KR20000018105A - The making method of a pillow's ball - Google Patents

Abstract

PURPOSE: A manufacturing method of a ball for a pillow is provided to control the air permeability and the humidity as well as the ground pressure effect when contacting with a head as using the manufactured ball with yellow soil as a main material as a pillow. CONSTITUTION: A ball for a pillow is manufactured by the steps of; mixing yellow soil powder of 200 meshes with starch at the ratio of 3 to 1; manufacturing a ball with its aperture of 1.5 cm; firstly drying the ball at a temperature of 40 to 80 deg.C; and secondarily drying the ball after dipping it into artemisia or pine needle liquid.

Description

{The making method of a pillow's ball}

The present invention relates to a method for manufacturing a ball for a pillow, and more particularly, to accommodate a ball made of ocher as a main material on a pillow to control the acupressure effect and breathability and humidity upon contact with the head when used as a pillow.

Conventionally used pillows are used to store grains such as wheat, beans, or herbal medicines or charcoal in the pillows.

They do not have acupressure effect or breathability and humidity control function when they come in contact with the head. Especially, if you use it for a long time, the body temperature of the head is transferred to the pillow. There has been a disability that causes disturbances in sleep.

Therefore, the present invention is to make the ball as a main material to be stored in the pillow to be used to store the ball in the pillow used to control the function of acupressure and ventilation and humidity in the head.

Starch grass was mixed with 200 mesh ocher powder at a ratio of 3: 1 to make a ball having a diameter of 1.5Cm and dried first at 40-80 ° C., which was then immersed in wormwood or pine needle juice for 40 hours. It is prepared by secondary drying at -60 ℃.

The present invention will be described in detail according to the manufacturing process as follows.

First process (ocher formation process)

The loess powder is formed by sifting the loess with a 200 mesh sieve.

Second Process (Pool Manufacturing Process)

300 g of flour per 10 L of water is mixed and warmed to prepare starch paste.

Third process (mixing process of ocher powder and grass)

The loess and grass of the first step are combined in a 3: 1 ratio and mixed to homogenize.

4th process (ball manufacturing process)

The ball is manufactured so that the ocher of the third process has a diameter of 1.5 cm.

5th process (1st drying process)

The ball of the fourth step is placed in a drying chamber, dried at 40 ° C for 30 minutes, warmed to 50-80 ° C, and dried for 4 hours.

6th process (the process of making mugwort or pine needle juice)

The washed phosphorus mugwort is pulverized in a grinder or juice or the washed pine needles are pulverized juice to form mugwort or pine needle juice.

7th process (immersion process of mugwort juice or pine needle juice)

The ball of the fifth step is immersed in wormwood juice or pine needle juice for 10 minutes.

8th process (secondary drying process)

The ball immersed in the seventh step is put in a drying chamber and dried for 2-3 hours at a temperature of 40-60 ℃.

9th Process (Production Process)

The ball dried in the eighth step is put into a certain amount in a pillow of a pillow standard and commercialized.

The ball produced in this way is the main material is ocher, so the yellow ocher emits moisture contained in the ocher when the room is dry, and absorbs water when the room is high humidity.

In addition, the grass gives viscosity to the loess to strengthen the strength of the manufactured ball so as not to break the ball,

In addition, mugwort juice or pine needle juice penetrates the cheeks and radiates mugwort or pine needles.

In addition, ocher and grass are mixed at a mixing ratio of 3: 1, but the mixing ratio can be adjusted according to the state of moisture contained in the loess.

When the ball manufactured in such a manufacturing process is stored in a pillow and used as a pillow, the pillow on which the head is located is composed of ocher balls. In addition, the ocher ball absorbs the heat and sweat emitted from the tofu, and the mugwort or pine needles penetrate into the cheek naturally diverge, so that a good night's sleep becomes clear after sleep.

The present invention as described above is made of ocher as a main material and mixed with starch grass to produce a ball and penetrate the wormwood or pine needle juice to form a ball for the pillow to emit the scent and put into the pillow to use as a pillow at bedtime It is a very useful invention that can achieve ventilation, humidity control and acupressure effects.

Claims (1)

Starch grass is mixed with 200 mesh ocher powder in the ratio of 3: 1, and it is composed of 1.5Cm diameter balls and dried first at 40-80 ℃, and then immersed in mugwort or pine needle juice for 40 hours. Pillow ball manufacturing method to dry at -60 ℃ (Independent Port)