoxy paint is applied on sand and pebble, and then dried on the synthetic resin film such as epoxy formed after drying. For disinfection or sterilization purposes, an organic disinfectant was applied by spraying additionally, or an organic disinfectant was added to the synthetic resin paint colorant such as an ordinary epoxy paint with a thinner. However, an unpleasant smell of the organic disinfectant itself was used. Due to the strong toxicity and strong usage, there was a tendency to avoid users. In addition, conventional organic disinfectants use chemical reactions of chemicals themselves. Generally, organic chemicals are decomposed by oxidation such as ultraviolet rays and oxygen within a few days or weeks. As a result, it was not possible to prevent the growth of bacteria and mold inside and outside the coating film, and as a result, the purpose of using the colored sand and pebbles used to construct and maintain the beautiful appearance of the tank, the fish tank, and the ornamental flower pot was not achieved.

본 발명은 에폭시 페인트 등 합성수지 도료 착색제의 원료성분으로 무독ㆍ무해하며 그 효과가 반영구적으로 발현되는 무기 항균제를 첨가하여 항균성 합성수지 도료 착색제를 제조하고 이를 모래 및 조약돌 위에 도포하여 수조, 어항 및 관상용 화분에 사용함으로서, 종래의 에폭시 페인트 등 합성수지 도료 착색제의 장점은 조금도 손상시키지 않고 그대로 유지하면서도 세균이나 곰팡이 등이 에폭시 등 합성수지 도막 내 외부에 부착ㆍ번식하지 못하도록 하여 미려한 외관의 구성ㆍ유지라는 본래의 사용목적에 최적인 상태를 통상의 종래의 에폭시 페인트 등 합성수지 도료 착색제를 도포한 경우보다 월등하게 장기간 유지시켜주는 방법을 제공한다.The present invention is a non-toxic and harmless as a raw material of synthetic resin paint colorants such as epoxy paint, and the addition of inorganic antimicrobial agent that the effect is semi-permanent to produce an antimicrobial synthetic resin paint colorant and apply it on sand and pebble to water tanks, fish tanks and ornamental pots By using it, the advantages of synthetic resin colorants such as epoxy paints are maintained without any damage, while preventing bacteria and molds from adhering and propagating inside and outside of synthetic resin coatings such as epoxy. The present invention provides a method of maintaining the optimum state for a long time superior to the case of applying a synthetic resin colorant such as a conventional conventional epoxy paint.

본 발명은 위에서 설명한 기술적 과제를 달성하기 위하여, 원적외선방사 목적으로 실리카, 대전방지 목적으로 알루미나, 항균ㆍ가스분해목적으로 은이온, 동이온, 아연이온, 티탄이온 등 금속이온, 가스흡착ㆍ제습목적으로 제오라이트 등 각소재로 이루어 지며, 강력한 항균기능과 탈취기능ㆍ정전기제거기능, 원적외선 방출기능을 동시에 그리고 반영구적으로 발휘하는 미크론단위의 분말상태의 무기(無幾)항균제를 종래의 에폭시 페인트 등 합성수지 도료 착색제에 첨가하여 항균성 에폭시 페인트 등 합성수지 도료 착색제를 제조하여 이를 모래 및 조약돌에 도포하여 사용함으로서 본래의 미려한 외관의 구성ㆍ유지라는 사용목적에 최적인 상태를 종래의 에폭시페인트 등 합성수지 도료 착색제에 비해 월등하게 장기간 유지시켜주는 방법을 제공한다.The present invention, in order to achieve the above technical problem, silica for far-infrared radiation purposes, alumina for antistatic purposes, silver ions, copper ions, zinc ions, titanium ions, such as titanium ions for antibacterial and gas decomposition purposes, gas adsorption, dehumidification purposes It is composed of various materials such as zeolite, and it is a micron powder inorganic antimicrobial agent that exhibits strong antibacterial function, deodorizing function, electrostatic removal function, and far infrared emission function simultaneously and semi-permanently. It is added to the synthetic resin paint colorants such as antibacterial epoxy paints and applied to sand and pebble, which is used for the purpose of constructing and maintaining the original beautiful appearance, which is superior to that of conventional resin paints such as epoxy paint. Providing a way to keep it for a long time .

즉, 조성중에 Ag이온, Cu이온, Zn이온, Ti이온 중 어느 한가지나 그것들의 혼합물을 0.1∼5%씩 각각 포함한 입자의 평균직경이 3미크론 이하인 실리카, 알루미나, 제오라이트의 분말중 어느 한가지나 또는 그것들의 혼합물로 이루어진 무독ㆍ무해하며 강력한 항균력을 갖고 있는 무기 항균제를 에폭시 페인트 등 합성수지 도료 착색제 고형분의 0.5∼5% 정도가 되도록 원료의 일부로 첨가하여 항균성 합성수지 도료 착색제를 제조한다.That is, any one of Ag, Cu, Zn and Ti ions in the composition, or any one of powders of silica, alumina and zeolite having an average diameter of 3 microns or less, each containing 0.1 to 5% of a mixture thereof, or A non-toxic, harmless and strong antimicrobial agent composed of a mixture thereof is added as a part of the raw material so as to be 0.5 to 5% of the solid content of the synthetic resin colorant such as epoxy paint to prepare an antimicrobial synthetic resin colorant.

본 발명의 항균성 에폭시 페인트를 물체의 표면에 도포하여 도막이 형성되면, 도막의 표면에 무수히 산포하고 있는 금속이온들을 흡착하고 있는 미크론 단위의 다공성 입자들이 도막의 표면에 접촉하는 세균, 곰팡이포자, 냄새성분을 흡착하며, 막속에 포함된 금속이온의 촉매작용에 의하여 접촉하는 공기중 또는 수중의 산소 일부를 활성화시키므로서(발생기산소 생성) 강력한 산화제로 작용하여 세균, 곰팡이, 냄새성분을 산화ㆍ분해시켜 제거하기 때문에 단 한 번의 항균성 에폭시 페인트의 도포에 의해 무기항균제가 포함된 항균성 도막이 형성되기만 하면, 항균성 도막이 세균이나 곰팡이포자 등을 흡착-분해, 흡착-분해하는 과정을 반복하므로서 항균ㆍ항곰팡이 효과가 반영구적으로 장기간 효과가 지속되고, 따라서 도막의 내구성도 반 영구적으로 장기간 지속되며 이와 동시에 습기제거, 정전기 제거, 원적외선 방출 등 다양한 기능을 발휘하기 때문에 건축물ㆍ구조물의 보호와 미려한 외관의 유지는 물론 환경정화, 위생관리에도 탁월한 효능을 갖는다.When the antimicrobial epoxy paint of the present invention is applied to the surface of an object to form a coating, bacteria, mold spores, and odor components in which micron-sized porous particles adsorbing metal ions scattered on the surface of the coating film contact the surface of the coating film. It acts as a powerful oxidant by activating a part of oxygen in the air or water that comes into contact by the catalytic action of metal ions contained in the membrane (generating oxygen generated by oxygen) to oxidize and decompose bacteria, mold, and odor components. Therefore, if the antimicrobial coating film containing inorganic antimicrobial agent is formed by applying only one antimicrobial epoxy paint, the antimicrobial coating film absorbs, decomposes and adsorbs and decomposes bacteria and mold spores. Effect lasts for a long time, so the durability of coating As it lasts for a long time and at the same time, it has various functions such as moisture removal, static electricity removal and far-infrared emission, so it is excellent in protecting buildings and structures, maintaining beautiful appearance, environmental cleanliness and hygiene management.

다음은 본발명의 방법에 의한 실시예를 설명한다.The following describes an embodiment by the method of the present invention.

호모믹서가 설치되어 있는 혼합조에 증류수 30부를 가하고, 200 알피엠(RPM)의 회전수로 교반하면서 입자크기가 최대 3미크론 이하인 알루미나 분말 50부를 서서히 가하여 균일한 혼합액으로 분산시킨다음, 교반기의 회전수를 3000 알피엠(RPM)으로 바꾸어 2시간 교반하여 충분히 분산시킨다.30 parts of distilled water was added to a mixing tank equipped with a homomixer, and 50 parts of alumina powder having a particle size of 3 microns or less was gradually added while stirring at a rotational speed of 200 Alp (RPM), and then dispersed in a uniform mixture. Change to 3000 Alp (RPM) and stir for 2 hours to fully disperse.

교반기의 회전수를 200 알피엠(RPM) 으로 낮춘후, 별도로 준비한 질산은 수용액 1부(은성분 기준), 질산동 수용액 0.5부(동성분 기준), 질산아연 수용액 0.5%(아연성분 기준), 산화티탄 수분산액 0.2부(티탄성분 기준)를 차례로 가하여 10시간이상 방치한다.After lowering the rotation speed of the stirrer to 200 AlpM (RPM), 1 part of silver nitrate aqueous solution prepared separately (based on silver component), 0.5 part of copper nitrate aqueous solution (based on copper component), 0.5% of zinc nitrate aqueous solution (based on zinc component), titanium oxide 0.2 parts of an aqueous dispersion (based on titanium) are added sequentially and left to stand for at least 10 hours.

상기 혼합액으로부터 고형분을 분리하여 105℃ 건조기에서 충분히 건조후 분쇄기에 넣어 원래의 제오라이트 입자분포에 도달하기까지 분쇄하여 미세 분말상태의 은이온 1%, 동이온 0.5%, 아연이온 0.5%, 티탄이온 0.2%를 포함하며 입자크기가 최대 3미크론 이하인 항균성 알루미나 분말을 만들었다.The solid is separated from the mixed solution, dried sufficiently in a 105 ° C. dryer, and then put into a grinder and pulverized until reaching the original zeolite particle distribution. 1% of silver ions in a fine powder state, 0.5% of copper ions, 0.5% of zinc ions, and 0.2 of titanium ions. The antimicrobial alumina powder containing% and having a particle size of up to 3 microns was made.

동일한 요령으로 은이온 1%, 동이온 0.5%, 아연이온 0.5%, 티탄이온 0.2%를포함하며 입자크기가 최대 3미크론 이하인 항균성 실리카 분말을 만들었다.In the same manner, an antimicrobial silica powder containing 1% silver ions, 0.5% copper ions, 0.5% zinc ions, 0.2% titanium ions and having a particle size of up to 3 microns was made.

역시 동일한 요령으로 은이온 1%, 동이온 0.5%, 아연이온 0.5%, 티탄이온 0.2%를 포함하며 입자크기가 최대 3미크론 이하인 항균성 제오라이트 분말을 만들었다.In the same manner, an antimicrobial zeolite powder containing 1% silver ions, 0.5% copper ions, 0.5% zinc ions, and 0.2% titanium ions and having a particle size of up to 3 microns was made.

항균성 알루미나 분말30부, 항균성 실리카분말 30부, 항균성 제오라이트 분말 40부를 골고루섞어 무기항균제를 만들었다.Inorganic antimicrobial agents were prepared by mixing 30 parts of antimicrobial alumina powder, 30 parts of antimicrobial silica powder, and 40 parts of antimicrobial zeolite powder.

통상의 에폭시 페인트의 주제 제조시에 고형분의 2%에 해당하는 상기 무기 항균제를 첨가하여 항균성 에폭시 페인트 주제를 만들었다. 여기에 통상의 경화제와 신너를 적절히 배합하여 10CM X 10 CM 의 철판에 도포하고, 120℃ 건조기에서 30분간 방치하여 시험편을 만들었다.In the preparation of the subject of a conventional epoxy paint, the inorganic antimicrobial agent corresponding to 2% of solids was added to make an antimicrobial epoxy paint subject. The usual hardening | curing agent and thinner were mix | blended suitably here, it apply | coated to the iron plate of 10CMX10CM, and it left to stand in a 120 degreeC dryer for 30 minutes, and created the test piece.

표에서 즉시 알수 있는바와 같이 본 발명의 항균성 에폭시 페인트는 항균기능, 탈취기능, 정전기 제거기능, 원적외선 방출기능이 탁월한 것으로 나타났다.As can be seen immediately from the table, the antimicrobial epoxy paint of the present invention was shown to be excellent in antibacterial function, deodorizing function, static elimination function, far infrared ray emitting function.

Claims

That is, any one of Ag, Cu, Zn and Ti ions in the composition, or any one of powders of silica, alumina and zeolite having an average diameter of 3 microns or less, each containing 0.1 to 5% of a mixture thereof, or A method of preparing a synthetic resin paint colorant, such as an antimicrobial epoxy paint, comprising 1 to 5% of a mixture thereof mixed with a synthetic resin paint such as an ordinary epoxy paint and coloring sand and pebble using the same.