KR102506376B1 - Flame retardant hook band and manufacturing method thereof - Google Patents

Flame retardant hook band and manufacturing method thereof Download PDF

Info

Publication number
KR102506376B1
KR102506376B1 KR1020200140212A KR20200140212A KR102506376B1 KR 102506376 B1 KR102506376 B1 KR 102506376B1 KR 1020200140212 A KR1020200140212 A KR 1020200140212A KR 20200140212 A KR20200140212 A KR 20200140212A KR 102506376 B1 KR102506376 B1 KR 102506376B1
Authority
KR
South Korea
Prior art keywords
flame retardant
hook band
ventilation
felt
band
Prior art date
Application number
KR1020200140212A
Other languages
Korean (ko)
Other versions
KR20220055773A (en
Inventor
이준영
Original Assignee
사이언스세이프티 주식회사
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 사이언스세이프티 주식회사 filed Critical 사이언스세이프티 주식회사
Priority to KR1020200140212A priority Critical patent/KR102506376B1/en
Publication of KR20220055773A publication Critical patent/KR20220055773A/en
Application granted granted Critical
Publication of KR102506376B1 publication Critical patent/KR102506376B1/en

Abstract

본 발명은 난연성 후크밴드 및 그 제조방법에 관한 것으로, 니들 펠트 방식으로 카본 섬유와 난연성 펠트를 재봉하여 제조되는 본체부; 상기 본체부의 양측 단부에 소정 간격 이격되게 다수개로 구성되어, 전선의 온도를 일정하게 유지시켜 주는 통기부; 및 상기 통기부의 내주면에 밀착되며, 상기 본체부의 양측 단부의 결합이 이루어지도록 지지하는 체결구;를 포함하는 난연성 후크 밴드와, 이 난연성 후크 밴드를 제조하는 방법을 제공하는 것을 특징으로 한다.The present invention relates to a flame retardant hook band and a manufacturing method thereof, comprising: a body part manufactured by sewing carbon fibers and a flame retardant felt in a needle felt method; a plurality of ventilating parts spaced apart from each other at predetermined intervals at both ends of the main body part to maintain a constant temperature of the electric wire; It is characterized in that it provides a flame retardant hook band including a; and a method for manufacturing the flame retardant hook band; and fasteners that are in close contact with the inner circumferential surface of the ventilation part and support the coupling of both ends of the main body part.

Description

난연성 후크밴드 및 그 제조방법{Flame retardant hook band and manufacturing method thereof}Flame retardant hook band and manufacturing method thereof {Flame retardant hook band and manufacturing method thereof}

본 발명은 난연성 후크밴드 및 그 제조방법에 관한 것으로, 더욱 상세하게는 부드럽고 유연하며, 얇은 두께를 이루도록 구성하여 화재 위험 구역의 다양한 환경에 쉽게 변형하여 적용이 가능하고, 적용 환경에 따라 다양하게 그 두께, 폭 등을 구성할 수 있어 난연성 후크밴드의 자유로운 생산성을 제공할 수 있는 난연성 후크밴드 및 그 제조방법에 관한 것이다. The present invention relates to a flame retardant hook band and a method for manufacturing the same, and more specifically, it is soft, flexible, and configured to form a thin thickness so that it can be easily transformed and applied to various environments in a fire risk zone, and it can be applied in various ways depending on the application environment. The present invention relates to a flame retardant hook band capable of providing free productivity of a flame retardant hook band and a method for manufacturing the same by configuring the thickness and width.

일반적으로, 다양한 건축물들에는 화재의 확산을 방지하기 위한 난연성 패널, 또는 시트가 시공되고 있다. 특히 건축물에 시공되는 전력 구조물에는 전기적 안전사고를 방지하기 위하여 별도의 난연성 패널, 또는 시트가 구비되어야만 한다. In general, flame retardant panels or sheets for preventing the spread of fire are being installed in various buildings. In particular, a power structure constructed in a building must be provided with a separate flame retardant panel or sheet in order to prevent electrical safety accidents.

그러나, 종래에는 전력 구조물로부터 발생하는 감전에 의한 화재의 확산을 방지하기 위하여 전선을 피복하는 피복체가 난연성 피복체로 이루어지거나, 또는 전선을 감싸는 방호관을 통해 해결하고 있다. However, conventionally, in order to prevent the spread of fire due to electric shock generated from power structures, the covering covering the electric wire is made of a flame retardant covering or a protective pipe covering the electric wire has been solved.

일 예로, 대한민국 등록특허 제10-2100090호에는, 전기적 안전사고를 예방하기 위해 절연전선을 감싸는 방호관을 난연캡으로 커버링함으로써 방호관이 절연전선과의 마찰에 의해 화재가 발생되는 것 자체를 방지하거나 확산을 방지하고, 난연캡을 절연전선과 테이핑 처리에 의해 위치 고정된 상태로 난연캡이 방호관을 구속함으로써 방호관의 임의적 이동이나 흔들림을 방지하고자 하는 절연전선의 선로 보호용 난연 구조체가 게재된 바 있다. For example, in Korean Patent Registration No. 10-2100090, in order to prevent electrical safety accidents, the protection tube surrounding the insulated wire is covered with a flame retardant cap to prevent fire itself caused by the friction of the protection tube with the insulated wire. A flame retardant structure for protecting the line of an insulated wire to prevent arbitrary movement or shaking of the protective tube by restraining the protective tube while the flame retardant cap is fixed in position by insulated wire and taping treatment. there is a bar

그러나, 전술한 선행기술문헌에 의하면, 직선형, 또는 방호관의 굴곡에 대해서만 전선의 배선이 가능하기 때문에 시공에 대한 건축물의 환경 조건에 따른 자유로운 시공이 어려울 뿐만 아니라, 해당 조건에 맞게 재가공을 해야만 하기 때문에 생산성이 현저하게 떨어지는 문제점이 있다. However, according to the above-mentioned prior art literature, since it is possible to wire wires only in a straight line or in a curved shape of a protective pipe, it is difficult to freely construct according to the environmental conditions of the building for construction, and reprocessing must be performed according to the conditions Therefore, there is a problem in that productivity is remarkably lowered.

또한, 대한민국 등록특허 제10-0921615호에는, 다양한 형태로 제직된 유리직물에 난연성과 디자인이 우수한 베이스 수지를 코팅한 다음 그 상부에 불소수지를 1회 이상 코팅함으로써, 외관 효과가 우수하고 불연 성능을 갖는 불연 유리직물 및 이를 이용한 건축 내벽판, 천정판 등의 불연 건축자재가 게재된 바 있다.In addition, Korean Patent Registration No. 10-0921615 discloses that glass fabrics woven in various shapes are coated with a base resin having excellent flame retardancy and design, and then coated with a fluororesin one or more times on top of the glass fabric, resulting in excellent appearance and non-combustible performance. Incombustible glass fabrics having and non-combustible building materials such as inner wall boards and ceiling boards using the same have been published.

그러나, 전술한 선행기술문헌에 의하면, 시공이 이루어질 전력 구조물의 상태나 환경에 따라 절단, 붙임 등의 재가공이 이루어지게 되는 경우, 유리섬유, 난연수지, 불소수지 등이 각각 분리되면서 본연이 기능성을 저하시키는 문제점이 발생하였고, 이로 인해 다양한 형태로의 변형이 어려워 건축물 내에 다양한 형태로 시공되는 전력 구조물에 난연성을 제공할 수 없는 문제점이 있다. However, according to the above-mentioned prior art documents, when reprocessing such as cutting and attaching is performed according to the state or environment of the power structure to be constructed, glass fiber, flame retardant resin, fluororesin, etc. There is a problem of deterioration, and due to this, it is difficult to transform into various forms, and there is a problem that flame retardancy cannot be provided to power structures constructed in various forms in a building.

대한민국 등록특허 제10-2100090호Republic of Korea Patent No. 10-2100090 대한민국 등록특허 제10-0921615호Republic of Korea Patent No. 10-0921615

이와 같은 문제점을 해결하기 위하여 본 발명은 전술한 배경기술에 의해서 안출된 것으로, 난연성 펠트와 카본섬유를 니들 펠트 방식으로 결합하여 제조하고, 전력 구조물, 또는 전선을 감싸면서 감전사고에 의한 화재의 확산을 방지할 수 있는 난연성 후크밴드 및 그 제조방법을 제공하는데 그 목적이 있다. In order to solve this problem, the present invention has been made by the above-described background art, and manufactures by combining flame retardant felt and carbon fiber in a needle felt method, and spreads fire due to electric shock while wrapping power structures or wires. It is an object of the present invention to provide a flame retardant hook band and a method for manufacturing the same.

또한, 본 발명은 부드럽고 유연하며, 얇은 두께를 이루도록 구성하여 화재 위험 구역의 다양한 환경에 쉽게 변형하여 적용이 가능하고, 적용 환경에 따라 다양하게 그 두께, 폭 등을 구성할 수 있어 난연성 후크밴드의 자유로운 생산성을 제공할 수 있는 난연성 후크밴드 및 그 제조방법을 제공하는데 그 목적이 있다. In addition, the present invention is soft, flexible, and configured to form a thin thickness so that it can be easily transformed and applied to various environments in fire risk areas, and the thickness and width can be configured in various ways according to the application environment, so that the flame retardant hook band The purpose is to provide a flame retardant hook band that can provide free productivity and a manufacturing method thereof.

또한, 본 발명은 난연성 후크밴드의 일면으로 관통 형성되는 통기부를 더 구성하여 감싸지는 전선 구조물, 또는 전선의 내부 온도를 일정하게 유지될 수 있도록 함으로써, 온도 상승시 전선의 송전률이 떨어지는 것을 방지할 수 있는 난연성 후크밴드 및 그 제조방법을 제공하는데 그 목적이 있다. In addition, the present invention further configures a ventilation part formed through one side of the flame retardant hook band so that the internal temperature of the wrapped wire structure or wire can be kept constant, thereby preventing the transmission rate of the wire from falling when the temperature rises. The purpose is to provide a flame retardant hook band and a method for manufacturing the same.

또한, 본 발명은 전력선과 신호선을 각각 분리하여 독립적으로 감싸는 형태로 시공이 이루어짐에 따라 전선들에 대한 종류를 쉽게 파악할 수 있음은 물론, 전력선에 의해 화재가 발생한다 하더라도 신호선을 보호할 수 있는 난연성 후크밴드 및 그 제조방법을 제공하는데 그 목적이 있다. In addition, according to the present invention, as the construction is carried out in a form of separately wrapping the power line and the signal line, the type of the wires can be easily identified, as well as flame retardancy that can protect the signal line even if a fire occurs due to the power line. Its purpose is to provide a hook band and its manufacturing method.

다만, 본 발명의 목적은 이에만 제한되는 것은 아니며, 명시적으로 언급하지 않더라도 과제의 해결수단이나 실시 형태로부터 파악될 수 있는 목적이나 효과도 이에 포함됨은 물론이다. However, the object of the present invention is not limited thereto, and even if not explicitly mentioned, the purpose or effect that can be grasped from the solution or embodiment of the problem is also included therein, of course.

이와 같은 과제를 달성하기 위한 본 발명의 일 실시예에 따르면, 니들 펠트 방식으로 카본 섬유와 난연성 펠트를 재봉하여 제조되는 본체부; 상기 본체부의 양측 단부에 소정 간격 이격되게 다수개로 구성되어, 전선의 온도를 일정하게 유지시켜 주는 통기부; 및 상기 통기부의 내주면에 밀착되며, 상기 본체부의 양측 단부의 결합이 이루어지도록 지지하는 체결구;를 포함하는 것을 특징으로 한다.According to one embodiment of the present invention for achieving the above object, the body portion manufactured by sewing the carbon fiber and the flame retardant felt needle felt method; a plurality of ventilating parts spaced apart from each other at predetermined intervals at both ends of the main body part to maintain a constant temperature of the electric wire; and a fastener that is closely attached to the inner circumferential surface of the ventilation unit and supports coupling of both ends of the main body unit.

본 발명의 일 실시예에 따르면, 상기 카본 섬유에는 상부면 및 하부면에 각각 흡착시트와 이형지가 부착되는 것을 특징으로 한다.According to one embodiment of the present invention, the carbon fiber is characterized in that an adsorption sheet and a release paper are attached to the upper and lower surfaces, respectively.

본 발명의 일 실시예에 따르면, 상기 난연성 펠트는 탄화가 이루어진 섬유에 난연성 코팅액이 코팅되는 것을 특징으로 한다.According to one embodiment of the present invention, the flame retardant felt is characterized in that a flame retardant coating liquid is coated on carbonized fibers.

본 발명의 일 실시예에 따르면, 상기 통기부는, 상기 난연성 후크 밴드의 양측 끝단부에 각각 서로 대응되는 위치에 구성되며, 상기 난연성 후크 밴드를 관통하는 형태로 구성되는 것을 특징으로 한다.According to one embodiment of the present invention, the ventilation unit is configured in a position corresponding to each other at both ends of the flame retardant hook band, and is characterized in that it is configured in a form penetrating the flame retardant hook band.

본 발명의 일 실시예에 따르면, 상기 체결구에는 상기 난연성 후크 밴드를 결합시키는 결합수단이 더 구성되는 것을 특징으로 한다.According to one embodiment of the present invention, the fastener is characterized in that the coupling means for coupling the flame retardant hook band is further configured.

본 발명의 일 실시예에 따르면, 상기 난연성 후크 밴드에는, 서로 대응되는 위치에 구성되는 각각의 상기 통기부들을 연결하기 위해 앙부가 관통되어 관통구를 형성하고, 상부면이 적층된 상기 난연성 후크 밴드의 양측 단부 중, 상부에 위치하는 일측 단부와 밀착되도록 구성되며, 중앙부가 상기 통기부, 또는 상기 통기부에 밀착된 체결구를 관통하는 체결수단; 상기 체결수단에 구성되며, 상기 난연성 후크 밴드의 양측 단부 중, 하부에 위치하는 타측 단부와 밀착되도록 구성되며, 중앙부가 일측 및 타측 단부에 각각 구성된 통기부를 관통하면서 상기 체결수단과 결합되는 체결 지지부재; 상기 통기부가 형성된 부분만을 감싸도록 구성되고, 상기 체결수단이 관통하면서 상기 난연성 후크 밴드와의 연결이 이루어지도록 구성되는 고정밴드;가 더 구성되는 것을 특징으로 한다. According to one embodiment of the present invention, in the flame retardant hook band, a bottom portion is penetrated to form a through hole in order to connect each of the ventilation units configured at positions corresponding to each other, and the flame retardant hook band has an upper surface laminated. Of both ends of the, it is configured to be in close contact with one end located at the top, the central portion of the fastening means passing through the ventilation portion or the fastener in close contact with the ventilation portion; It is composed of the fastening means, and is configured to be in close contact with the other end located at the bottom of both ends of the flame retardant hook band, and the central portion is coupled to the fastening means while passing through the ventilation part formed at one and the other end portion. absence; A fixed band configured to surround only the portion where the ventilation portion is formed and configured to be connected to the flame retardant hook band while the fastening means passes through is further configured.

본 발명의 일 실시예에 따르면, 상기 난연성 후크 밴드에는 전력 구조물, 또는 전선의 상부로 상기 통기부 및 체결구가 소정 간격 이격된 위치에 구성될 수 있도록 상기 난연성 후크 밴드의 양측부에 밀착되도록 구성되며, 외면으로 복수개의 결합돌기가 형성된 밴드 지지패널이 더 구성되는 것을 특징으로 한다. According to one embodiment of the present invention, the flame retardant hook band is configured to be in close contact with both sides of the flame retardant hook band so that the ventilation part and the fastener can be configured at positions spaced apart from each other by a predetermined interval on top of a power structure or electric wire. And, it is characterized in that the band support panel is further configured with a plurality of coupling protrusions formed on the outer surface.

본 발명의 다른 일 실시예에 따르면, 난연성 후크 밴드 제조 방법에 있어서,난연성 레이온 단섬유와 아크릴 섬유를 탄화시키고, 탄화가 이루어진 섬유에 난연성 코팅액이 일정 두께로 코팅시켜 난연성 펠트를 제조하는 난연성 펠트 제조단계; 메타아라미드(m-Aramid) 소재의 실로 직조된 원단에 카본블랙이 증착, 또는 도포된 카본 섬유를 제조하는 카본 섬유 제조단계; 상기 카본 섬유의 상부면에 상기 난연성 펠트를 안착시킨 후, 니들 펠트 방식으로 재봉하여 상기 카본 섬유와 난연성 펠트를 결합시켜 난연성 후크 밴드의 본체부를 제조하는 니들펠트 단계; 상기 본체부의 양측 단부를 관통시켜 다수개의 통기부를 형성하는 통기부 형성단계; 및 상기 통기부에 체결구를 결합하는 결합단계;를 포함하는 것을 특징으로 한다.According to another embodiment of the present invention, in the method for manufacturing a flame retardant hook band, flame retardant felt is prepared by carbonizing short flame retardant rayon fibers and acrylic fibers, and coating the carbonized fibers with a flame retardant coating solution to a certain thickness to produce a flame retardant felt. step; A carbon fiber manufacturing step of preparing carbon fibers in which carbon black is deposited or coated on a fabric woven with threads of meta aramid (m-Aramid); A needle felting step of seating the flame retardant felt on the upper surface of the carbon fiber and then sewing the carbon fiber and the flame retardant felt together in a needle felt method to manufacture a main body of the flame retardant hook band; Ventilation part forming step of forming a plurality of ventilation parts by penetrating both ends of the body part; And a coupling step of coupling a fastener to the ventilation unit; characterized in that it comprises a.

본 발명의 일 실시예에 따르면, 상기 카본 섬유 제조단계는, 상기 카본 섬유의 상부면으로 부직포 형태의 흡착시트를 부착하고, 하부면으로는 카본블랙의 탈리를 방지하는 이형를 부착하는 단계를 더 수행하는 것을 특징으로 한다.According to one embodiment of the present invention, in the carbon fiber manufacturing step, the step of attaching a non-woven fabric-type adsorbent sheet to the upper surface of the carbon fiber and attaching a mold release for preventing separation of carbon black to the lower surface is further performed. It is characterized by doing.

이와 같은 본 발명의 실시예에 의하면, 난연성 펠트와 카본섬유를 니들 펠트 방식으로 결합하여 제조하고, 전력 구조물, 또는 전선을 감싸면서 감전사고에 의한 화재의 확산을 방지할 수 있는 효과가 있다.According to such an embodiment of the present invention, it is produced by combining a flame retardant felt and carbon fiber in a needle felt method, and there is an effect of preventing the spread of fire due to an electric shock accident while wrapping a power structure or electric wire.

또한, 본 발명의 실시예에 의하면, 부드럽고 유연하며, 얇은 두께를 이루도록 구성하여 화재 위험 구역의 다양한 환경에 쉽게 변형하여 적용이 가능하고, 적용 환경에 따라 다양하게 그 두께, 폭 등을 구성할 수 있어 난연성 후크밴드의 자유로운 생산성을 제공할 수 있는 효과가 있다.In addition, according to an embodiment of the present invention, it is configured to be soft, flexible, and thin, so that it can be easily transformed and applied to various environments in a fire risk zone, and the thickness, width, etc. can be configured in various ways according to the application environment. There is an effect of providing free productivity of the flame retardant hook band.

또한, 본 발명의 실시예에 의하면, 난연성 후크밴드의 일면으로 관통 형성되는 통기부를 더 구성하여 감싸지는 전선 구조물, 또는 전선의 내부 온도를 일정하게 유지될 수 있도록 함으로써, 온도 상승시 전선의 송전률이 떨어지는 것을 방지할 수 있는 효과가 있다.In addition, according to an embodiment of the present invention, the ventilation part formed through one side of the flame retardant hook band is further configured so that the internal temperature of the wrapped wire structure or wire can be maintained constant, so that the wire is transmitted when the temperature rises. There is an effect that can prevent the rate from falling.

또한, 본 발명의 실시예에 의하면, 전력선과 신호선을 각각 분리하여 독립적으로 감싸는 형태로 시공이 이루어짐에 따라 전선들에 대한 종류를 쉽게 파악할 수 있음은 물론, 전력선에 의해 화재가 발생한다 하더라도 신호선을 보호할 수 있는 효과가 있다.In addition, according to an embodiment of the present invention, as the construction is performed in a form of separately wrapping the power line and the signal line, the type of the wires can be easily identified, and even if a fire occurs due to the power line, the signal line It has a protective effect.

더불어, 본 발명의 다양하면서도 유익한 장점과 효과는 상술한 내용에 한정되지 않으며, 본 발명의 구체적인 실시 형태를 설명하는 과정에서 보다 쉽게 이해될 수 있을 것이다. In addition, the various beneficial advantages and effects of the present invention are not limited to the above description, and will be more easily understood in the process of describing specific embodiments of the present invention.

도 1은 본 발명의 일 실시예에 따른 난연성 후크밴드를 나타낸 사시도,
도 2는 본 발명의 일 실시예에 따른 난연성 후크밴드를 개략적으로 나타낸 단면도,
도 3 내지 도 6은 본 발명의 일 실시예에 따른 난연성 후크밴드의 체결구 및 통기부를 개략적으로 나타낸 도면,
도 7 및 도 8은 본 발명의 일 실시예에 따른 난연성 후크밴드가 결합되는 상태를 나타낸 예시도,
도 9는 본 발명의 일 실시예에 따른 난연성 후크밴드의 제조 과정을 나타낸 순서도이다.1 is a perspective view showing a flame retardant hook band according to an embodiment of the present invention;
2 is a schematic cross-sectional view of a flame retardant hook band according to an embodiment of the present invention;
3 to 6 are diagrams schematically showing fasteners and vents of a flame retardant hook band according to an embodiment of the present invention;
7 and 8 are exemplary views showing a state in which a flame retardant hook band is coupled according to an embodiment of the present invention;
9 is a flowchart illustrating a manufacturing process of a flame retardant hook band according to an embodiment of the present invention.

이하, 본 발명의 바람직한 실시예를 첨부된 도면들을 참조하여 상세히 설명한다. 우선 각 도면의 구성요소들에 참조 부호를 부가함에 있어서, 동일한 구성요소들에 대해서는 비록 다른 도면상에 표시되더라도 가능한 동일한 부호를 가지도록 하고 있음에 유의해야 한다. 또한, 본 발명을 설명함에 있어, 관련된 공지 구성 또는 기능에 대한 구체적인 설명이 본 발명의 요지를 흐릴 수 있다고 판단되는 경우에는 그 상세한 설명은 생략한다. Hereinafter, preferred embodiments of the present invention will be described in detail with reference to the accompanying drawings. First, in adding reference numerals to components of each drawing, it should be noted that the same components have the same numerals as much as possible even if they are displayed on different drawings. In addition, in describing the present invention, if it is determined that a detailed description of a related known configuration or function may obscure the gist of the present invention, the detailed description will be omitted.

또한, 이하에서 기재된 "포함하다", "구성하다" 또는 "가지다" 등의 용어는, 특별히 반대되는 기재가 없는 한, 해당 구성 요소가 내재될 수 있음을 의미하는 것이므로, 다른 구성 요소를 제외하는 것이 아니라 다른 구성 요소를 더 포함할 수 있는 것으로 해석되어야 하며, 기술적이거나 과학적인 용어를 포함한 모든 용어들은, 다르게 정의되지 않는 한, 본 발명이 속하는 기술 분야에서 통상의 지식을 가진 자에 의해 일반적으로 이해되는 것과 동일한 의미를 가진다. 또한, 본 발명의 구성 요소를 설명하는 데 있어서, 제 1, 제 2, A, B, (a), (b) 등의 용어를 사용할 수 있다. 이러한 용어는 그 구성 요소를 다른 구성 요소와 구별하기 위한 것일 뿐, 그 용어에 의해 해당 구성 요소의 본질이나 차례 또는 순서 등이 한정되지 않는다. 어떤 구성 요소가 다른 구성요소에 "연결", "결합" 또는 "접속" 된다고 기재된 경우, 그 구성 요소는 그 다른 구성요소에 직접적으로 연결되거나 또는 접속될 수 있지만, 각 구성 요소 사이에 또 다른 구성 요소가 "연결", "결합" 또는 "접속"될 수도 있다고 이해되어야 할 것이다.In addition, terms such as "comprise", "comprise" or "having" described below mean that the corresponding component may be inherent unless otherwise stated, excluding other components. All terms, including technical or scientific terms, are generally understood by those skilled in the art to which the present invention belongs, unless otherwise defined. have the same meaning as understood. Also, terms such as first, second, A, B, (a), and (b) may be used in describing the components of the present invention. These terms are only used to distinguish the component from other components, and the nature, order, or order of the corresponding component is not limited by the term. When an element is described as being “connected”, “coupled” or “connected” to another element, that element is or may be directly connected to the other element, but there is another element between the elements. It will be understood that elements may be “connected”, “coupled” or “connected”.

이하, 첨부된 도면을 참고하여 본 발명의 실시예들을 상세히 설명하도록 한다. Hereinafter, embodiments of the present invention will be described in detail with reference to the accompanying drawings.

도시된 바와 같이, 본 발명의 난연성 후크 밴드(100)는 본체부(102)가 하부를 이루며, 난연 기능을 제공하는 카본섬유(110)와, 이 카본섬유(110)의 상부면을 이루며, 니들펠트 방식으로 카본섬유(110)와 결합되는 난연성 펠트(120)를 포함하여 구성되며, 전력 구조물의 형태, 크기, 또는 전선의 크기 및 그 개수에 따라 형상 및 두께의 변형이 가능하도록 구성되는 것이다. As shown, in the flame retardant hook band 100 of the present invention, the body portion 102 forms the lower part, the carbon fiber 110 providing the flame retardant function, and the upper surface of the carbon fiber 110, the needle It is configured to include a flame retardant felt 120 coupled to the carbon fiber 110 in a felt manner, and is configured to enable deformation of shape and thickness according to the shape and size of the power structure, or the size and number of wires.

이러한 난연성 후크 밴드(100)는 두께의 변형시 다수개의 난연성 후크 밴드(100)를 적층한 후 오버로크 방식으로 재봉하는 방식을 통해 구현될 수 있으며, 이로 인해 화재 위험 구역 내에 설비되는 전력 구조물, 또는 다수개의 전선들의 형태, 크기 및 그 개수 등과 무관하게 다양하게 적용할 수 있으며, 두께의 용이하고 자유로운 확장으로 인해 난연 기능을 더욱 극대화시킬 수 있는 것이다. Such a flame retardant hook band 100 may be implemented by stacking a plurality of flame retardant hook bands 100 when the thickness is modified and then sewing them in an overlock method. As a result, a power structure installed in a fire risk area, or a plurality of flame retardant hook bands 100 It can be applied in various ways regardless of the shape, size and number of wires of the dog, and the flame retardant function can be further maximized due to the easy and free expansion of the thickness.

이와 같은 난연성 후크 밴드(100)에 있어서, 카본 섬유(110)는 난연성을 제공하는 메타아라미드(m-Aramid) 소재의 실로 직조된 원단의 표면에 카본블랙(Carbon black) 박막을 일정 간격으로 배열한 후 증착하거나, 또는 분말 형태의 카본블랙이 일정 두께로 도포되는 형태로 구성된다. In such a flame-retardant hook band 100, the carbon fiber 110 is formed by arranging carbon black thin films at regular intervals on the surface of a fabric woven with m-Aramid yarn providing flame retardancy. It is composed of a form in which it is deposited after deposition, or carbon black in powder form is applied to a certain thickness.

또한, 카본 섬유(110)는 그 상부면으로 부직포 형태의 흡착시트(130)가 더 구성될 수 있으며, 이는 니들 펠트 방식으로 난연성 펠트(120)와의 결합이 이루어질 때, 증착, 또는 도포되어 있는 카본블랙이 카본 섬유(110)로부터 탈리되는 것을 방지하는 한편, 카본 섬유(110)와 난연성 펠트(120) 간의 결합력을 증진시켜 난연성 후크 밴드(100)에 대한 안정적인 견고성을 제공할 수 있도록 구성될 수 있다. In addition, the carbon fiber 110 may further include an adsorption sheet 130 in the form of a non-woven fabric on its upper surface, which is bonded to the flame retardant felt 120 in a needle felt method, deposited or applied carbon It can be configured to prevent the black from being detached from the carbon fibers 110 and to provide stable robustness to the flame retardant hook band 100 by enhancing the bonding force between the carbon fibers 110 and the flame retardant felt 120. .

아울러, 본 발명의 카본 섬유(110)는 하부면으로 카본블랙의 탈리를 방지하는 이형지(140)가 더 부착될 수 있으나, 이에 한정하는 것은 아니다. In addition, a release paper 140 for preventing separation of carbon black may be further attached to the lower surface of the carbon fiber 110 of the present invention, but is not limited thereto.

난연성 펠트(120)는 난연성 레이온 단섬유와 아크릴 섬유를 탄화시켜 제조되는 섬유로, 탄화가 이루어진 섬유에 난연성 코팅액이 일정 두께로 코팅된다. The flame retardant felt 120 is a fiber prepared by carbonizing short flame retardant rayon fibers and acrylic fibers, and a flame retardant coating liquid is coated to a certain thickness on the carbonized fibers.

이때, 난연성 코팅액은 고순도 실리카, 알루미나, 탄소 및 지르코니아가 일정 중량비로 혼합되게 구성될 수 있으며, 본 발명에서는 총 중량에 있어서, 실리카 50중량%~70중량%, 알루미나 20중량%~30중량%, 지르코니아 5중량%~10중량%, 탄소 5중량%~10중량%의 비율로 혼합된 혼합물로 이루어질 수 있다. At this time, the flame retardant coating liquid may be configured such that high purity silica, alumina, carbon and zirconia are mixed in a certain weight ratio, and in the present invention, in the total weight, 50% to 70% by weight of silica, 20% to 30% by weight of alumina, It may be made of a mixture mixed in a ratio of 5% to 10% by weight of zirconia and 5% to 10% by weight of carbon.

이와 같이 구성된 본 발명의 난연성 후크 밴드(100)는 전력 구조물, 또는 전선을 감싸는 방식을 통해 시공이 이루어지는 것으로, 시공시 전선으로부러 발산되는 열기를 외부로 방출시켜 전선이 배선된 전력 구조물, 또는 전선 자체에 대한 온도가 일정하게 유지될 수 있도록 하는 통기부(200)가 구성된다. The flame retardant hook band 100 of the present invention configured as described above is constructed by wrapping a power structure or electric wire, and during construction, the heat emitted from the electric wire is released to the outside, so that the electric power structure or electric wire in which the electric wire is wired. The ventilation unit 200 is configured so that its temperature can be maintained constant.

여기서, 통기부(200)는 난연성 후크 밴드(100)의 길이 방향으로 소정 간격 이격되게 다수개로 구성되되, 이 난연성 후크 밴드(100)의 양측 끝단부에 각각 서로 대응되는 위치에 구성되며, 난연성 후크 밴드(100)를 관통하는 형태로 구성된다. Here, the ventilation part 200 is composed of a plurality of pieces spaced apart at predetermined intervals in the longitudinal direction of the flame retardant hook band 100, and is configured at a position corresponding to each other at both ends of the flame retardant hook band 100, and the flame retardant hook It is configured in a form penetrating the band 100.

즉, 통기부(200)는 난연성 후크 밴드(100)가 전력 구조물, 또는 전선을 감싸도록 시공되는 경우, 상부 중앙에 서로 대응되는 위치에 각각 구성될 수 있도록 형성되는 것이다. That is, when the flame retardant hook band 100 is constructed to surround a power structure or an electric wire, the ventilation portion 200 is formed so that it can be configured at a position corresponding to each other in the upper center.

또한, 본 발명에는 통기부(200)의 내주면에 밀착되게 구성되며, 전력 구조물, 또는 전선을 감싸도록 시공된 난연성 후크 밴드(100)가 고정될 수 있도록 함과 동시에 난연성 후크 밴드(100)의 내부에 배치되는 전력 구조물, 또는 전선의 온도를 유지할 수 있도록 통기성을 제공하는 체결구(300)가 더 구성된다. In addition, in the present invention, the flame retardant hook band 100 is configured to be in close contact with the inner circumferential surface of the ventilation unit 200 and is constructed to surround a power structure or electric wire so that the flame retardant hook band 100 can be fixed and at the same time the inside of the flame retardant hook band 100 A fastener 300 providing air permeability is further configured to maintain the temperature of the electric power structure or electric wire disposed thereon.

여기서, 체결구(300)는 중앙부가 관통되어 통기부(200)와 같이 소정의 통기성을 제공하는 관통구(302)가 형성되고, 상단부 및 하단부 원주면을 따라 통기부(200)에 고정 결합되는 결합 플랜지가 형성되는 것으로, 금속링의 형태를 이루도록 구성된다. Here, the fastener 300 has a central portion through which a through-hole 302 providing a predetermined amount of air permeability is formed like the ventilation unit 200, and is fixedly coupled to the ventilation unit 200 along the upper and lower circumferential surfaces. A coupling flange is formed, which is configured to form a metal ring.

이러한 체결구(300)는 난연성 후크 밴드(100)의 양측 단부가 결합될 때, 다양한 형태로 이루어지는 결합수단과의 결합력을 제공하는 한편, 결합수단에 의해 통기부(200)가 훼손되어 통기성이 저하되는 것을 방지하는 역할을 한다. When both ends of the flame retardant hook band 100 are coupled to each other, the fastener 300 provides a coupling force with coupling means having various shapes, while the ventilation portion 200 is damaged by the coupling means, reducing air permeability. serves to prevent

이때, 결합수단은 도 4에 도시된 바와 같이, 와이어(310)로 이루어질 수 있으며, 체결구(300)에 형성된 관통구(302)를 관통하여 서로 대응되는 위치에 구성되는 각각의 통기부(200)들이 서로 연결되도록 구성될 수 있다. At this time, as shown in FIG. 4, the coupling means may be made of a wire 310, and each of the ventilation units 200 configured at positions corresponding to each other by penetrating through holes 302 formed in the fastener 300. ) may be configured to be connected to each other.

또한, 결합수단은 도 5에 도시된 바와 같이, 별도의 체결수단(320)에 의해 대응되는 위치에 구성되는 각각의 통기부(200)들을 연결하도록 구성될 수 있다. In addition, as shown in FIG. 5, the coupling means may be configured to connect the ventilation units 200 configured at corresponding positions by separate fastening means 320.

이때, 난연성 후크 밴드(100)는 통기부(200)가 형성되는 양측 단부가 서로 적층을 이루도록 구성되며, 이때, 통기부(200)의 중심이 동축선상에 위치할 수 있도록 구성될 수 있다. At this time, the flame retardant hook band 100 is configured such that both end portions at which the ventilation portion 200 is formed are stacked with each other, and at this time, the center of the ventilation portion 200 may be positioned on a coaxial line.

체결수단(320)은 중앙부가 관통되어 관통구(302)를 형성하고, 상부면이 적층된 난연성 후크 밴드(100)의 양측 단부 중, 상부에 위치하는 일측 단부와 밀착되도록 구성되며, 중앙부가 일측 및 타측 단부에 각각 구성된 통기부(200)를 관통하도록 구성된다. The fastening means 320 has a central portion passing through to form a through hole 302, and is configured to be in close contact with one end located at the upper portion of both ends of the flame retardant hook band 100 having an upper surface laminated thereon, And it is configured to pass through the ventilation part 200 respectively configured at the other end.

또한, 체결수단(320)에는 난연성 후크 밴드(100)의 양측 단부 중, 하부에 위치하는 타측 단부와 밀착되도록 구성되며, 중앙부가 일측 및 타측 단부에 각각 구성된 통기부(200)를 관통하면서 체결수단(320)과 끼움 결합 방식으로 결합이 이루어지도록 구성되는 체결 지지부재(340)를 더 구성할 수 있다. In addition, the fastening means 320 is configured to be in close contact with the other end located at the bottom of both ends of the flame retardant hook band 100, and the central portion passes through the ventilation part 200 formed at one and the other end, respectively, and the fastening means A fastening support member 340 configured to be coupled to 320 and a fitting coupling method may be further configured.

이와 같은 체결수단(320)은 통상의 가시 도트 단추, 또는 홀 가시 도트 단추로 이루어질 수 있으나, 이에 한정하는 것은 아니다.The fastening means 320 may be formed of a normal visible dot button or a hole visible dot button, but is not limited thereto.

아울러, 본 발명의 체결수단(320)은 도 6에 도시된 바와 같이, 난연성 후크 밴드(100)에는 전력 구조물, 또는 전선을 감싸는 시공이 이루어질 때, 난연성 후크 밴드(100)를 결합하기 위해 서로 대응되는 위치에 각각 구성되는 통기부(200)가 형성된 부분만을 감싸도록 구성되고, 체결수단(320)이 관통하면서 난연성 후크 밴드(100)와의 연결이 이루어지도록 구성되는 고정밴드(330)를 더 구성할 수 있다. In addition, as shown in FIG. 6, the fastening means 320 of the present invention correspond to each other in order to couple the flame retardant hook band 100 when construction is made to wrap the power structure or electric wire. It is configured to cover only the portion where the ventilation portion 200 is formed, respectively, and is configured to further configure a fixing band 330 configured to be connected to the flame retardant hook band 100 while the fastening means 320 penetrates. can

이때, 체결수단(320)은 고정밴드(330)를 통해 난연성 후크 밴드(100)의 결합이 이루어지는 경우, 전술한 단추로 구성될 수도 있으나, 바람직하게는 하단부에 체결구(300)와 접하면서 소정의 고정력을 제공하는 고정돌기가 형성되는 고정핀으로 구성될 수 있을 것이다.At this time, the fastening means 320 may be composed of the above-described button when the flame retardant hook band 100 is coupled through the fixing band 330, but preferably, while in contact with the fastener 300 at the lower end It may be composed of a fixing pin in which a fixing protrusion is formed to provide a fixing force of.

또한, 고정밴드(330)는 난연성 후크 밴드와 동일한 재질로 이루어질 수 있으나, 이에 한정하는 것은 아니며, 금속 재질의 밴드로 구성될 수도 있을 것이다.In addition, the fixing band 330 may be made of the same material as the flame retardant hook band, but is not limited thereto, and may be made of a metal band.

한편, 본 발명의 결합수단은 통상의 금속 재질의 클립으로도 구성될 수도 있다.On the other hand, the coupling means of the present invention may also be composed of a clip made of a conventional metal material.

아울러, 본 발명의 난연성 후크 밴드(100)에는 전력 구조물, 또는 전선을 감싸는 시공이 이루어질 때, 난연성 후크 밴드(100)의 형태를 유지하며, 상기 전력 구조물, 또는 전선의 상부로 통기부(200) 및 체결구(300)가 소정 간격 이격된 위치에 구성될 수 있도록 지지하는 밴드 지지패널(150)이 더 구성될 수 있다.In addition, the flame retardant hook band 100 of the present invention maintains the shape of the flame retardant hook band 100 when construction is performed to surround a power structure or wire, and the ventilation portion 200 is provided on top of the power structure or wire. And a band support panel 150 for supporting the fasteners 300 to be configured at positions spaced apart by a predetermined interval may be further configured.

밴드 지지패널(150)은 난연성 후크 밴드(100)의 양측부에 밀착되도록 구성되며, 이 난연성 후크 밴드(100)와의 결합력을 향상시키기 위하여 외면으로 복수개의 결합돌기(152)가 더 구성될 수도 있다. The band support panel 150 is configured to be in close contact with both sides of the flame retardant hook band 100, and a plurality of coupling protrusions 152 may be further configured on the outer surface to improve the bonding force with the flame retardant hook band 100. .

이때, 본 발명의 난연성 후크 밴드(100)는 전선, 특히 전력선과 신호선을 감싸는 시공이 이루어질 때, 도 7 및 도 8에 도시된 바와 같이, 전력선과 신호선을 각각 분리해서 감싸는 시공이 이루어지도록 구성된다. At this time, when the flame retardant hook band 100 of the present invention is constructed to wrap around wires, particularly power lines and signal lines, as shown in FIGS. 7 and 8, the power line and signal line are separately wrapped. .

즉, 종래에는 전력선과 신호선이 모두 뒤섞인 상태에서 시공이 이루어졌으며, 이로 인해 각각의 전선들의 종류를 파악하기 어려웠을 뿐만 아니라, 화재 발생시 신호선까지 화재에 의해 파손되어 건축물 내부에서의 통신이 원활하지 못하는 문제가 있었으나, 본 발명에서는 전력선과 신호선을 각각 분리하여 독립적으로 감싸는 형태로 시공이 이루어짐에 따라 전선들에 대한 종류를 쉽게 파악할 수 있음은 물론, 전력선에 의해 화재가 발생한다 하더라도 신호선을 보호할 수 있게 되는 것이다. That is, in the past, construction was performed in a state where both power lines and signal lines were mixed, which made it difficult to identify the types of each wire, and in the event of a fire, even the signal lines were damaged by fire, making communication within the building difficult. Although there was a problem, in the present invention, as the construction is carried out in the form of separating the power line and the signal line and wrapping them independently, the type of the wires can be easily identified, and the signal line can be protected even if a fire occurs due to the power line. there will be

한편, 본 발명의 상세한 설명에 미기재된 도면 부호 10은 전선을 지시하는 것이고, 도면부호 20은 전선이 배선되는 전력 구조물을 지시하는 것이다. 또한, 도면부호 30은 신호선을 지시하는 것이다.Meanwhile, reference numeral 10, which is not described in the detailed description of the present invention, indicates an electric wire, and reference numeral 20 indicates a power structure in which the electric wire is routed. Also, reference numeral 30 indicates a signal line.

이하에서는, 도 9를 참조하여 본 발명의 난연성 후크 밴드(100)에 대한 제조 방법을 설명하도록 한다. Hereinafter, a manufacturing method for the flame retardant hook band 100 of the present invention will be described with reference to FIG. 9 .

난연성 후크 밴드 제조 방법은 먼저, 난연성 레이온 단섬유와 아크릴 섬유를 탄화시키고, 탄화가 이루어진 섬유에 난연성 코팅액이 일정 두께로 코팅시켜 난연성 펠트(120)를 제조하는 난연성 펠트 제조단계(S110)를 수행한다. In the method for manufacturing a flame retardant hook band, first, a flame retardant felt manufacturing step (S110) of carbonizing short flame retardant rayon fibers and acrylic fibers and coating the carbonized fibers with a flame retardant coating solution to a certain thickness to produce a flame retardant felt 120 is performed. .

이후, 난연성을 제공하는 메타아라미드(m-Aramid) 소재의 실로 직조된 원단의 표면에 카본블랙(Carbon black) 박막을 일정 간격으로 배열한 후 증착하거나, 또는 분말 형태의 카본블랙이 일정 두께로 도포시켜 카본 섬유(110)를 제조하는 카본 섬유 제조단계(S120)를 수행한다. Subsequently, carbon black thin films are arranged at regular intervals on the surface of the fabric woven with m-Aramid yarns that provide flame retardancy, and then deposited, or carbon black in powder form is applied at a certain thickness. A carbon fiber manufacturing step (S120) of manufacturing the carbon fibers 110 is performed.

이때, 카본 섬유 제조단계(S120)는, 제조된 카본 섬유(110)의 상부면으로 부직포 형태의 흡착시트(130)를 부착하고, 하부면으로는 카본블랙의 탈리를 방지하는 이형지(140)를 부착하는 단계를 더 수행한다.At this time, in the carbon fiber manufacturing step (S120), an adsorbent sheet 130 in the form of a non-woven fabric is attached to the upper surface of the manufactured carbon fiber 110, and a release paper 140 for preventing separation of carbon black is attached to the lower surface. Further attaching steps are performed.

이후, 카본 섬유(110)의 상부면에 난연성 펠트(120)를 안착시킨 후, 니들 펠트 방식으로 재봉하여 카본 섬유(110)와 난연성 펠트(120)를 결합시켜 난연성 후크 밴드(100)의 본체를 제조하는 니들펠트 단계(S130)를 수행한다. Thereafter, after the flame retardant felt 120 is seated on the upper surface of the carbon fiber 110, sewing is performed using a needle felt method to combine the carbon fiber 110 and the flame retardant felt 120 to form the main body of the flame retardant hook band 100. The manufacturing needle felt step (S130) is performed.

다음으로, 전술한 니들펠트 단계(S130)를 통해 제조된 난연성 후크 밴드(100)의 양측 단부를 펀칭 등과 같은 설비로 관통시켜 다수개의 통기부(200)를 형성하는 통기부 형성단계(S140)를 수행한다. Next, a ventilation unit forming step (S140) of forming a plurality of ventilation units 200 by penetrating both ends of the flame retardant hook band 100 manufactured through the above-described needle felting step (S130) with equipment such as punching. carry out

한편, 본 발명에서는 상기 통기부(200)의 내주면에 밀착되며, 전력 구조물, 또는 전선을 감싸도록 시공된 난연성 후크 밴드(100)가 고정될 수 있도록 지지하고, 전력 구조물, 또는 전선의 온도를 유지할 수 있도록 통기성을 제공하는 체결구(300)를 결합하는 결합단계(S150)를 수행할 수 있다.On the other hand, in the present invention, the flame retardant hook band 100 is adhered to the inner circumferential surface of the ventilating part 200 and is constructed to surround a power structure or electric wire. A coupling step (S150) of coupling the fastener 300 that provides air permeability can be performed.

아울러, 상기 결합단계(S150)는 체결구(300)의 결합이 완료된 이후, 난연성 후크 밴드(100)의 양측 단부에 대한 용이한 결합이 이루어질 수 있도록 결합수단을 더 결합시키는 단계를 수행할 수도 있다.In addition, in the coupling step (S150), after the coupling of the fastener 300 is completed, a step of further coupling the coupling means may be performed so that both ends of the flame retardant hook band 100 can be easily coupled. .

이상의 설명은 본 발명의 기술 사상을 예시적으로 설명한 것에 불과한 것으로서, 본 발명이 속하는 기술 분야에서 통상의 지식을 가진 자라면 본 발명의 본질적인 특성에서 벗어나지 않는 범위에서 다양한 수정 및 변형이 가능할 것이다. 따라서, 본 발명에 개시된 실시예들은 본 발명의 기술 사상을 한정하기 위한 것이 아니라 설명하기 위한 것이고, 이러한 실시예에 의하여 본 발명의 기술 사상의 범위가 한정되는 것은 아니다. 본 발명의 보호 범위는 아래의 청구범위에 의하여 해석되어야 하며, 그와 동등한 범위 내에 있는 모든 기술 사상은 본 발명의 권리범위에 포함되는 것으로 해석되어야 할 것이다.The above description is merely an example of the technical idea of the present invention, and various modifications and variations can be made to those skilled in the art without departing from the essential characteristics of the present invention. Therefore, the embodiments disclosed in the present invention are not intended to limit the technical idea of the present invention, but to explain, and the scope of the technical idea of the present invention is not limited by these embodiments. The protection scope of the present invention should be construed according to the claims below, and all technical ideas within the equivalent range should be construed as being included in the scope of the present invention.

110: 카본 섬유 120: 난연성 펠트
130: 흡착시트 140: 이형지
200: 통기부 300: 체결구
302: 관통구 310: 와이어
320: 체결수단 330: 고정밴드
340: 체결 지지부재110: carbon fiber 120: flame retardant felt
130: adsorption sheet 140: release paper
200: ventilation part 300: fastener
302: through hole 310: wire
320: fastening means 330: fixed band
340: fastening support member

Claims (8)

니들 펠트 방식으로 상부면 및 하부면에 각각 흡착시트와 이형지가 부착된 카본 섬유와 난연성 펠트를 재봉하여 제조되는 본체부;
상기 본체부의 양측 단부에 소정 간격 이격되게 다수개로 구성되어, 전선의 온도를 일정하게 유지시켜 줄 수 있도록 난연성 후크 밴드의 양측 끝단부에 각각 서로 대응되는 위치에 구성되며, 상기 난연성 후크 밴드를 관통하는 형태로 구성되는 통기부;
상기 통기부의 내주면에 밀착되며, 상기 본체부의 양측 단부의 결합이 이루어지도록 지지하는 체결구;
상기 체결구를 관통하여 서로 대응되는 위치에 구성되는 각각의 상기 통기부들을 연결하여, 난연성 후크 밴드를 결합시키는 결합수단;
서로 대응되는 위치에 구성되는 각각의 상기 통기부들을 연결하기 위해 앙부가 관통되어 관통구를 형성하고, 상부면이 적층된 난연성 후크 밴드의 양측 단부 중, 상부에 위치하는 일측 단부와 밀착되도록 구성되며, 중앙부가 상기 통기부, 또는 상기 통기부에 밀착된 체결구를 관통하는 체결수단;
상기 체결수단에 구성되며, 상기 난연성 후크 밴드의 양측 단부 중, 하부에 위치하는 타측 단부와 밀착되도록 구성되며, 중앙부가 일측 및 타측 단부에 각각 구성된 통기부를 관통하면서 상기 체결수단과 결합되는 체결 지지부재;
상기 통기부가 형성된 부분만을 감싸도록 구성되고, 상기 체결수단이 관통하면서 상기 난연성 후크 밴드와의 연결이 이루어지도록 구성되는 고정밴드;를 포함하고,
상기 난연성 펠트는, 탄화가 이루어진 섬유에 총 중량에 있어서, 실리카 50중량%~70중량%, 알루미나 20중량%~30중량%, 지르코니아 5중량%~10중량%, 탄소 5중량%~10중량%의 비율로 혼합된 혼합물로 이루어지는 난연성 코팅액이 코팅되도록 구성되는 것을 특징으로 하는 난연성 후크 밴드.
A body part manufactured by sewing carbon fiber and a flame retardant felt to which an adsorption sheet and a release paper are attached to upper and lower surfaces, respectively, in a needle felt method;
It is composed of a plurality of pieces spaced apart from each other at a predetermined interval at both ends of the main body, and is configured at a position corresponding to each other at both ends of the flame retardant hook band to keep the temperature of the wire constant, penetrating the flame retardant hook band Ventilation unit configured in the form;
fasteners that are in close contact with the inner circumferential surface of the ventilating part and support such that both end portions of the main body part are coupled;
coupling means for coupling a flame retardant hook band by connecting the ventilation units configured at corresponding positions through the fasteners;
In order to connect each of the ventilation units configured at positions corresponding to each other, the rim part is penetrated to form a through hole, and the upper surface is configured to be in close contact with one end located on the upper side of both ends of the stacked flame retardant hook band, , Fastening means through which a central portion passes through the ventilation unit or a fastener in close contact with the ventilation unit;
It is composed of the fastening means, and is configured to be in close contact with the other end located at the bottom of both ends of the flame retardant hook band, and the central portion is coupled to the fastening means while passing through the ventilation part formed at one and the other end portion. absence;
A fixing band configured to surround only a portion where the ventilation portion is formed and configured to be connected to the flame retardant hook band while the fastening means passes through,
The flame retardant felt is composed of 50% to 70% by weight of silica, 20% to 30% by weight of alumina, 5% to 10% by weight of zirconia, and 5% to 10% by weight of carbon, based on the total weight of carbonized fibers. A flame retardant hook band, characterized in that configured to be coated with a flame retardant coating liquid consisting of a mixture mixed in a ratio of.
 삭제delete 삭제delete 삭제delete 삭제delete 제1항에 있어서,
상기 난연성 후크 밴드에는
전력 구조물, 또는 전선의 상부로 상기 통기부 및 체결구가 소정 간격 이격된 위치에 구성될 수 있도록 상기 난연성 후크 밴드의 양측부에 밀착되도록 구성되며, 외면으로 복수개의 결합돌기가 형성된 밴드 지지패널이 더 구성되는 것을 특징으로 하는 난연성 후크 밴드.
According to claim 1,
The flame retardant hook band
The band support panel is configured to be in close contact with both sides of the flame retardant hook band so that the ventilation part and the fastener can be configured at a position spaced apart from a predetermined distance on the top of the power structure or electric wire, and a plurality of coupling protrusions are formed on the outer surface. A flame retardant hook band, characterized in that further configured.
 난연성 후크 밴드 제조 방법에 있어서,
난연성 레이온 단섬유와 아크릴 섬유를 탄화시키고, 탄화가 이루어진 섬유에 총 중량에 있어서, 실리카 50중량%~70중량%, 알루미나 20중량%~30중량%, 지르코니아 5중량%~10중량%, 탄소 5중량%~10중량%의 비율로 혼합된 혼합물로 이루어지는 난연성 코팅액이 일정 두께로 코팅시켜 난연성 펠트를 제조하는 난연성 펠트 제조단계;
메타아라미드(m-Aramid) 소재의 실로 직조된 원단에 카본블랙이 증착, 또는 도포된 카본 섬유를 제조하는 카본 섬유 제조단계;
상기 카본 섬유의 상부면에 상기 난연성 펠트를 안착시킨 후, 니들 펠트 방식으로 재봉하여 상기 카본 섬유와 난연성 펠트를 결합시켜 난연성 후크 밴드의 본체부를 제조하는 니들펠트 단계;
상기 본체부의 양측 단부를 관통시켜 다수개의 통기부를 형성하는 통기부 형성단계; 및
상기 통기부에 체결구를 결합하는 결합단계;
를 포함하는 것을 특징으로 하는 난연성 후크 밴드 제조 방법.
In the flame retardant hook band manufacturing method,
Flame retardant short rayon fibers and acrylic fibers are carbonized, and in the total weight of the carbonized fibers, silica 50% to 70% by weight, alumina 20% to 30% by weight, zirconia 5% to 10% by weight, carbon 5 A flame retardant felt manufacturing step of preparing a flame retardant felt by coating a flame retardant coating solution consisting of a mixture in a ratio of weight% to 10% by weight to a certain thickness;
A carbon fiber manufacturing step of preparing carbon fibers in which carbon black is deposited or coated on a fabric woven with threads of meta aramid (m-Aramid);
A needle felting step of seating the flame retardant felt on the upper surface of the carbon fiber and then sewing the carbon fiber and the flame retardant felt together in a needle felt method to manufacture a main body of the flame retardant hook band;
Ventilation part forming step of forming a plurality of ventilation parts by penetrating both ends of the body part; and
A coupling step of coupling a fastener to the ventilation unit;
A flame retardant hook band manufacturing method comprising a.
 제7항에 있어서,
상기 카본 섬유 제조단계는,
상기 카본 섬유의 상부면으로 부직포 형태의 흡착시트를 부착하고, 하부면으로는 카본블랙의 탈리를 방지하는 이형를 부착하는 단계를 더 수행하는 것을 특징으로 하는 난연성 후크 밴드 제조 방법.
According to claim 7,
The carbon fiber manufacturing step,
The method of manufacturing a flame retardant hook band, characterized in that further performing the step of attaching a non-woven fabric type adsorption sheet to the upper surface of the carbon fiber and attaching a release for preventing separation of carbon black to the lower surface.
KR1020200140212A 2020-10-27 2020-10-27 Flame retardant hook band and manufacturing method thereof KR102506376B1 (en)