KR20010039410A - Waterproofing sheet using the asphalt and composite waterproofing method using the same - Google Patents

Waterproofing sheet using the asphalt and composite waterproofing method using the same Download PDF

Info

Publication number
KR20010039410A
KR20010039410A KR1019990047789A KR19990047789A KR20010039410A KR 20010039410 A KR20010039410 A KR 20010039410A KR 1019990047789 A KR1019990047789 A KR 1019990047789A KR 19990047789 A KR19990047789 A KR 19990047789A KR 20010039410 A KR20010039410 A KR 20010039410A
Authority
KR
South Korea
Prior art keywords
asphalt
layer
waterproofing
waterproof
coating
Prior art date
Application number
KR1019990047789A
Other languages
Korean (ko)
Other versions
KR100334602B1 (en
Inventor
김충엽
김기태
Original Assignee
김충엽
김기태
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 김충엽, 김기태 filed Critical 김충엽
Priority to KR1019990047789A priority Critical patent/KR100334602B1/en
Publication of KR20010039410A publication Critical patent/KR20010039410A/en
Application granted granted Critical
Publication of KR100334602B1 publication Critical patent/KR100334602B1/en

Abstract

PURPOSE: An asphalt waterproof sheet is provided which has an excellent durability and waterproof property. And a method of complex waterproof construction using thereof is also provided. CONSTITUTION: The asphalt waterproof sheet comprises: (i) a high weight non-woven fabric(22) having a unit weight of 120 gram/square meter; (ii) an upper part asphalt layer(25) which is formed on the upper side of the high weight non-woven fabric; (iii) a lower part asphalt layer(24) which is formed on the lower side of the high weight non-woven fabric; (iv) a low weight non-woven fabric(23) which is adhered to the upper part of the upper part asphalt layer and has a unit weight of 40-60 gram/square meter; and (v) a covering material(26) which is adhered to the lower part of the lower part asphalt layer. The method comprises steps of: (i) cleaning part of a structure to be waterproofed; (ii) forming a primer layer on the structure; (iii) adhering the consecutively connected asphalt water proof sheets to the primer; (iv) coating the asphalt water proof sheet with a waterproof materials of coating film(30); and (v) hardening the waterproof layer of coating film.

Description

아스팔트 방수시트 및 이를 이용한 복합방수공법{Waterproofing sheet using the asphalt and composite waterproofing method using the same}Waterproofing sheet using the asphalt and composite waterproofing method using the same}

본 발명은 아스팔트 방수시트 및 이를 이용한 복합방수공법에 관한 것이다. 더욱 구체적으로 본 발명은 시트방수와 도막방수의 장점을 결합하여 내구성능과 방수성능이 우수한 아스팔트 방수시트 및 이를 이용한 복합방수공법에 관한 것이다.The present invention relates to an asphalt waterproof sheet and a composite waterproof method using the same. More specifically, the present invention relates to an asphalt waterproof sheet having excellent durability and waterproof performance by combining the advantages of sheet waterproofing and waterproofing of a coating and a composite waterproofing method using the same.

건축 구조물에는 우수 및 지하수의 유입을 막아 구조체의 균열이나 내구성의 저하를 막기 위하여 필수적으로 방수작업이 요구된다.In order to prevent rainwater and groundwater from entering the building structure, watertight work is required to prevent cracking or deterioration of the structure.

방수공법에는 여러 가지 공법이 사용되고 있으나 주로 아스팔트 방수, 시멘트 액체방수, 시트방수 및 도막방수 등이 쓰인다.Various methods are used in the waterproofing method, but mainly waterproofing asphalt, cement liquid, sheet waterproofing and coating waterproofing.

아스팔트 방수는 가장 많이 사용하는 방수공법으로 고무 또는 수지를 혼합하여 신축성을 가진 아스팔트 펠트, 아스팔트 콤파운드 및 아스팔트 루핑 등의 용융아스팔트를 방수부위에 여러 겹 바르는 방법이다. 상기 아스팔트 방수는 그 자체의 신축성으로 구조체의 균열 등에 시멘트 액체방수보다는 잘 대응할 수 있지만 방수층 자체가 구조체와 밀착되어 국부적인 균열 등에 대응하지 못하고 갈라지는 문제점을 안고 있다.Asphalt waterproofing is the most widely used waterproofing method. It is a method of applying multiple layers of melted asphalt such as elastic asphalt felt, asphalt compound and asphalt roofing by mixing rubber or resin to the waterproofing part. Asphalt waterproofing can cope better with cement liquid waterproofing due to its own elasticity, but the waterproofing layer itself is in close contact with the structure and does not cope with local cracking.

시멘트 액체방수는 방수제를 첨가한 모르터를 상기 아스팔트 방수와 같이 방수부위에 바르는 방법으로 값이 싸고 시공이 간편하지만, 방수층에 균열이 생기기 쉽고 자주 보수작업을 해야하는 단점이 있다.Cement liquid waterproofing is inexpensive and easy to construct by applying a mortar with a waterproofing agent to a waterproofing portion such as asphalt waterproofing, but it is prone to cracking in the waterproofing layer and frequent maintenance work.

상술한 바와 같이 방수층이 갈라지는 문제점을 해결하기 위하여 오늘날 사용이 점차 증가하는 방수방법은 시트방수이다.As mentioned above, in order to solve the problem of cracking of the waterproofing layer, a waterproofing method that is increasingly used today is sheet waterproofing.

시트방수는 신축성이 우수한 합성고무나 합성수지 또는 고무화 아스팔트 등을 주원료로 하여 일정규격의 방수시트를 만든 것으로써, 주로 사용되는 아스팔트 시트방수를 예를 들어 설명하면 다음과 같다. 미리 공장제작된 일정크기의 아스팔트 방수시트(1)를 도1과 같이 일차적으로 표면에 프라이머 처리를 한 구조체와 상기 아스팔트 방수시트(1) 사이에 틈이 벌어지지 않도록 부착하고 상기 아스팔트 방수시트(1)와 아스팔트 방수시트(1)의 이음부를 겹친다. 이어서 상기 이음부를 토오치 램프 등을 사용하여 용융시켜 부착하여 물이 침투하지 않도록 한다. 상기 아스팔트 시트방수(1)는 시공이 간편하고 공기가 절감되는 장점이 있으나, 특히 이음부를 토오치 램프로 가열하여 용융시켜 부착시키기 때문에 과열되어 구멍이 뚫리거나, 미처 토오치 램프로 제대로 가열되지 않은 부분은 용융되지 않아 이음부가 균일하게 부착되지 않는 경우가 빈번히 발생되어 물이 스며드는 누수의 원인이 된다.Sheet waterproofing is made of synthetic rubber, synthetic resin or rubberized asphalt with excellent elasticity as a main raw material to make a waterproof sheet of a certain standard, the following describes the asphalt sheet waterproofing mainly used as an example. The asphalt waterproof sheet 1 of factory size is prepared in advance so as to prevent a gap between the asphalt treated sheet and the asphalt waterproof sheet 1 having a primary surface treated as shown in FIG. 1 and the asphalt waterproof sheet 1 ) And the joint of the asphalt waterproof sheet (1) overlap. The joint is then melted and attached using a torch lamp or the like to prevent water from penetrating. The asphalt sheet waterproof (1) has the advantage that the construction is easy and the air is reduced, but in particular because the joint is heated by melting with a torch lamp to attach it, the hole is overheated or not properly heated by the torch lamp The parts are not melted and the joints are not evenly attached frequently, which causes water leakage.

상기 아스팔트 방수시트(1)는 부직포(2)를 용융아스팔트에 통과시키기 위해 롤러 등을 이용하여 당겨서 상기 부직포(2)의 상·하부에 아스팔트 층(3)을 형성한 것으로써, 롤러 등을 이용하여 당길 때 상기 부직포(2)가 끊어지지 않도록 주로 단위중량 180g/㎡의 부직포(2)를 사용한다. 이어서 상부 및 하부에 폴리에틸렌 필름 또는 잔모래 등의 피복재(4)를 부착한다. 상기 피복재(4)는 폴리에틸렌 필름, 잔모래 및 탈부착이 가능한 이형지 등을 주로 사용하며, 구조체와 동일한 분포로 점접착되어 구조체에 발생되는 균열에 대해 신축성을 가지고 대응할 수 있다. 만약 상기 피복재(4)가 상기 아스팔트 방수시트(1)에 부착되어 있지 않으면 고온에서 아스팔트층(3)이 녹게 되어 구조체와 점접착이 되지 못하고 상술한 아스팔트 방수와 같이 구조체에 상기 아스팔트층(3)의 전면이 부착되어 구조체에 발생하는 균열에 대응하기 어렵다.The asphalt waterproof sheet 1 is formed by using a roller or the like to pass the nonwoven fabric 2 to the molten asphalt so as to form an asphalt layer 3 on the upper and lower portions of the nonwoven fabric 2, using a roller or the like. The nonwoven fabric 2 of unit weight 180g / m <2> is mainly used so that the said nonwoven fabric 2 may not be cut when it pulls. Subsequently, a covering 4 such as polyethylene film or fine sand is attached to the upper and lower portions. The coating material 4 mainly uses a polyethylene film, fine sand, and a release paper that can be attached and detached. The coating material 4 may be elastically coped with cracks generated in the structure by being adhesively bonded in the same distribution as the structure. If the coating material 4 is not attached to the asphalt waterproof sheet 1, the asphalt layer 3 is melted at a high temperature, and thus the adhesive layer is not adhered to the structure. It is difficult to cope with cracks occurring in the structure due to the front surface of.

도막방수는 폴리우레탄 또는 아크릴 고무를 주원료로 하는 액상의 도막방수재를 사용하여 일차적으로 표면에 프라이머 처리를 한 구조체에 상기 액상의 도막방수재를 여러 겹 도포하여 피막을 형성하는 것으로써, 이음새 없는 방수층을 형성할 수 있다. 그러나 상기 액상의 도막방수재를 여러 겹 차례로 도포할 때, 한 겹당 각기 약 24시간 이상의 경화 시간을 요구하므로 시공시간이 길어지며, 상기 구조체 자체가 지니는 함수률이 높게 되면 상기 구조체에 함유되어 있는 물이 증발됨에 따라 기포가 발생하여 도막방수층에 굴곡이 생겨 울퉁불퉁해지거나 상기 도막방수층 자체가 상기 구조체로부터 이탈되어 들뜨는 단점이 있다.Coating waterproof is to form a film by applying several layers of liquid coating waterproofing material to the structure that is primarily primer-treated on the surface using a liquid coating waterproofing material mainly made of polyurethane or acrylic rubber. Can be formed. However, when the liquid coating waterproofing material is applied in several layers, the construction time is long because the curing time requires about 24 hours or more per layer, and the water contained in the structure becomes high when the moisture content of the structure itself is high. As the evaporation occurs, bubbles are generated and the curvature of the coating waterproof layer becomes lumpy, or the coating waterproof layer itself is lifted off from the structure.

최근에는 아스팔트 시트방수와 도막방수의 단점을 보완하고 장점을 결합한 복합방수공법이 등장하고 있다.Recently, a composite waterproofing method combining the advantages and combining the advantages of asphalt sheet waterproofing and waterproofing has been introduced.

상기 복합방수공법은 개념상 간단히 설명하면 도2와 같이 다수개의 아스팔트 방수시트(11)를 방수부위에 부착하고 상기 부착한 아스팔트 방수시트(11) 위에 액상의 도막방수재(15)를 도포한 것이다. 그러나 복합방수공법에서 종래의 아스팔트 방수시트(1)를 그대로 사용하게 되면 아스팔트층(3)과 액상의 도막방수재(15)가 각기 재료적 특성으로 인하여 서로 부착되지 않고 들뜨게 되는 문제점이 있다. 이와 같은 문제점을 해결하기 위하여 상기 아스팔트 방수시트(1)를 개량하여 부직포(12)를 제일 상부에 형성함으로써 아스팔트층(13)과 도막방수층 사이의 매개체 역할을 하여 상기 아스팔트층(13)과 도막방수층의 결합을 단단히 해주는 아스팔트 방수시트(11)가 최근 등장하였으나 흡수율이 높은 단위중량 180g/㎡의 부직포(12)를 사용하므로 액상의 도막방수재(15)를 도포할 때, 상기 부직포(12)로 상기 액상의 도막방수재(15)가 다량 흡수된다. 그러므로 원하는 도막방수층을 형성하기 위해서는 3겹 이상 액상의 도막방수재(15)를 도포해야 하므로 긴 경화시간이 요구되어 종래의 도막방수와 마찬가지로 시공시간이 길어진다.In the composite waterproof method, the concept is briefly described, and a plurality of asphalt waterproof sheets 11 are attached to a waterproof portion as shown in FIG. 2, and a liquid film waterproofing material 15 is coated on the attached asphalt waterproof sheet 11. However, when the conventional asphalt waterproof sheet 1 is used as it is in the composite waterproofing method, there is a problem that the asphalt layer 3 and the liquid film waterproofing material 15 are lifted without being attached to each other due to their material properties. In order to solve the above problems, the asphalt waterproof sheet 1 is improved to form the nonwoven fabric 12 at the top, thereby acting as a medium between the asphalt layer 13 and the coating waterproof layer, thereby providing the asphalt layer 13 and the coating waterproof layer. Asphalt waterproof sheet 11 for firmly bonding of the recently appeared, but the non-woven fabric 12 having a high absorption rate unit weight 180g / ㎡ is used when applying the liquid film waterproofing material 15, the nonwoven fabric 12 to the A large amount of liquid film waterproofing material 15 is absorbed. Therefore, in order to form a desired coating waterproof layer, three or more layers of liquid coating waterproofing material 15 must be applied, so that a long curing time is required, and thus the construction time is long as in conventional coating film waterproofing.

본 발명의 목적은 구조체의 균열에 보다 효과적으로 대응할 수 있는 아스팔트 방수시트 및 이를 이용한 복합방수공법을 제공하는 것이다.An object of the present invention is to provide an asphalt waterproof sheet and a composite waterproof method using the same that can more effectively respond to the crack of the structure.

본 발명의 다른 목적은 종래의 아스팔트 시트방수의 이음부에서 발생하던 누수를 방지할 수 있는 아스팔트 방수시트 및 이를 이용한 복합방수공법을 제공하는 것이다.Another object of the present invention is to provide an asphalt waterproof sheet and a composite waterproof method using the same, which can prevent the leakage occurring in the joint portion of the conventional asphalt sheet waterproof.

본 발명의 또 다른 목적은 아스팔트 시트방수와 도막방수의 장점을 결합하여 시공시간이 짧고 내구성능과 방수성능이 우수한 아스팔트 방수시트 및 이를 이용한 복합방수공법을 제공하는 것이다.Still another object of the present invention is to provide an asphalt waterproof sheet having a short construction time and excellent durability and waterproof performance by combining the advantages of waterproofing and waterproofing the asphalt sheet and a composite waterproof method using the same.

본 발명의 또 다른 목적은 여러 겹으로 도막방수층을 형성하지 않고 한 겹만 상기 도막방수층을 형성하여 불필요한 도막방수층 피복공정 및 도막방수층 시공비용을 줄일 수 있는 아스팔트 방수시트 및 이를 이용한 복합방수공법을 제공하는 것이다.Still another object of the present invention is to provide an asphalt waterproof sheet and a composite waterproof method using the same, which can reduce unnecessary coating layer waterproofing process and coating layer waterproofing cost by forming the layer of waterproof layer without forming a layer of waterproof layer in multiple layers. will be.

도1은 종래의 아스팔트 방수시트의 설치 단면도 및 확대 단면도이다.1 is an installation cross-sectional view and an enlarged cross-sectional view of a conventional asphalt waterproof sheet.

도2는 종래의 복합방수공법의 아스팔트 방수시트의 설치 단면도 및 확대 단면도이다.Figure 2 is an installation cross-sectional view and enlarged cross-sectional view of the conventional asphalt waterproof sheet of the composite waterproof method.

도3은 본 발명의 아스팔트 방수시트의 설치 단면도 및 확대 단면도이다.3 is an installation cross-sectional view and an enlarged cross-sectional view of the asphalt waterproof sheet of the present invention.

도4는 도3에 이음부 결합재를 더 형성한 설치 단면도이다.4 is an installation sectional view in which a joint bonding material is further formed in FIG.

＜도면의 부호에 대한 간단한 설명＞<Brief description of the symbols in the drawings>

1, 11, 21: 아스팔트 방수시트 2, 12: 부직포1, 11, 21: asphalt waterproof sheet 2, 12: nonwoven fabric

3, 13: 아스팔트 층 4, 14, 26: 피복재3, 13: asphalt layer 4, 14, 26: cladding

15, 30: 도막방수재 22: 고중량 부직포15, 30: film waterproofing material 22: heavy weight nonwoven fabric

23: 저중량 부직포 24: 하부 아스팔트층23: low weight nonwoven fabric 24: lower asphalt layer

25: 상부 아스팔트층 31: 이음부 결합재25: upper asphalt layer 31: joint binder

도면에 따라 본 발명을 설명한다.The present invention will be described with reference to the drawings.

도3은 본 발명의 아스팔트 방수시트의 단면 사시도로써, 본 발명의 아스팔트 시트(21)는 고중량 부직포(22), 상부 아스팔트 층(25), 하부 아스팔트 층(24), 저중량 부직포(23) 및 피복재(26)로 구성된다.3 is a cross-sectional perspective view of the asphalt waterproof sheet of the present invention, wherein the asphalt sheet 21 of the present invention is a heavy nonwoven fabric 22, an upper asphalt layer 25, a lower asphalt layer 24, a low weight nonwoven fabric 23, and a covering material. It consists of 26.

고중량 부직포(22)는 종래의 아스팔트 방수시트(1, 11)에 사용되는 부직포(2, 12)의 단위중량 180g/㎡보다 적은 단위중량 120g/㎡의 부직포를 사용한다.The heavy weight nonwoven fabric 22 uses a nonwoven fabric having a unit weight of 120 g / m 2 less than the unit weight of 180 g / m 2 of the nonwoven fabrics 2 and 12 used in the conventional asphalt waterproof sheets 1 and 11.

상부 아스팔트층(25) 및 하부 아스팔트 층(24)은 상기 고중량 부직포(22)를 용융아스팔트 용액에 통과시킬 때, 상기 고중량 부직포(22)의 상부면과 하부면에 각각 아스팔트 피복을 형성한 것으로써, 주로 신축성이 우수한 고무화 아스팔트를 이용한다.When the upper asphalt layer 25 and the lower asphalt layer 24 pass the heavy weight nonwoven fabric 22 through the molten asphalt solution, the upper and lower surfaces of the heavy weight nonwoven fabric 22 respectively form asphalt coatings. In general, rubberized asphalt with excellent elasticity is used.

저중량 부직포(23)는 상기 상부 아스팔트층(25)이 형성된 고중량 부직포(22) 위에 부착된 것으로써 단위중량은 40 내지 60g/㎡이며, 상기 용융 아스팔트 용액을 통과하여 나온 상기 고중량 부직포(22)의 상부 아스팔트층(25) 위에, 버너를 사용하여 순간적으로 상기 상부 아스팔트층(25)을 용융시킨 후 아스팔트 특유의 접착력을 이용하여 부착된 것이다. 상기 저중량 부직포(23)는 나중에 본 발명의 아스팔트 방수시트(21) 위로 도포되는 도막방수재(30)와 상부 아스팔트층(25) 사이의 매개체 역할을 하여 상기 상부 아스팔트층(25)과 도막방수층의 결합을 단단히 해주는 역할을 하며, 단위중량 60g/㎡ 이상이 되면 도막방수재가 부직포로 다량 흡수되므로 상기 도막방수층을 여러 겹 도포해야 부직포 위로 일정두께의 도막방수층을 형성할 수 있어 비경제적이다.The low weight nonwoven fabric 23 is attached to the high weight nonwoven fabric 22 on which the upper asphalt layer 25 is formed and has a unit weight of 40 to 60 g / m 2. On the upper asphalt layer 25, the upper asphalt layer 25 is instantaneously melted using a burner, and then attached using an asphalt-specific adhesive force. The low weight nonwoven fabric 23 serves as a medium between the upper waterproof layer and the upper waterproof layer 30 and the coating waterproofing material 30 applied to the asphalt waterproof sheet 21 of the present invention, the upper asphalt layer 25 and the waterproof layer of the coating When the unit weight is more than 60g / ㎡ and the coating film waterproofing material is absorbed in a large amount of non-woven fabric, the coating film waterproofing layer should be applied several times to form a coating waterproof layer of a certain thickness on the nonwoven fabric is uneconomical.

피복재(26)는 폴리에틸렌 필름, 잔모래 및 탈부착이 가능한 이형지 등을 주로 사용하여 상기 하부 아스팔트층(24) 하부에 부착되며, 구조체와 동일한 분포로 점접착되어 구조체에 발생되는 균열에 대해 신축성을 가지고 대응하기 위한 것이다. 만약 상기 피복재(26)가 상기 아스팔트 방수시트(21)에 부착되어 있지 않으면 고온에서 하부 아스팔트층(24)이 녹게 되어 구조체와 점접착이 되지 못하고 아스팔트 방수와 같이 구조체에 상기 하부 아스팔트층(24)의 전면이 부착되어 구조체에 발생하는 균열에 대응하기 어렵다.The coating material 26 is mainly attached to the lower asphalt layer 24 by using a polyethylene film, fine sand, and a release paper that can be attached and detached, and is elastically bonded to cracks generated in the structure by adhesive bonding in the same distribution as the structure. It is to. If the coating material 26 is not attached to the asphalt waterproof sheet 21, the lower asphalt layer 24 is melted at a high temperature, and thus the lower asphalt layer 24 is not adhered to the structure. It is difficult to cope with cracks occurring in the structure due to the front surface of.

종래의 아스팔트 방수시트(1, 11)를 제작하기 위해서는 단위중량 180g/㎡의 부직포(2)가 사용된다. 왜냐하면 아스팔트 방수시트를 제작하기 위해서는 용융아스팔트를 통과한 부직포를 롤러 등을 사용하여 잡아당겨서 상기 부직포에 아스팔트 피복을 형성하게 되는데, 이때 단위중량이 모자라게 되면 상기 부직포는 상기 롤러가 당기는 장력으로 인하여 찢어지기 쉽기 때문이다.In order to produce conventional asphalt waterproof sheets 1 and 11, a nonwoven fabric 2 having a unit weight of 180 g / m 2 is used. In order to manufacture the asphalt waterproof sheet, the nonwoven fabric passed through the molten asphalt is pulled using a roller or the like to form an asphalt coating on the nonwoven fabric. When the unit weight is insufficient, the nonwoven fabric is torn due to the tension of the roller. Because it is easy.

그러나 상기 부직포의 단위중량 180g/㎡은 방수업계의 당업자들이 안전율을 고려하여 높게 잡은 수치로써, 본 발명의 아스팔트 방수시트(21)의 발명자는 여러 번 시험을 거듭하여, 롤러가 당기는 장력에 견딜 수 있어서 부직포가 찢어지지 않는 최소 단위중량 120g/㎡을 실현하였다.However, the unit weight of the nonwoven fabric 180g / ㎡ is a number that high skilled in the waterproof industry in consideration of the safety factor, the inventors of the asphalt waterproof sheet 21 of the present invention repeated the test several times, can withstand the tension pulled by the roller Thus, a minimum unit weight of 120 g / m 2 was achieved without causing the nonwoven fabric to tear.

본 발명의 아스팔트 방수시트를 이용한 복합방수공법을 설명하면 다음과 같다. 방수작업을 하고자 하는 구조체 부위를 청소한 후, 상기 구조체 위에 프라이머 작업을 한다. 상기 프라이머 위에 본 발명의 아스팔트 방수시트(21)를 다수 개 연속해서 부착한다. 상기 다수개 연속해서 부착한 아스팔트 방수시트(21) 위에 도막방수재(30)를 도포하여 도막방수층을 형성한다. 상기 도막방수층을 형성한 후 약 24시간 보양하여 경화시키면 방수작업은 완료된다. 또한 도4와 같이 상기 도막방수재(30)를 도포하기 전에 상기 아스팔트 방수시트(21)와 아스팔트 방수시트(21) 사이의 이음부에 폴리우레탄 등을 이용한 이음부 결합재(31)를 사용하여 상기 이음부를 코킹하여 상부 이음부를 통한 누수에 보다 근본적으로 대처할 수 있있다.Referring to the composite waterproof method using the asphalt waterproof sheet of the present invention. After cleaning the structure part to be waterproofed, primer work is performed on the structure. A plurality of asphalt waterproof sheet 21 of the present invention is successively attached on the primer. The coating film waterproofing material 30 is applied on the asphalt waterproof sheet 21 continuously attached to a plurality of them to form a coating film waterproofing layer. After forming the coating film waterproofing layer and curing for about 24 hours to complete the waterproofing work. In addition, as shown in Figure 4 before the coating film waterproofing material 30 is applied to the joint between the asphalt waterproof sheet 21 and the asphalt waterproof sheet 21 using a joint joint member 31 using a polyurethane or the like By caulking the part, it is possible to deal more fundamentally with the leak through the upper joint.

본 발명의 아스팔트 방수시트 및 이를 이용한 복합방수공법은 구조체의 균열에 보다 효과적으로 대응할 수 있으며, 종래의 아스팔트 시트방수의 이음부에서 발생하던 누수를 방지할 수 있다. 또한, 아스팔트 시트방수와 도막방수의 장점을 결합하여 아스팔트 방수시트 간의 이음부가 노출되지 않고 평탄한 방수면을 얻을 수 있으며, 시공시간이 짧고 내구성능과 방수성능이 우수하며, 종래와 같이 여러 겹으로 도막방수층을 형성하지 않고 한 겹만 상기 도막방수층을 형성하여 불필요한 도막방수층 피복공정 및 도막방수층 시공비용을 줄일 수 있다.Asphalt waterproof sheet of the present invention and the composite waterproof method using the same can more effectively cope with the crack of the structure, it is possible to prevent the leakage occurred in the joint of the conventional waterproof waterproof sheet. In addition, by combining the advantages of waterproofing the asphalt sheet and waterproofing the coating, it is possible to obtain a flat waterproof surface without exposing the joints between the asphalt waterproof sheets, the construction time is short, durability and waterproof performance is excellent, and the coating film in multiple layers as in the prior art Without forming a waterproof layer, only one layer of the coating layer is formed to reduce unnecessary coating layer coating process and coating layer waterproofing cost.

Claims (4)

단위중량 120g/㎡의 고중량 부직포(22);Heavy nonwoven fabric 22 having a unit weight of 120 g / m 2; 상기 고중량 부직포(22)의 상부면에 형성되는 상부 아스팔트층(25);An upper asphalt layer 25 formed on an upper surface of the heavy nonwoven fabric 22; 상기 고중량 부직포(22)의 하부면에 형성되는 하부 아스팔트층(24);A lower asphalt layer 24 formed on the lower surface of the heavy nonwoven fabric 22; 상기 상부 아스팔트 층(25) 위에 부착되는 단위중량 40 내지 60g/㎡의 저중량 부직포(23); 및,A low weight nonwoven fabric having a unit weight of 40 to 60 g / m 2 attached to the upper asphalt layer 25; And, 상기 하부 아스팔트층(24) 하부에 부착되는 피복재(26);A covering material 26 attached to the lower asphalt layer 24; 로 구성되는 것을 특징으로 하는 아스팔트 방수시트.Asphalt waterproof sheet, characterized in that consisting of. 구조체의 방수작업 부위를 청소하고;Clean the waterproofing site of the structure; 상기 구조체 위에 프라이머 층을 형성하고;Forming a primer layer over the structure; 상기 프라이머 위에 제1항의 아스팔트 방수시트(21)를 다수개 연속해서 연결하여 부착하고;Attaching and connecting a plurality of asphalt waterproof sheets 21 of claim 1 on the primer in series; 상기 아스팔트 방수시트(21) 위에 도막방수재(30)를 도포하여 도막방수층을 형성하고; 그리고,Coating the waterproofing material 30 on the asphalt waterproof sheet 21 to form a waterproofing film; And, 상기 도막방수층을 경화시키는 단계;Curing the coating waterproof layer; 로 구성되는 것을 특징으로 하는 복합방수공법.Composite waterproof method, characterized in that consisting of. 제2항에서, 상기 도막방수재(30)를 도포하기 전에 상기 아스팔트 방수시트(21) 간의 이음부에 이음부 결합재(31)를 코킹하는 단계를 더 포함하는 것을 특징으로 하는 복합방수공법.3. The composite waterproof method according to claim 2, further comprising caulking the joint bonding material (31) to the joints between the asphalt waterproof sheet (21) before applying the coating waterproofing material (30). 제2항 또는 제3항에서, 상기 도막방수재(30)로 폴리우레탄을 사용하는 것을 특징으로 하는 복합방수공법.The composite waterproof method according to claim 2 or 3, wherein polyurethane is used as the coating waterproofing material.
KR1019990047789A 1999-10-30 1999-10-30 Waterproofing sheet using the asphalt and composite waterproofing method using the same KR100334602B1 (en)