KR102636601B1 - Shading paper for ginseng fields - Google Patents
Shading paper for ginseng fields Download PDFInfo
- Publication number
- KR102636601B1 KR102636601B1 KR1020230159001A KR20230159001A KR102636601B1 KR 102636601 B1 KR102636601 B1 KR 102636601B1 KR 1020230159001 A KR1020230159001 A KR 1020230159001A KR 20230159001 A KR20230159001 A KR 20230159001A KR 102636601 B1 KR102636601 B1 KR 102636601B1
- Authority
- KR
- South Korea
- Prior art keywords
- polyethylene
- paper
- weight
- light
- shading
- Prior art date
Abstract
본 발명은 인삼밭 지붕에 설치되는 차광지의 표면에 백색의 광촉매조성물을 도포하여 태양광선을 적절하게 조정하고, 광촉매 작용으로 차광지에 쌓이는 먼지와 이물질을 분해하여 정화함으로써, 유해균을 해소하고, 차광지의 틈새를 매워 이물질과 해충의 침착이 발생하지 않도록 한 인삼밭용 차광지이다. The present invention applies a white photocatalyst composition to the surface of a shading paper installed on the roof of a ginseng field to appropriately adjust solar rays, and decomposes and purifies dust and foreign substances accumulating on the shading paper through the photocatalytic action, thereby eliminating harmful bacteria and removing the shading paper. This is a shading area for ginseng fields that fills in gaps to prevent the accumulation of foreign substances and pests.
Description
본 발명은 인삼밭 지붕에 설치되는 차광지의 표면에 백색의 광촉매조성물을 도포하여 태양광선을 적절하게 조정하고, 광촉매 작용으로 먼지와 같은 유해물질을 분해하여 정화함으로써, 유해균을 해소하고, 차광지의 틈새를 매워 이물질을 비롯한 해충의 침착이 발생하지 않도록 한 것인데 보다 구체적인 것은, The present invention applies a white photocatalyst composition to the surface of a shading paper installed on the roof of a ginseng field to appropriately adjust solar rays, decomposes and purifies harmful substances such as dust through photocatalytic action, eliminates harmful bacteria, and fills gaps in the shading paper. This is to prevent the deposition of foreign substances and other pests by filling the area. More specifically,
두께 0.1∼0.2mm, 폭 2.5∼3.5mm 되는 폴리에틸렌청색테이프사를 경사와 위사로 하거나, 두께 0.1∼0.2mm, 폭 2.5∼3.5mm 되는 폴리에틸렌청색테이프사를 경사로 하고, 두께 0.1∼0.2mm, 폭 2.5∼3.5mm 되는 폴리에틸렌무색테이프사를 위사로 하여, 평직으로 차광지를 제조한 다음, 차광지의 표면에는 Tio2(이산화티타늄) 68중량%, LDPE(Low Density Polyethylene) 25중량%, 스테아린산칼슘(calcium stearate) 2중량%, 폴리에틸렌왁스((Polyethylene Wax) 3중량%, UV제(Ultra Violet) 4∼7중량%로 조성한 광촉매조성물을 표면에 도포하여, 광촉매코팅층을 형성하고, 차광지 이면에 폴리에틸렌투명코팅제를 도포하여, 차광지의 틈새를 매워 먼지와 이물질을 비롯하여 해충이 침착하지 못하게 하고, 차광지의 표면에 가해지는 태양광선을 반사하여 태양광선을 적절하게 조절하고, 광촉매 작용으로 차광지 표면에 쌓이는 먼지와 같은 유해물질을 분해하여 정화함으로써, 항균 작용을 할 수 있게 하여 인삼밭의 환경을 좋게 하고, 안전을 도모할 수 있도록 한 것이다. Use polyethylene blue tape yarns with a thickness of 0.1 to 0.2 mm and a width of 2.5 to 3.5 mm as the warp and weft yarns, or use polyethylene blue tape yarns with a thickness of 0.1 to 0.2 mm and a width of 2.5 to 3.5 mm as the warp yarns, with a thickness of 0.1 to 0.2 mm and a width of 0.1 to 0.2 mm. Light-shielding paper was manufactured by plain weaving using 2.5-3.5 mm colorless polyethylene tape yarn as the weft, and then the surface of the light-shielding paper was covered with 68% by weight of Tio2 (titanium dioxide), 25% by weight of LDPE (Low Density Polyethylene), and calcium stearate. ) A photocatalyst composition composed of 2% by weight of polyethylene wax (3% by weight of polyethylene wax, and 4 to 7% by weight of UV agent (Ultra Violet)) is applied to the surface to form a photocatalytic coating layer, and a polyethylene transparent coating is applied to the back of the light-shielding paper. By applying it, it fills the gaps in the shading paper to prevent dust, foreign substances and pests from settling, and reflects the solar rays applied to the surface of the shading paper to properly control the solar rays, and the photocatalytic action removes dust and dirt that accumulates on the surface of the shading paper. By decomposing and purifying the same harmful substances, it has an antibacterial effect, improving the environment of ginseng fields and promoting safety.
삭제delete
종래의 인삼밭용 차광망은 검은색폴리에틸렌테이프사와 은색폴리에틸렌테이프사를 50:50의 비율로 배치하여 차광망을 제조하고, 이를 인삼밭 지붕에 설치함으로써, 하절기에 은색섬유가 태양광선을 반사하여 인삼밭은 온도를 28∼35℃로 유지할 수 있게 하고 있으나, 차광망의 조직에 틈새가 많아 먼지와 이물질이 쉽게 쌓이고, 해충의 침착이 용이한 불편이 있고, 차광망에 쌓이는 먼지를 정화시키는 기능이 부족하여 항균성이 떨어지는 결점이 있었다. Conventional shading nets for ginseng fields are manufactured by arranging black polyethylene tape yarns and silver polyethylene tape yarns in a ratio of 50:50, and installing them on the roof of the ginseng field. In the summer, the silver fibers reflect the sun's rays, which increases the temperature of the ginseng field. It is possible to maintain the temperature at 28-35℃, but there are many gaps in the structure of the shading net, so dust and foreign substances can easily accumulate, and pests can easily settle in, and it lacks the function of purifying dust accumulated on the shading net, so it has poor antibacterial properties. There was a flaw.
본 발명은 상기 불편을 해소하기 위하여 개발한 것이다. The present invention was developed to solve the above inconvenience.
본 발명은 인삼밭 지붕에 설치하는 차광지의 표리면에 코팅제를 도포하여, 틈새가 없도록 하여, 이물질과 해충의 침착을 방지하고, 차광지 표면 코팅제는 광촉매 작용을 하는 이산화티타늄(Tio2) 조성물을 코팅함으로써, 태양광선을 반사시켜 수광 량을 조절하여, 과열을 막고 광촉매작용으로 차광지에 쌓이는 먼지와 이물질을 분해 정화하여, 유해균을 해소하고, 자외선을 방지하여 내구성을 유지할 수 있도록 한 것이다. The present invention applies a coating agent to the front and back of a shading paper installed on the roof of a ginseng field to prevent the deposition of foreign substances and pests by ensuring that there are no gaps, and the surface coating of the shading paper is coated with a titanium dioxide (Tio2) composition that acts as a photocatalyst. By doing so, it reflects solar rays to control the amount of light received, prevents overheating, decomposes and purifies dust and foreign substances accumulating on the shaded area through photocatalyst action, eliminates harmful bacteria, and maintains durability by preventing ultraviolet rays.
이를 위해 본 발명은 두께 0.1∼0.2mm, 폭 2.5∼3.5mm 되는 폴리에틸렌청색테이프사를 경사(a)와 위사(b)로 하여, 평직하거나, 두께 0.1∼0.2mm 되고, 폭2.5∼3.5mm 되는 폴리에스텔청색테이프사를 경사(a)로 하고, 두께 0.1∼0.2mm되고, 폭 2.5∼3.5mm 되는 폴리에틸렌무색테이프사를 위사(b')로 하여 평직하는 차광지(1)를 형성하고, 차광지의 표면에는 Tio2 68중량%, LDPE 25중량%, 스테아린산칼슘 2중량%, 폴리에틸렌왁스 3중량%, UV제 4∼7중량%로 이루어지는 광촉매조성물을 1㎡ 면적에 13∼14g을 도포하여, 백색의 광촉매코팅층(2)을 형성하고, 차광지 이면에는 폴리에틸렌투명코팅제(3)를 도포하여 차광지를 형성하는 구성이다. For this purpose, the present invention uses polyethylene blue tape yarns with a thickness of 0.1 to 0.2 mm and a width of 2.5 to 3.5 mm as the warp (a) and weft (b) yarns, and is plainly woven or 0.1 to 0.2 mm in thickness and 2.5 to 3.5 mm in width. A light-shielding paper (1) is formed by plain weaving polyester blue tape yarn as the warp yarn (a) and polyethylene colorless tape yarn with a thickness of 0.1 to 0.2 mm and a width of 2.5 to 3.5 mm as the weft yarn (b'), and the light-shielding paper (1) is formed. On the surface of the paper, 13 to 14 g of a photocatalyst composition consisting of 68% by weight of Tio2, 25% by weight of LDPE, 2% by weight of calcium stearate, 3% by weight of polyethylene wax, and 4 to 7% by weight of UV agent was applied to an area of 1 m2 to produce a white A photocatalytic coating layer (2) is formed, and a polyethylene transparent coating agent (3) is applied to the back side of the light-shielding paper to form a light-shielding paper.
이와 같이 된 본 발명은 차광지의 표리면에 코팅층이 형성되어 틈새가 없게 되므로, 먼지를 비롯한 이물질과 해충의 침착이 방지되는 이점이 있고, 차광지 표면에는 광촉매작용을 하는 이산화티타늄 조성물 도포하여 백색의 광촉매코팅층을 형성하였기 때문에, 차광지에 조사되는 태양광을 반사하여 수광 량을 조절하므로, 하절기에 인삼밭 내부 온도가 38℃ 이상으로 크게 상승하는 것을 막아 28∼35℃를 유지할 수 있게 되어, 인삼생육환경을 좋게 할 수 있고, 차광지 표면에 쌓이는 먼지와 이물질 같은 유해물질을 분해하여 정화시키고, 항균작용을 하므로 차광지에서의 항균정화가 이루어지므로, 유해균에 의한 피해를 막을 수 있는 이점이 있고, 자외선을 막아 노화를 방지할 수 있어, 차광지의 수명을 오래유지할 수 있는 등의 이점을 얻을 수 있다. This invention has the advantage of preventing the deposition of dust and other foreign substances and pests by forming a coating layer on the front and back surfaces of the light-shielding paper so that there are no gaps, and by applying a titanium dioxide composition that acts as a photocatalyst to the surface of the light-shielding paper to create a white color. Because the photocatalytic coating layer is formed, the amount of light received is adjusted by reflecting sunlight irradiated on the shaded area, preventing the internal temperature of the ginseng field from rising significantly above 38℃ in the summer and maintaining 28-35℃, thereby improving ginseng growth. It can improve the environment, decomposes and purifies harmful substances such as dust and foreign substances accumulating on the surface of the shaded area, and has an antibacterial effect, so antibacterial purification is achieved in the shaded area, which has the advantage of preventing damage caused by harmful bacteria. By blocking ultraviolet rays, you can prevent aging and gain benefits such as maintaining the lifespan of the light-shielding paper for a long time.
도 1과 도 2는 본 발명 차광지의 평면 예시도
도 3은 본 발명의 단면도이다. 1 and 2 are planar illustrations of the light-shielding paper of the present invention.
Figure 3 is a cross-sectional view of the present invention.
본 발명은 인삼밭 지붕에 설치하는 차광지의 조직을 개량하여 표리면에 코팅층을 형성하여 틈새가 없게 하고, 차광지 표면에는 광촉매 작용을 하는 이산화티타늄(Tio2) 조성물을 코팅하여, 태양광선을 반사시켜 수광 량을 조절하고, 광촉매작용으로 차광지 표면에 쌓이는 먼지와 이물질의 유해성을 분해하여, 정화하는 항균 작용을 달성하고, 자외선방지 작용을 할 수 있게 하여 이루어진다. The present invention improves the structure of the shading paper installed on the roof of the ginseng field to form a coating layer on the front and back to eliminate gaps, and coats the surface of the shading paper with a titanium dioxide (Tio2) composition that acts as a photocatalyst to reflect solar rays. This is achieved by controlling the amount of light received, decomposing harmful dust and foreign substances accumulating on the surface of the light-shielding paper through photocatalysis, achieving purifying antibacterial action, and providing ultraviolet ray protection.
이를 위해 본 발명은 두께 0.1∼0.2mm, 폭 2.5∼3.5mm 되는 폴리에틸렌청색테이프사를 경사(a)와 위사(b)로 하여, 평직하거나, 두께 0.1∼0.2mm 되고, 폭2.5∼3.5mm 되는 폴리에틸렌청색테이프사를 경사(a)로 하고, 두께 0.1∼0.2mm되고, 폭 2.5∼3.5mm 되는 폴리에틸렌무색테이프사를 위사(b')로 하여 평직하는 차광지(1)를 형성하고, 차광지의 표면에는 Tio2 68중량%, LDPE 25중량%, 스테아린산칼슘 2중량%, 폴리에틸렌왁스 3중량%, UV제 4∼7중량%로 이루어지는 광촉매조성물을 1㎡ 면적에 13∼14g을 도포하여, 백색의 광촉매코팅층(2)을 형성하고, 차광지 이면에 폴리에틸렌투명코팅제(3)를 도포하여서 차광지를 형성하는 구성이다. For this purpose, the present invention uses polyethylene blue tape yarns with a thickness of 0.1 to 0.2 mm and a width of 2.5 to 3.5 mm as the warp (a) and weft (b) yarns, and is plainly woven or 0.1 to 0.2 mm in thickness and 2.5 to 3.5 mm in width. A light-shielding paper (1) is formed by plain weaving polyethylene blue tape yarns as warp yarns (a) and polyethylene colorless tape yarns with a thickness of 0.1 to 0.2 mm and a width of 2.5 to 3.5 mm as weft yarns (b'). On the surface, 13 to 14 g of a photocatalyst composition consisting of 68% by weight of Tio2, 25% by weight of LDPE, 2% by weight of calcium stearate, 3% by weight of polyethylene wax, and 4 to 7% by weight of UV agent was applied to an area of 1 m2 to produce a white photocatalyst. The configuration is to form a light-shielding paper by forming a coating layer (2) and applying a polyethylene transparent coating agent (3) to the back of the light-shielding paper.
1 : 차광지 2 : 백색의 광촉매코팅층
3 : 폴리에틸렌투명코팅제
a : 폴리에틸렌청색테이프사로 된 경사
b : 폴리에틸렌청색테이프사로 된 위사
b' 폴리에틸렌무색테이프사로 된 위사1: Light blocking paper 2: White photocatalyst coating layer
3: Polyethylene transparent coating agent
a: warp made of polyethylene blue tape yarn
b: weft made of polyethylene blue tape yarn
b' Weft yarn made of polyethylene colorless tape yarn
Claims (1)