KR19990032549A - Gasoline Corrosion Test Apparatus for Automotive Surface Treated Steel Sheet - Google Patents
Gasoline Corrosion Test Apparatus for Automotive Surface Treated Steel Sheet Download PDFInfo
- Publication number
- KR19990032549A KR19990032549A KR1019970053613A KR19970053613A KR19990032549A KR 19990032549 A KR19990032549 A KR 19990032549A KR 1019970053613 A KR1019970053613 A KR 1019970053613A KR 19970053613 A KR19970053613 A KR 19970053613A KR 19990032549 A KR19990032549 A KR 19990032549A
- Authority
- KR
- South Korea
- Prior art keywords
- treated steel
- steel sheet
- test apparatus
- gasoline
- container
- Prior art date
Abstract
본 발명은 자동차용 표면 처리 강판의 내가솔린 부식성 시험 장치에 관한 것으로서, 연료 탱크의 재질인 표면 처리 강판의 내가솔린 부식성을 실제적으로 정확하게 판단할 수 있도록 상기 표면 처리 강판을 연료 탱크의 형상과 같은 형상으로 절곡 형성하여 시험함으로서, 표면 처리 강판의 내가솔린 부식성에 대한 정확한 시험치를 얻어낼 수 있도록 한 자동차용 표면 처리 강판의 내가솔린 부식성 시험 장치를 제공하고자 한 것이다.BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a gasoline corrosion test apparatus for automotive surface treated steel, wherein the surface treated steel sheet is shaped like the shape of a fuel tank so that the gasoline corrosion resistance of the surface treated steel sheet, which is a material of the fuel tank, can be accurately determined. It is an object of the present invention to provide a gasoline corrosion resistance test apparatus for automotive surface treated steel sheet which is capable of obtaining an accurate test value for the gasoline corrosion resistance of a surface treated steel sheet.
Description
본 발명은 자동차용 표면 처리 강판의 내가솔린 부식성 시험 장치에 관한 것으로서, 특히 자동차의 연료 탱크에 사용되는 표면 처리 강판을 연료 탱크의 형상으로 제작하여 시험할 수 있도록 한 자동차용 표면 처리 강판의 내가솔린 부식성 시험 장치에 관한 것이다.BACKGROUND OF THE INVENTION 1. Field of the Invention [0001] The present invention relates to a gasoline corrosion resistance test apparatus for automotive surface treatment steels. In particular, the present invention relates to a gasoline resistance test for automotive surface treatment steel sheet, in which a surface treatment steel sheet used for a fuel tank of an automobile can be manufactured and tested in the shape of a fuel tank. Corrosion test apparatus.
통상적으로 자동차의 연료 탱크에는 연료로서 가솔린이 채워지게 되는 바, 상기 연료탱크는 표면 처리 강판으로 사용하게 된다.Typically, a fuel tank of an automobile is filled with gasoline as fuel, and the fuel tank is used as a surface-treated steel sheet.
따라서 상기 연료 탱크의 재질로서 사용되는 표면 처리 강판에 대한 내가솔린 부식성을 시험하게 된다.Therefore, the resistance to gasoline resistance to the surface-treated steel sheet used as the material of the fuel tank is tested.
첨부한 도 2는 종래의 자동차용 표면 처리 강판의 내가솔린 부식성 시험 장치의 사용 상태를 나타내는 개략도로서, 상기 시험 장치(10b)에는 좌우로 요동되는 지그(12)면 위에 원통(28)이 부착되어 있다.2 is a schematic view showing a state of use of a gasoline corrosion resistance test apparatus of a conventional automotive surface-treated steel sheet, wherein the test apparatus 10b has a cylinder 28 attached to a jig 12 surface that swings from side to side. have.
따라서 원통(28) 내부에 가솔린과 염화나트륨이 혼합된 액체를 일정량 채우는 동시에 시편(26) 즉, 시험용 표면 처리 강판 조각을 혼합 액체에 넣은 후, 원통(28)을 밀폐한다.Therefore, while filling a predetermined amount of liquid mixed with gasoline and sodium chloride in the cylinder 28, the specimen 26, that is, a test surface-treated steel sheet piece is put into the mixed liquid, and then the cylinder 28 is sealed.
이어서 상기 시험 장치(10b)의 지그(12)를 좌우로 요동시켜 상기 시편(26)의 부식성 여부를 시험하게 된다.Then, the jig 12 of the test apparatus 10b is swung left and right to test whether the specimen 26 is corrosive.
그러나 상기 종래의 시험 장치(10b)는 시편(26)이 평판 형태로 절단된 조각이기 때문에 실제의 연료 탱크의 형상에는 맞지 않아 내가솔린 부식성 시험치의 정확성이 떨어지는 단점이 있다.However, since the conventional test apparatus 10b is a piece in which the specimen 26 is cut into a flat plate shape, the test device 10b does not fit the shape of the actual fuel tank, and thus, the accuracy of the resistance test value of the gasoline resistance is poor.
본 발명은 상기와 같은 단점을 감안하여 안출한 것으로서, 연료 탱크의 재질인 표면 처리 강판의 내가솔린 부식성을 실제적으로 정확하게 판단할 수 있도록 상기 표면 처리 강판을 연료 탱크의 형상과 같은 형상으로 절곡 형성하여 시험함으로서, 표면 처리 강판의 내가솔린 부식성에 대한 정확한 시험치를 얻어낼 수 있도록 한 자동차용 표면 처리 강판의 내가솔린 부식성 시험 장치를 제공하는데 그 목적이 있는 것이다.The present invention has been made in view of the above disadvantages, by forming the surface-treated steel sheet bent in the same shape as the shape of the fuel tank so as to accurately determine the gasoline corrosion resistance of the surface-treated steel sheet which is the material of the fuel tank It is an object of the present invention to provide a gasoline corrosion resistance test apparatus for automotive surface treated steel sheet which is capable of obtaining an accurate test value for the gasoline corrosion resistance of a surface treated steel sheet.
도 1은 본 발명에 따른 자동차용 표면 처리 강판의 내가솔린 부식성 시험 장치의 사용 상태를 나타내는 개략도,1 is a schematic view showing a state of use of the gasoline corrosion resistance test apparatus for automotive surface treatment steel sheet according to the present invention,
도 2는 종래의 자동차용 표면 처리 강판의 내가솔린 부식성 시험 장치의 사용 상태를 나타내는 개략도.2 is a schematic view showing a state of use of a gasoline corrosion resistance test apparatus of a conventional automotive surface treated steel sheet.
<도면의 주요 부분에 대한 부호의 설명><Explanation of symbols for main parts of the drawings>
10a,10b:시험 장치 12:지그10a, 10b: Test apparatus 12: Jig
14:용기 16:상부 패널14: Container 16: upper panel
18:테두리단 20:시험 용액18: Border 20: Test solution
22:볼트 24:실링22: Bolt 24: Shilling
26:시편 28:원통Psalm 28: Psalm 28
30:오목구 32:홈30: concave ball 32: home
이하 첨부 도면을 참조하여 본 발명을 상세히 설명하면 다음과 같다.Hereinafter, the present invention will be described in detail with reference to the accompanying drawings.
본 발명의 자동차용 표면 처리 강판의 내가솔린 부식성 시험 장치는 상기 시험 장치(10a)의 좌우 요동되는 지그(12)면에 상부면이 일정 깊이로 함몰된 오목구(30)를 갖는 사각체를 부착하고, 상기 오목구(30)에 상부 둘레에 테두리단(18)이 일체로 된 표면 처리 강판재의 용기(14)를 삽입하며, 상기 용기(14)의 개방부를 포함하는 상기 사각체의 상부면에 표면 처리 강판재의 상부 패널(16)을 볼트(22)로 체결하며, 상기 상부 패널(16)과 용기(14)의 테두리단(18) 끝단을 실링(24)하여서, 상기 용기(14) 내부에 시험용액을 채우는 동시에 상기 지그(12)를 좌우로 요동시켜서 이루어지는 것을 특징으로 한다.The gasoline corrosion test apparatus of the automotive surface-treated steel sheet of the present invention attaches a rectangular body having a concave hole 30 having an upper surface recessed to a predetermined depth on the jig 12 surface of the test apparatus 10a. And inserting the container 14 of the surface-treated steel sheet in which the edge end 18 is integrally formed around the upper part of the recess 30, and on the upper surface of the quadrangular body including the opening of the container 14. The upper panel 16 of the surface-treated steel sheet is fastened with bolts 22, and the upper panel 16 and the edge of the edge 18 of the container 14 are sealed 24 so that the inside of the container 14 is sealed. It is characterized in that it is made by rocking the jig 12 from side to side while filling the test solution.
특히 상기 상부 패널(16)의 일정 부위에는 시험용액(20)을 투입하는 홈(32)이 형성되고, 시험 용액(20) 투입후에는 실링(24)하는 것을 특징으로 한다.In particular, the groove 32 for introducing the test solution 20 is formed in a predetermined portion of the upper panel 16, and after the test solution 20 is injected, it is characterized in that the sealing 24.
본 발명을 좀 더 상세히 설명하면 다음과 같다.The present invention is described in more detail as follows.
첨부한 도 1은 본 발명에 따른 자동차용 표면 처리 강판의 내가솔린 부식성 시험 장치의 사용 상태를 나타내는 개략도로서, 도면 부호 10a는 표면 처리 강판의 내가솔린 부식성 시험 장치이다.1 is a schematic diagram showing the state of use of the gasoline corrosion resistance test apparatus for automotive surface-treated steel sheet according to the present invention, wherein reference numeral 10a denotes the gasoline corrosion resistance test apparatus for a surface-treated steel sheet.
상기 시험 장치(10a)는 좌우로 요동되는 지그(12)면을 포함한다.The test apparatus 10a includes a jig 12 surface that swings from side to side.
여기서 상기 지그(12)면에 상부면에 일정 깊이로 함몰된 오목구(30)를 갖는 사각체를 부착한다.The jig 12 is attached to the square body having a concave hole 30 recessed in a predetermined depth on the upper surface.
또한 표면 처리 강재로서, 상부 둘레에 테두리단(18)을 가지는 용기(14)를 구비하여 상기 오목구(30)에 삽입한다.Moreover, it is a surface-treated steel material, Comprising: The container 14 which has the edge end 18 in the upper periphery is inserted in the said recess 30.
또한 상기 용기(14)를 포함하는 사각체의 상부면에 평판 형태인 표면 처리 강판재의 상부 패널(16)을 덮어 각 끝단을 상기 사각체에 볼트(22)를 사용하여 고정시킨다.Further, the upper panel 16 of the surface-treated steel sheet in the form of a plate is covered on the upper surface of the rectangular body including the container 14 to fix each end to the rectangular body using the bolts 22.
이때 상기 용기(14)의 테두리단(18)과 상부 패널(16)은 밀착된 상태인 바, 상기 테두리단(18)의 끝부분과 상기 상부 패널(16) 사이의 기밀을 유지하기 위하여 실링(24)을 한다.In this case, the edge 18 and the upper panel 16 of the container 14 are in close contact with each other, and a seal is formed to maintain the airtightness between the end of the edge 18 and the upper panel 16. 24).
한편 상기 상부 패널(16)의 일정 부위에는 상기 용기(14) 내부에 시험 용액(20)을 투입하기 위한 홈(32)이 형성된다.On the other hand, a predetermined portion of the upper panel 16 is formed with a groove 32 for introducing the test solution 20 into the container 14.
따라서 상기 홈(32)을 통하여 예를들어 주사기와 같은 도구를 사용하여 용기(14) 내부에 시험용액(20)을 투입한다.Therefore, the test solution 20 is introduced into the container 14 through the groove 32 using a tool such as a syringe.
상기 용기(14) 내부에 시험용액(20)이 일정량 채워진 후, 상기 홈(32)을 실링(24)한다.After the test solution 20 is filled in the container 14 with a predetermined amount, the groove 32 is sealed 24.
이에 따라 상기 시험 장치(10a)의 지그(12)면을 좌우로 요동시키며 시험을 하게 된다.Accordingly, the jig 12 surface of the test apparatus 10a is rocked from side to side to perform a test.
좀 더 상세하게는 상기 용기(14)와 상부 패널(16)은 표면 처리 강판재이고, 실제적인 연료 탱크의 형상과 같기 때문에 정확한 시험 결과를 얻어낼 수 있다.More specifically, the vessel 14 and the top panel 16 are surface-treated steel sheets, and because they are the same as the shape of the actual fuel tank, accurate test results can be obtained.
상술한 바와 같이 본 발명에 따른 자동차용 표면 처리 강판의 내가솔린 부식성 시험 장치에 의하면 연료 탱크의 소재인 표면 처리 강판을 실제적인 연료 탱크의 형상에 맞게 형성하여 내가솔린 부식성 시험을 함으로서, 보다 정확한 내가솔린 부식성을 판단할 수 있는 장점이 있다.As described above, according to the gasoline corrosion resistance test apparatus for automotive surface treatment steel sheets according to the present invention, the surface treatment steel sheet, which is the material of a fuel tank, is formed to match the shape of an actual fuel tank, thereby performing the gasoline corrosion resistance test. There is an advantage to determine the gasoline corrosion.
Claims (2)