KR19990081120A

KR19990081120A - Manufacturing method of candles

Info

Publication number: KR19990081120A
Application number: KR1019980014876A
Authority: KR
Inventors: 이은선
Original assignee: 이은선
Priority date: 1998-04-25
Filing date: 1998-04-25
Publication date: 1999-11-15

Abstract

본 발명은 양초의 제조방법에 관한 것으로, 양초의 심지를 제조할 때 심지사가 탄소,알루미늄, 은, 마그네슘, 숫가루, 3염화 안티몬, 철, 세륨, 과염소산 암모늄, 과염소산 칼륨, 질산칼륨(초석), 수산 소오다, 초산 스트로튬, 초산 바륨, 염소산 칼륨(염산 가리), 칼슘, 유황, 인 및 티타늄 파우더 들의 소량을 파라핀과 혼합한 혼합용액을 강제로 통과하는 중에 침지되어 경화된 심지로 형성되도록 하고,The present invention relates to a method for producing a candle, wherein when the wick of the candle is manufactured, the wick is carbon, aluminum, silver, magnesium, ground flour, antimony trichloride, iron, cerium, ammonium perchlorate, potassium perchlorate, potassium nitrate (stone) Sodium hydroxide, strontium acetate, barium acetate, potassium chlorate (Gary chloride), calcium, sulfur, phosphorus, and titanium powders are immersed during the passage through a mixed solution mixed with paraffin to form a hardened wick. and,

상기 혼합용액이 침지된 상태인 심지의 외면에 파라핀을 원통형으로 형성하면서 경화시켜 양초를 완성하도록 함으로써 심지에 불을 붙이면 심지에서 축포가 터지는 듯한 불꽃반응이 일어나면서 여러 색채의 불꽃이 발생되어 축하하는 즐거움이 배가되도록 한 것이다.The paraffin is formed on the outer surface of the wick in which the mixed solution is immersed in a cylindrical shape to cure the candle to cure the candle by igniting the wick. Pleasure is doubled.

Description

Manufacturing method of candles

본 발명은 양초의 제조방법에 관한 것으로, 특히 양초의 심지를 제조할 때 심지사가 탄소,알루미늄, 은, 마그네슘, 숫가루, 3염화 안티몬, 철, 세륨, 과염소산 암모늄, 과염소산 칼륨, 초석 등을 소량을 파라핀과 혼합한 혼합용액을 통과하는 중에 침지(浸漬)되도록 한 후 외면에 파라핀층을 형성하여 양초를 완성하여 심지에 불을 붙이면 심지에서 축포가 터지는 듯한 불꽃반응이 일어나면서 여러 색채의 불꽃이 발생되어 축하하는 즐거움이 배가되도록 한 양초의 제조방법에 관한 것이다.The present invention relates to a method for producing a candle, in particular, when preparing the wick of the candle, the wick is a small amount of carbon, aluminum, silver, magnesium, powder, antimony trichloride, iron, cerium, ammonium perchlorate, potassium perchlorate, saltpeter, etc. Immersed in the mixed solution mixed with paraffin, and then formed a paraffin layer on the outer surface to complete the candle and light the wick. It relates to a method for producing a candle that is generated and doubled the joy of celebration.

종래에는 심지사의 외면에 파라핀층을 형성하여 양초를 제조하였으므로 심지에 불을 붙여서 촛불을 밝힐 때 심지사의 외면에 원통형으로 형성된 파라핀층에 의해 서서히 타면서 불꽃만 발생하였다.Conventionally, since the candle was manufactured by forming a paraffin layer on the outer surface of the wick, the flame was only burned slowly by the paraffin layer formed in a cylindrical shape on the outer surface of the wick when the candle was lit by lighting the wick.

그러므로 정전이나 컴컴한 곳에서 사용하는 경우가 아니고 축하용으로 예식장 등에서 사용할 경우에는 그냥 단순히 불만 밝히는 상태로 인해 축하의 분위기를 상승시켜 주지 못하는 단점이 있었다.Therefore, when used in ceremonies, such as blackouts or combos, but not for use in celebrations, there was a drawback of not simply raising the mood of the celebration due to the state of dissatisfaction.

그러므로 한국공개특허 제 86-361호에 개시된 바와 같이 양초심지(1)의 외면에 발화성합금(2)인 산화제 질산바륨층을 형성하여 불을 밝힐 때 불티를 내도록 하는 방법을 제안하였었다.Therefore, as disclosed in Korean Patent Application Laid-Open No. 86-361, a method of forming a barium nitrate layer, an ignitable alloy (2), on the outer surface of the candle wick (1) has been proposed to ignite the light.

그러나 상기와 같은 종래의 방법은 양초심지의 외면에 산화제 질산바륨에 의한 발화성합금(2)을 형성하여 질산바륨의 자체 특성인 불꽃을 발생시키는 것이므로 특별한 상승효과가 없음은 물론, 질산바륨이 직접 연소되면서 근처의 인화물질에 인화되어 화재가 발생하게 되는 등의 문제점이 있었다.However, the conventional method as described above forms a pyrophoric alloy (2) by the oxidizing agent barium nitrate on the outer surface of the candle wick to generate a flame which is a characteristic of barium nitrate, so that there is no particular synergistic effect, and barium nitrate is directly burned. While there was a problem such as a fire caused by the flammable material nearby.

따라서 본 발명은 이와 같은 사정을 고려하여 착안한 것으로 양초의 심지를 제조할 때 심지사가 탄소,알루미늄, 은, 마그네슘, 숫가루, 3염화 안티몬, 철, 세륨, 과염소산 암모늄, 과염소산 칼륨, 초석 등을 파라핀과 혼합한 혼합용액층을 통과하는 중에 침지되도록 하여 불꽃이 발생되는 중에도 다른 인화물질에 착화되지 않아 안전하게 사용할 수 있으며 여러 색채의 불꽃이 발생되어 축하하는 즐거움이 배가되도록 한 양초의 제조방법을 제공하는 것을 그 목적으로 한다.Therefore, the present invention was conceived in view of such a situation that when the wick is manufactured in the candle wick, carbon, aluminum, silver, magnesium, powder, antimony trichloride, iron, cerium, ammonium perchlorate, potassium perchlorate, saltpeter and the like It is immersed while passing through the mixed solution layer mixed with paraffin so that it can be used safely because it is not ignited with other flammables even when a spark is generated. It is for that purpose.

상기와 같은 목적을 달성하기 위한 본 발명은 양초의 심지를 제조할 때 심지사가 탄소,알루미늄, 은, 마그네슘, 숫가루, 3염화 안티몬, 철, 세륨, 과염소산 암모늄, 과염소산 칼륨, 질산칼륨(초석), 수산 소오다, 초산 스트로튬, 초산 바륨, 염소산 칼륨(염산 가리), 칼슘, 유황, 인 및 티타늄 파우더 들의 소량을 파라핀과 혼합한 혼합용액을 강제로 통과하는 중에 침지되어 경화되도록 하고,In order to achieve the above object, the present invention provides a wick of carbon, aluminum, silver, magnesium, flour, antimony trichloride, iron, cerium, ammonium perchlorate, potassium perchlorate, potassium nitrate (stone) Sodium hydroxide, strontium acetate, barium acetate, potassium chlorate (garic acid chloride), small amounts of calcium, sulfur, phosphorus and titanium powders were immersed and hardened while passing through a mixed solution mixed with paraffin.

도 1 은 본 발명에 의한 심지의 제조과정을 나타낸 개략도.1 is a schematic view showing the manufacturing process of the wick according to the present invention.

* 도면의 주요 부분에 대한 부호의 설명 *Explanation of symbols on the main parts of the drawings

1 : 본체 2 : 굵은 구멍1: body 2: thick hole

3 : 공간부 4 : 밀편3: space part 4: wheat flour

5 : 가는 구멍 10 : 심지사5: thin hole 10: wick

11: 심지11: wick

이하 첨부된 도면에 의하여 본 발명의 바람직한 실시 형태를 상세히 설명하면 다음과 같다.Hereinafter, preferred embodiments of the present invention will be described in detail with reference to the accompanying drawings.

도 1 은 본 발명의 심지를 제조하는 장치를 개략적으로 도시한 것으로서, 본체(1)의 일측에 형성한 굵은 구멍(2)을 통하여 강제로 인입되는 심지사(10)는 중앙의 공간부(3)에서 상부로 부터 소정의 압력으로 미는 밀편(4)의 압력에 의해 혼합용액이 침지된 상태가 되도록 하고,FIG. 1 schematically shows an apparatus for manufacturing a wick according to the present invention, wherein a wick 10 forcibly drawn through a thick hole 2 formed at one side of a main body 1 has a central space 3. The mixed solution is immersed by the pressure of the push piece (4) to push at a predetermined pressure from the top,

상기 혼합용액이 침지된 상태인 심지사(10)는 본체(1) 타측의 작은 구멍(5)을 통해 단단하게 경화된 심지(11)로 토출되도록 한다.The wick 10 in which the mixed solution is immersed is discharged to the hardened wick 11 through the small hole 5 on the other side of the main body 1.

그리고 상기의 혼합용액은 중량비 81%의 파라핀과, 중량비 4.5%의 탄소와, 백광을 방출하는 중량비 3.75%의 알루미늄과, 감광재료인 중량비 3.2%의 은과, 플래시 램프의 재료인 중량비 1.4%의 마그네슘과, 중량비 1.2%의 숫가루와, 중량비 0.8%의 3염화 안티몬과, 성냥이나 화약의 재료가 되는 중량비 0.8%의 염소산 칼륨(염산 가리)과, 중량비 0.6%의 철과, 빛과 열을 발생하는 중량비 0.5%의 세륨과, 중량비 0.5%의 칼슘과, 400℃에서 발화하는 중량비 0.3%의 과염소산 암모늄과, 중량비 0.2%의 과염소산 칼륨과, 흑색화약이나 성냥의 재료인 중량비 0.1%의 질산칼륨(초석)과, 중량비 0.2%의 수산 소오다와, 중량비 0.1%의 초산 스트로튬과, 중량비 0.1%의 초산 바륨과, 성냥이나 화약의 재료인 중량비 0.06%의 유황과, 성냥의 원료인 중량비 0.02%의 인 및 중량비 0.005%의 티타늄 파우더들을 혼합하여 제조한다.The mixed solution may contain 81% paraffin by weight, 4.5% carbon by weight, 3.75% aluminum by which white light is emitted, 3.2% silver by weight as a photosensitive material, and 1.4% by weight as a material of a flash lamp. Magnesium, ground powder of 1.2% by weight, antimony trichloride of 0.8% by weight, 0.8% of potassium chlorate (gallic acid) by weight of 0.8% by weight to be a material of matches and gunpowder, iron of 0.6% by weight, light and heat Cerium at 0.5% by weight, calcium at 0.5% by weight, ammonium perchlorate at 0.3% by weight ignited at 400 ° C, potassium perchlorate at 0.2% by weight, and potassium nitrate at 0.1% by weight, which is a material of black powder and match (Stone), sodium hydroxide with a weight ratio of 0.2%, strontium acetate with a weight ratio of 0.1%, barium acetate with a weight ratio of 0.1%, sulfur with a weight ratio of 0.06%, which is a material of matches and gunpowder, and a weight ratio of 0.02 % Phosphorus and weight ratio of 0.005% Prepared by mixing titanium powders.

이와 같은 제조방법에 의해 완성된 심지(11)의 외면에 파라핀을 원통형으로 형성하면서 경화시키면 양초가 완성된다.If the cured while forming the paraffin in the cylindrical shape on the outer surface of the wick 11 completed by such a manufacturing method, the candle is completed.

이와 같은 본 발명은 중량비 81%의 파라핀, 중량비 4.5%의 탄소, 중량비 3.75%의 알루미늄, 중량비 3.2%의 은, 중량비 1.4%의 마그네슘, 중량비 1.2%의 숫가루, 중량비 0.8%의 3염화 안티몬, 중량비 0.8%의 염소산 칼륨, 중량비 0.6%의 철, 중량비 0.5%의 세륨, 중량비 0.5%의 칼슘, 중량비 0.3%의 과염소산 암모늄, 중량비 0.2%의 과염소산 칼륨, 중량비 0.1%의 질산칼륨, 중량비 0.2%의 수산 소오다, 중량비 0.1%의 초산 스트로튬, 중량비 0.1%의 초산 바륨, 중량비 0.06%의 유황, 중량비 0.02%의 인 및 중량비 0.005%의 티타늄 파우더를 잘 혼합한 용액을 본체(1)의 공간부(3)에 넘치거나 흐르지 않을 정도의 적당량을 공급한 후 밀편(4)으로 서서히 밀어주게 되면, 그 압력에 의해 본체(1)의 일측 굵은 구멍(2)을 통하여 강제로 인입되는 심지사(10)의 내부까지 침투되어 침지된 것과 같은 상태가 된다.The present invention is paraffin of 81% by weight, carbon by weight of 4.5%, aluminum by weight 3.75%, silver by weight 3.2%, magnesium by weight 1.4%, flour by weight 1.2%, antimony trichloride by weight 0.8%, By weight 0.8% potassium chlorate, by weight 0.6% iron, by weight 0.5% cerium, by weight 0.5% calcium, by weight 0.3% ammonium perchlorate, by weight 0.2% potassium perchlorate, by weight 0.1% potassium nitrate, by weight 0.2% The space part of the main body 1 was prepared by mixing a solution of sodium hydroxide, strontium acetate at 0.1% by weight, barium acetate at 0.1% by weight, sulfur at 0.06% by weight, phosphorus at 0.02% by weight, and titanium powder at 0.005% by weight. After supplying an appropriate amount such that it does not overflow or flow into (3) and gradually pushes it to the compact piece 4, the wick (10) forcibly pulled in through the one side thick hole (2) of the main body (1) by the pressure. As penetrated and submerged inside Is (a)

그리고 혼합용액이 침지된 상태인 심지사(10)를 본체(1)의 타측 가는 구멍(5)으로 강제로 토출시키게 되면, 가는 구멍(5)에 의해 압축되는 상태인 심지사(10)의 혼합용액이 더욱 침투되면서 경화되어 혼합용액이 침지된 심지(11)가 된다.When the wicks 10 in which the mixed solution is immersed are forcibly discharged to the other thin holes 5 of the main body 1, the mixed solution of the wicks 10 in the compressed state by the thin holes 5 As it penetrates further, it becomes a wick 11 in which the mixed solution is immersed.

그러므로 이러한 심지(11)를 이용하여 완성한 양초에 불을 붙이게 되면, 중량비 4.5%의 탄소와 중량비 1.2%의 숫가루 등에 의해 심지(11)가 착화된 상태에서 계속적인 발화가 이루어진다.Therefore, when the candle ignited using the wick 11 is ignited, continuous ignition is performed in a state in which the wick 11 is ignited by carbon in a weight ratio of 4.5% and a flour in a weight ratio of 1.2%.

그리고 중량비 3.75%의 알루미늄, 중량비 3.2%의 은, 중량비 1.4%의 마그네슘 및 중량비 0.5%의 세륨 등에 의해 다양한 색상의 빛이 방출된다.Light of various colors is emitted by aluminum having a weight ratio of 3.75%, silver having a weight ratio of 3.2%, magnesium having a weight ratio of 1.4%, cerium having a weight ratio of 0.5%, and the like.

또한 중량비 0.8%의 염소산 칼륨, 중량비 0.6%의 철, 중량비 0.5%의 칼슘, 중량비 0.3%의 과염소산 암모늄, 중량비 0.2%의 과염소산 칼륨, 중량비 0.1%의 질산칼륨, 중량비 0.2%의 수산 소오다, 중량비 0.1%의 초산 스트로튬, 중량비 0.1%의 초산 바륨, 중량비 0.06%의 유황, 중량비 0.02%의 인 및 중량비 0.005%의 티타늄 파우더에서 섬광과 같은 다양한 불꽃이 발생된다.In addition, 0.8% potassium chlorate by weight, 0.6% iron by weight, 0.5% calcium by weight, 0.3% ammonium perchlorate, 0.2% potassium perchlorate by weight, 0.1% potassium nitrate, 0.2% sodium hydroxide by weight, and weight ratio Various sparks such as flash are generated from 0.1% strontium acetate, 0.1% barium acetate by weight, 0.06% sulfur by weight, 0.02% phosphorus by weight, and 0.005% titanium powder by weight.

그리고 중량비 81%의 파라핀에 의해 심지(11)에서 불꽃과 광을 발생하면서 타는 동안에도 근처의 다른 인화물질에 착화가 되지 않으므로 안전하게 사용할 수 있다.In addition, since paraffin having a weight ratio of 81% generates sparks and light in the wick 11, it does not ignite other flammable substances in the vicinity while burning, and thus can be safely used.

따라서 본 발명의 양초의 제조방법에 의하여서는 심지사가 탄소,알루미늄, 은, 마그네슘, 숫가루, 3염화 안티몬, 철, 세륨, 과염소산 암모늄, 과염소산 칼륨, 질산칼륨, 수산 소오다, 초산 스트로튬, 초산 바륨, 염산 가리, 칼슘, 유황, 인 및 티타늄 파우더 들의 소량을 파라핀과 혼합한 혼합용액에 강제로 통과하는 중에 침지되어 경화된 심지가 형성되도록 함으로써 외면에 파라핀을 형성하면서 완성한 양초를 사용할 때 심지에서 축포가 터지는 듯한 불꽃반응이 일어나면서 여러 색채의 불꽃이 발생되어 보는 즐거움이 배가되고 안전하게 사용할 수 있는 것이다.Therefore, according to the method for producing a candle of the present invention, the core yarn is carbon, aluminum, silver, magnesium, ground flour, antimony trichloride, iron, cerium, ammonium perchlorate, potassium perchlorate, potassium nitrate, sodium hydroxide, strontium acetate, nitrate When a small amount of barium, gallium hydrochloride, calcium, sulfur, phosphorus, and titanium powders is forced through the mixed solution mixed with paraffin, it is immersed to form a hardened wick, forming paraffin on the outer surface, The flame reaction that pops up like a bubble is generated and the sparks of various colors are generated to double the pleasure of viewing and to use safely.

Claims

The mixed core 10 is forced through the thick hole 2 formed on one side of the main body 1 so that the mixed solution is well immersed by the pressure applied by the push piece 4 in the central space 3. ,

Method for producing a candle in which the mixed solution is immersed in the wick (10) through the small hole (5) formed on the other side of the main body (1) to be hardened and discharged to the wick (11).

The mixed solution according to claim 1, wherein the mixed solution is paraffin at 81% by weight, carbon at 4.5% by weight, aluminum at 3.75% by weight, silver at 3.2% by weight, magnesium at 1.4% by weight, ground flour at 1.2% by weight, and 0.8 by weight. % Antimony trichloride, 0.8% potassium chlorate by weight, 0.6% iron by weight, 0.5% cerium by weight, 0.5% calcium by weight, 0.3% ammonium perchlorate by weight, 0.2% potassium perchlorate by weight, 0.1% by weight nitric acid Preparation of candles well mixed with potassium, 0.2% sodium hydroxide by weight, 0.1% strontium acetate by weight, 0.1% barium acetate, 0.06% sulfur by weight, 0.02% phosphorus by weight, and 0.005% titanium powder by weight Way.