KR102469919B1 - A manufacturing method of magnet assembly for health approving of multi-functional using permanent magnet - Google Patents
A manufacturing method of magnet assembly for health approving of multi-functional using permanent magnet Download PDFInfo
- Publication number
- KR102469919B1 KR102469919B1 KR1020210012181A KR20210012181A KR102469919B1 KR 102469919 B1 KR102469919 B1 KR 102469919B1 KR 1020210012181 A KR1020210012181 A KR 1020210012181A KR 20210012181 A KR20210012181 A KR 20210012181A KR 102469919 B1 KR102469919 B1 KR 102469919B1
- Authority
- KR
- South Korea
- Prior art keywords
- powder
- permanent magnet
- magnet assembly
- magnet
- tourmaline
- Prior art date
Abstract
본 발명은 영구자석을 이용한 고효율의 건강증진용 복합기능 자석조립체 제조방법에 관한 것으로서, 그 절차는 토르말린, 게르마늄, 은 성분의 광물을 각각 기류식 분쇄기로 분쇄하여 분말화하고, 에폭시 수지 및 희토류계의 영구자석을 세절하여 준비하는 재료 준비단계; 토르말린 분말 3 ~ 6 중량%, 게르마늄 분말 3 ~ 5 중량% 및 은 분말 0.5 ~ 2 중량%을 혼합한 후, 에폭시 수지 0.5 ~ 1.5 중량과 혼합하여 혼합물을 형성하는 재료 혼합단계; 에폭시 수지에 토르말린 분말, 게르마늄 분말 및 은 분말이 혼합된 혼합물을 86 ~ 90 중량%의 영구자석 N극 또는 S극 상부에 주입하여 일체화하여 납작한 반구형의 지압돌기를 형성하는 성형단계; 및 상기 성형단계에서 구비된 반구형의 지압돌기를 소성하여 칩(chip) 형태의 자석조립체를 완성하는 소성단계;를 포함하여 구비되는 것을 특징으로 한다.
이에 의해, 본 발명은 토르말린, 게르마늄 분말, 은 분말 및 에폭시가 혼합된 혼합물이 영구자석 상에 안착하여 입체적으로 일정두께를 갖는 반구형의 지압돌기 형태로 돌출되도록 자석조립체로 성형됨으로써, 자속밀도를 증폭하여 영구자석에 의해 증폭된 자력과 원적외선, 음이온이 활성화되는 기능성 광물의 상호 보완적 상승작용을 통해 영구자석의 방사체의 이용 효율을 극대화하고 자력 전달 방향 및 자력 에너지 강도를 높여 건강증진에 유효한 효과를 제공한다.The present invention relates to a method for manufacturing a high-efficiency multi-functional magnet assembly for health promotion using a permanent magnet, the procedure of which is to pulverize tourmaline, germanium, and silver minerals with an airflow type grinder, respectively, and pulverize epoxy resin and rare earth-based minerals. Material preparation step of preparing by cutting the permanent magnet of; A material mixing step of mixing 3 to 6 wt% of tourmaline powder, 3 to 5 wt% of germanium powder, and 0.5 to 2 wt% of silver powder, and then mixing with 0.5 to 1.5 wt% of an epoxy resin to form a mixture; Forming a flat hemispherical acupressure protrusion by injecting a mixture of epoxy resin with tourmaline powder, germanium powder and silver powder in an amount of 86 to 90% by weight onto the N-pole or S-pole of the permanent magnet and integrating the mixture; and a firing step of completing a magnet assembly in the form of a chip by firing the hemispherical acupressure projection provided in the molding step.
Accordingly, in the present invention, a mixture of tourmaline, germanium powder, silver powder, and epoxy is seated on a permanent magnet and molded into a magnet assembly so that it protrudes in the form of a hemispherical acupressure protrusion having a certain thickness three-dimensionally, thereby amplifying the magnetic flux density. Through the mutually complementary synergistic action of magnetic force amplified by permanent magnets, far-infrared rays, and negative ions, the efficiency of using the emitter of permanent magnets is maximized, and the direction of magnetic force transmission and the strength of magnetic energy are increased, thereby providing effective effects on health promotion. to provide.
Description
본 발명은 자석조립체 제조에 관한 것으로서, 보다 구체적으로는, 토르말린 분말, 게르마늄 분말, 은 분말 및 에폭시가 혼합된 혼합물이 영구자석 상에 안착하여 입체적으로 일정두께를 갖는 반구형의 지압 돌기 형태로 돌출되도록 형성되어 영구자석과 기능성 광물의 상호 보완적 상승작용을 통해 원적외선, 음이온 방출 및 영구자석의 방사체의 이용 효율을 극대화할 수 있는 영구자석을 이용한 고효율의 건강증진용 복합기능 자석조립체 제조방법에 관한 것이다.The present invention relates to the manufacture of a magnet assembly, and more specifically, a mixture of tourmaline powder, germanium powder, silver powder, and epoxy is seated on a permanent magnet and three-dimensionally protrudes in the form of a hemispherical pressure protrusion having a certain thickness. It relates to a method for manufacturing a high-efficiency multifunctional magnet assembly for health promotion using a permanent magnet capable of maximizing the efficiency of using a emitter of a permanent magnet and emitting far infrared rays and anions through a mutually complementary synergistic action of a permanent magnet and a functional mineral. .
또한, 본 발명은 에폭시 수지와 일정 비율의 토르말린 분말, 게르마늄 분말 및 은 분말과 혼합하여 구비된 혼합물을 영구자석 N극 또는 S극 상부에 일체화시켜 외부로 노출되는 반구형 지압 돌기로 입체적으로 돌출되도록 칩(CHIP) 형태로 형성하여 팔찌, 손목밴드, 벨트, 버클, 매트 등의 접착밴드 부재의 일측에 삽입 또는 안착하여 칩 돌기 내부의 영구자석과 기능성 광물질의 상호작용에 따라 방출되는 자기장, 원적외선 및 음이온을 통해 통증부위 완화 또는 건강증진을 위한 방사체로 사용될 수 있는 영구자석을 이용한 고효율의 건강증진용 복합기능 자석조립체 제조방법에 관한 것이다.In addition, the present invention is a chip to three-dimensionally protrude into a hemispherical acupressure projection exposed to the outside by integrating the mixture provided by mixing epoxy resin with a certain ratio of tourmaline powder, germanium powder, and silver powder on the upper part of the N-pole or S-pole of the permanent magnet Magnetic field, far-infrared rays, and negative ions are emitted according to the interaction between the permanent magnet inside the chip protrusion and the functional mineral by being formed in the form of a chip and inserted or seated on one side of an adhesive band member such as a bracelet, wristband, belt, buckle, or mat. It relates to a method for manufacturing a high-efficiency multifunctional magnet assembly for health promotion using a permanent magnet that can be used as a emitter for pain relief or health promotion through
최근 웰빙 열풍으로 건강에 대한 다양한 욕구를 충족시키는 방식이 제안되며 자기장에 의한 자기치료 요법을 부분적으로 구현하는 건강자석 또는 원적외선 방사나 음이온 방출에 의한 건강자석 제품이 유통되고 있다. With the recent well-being craze, methods for satisfying various health needs have been proposed, and health magnets that partially implement magnetic therapy by magnetic fields or health magnet products by far-infrared radiation or negative ion emission are being distributed.
일반적으로 자력을 발생하는 자석은 경락치료요법을 시행하기 위한 수단으로서 인체의 각 부위에 분포되어 있는 경혈에 미세한 전류와 압력을 가해 자기장 에너지로서 치료를 하는 것으로서, 신체의 일부분 또는 아픈 부위에 자석을 붙이는 등 자극을 주거나 몸 전체에 자기장을 쪼이는 자기요법을 수행함으로써 자성체인 자석이 헤모글로빈의 주성분으로서 인체의 혈액 중에 함유된 철분에 자성을 유도하여 혈액순환을 촉진시키는 작용을 하게 하여 일부 연구에서는 경혈자극을 하였을 때 인체 내의 자기장의 세기가 50배가 증가했다고 보고됨으로써 경락의 흐름을 자기장의 흐름으로 보기도 한다.In general, a magnet that generates magnetic force is a means for implementing meridian therapy, which applies fine current and pressure to acupuncture points distributed in each part of the body to treat as magnetic field energy. By applying stimulation such as attaching or performing magnetic therapy by applying a magnetic field to the entire body, a magnet, which is a magnetic substance, induces magnetism in iron contained in the human blood as the main component of hemoglobin to act to promote blood circulation. It is reported that the strength of the magnetic field within the human body increased 50 times when stimulated, so the flow of the meridian is also regarded as the flow of the magnetic field.
즉 영구자석은 자기를 이용하여서 인체의 자기 면역의 방어력 부족으로 인한 자기 결핍으로 자율신경이 자제력을 잃는 것을 방지하고 순환기 및 다수의 병인에 의한 피해를 방지하는데 자기 치료는 영구자석 에너지가 신체를 관통하는 방법이라서 화학적 부작용 없이 모든 신체기관을 치료할 수 있다는 것이 증명되고 있다.In other words, permanent magnets use magnetism to prevent the autonomic nerves from losing self-control due to lack of self-defence due to the lack of defense of the body's autoimmunity, and to prevent damage caused by the circulatory system and various causes. It has been proven that it can treat all body organs without chemical side effects.
그러나 자기는 인체에 유해한 측면과 무해·유용한 측면 등의 양면성이 내포되고 있는바, 강한 자기는 인체의 신진대사 질서를 흐트려 놓지만 적당한 자기는 오히려 신진대사를 촉진시키는 작용을 한다.However, magnetism contains both sides, such as harmful and harmless/useful aspects to the human body. Strong magnetism disrupts the metabolic order of the human body, but moderate magnetism rather promotes metabolism.
또한, 원적외선은 생육광선으로서 파장이 30∼1000 미크론의 적외선으로 인체에 흡수되어 세포조직을 활성화시키고 혈액순환과 노폐물 배출을 촉진시키는 등의 건강증진 효과가 증명되고 있고 이로 인해 자연계에 존재하는 고효율 원적외선 방사물질로서 여러 물품이 다수 적용되어 사용되고 있다.In addition, far-infrared rays, as growth rays, are absorbed by the human body as infrared rays with a wavelength of 30 to 1000 microns, activating cell tissues, and promoting blood circulation and discharge of waste products. As a radioactive material, many articles are applied and used.
따라서, 종래의 일반적인 평등 자기장 등방성 자석의 특성으로 인하여 자속 밀도가 분산되어 강력한 자력이 환부에 충분히 전달되지 않음으로 인하여 인체에 자력에 의한 치료효과가 제한되는 등 제반 문제점이 있는데, 이는 자석에서 발생되는 자기력은 모서리 부위 및 측면에서 높게 발생하기 때문에 인체와 직접 접촉이 이루어지는 평판부위에서는 상대적으로 자기력의 세기가 미약하기 때문에 치료효과가 저감되어 적절하지 않은 자력(가우스)의 자석을 사용하고 자력의 손실이 많은 자석 배열로 인하여 신체에 미치는 자력선들의 영향이 미약하여 인체에 충분한 자력을 제공할 수 없는 구조로서 장시간 사용해야 효과가 있으며 충분한 자기치료 효과도 구현하지 못하는 문제점이 있다.Therefore, due to the characteristics of conventional general equal magnetic field isotropic magnets, magnetic flux density is dispersed and strong magnetic force is not sufficiently transmitted to the affected area, so there are various problems such as limited therapeutic effect by magnetic force on the human body, which is generated from the magnet Since magnetic force is high at the corners and sides, the strength of magnetic force is relatively weak in the flat part that is in direct contact with the human body, so the treatment effect is reduced, and a magnet of inappropriate magnetic force (Gauss) is used and loss of magnetic force occurs. Due to the large array of magnets, the effect of the lines of magnetic force on the body is weak, so it is a structure that cannot provide sufficient magnetic force to the human body.
이에 본 출원인은 종래의 자석이 인체에 미치는 자력의 흐름 방향이 맞지 않고 N극과 S극이 거의 대칭을 이루며 가장자리에 자력 에너지가 집중되는 종래 일반적인 평등 자기장 등방성 자석의 특성으로 인하여 자속밀도가 분산되어 출력이 저하되어 강력한 자력이 환부에 충분히 전달되지 않음으로 인하여 인체에 자력에 의한 치료효과를 크게 주지 못하는 등 제반 문제점을 해결하고, 자석의 자속밀도를 증폭시킴과 아울러 원적외선과 음이온이 함께 활성화되도록 하여 자력 전달 방향 및 자력 에너지 강도를 높이게 하는 자석 및 자성 에너지를 활성화시키고 다양한 종류의 물품에 적용하여 건강 증진에 도움을 주는 복합 기능의 자석조립체를 제안하고자 한다.Accordingly, the applicant of the present invention does not match the flow direction of the magnetic force applied to the human body by the conventional magnet, the N pole and the S pole are almost symmetrical, and the magnetic flux density is dispersed due to the characteristics of the conventional equal magnetic field isotropic magnet in which magnetic energy is concentrated at the edge. It solves various problems such as not giving a great therapeutic effect to the human body due to the strong magnetic force not being sufficiently transmitted to the affected area due to the decrease in output, and by amplifying the magnetic flux density of the magnet and activating far-infrared rays and negative ions together. We would like to propose a magnet assembly with multiple functions that activates magnets and magnetic energy that increase the direction of magnetic force transmission and magnetic energy intensity and helps improve health by applying them to various types of articles.
본 발명은 상기의 문제점을 해결하기 위한 것으로, 에폭시 수지와 일정 비율의 토르말린 분말, 게르마늄 분말 및 은 분말과 혼합하여 구비된 혼합물을 영구자석 N극 또는 S극 상부에 일체화시켜 외부로 노출되는 반구형 지압돌기로 입체적으로 돌출되는 칩(CHIP) 형태로 형성하여 팔찌, 손목밴드, 벨트, 패치, 매트 등의 접착밴드 부재의 일측에 삽입 또는 안착하여 칩 돌기 내부의 영구자석과 기능성 광물질의 상호작용에 따라 방출되는 자기장, 원적외선 및 음이온을 통해 통증부위 완화 또는 건강증진을 위한 방사체로 사용될 수 있는 영구자석을 이용한 고효율의 건강증진용 복합기능 자석조립체 제조방법을 제공하기 위한 것이다.The present invention is to solve the above problems, hemispherical acupressure exposed to the outside by integrating the mixture provided by mixing epoxy resin with a certain ratio of tourmaline powder, germanium powder and silver powder on the upper part of the permanent magnet N or S pole It is formed in the form of a three-dimensionally protruding chip (CHIP) with projections, inserted or seated on one side of an adhesive band member such as a bracelet, wristband, belt, patch, mat, etc. It is an object of the present invention to provide a high-efficiency method of manufacturing a multifunctional magnet assembly for health promotion using a permanent magnet that can be used as a radiator for relieving pain or promoting health through emitted magnetic fields, far-infrared rays, and negative ions.
또한, 본 발명은 토르말린 분말, 게르마늄 분말, 은 분말 및 에폭시가 혼합된 혼합물이 영구자석 상에 안착하여 입체적으로 일정두께를 갖는 반구형의 지압돌기 형태로 돌출되도록 성형됨으로써, 자속밀도를 증폭하여 영구자석에 의해 증폭된 자력과 원적외선, 음이온이 활성화되는 기능성 광물의 상호 보완적 상승작용을 통해 영구자석의 방사체의 이용 효율을 극대화하고 자력 전달 방향 및 자력 에너지 강도를 높이게 하는 자석 및 자성 에너지를 활성화할 수 있는 영구자석을 이용한 고효율의 건강증진용 복합기능 자석조립체 제조방법을 제공하기 위한 것이다.In addition, the present invention is formed so that a mixture of tourmaline powder, germanium powder, silver powder and epoxy is seated on a permanent magnet and three-dimensionally formed to protrude in the form of a hemispherical acupressure protrusion having a certain thickness, thereby amplifying the magnetic flux density to obtain a permanent magnet Through the mutually complementary synergistic action of magnetic force amplified by far-infrared rays and negative ions, it is possible to maximize the efficiency of using the emitter of permanent magnets and to activate magnets and magnetic energy that increase the direction of magnetic force transmission and the intensity of magnetic force energy. It is to provide a high-efficiency multifunctional magnet assembly manufacturing method for health promotion using permanent magnets.
그러나 본 발명의 목적들은 상기에 언급된 목적으로 제한되지 않으며, 언급되지 않은 또 다른 목적들은 아래의 기재로부터 당업자에게 명확하게 이해될 수 있을 것이다.However, the objects of the present invention are not limited to the above-mentioned objects, and other objects not mentioned will be clearly understood by those skilled in the art from the description below.
상기의 목적을 달성하기 위해 본 발명의 실시예에 따른 영구자석을 이용한 고효율의 건강증진용 복합기능 자석조립체 제조방법은 토르말린, 게르마늄, 은 성분의 광물을 각각 기류식 분쇄기로 분쇄하여 미분말화로 분체한 후, 분체를 사이클론으로 포집하고 분체를 복식 사이클론 분급기로 조분을 분리시켜 이 분쇄 동작을 5회 반복하여 20㎛ 이하 나노 크기의 초미립자 상태로 다공성이 유지되도록 미세 분말로 형성하고, 2,500 ∼ 3,000가우스의 자기적 특성을 갖는 희토류계의 영구자석을 반구형의 지압돌기 형태로 성형된 몰드내에 안착되도록 세절하는 재료 준비단계; 토르말린 분말 4.46 중량%, 게르마늄 분말 4.46 중량% 및 은 분말 1.05 중량%을 혼합한 후, 에폭시 수지 0.84 중량%과 혼합하여 혼합물을 형성하는 재료 혼합단계; 반구형의 지압돌기 형태로 성형된 몰드 내에 89.19 중량%의 영구자석을 위치하고 영구자석 N극 또는 S극 상부에 에폭시 수지와 토르말린 분말, 게르마늄 분말 및 은 분말이 혼합된 혼합물 10.81 중량%을 주입하여 납작한 반구형의 지압돌기를 형성하는 성형단계; 및 상기 성형단계에서 구비된 납작한 반구형의 지압돌기를 소성하여 칩(chip) 형태의 자석조립체(100)를 완성하는 소성단계;를 포함하여 구비되는 것을 특징으로 한다.In order to achieve the above object, the method for manufacturing a high-efficiency multi-functional magnet assembly for health promotion using a permanent magnet according to an embodiment of the present invention is to pulverize minerals of tourmaline, germanium, and silver with an air flow type grinder, respectively, and pulverize them into fine powder. Then, the powder is collected by a cyclone, and the powder is separated into coarse powder by a double cyclone classifier, and this grinding operation is repeated 5 times to form a fine powder so that the porosity is maintained in the state of nano-sized ultrafine particles of 20 μm or less, and 2,500 to 3,000 Gauss A material preparation step of cutting rare earth permanent magnets having magnetic properties to be seated in a mold molded in the form of a hemispherical acupressure protrusion; A material mixing step of mixing 4.46% by weight of tourmaline powder, 4.46% by weight of germanium powder, and 1.05% by weight of silver powder, and then mixing them with 0.84% by weight of an epoxy resin to form a mixture; 89.19% by weight of a permanent magnet is placed in a mold molded in the form of a hemispherical acupressure protrusion, and 10.81% by weight of a mixture of epoxy resin, tourmaline powder, germanium powder, and silver powder is injected on top of the N-pole or S-pole of the permanent magnet to form a flat hemispherical shape. A molding step of forming acupressure protrusions; And a firing step of completing the
삭제delete
또한, 본 발명의 실시예에 따른 영구자석을 이용한 고효율의 건강증진용 복합기능 자석조립체 제조방법은 소성단계를 통해 구비된 칩(chip) 형태의 자석조립체는 접착부재의 상부 표면 일측에 해당 칩(chip) 형태의 자석조립체를 위치하여 사용자의 특정 환부에 접착부재를 통해 고정 밀착되도록 사용하거나, 팔찌, 발찌 또는 목걸이에 사용자의 피부와 접촉되는 면에 일정 간격으로 식각된 요부홈에 칩(chip) 형태의 자석조립체가 삽입되어 체결되도록 구비되는 것을 특징으로 한다.In addition, in the method of manufacturing a high-efficiency multifunctional magnet assembly for health promotion using permanent magnets according to an embodiment of the present invention, the magnet assembly in the form of a chip provided through the firing step is placed on one side of the upper surface of the adhesive member ( A magnet assembly in the form of a chip is placed and used so that it is fixed and adhered to the user's specific affected part through an adhesive member, or a chip is etched into the concave groove etched at regular intervals on the surface in contact with the user's skin on a bracelet, anklet or necklace It is characterized in that the magnet assembly of the form is provided to be inserted and fastened.
본 발명의 실시예에 따른 영구자석을 이용한 고효율의 건강증진용 복합기능 자석조립체 제조 방법은 토르말린 분말, 게르마늄 분말, 은 분말 및 에폭시가 혼합된 혼합물이 영구자석 상에 안착하여 입체적으로 일정두께를 갖는 반구형의 지압돌기 형태로 돌출되도록 자석조립체로 성형됨으로써, 자속밀도를 증폭하여 영구자석에 의해 증폭된 자력과 원적외선, 음이온이 활성화되는 기능성 광물의 상호 보완적 상승작용을 통해 영구자석의 방사체의 이용 효율을 극대화하고 자력 전달 방향 및 자력 에너지 강도를 높여 건강증진에 유효한 효과를 제공한다.According to an embodiment of the present invention, a method for manufacturing a high-efficiency multifunctional magnet assembly for health promotion using a permanent magnet is a mixture of tourmaline powder, germanium powder, silver powder, and epoxy placed on a permanent magnet to have a three-dimensionally constant thickness. By being molded into a magnet assembly to protrude in the form of a hemispherical acupressure protrusion, the magnetic flux density is amplified and the efficiency of using the emitter of the permanent magnet through the complementary synergy of the magnetic force amplified by the permanent magnet and the functional minerals activating far-infrared rays and negative ions and increase the magnetic force transmission direction and magnetic energy intensity to provide an effective effect on health promotion.
또한, 본 발명의 실시예에 따른 영구자석을 이용한 고효율의 건강증진용 복합기능 자석조립체 제조방법은 에폭시 수지와 일정 비율의 토르말린 분말, 게르마늄 분말 및 은 분말과 혼합하여 구비된 혼합물을 영구자석 N극 또는 S극 상부에 일체화시켜 외부로 노출되는 반구형 지압돌기로 입체적으로 돌출되는 칩(CHIP) 형태의 자석조립체로 형성하여 팔찌, 손목밴드, 벨트, 버클, 패치, 매트 등에 삽입하여 제작, 접착 밴드부재의 상부 일측에 안착하여 착용 또는 환부에 부착함으로서 칩 돌기 내부의 영구자석과 기능성 광물질의 상호작용에 따라 방출되는 자기장, 원적외선 및 음이온을 통해 통증부위 완화 또는 건강증진을 위한 방사체로 사용될 수 있다.In addition, the method for manufacturing a high-efficiency multifunctional magnet assembly for health promotion using a permanent magnet according to an embodiment of the present invention is a mixture of epoxy resin and tourmaline powder, germanium powder and silver powder at a certain ratio, and the mixture is provided by mixing the permanent magnet N pole Or integrated into the top of the S pole to form a magnetic assembly in the form of a chip (CHIP) that protrudes three-dimensionally with a hemispherical acupressure projection exposed to the outside and inserted into a bracelet, wristband, belt, buckle, patch, mat, etc., adhesive band member It can be used as a radiator for relieving pain or promoting health through magnetic fields, far-infrared rays, and negative ions emitted according to the interaction between the permanent magnet inside the protrusion and the functional mineral by being seated on one side of the upper part of the chip and attached to the affected area.
또한, 본 발명의 실시예에 따른 영구자석을 이용한 고효율의 건강증진용 복합기능 자석조립체 제조방법은 N극 자기력선의 강력한 자력이 형성됨으로써 환부 접촉 시 고른 자력 배열로 작용점에 치료 효과가 집중되게 배열하고, 에폭시 수지에 미약 전류를 영구히 발산하는 토르말린 분말과 원적외선 및 음이온을 방출하는 게르마늄분말, 은(銀)분말을 일정 비율 혼합하여 포함하여 납작한 반구형의 자석조립체가 구비됨으로서 고효율의 방사체로서 영구자석의 이용 효율을 향상시키고 축방향으로 음이온, 원적외선과 자기력선이 집적되어 중심 자장이 형성됨으로써 작은 소형 자석만으로도 자기장 증폭효과로 인체의 피부 깊숙이 집중적으로 침투할 수 있는 자석조립체를 제공한다.In addition, in the method of manufacturing a high-efficiency multifunctional magnet assembly for health promotion using permanent magnets according to an embodiment of the present invention, strong magnetic force of the N-pole magnetic force line is formed, so that the treatment effect is concentrated on the action point with an even magnetic force arrangement when contacting the affected area. Using a permanent magnet as a high-efficiency emitter as a flat hemispherical magnet assembly is provided by mixing tourmaline powder that permanently emits weak current with epoxy resin, germanium powder and silver powder that emit far-infrared rays and negative ions in a certain ratio. It provides a magnet assembly that can intensively penetrate deep into the skin of the human body with a magnetic field amplification effect even with only small magnets by improving efficiency and forming a central magnetic field by integrating negative ions, far-infrared rays, and magnetic force lines in the axial direction.
또한, 본 발명의 실시예에 따른 에 따른 영구자석을 이용한 고효율의 건강증진용 복합기능 자석조립체 제조방법은 종래 일반적인 평등 자기장 등방성 자석의 특성으로 인하여 자속밀도가 분산되어 강력한 자력이 환부에 충분히 전달되지 않음으로 인하여 인체에 자력에 의한 미비한 치료효과의 제반 문제점을 해결하고 벨트, 액세서리, 귀금속 장신구, 매트, 의류, 모자 장갑 등의 다양한 용품에 광범위한 범위로 적용하여 착용에 따라 음이온 방출 및 원적외선 방사 물질의 특성상 마찰이나 압력, 열, 충격 등이 가해질수록 더 많은 음이온을 발산하여 자석조립체에 발생하는 유효한 성분을 통해 면역기능 강화 및 각종 질병예방으로 건강증진의 효과를 기대할 수 있다.In addition, the method for manufacturing a high-efficiency multi-functional magnet assembly for health promotion using a permanent magnet according to an embodiment of the present invention is not sufficiently transmitted to the affected area because the magnetic flux density is dispersed due to the characteristics of a conventional general equal magnetic field isotropic magnet. Therefore, it solves all problems of insufficient therapeutic effect by magnetic force on the human body and is applied to a wide range of products such as belts, accessories, precious metal accessories, mats, clothing, hats and gloves, and emits negative ions and emits far-infrared rays according to wear. Due to its characteristics, more negative ions are emitted as friction, pressure, heat, shock, etc. are applied, and the effect of improving health by strengthening immune function and preventing various diseases can be expected through effective components generated in the magnet assembly.
또한, 본 발명의 실시예에 따른 영구자석을 이용한 고효율의 건강증진용 복합기능 자석조립체 제조방법은 토르말린, 게르마늄 및 은을 미세 분말로 각각 사용하여 영구자석 N극(S극) 상부에 에폭시와 나노 크기로 미분쇄된 초미분의 미세 전류를 영구히 발산하는 전기석 분말로 적용됨으로써 음이온, 원적외선과 자기력선이 집적되어 영구자석 에너지가 활성화됨으로써 음이온, 원적외선과 자기력선이 집적되고 중심 자장이 형성되어 작은 소형 영구자석만으로도 자기장 증폭효과로 인체의 피부 깊숙이 집중적으로 침투하여 저출력의 자기 에너지로도 고효율을 유도하게 된다.In addition, the method of manufacturing a high-efficiency multifunctional magnet assembly for health promotion using a permanent magnet according to an embodiment of the present invention uses tourmaline, germanium, and silver as fine powder, respectively, and epoxy and nano It is applied as tourmaline powder that permanently radiates ultra-fine currents that are finely pulverized, and negative ions, far-infrared rays, and lines of magnetic force are integrated, and permanent magnet energy is activated. It penetrates deeply into the skin of the human body with a magnetic field amplification effect even with just this alone, and induces high efficiency even with low-output magnetic energy.
도 1은 본 발명에 따른 영구자석을 이용한 고효율의 건강증진용 복합기능 자석조립체의 제조절차를 도시한 흐름도
도 2는 본 발명에 따른 영구자석을 이용한 고효율의 건강증진용 복합기능 자석조립체의 상태도
도 3은 본 발명에 따른 영구자석을 이용한 고효율의 건강증진용 복합기능 자석조립체를 밴드부재에 부착된 사용상태도
도 4는 본 발명에 따른 영구자석을 이용한 고효율의 건강증진용 복합기능 자석조립체를 팔찌에 체결된 상태를 도시한 사용상태도
도 5는 본 발명에 따른 영구자석을 이용한 고효율의 건강증진용 복합기능 자석조립체가 벨트에 체결된 상태를 도시한 사용상태도1 is a flow chart showing a manufacturing procedure of a high-efficiency multifunctional magnet assembly for health promotion using permanent magnets according to the present invention.
Figure 2 is a state diagram of a high-efficiency multifunctional magnet assembly for health promotion using permanent magnets according to the present invention
Figure 3 is a state of use of the high-efficiency multifunctional magnet assembly for health promotion using a permanent magnet attached to a band member according to the present invention
4 is a use state diagram showing a state in which a high-efficiency multifunctional magnet assembly for health promotion using a permanent magnet according to the present invention is fastened to a bracelet
5 is a use state diagram showing a state in which a high-efficiency multifunctional magnet assembly for health promotion using a permanent magnet according to the present invention is fastened to a belt
이하, 본 발명의 바람직한 실시예에 따른 영구자석을 이용한 고효율의 건강증진용 복합기능 자석조립체(이하, 드림칩이라 칭함) 제조방법에 대하여 상세하게 설명하기로 한다.Hereinafter, a method for manufacturing a high-efficiency multifunctional magnet assembly for health promotion (hereinafter referred to as a dream chip) using a permanent magnet according to a preferred embodiment of the present invention will be described in detail.
상세한 설명은 첨부된 도면들을 참조하여 설명할 것이다. 하기에서 본 발명을 설명함에 있어서, 관련된 공지 기능 또는 구성에 대한 구체적인 설명이 본 발명의 요지를 불필요하게 흐릴 수 있다고 판단되는 경우에는 그 상세한 설명을 생략할 것이다.A detailed description will be given with reference to the accompanying drawings. In the following description of the present invention, if it is determined that a detailed description of a related known function or configuration may unnecessarily obscure the subject matter of the present invention, the detailed description will be omitted.
본 발명은 토르말린 분말, 게르마늄 분말, 은 분말 및 에폭시가 혼합된 혼합물이 영구자석 N극 또는 S극 상부에 안착하여 일체화시켜 일정두께를 갖는 입체적 반구형의 지압돌기 형태로 돌출되는 칩(chip) 형태로 성형하여 팔찌, 목걸이, 손목밴드, 벨트에 일정간격으로 체결하거나 밴드부재의 상부에 안착하여 지압돌기 칩(chip) 내부의 영구자석과 기능성 광물질의 상호작용에 따라 방출되는 자기장, 원적외선 및 음이온을 통해 통증부위 완화 또는 건강증진을 위한 방사체로 사용될 수 있는 영구자석을 이용한 고효율의 건강증진용 복합기능 자석조립체를 제공하는 것을 특징으로 한다.In the present invention, a mixture of tourmaline powder, germanium powder, silver powder, and epoxy is seated on the upper part of the N-pole or S-pole of a permanent magnet and integrated into a chip protruding in the form of a three-dimensional hemispherical pressure protrusion with a certain thickness. It is molded and fastened to bracelets, necklaces, wristbands, belts at regular intervals or seated on top of band members through magnetic fields, far-infrared rays, and negative ions emitted according to the interaction between permanent magnets and functional minerals inside the acupressure protrusion chips. It is characterized by providing a high-efficiency multifunctional magnet assembly for health promotion using a permanent magnet that can be used as a emitter for pain relief or health promotion.
이하, 본 발명에 따른 영구자석을 이용한 고효율의 건강증진용 복합기능 자석조립체는 토르말린 분말, 게르마늄 분말, 은 분말, 에폭시 수지 및 영구자석의 유기적인 결합에 의해 성형된 것으로, 각 물질의 특징을 살펴보면, 먼저, 영구자석의 강자성체는(强磁性體, FerroMagnetic substance)는 자석에 달라붙는 성질을 갖는 물질을 칭하는 것으로, 철, 코발트, 니켈 및 그 합금이 대표적이며 자성체에서는 개개의 원자가 자석과 같은 역할을 하는데, 이들 원자들은 외부의 자기장이 발생하지 않은 상황에서는 불규칙하게 정렬됨으로써 전체적으로 극이 다르면 서로 밀치는 자석과 같은 효과는 없지만, 외부에서 자력이 인가되면 그 원자들이 외부 자기장의 방향으로 배열하여 극성에 상관없이 자석에 달라붙는 성질을 가진다.Hereinafter, a high-efficiency multifunctional magnet assembly for health promotion using a permanent magnet according to the present invention is molded by an organic combination of tourmaline powder, germanium powder, silver powder, epoxy resin, and a permanent magnet. Looking at the characteristics of each material , First, the ferromagnetic substance of a permanent magnet refers to a substance that has the property of sticking to a magnet. Iron, cobalt, nickel, and their alloys are typical. In a magnetic substance, individual atoms play the same role as a magnet. However, these atoms are arranged irregularly in the absence of an external magnetic field, so there is no effect like a magnet pushing each other if the poles are different as a whole, but when a magnetic force is applied from the outside, the atoms are arranged in the direction of the external magnetic field and Regardless, it has the property of sticking to a magnet.
따라서, 본 발명의 영구자석은 2,500∼3,000가우스의 자기적 특성을 갖는 희토류계의 자석으로서 직접 피부에 접촉되지 않는 간접 방식으로 사용하는데, 원반형 영구자석은 외부로부터 전기에너지를 공급받지 않고서도 안정된 자기장을 발생하고 유지하면서 영구자석에 의하여 형성된 자계에 의해서 전자의 이동이 향상된다. 한편, 본 발명은 초강력 자성체로서 영구자석은 용도에 따라 네오디뮴자석(Nd) 또는 사마륨코발트자석(SmCo)으로 사용한다.Therefore, the permanent magnet of the present invention is a rare earth magnet having a magnetic characteristic of 2,500 to 3,000 Gauss and is used in an indirect manner without direct contact with the skin. The movement of electrons is improved by the magnetic field formed by the permanent magnet while generating and maintaining. On the other hand, in the present invention, neodymium magnet (Nd) or samarium cobalt magnet (SmCo) is used as a permanent magnet as a super strong magnetic material depending on the purpose.
또한, 에폭시 수지는 열경화성 수지로서, 영구자석 상부에서 다수의 기능성 광물질과 혼합되어 일체로 성형이 가능하며 매끄럽고 미려한 외관을 형성하고, 안착성, 내약품성, 전기적 성질이 뛰어나 우수한 표면 코팅제로서의 역할을 하고 다수의 기능성 광물질과 혼합하여 성형시 내열성, 내화학성, 내충격성이 우수한 특징이 있고, 투명창이 형성되고 고온 다습한 환경(온도차가 심한 물속 환경, 고온건조시스템, 충격환경)이나 화학적, 물리적으로 가혹한 환경에서도 견딜 수 있어 방수성, 내충격성이 뛰어나고 파손됨이 없으며 매끄러워 장식효과를 구현할 수도 있다.In addition, epoxy resin is a thermosetting resin, which can be molded integrally by being mixed with a plurality of functional minerals on the top of a permanent magnet, forms a smooth and beautiful appearance, and has excellent stability, chemical resistance, and electrical properties, and serves as an excellent surface coating agent. It has excellent heat resistance, chemical resistance and impact resistance when molded by mixing with a number of functional minerals, and a transparent window is formed. It can withstand the environment, has excellent waterproof and impact resistance, is not damaged, and can be smooth to realize decorative effects.
즉, 에폭시 수지는 에폭시와 혼합하는 토르말린 분말, 게르마늄 분말, 은(銀) 분말과 일체로 영구자석과 성형되어 구비된 돌기 형태의 칩(chip)이 구비됨으로써 마찰이나 압력, 열, 충격 등이 가해질수록 더 많은 음이온을 발산하여 착용하거나 밀착상태에서 그 기능성 효과가 극대화된다.That is, the epoxy resin is formed integrally with the tourmaline powder, germanium powder, and silver powder mixed with the epoxy and is provided with a protrusion-shaped chip formed integrally with the permanent magnet, so that friction, pressure, heat, shock, etc. are applied. The more negative ions are emitted, the more functional effects are maximized when worn or in close contact.
또한, 토르말린(tourmaline)은 일명 전기석으로 불리는 육방정계에 속하는 광물로서, 일정한 온도를 유지하며 원적외선 발생량이 경이적으로 높아 강력한 열 효과와 높은 침투력으로 인체 혈액 순환을 촉진하는 소재로서, 미세한 분말, 예컨대 0,3㎛ 크기의 입자로 분쇄하여도 양극과 음극을 구비하고, 열이나 압력을 가하면 전기를 발생시키는 성질이 있으며 외부적인 열이나 압력을 가하지 않는 경우에도 음극을 통하여 0.06㎃의 미세 전류를 영구적으로 방출한다.In addition, tourmaline is a mineral belonging to the hexagonal system called tourmaline, which maintains a constant temperature and has a surprisingly high amount of far-infrared rays, which promotes blood circulation in the human body with a strong thermal effect and high penetration. , Even if it is pulverized into 3㎛ size particles, it has an anode and a cathode, and has the property of generating electricity when heat or pressure is applied. emit
토르말린은 미세한 열에 의해 입자가 전기를 발생시켜 미세 전류를 흐르게 하여 인체의 열(체온)과 접촉하므로서 열전달이 되어 보온작용을 하고 경혈 자극, 혈류를 촉진하여 말초순환계를 개선하고, 음이온이 발생되어 항균, 탈취, 세정효과가 있으며, 세포활성화작용으로 체질개선, 혈액정화작용의 전위치료효과가 있다. Tourmaline generates electricity by microscopic heat and allows microcurrent to flow, which transfers heat as it comes in contact with the human body temperature (body temperature) to keep warm, stimulates acupuncture points and promotes blood flow to improve the peripheral circulatory system, and generates negative ions to provide antibacterial properties. It has , deodorizing and cleaning effects, improves the constitution through cell activating action, and has potential therapeutic effect of blood purification action.
또한 토르말린은 광물의 특성상 원적외선이 다량 방출됨으로써 세포를 깊숙히 덮혀주고 혈행을 촉진하고 신진대사를 왕성하게 하여줌으로써 피로회복, 위장활성화, 통증과 어깨결림 완화, 숙면 및 냉증의 완화에 도움이 되고 항균 및 살균작용을 하여 가전제품에서 발생되는 유해한 양이온을 음이온으로 변환시켜 전자파를 차단하는 기능을 하기도 하고, 적정한 미세전류는 세포재생, 통증완화, 혈액 순환 개선 및 호르몬 분비 촉진에 효능이 있는 것으로 알려져 있으며, 치료나 마사지용으로 사용된다.In addition, due to the nature of the mineral, tourmaline emits a large amount of far-infrared rays, so it covers cells deeply, promotes blood circulation, and boosts metabolism, helping to recover from fatigue, activate the stomach, relieve pain and stiff shoulders, sleep well, and alleviate cold sensitivity. It sterilizes and converts harmful cations generated from home appliances into negative ions to block electromagnetic waves. Appropriate microcurrent is known to be effective in cell regeneration, pain relief, blood circulation improvement, and hormone secretion promotion. It is used for treatment or massage.
또한, 게르마늄은 산소 촉매제 역할을 하며 세포에 산소를 공급하여 혈액을 맑게 하는 동시에 몸속의 중금속을 배출시키며 병원체를 포위 공격하는 대식세포를 활성화하여 면역성을 높이는 효과가 있으며, 인체 내의 산소를 활성화시켜서 자연치유력을 향상시켜 신진대사를 촉진시키고 인체 내의 항암작용을 하는 인터페론(interferon)을 생성 면역기능을 강화시켜 각종 질병을 예방하며 몸속의 노폐물과 독소, 콜레스테롤을 몸 밖으로 축출시켜 성인병 예방에 효과가 있다.In addition, germanium acts as an oxygen catalyst, supplies oxygen to cells to purify the blood, discharges heavy metals from the body, activates macrophages that attack pathogens, and enhances immunity. It enhances healing power to promote metabolism, creates interferon, which acts as an anti-cancer agent in the human body, prevents various diseases by strengthening immune function, and is effective in preventing adult diseases by expelling wastes, toxins, and cholesterol from the body.
또한, 게르마늄의 음이온은 음전하(-)를 띈 이온으로서 각종 오염으로부터 생활주변에 방출된 양이온을 흡착·중화시키고 인체의 신진대사를 원활하게 해주는 것으로서 전위치료효과가 있어 세포부활작용 및 혈액정화작용, 자율신경 조절작용, 저항력 증진작용을 하고, 음이온 방출물질을 이용한 제품이 개발되고 있으며 다양한 용도로 사용된다.In addition, the anion of germanium is a negatively charged (-) ion that adsorbs and neutralizes positive ions emitted from various types of pollution to the surroundings and facilitates the metabolism of the human body. It has autonomic nervous regulation action, resistance enhancement action, and products using negative ion releasing substances are being developed and used for various purposes.
한편, 은(銀)은 인체 내 호르몬 계통의 균형을 유지하며 강력한 살균력으로 단세포 동물(박테리아, 바이러스, 전균류 등)이 그들의 산소, 소화대사작용을 하는 특수한 효소에 작용하여 무력화시킴으로써 균들을 질식 및 아사 기능의 촉매(Catalyst)제 역할을 하며 은 전극이 뼈의 성장을 촉진시키고 세포재생을 돕는 기능이 있다.On the other hand, silver maintains the balance of the hormonal system in the human body, and with its strong sterilizing power, single-celled animals (bacteria, viruses, whole fungi, etc.) act on and neutralize special enzymes that metabolize their oxygen and digestion, suffocating and killing germs. It acts as a catalyst for starvation, and the silver electrode promotes bone growth and helps cell regeneration.
또한, 은(銀) 금속 안의 자유전자는 상온에서 다른 어떤 물질보다도 열과 전기의 전도도를 좋게 만들어 게르마늄의 열과 전기의 전도도를 높이는 역할을 한다.In addition, the free electrons in the silver metal increase the thermal and electrical conductivity of germanium by making the conductivity of heat and electricity better than any other material at room temperature.
상기의 특징을 갖는 광물질을 통해 본 발명은 원적외선 및 음이온을 방출하는 물성의 등가물을 다양하게 선택하고 하나 이상 중량비로 혼합할 수 있으며 광물 원석을 미세한 분말로 가공함에 있어서 전기적 성질과 음이온 방출, 원적외선 방사 등의 유효한 특성이 유지되도록 적절한 온도로 건조한 다음 나노 크기 초미립자 상태로 조밀하게 미분쇄하여 분말 형태로 사용한다.Through the mineral material having the above characteristics, the present invention can select various equivalents of physical properties that emit far-infrared rays and anions and mix one or more in a weight ratio, and in processing mineral ore into fine powder, electrical properties, anion emission, and far-infrared radiation It is dried at an appropriate temperature to maintain effective properties such as, etc., and then is finely pulverized into nano-sized ultra-fine particles and used in powder form.
또한, 본 발명에 사용되는 토르말린, 게르마늄, 은 성분은 분말형태로 구비하여 사용되는데, 토르말린, 게르마늄, 은의 기능성 광물질은 기류식 분쇄기로 분쇄하여 미분말화로 분체화 한 다음 분체를 포집하는 사이클론을 포함하며 사이클론으로 포집된 분체로부터 조분을 분리하는 복식 사이클론 분급기로 분급시키되 분쇄하는 동작을 5차례 반복하여 나노 사이즈의 초미분으로 분급시키는 폐회로(Closed Circuit System) 분쇄로 20㎛ 이하의 나노 크기의 초미립자 상태로 미세 분말화하고 나노 분체에 의하여 다공성을 유지하여 사용한다. In addition, the tourmaline, germanium, and silver components used in the present invention are used in powder form. The functional minerals of tourmaline, germanium, and silver are pulverized with an air flow type grinder to finely powder, and then a cyclone that collects the powder It is classified with a double cyclone classifier that separates the coarse powder from the powder collected by the cyclone, and the grinding operation is repeated 5 times to classify the coarse powder into nano-sized ultra-fine powder. It is a closed-circuit system pulverization to obtain nano-sized ultra-fine particles of 20㎛ or less. It is finely powdered and used while maintaining porosity by nano-powder.
한편, 나노 물질화된 본 발명의 나노화된 분체는 가공되어 소량의 첨가만으로도 전체 표면적이 넓어지고 입자 간의 접촉면적이 많아져 결착력이 강해지게 되며 항균 기능성도 부여되고 강도도 상승하게 된다.On the other hand, the nano-materialized powder of the present invention is processed and the total surface area is widened and the contact area between the particles is increased even with the addition of a small amount, so that the binding force is strengthened, antibacterial function is imparted, and the strength is also increased.
첨부된 도 1은 본 발명에 따른 영구자석을 이용한 고효율의 건강증진용 복합기능 자석조립체의 제조공정 절차를 흐름도이고, 도 2는 도 1의 공정에 의해 구비된 영구자석을 이용한 고효율의 건강증진용 복합기능 자석조립체의 상태를 도시한 것으로서, 그 자석조립체 제조공정은 크게 재료준비 단계, 혼합 단계, 성형 단계 및 소성 단계를 포함하여 구성된다. 이하, 첨부된 도 1 내지 도 2를 참조하여 본 발명에 따른 영구자석을 이용한 고효율의 건강증진용 복합기능 자석조립체의 세부적인 제조 절차 및 특징을 상세히 기술한다.Attached Figure 1 is a flow chart of a manufacturing process of a multifunctional magnet assembly for high efficiency health promotion using a permanent magnet according to the present invention, Figure 2 is a high efficiency health promotion using a permanent magnet provided by the process of FIG. As shown in the state of the multifunctional magnet assembly, the manufacturing process of the magnet assembly largely includes a material preparation step, a mixing step, a molding step, and a firing step. Hereinafter, detailed manufacturing procedures and characteristics of a high-efficiency multifunctional magnet assembly for health promotion using a permanent magnet according to the present invention will be described with reference to FIGS. 1 and 2 attached.
1. 재료 준비단계1. Material preparation step
영구자석, 토르말린, 게르마늄, 은 및 에폭시 수지를 준비한다. Prepare permanent magnet, tourmaline, germanium, silver and epoxy resin.
보다 세부적으로, 2,500∼3,000가우스의 자기적 특성을 갖는 희토류계의 자석인 원반형 영구자석을 구비하여 자석조립체의 크기에 따라 해당 영구자석을 세절하여 준비한다. 원반형 영구자석은 외부로부터 전기에너지를 공급받지 않고서도 안정된 자기장을 발생하고 유지하면서 영구자석에 의하여 형성된 자계에 의해서 전자의 이동이 향상된다. More specifically, a disc-shaped permanent magnet, which is a rare earth magnet having a magnetic characteristic of 2,500 to 3,000 gauss, is prepared by cutting the corresponding permanent magnet according to the size of the magnet assembly. The disk-shaped permanent magnet generates and maintains a stable magnetic field without receiving electrical energy from the outside, and the movement of electrons is improved by the magnetic field formed by the permanent magnet.
적절한 온도로 건조된 상기 토르말린, 은 및 게르마늄을 나노 크기 초미립자 상태로 조밀하게 미분쇄하여 분말 형태로 구비한다.The tourmaline, silver, and germanium dried at an appropriate temperature are densely pulverized into nano-sized ultra-fine particles and provided in powder form.
보다 구체적으로 토르말린, 게르마늄, 은 성분의 광물을 각각 기류식 분쇄기로 분쇄하여 미분말화로 분체화 한 다음 분체를 사이클론으로 포집한 분체를 복식 사이클론 분급기로 조분을 분리시켜 이 분쇄 동작을 5회 반복하여 나노 사이즈의 미세 분말로 형성하는데, 이는 분쇄로 20㎛ 이하의 나노 크기의 초미립자 상태로 다공성이 유지되도록 한다.More specifically, the minerals of tourmaline, germanium, and silver are pulverized with an air flow type grinder, respectively, into fine powder, and then the powder collected by a cyclone is separated from the coarse powder by a double cyclone classifier, and this grinding operation is repeated 5 times to obtain nano It is formed into fine powder of the size, which maintains porosity in the state of ultra-fine nano-sized particles of 20 μm or less by grinding.
상기 나노 입자를 통해 나노화된 분체는 가공되어 소량의 첨가만으로도 전체 표면적이 넓어지고 입자 간의 접촉면적이 많아져 결착력이 강해지게 되며 항균 기능성도 부여되고 강도도 상승하게 된다.Nanonized powder is processed through the nanoparticles, and the total surface area is widened and the contact area between the particles is increased to increase the binding force, and antibacterial functionality is also imparted and strength is also increased.
한편, 에폭시 수지는 열경화성 수지로서, 영구자석 상부에서 다수의 기능성 광물질과 혼합되어 일체로 성형이 가능하며 매끄럽고 미려한 외관을 형성하고, 안착성, 내약품성, 전기적 성질이 뛰어나 우수한 표면 코팅제로서의 역할을 하고 다수의 기능성 광물질과 혼합하여 성형시 내열성, 내화학성, 내충격성이 우수하고, 방수성, 내충격성이 뛰어나고 표면을 매끄럽게 구현하게 된다.On the other hand, epoxy resin is a thermosetting resin, which can be molded integrally by being mixed with a number of functional minerals on the top of a permanent magnet, forms a smooth and beautiful appearance, and has excellent stability, chemical resistance, and electrical properties, serving as an excellent surface coating agent. When mixed with a number of functional minerals, it has excellent heat resistance, chemical resistance, and impact resistance, excellent waterproofness and impact resistance, and a smooth surface when molded.
2. 혼합 단계2. Mixing step
상기 재료 준비단계에서 구비된 토르말린 분말 3 ~ 6 중량%, 게르마늄 분말 3 ~ 5 중량% 및 은 분말 0.5 ~ 2 중량%을 혼합한 후, 에폭시 수지 0.5 ~ 1.5 중량과 혼합하여 혼합물을 구성한다.After mixing 3 to 6 wt% of tourmaline powder, 3 to 5 wt% of germanium powder, and 0.5 to 2 wt% of silver powder provided in the material preparation step, they are mixed with 0.5 to 1.5 wt% of epoxy resin to form a mixture.
이때, 상기 에폭시 수지는 열경화성 수지로서, 하기에 기술될 86 ~ 90 중량%의 영구자석 상부에서 혼합된 혼합물이 안착되어 성형함으로써 매끄럽고 미려한 외관을 구비되며, 안착성, 내약품성, 전기적 성질이 뛰어나 우수한 표면 코팅제로서의 역할을 한다.At this time, the epoxy resin is a thermosetting resin, and a mixture mixed with 86 to 90% by weight of a permanent magnet, which will be described below, is seated and molded to have a smooth and beautiful appearance, and has excellent seating properties, chemical resistance, and electrical properties. It serves as a surface coating agent.
또한, 에폭시 수지와 혼합된 광물질이 영구자석 상부에 안착되어 성형시 우수한 내열성, 내화학성, 내충격성이 구비되고 방수성이 보장된 매끄러워 장식효과가 구현된다.In addition, since the mineral material mixed with the epoxy resin is seated on the upper part of the permanent magnet, excellent heat resistance, chemical resistance, and impact resistance are provided during molding, and waterproofness is guaranteed and a smooth decorative effect is realized.
부가적으로 상기 토르말린, 은, 게르마늄을 나노 크기로 각각 미분쇄된 분말을 혼합함으로써 분말의 성질에 의해 모양, 형태가 자유롭게 성형할 수 있다.Additionally, by mixing the tourmaline, silver, and germanium finely pulverized powders, respectively, the shape and form can be freely molded according to the properties of the powder.
한편, 상기 영구자석 89.19 중량%, 토르말린 분말 4.46 중량%, 게르마늄 분말 4.46 중량%, 은 분말 1.05 중량% 및 에폭시 수지 0.84 중량%을 구비되는 것이 바람직하다.Meanwhile, it is preferable to include 89.19% by weight of the permanent magnet, 4.46% by weight of tourmaline powder, 4.46% by weight of germanium powder, 1.05% by weight of silver powder, and 0.84% by weight of an epoxy resin.
3. 성형 단계3. Forming step
상기 에폭시 수지에 토르말린 분말, 게르마늄 분말 및 은 분말이 혼합된 혼합물을 상기 영구자석 N극 또는 S극 상부에 주입하여 일체화하여 납작한 반구형의 지압돌기 형태로 성형한다.A mixture of tourmaline powder, germanium powder, and silver powder in the epoxy resin is injected into the upper part of the permanent magnet N-pole or S-pole and integrated to form a flat hemispherical acupressure protrusion.
보다 구체적으로 반구형의 지압돌기 형태로 성형된 몰드 내에 영구자석을 위치하고 영구자석 N극 또는 S극 상부에 에폭시 수지와 토르말린 분말, 게르마늄 분말 및 은 분말이 혼합된 혼합물을 주입하여 납작한 반구형의 지압돌기가 형성되도록 성형한다.More specifically, by placing a permanent magnet in a mold formed in the form of a hemispherical acupressure projection and injecting a mixture of epoxy resin, tourmaline powder, germanium powder and silver powder on top of the permanent magnet N pole or S pole, a flat hemispherical acupressure projection molded to form
즉, 영구자석 89.19 중량%에 에폭시 수지 0.84 중량%과 토르말린 분말 4.46 중량%, 게르마늄 분말 4.46 중량% 및 은 분말 1.05 중량%이 혼합된 혼합물 10.81중량%을 주입하여 총 중량비 100의 반구형의 지압돌기가 성형되도록 한다.That is, by injecting 10.81% by weight of a mixture of 89.19% by weight of permanent magnet, 0.84% by weight of epoxy resin, 4.46% by weight of tourmaline powder, 4.46% by weight of germanium powder, and 1.05% by weight of silver powder, a hemispherical acupressure protrusion with a total weight ratio of 100 was formed. to be molded.
한편, 상기 지압돌기는 산업적으로 적용될 형태에 따라 사각, 육각, 원형 및 다양한 형태(形態)의 일정두께를 가지게 되는데, 사각, 육각, 원형 및 다양한 형태(形態)의 일정두께의 납작한 영구자석을 쓰임에 따라 N극 상부 또는 S극 상부에 나노 크기로 분쇄한 토르말린 분말, 게르마늄 분말, 은(銀;Ag) 분말을 일정 비율로 인위적으로 에폭시와 혼합하여 영구자석과 일체화시켜 외부로 반구형 지압 돌기(突起)형태로 외부로 노출되도록 성형한다.On the other hand, the acupressure protrusion has a certain thickness of square, hexagonal, circular and various shapes depending on the shape to be applied industrially. Flat permanent magnets of a certain thickness of square, hexagonal, circular and various shapes are used. According to the above, tourmaline powder, germanium powder, and silver (銀; Ag) powder ground into nano-size on the upper part of the N pole or the upper part of the S pole are artificially mixed with epoxy at a certain ratio and integrated with the permanent magnet to form a hemispherical acupressure projection to the outside. ) shape to be exposed to the outside.
4. 소성 단계4. Firing step
상기 성형단계에서 구비된 반구형의 지압돌기를 일정 온도로 소성하여 칩(chip) 형태의 자석조립체(100)를 완성한다.The
첨부된 도 2와 같이 상기 소성단계의 의해 칩(chip) 형태의 자석조립체(100)가 형성되며, 소성된 자석조립체(100)는 은 분말 성분을 통해 네오디뮴자석이 투명하게 표시되는 것을 확인할 수 있다.As shown in FIG. 2, a
상기 절차에 의해 제조된 지압돌기 형태로 돌출되는 칩(chip) 형태의 자석조립체(100)는 내부의 영구자석을 인체에 이로운 극이 인체방향으로 향하도록 자력이 외측으로 퍼져나가지 못하도록 적층 형성된 복합 기능자석으로 상단부에 일정두께로 납작한 반구형으로 구비되는데, 이를 통해 자석복합 소재와 배치 구조가 유기적으로 결합되어 복합 상승효과로 인체에 유익한 음이온, 원적외선과 자기력선이 집적되어 영구자석 에너지가 활성화됨으로써 중심 자장이 형성되어 작은 소형 영구자석만으로도 자기장 증폭효과로 인체의 피부 깊숙이 집중적으로 침투하여 저출력의 자기 에너지로도 고 효율을 낼 수 있게 된다.The
따라서, 본 발명의 자석조립체(100)는 별도의 전류원 없이도 자체적으로 인체에 이로운 미세 전류를 영구히 발산하는 전기석 분말을 적정 비율로 혼합하여 전도성 수지층을 형성함으로써, 자석이 피부에서 이격된 상태에서도 영구자석에서 발산되는 자속밀도 즉, 자계와 전기석에서 발생되는 미세 전류를 균일하고 강하게 유지시킬 수 있는데 영구자석에 의한 자기장 속에서 전류가 흘러 생기는 자기장의 상호작용으로 자기력이 강화되는 것이다.Therefore, the
한편, 상기 절차에 의해 구비된 자석조립체는 그 용도에 따라 다양하게 적용할 수 있는데, 먼저 첨부된 도 3과 같이 접착부재(200)의 상부 표면 일측에 해당 자석조립체(100)를 위치하여 사용자의 특정 환부에 밀착 접착하여 사용하는데, 상기 자석조립체(100)는 접착부재(200)에 의해 특정 환부에 고정 밀착되고, 자석조립체(100)의 원적외선, 음이온이 환부로 침투되어 혈액순환 등을 통해 통증을 완화되는 효과가 있다.On the other hand, the magnet assembly provided by the above procedure can be applied in various ways according to its use. First, as shown in the attached FIG. It is used by closely adhering to a specific affected area, and the
또한, 본 발명은 첨부된 도 4와 같이 팔찌의 일측에 자석조립체(100)가 삽입하여 구비되도록 사용될 수 있는데, 이는 사용자가 팔찌 착용시 사용자의 피부와 접촉하는 면에 일정 간격으로 식각된 요부홈에 자석조립체(100)가 삽입되어 체결되어 구비함으로써 다수개의 자석조립체(100)의 유효성분을 통해 사용자에 미세전류가 발산하여 토르말린의 원적외선 및 음이온을 방출되도록 하여 인체의 면역력 강화, 게르마늄의 통증. 염증제거 및 혈액순환 등의 효과가 발휘하여 인체 내 호르몬 계통의 균형을 유지할 수 있다.In addition, the present invention can be used so that the
한편, 상기 장신구는 발찌 및 목걸이의 배면 일측에 식각된 요부홈을 구비하여 자석조립체(100)가 삽입되어 체결되어 구비되도록 형성할 수도 있다.On the other hand, the ornament may be formed such that a concave groove etched on one side of the rear surface of the anklet and necklace is provided so that the
부가적으로 본원발명은 첨부된 도 5에 도시된 바와 같이 벨트의 일면에 다수개의 자석조립체(100)가 일정간격으로 삽입되어 구비됨으로써 사용자가 벨트 착용시 벨트 면부위에 삽입된 다수개의 자석조립체(100)에 의해 그 유효성분을 향유할 수 있다.Additionally, as shown in FIG. 5, the present invention provides a plurality of
또한, 본 발명에 따른 영구자석을 이용한 고효율의 건강증진용 복합기능 자석조립체는 버클, 벨트, 팔찌, 발찌, 목걸이 등의 장신구, 액세서리, 매트, 의류, 모자, 장갑, 패치 등에 다양하게 적용 실시할 수 있으며, 상기 실시예는 여러 형태 중 원반형영구자석 N극 상부에 제1항의 기능성 물질들을 일체화시켜 외부로 노출 형성되는 반구형 지압 돌기 형태를 입체적으로 돌출(突出)된 칩(chip)을 장신구인 팔찌, 벨트 및 혈액개선을 위한 밴드부재에 적용하여 자석조립체(100)의 자력 에너지가 환부 접촉 시 강하고 빠른 경혈자극 효과를 구현하도록 한정하여 설명한 실시예를 제시한 것이다.In addition, the high-efficiency multifunctional magnet assembly for health promotion using permanent magnets according to the present invention can be applied to various accessories such as buckles, belts, bracelets, anklets, necklaces, accessories, mats, clothing, hats, gloves, patches, etc. Among various forms, in the above embodiment, a bracelet, which is an accessory, is a hemispherical acupressure projection formed by integrating the functional materials of claim 1 on the upper part of the N-pole of the disk-shaped permanent magnet to be exposed to the outside. , It is applied to a belt and a band member for blood improvement, and the magnetic energy of the
이상과 같이, 본 명세서와 도면에는 본 발명의 바람직한 실시예에 대하여 개시하였으며, 비록 특정 용어들이 사용되었으나, 이는 단지 본 발명의 기술 내용을 쉽게 설명하고 발명의 이해를 돕기 위한 일반적인 의미에서 사용된 것이지, 본 발명의 범위를 한정하고자 하는 것은 아니다. 여기에 개시된 실시예 외에도 본 발명의 기술적 사상에 바탕을 둔 다른 변형 예들이 실시 가능하다는 것은 본 발명이 속하는 기술 분야에서 통상의 지식을 가진 자에게 자명한 것이다.As described above, preferred embodiments of the present invention have been disclosed in the present specification and drawings, and although specific terms have been used, they are only used in a general sense to easily explain the technical content of the present invention and help understanding of the present invention. However, it is not intended to limit the scope of the present invention. It is obvious to those skilled in the art that other modified examples based on the technical spirit of the present invention can be implemented in addition to the embodiments disclosed herein.
100 : 자석조립체
200 : 밴드부재100: magnet assembly
200: band member
Claims (3)
토르말린 분말 4.46 중량%, 게르마늄 분말 4.46 중량% 및 은 분말 1.05 중량%을 혼합한 후, 에폭시 수지 0.84 중량%과 혼합하여 혼합물을 형성하는 재료 혼합단계;
반구형의 지압돌기 형태로 성형된 몰드 내에 89.19 중량%의 영구자석을 위치하고 영구자석 N극 또는 S극 상부에 에폭시 수지와 토르말린 분말, 게르마늄 분말 및 은 분말이 혼합된 혼합물 10.81 중량%을 주입하여 납작한 반구형의 지압돌기를 형성하는 성형단계; 및
상기 성형단계에서 구비된 납작한 반구형의 지압돌기를 소성하여 칩(chip) 형태의 자석조립체(100)를 완성하는 소성단계;를 포함하여 구비되는 것을 특징으로 하는 영구자석을 이용한 고효율의 건강증진용 복합기능 자석조립체 제조방법.
Minerals of tourmaline, germanium, and silver are individually pulverized with an air flow type grinder and powdered into fine powder. A material preparation step of forming a rare earth permanent magnet having magnetic properties of 2,500 to 3,000 gauss so as to be placed in a mold molded in the form of a hemispherical pressure protrusion;
A material mixing step of mixing 4.46% by weight of tourmaline powder, 4.46% by weight of germanium powder, and 1.05% by weight of silver powder, and then mixing them with 0.84% by weight of an epoxy resin to form a mixture;
89.19% by weight of a permanent magnet is placed in a mold molded in the form of a hemispherical acupressure protrusion, and 10.81% by weight of a mixture of epoxy resin, tourmaline powder, germanium powder, and silver powder is injected on top of the N-pole or S-pole of the permanent magnet to form a flat hemispherical shape. A molding step of forming acupressure protrusions; and
A high-efficiency health promotion complex using permanent magnets, characterized in that it is provided, including a firing step of firing the flat hemispherical acupressure protrusions provided in the molding step to complete the magnet assembly 100 in the form of a chip. Functional magnet assembly manufacturing method.
상기 소성단계를 통해 구비된 칩(chip) 형태의 자석조립체(100)는
접착부재(200)의 상부 표면 일측에 해당 칩(chip) 형태의 자석조립체(100)를 위치하여 사용자의 특정 환부에 접착부재(200)를 통해 고정 밀착되도록 사용하거나,
팔찌, 발찌 또는 목걸이에 사용자의 피부와 접촉되는 면에 일정 간격으로 식각된 요부홈에 칩(chip) 형태의 자석조립체(100)가 삽입되어 체결되도록 구비되는 것을 특징으로 하는 영구자석을 이용한 고효율의 건강증진용 복합기능 자석조립체 제조방법.
According to claim 1,
The magnet assembly 100 in the form of a chip provided through the firing step is
Place the magnet assembly 100 in the form of a chip on one side of the upper surface of the adhesive member 200 and use it to be in close contact with the specific affected part of the user through the adhesive member 200,
High-efficiency using permanent magnets, characterized in that the magnet assembly 100 in the form of a chip is inserted into concave grooves etched at regular intervals on the surface in contact with the user's skin in a bracelet, anklet or necklace to be fastened. Manufacturing method of multifunctional magnet assembly for health promotion.