KR19990078900A - Manufacturing Method for flooring paint - Google Patents

Abstract

The present invention relates to a method for producing a flooring material using the main raw material of the clay and the anion is discharged loess and far infrared rays, which is the main raw material and the vegetable adhesive extracted from charcoal and algae is released from the loess powder and silver ions It is an object of the present invention to provide a paint for flooring using an epoxy resin, aluminum silicate, polydimethylsiloxane, and the like to prevent moss and fungus in advance by causing non-toxic, odorless, anti-corrosion and antibacterial and hygroscopic effects.

The ground paint of the present invention for achieving the above object is 10 wt%-20wt% of ocher powder obtained by calcining pure ocher extracted from impurity containing ocher to 1100 ℃-1300 ℃ and powdered to 330-350 mesh And charcoal powder made by burning wood to 330-350mesh, 10wt%-20wt% charcoal powder, 5wt%-10wt% vegetable adhesive extracted from gambling, 20wt%-30wt% epoxy resin, aluminum silicate It is a summary that 20 wt%-30 wt% and 5 wt%-10 wt% of polydimethylsiloxane are mixed.

Description

Manufacturing method for flooring paint

The present invention relates to a method for manufacturing a flooring material using the main raw material of the clay and the anion is emitted clay and far-infrared rays, and more specifically, natural adhesive extracted from charcoal powder and algae baked by baking high-temperature calcined ocher powder and wood; Epoxy resin and silicone-based polydimethylsiloxane and the like to produce a beneficial and environmentally friendly paint.

Conventional paint production method using ocher, first to prepare 100 parts by weight of rosin and 40 parts by weight of triethanolamine to 100 ℃ or more in order to prepare the adhesive, 300 parts by weight of 100 ℃ or more water is gradually added to the rosin and triethanolamine water The mixture was uniformly mixed with 100 parts by weight of ethylene-vinylacetate copolymer to the rosin / triethanolamine / water mixture to prepare a rosin / triethanolamine / water / ethylene-vinylacetate mixed solution.

The adhesive prepared in this way is to mix the rosin / triethanolamine / water / ethylene-vinylacetate mixed solution and the particulate ocher powder in a 1: 1 weight ratio to give coating properties, adhesiveness and strength, but it is fluid And lack of elasticity, there was a problem that is very difficult to apply to the construction wall surface or the intended place.

In addition, the prepared adhesive and ocher are not mixed well, so when you want to apply to the construction wall or the target, evenly stir every need to use accordingly, there is a hassle according to the use of toxic chemicals, etc. There was a problem.

In addition, rosin and triethanolamine, which are raw materials of the adhesive mixed with the loess powder, are not easily available on the market, and the purchase cost is high, thereby increasing the manufacturing cost, thereby increasing the customer's provision of paint.

In addition, the conventional paints are provided using paints prepared using chemicals, pigments and chemical adhesives extracted from petroleum, and coatings prepared using ganbanite powder having a far-infrared emission function, and pigments and chemical adhesives. They all have toxic and odorous problems that can harm their health.

The present invention has been invented to solve this problem in consideration of the above-mentioned problems, the main raw material and the epoxy resins, aluminum silicates, poly-chemicals such as ocher powder which emits far infrared rays and vegetable adhesives extracted from char and algae which emit silver ions Providing eco-friendly floor paints by mixing dimethyl siloxane in proper ratio to prevent far-infrared emission, silver ion release and non-toxicity, odorless and corrosion prevention, antibacterial and hygroscopic effect to prevent moss and fungus forms in advance. Is there.

1 is a process chart showing a paint manufacturing process of the present invention.

Characteristic technical configuration for producing a coating using the loess of the present invention having the above object is as follows.

The present invention is made of 10 wt%-20wt% of ocher powder, which is made by calcining pure ocher extracted from impurity loess to 1100 ℃-1300 ℃ and powdered to 330-350mesh, and burning charcoal lumps. Charcoal powder powdered to 350mesh, 10wt% -20wt%, vegetable adhesive extracted from gambling 5wt% -10wt%, epoxy resin 20wt% -30wt%, aluminum silicate 20wt% -30wt%, polydimethylsiloxane 5wt It is characterized by producing a flooring paint by mixing%-10wt%.

The present invention configured as described above will be described in more detail with reference to the accompanying drawings.

The present invention first describes the operation and efficacy of each component for producing a floor coating.

First, ocher contains calcium carbonate, magnesium, potassium, aluminum, selenium, germanium, calcium, etc., so it has excellent resolution, self-cleaning, absorption, transparency, etc. It is a mineral that is radiated abnormally.

Secondly, charcoal is made by baking wood in a charcoal kiln, which is mainly composed of carbon, which is self-cleaning, deodorizing, sterilizing and hygroscopic.

Third, the vegetable adhesive is taken from the sea gambling (red algae with white barley grass and grows on the rocks of the coast) and dried. The dried gambling is heated and concentrated with water, and a small amount of vegetable oil is added thereto. As manufactured, it is good for human body because it has excellent adhesive strength, eco-friendly, non-toxic and odorless.

Fourth, epoxy resin is composed of epichlorohydrion + bisphenol A, and is used as an adhesive for optical, glass, porcelain or light metal plates, and is a thermosetting resin used for paints and plasticizers.

Fifth, aluminum silicate releases a small amount of far-infrared rays and acts as a film forming and filler.

The sixth additive, polydimethyl siloxane, is used to prevent foaming, to maintain smoothness and to shorten drying time.

It describes the preparation process of ocher and charcoal and vegetable adhesives used for the manufacture of the flooring paint of the present invention using each component having such an action and efficacy,

As shown in 1999 Patent Application No. 8849, which I filed earlier, the ocher is taken clay clay with strong viscosity and diluted with water to remove sand, gravel and other impurities contained in ocher, and only pure ocher Screening. The reason for this is to increase the ratio of the pure component of ocher, increase the rate of divergence of beneficial ingredients, namely, far infrared rays generated from the ocher, and increase the performance of resolution, self-cleaning, absorption, transparency and so on.

On the other hand, when the screening operation of the pure loess is finished, the selected pure loess is calcined at 1100 ° C. to 1300 ° C. at high temperature to evaporate all the moisture contained in the loess. However, when the calcination temperature of the loess is less than 1100 ° C., moisture is present in the loess, which adversely affects the paint. When the loess is more than 1300 ° C., the loess burns black, and thus, the above-described effects cannot be exhibited. Therefore, the firing temperature of the loess is suitable 1100 ℃-1300 ℃.

As such, when the high temperature firing of the loess is made, the loess becomes a solid mass and is put into a blender and pulverized to have a particle size of 310mesh-340mesh. The reason is that when the mesh is 310 mesh or less, the paint smoothness decreases after the paint is manufactured. When the mesh is 340 mesh or more, the paint particles are so fine that the paintability is deteriorated. Therefore, the particle size of the char is 310mesh-340mesh is suitable.

The charcoal is cut into a predetermined size of wood and then put it in a charcoal kiln, and the fire is burned to burn the wood, the main ingredient is carbon black lumps, the charcoal lumps are pulverized to have a particle size of 310mesh-340mesh like ocher. The reason is that when the mesh is 310 mesh or less, the paint smoothness is lowered after the paint is manufactured. When the mesh is 340 mesh or more, the paint particles are so fine that the paintability is deteriorated.

The vegetable adhesive is taken from the patent application No. 1999-8850, which is filed by the applicant, and dried by gambling which is red algae, mixed with water and concentrated in vacuo. The stock solution is heated to make it into a liquid phase, and then mixed with evenly mixed vegetable oil, which is excellent in adhesive strength, non-toxic, odorless and environmentally friendly, and thus the vegetable adhesive is unique to the human body.

When the preparation process of the ocher and charcoal and vegetable adhesives is completed, an epoxy resin, aluminum silicate, and polydimethylsiloxane, which are mixed with them, are prepared by appropriate amounts, and then mixed with each other. The reason for use limitation with respect to the mixing amount is as follows.

Pure loess collected from impurity loess was calcined at 1100 ℃-1300 ℃ at high temperature and powdered to 310mesh-340mesh, and the powdered charcoal powder was made into 10wt%-20wt% and particle size 310mesh-340mesh. 10wt%-20wt%, 5wt%-10wt% vegetable adhesive extracted from red algae gamble, 20wt%-30wt% epoxy resin available on the market, 20wt%-30wt% aluminum silicate, 5wt%-10wt polyamide siloxane Mix% to prepare a paint for flooring.

When the ocher powder is used at less than 10wt%, the effect of far infrared radiation beneficial to the human body is too small to expect an effect, and also the degradation, self-cleaning, absorption, transparency, etc. are degraded, and the use of ocher is more than 20wt%. It only adds the cost, but the far infrared radiation, resolution, self-cleaning, absorption and transparency do not improve anymore. Therefore, it is appropriate to use 10wt%-20wt% of ocher powder.

If the charcoal powder is used at 10wt% or less, self-cleaning, odor elimination, sterilization and hygroscopicity are lowered. Falls. Therefore, charcoal powder is suitable to use 10wt%-20wt%.

When the vegetable adhesive is used at 5wt% or less, the environmental friendliness of the paint is lowered, as well as the adhesive strength of the paint is lowered and when used at 10wt% or more, the environmental friendliness of the paint is improved, but the paintability and the foaming rate of the paint are increased, thereby degrading the quality. Therefore, it is appropriate to use a vegetable adhesive 5wt%-10wt%.

If the epoxy resin is used at 20wt% or less, the adhesive strength of the paint is reduced and the decomposability is lowered. If it is used at 30wt% or higher, the paintability and foaming rate are increased, resulting in deterioration of quality and toxic and odor formation on the paint, which is harmful to the human body. Therefore, the epoxy resin is suitable to use 20wt%-30wt%.

If the aluminum silicate is used at 20wt% or less, the coating film is not formed, of course, the filler does not play a role, and if more than 30wt% is used, the film formation and the filler role is good, but the disadvantages of costly and environmentally friendly. Therefore, aluminum silicate is suitable to use 20wt%-30wt%.

If the polydimethylsiloxane is used at 5wt% or less, foaming of the paint cannot be prevented, the smoothness is decreased, the drying time is long, and if the use is more than 10wt%, the above problems can be prevented, but the disadvantages of costly and environmentally friendly There is a problem falling. Therefore, it is suitable to use 20wt% -30wt% of polydimethylsiloxane.

The paints of the present invention as described above can be processed by ocher or charcoal and vegetable adhesives that can be easily obtained from nature and used as a coating material, thereby lowering the manufacturing cost of the paint and maintaining economic efficiency, and thus preventing environmental pollution. Of course, it can be beneficial to the human body.

As mentioned above, the flooring material manufactured by using ocher, charcoal, and vegetable adhesive is harmless to human body because it does not have irritating odor or toxicity generated from existing chemical paints. Especially, far infrared emission is more than 90% and anion due to char It promotes metabolism of the human body by neutralizing cations, and it has the effect of deodorizing function, antibacterial, anti-humidity and blocking the growth of moss or fungus.

Claims (1)

Pure loess extracted from impurity loess was calcined to 1100 ℃ -1300 ℃ and powdered to 330-350mesh to 10wt% -20wt% of ocher powder and 330-350mesh of charcoal made by burning wood. Powdered charcoal powder 10wt%-20wt%, vegetable adhesive extracted from gambling 5wt%-10wt%, epoxy resin 20wt%-30wt%, aluminum silicate 20wt%-30wt%, polydimethylsiloxane 5wt%-10wt Method for producing a paint for flooring, characterized in that by mixing the%.