KR102642006B1 - Adhesive brassiere with improved fit and coverage and method for manufacturing the same - Google Patents
Adhesive brassiere with improved fit and coverage and method for manufacturing the same Download PDFInfo
- Publication number
- KR102642006B1 KR102642006B1 KR1020230001228A KR20230001228A KR102642006B1 KR 102642006 B1 KR102642006 B1 KR 102642006B1 KR 1020230001228 A KR1020230001228 A KR 1020230001228A KR 20230001228 A KR20230001228 A KR 20230001228A KR 102642006 B1 KR102642006 B1 KR 102642006B1
- Authority
- KR
- South Korea
- Prior art keywords
- adhesive
- silicone
- molded body
- bra
- adhesive bra
- Prior art date
Abstract
본 발명은 피부에 부착하여 사용하는 점착식 브라 본체를 제조하기 위한 실리콘 조성물로서, 실리콘 고무 60 내지 75 중량%, 세라믹 분말 20 내지 40 중량% 및 실리콘 오일 3 내지 5 중량%를 포함하는 실리콘 조성물, 이를 이용한 점착식 브라 성형체 및 점착식 브라의 제조방법에 관한 것이다.The present invention is a silicone composition for manufacturing an adhesive bra body used by attaching to the skin, comprising 60 to 75% by weight of silicone rubber, 20 to 40% by weight of ceramic powder, and 3 to 5% by weight of silicone oil, It relates to an adhesive bra molded body and a method of manufacturing an adhesive bra using this.
Description
본 발명은 인체 무해한 소재를 활용하되, 밀착력이 우수하면서도, 커버력이 우수하며, 사용감이 우수한 효과를 가지는 점착식 브라용 실리콘 조성물, 이를 이용한 점착식 브라용 성형체 및 점착식 브라의 제조방법에 관한 것이다.The present invention relates to a silicone composition for an adhesive bra that utilizes a material harmless to the human body and has excellent adhesion, excellent coverage, and excellent feeling of use, a molded body for an adhesive bra using the same, and a method of manufacturing an adhesive bra. .
브래지어는 여성의 가슴을 받쳐주고 감싸주는 속옷으로서, 가슴의 모양을 내거나, 가슴의 결점을 보완하여 겉옷의 라인을 아름답게 해주는 등의 다양한 부가 기능을 위해 착용하는 속옷이다.Bras are underwear that supports and covers a woman's breasts and is worn for various additional functions, such as shaping the breasts or making up for imperfections in the breasts to beautify the lines of outerwear.
브래지어의 기본 형태는 돌출된 가슴 부분을 감싸는 패드, 패드로부터 연장되어 겨드랑이 아래부분으로 감싸지는 밴드 부분과 어깨를 가로 질러 신체 앞부분의 패드와 신체 뒷부분의 밴드를 연결하는 어깨끈으로 구성된다.The basic form of a bra consists of a pad that covers the protruding chest, a band extending from the pad and wrapping around the lower armpits, and shoulder straps that connect the pad at the front of the body and the band at the back of the body across the shoulders.
최근에는 브래지어의 착용이 신체를 결박하여 혈액순환을 원활하지 않게 하거나, 어깨 일부에 착색을 유발하는 문제 내지는 피부가 예민한 여성들에게서 불필요한 피부 트러블을 유발하는 등의 문제로 인하여, 브래지어를 대체하거나 브래지어를 착용하지 않는 경향이 증가하고 있다.Recently, due to problems such as wearing a bra binding the body and impeding blood circulation, causing discoloration of some parts of the shoulders, or causing unnecessary skin troubles in women with sensitive skin, bras have been replaced or worn. The tendency not to wear them is increasing.
더욱이, 민소매나 어깨끈이 부착된 원피스나 점프 수트, 오프 숄더 타입의 의류 등의 다양한 형태의 의복이 디자인됨에 따라, 전형적이고 전통적이 형태의 브래지어 착용이 어려운 상황이 증가하게 되어, 브래지어를 착용하지 않거나, 이를 대체할 수 있는 간단한 형태의 브래지어 내지는 대체품의 개발이 활발하게 진행되고 있다.Moreover, as various types of clothing such as sleeveless or shoulder strap dresses, jumpsuits, and off-shoulder type clothing are designed, situations in which it is difficult to wear a typical and traditional type of bra are increasing, making it difficult to wear a bra. The development of simple bras or substitute products that can replace them is actively underway.
브래지어의 대체품으로 가장 활발하게 소비되고 있는 대체품으로는, 점착식 브래지어, 끈없는 브래지어 및 니플 패치 등이 있다.The most actively consumed substitutes for bras include adhesive bras, strapless bras, and nipple patches.
다만, 점착식 브래지어나 니플 패치와 같이 피부에 직접 부착하는 형태의 대체품은 점착성의 수단이 피부에 직접 접촉하게 된다는 점에서, 점착과 탈착 시 피부 자극을 유발할 수 있고, 가슴에 부착된 상태로 장시간 활동하게 됨에 따라, 사람에 따라서는 피부 발진이나, 통증 등을 유발할 수 있는 문제가 있다.However, replacement products that are attached directly to the skin, such as adhesive bras or nipple patches, can cause skin irritation when attached and detached because the adhesive means comes into direct contact with the skin, and can cause skin irritation when attached and detached for a long period of time while attached to the chest. As people become more active, some people may experience problems such as skin rashes or pain.
또한, 점착 수단이 피부에 직접 부착되어 있으므로, 땀이 나거나, 피부에서 분비되는 피지나 각질 등의 물질로 인하여 점착 수단의 점착성이 초기 대비 빠르게 저감될 수 있는 문제, 저온이나 고온의 상황에서 형상이 변형되거나 점착성이 저하되는 등의 문제가 발생될 수 있어 사용 시의 신뢰성을 보전하는 것 또한 중요하다.In addition, since the adhesive means is directly attached to the skin, the adhesiveness of the adhesive means may quickly decrease compared to the initial period due to sweat or substances such as sebum or dead skin cells secreted from the skin, and the shape may change in low or high temperature situations. It is also important to preserve reliability during use as problems such as deformation or reduced adhesion may occur.
대한민국 등록특허 제2333740호는 남성용 니플 패치에 관한 것으로서, 거미줄구조를 갖는 스파이더필름을 사용해 유두의 커버력을 높이고, 마감필름을 통해 유두의 커버력을 극대화하고, 부드러운 촉감과 자유로운 움직임을 제공하는 니플 패치에 관한 것이다.Republic of Korea Patent No. 2333740 relates to a nipple patch for men. It uses a spider film with a spider web structure to increase nipple coverage, maximizes nipple coverage through a finishing film, and provides a soft feel and free movement to the nipple patch. It's about.
다만, 상기 특허는 여성의 가슴에 사용하기에 탁월한 밀착력과 커버력을 갖는 여성용 점착식 브라에 대해서는 개시하고 있지 않다.However, the patent does not disclose an adhesive bra for women that has excellent adhesion and coverage for use on women's breasts.
대한민국 등록특허 제2426039호는 유두와 그 주변 피부에 점착되는 점착층을 갖는 점착시트, 상기 점착시트의 외면에 부착되고, 매쉬구조의 원단을 사용하여 유두의 누름기능을 강화하는 커버시트, 상기 커버시트의 외면에 부착되고, 신축성을 갖는 엘라스토머시트를 포함하는 유두커버패드에 관한 것이다.Republic of Korea Patent No. 2426039 is an adhesive sheet having an adhesive layer that adheres to the nipple and the surrounding skin, a cover sheet attached to the outer surface of the adhesive sheet and using a fabric with a mesh structure to strengthen the pressing function of the nipple, and the cover. It relates to a nipple cover pad that is attached to the outer surface of the sheet and includes an elastic elastomer sheet.
다만, 상기 특허는 여성의 가슴에 사용하기에 탁월한 밀착력과 커버력을 갖는 여성용 점착식 브라에 대해서는 개시하고 있지 않다.However, the patent does not disclose an adhesive bra for women that has excellent adhesion and coverage for use on women's breasts.
이와 같이, 여성의 가슴에 부착하여 사용하여도 사용감이 우수하고 인체에 무해한 특성을 가지며, 밀착력과 커버력이 우수한 점착식 브라에 대한 개발이 필요한 실정이다.In this way, there is a need to develop an adhesive bra that has excellent usability and is harmless to the human body even when attached to a woman's breast, and has excellent adhesion and coverage.
본 발명은 상기와 같은 종래 기술의 문제를 해결하기 위한 것으로, 인체 무해한 소재를 활용하되, 밀착력이 우수하면서도, 커버력이 우수한 점착식 브라를 제조할 수 있는 실리콘 조성물, 이를 이용한 점착식 브라용 성형체 및 점착식 브라의 제조방법을 제공하는 것을 목적으로 한다.The present invention is intended to solve the problems of the prior art as described above, and includes a silicone composition capable of producing an adhesive bra with excellent adhesion and coverage using materials harmless to the human body, a molded body for an adhesive bra using the same, and The purpose is to provide a method for manufacturing an adhesive bra.
본 발명은 또한, 착용 후 피부과 같은 촉감을 제공하며, 부착, 탈착 시 피부에 자극을 유발하지 않는 실리콘 조성물, 이를 이용한 점착식 브라용 성형체 및 점착식 브라의 제조방법을 제공하는 것을 목적으로 한다.Another object of the present invention is to provide a silicone composition that provides a skin-like feel after wearing and does not cause skin irritation when attached or detached, a molded body for an adhesive bra using the same, and a method of manufacturing an adhesive bra.
본 발명은 기온이 낮은 겨울 등의 저온의 환경에서도 우수한 밀착력을 갖는 실리콘 조성물, 이를 이용한 점착식 브라용 성형체 및 점착식 브라의 제조방법을 제공하는 것을 목적으로 한다.The purpose of the present invention is to provide a silicone composition that has excellent adhesion even in low-temperature environments such as winter, a molded body for an adhesive bra using the same, and a method for manufacturing an adhesive bra.
상술한 과제를 해결하기 위한 본 발명에 따른 점착식 브라용 실리콘 조성물은, 피부에 부착하여 사용하는 점착식 브라 본체를 제조하기 위한 실리콘 조성물로서, 실리콘 고무 60 내지 75 중량%, 세라믹 분말 20 내지 40 중량% 및 실리콘 오일 3 내지 5 중량%를 포함한다.The silicone composition for an adhesive bra according to the present invention to solve the above-mentioned problems is a silicone composition for manufacturing an adhesive bra body used by attaching to the skin, and includes 60 to 75% by weight of silicone rubber and 20 to 40% of ceramic powder. % by weight and 3 to 5% by weight silicone oil.
본 발명에 있어서, 상기 실리콘 고무는 메틸비닐폴리실록산(Methyl vinyl polysiloxane)이고, 상기 세라믹 분말은 화이트 카본 블랙(White carbon black)이고, 상기 실리콘 오일은 수산화 실리콘 오일(Hydroxy silicone oil)일 수 있다.In the present invention, the silicone rubber may be methyl vinyl polysiloxane, the ceramic powder may be white carbon black, and the silicone oil may be hydroxy silicone oil.
본 발명에 있어서, 상기 실리콘 조성물은 점착 보조 복합체를 더 포함하고, 상기 점착 보조 복합체는, 다수의 포어가 표면에 형성된 메틸비닐폴리실록산을 포함하는 다공성 필라멘트 및 상기 다수의 포어에 담지된 실리콘 오일을 포함할 수 있다.In the present invention, the silicone composition further includes an adhesion auxiliary composite, and the adhesive auxiliary composite includes a porous filament containing methylvinylpolysiloxane with a plurality of pores formed on the surface and silicone oil supported on the plurality of pores. can do.
본 발명은 또한, 상술한 실리콘 조성물로 제조된 점착식 브라용 성형체로서, 상기 성형체는 돌출된 전면과 피부와 접촉하는 함몰된 배면으로 이루어지며 구의 일부와 같은 형태를 갖는 점착식 브라용 성형체를 제공한다.The present invention also provides a molded body for an adhesive bra made from the above-described silicone composition, wherein the molded body has a protruding front surface and a depressed back surface in contact with the skin and has a shape like a part of a sphere. do.
본 발명은 또한, 상술한 점착식 브라용 성형체를 포함하는 점착식 브라로서, 점착식 브라용 성형체의 함몰된 배면의 표면에는 실리콘 점착제가 도포된 점착식 브라를 제공한다.The present invention also provides an adhesive bra including the above-described molded body for an adhesive bra, wherein a silicone adhesive is applied to the recessed back surface of the molded body for an adhesive bra.
보다 상세하게는, 상기 실리콘 점착제는, 실리콘 비닐 폴리머 점착제 및 디오가노폴리실록산 점착제로 이루어진 군에서 선택된 어느 하나일 수 있다.More specifically, the silicone adhesive may be any one selected from the group consisting of silicone vinyl polymer adhesives and diorganopolysiloxane adhesives.
보다 상세하게는, 상기 실리콘 점착제는, 0.3 내지 0.7 mm의 두께로 도포된 것일 수 있다.More specifically, the silicone adhesive may be applied to a thickness of 0.3 to 0.7 mm.
본 발명은 또한, 점착식 브라의 제조방법으로서, a) 실리콘 조성물을 몰드에 넣고 프레스 가공하여 점착식 브라용 성형체를 제조하는 단계 및 b) 상기 점착식 브라용 성형체의 일면에 실리콘 점착제를 도포하는 단계를 포함하는 점착식 브라의 제조방법을 제공한다.The present invention also provides a method for manufacturing an adhesive bra, comprising: a) putting a silicone composition into a mold and press-processing it to produce a molded body for an adhesive bra; and b) applying a silicone adhesive to one side of the molded body for an adhesive bra. A method for manufacturing an adhesive bra comprising the following steps is provided.
상세하게는, 상기 a) 단계는, a-1) 점착 보조 복합체를 제조하는 단계, a-2) 상기 점착 보조 복합체와 실리콘 고무, 세라믹 분말 및 실리콘 오일을 혼합하여 실리콘 조성물을 제조하는 단계, a-3) 실리콘 조성물을 몰드에 넣고 프레스 가공하여 점착식 브라용 성형체를 제조하는 단계를 포함할 수 있다.Specifically, step a) includes a-1) preparing an adhesion auxiliary composite, a-2) mixing the adhesion auxiliary composite with silicone rubber, ceramic powder, and silicone oil to prepare a silicone composition, a -3) It may include the step of manufacturing a molded body for an adhesive bra by putting the silicone composition into a mold and press processing it.
상세하게는, 상기 점착식 브라용 성형체는 돌출된 전면과 피부와 접촉하는 함몰된 배면을 포함하고, 상기 b) 단계는, 상기 함몰된 배면의 표면에 320 내지 330nm 파장의 자외선을 30초간 조사한 후, 암실에서 1분간 휴지시킨 후, 표면에 실리콘 점착제를 도포하는 것일 수 있다.In detail, the adhesive bra molded body includes a protruding front surface and a recessed back surface in contact with the skin, and step b) is performed by irradiating ultraviolet rays with a wavelength of 320 to 330 nm for 30 seconds on the surface of the recessed back surface. , it can be left to rest for 1 minute in a dark room, and then a silicone adhesive can be applied to the surface.
본 발명에 따른 점착식 브라는, 인체 무해하며, 밀착력과 커버력이 우수한 효과를 갖는다.The adhesive bra according to the present invention is harmless to the human body and has excellent adhesion and coverage.
본 발명에 따른 점착식 브라는, 착용 후 피부과 같은 촉감을 제공하며, 부착, 탈착 시 피부에 자극을 유발하지 않는 효과를 갖는다.The adhesive bra according to the present invention provides a skin-like feel after wearing and has the effect of not causing irritation to the skin when attached or detached.
본 발명에 따른 점착식 브라는, 기온이 낮은 겨울 등의 저온의 환경에서도 우수한 밀착력을 갖는다.The adhesive bra according to the present invention has excellent adhesion even in low-temperature environments such as winter.
도 1은 본 발명의 일 실시예에 따른 점착식 브라의 수직 단면도이다.
도 2는 본 발명의 일 실시예에 따른 점착식 브라용 성형체의 전면을 촬영한 사진이다.
도 3은 본 발명의 일 실시예에 따른 점착식 브라용 성형체의 배면을 촬영한 사진이다.
도 4는 본 발명의 일 실시예에 따른 점착식 브라를 착용한 상태를 도식화한 도면이다.
도 5는 본 발명의 일 실시예에 따른 점착식 브라의 제조방법을 나타낸 공정 순서도이다.
도 6은 본 발명의 일 실시예에 따른 점착식 브라의 제조방법 중 a) 단계의 세부 공정을 나타낸 공정 순서도이다.
도 7은 본 발명의 일 실시예에 따른 점착식 브라용 성형체를 제조하기 위한 몰드 형상이다.
도 8 내지 도 10은 본 발명의 일 실시예에 따른 점착식 브라용 성형체의 제조과정을 나타낸 도면이다.
도 11은 실시예와 참고예의 밀착력 시험 사진이다.
도 12는 실시예와 참고예의 커버력 시험 사진이다.
도 13은 실시예의 인체적용시험 확인서이다.1 is a vertical cross-sectional view of an adhesive bra according to an embodiment of the present invention.
Figure 2 is a photograph of the front of a molded body for an adhesive bra according to an embodiment of the present invention.
Figure 3 is a photograph of the back of a molded body for an adhesive bra according to an embodiment of the present invention.
Figure 4 is a diagram illustrating a state in which an adhesive bra according to an embodiment of the present invention is worn.
Figure 5 is a process flow chart showing a method of manufacturing an adhesive bra according to an embodiment of the present invention.
Figure 6 is a process flow chart showing the detailed process of step a) in the method of manufacturing an adhesive bra according to an embodiment of the present invention.
Figure 7 is a mold shape for manufacturing a molded body for an adhesive bra according to an embodiment of the present invention.
Figures 8 to 10 are views showing the manufacturing process of a molded body for an adhesive bra according to an embodiment of the present invention.
Figure 11 is a photograph of an adhesion test of an example and a reference example.
Figure 12 is a photograph of the covering power test of examples and reference examples.
Figure 13 is a human application test confirmation of the example.
이하, 본 발명이 속하는 기술 분야에서 통상의 지식을 가진 자가 용이하게 실시할 수 있도록 본 발명의 각 구성을 보다 상세히 설명하나, 이는 하나의 예시에 불과할 뿐, 본 발명의 권리범위가 다음 내용에 의해 제한되지 아니한다.Hereinafter, each configuration of the present invention will be described in more detail so that those skilled in the art can easily implement it. However, this is only an example, and the scope of rights of the present invention is determined by the following contents. Not limited.
본 발명에 사용된 "바람직한" 또는 "바람직하게는"은 특정 조건에서 특정 장점을 갖는 본 발명의 실시예를 나타낸다. 그러나, 다른 실시예 또한 동일 조건 또는 다른 조건에서 바람직할 수 있다. 또한, 하나 이상의 바람직한 실시예는 다른 실시예가 유용하지 않다는 것을 의미하는 것은 아니며, 본 발명의 범위 내에 있는 다른 실시예를 배제하는 것도 아니다.As used herein, “preferred” or “preferably” refers to an embodiment of the invention that has certain advantages under certain conditions. However, other embodiments may also be preferred under the same or different conditions. Additionally, the identification of one or more preferred embodiments does not mean that other embodiments are not useful, nor does it exclude other embodiments that are within the scope of the invention.
본 명세서에 사용된 "포함한다"는 용어는 본 발명에 유용한 재료, 조성물, 장치, 및 방법들을 나열할 때 사용되며 그 나열된 예에 제한되는 것은 아니다.As used herein, the term “comprising” is used to list materials, compositions, devices, and methods useful in the present invention and is not limited to the listed examples.
이하에서는, 본 발명은, 피부에 부착하여 사용하는 점착식 브라 본체를 제조하기 위한 실리콘 조성물로서, 실리콘 고무 60 내지 75 중량%, 세라믹 분말 20 내지 40 중량% 및 실리콘 오일 3 내지 5 중량%를 포함하는 실리콘 조성물, 이를 이용한 점착식 브라용 성형체 및 점착식 브라의 제조방법에 관한 것이다.Hereinafter, the present invention is a silicone composition for manufacturing an adhesive bra body used by attaching to the skin, comprising 60 to 75% by weight of silicone rubber, 20 to 40% by weight of ceramic powder, and 3 to 5% by weight of silicone oil. It relates to a silicone composition, a molded body for an adhesive bra using the same, and a method of manufacturing an adhesive bra.
상술한 실리콘 조성물을 사용하여 제조된 점착식 브라용 성형체는, 다양한 모양의 여성 가슴에 부착하여도 밀착력이 우수한 특성을 가지며, 착용 후 육안으로 관찰하여도 착용한 티가 나지 않는 우수한 커버력을 가지며, 피부색과 유사한 색상을 가져, 흰 티 등의 하얀색 옷을 입은 상태에서도 비침이 없는 우수한 커버력을 갖는다.The molded body for an adhesive bra manufactured using the above-mentioned silicone composition has excellent adhesion properties even when attached to female breasts of various shapes, and has excellent covering power so that it is not noticeable even when observed with the naked eye after wearing, It has a color similar to skin color and has excellent coverage without being transparent even when wearing white clothes such as a white T-shirt.
이하에서는, 본 발명의 구성을 보다 자세히 설명한다.Below, the configuration of the present invention will be described in more detail.
1. 실리콘 조성물1. Silicone composition
본 발명에 따른 점착식 브라용 실리콘 조성물은 일반적인 브래지어의 패드부분에 해당되는 부분의 컵을 이루는 가장 메인 본체에 해당되는 부분을 제조하기 위한 조성물이다.The silicone composition for an adhesive bra according to the present invention is a composition for manufacturing the main body of the cup of the pad portion of a typical bra.
구체적으로, 상기 실리콘 조성물의 전체 중량을 기준으로, 실리콘 고무 60 내지 75 중량%, 세라믹 분말 20 내지 40 중량% 및 실리콘 오일 3 내지 5 중량%를 포함한다.Specifically, based on the total weight of the silicone composition, it includes 60 to 75% by weight of silicone rubber, 20 to 40% by weight of ceramic powder, and 3 to 5% by weight of silicone oil.
실리콘 고무는 규소, 산소 결합을 기본 사슬로 하는 고분자 화합물로서, 기본적으로 유연성을 가지며, 분자량이나 첨가제의 유무에 따라 유동성을 가지거나, 일정한 경도를 가져, 특정 형상으로 성형이 가능하고, 탄성을 갖는 고무와 같은 특성을 갖는다.Silicone rubber is a polymer compound with silicon and oxygen bonds as its basic chain. It is basically flexible and has fluidity depending on molecular weight or the presence or absence of additives, or has a certain hardness, can be molded into a specific shape, and has elasticity. It has rubber-like properties.
상기 실리콘 고무는 피부에 직접 접촉하는 특성을 고려하여, 인체에 무해한 실리콘 고무를 사용하는 것이 바람직하며, 의료용이나 식품 보관/포장 용도로 사용되는 실리콘 고무와 같은 인체 무해한 실리콘 고무를 사용하는 것이 바람직하다.Considering the nature of the silicone rubber that comes in direct contact with the skin, it is desirable to use silicone rubber that is harmless to the human body, and it is desirable to use silicone rubber that is harmless to the human body, such as silicone rubber used for medical or food storage/packaging purposes. .
인체 무해하며, 점착식 브라에 사용하기 적합한 특성을 갖는 것이면 어떠한 것이든 사용이 가능하나, 바람직하게는, 메틸비닐폴리실록산을 사용할 수 있다.Any material can be used as long as it is harmless to the human body and has properties suitable for use in an adhesive bra. Preferably, methylvinylpolysiloxane can be used.
상기 실리콘 고무는 상기 함량범위로 첨가되는 것이 바람직하며, 상기 함량보다 과량으로 첨가되는 경우에는, 상대적으로 세라믹 분말의 함량이 적어지게 되어 착용 시의 커버력이 저하되는 문제가 있고, 유연성/유동성의 증가로 인하여, 사용감이 저하되는 문제가 있고, 상기 함량보다 소량으로 첨가되는 경우에는, 상대적으로 세라믹 분말의 함량이 증가됨에 따라, 몰드에 넣어 프레스 가공하기 어렵거나, 조성물 상태에서 점도가 높고 유동성이 떨어지는 문제가 있다.It is preferable that the silicone rubber is added in the above content range, and if it is added in excess than the above content, the content of ceramic powder becomes relatively small, which causes the problem of lowering the covering power when worn and increasing flexibility/liquidity. Due to this, there is a problem that the feeling of use is reduced, and when it is added in a smaller amount than the above content, as the content of ceramic powder increases, it is difficult to press it into a mold or the composition has high viscosity and poor fluidity. there is a problem.
세라믹 분말은 무기 소재의 분말 성분으로서, 바람직하게는, 백색이나 미색의 세라믹 분말을 사용할 수 있다.Ceramic powder is a powder component of an inorganic material. Preferably, white or off-white ceramic powder can be used.
피부색과 유사하게 형성할 수 있으며, 인체 무해한 성분이라면 특별히 제한되지 않고 사용이 가능하나, 바람직하게는, 콜로이달 실리카로서, 화이트 카본 블랙 등을 사용할 수 있다.It can be formed similar to skin color, and can be used without particular restrictions as long as it is a harmless ingredient to the human body. Preferably, colloidal silica, such as white carbon black, can be used.
상기 세라믹 분말 20 내지 40 중량%로 포함될 수 있고, 상기 함량보다 과량으로 첨가되는 경우에는, 실리콘 조성물의 점도가 증가하여 컵 형상의 몰드에 넣어 제조하기 어렵거나, 제조하더라도 결합이 많이 형성되는 문제가 있다. 상기 함량보다 소량으로 첨가되는 경우에는, 착용 시의 커버력이 저하되는 문제가 있다.The ceramic powder may be included in an amount of 20 to 40% by weight, and if it is added in excess of the above content, the viscosity of the silicone composition increases, making it difficult to manufacture it by placing it in a cup-shaped mold, or even if it is manufactured, there is a problem that many bonds are formed. there is. If it is added in a smaller amount than the above amount, there is a problem that the covering power when worn is reduced.
실리콘 오일은 실리콘 폴리머 중에서 상대적으로 저분자량을 가져 액체와 같은 높은 유동성을 갖는 폴리머 화합물이다. 실리콘 오일은 실리콘 수지를 활용한 다양한 제품의 제조 시 내지는 실리콘 성형체를 형성하기 위한 전구 물질 상태의 조성물에 첨가하여, 조성물의 유동성을 확보하고, 다양한 물질 간에 서로 혼합이 잘 되도록 돕는 기능을 한다.Silicone oil is a polymer compound that has a relatively low molecular weight among silicone polymers and has high fluidity like a liquid. Silicone oil is added to a composition in a precursor state for manufacturing various products using silicone resin or to form a silicone molded body, and functions to ensure the fluidity of the composition and help various substances mix well with each other.
상기 실리콘 오일은 그 종류에 구애되지 않고 인체에 무해한 것이면 다양한 물질을 단독 내지 혼합하여 사용하는 것이 가능하다. 예를 들면, 수산화 실리콘 오일 등을 사용할 수 있으나, 이는 하나의 예시에 불과할 뿐 이에 제한되지 않는다.The silicone oil is not limited to its type and can be used singly or in combination with various substances as long as they are harmless to the human body. For example, hydroxyl silicone oil may be used, but this is only an example and is not limited thereto.
상기 실리콘 오일의 함량은 3 내지 5 중량%로 포함되는 것이 바람직한데, 상기 함량보다 과량으로 첨가되는 경우에는, 커버력이 저하되고, 성형체의 경도 저하로 인하여 사용감이 저하되는 문제가 있다.The content of the silicone oil is preferably 3 to 5% by weight. However, if it is added in excess of the above content, the covering power is reduced and the feeling of use is reduced due to a decrease in the hardness of the molded body.
한편, 본 발명에 따른 실리콘 조성물은, 점착 보조 복합체를 더 포함하고,Meanwhile, the silicone composition according to the present invention further includes an adhesion auxiliary composite,
상기 점착 보조 복합체는, 다수의 포어가 표면에 형성된 메틸비닐폴리실록산을 포함하는 다공성 필라멘트 및 상기 다수의 포어에 담지된 실리콘 오일을 포함할 수 있다.The adhesion auxiliary composite may include a porous filament containing methylvinylpolysiloxane with a plurality of pores formed on the surface, and silicone oil supported on the plurality of pores.
상기 점착 보조 복합체는 실리콘 조성물 내에 포함되어, 성형체로 가공된 후에, 시간 경과에 따라 실리콘 오일이 상기 다수의 포어에서 토출되어, 재사용성을 증가시키는 역할을 하며, 또한, 저온 상태에 노출된 상태에서 신체에 부착하는 경우에, 밀착력이 향상되는 특성을 갖는다.The adhesion auxiliary composite is included in the silicone composition, and after being processed into a molded body, silicone oil is discharged from the plurality of pores over time, thereby increasing reusability, and also serves to increase reusability when exposed to low temperature conditions. When attached to the body, it has the property of improving adhesion.
상기 다수의 포어는 직경 50 내지 200 nm(나노미터)일 수 있다.The plurality of pores may have a diameter of 50 to 200 nm (nanometers).
상기 점착 보조 복합체는 실리콘 조성물의 전체 중량을 기준으로 2 내지 4 중량%로 포함될 수 있다.The adhesion auxiliary composite may be included in an amount of 2 to 4% by weight based on the total weight of the silicone composition.
더욱이, 상기 다수의 포어는 상기 포어 내부 표면이 실릴화될 수 있으며, 이로 인하여, 실리콘 오일의 함침이 용이하게 된다.Furthermore, the plurality of pores may have silylated inner surfaces, which facilitates impregnation with silicone oil.
2. 점착식 브라용 성형체2. Molded body for adhesive bra
상술한 실리콘 조성물로 제조된 점착식 브라용 성형체로서, 상기 성형체는 돌출된 전면과 피부와 접촉하는 함몰된 배면으로 이루어지며 구의 일부와 같은 형태를 가지는 것일 수 있다.A molded body for an adhesive bra made from the above-described silicone composition. The molded body may have a protruding front surface and a depressed back surface in contact with the skin and may have a shape like a part of a sphere.
상기 점착식 브라용 성형체는 상술한 실리콘 조성물을 컵 형태의 성형체를 형성할 수 있는 상부와 하부로 구성된 몰드를 눌러 제조된다.The molded body for the adhesive bra is manufactured by pressing the above-described silicone composition into a mold consisting of an upper and lower part that can form a cup-shaped molded body.
상기 성형체는 컵 모양과 같이 구의 일부를 잘라낸 형태를 가지며, 컵 모양의 외면, 즉, 돌출된 전면과 가슴을 감싸며 피부와 직접 접촉하는 함몰된 배면으로 구성된다.The molded body has a shape in which a portion of a sphere is cut out, like a cup shape, and is composed of a cup-shaped outer surface, that is, a protruding front surface and a recessed rear surface that surrounds the chest and is in direct contact with the skin.
상기 성형체의 두께는 2.2 내지 2.5 mm일 수 있다. 상기 두께보다 두꺼운 경우, 밀착력이 떨어지고, 중량이 증가하여, 착용 시 불편함을 유발할 수 있다.The thickness of the molded body may be 2.2 to 2.5 mm. If it is thicker than the above thickness, adhesion may decrease and weight may increase, causing discomfort when worn.
상기 두께보다 얇은 경우에는, 커버력이 떨어지고, 사용 시 경도가 떨어져 사용감이 저하되는 문제가 있다.If it is thinner than the above thickness, there is a problem that the covering power is reduced and the feeling of use is deteriorated due to reduced hardness during use.
상기와 같은 두께로 제조되는 경우, 쇼어 A(Shore A) 경도 20 내지 35를 만족하게 되며, 이에 따라, 반복 점착과 탈착이 용이하면서도, 브라의 착용 시 유두의 모양이 드러나지 않고, 착용 시의 사용감이 우수하게 된다.When manufactured to the above thickness, it satisfies Shore A hardness of 20 to 35, and as a result, repeated attachment and detachment are easy, the shape of the nipple is not revealed when the bra is worn, and the feeling of use when worn is improved. This becomes excellent.
3. 점착식 브라3. Adhesive bra
상술한 점착식 브라용 성형체의 일면, 즉, 가슴과 직접 접촉하는 함몰된 배면에 실리콘 점착제를 도포하여, 점착식 브라를 구성한다. 상기 실리콘 점착제는 인체에 무해한 성분을 사용하고, 점착력이 너무 높지 않아 반복하여 점착과 탈착을 반복할 수 있는 것이면 어떤 것이든 사용이 가능하다.A silicone adhesive is applied to one side of the molded body for the adhesive bra described above, that is, to the depressed back surface that is in direct contact with the breast, to form an adhesive bra. The silicone adhesive can be used as long as it uses ingredients that are harmless to the human body and the adhesive strength is not too high so that repeated adhesion and desorption can be repeated.
예를 들면, 상기 실리콘 점착제는, 실리콘 비닐 폴리머 점착제 및 디오가노폴리실록산 점착제로 이루어진 군에서 선택된 어느 하나로 이루어진 군에서 선택된 어느 하나일 수 있다. For example, the silicone adhesive may be any one selected from the group consisting of a silicone vinyl polymer adhesive and a diorganopolysiloxane adhesive.
또한, 상기 실리콘 점착제는, 0.3 내지 0.7 mm의 두께로 도포될 수 있다. 상기 두께보다 두껍게 도포되는 경우, 점착식 브라 자체의 중량 증가로 인하여, 가슴에서 쉽게 탈락되는 문제가 있고, 상기 두께보다 얇게 도포되는 경우에는, 점착과 탈착을 반복하는 과정에서 점착층의 마모 정도가 급격히 증가하여, 재사용성이 저하되는 문제가 있다.Additionally, the silicone adhesive may be applied to a thickness of 0.3 to 0.7 mm. When applied thicker than the above thickness, there is a problem of the adhesive bra itself easily falling off from the chest due to an increase in weight, and when applied thinner than the above thickness, the degree of wear of the adhesive layer is increased during repeated adhesion and detachment. As it increases rapidly, there is a problem of reduced reusability.
도 1은 본 발명에 따른 점착식 브라의 점착식 브라의 수직 단면도이고, 도 2는 본 발명의 일 실시예에 따른 점착식 브라용 성형체의 전면을 촬영한 사진이며, 도 3은 본 발명의 일 실시예에 따른 점착식 브라용 성형체의 배면 사진이다.Figure 1 is a vertical cross-sectional view of an adhesive bra according to the present invention, Figure 2 is a photograph of the front of a molded body for an adhesive bra according to an embodiment of the present invention, and Figure 3 is an embodiment of the present invention. This is a rear photo of the molded body for an adhesive bra according to an example.
도 1 내지 3을 참고하면, 점착식 브라용 성형체(10)은 점착식 브라의 본체로서, 전체 형상을 구성하며, 이의 함몰된 배면에 도포된 실리콘 점착제(20)는 가슴에 반복 부착이 가능하게 한다.Referring to Figures 1 to 3, the molded body 10 for an adhesive bra is the main body of an adhesive bra and constitutes the overall shape, and the silicone adhesive 20 applied to its depressed back allows repeated attachment to the chest. do.
도 2는 완성된 점착식 브라의 볼록한 전면을 촬영한 사진이고, 도 3은 점착식 브라용 성형체의 함몰된 배면을 촬영한 사진으로서, 성형체의 함몰된 배면에 도포된 실리콘 점착제가 관찰된다.Figure 2 is a photograph of the convex front of the completed adhesive bra, and Figure 3 is a photograph of the concave back of the molded body for an adhesive bra, in which the silicone adhesive applied to the depressed back of the molded body is observed.
도 4는 본 발명의 일 실시예에 따른 점착식 브라를 착용한 상태를 도식화한 도면으로서, 본 발명에 따른 점착식 브라를 착용할 경우에 가슴에 부착하여 적합한 점착력을 유지하는 한편, 다양한 모양과 크기의 가슴에 적용하여도 밀착력이 우수하며, 우수한 사용감을 부여하게 된다.Figure 4 is a diagram illustrating a state in which an adhesive bra according to an embodiment of the present invention is worn. When the adhesive bra according to the present invention is worn, it is attached to the chest to maintain appropriate adhesive strength, and has various shapes and shapes. Even when applied to breasts of any size, it has excellent adhesion and provides an excellent feeling of use.
4. 점착식 브라의 제조방법4. Manufacturing method of adhesive bra
도 5는 본 발명의 일 실시예에 따른 점착식 브라의 제조방법을 나타낸 공정 순서도이고, 도 6은 본 발명의 일 실시예에 따른 점착식 브라의 제조방법 중 a) 단계의 세부 공정을 나타낸 공정 순서도이다.Figure 5 is a process flow chart showing a manufacturing method of an adhesive bra according to an embodiment of the present invention, and Figure 6 is a process showing the detailed process of step a) of the manufacturing method of an adhesive bra according to an embodiment of the present invention. This is a flowchart.
이하에서는, 도 5 및 도 6을 참고하여 본 발명에 따른 제조방법을 보다 상세히 설명한다.Below, the manufacturing method according to the present invention will be described in more detail with reference to FIGS. 5 and 6.
본 발명에 따른 점착식 브라의 제조방법은, a) 실리콘 조성물을 몰드에 넣고 프레스 가공하여 점착식 브라용 성형체를 제조하는 단계 및 b) 상기 점착식 브라용 성형체의 일면에 실리콘 점착제를 도포하는 단계를 포함한다.The method for manufacturing an adhesive bra according to the present invention includes the steps of a) putting a silicone composition into a mold and press-processing it to produce a molded body for an adhesive bra, and b) applying a silicone adhesive to one side of the molded body for an adhesive bra. Includes.
상기 a) 단계는 점착식 브라용 성형체를 제조하는 단계이고, 상기 b) 단계는 점착식 브라의 일 표면에 점착제를 도포하는 단계이다.Step a) is a step of manufacturing a molded body for an adhesive bra, and step b) is a step of applying an adhesive to one surface of the adhesive bra.
보다 구체적으로, 상기 a) 단계는, a-1) 점착 보조 복합체를 제조하는 단계, a-2) 상기 점착 보조 복합체와 실리콘 고무, 세라믹 분말 및 실리콘 오일을 혼합하여 실리콘 조성물을 제조하는 단계, a-3) 실리콘 조성물을 몰드에 넣고 프레스 가공하여 점착식 브라용 성형체를 제조하는 단계를 포함할 수 있다.More specifically, step a) includes a-1) preparing an adhesion auxiliary composite, a-2) mixing the adhesion auxiliary composite with silicone rubber, ceramic powder, and silicone oil to prepare a silicone composition, a -3) It may include the step of manufacturing a molded body for an adhesive bra by putting the silicone composition into a mold and press processing it.
도 7은 본 발명의 일 실시예에 따른 점착식 브라용 성형체를 제조하기 위한 몰드 형상이고, 도 8 내지 도 10은 본 발명의 일 실시예에 따른 점착식 브라용 성형체의 제조과정을 나타낸 모식도이다.Figure 7 is a mold shape for manufacturing a molded body for an adhesive bra according to an embodiment of the present invention, and Figures 8 to 10 are schematic diagrams showing the manufacturing process of a molded body for an adhesive bra according to an embodiment of the present invention. .
도 7의 상단금형은 볼록한 몰드 형상을 가져, 점착식 브라용 성형체의 함몰된 배면을 형성한다. 도 7의 하단금형은 함몰된 몰드 형상을 가져, 점착식 브라용 성형체의 볼록한 전면을 형성한다. 상기 상단금형과 하단금형의 사이에 본 발명에 따른 실리콘 조성물을 넣고, 프레스 가공함으로써, 점착식 브라용 성형체가 제조된다.The upper mold in FIG. 7 has a convex mold shape, forming a recessed back surface of the molded body for an adhesive bra. The lower mold in FIG. 7 has a recessed mold shape, forming a convex front surface of the molded body for an adhesive bra. A molded body for an adhesive bra is manufactured by placing the silicone composition according to the present invention between the upper mold and the lower mold and performing press processing.
상기 점착 보조 복합체를 제조하는 단계는, 다음과 같다.The steps for preparing the adhesion auxiliary composite are as follows.
먼저, 메틸비닐폴리실록산 100 중량부를 진공 챔버에 넣고 질소 가스를 대기압의 1.5배로 주입하고 대기압의 2배까지 압력을 높이며 2시간 동안 혼합한 다음, 챔버 내의 온도를 영하 10~15℃로 설정하고, 챔버 내에서 전기 방사하여 직경 0.01 mm의 연속사 형태로 제조한다.First, 100 parts by weight of methylvinylpolysiloxane was placed in a vacuum chamber, nitrogen gas was injected at 1.5 times the atmospheric pressure, the pressure was increased to twice the atmospheric pressure and mixed for 2 hours, the temperature in the chamber was set to -10 to 15°C, and the chamber was It is manufactured into a continuous yarn with a diameter of 0.01 mm by electrospinning within the chamber.
즉시 진공 챔버로 이동시켜 다수의 포어를 형성하도록 하여 다수의 포어를 갖는 연속사로 제조한다. 연속사를 0.02 내지 0.03 mm의 길이로 잘라 다공성 필라멘트를 제조하고, 이의 표면와 내부 포어를 실란화시킨다. 실란화된 다공성 필라멘트는 실리콘 오일 20 중량부를 내부에 담지시키는 공정을 거쳐, 점착 보조 복합체를 제조한다.It is immediately moved to a vacuum chamber to form a plurality of pores and manufactured into a continuous yarn having a plurality of pores. The continuous yarn is cut to a length of 0.02 to 0.03 mm to prepare a porous filament, and its surface and internal pores are silanized. The silanized porous filament goes through a process of supporting 20 parts by weight of silicone oil inside, thereby producing an adhesive auxiliary composite.
제조된 점착 보조 복합체는 실리콘 조성물에 첨가되는 실리콘 고무, 세라믹 분말 및 실리콘 오일과 혼합하여 실리콘 조성물로 제조되고, 이를 몰드에 넣어 프레스 가공하여 성형체로 제조한다.The prepared adhesion auxiliary composite is made into a silicone composition by mixing it with silicone rubber, ceramic powder, and silicone oil added to the silicone composition, and then placed in a mold and pressed to form a molded body.
상기 b) 단계에서는, 돌출된 전면과 피부와 접촉하는 함몰된 배면을 포함하는 상기 점착식 브라용 성형체의 상기 함몰된 배면의 표면에 320 내지 330nm 파장의 자외선을 30초간 조사한 후, 암실에서 1분간 휴지시킨 후, 표면에 실리콘 점착제를 도포하는 과정으로 수행된다. 이와 같은 과정을 수행함으로써, 실리콘 점착제의 도포가 균일하게 이루어지며, 성형체로부터 점착 필름의 형태로 탈락되지 않도록 한다.In step b), ultraviolet rays with a wavelength of 320 to 330 nm are irradiated for 30 seconds on the surface of the recessed back surface of the adhesive bra molded body, which includes a protruding front surface and a recessed back surface in contact with the skin, and then irradiated in a dark room for 1 minute. After resting, it is performed by applying a silicone adhesive to the surface. By performing this process, the silicone adhesive is applied uniformly and is prevented from falling off in the form of an adhesive film from the molded body.
보다 더 상세하게는, 암실에서 1분간 휴지시킨 후에는, 해당 오목한 면에만 마이크로 웨이브를 20초간 조사하고 그 후, 다시 암실에서 1분간 휴지시킨 다음에 그 표면에 실리콘 점착제를 도포할 수 있다.More specifically, after resting in a dark room for 1 minute, a microwave can be irradiated only to the concave surface for 20 seconds, and then rested in a dark room again for 1 minute, and then a silicone adhesive can be applied to the surface.
이하에서는, 본 발명의 내용을 실시예에 기초하여 보다 상세히 설명한다.Below, the content of the present invention will be described in more detail based on examples.
<실시예 1><Example 1>
하기 표 1에 기초하여, 실리콘 조성물을 제조하고, 이를 준비된 몰드에 넣고 프레스 가공하여 점착식 브라용 성형체를 제조하였다.Based on Table 1 below, a silicone composition was prepared, placed in a prepared mold, and pressed to produce a molded body for an adhesive bra.
상기 성형체의 오목한 면의 표면에 320 내지 330nm 파장의 자외선을 30초간 조사한 후, 암실에서 1분간 휴지시킨 후, 해당 오목한 면에만 마이크로 웨이브를 20초간 조사하였다. 그 후, 다시 암실에서 1분간 휴지시킨 후, 실리콘 점착제를 0.4 mm의 두께로 도포하였다. After irradiating ultraviolet light with a wavelength of 320 to 330 nm for 30 seconds on the surface of the concave side of the molded body, it was left to rest in a dark room for 1 minute, and then microwaves were irradiated only to the concave side for 20 seconds. Afterwards, after resting again in the dark for 1 minute, the silicone adhesive was applied to a thickness of 0.4 mm.
<실시예 2><Example 2>
상기 실시예 1에서, 실리콘 조성물을 제조하기 전에 다음과 같은 과정으로 점착 보조 복합체를 제조하였다.In Example 1, before preparing the silicone composition, an adhesion auxiliary composite was prepared as follows.
메틸비닐폴리실록산 100 중량부를 진공 챔버에 넣고 질소 가스를 대기압의 1.5배로 주입하고 대기압의 2배까지 압력을 높이며 2시간 동안 혼합하였다. 챔버 내의 온도를 영하 10~15℃로 설정하고, 챔버 내에서 전기 방사하여 직경 0.01 mm의 연속사 형태로 제조하였다. 100 parts by weight of methylvinylpolysiloxane was placed in a vacuum chamber, nitrogen gas was injected at 1.5 times the atmospheric pressure, the pressure was increased to 2 times the atmospheric pressure, and the mixture was mixed for 2 hours. The temperature in the chamber was set to -10-15°C, and electrospinning was performed in the chamber to form a continuous yarn with a diameter of 0.01 mm.
즉시 진공 챔버로 이동시켜 다수의 포어를 형성하도록 하여 다수의 포어를 갖는 연속사를 제조하였다. 연속사를 0.02 내지 0.03 mm의 길이로 잘라 다공성 필라멘트를 제조하고, 이의 표면와 내부 포어를 실란화시킨다. 실란화된 다공성 필라멘트는 실리콘 오일 20 중량부를 내부에 담지시키는 공정을 거쳐, 점착 보조 복합체를 제조하였다.It was immediately moved to a vacuum chamber to form a plurality of pores to produce a continuous yarn having a plurality of pores. The continuous yarn is cut to a length of 0.02 to 0.03 mm to prepare a porous filament, and its surface and internal pores are silanized. The silanized porous filament went through a process of supporting 20 parts by weight of silicone oil inside, thereby producing an adhesive auxiliary composite.
제조된 점착 보조 복합체를 실리콘 고무, 세라믹 분말 및 실리콘 오일과 혼합하여 실리콘 조성물로 제조한 후, 상기 실시예 1과 동일한 방법으로 점착식 브라를 제조하였다.The prepared adhesive auxiliary composite was mixed with silicone rubber, ceramic powder, and silicone oil to prepare a silicone composition, and then an adhesive bra was manufactured in the same manner as in Example 1.
니플
패치
(A사)city
nipple
patch
(Company A)
[실험방법][Experimental method]
1. 인체 피부 일차 자극 시험1. Human skin primary irritation test
피부과학연구소에 의뢰하여, 인체 피부 자극 시험을 진행하였으며, 그 결과를 도 13에 나타냈다.We commissioned a dermatological research institute and conducted a human skin irritation test, and the results are shown in Figure 13.
1) 연구대상자: 선정기준 및 제외기준에 의한 20~60세의 여성 지원자 32명1) Research subjects: 32 female volunteers aged 20 to 60 based on selection and exclusion criteria
2) 첩포 방식: 단일/폐쇄 첩포 시험(48h single patch test)2) Patch method: single/closed patch test (48h single patch test)
3) 첩포 시간: 48 시간3) Patch time: 48 hours
4) 첩포 방법: 시험물질을 챔버에 적하하여 연구대상자 등 부위에 부착한 다음 48 시간 후 제거하고 30분 후 및 24시간 후에 피부 반응을 관찰함4) Patch method: Drop the test substance into the chamber and attach it to the study subject's back, then remove it after 48 hours and observe the skin reaction after 30 minutes and 24 hours.
5) 평가기준: Frosch & Kligman, ICDRG 및 PCPC guideline 의거하여 진단5) Evaluation criteria: Diagnosis based on Frosch & Kligman, ICDRG, and PCPC guidelines
2. 커버력 평가12. Coverage evaluation 1
모형 가슴의 표면에 실시예와 비교예의 샘플을 부착한 후, 육안으로 유두의 모양이나 색이 비치는지 육안으로 확인하는 평가를 진행하였다. 모양이나, 색상이 비치는 정도에 따라, 많이 비치거나 티가 나는 경우에는 X로 평가하고, 모양이나 색상이 비치지만 그 정도가 미미한 경우는 △, 모양이나 색상이 전혀 비치지 않는 경우에는 O로 평가한다. 그 결과를 하기 표 2에 기재하고, 시험 사진을 도 12에 나타냈다.After attaching the samples of the examples and comparative examples to the surface of the model breast, an evaluation was conducted to visually check whether the shape and color of the nipple were visible. Depending on the degree to which the shape or color is visible, if it is a lot or noticeable, it is rated as . The results are shown in Table 2 below, and a test photograph is shown in Figure 12.
3. 커버력 평가23. Coverage evaluation 2
모형 가슴의 표면에 실시예와 비교예의 샘플을 부착한 후 그 표면에 30수 면티 원단을 거치하고, 브라색이 비치는지 육안으로 확인하는 평가를 진행하였다. 색상이 비치는 정도에 따라, 많이 비치는 경우에는 X로 평가하고, 색상이 비치지만 그 정도가 미미한 경우는 △, 색상이 전혀 비치지 않는 경우에는 O로 평가한다. 그 결과를 하기 표 2에 기재하고, 시험 사진을 도 12에 나타냈다.After attaching the samples of the examples and comparative examples to the surface of the model chest, a 30-count cotton tee fabric was placed on the surface, and an evaluation was conducted to visually check whether the bra color was visible. Depending on the degree to which the color is visible, if a lot of the color is visible, it is evaluated as The results are shown in Table 2 below, and a test photograph is shown in Figure 12.
4. 사용감 평가4. Evaluation of feeling of use
20~40세의 여성 20명에 대하여 사용감 평가를 진행하였다. 실시예와 비교예의 샘플을 부착한 후, 24시간 동안 활동하며 밀착력, 점착력 및 이질감을 0점(나쁨)~5점(좋음, 편안함)으로 평가하도록 하여, 이의 평균값을 다음 표 2에 나타냈다.A usability evaluation was conducted on 20 women aged 20 to 40. After attaching the samples of the examples and comparative examples, they were active for 24 hours and evaluated for adhesion, adhesion, and heterogeneity from 0 (bad) to 5 (good, comfortable), and the average values are shown in Table 2 below.
이와 별도로, 도 11에서는 모형 가슴의 표면에 실시예와 참고예의 샘플을 부착한 후 브라의 밀착력을 육안으로 확인하였다. 도 11에서 확인된 바와 같이, 참고예의 샘플을 가슴에 밀착되지 않고 외주변이 들떠 밀착력이 떨어지는 것을 육안으로 확인할 수 있고, 반면, 실시예의 점착식 브라는 모형 가슴에 밀착된 형태로, 외주변이 들뜸이 육안으로 거의 확인되지 않았다.Separately, in Figure 11, the adhesion of the bra was visually confirmed after attaching the samples of the example and reference examples to the surface of the model breast. As confirmed in FIG. 11, it can be visually confirmed that the sample of the reference example does not adhere closely to the chest and the outer periphery is lifted and the adhesive strength is reduced. On the other hand, the adhesive bra of the example is in close contact with the model chest, and the outer periphery is The lifting was barely noticeable with the naked eye.
5. 재사용성 평가5. Reusability evaluation
20~40세의 여성 20명에 대하여 재사용성 평가를 진행하였다. 각 패널들이 하루 6시간 이상 착용하도록 하고, 권장된 세척법으로 세척하여 관리하도록 한 후, 더 이상 브라로서 기능할 수 있을 만큼의 점착력보다 떨어지는 상태, 즉, 마지막 브라 착용 시까지의 재사용회수를 측정하도록 하고, 이의 평균값(소수점 제외)을 다음 표 2에 나타냈다.A reusability evaluation was conducted on 20 women aged 20 to 40. After each panel is worn for more than 6 hours a day, cleaned and maintained using the recommended cleaning method, the number of reuses is measured until the adhesive strength is no longer sufficient to function as a bra, that is, until the last bra worn. And the average value (excluding decimal points) is shown in Table 2 below.
6. 저온 밀착력 평가6. Low-temperature adhesion evaluation
20~40세의 여성 20명에 대하여 저온에서의 밀착력 평가를 진행하였다. 실시예와 비교예의 샘플을 5~7℃의 온도로 유지된 냉장고에 넣어 24시간 유지한 후, 패널에게 제공하기 직전에 냉장고에서 꺼내어 가슴에 부착한 후, 점착 직후의 밀착력 평가를 다음과 같은 기준에 따라 평가하였다.Adhesion evaluation at low temperatures was conducted on 20 women aged 20 to 40. The samples of Examples and Comparative Examples were placed in a refrigerator maintained at a temperature of 5 to 7°C and kept for 24 hours, then taken out of the refrigerator and attached to the chest immediately before being provided to the panel, and adhesion was evaluated immediately after adhesion using the following criteria. It was evaluated according to.
점착되지 않거나 점착 후 2초 내에 떨어지는 경우, X로 평가하고, 점착되나 30초 내에 떨어지는 경우 △, 점착이 잘 되는 경우에는 O로 평가한다.If it does not stick or falls off within 2 seconds after sticking, it is rated as
도 12의 실시예와 참고예의 커버력 시험 사진과 상기 표 1 및 2를 참고하면, 실시예에 따른 점착식 브라가 부착 후 육안으로 확인한 경우와 흰 티를 올려 육안으로 관찰한 경우에 모두 커버력이 우수한 것으로 평가되었다.Referring to the coverage test photos of the examples and reference examples in FIG. 12 and Tables 1 and 2 above, the adhesive bra according to the examples had excellent coverage both when visually inspected after attachment and when visually observed with a white tee on. It was evaluated as
재사용성 평가에서는 실시예와 비교예 5 및 6에서 우수한 것으로 평가되었으며, 특히 실시예 2는 점착 보조 복합체를 더 포함함에 따라, 재사용성이 크게 증가한 것을 확인할 수 있다.In the reusability evaluation, Example and Comparative Examples 5 and 6 were evaluated as excellent, and in particular, Example 2 was confirmed to have significantly increased reusability as it further included an adhesion auxiliary composite.
또한, 비교예 5는 실시예 1과 대비하여 상대적으로 더 얇은 두께로 구성함에 따라, 커버력이 다소 떨어지는 한편, 얇아진 성형체의 경도가 저하되어 밀착력이 오히려 저감되고, 반복적인 점착과 탈착을 반복함에 따라 쉽게 변형되는 등의 이유로 재사용 횟수가 증가할수록 사용감이 크게 저하된다는 의견이 있었다. 반면에 비교예 6은 성형체의 두께가 두꺼워서 가슴에 부착하였을 때 무거운 느낌이 들거나, 밀착력이 저하되는 느낌이 있어 사용감이 저하된다는 의견이 있었다.In addition, Comparative Example 5 was composed of a relatively thinner thickness compared to Example 1, so the covering power was somewhat reduced, and the hardness of the thinned molded body was lowered, so the adhesion was actually reduced, and repeated adhesion and desorption were repeated. There was an opinion that the feeling of use deteriorates significantly as the number of reuses increases due to reasons such as being easily deformed. On the other hand, in Comparative Example 6, there was an opinion that the thickness of the molded body was thick, so it felt heavy when attached to the chest, or the adhesion seemed to be reduced, deteriorating the feeling of use.
Claims (10)
메틸비닐폴리실록산(Methyl vinyl polysiloxane) 63 중량%, 화이트 카본 블랙(White carbon black) 31.5 중량%, 수산화 실리콘 오일(Hydroxy silicone oil) 2.5 중량% 및 점착 보조 복합체 3 중량%를 포함하는 실리콘 조성물로 제조된 점착식 브라용 성형체를 포함하고,
상기 점착 보조 복합체는, 다수의 포어가 표면에 형성되어 있는 다공성 필라멘트를 포함하고,
상기 다공성 필라멘트는 메틸비닐폴리실록산으로 이루어져 있고, 직경 0.01 mm이고, 길이 0.02 내지 0.03 mm인 것이고,
상기 다공성 필라멘트는 수산화 실리콘 오일을 담지시키는 공정을 거쳐 제조된 것이며,
상기 점착식 브라용 성형체는 돌출된 전면과 피부에 접촉하는 함몰된 배면으로 이루어지며 구의 일부와 같은 형태를 가지는 것이고,
상기 점착식 브라용 성형체의 두께는 2.2 내지 2.5 mm이며,
상기 점착식 브라용 성형체의 함몰된 배면의 표면에는 실리콘 점착제가 0.3 내지 0.7 mm의 두께로 도포된 것인, 점착식 브라.
It is an adhesive bra that is used by attaching it to the skin.
Made of a silicone composition containing 63% by weight of methyl vinyl polysiloxane, 31.5% by weight of white carbon black, 2.5% by weight of hydroxy silicone oil, and 3% by weight of an adhesive auxiliary complex. Contains a molded body for an adhesive bra,
The adhesion auxiliary composite includes a porous filament with a plurality of pores formed on the surface,
The porous filament is made of methylvinylpolysiloxane, has a diameter of 0.01 mm, and a length of 0.02 to 0.03 mm,
The porous filament is manufactured through a process of supporting hydroxyl silicone oil,
The molded body for the adhesive bra consists of a protruding front surface and a recessed rear surface in contact with the skin and has a shape like a part of a sphere,
The thickness of the molded body for the adhesive bra is 2.2 to 2.5 mm,
An adhesive bra, wherein a silicone adhesive is applied to the depressed back surface of the molded body for the adhesive bra to a thickness of 0.3 to 0.7 mm.
상기 실리콘 점착제는, 실리콘 비닐 폴리머 점착제 및 디오가노폴리실록산 점착제로 이루어진 군에서 선택된 어느 하나인 점착식 브라.
According to paragraph 1,
The silicone adhesive is an adhesive bra selected from the group consisting of a silicone vinyl polymer adhesive and a diorganopolysiloxane adhesive.
a) 실리콘 조성물을 몰드에 넣고 프레스 가공하여 점착식 브라용 성형체를 제조하는 단계; 및
b) 상기 점착식 브라용 성형체의 일면에 실리콘 점착제를 0.3 내지 0.7 mm의 두께로 도포하는 단계;
를 포함하고,
상기 점착식 브라용 성형체는 돌출된 전면과 피부와 접촉하는 함몰된 배면으로 이루어지며 구의 일부와 같은 형태를 가지며,
상기 a) 단계는,
a-1) 점착 보조 복합체를 제조하는 단계;
a-2) 상기 점착 보조 복합체와 메틸비닐폴리실록산, 화이트 카본 블랙 및 수산화 실리콘 오일을 혼합하여 실리콘 조성물을 제조하는 단계;
a-3) 상기 a-2) 단계에서 제조된 실리콘 조성물을 몰드에 넣고 프레스 가공하여 점착식 브라용 성형체를 제조하는 단계;
를 포함하고,
상기 b) 단계의 실리콘 점착제는 상기 점착식 브라용 성형체의 함몰된 배면에 도포되는 것인, 점착식 브라의 제조방법.
A method of manufacturing an adhesive bra according to claim 1,
a) manufacturing a molded body for an adhesive bra by placing a silicone composition in a mold and press processing; and
b) applying a silicone adhesive to one surface of the molded body for the adhesive bra to a thickness of 0.3 to 0.7 mm;
Including,
The molded body for the adhesive bra consists of a protruding front surface and a depressed back surface in contact with the skin and has a shape like a part of a sphere,
In step a),
a-1) preparing an adhesion auxiliary composite;
a-2) preparing a silicone composition by mixing the adhesion auxiliary composite with methylvinylpolysiloxane, white carbon black, and hydroxyl silicone oil;
a-3) manufacturing a molded body for an adhesive bra by placing the silicone composition prepared in step a-2) into a mold and press processing;
Including,
A method of manufacturing an adhesive bra, wherein the silicone adhesive of step b) is applied to the recessed back surface of the molded body for the adhesive bra.
상기 b) 단계는, 상기 함몰된 배면의 표면에 320 내지 330nm 파장의 자외선을 30초간 조사한 후, 암실에서 1분간 휴지시킨 후, 표면에 실리콘 점착제를 도포하는 것인, 점착식 브라의 제조방법.According to clause 8,
In step b), ultraviolet rays with a wavelength of 320 to 330 nm are irradiated for 30 seconds on the surface of the depressed back, left to rest in a dark room for 1 minute, and then a silicone adhesive is applied to the surface.