KR19990064458A - An incense and the method of manufacture - Google Patents

Abstract

The present invention relates to incense, which is used in rituals. More specifically, it is a material capable of maintaining its original shape, such as charcoal, even when burned. By installing in the incense, the outside of the incense burns when the incense is burned by burning the burnt ashes, but the decorative core material relates to the incense and the method for producing the incense to maintain the original shape.

The fragrance according to the present invention, the seating groove 9 and the trough 10 are formed in two stages, respectively, the pedestal formed so that the air vent 8 can be vented in all directions of the gutter (10) toward the outside ( 7) and the decorative core (3) which is installed perpendicular to the pedestal (7), the ventilation hole (4) is formed in the vertical direction in the longitudinal direction and charcoal powder and calcined gypsum are formed of the main material and remain intact even when burned. The tip end closed by being vertically installed on the outer side of the decorative core 3 is cut in a cross shape to form an incision 2, and a charcoal powder coating layer 5a is formed on the closed tip having the incision. The fragrance powder coating layer 1a is formed on the outer circumference of the outer circumference, and the paper material is formed of the main material, and the ash falls down when burning, and the charcoal powder is kneaded, and the inner circumference of the fragrance pipe 1 Filled between the outer circumferential surface of the decorative core (3) and the incense pipe (1) Characterized by consisting of the charcoal dough (5) to maintain the gap with the decorative core material (3).

Description

Incense and its method of manufacture

The present invention relates to an incense used for ritual, and more particularly, to a decorative core having a predetermined shape, such as a buddha, as a material capable of maintaining its original shape, such as charcoal, even when burned. When installed in the fire, when the incense is burned by burning the incense, the outside of the incense is burned and ashes, but the decorative core material relates to the incense and the method for producing the incense to maintain the original shape.

The common fragrances used during rituals give off a wet fragrance upon burning and are formed in the form of thin rods. The rod-like incense is burned down from the top of the entire incense formed in the shape of a rod, the incense burned as described above falls down as ash and can not find the shape.

Such a conventional incense has a thin and long incense, so that the fragrance is easily broken and burns easily, and all of the thin incense burns out and has no meaning other than releasing the fragrance. It was.

In addition, the conventional general incense is not provided with a separate decorative means to decorate the incense was not able to decorate the altar more beautiful and mysterious.

The present invention is to solve the conventional problems as described above, the object of the present invention, to decorate the altar beautifully while elevating the value of the incense to further decorate the incense used in the sacrifice. And, as the incense burns out as the Buddha-like appearance appears inside the incense, to provide an incense and a method for producing the incense to decorate the altar mysteriously and sacred.

The fragrance of the present invention for achieving the above object, the seating groove 9 and the trough 10 are formed in two stages, respectively, the vent hole 8 that can be ventilated in all directions of the trough 10 is the outside Pedestal (7) formed so as to face, and is installed vertically to the pedestal (7), the ventilation hole (4) is formed in the longitudinal direction up and down and charcoal powder and calcined gypsum is formed as a main material to remain intact The decorative core 3 and the tip end closed by being vertically installed outside the decorative core 3 are cut in a twelfth shape to form an incision 2, and a charcoal dough coating layer on the closed tip having the incision. (5a) is formed, the fragrance powder coating layer (1a) is formed on the entire circumference of the outer circumferential surface and the paper material is formed as a main material to burn the fragrance pipe (1) and the charcoal powder kneaded when the material collapses when burned; Inner circumference of the incense pipe (1) and outer circumference of the decorative core material (3) The so filled is characterized as consisting of hyanggwan 1 and the decoration core member 3 char pasty 5 for maintaining the distance between.

Further, the method for producing incense according to the present invention includes charcoal powder 35 to 40%, calcined gypsum 25 to 30%, sodium nitrate 5 to 10%, flavor powder 3 to 5%, paper 3 to 5%, 5-8% corn cooking oil and 20-30% water are mixed, and 2-5% adhesive is added to the mixed mixture and stirred in a blender. Extruded to dry, press-molded to a predetermined shape in a molding mold having a shape for molding the extruded material, the decoration for molding the decorative core material (3) by curing and drying the semi-finished product molded in a predetermined shape in a drying furnace Core shaping process (16), 70-80% paper, 8-10% wood powder, 3-6% charcoal powder, 5-8% fragrance powder, 3-5% sodium nitrate, 10-10 water 15% of the mixture is stirred, and the mixed and stirred mixture is pressurized into a cylindrical tube in which the tip is closed in a mold having a predetermined shape. After molding, the primary curing drying (19) in a drying furnace, and cut the closed tip of the cured semi-finished product in a cross shape, and then apply charcoal dough to the closed tip and coat the flavor powder on the entire circumference of the outer periphery ( 1) The incense pipe forming process (21) and the incense pipe (1) inserted into the decorative core material (3) while filling the charcoal dough (5) into the inside of the incense pipe (1) and the decorative core material (3) ) Is installed in the drying groove (2c) after the secondary curing drying (20c) vertically installed in the seating groove (9) of the pedestal (7) characterized in that it consists of an assembling process 22 is manufactured.

1 is a perspective view showing a fragrance according to the present invention.

2 is a cross-sectional view of the present invention shown in FIG.

3 is a front view of the present invention shown in FIG.

4 is a plan view of the present invention shown in FIG.

5 is a process chart showing a manufacturing method of incense according to the present invention.

Explanation of symbols for main parts of the drawings

1. Incense tube 2. Incision 3. Decorative heartwood

4. Aerator 5. Charcoal dough 6. Location indicator

7. Pedestal 8. Ventilator 9. Inclined groove

10. Gutter 11. Mixing step of decorative core molding material

12. Stirring step 13. Extrusion step 14. Press molding step

15. Drying Steps 16. Decorative Core Forming Process

17. Mixing and stirring the fragrance forming material 18. Extrusion step 18a. Press Molding Step

19. First drying step 20. Incision forming step

20a. Charcoal dough application step 20b. Fragrance Powder Coating Step 20c. Second drying stage

21. Perfume forming process 22. Assembly process

Hereinafter, the present invention according to the accompanying drawings in detail as follows.

1 to 4, the upper part of the pedestal (7) is provided with an incline pipe seating groove (9) for vertical installation of the incense pipe (1) and the decorative core material (3), the center of the seating groove (9) In the trough 10 is formed, the trough 10 is formed radially in all directions so that the air vent 8 to allow the air to be easily vented toward the outside.

In addition, only 5 to 10 mm of the upper head is blocked in the seating groove of the pedestal 7, and the lower end of the decorative core material 3 having the ventilation hole 4 formed in the center direction over the entire length is vertically installed. At this time, the decorative core material 3 is formed in a predetermined shape such as a Buddha statue, and the decorative core material 3 is formed of charcoal powder and calcined gypsum as the main material and remains intact as charcoal after being burned, but external force is applied. It is designed to break easily.

In addition, the incense pipe 1 extrapolated to the outside of the decorative core material 3 is inserted into the inclined pipe seating groove 9 of the pedestal 7 with the decorative core material 3 inserted therein.

The incense tube 1 is formed in the shape of a cylindrical tube with a closed tip, and the closed tip is cut in a cross shape to have an incision 2, and a charcoal dough is formed at a closed tip of the incense tube 1. It is applied to a thickness to form a charcoal dough layer (5a), and a powder coating layer (1a) is formed on the entire circumference of the outer peripheral surface, the upper surface of the incense pipe (1) to indicate the front position of the decorative core material (3) The position display section 6 is formed.

The fragrance tube 1 is made of a paper material as a main material and can be burned. When the fragrance tube 1 is burned, the fragrance tube 1 becomes ash together with the charcoal dough kneaded with charcoal powder.

And, between the inner circumferential surface of the incense pipe (1) and the outer circumferential surface of the decorative heart material (3) is filled with charcoal dough kneading charcoal powder (5) so that the incense pipe (1) and the decorative heart material (3) to maintain a constant interval It is.

The fragrance constructed as described above is manufactured through the process as shown in FIG. 5. First, the decorative core molding process 16 will be described.

First, charcoal powder 35-40%, calcined gypsum 25-30%, sodium nitrate 5-10%, flavor powder 3-5%, paper 3-5%, corn cooking oil 5-8%, water 20 After mixing -30% (decorative core molding material mixing step: 11), 2-5% of the adhesive is added to the mixture mixed in the decorative core molding material mixing step (11) and stirred in a mixer to make a dough state. (Stirring stage: 12)

As described above, the dough material prepared in the stirring step 12 is extruded in an extruder and extruded to have a moisture content of about 5% to dry the first part of the semi-finished product. (Extrusion step: 13)

Thereafter, the molded material (primary molded semi-finished product) formed in the extrusion step 13 is put into a molding mold having the same shape as the shape to be molded and then press-molded to mold the semi-finished product (press molding step 14). Then, the semi-finished product molded in the pressure forming stage (14) is dried to cure in a drying furnace to complete the manufacture of the decorative core material 3 having a predetermined shape. (Drying step: 15)

Next, the fragrance tube forming process 21 will be described.

After mixing 70 to 80% of paper, 8 to 10% of wood powder, 3 to 6% of charcoal powder, 5 to 8% of flavor powder, 3 to 5% of sodium nitrate, and 10 to 15% of water, stirring To form a dough (mixing and stirring the fragrance forming material: 17) and extrude the material of the mixed dough form so as to dry the moisture content of about 5% in an extruder to partially mold the semi-finished product firstly (extrusion step: 18). The mixture is press-molded the material (primary molded semi-finished product) formed in the extrusion step 18 in a forming mold having a predetermined shape to form a semi-finished fragrance tube 1 in the form of a cylindrical tube with its tip closed (press molding). Step 18a).

After forming the semi-finished product formed in the press molding step (18a) by primary curing drying (drying step: 19) in a drying furnace (19), the closed semi-finished product of the cured semi-finished product is cut into a cross shape to form an incision (2). Formation step: 20).

Then, charcoal dough is applied to the front end of the incense tube 1 having the cutout 2 formed at a predetermined thickness (charcoal dough dough applying step: 20a), and the natural herbal fragrance powder is coated on the entire circumference of the outer circumference. Powder coating step: 20b) to secondary curing drying (drying step: 20c) to complete the manufacture of the fragrance tube (1).

Thereafter, the assembly process 22 is made, and this assembly process 22 is completed after shaping the decorative core material 3 and the incense pipe 1, respectively, as described above, the charcoal dough (5) inside the incense pipe 1 The filling core (3) is inserted into the inside of the incense pipe (1) while filling the c) so that the incense pipe (1) and the decorative core material (3) can maintain a constant interval.

The incense pipe 1 inserted in the vertical direction so that the decorative core 3 in the vertical direction is installed vertically to the pedestal 7 to complete the production of incense.

Looking at the effects of the present invention configured as described above are as follows.

When the incense according to the present invention is placed on the altar and the fire is lit on the tip of the incense, the flame is burned while the charcoal dough coating layer 5a and the flavor powder coating layer la applied to the closed tip of the incense tube 1 are burned. Slowly ride down.

The fragrance powder of the fragrance powder coating gun 1a is a natural herbal fragrance powder, and when burned, it gives out a natural harbor.

When the charcoal dough coating layer (5a) and the fragrance powder coating layer (1a) is burned down so that both the charcoal powder dough coating layer (5a) is burned, the embers are burned while being transferred to the closed upper part of the incense pipe (1), Subsequently, the embers are delivered to the charcoal dough (5) inside the incense pipe (1) and burned down. In the process of burning the charcoal dough (5), the embers are transferred to the upper portion of the decorative heart material (3) and the decorative heartwood ( 3) will also ride down.

In the process of burning down the incense pipe (1), charcoal dough (5) and the decorative core material (3) as described above, the incense pipe (1) has a predetermined two while the main material is formed of paper material and burned down while burning When the ash is made of ash, the ash is cut in a cross shape by the tip of the incense tube 1, and the leaf 2 is opened and fallen as if the leaves of the petal are opened by the cutout 2.

Then, the charcoal dough (5) formed by kneading the charcoal powder is also burned by the embers and becomes a ash in the form of powder, which will fall down.

However, since the decorative core material (3) located inside the incense pipe (1) and charcoal dough (5) is formed of charcoal powder and calcined gypsum as the main material, the decorative core material (3) maintains its original form as charcoal even when the decorative core material (3) is burned. Done.

At this time, the decorative core material 3 is formed with a vent hole 4 in the vertical direction, and the decorative core material 3 communicates with the air vent hole 4 of the decorative core material 3 even in the pedestal 7 installed vertically. The vent hole 8 is formed so that the air is supplied through the vent holes 8 and 4 to facilitate the combustion of the decorative core 3.

And, the decorative core (3) is not easily broken even when burned like charcoal, but when the decorative core (3) is burned and exerts external force on the remaining ash, the ash remaining after the decorative core (3) is burned easily forms Will be lost.

In the upper portion of the incense according to the present invention is formed a position display portion 6 to indicate that the front of the decorative core is concealed inside the incense, the position display portion 6 to face in the case of incense at the altar If the incense is smoked in a standing state, the front of the decoration core material 3, such as Buddha statues are immediately visible when the shape of the inner decoration core material 3 appears while burning the incense.

As described above, the incense of the present invention is burnt from the top of the incense to the bottom of the incense, which is located on the outermost side of the incense, falling like a leaf of petals and falling down, and the charcoal powder filled between the incense and the decorative heartwood. The dough also becomes powdered ash and falls, but the decorative core installed vertically in the center is burned without breaking its original shape, but changes its color and burns in its original shape.

As described above, the outer incense tube is opened like a leaf of petals and falls off, and the decorative core material in the center is burned in its original shape without deteriorating its shape, thus creating a new style of incense, as well as a decoration that appears in the center. The shape of the heartwood is made into a sacred shape like a Buddha statue so that the sacrifice can be offered with a mysterious and godly heart.

Claims (2)

At the top of the pedestal (7), the incline tube seating groove (9) and the trough (10) are formed in two stages, and the trough (10) is at least one vent hole (8) facing outwards is formed radially, Ventilation holes (4) are formed in the pedestal (7) in the vertical direction, and the decorative core material (3) is formed vertically, which remains charcoal powder and calcined gypsum as the main material and remains intact even when burned. The inclined tube seating groove 9 on the outer side of the decorative core 3 is formed in the shape of a cylindrical tube in which the distal end is closed, and the distal end is cut in a cross shape to form an incision 2, and the charcoal dough coating layer 5a is distal to the distal end. ) Is coated, the fragrance powder coating layer (1a) is formed on the entire circumference of the outer circumferential surface, and the fragrance tube (1) is vertically installed, which is formed of a paper material main material and loses its shape when burned. Charcoal dough (5) is filled between the inner circumferential surface of the incense pipe (1) and the outer circumferential surface of the decorative heart material (3) to maintain a distance between the incense pipe (1) and the decorative heart material (3), the charcoal powder dough coating layer (5a) Incense is characterized in that the position display portion (6) is formed on the upper surface of the decorative core (3) indicating the front position. Charcoal powder 35-40%, plaster 30-25%, sodium nitrate 5-10%, flavor powder 3-5%, paper 3-5%, corn cooking oil 5-8%, water 20-30 Decorative material material mixing step (11) of mixing%, A stirring step 12 of adding 2 to 5% of the adhesive to the mixture mixed in the decorative material forming material mixing step 11 and stirring in a mixer to make a dough state; An extrusion step 13 of extruding the dough material prepared in the stirring step 12 in an extruder so that the moisture content is about 5%, and A press molding step 14 for press molding to a predetermined shape in a mold having a shape for molding the material molded in the extrusion step 13; The decorative core material forming process 16 is made as a drying step 15 for curing and drying the semi-finished product formed in the pressure forming step 14 in a drying furnace, Perfume mixing and stirring 70 to 80% of paper, 8 to 10% of wood powder, 3 to 6% of charcoal powder, 5 to 8% of flavor powder, 3 to 5% of sodium nitrate, and 10 to 15% of water Molding material mixing and stirring step (17), (18) extruding the mixed material prepared in the mixing and stirring step 17 of the fragrance forming material in an extruder so that the moisture content is about 5%; Press molding step (18a) to a predetermined shape in a molding mold having a shape for molding the material molded in the extrusion step 18, A drying step 19 of primary curing the semi-finished product formed in the pressing molding step 18a in a drying furnace; An incision forming step 20 of forming a cutout 2 by cutting the closed tip of the cured semifinished product in a cross shape; Charcoal powder dough coating step (20a) and flavor powder coating step (20b) and 2 for coating the flavor powder on the entire circumference of the outer circumferential surface after charting the charcoal dough in a predetermined thickness at the tip of the incense pipe (1) having the incision As the hardening drying (20c) step, the fragrance tube forming process 21 is made, Filling the charcoal dough (5) into the inside of the incense pipe (1) while inserting the formal core material (3), the incense pipe (1) in which the decorative core material (3) is inserted into the seating groove (9) of the pedestal (7) The installation method of incense, characterized in that made by the vertical installation (22) the incense is manufactured.