KR102473642B1 - IR blocking windowfilm for easy attachment through pattern printing - Google Patents
IR blocking windowfilm for easy attachment through pattern printing Download PDFInfo
- Publication number
- KR102473642B1 KR102473642B1 KR1020200156696A KR20200156696A KR102473642B1 KR 102473642 B1 KR102473642 B1 KR 102473642B1 KR 1020200156696 A KR1020200156696 A KR 1020200156696A KR 20200156696 A KR20200156696 A KR 20200156696A KR 102473642 B1 KR102473642 B1 KR 102473642B1
- Authority
- KR
- South Korea
- Prior art keywords
- weight
- parts
- adhesive
- monomer
- blocking
- Prior art date
Abstract
본 발명은 에 관한 것으로, 본 발명에 따르면, 기재필름; 상기 기재필름 일면에 형성되어 적외선을 차단하는 IR 차단층 및 상기 기재필름 타면에 로타리스크린을 통해 무용제 UV 점착제로 패턴 코팅되어 형성되는 점착층을 포함하는 IR 차단 윈도우필름을 제공할 수 있다.The present invention relates to, according to the present invention, a base film; It is possible to provide an IR blocking window film including an IR blocking layer formed on one side of the base film to block infrared rays and an adhesive layer formed by pattern coating the other side of the base film with a solvent-free UV adhesive through a rotary screen.
Description
본 발명은 패턴 인쇄를 통해 부착이 용이한 IR 차단 윈도우필름에 관한 것으로, 더욱 자세하게는 로타리스크린 인쇄를 통해 무용제 UV 점착제를 기재필름에 패턴 코팅시킴으로써, 잔사가 남지 않고 에어프리 기능을 나타낼 수 있는 패턴 인쇄를 통해 부착이 용이한 IR 차단 윈도우필름에 관한 것이다.The present invention relates to an IR blocking window film that is easily attached through pattern printing, and more particularly, a pattern that can exhibit an air-free function without leaving residues by coating a base film with a solvent-free UV adhesive in a pattern through rotary screen printing It relates to an IR blocking window film that is easily attached through printing.
종래 차량이나 건물의 유리창에는 다양한 기능성 필름이 부착되어 사용되었다. 이들 필름이 제공하는 기능은 예를 들어, 실내에서 활동하는 사람들의 피부노화나 실내 용품의 탈색, 변색 등을 일으킬 수 있는 자외선을 차단하는 기능, 실내 온도를 유지할 수 있도록 적외선을 차단하는 기능, 또는 외부충격으로 유리가 파손되는 것을 막아주거나 파손된 유리가 비산하지 않도록 하는 안전 기능, 또는 적정한 착색을 이용해 실내 생활 공간에 대한 프라이버시를 보호하는 기능 등 다양하다. 이러한 기능성 필름은 다층의 필름들 사이에 여러가지 물질이 코팅된 적층 구조를 가지는 것이 일반적이다.Conventionally, various functional films have been attached to and used on glass windows of vehicles or buildings. The functions provided by these films include, for example, a function to block ultraviolet rays that can cause skin aging of people who are active indoors or discoloration or discoloration of indoor products, a function to block infrared rays to maintain indoor temperature, or There are various safety functions such as preventing glass from being damaged by external impact or preventing broken glass from scattering, or protecting the privacy of the indoor living space by using appropriate coloring. These functional films generally have a laminated structure in which various materials are coated between multi-layered films.
일 예로, 한국등록특허 제10-1472861호(발명의 명칭: 가시광선 및 근적외선 차단특성을 가지는 필름)은 질소를 함유하는 무기화합물 입자를 포함하는 차폐층과, 상기 차폐층의 일면에 위치하여 상기 차폐층을 지지하는 지지층을 포함하는 필름을 개시하고 있다.For example, Korean Patent Registration No. 10-1472861 (title of the invention: a film having visible and near infrared ray blocking properties) discloses a shielding layer containing inorganic compound particles containing nitrogen and located on one side of the shielding layer, A film comprising a support layer supporting a shielding layer is disclosed.
종래의 열차단점착필름은 필름과 피착면의 두 층 사이에 공기를 제거하기가 어려웠다. 공기가 남아있지 않도록 시공하려면 시공 전문가이거나 일반인의 경우 상당한 주의와 노력이 필요했다.In the conventional thermal barrier adhesive film, it is difficult to remove air between the two layers of the film and the adherend surface. Construction experts or ordinary people needed considerable attention and effort to construct so that there was no air left.
또한, 이러한 종래의 필름은 유리창 등의 기재에 부착되는데 있어서 필름과 기재 사이에 쉽게 공기층이 형성되어 시간이 지날 시 접착력이 떨어지는 문제가 있었다. In addition, when these conventional films are attached to a substrate such as a glass window, an air layer is easily formed between the film and the substrate, resulting in poor adhesive strength over time.
또한, 이와 같이 형성된 공기층을 그대로 두기에는 미관상으로 문제가 있었으며, 공기층을 제거하기 위해 필름에 흠집을 내게되면 시간이 지남에 따라 흠집부분이 벌어져 하자가 발생하는 문제점이 있었다.In addition, there was an aesthetic problem in leaving the formed air layer as it is, and when the film is scratched to remove the air layer, the scratched portion widens over time, resulting in a defect.
상기와 같은 문제를 해결하기 위해 최근 점착 시트에 엠보 패턴을 형성하여 점착층에 기포가 형성되지 않도록 하여 부착력을 높이는 에어프리 기능을 겸비한 점착시트가 개발되었다.In order to solve the above problems, recently, a pressure-sensitive adhesive sheet having an air-free function that increases adhesion by forming an embossed pattern on the pressure-sensitive adhesive sheet to prevent air bubbles from forming on the pressure-sensitive adhesive layer has been developed.
이러한 점착시트를 제조하기 위한 종래의 방법으로, 로타리스크린 인쇄를 통해 점착제를 기재에 패턴 코팅시켜 점착시트를 제조하는 방법이 있으며, 여기서 점착제는 수분산점착제가 사용되었다.As a conventional method for manufacturing such an adhesive sheet, there is a method of manufacturing an adhesive sheet by pattern-coating an adhesive on a substrate through rotary screen printing, wherein a water-dispersible adhesive is used as the adhesive.
이러한 방법에는 유화제로 인해 마이그레이션이 되어 점착력이 저하되고 내수성에 취약하고, 기재밀착성이 좋지 않아 잔사가 발생하는 문제가 있었다.In this method, there was a problem in that the emulsifier migrated, resulting in reduced adhesive strength, poor water resistance, and poor adhesion to the substrate, resulting in residue.
또한, 수분산점착제를 건조시키기 위해 열에너지가 많이 필요하며, 패턴의 입체감이 저하되는 단점이 있었다.In addition, a lot of heat energy is required to dry the water-dispersible pressure-sensitive adhesive, and there is a disadvantage in that the three-dimensional effect of the pattern is lowered.
또한, 유리전이온도(Tg)가 낮은 기재에는 적용할 수 없는 한계가 있었으며, 유리전이온도(Tg)가 낮은 기재에 적용하기 위해서는 이형지에 패턴을 코팅한 후 이형지 위에 점착제를 코팅하여 기재에 전사시켜야 하는 방법을 이용해야 했으므로, 공정과정이 매우 복잡해지는 큰 문제가 있었다.In addition, there is a limitation that it cannot be applied to substrates with a low glass transition temperature (Tg), and in order to apply to substrates with a low glass transition temperature (Tg), it is necessary to coat a pattern on release paper and then coat an adhesive on the release paper to transfer it to the substrate. Since the method had to be used, there was a big problem that the process was very complicated.
상기와 같은 문제를 해결하고자, 본 발명은 로타리스크린 인쇄를 통해 무용제 UV 점착제를 기재필름에 패턴 코팅시킴으로써, 잔사가 남지 않고 에어프리 기능을 나타낼 수 있는 패턴 인쇄를 통해 부착이 용이한 IR 차단 윈도우필름을 제공하는데 목적이 있다.In order to solve the above problems, the present invention is an IR blocking window film that is easy to attach through pattern printing that can exhibit an air-free function without leaving residues by pattern-coating a solvent-free UV adhesive on a base film through rotary screen printing. It aims to provide
상기와 같은 과제를 해결하기 위하여, 본 발명의 실시예에 따른 패턴 인쇄를 통해 부착이 용이한 IR 차단 윈도우필름은 기재필름; 상기 기재필름 일면에 형성되어 적외선을 차단하는 IR 차단층 및 상기 기재필름 타면에 로타리스크린을 통해 무용제 UV 점착제로 패턴 코팅되어 형성되는 점착층을 포함하는 IR 차단 윈도우필름을 제공할 수 있다.In order to solve the above problems, an IR blocking window film that is easily attached through pattern printing according to an embodiment of the present invention includes a base film; It is possible to provide an IR blocking window film including an IR blocking layer formed on one side of the base film to block infrared rays and an adhesive layer formed by pattern coating the other side of the base film with a solvent-free UV adhesive through a rotary screen.
여기서, 상기 IR 차단층은 무기입자 분산액, 열경화성 수지, UV흡수첨가제 및 경화제를 포함할 수 있다.Here, the IR blocking layer may include an inorganic particle dispersion, a thermosetting resin, a UV absorbing additive, and a curing agent.
또한 상기 무기입자 분산액은 세슘, 텅스텐, 주석, 안티모니 중 2종 이상의 분산액인 것을 특징으로 한다.In addition, the inorganic particle dispersion is characterized in that it is a dispersion of two or more kinds of cesium, tungsten, tin, and antimony.
또한 상기 IR 차단층은 상기 무기입자 분산액 10 내지 20중량부, 열경화성 수지 80 내지 90중량부, UV흡수첨가제 1 내지 4중량부 및 경화제 1 내지 9중량부를 포함하는 것을 특징으로 한다.In addition, the IR blocking layer may include 10 to 20 parts by weight of the inorganic particle dispersion, 80 to 90 parts by weight of a thermosetting resin, 1 to 4 parts by weight of a UV absorbing additive, and 1 to 9 parts by weight of a curing agent.
또한 상기 무용제 UV 점착제는 주제, 모노머, 다관능 아크릴레이트 및 개시제를 포함할 수 있다.In addition, the non-solvent UV adhesive may include a main agent, a monomer, a multifunctional acrylate, and an initiator.
또한 상기 주제는 폴리에스테르, 폴리염화비닐, 폴리비닐알콜, 폴리에틸렌비닐아세테이트, 폴리에틸렌비닐알콜, 폴리우레탄, 폴리비닐아세테이트, 폴리우레탄아크릴레이트 및 폴리아크릴레이트 중 1종 이상인 것을 특징으로 한다.In addition, the subject is characterized in that at least one of polyester, polyvinyl chloride, polyvinyl alcohol, polyethylene vinyl acetate, polyethylene vinyl alcohol, polyurethane, polyvinyl acetate, polyurethane acrylate and polyacrylate.
또한 상기 모노머는 산 관능기를 가지는 아크릴계 모노머; 하이드록시 관능기를 갖는 아크릴계 모노머; 아크릴 모노머 및 비닐계 모노머로 이루어진 군으로부터 선택된 1종 이상의 중합성 모노머; 중 2종 이상을 포함하는 것을 특징으로 한다.In addition, the monomer may include an acrylic monomer having an acid functional group; an acrylic monomer having a hydroxyl functional group; At least one polymerizable monomer selected from the group consisting of an acrylic monomer and a vinyl monomer; It is characterized by including two or more of them.
또한 상기 모노머는 산 관능기를 가지는 아크릴계 모노머 5 내지 15중량%, 하이드록시 관능기를 갖는 아크릴계 모노머 25 내지 65중량% 및 중합성 모노머 29 내지 60중량%를 포함하는 것을 특징으로 한다.In addition, the monomer is characterized by comprising 5 to 15% by weight of an acrylic monomer having an acid functional group, 25 to 65% by weight of an acrylic monomer having a hydroxyl functional group, and 29 to 60% by weight of a polymerizable monomer.
또한 상기 산 관능기를 가지는 아크릴계 모노머는 아크릴산(AA)이고, 상기 하이드록시 관능기를 갖는 아크릴계 모노머는 하이드록시프로필 아크릴레이트(HPA)이며, 상기 중합성 모노머는 에틸헥실 아크릴레이트(EHA) 및 이소보닐 아크릴레이트 (IBOA)인 것을 특징으로 한다.In addition, the acrylic monomer having the acid functional group is acrylic acid (AA), the acrylic monomer having the hydroxy functional group is hydroxypropyl acrylate (HPA), and the polymerizable monomer is ethylhexyl acrylate (EHA) and isobornyl acryl rate (IBOA).
또한 상기 무용제 UV 점착제는 주제 40 내지 80중량부, 모노머 10 내지 30중량부, 다관능 아크릴레이트 0.1 내지 30중량부 및 개시제 0.1 내지 9중량부를 포함하는 것을 특징으로 한다.In addition, the solvent-free UV adhesive is characterized in that it comprises 40 to 80 parts by weight of the main agent, 10 to 30 parts by weight of the monomer, 0.1 to 30 parts by weight of the multifunctional acrylate, and 0.1 to 9 parts by weight of the initiator.
상기와 같은 본 발명의 실시예에 따른 패턴 인쇄를 통해 부착이 용이한 IR 차단 윈도우필름은 로타리스크린 인쇄를 통해 무용제 UV 점착제를 기재필름에 패턴 코팅시켜 점착층을 형성시킴으로써, 에어프리 기능을 통해 시공편의성 및 부착성이 개선되며 잔사가 남지 않을 수 있다.The IR blocking window film that is easily attached through pattern printing according to the embodiment of the present invention as described above is applied through the air-free function by pattern coating the base film with a solvent-free UV adhesive through rotary screen printing to form an adhesive layer. Convenience and adhesion are improved, and residues may not be left.
또한, 유리전이온도(Tg)가 낮은 기재필름에도 적용할 수 있어 다양한 기재필름을 사용할 수 있다.In addition, since it can be applied to a base film having a low glass transition temperature (Tg), various base films can be used.
도 1은 본 발명의 실시예에 따른 패턴 인쇄를 통해 부착이 용이한 IR 차단 윈도우필름을 개략적으로 도시한 예시도.1 is an exemplary view schematically showing an IR blocking window film that is easily attached through pattern printing according to an embodiment of the present invention.
이하, 도면을 참조한 본 발명의 설명은 특정한 실시 형태에 대해 한정되지 않으며, 다양한 변환을 가할 수 있고 여러 가지 실시예를 가질 수 있다. 또한, 이하에서 설명하는 내용은 본 발명의 사상 및 기술 범위에 포함되는 모든 변환, 균등물 내지 대체물을 포함하는 것으로 이해되어야 한다.Hereinafter, the description of the present invention with reference to the drawings is not limited to specific embodiments, and various transformations may be applied and various embodiments may be applied. In addition, the content described below should be understood to include all conversions, equivalents, or substitutes included in the spirit and scope of the present invention.
이하의 설명에서 제1, 제2 등의 용어는 다양한 구성요소들을 설명하는데 사용되는 용어로서, 그 자체에 의미가 한정되지 아니하며, 하나의 구성요소를 다른 구성요소로부터 구별하는 목적으로만 사용된다.In the following description, terms such as first and second are terms used to describe various components, and are not limited in meaning per se, and are used only for the purpose of distinguishing one component from another.
본 명세서 전체에 걸쳐 사용되는 동일한 참조번호는 동일한 구성요소를 나타낸다.Like reference numbers used throughout this specification indicate like elements.
본 발명에서 사용되는 단수의 표현은 문맥상 명백하게 다르게 뜻하지 않는 한, 복수의 표현을 포함한다. 또한, 이하에서 기재되는 "포함하다", "구비하다" 또는 "가지다" 등의 용어는 명세서상에 기재된 특징, 숫자, 단계, 동작, 구성요소, 부품 또는 이들을 조합한 것이 존재함을 지정하려는 것으로 해석되어야 하며, 하나 또는 그 이상의 다른 특징들이나, 숫자, 단계, 동작, 구성요소, 부품 또는 이들을 조합한 것들의 존재 또는 부가 가능성을 미리 배제하지 않는 것으로 이해되어야 한다.Singular expressions used in the present invention include plural expressions unless the context clearly dictates otherwise. In addition, terms such as "include", "include" or "have" described below are intended to designate that features, numbers, steps, operations, components, parts, or combinations thereof described in the specification exist. should be construed, and understood not to preclude the possibility of the presence or addition of one or more other features, numbers, steps, operations, components, parts, or combinations thereof.
이하, 본 발명의 실시 예를 첨부한 도 1을 참조하여 상세히 설명하기로 한다.Hereinafter, an embodiment of the present invention will be described in detail with reference to FIG. 1 attached.
도 1은 본 발명의 실시예에 따른 패턴 인쇄를 통해 부착이 용이한 IR 차단 윈도우필름을 개략적으로 도시한 예시도이다.1 is an exemplary view schematically showing an IR blocking window film that is easily attached through pattern printing according to an embodiment of the present invention.
도 1을 참조하면, 본 발명의 실시예에 따른 패턴 인쇄를 통해 부착이 용이한 IR 차단 윈도우필름(이하, 'IR 차단 윈도우필름'이라 함)은 기재필름(10), IR 차단층(20), 점착층(30) 및 이형지(40)를 포함할 수 있다.Referring to FIG. 1 , an IR blocking window film (hereinafter referred to as 'IR blocking window film') that is easily attached through pattern printing according to an embodiment of the present invention includes a
기재필름(10)은 투명, 반투명, 불투명 필름 중 하나로 이루어질 수 있으며, 발포필름 등으로도 이루어질 수 있다.The
바람직하게는 폴리올레핀, 폴리염화비닐, 폴리프로필렌(PP), 폴리에틸렌 테레프탈레이트(PET), 폴리스티렌, 폴리 메타크릴레이트 및 폴리카보네이트(PC) 중 하나로 구성된 필름 또는 2종 이상으로 구성된 복합필름일 수 있으나, 이에 한정되지 않고 트라이아세틸셀룰로오스(TAC), 폴리에터설폰, 폴리아크릴계 수지, 폴리우레탄계수지, 폴리에스터, 폴리술폰, 폴리메틸펜텐, 폴리에터케톤, 다이아세틸렌셀룰로오스, 아세테이트뷰틸레이트셀룰로오스, (메타)아크릴나이트릴 등의 플라스틱 필름으로도 이루어질 수 있다.Preferably, it may be a film composed of one of polyolefin, polyvinyl chloride, polypropylene (PP), polyethylene terephthalate (PET), polystyrene, polymethacrylate, and polycarbonate (PC), or a composite film composed of two or more kinds, It is not limited to triacetyl cellulose (TAC), polyethersulfone, polyacrylic resin, polyurethane resin, polyester, polysulfone, polymethylpentene, polyether ketone, diacetylene cellulose, acetate butylate cellulose, (meta ) It may also be made of a plastic film such as acrylonitrile.
또한, 기재필름(10)은 폴리에틸렌테레프탈레이트(PET) 또는 폴리카보네이트(PC) 100중량부에 대하여 TPAE(Thermoplastic Polyamide Elastomers) 5 내지 30중량부를 포함하여 형성될 수 있다.In addition, the
이때, TPAE의 배합량이 5 중량부 미만일 경우, 폴리에틸렌테레프탈레이트(PET) 또는 폴리카보네이트(PC)의 성형성에 대한 효과가 미미할 수 있고, 30중량부를 초과할 경우, 폴리에틸렌테레프탈레이트(PET) 또는 폴리카보네이트(PC)와 혼용성이 떨어져 기재필름(10)이 가지고 있는 유연성이 저하될 수 있다.At this time, when the blending amount of TPAE is less than 5 parts by weight, the effect on the moldability of polyethylene terephthalate (PET) or polycarbonate (PC) may be insignificant, and when it exceeds 30 parts by weight, polyethylene terephthalate (PET) or polycarbonate The compatibility with (PC) is poor, and the flexibility of the
기재필름(10)은 플라스틱 필름으로 구비될 시 세라믹이 혼합되어 형성될 수 있다.When provided as a plastic film, the
이는, 표면이 수분을 배척하는 소수성을 형성하며, 통기성이 좋지 못한 플라스틱의 특성을 보완하기 위한 것으로서, 플라스틱 필름에 세라믹을 첨가함으로써 강도가 우수하면서도 친수성과 통기성이 향상된 플라스틱 필름이 구비될 수 있다. This is to form a hydrophobic surface that rejects moisture and to compensate for the characteristics of plastic with poor air permeability, and by adding ceramic to the plastic film, a plastic film with excellent strength and improved hydrophilicity and air permeability can be provided.
여기서, 세라믹은 이산화규소, 이산화 타이타늄, 운모, 점토, 황토, 제올라이트 중 하나의 입자로 구비될 수 있다.Here, the ceramic may be provided with particles of one of silicon dioxide, titanium dioxide, mica, clay, loess, and zeolite.
또한, 플라스틱 필름, 세라믹, 상용화제의 비율은 8:1:1 내지 5:4:1의 비율로 혼합될 수 있다. (상용화제는 항상 1의 비율을 유지하며, 5:4:1의 비율로 근접할수록 친수성과 통기성이 우수하게 형성된다)In addition, the plastic film, ceramic, and compatibilizer may be mixed in a ratio of 8:1:1 to 5:4:1. (The compatibilizer always maintains a ratio of 1, and the closer the ratio of 5:4:1, the better the hydrophilicity and air permeability)
또한, 세라믹은 항균성을 가미하기 위하여 플라스틱과의 혼합 전에 은이 함유되도록 형성될 수 있다. In addition, the ceramic may be formed to contain silver before mixing with plastic to add antibacterial properties.
즉, 세라믹이 혼합되어 형성되는 플라스틱 필름은 친수성과 통기성이 향상될 뿐 아니라 항균성도 향상될 수 있다.That is, a plastic film formed by mixing ceramics may have improved hydrophilicity and air permeability as well as improved antibacterial properties.
이를 통해, 기재필름(10)은 플라스틱 필름으로 형성될 시에 IR 차단층(20) 및 점착층(30)이 보다 잘 형성될 수 있다.Through this, when the
이러한 기재필름(10)은 20㎛ 내지 250㎛의 두께로 형성되는 것이 다른 층을 형성하기에 바람직하며, 제거 시 가해지는 일정 힘을 버티는데 바람직하다.The
IR 차단층(20)은 기재필름(10) 일면에 형성되어 적외선을 차단할 수 있다. 이를 위해, 무기입자 분산액, 열경화성 수지, UV흡수첨가제 및 경화제를 포함할 수 있으나, 이에 한정되지 않고, UV흡수첨가제 등이 빠지거나 다른 조성물이 더 포함되는 등 다양하게 변경될 수도 있다.The
무기입자 분산액은 IR을 흡수할 수 있도록 하는 것으로, 세슘, 텅스텐, 주석, 안티모니 중 2종 이상의 분산액일 수 있으며, 모두 포함하는 것이 바람직하나 이에 한정되지는 않는다. 세슘, 텅스텐, 주석, 안티모니를 단독으로 사용하지 않고 혼합하여 사용함으로써 IR을 보다 용이하게 흡수할 수 있다.The inorganic particle dispersion is capable of absorbing IR, and may be a dispersion of two or more of cesium, tungsten, tin, and antimony, and preferably includes all, but is not limited thereto. IR can be more easily absorbed by mixing and using cesium, tungsten, tin, and antimony instead of alone.
이러한 무기입자 분산액은 10 내지 20중량부를 포함할 수 있는데, 10중량부 미만일 경우 IR 흡수가 용이하게 이루어지지 않을 수 있고, 20중량부 초과일 경우 층 형성에 어려움이 발생할 수 있기 때문이다.This inorganic particle dispersion may include 10 to 20 parts by weight, because IR absorption may not be easily achieved when less than 10 parts by weight, and difficulties may occur in layer formation when it exceeds 20 parts by weight.
열경화성 수지는 IR 차단층(20)이 코팅에 의해 층으로 형성될 수 있도록 하는 것으로, 우레탄 수지, 에폭시 수지 및 폴리염화비닐 수지 중 단독 또는 2종 이상일 수 있으나, 이에 한정되지는 않는다.The thermosetting resin is to allow the
또한 열경화성 수지는 80 내지 90중량부를 포함할 수 있다. 이때 열경화성 수지가 80중량부 미만일 경우 층 형성에 문제가 발생할 수 있고, 90중량부 초과할 경우 경화가 어려울 수 있다.In addition, the thermosetting resin may include 80 to 90 parts by weight. At this time, if the thermosetting resin is less than 80 parts by weight, problems may occur in layer formation, and if it exceeds 90 parts by weight, curing may be difficult.
UV흡수첨가제는 IR의 흡수만이 아닌 UV도 함께 차단할 수 있도록 첨가되는 것으로, 1 내지 4중량부가 포함될 수 있다. 1중량부 미만일 경우 UV 차단 기능을 바람직하게 나타낼 수 없으며, 4중량부 초과일 경우 층의 경화를 방해할 수 있기 때문이다.The UV absorbing additive is added to block UV as well as IR absorption, and may be included in an amount of 1 to 4 parts by weight. This is because when it is less than 1 part by weight, the UV blocking function cannot be preferably exhibited, and when it is greater than 4 parts by weight, curing of the layer may be hindered.
경화제는 열경화성 수지의 경화가 이루어지도록 하는 것으로, 1 내지 9중량부를 포함할 수 있다. 여기서 경화제가 1중량부 미만일 경우 경화가 이루어지지 않을 수 있으며, 9중량부 초과일 경우 IR 차단층(20)의 유연성 등이 저하되어 IR 차단 윈도우필름의 품질이 저하될 수 있다.The curing agent is to achieve curing of the thermosetting resin, and may include 1 to 9 parts by weight. Here, if the amount of the curing agent is less than 1 part by weight, curing may not be achieved, and if it is greater than 9 parts by weight, the flexibility of the
상기에서 설명한 바와 같이, IR 차단층(20)은 무기입자 분산액 10 내지 20중량부, 열경화성 수지 80 내지 90중량부, UV흡수첨가제 1 내지 4중량부 및 경화제 1 내지 9중량부를 포함할 수 있으나, 이에 한정되지는 않는다.As described above, the
또한, IR 차단층(20)은 비닐아세테이트계 공중합체, 블록이소시아네이트(blocked isocyanate) 중 하나 이상을 더 포함할 수 있다.In addition, the
비닐아세테이트계 공중합체는 IR 차단층(20)의 점도를 조절하여 유연성을 가지도록 할 수 있는데, 점도를 조절함으로써 코팅 후 컬 현상 등을 방지할 수 있다.The vinyl acetate-based copolymer can adjust the viscosity of the
구체적으로, 비닐아세테이트계 공중합체는 선형 구조를 가지며, 유리전이온도(Tg)가 -5 내지 15℃일 수 있다.Specifically, the vinyl acetate-based copolymer may have a linear structure and a glass transition temperature (Tg) of -5 to 15 °C.
이러한, 선형 구조를 갖는 비닐아세테이트계 공중합체는 단량체인 비닐아세테이트(Vinyl <21> acetate)에, 비닐버사테이트(Vinyl versatate), 이소부틸아크릴레이트(iso-butyl acrylate), n-부틸아크릴레이트(n-Butyl acrylate), 에틸아크릴레이트(Ethyl acrylate), 2-에틸헥실아크릴레이트(2-Ethylhexyl acrylate), 라우릴아크릴레이트(Lauryl acrylate), 에틸렌(Ethylene) 등의 공단량체를 중합하여 선형의 중합구조를 지니도록 합성된 비닐아세테이트계 공중합체일 수 있다.Such a vinyl acetate-based copolymer having a linear structure includes vinyl acetate as a monomer, vinyl versatate, iso-butyl acrylate, n-butyl acrylate ( Linear polymerization by polymerizing comonomers such as n-Butyl acrylate, Ethyl acrylate, 2-Ethylhexyl acrylate, Lauryl acrylate, and Ethylene It may be a vinyl acetate-based copolymer synthesized to have a structure.
또한 선형 구조를 갖는 비닐아세테이트계 공중합체의 유리전이온도(Tg)가 -5℃ 미만일 경우 점도가 너무 증가하여 IR 차단층(20)의 경화 및 물성에 문제가 발생할 수 있고, 15℃를 초과할 경우 컬 현상을 방지하기 어려울 수 있다.In addition, when the glass transition temperature (Tg) of the vinyl acetate-based copolymer having a linear structure is less than -5 ° C, the viscosity increases too much, which may cause problems with curing and physical properties of the
또한 선형 구조를 갖는 비닐아세테이트계 공중합체는 1중량부 미만일 경우 컬 현상 방지 기능이 미미하고 4중량부 초과일 경우 점도가 너무 증가하여 바람직하지 않을 수 있으므로, 1 내지 4중량부가 포함될 수 있으나, 이에 한정되지는 않는다.In addition, since the vinyl acetate-based copolymer having a linear structure has an insignificant anti-curling function when it is less than 1 part by weight, and the viscosity increases too much when it is greater than 4 parts by weight, which may be undesirable, 1 to 4 parts by weight may be included. Not limited.
블록이소시아네이트(blocked isocyanate)는 자연스럽게 경화가 이루어짐으로써 작업시간을 단축시킬 수 있고, 충분한 물성을 얻을 수 있도록 하는 것으로, 디이소시아네이트(isocyanate)와 블록킹제(blocking agent)를 반응시켜 제조한 것일 수 있다.Blocked isocyanate is cured naturally, thereby reducing working time and obtaining sufficient physical properties, and may be prepared by reacting diisocyanate with a blocking agent.
여기서, 디이소시아네이트(isocyanate)는 디페닐메탄 디이소시아네이트(diphenylmethane diisocyanate, MDI), 톨루엔 디이소시아네이트(toluene diisocyanate, TDI), 이소프렌 디이소시아네이트(isophorone diisocyanate, IPDI), 헥사메틸렌 디이소시아네이트(hexamethylene diisocyanate, HDI), 나프탈렌 디이소시아네이트(naphthalene diisocyanate, NDI) 중에서 1종 또는 그 이상을 사용하는 것이 바람직하다.Here, the diisocyanate is diphenylmethane diisocyanate (MDI), toluene diisocyanate (TDI), isoprene diisocyanate (IPDI), hexamethylene diisocyanate (HDI) , It is preferable to use one or more of naphthalene diisocyanate (naphthalene diisocyanate, NDI).
또한, 블록킹제(blockingagent)는 페놀(phenol), e-카프로락탐(e-caprolactam), 2-부타논 옥심(2-butanone oxime), 아세톤 옥심(acetone oxime), 디메틸 피라졸(dimethyl pyrazole), 벤조페논 옥심(benzophenone oxime), 디이소프로필 아민(diisopropyl amine), 1,2,4-트리아졸(1,2,4-triazole) 중에서 1종 또는 그 이상을 사용하는 것이 바람직하다.In addition, blocking agents include phenol, e-caprolactam, 2-butanone oxime, acetone oxime, dimethyl pyrazole, It is preferable to use one or more of benzophenone oxime, diisopropyl amine, and 1,2,4-triazole.
또한 블록이소시아네이트는 1 내지 4중량부가 포함될 수 있으나, 이에 한정되지는 않는다.In addition, 1 to 4 parts by weight of block isocyanate may be included, but is not limited thereto.
또한, IR 차단층(20)은 불포화 카르복시산계 수지 및 불포화 칼슘 중 하나 이상을 더 포함할 수 있다.In addition, the
불포화 카르복시산계 수지는 IR 차단층(20)의 내마모성, 내수성 등을 향상시킬 수 있는 것으로, 아크릴산, 메타크릴산, 말레산, 푸마르산, 이타콘산 중 하나일 수 있다.The unsaturated carboxylic acid-based resin can improve wear resistance and water resistance of the
여기서 불포화 카르복시산계 수지는 IR 차단층(20)에 3 내지 6중량부가 포함될 수 있는데, 3중량부 미만일 경우 내마모성 등 향상 후 안전성이 떨어지며, 부착성이 저하될 수 있고, 6중량부 초과할 경우 내수성, 건조성이 저하될 수 있다.Here, the unsaturated carboxylic acid-based resin may be included in 3 to 6 parts by weight in the
불포화 칼슘은 IR 차단층(20)의 경도를 높여 내스크레치성을 향상시킬 수 있는 것으로, 3 내지 6중량부가 포함되는 것이 바람직하나, 이에 한정되지는 않는다.Unsaturated calcium can increase the hardness of the
이는 불포화 칼슘이 3중량부 미만일 경우 경도 증가 효과가 미미하며, 6중량부를 초과할 경우 제품의 제조단가가 상승하며 크랙 등이 발생할 수 있기 때문이다.This is because when the amount of unsaturated calcium is less than 3 parts by weight, the effect of increasing the hardness is insignificant, and when it exceeds 6 parts by weight, the manufacturing cost of the product increases and cracks and the like may occur.
또한 IR 차단층(20)은 세리아(ceria) 및 이트리아(yttria) 중 하나 이상을 더 포함할 수 있다.In addition, the
세리아(ceria) 및 이트리아(yttria)는 IR 차단층(20)에 포함됨으로써 경화 시 특성 변화가 최소화되도록 할 수 있는데, 각각 IR 차단층(20)에 0.05 내지 0.5중량부가 포함될 수 있다.Ceria and yttria may be included in the
또한, IR 차단층(20)은 대전 방지제, 가소제, 자외선 안정제, 분산제, 소포제, 습윤제, 라벨링제 등을 더 포함할 수 있으나, 이에 한정되지 않으며, 필요에 따라 다양한 조성물들을 더 포함할 수 있다.In addition, the
이러한 IR 차단층(20)은 2 내지 10㎛의 두께로 형성되는 것이 바람직하며, 이는 2㎛ 미만일 경우 자외선의 투과율에 대한 조절 기능을 할 수 없고, 10㎛를 초과할 경우 투명성을 떨어뜨리는 부작용이 나타날 수 있기 때문이다.The
점착층(30)은 기재필름(10) 타면에 로타리스크린을 통해 무용제 UV 점착제로 패턴 코팅되어 형성될 수 있다. 즉, 로타리스크린의 원통형의 스크린 롤러 내부에 무용제 UV 점착제를 투입하고, 회전에 의한 원심력으로 무용제 UV 점착제를 기재필름(10)에 패턴 코팅시켜 점착층(30)을 형성할 수 있는 것이다.The
점착층(30)이 무용제 UV 점착제로 형성되기 때문에, 기재필름(10)으로 유리전이전도가 낮은 필름도 사용할 수 있도록 할 수 있다.Since the
여기서 사용되는 무용제 UV 점착제는 주제, 모노머, 다관능 아크릴레이트 및 개시제를 포함할 수 있다.The non-solvent UV adhesive used herein may include a main agent, a monomer, a multifunctional acrylate, and an initiator.
구체적으로, 주제는 폴리에스테르, 폴리염화비닐, 폴리비닐알콜, 폴리에틸렌비닐아세테이트, 폴리에틸렌비닐알콜, 폴리우레탄, 폴리비닐아세테이트, 폴리우레탄아크릴레이트 및 폴리아크릴레이트 중 1종 이상일 수 있으며, 이에 한장되지 않고 다양한 고분자 수지가 사용될 수 있다.Specifically, the subject may be one or more of polyester, polyvinyl chloride, polyvinyl alcohol, polyethylene vinyl acetate, polyethylene vinyl alcohol, polyurethane, polyvinyl acetate, polyurethane acrylate, and polyacrylate, but is not limited thereto. A variety of polymeric resins may be used.
또한, 주제는 40 내지 80중량부가 포함될 수 있다.In addition, 40 to 80 parts by weight of the subject may be included.
이때, 주제가 40중량부 미만일 경우 점착력이 저하되며, 80중량부를 초과할 경우 로타리스크린을 이용하여 기재에 코팅되기에 부적합한 점도를 나타내어 코팅작업에 어려움이 발생할 수 있다.At this time, if the subject is less than 40 parts by weight, the adhesive strength is lowered, and if it exceeds 80 parts by weight, difficulty may occur in the coating operation because it exhibits an inappropriate viscosity for coating on the substrate using a rotary screen.
모노머는 산 관능기를 가지는 아크릴계 모노머, 하이드록시 관능기를 갖는 아크릴계 모노머, 아크릴 모노머 및 비닐계 모노머로 이루어진 군으로부터 선택된 1종 이상의 중합성 모노머 중 2종 이상을 포함할 수 있으며, 산 관능기를 가지는 아크릴계 모노머, 하이드록시 관능기를 갖는 아크릴계 모노머, 아크릴 모노머 및 비닐계 모노머로 이루어진 군으로부터 선택된 1종 이상의 중합성 모노머를 모두 포함하는 것이 바람직하다.The monomer may include at least two kinds of polymerizable monomers selected from the group consisting of an acrylic monomer having an acid functional group, an acrylic monomer having a hydroxy functional group, an acrylic monomer, and a vinyl monomer, and an acrylic monomer having an acid functional group , It is preferable to include all of one or more polymerizable monomers selected from the group consisting of an acrylic monomer having a hydroxyl functional group, an acrylic monomer, and a vinyl monomer.
이와 같이 모두 포함할 경우, 보다 바람직하게, 모노머는 산 관능기를 가지는 아크릴계 모노머, 하이드록시 관능기를 갖는 아크릴계 모노머, 아크릴 모노머 및 비닐계 모노머로 이루어진 군으로부터 선택된 1종 이상의 중합성 모노머를 공중합하여 제조된 아크릴 공중합체일 수 있다.In the case of including all of these, more preferably, the monomer is prepared by copolymerizing at least one polymerizable monomer selected from the group consisting of an acrylic monomer having an acid functional group, an acrylic monomer having a hydroxy functional group, an acrylic monomer, and a vinyl monomer. It may be an acrylic copolymer.
상기 공중합은 한정되지 않고, 통상적으로 알려진 다수의 방법 중 하나로 이루어질 수 있다.The copolymerization is not limited and may be performed by one of a number of conventionally known methods.
이러한 모노머는 바람직한 일 예로, 산 관능기를 가지는 아크릴계 모노머 5 내지 15중량부, 하이드록시 관능기를 갖는 아크릴계 모노머 25 내지 65중량부 및 중합성 모노머 29 내지 60중량부를 포함할 수 있다.Such a monomer may include, for example, 5 to 15 parts by weight of an acrylic monomer having an acid functional group, 25 to 65 parts by weight of an acrylic monomer having a hydroxy functional group, and 29 to 60 parts by weight of a polymerizable monomer.
이때, 산 관능기를 가지는 아크릴계 모노머가 5중량부 미만일 경우 점착력이 저하되며, 15중량부를 초과할 경우 접착제와 비슷해져 코팅을 통해 점착층(30)을 형성하기에 어려움이 따를 수 있으며, 내오염 및 신율 등의 물성 구현에 있어 국부적으로 취약한 부분이 발생할 수 있다.At this time, if the acrylic monomer having an acid functional group is less than 5 parts by weight, the adhesive strength is lowered, and if it exceeds 15 parts by weight, it becomes similar to an adhesive, and it may be difficult to form the
또한, 하이드록시 관능기를 갖는 아크릴계 모노머가 25중량부 미만일 경우 점착력이 저하되며, 65중량부를 초과할 경우 접착제와 비슷해져 코팅을 통해 점착층(30)을 형성하기에 어려움이 따를 수 있으며 내오염성이 저하될 수 있다.In addition, when the amount of the acrylic monomer having a hydroxyl functional group is less than 25 parts by weight, the adhesive strength decreases, and when it exceeds 65 parts by weight, it becomes similar to an adhesive, and it may be difficult to form the
또한, 중합성 모노머가 29중량부 미만일 경우 무용제 UV 점착제의 코팅에 어려움이 발생할 수 있으며, 60중량부 초과할 경우 점착력 및 점도가 저하되고 입체감이 저하될 수 있다.In addition, when the amount of the polymerizable monomer is less than 29 parts by weight, it may be difficult to coat the solvent-free UV adhesive, and when it exceeds 60 parts by weight, the adhesive force and viscosity may decrease and the three-dimensional effect may decrease.
또한 모노머는 비람직한 이 예로, 하이드록시 관능기를 갖는 아크릴계 모노머 20 내지 75중량부 및 중합성 모노머 25 내지 80중량부를 포함할 수 있다.In addition, the monomer may include 20 to 75 parts by weight of an acrylic monomer having a hydroxyl functional group and 25 to 80 parts by weight of a polymerizable monomer in this preferred example.
이때, 하이드록시 관능기를 갖는 아크릴계 모노머가 20중량브 미만일 경우 나타내고자 하는 점착력을 구현하기 힘들며, 75중량부 접착제와 비슷해져 층으로 형성하기에 어려움이 따를 수 있으며 내오염성이 저하될 수 있다.At this time, if the acrylic monomer having a hydroxyl functional group is less than 20 parts by weight, it is difficult to realize the desired adhesive strength, and it may be difficult to form a layer as it is similar to 75 parts by weight of an adhesive, and stain resistance may be lowered.
또한, 중합성 모노머가 25중량부 미만일 경우 무용제 UV 점착제의 코팅에 어려움이 발생할 수 있으며, 80중량부 초과할 경우 점착력 및 점도가 저하되고 입체감이 저하될 수 있다.In addition, when the amount of the polymerizable monomer is less than 25 parts by weight, it may be difficult to coat the solventless UV adhesive, and when it exceeds 80 parts by weight, the adhesive force and viscosity may decrease and the three-dimensional effect may decrease.
상기에서 설명된 산 관능기를 가지는 모노머는 점착력을 증진시킬 수 있는 것으로, (메타)아크릴산 및 카르복시 C1~C6 알킬 (메타)아크릴레이트로 이루어진 군으로부터 선택된 1종 이상의 모노머를 포함할 수 있다.The above-described monomer having an acid functional group may improve adhesive strength, and may include at least one monomer selected from the group consisting of (meth)acrylic acid and carboxy C 1 -C 6 alkyl (meth)acrylate.
구체적으로, 산 관능기를 가지는 모노머는 아크릴산, 메타아크릴산, 카르복시에틸 (메타)아크릴레이트, 카르복시프로필 (메타)아크릴레이트 및 카르복시부틸 (메타)아크릴레이트 등 중 1종 이상을 포함할 수 있다. Specifically, the monomer having an acid functional group may include at least one of acrylic acid, methacrylic acid, carboxyethyl (meth)acrylate, carboxypropyl (meth)acrylate, and carboxybutyl (meth)acrylate.
한편, 카르복시 관능기를 가지는 아크릴계 모노머는 이 중에서도 아크릴산(AA)이 저렴하면서 반응성도 좋기 때문에 바람직하다.On the other hand, among acrylic monomers having a carboxy functional group, acrylic acid (AA) is preferable because it is inexpensive and highly reactive.
하이드록시 관능기를 갖는 아크릴계 모노머는 점착력을 증진시킬 수 있는 것으로, 하이드록시 C1~C6알킬 (메타)아크릴레이트로 이루어진 군으로부터 선택된 1종 이상의 모노머를 포함할 수 있다.The acrylic monomer having a hydroxyl functional group may improve adhesive strength and may include one or more monomers selected from the group consisting of hydroxy C 1 -C 6 alkyl (meth)acrylates.
구체적으로, 하이드록시 관능기를 갖는 아크릴계 모노머는 하이드록시에틸 아크릴레이트(HEA), 하이드록시에틸 메타크릴레이트, 하이드록시프로필 아크릴레이트, 하이드록시프로필 메타크릴레이트, 하이드록시부틸 아크릴레이트, 하이드록시부틸 메타아크릴레이트 등 중 1종 이상을 포함할 수 있다. Specifically, the acrylic monomer having a hydroxy functional group is hydroxyethyl acrylate (HEA), hydroxyethyl methacrylate, hydroxypropyl acrylate, hydroxypropyl methacrylate, hydroxybutyl acrylate, hydroxybutyl meta One or more of acrylates and the like may be included.
한편, 하이드록시 관능기를 가지는 아크릴계 모노머는 이 중에서도 하이드록시프로필 아크릴레이트(HPA)가 바람직하다.On the other hand, as for the acrylic monomer having a hydroxyl functional group, among these, hydroxypropyl acrylate (HPA) is preferable.
중합성 모노머는 희석용도로 사용되는 것으로, 아크릴 모노머 및 비닐계 모노머로 이루어진 군으로부터 선택된 1종 이상을 포함할 수 있다.The polymerizable monomer is used for dilution and may include at least one selected from the group consisting of an acrylic monomer and a vinyl monomer.
구체적으로, 아크릴 모노머는 메틸 아크릴레이트, 메틸 메타크릴레이트, 에틸 아크릴레이트, 에틸 메타크릴레이트, 이소프로필 아크릴레이트, 이소프로필 메타크릴레이트, 노말부틸 아크릴레이트, 노말부틸 메타크릴레이트, 이소부틸 아크릴레이트, 이소부틸 메타크릴레이트, t-부틸 아크릴레이트, t-부틸 메타크릴레이트, 에틸헥실 아크릴레이트, 에틸헥실 메타크릴레이트, 라우릴 아크릴레이트, 라우릴 메타크릴레이트, 스테아릴 아크릴레이트, 스테아릴 메타크릴레이트시클로프로필 아크릴레이트, 시클로헥실 아크릴레이트, 페닐 아크릴레이트, 벤질 아크릴레이트, 폴리에틸렌글리콜 모노(메타)아크릴레이트, 폴리에틸렌글리콜 디(메타)아크릴레이트, 메톡시메틸 아크릴레이트, 에톡시메틸 아크릴레이트, 에톡시에틸 아크릴레이트 등 중 1종 이상을 포함할 수 있다.Specifically, the acrylic monomer is methyl acrylate, methyl methacrylate, ethyl acrylate, ethyl methacrylate, isopropyl acrylate, isopropyl methacrylate, normal butyl acrylate, normal butyl methacrylate, isobutyl acrylate , isobutyl methacrylate, t-butyl acrylate, t-butyl methacrylate, ethylhexyl acrylate, ethylhexyl methacrylate, lauryl acrylate, lauryl methacrylate, stearyl acrylate, stearyl meth Cyclopropyl acrylate, cyclohexyl acrylate, phenyl acrylate, benzyl acrylate, polyethylene glycol mono(meth)acrylate, polyethylene glycol di(meth)acrylate, methoxymethyl acrylate, ethoxymethyl acrylate, At least one of ethoxyethyl acrylate and the like may be included.
비닐계 모노머는 티렌, 아세트산 비닐, 프로피온산 비닐, 벤조산 비닐, 비닐 톨루엔, 비닐 피롤리돈 등 중 1종 이상을 포함할 수 있다.The vinyl-based monomer may include at least one of ethylene, vinyl acetate, vinyl propionate, vinyl benzoate, vinyl toluene, and vinyl pyrrolidone.
한편, 중합성 모노머는 이 중에서도 에틸헥실 아크릴레이트(EHA) 및 이소보닐 아크릴레이트(IBOA)가 바람직하다.Meanwhile, as the polymerizable monomer, among these, ethylhexyl acrylate (EHA) and isobornyl acrylate (IBOA) are preferable.
이와 같은 모노머는 10 내지 30중량부를 포함할 수 있는데, 이는 모노머가 10중량부 미만일 경우 바람직한 점착력과 점도가 나타나지 않고, 30중량부 초과일 경우 너무 묽어 질 수 있기 때문이다.Such a monomer may include 10 to 30 parts by weight, because if the monomer is less than 10 parts by weight, desirable adhesive force and viscosity may not appear, and if the monomer is greater than 30 parts by weight, it may become too thin.
다관능 아크릴레이트는 경화 효율을 향상시키는 것으로, 트라이메틸올프로페인 트라이아크릴레이트(TMPTA), 폴리에틸렌글리콜 디아크릴레이트(PEGDA) 및 디프로필렌글리콜 디아크릴레이트(DPGDA) 중 1종 이상을 포함할 수 있으며, 트라이메틸올프로페인 트라이아크릴레이트(TMPTA)가 바람직하나, 이에 한정되지는 않는다.The multifunctional acrylate improves curing efficiency and may include at least one of trimethylolpropane triacrylate (TMPTA), polyethylene glycol diacrylate (PEGDA) and dipropylene glycol diacrylate (DPGDA). And, trimethylolpropane triacrylate (TMPTA) is preferred, but is not limited thereto.
이러한 다관능 아크릴레이트는 0.1 내지 30중량부를 포함할 수 있다.These multifunctional acrylates may contain 0.1 to 30 parts by weight.
이때, 다관능 아크릴레이트는 0.1중량부 미만일 경우 경화 향상 효과가 미미하고, 30중량부를 초과할 경우 경화 시 점착층(30)이 너무 딱딱해져 점착력을 잃어버릴 수 있다.At this time, when the multifunctional acrylate is less than 0.1 parts by weight, the curing improvement effect is insignificant, and when it exceeds 30 parts by weight, the
개시제는 0.1중량부 미만일 경우 경화가 잘 이루어지지 않고, 9중량부 초과일 경우에도 역으로 경화가 되지 않을 수 있어, 0.1 내지 9중량부를 포함할 수 있으나, 이에 한정되지는 않는다.If the initiator is less than 0.1 parts by weight, curing may not be performed well, and even if it is greater than 9 parts by weight, it may not be cured conversely, so it may include 0.1 to 9 parts by weight, but is not limited thereto.
상기와 같이 무용제 UV 점착제는 주제 40 내지 80중량부, 모노머 10 내지 30중량부, 다관능 아크릴레이트 0.1 내지 30중량부 및 개시제 0.1 내지 9중량부를 포함하는 것이 바람직하나, 이에 한정되지는 않는다.As described above, the non-solvent UV adhesive preferably includes 40 to 80 parts by weight of the main agent, 10 to 30 parts by weight of the monomer, 0.1 to 30 parts by weight of the multifunctional acrylate, and 0.1 to 9 parts by weight of the initiator, but is not limited thereto.
또한 무용제 UV 점착제는 말레익 무수수화물 중합 폴리프로필렌 및 실란계 수지 중 하나 이상인 점착촉진제를 더 포함할 수 있다.In addition, the non-solvent UV adhesive may further include an adhesion promoter that is at least one of maleic anhydride polymerized polypropylene and a silane-based resin.
상기 점착촉진제는 점착층(30)의 점착력을 향상시킬 수 있어, 기재필름(10)과의 밀착력이 향상되도록 하며 IR 차단 윈도우필름의 부착성도 향상되도록 할 수 있다.The adhesion accelerator can improve the adhesiveness of the
여기서 점착촉진제는 5 내지 8중량부가 포함될 수 있는데, 5중량부 미만일 경우 점착층(30)의 점착력 향상 효과가 미미하고, 8중량부 초과일 경우 점착촉진제가 변질되거나 석출되어 이물로 나타날 수 있기 때문이다.Here, the adhesion promoter may be included in an amount of 5 to 8 parts by weight. If it is less than 5 parts by weight, the effect of improving the adhesion of the
또한 무용제 UV 점착제는 알긴산, 히알루론산 및 키틴을 더 포함할 수 있다.In addition, the solvent-free UV adhesive may further include alginic acid, hyaluronic acid, and chitin.
알긴산은 카르복시기를 포함하여 점착층(30)의 피착제에 대한 점착성을 향상시키고 잔사 방지 역할을 할 수 있고, 히알루론산은 카르복시기를 포함하여 피착제에 대한 점착성을 향상시켜 잔사 방지 역할을 할 수 있고 유연성을 향상시키며, 키틴은 점착층(30)의 형태안정성을 향상시킬 수 있다.Alginic acid contains a carboxy group to improve the adhesiveness of the
즉, 무용제 UV 점착제는 모노머를 보조하는 알긴산, 히알루론산 및 키틴을 더 포함함으로써, 점착층(30)의 피착제에 대한 점착성이 향상되어 잔사 발생을 방지할 수 있고, 유연성 및 형태안정성이 향상되어 엠보패턴 형성에 바람직하고, 에어프리 기능이 좀더 잘 나타날 수 있도록 할 수 있다. That is, the non-solvent UV adhesive further includes alginic acid, hyaluronic acid, and chitin, which assist monomers, so that the adhesiveness of the
이때, 알긴산, 히알루론산 및 키틴을 혼합하여 사용함으로써, 하나를 사용할 때보다 상기 효과를 효과적으로 나타낼 수 있다. At this time, by using a mixture of alginic acid, hyaluronic acid and chitin, the effect can be more effectively exhibited than when using one.
보다 바람직한 효과를 위해서는 알긴산 2 내지 7중량부, 히알루론산 2 내지 7중량부 및 키틴 1 내지 3중량부가 포함될 수 있다.For a more desirable effect, 2 to 7 parts by weight of alginic acid, 2 to 7 parts by weight of hyaluronic acid, and 1 to 3 parts by weight of chitin may be included.
구체적으로, 알긴산 및 히알루론산이 각각 2중량부 미만일 경우 점착성 향상 및 잔사 방지 향상 효과가 저하될 수 있고, 7중량부 초과일 경우 점착층(30)의 물성 등이 저하될 수 있기 때문이다. 또한 키틴이 1중량부 미만일 경우 형태안정성 향상 효과가 미미하고, 3중량부 초과일 경우 유연성이 저하되어 에어프리 기능에 영향을 끼칠 수도 있다.Specifically, this is because when the amount of alginic acid and hyaluronic acid is less than 2 parts by weight, the effect of improving adhesion and preventing residue may decrease, and when the amount exceeds 7 parts by weight, the physical properties of the
또한 무용제 UV 점착제는 페녹시 에틸 아크릴 레이트(phenoxyethyl acrylate) 1 내지 4중량부 및 페닐말레이미드(phenyl maleimide) 3 내지 6중량부를 더 포함할 수 있다.In addition, the non-solvent UV adhesive may further include 1 to 4 parts by weight of phenoxyethyl acrylate and 3 to 6 parts by weight of phenyl maleimide.
점착층(30)의 경우, 수축응력이 양쪽에 균일하게 발생해야 하기 때문에 탄성 제어가 중요하며, 수축응력이 균일하게 발생하지 않을 경우, 낮은 내구성, 위상차, 복굴절, 빛샘현상 등 문제점이 발생할 수 있다. 상기 문제점을 방지하기 위해서는 높은 굴절률, 탄성률 등을 가지도록 설계하는 것이 바람직하다.In the case of the
페녹시 에틸 아크릴 레이트(phenoxyethyl acrylate) 및 페닐말레이미드(phenyl maleimide)는 상기와 같은 문제를 개선시키고자 포함되는 것으로, 페녹시 에틸 아크릴 레이트(phenoxyethyl acrylate)는 고굴절 물질로 점착층(30)의 굴절률을 조절할 수 있으며, 페닐말레이미드(phenyl maleimide)는 고탄성을 가지므로 점착층(30)의 탄성을 제어할 수 있다.Phenoxyethyl acrylate and phenyl maleimide are included to improve the above problems, and phenoxyethyl acrylate is a high refractive index material and has a high refractive index can be adjusted, and since phenyl maleimide has high elasticity, the elasticity of the
이때, 페녹시 에틸 아크릴 레이트(phenoxyethyl acrylate)가 1중량부 미만일 경우 굴절률이 충분히 증가하지 않아 복굴절 및 빛샘이 발생할 수 있으며, 4중량부 초과일 경우 굴절률이 충분히 증가하여 비효율적이라는 문제점이 발생할 수 있다.At this time, if the amount of phenoxyethyl acrylate is less than 1 part by weight, the refractive index is not sufficiently increased, which may cause birefringence and light leakage, and if it is greater than 4 parts by weight, the refractive index is sufficiently increased, resulting in inefficiency.
또한, 페닐말레이미드(phenyl maleimide)가 3중량부 미만일 경우 탄성력이 충분히 증가되지 않아 내구성이 저하되며, 6중량부 초과일 경우 탄성력이 과하게 증가하여 점착층(30)의 엠보 패턴 형성이 원활하지 않다는 문제점이 발생할 수 있다.In addition, when the amount of phenyl maleimide is less than 3 parts by weight, the elastic force is not sufficiently increased, resulting in a decrease in durability, and when the amount of the phenyl maleimide is greater than 6 parts by weight, the elastic force is excessively increased, so that the formation of the embossed pattern of the
또한 무용제 UV 점착제는 석고, 황산칼륨 및 호박산이나트륨을 더 포함할 수 있다.In addition, the solvent-free UV adhesive may further include gypsum, potassium sulfate, and disodium succinate.
석고, 황산칼륨 및 호박산이나트륨은 점착층(30)에 포함되어 점착층(30)의 수축 및 팽창을 저감시켜 형상 변형을 방지하고, 형태안정성이 향상되도록 하며, 경화시간을 단축시킬 수 있다. 또한, 기재필름(10)과의 부착력 및 피착제에 대한 점착력이 향상되도록 할 수 있다.Gypsum, potassium sulfate, and disodium succinate are included in the
이러한 석고, 황산칼륨 및 호박산이나트륨은 각각 1 내지 4중량부, 10 내지 15중량부 및 5 내지 8중량부가 포함될 수 있다.These gypsum, potassium sulfate and disodium succinate may be included in 1 to 4 parts by weight, 10 to 15 parts by weight, and 5 to 8 parts by weight, respectively.
이때, 석고가 1중량부 미만일 경우 수축이 일어나 점착층(30)의 형태안정성이 저하될 수 있고, 4중량부 초과일 경우 팽창이 일어나 형태안정성이 저하되며 석출되어 이물로 나타날 수 있다.At this time, when the amount of gypsum is less than 1 part by weight, shrinkage may occur and the shape stability of the
또한, 황산칼륨이 10중량부 미만일 경우 경화시간 단축 효과가 미미하고 팽창이 일어나 점착층(30)의 형태안정성이 저하될 수 있으며, 15중량부 초과일 경우 유연성에 영향을 줄 수 있으며 수축이 일어나 형태안정성이 저하될 수 있다.In addition, when the amount of potassium sulfate is less than 10 parts by weight, the effect of reducing the curing time is insignificant and expansion occurs, which may decrease the shape stability of the
또한, 호박산이나트륨이 5중량부 미만일 경우 부착력 향상 효과가 미미하고, 38중량부 초과일 경우 유연성에 영향을 주어 에어프리 기능이 저하될 수 있다.In addition, when disodium succinate is less than 5 parts by weight, the effect of improving adhesion is insignificant, and when it is greater than 38 parts by weight, flexibility may be affected and the air-free function may deteriorate.
이와 같이 석고, 황산칼륨 및 호박산이나트륨는 서로 상호작용하여 상기와 같은 효과를 나타내기 때문에, 상기와 같은 중량부로 혼합되어 최적의 효과를 나타낼 수 있다.In this way, since gypsum, potassium sulfate, and disodium succinate interact with each other to exhibit the above effects, they can be mixed in the above weight parts to exhibit optimal effects.
상기와 같은 무용제 UV 점착제로 형성되는 점착층(30)은 10 내지 50㎛의 두께로 형성될 수 있다.The
이때, 두께가 10㎛ 미만일 경우 점착력이 저하되고 에어프리의 기능이 저하될 수 있으며, 50㎛를 초과할 경우 경화에 어려움이 있고 비효율적이며, 윈도우필름의 두께가 너무 두꺼워 질 수 있다.At this time, if the thickness is less than 10 μm, the adhesive force may decrease and the function of the airfree may deteriorate, and if the thickness exceeds 50 μm, curing may be difficult and inefficient, and the thickness of the window film may become too thick.
이형지(40)는 점착층(30)의 타면과 접하여, 사용하기 전 점착층(30)이 손상되거나 변질되는 등 현상이 발생하지 않도록 보호할 수 있다.The
상기에서 설명한 바와 같이, 본 발명의 본 발명의 실시예에 따른 패턴 인쇄를 통해 부착이 용이한 IR 차단 윈도우필름은 로타리스크린 인쇄를 통해 무용제 UV 점착제를 기재필름에 패턴 코팅시켜 점착층을 형성시킴으로써, 에어프리 기능을 통해 시공편의성 및 부착성이 개선되며 잔사가 남지 않을 수 있다.As described above, the IR blocking window film, which is easily attached through pattern printing according to the embodiment of the present invention, is pattern-coated with a non-solvent UV adhesive on the base film through rotary screen printing to form an adhesive layer, The air-free function improves installation convenience and adhesion, and may not leave residues.
또한, 유리전이온도(Tg)가 낮은 기재필름에도 적용할 수 있어 다양한 기재필름을 사용할 수 있다.In addition, since it can be applied to a base film having a low glass transition temperature (Tg), various base films can be used.
이하, 실시예에 의하여 본 발명을 더욱 상세히 설명하고자 한다.Hereinafter, the present invention will be described in more detail by examples.
단, 하기 실시예는 본 발명을 예시하는 것일 뿐, 본 발명의 내용이 하기 실시예에 의해 한정되는 것은 아니다.However, the following examples are only to illustrate the present invention, and the content of the present invention is not limited by the following examples.
[[ 실시예Example ]]
[실시예 1][Example 1]
무기입자 분산액 15중량부, 열경화성 수지 85중량부, UV흡수첨가제 3중량부 및 경화제 8중량부를 교반하고 교반한 용액을 기재필름 위에 도포하고 건조하여 IR 차단층을 형성한 후, 기재필름타면에 로타리스크린을 통해 무용제 UV 점착제로 패턴 코팅한 후 경화하여 점착층을 형성해 IR 차단 윈도우필름을 제조하였다.15 parts by weight of inorganic particle dispersion, 85 parts by weight of thermosetting resin, 3 parts by weight of UV absorbing additive and 8 parts by weight of curing agent were stirred, and the stirred solution was applied on a base film, dried to form an IR blocking layer, and then applied to the other side of the base film by rotary An IR blocking window film was prepared by pattern coating with a non-solvent UV adhesive through a screen and then curing to form an adhesive layer.
여기서, 무기입자 분산액은 세슘, 텅스텐, 주석 및 안티모니의 분산액이다.Here, the inorganic particle dispersion is a dispersion of cesium, tungsten, tin and antimony.
또한 무용제 UV 점착제는 주제 60중량부, 모노머 15중량부, 다관능 아크릴레이트 0.8중량부 및 개시제 3.5중량부를 포함할 수 있다.In addition, the solvent-free UV adhesive may include 60 parts by weight of the main agent, 15 parts by weight of the monomer, 0.8 parts by weight of the multifunctional acrylate, and 3.5 parts by weight of the initiator.
[실시예 2][Example 2]
무용제 UV 점착제가 알긴산 4중량부, 히알루론산 4중량부 및 키틴 2중량부를 더 포함하는 것을 제외하고, 실시예 1과 동일하게 제조하였다.It was prepared in the same manner as in Example 1, except that the solventless UV adhesive further included 4 parts by weight of alginic acid, 4 parts by weight of hyaluronic acid, and 2 parts by weight of chitin.
[실시예 3][Example 3]
무용제 UV 점착제가 페녹시 에틸 아크릴 레이트(phenoxyethyl acrylate) 2중량부 및 페닐말레이미드(phenyl maleimide) 4중량부를 더 포함하는 것을 제외하고, 실시예 1과 동일하게 제조하였다.It was prepared in the same manner as in Example 1, except that the solventless UV adhesive further included 2 parts by weight of phenoxyethyl acrylate and 4 parts by weight of phenyl maleimide.
[실시예 4][Example 4]
무용제 UV 점착제가 석고 3중량부, 황산칼륨 12중량부 및 호박산이나트륨 6중량부를 더 포함하는 것을 제외하고, 실시예 1과 동일하게 제조하였다.It was prepared in the same manner as in Example 1, except that the solventless UV adhesive further included 3 parts by weight of gypsum, 12 parts by weight of potassium sulfate, and 6 parts by weight of disodium succinate.
[비교예][Comparative example]
무기입자 분산액 8중량부, 열경화성 수지 85중량부 및 경화제 8중량부를 교반하고 교반한 용액을 기재필름 위에 도포하고 건조하여 IR 차단층을 형성한 후, 기재필름 타면에 실리콘계 점착제를 도포하여 평면 점착층을 형성하는 것으로 IR 차단 윈도우필름을 제조하였다.After stirring 8 parts by weight of inorganic particle dispersion, 85 parts by weight of thermosetting resin, and 8 parts by weight of curing agent, the stirred solution was applied on a base film and dried to form an IR blocking layer, and then a silicone adhesive was applied to the other side of the base film to form a flat adhesive layer. An IR blocking window film was prepared by forming a.
여기서 무기입자 분산액은 세슘의 분산액이다.Here, the inorganic particle dispersion is a dispersion of cesium.
[[ 실험예Experimental example ] IR 차단 ] IR blocking 윈도우window 필름 평가 film evaluation
실시예 1 내지 4, 비교예의 윈도우필름의 IR 차단율, 점착력, 에어프리기능 및 잔사를 평가하였다.The IR blocking rate, adhesive strength, air-free function, and residue of the window films of Examples 1 to 4 and Comparative Examples were evaluated.
IR 차단율 측정은 광투과측정기를 통해 측정하였다.IR blocking rate measurement was measured through a light transmittance meter.
점착력은 MD 방향으로 25mm * 120mm로 절단하고 시편 각각을 Polyimide 필름(Apical 25NPI)에 부착한 후 무게 4kgf/cm 압력으로 합지하고, 23℃, 50%RH의 분위기에서 60분간 방치한 후 상기의 시료를 박리각도 180˚, 박리속도 300mm/min로 박리시 이에 대한 응력을 측정하는 것으로 측정하였다.Adhesion was cut into 25mm * 120mm in the MD direction, each specimen was attached to a polyimide film (Apical 25NPI), and then laminated under a pressure of 4kgf/cm in weight, left for 60 minutes in an atmosphere of 23℃, 50%RH, and then the above sample was measured by measuring the stress on it during peeling at a peeling angle of 180˚ and a peeling speed of 300mm/min.
잔사는 100℃, 1시간 동안 유리판에 부착한 뒤, 유리면에 점착제가 남아있는지를 측정하였다.After the residue was attached to a glass plate at 100° C. for 1 hour, it was measured whether or not the adhesive remained on the glass surface.
그 결과는 하기 표 1과 같다.The results are shown in Table 1 below.
여기서, 에어프리기능은 ◎: 뛰어남, ○: 우수, △: 보통, X : 나쁨로 평가하였고, 잔사는 ○: 있음, X: 없음으로 평가하였다.Here, the air-free function was evaluated as ◎: excellent, ○: excellent, △: average, X: poor, and the residue was evaluated as ○: present and X: absent.
상기 표 1에서 볼 수 있듯이, 실시예 1 내지 4는 비교예보다 IR차단율이 높은 것을 확인할 수 있었다.또한 실시예 1 내지 4는 우수한 에어프리기능을 나타내나 비교예는 에어프리기능을 나타내지 못하는 것을 확인할 수 있었다.As can be seen in Table 1, it was confirmed that Examples 1 to 4 had a higher IR blocking rate than Comparative Example. In addition, Examples 1 to 4 showed excellent air-free function, but Comparative Example did not show air-free function. I was able to confirm.
또한, 실시예 1 내지 4는 비교예보다 점착력이 다소 낮으나 큰 차이가 없었으며, 잔사가 남지 않는 것을 확인할 수 있었다.In addition, although the adhesiveness of Examples 1 to 4 was slightly lower than that of Comparative Example, there was no significant difference, and it was confirmed that no residue was left.
그러나, 비교예는 잔사가 남는 것을 확인할 수 있었다.However, it was confirmed that residues remained in the Comparative Example.
즉, 실시예 1 내지 4는 비교예보다 IR차단율 높으며 점착력이 크게 떨어지지 않으면서도 잔사가 남지않고 에어프리기능을 나타내 IR 차단 윈도우필름으로써 우수하다고 판단할 수 있었다.That is, Examples 1 to 4 had a higher IR blocking rate than Comparative Examples, and showed an air-free function without leaving residues without a significant decrease in adhesiveness, so it could be judged that they were excellent as IR blocking window films.
이상에서 본 발명의 실시예에 대하여 상세하게 설명하였지만 본 발명의 권리범위는 이에 한정되는 것은 아니고 다음의 청구범위에서 정의하고 있는 본 발명의 기본 개념을 이용한 당업자의 여러 변형 및 개량 형태 또한 본 발명의 권리범위에 속하는 것이다.Although the embodiments of the present invention have been described in detail above, the scope of the present invention is not limited thereto, and various modifications and improvements made by those skilled in the art using the basic concept of the present invention defined in the following claims are also included in the scope of the present invention. that fall within the scope of the right.
10: 기재필름
20: IR 차단층
30: 점착층
40: 이형지10: base film
20: IR blocking layer
30: adhesive layer
40: release paper
Claims (8)
상기 기재필름 일면에 형성되어 적외선을 차단하는 IR 차단층 및
상기 기재필름 타면에 로타리스크린을 통해 무용제 UV 점착제로 패턴 코팅되어 형성되는 점착층을 포함하고,
상기 IR 차단층은,
무기입자 분산액 10 내지 20중량부, 열경화성 수지 80 내지 90중량부, UV흡수첨가제 1 내지 4중량부 및 경화제 1 내지 9중량부를 포함하고,
상기 무기입자 분산액은,
세슘, 텅스텐, 주석, 안티모니 중 2종 이상의 분산액이고,
상기 점착층은 10 내지 50㎛의 두께로 형성되고,
상기 무용제 UV 점착제는,
주제, 모노머, 다관능 아크릴레이트 및 개시제를 포함하고,
상기 무용제 UV 점착제는,
석고 1 내지 4중량부, 황산칼륨 10 내지 15중량부 및 호박산이나트륨 5 내지 8중량부를 더 포함하고,
상기 무용제 UV 점착제는,
알긴산 2 내지 7중량부, 히알루론산 2 내지 7중량부 및 키틴 1 내지 3중량부를 더 포함하는 IR 차단 윈도우필름.
base film;
An IR blocking layer formed on one side of the base film to block infrared rays, and
An adhesive layer formed by pattern coating the other surface of the base film with a solvent-free UV adhesive through a rotary screen,
The IR blocking layer,
10 to 20 parts by weight of an inorganic particle dispersion, 80 to 90 parts by weight of a thermosetting resin, 1 to 4 parts by weight of a UV absorbing additive, and 1 to 9 parts by weight of a curing agent,
The inorganic particle dispersion,
A dispersion of two or more of cesium, tungsten, tin, and antimony;
The adhesive layer is formed to a thickness of 10 to 50 μm,
The solvent-free UV adhesive,
Including a subject, a monomer, a multifunctional acrylate and an initiator,
The solvent-free UV adhesive,
Further comprising 1 to 4 parts by weight of gypsum, 10 to 15 parts by weight of potassium sulfate and 5 to 8 parts by weight of disodium succinate,
The solvent-free UV adhesive,
An IR blocking window film further comprising 2 to 7 parts by weight of alginic acid, 2 to 7 parts by weight of hyaluronic acid, and 1 to 3 parts by weight of chitin.
상기 주제는,
폴리에스테르, 폴리염화비닐, 폴리비닐알콜, 폴리에틸렌비닐아세테이트, 폴리에틸렌비닐알콜, 폴리우레탄, 폴리비닐아세테이트, 폴리우레탄아크릴레이트 및 폴리아크릴레이트 중 1종 이상인 것을 특징으로 하는 IR 차단 윈도우필름.
According to claim 1,
The subject is
An IR blocking window film, characterized in that at least one of polyester, polyvinyl chloride, polyvinyl alcohol, polyethylene vinyl acetate, polyethylene vinyl alcohol, polyurethane, polyvinyl acetate, polyurethane acrylate and polyacrylate.
상기 모노머는,
산 관능기를 가지는 아크릴계 모노머;
하이드록시 관능기를 갖는 아크릴계 모노머;
아크릴 모노머 및 비닐계 모노머로 이루어진 군으로부터 선택된 1종 이상의 중합성 모노머; 중 2종 이상을 포함하는 것을 특징으로 하는 IR 차단 윈도우필름.
According to claim 1,
The monomer,
an acrylic monomer having an acid functional group;
an acrylic monomer having a hydroxyl functional group;
At least one polymerizable monomer selected from the group consisting of an acrylic monomer and a vinyl monomer; IR blocking window film, characterized in that it comprises two or more of the.
상기 무용제 UV 점착제는,
주제 40 내지 80중량부, 모노머 10 내지 30중량부, 다관능 아크릴레이트 0.1 내지 30중량부 및 개시제 0.1 내지 9중량부를 포함하는 것을 특징으로 하는 IR 차단 윈도우필름.
According to claim 1,
The solvent-free UV adhesive,
An IR blocking window film comprising 40 to 80 parts by weight of a main agent, 10 to 30 parts by weight of a monomer, 0.1 to 30 parts by weight of a multifunctional acrylate, and 0.1 to 9 parts by weight of an initiator.